WO2012057321A1 - 透明導電積層体およびその製造方法 - Google Patents
透明導電積層体およびその製造方法 Download PDFInfo
- Publication number
- WO2012057321A1 WO2012057321A1 PCT/JP2011/074944 JP2011074944W WO2012057321A1 WO 2012057321 A1 WO2012057321 A1 WO 2012057321A1 JP 2011074944 W JP2011074944 W JP 2011074944W WO 2012057321 A1 WO2012057321 A1 WO 2012057321A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- carbon nanotube
- resistance value
- transparent conductive
- layer
- surface resistance
- Prior art date
Abstract
Description
透明基材上に、カーボンナノチューブを含む導電層を有する透明導電積層体であって、次の[A]~[C]の少なくとも1つを満たし、かつ、60℃、相対湿度90%で1hr湿熱処理を行い、次いで25℃、相対湿度50%で3min間放置した後における表面抵抗値の、該処理前の表面抵抗値に対する割合が、0.7~1.3である透明導電積層体、である。
[A]白反射率75%における表面抵抗値が1.1×103Ω/□以下
[B]カーボンナノチューブ層光吸収率5%における表面抵抗値が1.1×103Ω/□以下
[C]全光線透過率90%における表面抵抗値が1.1×103Ω/□以下
また、本発明の透明導電積層体の製造方法は次の構成を有する。すなわち、
透明基材上に、水接触角が5~25°であるアンダーコート層を設けるアンダーコート層形成工程と、分散剤を含むカーボンナノチューブ分散液をアンダーコート層上に塗布する塗布工程と、アンダーコート層上に塗布された前記カーボンナノチューブ分散液から分散媒を除去する乾燥工程とを有する透明導電積層体の製造方法、である。
前記透明導電積層体を用いた電子ペーパー、である。
前記透明導電積層体を用いたタッチパネル、である。
本発明の透明導電積層体の製造方法は、前記カーボンナノチューブ分散液のpHが5.5~11の範囲にあることが好ましい。
[透明基材]
本発明に用いられる透明基材の素材としては、樹脂、ガラスなどを挙げることができる。樹脂としては、ポリエチレンテレフタレート(PET)、ポリエチレンナフタレート(PEN)などのポリエステル、ポリカーボネート(PC)、ポリメチルメタクリレート(PMMA)、ポリイミド、ポリフェニレンスルフィド、アラミド、ポリプロピレン、ポリエチレン、ポリ乳酸、ポリ塩化ビニル、ポリメタクリル酸メチル、脂環式アクリル樹脂、シクロオレフィン樹脂、トリアセチルセルロースなどを用いることができる。ガラスとしては、通常のソーダガラスを用いることができる。また、これらの複数の透明基材を組み合わせて用いることもできる。例えば、樹脂とガラスを組み合わせた透明基材、2種以上の樹脂を積層した透明基材などの複合透明基材であってもよい。樹脂フィルムにハードコートを設けたようなものであっても良い。透明基材の種類は前記に限定されることはなく、用途に応じて耐久性やコスト等から最適なものを選ぶことができる。透明基材の厚みは特に限定されるものではないが、タッチパネル、液晶ディスプレイ、有機エレクトロルミネッセンス、電子ペーパーなどのディスプレイ関連の電極に用いる場合、10μm~1,000μmの間にあることが好ましい。
[アンダーコート層]
本発明においては前記透明基材上にアンダーコート層を設ける。アンダーコート層の素材としては、親水性の高い素材であることが好ましい。具体的には、水接触角が5~25°の範囲にある素材が好ましい。具体的には無機酸化物を用いることが好ましい。より好ましくは、チタニア、アルミナ、シリカである。これらの物質は、表面に親水基-OH基を有しており、高い親水性が得られるため好ましい。さらに、アンダーコート層が、シリカ微粒子とポリシリケートの複合物を主たる成分とするのがより好ましい。
[アンダーコート層の形成方法]
本発明において、アンダーコート層を透明基材上に設ける方法は特に限定されない。既知の湿式コーティング方法、例えば吹き付け塗装、浸漬コーティング、スピンコーティング、ナイフコーティング、キスコーティング、グラビアコーティング、スロットダイコーティング、ロールコーティング、バーコーティング、スクリーン印刷、インクジェット印刷、パット印刷、他の種類の印刷などが利用できる。また、乾式コーティング方法を用いてもよい。乾式コーティング方法としては、スパッタリング、蒸着などの物理気相成長や化学気相成長などが利用できる。また塗布は、複数回に分けて行ってもよく、異なる2種類の塗布方法を組み合わせても良い。好ましい塗布方法は、湿式コーティングであるグラビアコーティング、バーコーティングである。
[アンダーコート層厚みの調整]
アンダーコート層厚みはカーボンナノチューブ分散液塗布時に分散剤が移行できる厚みであれば、限定されない。光学干渉による反射防止効果が有効に得られる厚みであれば、光線透過率が向上するため好ましい。このため、後述するオーバーコート層の厚みと合わせて80~120nmの範囲にあることが好ましい。
[アンダーコート層の水接触角]
水接触角は市販の接触角測定装置を用いて測定することができる。水接触角の測定は、JIS R 3257 (1999)に従い、室温25℃、相対湿度50%の雰囲気下で、アンダーコート層表面に1~4μLの水をシリンジで滴下し、液滴を水平断面から観察し、液滴端部の接線と膜平面とのなす角を求める。
[カーボンナノチューブ]
本発明において用いられるカーボンナノチューブは、実質的にグラファイトの1枚面を巻いて筒状にした形状を有するものであれば特に限定されず、グラファイトの1枚面を1層に巻いた単層カーボンナノチューブ、多層に巻いた多層カーボンナノチューブいずれも適用できるが、中でもグラファイトの1枚面を2層に巻いた特に2層カーボンナノチューブが100本中に50本以上含まれているカーボンナノチューブであると、導電性ならびに塗布用分散液中でのカーボンナノチューブの分散性が極めて高くなることから好ましい。さらに好ましくは100本中75本以上が二層カーボンナノチューブ、最も好ましくは100本中80本以上が二層カーボンナノチューブである。なお、2層カーボンナノチューブが100本中に50本含まれていることを、2層カーボンナノチューブの割合が50%と表示することもある。また、二層カーボンナノチューブは酸処理などによって表面が官能基化されても導電性などの本来の機能が損なわれない点からも好ましい。
[分散剤]
カーボンナノチューブの分散剤としては、界面活性剤、各種高分子材料(水溶性高分子材料等)等を用いることができるが、分散性が高いイオン性高分子材料が好ましい。イオン性高分子材料としてはアニオン性高分子材料やカチオン性高分子材料、両性高分子材料がある。カーボンナノチューブ分散能が高く、分散性を保持できるもので有ればどの種類も用いることができるが、分散性、および分散保持性に優れることから、アニオン性高分子材料が好ましい。なかでも、カルボキシメチルセルロースおよびその塩(ナトリウム塩、アンモニウム塩等)、ポリスチレンスルホン酸の塩がカーボンナノチューブ分散液においてカーボンナノチューブを効率的に分散することができ好ましい。
[分散媒]
本発明において用いられる分散媒は、前記分散剤を安全に溶解できる点、廃液の処理が容易である等の観点から、水が好ましい。
[カーボンナノチューブ分散液]
本発明において用いるカーボンナノチューブ分散液の調製方法は、特に限定されないが、例えば次のような手順で行うことができる。分散時の処理時間が短縮できることから、一旦、分散媒中にカーボンナノチューブを0.003~0.15質量%の濃度範囲で含まれる分散液を調製した後、希釈することで、所定の濃度とすることが好ましい。本発明において、カーボンナノチューブに対する分散剤の質量比は10以下であることが好ましい。かかる好ましい範囲であると、均一に分散させることが容易である一方、導電性低下の影響がない。質量比は0.5~9であることがより好ましく、1~6であることがさらに好ましく、質量比が2~3であれば、高い透明導電性を得ることができるので特に好ましい。調製時の分散手段としては、カーボンナノチューブと分散剤を分散媒中で塗装製造に慣用の混合分散機(例えばボールミル、ビーズミル、サンドミル、ロールミル、ホモジナイザー、超音波ホモジナイザー、高圧ホモジナイザー、超音波装置、アトライター、デゾルバー、ペイントシェーカー等)を用いて混合することが挙げられる。また、これら複数の混合分散機を組み合わせて段階的に分散を行ってもよい。中でも、振動ボールミルで予備的に分散を行った後、超音波装置を用いて分散する方法が、得られる塗布用分散液中のカーボンナノチューブの分散性が良好であることから好ましい。
[カーボンナノチューブ分散液の特性]
本発明に用いる分散液は、pHが5.5~11の範囲にあることが好ましい。
[カーボンナノチューブ分散液のpH調整]
カーボンナノチューブ分散液のpH調整は、pHを測定しながら、上記酸性物質および/または塩基性物質を所望のpHとなるまで添加することで行う。pH測定法としては、リトマス試験紙などのpH試験紙を用いる方法、水素電極法、キンヒドロン電極法、アンチモン電極法、ガラス電極法などが挙げられるが、この中でもガラス電極法が簡便であり、必要な精度を得られるため好ましい。また、酸性物質、あるいは、塩基性物質を過剰に添加して所望のpH値を越えてしまった場合には、逆の特性を持つ物質を添加してpHを調整すれば良い。かかる調整に適用する酸性物質としては硝酸が、塩基性物質としてはアンモニアが好ましい。
[カーボンナノチューブ層の形成]
本発明の透明導電積層体を製造する方法において、カーボンナノチューブ層は、カーボンナノチューブ分散液を透明基材に塗布する塗布工程と、その後分散媒を除去する乾燥工程を経て形成される。塗布工程では、前記方法により得た分散液を、前記アンダーコート層を設けた透明基材上に塗布するとき親水性の部位を持つ分散剤が、親水基を有するアンダーコート層の表面に引き寄せられ、吸着されると考えられる。また、その後分散媒を乾燥させてカーボンナノチューブをアンダーコート層上に固定してカーボンナノチューブ層を形成するが、分散媒がアンダコート層の上に残存しており、分散剤がカーボンナノチューブからアンダーコート層の表面へ移動可能な状態である間は、塗布時と同様、分散剤が親水基を有するアンダーコート層の表面に引き寄せられ、吸着されると考えられる。これらのように、親水基を有するアンダコート層に分散剤が吸着されることで、カーボンナノチューブ層の分散剤量が低下しているものと考えられる。かかるアンダコート層への分散剤の吸着は、水の接触角5°~25°の親水性のアンダーコート層を用いることにより、達成される。また、カーボンナノチューブ分散液を塗布厚み1μm~50μmの範囲で塗布し、分散媒がカーボンナノチューブ層中から乾燥によって除去される時間が0.1sec~100secの範囲であれば、かかるメカニズムによる分散剤の吸着をより効果的に生じさせることができるため好ましい。
(E:光電子のエネルギー値、hν:照射X線のエネルギー値、EB:電子の結合エネルギー)
一定のエネルギー値を持つX線を照射し、光電子のエネルギー値を測定することで、EBを求めることができる。EBは、各元素に固有の軌道エネルギーとなることから、この値から元素の種類を同定することができる。また、同じ元素であっても、その結合状態によってエネルギー値のピークがシフトする。このシフトを測定することにより、結合状態も知ることができる。
[カーボンナノチューブ層の厚みの調整]
カーボンナノチューブ分散液を透明基材上に塗布する際の塗布厚み(ウェット状態の厚み)は、カーボンナノチューブ分散液の濃度にも依存するため、望む表面抵抗値が得られるように適宜調整すればよい。本発明におけるカーボンナノチューブ塗布量は、導電性を必要とする種々の用途を達成するために、容易に調整可能である。例えば、塗布量が1mg/m2~40mg/m2であれば表面抵抗値は1×100~1×104Ω/□とすることができ、好ましい。
[オーバーコート層]
本発明においてはカーボンナノチューブ層形成後、この層の上面に透明被膜からなるオーバーコート層を形成しうる。オーバーコート層を形成することにより、さらに透明導電性や耐熱性安定性、耐湿熱安定性が向上できるため好ましい。
[オーバーコート層の形成方法]
本発明において、オーバーコート層をカーボンナノチューブ層上に設ける方法は特に限定されない。既知の湿式コーティング方法、例えば吹き付け塗装、浸漬コーティング、スピンコーティング、ナイフコーティング、キスコーティング、ロールコーティング、グラビアコーティング、スロットダイコーティング、バーコーティング、スクリーン印刷、インクジェット印刷、パット印刷、他の種類の印刷、または他の種類の印刷などが利用できる。また、乾式コーティング方法を用いてもよい。乾式コーティング方法としては、スパッタリング、蒸着などの物理気相成長や化学気相成長などが利用できる。またオーバーコート層をカーボンナノチューブ層上に設ける操作は、複数回に分けて行ってもよく、異なる2種類の方法を組み合わせても良い。好ましい方法は、湿式コーティングであるグラビアコーティング、バーコーティングである。
[透明導電性]
上述のようにして透明導電性に優れる透明導電積層体を得ることができる。透明導電性とは透明性と導電性を兼ね備えていることを示す。
導電性の指標としては表面抵抗値が用いられ、表面抵抗値が低い方が導電性は高い。表面抵抗値は、1×100~1×104Ω/□の範囲にあることが好ましい。より好ましくは表面抵抗値が1×100~1×103Ω/□の範囲である。
本発明において、透明性の指標としてカーボンナノチューブ層光吸収率を採った場合には、カーボンナノチューブ層光吸収率5%における表面抵抗値を指標とする。本願により得られる透明導電積層体は、カーボンナノチューブ層光吸収率5%における表面抵抗値が1.1×103Ω/□以下である。
[耐湿熱安定性]
本発明の透明導電積層体の製造方法によれば、上記の透明導電性を満たしてかつ耐湿熱安定性に優れる透明導電積層体が得られる。本発明における耐湿熱安定性の指標としては、60℃、相対湿度90%で、1hr湿熱処理を行い、次いで25℃、相対湿度50%で3min間放置した後の表面抵抗値の、該処理前の表面抵抗値に対する割合を用いる。本発明の透明導電積層体は、かかる耐湿熱安定性を0.7~1.3とするものであり、好ましくは0.8~1.2である。
[耐熱安定性]
本発明の透明導電積層体の好ましい製造方法によれば、さらに耐熱安定性に優れる透明導電積層体が得られる。本発明における耐熱安定性の指標としては、150℃、1hr熱処理を行い、次いで25℃、相対湿度50%で24hr放置した後の表面抵抗値の、該処理前の表面抵抗値に対する割合を用いる。なお、150℃熱処理では相対湿度を制御していないが、150℃での飽和水蒸気圧は4.8atm、常温である25℃の飽和水蒸気圧は0.03atmであるため、常温で相対湿度にばらつきがあったとしても、150℃まで温度を上昇させた場合、相対湿度はほぼ0と見なすことができる。本発明の透明導電積層体は、かかる耐熱安定性を0.7~1.3とするのが好ましく、より好ましくは0.8~1.2である。
[長期耐熱安定性]
本発明の透明導電積層体のより好ましい製造方法によればさらに長期耐熱安定性に優れる透明導電積層体が得られる。本発明における長期耐熱安定性の指標としては、80℃で500hr熱処理を行い、次いで25℃、相対湿度50%で3min間放置した後の表面抵抗値の、該処理前の表面抵抗値に対する割合を用いる。なお、80℃熱処理では相対湿度を制御していないが、80℃での飽和水蒸気圧は0.47atm、常温である25℃の飽和水蒸気圧は0.03atmであるため、常温で相対湿度にばらつきがあったとしても、80℃まで温度を上昇させた場合、相対湿度はほぼ0と見なすことができる。本発明の透明導電積層体は、かかる長期耐熱安定性を0.7~1.3とするのが好ましく、より好ましくは0.8~1.2である。
(1)表面抵抗値
5cm×10cmにサンプリングした透明導電積層体のカーボンナノチューブ層側の中央部にプローブを密着させて、4端子法により室温下で抵抗値を測定した。使用した装置は、ダイアインスツルメンツ(株)製の抵抗率計MCP-T360型、使用したプローブはダイアインスツルメンツ(株)製の4探針プローブMCP-TPO3Pである。
(2)白反射率
白反射板として東レ(株)製“ルミラー”ES6R、粘着層として日東電工(株)製“LUCIACS” CS9621Tを用い、図2のように透明導電積層体の導電面が粘着層と接するように積層させた。この積層体の透明導電積層体側から、コニカミノルタセンシング(株)製“CM-2500d"を用いて、波長550nmにおける反射率を測定し、白反射率とした。
(3)カーボンナノチューブ層光吸収率
(3-1)導電面反射率、導電面逆面反射率
測定面の反対側表面を60°光沢度(JIS Z 8741 (1997年))が10以下になるように320~400番の耐水サンドペーパーで均一に粗面化した後、可視光線透過率が5%以下となるように黒色塗料を塗布して着色した。測定面を(株)島津製作所製の分光光度計“UV-3150”にて、測定面から5°の入射角で、550nmでの導電面反射率、導電面逆面反射率測定を行った。
(株)島津製作所製の分光光度計“UV-3150”にて、導電面から光を入射させて550nmにおける光透過率測定を行った。
(3-1)、(3-2)で測定した導電面反射率、導電面逆面反射率光透過率、光透過率から下記式を用いて導出した。
(4)全光線透過率
JIS K 7361(1997年)に基づき、日本電色工業(株)製の濁度計NDH2000を用いて測定した。
(5)水接触角
室温25℃、相対湿度50%の雰囲気下で、膜表面に1~4μLの水をシリンジで滴下した。接触角計(協和界面科学(株)製、接触角計CA-X型)を用いて、液滴を水平断面から観察し、液滴端部の接線と膜平面とのなす角を求めた。
(6)耐熱安定性
5cm×10cmにサンプリングした透明導電積層体に以下に記す熱処理を施し、熱処理後のサンプルの表面抵抗値を熱処理前のサンプルの表面抵抗値で除した値を耐熱安定性の指標とした。
(ii)室温25℃、相対湿度50%の雰囲気下で24hr放置
(7)耐湿熱安定性
5cm×10cmにサンプリングした透明導電積層体に以下に記す湿熱処理を施し、湿熱処理後のサンプルの表面抵抗値を熱処理前のサンプルの表面抵抗値で除した値を耐熱安定性の指標とした。
(iv)室温25℃、相対湿度50%の雰囲気下で3min間放置
(8)長期耐熱安定性
5cm×10cmにサンプリングした透明導電積層体に以下に記す長期耐熱処理を施し、長期耐熱処理後のサンプルの表面抵抗値を熱処理前のサンプルの表面抵抗値で除した値を耐熱安定性の指標とした。
(vi)室温25℃、相対湿度50%の雰囲気下で3min間放置
(9)カーボンナノチューブ層全光線透過率96%での表面抵抗値
カーボンナノチューブ塗布前後の透明導電積層体の全光線透過率の比(カーボンナノチューブ層全光線透過率)の値が96%以上のサンプルと、96%以下のサンプルを、後述する[カーボンナノチューブ層の形成]の項に示した方法で少なくともそれぞれ1水準以上作製し、各々の表面抵抗値、カーボンナノチューブ層全光線透過率を測定、カーボンナノチューブ層全光線透過率96%での表面抵抗値を内挿して算出した。
(10)白反射率75%での表面抵抗値
オーバーコート層の形成後の白反射率75%以上のサンプルと、75%以下のサンプルを、後述する[カーボンナノチューブ層の形成]の項に示した方法で少なくともそれぞれ1水準以上作製し、各々の表面抵抗値、白反射率を測定、白反射率75%での表面抵抗値を内挿して算出した。
(11)カーボンナノチューブ層光吸収率5%での表面抵抗値
オーバーコート層の形成後のカーボンナノチューブ層光吸収率5%以上のサンプルと、5%以下のサンプルを、後述する[カーボンナノチューブ層の形成]の項に示した方法で少なくともそれぞれ1水準以上作製し、各々の表面抵抗値、カーボンナノチューブ層光吸収率を測定、カーボンナノチューブ層光吸収率5%での表面抵抗値を内挿して算出した。
(12)オーバーコート層の形成後の全光線透過率90%での表面抵抗値
オーバーコート層の形成後の全光線透過率が90%以上のサンプルと、90%以下のサンプルを、後述する[カーボンナノチューブ層の形成]の項に示した方法で少なくともそれぞれ1水準以上作製し、各々の表面抵抗値、カーボンナノチューブ層全光線透過率を測定、全光線透過率90%での表面抵抗値を内挿して算出した。
(13)アンダーコート層の厚み
基材であるPETフィルムの上にアンダーコート層のみを設けた状態で、アンダーコート層の設置面の反対側表面を60°光沢度(JIS Z 8741(1997年))が10以下になるように320~400番の耐水サンドペーパーで均一に粗面化した後、可視光線透過率が5%以下となるように黒色塗料を塗布して着色した。測定面を島津製作所製の分光光度計(UV-3150)にて、測定面から5°の入射角で、波長領域200nm~1,200nmにおける絶対反射スペクトルを1nm間隔で測定し、200nm~1,200nmの領域での反射率の極小値を示す波長を求めた。
(dU:アンダーコート層の厚み(nm)、λ:極小反射率を示す波長(nm)、n:透明保護膜(材質シリカ)の屈折率、1.44)
なお、本実施例において、λが200nm未満、1,200nm超となった場合には以下で示すアンダーコート層の理論厚みをアンダーコート層の厚みとして代用した。
(14)オーバーコート層の厚み
基材であるPETフィルムの上にオーバーコート層のみを設けた状態で、オーバーコート層の設置面の反対側表面を60°光沢度(JIS Z 8741 (1997年))が10以下になるように320~400番の耐水サンドペーパーで均一に粗面化した後、可視光線透過率が5%以下となるように黒色塗料を塗布して着色した。測定面を(株)島津製作所製の分光光度計(UV-3150)にて、測定面から5°の入射角で、波長領域200nm~1,200nmにおける絶対反射スペクトルを1nm間隔で測定し、200nm~1,200nmの領域での反射率の極小値を示す波長を求めた。
(dO:オーバーコート層の厚み(nm)、λ:極小反射率を示す波長(nm)、n:透明保護膜(材質シリカ)の屈折率、1.44)
なお、オーバーコート層の厚みにおいても、λが200nm未満、1,200nm超となった場合にはアンダーコート層の理論厚みと同様の方法で導出した理論厚みをオーバーコート層の厚みとして代用した。
(15)XPS
アルバック・ファイ(株)製“Quantera SXM”を用いて、励起X線をAlKα1、2線(1486.6eV)とし、光電子X線角度15°の条件下で、C1sの結合エネルギー測定を行った。この際、横軸補正はC1sのメインピークを284.6eVとして行った。
(16) アンダーコートまたはPET基材表面へのカーボンナノチューブ分散液の濡れ性
アンダーコートまたはPET基材表面へのカーボンナノチューブ分散液の濡れ性は、カーボンナノチューブ分散液を前記アンダーコートまたはPET基材表面へ塗布し、乾燥固定した後の乾燥カーボンナノチューブ塗膜が均一に形成されていれば良好、均一に形成されていなければ劣ると目視で判断した。
[アンダーコート層形成例1]
以下の操作によりポリシリケートをバインダーとし、直径約30nmのシリカ微粒子が表出する親水シリカアンダーコート層を形成した。
[アンダーコート層形成例2]
ワイヤーバー#3を用いた以外は[アンダーコート層形成例1]と同様にして、ポリシリケートをバインダーとし、直径約30nmのシリカ微粒子が表出する親水シリカアンダーコート層を形成した。
[アンダーコート層形成例3]
直径約30nmの親水シリカ微粒子とポリシリケートを含む(株)菱和製メガアクア親水DMコート DM-30-26G-N1-A[アンダーコート層形成例1]で用いたものより親水性を若干低下させたもの)をシリカ膜形成用塗液として用いた以外は[アンダーコート層形成例1]と同様にして、ポリシリケートをバインダーとし、直径約30nmのシリカ微粒子が表出する親水シリカアンダーコート層を形成した。
[アンダーコート層形成例4]
以下の操作によりゾルゲル法で作製したシリカからなる親水シリカアンダーコート層を形成した。
[アンダーコート層形成例5]
以下の操作によりアルミナからなる親水アルミナアンダーコート層を形成した。
408, 409を介して、クーリングドラム410に通す。ボート406上にはアルミニウム等のワイヤーが導入されていて、ボート406からアルミニウムを蒸発させ、ガス導入機構を有するプラズマ電極412から、酸素ガス流量0.6L/min、プラズマ投入電力は3.0kWの条件で酸素プラズマを照射することにより、このクーリングドラム410上の位置において高分子フィルム401の表面に酸化アルミニウム層(図示しない)を形成した。その後、このアルミナ層を形成した高分子フィルムをガイドロール413,
414, 415を介して、巻き取りロール416に巻き取った。
[アンダーコート層形成例6]
コロナ処理を実施しなかったほかは[アンダーコート層形成例4]と同様にして、ゾルゲル法で作製したシリカからなる親水シリカアンダーコート層を形成した。
[基材表面処理例1]
東レ(株)製“ルミラー” U46上に[アンダーコート層形成例4]と同様のコロナ処理を実施した。この処理により基材表面の親水性が増し、水接触角が62°から52°に低下した。
[触媒調製例:マグネシアへの触媒金属塩の担持]
クエン酸アンモニウム鉄(和光純薬工業(株)製)2.46gをメタノール(関東化学(株)製)500mLに溶解した。この溶液に、酸化マグネシウム(岩谷化学工業(株)製
MJ-30)を100.0g加え、撹拌機で60min間激しく撹拌処理し、懸濁液を減圧下、40℃で濃縮乾固した。得られた粉末を120℃で加熱乾燥してメタノールを除去し、酸化マグネシウム粉末に金属塩が担持された触媒体を得た。得られた固形分は篩い上で、乳鉢で細粒化しながら、20~32メッシュ(0.5~0.85mm)の範囲の粒径を回収した。得られた触媒体に含まれる鉄含有量は0.38質量%であった。また、かさ密度は、0.61g/mLであった。上記の操作を繰り返し、以下の実験に供した。
[カーボンナノチューブ集合体製造例:カーボンナノチューブ集合体の合成]
図5に示した装置を用いてカーボンナノチューブの合成を行った。反応器503は内径75mm、長さは1,100mmの円筒形石英管である。中央部に石英焼結板502を具備し、石英管下方部には、不活性ガスおよび原料ガス供給ラインである混合ガス導入管508、上部には廃ガス管506を具備する。さらに、反応器を任意温度に保持できるように、反応器の円周を取り囲む加熱器として3台の電気炉501を具備する。また反応管内の温度を検知するために熱電対505を具備する。
[カーボンナノチューブ集合体の精製および酸化処理]
カーボンナノチューブ集合体製造例で得られた触媒体とカーボンナノチューブを含有するカーボンナノチューブ含有組成物を130g用いて4.8Nの塩酸水溶液2,000mL中で1hr撹拌することで触媒金属である鉄とその担体であるMgOを溶解した。得られた黒色懸濁液は濾過した後、濾取物は再度4.8Nの塩酸水溶液400mLに投入し脱MgO処理をし、濾取した。この操作を3回繰り返した(脱MgO処理)。その後、イオン交換水で濾取物の懸濁液が中性となるまで水洗後、水を含んだウェット状態のままカーボンナノチューブ含有組成物を保存した。このとき水を含んだウェット状態のカーボンナノチューブ含有組成物全体の重量は102.7gであった(カーボンナノチューブ含有組成物濃度:3.12質量%)。
[カーボンナノチューブ分散液1の調製]
得られたウェット状態のカーボンナノチューブ集合体(乾燥重量換算で25mg)、1質量%カルボキシメチルセルロースナトリウム(ダイセルファインケム(株)製、ダイセル1140(重量平均分子量:45万))水溶液2.5g、ジルコニアビーズ(東レ(株)社製、トレセラム、ビーズサイズ:0.8mm)6.7gを容器に加え、28%アンモニア水溶液(キシダ化学(株)製)を用いてpH10に調整した。この容器を振動ボールミル((株)入江商会社製、VS-1、振動数:1,800cpm(60Hz))を用いて2hr振盪させ、カーボンナノチューブペーストを調製した。
[カーボンナノチューブ分散液2の調製]
得られたウェット状態のカーボンナノチューブ集合体(乾燥重量換算で25mg)、6質量%カルボキシメチルセルロースナトリウム(第一工業製薬(株)製、セロゲン5A(重量平均分子量:8万))水溶液0.833g、イオン交換水0.8g、ジルコニアビーズ(東レ(株)社製、トレセラム、ビーズサイズ:0.8mm)13.3gを容器に加え、28%アンモニア水溶液(キシダ化学(株)製)を用いてpH10に調整した。(分散剤/カーボンナノチューブ質量比=2)この容器を振動ボールミル((株)入江商会社製、VS-1、振動数:1,800cpm(60Hz))を用いて2hr振盪させ、カーボンナノチューブペーストを調製した。
[カーボンナノチューブ分散液3の調製]
6質量%カルボキシメチルセルロースナトリウム添加量を1.04g(分散剤/カーボンナノチューブ質量比=2.5)とした以外はカーボンナノチューブ分散液2の調製と同様にしてカーボンナノチューブ分散液9gを得た。
[カーボンナノチューブ分散液4の調製]
6質量%カルボキシメチルセルロースナトリウム添加量を1.25g(分散剤/カーボンナノチューブ質量比=3)とした以外はカーボンナノチューブ分散液2の調製と同様にしてカーボンナノチューブ分散液9gを得た。
[カーボンナノチューブ分散液5の調製]
6質量%カルボキシメチルセルロースナトリウム添加量を2.50g(分散剤/カーボンナノチューブ質量比=6)とした以外はカーボンナノチューブ分散液2の調製と同様にしてカーボンナノチューブ分散液9gを得た。
[カーボンナノチューブ分散液6の調製]
20mLの容器にカーボンナノチューブ含有組成物製造工程で得られたカーボンナノチューブ15mg(乾燥時質量換算)、30質量%のポリスチレンスルホン酸アンモニウム水溶液(アルドリッチ社製、重量平均分子量20万、)300mg(分散剤/カーボンナノチューブ質量比=6)を量りとり、蒸留水を加え10gにし、超音波ホモジナイザー(家田貿易(株)製、VCX-130)の出力を20Wとし、7.5min間で氷冷下分散処理しカーボンナノチューブ液を調製した。この液ではカーボンナノチューブ質量に対する分散剤の質量比は6となる。得られた液を高速遠心分離機((株)トミー精工、MX-300)にて10,000G、15min遠心し、カーボンナノチューブ分散液9gを得た。
[カーボンナノチューブ分散液7の調製]
カーボンナノチューブペースト調整、カーボンナノチューブ分散液調整時のpHを4.5とした以外はカーボンナノチューブ分散液2の調製と同様にしてカーボンナノチューブ分散液9gを得た。
[カーボンナノチューブ分散液8の調製]
カーボンナノチューブペースト調整、カーボンナノチューブ分散液調整時のpHを5.5とした以外はカーボンナノチューブ分散液2の調製と同様にしてカーボンナノチューブ分散液9gを得た。
[カーボンナノチューブ分散液9の調製]
カーボンナノチューブペースト調整、カーボンナノチューブ分散液調整時のpHを7とした以外はカーボンナノチューブ分散液2の調製と同様にしてカーボンナノチューブ分散液9gを得た。
[カーボンナノチューブ分散液10の調製]
カーボンナノチューブペースト調整、カーボンナノチューブ分散液調整時のpHを9とした以外はカーボンナノチューブ分散液2の調製と同様にしてカーボンナノチューブ分散液9gを得た。
[カーボンナノチューブ分散液11の調製]
カーボンナノチューブペースト調整、カーボンナノチューブ分散液調整時のpHを11とした以外はカーボンナノチューブ分散液2の調製と同様にしてカーボンナノチューブ分散液9gを得た。
[カーボンナノチューブ分散液12の調製]
得られたウェット状態のカーボンナノチューブ集合体(乾燥重量換算で15mg)、1wt%カルボキシメチルセルロースナトリウム(シグマ社製、90kDa,50~200cps)水溶液4.5g(分散剤/カーボンナノチューブ質量比=3)を量りとり、イオン交換水を加え10gにした。硝酸を用いてpHを4.0に合わせ、超音波ホモジナイザー(家田貿易(株)製,
CX-130)の出力を20Wとし、7.5min間で氷冷下分散処理しカーボンナノチューブ液を調製した。分散中液温が10℃以下となるようにした。得られた液を高速遠心分離機((株)トミー精工,
MX-300)にて10,000G、15min遠心し、カーボンナノチューブ分散液9gを得た。
[カーボンナノチューブ層の形成]
前記カーボンナノチューブ分散液にイオン交換水を添加して、0.03質量%~0.04質量%に調整後、前記アンダーコート層を設けた透明基材またはPET透明基材にワイヤーバーを用いて塗布、80℃乾燥機内で1min間乾燥させカーボンナノチューブ組成物を固定化した。光線透過率の調整は前記カーボンナノチューブ濃度とワイヤーバーの番手を調整して行った。
[リンス処理]
カーボンナノチューブ層を形成した透明導電積層体をイオン交換水にて30secリンスし、分散剤を除去した。リンス後、フィルムに付着した水滴をエアダスターで除去、その後常温で乾燥させた。
[オーバーコート層形成例1]
100mLポリ容器中に、エタノール20gを入れ、n-ブチルシリケート40gを添加し30min間撹拌した。その後、0.1N塩酸水溶液を10g添加した後2hr撹拌を行い4℃で12hr静置した。この溶液をトルエンとイソプロピルアルコールとメチルエチルケトンの混合液で固形分濃度が0.1質量%となるように希釈した。
[オーバーコート層形成例2]
トルエンとイソプロピルアルコールとメチルエチルケトンの混合液で固形分濃度が1質量%となるように希釈した以外は[オーバーコート層形成例1]と同様にしてオーバーコート層を形成した。
(実施例1)
[アンダーコート層形成例1]に従って、アンダーコート層を形成した。アンダーコート層上にカーボンナノチューブ分散液1を用いて、カーボンナノチューブ層を形成した。カーボンナノチューブ層上に[オーバーコート層形成例1]の手法でオーバーコート層を設け、透明導電積層体を作製した。
(実施例2~13、比較例1~6)
基材表面処理、アンダーコート層の形成、カーボンナノチューブ分散液、オーバーコート層の形成、リンス処理の組み合わせを、表1に示す組み合わせとした以外は、実施例1と同様にして透明導電積層体を作製した。なお、表中“基材表面処理またはアンダーコートなし”の項目で、“なし”と記載があるのは、東レ(株)製“ルミラー”
U46上にアンダーコートを設けることなく、または基材にコロナ処理を実施することなく、直接カーボンナノチューブ分散液を塗布したことを表す。
[アンダーコート層形成例2]でアンダーコート層を形成した基材上に[カーボンナノチューブ分散液3]を0.06質量%で調整した塗液をワイヤーバー#3を用いて塗工した。
[XPS測定サンプル2]
アンダーコート層を形成していない#188 U46上に[アンダーコート層形成例4]で実施したコロナ処理を実施し、さらに[カーボンナノチューブ分散液3]を0.06質量%で調整した塗液をワイヤーバー#20を用いて塗工した。なお、ワイヤーバー#20とXPS測定サンプル1よりもカーボンナノチューブ層厚みを大きくしたのは、X線がPET基材まで進入することを防ぐためであり、このようにすることで、カーボンナノチューブ層中でのカーボンの結合状態に関する情報のみを得ることができる。
102:電極
103:隔壁
104:透明基材
201:白反射板
202:粘着層
203:透明導電積層体
204:導電層
205:透明基材
401:高分子フィルム
403:巻き取り式真空蒸着装置
404:巻き取り室
405:巻き出しロール
406:ボート
407、408、409:巻き出し側ガイドロール
410:クーリングドラム
411:酸素導入ノズル
412:プラズマ電極
413、414、415:巻き取り側ガイドロール
416:巻き取りロール
501:電気炉
502:石英焼結板
503:反応器
504:触媒層
505:熱電対
506:廃ガス管
507:マスフローコントローラー
508:混合ガス導入管
Claims (13)
- 透明基材上に、カーボンナノチューブを含む導電層を有する透明導電積層体であって、次の[A]~[C]の少なくとも1つを満たし、かつ、60℃、相対湿度90%で1hr湿熱処理を行い、次いで25℃、相対湿度50%で3min間放置した後における表面抵抗値の、該処理前の表面抵抗値に対する割合が、0.7~1.3である透明導電積層体。
[A]白反射率75%における表面抵抗値が1.1×103Ω/□以下
[B]カーボンナノチューブ層光吸収率5%における表面抵抗値が1.1×103Ω/□以下
[C]全光線透過率90%における表面抵抗値が1.1×103Ω/□以下 - 150℃で1hr熱処理を行い、次いで25℃、相対湿度50%で24hr放置した後の表面抵抗値の、該処理前の表面抵抗値に対する割合が、0.7~1.3である請求項1に記載の透明導電積層体。
- 80℃で500hr熱処理を行い、次いで25℃、相対湿度50%で3min間放置した後の表面抵抗値の、該処理前の表面抵抗値に対する割合が、0.7~1.3である請求項1または2に記載の透明導電積層体。
- 前記導電層の下部に無機酸化物を含むアンダーコート層が配置されている請求項1~3のいずれかに記載の透明導電積層体。
- 前記無機酸化物がアルミナおよび/またはシリカを主たる成分とする請求項4に記載の透明導電積層体。
- 前記アンダーコート層が、シリカ微粒子とポリシリケートの複合物を主たる成分とする請求項4に記載の透明導電積層体。
- 前記シリカ微粒子の直径が10nm~200nmの範囲にある請求項6に記載の透明導電積層体。
- 透明基材上に、水接触角が5~25°であるアンダーコート層を設けるアンダーコート層形成工程と、分散剤を含むカーボンナノチューブ分散液をアンダーコート層上に塗布する塗布工程と、アンダーコート層上に塗布された前記カーボンナノチューブ分散液から分散媒を除去する乾燥工程とを有する透明導電積層体の製造方法。
- 前記カーボンナノチューブ分散液のpHが5.5~11の範囲にある請求項8に記載の透明導電体の製造方法。
- 前記塗布工程、および/または、乾燥工程で、カーボンナノチューブ表面および/またはカーボンナノチューブ分散液中から分散剤を、前記アンダーコート層に移行させる請求項8または9に記載の透明導電積層体の製造方法。
- 前記カーボンナノチューブ分散液中のカーボンナノチューブに対する分散剤の質量比が0.5~9である請求項8~10のいずれかに記載の透明導電積層体の製造方法。
- 請求項1~7のいずれかに記載の透明導電積層体を用いた電子ペーパー。
- 請求項1~7のいずれかに記載の透明導電積層体を用いたタッチパネル。