JP4486966B2 - 銅合金改質用マスターアロイおよびそれを用いる鋳造方法 - Google Patents
銅合金改質用マスターアロイおよびそれを用いる鋳造方法 Download PDFInfo
- Publication number
- JP4486966B2 JP4486966B2 JP2006531691A JP2006531691A JP4486966B2 JP 4486966 B2 JP4486966 B2 JP 4486966B2 JP 2006531691 A JP2006531691 A JP 2006531691A JP 2006531691 A JP2006531691 A JP 2006531691A JP 4486966 B2 JP4486966 B2 JP 4486966B2
- Authority
- JP
- Japan
- Prior art keywords
- casting
- alloy
- mass
- copper alloy
- phase
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(A)の微細化を実現する従来手法としては、(a)〜(d)が提案されている。
(a)Ti、Zr等の微細化元素を添加させることにより、晶出物等を結晶核として作用させる手法(有効な異質核の導入)(例えば、特許文献1参照)。
(b)非常に狭い温度範囲で鋳込ことにより、過冷を利用して、均質核を生成させる方法。
(c)電磁誘導攪拌やステアリング(溶湯をかき混ぜる装置)を使用して、結晶核の生成の促進や成長してきたデンドライト(樹枝状晶)アームを切断,分断させる方法、主として(b)の手法と組み合わせて行われる。
(d)ダイキャスト等による急速凝固法や冷やし金を使用して鋳物を局部的に急速凝固させる方法。
これらは、デンドライトが成長する前に凝固させることにより結晶粒を微細化させるものである。
(e)鋳塊等の溶融固化合金材に適当な加工(圧延,伸線,鍛造等)を加えることによって付与される歪エネルギーの一部が、金属内に蓄積され、そのエネルギーの増加が再結晶核の増加をもたらすようにするものであり、それが駆動力となって結晶粒を微細化するようにしたものである(例えば、特許文献2参照)。
(f)鋳塊等の溶融固化合金材に適宜の歪エネルギーを加えた上で加熱処理を施すことにより、その加熱による蓄積エネルギーを開放した結果が再結晶粒として現れるようにしたものである。
本発明のマスターアロイは、Zrの溶湯中での残留を容易にするため、更にMg:0.01〜1%、Al:0.01〜5%、Sn:0.1〜5%、B:0.01〜0.5%、Mn:0.01〜5%、及びSi:0.01〜1%からなる群から選ばれる1種を含むのが好ましい。特に、Cuは50〜65%であって、Zrは1〜10%で上記マスターアロイを組成すると、融点を低減し、溶湯への迅速な溶け込みを実現することができるので好ましい。
また、本発明によれば、Zr及びPを含有する銅合金の溶湯を鋳造して銅合金を製造するにあたり、少なくともZrをCu−Zn−ZrまたはCu−Zn−Zr−Pの合金形態のマスターアロイで添加し、改質銅合金を鋳造することができ、上記鋳造法では、銅合金溶湯に対し結晶微細化に必要な溶湯中に金属Zr濃度を5ppm以上、好ましくは20ppm以上500ppm以下にコントロールすることが容易であるので、効率的に、初晶アルファを晶出させ、結晶粒の微細化を行うことができる。
非酸化性雰囲気で純Cuを溶かし、次に脱酸目的で、Znを添加する。そのときのZn濃度は、溶湯温度とZn蒸気圧との関係から3〜25%にする。溶湯の温度を、1100〜1200度に上げ、市販のCu−10〜60%Zrを所定量装入し、最後に低融点のZnを装入する。副成分の:B、Mg(活性金属)については、最後のZnと同時または装入後に添加する。Sn、Al、Mn、Si(純SiまたはCu-15Siで添加)、P(Cu-15Pで添加)については、最初のZn投入後または最後のZn装入と同時または装入後に所定量添加するのがよい。
これらの中間合金は、舟形、粒形等の形状に鋳込んだり、連続鋳造で棒または線形状に作られる。あるいは、大型鋳物を作って、熱間押出または、熱間圧延により線、棒、板、薄板形状に作られる。
基本的に、Zr以外の成分を所定の合金の組成範囲に入れる。原料事情を考慮に入れ、脱硫、脱酸用の添加元素:Mg、Sn、Al、Mn、Siを適宜、合金の有効成分範囲(あるいは不純物濃度以下)で追加装入し、脱硫、脱酸を念のため行う。一般的には大気と遮断するために、溶解炉、樋、タンディッシュ、ディストリビューターは木炭で被覆される。なお、微細化元素Pについては、不足分をCu-P(一般的には10〜15%P)として溶解炉に投入するほうがよい。
まず、Zrが所定の量になるようマスターアロイを溶解炉に装入する。そして、鋳造する。ところがすべて鋳造(半連続鋳造)を終了させるには、時間がかかり溶解炉等でZrが酸化ロスする。この分を補うために、鋳込み直前のタンディッシュ、ディストリビューターでZrの不足分を、数ミリ〜20mm程度の大きさの粒状マスターアロイ、または、線状、棒状のマスターアロイを連続的または一定時間ごとに追加添加する。このときのマスターアロイは、合金の鋳込み温度より当然低いものを選択する。少なくとも、タンディッシュ、ディストリビューター内で、1分間以内に撹拌なしにマスターアロイが完全に溶解するものであれば、鋳造中の溶解ロスについては予め計測しておくと、精度よくZrを添加できる。
なお、連続的に装入する場合は、早く溶融することが第1の条件になるので(第2は酸化しないこと)、1〜10%Zrを含有し、かつCu濃度が50〜65%のものが好ましく、適宜合金にあった融点を下げる副成分のマスターアロイが好ましい。一方、溶解炉に入れる場合は、早く溶けることも大切であるが、Zrのロスが少なく、Zrが酸化物および/または硫化物の形態をなさないようにすることが重要である。
この種のタイプの鋳造方法は、比較的密閉度のよい溶解炉を持っており、鋳造物を作りながら、作った鋳造物に見合う、原料を順次追加装入するタイプの溶解炉が多い。また、一度に原料を装入すると、溶解炉の温度が下がりこれは鋳造温度の低下を招くので、朝、昼、夜等の作業のつなぎ目以外にはバッチ的な原料装入は行わないのが一般的である。つまり、定常的には、温度変化が少なくなるよう少量の原料装入が通例である。この連続操業にも大きく2つの方法がある。
他は、合金に所定量のZrを含んだ(Zrロス分を考慮に入れた)インゴットを定期的に装入する。
大きな溶解炉で一度に溶解するので上記工程と基本的に同じである。異なるところとして、連続的な鋳造とよりバッチ的な鋳造の差はある。最終、取り鍋に溶湯をとり、砂型に溶湯を注ぎ込むタイプが多い。十分に脱酸、脱硫された溶湯を溶解炉の中にマスターアロイを装入するかまたは、取り鍋でマスターアロイを装入するかの相違はある。
上記マスターアロイの製造方法により以下表1〜表3に示すマスターアロイを製造する。
なお、比較例としてCu-35Zr、Cu-50Zr合金を所定量添加した。
各々のマスターアロイは、1辺が約5mmの立方体になるよう切り出し、さらに所定量になるよう再切断したものを使用した。
Claims (13)
- Cu:40〜80質量%、Zr:0.5〜35質量%、残部Znとからなる合金形態である銅合金鋳造用マスターアロイ。
- Cu:40〜80質量%、Zr:0.5〜35質量%、P:0.01〜3質量%、残部Znとからなる合金形態である銅合金鋳造用マスターアロイ。
- 更にMg:0.01〜1質量%、Al:0.01〜5質量%、Sn:0.1〜5質量%、B:0.01〜0.5質量%、Mn:0.01〜5質量%及びSi:0.01〜1質量%からなる群から選ばれる1種を含む請求項1又は2記載の銅合金鋳造用マスターアロイ。
- Cu:50〜65質量%、Zr:1〜10質量%である請求項1または2記載の銅合金鋳造用マスターアロイ。
- 舟形インゴット、棒状または線状の連続鋳造材、または棒状または線状の熱間押出材である請求項1又は2記載の銅合金鋳造用マスターアロイ。
- Zr及びPを含有する銅合金の溶湯を鋳造して銅合金を製造するにあたり、少なくともZrをCu:40〜80質量%とZr:0.5〜35質量%と残部Znとからなる合金形態またはCu:40〜80質量%とZr:0.5〜35質量%とP:0.01〜3質量%と残部Znとからなる合金形態で添加し、鋳造することを特徴とする改質銅合金の鋳造方法。
- 銅合金溶湯に対し凝固開始時P存在下に溶湯中金属Zr濃度を質量比で5ppm以上存在させる請求項6記載の改質銅合金の鋳造方法。
- ZrとPの含有量との間に0.5<P/Zr<150の関係が成立する請求項7記載の改質銅合金の鋳造方法。
- 凝固時に初晶アルファを晶出させる請求項7記載の改質銅合金の鋳造方法。
- さらに、包晶反応または共晶反応によりベータ相を晶出させる請求項9記載の改質銅合金の鋳造方法。
- さらに、固相内反応によりアルファ相マトリックス内にカッパ相、ガンマ相、デルタ相及び/又はミュー相を析出させる請求項9記載の改質銅合金の鋳造方法。
- 銅合金がCu−Zn−Zr−P、Cu−Zn−Si−Zr−P、Cu−Zn−Sn−Zr−P,Cu−Zn−Al−Zr−P,Cu−Zn−Bi−Zr−P,Cu−Zn−Pb−Zr−P,Cu−Zn−Si−Mn−Zr−P、Cu−Zn−Si−Pb−Zr−P,Cu−Zn−Si−Sn−Zr−P,Cu−Zn−Si−Al−Zr−P,Cu−Zn−Sn−Pb−Zr−P,Cu−Zn−Sn−Bi−Zr−P,Cu−Zn−Sn−Al−Zr−P,Cu−Sn−Zr−P,Cu−Sn−Pb−Zr−P,Cu−Sn−Bi−Zr−P,Cu−Al−Zr−P,Cu−Al−Si−Zr−P,Cu−Si−Zr−P,Cu−Cr−Zr−P,Cu−Pb−Zr−P,Cu−P−Zr−P,及びCu−Te−Zr−Pからなる群から選ばれる1種である請求項6記載の改質銅合金の鋳造方法。
- 銅合金が60<Cu−3.5Si−1.8Al−0.5X+0.5Y+Mn<90(但し、XはSn,Sb,As、Mg;YはPb,Bi,Se,Te,Cr)を満たす請求項12記載の改質銅合金の鋳造方法。