JP2017535498A - 圧縮深さが非常に深い強化ガラス - Google Patents
圧縮深さが非常に深い強化ガラス Download PDFInfo
- Publication number
- JP2017535498A JP2017535498A JP2017502202A JP2017502202A JP2017535498A JP 2017535498 A JP2017535498 A JP 2017535498A JP 2017502202 A JP2017502202 A JP 2017502202A JP 2017502202 A JP2017502202 A JP 2017502202A JP 2017535498 A JP2017535498 A JP 2017535498A
- Authority
- JP
- Japan
- Prior art keywords
- mol
- glass
- mpa
- glass article
- depth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
ガラス物品において、該ガラス物品の表面で約100MPaから約400MPaの範囲にある圧縮応力CSsを有する圧縮領域を有し、該圧縮領域が、前記表面から圧縮深さDOCまで延在し、圧縮応力プロファイルを有し、ここで、0.1・t≦DOC≦0.25・tであり、該圧縮応力プロファイルは、前記表面から深さdaまで延在し、勾配maを有する部分aを有し、該深さdaは前記圧縮深さDOCと等しく、−0.4MPa/μm≧ma≧−3.0MPa/μmである、ガラス物品。
前記圧縮深さDOCが約95μmから約250μmの範囲にある、実施形態1に記載のガラス物品。
前記圧縮深さDOCが約100μmから約190μmの範囲にある、実施形態2に記載のガラス物品。
0.12・t≦DOC≦0.22・tである、実施形態1に記載のガラス物品。
前記ガラス物品が約0.15mmから約2.0mmの範囲の厚さtを有する、実施形態1に記載のガラス物品。
前記勾配maが約−0.7MPa/μmから−2.7MPa/μmの範囲にある、実施形態1に記載のガラス物品。
前記勾配maが約−1.5MPa/μmから−2.7MPa/μmの範囲にある、実施形態1に記載のガラス物品。
前記ガラス物品がアルカリアルミノケイ酸塩ガラスから作られている、実施形態1に記載のガラス物品。
前記アルカリアルミノケイ酸塩ガラスが約10モル%までのLi2Oを含む、実施形態8に記載のガラス物品。
前記アルカリアルミノケイ酸塩ガラスが少なくとも約4モル%のP2O5および0モル%から約4モル%のB2O3を含み、1.3<[(P2O5+R2O)/M2O3]≦2.3、M2O3=Al2O3+B2O3、R2Oは、前記アルカリアルミノケイ酸塩ガラス中に存在する一価の陽イオン酸化物の合計である、実施形態8に記載のガラス物品。
前記ガラスがリチウムを含まない、実施形態8に記載のガラス物品。
少なくとも約4モル%のP2O5および0モル%から約4モル%のB2O3を含むアルカリアルミノケイ酸塩ガラスであって、1.3<[(P2O5+R2O)/M2O3]≦2.3、M2O3=Al2O3+B2O3、R2Oは、前記アルカリアルミノケイ酸塩ガラス中に存在する一価の陽イオン酸化物の合計であり、
a.前記アルカリアルミノケイ酸塩ガラスが、イオン交換されており、厚さtおよび圧縮領域を有し、該圧縮領域が、前記アルカリアルミノケイ酸塩ガラスの表面で約100MPaから約400MPaの範囲にある圧縮応力CSsを有し、
b.前記圧縮領域が前記表面から圧縮深さDOCまで延在し、0.1・t≦DOC≦0.25・tであり、
c.前記圧縮領域が圧縮応力プロファイルを有し、該圧縮応力プロファイルは、前記表面から深さdaまで延在し、勾配maを有する部分aを有し、該深さdaは前記圧縮深さDOCと等しく、−0.4MPa/μm≧ma≧−3.0MPa/μmである、
アルカリアルミノケイ酸塩ガラス。
前記ガラスがリチウムを含まない、実施形態12に記載のアルカリアルミノケイ酸塩ガラス。
前記ガラスが、約40モル%から約70モル%のSiO2、約11モル%から約25モル%のAl2O3、約4モル%から約15モル%のP2O5、約13モル%から約25モル%のNa2O、約13モル%から約30モル%のRxO、約11モル%から約30モル%のM2O3、0モル%から約1モル%のK2O、0モル%から約4モル%のB2O3、および3モル%以下の、TiO2、MnO、Nb2O5、MoO3、Ta2O5、WO3、ZrO2、Y2O3、La2O3、HfO2、CdO、SnO2、Fe2O3、CeO2、As2O3、Sb2O3、Cl、およびBrの内の1種類以上から実質的になり、1.3<[(P2O5+R2O)/M2O3]≦2.3、式中、RxOは、該ガラス中に存在するアルカリ金属酸化物、アルカリ土類金属酸化物、および遷移金属一酸化物の合計であり、M2O3=Al2O3+B2O3、R2Oは、該ガラス中に存在する一価の陽イオン酸化物の合計である、実施形態12に記載のアルカリアルミノケイ酸塩ガラス。
前記圧縮深さDOCが約95μmから約250μmの範囲にある、実施形態12に記載のアルカリアルミノケイ酸塩ガラス。
前記圧縮深さDOCが約100μmから約190μmの範囲にある、実施形態15に記載のアルカリアルミノケイ酸塩ガラス。
0.12・t≦DOC≦0.22・tである、実施形態12に記載のアルカリアルミノケイ酸塩ガラス。
前記厚さが約0.1mmから約2.0mmの範囲にある、実施形態12に記載のアルカリアルミノケイ酸塩ガラス。
前記勾配maが約−0.7MPa/μmから−2.7MPa/μmの範囲にある、実施形態12に記載のアルカリアルミノケイ酸塩ガラス。
前記勾配maが約−1.5MPa/μmから−2.7MPa/μmの範囲にある、実施形態12に記載のアルカリアルミノケイ酸塩ガラス。
ガラス物品において、厚さt、および該ガラス物品の表面で約400MPaから約1200MPaの範囲にある圧縮応力CSsを有する圧縮領域を有し、該圧縮領域が、前記表面から圧縮深さDOCまで延在し、圧縮応力プロファイルを有し、ここで、0.1・t≦DOC≦0.25・tであり、該圧縮応力プロファイルは、
a.前記表面から該表面の下の深さdbまで延在し、勾配mbを有する第1の部分b、ここで、−40MPa/μm≧mb≧−200MPa/μm;および
b.ほぼ前記深さdcから前記圧縮深さDOCまで延在し、勾配mcを有する第2の実質的に線形の部分c、ここで、−0.4MPa/μm≧mc≧−3.0MPa/μm;
を有する、ガラス物品。
前記圧縮深さDOCが約95μmから約250μmの範囲にある、実施形態21に記載のガラス物品。
前記圧縮深さDOCが約100μmから約190μmの範囲にある、実施形態22に記載のガラス物品。
0.12・t≦DOC≦0.22・tである、実施形態21に記載のガラス物品。
前記厚さtが約0.15mmから約2.0mmの範囲にある、実施形態21に記載のガラス物品。
前記勾配mcが約−0.7MPa/μmから−2.7MPa/μmの範囲にある、実施形態21に記載のガラス物品。
前記勾配mcが約−1.5MPa/μmから−2.7MPa/μmの範囲にある、実施形態26に記載のガラス物品。
前記ガラス物品がアルカリアルミノケイ酸塩ガラスから作られている、実施形態21に記載のガラス物品。
前記アルカリアルミノケイ酸塩ガラスが約10モル%までのLi2Oを含む、実施形態28に記載のガラス物品。
前記アルカリアルミノケイ酸塩ガラスが少なくとも約4モル%のP2O5および0モル%から約4モル%のB2O3を含み、1.3<[(P2O5+R2O)/M2O3]≦2.3、M2O3=Al2O3+B2O3、R2Oは、前記アルカリアルミノケイ酸塩ガラス中に存在する一価の陽イオン酸化物の合計である、実施形態28に記載のガラス物品。
前記ガラスがリチウムを含まない、実施形態28に記載のガラス物品。
前記ガラスが、約40モル%から約70モル%のSiO2、約11モル%から約25モル%のAl2O3、約4モル%から約15モル%のP2O5、約13モル%から約25モル%のNa2O、約13モル%から約30モル%のRxO、約11モル%から約30モル%のM2O3、0モル%から約1モル%のK2O、0モル%から約4モル%のB2O3、および3モル%以下の、TiO2、MnO、Nb2O5、MoO3、Ta2O5、WO3、ZrO2、Y2O3、La2O3、HfO2、CdO、SnO2、Fe2O3、CeO2、As2O3、Sb2O3、Cl、およびBrの内の1種類以上から実質的になり、1.3<[(P2O5+R2O)/M2O3]≦2.3、式中、RxOは、該ガラス中に存在するアルカリ金属酸化物、アルカリ土類金属酸化物、および遷移金属一酸化物の合計であり、M2O3=Al2O3+B2O3、R2Oは、該ガラス中に存在する一価の陽イオン酸化物の合計である、実施形態28に記載のガラス物品。
110 第1の表面
112 第2の表面
120 第1の圧縮領域
130 中央領域
200 装置
212 基体
214 研磨紙、研磨材を有するシート
215 サンプル保持器
216 空隙
218、220 ガラスサンプル
230 鋼球
250 球落下試験アセンブリ
400 研磨時リング・オン・リング構成
410 ガラス試料
420 支持リング
430 荷重リング
Claims (16)
- ガラス物品において、アルカリアルミノケイ酸塩ガラスから作られており、厚さt、および該ガラス物品の表面で約100MPaから約400MPaの範囲にある圧縮応力CSsを有する圧縮領域を有し、該圧縮領域が、前記表面から圧縮深さDOCまで延在し、圧縮応力プロファイルを有し、ここで、0.1・t≦DOC≦0.25・tであり、該圧縮応力プロファイルは、前記表面から深さdaまで延在し、勾配maを有する実質的に線形の部分aを有し、該深さdaは前記圧縮深さDOCと等しく、−0.4MPa/μm≧ma≧−3.0MPa/μmである、ガラス物品。
- 少なくとも約4モル%のP2O5および0モル%から約4モル%のB2O3を含むアルカリアルミノケイ酸塩ガラスであって、1.3<[(P2O5+R2O)/M2O3]≦2.3、M2O3=Al2O3+B2O3、R2Oは、前記アルカリアルミノケイ酸塩ガラス中に存在する一価の陽イオン酸化物の合計であり、
a.前記アルカリアルミノケイ酸塩ガラスが、イオン交換されており、厚さtおよび圧縮領域を有し、該圧縮領域が、前記アルカリアルミノケイ酸塩ガラスの表面で約100MPaから約400MPaの範囲にある圧縮応力CSsを有し、
b.前記圧縮領域が前記表面から圧縮深さDOCまで延在し、0.1・t≦DOC≦0.25・tであり、
c.前記圧縮領域が圧縮応力プロファイルを有し、該圧縮応力プロファイルは、前記表面から深さdaまで延在し、勾配maを有する実質的に線形の部分aを有し、該深さdaは前記圧縮深さDOCと等しく、−0.4MPa/μm≧ma≧−3.0MPa/μmである、
アルカリアルミノケイ酸塩ガラス。 - ガラス物品において、アルカリアルミノケイ酸塩から作られており、厚さt、および該ガラス物品の表面で約400MPaから約1200MPaの範囲にある圧縮応力CSsを有する圧縮領域を有し、該圧縮領域が、前記表面から圧縮深さDOCまで延在し、圧縮応力プロファイルを有し、ここで、0.1・t≦DOC≦0.25・tであり、該圧縮応力プロファイルは、
a.前記表面から該表面の下の深さdbまで延在し、勾配mbを有する第1の実質的に線形の部分b、ここで、−40MPa/μm≧mb≧−200MPa/μm;
b.深さdcから前記圧縮深さDOCまで延在し、勾配mcを有する第2の実質的に線形の部分c、ここで、−0.4MPa/μm≧mc≧−3.0MPa/μm;および
c.前記勾配mbから前記勾配mcまで移行する勾配を有する、前記深さdbと前記深さdcとの間に延在する移行領域;
を有する、ガラス物品。 - 前記圧縮深さDOCが約95μmから約250μmの範囲にある、請求項1から3いずれか1項記載のガラス物品。
- 前記圧縮深さDOCが約100μmから約190μmの範囲にある、請求項4記載のガラス物品。
- 0.12・t≦DOC≦0.22・tである、請求項1から3いずれか1項記載のガラス物品。
- 前記厚さtが約0.15mmから約2.0mmの範囲にある、請求項1から3いずれか1項記載のガラス物品。
- 前記勾配maが約−0.7MPa/μmから−2.7MPa/μmの範囲にある、請求項1または2記載のガラス物品。
- 前記勾配maが約−1.5MPa/μmから−2.7MPa/μmの範囲にある、請求項8記載のガラス物品。
- 前記勾配mcが約−0.7MPa/μmから−2.7MPa/μmの範囲にある、請求項3記載のガラス物品。
- 前記勾配mcが約−1.5MPa/μmから−2.7MPa/μmの範囲にある、請求項10記載のガラス物品。
- 前記アルカリアルミノケイ酸塩ガラスが約10モル%までのLi2Oを含む、請求項1から3いずれか1項記載のガラス物品。
- 前記アルカリアルミノケイ酸塩ガラスが少なくとも約4モル%のP2O5および0モル%から約4モル%のB2O3を含み、1.3<[(P2O5+R2O)/M2O3]≦2.3、M2O3=Al2O3+B2O3、R2Oは、前記アルカリアルミノケイ酸塩ガラス中に存在する一価の陽イオン酸化物の合計である、請求項1または3記載のガラス物品。
- 前記ガラスがリチウムを含まない、請求項1から3いずれか1項記載のガラス物品。
- 前記ガラスが、約40モル%から約70モル%のSiO2、約11モル%から約25モル%のAl2O3、約4モル%から約15モル%のP2O5、約13モル%から約25モル%のNa2O、約13モル%から約30モル%のRxO、約11モル%から約30モル%のM2O3、0モル%から約1モル%のK2O、0モル%から約4モル%のB2O3、および3モル%以下の、TiO2、MnO、Nb2O5、MoO3、Ta2O5、WO3、ZrO2、Y2O3、La2O3、HfO2、CdO、SnO2、Fe2O3、CeO2、As2O3、Sb2O3、Cl、およびBrの内の1種類以上から実質的になり、1.3<[(P2O5+R2O)/M2O3]≦2.3、式中、RxOは、該ガラス中に存在するアルカリ金属酸化物、アルカリ土類金属酸化物、および遷移金属一酸化物の合計であり、M2O3=Al2O3+B2O3、R2Oは、該ガラス中に存在する一価の陽イオン酸化物の合計である、請求項2または3記載のガラス物品。
- 請求項1から15いずれか1項記載のガラス物品を備えた電子機器。