US20090098012A1 - High-Purity Tin or Tin Alloy and Process for Producing High-Purity Tin - Google Patents
High-Purity Tin or Tin Alloy and Process for Producing High-Purity Tin Download PDFInfo
- Publication number
- US20090098012A1 US20090098012A1 US11/916,906 US91690606A US2009098012A1 US 20090098012 A1 US20090098012 A1 US 20090098012A1 US 91690606 A US91690606 A US 91690606A US 2009098012 A1 US2009098012 A1 US 2009098012A1
- Authority
- US
- United States
- Prior art keywords
- tin
- high purity
- less
- cph
- respective contents
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
- ATJFFYVFTNAWJD-UHFFFAOYSA-N Tin Chemical compound [Sn] ATJFFYVFTNAWJD-UHFFFAOYSA-N 0.000 title claims abstract description 122
- 238000000034 method Methods 0.000 title description 6
- 230000005260 alpha ray Effects 0.000 claims abstract description 42
- 238000004519 manufacturing process Methods 0.000 claims abstract description 35
- 229910052776 Thorium Inorganic materials 0.000 claims abstract description 34
- 229910052770 Uranium Inorganic materials 0.000 claims abstract description 34
- 229910001128 Sn alloy Inorganic materials 0.000 claims abstract description 28
- 229910052797 bismuth Inorganic materials 0.000 claims abstract description 27
- 229910052745 lead Inorganic materials 0.000 claims abstract description 26
- 229910052799 carbon Inorganic materials 0.000 claims abstract description 12
- 229910052757 nitrogen Inorganic materials 0.000 claims abstract description 8
- 229910052739 hydrogen Inorganic materials 0.000 claims abstract description 7
- 229910052760 oxygen Inorganic materials 0.000 claims abstract description 7
- 229910052698 phosphorus Inorganic materials 0.000 claims abstract description 7
- 229910052717 sulfur Inorganic materials 0.000 claims abstract description 7
- 239000008151 electrolyte solution Substances 0.000 claims description 19
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 claims description 17
- 239000002994 raw material Substances 0.000 claims description 16
- 238000007670 refining Methods 0.000 claims description 16
- 239000012535 impurity Substances 0.000 claims description 14
- 239000002253 acid Substances 0.000 claims description 4
- 239000003463 adsorbent Substances 0.000 claims description 4
- 238000002386 leaching Methods 0.000 claims description 2
- 239000000463 material Substances 0.000 abstract description 45
- 239000004065 semiconductor Substances 0.000 abstract description 41
- 238000005476 soldering Methods 0.000 abstract description 4
- 230000005855 radiation Effects 0.000 description 28
- 238000005868 electrolysis reaction Methods 0.000 description 26
- 230000002285 radioactive effect Effects 0.000 description 20
- 239000002245 particle Substances 0.000 description 19
- 239000000654 additive Substances 0.000 description 17
- 230000000996 additive effect Effects 0.000 description 17
- QAOWNCQODCNURD-UHFFFAOYSA-N Sulfuric acid Chemical compound OS(O)(=O)=O QAOWNCQODCNURD-UHFFFAOYSA-N 0.000 description 16
- XKRFYHLGVUSROY-UHFFFAOYSA-N Argon Chemical compound [Ar] XKRFYHLGVUSROY-UHFFFAOYSA-N 0.000 description 14
- 239000012298 atmosphere Substances 0.000 description 14
- 229910052709 silver Inorganic materials 0.000 description 14
- VEXZGXHMUGYJMC-UHFFFAOYSA-N Hydrochloric acid Chemical compound Cl VEXZGXHMUGYJMC-UHFFFAOYSA-N 0.000 description 13
- 239000000956 alloy Substances 0.000 description 11
- 239000007789 gas Substances 0.000 description 11
- PXHVJJICTQNCMI-UHFFFAOYSA-N Nickel Chemical compound [Ni] PXHVJJICTQNCMI-UHFFFAOYSA-N 0.000 description 10
- 229910045601 alloy Inorganic materials 0.000 description 10
- 239000010949 copper Substances 0.000 description 10
- LBDSXVIYZYSRII-IGMARMGPSA-N alpha-particle Chemical compound [4He+2] LBDSXVIYZYSRII-IGMARMGPSA-N 0.000 description 9
- 230000003247 decreasing effect Effects 0.000 description 9
- 239000011701 zinc Substances 0.000 description 9
- 230000000052 comparative effect Effects 0.000 description 8
- 238000005516 engineering process Methods 0.000 description 8
- 229910052725 zinc Inorganic materials 0.000 description 8
- 229910052786 argon Inorganic materials 0.000 description 7
- 229910052802 copper Inorganic materials 0.000 description 7
- 229910052713 technetium Inorganic materials 0.000 description 6
- GKLVYJBZJHMRIY-UHFFFAOYSA-N technetium atom Chemical compound [Tc] GKLVYJBZJHMRIY-UHFFFAOYSA-N 0.000 description 6
- 239000004332 silver Substances 0.000 description 5
- 229910000679 solder Inorganic materials 0.000 description 5
- GWEVSGVZZGPLCZ-UHFFFAOYSA-N Titan oxide Chemical compound O=[Ti]=O GWEVSGVZZGPLCZ-UHFFFAOYSA-N 0.000 description 4
- 229910052759 nickel Inorganic materials 0.000 description 4
- XOLBLPGZBRYERU-UHFFFAOYSA-N tin dioxide Chemical compound O=[Sn]=O XOLBLPGZBRYERU-UHFFFAOYSA-N 0.000 description 4
- 229910001887 tin oxide Inorganic materials 0.000 description 4
- RYGMFSIKBFXOCR-UHFFFAOYSA-N Copper Chemical compound [Cu] RYGMFSIKBFXOCR-UHFFFAOYSA-N 0.000 description 3
- HCHKCACWOHOZIP-UHFFFAOYSA-N Zinc Chemical compound [Zn] HCHKCACWOHOZIP-UHFFFAOYSA-N 0.000 description 3
- 239000003153 chemical reaction reagent Substances 0.000 description 3
- 230000000694 effects Effects 0.000 description 3
- 229910052751 metal Inorganic materials 0.000 description 3
- 239000002184 metal Substances 0.000 description 3
- OGIDPMRJRNCKJF-UHFFFAOYSA-N titanium oxide Inorganic materials [Ti]=O OGIDPMRJRNCKJF-UHFFFAOYSA-N 0.000 description 3
- IJGRMHOSHXDMSA-UHFFFAOYSA-N Atomic nitrogen Chemical compound N#N IJGRMHOSHXDMSA-UHFFFAOYSA-N 0.000 description 2
- 229910017770 Cu—Ag Inorganic materials 0.000 description 2
- KRHYYFGTRYWZRS-UHFFFAOYSA-N Fluorane Chemical compound F KRHYYFGTRYWZRS-UHFFFAOYSA-N 0.000 description 2
- GRYLNZFGIOXLOG-UHFFFAOYSA-N Nitric acid Chemical compound O[N+]([O-])=O GRYLNZFGIOXLOG-UHFFFAOYSA-N 0.000 description 2
- 229910020836 Sn-Ag Inorganic materials 0.000 description 2
- 229910020994 Sn-Zn Inorganic materials 0.000 description 2
- 229910020988 Sn—Ag Inorganic materials 0.000 description 2
- 229910009069 Sn—Zn Inorganic materials 0.000 description 2
- 238000005219 brazing Methods 0.000 description 2
- 238000005266 casting Methods 0.000 description 2
- AUYOHNUMSAGWQZ-UHFFFAOYSA-L dihydroxy(oxo)tin Chemical compound O[Sn](O)=O AUYOHNUMSAGWQZ-UHFFFAOYSA-L 0.000 description 2
- 239000000945 filler Substances 0.000 description 2
- 229910017604 nitric acid Inorganic materials 0.000 description 2
- TWNQGVIAIRXVLR-UHFFFAOYSA-N oxo(oxoalumanyloxy)alumane Chemical compound O=[Al]O[Al]=O TWNQGVIAIRXVLR-UHFFFAOYSA-N 0.000 description 2
- 238000000746 purification Methods 0.000 description 2
- ZSLUVFAKFWKJRC-IGMARMGPSA-N 232Th Chemical compound [232Th] ZSLUVFAKFWKJRC-IGMARMGPSA-N 0.000 description 1
- BQCADISMDOOEFD-UHFFFAOYSA-N Silver Chemical compound [Ag] BQCADISMDOOEFD-UHFFFAOYSA-N 0.000 description 1
- 229910021607 Silver chloride Inorganic materials 0.000 description 1
- 229910020816 Sn Pb Inorganic materials 0.000 description 1
- 229910020922 Sn-Pb Inorganic materials 0.000 description 1
- 229910008783 Sn—Pb Inorganic materials 0.000 description 1
- 229910052783 alkali metal Inorganic materials 0.000 description 1
- 238000005275 alloying Methods 0.000 description 1
- 229910052787 antimony Inorganic materials 0.000 description 1
- 239000007864 aqueous solution Substances 0.000 description 1
- 239000012300 argon atmosphere Substances 0.000 description 1
- 229910052788 barium Inorganic materials 0.000 description 1
- 239000000919 ceramic Substances 0.000 description 1
- 229910052804 chromium Inorganic materials 0.000 description 1
- 238000004140 cleaning Methods 0.000 description 1
- 238000007865 diluting Methods 0.000 description 1
- 238000004090 dissolution Methods 0.000 description 1
- 238000005363 electrowinning Methods 0.000 description 1
- 230000008030 elimination Effects 0.000 description 1
- 238000003379 elimination reaction Methods 0.000 description 1
- 238000001704 evaporation Methods 0.000 description 1
- 230000008020 evaporation Effects 0.000 description 1
- 238000001914 filtration Methods 0.000 description 1
- 239000010439 graphite Substances 0.000 description 1
- 229910002804 graphite Inorganic materials 0.000 description 1
- 229910001385 heavy metal Inorganic materials 0.000 description 1
- 238000010348 incorporation Methods 0.000 description 1
- 239000002440 industrial waste Substances 0.000 description 1
- 239000011261 inert gas Substances 0.000 description 1
- 239000004615 ingredient Substances 0.000 description 1
- 238000002955 isolation Methods 0.000 description 1
- 229910052748 manganese Inorganic materials 0.000 description 1
- 238000005259 measurement Methods 0.000 description 1
- 238000002844 melting Methods 0.000 description 1
- 230000008018 melting Effects 0.000 description 1
- 238000012986 modification Methods 0.000 description 1
- 230000004048 modification Effects 0.000 description 1
- 229910052758 niobium Inorganic materials 0.000 description 1
- 239000012299 nitrogen atmosphere Substances 0.000 description 1
- 229910052699 polonium Inorganic materials 0.000 description 1
- HZEBHPIOVYHPMT-UHFFFAOYSA-N polonium atom Chemical compound [Po] HZEBHPIOVYHPMT-UHFFFAOYSA-N 0.000 description 1
- 229910052700 potassium Inorganic materials 0.000 description 1
- 238000001556 precipitation Methods 0.000 description 1
- 239000012857 radioactive material Substances 0.000 description 1
- 229910052704 radon Inorganic materials 0.000 description 1
- SYUHGPGVQRZVTB-UHFFFAOYSA-N radon atom Chemical compound [Rn] SYUHGPGVQRZVTB-UHFFFAOYSA-N 0.000 description 1
- 229910052710 silicon Inorganic materials 0.000 description 1
- HKZLPVFGJNLROG-UHFFFAOYSA-M silver monochloride Chemical compound [Cl-].[Ag+] HKZLPVFGJNLROG-UHFFFAOYSA-M 0.000 description 1
- 229910052708 sodium Inorganic materials 0.000 description 1
- 239000007787 solid Substances 0.000 description 1
- 229910052712 strontium Inorganic materials 0.000 description 1
- 239000000126 substance Substances 0.000 description 1
- 239000000758 substrate Substances 0.000 description 1
- 239000000725 suspension Substances 0.000 description 1
- 229910052715 tantalum Inorganic materials 0.000 description 1
- 229910052723 transition metal Inorganic materials 0.000 description 1
- JFALSRSLKYAFGM-UHFFFAOYSA-N uranium(0) Chemical compound [U] JFALSRSLKYAFGM-UHFFFAOYSA-N 0.000 description 1
- 229910052720 vanadium Inorganic materials 0.000 description 1
- 229910052726 zirconium Inorganic materials 0.000 description 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22B—PRODUCTION AND REFINING OF METALS; PRETREATMENT OF RAW MATERIALS
- C22B25/00—Obtaining tin
- C22B25/04—Obtaining tin by wet processes
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22B—PRODUCTION AND REFINING OF METALS; PRETREATMENT OF RAW MATERIALS
- C22B25/00—Obtaining tin
- C22B25/08—Refining
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C13/00—Alloys based on tin
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
- C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
- C22F1/16—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of other metals or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25C—PROCESSES FOR THE ELECTROLYTIC PRODUCTION, RECOVERY OR REFINING OF METALS; APPARATUS THEREFOR
- C25C1/00—Electrolytic production, recovery or refining of metals by electrolysis of solutions
- C25C1/14—Electrolytic production, recovery or refining of metals by electrolysis of solutions of tin
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25F—PROCESSES FOR THE ELECTROLYTIC REMOVAL OF MATERIALS FROM OBJECTS; APPARATUS THEREFOR
- C25F1/00—Electrolytic cleaning, degreasing, pickling or descaling
- C25F1/02—Pickling; Descaling
- C25F1/04—Pickling; Descaling in solution
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22B—PRODUCTION AND REFINING OF METALS; PRETREATMENT OF RAW MATERIALS
- C22B13/00—Obtaining lead
- C22B13/06—Refining
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
- H01L2224/00—Indexing scheme for arrangements for connecting or disconnecting semiconductor or solid-state bodies and methods related thereto as covered by H01L24/00
- H01L2224/01—Means for bonding being attached to, or being formed on, the surface to be connected, e.g. chip-to-package, die-attach, "first-level" interconnects; Manufacturing methods related thereto
- H01L2224/10—Bump connectors; Manufacturing methods related thereto
- H01L2224/12—Structure, shape, material or disposition of the bump connectors prior to the connecting process
- H01L2224/13—Structure, shape, material or disposition of the bump connectors prior to the connecting process of an individual bump connector
- H01L2224/13001—Core members of the bump connector
- H01L2224/13099—Material
- H01L2224/131—Material with a principal constituent of the material being a metal or a metalloid, e.g. boron [B], silicon [Si], germanium [Ge], arsenic [As], antimony [Sb], tellurium [Te] and polonium [Po], and alloys thereof
- H01L2224/13101—Material with a principal constituent of the material being a metal or a metalloid, e.g. boron [B], silicon [Si], germanium [Ge], arsenic [As], antimony [Sb], tellurium [Te] and polonium [Po], and alloys thereof the principal constituent melting at a temperature of less than 400°C
- H01L2224/13111—Tin [Sn] as principal constituent
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
- H01L23/00—Details of semiconductor or other solid state devices
- H01L23/48—Arrangements for conducting electric current to or from the solid state body in operation, e.g. leads, terminal arrangements ; Selection of materials therefor
- H01L23/482—Arrangements for conducting electric current to or from the solid state body in operation, e.g. leads, terminal arrangements ; Selection of materials therefor consisting of lead-in layers inseparably applied to the semiconductor body
- H01L23/4827—Materials
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
- H01L2924/00—Indexing scheme for arrangements or methods for connecting or disconnecting semiconductor or solid-state bodies as covered by H01L24/00
- H01L2924/0001—Technical content checked by a classifier
- H01L2924/00011—Not relevant to the scope of the group, the symbol of which is combined with the symbol of this group
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
- H01L2924/00—Indexing scheme for arrangements or methods for connecting or disconnecting semiconductor or solid-state bodies as covered by H01L24/00
- H01L2924/0001—Technical content checked by a classifier
- H01L2924/00014—Technical content checked by a classifier the subject-matter covered by the group, the symbol of which is combined with the symbol of this group, being disclosed without further technical details
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
- H01L2924/00—Indexing scheme for arrangements or methods for connecting or disconnecting semiconductor or solid-state bodies as covered by H01L24/00
- H01L2924/10—Details of semiconductor or other solid state devices to be connected
- H01L2924/102—Material of the semiconductor or solid state bodies
- H01L2924/1025—Semiconducting materials
- H01L2924/10251—Elemental semiconductors, i.e. Group IV
- H01L2924/10253—Silicon [Si]
Definitions
- the present invention relates to high purity tin or tin alloy with a reduced ⁇ dose of tin to be used in the manufacture of semiconductor manufacturing equipment or the like, and to the manufacturing method of such high purity tin.
- tin is a material that is used in the manufacture of semiconductors, and in particular is a primary ingredient of a solder material.
- soldering is used to bond the semiconductor chip and substrate, to bond or seal a Si chip such as an IC or LSI to or in a lead frame or a ceramics package, to form bumps during TAB (Tape Automated Bonding) or during the manufacture of flip chips, or on semiconductor wiring materials.
- Patent Document 1 describes a manufacturing method of low ⁇ ray tin including the steps of alloying tin and lead having an ⁇ dose of 10 cph/cm 2 or less, and thereafter removing the lead contained in the tin by refining.
- the object of this technology is to reduce the ⁇ dose by diluting the 210 Pb in the tin through the addition of high purity Pb. Nevertheless, in the foregoing case, such a complicated process is required as to additionally remove Pb after adding to the tin.
- the numerical value of the ⁇ dose is considerably low after the lapse of 3 years after refining the tin, this can also be comprehended as not being able to use the tin with the low ⁇ dose until 3 years has lapsed from the refining of the tin, and it cannot be said that this is an industrially efficient method.
- Patent Document 2 describes that the radiation ⁇ particle count can be reduced to 0.5 cph/cm 2 or less by adding 10 to 5000 ppm of a material selected among Na, Sr, K, Cr, Nb, Mn, V, Ta, Si, Zr and Ba to a Sn—Pb alloy solder.
- the radiation ⁇ particle count could only be reduced to a level of 0.015 cph/cm 2 , and this has not achieved a promising level as a present-day material for semiconductor devices.
- Patent Document 3 describes reducing the count of radiation ⁇ particles emitted from solder ultra fine wires to 0.5 cph/cm 2 or less, and using the same as the connection wiring of semiconductor devices. Nevertheless, this kind of count level of radiation ⁇ particles is not at a level as a present-day material for semiconductor devices.
- Patent Document 4 describes using highly refined sulfuric acid such as top-grade sulfuric acid and highly refined hydrochloric acid such as top-grade hydrochloric acid in order to obtain an electrolytic solution, and using high purity tin as the anode to perform electrolysis so as to obtain high purity tin having low lead concentration and a lead ⁇ ray count of 0.005 cph/cm 2 or less. It goes without saying that a high purity material can be obtained by using a high purity raw material (reagent) without regard to cost, but the lowest ⁇ ray count of the deposited tin indicated in the Examples of Patent Document 4 is 0.002 cph/cm 2 , and an expected level cannot be achieved despite the high cost.
- Patent Document 5 describes a manufacturing method for obtaining metallic tin of 5N or higher through electrowinning performed with the electrolytic solution that is obtained according to the procedures, which are precipitation of metastannic acid by adding nitric acid to a heated aqueous solution previously added with crude metallic tin, filtration, cleaning, and thereafter dissolution of such metastannic acid in hydrochloric acid or hydrofluoric acid.
- this technology vaguely describes its application in semiconductor devices, there is no specific reference to the limitation of U and Th as the radioactive elements or the radiation ⁇ particle count, and it could be said that the interest concerning the foregoing limitation is of a low level in Patent Document 5.
- Patent Document 6 describes technology of reducing the amount of Pb contained in Sn constituting the solder alloy, and using Bi, Sb, Ag or Zn as the alloy material. Nevertheless, even if the amount of Pb is reduced as much as possible in the foregoing case, Patent Document 6 does not particularly disclose any means for fundamentally overcoming the problem of the radiation ⁇ particle count caused by Pb that gets mixed in inevitably.
- Patent Document 7 discloses tin having a grade of 99.99% or higher and a radiation ⁇ particle count of 0.03 cph/cm 2 or less manufactured by performing electrolysis using a top-grade sulfuric acid reagent. Also in this case, it goes without saying that a high purity material can be obtained by using a high purity raw material (reagent) without regard to cost, but the lowest ⁇ ray count of the deposited tin indicated in the Examples of Patent Document 7 is 0.003 cph/cm 2 , and an expected level cannot be achieved despite the high cost.
- Patent Document 8 describes lead as a brazing filler metal for use in semiconductor devices having a grade of 4N or higher, radioisotope of less than 50 ppm, and a radiation ⁇ particle count of 0.5 cph/cm 2 or less.
- Patent Document 9 describes tin as a brazing filler metal for use in semiconductor devices having a grade of 99.95% or higher, radioisotope of less than 30 ppm, and a radiation ⁇ particle count of 0.2 cph/cm 2 or less.
- Patent Document 8 and Patent Document 9 have a lenient allowable value concerning the radiation ⁇ particle count, and there is a problem in that the technology described in these Documents is not at a level as a present-day material for semiconductor devices.
- Patent Document 10 shows an example of Sn having a purity of 99.999% (5N), this Sn is to be used as a metal plug material for a seismic isolation structure, and there is no description concerning the limitation of U and Th as the radioactive elements or the radiation ⁇ particle count. This kind of material cannot be used as a material for assembling semiconductor devices.
- Patent Document 11 discloses a method of eliminating technetium from nickel contaminated with a large quantity of technetium (Tc), uranium and thorium by using graphite or activated carbon powder.
- Tc technetium
- uranium and thorium by using graphite or activated carbon powder.
- technetium will follow nickel and codeposit on the cathode, and cannot be separated from such cathode.
- technetium as the radioactive material contained in the nickel cannot be eliminated with electrolytic refining.
- the technology of Patent Document 11 relates specifically to nickel contaminated with technetium, and cannot be applied to other substances.
- Patent Document 11 merely relates to low-level technology in terms of high purification of treating industrial wastes that are harmful to the human body, and is not at a level as a material for semiconductor devices.
- an object of the present invention is to provide high purity tin or tin alloy and the manufacturing method of such high purity tin by reducing the ⁇ dose of tin so as to be adaptable as the foregoing material.
- the present invention provides high purity tin or tin alloy wherein the respective contents of U and Th as radioactive elements are 5 ppb or less, the respective contents of Pb and Bi that emit radiation ⁇ particles are 1 ppm or less, and the purity is 5N or higher (provided that this excludes the gas components of O, C, N, H, S and P).
- the present invention aims at eliminating as much as possible the influence of the ⁇ ray on semiconductor chips. (Incidentally, the signs of %, ppm and ppb used herein all represent weight (wt).)
- the high purity tin or tin alloy of the present invention is ultimately manufactured by being rolled and cut when needed as well as being dissolved and cast. It is desirable that the ⁇ ray count of such high purity tin is 0.001 cph/cm 2 or less.
- the high purity tin or tin alloy of the present invention realizes the foregoing numerical value.
- the manufacture of high purity tin is particularly important in the present invention, and, as a manufacturing method of such high purity tin, the present invention includes the steps of leaching tin as the raw material with acid (sulfuric acid, for instance), using the obtained leachate as an electrolytic solution, suspending an adsorbent of impurities in the electrolytic solution, and performing electrolytic refining using a raw material Sn anode so as to obtain high purity tin wherein the respective contents of U and Th as radioactive elements are 5 ppb or less, the respective contents of Pb and Bi that emit radiation ⁇ particles are 1 ppm or less, and the purity is 5N or higher (provided that this excludes the gas components of O, C, N, H, S and P).
- acid sulfuric acid
- Oxides such as titanium oxide, aluminum oxide and tin oxide, activated carbon and carbon may be used as the adsorbent to be suspended in the electrolytic solution.
- the high purity tin obtained based on the foregoing electrolytic refining is dissolved and cast at 250 to 500° C., and the ⁇ ray count of the cast ingot after the lapse of 6 months or longer is made to be 0.001 cph/cm 2 or less.
- the lapse of 6 months or longer is required for the foregoing impurities and ⁇ dose to stabilize.
- the ⁇ ray count stabilizes at 0.001 cph/cm 2 or less after the lapse of 6 months or longer.
- the additive component (alloy component) of high purity tin alloy silver, copper, zinc and the like may be used, but the additive component (alloy component) is not limited to the foregoing elements.
- the standard additive amount is 0.1 to 20 wt %, there is no limitation on this amount either. It is necessary to similarly use high purity materials.
- the high purity tin or tin alloy of the present invention has a purity of 5N or higher (provided that this excludes the gas components of O, C, N, H, S and P), and is further characterized in that the respective contents of U and Th as the radioactive elements are 5 ppb or less, and the respective contents of Pb and Bi that emit radiation ⁇ particles are 1 ppm or less, and it is therefore possible to eliminate as much as possible the influence of the ⁇ ray on semiconductor chips.
- the high purity tin or tin alloy of the present invention is ultimately manufactured by being dissolved and cast, and it yields a superior effect in that it is able to make the ⁇ ray count of such high purity tin 0.001 cph/cm 2 or less. It is thereby possible to considerably reduce the occurrence of soft errors caused by the influence of ⁇ rays of the semiconductor device.
- the raw material tin commercially available tin having a purity level of 2 to 3N is used.
- the raw material tin does not have to be limited to the foregoing commercially available product.
- the raw material tin is leached with acid, and the obtained leachate is used as the electrolytic solution.
- the acid to be used hydrochloric acid, sulfuric acid and the like are preferably used.
- Sn having a purity level of 2 to 4N is used as the anode. Subsequently, electrolysis is performed under the conditions of electrolysis temperature of 10 to 80° C., and current density of 0.1 to 50 A/dm 2 .
- Oxides such as titanium oxide, aluminum oxide, tin oxide and the like, activated carbon and carbon are suspended in the electrolytic solution in order to adsorb the impurities. This is particularly effective in eliminating Pb and Bi.
- the deposited electrolytic tin is dissolved and cast at a temperature of 250 to 500° C. to prepare a tin ingot.
- This temperature range is effective in eliminating the radioactive elements such as Po. If the temperature is below 250° C. and directly on the melting point, this is not preferable since casting is difficult, and if the temperature exceeds 500° C., this is not preferable since Sn will evaporate. Therefore, the electrolytic tin is dissolved and cast within the foregoing temperature range.
- the cast tin ingot was stored for 6 months in an inert gas atmosphere or a vacuum (reduced pressure).
- the ⁇ dose decreased and it was possible to make it 0.001 cph/cm 2 or less.
- the high purity tin or tin alloy of the present invention obtained as described above yields a superior effect of being able to considerably reduce the occurrence of soft errors caused by the influence of ⁇ rays of the semiconductor device.
- Raw material tin was leached with sulfuric acid, and the obtained leachate was used as the electrolytic solution. Sn having a purity level of 3N was used as the anode. Electrolysis was performed thereto under the conditions of electrolysis temperature of 20° C. and current density of 1 A/dm 2 . The analytical values of the raw material tin are shown in Table 1.
- titanium oxide TiO 2
- the Pb content was 0.7 ppm and the Bi content was 0.1 ppm.
- the respective contents of U and Th were less than 5 ppb.
- the reason why Pb and Bi as impurities decreased is because they were adsorbed to the suspended titanium oxide, and the reason why U and Th as impurities decreased is because of the electrolysis.
- the deposited electrolytic tin was dissolved and cast at a temperature of 260° C. to prepare a tin ingot.
- the cast tin ingot was stored for 6 months in an argon gas atmosphere.
- the ⁇ ray count was 0.0007 cph/cm 2 .
- the analytical values of the refined tin are similarly shown in Table 1.
- Raw material tin was leached with sulfuric acid, and the obtained leachate was used as the electrolytic solution.
- the same Sn as Example 1 having a purity level of 3N was used as the anode. Electrolysis was performed thereto under the conditions of electrolysis temperature of 25° C. and current density of 3 A/dm 2 .
- the deposited electrolytic tin was dissolved and cast at a temperature of 500° 0 C. to prepare a tin ingot.
- the cast tin ingot was stored for 10 months in a nitrogen atmosphere.
- the ⁇ ray count was 0.0005 cph/cm 2 .
- the analytical values of the refined tin are similarly shown in Table 1.
- Raw material tin was leached with hydrochloric acid, and the obtained leachate was used as the electrolytic solution.
- the same Sn as Example 1 having a purity level of 3N was used as the anode. Electrolysis was performed thereto under the conditions of electrolysis temperature of 50° C. and current density of 10 A/dm 2 .
- the deposited electrolytic tin was dissolved and cast at a temperature of 350° C. to prepare a tin ingot.
- the cast tin ingot was stored for 20 months in a vacuum.
- the ⁇ ray count was 0.0009 cph/cm 2 .
- the analytical values of the refined tin are similarly shown in Table 1.
- Raw material tin was leached with hydrochloric acid, and the obtained leachate was used as the electrolytic solution.
- the same Sn as Example 1 having a purity level of 3N was used as the anode. Electrolysis was performed thereto under the conditions of electrolysis temperature of 40° C. and current density of 15 A/dm 2 .
- the deposited electrolytic tin was dissolved and cast at a temperature of 400° C. to prepare a tin ingot.
- the cast tin ingot was stored for 50 months in a desiccator.
- the ⁇ ray count was less than 0.0005 cph/cm 2 .
- the analytical values of the refined tin are similarly shown in Table 1.
- a suspension material was not placed in the electrolytic solution.
- the Pb content was 200 ppm and the Bi content was 20 ppm.
- the respective contents of U and Th were 0.01 ppb and 0.006 ppb. This resulted in an impurity level that was not much different from the raw material.
- the deposited electrolytic tin was dissolved and cast at a temperature of 240° C. to prepare a tin ingot.
- the cast tin ingot was stored for 6 months in an argon atmosphere.
- the ⁇ ray count was 8.0 cph/cm 2 .
- the analytical values of the refined tin are similarly shown in Table 1.
- the high purity tin manufactured in Example 1 was prepared.
- As the additive elements of tin alloy in this Example commercially available silver and copper were purified through electrolysis to obtain Ag of 5N5 and Cu of 6N. These additive elements were added to the foregoing high purity tin, which was dissolved and cast in an inert atmosphere at a temperature of 260° C. to manufacture a Sn—Cu—Ag alloy ingot comprised of 0.5% Cu, 3% Ag and remnant Sn.
- the cast tin ingot was stored for 6 months in an argon gas atmosphere.
- the ⁇ ray count was 0.0007 cph/cm 2 .
- the analytical values of the tin alloy are shown in Table 2.
- the high purity tin manufactured in Example 1 was prepared.
- As the additive element of tin alloy in this Example commercially available Ag was dissolved in nitric acid, HCl was added thereto to deposit AgCl, and this was further subject to nitrogen reduction to obtain high purity Ag of 5N.
- This additive element was added to the foregoing high purity tin, which was dissolved and cast in an inert atmosphere at a temperature of 260° C. to manufacture a Sn—Ag alloy ingot comprised of 3.5% Ag and remnant Sn.
- the cast tin ingot was stored for 6 months in an argon gas atmosphere.
- the ⁇ ray count was 0.0005 cph/cm 2 .
- the analytical values of the tin alloy are shown in Table 2.
- the high purity tin manufactured in Example 1 was prepared.
- As the additive elements of tin alloy in this Example commercially available silver and zinc were purified through electrolysis to obtain Zn of 6N. These additive elements were added to the foregoing high purity tin, which was dissolved and cast in an inert atmosphere at a temperature of 260° C. to manufacture a Sn—Zn alloy ingot comprised of 9% Zn and remnant Sn.
- the cast tin ingot was stored for 6 months in an argon gas atmosphere.
- the ⁇ ray count was 0.0008 cph/cm 2 .
- the analytical values of the tin alloy are shown in Table 2.
- the high purity tin manufactured in Example 1 was prepared.
- As the additive elements of tin alloy in this Example commercially available silver and copper having a purity level of 3N were used. These additive elements were added to the foregoing high purity tin, which was dissolved and cast in an inert atmosphere at a temperature of 260° C. to manufacture a Sn—Cu—Ag alloy ingot comprised of 0.5% Cu, 3% Ag and remnant Sn.
- the cast tin ingot was stored for 6 months in an argon gas atmosphere.
- the ⁇ ray count was 0.1 cph/cm 2 .
- the analytical values of the tin alloy are shown in Table 2.
- the high purity tin manufactured in Example 1 was prepared.
- As the additive element of tin alloy in this Example commercially available Ag having a purity level of 3N was used. This additive element was added to the foregoing high purity tin, which was dissolved and cast in an inert atmosphere at a temperature of 260° C. to manufacture a Sn—Ag alloy ingot comprised of 3.5% Ag and remnant Sn.
- the cast tin ingot was stored for 6 months in an argon gas atmosphere.
- the ⁇ ray count was 0.03 cph/cm 2 .
- the analytical values of the tin alloy are shown in Table 2.
- the high purity tin manufactured in Example 1 was prepared.
- As the additive elements of tin alloy in this Example commercially available silver and zinc having a purity level of 3N were used. These additive elements were added to the foregoing high purity tin, which was dissolved and cast in an inert atmosphere at a temperature of 260° C. to manufacture a Sn—Zn alloy ingot comprised of 9% Zn and remnant Sn.
- the cast tin ingot was stored for 6 months in an argon gas atmosphere.
- the ⁇ ray count was 0.5 cph/cm 2 .
- the analytical values of the tin alloy are shown in Table 2.
- the present invention enables provision of high purity tin having a purity of 5N or higher (provided that this excludes the gas components of O, C, N, H, S and P), and in which the respective contents of U and Th as radioactive elements are 5 ppb or less, the respective contents of Pb and Bi that emit radiation ⁇ particles are 1 ppm or less, and the ⁇ ray count of high purity tin having a cast structure is 0.001 cph/cm 2 or less. It is therefore possible to eliminate as much as possible the influence of the ⁇ ray on semiconductor chips. Accordingly, since it is possible to significantly reduce the occurrence of soft errors caused by the influence of the ⁇ ray of semiconductor devices, the present invention is useful as a material to be used at locations where tin is to be used as the soldering material or the like.
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2005193323 | 2005-07-01 | ||
JP2005-193323 | 2005-07-01 | ||
PCT/JP2006/311912 WO2007004394A1 (ja) | 2005-07-01 | 2006-06-14 | 高純度錫又は錫合金及び高純度錫の製造方法 |
Related Parent Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2006/311912 A-371-Of-International WO2007004394A1 (ja) | 2005-07-01 | 2006-06-14 | 高純度錫又は錫合金及び高純度錫の製造方法 |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US14/340,933 Division US9340850B2 (en) | 2005-07-01 | 2014-07-25 | Process for producing high-purity tin |
Publications (1)
Publication Number | Publication Date |
---|---|
US20090098012A1 true US20090098012A1 (en) | 2009-04-16 |
Family
ID=37604269
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/916,906 Abandoned US20090098012A1 (en) | 2005-07-01 | 2006-06-14 | High-Purity Tin or Tin Alloy and Process for Producing High-Purity Tin |
US14/340,933 Active 2026-07-29 US9340850B2 (en) | 2005-07-01 | 2014-07-25 | Process for producing high-purity tin |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US14/340,933 Active 2026-07-29 US9340850B2 (en) | 2005-07-01 | 2014-07-25 | Process for producing high-purity tin |
Country Status (8)
Country | Link |
---|---|
US (2) | US20090098012A1 (ja) |
EP (1) | EP1900853B1 (ja) |
JP (3) | JP4472752B2 (ja) |
KR (1) | KR100958652B1 (ja) |
CN (2) | CN101880893A (ja) |
SG (1) | SG138124A1 (ja) |
TW (1) | TW200712263A (ja) |
WO (1) | WO2007004394A1 (ja) |
Cited By (22)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20100206133A1 (en) * | 2002-10-08 | 2010-08-19 | Honeywell International Inc. | Method of refining solder materials |
US8277774B2 (en) | 2011-01-27 | 2012-10-02 | Honeywell International | Method for the preparation of high purity stannous oxide |
US20120298586A1 (en) * | 2011-05-24 | 2012-11-29 | Dow Global Technologies Llc | Alpha-particle emitter removal |
WO2013192065A1 (en) * | 2012-06-20 | 2013-12-27 | Honeywell International Inc. | Refining process for producing low alpha tin |
US20140010705A1 (en) * | 2011-03-07 | 2014-01-09 | Jx Nippon Mining & Metals Corporation | Copper or copper reduced in alpha ray emission, and bonding wire obtained from the copper or copper alloy as raw material |
US20140060252A1 (en) * | 2011-06-07 | 2014-03-06 | Jaepil Jung | Method of producing tin emitted low alpha radiation by using vacuum refining |
CN103667744A (zh) * | 2013-12-13 | 2014-03-26 | 来宾华锡冶炼有限公司 | 一种含Sn99.99%等级锡的生产方法 |
US8992759B1 (en) | 2014-02-20 | 2015-03-31 | Honeywell International Inc. | Metal refining process using mixed electrolyte |
US20150209912A1 (en) * | 2014-01-28 | 2015-07-30 | Senju Metal lndustry Co., Ltd. | Cu CORE BALL, SOLDER PASTE AND SOLDER JOINT |
EP2905349A3 (en) * | 2014-02-04 | 2016-01-13 | Senju Metal Industry Co., Ltd. | Ag ball, Ag core ball, flux-coated Ag ball, flux-coated Ag core ball, solder joint, formed solder, solder paste and Ag paste |
US9359687B1 (en) | 2015-11-24 | 2016-06-07 | International Business Machines Corporation | Separation of alpha emitting species from plating baths |
US9394590B2 (en) | 2010-03-16 | 2016-07-19 | Jx Nippon Mining & Metals Corporation | Low α-dose tin or tin alloy, and method for producing same |
US9425164B1 (en) | 2015-11-24 | 2016-08-23 | International Business Machines Corporation | Low alpha tin |
US9546433B1 (en) | 2015-11-24 | 2017-01-17 | International Business Machines Corporation | Separation of alpha emitting species from plating baths |
US20170179058A1 (en) * | 2015-12-16 | 2017-06-22 | Lite-On Semiconductor Corporation | Bump structure having first portion of copper and second portion of pure tin covering the first portion, and interconnect structure using the same |
US10147695B2 (en) | 2013-06-19 | 2018-12-04 | Senju Metal Industry Co., Ltd. | Cu core ball |
US10337109B2 (en) | 2013-12-02 | 2019-07-02 | Jx Nippon Minig & Metals Corporation | High purity cobalt chloride and manufacturing method therefor |
US10400342B2 (en) | 2015-10-19 | 2019-09-03 | Jx Nippon Mining & Metals Corporation | High purity tin and method for manufacturing same |
US10711358B2 (en) | 2014-02-20 | 2020-07-14 | Jx Nippon Mining & Metals Corporation | Method of producing low alpha-ray emitting bismuth, and low alpha-ray emitting bismuth |
US11118276B2 (en) | 2016-03-09 | 2021-09-14 | Jx Nippon Mining & Metals Corporation | High purity tin and method for producing same |
CN115091072A (zh) * | 2022-07-01 | 2022-09-23 | 天津市松本环保科技有限公司 | 一种自动焊接用焊锡丝合金配方及制作方法 |
US11572632B2 (en) | 2014-10-02 | 2023-02-07 | Jx Nippon Mining & Metals Corporation | Method for manufacturing high purity tin, electrowinning apparatus for high purity tin and high purity tin |
Families Citing this family (33)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP5822250B2 (ja) * | 2010-03-31 | 2015-11-24 | Jx日鉱日石金属株式会社 | α線量が少ない銀又は銀を含有する合金及びその製造方法 |
JP5966449B2 (ja) * | 2012-03-06 | 2016-08-10 | 三菱マテリアル株式会社 | バンプ用はんだ合金粉末、バンプ用はんだペースト及びはんだバンプ |
JP2013185214A (ja) * | 2012-03-08 | 2013-09-19 | Jx Nippon Mining & Metals Corp | α線量が少ないビスマス又はビスマス合金及びその製造方法 |
WO2014069357A1 (ja) * | 2012-11-02 | 2014-05-08 | Jx日鉱日石金属株式会社 | 低α線ビスマスの製造方法並びに低α線ビスマス及びビスマス合金 |
KR20160012878A (ko) * | 2013-05-29 | 2016-02-03 | 신닛테츠스미킹 마테리알즈 가부시키가이샤 | 땜납 볼 및 전자 부재 |
WO2014207897A1 (ja) * | 2013-06-28 | 2014-12-31 | 千住金属工業株式会社 | はんだ材料及びはんだ継手 |
WO2015114770A1 (ja) * | 2014-01-30 | 2015-08-06 | 千住金属工業株式会社 | OSP処理Cuボール、はんだ継手、フォームはんだ、およびはんだペースト |
JP5773106B1 (ja) * | 2014-01-31 | 2015-09-02 | 千住金属工業株式会社 | フラックスコートボール、はんだペースト、フォームはんだ及びはんだ継手 |
EP3103567A4 (en) * | 2014-02-04 | 2017-11-01 | Senju Metal Industry Co., Ltd | Method for producing metal ball, joining material, and metal ball |
JP5534122B1 (ja) * | 2014-02-04 | 2014-06-25 | 千住金属工業株式会社 | 核ボール、はんだペースト、フォームはんだ、フラックスコート核ボールおよびはんだ継手 |
JP5847256B2 (ja) * | 2014-07-30 | 2016-01-20 | Jx日鉱日石金属株式会社 | α線量が少ない銀又は銀を含有する合金及びその製造方法 |
JP6410131B2 (ja) * | 2014-07-31 | 2018-10-24 | 佐々木半田工業株式会社 | 錫の高電流密度電解精製法 |
JP6448417B2 (ja) * | 2014-10-02 | 2019-01-09 | Jx金属株式会社 | 高純度錫の製造方法、高純度錫の電解採取装置及び高純度錫 |
US9708689B2 (en) * | 2015-04-08 | 2017-07-18 | Honeywell International Inc. | Isotope displacement refining process for producing low alpha materials |
JP6471072B2 (ja) * | 2015-09-15 | 2019-02-13 | Jx金属株式会社 | 低α線高純度亜鉛及び低α線高純度亜鉛の製造方法 |
CN106903452A (zh) * | 2017-05-02 | 2017-06-30 | 泰州朗瑞新能源科技有限公司 | 一种铸造锡铅焊接材料及其制备方法 |
JP6512354B2 (ja) * | 2017-08-17 | 2019-05-15 | 三菱マテリアル株式会社 | 低α線放出量の金属又は錫合金及びその製造方法 |
WO2019035446A1 (ja) | 2017-08-17 | 2019-02-21 | 三菱マテリアル株式会社 | 低α線放出量の金属及び錫合金並びにその製造方法 |
JP7314658B2 (ja) * | 2018-07-30 | 2023-07-26 | 三菱マテリアル株式会社 | 低α線放出量の酸化第一錫の製造方法 |
EP3872200A4 (en) * | 2019-03-04 | 2021-12-29 | JX Nippon Mining & Metals Corporation | Oxidation-resistant metallic tin |
JP6649597B1 (ja) * | 2019-05-27 | 2020-02-19 | 千住金属工業株式会社 | はんだ合金、はんだ粉末、およびはんだ継手 |
US11450516B2 (en) * | 2019-08-14 | 2022-09-20 | Honeywell International Inc. | Large-grain tin sputtering target |
CN111118305B (zh) * | 2020-01-17 | 2020-09-18 | 东莞永安科技有限公司 | 一种低α剂量锡或低α剂量锡合金及其制备方法 |
KR20220152208A (ko) | 2020-03-12 | 2022-11-15 | 린텍 가부시키가이샤 | 보호막 형성용 시트 |
WO2021205760A1 (ja) * | 2020-04-10 | 2021-10-14 | 千住金属工業株式会社 | はんだ合金、はんだ粉末、ソルダペースト、はんだボール、ソルダプリフォーム及びはんだ継手 |
JP6836091B1 (ja) * | 2020-04-10 | 2021-02-24 | 千住金属工業株式会社 | はんだ合金、はんだ粉末、ソルダペースト、はんだボール、ソルダプリフォーム及びはんだ継手 |
JP7041710B2 (ja) * | 2020-04-30 | 2022-03-24 | 千住金属工業株式会社 | 鉛フリーかつアンチモンフリーのはんだ合金、はんだボール、Ball Grid Arrayおよびはんだ継手 |
WO2021256172A1 (ja) * | 2020-06-16 | 2021-12-23 | アートビーム有限会社 | SnZn半田およびその製造方法 |
JP6928296B1 (ja) * | 2020-10-02 | 2021-09-01 | 千住金属工業株式会社 | ソルダペースト |
JP6928294B1 (ja) * | 2020-10-02 | 2021-09-01 | 千住金属工業株式会社 | ソルダペースト |
JP6928295B1 (ja) * | 2020-10-02 | 2021-09-01 | 千住金属工業株式会社 | フラックス及びソルダペースト |
CN112192086A (zh) * | 2020-10-13 | 2021-01-08 | 重庆群崴电子材料有限公司 | 低阿尔法bga锡球的制备方法以及bga锡球 |
CN112410578A (zh) * | 2020-10-23 | 2021-02-26 | 刘罗平 | 一种含锡物料的氧压碱浸钙盐沉锡的综合回收法 |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4800024A (en) * | 1986-04-07 | 1989-01-24 | Iso-Clear Systems Corporation | Removal of heavy metals and heavy metal radioactive isotopes from liquids |
JPH01283398A (ja) * | 1988-05-09 | 1989-11-14 | Mitsui Mining & Smelting Co Ltd | 錫およびその製造方法 |
US5217585A (en) * | 1991-12-20 | 1993-06-08 | Westinghouse Electric Corp. | Transition metal decontamination process |
US20040132299A1 (en) * | 2002-12-25 | 2004-07-08 | Nec Electronics Corporation | Method for depositing lead-free tin alloy |
US20130028786A1 (en) * | 2010-03-16 | 2013-01-31 | Jx Nippon Mining & Metals Corporation | Low alpha-Dose Tin or Tin Alloy, and Method for Producing Same |
Family Cites Families (16)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US1964948A (en) * | 1932-11-23 | 1934-07-03 | American Brass Co | Process of refining hard tin |
JPS5964791A (ja) | 1982-09-30 | 1984-04-12 | Mitsubishi Metal Corp | 放射性α粒子カウント数の低い鉛およびその電解精製方法 |
JPS5964790A (ja) | 1982-10-01 | 1984-04-12 | Mitsubishi Metal Corp | 放射性α粒子カウント数の低い錫およびその製造方法 |
JP2754030B2 (ja) | 1989-03-02 | 1998-05-20 | 三井金属鉱業株式会社 | 高純度錫の製造方法 |
JP2913908B2 (ja) | 1991-06-28 | 1999-06-28 | 三菱マテリアル株式会社 | 半田極細線およびその製造方法 |
JP3227851B2 (ja) | 1992-12-15 | 2001-11-12 | 三菱マテリアル株式会社 | 低α線Pb合金はんだ材およびはんだ膜 |
JP3568676B2 (ja) * | 1996-03-19 | 2004-09-22 | 富士通株式会社 | 半導体装置、回路基板及び電子回路装置 |
JP3528532B2 (ja) | 1997-09-02 | 2004-05-17 | 三菱マテリアル株式会社 | 低α線量錫の製造方法 |
JP3972464B2 (ja) | 1998-05-29 | 2007-09-05 | 三菱マテリアル株式会社 | 高純度錫の製造方法 |
JP2001009588A (ja) | 1999-06-25 | 2001-01-16 | Mitsubishi Materials Corp | Pb−Sn系ハンダ材 |
JP2001082538A (ja) | 1999-09-13 | 2001-03-27 | Kobe Steel Ltd | 免震構造体用金属プラグ材料 |
JP4533498B2 (ja) | 2000-03-24 | 2010-09-01 | アルバックマテリアル株式会社 | スパッタリングターゲットないし蒸着材料とその分析方法 |
JP2003193283A (ja) | 2001-12-28 | 2003-07-09 | Fujitsu Ltd | 電解めっき液及びその調製方法、半導体装置の製造方法ならびに放射性不純物の分析方法 |
JP4421170B2 (ja) * | 2002-04-11 | 2010-02-24 | 日鉱金属株式会社 | Ni−Sn合金からなるバリヤー層を備えた回路基板 |
AU2003272790A1 (en) * | 2002-10-08 | 2004-05-04 | Honeywell International Inc. | Semiconductor packages, lead-containing solders and anodes and methods of removing alpha-emitters from materials |
JP4242662B2 (ja) | 2003-02-17 | 2009-03-25 | ハリマ化成株式会社 | 低α線錫合金の製造方法 |
-
2006
- 2006-06-14 SG SG2007184468A patent/SG138124A1/en unknown
- 2006-06-14 CN CN2010102177417A patent/CN101880893A/zh active Pending
- 2006-06-14 EP EP06766681.8A patent/EP1900853B1/en active Active
- 2006-06-14 CN CN2006800239270A patent/CN101213326B/zh active Active
- 2006-06-14 US US11/916,906 patent/US20090098012A1/en not_active Abandoned
- 2006-06-14 JP JP2007523392A patent/JP4472752B2/ja active Active
- 2006-06-14 WO PCT/JP2006/311912 patent/WO2007004394A1/ja active Application Filing
- 2006-06-14 KR KR1020087001110A patent/KR100958652B1/ko active IP Right Grant
- 2006-06-20 TW TW095122010A patent/TW200712263A/zh unknown
-
2010
- 2010-01-29 JP JP2010017939A patent/JP5295987B2/ja active Active
-
2013
- 2013-04-02 JP JP2013076802A patent/JP5296269B1/ja active Active
-
2014
- 2014-07-25 US US14/340,933 patent/US9340850B2/en active Active
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4800024A (en) * | 1986-04-07 | 1989-01-24 | Iso-Clear Systems Corporation | Removal of heavy metals and heavy metal radioactive isotopes from liquids |
JPH01283398A (ja) * | 1988-05-09 | 1989-11-14 | Mitsui Mining & Smelting Co Ltd | 錫およびその製造方法 |
US5217585A (en) * | 1991-12-20 | 1993-06-08 | Westinghouse Electric Corp. | Transition metal decontamination process |
US20040132299A1 (en) * | 2002-12-25 | 2004-07-08 | Nec Electronics Corporation | Method for depositing lead-free tin alloy |
US20130028786A1 (en) * | 2010-03-16 | 2013-01-31 | Jx Nippon Mining & Metals Corporation | Low alpha-Dose Tin or Tin Alloy, and Method for Producing Same |
Cited By (36)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US9666547B2 (en) | 2002-10-08 | 2017-05-30 | Honeywell International Inc. | Method of refining solder materials |
US20100206133A1 (en) * | 2002-10-08 | 2010-08-19 | Honeywell International Inc. | Method of refining solder materials |
US9394590B2 (en) | 2010-03-16 | 2016-07-19 | Jx Nippon Mining & Metals Corporation | Low α-dose tin or tin alloy, and method for producing same |
US8277774B2 (en) | 2011-01-27 | 2012-10-02 | Honeywell International | Method for the preparation of high purity stannous oxide |
US9597754B2 (en) * | 2011-03-07 | 2017-03-21 | Jx Nippon Mining & Metals Corporation | Copper or copper alloy, bonding wire, method of producing the copper, method of producing the copper alloy, and method of producing the bonding wire |
US20140010705A1 (en) * | 2011-03-07 | 2014-01-09 | Jx Nippon Mining & Metals Corporation | Copper or copper reduced in alpha ray emission, and bonding wire obtained from the copper or copper alloy as raw material |
KR101927868B1 (ko) * | 2011-05-24 | 2018-12-11 | 롬 앤드 하스 일렉트로닉 머트어리얼즈 엘엘씨 | 알파-입자 방출원의 제거 |
US20120298586A1 (en) * | 2011-05-24 | 2012-11-29 | Dow Global Technologies Llc | Alpha-particle emitter removal |
US9099208B2 (en) * | 2011-05-24 | 2015-08-04 | Rohm And Haas Electronic Materials Llc | Alpha-particle emitter removal |
US20140060252A1 (en) * | 2011-06-07 | 2014-03-06 | Jaepil Jung | Method of producing tin emitted low alpha radiation by using vacuum refining |
US9163301B2 (en) * | 2011-06-07 | 2015-10-20 | Jaepil Jung | Method of producing tin emitted low alpha radiation by using vacuum refining |
WO2013192065A1 (en) * | 2012-06-20 | 2013-12-27 | Honeywell International Inc. | Refining process for producing low alpha tin |
US10147695B2 (en) | 2013-06-19 | 2018-12-04 | Senju Metal Industry Co., Ltd. | Cu core ball |
US10337109B2 (en) | 2013-12-02 | 2019-07-02 | Jx Nippon Minig & Metals Corporation | High purity cobalt chloride and manufacturing method therefor |
CN103667744A (zh) * | 2013-12-13 | 2014-03-26 | 来宾华锡冶炼有限公司 | 一种含Sn99.99%等级锡的生产方法 |
US10370771B2 (en) | 2014-01-28 | 2019-08-06 | Senju Metal Industry Co., Ltd. | Method of manufacturing cu core ball |
US20150209912A1 (en) * | 2014-01-28 | 2015-07-30 | Senju Metal lndustry Co., Ltd. | Cu CORE BALL, SOLDER PASTE AND SOLDER JOINT |
EP2905349A3 (en) * | 2014-02-04 | 2016-01-13 | Senju Metal Industry Co., Ltd. | Ag ball, Ag core ball, flux-coated Ag ball, flux-coated Ag core ball, solder joint, formed solder, solder paste and Ag paste |
US10711358B2 (en) | 2014-02-20 | 2020-07-14 | Jx Nippon Mining & Metals Corporation | Method of producing low alpha-ray emitting bismuth, and low alpha-ray emitting bismuth |
US8992759B1 (en) | 2014-02-20 | 2015-03-31 | Honeywell International Inc. | Metal refining process using mixed electrolyte |
US11572632B2 (en) | 2014-10-02 | 2023-02-07 | Jx Nippon Mining & Metals Corporation | Method for manufacturing high purity tin, electrowinning apparatus for high purity tin and high purity tin |
US11136680B2 (en) | 2015-10-19 | 2021-10-05 | Jx Nippon Mining & Metals Corporation | High purity tin and method for manufacturing same |
US10400342B2 (en) | 2015-10-19 | 2019-09-03 | Jx Nippon Mining & Metals Corporation | High purity tin and method for manufacturing same |
US10167568B2 (en) | 2015-11-24 | 2019-01-01 | International Business Machines Corporation | Separation of alpha emitting species from plating baths |
US10287698B2 (en) | 2015-11-24 | 2019-05-14 | International Business Machines Corporation | Separation of alpha emitting species from plating baths |
US10287702B2 (en) | 2015-11-24 | 2019-05-14 | International Business Machines Corporation | Separation of alpha emitting species from plating baths |
US9425164B1 (en) | 2015-11-24 | 2016-08-23 | International Business Machines Corporation | Low alpha tin |
US10030315B2 (en) | 2015-11-24 | 2018-07-24 | International Business Machines Corporation | Separation of alpha emitting species from plating baths |
US10458033B2 (en) | 2015-11-24 | 2019-10-29 | International Business Machines Corporation | Separation of alpha emitting species from plating baths |
US10577703B2 (en) | 2015-11-24 | 2020-03-03 | International Business Machines Corporation | Separation of alpha emitting species from plating baths |
US9546433B1 (en) | 2015-11-24 | 2017-01-17 | International Business Machines Corporation | Separation of alpha emitting species from plating baths |
US9359687B1 (en) | 2015-11-24 | 2016-06-07 | International Business Machines Corporation | Separation of alpha emitting species from plating baths |
US10138568B2 (en) | 2015-11-24 | 2018-11-27 | International Business Machines Corporation | Separation of alpha emitting species from plating baths |
US20170179058A1 (en) * | 2015-12-16 | 2017-06-22 | Lite-On Semiconductor Corporation | Bump structure having first portion of copper and second portion of pure tin covering the first portion, and interconnect structure using the same |
US11118276B2 (en) | 2016-03-09 | 2021-09-14 | Jx Nippon Mining & Metals Corporation | High purity tin and method for producing same |
CN115091072A (zh) * | 2022-07-01 | 2022-09-23 | 天津市松本环保科技有限公司 | 一种自动焊接用焊锡丝合金配方及制作方法 |
Also Published As
Publication number | Publication date |
---|---|
US20140332404A1 (en) | 2014-11-13 |
US9340850B2 (en) | 2016-05-17 |
JP5295987B2 (ja) | 2013-09-18 |
EP1900853A4 (en) | 2011-07-06 |
CN101213326B (zh) | 2010-11-17 |
KR20080015942A (ko) | 2008-02-20 |
TW200712263A (en) | 2007-04-01 |
CN101880893A (zh) | 2010-11-10 |
EP1900853B1 (en) | 2018-05-09 |
CN101213326A (zh) | 2008-07-02 |
JP5296269B1 (ja) | 2013-09-25 |
JP4472752B2 (ja) | 2010-06-02 |
SG138124A1 (en) | 2008-09-30 |
WO2007004394A1 (ja) | 2007-01-11 |
EP1900853A1 (en) | 2008-03-19 |
JPWO2007004394A1 (ja) | 2009-01-22 |
JP2010156052A (ja) | 2010-07-15 |
JP2013189710A (ja) | 2013-09-26 |
TWI320433B (ja) | 2010-02-11 |
KR100958652B1 (ko) | 2010-05-20 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US9340850B2 (en) | Process for producing high-purity tin | |
US9394590B2 (en) | Low α-dose tin or tin alloy, and method for producing same | |
KR101623629B1 (ko) | 구리 또는 구리 합금, 본딩 와이어, 구리의 제조 방법, 구리 합금의 제조 방법 및 본딩 와이어의 제조 방법 | |
JP5822250B2 (ja) | α線量が少ない銀又は銀を含有する合金及びその製造方法 | |
JP2013185214A (ja) | α線量が少ないビスマス又はビスマス合金及びその製造方法 | |
JP5903497B2 (ja) | 低α線ビスマスの製造方法並びに低α線ビスマス及びビスマス合金 | |
TWI670233B (zh) | 低α射線鉍之製造方法及低α射線鉍 | |
JP5960341B2 (ja) | 低α線ビスマスの製造方法 | |
JP5941596B2 (ja) | 低α線ビスマスの製造方法及び低α線ビスマス | |
JP2015028215A (ja) | α線量が少ない銀又は銀を含有する合金及びその製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: NIPPON MINING & METALS CO., LTD., JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:SHINDO, YUICHIRO;TAKEMOTO, KOUICHI;REEL/FRAME:020228/0660 Effective date: 20071204 |
|
AS | Assignment |
Owner name: NIPPON MINING HOLDINGS, INC., JAPAN Free format text: MERGER;ASSIGNOR:NIPPON MINING & METALS CO., LTD.;REEL/FRAME:025115/0062 Effective date: 20100701 |
|
AS | Assignment |
Owner name: JX NIPPON MINING & METALS CORPORATION, JAPAN Free format text: CHANGE OF NAME;ASSIGNOR:NIPPON MINING HOLDINGS, INC.;REEL/FRAME:025123/0358 Effective date: 20100701 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- AFTER EXAMINER'S ANSWER OR BOARD OF APPEALS DECISION |