KR20050075747A - 가소화된 폴리올레핀 조성물 - Google Patents

가소화된 폴리올레핀 조성물 Download PDF

Info

Publication number
KR20050075747A
KR20050075747A KR1020057002168A KR20057002168A KR20050075747A KR 20050075747 A KR20050075747 A KR 20050075747A KR 1020057002168 A KR1020057002168 A KR 1020057002168A KR 20057002168 A KR20057002168 A KR 20057002168A KR 20050075747 A KR20050075747 A KR 20050075747A
Authority
KR
South Korea
Prior art keywords
weight
polyolefin
propylene
plasticizer
another embodiment
Prior art date
Application number
KR1020057002168A
Other languages
English (en)
Other versions
KR101008786B1 (ko
Inventor
촌-예 린
시아 융 쳉
헨리 위-쉬앙 양
Original Assignee
엑손모빌 케미칼 패턴츠 인코포레이티드
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 엑손모빌 케미칼 패턴츠 인코포레이티드 filed Critical 엑손모빌 케미칼 패턴츠 인코포레이티드
Publication of KR20050075747A publication Critical patent/KR20050075747A/ko
Application granted granted Critical
Publication of KR101008786B1 publication Critical patent/KR101008786B1/ko

Abstract

본 발명은 폴리올레핀 및 작용화되지 않은 가소화제를 포함하는 가소화된 폴리올레핀 조성물에 관한 것으로서, 작용화되지 않은 가소화제는 -5℃ 미만의 유동점을 갖는 C6 내지 C200 파라핀(분지된 파라핀 및 선형 파라핀 포함)을 포함할 수 있다. 한 실시태양에서, 작용화되지 않은 가소화제는 C6 내지 C25 아이소파라핀을 포함하는 아이소파라핀이다. 다른 실시태양에서, 작용화되지 않은 가소화제는 C10 내지 C100 n-파라핀을 포함하는 폴리알파올레핀이다. 폴리올레핀은 폴리프로필렌 단독중합체, 공중합체, 충격 공중합체 또는 이들의 블렌드일 수 있고, 플라스토머를 포함할 수 있다. 본 발명의 조성물로부터 제조된 바람직한 제품의 비한정적인 예는 필름, 관, 파이프, 시이트, 섬유, 직물, 부직포, 자동차 부품, 가구, 운동용품, 식품 저장 용기, 투명 및 반투명 제품, 장난감, 관재 및 파이프, 및 의료 기기를 포함한다.

Description

가소화된 폴리올레핀 조성물{PLASTICIZED POLYOLEFIN COMPOSITIONS}
본 발명은 C6 내지 C200 파라핀 같은 작용화되지 않은 가소화제 및 폴리올레핀을 포함하는 가소화된 폴리올레핀에 관한 것이다. 더욱 구체적으로, 본 발명은 가요성 및 내충격성 같은 특성 및 가공성이 개선된 가소화된 폴리올레핀(예: 프로필렌 중합체)에 관한 것이다.
폴리올레핀은 다양한 일상용품에 유용하다. 그러나, 많은 폴리올레핀, 특히 폴리프로필렌 단독중합체 및 공중합체의 결점 하나는 비교적 높은 유리전이온도이다. 이 특징으로 인해 이들 폴리올레핀은 특히 저온에서 깨지기 쉬워진다. 광범위한 온도에 견딜 수 있는 제품을 제조하고자 한다면, 충격 강도 및 인성을 향상시키면서 고온 성능 등과 같은 목적하는 특징을 유지할 수 있는 폴리올레핀을 제공할 필요가 있다. 구체적으로, 인성 및 다른 바람직한 특성을 희생시키지 않으면서 개선된 인성을 갖는 프로필렌 중합체를 제공하는 것이 유리하다.
폴리올레핀에 가소화제 또는 다른 성분을 첨가하는 것은 충격 강도 및 인성 같은 특성을 개선시키는 한 방법이다. 미국 특허 제 4,960,820 호; 제 4,132,698 호; 제 3,201,364 호; WO 02/31044 호; WO 01/18109 A1 호; 및 유럽 특허 공개 제 0 300 689 A2 호 같은 몇몇 문헌은 이러한 목적에 관한 것이다. 이들 개시내용은 작용화된 가소화제와 블렌딩된 폴리올레핀 및 엘라스토머에 관한 것이다. 작용화된 가소화제는 방향족기를 함유하는 광유 및 높은(-20℃보다 높은) 유동점을 갖는 화합물 같은 물질이다. 이들 화합물을 사용하면 전형적으로 폴리올레핀의 투명성이 보존되지 않으며, 충격 강도가 종종 개선되지 않는다.
다른 배경 문헌은 유럽 특허 공개 제 0 448 259 A 호, 제 1 028 145 A 호, 미국 특허 제 4,073,782 호 및 제 3,415,925 호를 포함한다.
폴리올레핀의 융점, 폴리올레핀 결정화 속도, 그의 투명성에 영향을 끼치지 않고 이로부터 제조된 제품의 표면으로 가소화제가 최소한으로만 이동되는, 개선된 유연성, 더욱 우수한 가요성(보다 낮은 굴곡 모듈러스), 낮아진 유리전이온도 및 저온(0℃ 미만)에서의 개선된 충격 강도(개선된 가드너(Gardner) 충격)를 갖는 가소화된 폴리올레핀이 필요하다. 또한, 식품 용기 및 장난감 같은 용도에 사용될 수 있는 가소화된 폴리프로필렌이 필요하다.
파라핀 같은 간단한 비반응성 화합물을 사용함으로써 폴리올레핀을 가소화시키는 것이 특히 바람직하다. 그러나, 지방족 또는 파라핀계 화합물이 폴리올레핀의 특성을 손상시키며, 따라서 권장되지 않음이 이미 교시되었다(예를 들어, 문헌[CHEMICAL ADDITIVES FOR PLASTICS INDUSTRY, 107-116(Radian Corp., Noyes Data Corporation, 뉴저지주 1987)] 및 WO 01/18109 A1 호 참조). 놀랍게도 본 발명의 발명자들은 파라핀계 화합물이 폴리올레핀에 대해 유용한 가소화제임을 발견하였다. 본 발명은 이러한 가소화된 폴리올레핀에 관한 것이다.
발명의 개요
본 발명은 폴리올레핀 및 작용화되지 않은 가소화제를 포함하는 가소화된 폴리올레핀 조성물에 관한 것으로, 이 때 작용화되지 않은 가소화제는 -5℃ 미만의 유동점을 갖는 C6 내지 C200 파라핀(분지된 파라핀 및 선형 파라핀 포함)을 포함할 수 있다. 한 실시태양에서, 작용화되지 않은 가소화제는 C6 내지 C25 아이소파라핀을 포함하는 아이소파라핀이다. 다른 실시태양에서, 작용화되지 않은 가소화제는 C10 내지 C100 n-파라핀을 포함하는 폴리알파올레핀이다. 폴리올레핀은 폴리프로필렌 단독중합체, 공중합체, 충격 공중합체, 또는 이들의 블렌드일 수 있으며, 플라스토머를 포함할 수 있다. 본 발명의 조성물로부터 제조되는 바람직한 제품의 비한정적인 예는 필름, 시이트, 섬유, 직물 및 부직포, 관, 파이프, 자동차 부품, 가구, 운동용품, 식품 저장 용기, 투명 및 반투명 제품, 장난감, 관재(tubing) 및 파이프, 및 의료 기기를 포함한다. 본 발명의 조성물은 다른 바람직한 특성을 유지하면서 출발 폴리올레핀에 비해 개선된(감소된) Tg를 가짐을 특징으로 할 수 있다.
도 1은 본원에 인용된 다양한 가소화된 프로필렌 단독중합체 예에 있어서 온도의 함수로서의 저장 모듈러스(E')의 그래프이다.
도 2는 본원에 인용된 다양한 가소화된 프로필렌 단독중합체 예에 있어서 온도의 함수로서의 Tan δ의 그래프이다.
도 3은 본원에 인용된 다양한 가소화된 프로필렌 공중합체 예에 있어서 온도의 함수로서의 Tan δ의 그래프이다.
도 4는 본원에 인용된 다양한 가소화된 프로필렌 충격 공중합체 예에 있어서 온도의 함수로서의 Tan δ의 그래프이다.
도 5는 본 발명의 예시적인 다양한 가소화된 프로필렌 단독중합체 샘플에 있어서 온도의 함수로서의 DSC로부터의 용융 열 유동의 그래프이다.
도 6은 본 발명의 예시적인 다양한 가소화된 프로필렌 단독중합체 샘플에 있어서 온도의 함수로서의 DSC로부터의 결정화 열 유동의 그래프이다.
도 7은 본 발명의 예시적인 다양한 가소화된 프로필렌 공중합체 샘플에 있어서 온도의 함수로서의 DSC로부터의 용융 열 유동의 그래프이다.
도 8은 본 발명의 예시적인 다양한 가소화된 프로필렌 공중합체 샘플에 있어서 온도의 함수로서의 DSC로부터의 결정화 열 유동의 그래프이다.
도 9는 본 발명의 예시적인 다양한 가소화된 프로필렌 충격 공중합체 샘플에 있어서 온도의 함수로서의 DSC로부터의 용융 열 유동의 그래프이다.
도 10은 본 발명의 예시적인 다양한 가소화된 프로필렌 충격 공중합체 샘플에 있어서 온도의 함수로서의 DSC로부터의 결정화 열 유동의 그래프이다.
도 11은 본 발명의 예시적인 다양한 가소화된 프로필렌 단독중합체 샘플에 있어서 전단 속도의 함수로서의 전단 점도의 그래프이다.
도 12는 본 발명의 예시적인 다양한 가소화된 프로필렌 공중합체 샘플에 있어서 전단 속도의 함수로서의 전단 점도의 그래프이다.
도 13은 본 발명의 예시적인 다양한 가소화된 프로필렌 충격 공중합체 샘플에 있어서 전단 속도의 함수로서의 전단 점도의 그래프이다.
도 14는 본 발명의 예시적인 다양한 가소화된 프로필렌 단독중합체 샘플에 있어서 분자량 분포의 그래프이다.
본 발명은 폴리올레핀 및 작용화되지 않은 가소화제(NFP)를 포함하는 가소화된 폴리올레핀 조성물이다. NFP는 전형적으로 C6 내지 C200 파라핀을 포함하는 파라핀 또는 지방족 탄화수소일 수 있다. 본원에 사용되는 용어 "파라핀"은 분지된 구조 및 선형 구조를 비롯한 C6 내지 C200 파라핀의 모든 이성질체, 및 이들의 블렌드를 포함한다. 개별 파라핀은 포화 환상 탄화수소를 포함할 수 있다. 바람직하게는, NFP는 0℃ 미만의 유동점 및 100℃에서 0.1 내지 3000cSt의 점도(ASTM D445-97)를 갖는다. 유용한 NFP는 소위 폴리알파올레핀(PAO) 및 아이소파라핀을 포함할 수 있다.
본 발명의 특정 조성물은, 폴리올레핀의 융점 및 결정화 온도를 일정하게 유지하면서(1 내지 2℃ 이내로), 이 조성물의 유리전이온도(Tg)가 한 실시태양에서는 조성물에 존재하는 NFP 매 4중량%에 대해 2℃ 이상씩 감소하고, 다른 실시태양에서는 조성물에 존재하는 NFP 매 4중량%에 대해 3℃ 이상씩 감소하며, 또 다른 실시태양에서는 조성물에 존재하는 NFP 매 4중량%에 대해 4 내지 10℃ 이상씩 감소함을 특징으로 할 수 있다. 또한, 본 발명의 조성물은 NFP가 프로필렌 중합체와 상용성 및 혼화성이며 별도의 상을 형성하지 않음을 특징으로 한다. 이는 예컨대 DMTA(동적 기계적 열 분석)에 의해 조성물에 대해 관찰된 Tg 프로파일에 의해 입증된다.
임의의 적합한 수단에 의해 폴리올레핀과 NFP를 블렌딩할 수 있다. 예를 들어, 텀블러, 압출기 또는 이들의 조합에서 이들을 블렌딩할 수 있다. 본원에 기재된 가소화된 폴리올레핀 조성물의 향상된 특성은 요리 및 저장용품, 및 가구, 자동차 부품, 장난감, 운동용품, 의료 기기, 멸균가능한 의료 기기 및 멸균 용기 같은 다른 제품에서의 투명 부품; 부직포 및 직물, 및 드레이프, 가운, 필터, 위생 제품, 기저귀 및 필름, 배향 필름, 시이트, 관, 파이프 및 유연성, 높은 충격 강도 및 동결점 미만의 충격 강도가 중요한 다른 품목 같은 이들로부터의 제품을 비롯한 다수의 용도에 유용하다. 사출 성형, 압출, 열성형, 취입 성형, 회전 성형, 방사 결합, 용융취입, 섬유 방사, 취입 필름, 배향된 필름을 위한 연신 및 다른 통상적인 처리 방법을 비롯한 다수의 기법을 이용하여 본 발명의 가소화된 폴리올레핀을 가공함으로써 이들 제품을 제조할 수 있다.
아래에서는, 폴리올레핀, NFP 및 그의 실시태양과 관련하여 본 발명을 추가로 기재한다.
폴리올레핀
폴리올레핀은 본 발명의 NFP에 의해 가소화되거나 본 발명의 NFP와 블렌딩되어, 더욱 가요성이지만 내충격성인 조성물을 형성할 수 있다. 본 발명의 한 요지에서, 폴리올레핀은 폴리프로필렌 단독중합체, 폴리프로필렌 공중합체 및 이들의 블렌드로부터 선택된다. 단독중합체는 어택틱(atactic) 폴리프로필렌, 아이소택틱(isotactic) 폴리프로필렌, 신디오택틱(syndiotactic) 폴리프로필렌 및 이들의 블렌드일 수 있다. 공중합체는 랜덤 공중합체, 블록 공중합체 및 이들의 블렌드일 수 있다. 특히, 중합체 블렌드는 소위 충격 공중합체, 엘라스토머 및 플라스토머를 포함하며, 이들은 폴리프로필렌 및 폴리프로필렌 공중합체의 물리적 블렌드 또는 동일 반응계내 블렌드일 수 있다. 폴리프로필렌은 슬러리, 용액, 또는 기상 방법에 의해, 또한 지글러-나타-유형의 촉매, 메탈로센-유형 촉매 또는 이들의 조합을 사용함으로써 제조될 수 있으므로, 이들의 제조 방법은 중요하지 않다. 이들 촉매는 당해 분야에 널리 공지되어 있으며, 예를 들어 문헌[ZIEGLER CATALYSTS(게르하르트 핑크, 롤프 물하우프트 및 한스 에이취. 브린트징거 편집, Springer-Verlag 1995)]; 레스코니(Resconi) 등의 문헌[Selectivity in Propene Polymerization with Metallocene Catalysts, 100 CHEM. REV. 1253-1345(2000)]; 및 문헌[I, II METALLOCENE-BASED POLYOLEFINS (Wiley & Sons 2000)]에 기재되어 있다.
폴리올레핀은 프로필렌 단독중합체일 수 있다. 바람직한 프로필렌 단독중합체는 1.5 내지 10, 다른 실시태양에서는 2.0 내지 7, 또 다른 실시태양에서는 2.0내지 5, 다른 실시태양에서는 2.0 내지 4의 분자량 분포(Mw/Mn)를 갖는다. 23℃에서 0.125인치 디스크에서 시험한 프로필렌 단독중합체의 가드너 충격 강도는 한 실시태양에서 20 내지 1000in-lb, 다른 실시태양에서 30 내지 500in-lb, 또 다른 실시태양에서 40 내지 400in-lb일 수 있다. 또 다른 실시태양에서, 프로필렌 단독중합체의 1% 시컨트(secant) 굴곡 모듈러스는 100MPa 내지 2300MPa, 다른 실시태양에서는 200MPa 내지 2100MPa, 또 다른 실시태양에서는 300MPa 내지 2000MPa이며, 바람직한 폴리올레핀은 임의의 굴곡 모듈러스 상한과 임의의 굴곡 모듈러스 하한의 임의의 조합을 나타낼 수 있다. 프로필렌 단독중합체의 용융 유속(MFR)(ASTM D 1238, 230℃, 2.16kg)은 한 실시태양에서 0.1 내지 2500dg/분이고, 다른 실시태양에서 0.3 내지 500dg/분이다.
본 발명에 유용한 폴리프로필렌 단독중합체 또는 공중합체는 일정 수준의 아이소택티서티를 가질 수 있다. 따라서, 한 실시태양에서는 아이소택틱 폴리프로필렌이 유용한 폴리올레핀이고, 다른 실시태양에서는 고도의 아이소택틱 폴리프로필렌이 유용한 폴리올레핀이다. 본원에 사용되는 "아이소택틱"은 13C-NMR에 의한 분석에 따라 10% 이상의 아이소택틱 펜타드를 갖는 것으로 정의된다. 본원에 사용되는 "고도의 아이소택틱"은 13C-NMR에 의한 분석에 따라 60% 이상의 아이소택틱 펜타드를 갖는 것으로 정의된다. 바람직한 실시태양에서는 85% 이상의 아이소택티서티를 갖는 폴리프로필렌 단독중합체가 폴리올레핀이고, 다른 실시태양에서는 90% 이상의 아이소택티서티를 갖는 폴리프로필렌 단독중합체가 폴리올레핀이다.
본 발명의 다른 실시태양에서, 폴리올레핀은 프로필렌 유도된 단위, 및 에틸렌 및 C4 내지 C20 α-올레핀 유도된 단위로부터 선택된 단위, 다른 실시태양에서는 에틸렌 및 C4 내지 C10 α-올레핀 유도된 단위로부터 선택된 단위의 랜덤 또는 블록 프로필렌 공중합체이다. 에틸렌 또는 C4 내지 C20 α-올레핀 유도된 단위는 한 실시태양에서 공중합체의 0.1 내지 50중량%, 다른 실시태양에서는 0.5 내지 30중량%, 또 다른 실시태양에서는 1 내지 15중량%, 또 다른 실시태양에서는 0.1 내지 5중량%로 존재하며, 바람직한 공중합체는 에틸렌 및 C4 내지 C20 α-올레핀 유도된 단위를 본원에 기재된 임의의 중량% 상한과 임의의 중량% 하한의 임의의 조합으로 포함한다. 프로필렌 공중합체는 한 실시태양에서 8,000g/몰보다 큰 중량평균 분자량을 갖고, 다른 실시태양에서는 10,000g/몰보다 큰 분자량, 또 다른 실시태양에서는 12,000g/몰보다 큰 분자량, 또 다른 실시태양에서는 20,000g/몰보다 큰 분자량, 또 다른 실시태양에서는 1,000,000g/몰 미만의 분자량, 또 다른 실시태양에서는 800,000g/몰 미만의 분자량을 갖는데, 바람직한 공중합체는 본원에 기재된 분자량의 임의의 상한과 임의의 하한을 포함할 수 있다.
또 다른 실시태양에서, 23℃에서 0.125인치 디스크 상에서 시험된 프로필렌 공중합체의 가드너 충격 강도는 20 내지 1000in-lb, 다른 실시태양에서는 30 내지 500in-lb, 또 다른 실시태양에서는 40 내지 400in-lb이다. 또한, 프로필렌 공중합체는 100MPa 내지 2300MPa, 다른 실시태양에서는 200MPa 내지 2100MPa, 또 다른 실시태양에서는 300MPa 내지 2000MPa의 1% 시컨트 굴곡 모듈러스를 가질 수 있으며, 바람직한 폴리올레핀은 임의의 굴곡 모듈러스 상한과 임의의 굴곡 모듈러스 하한의 임의의 조합을 나타낼 수 있다. 바람직한 공중합체의 용융 유속(MFR)(ASTM D 1238, 230℃)은 한 실시태양에서 0.1dg/분 내지 2500dg/분, 다른 실시태양에서 0.1 내지 500dg/분이다.
또 다른 실시태양에서, 폴리올레핀은 소위 "충격 공중합체" 또는 블록 공중합체일 수 있다. 이 충격 공중합체는 반응기 블렌드(동일 반응계내 블렌드) 또는 물리적 블렌드일 수 있다. 한 실시태양에서, 적합한 충격 공중합체는 충격 공중합체의 총 중량에 기초하여 40 내지 95중량%의 성분 A 및 5 내지 60중량%의 성분 B를 포함하며; 성분 A는 프로필렌 단독중합체 또는 공중합체(이 때, 공중합체는 10중량% 이하의 에틸렌, 뷰텐, 헥센 또는 옥텐 공단량체를 포함함)를 포함하고; 성분 B는 5 내지 70중량%의 에틸렌, 뷰텐, 헥센 및/또는 옥텐 공단량체 및 약 95 내지 약 30중량%의 프로필렌을 포함하는 프로필렌 공중합체를 포함한다. 충격 공중합체의 한 실시태양에서, 성분 B는 본질적으로 프로필렌 및 30 내지 65중량%의 에틸렌으로 이루어진다. 다른 실시태양에서, 성분 B는 에틸렌-프로필렌 공중합체, 에틸렌-프로필렌-다이엔 삼원공중합체, 에틸렌-아크릴레이트 공중합체, 에틸렌-비닐 아세테이트, 스타이렌-뷰타다이엔 공중합체, 에틸렌-아크릴산 에스터 공중합체, 폴리뷰타다이엔, 폴리아이소프렌, 천연 고무, 아이소뷰틸렌, 탄화수소 수지(5000 미만의 분자량, 약 50 내지 100℃의 Tg, 및 약 140℃의 연화점을 특징으로 함), 로진 및 이들의 혼합물을 포함한다. 다른 실시태양에서, 성분 B는 3.5 미만의 분자량 분포를 갖는다. 또 다른 실시태양에서, 성분 B는 20,000 이상의 중량평균 분자량을 갖는다. 유용한 충격 공중합체는 예를 들어 미국 특허 제 6,342,566 호 및 제 6,384,142 호에 개시되어 있다.
또 다른 실시태양에서, -29℃에서 0.125인치 디스크 상에서 시험된 프로필렌 충격 공중합체의 가드너 충격 강도는 20in-lb 내지 1000in-lb, 다른 실시태양에서 30in-lb 내지 500in-lb, 또 다른 실시태양에서 40 내지 400in-lb이다. 또한, 프로필렌 충격 공중합체의 1% 시컨트 굴곡 모듈러스는 한 실시태양에서 100 내지 2300MPa, 다른 실시태양에서 200 내지 2100MPa, 또 다른 실시태양에서 300 내지 2000MPa이며, 바람직한 폴리올레핀은 임의의 굴곡 모듈러스 상한과 임의의 굴곡 모듈러스 하한의 임의의 조합을 나타낼 수 있다. 바람직한 단독중합체의 용융 유속(MFR)(ASTM D 1238, 230℃, 2.16kg)은 한 실시태양에서 0.1dg/분 내지 2500dg/분, 다른 실시태양에서 0.3 내지 500dg/분이다.
다른 적합한 폴리올레핀은 폴리프로필렌 단독중합체 또는 공중합체와 소위 "플라스토머"의 블렌드를 포함한다. 본 발명에 유용한 플라스토머는 0.85 내지 0.915g/cm3의 밀도 및 0.10 내지 30dg/분의 용융지수(MI)(ASTM D 1238; 190℃, 2.1kg)를 갖는 폴리올레핀 공중합체로서 기재될 수 있다. 한 실시태양에서, 유용한 플라스토머는 에틸렌 유도된 단위 및 하나 이상의 C3 내지 C10 α-올레핀 유도된 단위의 공중합체로서, 0.915g/cm3 미만의 밀도를 갖는다. 플라스토머에 존재하는 공단량체(C3 내지 C10 α-올레핀 유도된 단위)의 양은 한 실시태양에서 2 내지 35중량%, 다른 실시태양에서 5 내지 30중량%, 또 다른 실시태양에서 15 내지 25중량%, 또 다른 실시태양에서 20 내지 30중량%이다.
본 발명에 유용한 플라스토머는 한 실시태양에서 0.10 내지 20dg/분, 다른 실시태양에서 0.2 내지 10dg/분, 또 다른 실시태양에서 0.3 내지 8dg/분의 용융 지수(MI)를 갖는다. 유용한 플라스토머의 평균 분자량은 한 실시태양에서 10,000 내지 800,000, 다른 실시태양에서 20,000 내지 700,000이다. 유용한 플라스토머의 1% 시컨트 굴곡 모듈러스(ASTM D 790)는 한 실시태양에서 10 내지 150MPa, 다른 실시태양에서 20 내지 100MPa이다. 또한, 본 발명의 조성물에 유용한 플라스토머는 한 실시태양에서 30 내지 80℃(제 1 용융 피크) 및 50 내지 125℃(제 2 용융 피크), 다른 실시태양에서 40 내지 70℃(제 1 용융 피크) 및 50 내지 100℃(제 2 용융 피크)의 융점(Tm)을 갖는다.
본 발명에 유용한 플라스토머는 에틸렌 유도된 단위 및 고급 α-올레핀 유도된 단위(예: 프로필렌, 1-뷰텐, 1-헥센 및 1-옥텐)의 메탈로센 촉진된 공중합체(이는 한 실시태양에서 이들 공단량체중 하나 이상을 0.860 내지 0.900g/cm3의 밀도를 갖도록 하기에 충분하게 함유함)이다. 바람직한 플라스토머의 분자량 분포(Mw/Mn)는 한 실시태양에서 1.5 내지 5, 다른 실시태양에서 2.0 내지 4이다. 시판중인 플라스토머의 예는 1-헥센 유도된 단위가 플라스토머의 18 내지 22중량%를 구성하고, 0.895g/cm3의 밀도 및 3.5dg/분의 MI를 갖는, 에틸렌과 1-헥센의 공중합체인 EXACT 4150(텍사스주 휴스턴 소재의 엑손모빌 케미칼 캄파니); 및 1-옥텐 유도된 단위가 플라스토머의 25 내지 30중량%를 구성하고, 0.882g/cm3의 밀도 및 1.0dg/분의 MI를 갖는, 에틸렌과 1-옥텐의 공중합체인 EXACT 8201(텍사스주 휴스턴 소재의 엑손모빌 케미칼 캄파니)이다.
본 발명에 사용하기 적합한 폴리올레핀은 본 발명의 NFP와 블렌딩시키는데 사용될 때 임의의 물리적 형태일 수 있다. 한 실시태양에서는, 임의의 가공 절차 전에 중합 반응기로부터 단리된 중합체의 과립으로서 정의되는 반응기 과립을 사용하여 본 발명의 NFP와 블렌딩시킨다. 반응기 과립은 한 실시태양에서 50㎛ 내지 10mm, 다른 실시태양에서 10㎛ 내지 5mm의 평균 직경을 갖는다. 다른 실시태양에서, 폴리올레핀은 예컨대 반응기 과립의 용융 압출로부터 형성된 평균 직경 1mm 내지 10mm의 펠렛 형태이다.
본 발명의 한 실시태양에서, 조성물에 적합한 폴리올레핀은 폴리프로필렌과 다른 폴리올레핀의 물리적 블렌드를 제외하며, 특히 저분자량(500 내지 10,000g/몰) 폴리에틸렌 또는 폴리에틸렌 공중합체와 폴리프로필렌의 물리적 블렌드를 제외한다. 이는 예컨대 WO 01/18109 A1 호에서와 같이 저분자량 폴리에틸렌 또는 폴리에틸렌 공중합체를 어떠한 양으로라도 폴리올레핀(예: 폴리프로필렌 단독중합체 또는 공중합체)에 의도적으로 첨가하지 않음을 의미한다.
폴리올레핀은 한 실시태양에서 40 내지 99.9중량%, 다른 실시태양에서 50 내지 99중량%, 또 다른 실시태양에서 60 내지 98중량%, 다른 실시태양에서 70 내지 97중량%, 또 다른 실시태양에서 80 내지 97중량%, 또 다른 실시태양에서 90 내지 98중량%의 양으로 본 발명의 조성물에 존재하며, 바람직한 범위는 본원에 기재된 임의의 중량% 상한과 임의의 중량% 하한의 임의의 조합일 수 있다.
따라서, 본 발명에 사용하기 바람직한 폴리올레핀은 본원의 임의의 실시태양 또는 본원에 기재된 실시태양의 임의의 조합에 의해 기재될 수 있다.
작용화되지 않은 가소화제
본 발명의 폴리올레핀 조성물은 작용화되지 않은 가소화제("NFP")를 포함한다. 본 발명의 NFP는 탄소와 수소를 포함하는 화합물이고, 하이드록사이드, 아릴 및 치환된 아릴, 할로겐, 알콕시, 카복실레이트, 에스터, 탄소 불포화, 아크릴레이트, 산소, 질소 및 카복실로부터 선택되는 작용기를 인지가능한 한도로 포함하지 않는다. "인지가능한 한도"란 이들 기 및 이들 기를 포함하는 화합물을 NFP에 일부러 첨가하지 않으며, 기껏 존재한다고 해봐야 한 실시태양에서는 NFP의 5중량% 미만, 다른 실시태양에서는 1중량% 미만, 또 다른 실시태양에서는 0.5중량% 미만으로 존재함을 의미한다.
한 실시태양에서, NFP는 C6 내지 C200 파라핀으로 이루어지며, 다른 실시태양에서는 C8 내지 C100 파라핀으로 구성된다. 다른 실시태양에서, NFP는 본질적으로 C6 내지 C200 파라핀으로 이루어지고, 다른 실시태양에서는 본질적으로 C8 내지 C100 파라핀으로 이루어진다. 본 발명 및 본원에 기재된 내용에서, 용어 "파라핀"은 n-파라핀, 분지된 파라핀, 아이소파라핀 같은 모든 이성질체를 포함하며, 환상 지방족 파라핀 및 이들의 블렌드를 포함할 수 있고, 당해 분야에 공지되어 있는 수단에 의해, 또는 본원에 기재된 바람직한 NFP에 대해 기재되어 있는 조건을 충족시키는 방식으로 정제된 원유로부터 합성될 수 있다. NFP로서 유용한 것으로 본원에 기재된 부류의 물질을 단독으로 사용할 수 있거나 또는 목적하는 특성을 수득하기 위해 본원에 기재되어 있는 다른 NFP와 혼합하여 사용할 수 있다.
NFP는 한 실시태양에서 0.1 내지 60중량%, 다른 실시태양에서 0.5 내지 40중량%, 또 다른 실시태양에서 1 내지 20중량%, 또 다른 실시태양에서 2 내지 10중량%의 양으로 본 발명의 폴리올레핀 조성물에 존재할 수 있고, 바람직한 범위는 본원에 기재된 임의의 중량% 상한과 임의의 중량% 하한을 포함할 수 있다.
NFP는 또한 본원에 기재되어 있는 다수의 변수 또는 이들 변수의 임의의 조합에 의해 기재될 수 있다. 한 실시태양에서, 본 발명의 NFP는 한 실시태양에서 0℃ 미만, 다른 실시태양에서 -5℃ 미만, 또 다른 실시태양에서 -10℃ 미만, 또 다른 실시태양에서 -20℃ 미만, 다른 실시태양에서 -40℃ 미만, 또 다른 실시태양에서 -50℃ 미만, 다른 실시태양에서 -60℃ 미만, 또 다른 실시태양에서 -120℃ 이상, 다른 실시태양에서 -200℃ 이상의 유동점(ASTM D97)을 가지며, 바람직한 범위는 본원에 기재되어 있는 임의의 유동점 상한과 임의의 유동점 하한을 포함할 수 있다. 한 실시태양에서, NFP는 40℃에서 0.5 내지 200cSt(ASTM D445-97)의 점도 범위에서 -30℃ 미만, 다른 실시태양에서 -30℃ 내지 -90℃의 유동점을 갖는 파라핀 또는 다른 화합물이다. 전형적으로 방향족 잔기 및 다른 작용기를 포함하는 대부분의 광유는 동일한 점도 범위에서 10℃ 내지 -20℃의 유동점을 갖는다.
NFP는 한 실시태양에서 3.0 미만, 다른 실시태양에서 2.8 미만, 다른 실시태양에서 2.5 미만, 또 다른 실시태양에서 2.3 미만, 또 다른 실시태양에서 2.1 미만의 20℃에서의 유전상수를 가질 수 있다. 폴리에틸렌 및 폴리프로필렌은 각각 2.3 이상의 유전상수(1kHz, 23℃)를 갖는다[CRC HANDBOOK OF CHEMISTRY AND PHYSICS(라이드 편집, 제82판, CRC Press 2001)].
NFP는 100℃에서 0.1 내지 3000cSt, 다른 실시태양에서 0.5 내지 1000cSt, 또 다른 실시태양에서 1 내지 250cSt, 또 다른 실시태양에서 1 내지 200cSt, 다른 실시태양에서 10 내지 500cSt의 점도(ASTM D445-97)를 가지며, 바람직한 범위는 본원에 기재된 임의의 점도 상한과 임의의 점도 하한을 포함할 수 있다.
NFP는 한 실시태양에서 0.920g/cm3 미만, 다른 실시태양에서 0.910g/cm3 미만, 다른 실시태양에서 0.650 내지 0.900g/cm3, 또 다른 실시태양에서 0.700 내지 0.860g/cm3, 다른 실시태양에서 0.750 내지 0.855g/cm3, 또 다른 실시태양에서 0.790 내지 0.850g/cm3, 다른 실시태양에서 0.800 내지 0.840g/cm3의 비중(ASTM D 4052, 15.6/15.6℃)을 갖고, 바람직한 범위는 본원에 기재되어 있는 임의의 비중 상한과 임의의 비중 하한을 포함할 수 있다. NFP는 한 실시태양에서 100 내지 800℃, 다른 실시태양에서 200 내지 600℃, 또 다른 실시태양에서 250 내지 500℃의 비점을 갖는다. 또한, NFP는 한 실시태양에서 20,000g/몰 미만, 다른 실시태양에서 10,000g/몰 미만, 또 다른 실시태양에서 5,000g/몰 미만, 또 다른 실시태양에서 4,000g/몰 미만, 또 다른 실시태양에서 2,000g/몰 미만, 다른 실시태양에서 500g/몰 미만, 또 다른 실시태양에서 100g/몰 미만의 중량평균 분자량(GPC 또는 GC)을 가지며, 바람직한 분자량 범위는 본원에 기재되어 있는 임의의 분자량 상한과 임의의 분자량 하한의 임의의 조합일 수 있다.
본 발명의 폴리올레핀에 대한 NFP로서 적합한 화합물은 소위 "아이소파라핀", "폴리알파올레핀"(PAO) 및 "폴리뷰텐"(PAO의 아군) 같은 시판중인 화합물로부터 선택될 수 있다. 이들 세 부류의 화합물은 분지, 환상 및 선형 구조를 포함할 수 있는 파라핀 및 이들의 블렌드로서 기재될 수 있다. 이들 NFP는 한 실시태양에서 C6 내지 C200 파라핀, 다른 실시태양에서 C8 내지 C100 파라핀을 포함하는 것으로 기재될 수 있다.
소위 "아이소파라핀"은 다음과 같이 기재된다. 이들 파라핀은 바람직하게는 아이소파라핀이며, 이는 파라핀 쇄가 각 파라핀 쇄의 적어도 일부를 따라 C1 내지 C10 알킬 분지를 갖는다는 의미이다. C6 내지 C200 파라핀은 한 실시태양에서 C6 내지 C25 아이소파라핀, 다른 실시태양에서 C8 내지 C20 아이소파라핀을 포함할 수 있다.
더욱 구체적으로, 아이소파라핀은 그 분자가 셋 이상의 다른 탄소원자 또는 하나 이상의 측쇄에 결합된 하나 이상의 탄소원자를 갖는(즉, 하나 이상의 3급 또는 4급 탄소원자를 갖는 분자) 포화 지방족 탄화수소이며, 바람직하게는 분자당 탄소원자의 총 수는 6 내지 50개, 다른 실시태양에서 10 내지 24개, 또 다른 실시태양에서 10 내지 15개이다. 각 탄소수의 다양한 이성질체가 전형적으로 존재한다. 아이소파라핀은 또한 통상 아이소파라핀의 미량 성분으로서 분지된 측쇄를 갖는 사이클로파라핀도 포함할 수 있다. 이들 아이소파라핀의 밀도(ASTM 4052, 15.6/15.6℃)는 0.70 내지 0.83g/cm3이고; 유동점은 한 실시태양에서 -40℃ 미만, 다른 실시태양에서 -50℃ 미만이고; 점도(ASTM 445, 25℃)는 25℃에서 0.5 내지 20cSt이고; 평균 분자량은 100 내지 300g/몰이다. 아이소파라핀은 상표명 ISOPAR(엑손모빌 케미칼 캄파니, 텍사스주 휴스턴 소재)로 구입가능하며, 예컨대 미국 특허 제 6,197, 285 호, 제 3,818,105 호 및 제 3,439,088 호에 기재되어 있고, 아이소파라핀의 ISOPAR 씨리즈로서 시판되고 있으며, 이들중 몇몇은 아래 표 1에 요약되어 있다.
다른 실시태양에서, 아이소파라핀은 분자에 탄소원자 6 내지 50개, 다른 실시태양에서 탄소원자 10 내지 24개를 갖는 분지된 파라핀과 선형 파라핀의 혼합물이다. 아이소파라핀 조성물은 한 실시태양에서 0.5:1 내지 9:1, 다른 실시태양에서 1:1 내지 4:1의 분지된 파라핀:n-파라핀 비를 갖는다. 이 실시태양에서 혼합물중 아이소파라핀은 혼합물중 아이소파라핀의 총 중량에 기초하여 탄소수가 1개보다 많은 치환기(예컨대, 에틸, 프로필, 뷰틸 등)를 갖는 분지를 최소한으로 생성시키면서 50중량%(아이소파라핀 조성물의 총 중량에 기초하여)보다 많은 모노-메틸(예: 2-메틸, 3-메틸, 4-메틸, 5-메틸 등)을 함유한다. 한 실시태양에서, 혼합물의 아이소파라핀은 혼합물중 아이소파라핀의 총 중량에 기초하여 70중량%보다 많은 모노-메틸을 함유한다. 아이소파라핀 혼합물은 한 실시태양에서 100 내지 350℃, 다른 실시태양에서 110 내지 320℃의 범위 내에서 비등한다. 상이한 등급의 제조시에는, 파라핀 혼합물을 통상 좁은 비등 범위, 예컨대 35℃의 비등 범위를 갖는 컷(cut)으로 분별시킨다. 이들 분지된 파라핀/n-파라핀 블렌드는 예를 들어 미국 특허 제 5,906,727 호에 기재되어 있다.
다른 적합한 아이소파라핀은 또한 상표명 SHELLSOL(쉘(Shell) 제품), SOLTROL(쉐브론 필립스(Chevron Phillips) 제품) 및 SASOL(사솔 리미티드(Sasol Limited) 제품)로 구입할 수 있다. SHELLSOL은 로얄 더취/쉘 그룹 오브 캄파니즈(Royal Dutch/Shell Group of Companies)의 제품, 예컨대 Shellsol TM(비점=215-260℃)이다. SOLTROL은 쉐브론 필립스 케미칼 캄파니. 엘피(Chevron Phillips Chemical Co. LP)의 제품, 예컨대 SOLTROL 220(비점=233-280℃)이다. SASOL은 사솔 리미티드(남아프리카공화국 요하네스버그 소재)의 제품, 예를 들어 SASOL LPA-210, SASOL-47(비점=238-274℃)이다.
본 발명의 NFP로서 적합한 파라핀은 또한 다음과 같이 기재되는 소위 PAO도 포함한다. 본 발명에 유용한 PAO는 C6 내지 C200 파라핀, 다른 실시태양에서는 C10 내지 C100 n-파라핀을 포함한다. PAO는 한 실시태양에서 C4 내지 C12 α-올레핀의 이량체, 삼량체, 사량체, 오량체 등이고, 다른 실시태양에서 C5 내지 C12 α-올레핀의 이량체, 삼량체, 사량체, 오량체 등이다. 적합한 올레핀은 1-뷰텐, 1-펜텐, 1-헥센, 1-헵텐, 1-옥텐, 1-노넨, 1-데센, 1-운데센 및 1-도데센을 포함한다. 한 실시태양에서, 올레핀은 1-데센이고, NFP는 1-데센의 이량체, 삼량체, 사량체 및 오량체(및 그 이상)의 혼합물이다. PAO는 예를 들어 미국 특허 제 5,171,908 호, 제 5,783,531 호 및 문헌[SYNTHETIC LUBRICANTS AND HIGH-PERFORMANCE FUNCTIONAL FLUIDS 1-52(루드닉 및 슈브킨 편집, Marcel Dekker, Inc. 1999)]에 더욱 구체적으로 기재되어 있다.
본 발명의 PAO는 한 실시태양에서 100 내지 20,000, 다른 실시태양에서 200 내지 10,000, 또 다른 실시태양에서 200 내지 7,000, 다른 실시태양에서 200 내지 2,000, 또 다른 실시태양에서 200 내지 500의 중량평균 분자량을 갖는다. 일반적으로, PAO는 100℃에서 0.1 내지 150cSt, 다른 실시태양에서 100℃에서 0.1 내지 3000cSt의 점도(ASTM 445)를 갖는다. 본 발명에 유용한 PAO는 한 실시태양에서 0℃ 미만, 다른 실시태양에서 -10℃ 미만, 또 다른 실시태양에서 -20℃ 미만, 다른 실시태양에서 -40℃ 미만의 유동점을 갖는다. 바람직한 PAO는 SHF 및 SuperSyn PAO(엑손모빌 케미칼 캄파니, 텍사스주 휴스턴 소재)로서 시판중이며, 이들중 일부가 아래 표 2에 요약되어 있다.
PAO의 부분집합인 폴리뷰텐은 본 발명의 다른 유용한 NFP이고, 다음과 같이 기재된다. 본 발명의 한 실시태양에서, 폴리뷰텐 가공유는 한 실시태양에서 3 내지 8개의 탄소원자, 바람직하게는 다른 실시태양에서 4 내지 6개의 탄소원자를 갖는 올레핀 유도된 단위의 저분자량(15,000 미만의 수평균 분자량; 60,000 미만의 중량평균 분자량) 단독중합체 또는 공중합체이다. 또 다른 실시태양에서, 폴리뷰텐은 C4 라피네이트의 단독중합체 또는 공중합체이다. "폴리뷰텐" 중합체로 지칭되는 이러한 저분자량 중합체의 실시태양은 예를 들어 문헌[SYNTHETIC LUBRICANTS AND HIGH-PERFORMANCE FUNCTIONAL FLUIDS 357-392 (루드닉 및 슈브킨 편집, Marcel Dekker 1999)]에 기재되어 있다(이후, "폴리뷰텐 가공유" 또는 "폴리뷰텐"이라고 함).
다른 방식으로 기재하자면, 폴리뷰텐은 적어도 아이소뷰틸렌 유도된 단위, 1-뷰텐 유도된 단위 및 2-뷰텐 유도된 단위의 공중합체이다. 한 실시태양에서, 폴리뷰텐은 세 단위의 단독중합체, 공중합체 또는 삼원공중합체이며, 이 때 아이소뷰틸렌 유도된 단위는 공중합체의 40 내지 100중량%이고, 1-뷰텐 유도된 단위는 공중합체의 0 내지 40중량%이며, 2-뷰텐 유도된 단위는 공중합체의 0 내지 40중량%이다. 다른 실시태양에서, 폴리뷰텐은 세 단위의 공중합체 또는 삼원공중합체이고, 이 때 아이소뷰틸렌 유도된 단위는 공중합체의 40 내지 99중량%이고, 1-뷰텐 유도된 단위는 공중합체의 2 내지 40중량%이며, 2-뷰텐 유도된 단위는 공중합체의 0 내지 30중량%이다. 또 다른 실시태양에서, 폴리뷰텐은 세 단위의 삼원공중합체로서, 여기에서 아이소뷰틸렌 유도된 단위는 공중합체의 40 내지 96중량%이고, 1-뷰텐 유도된 단위는 공중합체의 2 내지 40중량%이며, 2-뷰텐 유도된 단위는 공중합체의 2 내지 20중량%이다. 또 다른 실시태양에서, 폴리뷰텐은 아이소뷰틸렌과 1-뷰텐의 단독중합체 또는 공중합체로서, 아이소뷰틸렌 유도된 단위는 단독중합체 또는 공중합체의 65 내지 100중량%이고, 1-뷰텐 유도된 단위는 공중합체의 0 내지 35중량%이다.
본 발명에 유용한 폴리뷰텐 가공유는 전형적으로 한 실시태양에서 10,000g/몰 미만, 다른 실시태양에서 8000g/몰 미만, 또 다른 실시태양에서 6000g/몰 미만의 수평균 분자량(Mn)을 갖는다. 한 실시태양에서, 폴리뷰텐 오일은 400g/몰보다 큰 수평균 분자량, 다른 실시태양에서는 700g/몰보다 큰 수평균 분자량, 또 다른 실시태양에서는 900g/몰보다 큰 수평균 분자량을 갖는다. 바람직한 실시태양은 본원에 기재된 임의의 분자량 하한과 임의의 분자량 상한의 조합일 수 있다. 예를 들어, 본 발명의 폴리뷰텐의 한 실시태양에서, 폴리뷰텐은 400 내지 10,000g/몰, 다른 실시태양에서 700 내지 8000g/몰, 또 다른 실시태양에서 900 내지 3000g/몰의 수평균 분자량을 갖는다. 폴리뷰텐 가공유의 유용한 점도는 한 실시태양에서 100℃에서 10 내지 6000cSt(센티스톡), 다른 실시태양에서 100℃에서 35 내지 5000cSt이고, 또 다른 실시태양에서 100℃에서 35cSt보다 크고, 다른 실시태양에서 100℃에서 100cSt보다 크다.
폴리뷰텐의 시판중인 예는 PARAPOLTM 씨리즈의 가공유(인피늄(Infineum)), 뉴저지주 린덴 소재), 예를 들어 PARAPOLTM 450, 700, 950, 1300, 2400 및 2500이다. 시판중인 PARAPOLTM 씨리즈의 폴리뷰텐 가공유는 합성 액체 폴리뷰텐이며, 개별적인 제제 각각은 특정 분자량을 갖고, 모든 제제는 본 발명의 조성물에 사용될 수 있다. PARAPOLTM 오일의 분자량은 겔 투과 크로마토그래피에 의해 결정할 때 420 Mn(PARAPOLTM 450) 내지 2700 Mn(PARAPOLTM 2500)이다. PARAPOLTM 오일의 MWD는 한 실시태양에서 1.8 내지 3, 다른 실시태양에서 2 내지 2.8이고; 이들 폴리뷰텐의 유동점은 한 실시태양에서 25℃ 미만, 다른 실시태양에서 0℃ 미만, 또 다른 실시태양에서 -10℃ 미만, 다른 실시태양에서 -80 내지 25℃이며; 밀도(20℃에서 IP 190/86)는 0.79 내지 0.92g/cm3, 다른 실시태양에서 0.81 내지 0.90g/cm3이다.
아래 표 3에는 본 발명의 실시태양에 유용한 PARAPOLTM 오일의 특성중 일부가 기재되어 있으며, 그중 점도는 ASTM D445-97에 따라 결정되었고, 수평균 분자량(Mn)은 겔 투과 크로마토그래피에 의해 결정되었다.
따라서, 본 발명에 사용하기 바람직한 NFP는 본원에 기재된 임의의 실시태양, 또는 본원에 기재된 실시태양의 임의의 조합에 의해 기재될 수 있다. 예를 들어, 한 실시태양에서, NFP는 25℃ 미만의 유동점을 갖는 C6 내지 C200 파라핀이다. 다른 방식으로 기재하면, NFP는 100℃에서 0.1 내지 1000cSt의 점도를 갖는 지방족 탄화수소를 포함한다. 또 다른 방식으로 기재하자면, NFP는 8 내지 25개의 탄소원자를 갖는 n-파라핀, 분지된 아이소파라핀 및 이들의 블렌드로부터 선택된다. NFP는 폴리올레핀과 블렌딩되어 가소화된 조성물을 형성할 때 NFP가 프로필렌 중합체와 상용성 및 혼화성이고 별도의 상을 형성하지 않는다는 점을 특징으로 한다.
본 발명의 조성물의 한 실시태양에서, 폴리(비닐 클로라이드)에 대해 통상적으로 사용되는 것과 같은 통상적인 가소화제는 실질적으로 존재하지 않는다. 구체적으로, 프탈레이트, 아디페이트, 트라이멜리테이트 에스터, 폴리에스터, 및 예컨대 미국 특허 제 3,318,835 호, 제 4,409,345 호, WO 02/31044 A1 호 및 문헌[PLASTICS ADDITIVES 499-504(프릿챠드 편집, Chapman & Hall 1998)]에 개시되어 있는 다른 작용화된 가소화제 같은 가소화제는 실질적으로 존재하지 않는다. "실질적으로 존재하지 않는"이란, 이들 화합물을 의도적으로 조성물에 첨가하지 않음을 의미한다.
다른 실시태양에서는 나프텐 및 다른 방향족 함유 오일 같은 오일이 본 발명의 조성물의 0.5중량% 미만으로 존재한다. 또한, 또 다른 실시태양에서는 방향족 잔기 및 탄소-탄소 불포화가 본 발명에 사용되는 작용화되지 않은 가소화제에 실질적으로 존재하지 않는다. 방향족 잔기는 그 분자가 벤젠, 나프탈렌, 페난트렌, 안트라센 등의 고리 구조 특징을 갖는 화합물을 포함한다. "실질적으로 존재하지 않는"은 이들 방향족 화합물 또는 잔기를 조성물에 일부러 첨가하지 않으며, 존재하는 경우에도 NFP의 조성물의 0.5중량% 미만으로 존재함을 의미한다. 따라서, 대부분의 "광유"는 본 발명의 조성물에 실질적으로 존재하지 않는다.
본 발명의 조성물의 다른 실시태양에서는, 통상적인 가소화제, 엘라스토머 또는 "상용화제", 예컨대 저분자량 폴리에틸렌이 실질적으로 존재하지 않는다. 구체적으로, 500 내지 10,000의 중량평균 분자량을 갖는 폴리에틸렌 단독중합체 및 공중합체는 실질적으로 존재하지 않는다. 이러한 폴리에틸렌 상용화제는 예컨대 WO 01/18109 A1 호에 개시되어 있다. "실질적으로 존재하지 않는"이란 이들 화합물을 조성물에 의도적으로 첨가하지 않는다는 의미이다.
블렌딩 및 제품 제조
본 발명의 폴리올레핀 조성물은 다른 첨가제도 함유할 수 있다. 이들 첨가제는 산화방지제, 핵형성제, 산 소거제, 안정화제, 부식 방지제, 발포제, 쇄-파괴 산화방지제 등과 같은 다른 UV 흡수제, 급랭제, 대전방지제, 미끄럼제, 안료, 염료 및 충전제, 및 퍼옥사이드 같은 경화제를 포함한다. 당해 분야에 통상적인 염료 및 다른 착색제는 한 실시태양에서 0.01 내지 10중량%, 다른 실시태양에서 0.1 내지 6중량%로 존재할 수 있다. 적합한 핵형성제는 예를 들어 벡크(H. N. Beck)의 문헌[Heterogeneous Nucleating Agents for Polypropylene Crystallization, 11 J. APPLIED POLY. SCI. 673-685 (1967) 및 Heterogeneous Nucleation Studies on Polypropylene, 21 J. POLY. SCI.: POLY. LETTERS 347-351 (1983)]에 개시되어 있다. 적합한 핵형성제의 예는 소듐 벤조에이트, 소듐 2,2'-메틸렌비스(4,6-다이-3급-뷰틸페닐) 포스페이트, 알루미늄 2,2'-메틸렌비스(4,6-다이-3급-뷰틸페닐) 포스페이트, 다이벤질리덴 솔비톨, 다이(p-톨릴리덴) 솔비톨, 다이(p-에틸벤질리덴) 솔비톨, 비스(3,4-다이메틸벤질리덴) 솔비톨 및 N',N'-다이사이클로헥실-2,6-나프탈렌다이카복사마이드, 및 불균화(disproportionated) 로진 에스터의 염이다. 전술한 목록은 본 폴리프로필렌 배합물에 포함시키기 위한 적합한 핵형성제의 선택을 예시하고자 한다.
구체적으로, 유기 포스파이트, 장애 아민 및 페놀 산화방지제 같은 산화방지제 및 안정화제는 본 발명의 폴리올레핀 조성물에 한 실시태양에서는 0.001 내지 2중량%로, 다른 실시태양에서는 0.01 내지 0.8중량%로, 또 다른 실시태양에서는 0.02 내지 0.5중량%로 존재할 수 있다. 적합한 유기 포스파이트의 비한정적인 예는 트리스(2,4-다이-3급-뷰틸페닐)포스파이트(IRGAFOS 168) 및 다이(2,4-다이-3급-뷰틸페닐)펜타에리트리톨 다이포스파이트(ULTRANOX 626)이다. 장애 아민의 비제한적인 예는 폴리[2-N,N'-다이(2,2,6,6-테트라메틸-4-피페리딘일)-헥세인다이아민-4-(1-아미노-1,1,3,3-테트라메틸뷰테인)심-트라이아진](CHIMASORB 944); 비스(1,2,2,6,6-펜타메틸-4-피페리딜)세바케이트(TINUVIN 770)를 포함한다. 페놀 산화방지제의 비한정적인 예는 펜타에리트리틸 테트라키스(3,5-다이-3급-뷰틸-4-하이드록시페닐) 프로피온에이트(IRGANOX 1010); 및 1,3,5-트리스(3,5-다이-3급-뷰틸-4-하이드록시벤질-아이소사이아뉴레이트(IRGANOX 3114)를 포함한다.
충전제는 한 실시태양에서 조성물의 0.1 내지 50중량%로, 다른 실시태양에서 조성물의 0.1 내지 25중량%로, 또 다른 실시태양에서 0.2 내지 10중량%로 존재할 수 있다. 바람직한 충전제는 이산화티탄, 탄화규소, 실리카(및 침전되거나 침전되지 않은 실리카의 다른 산화물), 산화안티몬, 탄산납, 징크 화이트(zinc white), 리소폰, 지르콘, 강옥, 청정석, 인회석, 중정석 분말, 황산바륨, 마그네사이터, 카본 블랙, 돌로마이트, 탄산칼슘, 활석, 및 수화되거나 되지 않은 이온 Mg, Ca 또는 Zn 및 Al, Cr 또는 Fe 및 CO3 및/또는 HPO4의 하이드로탈사이트 화합물; 석영 분말, 하이드로클로릭 마그네슘 카본에이트, 유리 섬유, 점토, 알루미나 및 다른 금속 산화물 및 탄산염, 금속 수산화물, 크롬, 인 및 브롬화 난연제, 삼산화안티몬, 실리카, 실리콘 및 이들의 블렌드를 포함하지만, 이들로 한정되는 것은 아니다. 이들 충전제는 특히 당해 분야에 공지되어 있는 임의의 다른 충전제 및 다공성 충전제와 지지체를 포함할 수 있으며, 한 실시태양에서는 폴리올레핀에 첨가하기 전에 충전제 내로 미리 접촉시키거나 미리 흡수시킨 본 발명의 NFP를 가질 수 있다.
더욱 구체적으로, 본 발명의 한 실시태양에서는, NFP 또는 NFP중 일부를 충전제, 바람직하게는 다공성 충전제와 블렌딩시킬 수 있다. 예컨대 텀블러 또는 다른 습식 블렌딩 장치에 의해 NFP와 충전제를 블렌딩시킬 수 있다. NFP와 충전제의 균질한 조성물을 형성시키기에 적합한 시간, 바람직하게는 한 실시태양에서 1분 내지 5시간동안 이 실시태양의 NFP와 충전제를 블렌딩시킨다. 이어, 폴리올레핀의 가소화를 수행하기 위하여 이 NFP/충전제 블렌드를 본 발명에 유용한 폴리올레핀과 블렌딩시킬 수 있다. 다른 실시태양에서는, 폴리올레핀과 충전제를 접촉시키기 전에 다공성 충전제를 NFP 또는 그의 일부와 접촉시킬 수 있다. 다른 실시태양에서는, 다공성 충전제, 폴리올레핀 및 NFP를 동시에(또는 동일한 블렌딩 장치에서) 접촉시킨다. 어느 경우에나, NFP는 조성물의 0.1 내지 60중량%로, 다른 실시태양에서는 0.2 내지 40중량%로, 또 다른 실시태양에서는 0.3 내지 20중량%로 존재할 수 있다.
지방산 염도 또한 본 발명의 폴리올레핀 조성물에 존재할 수 있다. 이들 염은 한 실시태양에서 조성물의 0.001 내지 1중량%로, 다른 실시태양에서 0.01 내지 0.8중량%로 존재할 수 있다. 지방산 금속 염의 예는 라우르산, 스테아르산, 석신산, 스테아릴 락트산, 락트산, 프탈산, 벤조산, 하이드록시스테아르산, 리시놀레산, 나프텐산, 올레산, 팔미트산 및 에루스산을 포함하며, 적합한 금속은 Li, Na, Mg, Ca, Sr, Ba, Zn, Cd, Al, Sn, Pb 등을 포함한다. 바람직한 지방산 염은 스테아르산마그네슘, 스테아르산칼슘, 스테아르산나트륨, 스테아르산아연, 올레산칼슘, 올레산아연 및 올레산마그네슘으로부터 선택된다.
생성된 본 발명의 가소화된 폴리올레핀은 캘린더링, 주조, 코팅, 배합, 압출, 발포, 적층, 취입 성형, 압축 성형, 사출 성형, 열성형, 이송 성형(transfer molding), 주조 성형 , 회전 성형, 필름으로의 주조, 섬유로의 방사 또는 용융 결합, 또는 예컨대 문헌[PLASTICS PROCESSING (Radian Corporation, Noyes Data Corp. 1986)]에 기재되어 있는 것과 같은 다른 가공 형태 같은 임의의 적합한 수단에 의해 가공될 수 있다. 더욱 구체적으로는, 블렌드를 생성시키는 물리적 방법과 관련하여, 최종 제품으로 전환시키기 전에 균일한 블렌드가 생성되도록 하기에 충분히 혼합시켜야 한다.
더욱 구체적으로는, 임의의 적합한 수단에 의해 본 발명의 폴리올레핀 조성물의 성분을 블렌딩시켜 가소화된 폴리올레핀을 형성시킬 수 있으며, 이는 유용한 제품으로 추가로 가공하기에 적합하다. 본 발명의 한 요지에서는, 압출기 또는 브라벤더 혼합기 같은 장치에서 폴리올레핀과 NFP를 블렌딩시키거나 또는 용융 블렌딩시킨다. 또한, 텀블러, 이중-원뿔 블렌더, 리본 블렌더 또는 다른 적합한 블렌더를 이용하여 폴리올레핀을 NFP와 블렌딩시킬 수도 있다. 또 다른 실시태양에서는, 예컨대 텀블러와 압출기에서의 용융 블렌딩의 조합에 의해 폴리올레핀을 NFP와 블렌딩시킨다. 폴리프로필렌에 대한 압출 기법은 예컨대 문헌[PLASTICS EXTRUSION TECHNOLOGY 26-37(헨센 편집, Hanser Publishers 1988) 및 POLYPROPYLENE HANDBOOK 304-348(무어, 2세 편집, Hanser Publishers 1996)]에 더욱 상세하게 기재되어 있다.
본 발명에 사용하기 적합한 폴리올레핀은 본 발명의 NFP와 블렌딩시키는데 사용될 때 임의의 물리적 형태일 수 있다. 한 실시태양에서는, 중합 반응기로부터 단리된 중합체의 과립으로서 정의되는 반응기 과립을 사용하여 본 발명의 NFP와 블렌딩시킨다. 반응기 과립은 10㎛ 내지 5mm, 다른 실시태양에서는 50㎛ 내지 10mm의 평균 직경을 갖는다. 다르게는, 폴리올레핀은 예컨대 반응기 과립의 용융 압출로부터 형성된 평균 직경 1mm 내지 6mm의 펠렛의 형태이다.
NFP를 폴리올레핀과 블렌딩시키는 한 방법은 폴리올레핀이 반응기 과립의 형태인 경우 이들 성분을 텀블러에서 접촉시키는 것이다. 이는 폴리프로필렌 단독중합체의 경우에 특히 잘 작용한다. 이어, 필요한 경우 압출기에서 용융 블렌딩시킬 수 있다. 성분들을 블렌딩시키는 다른 방법은 압출기 또는 브라벤더에서 폴리올레핀 펠렛을 NFP와 바로 용융 블렌딩시키는 것이다.
따라서, 다양한 제품의 사출 성형의 경우, 성형 과정이 원료 물질의 재용융 및 혼합을 포함하기 때문에, 펠렛의 단순한 고체 상태 블렌드가, 원료 중합체 과립의 펠렛화된 용융 상태 블렌드, 과립과 펠렛의 펠렛화된 용융 상태 블렌드 또는 두 성분의 펠렛의 펠렛화된 용융 상태 블렌드와 동일하게 작용한다. 그러나, 의료 기기의 압축 성형 과정에서는, 용융 성분의 혼합이 거의 이루어지지 않으며, 구성성분 펠렛 및/또는 과립의 단순한 고체 상태 블렌드보다 펠렛화된 용융 블렌드가 바람직하다. 당해 분야의 숙련자는 구성성분의 긴밀한 혼합의 필요성과 공정 경제성에 대한 욕구의 균형을 맞추기에 적절한 중합체 블렌딩 절차를 결정할 수 있을 것이다.
본 발명의 폴리올레핀 조성물은 자동성 부품, 와이어 및 케이블 쟈켓팅, 파이프, 농업용 필름, 지오멤브레인(geomembrane), 장난감, 운동용품, 의료 기기, 포장 필름의 주조 및 발포, 관재, 파이프 및 프로파일의 압출, 운동용품, 옥외용 가구(예: 정원용 가구) 및 놀이터 설비, 보트 및 선박 부품 및 이러한 다른 제품 등의 제품에 적합하다. 특히, 본 조성물은 범퍼, 그릴, 트림 부품, 계기반 및 계기판, 외장용 문 및 후드 부품, 스포일러, 바람막이, 휠캡, 거울 틀, 몸체 패널, 보호용 측면 몰딩 같은 자동차 부품, 및 자동차, 트럭, 보트 및 다른 차량에 수반되는 다른 내장용 및 외장용 부품에 적합하다.
본 발명을 실행함으로써 경제적으로 제조될 수 있는 다른 유용한 제품 및 상품은 틀상자, 용기, 포장재, 실험용품(예: 배양액 성장용 롤러 병 및 배지 병), 사무실용 바닥 매트, 기계류 샘플 홀더 및 샘플 윈도우; 액체 저장 용기(예: 백, 파우치 및 혈액 또는 용액의 저장 및 IV 주입을 위한 병); 단위-투여 또는 다른 블리스터 또는 버블 팩을 비롯한, 임의의 의료 기기 또는 약물용 포장재 및 조사에 의해 보존되는 식품의 포장 또는 보관용 포장재를 포함하는 포장재를 포함한다. 다른 유용한 품목은 주입 키트, 카테터 및 호흡 요법을 비롯한 임의의 의료 기기에 사용하기 위한 의료용 관재 및 밸브, 및 의료 기기 또는 트레이를 포함하는 조사된 식품, 및 저장 액체, 특히 물, 우유 또는 쥬스용 포장재, 단위 투여용을 비롯한 용기 및 벌크 저장 용기, 및 관재, 파이프 등과 같은 전달 수단을 포함한다.
이들 기기는 폴리올레핀을 성형시키기 위한 임의의 유용한 성형 수단에 의해 제조 또는 성형될 수 있다. 이는 적어도 압출 성형, 사출 성형, 취입 성형 및 이송 성형을 비롯한 성형; 필름 취입 또는 주조; 압출 및 열 성형; 및 적층, 인발 성형(pultrusion), 돌출, 드로 리덕션(draw reduction), 회전 성형, 방사 결합, 용융 방사, 용융 취입; 또는 이들의 조합을 포함한다. 적어도 열 성형 또는 필름 도포를 이용함으로써, 방사선 내성 물질의 1축 또는 2축 배향의 이점을 취할 수 있으며 이러한 이점을 유도할 수 있다.
한 실시태양에서, 본 발명은 99.9중량% 내지 60중량%의 폴리올레핀 및 0.1중량% 내지 40중량%의 NFP를 포함하며, 이 때 NFP가 -5℃ 미만의 유동점을 갖는 C6 내지 C200 파라핀을 포함하는, 가소화된 폴리올레핀 조성물이다. 또 다른 실시태양에서, 작용화되지 않은 가소화제는 C8 내지 C100 파라핀을 포함한다. 또 다른 실시태양에서, NFP는 C6 내지 C50 아이소파라핀을 포함하고, 다른 실시태양에서는 C10 내지 C100 n-파라핀을 포함한다.
다른 방식으로 기재하면, 본 발명의 가소화된 폴리올레핀은 폴리올레핀과 작용화되지 않은 가소화제의 블렌드로서, 이 때 작용화되지 않은 가소화제는 한 실시태양에서는 40℃에서 0.5 내지 200cSt의 점도 범위(ASTM D445-97)에서 -30℃ 미만의 유동점을 갖는 화합물, 다른 실시태양에서는 40℃에서 0.5 내지 200cSt의 점도 범위(ASTM D445-97)에서 -30℃ 내지 -90℃의 유동점을 갖는 화합물이다.
조성물은 또한 임의의 수의 물리적 특성 및 화학적 특성에 의해 기재될 수도 있다. 예를 들어, 한 실시태양에서, 본 발명의 조성물은 Tm은 1 내지 2℃ 내로 유지하면서 폴리올레핀의 Tg가 조성물에 첨가되는 매 4중량%의 NFP에 대해 4 내지 10℃ 감소됨을 특징으로 한다.
본 발명의 NFP는 본원에 기재된 임의의 수의 물리적 특성 및 화학적 특성에 의해 기재될 수 있다. 예를 들어, 한 실시태양에서 작용화되지 않은 가소화제는 -30℃ 미만의 유동점; 다른 실시태양에서 100℃에서 0.1 내지 3000cSt의 점도; 또 다른 실시태양에서 2.1 미만의 20℃에서의 유전상수; 및 또 다른 실시태양에서 0.91g/cm3 미만의 비중을 갖는다. NFP의 다른 실시태양에서는, 방향족 잔기가 실질적으로 존재하지 않는다.
또한, NFP는 100 내지 25,000g/몰, 다른 실시태양에서는 200 내지 10,000g/몰의 중량평균 분자량을 갖는다.
본 발명의 조성물에 적합한 폴리올레핀은 임의의 수의 실시태양에 의해 기재될 수 있다. 한 실시태양에서, 폴리올레핀은 아이소택틱 분절을 포함한다. 다른 실시태양에서, 폴리올레핀은 프로필렌 단독중합체, 프로필렌 공중합체, 프로필렌 충격 공중합체, 및 이들의 혼합물로부터 선택된다. 또 다른 실시태양에서, 폴리올레핀은 아이소택틱 폴리프로필렌이다. 또 다른 실시태양에서, 폴리올레핀은 에틸렌 유도된 단위 및 C4 내지 C20 α-올레핀 유도된 단위로부터 선택되는 단위 및 프로필렌 유도된 단위를 포함하는 공중합체이다.
또 다른 실시태양에서, 폴리올레핀은 공중합체의 총 중량에 기초하여 40 내지 95중량%의 성분 A 및 5 내지 60중량%의 성분 B를 포함하는 프로필렌 충격 공중합체이며; 이 때 성분 A는 프로필렌 단독중합체 또는 공중합체를 포함하고, 이 공중합체는 10중량% 이하의 에틸렌, 뷰텐, 헥센 또는 옥텍 공단량체를 포함하며; 성분 B는 5 내지 70중량%의 에틸렌, 뷰텐, 헥센 및/또는 옥텐 공단량체 및 95 내지 30중량%의 프로필렌을 포함하는 프로필렌 공중합체를 포함한다.
폴리올레핀은 플라스토머를 추가로 포함할 수 있다.
본 발명의 조성물은 500 내지 10,000의 중량평균 분자량을 갖는 폴리에틸렌이 실질적으로 존재하지 않는 다른 실시태양으로 기재될 수 있다.
본 발명은 또한 폴리올레핀을 작용화되지 않은 가소화제와 블렌딩시킴을 포함하며, 이 때 작용화되지 않은 가소화제가 -5℃ 미만의 유동점을 갖는 C6 내지 C200 파라핀을 포함하는, 폴리올레핀을 가소화시키는 방법에 관한 것이다. 한 실시태양에서, 블렌딩은 용융 블렌딩을 포함한다. 한 실시태양에서는 압출기에서 용융 블렌딩을 수행한다.
한 실시태양에서, 블렌딩은 고체 폴리올레핀의 습식 블렌딩을 포함한다. 폴리올레핀은 한 실시태양에서 반응기 과립의 형태이거나, 다른 실시태양에서 압출된 펠렛의 형태이거나, 또는 이들의 블렌드 형태이다. 반응기 과립이 사용되는 경우, 반응기 과립은 한 실시태양에서 10㎛ 내지 5mm의 평균 직경을 갖는다.
본 발명의 조성물로부터 제품을 제조할 수 있으며, 이러한 제품의 비한정적인 예는 필름, 시이트, 섬유, 직물 및 부직포, 관, 파이프, 자동차 부품, 가구, 운동용품, 식품 저장 용기, 투명 및 반투명 제품, 장난감, 관재 및 파이프, 및 의료 기기를 포함한다.
본 발명은 하기 실시예 및 표를 참조함으로써(그러나, 이들로 한정되지는 않음) 더욱 잘 이해될 수 있다.
동적 기계적 열분석("DMTA")에 의해 다음과 같이 유리전이온도(Tg) 및 저장 모듈러스(E')를 결정하였다. 임의의 편향 각도로 한쪽 단부가 고정된 강한 직사각형 빔을 진동시킴으로써, 동적 기계적 시험을 수행하였다. 힘 및 편향 각도를 사용하여 각각 응력 및 변형을 계산한다. 응력 대 변형의 비는 모듈러스를 생성시킨다. 시험 동안 온도를 변화시켜 물질의 행태에 대한 정보를 온도의 함수로서 수득한다. 시험 변수는 단일 캔틸레버, 1Hz의 주파수, -130℃의 출발 온도 및 60℃의 최대 온도를 포함한다. 온도는 2℃/분의 속도로 증가한다. Tan δ는 E"/E'의 비이고, 여기에서 E"은 손실 모듈러스, E'은 저장 모듈러스 또는 탄성 모듈러스이다. 유리 전이 온도는 Tan δ가 그의 최대값에 도달할 때의 온도에 의해 결정된다.
결정화 온도(Tc) 및 융점(Tm)은 다음과 같이 측정하였다: 시차 주사 열계량법(DSC, 10℃/분의 가열 속도). 예로서, 약 150℃ 내지 200℃에서 가압된 중합체 또는 가소화된 중합체 시이트 약 6 내지 10mg을 펀치 다이에서 제거한다. 샘플을 시차 주사 열계량기(퍼킨 엘머 7 씨리즈 열분석 시스템(Perkin Elmer 7 Series Thermal Analysis System))에 놓고, 200℃로 가열한 다음 10분간 유지시킨다. 샘플을 10℃/분으로 냉각시켜 25℃의 최종 온도를 달성한다. 열 출력을 기록하고, 열 출력 데이터를 전자적으로 주사시킴으로써 열 용량의 변화를 나타내는 열 출력 데이터의 굴절 지점을 결정한다. 주사 열 출력 데이터의 최대치는 샘플의 결정화 온도에 상응한다. 샘플을 25℃에서 10분간 유지시키고, 10℃/분으로 가열하여 200℃로 높인다. 열 출력을 기록하고, 열 출력 데이터를 전자적으로 주사시킴으로써 열 용량 변화를 나타내는 열 출력 데이터의 굴절 지점을 결정한다. 주사 열 출력 데이터의 최대치는 샘플의 융점에 상응한다.
겔 투과 크로마토그래피를 이용하여 분자량 분포를 결정하였다.
이중-배럴 모세관 유동계에 의해, 전단 속도의 함수로서의 전단 점도를 결정하였다. 모세관 유동계(보은 인스트루먼츠(Bohun Instruments)의 로전드(Rosand) 모델 RAH7/2)는 모세관의 길이 대 직경 비가 30:1이 되도록 설치된다. 총 질량 25 내지 30g의 펠렛을 모세관 배럴 내에 팩킹시키고, 230℃에서 10분간 예열시켜 시험 전에 임의의 연생된 공기를 제거하였다. 230℃에서 30 내지 3000s-1의 전단 속도에 걸쳐 각 시험을 수행하였다. 유동계의 제 2 배럴 내로 설치된 구멍을 통한 물질의 유동에 대한 동시 압력 손실 측정을 통해 온-라인으로 입구 압력 손실 데이터에 대한 보정(즉, 베이글리(Bagley) 보정)을 수행하였다.
당해 분야에 공지되어 있는 방사 결합 부직포의 유연성 또는 "핸드(hand)"는 튜잉-앨버트 핸들-오-미터(Thwing-Albert Handle-O-Meter)(모델 211-10-B/America)를 사용하여 측정하였다. "핸드"의 품질은 직물의 표면 마찰로 인한 저항성과 가요성의 조합인 것으로 생각된다. 핸드-오-미터는 평행한 가장자리의 슬롯 내로 물질의 시편을 통과시킬 때 블레이드가 겪게 되는 저항성을 측정하는 LVDT(선형 가변 주사 변형기)를 사용하여 상기 두 인자를 측정한다. 3½ 숫자 디지털 전압계(DVM)는 저항성을 직접 g 단위로 나타낸다. 임의의 소정 물질 시이트의 "전체 핸드"는 시험 샘플의 양쪽면에서 양쪽 방향으로 취한 4가지 판독치의 평균이며, 샘플 물질의 표준 폭당 g 단위로 기록된다. "전체 핸드"의 감소는 직물 유연성의 개선을 나타낸다.
다른 시험 방법은 아래 표에 기재되어 있다.
임의의 적합한 수단에 의해 본 발명의 성분을 블렌딩시킬 수 있다. 아래 실시예는 성분을 블렌딩시키는 한 방법을 예시한다. 샘플 1 내지 5의 경우, 먼저 텀블 블렌더에서 산화방지제(즉, Irganox 1076 600ppm 및 스테아르산칼슘 260ppm) 및 블렌드 성분을 균질하게 혼합시키기 위한 가소화된 샘플용 NFP 4중량%를 첨가하여, 메탈로센 제조된 프로필렌 단독중합체의 반응기 과립을 블렌딩시켰다. 230℃의 압출 온도에서 57mm 2축 압출기를 사용하여, 블렌딩된 중합체를 배합 및 펠렛화시켰다. 샘플 10 내지 14의 경우, 먼저 텀블 블렌더에서 반응기 과립 및 산화방지제(즉, 스테아르산칼슘 825ppm, Ultranox 626 800ppm, TINUVIN 622 500ppm 및 Millad 3940 2500ppm), 및 블렌드 성분을 균질하게 혼합시키기 위한 가소화된 샘플용 NFP 5중량%를 첨가하여, 프로필렌 랜덤 공중합체의 반응기 과립을 블렌딩시켰다. 216℃의 압출 온도에서 30mm 2축 압출기를 이용하여, 블렌딩된 중합체를 배합 및 펠렛화시켰다. 샘플 15 내지 19의 경우, 먼저 텀블 블렌더에서 반응기 과립 및 산화방지제(즉, 스테아르산칼슘 800ppm, IRGANOX 1010 1500ppm, ULTRANOX 626 500ppm 및 벤조산나트륨 675ppm), 및 블렌드 성분을 균질하게 혼합하기 위한 가소화된 샘플용 NFP 5중량%를 첨가하여, 프로필렌 충격 공중합체의 반응기 과립을 블렌딩시켰다. 205℃의 압출 온도에서 30mm 1축 압출기를 사용하여, 블렌딩된 중합체를 배합 및 펠렛화시켰다. 샘플 6 내지 9의 경우, 샘플 1 내지 5에 대해 기재된 바와 같은 방식으로 10중량% 가소화된 메탈로센 프로필렌 단독중합체를 제조하였다. 샘플 21 내지 24의 경우에는, 샘플 6 내지 9에 대해 상기 기재된 것과 동일한 방식으로 제조된 10중량% 가소화된 메탈로센 제조된 프로필렌 단독중합체를 펠렛 형태의 순수한 프로필렌 중합체(AchieveTM 3854)와 건식 블렌딩시켜, 블렌드중 4중량%의 활성 가소화 샘플을 수득하였다.
120톤 사출 성형 장치를 사용하여, 표준 ASTM 인장 및 HDT 바, 및 가드너 충격 디스크를 제조하였다. 제조된 샘플의 물리적 특성은 아래 표에 기재되어 있다. 본 발명의 가소화된 폴리프로필렌 단독중합체로부터의 성형 부품은, 인장 강도, 실온 아이조드(Izod) 내충격성 및 열변형 온도를 유지하면서, 4중량%의 PAO 또는 아이소파라핀이 첨가될 때 굴곡 모듈러스 및 인장 모듈러스의 상당한 감소를 나타낸다. 비교하기 위하여, 성형 부품 표면 마찰을 감소시키도록 디자인된 통상적인 윤활제인 에루카마이드(표 11)를 4중량% 농도로 사용하여 또한 성형 부품을 제조하였다. 굴곡 모듈러스에 대한 에루카마이드의 효과는 미미하다.
전형적인 방사 결합 방법은 연속 필라멘트 압출, 인발, 몇몇 유형의 방출기를 사용함에 의한 웹 형성 및 웹 결합으로 이루어진다. 먼저 중합체 펠렛을 압출기에 공급한다. 압출기에서는, 펠렛을 동시에 용융시키고, 가열 용융 스크류에 의해 시스템을 통해 통과시킨다. 스크류 다음에는, 방사 펌프가 용융된 중합체를 필터를 통해 방사구금으로 칭량해 넣고, 방사구금에서는 용융된 중합체를 모세관을 통해 가압하에 구멍 1개당 1분당 0.4g의 속도로 압출시킨다. 방사구금은 직경이 0.4mm인 수백개의 모세관을 갖는다. 중합체를 그의 융점보다 약 30 내지 50℃ 더 높은 온도에서 용융시켜, 압출시키기에 충분히 낮은 용융 점도를 달성한다. 방사수금에서 나오는 섬유를 급랭시키고, 직경 약 16마이크론의 미세한 섬유로 인발한다. 고화된 섬유를 이동하는 벨트상에 무작위적으로 놓아, 당해 분야에서 웹으로 공지되어 있는 무작위적인 그물상 구조를 형성한다. 벨트 이동 속도를 조절함으로써, 25 평량(g/m2)의 웹을 수득한다. 웹 형성 후, 당해 분야에서 열결합 캘린더로 알려져 있는 가열된 텍스타일 캘린더를 사용하여 웹을 결합시킴으로써, 그의 최종 강도를 달성한다. 캘린더는 2개의 가열된 강 롤로 이루어지며; 하나의 롤은 편평하고 다른 하나의 롤은 융기된 점의 패턴을 갖는다. 웹을 캘린더로 운송하고, 여기에서 약 138℃의 결합 온도에서 웹을 두 롤 사이에서 가압함으로써 직물을 제조한다.
하기 공정을 이용하여 주조 필름을 제조하였다. 킬리온(Killion) 주조 필름 라인에서 주조 단일층 필름을 제작하였다. 이 라인은 3개의 24:1 L/D 2.54cm 직경 압출기를 갖는데, 이들은 중합체를 공급 블록으로 공급한다. 공급 블록은 용융된 중합체를 압출기로부터 폭 20.32cm의 클레렌(Cloeren) 다이로 보낸다. 용융된 중합체는 230℃에서 다이로부터 나오고, 이를 21℃의 냉각 롤(20.3cm 직경, 25.4cm 롤 표면) 상에서 주조한다. 주조 단위장치는 권취 속도를 조정할 수 있도록 설치되어 표적 두께의 필름을 수득하게 된다.
가소화된 프로필렌 단독중합체, 프로필렌 공중합체 및 프로필렌 충격 공중합체의 수지 특성이 각각 표 5 내지 7에 나열되어 있다. 프로필렌 중합체에 NFP를 첨가하면, 용융 유속의 상당한 증가에 의해 표시되는 것처럼 용융 유동성이 개선된다. 도 11 내지 13에 도시되어 있는 바와 같이, 용융 유동성의 개선은 전단 속도 범위의 함수로서의 전단 점도의 감소를 그 특징으로 할 수 있다. 퍼옥사이드 열화 또는 소위 "비스-브레이킹(vis-breaking)" 과정과는 대조적으로, 본 발명의 용융 유동성의 증가는 주로 NFP의 가소화 효과에 기인하며, 중합체 분자량은 변화되지 않는다. 이는 도 14에 도시되어 있는 바와 같이 분자량 분포의 비교시 명백하다. 용융 유동성의 개선은 통상 제작 공정, 즉 섬유 방사, 필름 주조, 압출, 사출 성형과 관련하여 보다 우수한 드로-다운(draw-down), 보다 낮은 압출기 토크, 얇은 벽 사출 및 보다 빠른 싸이클 시간 면에서 유리하다.
본 발명의 NFP는 프로필렌 중합체의 저장 모듈러스를 상당히 저하시킨다. 도 1에 도시되어 있는 바와 같이, 가소화된 프로필렌 중합체의 저장 모듈러스는 가소화되지 않은 폴리올레핀에 비해 온도의 함수로서 크게 감소된다. 임의의 특정 온도 범위에서 보다 낮은 저장 모듈러스(또는 탄성 모듈러스)를 갖는 프로필렌 중합체는 상기 특정 온도 조건에서 최종-용도에 보다 우수한 가요성을 제공할 수 있는 능력을 나타낸다.
본 발명의 NFP는 도 5 내지 도 10에 도시되어 있는 바와 같이 프로필렌 중합체의 융점 및 결정화 온도를 변화시키지 않으면서 Tg를 저하시키는 능력을 나타낸다. Tg를 저하시키는 전통적인 방법은 프로필렌 공중합체의 경우에서와 같이 공단량체의 혼입을 포함하는데, 이는 중합체의 융점 및 결정화 온도도 저하시킨다. 용융 특징을 희생시키지 않으면서 보다 낮은 Tg를 갖는 중합체가 매우 바람직하며, 이 중합체는 고온 사용능을 유지하면서 특히 동결점 미만 내충격성 면에서 보다 우수한 내충격성을 제공할 수 있다. 본 발명의 가소화된 폴리올레핀은 이를 제공한다.
본 발명의 NFP는, 예컨대 가소화된 프로필렌 단독중합체 및 프로필렌 공중합체의 단일 Tg 프로파일에 의해 결정되는 바와 같이, 프로필렌 중합체와 상용성 및 혼화성이다. 이는 도 2 및 도 3에 그래프로 도시되어 있다. 본 발명의 NFP는 또한, 예컨대 가소화된 프로필렌 충격 공중합체의 두 Tg 프로파일(여기에서, 보다 낮은 Tg 프로파일은 에틸렌-프로필렌 고무 상에 대한 것이고, 보다 높은 Tg 프로파일은 프로필렌 중합체 상에 대한 것임)에 의해 결정되는 바와 같이, 프로필렌 충격 공중합체와도 상용성 및 혼화성이다. 이는 도 4에 그래프로 도시되어 있다.
프로필렌 단독중합체, 프로필렌 공중합체 및 프로필렌 충격 공중합체의 사출 성형 특성이 각각 표 8 내지 10에 요약되어 있다. NFP의 첨가는 열변형 온도를 크게 감소시키지 않으면서 성형 부품의 내충격성을 실질적으로 개선시킨다. 예를 들어, 실온 및 동결점에서 가드너 충격 강도는 NFP 4 내지 5중량% 첨가에 의해 프로필렌 단독중합체의 경우 350% 내지 400%, 프로필렌 공중합체의 경우 140% 내지 165%, 프로필렌 충격 공중합체의 경우 20% 내지 40% 개선되었다. 프로필렌 중합체중 NFP 농도의 증가에 의해 내충격성이 추가로 증가될 수 있을 것으로 생각된다. 실온 및 동결점에서의 아이조드 충격을 비롯한 내충격성의 다른 척도도 또한 상당히 개선된다.
본 발명의 다른 이점은 가소화된 폴리올레핀의 열변형 온도가 희생되지 않는다(유지되거나 아주 미미하게 감소된다)는 것이며, 이는 성형 제품 치수가 고온에서도 유지되어야 하는 용도에 매우 중요하다. 인성 개선의 다른 표시는 생성시 및 파괴시 신장도(elongation)의 상당한 증가에 의해 예시된다. 많은 용도에서는 최종 사용 동안 순응성이 우수할 것을 필요로 한다. 신장도가 높을수록 전환 공정 또는 최종-사용시 변형에 대한 성형 제품의 순응이 용이해진다.
NFP는 또한 표 12에서 보다 낮은 "전체 핸드"에 의해 제공되듯이, 방사 결합 부직포에서의 실질적인 유연성 개선을 제공하는 능력을 보여준다. 많은 용도에서, 특히 개인 위생 및 건강 용도에서, 유연한 부직포는 피부 접촉 안락감에 매우 바람직하다. 본 발명은 유연성을 개선시킬 뿐만 아니라 필요한 인장 강도, 내인열성 및 직물 균일성을 유지시킨다.
필름 특성을 비교한 결과가 표 13에 기재되어 있다. NFP, 특히 Isopar-V 가소화된 프로필렌 단독중합체(샘플 2)는, 기계방향(MD) 및 횡방향(TD)에서의 비교적 높은(가소화되지 않은 폴리올레핀에 비해) 엘멘도르프 인열 및 실온 및 동결점에서의 다트 충격에 의해 보여지듯이, 내인열성 및 내충격성을 개선시킨다. 또한, 광학 특성, 즉 헤이즈 및 광택도 개선된다. 이러한 개선은, 많은 필름 용도, 예를 들어 식품 포장, 문구 커버, 테이프, 의료용 및 전자 제품 포장에 이점을 제공한다.
특정 실시태양을 참조함으로써 본 발명을 기재 및 예시하였으나, 당해 분야의 숙련자는 본 발명을 본원에 예시되지 않은 많은 상이한 형태로 변화시킬 수 있음을 알 것이다. 이러한 이유로, 본 발명의 영역을 결정하기 위해서는 첨부된 청구의 범위만 참조해야 한다. 또한, 본 발명의 특정 특징은 수치 상한 세트와 수치 하한 세트로 기재된다. 달리 표시되지 않는 한, 이러한 상한, 하한의 임의의 조합에 의해 만들어진 범위가 본 발명의 영역 내에 있음을 알아야 한다.
모든 우선권 증명 서류는 이의 혼입이 허용되는 모든 관할권에서 본원에 참고로 인용된다. 또한, 시험 절차를 포함하는 본원에 인용된 모든 서류는 이러한 서류의 혼입이 허용되는 모든 관할권에서 본원에 참고로 인용된다.

Claims (31)

  1. 99.9중량% 내지 60중량%의 폴리올레핀 및 0.1중량% 내지 40중량%의 작용화되지 않은 가소화제를 포함하되, 작용화되지 않은 가소화제가 -5℃ 미만의 유동점을 갖는 C6 내지 C200 파라핀을 포함하는, 가소화된 폴리올레핀 조성물.
  2. 제 1 항에 있어서,
    작용화되지 않은 가소화제가 C8 내지 C100 파라핀을 포함하는 조성물.
  3. 제 1 항에 있어서,
    작용화되지 않은 가소화제가 C6 내지 C50 아이소파라핀을 포함하는 조성물.
  4. 제 1 항에 있어서,
    작용화되지 않은 가소화제가 C10 내지 C100 n-파라핀을 포함하는 조성물.
  5. 제 1 항 내지 제 4 항중 어느 한 항에 있어서,
    Tm은 일정하게 유지되는 반면, 폴리올레핀의 Tg가 조성물에 첨가된 작용화되지 않은 가소화제 매 4중량%에 대해 2℃ 이상 감소되는 조성물.
  6. 제 5 항에 있어서,
    Tm은 일정하게 유지되는 반면, 폴리올레핀의 Tg가 조성물에 첨가된 작용화되지 않은 가소화제 매 4중량%에 대해 4 내지 10℃ 감소되는 조성물.
  7. 제 1 항 내지 제 6 항중 어느 한 항에 있어서,
    작용화되지 않은 가소화제가 -30℃ 미만의 유동점을 갖는 조성물.
  8. 제 1 항 내지 제 7 항중 어느 한 항에 있어서,
    작용화되지 않은 가소화제가 100℃에서 0.1 내지 3000cSt의 점도를 갖는 조성물.
  9. 제 1 항 내지 제 8 항중 어느 한 항에 있어서,
    작용화되지 않은 가소화제가 100℃에서 1 내지 3000cSt의 점도를 갖는 조성물.
  10. 제 1 항 내지 제 9 항중 어느 한 항에 있어서,
    작용화되지 않은 가소화제가 100℃에서 2 내지 300cSt의 점도를 갖는 조성물.
  11. 제 1 항 내지 제 10 항중 어느 한 항에 있어서,
    작용화되지 않은 가소화제가 20℃에서 2.1 미만의 유전 상수를 갖는 조성물.
  12. 제 1 항 내지 제 11 항중 어느 한 항에 있어서,
    작용화되지 않은 가소화제가 0.91g/cm3 미만의 비중을 갖는 조성물.
  13. 제 1 항 내지 제 12 항중 어느 한 항에 있어서,
    방향족 잔기가 작용화되지 않은 가소화제에 실질적으로 존재하지 않는 조성물.
  14. 제 1 항 내지 제 13 항중 어느 한 항에 있어서,
    프탈레이트, 아디페이트, 트라이멜리테이트 에스터 및 폴리에스터로부터 선택되는 가소화제가 실질적으로 존재하지 않는 조성물.
  15. 제 1 항 내지 제 14 항중 어느 한 항에 있어서,
    작용화되지 않은 가소화제의 중량평균 분자량이 100 내지 25,000g/몰인 조성물.
  16. 제 15 항에 있어서,
    작용화되지 않은 가소화제의 중량평균 분자량이 200 내지 25,000g/몰인 조성물.
  17. 제 16 항에 있어서,
    작용화되지 않은 가소화제의 중량평균 분자량이 200 내지 10,000g/몰인 조성물.
  18. 제 1 항 내지 제 17 항중 어느 한 항에 있어서,
    폴리올레핀이 아이소택틱(isotactic) 분절을 포함하는 조성물.
  19. 제 1 항 내지 제 18 항중 어느 한 항에 있어서,
    폴리올레핀이 프로필렌 단독중합체, 프로필렌 공중합체, 프로필렌 랜덤 공중합체, 프로필렌 블록 공중합체, 프로필렌 충격 공중합체 및 이들의 혼합물로부터 선택되는 조성물.
  20. 제 19 항에 있어서,
    프로필렌 단독중합체가 아이소택틱 폴리프로필렌인 조성물.
  21. 제 1 항 내지 제 17 항중 어느 한 항에 있어서,
    폴리올레핀이 에틸렌 유도된 단위 및 C4 내지 C20 α-올레핀 유도된 단위로부터 선택되는 단위 및 프로필렌 유도된 단위를 포함하는 공중합체인 조성물.
  22. 제 1 항 내지 제 17 항중 어느 한 항에 있어서,
    폴리올레핀이 공중합체의 총 중량에 기초하여 40 내지 95중량%의 성분 A 및 5 내지 60중량%의 성분 B를 포함하는 프로필렌 충격 공중합체이고; 이 때 성분 A가 프로필렌 단독중합체, 또는 에틸렌, 뷰텐, 헥센 또는 옥텐 공단량체를 10중량% 이하로 포함하는 프로필렌 공중합체를 포함하며; 성분 B가 에틸렌, 뷰텐, 헥센 및/또는 옥텐 공단량체 5 내지 70중량% 및 프로필렌 95 내지 30중량%를 포함하는 프로필렌 공중합체를 포함하는 조성물.
  23. 제 1 항 내지 제 22 항중 어느 한 항에 있어서,
    플라스토머를 추가로 포함하는 조성물.
  24. 제 1 항 내지 제 23 항중 어느 한 항에 있어서,
    500 내지 10,000의 중량평균 분자량을 갖는 폴리에틸렌이 실질적으로 존재하지 않는 조성물.
  25. 제 1 항 내지 제 24 항중 어느 한 항에서 정의된 바와 같은, 폴리올레핀과 작용화되지 않은 가소화제를 블렌딩시킴을 포함하는, 폴리올레핀을 가소화시키는 방법.
  26. 제 25 항에 있어서,
    블렌딩이 용융 블렌딩을 포함하는 방법.
  27. 제 26 항에 있어서,
    용융 블렌딩을 압출기에서 수행하는 방법.
  28. 제 25 항에 있어서,
    블렌딩이 고체 폴리올레핀의 습식 블렌딩을 포함하는 방법.
  29. 제 25 항 내지 제 28 항중 어느 한 항에 있어서,
    폴리올레핀이 반응기 과립 또는 압출된 펠렛의 형태인 방법.
  30. 제 29 항에 있어서,
    반응기 과립이 10㎛ 내지 5mm의 평균 직경을 갖는 방법.
  31. 제 1 항 내지 제 24 항중 어느 한 항의 조성물을 포함하거나 또는 제 25 항 내지 제 30 항중 어느 한 항의 방법에 의해 제조된, 필름, 시이트, 섬유, 직물, 부직포, 관, 파이프, 자동차 부품, 가구, 운동용품, 식품 저장 용기, 투명 및 반투명 제품, 장난감, 관재 및 파이프, 및 의료 기기로부터 선택되는 제품.
KR1020057002168A 2002-08-12 2003-08-04 가소화된 폴리올레핀 조성물 KR101008786B1 (ko)