WO2004106420A2 - Nanocomposites and method for production - Google Patents
Nanocomposites and method for production Download PDFInfo
- Publication number
- WO2004106420A2 WO2004106420A2 PCT/US2004/016226 US2004016226W WO2004106420A2 WO 2004106420 A2 WO2004106420 A2 WO 2004106420A2 US 2004016226 W US2004016226 W US 2004016226W WO 2004106420 A2 WO2004106420 A2 WO 2004106420A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- nanocomposite
- functionalized
- solubilized
- nanomaterial
- host
- Prior art date
Links
- 0 C*C*C(*C)*[N+] Chemical compound C*C*C(*C)*[N+] 0.000 description 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
- C08J5/005—Reinforced macromolecular compounds with nanosized materials, e.g. nanoparticles, nanofibres, nanotubes, nanowires, nanorods or nanolayered materials
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/01—Use of inorganic substances as compounding ingredients characterized by their specific function
- C08K3/013—Fillers, pigments or reinforcing additives
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B32/00—Carbon; Compounds thereof
- C01B32/15—Nano-sized carbon materials
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B82—NANOTECHNOLOGY
- B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
- B82Y30/00—Nanotechnology for materials or surface science, e.g. nanocomposites
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B32/00—Carbon; Compounds thereof
- C01B32/20—Graphite
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/515—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics
- C04B35/56—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on carbides or oxycarbides
- C04B35/563—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on carbides or oxycarbides based on boron carbide
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/515—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics
- C04B35/56—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on carbides or oxycarbides
- C04B35/565—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on carbides or oxycarbides based on silicon carbide
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/515—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics
- C04B35/58—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on borides, nitrides, i.e. nitrides, oxynitrides, carbonitrides or oxycarbonitrides or silicides
- C04B35/583—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on borides, nitrides, i.e. nitrides, oxynitrides, carbonitrides or oxycarbonitrides or silicides based on boron nitride
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/66—Monolithic refractories or refractory mortars, including those whether or not containing clay
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G61/00—Macromolecular compounds obtained by reactions forming a carbon-to-carbon link in the main chain of the macromolecule
- C08G61/02—Macromolecular compounds containing only carbon atoms in the main chain of the macromolecule, e.g. polyxylylenes
- C08G61/10—Macromolecular compounds containing only carbon atoms in the main chain of the macromolecule, e.g. polyxylylenes only aromatic carbon atoms, e.g. polyphenylenes
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/02—Elements
- C08K3/04—Carbon
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/02—Elements
- C08K3/04—Carbon
- C08K3/041—Carbon nanotubes
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/02—Elements
- C08K3/04—Carbon
- C08K3/045—Fullerenes
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/02—Elements
- C08K3/04—Carbon
- C08K3/046—Carbon nanorods, nanowires, nanoplatelets or nanofibres
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/38—Boron-containing compounds
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K7/00—Use of ingredients characterised by shape
- C08K7/02—Fibres or whiskers
- C08K7/04—Fibres or whiskers inorganic
- C08K7/06—Elements
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K7/00—Use of ingredients characterised by shape
- C08K7/22—Expanded, porous or hollow particles
- C08K7/24—Expanded, porous or hollow particles inorganic
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K9/00—Use of pretreated ingredients
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/38—Boron-containing compounds
- C08K2003/382—Boron-containing compounds and nitrogen
- C08K2003/385—Binary compounds of nitrogen with boron
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K2201/00—Specific properties of additives
- C08K2201/011—Nanostructured additives
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L21/00—Compositions of unspecified rubbers
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
- H01L2224/00—Indexing scheme for arrangements for connecting or disconnecting semiconductor or solid-state bodies and methods related thereto as covered by H01L24/00
- H01L2224/73—Means for bonding being of different types provided for in two or more of groups H01L2224/10, H01L2224/18, H01L2224/26, H01L2224/34, H01L2224/42, H01L2224/50, H01L2224/63, H01L2224/71
- H01L2224/732—Location after the connecting process
- H01L2224/73251—Location after the connecting process on different surfaces
- H01L2224/73253—Bump and layer connectors
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
- H01L2924/00—Indexing scheme for arrangements or methods for connecting or disconnecting semiconductor or solid-state bodies as covered by H01L24/00
- H01L2924/01—Chemical elements
- H01L2924/01021—Scandium [Sc]
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
- H01L2924/00—Indexing scheme for arrangements or methods for connecting or disconnecting semiconductor or solid-state bodies as covered by H01L24/00
- H01L2924/01—Chemical elements
- H01L2924/01046—Palladium [Pd]
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
- H01L2924/00—Indexing scheme for arrangements or methods for connecting or disconnecting semiconductor or solid-state bodies as covered by H01L24/00
- H01L2924/01—Chemical elements
- H01L2924/01077—Iridium [Ir]
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
- H01L2924/00—Indexing scheme for arrangements or methods for connecting or disconnecting semiconductor or solid-state bodies as covered by H01L24/00
- H01L2924/01—Chemical elements
- H01L2924/01078—Platinum [Pt]
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
- H01L2924/00—Indexing scheme for arrangements or methods for connecting or disconnecting semiconductor or solid-state bodies as covered by H01L24/00
- H01L2924/01—Chemical elements
- H01L2924/01079—Gold [Au]
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
- H01L2924/00—Indexing scheme for arrangements or methods for connecting or disconnecting semiconductor or solid-state bodies as covered by H01L24/00
- H01L2924/10—Details of semiconductor or other solid state devices to be connected
- H01L2924/102—Material of the semiconductor or solid state bodies
- H01L2924/1025—Semiconducting materials
- H01L2924/10251—Elemental semiconductors, i.e. Group IV
- H01L2924/10253—Silicon [Si]
Definitions
- the present patent application relates generally to the technical field of nanomaterial-based nanocomposites and their applications.
- a carbon nanotube can be visualized as a sheet of hexagonal graph paper rolled up into a seamless tube and joined. Each line on the graph paper represents a carbon-carbon bond, and each intersection point represents a carbon atom.
- carbon nanotubes are elongated tubular bodies which are typically only a few atoms in circumference.
- the carbon nanotubes are hollow and have a linear fullerene structure.
- the length of the carbon nanotubes potentially may be millions of times greater than their molecular-sized diameter.
- SWNTs single-walled carbon nanotubes
- MWNTs multi-walled carbon nanotubes
- Carbon nanotubes are currently being proposed for a number of applications since they possess a very desirable and unique combination of physical properties relating to, for example, strength and weight. Carbon nanotubes have also demonstrated electrical conductivity (Yakobson, B.I., et al, American Scientist, 85, (1997), 324-337; and Dresselhaus, M.S., et al, Science of Fullerenes and Carbon Nanotubes, (1996), San Diego, Academic Press, 902-905). For example, carbon nanotubes conduct heat and electricity better than copper or gold and have 100 times the tensile strength of steel, with only a sixth of the weight of steel. Carbon nanotubes may be produced having extraordinary small size.
- carbon nanotubes are being produced that are approximately the size of a DNA double helix (or approximately l/50,000th the width of a human hair).
- carbon nanotubes are well suited for a variety of uses, such as building computer circuits, reinforcing composite materials, and even to delivering medicine.
- carbon nanotubes may be useful in microelectronic device applications, which often demand high thermal conductivity, small dimensions, and lightweight.
- One application of carbon nanotubes that has been recognized from their use in flat-panel displays uses electron field-emission technology (since carbon nanotubes can be good conductors and electron emitters).
- Further applications that have been recognized include electromagnetic shielding, for cellular phones and laptop computers, radar absorption for stealth aircraft, nano-electronics (including memories in new generations of computers), and use as high-strength, lightweight, multifunctional composites.
- CNTs have exceptional physical properties, incorporating them into other materials has been inhibited by the surface chemistry of carbon. Problems such as phase separation, aggregation, poor dispersion within a matrix, and poor adhesion to the host must be overcome.
- SWNTs were solubilized in chloroform with poly(phenyleneethynylene)s (PPE) along with vigorous shaking and/or short bath-sonication as described by Chen et al (ibid) and in U.S. patent application US 2004/0034177 published February 19, 2004, having USSN 10/255,122, filed September 24, 2002, and U.S. patent application USSN 10/318,730 filed December 13, 2002.
- PPE poly(phenyleneethynylene)s
- the present inventors have addressed the problem of nanocomposites having nonuniform dispersion of nanomaterials in host polymer matrices that cause undesirable consequences to the composite material such as loss of strength, particle generation, increased viscosity, loss of processability, or other material degradation, and provide herein nanocomposites having improved properties.
- the present invention provides nanocomposites of functionalized, solubilized nanomaterials and host matrices where the nanocomposites provide increased electrical conductivity with lower electrical percolation thresholds, increased thermal conductivity with lower thermal percolation thresholds, or an improved mechanical property as compared to those of nanocomposites comprising the host matrix and nanomaterial other than the functionalized, solubilized nanomaterial.
- the low percolation thresholds demonstrate that a high dispersion of the nanomaterials in host matrices is achieved. Further, since a small amount of functionalized solubilized nanomaterial is needed to achieve increased conductivity or improved properties of a host matrix, the host matrix's other desired physical properties and processability are not compromised.
- a nanocomposite comprising a host matrix comprising polymer matrix or nonpolymer matrix and functionalized, solubilized nanomaterial dispersed within the host matrix is an embodiment of the invention.
- the nanocomposite has an electrical conductivity percolation threshold or a thermal conductivity percolation threshold that is lower than that of a nanocomposite comprising the host matrix and nanomaterial other than the functionalized, solubilized nanomaterial.
- the host matrix may be an organic polymer matrix, an inorganic polymer matrix, or a nonpolymer matrix, as described infra, or a combination thereof.
- a further embodiment of the invention is the above-cited nanocomposite wherein the functionalized, solubilized nanomaterial of the nanocomposite is a first filler and the nanocomposite further comprises a second filler to form a complex nanocomposite.
- the second filler comprises a continuous fiber, a discontinuous fiber, a nanoparticle, a microparticle, a macroparticle, or a combination thereof, and the second filler is other than a functionalized, solubilized nanomaterial.
- a nanocomposite comprising a host matrix of polymer matrix or nonpolymer matrix, wherein the polymer matrix is other than polystyrene and polycarbonate, and functionalized, solubilized nanomaterial dispersed within the host matrix is a further embodiment of the invention.
- the nanocomposite has a mechanical property that is enhanced as compared to that of a nanocomposite comprising the host matrix and the nanomatrial other than the functionalized, solubilized nanomaterial.
- the nanocomposite may further comprise a second host polymer matrix wherein the functionalized, solubilized nanomaterial is dispersed within the first and second host polymer matrices.
- the nanocomposite may further comprise a second filler to form a complex nanocomposite wherein the second filler is other than a functionalized, solubilized nanomaterial.
- a further nanocomposite of the present invention comprises a polystyrene, and a functionalized, solubilized nanomaterial dispersed within the polystyrene.
- a nanocomposite has a mechanical property that is enhanced as compared to that of a nanocomposite comprising the host matrix and the nanomatrial other than the functionalized, solubilized nanomaterial.
- the nanocomposite may further comprise a second host polymer matrix, wherein the functionalized, solubilized nanomaterial is dispersed within the first and second host polymer matrices.
- a nanocomposite comprises a host matrix comprising a first polymer matrix and a second polymer matrix and functionalized, solubilized nanomaterial dispersed within the host matrix wherein the first polymer matrix is polycarbonate.
- a method of increasing electrical or thermal conductivity of a host matrix comprising a polymer matrix or a nonpolymer matrix comprises dispersing functionalized, solubilized nanomaterial within host matrix material to form a nanocomposite.
- the nanocomposite has an electrical conductivity percolation threshold or a thermal conductivity percolation threshold that is lower than that of a nanocomposite comprising the host matrix and nanomaterial other than the functionalized, solubilized nanomaterial.
- the host matrix material may be the host matrix or a monomer of a host polymer matrix and, in such an embodiment, the method further comprises the step of polymerizing the host polymer matrix material in the presence of the functionalized, solubilized nanomaterial.
- the host matrix is a first host polymer matrix and the method further comprises dispersing a second host polymer matrix material with functionalized, solubilized nanomaterial and with first host polymer matrix material to form a nanocomposite comprising a first host polymer matrix and a second host polymer matrix.
- functionalized, solubilized nanomaterial is a first filler
- the dispersing further comprises dispersing a second filler within host matrix material to fonn a complex nanocomposite, wherein the second filler comprises a continuous fiber, a discontinuous fiber, a nanoparticle, a microparticle, a macroparticle, or a combination thereof, and wherein the second filler is other than a functionalized, solubilized nanomaterial.
- a method of improving a mechanical property of a host matrix comprising a polymer matrix or a nonpolymer matrix, wherein the host matrix is other than polystyrene or polycarbonate is an aspect of the present invention.
- the method comprises dispersing functionalized, solubilized nanomaterial within host matrix material to form a nanocomposite wherein the nanocomposite has an improved mechanical property compared to that of a nanocomposite comprising the host matrix and nanomaterial other than the functionalized, solubilized nanomaterial.
- the host matrix material may be the host matrix or comprise a monomer of the host matrix and the method then further comprises the step of polymerizing the host matrix material in the presence of the functionalized, solubilized nanomaterial.
- the method may further comprise dispersing a second host polymer matrix material with functionalized, solubilized nanomaterial and with first host polymer matrix material to form a nanocomposite comprising a first host polymer matrix and a second host polymer matrix.
- the dispersing may further comprise dispersing a second filler within host matrix material to form a complex nanocomposite wherein the second filler is other than a functionalized, solubilized nanomaterial.
- a method of improving a mechanical property of a polystyrene comprises dispersing functionalized, solubilized nanomaterial within styrene polymeric material to form a nanocomposite wherein the nanocomposite has an improved mechanical property compared to that of a nanocomposite comprising the polystyrene and nanomaterial other than the functionalized, solubilized nanomaterial.
- a second host matrix or a second filler may be added to produce further embodiments for improving a mechanical property of a polystyrene.
- a method of improving a mechanical property of a host matrix comprising a first polymer matrix and a second polymer matrix wherein the first polymer matrix is polycarbonate is an aspect of the present invention.
- the method comprises dispersing functionalized, solubilized nanomaterial within host polymeric material to form a nanocomposite wherein the nanocomposite has an improved mechanical property compared to that of a nanocomposite comprising the host matrix and nanomaterial other than the functionalized, solubilized nanomaterial.
- a second filler may be added to produce a complex nanocomposite.
- An article of manufacture comprising a nanocomposite having an improved electrical, thermal, or mechanical property as described herein is a further embodiment of the invention. Further, a product produced by a method as described herein is an embodiment of the present invention.
- FIG. 1A is a scanning electron microscopy image showing the surface of PPE- SWNTs/polystyrene nanocomposite film prepared by an embodiment of the present invention using 5 wt% of SWNTs.
- FIG. IB is a scanning electron microscopy image showing the cross-section of PPE- SWNTs/polystyrene nanocomposite film prepared by an embodiment of the present invention using 5 wt% of SWNTs.
- FIG. 2A shows room temperature electrical conductivity in siemens/meter (S/m) (also known as measured volume conductivity) of a PPE-SWNTs/polystyrene nanocomposite versus the SWNT weight loading for embodiments formed in accordance with the present invention.
- the dashed lines represent approximate conductivity lower bounds required for EMI shielding, electrostatic painting, and for electrostatic dissipation. At 0% mass fraction, the conductivity is about 10 "14 S/m.
- FIG. 2B shows room temperature conductivity of the PPE-SWNTs/polystyrene nanocomposite as a function of reduced mass fraction of SWNTs.
- the percolation threshold m o is 0.045%.
- 3A shows room temperature electrical conductivity of a PPE-SWNTs/polycarbonate nanocomposite versus SWNT weight loading prepared by an embodiment of the present invention.
- the dashed lines represent approximate conductivity lower bounds required for EMI shielding, electrostatic painting, and for electrostatic dissipation.
- FIG. 3B shows room temperature conductivity of the PPE-SWNTs/polycarbonate nanocomposite as a function of reduced mass fraction of SWNTs.
- the percolation threshold m o is 0.110%.
- FIG. 4 shows a field-emission scanning electron microscopy image of a fracture surface at a broken end of a f-s-SWNTs polycarbonatenanocomposite film loaded at 1 wt% of SWNTs.
- FIG. 5A and FIG. 5B show example heat transfer applications of a CNT-polymer composite in accordance with certain embodiments of the present invention.
- FIG. 5A shows an architecture typically used in laptop applications
- FIG. 5B shows an architecture typically used in desktop and server applications.
- the large arrow pointing upward indicates the primary heat transfer path in each architecture. See Example 2 for designation of components.
- FIG. 6A shows tensile stress vs. tensile strain of pure polycarbonate film prepared by solution casting.
- FIG. 6B shows tensile stress vs. tensile strain of f-s-SWNTs/polycarbonate film having 2 wt% SWNTs prepared by solution casting.
- f-s-SWNTs functionalized, solubilized single-walled carbon nanotubes
- Such nanocomposites have demonstrated, for example, electrical conductivity with very low percolation threshold (0.05-0.1 wt% of SWNT loading).
- a very low f-s-SWNT loading is needed to achieve conductivity levels required for various electrical applications without compromising the host polymer's other preferred physical properties and processability.
- Nanocomposite means a noncovalently functionalized solubilized nanomaterial dispersed within a host matrix.
- the host matrix may be a host polymer matrix or a host nonpolymer matrix.
- Host polymer matrix means a polymer matrix within which the nanomaterial is dispersed.
- a host polymer matrix may be an organic polymer matrix or an inorganic polymer matrix, or a combination thereof.
- Examples of a host polymer matrix include a nylon, polyethylene, epoxy resin, polyisoprene, sbs rubber, polydicyclopentadiene, polytetrafluoroethulene, poly(phenylene sulfide), poly(phenylene oxide), silicone, polyketone, aramid, cellulose, polyimide, rayon, pofy(methyl methacrylate), poly(vinylidene chloride), poly(vinylidene fluoride), carbon fiber, polyurethane, polycarbonate, polyisobutylene, polychloroprene, polybutadiene, polypropylene, poly(vinyl chloride), poly(ether sulfone), poly(vinyl acetate), polystyrene, polyester, polyvinylpyrrolidone, polycyanoacrylate, polyacrylonitrile, polyamide, poly(aryleneethynylene), poly(phenyleneethynylene), polythiophene, them
- a host polymer matrix includes a thermoplastic, such as ethylene vinyl alcohol, a fluoroplastic such as polytetrafluoroethylene, fiuoroethylene propylene, perfluoroalkoxyalkane, chlorotrifluoroethylene, ethylene chlorotrifluoroethylene, or ethylene tetrafluoroethylene, ionomer, polyacrylate, polybutadiene, polybutylene, polyethylene, polyethylenechlorinates, polymethylpentene, polypropylene, polystyrene, polyvinylchloride, polyvinylidene chloride, polyamide, polyamide-imide, polyaryletherketone, polycarbonate, polyketone, polyester, polyetheretherketone, polyetherimide, polyethersulfone, polyimide, polyphenylene oxide, polyphenylene sulfide, polyphthalamide, polysulfone, or polyurethane.
- the host polymer includes a thermoset, such as ethylene vinyl alcohol, a flu
- inorganic host polymers include a silicone, polysilane, polycarbosilane, polygermane, polystannane, a polyphosphazene, or a combination thereof.
- More than one host matrix may be present in a nanocomposite.
- mechanical, thermal, chemical, or electrical properties of a single host matrix nanocomposite are optimized by adding f-s-SWNTs to the matrix of the nanocomposite material.
- Example 4 infra provides an example of such an embodiment where polycarbonate and epoxy are provided as host polymers in a nanocomposite material of the present invention. Addition of polycarbonate in addition to epoxy appears to reduce voids in a nanocomposite film as compared to a nanocomposite film with just epoxy as the host polymer. Such voids degrade the performance of nanocomposites.
- using two host polymers is designed for solvent cast epoxy nanocomposites where the f-s-SWNTs, the epoxy resin and hardener, and the polycarbonate are dissolved in solvents and the nanocomposite film is formed by solution casting or spin coating.
- Host nonpolymer matrix means a nonpolymer matrix within which the nanomaterial is dispersed.
- host nonpolymer matrices include a ceramic matrix (such as silicon carbide, boron carbide, or boron nitride), or a metal matrix (such as aluminum, titanium, iron, or copper), or a combination thereof.
- Functionalized solubilized SWNTs are mixed with, for example, polycarbosilane in organic solvents, and then the solvents are removed to form a solid (film, fiber, or powder).
- the resulting solid f-s-SWNTs/polycarbosilane nanocomposite is further converted to SWNTs/SiC nanocomposite by heating at 900-1600 °C either under vacuum or under inert atmosphere (such as Ar).
- Nanomaterial includes, but is not limited to, functionalized and solubilized multi-wall carbon or boron nitride nanotubes, single-wall carbon or boron nitride nanotubes, carbon or boron nitride nanoparticles, carbon or boron nitride nanofibers, carbon or boron nitride nanoropes, carbon or boron nitride nanoribbons, carbon or boron nitride nanofibrils, carbon or boron nitride nanoneedles, carbon or boron nitride nanosheets, carbon or boron nitride nanorods, carbon or boron nitride nanohorns, carbon or boron nitride nanocones, carbon or boron nitride nanoscrolls, graphite nanoplatelets, nanodots, other fullerene materials, or or
- nanotubes is used broadly herein and, unless otherwise qualified, is intended to encompass any type of nanomaterial.
- a “nanotube” is a tubular, strand-like structure that has a circumference on the atomic scale.
- the diameter of single walled nanotubes typically ranges from approximately 0.4 nanometers (nm) to approximately 100 nm, and most typically have diameters ranging from approximately 0.7 nm to approximately 5 nm.
- SWNTs single walled nanotubes
- the term means that other nanomaterials as cited supra may be substituted unless otherwise stated herein.
- Functionalized, solubilized nanomaterial means that the nanomaterial is solubilized by a nonwrapping, noncovalent functionalization with a rigid, conjugated polymer. Such functionalization and solubilization is exemplified by the process and compositions for carbon nanotubes of Chen, J. et al. (J. Am. Chem. Soc, 124, 9034 (2002)) which process results in excellent nanotube dispersion and is described in U.S.
- the term "rigid, conjugated polymer,” as used herein for functionalization and solubilization contains a backbone portion for noncovalently bonding with a nanotube in a non-wrapping fashion.
- the backbone portion may comprise a group having the formula:
- each of Ri-Rs in the above-listed backbone portions a)-q) represents H, or F, or an R group bonded to the backbone via a carbon or an oxygen linkage as described infra.
- an R group may be any organic radical or any combination thereof. That is, an R group may be any organic radical or any combination thereof. That is, an R group may be any organic radical or any combination thereof. That is, an R group may be any organic radical or any combination thereof. That is, an R group may be any organic radical or any combination thereof. That is, an R group may be any organic radical or any combination thereof. That is, an R group may be any organic radical or any combination thereof. That is, an R group may be any organic radical or any combination thereof. That is, an R group may be any organic radical or any combination thereof. That is, an R group may be any organic radical or any combination thereof. That is, an R group may be any organic radical or any combination thereof. That is, an R group may be any organic radical or any combination thereof. That is, an R group may be any organic radical or any combination thereof. That is, an R group may be any organic radical or any combination thereof. That is, an R group may be any organic radical or any combination thereof. That is, an R group may be any organic radical
- a rigid, conjugated polymer include those having a backbone and R groups bonded to a backbone via an ether linkage as follows:
- the R group is designed to adjust the CNTs' solubility in various solvents, for example, using PPE polymers with linear or branched glycol side chains provides for high solubility of SWNTs in DMF or NMP, which further provides for uniform mixing of f-s-SWNTs with host polymers (for example, polyacrylonitrile) that are soluble in DMF or NMP, but not in halogenated solvents (such as chloroform).
- the R groups bonded to the backbone via a carbon-carbon bond or an oxygen-carbon bond as described supra may have additional reactive species, i.e, functional groups, at the periphery of the R groups.
- peripheral means at the outer end of such R group side chains, away or distal from the backbone.
- functional groups include, for example, acetal, acid halide, acyl azide, aldehyde, alkane, anhydride, cyclic alkane, arene, alkene, alkyne, alkyl halide, aryl halide, amine, amide, amino acid, alcohol, azide, aziridine, azo compounds, calixarene, carbohydrate, carbonate, carboxylic acid, carboxylate, carbodiimide, cyclodextrin, crown ether, cryptand, diaminopyridine, diazonium compounds, ester, ether, epoxide, fullerene, glyoxal, imide, inline, imidoester, ketone, nitrile, isothiocyanate, isocyanate, isonitrile, lactone, maleimide, metalloc
- Peripheral functional groups at the ends of R groups distal to the backbone of the functionalized, solubilized nanotube enhance interaction between the functionalized, solubilized nanomaterial and the host matrix of composites of the present invention.
- Such peripheral functional groups are designed to improve the interfacial bonding between functionalized, solubilized CNTs and the host matrix.
- PPE polymers with reactive functional groups such as epoxide, or amine, or pyridine
- reactive functional groups such as epoxide, or amine, or pyridine
- a PPE polymer with a thiol group at or near the end of a linear or branched side chain provides for enhanced interaction between f-s-SWNTs and gold or silver nanoparticles (host matrices), for example.
- a further example provides SWNTs functionalized with a PPE polymer having thymine at the end of a linear side chain.
- a fiber can then be assembled with SWNTs functionalized with such PPE polymers and with PPE polymers having diaminopyridine in the end of linear side chain by forming extensive parallel triple (three-point) hydrogen bonds.
- f-s-SWNTs means functionalized, solubilized single walled nanotubes, the term means that other nanomaterials as cited supra may be substituted unless otherwise stated herein.
- Rigid, conjugated polymers for functionalization include a poly(phenyleneethynylene) (PPE), poly(aryleneethynylene), or poly(3-decylthiophene), for example.
- PPE poly(phenyleneethynylene)
- Such functionalization provides for a solubility of carbon nanomaterial in solvents and lengthy sonication procedures are not needed.
- This non- wrapping functionalization is suitable for nanomaterial as described herein. Since the polymer is attached to the nanomaterial surface by noncovalent bonding instead of covalent bonding, the underlying electronic structure of the nanotubes and their key attributes are not affected.
- Nanocomposites can themselves be used as a host matrix for a second filler to form a complex nanocomposites.
- a second filler include: continuous fibers (such as carbon fibers, carbon nanotube fibers, carbon nanotube nanocomposite fibers, KEVLAR® fibers, ZYLON® fibers, SPECTRA® fibers, nylon fibers, or a combination thereof, for example), discontinuous fibers (such as carbon fibers, carbon nanotube fibers, carbon nanotube nanocomposite fibers, KEVLAR® fibers, ZYLON® fibers, SPECTRA® fibers, nylon fibers, or a combination thereof, for example), nanoparticles (such as metallic particles, polymeric particles, ceramic particles, nanoclays, diamond particles, or a combination thereof, for example), and microparticles (such as metallic particles, polymeric particles, ceramic particles, clays, diamond particles, or a combination thereof, for example).
- a number of existing materials use continuous fibers, such as carbon fibers, in a matrix. These fibers are much larger than carbon nanotubes. Adding f-s-SWNTs to the matrix of a continuous fiber reinforced nanocomposite results in a complex nanocomposite material having improved properties such as improved impact resistance, reduced thermal stress, reduced microcracking, reduced coefficient of thermal expansion, or increased transverse or through-thickness thermal conductivity. Resulting advantages in complex nanocomposite structures include improved durability, improved dimensional stability, elimination of leakage in cryogenic fuel tanks or pressure vessels, improved through-thickness or inplane thermal conductivity, increased grounding or electromagnetic interference (EMI) shielding, increased flywheel energy storage, or tailored radio frequency signature (Stealth), for example.
- EMI electromagnetic interference
- Improved thermal conductivity also could reduce infrared (IR) signature.
- Further existing materials that demonstrate improved properties by adding f-s-SWNTs include metal particle nanocomposites for electrical or thermal conductivity, nano-clay nanocomposites, or diamond particle nanocomposites, for example.
- Methods to incorporate nanomaterial into the host matrix include, but are not limited to: (i) in-situ polymerization of monomer(s) of the host polymer in a solvent system in the presence of functionalized solubilized nanomaterial; (ii) mixing both functionalized solubilized nanomaterial and host matrix in a solvent system; or (iii) mixing functionalized solubilized nanomaterial with a host polymer melt.
- a method of forming nanocomposites in accordance with certain embodiments of the present invention includes the use of solvents for dissolving functionalized solubilized nanomaterial and host matrix.
- a solvent may be organic or aqueous such as, for example, CHC1 3 , chlorobenzene, water, acetic acid, acetone, acetonitrile, aniline, benzene, benzonitrile, benzyl alcohol, bromobenzene, bromoform, 1- butanol, 2-butanol, carbon disulfide, carbon tetrachloride, chlorobenzene, chloroform, cyclohexane, cyclohexanol, decalin, dibromethane, diethylene glycol, diethylene glycol ethers, diethyl ether, diglyme, dimethoxymethane, N,N-dimethylformamide, ethanol, ethylamine, ethylbenzene, ethylene glycol ether
- solvents include ionic liquids or supercritical solvents.
- ionic liquids include, for example, tetra-n-butylphosphonium bromide, tetra-n-butylammonium bromide, 1- ethyl-3-methyl-imidazolium chloride, l-butyl-3-methyl-imidazolium chloride, l-hexyl-3-methyl- imidazolium chloride, l-methyl-3-octyl-imidazolium chloride, l-butyl-4-methyl-pyridinium chloride, 1- ethyl-3-methyl-imidazolium tetrafluoroborate, l-butyl-3-methyl-imidazolium tetrafluoroborate, 1-hexyl- 3-methyl-imidazolium tetrafluoroborate, 3 -methyl- 1-octyl-imidazolium tetrafluoroborate
- the functionalized solubilized nanomaterial may comprise an amount by weight or volume of the nanocomposite greater than zero and less than 100%; an amount equal to or witliin a range of any of the following percentages: 0.01%, 0.02%, 0.04%, 0.05%, 0.075%, 0.1% 0.5%, 1.0%, 1.5%, 2.0%, 2.5%, 3.0%, 3.5%, 4.0%, 4.5%, 5.0%, 5.5%, 6.0%, 7.0%, 8.0%, 9.0%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, and 75%; an amount by weight or volume of the nanocomposite equal to or greater than 0.1% and less than or equal to 50%; or an amount by weight or volume of the nanocomposite equal to or greater than 1% to 10%.
- Nanocomposites of the present invention provide superior electrical or thermal conductivity, or superior mechanical properties as compared with nanocomposites that lack functionalized solubilized nanomaterial.
- One measure of such nanocomposite properties is the percolation threshold of the nanocomposite.
- the percolation threshold is the minimum amount by weight or volume of functionalized solubilized nanomaterial present within the host matrix that provides an interconnectivity within the matrix. A low percolation threshold indicates good dispersion of nanomaterial within the host matrix.
- the percolation threshold is unique to the type of host matrix, type of nanomaterial, type of functionalization solubilization, and conditions of fabricating the nanocomposites.
- the percolation threshold is also unique to a particular property, i.e., a percolation threshold for an electrical property may be different from a percolation threshold for a thermal property for a particular nanocomposite since an electrical property enhancement mechanism is different from a thermal property enhancement mechanism.
- Composites of the present invention demonstrate a percolation threshold for electrical conductivity, or a percolation threshold for thermal conductivity within a range of any of the following percentages: 0.01%, 0.02%, 0.04%, 0.05%, 0.075%, 0.1% 0.5%, 1.0%, 1.5%, 2.0%, 2.5%, 3.0%, 3.5%, 4.0%, 4.5%, 5.0%, 6%, 7%, 8%, 9%, 10%, 15%, 20%, 25%, 30% and 33% by weight of volume.
- a percolation threshold for electrical conductivity or a percolation threshold for thermal conductivity is equal to or greater than 0.01%, 0.02%, 0.04%, 0.05%, 0.1% 0.5%, 1.0%, 1.5%, 2.0%, 3.0%, 4.0%, 5.0%, 10% and less than or equal to 20.0% by weight or volume.
- a percolation threshold for electrical conductivity or a percolation threshold for thermal conductivity is equal to or greater than 0.01%, 0.02%, 0.04%, 0.05%, 0.1%, 0.5%, 1.0%, 1.5%, 2.0%, 3.0%, 4.0%, and less than or equal to 5.0% by weight or volume.
- Percolation threshold is determined by measuring the property of interest of a nanocomposite versus the mass fraction of loading of functionalized, solubilized nanomaterial into a matrix such as provided in the examples infra.
- the nanocomposite PPE-SWNTs/polystyrene has a percolation threshold for electrical conductivity of 0.045 wt% of SWNT loading
- the nanocomposite PPE-SWNTs/polycarbonate has a percolation threshold for electrical conductivity of 0.11 wt% of SWNT loading.
- Nanocomposite embodiments of the present invention have an electrical conductivity percolation threshold that is lower than that of the nanocomposite comprising the host matrix and nanomaterial other than the functionalized, solubilized nanomaterial.
- an electrical conductivity percolation threshold that is lower than that of the nanocomposite comprising the host matrix and nanomaterial other than the functionalized, solubilized nanomaterial.
- embodiments of the present invention make possible applications such as electrostatic dissipation, electrostatic painting, electromagnetic interference (EMI) shielding, printable circuit wiring, transparent conductive coatings.
- EMI electromagnetic interference
- Articles of manufacture comprising a nanocomposite of the present invention include wire, printable circuit wire, coatings, transparent coatings, coatings for resist materials, resist materials, films, fibers, powders, inks, ink jettable nanocomposite solutions, paints, electrosprayed paints, EMI shields, conductive sealants, conductive caulks, conductive adhesives, opto-electronic devices, for example, and other articles for electrically conductive applications such as electrostatic dissipation, electrostatic painting, or electromagnetic interference (EMI) shielding, for example.
- EMI electromagnetic interference
- Nanocomposites for thermal applications Nanocomposite embodiments of the present invention have a thermal conductivity percolation threshold that is lower than that of the nanocomposite comprising the host matrix and nanomaterial other than the functionalized, solubilized nanomaterial. Enhanced thermal conductivity provides many applications. Nanocomposite materials can be engineered to be more compliant and conforming, thus providing much better heat transfer to take advantage of the high thermal conductivity in the material. Therefore, nanocomposites herein are useful for heat transfer, either heating or cooling, or packaging, for example.
- Articles of manufacture comprising a nanocomposite of the present invention include electronics, photonics, microelectromechanical (MEMS) packaging, heat spreaders, heat sinks, packages, modules, heat pipes, housings, enclosures, heat exchangers, radiant heaters, thermal interface materials, heat spreaders, films, fibers, powders, coatings, automotive applications including, for example, under-hood components, radiators, sensor housings, electronic modules, or fuel cells, industrial applications, including, for example, electrical coil components, pump parts, electric motor parts, transformers, piping, tubing, or heating, ventilation or air conditioning (HVAC) equipment.
- MEMS microelectromechanical
- FIG. 5A and FIG. 5B a heat transfer application using nanocomposites of the present invention as a thermal interface between an integrated circuit ("IC") (or IC package) and an accompanying heat sink is shown in FIG. 5A and FIG. 5B and includes heatsink 10, TIM2 20 (thermal-interface material over the integrated heat spreader), integrated heat spreader 30 (HIS), TDVH 40 (thermal-interface material over the die), die 50, underfill 60, and substrate 70.
- FIG. 5A shows an example thermal-solution architecture that is typically used in laptop applications.
- the example architecture of FIG. 5A comprises heatsink 10, TEVll (thermal-interface material over the die) 40, die 50, underfill 60, and substrate 70.
- FIG. 5A shows an example thermal-solution architecture that is typically used in laptop applications.
- the example architecture of FIG. 5A comprises heatsink 10, TEVll (thermal-interface material over the die) 40, die 50, underfill 60, and substrate 70.
- FIG. 5B shows another example thermal-solution architecture that is typically used in desktop and server applications.
- the example architecture of FIG. 5B comprises heatsink 10, TIM2 (tliermal-interface material over the integrated heat spreader) 20, integrated heat spreader (HIS) 30, TEVll (thermal-interface material over the die) 40, die 50, underfill 60, and substrate 70.
- TIMl 40 or TIM2 20 in the architectures of FIG. 5A and FIG. 5B.
- nanocomposites of the present invention make the nanocomposites suitable for cooling electrical components, such as in the example architectures of FIG. 5A and FIG. 5B, by effectively conducting heat away from the component (e.g., to a heat sink 10).
- the nanocomposite interface e.g., TIMl 40 and/or TIM2 20
- the nanocomposite interface may be implemented as a solid material (e.g., a solid sheet) that is formed to fit in the architecture in a desired manner.
- the nanocomposite interface may be implemented as a viscous (e.g., "gooey”) substance.
- Nanocomposite embodiments of the present invention have an improved mechanical property, such as any one of tensile stress, tensile strain, stiffness, strength, fracture toughness, creep resistance, creep rupture resistance, and fatigue resistance, as compared to that of the nanocomposite comprising the host matrix and nanomaterial other than the functionalized, solubilized nanomaterial.
- an improved mechanical property such as any one of tensile stress, tensile strain, stiffness, strength, fracture toughness, creep resistance, creep rupture resistance, and fatigue resistance
- Articles of manufacture comprising a nanocomposite of the present invention include adhesives, reinforced continuous fiber materials, aircraft structures, aircraft gas turbine engine components, spacecraft structures, instrument structures, missiles, launch vehicle structures, reusable launch vehicle cryogenic fuel tanks fitting attachment, compressed natural gas and hydrogen fuel tanks, ship and boat structures, pressure vessel fitting attachment, sporting goods, industrial equipment, automotive and mass transit vehicles, offshore oil exploration and production equipment, wind turbine blades, medical equipment (e.g. x-ray tables), orthotics, prosthetics, films, fibers, powders, or furnitures.
- Nanocomposites having low percolation thresholds for more than one property or more than one improved property While a nanocomposite of the present invention may have different percolation thresholds for different properties, a nanocomposite may have low percolation thresholds for more than one property and therefore provide multiple advantageous properties. For example, a nanocomposite may have an increased electrical conductivity at a low f-s-SWNT loading and, in addition, an enhanced mechanical or thermal property at that loading. Due to the multifunctional nature of f-s-SWNTs, nanocomposites herein may be useful for one or more than one of electrical, mechanical, thermal, chemical, sensing and actuating applications, for example.
- Adhesives are widely used to assemble electronics. In many applications, they must be electrical insulators. However, there many applications for which electrical conductivity is desirable or at least acceptable. There are also strong drivers for adhesives with improved thermal conductivity. For example, diamond particle-reinforced adhesives are now used in production applications. Based on the advantageous thermal conductivity of nanocomposites herein, this could be an important application. In instances where high thermal conductivity is desirable, but electrical insulation is required, very thin electrically insulating interfaces can be used in conjunction with nanocomposites so that the multi-layered structure would provide both electrical insulation and high thermal conductivity.
- Further articles of manufacture comprising nanocomposites of the present invention include aircraft structures, aircraft gas turbine engine components, spacecraft structures, instrument structures, missiles, launch vehicle structures, reusable launch vehicle cryogenic fuel tanks, ship or boat structures, sporting goods, industrial equipment, automotive or mass transit vehicles, offshore oil exploration or production equipment, wind turbine blades, medical equipment (e.g. x-ray tables), ortliotics, or prosthetics, for example.
- SWNTs produced by high pressure carbon monoxide process were purchased from Carbon Nanotechnologies, Inc. (Houston, TX), and were solubilized in chloroform with poly(phenyleneethynylene)s (PPE) along with vigorous shaking and or short bath-sonication as described by Chen et al. (ibid) and in U.S.
- Noncovalently functionalized, soluble SWNTs/polymer nanocomposites of the present example show improvements in electrical conductivity over the polymer itself, with very low percolation thresholds (0.05-0.1 wt% of SWNT loading).
- PPE-functionalized SWNT solutions were mixed with a host polymer (polycarbonate or polystyrene) solution in chloroform to give a homogeneous nanotube/polymer nanocomposite solution.
- a uniform nanocomposite film was prepared from this solution on a silicon wafer with a 100 nm thick thermal oxide layer either by drop casting or by slow-speed spin coating. The samples were then heated to 80 °C to 90 °C to remove residual solvent.
- SWNT loadings from 0.01 wt% to 10 wt% in polystyrene as well as in polycarbonate were prepared. Thicl ⁇ iesses of the films were measured using a LEO 1530 Scanning Electron Microscope or a profilameter. A typical thickness of a nanocomposite film was in the range of 2-10 ⁇ m.
- the SWNT mass-fraction loading values for f-s-SWNTs/host polymer nanocomposites are based on pristine SWNT material only and exclude the additive material.
- IB show scanning electron microscope (SEM) images of the surface (1A) and the cross section (IB) of PPE-SWNTs/polystyrene nanocomposite film (5 wt% SWNTs) prepared by solution casting.
- the images show excellent dispersion of PPE-functionalized SWNTs in host polymer matrix.
- f-s-SWNTs are randomly distributed not only along the surface (FIG. 1A), but also through the cross section (FIG. IB), indicating the formation of an isotropic, three dimensional nanotube network in host polymer matrix, thereby allowing for the possibility that the nanocomposites demonstrate isotropic electrical conductivity.
- the films show individual and bundles of f-s-SWNTs uniformly mixed in the polymer matrix.
- FIG. 2A shows the measured volume conductivity of PPE-SWNTs/polystyrene nanocomposites as a function of the SWNT loading and formed in accordance with an embodiment of the present invention. The conductivity of the composite increases sharply between 0.02 wt% to 0.05 wt% SWNT loading, indicating the formation of a percolating network.
- the electrical conductivity obeys the power law relation ⁇ c « (v-v c ) p (1)
- ⁇ c is the composite conductivity
- v is the SWNT volume fraction
- v c is the percolation threshold
- ⁇ is the critical exponent.
- the densities of the polymer and the SWNT are similar, therefore, the mass fraction m and volume fraction v of the SWNT in the polymer are assumed to be the same.
- the PPE-SWNTs/polystyrene conductivity agrees very well with the percolation behavior of equation (1) above.
- the very low percolation threshold is a signature of excellent dispersion of high aspect ratio soluble f-s-SWNTs.
- the conductivity of pure polystyrene is about 10 "14 S/m (C. A. Harper, Handbook of Plastics, Elastomers, and Composites, 4th ed. (McGraw-Hill, 2002))
- the conductivity of pristine (unfunctionalized) HiPco-SWNT buckypaper is about 5.1xl0 4 S/m.
- Buckypaper is not a nanocomposite as used herein since there is no host polymer present.
- the conductivity of the nanocomposite reached 6.89 S/m at 7 wt% of SWNT loading, which is 14 orders of magnitude higher than that (10 "14 S/m) of pure polystyrene.
- the conductivity of 6.89 S/m at 7 wt% of SWNT loading is 5 orders of magnitude higher than that of a nonfunctionalized SWNTs(8.5 wt%)/polystyrene nanocomposite (1.34xl0 '5 S/m) that was prepared by in situ polymerization (H. J. Barraza, et al, Nano Lett. 2, 797 (2002)).
- this method of using functionalized carbon nanotube to obtain highly dispersed nanocomposite is applicable to various host matrices and does not require lengthy sonication procedures.
- FIG. 3A and FIG. 3B show the electrical conductivity (measured volume conductivity) of PPE- SWNTs/polycarbonate nanocomposites as a function of the SWNT loading for nanocomposites prepared by the same procedure as that of FIG. 2A and FIG. 2B.
- the conductivity of PPE-SWNTs/polycarbonate is generally higher that that of PPE-SWNTs/polystyrene at the same SWNT loading.
- the conductivity reached 4.81xl0 2 S/m at 7 wt% of SWNT loading, which is 15 orders of magnitude higher than that of pure polycarbonate (about 10 "13 S/m, C. A. Harper, ibid.).
- FIG. 2A and FIG. 3A also show conductivity levels for electrical applications such as electrostatic dissipation, electrostatic painting and EMI shielding (Miller, Plastics World, 54, September, 73 (1996)).
- EMI shielding Miller, Plastics World, 54, September, 73 (1996).
- 0.3 wt% of SWNT loading in polycarbonate is sufficient for applications such as electrostatic dissipation and electrostatic painting, and 3 wt% of SWNT loading is adequate for EMI shielding applications. Since only a very low f-s-SWNT loading is required to achieve the cited conductivity levels, the host polymer's other preferred physical properties and processability would be minimally compromised within the nanocomposite.
- Noncovalently functionalized, soluble SWNTs/polymer nanocomposites of the present example show improvements in thermal conductivity as compared to that of the polymer itself.
- Thermal conductivity was measured on nanocomposites with various amounts of SWNT loadings from 0.5 wt% to 10 wt%. Films of the nanocomposites were prepared by solution casting on a PTFE substrate and the free standing films were peeled off from the substrate. A typical film thickness was about 50-100 microns. Out-of-plane thermal conductivity was measured using a commercial Hitachi
- the present example provides improved mechanical properties of nanocomposites of f-s-SWNTs and polymer as compared with that of the polymer itself.
- PARMAX® (Mississippi Polymer Technologies, Inc., Bay Saint Louis, MS), refers to a class of thermoplastic rigid-rod polymers that are soluble in organic solvents and melt processable.
- PARMAX® is based on a substituted poly(l,4-phenylene) in wliich each phenylene ring has a substituted organic group R.
- the general structure of PARMAX® is shown at I.
- a PARMAX®-1200 solution in chloroform was mixed with a PPE-SWNT solution in chloroform.
- the solution was cast on a substrate, for example, glass, and let dry to form a film.
- the film was further dried under vacuum and at a temperature appropriate for the solvent; for chloroform, ambient temperature is appropriate.
- FIG. 6A shows the mechanical property of tensile stess vs. tensile strain for pure polycarbonate film
- FIG. 6B shows the mechanical property of tensile stress vs. tensile strain for f-s-SWNTs (2 wt% of SWNTs)/polycarbonate film.
- the 2 wt% of SWNTs filling results in 79% increase in tensile strength of polycarbonate, and the break strain (tensile strain) is increased by approximately a factor of 10.
- the PPE-SWNT/ PARMAX® nanocomposite can also be manufactured by other methods, such as compression molding, extrusion, or fiber spinning, for example.
- a PARMAX®- 1200 solution in chloroform was mixed with a PPE-SWNT solution in chloroform to form a uniform solution of PPE-SWNTs/ PARMAX® nanocomposite.
- Ethanol was added to the PPE-SWNTs/ PARMAX® nanocomposite solution with vigorous stirring to precipitate the nanocomposite.
- a uniform powder of PPE-SWNTs/ PARMAX® nanocomposite was obtained.
- the resulting nanocomposite powder is fabricated into a variety of shaped- solids by compression molding at 200-400 °C (preferably 315 °C) for ⁇ 30 min.
- FIG. 4 shows a fracture surface in an f-s-SWNTs/polycarbonate nanocomposite.
- the nanotubes remain in the matrix even after the fracture, indicating strong interaction with the host polymer.
- Raw nanotubes often interact poorly with a matrix, that is, a fracture expels them and leaves behind voids in the material.
- the present example provides improved mechanical and electrical properties of nanocomposites of f-s-SWNTs and two host polymers as compared with that of one host polymer.
- SWNTs/epoxy plus polycarbonate as host polymer(s) regarding electrical and mechanical properties.
- the nanocomposites were assembled from epoxy resin, epoxy hardener, PPE-SWNTs, and with or without polycarbonate.
- the processing steps are dispersing PPE-SWNTs and epoxy resin, hardener, and 5% by weight of the final composition of polycarbonate (in those compositions that contain polycarbonate) and stirring or shaking until the mixture is well dispersed to form a nanocomposite.
- the mixture was either solution-cast or spin-coated and the solvent was removed by evaporation to produce a nanocomposite film with excellent nanotube dispersion.
- Film having the two-polymer nanocomposite provides about a 20-fold improvement in electrical conductivity over that of the one-polymer-composite (1.17 S/m for the two-polymer nanocomposite as compared to 0.053 for the one-polymer-composite).
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB0523751A GB2421506B (en) | 2003-05-22 | 2004-05-21 | Nanocomposites and methods thereto |
JP2006533339A JP2007516314A (ja) | 2003-05-22 | 2004-05-21 | ナノコンポジットおよびナノコンポジットに関する方法 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US47282003P | 2003-05-22 | 2003-05-22 | |
US60/472,820 | 2003-05-22 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2004106420A2 true WO2004106420A2 (en) | 2004-12-09 |
WO2004106420A3 WO2004106420A3 (en) | 2005-04-21 |
Family
ID=33490525
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2004/016226 WO2004106420A2 (en) | 2003-05-22 | 2004-05-21 | Nanocomposites and method for production |
Country Status (6)
Cited By (60)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2005102406A1 (en) * | 2004-03-25 | 2005-11-03 | Boston Scientific Limited | Medical device comprising thermoplastic rigid-rod polymer |
WO2006028282A1 (en) * | 2004-09-09 | 2006-03-16 | Toyota Jidosha Kabushiki Kaisha | Nanoimprint mold, method of forming a nanopattern, and a resin-molded product |
WO2007011313A1 (en) * | 2005-07-20 | 2007-01-25 | Agency For Science, Technology And Research | Electroconductive curable resins |
JP2007146081A (ja) * | 2005-11-30 | 2007-06-14 | Teijin Ltd | ポリカーボネート系樹脂成形体およびその製造法 |
JP2007146039A (ja) * | 2005-11-29 | 2007-06-14 | Teijin Ltd | 樹脂組成物およびその成形体 |
JP2007146038A (ja) * | 2005-11-29 | 2007-06-14 | Teijin Ltd | 樹脂組成物およびその製造方法 |
GB2433262A (en) * | 2005-12-16 | 2007-06-20 | Schlumberger Holdings | Nanocomposites for use in oilfield elements |
JP2007197555A (ja) * | 2006-01-26 | 2007-08-09 | Teijin Ltd | 耐熱性樹脂組成物およびその製造方法 |
JP2007197597A (ja) * | 2006-01-27 | 2007-08-09 | Teijin Ltd | 耐熱性、寸法安定性に優れた樹脂組成物およびその製造方法 |
JP2007197554A (ja) * | 2006-01-26 | 2007-08-09 | Teijin Ltd | 立体規則性ポリアクリロニトリル系樹脂組成物およびその製造方法 |
JP2007197594A (ja) * | 2006-01-27 | 2007-08-09 | Teijin Ltd | 強化フェノキシ樹脂系組成物およびその製造方法 |
JP2007197596A (ja) * | 2006-01-27 | 2007-08-09 | Teijin Ltd | 機械特性に優れた耐熱樹脂組成物およびその製造方法 |
JP2007197595A (ja) * | 2006-01-27 | 2007-08-09 | Teijin Ltd | 熱安定性に優れたポリエーテルスルホン系樹脂組成物及びその製造方法 |
WO2007092032A2 (en) * | 2005-06-14 | 2007-08-16 | Dow Corning Corporation | Reinforced silicone resin film and method of preparing same |
JP2007217449A (ja) * | 2006-02-14 | 2007-08-30 | Teijin Ltd | 耐熱樹脂組成物およびその製造法 |
JP2007231155A (ja) * | 2006-03-01 | 2007-09-13 | Teijin Ltd | 耐熱樹脂組成物およびその製造法 |
JP2007231031A (ja) * | 2006-02-27 | 2007-09-13 | National Institute For Materials Science | 複合フィルムとその製造方法 |
JP2007254654A (ja) * | 2006-03-24 | 2007-10-04 | Teijin Ltd | 透明耐熱樹脂組成物およびその製造法 |
JP2007297463A (ja) * | 2006-04-28 | 2007-11-15 | Teijin Ltd | 強化樹脂組成物およびその製造法 |
JP2008007699A (ja) * | 2006-06-30 | 2008-01-17 | Teijin Ltd | 耐熱樹脂複合組成物及びその製造方法 |
JP2008031206A (ja) * | 2006-07-26 | 2008-02-14 | Teijin Ltd | 樹脂複合組成物及びその製造方法 |
WO2008034939A1 (en) * | 2006-09-04 | 2008-03-27 | Natucell Ay | Functionalized cellulose - carbon nanotube nanocomposites and hybride materials |
JP2008069194A (ja) * | 2006-09-12 | 2008-03-27 | Teijin Ltd | 耐熱性樹脂複合組成物及びその製造方法 |
WO2008046010A3 (en) * | 2006-10-11 | 2008-06-26 | Univ Florida | Electroactive polymers containing pendant pi-interacting/binding substituents, their carbon nanotube composites, and processes to form the same |
JP2008144046A (ja) * | 2006-12-11 | 2008-06-26 | Teijin Ltd | 耐熱性樹脂複合組成物及びその製造方法 |
WO2008082225A1 (en) * | 2006-12-29 | 2008-07-10 | Cheil Industries Inc. | Thermoplastic nanocomposite resin composition with improved scratch resistance |
WO2008103221A1 (en) * | 2007-02-22 | 2008-08-28 | Dow Corning Corporation | Process for preparing conductive films and articles prepared using the process |
JP2008291133A (ja) * | 2007-05-25 | 2008-12-04 | Teijin Ltd | 耐熱性に優れた樹脂組成物及びその製造方法 |
CN100453955C (zh) * | 2005-01-07 | 2009-01-21 | 鸿富锦精密工业(深圳)有限公司 | 热管及其制造方法 |
WO2009059387A1 (en) * | 2007-11-08 | 2009-05-14 | Braskem S. A. | Process for the production of high tensile strength and low creep polymer yarns, high tensile strength and low creep polymer or copolymer yarns, and, the use of such yarns |
GB2456484A (en) * | 2009-06-10 | 2009-07-22 | Vestas Wind Sys As | Wind turbine blade incorporating nanoclay |
EP2088122A1 (en) * | 2006-10-25 | 2009-08-12 | Kuraray Co., Ltd. | Transparent conductive film, transparent electrode substrate and method for producing liquid crystal alignment film by using the same, and carbon nanotube and method for producing the same |
WO2009127281A1 (de) * | 2008-04-17 | 2009-10-22 | FRÖTEK Kunststofftechnik GmbH | Flügel einer flügelzellenpumpe oder eines flügelzellenkompressors |
US20100022706A1 (en) * | 2007-02-07 | 2010-01-28 | Bayer Materialscience Ag | Polyurethanes filled with carbon black and with a high dielectric constant breakdown strength |
WO2010057502A2 (en) * | 2008-11-24 | 2010-05-27 | Vestas Wind Systems A/S | Wind turbine blade comprising particle-reinforced bonding material |
JPWO2008146400A1 (ja) * | 2007-05-25 | 2010-08-19 | 帝人株式会社 | 樹脂組成物 |
US7931828B2 (en) * | 2008-05-22 | 2011-04-26 | Rolls-Royce Corporation | Gas turbine engine and method including composite structures with embedded integral electrically conductive paths |
WO2011076979A1 (en) * | 2009-12-22 | 2011-06-30 | Moilanen, Pasi | Fabrication and application of polymer-graphitic material nanocomposites and hybride materials |
US8084532B2 (en) | 2006-01-19 | 2011-12-27 | Dow Corning Corporation | Silicone resin film, method of preparing same, and nanomaterial-filled silicone composition |
US8084097B2 (en) | 2006-02-20 | 2011-12-27 | Dow Corning Corporation | Silicone resin film, method of preparing same, and nanomaterial-filled silicone composition |
US8088449B2 (en) | 2005-02-16 | 2012-01-03 | Dow Corning Toray Co., Ltd. | Reinforced silicone resin film and method of preparing same |
US8092910B2 (en) | 2005-02-16 | 2012-01-10 | Dow Corning Toray Co., Ltd. | Reinforced silicone resin film and method of preparing same |
WO2012041715A1 (de) * | 2010-09-29 | 2012-04-05 | Siemens Aktiengesellschaft | Elektrisch isolierender nanokomposit mit halbleitenden oder nichtleitenden nanopartikeln, verwendung dieses nanokomposits und verfahren zu dessen herstellung |
US8242181B2 (en) | 2007-10-12 | 2012-08-14 | Dow Corning Corporation | Aluminum oxide dispersion and method of preparing same |
US8262939B2 (en) | 2005-12-30 | 2012-09-11 | Cheil Industries Inc. | Thermoplastic nanocomposite resin composite materials |
US8273448B2 (en) | 2007-02-22 | 2012-09-25 | Dow Corning Corporation | Reinforced silicone resin films |
US8283025B2 (en) | 2007-02-22 | 2012-10-09 | Dow Corning Corporation | Reinforced silicone resin films |
WO2012146703A1 (en) * | 2011-04-27 | 2012-11-01 | Stichting Dutch Polymer Institute | Process for the preparation of a conductive polymer composition |
US8334022B2 (en) | 2005-08-04 | 2012-12-18 | Dow Corning Corporation | Reinforced silicone resin film and method of preparing same |
RU2476457C2 (ru) * | 2007-09-18 | 2013-02-27 | Шлюмбергер Технолоджи Б.В. | Нефтепромысловое устройство, нефтепромысловый элемент указанного устройства, содержащий функционализированные графеновые пластинки, способ осуществления нефтепромысловой операции и способ модификации функционализированных графеновых пластинок |
US8912268B2 (en) | 2005-12-21 | 2014-12-16 | Dow Corning Corporation | Silicone resin film, method of preparing same, and nanomaterial-filled silicone composition |
WO2015155040A1 (en) * | 2014-04-09 | 2015-10-15 | Re-Turn As | Paints and gelcoats with high cnt content |
US9346991B2 (en) | 2011-04-14 | 2016-05-24 | Ada Technologies, Inc. | Thermal interface materials and systems and devices containing the same |
US9422413B1 (en) | 2010-12-14 | 2016-08-23 | Molecular Rebar Design, Llc | Elastomer formulations comprising discrete carbon nanotube fibers |
US9475921B2 (en) | 2011-06-23 | 2016-10-25 | Molecular Rebar Design, Llc | Nanoplate-nanotube composites, methods for production thereof and products obtained therefrom |
WO2017180102A1 (en) * | 2016-04-12 | 2017-10-19 | Siemens Aktiengesellschaft | Management of heat conduction using phononic regions having non-metallic nanostructures |
US9997785B2 (en) | 2011-06-23 | 2018-06-12 | Molecular Rebar Design, Llc | Nanoplate-nanotube composites, methods for production thereof and products obtained therefrom |
CN108504250A (zh) * | 2018-04-11 | 2018-09-07 | 启东海大聚龙新材料科技有限公司 | 一种环氧树脂复合耐磨涂层及其制备方法 |
WO2021120245A1 (zh) * | 2019-12-19 | 2021-06-24 | 宁波长阳科技股份有限公司 | 人造石墨复合膜及其制备方法 |
EP3988621A4 (en) * | 2019-06-20 | 2022-08-17 | Posco | HEAT-CONDUCTIVE AND ELECTRICALLY INSULATING COLOR COMPOSITION, AS WELL AS OUTER STEEL SHEET FOR SOLAR CELL WITH IT |
Families Citing this family (150)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6861481B2 (en) * | 2000-09-29 | 2005-03-01 | Solvay Engineered Polymers, Inc. | Ionomeric nanocomposites and articles therefrom |
US10340424B2 (en) | 2002-08-30 | 2019-07-02 | GE Lighting Solutions, LLC | Light emitting diode component |
WO2004039893A1 (ja) * | 2002-11-01 | 2004-05-13 | Mitsubishi Rayon Co., Ltd. | カーボンナノチューブ含有組成物、これからなる塗膜を有する複合体、及びそれらの製造方法 |
KR20070045192A (ko) * | 2004-06-14 | 2007-05-02 | 카단트 웹 시스템즈, 인코포레이티드 | 제지 기계에 사용하기 위한 편평 소자 |
AU2006347615A1 (en) * | 2005-08-08 | 2008-04-10 | Cabot Corporation | Polymeric compositions containing nanotubes |
KR100761799B1 (ko) * | 2005-08-24 | 2007-10-05 | 제일모직주식회사 | 나노복합체 및 이를 이용한 열가소성 나노복합재 수지조성물 |
US8133465B2 (en) * | 2005-09-12 | 2012-03-13 | University Of Dayton | Polymer-carbon nanotube composite for use as a sensor |
US7465605B2 (en) * | 2005-12-14 | 2008-12-16 | Intel Corporation | In-situ functionalization of carbon nanotubes |
JP5154760B2 (ja) * | 2006-03-01 | 2013-02-27 | 帝人株式会社 | ポリエーテルエステルアミド系エラストマー樹脂組成物およびその製造法 |
US8703235B2 (en) * | 2007-02-23 | 2014-04-22 | The United States Of America As Represented By The Administrator Of The National Aeronautics And Space Administration | Preparation of metal nanowire decorated carbon allotropes |
US10144638B2 (en) * | 2006-03-09 | 2018-12-04 | Battelle Memorial Institute | Methods of dispersing carbon nanotubes |
WO2008048705A2 (en) * | 2006-03-10 | 2008-04-24 | Goodrich Corporation | Low density lightning strike protection for use in airplanes |
KR100838824B1 (ko) * | 2006-04-20 | 2008-06-17 | 인하대학교 산학협력단 | 열안정성 및 마찰, 마모 특성이 향상된 탄소나노섬유/폴리메틸메타크릴레이트 나노복합재의 제조방법 |
JP2007321071A (ja) * | 2006-06-01 | 2007-12-13 | Teijin Ltd | 樹脂複合組成物及びその製造方法 |
KR100784822B1 (ko) * | 2006-09-12 | 2007-12-14 | 김주용 | 능동 냉각을 위한 전자 섬유 |
KR100819004B1 (ko) * | 2006-11-15 | 2008-04-02 | 삼성전자주식회사 | 미세 전자 소자 및 그 제조 방법 |
KR100818264B1 (ko) * | 2006-12-22 | 2008-04-01 | 삼성에스디아이 주식회사 | 나노복합체, 나노복합 전해질막 및 이를 이용한 연료전지 |
KR100818265B1 (ko) * | 2006-12-22 | 2008-04-01 | 삼성에스디아이 주식회사 | 나노복합체, 나노복합 전해질막 및 이를 이용한 연료전지 |
US20080186678A1 (en) * | 2007-02-06 | 2008-08-07 | Dell Products L.P. | Nanoparticle Enhanced Heat Conduction Apparatus |
US20080227168A1 (en) * | 2007-02-16 | 2008-09-18 | Board Of Regents, The University Of Texas System | Methods and materials for extra and intracellular delivery of carbon nanotubes |
US20080310956A1 (en) * | 2007-06-13 | 2008-12-18 | Jain Ashok K | Variable geometry gas turbine engine nacelle assembly with nanoelectromechanical system |
FR2918067B1 (fr) * | 2007-06-27 | 2011-07-01 | Arkema France | Materiau composite comprenant des nanotubes disperses dans une matrice polymerique fluroree. |
FR2918082B1 (fr) * | 2007-06-27 | 2011-07-01 | Arkema France | Procede d'impregnation de fibres continues par une matrice polymerique composite renfermant un polymere fluore greffe. |
WO2009042076A1 (en) * | 2007-09-21 | 2009-04-02 | Abb Technology Ag | A dry-type transformer with a polymer shield case and a method of manufacturing the same |
US8919428B2 (en) * | 2007-10-17 | 2014-12-30 | Purdue Research Foundation | Methods for attaching carbon nanotubes to a carbon substrate |
JP2009102504A (ja) * | 2007-10-23 | 2009-05-14 | Teijin Ltd | 機械特性に優れた耐熱性樹脂組成物及びその製造方法 |
WO2009105085A1 (en) * | 2007-11-28 | 2009-08-27 | National Institute Of Aerospace Associates | Metallized nanotube polymer composite (mnpc) and methods for making same |
US8211958B2 (en) * | 2007-12-05 | 2012-07-03 | The Research Foundation Of State University Of New York | Polyolefin nanocomposites with functional ionic liquids and carbon nanofillers |
WO2009145813A1 (en) | 2008-03-04 | 2009-12-03 | Qd Vision, Inc. | Particles including nanoparticles, uses thereof, and methods |
JP2009256534A (ja) * | 2008-04-21 | 2009-11-05 | Teijin Ltd | 機械特性、寸法安定性に優れた高分子電解質組成物及びその製造方法 |
JP2009292907A (ja) * | 2008-06-04 | 2009-12-17 | Teijin Ltd | 機械特性、寸法安定性に優れた樹脂組成物及びその製造方法 |
US9447251B2 (en) * | 2008-07-01 | 2016-09-20 | Vobeck Materials Corp. | Articles having a compositional gradient and methods for their manufacture |
US20100009165A1 (en) * | 2008-07-10 | 2010-01-14 | Zyvex Performance Materials, Llc | Multifunctional Nanomaterial-Containing Composites and Methods for the Production Thereof |
CN101654555B (zh) * | 2008-08-22 | 2013-01-09 | 清华大学 | 碳纳米管/导电聚合物复合材料的制备方法 |
CN101659789B (zh) * | 2008-08-29 | 2012-07-18 | 清华大学 | 碳纳米管/导电聚合物复合材料的制备方法 |
US8512417B2 (en) | 2008-11-14 | 2013-08-20 | Dune Sciences, Inc. | Functionalized nanoparticles and methods of forming and using same |
US20100128439A1 (en) * | 2008-11-24 | 2010-05-27 | General Electric Company | Thermal management system with graphene-based thermal interface material |
US20110319554A1 (en) * | 2008-11-25 | 2011-12-29 | The Board Of Trustees Of The University Of Alabama | Exfoliation of graphite using ionic liquids |
FR2940659B1 (fr) * | 2008-12-26 | 2011-03-25 | Arkema France | Fibre composite a base de pekk, son procede de fabrication et ses utilisations |
JP5603059B2 (ja) * | 2009-01-20 | 2014-10-08 | 大陽日酸株式会社 | 複合樹脂材料粒子及びその製造方法 |
BRPI1007300A2 (pt) | 2009-02-17 | 2019-09-24 | Applied Nanostructured Sols | compósitos compreendendo nanotubos de carbono sobre fibra |
US8541058B2 (en) * | 2009-03-06 | 2013-09-24 | Timothy S. Fisher | Palladium thiolate bonding of carbon nanotubes |
US7862342B2 (en) * | 2009-03-18 | 2011-01-04 | Eaton Corporation | Electrical interfaces including a nano-particle layer |
BRPI1016242A2 (pt) * | 2009-04-24 | 2016-04-26 | Applied Nanostructured Sols | material de controle de assinatura baseado em cnt. |
JP2010254839A (ja) * | 2009-04-27 | 2010-11-11 | Teijin Ltd | 耐磨耗性に優れたフルオロカーボン系樹脂組成物およびその製造方法 |
WO2010135721A2 (en) * | 2009-05-22 | 2010-11-25 | Mesocoat, Inc. | Article and method of manufacturing related to nanocomposite overlays |
CH701115A2 (de) | 2009-05-25 | 2010-11-30 | Fischer Georg Rohrleitung | Polyolefinzusammensetzung. |
KR101470524B1 (ko) * | 2009-06-30 | 2014-12-08 | 한화케미칼 주식회사 | 혼화성이 증대된 복합탄소소재 및 이의 연속적인 제조 방법 |
US8420729B2 (en) * | 2009-07-08 | 2013-04-16 | Mohamad Ali Sharif Sheikhaleslami | Method of preparing phenolic resin/carbon nano materials (hybrid resin) |
US9823133B2 (en) * | 2009-07-20 | 2017-11-21 | Applied Materials, Inc. | EMI/RF shielding of thermocouples |
US8545167B2 (en) * | 2009-08-26 | 2013-10-01 | Pratt & Whitney Canada Corp. | Composite casing for rotating blades |
US8561934B2 (en) | 2009-08-28 | 2013-10-22 | Teresa M. Kruckenberg | Lightning strike protection |
US7976935B2 (en) * | 2009-08-31 | 2011-07-12 | Xerox Corporation | Carbon nanotube containing intermediate transfer members |
EP2475717A4 (en) | 2009-09-09 | 2015-01-07 | Qd Vision Inc | PARTICLES WITH NANOPARTICLES, USES THEREOF AND METHOD THEREFOR |
WO2011031876A1 (en) | 2009-09-09 | 2011-03-17 | Qd Vision, Inc. | Formulations including nanoparticles |
CN102753475B (zh) | 2009-09-21 | 2016-07-13 | 迪肯大学 | 制造方法 |
US8593040B2 (en) | 2009-10-02 | 2013-11-26 | Ge Lighting Solutions Llc | LED lamp with surface area enhancing fins |
EP2504164A4 (en) | 2009-11-23 | 2013-07-17 | Applied Nanostructured Sols | CERAMIC COMPOSITE MATERIALS CONTAINING FIBER MATERIALS IMPREGNATED WITH CARBON NANOTUBES AND METHODS OF MAKING SAME |
EP2504464A4 (en) * | 2009-11-23 | 2015-01-21 | Applied Nanostructured Sols | COMPOSITE-SPACE-BASED STRUCTURES SUITABLE FOR CARBON NANOTUBES |
KR20120104600A (ko) | 2009-12-14 | 2012-09-21 | 어플라이드 나노스트럭처드 솔루션스, 엘엘씨. | 탄소 나노튜브 주입된 섬유 물질을 포함하는 방염 복합재 물질 및 물품 |
WO2011081659A1 (en) * | 2009-12-15 | 2011-07-07 | Massachusetts Institute Of Technology | Degradable polymer nanostructure materials |
JP2013515847A (ja) * | 2009-12-28 | 2013-05-09 | 日本ポリプロ株式会社 | ポリオレフィン中のナノチューブ及び/又はナノ小板の分散 |
US8541933B2 (en) | 2010-01-12 | 2013-09-24 | GE Lighting Solutions, LLC | Transparent thermally conductive polymer composites for light source thermal management |
US8518473B2 (en) | 2010-01-27 | 2013-08-27 | Rensselaer Polytechnic Institute | Nanofilled polymeric nanocomposites with tunable index of refraction |
BR112012018244A2 (pt) | 2010-02-02 | 2016-05-03 | Applied Nanostructured Sols | materiais de fibra infundidos com nanotubo de carbono contendo nanotubos de carbono alinhados em paralelo, métodos para produção dos mesmos e materiais compósitos derivados dos mesmos |
WO2011096898A1 (en) * | 2010-02-05 | 2011-08-11 | Nanyang Technological University | Method of modifying electrical properties of carbon nanotubes using nanoparticles |
KR101724064B1 (ko) * | 2010-02-18 | 2017-04-10 | 삼성전자주식회사 | 전도성 탄소나노튜브-금속 복합체 잉크 |
KR101643760B1 (ko) * | 2010-02-19 | 2016-08-01 | 삼성전자주식회사 | 전도성 섬유 및 그의 용도 |
US8920682B2 (en) * | 2010-03-19 | 2014-12-30 | Eastern Michigan University | Nanoparticle dispersions with ionic liquid-based stabilizers |
US20110265979A1 (en) * | 2010-04-30 | 2011-11-03 | Sihai Chen | Thermal interface materials with good reliability |
EP2585402A2 (en) * | 2010-06-22 | 2013-05-01 | Designed Nanotubes, LLC | Modified carbon nanotubes, methods for production thereof and products obtained therefrom |
JP5670716B2 (ja) * | 2010-06-25 | 2015-02-18 | ビジョン開発株式会社 | ダイヤモンド微粒子を含有するポリエステル樹脂組成物の製造方法 |
US8895962B2 (en) * | 2010-06-29 | 2014-11-25 | Nanogram Corporation | Silicon/germanium nanoparticle inks, laser pyrolysis reactors for the synthesis of nanoparticles and associated methods |
CN102336942B (zh) * | 2010-07-22 | 2014-06-11 | 合肥杰事杰新材料股份有限公司 | 一种聚酯/聚乙烯/碳纳米管三元复合材料及其制备方法 |
US8431048B2 (en) * | 2010-07-23 | 2013-04-30 | International Business Machines Corporation | Method and system for alignment of graphite nanofibers for enhanced thermal interface material performance |
US8816007B2 (en) * | 2010-07-28 | 2014-08-26 | Fpinnovations | Phenol-formaldehyde polymer with carbon nanotubes, a method of producing same, and products derived therefrom |
US9017854B2 (en) | 2010-08-30 | 2015-04-28 | Applied Nanostructured Solutions, Llc | Structural energy storage assemblies and methods for production thereof |
US8608992B2 (en) | 2010-09-24 | 2013-12-17 | The Board Of Trustees Of The University Of Illinois | Carbon nanofibers derived from polymer nanofibers and method of producing the nanofibers |
KR101804000B1 (ko) * | 2010-11-03 | 2018-01-10 | 헤레우스 프레셔스 메탈스 게엠베하 운트 코. 카게 | 유기 용매에 pedot 분산액 |
KR101234257B1 (ko) * | 2010-12-08 | 2013-02-18 | 금오공과대학교 산학협력단 | 아라미드/그래핀 복합체 및 그 제조 방법 |
KR101333587B1 (ko) * | 2010-12-21 | 2013-11-28 | 제일모직주식회사 | 낮은 열팽창계수를 갖는 폴리아미드계 수지 조성물 |
RU2465286C2 (ru) * | 2011-01-27 | 2012-10-27 | Закрытое акционерное общество "СИБУР Холдинг" (ЗАО "СИБУР Холдинг") | Материал, содержащий полидициклопентадиен, и способ его получения (варианты) |
WO2012112435A1 (en) * | 2011-02-14 | 2012-08-23 | William Marsh Rice University | Graphene nanoribbon composites and methods of making the same |
KR101373575B1 (ko) * | 2011-03-31 | 2014-03-13 | 고려대학교 산학협력단 | 다이아몬드가 증착된 나노선 및 이의 제조방법 |
FI20110232L (fi) * | 2011-07-05 | 2013-01-11 | Hafmex Oy | Lämmitettävä tuulivoimalan roottori |
WO2013020106A1 (en) * | 2011-08-03 | 2013-02-07 | Anchor Science Llc | Dynamic thermal interface material |
JP6096190B2 (ja) * | 2011-08-16 | 2017-03-15 | シンセス・ゲーエムベーハーSynthes GmbH | 熱可塑性多層物品 |
KR101378949B1 (ko) * | 2011-09-23 | 2014-04-18 | 한국과학기술원 | 공중합체로 기능화된 나노 입자를 포함하는 주형 고분자와 전도성 고분자 복합재 조성물 |
KR101278161B1 (ko) | 2011-10-27 | 2013-06-27 | 금오공과대학교 산학협력단 | 에폭시수지 나노복합재료 및 그 제조 방법 |
RU2490204C1 (ru) * | 2011-12-19 | 2013-08-20 | Федеральное государственное автономное образовательное учреждение высшего профессионального образования "Казанский (Приволжский) Федеральный Университет" (ФГАОУ ВПО КФУ) | Способ получения композиций на основе углеродных нанотрубок и полиолефинов |
US9957379B2 (en) * | 2012-01-03 | 2018-05-01 | Lockheed Martin Corporation | Structural composite materials with high strain capability |
MX364402B (es) * | 2012-01-27 | 2019-04-24 | Univ Rice William M | Fluidos de perforacion que incorporan nanocintas de carbono magnetico y nanocintas de carbono funcionalizado magnetico y metodos de uso de las mismas. |
US9500355B2 (en) | 2012-05-04 | 2016-11-22 | GE Lighting Solutions, LLC | Lamp with light emitting elements surrounding active cooling device |
US20150240658A1 (en) * | 2012-10-01 | 2015-08-27 | United Technologies Corporation | Carbon Nanotubes for Increasing Vibration Damping In Polymer Matrix Composite Containment Cases for Aircraft Engines |
US9090756B2 (en) | 2012-11-30 | 2015-07-28 | The Goodyear Tire & Rubber Company | Tire with component comprised of rubber composition containing silica and graphene platelet reinforcement |
TWI481644B (zh) * | 2012-12-11 | 2015-04-21 | Nat Univ Tsing Hua | 聚苯胺複合材料及其製造方法 |
MX361304B (es) * | 2012-12-20 | 2018-12-03 | Dow Global Technologies Llc | Componentes de compuestos polimericos para torres de comunicaciones inalambricas. |
GB2509173A (en) * | 2012-12-24 | 2014-06-25 | Mahle Int Gmbh | A sliding bearing |
KR101926808B1 (ko) * | 2012-12-28 | 2018-12-07 | 삼성전기주식회사 | 작업성이 우수한 수지 조성물, 절연필름 및 프리프레그 |
US9162530B2 (en) * | 2013-02-14 | 2015-10-20 | The Goodyear Tire & Rubber Company | Tire with rubber tread containing precipitated silica and functionalized carbon nanotubes |
US20140256204A1 (en) * | 2013-03-08 | 2014-09-11 | E I Du Pont De Nemours And Company | Method of coupling and aligning carbon nanotubes in a nonwoven sheet and aligned sheet formed therefrom |
RU2555859C2 (ru) * | 2013-03-26 | 2015-07-10 | Федеральное государственное бюджетное учреждение Национальный исследовательский центр "Курчатовский институт" | Однокамерный топливный элемент и способ получения проводящего нанокомпозитного материала для него |
JP6359081B2 (ja) * | 2013-04-18 | 2018-07-18 | ナショナル リサーチ カウンシル オブ カナダ | 窒化ホウ素ナノチューブ及びその製造方法 |
US9321245B2 (en) | 2013-06-24 | 2016-04-26 | Globalfoundries Inc. | Injection of a filler material with homogeneous distribution of anisotropic filler particles through implosion |
US9090757B2 (en) | 2013-07-15 | 2015-07-28 | The Goodyear Tire & Rubber Company | Preparation of rubber reinforced with at least one of graphene and carbon nanotubes with specialized coupling agent and tire with component |
ES2682360T3 (es) * | 2013-08-23 | 2018-09-20 | Lockheed Martin Corporation | Dispositivos electrónicos de alta potencia que contienen materiales de interfaz térmica a base de nanopartículas metálicas y métodos relacionados |
US20150064458A1 (en) * | 2013-08-28 | 2015-03-05 | Eaton Corporation | Functionalizing injection molded parts using nanofibers |
US9745499B2 (en) * | 2013-09-06 | 2017-08-29 | Korea Advanced Institute Of Science And Technology | Hexagonal boron nitride nanosheet/ceramic nanocomposite powder and producing method of the same, and hexagonal boron nitride nanosheet/ceramic nanocomposite materials and producing method of the same |
KR101634160B1 (ko) * | 2013-09-06 | 2016-06-28 | 한국과학기술원 | 육방정 질화붕소 나노시트/세라믹 나노 복합 분말 및 그의 제조 방법, 및 육방정 질화붕소/세라믹 나노 복합 소재 및 그의 제조 방법 |
CN103556450B (zh) * | 2013-11-20 | 2016-06-08 | 苏州东奇生物科技有限公司 | 一种阳离子交换用亲水型纳米纤维固相萃取材料制备方法 |
CN103614916B (zh) * | 2013-11-20 | 2016-02-17 | 苏州东奇生物科技有限公司 | 一种固相萃取用复合纳米纤维材料制备方法 |
US20150153687A1 (en) * | 2013-12-02 | 2015-06-04 | Xerox Corporation | Fuser member |
US9657397B2 (en) * | 2013-12-31 | 2017-05-23 | Lam Research Ag | Apparatus for treating surfaces of wafer-shaped articles |
US20150210811A1 (en) * | 2014-01-29 | 2015-07-30 | Korea Advanced Institute Of Science And Technology | Carbon nanomaterial, carbon nanomaterial-polymer composite material, carbon fiber-carbon nanomaterial-polymer composite material, and methods of preparing the same |
KR101709156B1 (ko) * | 2014-03-18 | 2017-02-22 | 서울대학교산학협력단 | 나노 복합재료 |
US9477190B2 (en) | 2014-04-14 | 2016-10-25 | Xerox Corporation | Fuser member |
US20170055339A1 (en) * | 2014-04-30 | 2017-02-23 | Rogers Corporation | Thermally conductive composites and methods of manufacture thereof, and articles containing the composites |
US10490521B2 (en) * | 2014-06-26 | 2019-11-26 | Taiwan Semiconductor Manufacturing Company, Ltd. | Advanced structure for info wafer warpage reduction |
US9482477B2 (en) * | 2014-07-28 | 2016-11-01 | Northrop Grumman Systems Corporation | Nano-thermal agents for enhanced interfacial thermal conductance |
US20160082774A1 (en) | 2014-09-23 | 2016-03-24 | The Goodyear Tire & Rubber Company | Tire with directional heat conductive conduit |
JP6677898B2 (ja) * | 2015-09-11 | 2020-04-08 | 株式会社豊田中央研究所 | 樹脂複合材料及びその製造方法 |
JP6560599B2 (ja) * | 2015-11-19 | 2019-08-14 | 積水化学工業株式会社 | 熱硬化性シート、硬化物シート及び積層体 |
US9493696B1 (en) | 2015-11-24 | 2016-11-15 | International Business Machines Corporation | Multiphase resins with reduced percolation threshold |
JP6899048B2 (ja) * | 2015-12-16 | 2021-07-07 | ナノサミット株式会社 | 新規なナノカーボン複合体 |
TWI671364B (zh) | 2015-12-30 | 2019-09-11 | 美商聖高拜陶器塑膠公司 | 改質氮化物顆粒、寡聚物官能化氮化物顆粒及基於聚合物之複合材料 |
CN105623264A (zh) * | 2016-04-06 | 2016-06-01 | 汤卓群 | 一种纳米改性有机聚合薄膜及其制备方法 |
CN105860969B (zh) * | 2016-05-13 | 2017-12-05 | 天津大学 | 一种提高碳量子点荧光性能的方法 |
US20170342844A1 (en) * | 2016-05-31 | 2017-11-30 | United Technologies Corporation | High Temperature Composites With Enhanced Matrix |
CN105949571A (zh) * | 2016-06-17 | 2016-09-21 | 无锡英普林纳米科技有限公司 | 一种纳米压印抗蚀剂 |
JP7088014B2 (ja) * | 2016-09-05 | 2022-06-21 | 日本電気株式会社 | 電磁波吸収材料 |
US10745569B2 (en) | 2016-10-23 | 2020-08-18 | Sepideh Pourhashem | Anti-corrosion nanocomposite coating |
US10934016B2 (en) * | 2016-12-12 | 2021-03-02 | Raytheon Technologies Corporation | Protective shield including hybrid nanofiber composite layers |
US20180199461A1 (en) * | 2017-01-09 | 2018-07-12 | Hamilton Sundstrand Corporation | Electronics thermal management |
US10968340B1 (en) | 2017-01-31 | 2021-04-06 | Eaton Intelligent Power Limited | Electrically conductive, high strength, high temperature polymer composite for additive manufacturing |
US10941258B2 (en) | 2017-03-24 | 2021-03-09 | The Board Of Trustees Of The University Of Alabama | Metal particle-chitin composite materials and methods of making thereof |
DE102017206744B9 (de) * | 2017-04-21 | 2023-01-12 | Infineon Technologies Ag | Mems package mit hoher wärmekapazität und verfahren zum herstellen selbiger |
US11391297B2 (en) | 2017-11-09 | 2022-07-19 | Pratt & Whitney Canada Corp. | Composite fan case with nanoparticles |
JP6939903B2 (ja) * | 2017-12-13 | 2021-09-22 | 日本電気株式会社 | 繊維状のカーボンナノホーン集合体の短尺化方法及び短尺化された繊維状のカーボンナノホーン集合体 |
CN112771190B (zh) * | 2018-09-19 | 2022-06-28 | 住友电气工业株式会社 | 立方氮化硼烧结体的制造方法、立方氮化硼烧结体和包括该立方氮化硼烧结体的切削工具 |
CN109608623A (zh) * | 2018-12-24 | 2019-04-12 | 山东省科学院新材料研究所 | 一种用于碳纳米管分散的间苯乙炔基高分子聚合物及其制备方法 |
CN109694647B (zh) * | 2018-12-26 | 2021-03-02 | 中国科学院兰州化学物理研究所 | 一种具有优异耐空间环境性能的长效固体润滑防护涂料 |
CN109970047B (zh) * | 2019-03-27 | 2022-08-26 | 昆明理工大学 | 一种由碳纳米角制备石墨烯量子点的方法 |
US11708276B2 (en) * | 2019-05-03 | 2023-07-25 | Uti Limited Partnership | Dispersion of bare nanoparticles in nonpolar solvents |
WO2020250165A1 (en) * | 2019-06-11 | 2020-12-17 | Bedimensional S.P.A. | Multifunctional product in the form of electrically conductive and/or electrically and/or magnetically polarizable and/or thermally conductive paste or ink or glue, method for the production thereof and use of said product |
US11881440B2 (en) * | 2020-02-21 | 2024-01-23 | Intel Corporation | Carbon based polymer thermal interface materials with polymer chain to carbon based fill particle bonds |
CN115461394A (zh) | 2020-02-25 | 2022-12-09 | 卡博特公司 | 用于导电和emi屏蔽应用的含有碳纳米结构体的基于有机硅的组合物 |
CN111534094B (zh) * | 2020-05-20 | 2021-02-12 | 吉林大学 | 一种聚酰亚胺薄膜及其制备方法和应用 |
US11587834B1 (en) * | 2020-06-29 | 2023-02-21 | Plasma-Therm Llc | Protective coating for plasma dicing |
KR20220054062A (ko) * | 2020-10-23 | 2022-05-02 | 한국전기연구원 | 탄소나노혼-고분자 복합체, 이를 이용한 전기 절연체 |
CN113831350B (zh) * | 2021-09-22 | 2023-08-04 | 同济大学 | 一种卟啉共价功能化Ti3C2Tx纳米片非线性纳米杂化材料及其制备与应用 |
Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE3118503A1 (de) * | 1981-05-09 | 1982-11-18 | Fa. J.S. Staedtler, 8500 Nürnberg | Behandelter graphit bzw. kohlenstoff, verfahren zu seiner herstellung, verfahren zu seiner weiterverarbeitung und daraus hergestellte gegenstaende |
US6187823B1 (en) * | 1998-10-02 | 2001-02-13 | University Of Kentucky Research Foundation | Solubilizing single-walled carbon nanotubes by direct reaction with amines and alkylaryl amines |
US20010010809A1 (en) * | 1998-10-02 | 2001-08-02 | Haddon Robert C. | Method of solubilizing single-walled carbon nanotubes in organic solutions |
US20020046872A1 (en) * | 2000-08-24 | 2002-04-25 | Smalley Richard E. | Polymer-wrapped single wall carbon nanotubes |
US20020054995A1 (en) * | 1999-10-06 | 2002-05-09 | Marian Mazurkiewicz | Graphite platelet nanostructures |
WO2002076888A1 (en) * | 2001-03-26 | 2002-10-03 | Ben-Gurion University Of The Negev | Method for the preparation of stable suspensions and powders of single carbon nanotubes |
US20030001141A1 (en) * | 2001-04-26 | 2003-01-02 | Yi Sun | Method for dissolving nanostructural materials |
Family Cites Families (167)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5165909A (en) | 1984-12-06 | 1992-11-24 | Hyperion Catalysis Int'l., Inc. | Carbon fibrils and method for producing same |
US5611964A (en) | 1984-12-06 | 1997-03-18 | Hyperion Catalysis International | Fibril filled molding compositions |
US4663230A (en) | 1984-12-06 | 1987-05-05 | Hyperion Catalysis International, Inc. | Carbon fibrils, method for producing same and compositions containing same |
US5707916A (en) | 1984-12-06 | 1998-01-13 | Hyperion Catalysis International, Inc. | Carbon fibrils |
US6464908B1 (en) | 1988-01-28 | 2002-10-15 | Hyperion Catalysis International, Inc. | Method of molding composites containing carbon fibrils |
WO1990014221A1 (en) | 1989-05-15 | 1990-11-29 | Hyperion Catalysis International | Surface treatment of carbon microfibers |
US5098771A (en) | 1989-07-27 | 1992-03-24 | Hyperion Catalysis International | Conductive coatings and inks |
US5204038A (en) | 1990-12-27 | 1993-04-20 | The Regents Of The University Of California | Process for forming polymers |
US5281406A (en) | 1992-04-22 | 1994-01-25 | Analytical Bio-Chemistry Laboratories, Inc. | Recovery of C60 and C70 buckminsterfullerenes from carbon soot by supercritical fluid extraction and their separation by adsorption chromatography |
JPH0822733B2 (ja) | 1993-08-04 | 1996-03-06 | 工業技術院長 | カーボンナノチューブの分離精製方法 |
JP2526408B2 (ja) | 1994-01-28 | 1996-08-21 | 工業技術院長 | カ―ボンナノチュ―ブの連続製造方法及び装置 |
US5866434A (en) | 1994-12-08 | 1999-02-02 | Meso Scale Technology | Graphitic nanotubes in luminescence assays |
US6203814B1 (en) * | 1994-12-08 | 2001-03-20 | Hyperion Catalysis International, Inc. | Method of making functionalized nanotubes |
WO1996028538A1 (en) | 1995-03-10 | 1996-09-19 | Meso Scale Technologies, Llc | Multi-array, multi-specific electrochemiluminescence testing |
US6140045A (en) | 1995-03-10 | 2000-10-31 | Meso Scale Technologies | Multi-array, multi-specific electrochemiluminescence testing |
US5627140A (en) | 1995-05-19 | 1997-05-06 | Nec Research Institute, Inc. | Enhanced flux pinning in superconductors by embedding carbon nanotubes with BSCCO materials |
US5824470A (en) | 1995-05-30 | 1998-10-20 | California Institute Of Technology | Method of preparing probes for sensing and manipulating microscopic environments and structures |
US6017390A (en) | 1996-07-24 | 2000-01-25 | The Regents Of The University Of California | Growth of oriented crystals at polymerized membranes |
WO1998005920A1 (en) | 1996-08-08 | 1998-02-12 | William Marsh Rice University | Macroscopically manipulable nanoscale devices made from nanotube assemblies |
US6180114B1 (en) | 1996-11-21 | 2001-01-30 | University Of Washington | Therapeutic delivery using compounds self-assembled into high axial ratio microstructures |
US5753088A (en) | 1997-02-18 | 1998-05-19 | General Motors Corporation | Method for making carbon nanotubes |
US6683783B1 (en) | 1997-03-07 | 2004-01-27 | William Marsh Rice University | Carbon fibers formed from single-wall carbon nanotubes |
US6770583B2 (en) | 1997-03-14 | 2004-08-03 | The United States Of America As Represented By The Secretary Of The Navy | Transistion metal containing ceramic with metal nanoparticles |
US6205016B1 (en) | 1997-06-04 | 2001-03-20 | Hyperion Catalysis International, Inc. | Fibril composite electrode for electrochemical capacitors |
US5968650A (en) | 1997-11-03 | 1999-10-19 | Hyperion Catalysis International, Inc. | Three dimensional interpenetrating networks of macroscopic assemblages of randomly oriented carbon fibrils and organic polymers |
US6113819A (en) | 1997-11-03 | 2000-09-05 | Hyperion Catalysis International, Inc. | Three dimensional interpenetrating networks of macroscopic assemblages of oriented carbon fibrils and organic polymers |
US6276214B1 (en) | 1997-12-26 | 2001-08-21 | Toyoaki Kimura | Strain sensor functioned with conductive particle-polymer composites |
ES2205746T3 (es) | 1998-04-09 | 2004-05-01 | Horcom Limited | Composicion a base de nanotubos y de un compuesto organico. |
DE69921472T2 (de) * | 1998-05-07 | 2006-02-02 | Commissariat à l'Energie Atomique | Verfahren zur fixierung und selbstorganisation von biologischen macromolekulen auf kohlenstoffnanoröhren und deren verwendung |
US6287765B1 (en) | 1998-05-20 | 2001-09-11 | Molecular Machines, Inc. | Methods for detecting and identifying single molecules |
US6426134B1 (en) * | 1998-06-30 | 2002-07-30 | E. I. Du Pont De Nemours And Company | Single-wall carbon nanotube-polymer composites |
US7282260B2 (en) * | 1998-09-11 | 2007-10-16 | Unitech, Llc | Electrically conductive and electromagnetic radiation absorptive coating compositions and the like |
US6835366B1 (en) | 1998-09-18 | 2004-12-28 | William Marsh Rice University | Chemical derivatization of single-wall carbon nanotubes to facilitate solvation thereof, and use of derivatized nanotubes |
KR100775878B1 (ko) | 1998-09-18 | 2007-11-13 | 윌리엄 마쉬 라이스 유니버시티 | 단일벽 탄소 나노튜브의 용매화를 용이하게 하기 위한 단일벽 탄소 나노튜브의 화학적 유도체화 및 그 유도체화된 나노튜브의 사용 방법 |
US6630772B1 (en) | 1998-09-21 | 2003-10-07 | Agere Systems Inc. | Device comprising carbon nanotube field emitter structure and process for forming device |
JP4409003B2 (ja) | 1998-09-24 | 2010-02-03 | 三星エスディアイ株式会社 | フィールドエミッションディスプレイ用エレクトロンエミッタ組成物及びこれを利用したエレクトロンエミッタの製造方法 |
US6597090B1 (en) | 1998-09-28 | 2003-07-22 | Xidex Corporation | Method for manufacturing carbon nanotubes as functional elements of MEMS devices |
US6146227A (en) | 1998-09-28 | 2000-11-14 | Xidex Corporation | Method for manufacturing carbon nanotubes as functional elements of MEMS devices |
US6331262B1 (en) | 1998-10-02 | 2001-12-18 | University Of Kentucky Research Foundation | Method of solubilizing shortened single-walled carbon nanotubes in organic solutions |
US6368569B1 (en) | 1998-10-02 | 2002-04-09 | University Of Kentucky Research Foundation | Method of solubilizing unshortened carbon nanotubes in organic solutions |
US6531513B2 (en) | 1998-10-02 | 2003-03-11 | University Of Kentucky Research Foundation | Method of solubilizing carbon nanotubes in organic solutions |
US6284832B1 (en) | 1998-10-23 | 2001-09-04 | Pirelli Cables And Systems, Llc | Crosslinked conducting polymer composite materials and method of making same |
US6432320B1 (en) | 1998-11-02 | 2002-08-13 | Patrick Bonsignore | Refrigerant and heat transfer fluid additive |
JP2003530610A (ja) | 1999-01-21 | 2003-10-14 | サウス カロライナ大学 | 分子コンピュータ |
US6555945B1 (en) | 1999-02-25 | 2003-04-29 | Alliedsignal Inc. | Actuators using double-layer charging of high surface area materials |
US6280697B1 (en) | 1999-03-01 | 2001-08-28 | The University Of North Carolina-Chapel Hill | Nanotube-based high energy material and method |
US6315956B1 (en) | 1999-03-16 | 2001-11-13 | Pirelli Cables And Systems Llc | Electrochemical sensors made from conductive polymer composite materials and methods of making same |
US6299812B1 (en) | 1999-08-16 | 2001-10-09 | The Board Of Regents Of The University Of Oklahoma | Method for forming a fibers/composite material having an anisotropic structure |
US6741019B1 (en) | 1999-10-18 | 2004-05-25 | Agere Systems, Inc. | Article comprising aligned nanowires |
US6790425B1 (en) | 1999-10-27 | 2004-09-14 | Wiliam Marsh Rice University | Macroscopic ordered assembly of carbon nanotubes |
US6352782B2 (en) | 1999-12-01 | 2002-03-05 | General Electric Company | Poly(phenylene ether)-polyvinyl thermosetting resin |
US6599961B1 (en) | 2000-02-01 | 2003-07-29 | University Of Kentucky Research Foundation | Polymethylmethacrylate augmented with carbon nanotubes |
US6991528B2 (en) * | 2000-02-17 | 2006-01-31 | Applied Materials, Inc. | Conductive polishing article for electrochemical mechanical polishing |
EP1261862A2 (en) | 2000-02-22 | 2002-12-04 | California Institute of Technology | Development of a gel-free molecular sieve based on self-assembled nano-arrays |
US6610351B2 (en) | 2000-04-12 | 2003-08-26 | Quantag Systems, Inc. | Raman-active taggants and their recognition |
JP2003533276A (ja) * | 2000-05-16 | 2003-11-11 | レンセラール ポリテクニック インスティチュート | 生物医学的適用のための電気伝導性ナノ複合材料 |
US6524466B1 (en) | 2000-07-18 | 2003-02-25 | Applied Semiconductor, Inc. | Method and system of preventing fouling and corrosion of biomedical devices and structures |
US6709566B2 (en) | 2000-07-25 | 2004-03-23 | The Regents Of The University Of California | Method for shaping a nanotube and a nanotube shaped thereby |
US6982174B2 (en) * | 2000-08-15 | 2006-01-03 | The Trustees Of The University Of Pennsylvania | Directed assembly of nanometer-scale molecular devices |
WO2002039051A2 (en) | 2000-08-23 | 2002-05-16 | Cynthia A Kuper | METHOD FOR UTILIZING SOL-GEL PROCESSING IN THE PRODUCTION OF A MACROSCOPIC TWO OR THREE DIMENSIONALLY ORDERED ARRAY OF SINGLE WALL NANOTUBES (SWNTs) |
EP1186572A1 (en) * | 2000-09-06 | 2002-03-13 | Facultés Universitaires Notre-Dame de la Paix | Short carbon nanotubes and method for the production thereof |
US20050001100A1 (en) * | 2000-09-19 | 2005-01-06 | Kuang Hsi-Wu | Reinforced foam covering for cryogenic fuel tanks |
US20040018139A1 (en) * | 2000-09-25 | 2004-01-29 | Xidex Corporation | Nanotube apparatus |
US6861481B2 (en) | 2000-09-29 | 2005-03-01 | Solvay Engineered Polymers, Inc. | Ionomeric nanocomposites and articles therefrom |
KR100395902B1 (ko) | 2000-11-01 | 2003-08-25 | 학교법인 서강대학교 | 제올라이트 또는 유사분자체의 패턴화된 단층 또는 다층복합체의 제조 방법 및 이에 의해 제조된 복합체 |
US6682677B2 (en) | 2000-11-03 | 2004-01-27 | Honeywell International Inc. | Spinning, processing, and applications of carbon nanotube filaments, ribbons, and yarns |
US20040018371A1 (en) * | 2002-04-12 | 2004-01-29 | Si Diamond Technology, Inc. | Metallization of carbon nanotubes for field emission applications |
US6783746B1 (en) | 2000-12-12 | 2004-08-31 | Ashland, Inc. | Preparation of stable nanotube dispersions in liquids |
US6634321B2 (en) | 2000-12-14 | 2003-10-21 | Quantum Fuel Systems Technologies Worldwide, Inc. | Systems and method for storing hydrogen |
WO2002093738A2 (en) | 2001-01-19 | 2002-11-21 | California Institute Of Technology | Carbon nanobimorph actuator and sensor |
EP1373430A4 (en) | 2001-01-30 | 2007-04-25 | Mat & Electrochem Res Corp | CARBON MATERIALS, OF A NANOMETRIC SIZE, FOR IMPROVING THERMAL TRANSFER IN FLUIDS |
US6782154B2 (en) | 2001-02-12 | 2004-08-24 | Rensselaer Polytechnic Institute | Ultrafast all-optical switch using carbon nanotube polymer composites |
JP3991602B2 (ja) | 2001-03-02 | 2007-10-17 | 富士ゼロックス株式会社 | カーボンナノチューブ構造体の製造方法、配線部材の製造方法および配線部材 |
US6803840B2 (en) | 2001-03-30 | 2004-10-12 | California Institute Of Technology | Pattern-aligned carbon nanotube growth and tunable resonator apparatus |
EP1384322A1 (en) | 2001-03-30 | 2004-01-28 | California Institute Of Technology | Carbon nanotube array rf filter |
US7160531B1 (en) * | 2001-05-08 | 2007-01-09 | University Of Kentucky Research Foundation | Process for the continuous production of aligned carbon nanotubes |
US6723299B1 (en) | 2001-05-17 | 2004-04-20 | Zyvex Corporation | System and method for manipulating nanotubes |
US6872681B2 (en) | 2001-05-18 | 2005-03-29 | Hyperion Catalysis International, Inc. | Modification of nanotubes oxidation with peroxygen compounds |
CA2450014A1 (en) | 2001-06-08 | 2002-12-19 | Eikos, Inc. | Nanocomposite dielectrics |
US6824974B2 (en) | 2001-06-11 | 2004-11-30 | Genorx, Inc. | Electronic detection of biological molecules using thin layers |
WO2003001889A2 (en) * | 2001-06-29 | 2003-01-09 | Meso Scale Technologies, Llc. | Assay plates reader systems and methods for luminescence test measurements |
US6878361B2 (en) * | 2001-07-10 | 2005-04-12 | Battelle Memorial Institute | Production of stable aqueous dispersions of carbon nanotubes |
US6896864B2 (en) * | 2001-07-10 | 2005-05-24 | Battelle Memorial Institute | Spatial localization of dispersed single walled carbon nanotubes into useful structures |
US6783702B2 (en) | 2001-07-11 | 2004-08-31 | Hyperion Catalysis International, Inc. | Polyvinylidene fluoride composites and methods for preparing same |
US6670179B1 (en) | 2001-08-01 | 2003-12-30 | University Of Kentucky Research Foundation | Molecular functionalization of carbon nanotubes and use as substrates for neuronal growth |
US6669918B2 (en) | 2001-08-07 | 2003-12-30 | The Mitre Corporation | Method for bulk separation of single-walled tubular fullerenes based on chirality |
KR100438408B1 (ko) * | 2001-08-16 | 2004-07-02 | 한국과학기술원 | 금속간의 치환 반응을 이용한 코어-쉘 구조 및 혼합된합금 구조의 금속 나노 입자의 제조 방법과 그 응용 |
US6680016B2 (en) * | 2001-08-17 | 2004-01-20 | University Of Dayton | Method of forming conductive polymeric nanocomposite materials |
JP2003073591A (ja) | 2001-09-03 | 2003-03-12 | Fuji Photo Film Co Ltd | インク組成物およびインクジェット記録方法 |
US6758891B2 (en) | 2001-10-09 | 2004-07-06 | Degussa Ag | Carbon-containing material |
JP3654236B2 (ja) | 2001-11-07 | 2005-06-02 | 株式会社日立製作所 | 電極デバイスの製造方法 |
JP3579689B2 (ja) * | 2001-11-12 | 2004-10-20 | 独立行政法人 科学技術振興機構 | 吸熱性反応を利用した機能性ナノ材料の製造方法 |
JP3453377B2 (ja) * | 2002-01-08 | 2003-10-06 | 科学技術振興事業団 | カーボンナノチューブ・カーボンナノホーン複合体とその製造方法 |
US20040029706A1 (en) * | 2002-02-14 | 2004-02-12 | Barrera Enrique V. | Fabrication of reinforced composite material comprising carbon nanotubes, fullerenes, and vapor-grown carbon fibers for thermal barrier materials, structural ceramics, and multifunctional nanocomposite ceramics |
JP3922039B2 (ja) | 2002-02-15 | 2007-05-30 | 株式会社日立製作所 | 電磁波吸収材料及びそれを用いた各種製品 |
JP4208722B2 (ja) * | 2002-03-04 | 2009-01-14 | ウィリアム・マーシュ・ライス・ユニバーシティ | 単層カーボンナノチューブを分離する方法 |
US6805801B1 (en) | 2002-03-13 | 2004-10-19 | Novellus Systems, Inc. | Method and apparatus to remove additives and contaminants from a supercritical processing solution |
WO2003078317A1 (en) * | 2002-03-14 | 2003-09-25 | Carbon Nanotechnologies, Inc. | Composite materials comprising polar polyers and single-wall carbon naotubes |
EP1349179A1 (en) * | 2002-03-18 | 2003-10-01 | ATOFINA Research | Conductive polyolefins with good mechanical properties |
US6774333B2 (en) | 2002-03-26 | 2004-08-10 | Intel Corporation | Method and system for optically sorting and/or manipulating carbon nanotubes |
KR20040101200A (ko) * | 2002-04-08 | 2004-12-02 | 윌리엄 마쉬 라이스 유니버시티 | 불소화를 이용한 단일-장벽 탄소 나노튜브의 절단 방법 |
US6975063B2 (en) * | 2002-04-12 | 2005-12-13 | Si Diamond Technology, Inc. | Metallization of carbon nanotubes for field emission applications |
DE10217362B4 (de) | 2002-04-18 | 2004-05-13 | Infineon Technologies Ag | Gezielte Abscheidung von Nanoröhren |
AU2003226428A1 (en) * | 2002-04-18 | 2003-11-03 | Northwestern University | Encapsulation of nanotubes via self-assembled nanostructures |
US6905667B1 (en) * | 2002-05-02 | 2005-06-14 | Zyvex Corporation | Polymer and method for using the polymer for noncovalently functionalizing nanotubes |
US20040034177A1 (en) * | 2002-05-02 | 2004-02-19 | Jian Chen | Polymer and method for using the polymer for solubilizing nanotubes |
US20030215816A1 (en) * | 2002-05-20 | 2003-11-20 | Narayan Sundararajan | Method for sequencing nucleic acids by observing the uptake of nucleotides modified with bulky groups |
US7438953B2 (en) * | 2002-06-07 | 2008-10-21 | The Board Of Regents For Oklahoma State University | Preparation of the layer-by-layer assembled materials from dispersions of highly anisotropic colloids |
US7029598B2 (en) * | 2002-06-19 | 2006-04-18 | Fuji Photo Film Co., Ltd. | Composite material for piezoelectric transduction |
US7153903B1 (en) * | 2002-06-19 | 2006-12-26 | The Board Of Regents Of The University Of Oklahoma | Carbon nanotube-filled composites prepared by in-situ polymerization |
US6852410B2 (en) | 2002-07-01 | 2005-02-08 | Georgia Tech Research Corporation | Macroscopic fiber comprising single-wall carbon nanotubes and acrylonitrile-based polymer and process for making the same |
US20040007528A1 (en) * | 2002-07-03 | 2004-01-15 | The Regents Of The University Of California | Intertwined, free-standing carbon nanotube mesh for use as separation, concentration, and/or filtration medium |
ITTO20020643A1 (it) * | 2002-07-23 | 2004-01-23 | Fiat Ricerche | Pila a combustibile ad alcool diretto e relativo metodo di realizzazione |
US8999200B2 (en) * | 2002-07-23 | 2015-04-07 | Sabic Global Technologies B.V. | Conductive thermoplastic composites and methods of making |
US7358121B2 (en) * | 2002-08-23 | 2008-04-15 | Intel Corporation | Tri-gate devices and methods of fabrication |
JP4120315B2 (ja) | 2002-08-22 | 2008-07-16 | 富士ゼロックス株式会社 | 光スイッチングシステム |
US6843850B2 (en) | 2002-08-23 | 2005-01-18 | International Business Machines Corporation | Catalyst-free growth of single-wall carbon nanotubes |
US20040036056A1 (en) * | 2002-08-26 | 2004-02-26 | Shea Lawrence E. | Non-formaldehyde reinforced thermoset plastic composites |
US6660227B2 (en) * | 2002-09-20 | 2003-12-09 | Innovatek Corporation | Device and method for detecting, isolating and eliminating hazardous microbiological polluting agents |
US6798127B2 (en) | 2002-10-09 | 2004-09-28 | Nano-Proprietary, Inc. | Enhanced field emission from carbon nanotubes mixed with particles |
US6805642B2 (en) | 2002-11-12 | 2004-10-19 | Acushnet Company | Hybrid golf club shaft |
US6790790B1 (en) | 2002-11-22 | 2004-09-14 | Advanced Micro Devices, Inc. | High modulus filler for low k materials |
JP2006505483A (ja) * | 2002-11-26 | 2006-02-16 | カーボン ナノテクノロジーズ インコーポレーテッド | カーボンナノチューブ微粒子、組成物及びその使用法 |
US6746971B1 (en) | 2002-12-05 | 2004-06-08 | Advanced Micro Devices, Inc. | Method of forming copper sulfide for memory cell |
US6770905B1 (en) | 2002-12-05 | 2004-08-03 | Advanced Micro Devices, Inc. | Implantation for the formation of CuX layer in an organic memory device |
US6773954B1 (en) | 2002-12-05 | 2004-08-10 | Advanced Micro Devices, Inc. | Methods of forming passive layers in organic memory cells |
DE60239138D1 (de) * | 2002-12-12 | 2011-03-24 | Sony Deutschland Gmbh | Lösliche Kohlenstoff-Nanoröhren |
EP1577352A4 (en) * | 2002-12-25 | 2010-06-16 | Fuji Xerox Co Ltd | LIQUID MIXTURE, CONSTRUCTION AND METHOD FOR PRODUCING A CONSTRUCTION |
US6875274B2 (en) | 2003-01-13 | 2005-04-05 | The Research Foundation Of State University Of New York | Carbon nanotube-nanocrystal heterostructures and methods of making the same |
US6656763B1 (en) | 2003-03-10 | 2003-12-02 | Advanced Micro Devices, Inc. | Spin on polymers for organic memory devices |
JP3973662B2 (ja) * | 2003-03-31 | 2007-09-12 | 富士通株式会社 | カーボンナノチューブ製造方法 |
US6825060B1 (en) | 2003-04-02 | 2004-11-30 | Advanced Micro Devices, Inc. | Photosensitive polymeric memory elements |
US20050008919A1 (en) * | 2003-05-05 | 2005-01-13 | Extrand Charles W. | Lyophilic fuel cell component |
US6842328B2 (en) | 2003-05-30 | 2005-01-11 | Joachim Hossick Schott | Capacitor and method for producing a capacitor |
US7169329B2 (en) * | 2003-07-07 | 2007-01-30 | The Research Foundation Of State University Of New York | Carbon nanotube adducts and methods of making the same |
TWI297709B (en) * | 2003-07-08 | 2008-06-11 | Canon Kk | Lens barrel |
US7259039B2 (en) * | 2003-07-09 | 2007-08-21 | Spansion Llc | Memory device and methods of using and making the device |
JP4927319B2 (ja) * | 2003-07-24 | 2012-05-09 | 韓国科学技術園 | 高密度カーボンナノチューブフィルムまたはパターンを用いたバイオチップの製造方法 |
JP2005050669A (ja) * | 2003-07-28 | 2005-02-24 | Tdk Corp | 電極、及び、それを用いた電気化学素子 |
US20050029498A1 (en) * | 2003-08-08 | 2005-02-10 | Mark Elkovitch | Electrically conductive compositions and method of manufacture thereof |
US7026432B2 (en) * | 2003-08-12 | 2006-04-11 | General Electric Company | Electrically conductive compositions and method of manufacture thereof |
JP4583044B2 (ja) * | 2003-08-14 | 2010-11-17 | 東芝モバイルディスプレイ株式会社 | 液晶表示装置 |
US7182886B2 (en) * | 2003-08-16 | 2007-02-27 | General Electric Company | Poly (arylene ether)/polyamide composition |
US7166243B2 (en) * | 2003-08-16 | 2007-01-23 | General Electric Company | Reinforced poly(arylene ether)/polyamide composition |
US7195721B2 (en) * | 2003-08-18 | 2007-03-27 | Gurin Michael H | Quantum lilypads and amplifiers and methods of use |
US7220818B2 (en) * | 2003-08-20 | 2007-05-22 | The Regents Of The University Of California | Noncovalent functionalization of nanotubes |
JP2005072209A (ja) * | 2003-08-22 | 2005-03-17 | Fuji Xerox Co Ltd | 抵抗素子、その製造方法およびサーミスタ |
US6989325B2 (en) * | 2003-09-03 | 2006-01-24 | Industrial Technology Research Institute | Self-assembled nanometer conductive bumps and method for fabricating |
US7759413B2 (en) * | 2003-10-30 | 2010-07-20 | The Trustees Of The University Of Pennsylvania | Dispersion method |
US20060029537A1 (en) * | 2003-11-20 | 2006-02-09 | Xiefei Zhang | High tensile strength carbon nanotube film and process for making the same |
KR100557338B1 (ko) * | 2003-11-27 | 2006-03-06 | 한국과학기술원 | 자기조립 물질로 랩핑된 탄소나노튜브의 제조방법 |
MXPA06006805A (es) * | 2004-01-09 | 2006-12-19 | Olga Matarredona | Pastas de nanotubo de carbono y metodos de uso. |
CN1954028A (zh) * | 2004-04-13 | 2007-04-25 | 塞威公司 | 模块式聚(亚苯基亚乙炔基)的合成方法以及微调它们的电子性能以实现纳米材料的官能化 |
CN100595950C (zh) * | 2004-06-10 | 2010-03-24 | 加利福尼亚技术学院 | 制造固体酸燃料电池膜电极组件的生产工艺 |
US7282294B2 (en) * | 2004-07-02 | 2007-10-16 | General Electric Company | Hydrogen storage-based rechargeable fuel cell system and method |
US20060014155A1 (en) * | 2004-07-16 | 2006-01-19 | Wisconsin Alumni Research Foundation | Methods for the production of sensor arrays using electrically addressable electrodes |
US7094467B2 (en) * | 2004-07-20 | 2006-08-22 | Heping Zhang | Antistatic polymer monofilament, method for making an antistatic polymer monofilament for the production of spiral fabrics and spiral fabrics formed with such monofilaments |
US20060016552A1 (en) * | 2004-07-20 | 2006-01-26 | George Fischer Sloane, Inc. | Electrofusion pipe-fitting joining system and method utilizing conductive polymeric resin |
US20060025515A1 (en) * | 2004-07-27 | 2006-02-02 | Mainstream Engineering Corp. | Nanotube composites and methods for producing |
US20060032702A1 (en) * | 2004-07-29 | 2006-02-16 | Oshkosh Truck Corporation | Composite boom assembly |
US7189455B2 (en) * | 2004-08-02 | 2007-03-13 | The Research Foundation Of State University Of New York | Fused carbon nanotube-nanocrystal heterostructures and methods of making the same |
US20060027499A1 (en) * | 2004-08-05 | 2006-02-09 | Banaras Hindu University | Carbon nanotube filter |
US7704422B2 (en) * | 2004-08-16 | 2010-04-27 | Electromaterials, Inc. | Process for producing monolithic porous carbon disks from aromatic organic precursors |
US20060036045A1 (en) * | 2004-08-16 | 2006-02-16 | The Regents Of The University Of California | Shape memory polymers |
US7296576B2 (en) * | 2004-08-18 | 2007-11-20 | Zyvex Performance Materials, Llc | Polymers for enhanced solubility of nanomaterials, compositions and methods therefor |
US20060040381A1 (en) * | 2004-08-20 | 2006-02-23 | Board Of Trustees Of The University Of Arkansas | Surface-modified single-walled carbon nanotubes and methods of detecting a chemical compound using same |
US7964159B2 (en) * | 2005-07-08 | 2011-06-21 | The Trustees Of The University Of Pennsylvania | Nanotube-based sensors and probes |
-
2004
- 2004-05-21 US US10/850,721 patent/US7479516B2/en active Active
- 2004-05-21 KR KR1020057022277A patent/KR100827861B1/ko active IP Right Grant
- 2004-05-21 CN CNA2004800181603A patent/CN1813023A/zh active Pending
- 2004-05-21 GB GB0523751A patent/GB2421506B/en not_active Expired - Fee Related
- 2004-05-21 WO PCT/US2004/016226 patent/WO2004106420A2/en active Application Filing
- 2004-05-21 JP JP2006533339A patent/JP2007516314A/ja active Pending
Patent Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE3118503A1 (de) * | 1981-05-09 | 1982-11-18 | Fa. J.S. Staedtler, 8500 Nürnberg | Behandelter graphit bzw. kohlenstoff, verfahren zu seiner herstellung, verfahren zu seiner weiterverarbeitung und daraus hergestellte gegenstaende |
US6187823B1 (en) * | 1998-10-02 | 2001-02-13 | University Of Kentucky Research Foundation | Solubilizing single-walled carbon nanotubes by direct reaction with amines and alkylaryl amines |
US20010010809A1 (en) * | 1998-10-02 | 2001-08-02 | Haddon Robert C. | Method of solubilizing single-walled carbon nanotubes in organic solutions |
US20020054995A1 (en) * | 1999-10-06 | 2002-05-09 | Marian Mazurkiewicz | Graphite platelet nanostructures |
US20020046872A1 (en) * | 2000-08-24 | 2002-04-25 | Smalley Richard E. | Polymer-wrapped single wall carbon nanotubes |
US20020048632A1 (en) * | 2000-08-24 | 2002-04-25 | Smalley Richard E. | Polymer-wrapped single wall carbon nanotubes |
WO2002076888A1 (en) * | 2001-03-26 | 2002-10-03 | Ben-Gurion University Of The Negev | Method for the preparation of stable suspensions and powders of single carbon nanotubes |
US20030001141A1 (en) * | 2001-04-26 | 2003-01-02 | Yi Sun | Method for dissolving nanostructural materials |
Non-Patent Citations (2)
Title |
---|
C.J.BRABEC, A.CRAVINO, G.ZERZA, N.C.SARICIFTCI, R.KIEBOOMS, D.VANDERZANDE, J.C.HUMMELEN: "Photoactive blends of poly(para-phenylenevinylene) (PPV) with methanofullerenes from a novel precursor: photophysics and device performance" JOURNAL OF CHEMICAL PHYSICS, vol. 105, 31 January 2001 (2001-01-31), pages 1528-1536, XP002301150 * |
HIRSCH A: "FUNCTIONALIZATION OF SINGLE-WALLED CARBON NANOTUBES" ANGEWANDTE CHEMIE. INTERNATIONAL EDITION, VERLAG CHEMIE. WEINHEIM, DE, vol. 41, no. 11, 2002, pages 1853-1859, XP001122544 ISSN: 0570-0833 * |
Cited By (73)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US8067073B2 (en) | 2004-03-25 | 2011-11-29 | Boston Scientific Scimed, Inc. | Thermoplastic medical device |
WO2005102406A1 (en) * | 2004-03-25 | 2005-11-03 | Boston Scientific Limited | Medical device comprising thermoplastic rigid-rod polymer |
WO2006028282A1 (en) * | 2004-09-09 | 2006-03-16 | Toyota Jidosha Kabushiki Kaisha | Nanoimprint mold, method of forming a nanopattern, and a resin-molded product |
CN100453955C (zh) * | 2005-01-07 | 2009-01-21 | 鸿富锦精密工业(深圳)有限公司 | 热管及其制造方法 |
US8092910B2 (en) | 2005-02-16 | 2012-01-10 | Dow Corning Toray Co., Ltd. | Reinforced silicone resin film and method of preparing same |
US8088449B2 (en) | 2005-02-16 | 2012-01-03 | Dow Corning Toray Co., Ltd. | Reinforced silicone resin film and method of preparing same |
KR101261254B1 (ko) | 2005-06-14 | 2013-05-07 | 다우 코닝 코포레이션 | 강화 실리콘 수지 필름 및 이의 제조방법 |
WO2007092032A3 (en) * | 2005-06-14 | 2007-09-27 | Dow Corning | Reinforced silicone resin film and method of preparing same |
WO2007092032A2 (en) * | 2005-06-14 | 2007-08-16 | Dow Corning Corporation | Reinforced silicone resin film and method of preparing same |
US8114314B2 (en) | 2005-07-20 | 2012-02-14 | Agency For Science, Technology And Research | Electroconductive curable resins |
WO2007011313A1 (en) * | 2005-07-20 | 2007-01-25 | Agency For Science, Technology And Research | Electroconductive curable resins |
US8334022B2 (en) | 2005-08-04 | 2012-12-18 | Dow Corning Corporation | Reinforced silicone resin film and method of preparing same |
JP2007146038A (ja) * | 2005-11-29 | 2007-06-14 | Teijin Ltd | 樹脂組成物およびその製造方法 |
JP2007146039A (ja) * | 2005-11-29 | 2007-06-14 | Teijin Ltd | 樹脂組成物およびその成形体 |
JP2007146081A (ja) * | 2005-11-30 | 2007-06-14 | Teijin Ltd | ポリカーボネート系樹脂成形体およびその製造法 |
US7604049B2 (en) | 2005-12-16 | 2009-10-20 | Schlumberger Technology Corporation | Polymeric composites, oilfield elements comprising same, and methods of using same in oilfield applications |
GB2433262A (en) * | 2005-12-16 | 2007-06-20 | Schlumberger Holdings | Nanocomposites for use in oilfield elements |
GB2433262B (en) * | 2005-12-16 | 2010-09-08 | Schlumberger Holdings | Nanocomposites for use in oilfield elements |
US8912268B2 (en) | 2005-12-21 | 2014-12-16 | Dow Corning Corporation | Silicone resin film, method of preparing same, and nanomaterial-filled silicone composition |
US8262939B2 (en) | 2005-12-30 | 2012-09-11 | Cheil Industries Inc. | Thermoplastic nanocomposite resin composite materials |
US8084532B2 (en) | 2006-01-19 | 2011-12-27 | Dow Corning Corporation | Silicone resin film, method of preparing same, and nanomaterial-filled silicone composition |
JP2007197554A (ja) * | 2006-01-26 | 2007-08-09 | Teijin Ltd | 立体規則性ポリアクリロニトリル系樹脂組成物およびその製造方法 |
JP2007197555A (ja) * | 2006-01-26 | 2007-08-09 | Teijin Ltd | 耐熱性樹脂組成物およびその製造方法 |
JP2007197594A (ja) * | 2006-01-27 | 2007-08-09 | Teijin Ltd | 強化フェノキシ樹脂系組成物およびその製造方法 |
JP2007197597A (ja) * | 2006-01-27 | 2007-08-09 | Teijin Ltd | 耐熱性、寸法安定性に優れた樹脂組成物およびその製造方法 |
JP2007197596A (ja) * | 2006-01-27 | 2007-08-09 | Teijin Ltd | 機械特性に優れた耐熱樹脂組成物およびその製造方法 |
JP2007197595A (ja) * | 2006-01-27 | 2007-08-09 | Teijin Ltd | 熱安定性に優れたポリエーテルスルホン系樹脂組成物及びその製造方法 |
JP2007217449A (ja) * | 2006-02-14 | 2007-08-30 | Teijin Ltd | 耐熱樹脂組成物およびその製造法 |
US8084097B2 (en) | 2006-02-20 | 2011-12-27 | Dow Corning Corporation | Silicone resin film, method of preparing same, and nanomaterial-filled silicone composition |
JP2007231031A (ja) * | 2006-02-27 | 2007-09-13 | National Institute For Materials Science | 複合フィルムとその製造方法 |
JP2007231155A (ja) * | 2006-03-01 | 2007-09-13 | Teijin Ltd | 耐熱樹脂組成物およびその製造法 |
JP2007254654A (ja) * | 2006-03-24 | 2007-10-04 | Teijin Ltd | 透明耐熱樹脂組成物およびその製造法 |
JP2007297463A (ja) * | 2006-04-28 | 2007-11-15 | Teijin Ltd | 強化樹脂組成物およびその製造法 |
JP2008007699A (ja) * | 2006-06-30 | 2008-01-17 | Teijin Ltd | 耐熱樹脂複合組成物及びその製造方法 |
JP2008031206A (ja) * | 2006-07-26 | 2008-02-14 | Teijin Ltd | 樹脂複合組成物及びその製造方法 |
WO2008034939A1 (en) * | 2006-09-04 | 2008-03-27 | Natucell Ay | Functionalized cellulose - carbon nanotube nanocomposites and hybride materials |
JP2008069194A (ja) * | 2006-09-12 | 2008-03-27 | Teijin Ltd | 耐熱性樹脂複合組成物及びその製造方法 |
WO2008046010A3 (en) * | 2006-10-11 | 2008-06-26 | Univ Florida | Electroactive polymers containing pendant pi-interacting/binding substituents, their carbon nanotube composites, and processes to form the same |
US8961830B2 (en) | 2006-10-11 | 2015-02-24 | University Of Florida Research Foundation, Inc. | Electroactive polymers containing pendant pi-interacting/binding substituents, their carbon nanotube composites, and processes to form the same |
EP2088122A4 (en) * | 2006-10-25 | 2010-01-13 | Kuraray Co | TRANSPARENT CONDUCTIVE FILM, TRANSPARENT ELECTRODE SUBSTRATE, AND PROCESS FOR PRODUCING LIQUID CRYSTAL ALIGNMENT FILM USING THE SAME, AND CARBON NANOTUBE AND PROCESS FOR PRODUCING THE SAME |
EP2088122A1 (en) * | 2006-10-25 | 2009-08-12 | Kuraray Co., Ltd. | Transparent conductive film, transparent electrode substrate and method for producing liquid crystal alignment film by using the same, and carbon nanotube and method for producing the same |
JP2008144046A (ja) * | 2006-12-11 | 2008-06-26 | Teijin Ltd | 耐熱性樹脂複合組成物及びその製造方法 |
WO2008082225A1 (en) * | 2006-12-29 | 2008-07-10 | Cheil Industries Inc. | Thermoplastic nanocomposite resin composition with improved scratch resistance |
US20100022706A1 (en) * | 2007-02-07 | 2010-01-28 | Bayer Materialscience Ag | Polyurethanes filled with carbon black and with a high dielectric constant breakdown strength |
US8273448B2 (en) | 2007-02-22 | 2012-09-25 | Dow Corning Corporation | Reinforced silicone resin films |
WO2008103221A1 (en) * | 2007-02-22 | 2008-08-28 | Dow Corning Corporation | Process for preparing conductive films and articles prepared using the process |
US8283025B2 (en) | 2007-02-22 | 2012-10-09 | Dow Corning Corporation | Reinforced silicone resin films |
JPWO2008146400A1 (ja) * | 2007-05-25 | 2010-08-19 | 帝人株式会社 | 樹脂組成物 |
JP2008291133A (ja) * | 2007-05-25 | 2008-12-04 | Teijin Ltd | 耐熱性に優れた樹脂組成物及びその製造方法 |
RU2476457C2 (ru) * | 2007-09-18 | 2013-02-27 | Шлюмбергер Технолоджи Б.В. | Нефтепромысловое устройство, нефтепромысловый элемент указанного устройства, содержащий функционализированные графеновые пластинки, способ осуществления нефтепромысловой операции и способ модификации функционализированных графеновых пластинок |
US8242181B2 (en) | 2007-10-12 | 2012-08-14 | Dow Corning Corporation | Aluminum oxide dispersion and method of preparing same |
WO2009059387A1 (en) * | 2007-11-08 | 2009-05-14 | Braskem S. A. | Process for the production of high tensile strength and low creep polymer yarns, high tensile strength and low creep polymer or copolymer yarns, and, the use of such yarns |
WO2009127281A1 (de) * | 2008-04-17 | 2009-10-22 | FRÖTEK Kunststofftechnik GmbH | Flügel einer flügelzellenpumpe oder eines flügelzellenkompressors |
US7931828B2 (en) * | 2008-05-22 | 2011-04-26 | Rolls-Royce Corporation | Gas turbine engine and method including composite structures with embedded integral electrically conductive paths |
WO2010057502A2 (en) * | 2008-11-24 | 2010-05-27 | Vestas Wind Systems A/S | Wind turbine blade comprising particle-reinforced bonding material |
WO2010057502A3 (en) * | 2008-11-24 | 2010-07-22 | Vestas Wind Systems A/S | Wind turbine blade comprising particle-reinforced bonding material |
GB2456484A (en) * | 2009-06-10 | 2009-07-22 | Vestas Wind Sys As | Wind turbine blade incorporating nanoclay |
US9613758B2 (en) | 2009-12-22 | 2017-04-04 | Pasi Moilanen | Fabrication and application of polymer-graphitic material nanocomposites and hybride materials |
WO2011076979A1 (en) * | 2009-12-22 | 2011-06-30 | Moilanen, Pasi | Fabrication and application of polymer-graphitic material nanocomposites and hybride materials |
US9171656B2 (en) | 2010-09-29 | 2015-10-27 | Siemens Aktiengesellschaft | Electrically insulating nanocomposite having semiconducting or nonconductive nanoparticles, use of this nanocomposite and process for producing it |
WO2012041715A1 (de) * | 2010-09-29 | 2012-04-05 | Siemens Aktiengesellschaft | Elektrisch isolierender nanokomposit mit halbleitenden oder nichtleitenden nanopartikeln, verwendung dieses nanokomposits und verfahren zu dessen herstellung |
US9422413B1 (en) | 2010-12-14 | 2016-08-23 | Molecular Rebar Design, Llc | Elastomer formulations comprising discrete carbon nanotube fibers |
US9493626B1 (en) | 2010-12-14 | 2016-11-15 | Molecular Rebar Design, Llc | Dispersions comprising discrete carbon nanotube fibers |
US9636649B2 (en) | 2010-12-14 | 2017-05-02 | Molecular Rebar Design, Llc | Dispersions comprising discrete carbon nanotube fibers |
US9346991B2 (en) | 2011-04-14 | 2016-05-24 | Ada Technologies, Inc. | Thermal interface materials and systems and devices containing the same |
WO2012146703A1 (en) * | 2011-04-27 | 2012-11-01 | Stichting Dutch Polymer Institute | Process for the preparation of a conductive polymer composition |
US9475921B2 (en) | 2011-06-23 | 2016-10-25 | Molecular Rebar Design, Llc | Nanoplate-nanotube composites, methods for production thereof and products obtained therefrom |
US9997785B2 (en) | 2011-06-23 | 2018-06-12 | Molecular Rebar Design, Llc | Nanoplate-nanotube composites, methods for production thereof and products obtained therefrom |
WO2015155040A1 (en) * | 2014-04-09 | 2015-10-15 | Re-Turn As | Paints and gelcoats with high cnt content |
WO2017180102A1 (en) * | 2016-04-12 | 2017-10-19 | Siemens Aktiengesellschaft | Management of heat conduction using phononic regions having non-metallic nanostructures |
CN108504250A (zh) * | 2018-04-11 | 2018-09-07 | 启东海大聚龙新材料科技有限公司 | 一种环氧树脂复合耐磨涂层及其制备方法 |
EP3988621A4 (en) * | 2019-06-20 | 2022-08-17 | Posco | HEAT-CONDUCTIVE AND ELECTRICALLY INSULATING COLOR COMPOSITION, AS WELL AS OUTER STEEL SHEET FOR SOLAR CELL WITH IT |
WO2021120245A1 (zh) * | 2019-12-19 | 2021-06-24 | 宁波长阳科技股份有限公司 | 人造石墨复合膜及其制备方法 |
Also Published As
Publication number | Publication date |
---|---|
CN1813023A (zh) | 2006-08-02 |
GB0523751D0 (en) | 2005-12-28 |
KR100827861B1 (ko) | 2008-05-07 |
JP2007516314A (ja) | 2007-06-21 |
GB2421506A (en) | 2006-06-28 |
US20070265379A1 (en) | 2007-11-15 |
US7479516B2 (en) | 2009-01-20 |
GB2421506B (en) | 2008-07-09 |
WO2004106420A3 (en) | 2005-04-21 |
KR20060028679A (ko) | 2006-03-31 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US7479516B2 (en) | Nanocomposites and methods thereto | |
Ghaleb et al. | Properties of graphene nanopowder and multi-walled carbon nanotube-filled epoxy thin-film nanocomposites for electronic applications: The effect of sonication time and filler loading | |
Choudhary et al. | Polymer/carbon nanotube nanocomposites | |
Anwar et al. | Advances in epoxy/graphene nanoplatelet composite with enhanced physical properties: A review | |
US9202607B2 (en) | Conductivity of resin materials and composite materials | |
US7296576B2 (en) | Polymers for enhanced solubility of nanomaterials, compositions and methods therefor | |
Wang et al. | Achieving excellent thermally conductive and electromagnetic shielding performance by nondestructive functionalization and oriented arrangement of carbon nanotubes in composite films | |
Ramasubramaniam et al. | Homogeneous carbon nanotube/polymer composites for electrical applications | |
Gantayat et al. | Carbon nanomaterial–reinforced epoxy composites: a review | |
Al-Saleh et al. | A review of vapor grown carbon nanofiber/polymer conductive composites | |
Ogasawara et al. | Characterization of multi-walled carbon nanotube/phenylethynyl terminated polyimide composites | |
Breuer et al. | Big returns from small fibers: a review of polymer/carbon nanotube composites | |
US6762237B2 (en) | Nanocomposite dielectrics | |
Sun et al. | A review of the thermal conductivity of silver-epoxy nanocomposites as encapsulation material for packaging applications | |
Kausar et al. | Effectiveness of polystyrene/carbon nanotube composite in electromagnetic interference shielding materials: a review | |
CN104830031B (zh) | 一种兼具导热和抗静电特性的环氧树脂复合材料及其制备方法 | |
US20120259073A1 (en) | Methods for the synthesis of modular poly(phenyleneethynylenes) and fine tuning the electronic properties thereof for the functionalization of nanomaterials | |
Kausar | Fullerene nanofiller reinforced epoxy nanocomposites—Developments, progress and challenges | |
Oh et al. | Silver-plated carbon nanotubes for silver/conducting polymer composites | |
US20090032806A1 (en) | Polymer composite p-n junction and method for manufacturing same and polymer composite diode incorporating same | |
Yao et al. | Acidified multi-wall carbon nanotubes/polyaniline composites with high negative permittivity | |
Suriati et al. | Silver-filled epoxy composites: effect of hybrid and silane treatment on thermal properties | |
Zhang et al. | Enhancement of the electrical and thermal conductivity of epoxy-based composite films through the construction of the multi-scale conductive bridge structure | |
Zhang et al. | Facile preparation of electromagnetic interference shielding materials enabled by constructing interconnected network of multi-walled carbon nanotubes in a miscible polymeric blend | |
Li et al. | Recyclable thermally conductive poly (butylene adipate‐co‐terephthalate) composites prepared via forced infiltration |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A2 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A2 Designated state(s): GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
WWE | Wipo information: entry into national phase |
Ref document number: 0523751.6 Country of ref document: GB Ref document number: 1020057022277 Country of ref document: KR Ref document number: 2006533339 Country of ref document: JP Ref document number: 0523751 Country of ref document: GB |
|
WWE | Wipo information: entry into national phase |
Ref document number: 20048181603 Country of ref document: CN |
|
WWP | Wipo information: published in national office |
Ref document number: 1020057022277 Country of ref document: KR |
|