JPWO2011096522A1 - リチウムイオン電池用正極活物質、リチウムイオン電池用正極、及び、リチウムイオン電池 - Google Patents

リチウムイオン電池用正極活物質、リチウムイオン電池用正極、及び、リチウムイオン電池 Download PDF

Info

Publication number
JPWO2011096522A1
JPWO2011096522A1 JP2011552835A JP2011552835A JPWO2011096522A1 JP WO2011096522 A1 JPWO2011096522 A1 JP WO2011096522A1 JP 2011552835 A JP2011552835 A JP 2011552835A JP 2011552835 A JP2011552835 A JP 2011552835A JP WO2011096522 A1 JPWO2011096522 A1 JP WO2011096522A1
Authority
JP
Japan
Prior art keywords
positive electrode
lithium ion
ion battery
active material
electrode active
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2011552835A
Other languages
English (en)
Other versions
JP5819199B2 (ja
Inventor
梶谷 芳男
芳男 梶谷
健太郎 岡本
健太郎 岡本
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JX Nippon Mining and Metals Corp
Original Assignee
JX Nippon Mining and Metals Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=44355516&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=JPWO2011096522(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by JX Nippon Mining and Metals Corp filed Critical JX Nippon Mining and Metals Corp
Priority to JP2011552835A priority Critical patent/JP5819199B2/ja
Publication of JPWO2011096522A1 publication Critical patent/JPWO2011096522A1/ja
Application granted granted Critical
Publication of JP5819199B2 publication Critical patent/JP5819199B2/ja
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

良好な電池特性を有するリチウムイオン電池用正極活物質を提供する。リチウムイオン電池用正極活物質は、組成式:LixNi1-yMyO2+α(前記式において、MはSc、Ti、V、Cr、Mn、Fe、Co、Cu、Zn、Ga、Ge、Al、Bi、Sn、Mg、Ca、B及びZrから選択される1種以上であり、0.9≦x≦1.2であり、0<y≦0.7であり、α>0.1である。)で表される。

Description

本発明は、リチウムイオン電池用正極活物質、リチウムイオン電池用正極、及び、リチウムイオン電池に関する。
リチウムイオン電池の正極活物質には、一般にリチウム含有遷移金属酸化物が用いられている。具体的には、コバルト酸リチウム(LiCoO2)、ニッケル酸リチウム(LiNiO2)、マンガン酸リチウム(LiMn24)等であり、特性改善(高容量化、サイクル特性、保存特性、内部抵抗低減、レート特性)や安全性を高めるためにこれらを複合化することが進められている。車載用やロードレベリング用といった大型用途におけるリチウムイオン電池には、これまでの携帯電話用やパソコン用とは異なった特性が求められている。
電池特性の改善には、従来、種々の方法が用いられており、例えば特許文献1には、
LixNi1-yy2-δ
(0.8≦x≦1.3、0<y≦0.5であり、Mは、Co、Mn、Fe、Cr、V、Ti、Cu、Al、Ga、Bi、Sn、Zn、Mg、Ge、Nb、Ta、Be、B、Ca、Sc及びZrからなる群から選ばれる少なくとも一種の元素を示し、δは酸素欠損又は酸素過剰量に相当し、−0.1<δ<0.1を表す。)の組成で表されるリチウムニッケル複合酸化物を分級機に通し、粒子径の大きい物と小さい物とに平衡分離粒子径Dh=1〜10μmで分離し、粒子径の大きい物と小さい物を、重量比で0:100〜100:0で配合することを特徴とするリチウム二次電池用正極材料の製造方法が開示されている。そして、これによれば、レート特性と容量のさまざまなバランスのリチウム二次電池用正極材料を容易に製造できる、と記載されている。
特許第4175026号公報
特許文献1に記載のリチウムニッケル複合酸化物は、その組成式中の酸素量が過剰のものであるが、それでもなお高品質のリチウムイオン電池用正極活物質としては改善の余地がある。
そこで、本発明は、良好な電池特性を有するリチウムイオン電池用正極活物質を提供することを課題とする。
本発明者は、鋭意検討した結果、正極活物質の酸素量と電池特性との間に密接な相関関係があることを見出した。すなわち、正極活物質の酸素量がある値以上であるとき、特に良好な電池特性が得られることを見出した。
上記知見を基礎にして完成した本発明は一側面において、
組成式:LixNi1-yy2+α
(前記式において、MはSc、Ti、V、Cr、Mn、Fe、Co、Cu、Zn、Ga、Ge、Al、Bi、Sn、Mg、Ca、B及びZrから選択される1種以上であり、0.9≦x≦1.2であり、0<y≦0.7であり、α>0.1)
で表されるリチウムイオン電池用正極活物質である。
本発明に係るリチウムイオン電池用正極活物質は一実施形態において、Mが、Mn及びCoから選択される1種以上である。
本発明に係るリチウムイオン電池用正極活物質は別の実施形態において、組成式において、α>0.15である。
本発明に係るリチウムイオン電池用正極活物質は更に別の実施形態において、組成式において、α>0.20である。
本発明に係るリチウムイオン電池用正極活物質は更に別の実施形態において、粉末X線回折で(003)面のピーク強度(Ps003)と、(104)面のピーク強度(Ps104)との比(Ps104/Ps003)が0.9以下で、且つ、(110)面の2θが64.6°以上である。
本発明に係るリチウムイオン電池用正極活物質は更に別の実施形態において、ピーク強度比(Ps104/Ps003)が0.85以下である。
本発明に係るリチウムイオン電池用正極活物質は更に別の実施形態において、(110)面の2θが64.7°以上である。
本発明に係るリチウムイオン電池用正極活物質は更に別の実施形態において、(018)面の2θが64.45°以下であり、(018)面と(110)面との2θの差が0.1°超である。
本発明は、別の側面において、本発明に係るリチウムイオン電池用正極活物質を用いたリチウムイオン電池用正極である。
本発明は、更に別の側面において、本発明に係るリチウムイオン電池用正極を用いたリチウムイオン電池である。
本発明によれば、良好な電池特性を有するリチウムイオン電池用正極活物質を提供することができる。
(リチウムイオン電池用正極活物質の構成)
本発明のリチウムイオン電池用正極活物質の材料としては、一般的なリチウムイオン電池用正極用の正極活物質として有用な化合物を広く用いることができるが、特に、コバルト酸リチウム(LiCoO2)、ニッケル酸リチウム(LiNiO2)、マンガン酸リチウム(LiMn24)等のリチウム含有遷移金属酸化物を用いるのが好ましい。このような材料を用いて作製される本発明のリチウムイオン電池用正極活物質は、
組成式:LixNi1-yy2+α
(前記式において、MはSc、Ti、V、Cr、Mn、Fe、Co、Cu、Zn、Ga、Ge、Al、Bi、Sn、Mg、Ca、B及びZrから選択される1種以上であり、0.9≦x≦1.2であり、0<y≦0.7であり、α>0.1である。)
で表される。
リチウムイオン電池用正極活物質における全金属に対するリチウムの比率が0.9〜1.2であるが、これは、0.9未満では、安定した結晶構造を保持し難く、1.2超では電池の高容量が確保できなくなるためである。
本発明のリチウムイオン電池用正極活物質は、酸素が組成式において上記のようにO2+α(α>0.1)と示され、過剰に含まれており、リチウムイオン電池に用いた場合、容量、レート特性及び容量保持率等の電池特性が良好となる。ここで、αについて、好ましくはα>0.15であり、より好ましくはα>0.20である。
本発明のリチウムイオン電池用正極活物質は、粉末X線回折で(003)面のピーク強度(Ps003)と、(104)面のピーク強度(Ps104)との比(Ps104/Ps003)が0.9以下である。ピーク強度比(Ps104/Ps003)がこのように0.9以下であると、Niの2価イオンがLiサイトに混入する、いわゆるカチオンミキシング量が少なくなるため好ましい。また、ピーク強度比(Ps104/Ps003)は、より好ましくは0.85以下である。
本発明のリチウムイオン電池用正極活物質は、(110)面の2θが64.6°以上である。(110)面の2θが64.6°以上あると、粉体の電子伝導性が向上するため好ましい。また、(110)面の2θは、より好ましくは64.7°以上である。
本発明のリチウムイオン電池用正極活物質は、(018)面の2θが、Niのモル比率が50%未満のとき64.4°以下、Niのモル比率が50%以上のときは64.45°以下であり低い角度にシフトしている。(018)面と(110)面との2θに差が生じていれば、それが大きいほど、結晶性に優れ、且つ、均一に焼成されて、酸素が結晶中で欠損していない(過剰の場合も含む)状態となっていることを示す。この点で、本発明のリチウムイオン電池用正極活物質は、(018)面と(110)面との2θの差が0.1°超であるのが好ましい。また、Niのモル比率が50%未満のとき0.6°以上、Niのモル比率が50%以上のときは0.4°以上であるのがより好ましく、いずれの場合も、両面のピーク位置の差が大きくなっている。このことは、より結晶性に優れ、且つ、均一に焼成されて、酸素が結晶中で欠損していない(過剰の場合も含む)状態となっていることを示す。
(018)面の2θは、典型的には64.2〜64.45°である。
(018)面と(110)面との2θの差は、より好ましくは0.5°超であり、典型的には0.4〜1.0°である。
リチウムイオン電池用正極活物質は、一次粒子、一次粒子が凝集して形成された二次粒子、又は、一次粒子及び二次粒子の混合物で構成されている。リチウムイオン電池用正極活物質は、その一次粒子又は二次粒子の平均粒径が2〜15μmであるのが好ましい。
平均粒径が2μm未満であると集電体への塗布が困難となる。平均粒径が15μm超であると充填時に空隙が生じやすくなり、充填性が低下する。また、平均粒径は、より好ましくは3〜10μmである。
(リチウムイオン電池用正極及びそれを用いたリチウムイオン電池の構成)
本発明の実施形態に係るリチウムイオン電池用正極は、例えば、上述の構成のリチウムイオン電池用正極活物質と、導電助剤と、バインダーとを混合して調製した正極合剤をアルミニウム箔等からなる集電体の片面または両面に設けた構造を有している。また、本発明の実施形態に係るリチウムイオン電池は、このような構成のリチウムイオン電池用正極を備えている。
(リチウムイオン電池用正極活物質の製造方法)
次に、本発明の実施形態に係るリチウムイオン電池用正極活物質の製造方法について詳細に説明する。
まず、金属塩溶液を作製する。当該金属は、Ni、及び、Sc、Ti、V、Cr、Mn、Fe、Co、Cu、Zn、Ga、Ge、Al、Bi、Sn、Mg、Ca、B及びZrから選択される1種以上である。また、金属塩は硫酸塩、塩化物、硝酸塩、酢酸塩等であり、特に硝酸塩が好ましい。これは、焼成原料中に不純物として混入してもそのまま焼成できるため洗浄工程が省けることと、硝酸塩が酸化剤として機能し、焼成原料中の金属の酸化を促進する働きがあるためである。金属塩に含まれる各金属を所望のモル比率となるように調整しておく。これにより、正極活物質中の各金属のモル比率が決定する。
次に、炭酸リチウムを純水に懸濁させ、その後、上記金属の金属塩溶液を投入して金属炭酸塩溶液スラリーを作製する。このとき、スラリー中に微小粒のリチウム含有炭酸塩が析出する。なお、金属塩として硫酸塩や塩化物等熱処理時にそのリチウム化合物が反応しない場合は飽和炭酸リチウム溶液で洗浄した後、濾別する。硝酸塩や酢酸塩のように、そのリチウム化合物が熱処理中にリチウム原料として反応する場合は洗浄せず、そのまま濾別し、乾燥することにより焼成前駆体として用いることができる。
次に、濾別したリチウム含有炭酸塩を乾燥することにより、リチウム塩の複合体(リチウムイオン電池正極材用前駆体)の粉末を得る。
次に、所定の大きさの容量を有する焼成容器を準備し、この焼成容器にリチウムイオン電池正極材用前駆体の粉末を充填する。次に、リチウムイオン電池正極材用前駆体の粉末が充填された焼成容器を、焼成炉へ移設し、焼成を行う。焼成は、酸素雰囲気下で所定時間加熱保持することにより行う。また、101〜202KPaでの加圧下で焼成を行うと、さらに組成中の酸素量が増加するため、好ましい。このとき、リチウムイオン電池正極材用前駆体の粉末として、十分に水分を除き乾燥したものを用いることにより、粉末間の空間が出来やすくなり、且つ、なるべく圧力を加えることなくこう鉢に充填することにより、酸素を十分に過剰に含む組成とすることが出来る。従来は水分の除去が不十分であると、焼成時に内部まで熱が伝わりにくく、組成が不均一となるため、こう鉢のすり切りに対して50%程度までしか充填できなかったが、上記のようにして、こう鉢に対して充填量を80%以上として焼成することにより、酸素を十分に含む組成とすることが出来る。そして、このような製法により、正極活物質の(110)面の2θ、(018)面の2θ及び(018)面と(110)面との2θの差等を制御している。
その後、焼成容器から粉末を取り出し、粉砕を行うことにより正極活物質の粉体を得る。
以下、本発明及びその利点をより良く理解するための実施例を提供するが、本発明はこれらの実施例に限られるものではない。
(実施例1〜15)
まず、表1に記載の投入量の炭酸リチウムを純水3.2リットルに懸濁させた後、金属塩溶液を4.8リットル投入した。ここで、金属塩溶液は、各金属の硝酸塩の水和物を、各金属が表1に記載の組成比になるように調整し、また全金属モル数が14モルになるように調整した。
なお、炭酸リチウムの懸濁量は、製品(リチウムイオン二次電池正極材料、すなわち正極活物質)をLixNi1-yy2+αでxが表1の値となる量であって、それぞれ次式で算出されたものである。
W(g)=73.9×14×(1+0.5X)×A
上記式において、「A」は、析出反応として必要な量の他に、ろ過後の原料に残留する炭酸リチウム以外のリチウム化合物によるリチウムの量をあらかじめ懸濁量から引いておくために掛ける数値である。「A」は、硝酸塩や酢酸塩のように、リチウム塩が焼成原料として反応する場合は0.9であり、硫酸塩や塩化物のように、リチウム塩が焼成原料として反応しない場合は1.0である。
この処理により溶液中に微小粒のリチウム含有炭酸塩が析出したが、この析出物を、フィルタープレスを使用して濾別した。
続いて、析出物を乾燥してリチウム含有炭酸塩(リチウムイオン電池正極材用前駆体)を得た。
次に、焼成容器を準備し、この焼成容器内にリチウム含有炭酸塩を充填した。次に、焼成容器を、大気圧下、酸素雰囲気炉に入れて、表1に記載の焼成温度で10時間加熱保持した後冷却して酸化物を得た。次に、得られた酸化物を解砕し、リチウムイオン二次電池正極材の粉末を得た。
(実施例16)
実施例16として、原料の各金属を表1に示すような組成とし、金属塩を塩化物とし、リチウム含有炭酸塩を析出させた後、飽和炭酸リチウム溶液で洗浄し、濾過する以外は、実施例1〜15と同様の処理を行った。
(実施例17)
実施例17として、原料の各金属を表1に示すような組成とし、金属塩を硫酸塩とし、リチウム含有炭酸塩を析出させた後、飽和炭酸リチウム溶液で洗浄し、濾過する以外は、実施例1〜15と同様の処理を行った。
(実施例18)
実施例18として、原料の各金属を表1に示すような組成とし、焼成を大気圧下ではなく1200KPaの加圧下で行った以外は、実施例1〜15と同様の処理を行った。
(比較例1〜6)
比較例1〜6として、原料の各金属を表1に示すような組成とし、酸素雰囲気炉ではなく空気雰囲気炉で焼成工程を行うことを除いて、実施例1〜15と同様の処理を行った。
(評価)
各正極材中の金属含有量は、誘導結合プラズマ発光分光分析装置(ICP−OES)で測定し、各金属の組成比(モル比)を算出した。また、酸素含有量はLECO法で測定しαを算出した。
各正極材の粉末を採取し、(003)面のピーク強度(Ps003)と、(104)面のピーク強度(Ps104)とを、粉末X線回折装置(CuKα線、電圧40V、電流30A)によって測定し、これらの比(Ps104/Ps003)を算出した。また、(110)面の2θ及び(018)面の2θを同様に粉末X線回折装置によって測定した。さらに、これらの測定結果から(018)面と(110)面との2θの差を算出した。
各正極材と、導電材と、バインダーとを85:8:7の割合で秤量し、バインダーを有機溶媒(N−メチルピロリドン)に溶解したものに、正極材料と導電材とを混合してスラリー化し、Al箔上に塗布して乾燥後にプレスして正極とした。続いて、対極をLiとした評価用の2032型コインセルを作製し、電解液に1M−LiPF6をEC−DMC(1:1)に溶解したものを用いて、電流密度0.2Cの際の放電容量を測定した。また電流密度0.2Cのときの電池容量に対する電流密度2Cのときの、放電容量の比を算出してレート特性を得た。さらに、容量保持率は、室温で1Cの放電電流で得られた初期放電容量と100サイクル後の放電容量を比較することによって測定した。
これらの結果を表1及び2に示す。
Figure 2011096522
Figure 2011096522
【0002】
示されている。そして、これによれば、レート特性と容量のさまざまなバランスのリチウム二次電池用正極材料を容易に製造できる、と記載されている。
先行技術文献
特許文献
[0004]
特許文献1:特許第4175026号公報
発明の概要
発明が解決しようとする課題
[0005]
特許文献1に記載のリチウムニッケル複合酸化物は、その組成式中の酸素量が過剰のものであるが、それでもなお高品質のリチウムイオン電池用正極活物質としては改善の余地がある。
[0006]
そこで、本発明は、良好な電池特性を有するリチウムイオン電池用正極活物質を提供することを課題とする。
課題を解決するための手段
[0007]
本発明者は、鋭意検討した結果、正極活物質の酸素量と電池特性との間に密接な相関関係があることを見出した。すなわち、正極活物質の酸素量がある値以上であるとき、特に良好な電池特性が得られることを見出した。
[0008]
上記知見を基礎にして完成した本発明は一側面において、
組成式:LiNi1−y2+α
(前記式において、Mは必須成分としてのCo、及び、Sc、Ti、V、Cr、Mn、Fe、Cu、Zn、Ga、Ge、Bi、Sn、Mg、Ca、B及びZrから選択される1種以上であり、0.9≦x≦1.2であり、0<y≦0.7であり、α≧0.1である。)
で表され、
粉末X線回折で(003)面のピーク強度(Ps003)と、(104)面のピーク強度(Ps104)との比(Ps104/Ps003)が0.9以下で、且つ、(110)面の2θが64.6°以上であるリチウムイオン電池用正極活物質である。
[0009]
本発明に係るリチウムイオン電池用正極活物質は一実施形態において、Mが、Mn及びCoから選択される1種以上である。
[0010]
本発明に係るリチウムイオン電池用正極活物質は別の実施形態において、
【0004】
発明のリチウムイオン電池用正極活物質は、
組成式:LiNi1−y2+α
(前記式において、Mは必須成分としてのCo、及び、Sc、Ti、V、Cr、Mn、Fe、Cu、Zn、Ga、Ge、Bi、Sn、Mg、Ca、B及びZrから選択される1種以上であり、0.9≦x≦1.2であり、0<y≦0.7であり、α≧0.1である。)
で表される。
リチウムイオン電池用正極活物質における全金属に対するリチウムの比率が0.9〜1.2であるが、これは、0.9未満では、安定した結晶構造を保持し難く、1.2超では電池の高容量が確保できなくなるためである。
[0020]
本発明のリチウムイオン電池用正極活物質は、酸素が組成式において上記のようにO2+α(α≧0.1)と示され、過剰に含まれており、リチウムイオン電池に用いた場合、容量、レート特性及び容量保持率等の電池特性が良好となる。ここで、αについて、好ましくはα>0.15であり、より好ましくはα>0.20である。
[0021]
本発明のリチウムイオン電池用正極活物質は、粉末X線回折で(003)面のピーク強度(Ps003)と、(104)面のピーク強度(Ps104)との比(Ps104/Ps003)が0.9以下である。ピーク強度比(Ps104/Ps003)がこのように0.9以下であると、Niの2価イオンがLiサイトに混入する、いわゆるカチオンミキシング量が少なくなるため好ましい。また、ピーク強度比(Ps104/Pa003)は、より好ましくは0.85以下である。
[0022]
本発明のリチウムイオン電池用正極活物質は、(110)面の2θが64.6°以上である。(110)面の2θが64.6°以上あると、粉体の電子伝導性が向上するため好ましい。また、(110)面の2θは、より好ましくは64.7°以上である。
[0023]
本発明のリチウムイオン電池用正極活物質は、(018)面の2θが、Niのモル比率が50%未満のとき64.4°以下、Niのモル比率が50%
【0008】
析出物を、フィルタープレスを使用して濾別した。
続いて、析出物を乾燥してリチウム含有炭酸塩(リチウムイオン電池正極材用前駆体)を得た。
次に、焼成容器を準備し、この焼成容器内にリチウム含有炭酸塩を充填した。次に、焼成容器を、大気圧下、酸素雰囲気炉に入れて、表1に記載の焼成温度で10時間加熱保持した後冷却して酸化物を得た。次に、得られた酸化物を解砕し、リチウムイオン二次電池正極材の粉末を得た。
[0031]
(実施例16)
実施例16として、原料の各金属を表1に示すような組成とし、金属塩を塩化物とし、リチウム含有炭酸塩を析出させた後、飽和炭酸リチウム溶液で洗浄し、濾過する以外は、実施例1〜15と同様の処理を行った。
[0032]
(実施例17)
実施例17として、原料の各金属を表1に示すような組成とし、金属塩を硫酸塩とし、リチウム含有炭酸塩を析出させた後、飽和炭酸リチウム溶液で洗浄し、濾過する以外は、実施例1〜15と同様の処理を行った。
[0033]
(実施例18)
実施例18として、原料の各金属を表1に示すような組成とし、焼成を大気圧下ではなく1200KPaの加圧下で行った以外は、実施例1〜15と同様の処理を行った。
[0034]
(比較例1〜6)
比較例1〜6として、原料の各金属を表1に示すような組成とし、酸素雰囲気炉ではなく空気雰囲気炉で焼成工程を行うことを除いて、実施例1〜15と同様の処理を行った。
[0035]
(評価)
各正極材中の金属含有量は、誘導結合プラズマ発光分光分析装置(ICP−OES)で測定し、各金属の組成比(モル比)を算出し、表1の通りとなることを確認した。また、酸素含有量はLECO法で測定しαを算出した。
各正極材の粉末を採取し、(003)面のピーク強度(Ps003)と、

Claims (10)

  1. 組成式:LixNi1-yy2+α
    (前記式において、MはSc、Ti、V、Cr、Mn、Fe、Co、Cu、Zn、Ga、Ge、Al、Bi、Sn、Mg、Ca、B及びZrから選択される1種以上であり、0.9≦x≦1.2であり、0<y≦0.7であり、α>0.1である。)
    で表されるリチウムイオン電池用正極活物質。
  2. 前記Mが、Mn及びCoから選択される1種以上である請求項1に記載のリチウムイオン電池用正極活物質。
  3. 前記組成式において、α>0.15である請求項1又は2に記載のリチウムイオン電池用正極活物質。
  4. 前記組成式において、α>0.20である請求項3に記載のリチウムイオン電池用正極活物質。
  5. 粉末X線回折で(003)面のピーク強度(Ps003)と、(104)面のピーク強度(Ps104)との比(Ps104/Ps003)が0.9以下で、且つ、(110)面の2θが64.6°以上である請求項1〜4のいずれかに記載のリチウムイオン電池用正極活物質。
  6. 前記ピーク強度比(Ps104/Ps003)が0.85以下である請求項5に記載のリチウムイオン電池用正極活物質。
  7. 前記(110)面の2θが64.7°以上である請求項5又は6に記載のリチウムイオン電池用正極活物質。
  8. (018)面の2θが64.45°以下であり、(018)面と(110)面との2θの差が0.1°超である請求項1〜7のいずれかに記載のリチウムイオン電池用正極活物質。
  9. 請求項1〜8のいずれかに記載のリチウムイオン電池用正極活物質を用いたリチウムイオン電池用正極。
  10. 請求項9に記載のリチウムイオン電池用正極を用いたリチウムイオン電池。
JP2011552835A 2010-02-05 2011-02-04 リチウムイオン電池用正極活物質、リチウムイオン電池用正極、及び、リチウムイオン電池 Active JP5819199B2 (ja)