CN102656297B - SiC外延晶片及其制造方法 - Google Patents

SiC外延晶片及其制造方法 Download PDF

Info

Publication number
CN102656297B
CN102656297B CN201080056408.0A CN201080056408A CN102656297B CN 102656297 B CN102656297 B CN 102656297B CN 201080056408 A CN201080056408 A CN 201080056408A CN 102656297 B CN102656297 B CN 102656297B
Authority
CN
China
Prior art keywords
growth
sic
gas
sic epitaxial
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201080056408.0A
Other languages
English (en)
Chinese (zh)
Other versions
CN102656297A (zh
Inventor
武藤大祐
百瀬賢治
小田原道哉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Resonac Holdings Corp
Resonac Corp
Original Assignee
Showa Denko KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Showa Denko KK filed Critical Showa Denko KK
Publication of CN102656297A publication Critical patent/CN102656297A/zh
Application granted granted Critical
Publication of CN102656297B publication Critical patent/CN102656297B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B29/00—Single crystals or homogeneous polycrystalline material with defined structure characterised by the material or by their shape
    • C30B29/10—Inorganic compounds or compositions
    • C30B29/36—Carbides
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B25/00—Single-crystal growth by chemical reaction of reactive gases, e.g. chemical vapour-deposition growth
    • C30B25/02—Epitaxial-layer growth
    • C30B25/18—Epitaxial-layer growth characterised by the substrate
    • C30B25/20—Epitaxial-layer growth characterised by the substrate the substrate being of the same materials as the epitaxial layer
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
    • C23C16/22—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the deposition of inorganic material, other than metallic material
    • C23C16/30—Deposition of compounds, mixtures or solid solutions, e.g. borides, carbides, nitrides
    • C23C16/32—Carbides
    • C23C16/325—Silicon carbide
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B25/00—Single-crystal growth by chemical reaction of reactive gases, e.g. chemical vapour-deposition growth
    • C30B25/02—Epitaxial-layer growth
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B25/00—Single-crystal growth by chemical reaction of reactive gases, e.g. chemical vapour-deposition growth
    • C30B25/02—Epitaxial-layer growth
    • C30B25/16—Controlling or regulating
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B25/00—Single-crystal growth by chemical reaction of reactive gases, e.g. chemical vapour-deposition growth
    • C30B25/02—Epitaxial-layer growth
    • C30B25/16—Controlling or regulating
    • C30B25/165—Controlling or regulating the flow of the reactive gases
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B25/00—Single-crystal growth by chemical reaction of reactive gases, e.g. chemical vapour-deposition growth
    • C30B25/02—Epitaxial-layer growth
    • C30B25/18—Epitaxial-layer growth characterised by the substrate
    • C30B25/186—Epitaxial-layer growth characterised by the substrate being specially pre-treated by, e.g. chemical or physical means
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/20—Formation of materials, e.g. in the shape of layers or pillars of semiconductor materials
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/20—Formation of materials, e.g. in the shape of layers or pillars of semiconductor materials
    • H10P14/24—Formation of materials, e.g. in the shape of layers or pillars of semiconductor materials using chemical vapour deposition [CVD]
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/20—Formation of materials, e.g. in the shape of layers or pillars of semiconductor materials
    • H10P14/29—Formation of materials, e.g. in the shape of layers or pillars of semiconductor materials characterised by the substrates
    • H10P14/2901—Materials
    • H10P14/2902—Materials being Group IVA materials
    • H10P14/2904—Silicon carbide
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/20—Formation of materials, e.g. in the shape of layers or pillars of semiconductor materials
    • H10P14/29—Formation of materials, e.g. in the shape of layers or pillars of semiconductor materials characterised by the substrates
    • H10P14/2926—Crystal orientations
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/20—Formation of materials, e.g. in the shape of layers or pillars of semiconductor materials
    • H10P14/34—Deposited materials, e.g. layers
    • H10P14/3402—Deposited materials, e.g. layers characterised by the chemical composition
    • H10P14/3404—Deposited materials, e.g. layers characterised by the chemical composition being Group IVA materials
    • H10P14/3408—Silicon carbide
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/20—Formation of materials, e.g. in the shape of layers or pillars of semiconductor materials
    • H10P14/36—Formation of materials, e.g. in the shape of layers or pillars of semiconductor materials characterised by treatments done before the formation of the materials
    • H10P14/3602—In-situ cleaning
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10D—INORGANIC ELECTRIC SEMICONDUCTOR DEVICES
    • H10D62/00—Semiconductor bodies, or regions thereof, of devices having potential barriers
    • H10D62/40—Crystalline structures
    • H10D62/405—Orientations of crystalline planes
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10D—INORGANIC ELECTRIC SEMICONDUCTOR DEVICES
    • H10D62/00—Semiconductor bodies, or regions thereof, of devices having potential barriers
    • H10D62/80—Semiconductor bodies, or regions thereof, of devices having potential barriers characterised by the materials
    • H10D62/83—Semiconductor bodies, or regions thereof, of devices having potential barriers characterised by the materials being Group IV materials, e.g. B-doped Si or undoped Ge
    • H10D62/832—Semiconductor bodies, or regions thereof, of devices having potential barriers characterised by the materials being Group IV materials, e.g. B-doped Si or undoped Ge being Group IV materials comprising two or more elements, e.g. SiGe
    • H10D62/8325—Silicon carbide

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Inorganic Chemistry (AREA)
  • Mechanical Engineering (AREA)
  • Crystals, And After-Treatments Of Crystals (AREA)
  • Chemical Vapour Deposition (AREA)
CN201080056408.0A 2009-12-14 2010-12-08 SiC外延晶片及其制造方法 Active CN102656297B (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2009283113A JP4887418B2 (ja) 2009-12-14 2009-12-14 ＳｉＣエピタキシャルウェハの製造方法
JP283113/2009 2009-12-14
PCT/JP2010/071989 WO2011074453A1 (ja) 2009-12-14 2010-12-08 ＳｉＣエピタキシャルウェハ及びその製造方法

Publications (2)

Publication Number Publication Date
CN102656297A CN102656297A (zh) 2012-09-05
CN102656297B true CN102656297B (zh) 2015-03-04

Family

ID=44167210

Family Applications (1)

Application Number Title Priority Date Filing Date
CN201080056408.0A Active CN102656297B (zh) 2009-12-14 2010-12-08 SiC外延晶片及其制造方法

Country Status (6)

Country Link
US (1) US20120280254A1 (https=)
EP (1) EP2514857B1 (https=)
JP (1) JP4887418B2 (https=)
KR (1) KR101377813B1 (https=)
CN (1) CN102656297B (https=)
WO (1) WO2011074453A1 (https=)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN106233430A (zh) * 2014-04-18 2016-12-14 国立研究开发法人产业技术综合研究所 碳化硅外延晶片及其制造方法

Families Citing this family (102)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9464366B2 (en) 2009-08-20 2016-10-11 The United States Of America, As Represented By The Secretary Of The Navy Reduction of basal plane dislocations in epitaxial SiC
US10256090B2 (en) * 2009-08-20 2019-04-09 The United States Of America, As Represented By The Secretary Of The Navy Reduction of basal plane dislocations in epitaxial SiC using an in-situ etch process
US10256094B2 (en) * 2009-08-20 2019-04-09 The Government Of The United States Of America, As Represented By The Secretary Of The Navy Reduction of basal plane dislocations in epitaxial SiC using an in-situ etch process
KR101454978B1 (ko) * 2009-08-27 2014-10-27 신닛테츠스미킨 카부시키카이샤 ＳｉＣ 단결정 웨이퍼와 그 제조 방법
JP5445694B2 (ja) * 2011-04-21 2014-03-19 新日鐵住金株式会社 エピタキシャル炭化珪素単結晶基板の製造方法
JP5897834B2 (ja) * 2011-07-19 2016-03-30 昭和電工株式会社 ＳｉＣエピタキシャルウェハの製造方法
JP5961357B2 (ja) 2011-09-09 2016-08-02 昭和電工株式会社 ＳｉＣエピタキシャルウェハ及びその製造方法
US20130062628A1 (en) * 2011-09-10 2013-03-14 Semisouth Laboratories, Inc. Methods for the epitaxial growth of silicon carbide
JP5853648B2 (ja) 2011-11-30 2016-02-09 住友電気工業株式会社 炭化珪素半導体装置の製造方法
KR101942514B1 (ko) * 2011-12-16 2019-01-28 엘지이노텍 주식회사 탄화규소 증착 방법 및 탄화규소 에피 웨이퍼
KR101942536B1 (ko) * 2011-12-19 2019-01-29 엘지이노텍 주식회사 탄화규소 에피 웨이퍼 제조 방법
KR101936171B1 (ko) * 2011-12-19 2019-04-04 엘지이노텍 주식회사 탄화규소 에피 웨이퍼 제조 방법 및 탄화규소 에피 웨이퍼
KR101936170B1 (ko) * 2011-12-19 2019-01-08 엘지이노텍 주식회사 탄화규소 에피 웨이퍼 제조 방법
WO2013161022A1 (ja) * 2012-04-25 2013-10-31 株式会社エコトロン 炭化珪素半導体薄膜の形成方法および炭化珪素半導体基板
KR101926694B1 (ko) * 2012-05-30 2018-12-07 엘지이노텍 주식회사 탄화규소 에피 웨이퍼 및 이의 제조 방법
KR101926678B1 (ko) * 2012-05-31 2018-12-11 엘지이노텍 주식회사 탄화규소 에피 웨이퍼 및 이의 제조 방법
JP6037671B2 (ja) 2012-06-19 2016-12-07 昭和電工株式会社 ＳｉＣエピタキシャルウェハ及びその製造方法
US8860040B2 (en) 2012-09-11 2014-10-14 Dow Corning Corporation High voltage power semiconductor devices on SiC
US9018639B2 (en) 2012-10-26 2015-04-28 Dow Corning Corporation Flat SiC semiconductor substrate
TW201417149A (zh) * 2012-10-31 2014-05-01 Ｌｇ伊諾特股份有限公司 磊晶晶圓
TW201417150A (zh) * 2012-10-31 2014-05-01 Ｌｇ伊諾特股份有限公司 磊晶晶圓
KR102119755B1 (ko) * 2012-11-30 2020-06-08 엘지이노텍 주식회사 에피택셜 웨이퍼 및 그 제조 방법
US11309389B2 (en) 2012-11-30 2022-04-19 Lx Semicon Co., Ltd. Epitaxial wafer and switch element and light-emitting element using same
KR102098209B1 (ko) * 2013-02-05 2020-04-08 엘지이노텍 주식회사 에피택셜 웨이퍼 및 그 제조 방법
KR102053077B1 (ko) * 2012-11-30 2020-01-08 엘지이노텍 주식회사 에피택셜 웨이퍼 및 그 제조 방법
US9738991B2 (en) 2013-02-05 2017-08-22 Dow Corning Corporation Method for growing a SiC crystal by vapor deposition onto a seed crystal provided on a supporting shelf which permits thermal expansion
US9017804B2 (en) 2013-02-05 2015-04-28 Dow Corning Corporation Method to reduce dislocations in SiC crystal growth
US9797064B2 (en) 2013-02-05 2017-10-24 Dow Corning Corporation Method for growing a SiC crystal by vapor deposition onto a seed crystal provided on a support shelf which permits thermal expansion
US9988738B2 (en) 2013-02-13 2018-06-05 Mitsubishi Electric Corporation Method for manufacturing SiC epitaxial wafer
CN103199008A (zh) * 2013-03-11 2013-07-10 西安电子科技大学 零偏4H-SiC衬底上的同质外延方法
US8940614B2 (en) * 2013-03-15 2015-01-27 Dow Corning Corporation SiC substrate with SiC epitaxial film
JP6123408B2 (ja) 2013-03-26 2017-05-10 三菱電機株式会社 単結晶４Ｈ−ＳｉＣ基板及びその製造方法
JP2014189442A (ja) 2013-03-27 2014-10-06 Sumitomo Electric Ind Ltd 炭化珪素半導体基板の製造方法
JP6112712B2 (ja) * 2013-03-27 2017-04-12 国立研究開発法人産業技術総合研究所 炭化珪素エピタキシャルウエハの製造方法
JP2014210690A (ja) * 2013-04-22 2014-11-13 住友電気工業株式会社 炭化珪素基板の製造方法
JP6136731B2 (ja) * 2013-08-06 2017-05-31 住友電気工業株式会社 炭化珪素半導体基板およびその製造方法、ならびに炭化珪素半導体装置の製造方法
JP6386706B2 (ja) * 2013-09-06 2018-09-05 住友電気工業株式会社 炭化珪素エピタキシャル基板、炭化珪素エピタキシャル基板の製造方法、炭化珪素半導体装置の製造方法、炭化珪素成長装置および炭化珪素成長装置用部材
JP6172672B2 (ja) * 2013-10-11 2017-08-02 大陽日酸株式会社 気相成長装置の膜厚測定方法
CN103820768A (zh) * 2014-03-11 2014-05-28 中国科学院半导体研究所 4H-SiC衬底上同质快速外延生长4H-SiC外延层的方法
JP6311384B2 (ja) 2014-03-24 2018-04-18 三菱電機株式会社 炭化珪素半導体装置の製造方法
JP6479347B2 (ja) * 2014-06-06 2019-03-06 ローム株式会社 ＳｉＣエピタキシャルウェハの製造装置、およびＳｉＣエピタキシャルウェハの製造方法
US9279192B2 (en) 2014-07-29 2016-03-08 Dow Corning Corporation Method for manufacturing SiC wafer fit for integration with power device manufacturing technology
DE112015003559B4 (de) 2014-08-01 2024-08-22 Sumitomo Electric Industries, Ltd. Epitaxialer Wafer
CN106796886B (zh) * 2014-08-29 2020-05-01 住友电气工业株式会社 碳化硅半导体器件和用于制造碳化硅半导体器件的方法
JP6259740B2 (ja) * 2014-09-11 2018-01-10 国立大学法人名古屋大学 炭化ケイ素の結晶の製造方法及び結晶製造装置
CN106715767A (zh) * 2014-10-01 2017-05-24 住友电气工业株式会社 碳化硅外延基板
WO2016075957A1 (ja) * 2014-11-12 2016-05-19 住友電気工業株式会社 炭化珪素エピタキシャル基板の製造方法および炭化珪素エピタキシャル基板
JP2016127201A (ja) * 2015-01-07 2016-07-11 三菱電機株式会社 炭化珪素エピタキシャル基板の製造方法および炭化珪素半導体装置の製造方法
JP2016132604A (ja) * 2015-01-21 2016-07-25 住友電気工業株式会社 炭化珪素基板および炭化珪素基板の製造方法
JP6537590B2 (ja) * 2015-02-18 2019-07-03 昭和電工株式会社 炭化珪素単結晶インゴットの製造方法
CN107002282A (zh) 2015-02-18 2017-08-01 新日铁住金株式会社 外延碳化硅单晶晶片的制造方法以及外延碳化硅单晶晶片
EP3266907A4 (en) * 2015-03-03 2018-10-24 Showa Denko K.K. Sic epitaxial wafer and method for manufacturing sic epitaxial wafer
CN105006425A (zh) * 2015-06-08 2015-10-28 国网智能电网研究院 一种无台阶聚集低偏角碳化硅外延生长方法
KR102106722B1 (ko) * 2015-07-29 2020-05-04 쇼와 덴코 가부시키가이샤 에피택셜 탄화규소 단결정 웨이퍼의 제조 방법
DE112015006240T5 (de) * 2015-07-30 2017-11-09 Fuji Electric Co., Ltd. HERSTELLUNGSVERFAHREN EINES SiC-SUBSTRATS
JP6641814B2 (ja) 2015-09-11 2020-02-05 住友電気工業株式会社 炭化珪素エピタキシャル基板および炭化珪素半導体装置の製造方法
JP6544166B2 (ja) * 2015-09-14 2019-07-17 信越化学工業株式会社 ＳｉＣ複合基板の製造方法
JP6584253B2 (ja) 2015-09-16 2019-10-02 ローム株式会社 ＳｉＣエピタキシャルウェハ、ＳｉＣエピタキシャルウェハの製造装置、ＳｉＣエピタキシャルウェハの製造方法、および半導体装置
JP6573514B2 (ja) * 2015-09-17 2019-09-11 昭和電工株式会社 ＳｉＣ単結晶基板の前処理方法及びエピタキシャルＳｉＣウェハの製造方法
DE112016004600B4 (de) * 2015-10-07 2025-10-23 Sumitomo Electric Industries, Ltd. Epitaktisches Siliziumkarbidsubstrat, Verwendung des Siliziumkarbidsubstrats und Verfahren zum Herstellen einer Siliziumkarbid-Halbleitervorrichtung
CN105826186B (zh) * 2015-11-12 2018-07-10 中国电子科技集团公司第五十五研究所 高表面质量碳化硅外延层的生长方法
JP6069545B2 (ja) * 2016-01-20 2017-02-01 昭和電工株式会社 ＳｉＣエピタキシャルウェハの評価方法
JP6969628B2 (ja) * 2016-02-15 2021-11-24 住友電気工業株式会社 炭化珪素エピタキシャル基板および炭化珪素半導体装置の製造方法
JP6690282B2 (ja) 2016-02-15 2020-04-28 住友電気工業株式会社 炭化珪素エピタキシャル基板および炭化珪素半導体装置の製造方法
US11320388B2 (en) 2016-08-31 2022-05-03 Showa Denko K.K. SiC epitaxial wafer containing large pit defects with a surface density of 0.5 defects/CM2 or less, and production method therefor
JP6459132B2 (ja) * 2016-08-31 2019-01-30 昭和電工株式会社 ＳｉＣエピタキシャルウェハ及びその製造方法、並びに、欠陥識別方法
JP6493690B2 (ja) * 2016-08-31 2019-04-03 昭和電工株式会社 ＳｉＣエピタキシャルウェハ及びその製造方法、並びに、ラージピット欠陥検出方法、欠陥識別方法
US11293115B2 (en) 2016-08-31 2022-04-05 Showa Denko K.K. Method for producing a SiC epitaxial wafer containing a total density of large pit defects and triangular defects of 0.01 defects/cm2 or more and 0.6 defects/cm2 or less
JP6915627B2 (ja) * 2016-10-28 2021-08-04 住友電気工業株式会社 炭化珪素エピタキシャル基板の製造方法
JP6748572B2 (ja) * 2016-12-28 2020-09-02 昭和電工株式会社 ｐ型ＳｉＣエピタキシャルウェハ及びその製造方法
JP6762484B2 (ja) * 2017-01-10 2020-09-30 昭和電工株式会社 ＳｉＣエピタキシャルウェハ及びその製造方法
CN110214363B (zh) * 2017-01-31 2023-07-28 住友电气工业株式会社 碳化硅外延衬底和制造碳化硅半导体器件的方法
JP6930640B2 (ja) * 2017-03-08 2021-09-01 住友電気工業株式会社 炭化珪素単結晶基板、炭化珪素エピタキシャル基板および炭化珪素半導体装置の製造方法
JP6824088B2 (ja) * 2017-03-24 2021-02-03 昭和電工株式会社 炭化珪素のエピタキシャル成長方法
JP6841321B2 (ja) * 2017-04-06 2021-03-10 三菱電機株式会社 ＳｉＣエピタキシャルウエハの製造方法
JP6758491B2 (ja) * 2017-05-17 2020-09-23 三菱電機株式会社 ＳｉＣエピタキシャルウエハおよびその製造方法
WO2019043927A1 (ja) * 2017-09-01 2019-03-07 住友電気工業株式会社 炭化珪素エピタキシャル基板
JP7002932B2 (ja) * 2017-12-22 2022-01-20 昭和電工株式会社 ＳｉＣインゴットの製造方法
JP2018067736A (ja) * 2018-01-16 2018-04-26 三菱電機株式会社 炭化珪素半導体装置及びその製造方法
WO2019224953A1 (ja) * 2018-05-23 2019-11-28 三菱電機株式会社 ＳｉＣエピタキシャル基板の製造方法
JP7400715B2 (ja) * 2018-07-20 2023-12-19 住友電気工業株式会社 炭化珪素エピタキシャル基板および炭化珪素半導体装置の製造方法
JP7447392B2 (ja) * 2018-09-10 2024-03-12 株式会社レゾナック ＳｉＣ基板の評価方法及びＳｉＣエピタキシャルウェハの製造方法
JP6585799B1 (ja) * 2018-10-15 2019-10-02 昭和電工株式会社 ＳｉＣ基板の評価方法及びＳｉＣエピタキシャルウェハの製造方法
JP7217608B2 (ja) * 2018-10-16 2023-02-03 昭和電工株式会社 ＳｉＣ基板、ＳｉＣエピタキシャルウェハ及びその製造方法
JP7063259B2 (ja) * 2018-12-27 2022-05-09 株式会社Sumco シリコンエピタキシャルウェーハの製造方法
JP7148427B2 (ja) 2019-02-06 2022-10-05 昭和電工株式会社 ＳｉＣエピタキシャルウェハ及びその製造方法
JP7046026B2 (ja) * 2019-03-01 2022-04-01 三菱電機株式会社 ＳｉＣエピタキシャルウエハ、半導体装置、電力変換装置
JP2020170816A (ja) * 2019-04-05 2020-10-15 三菱電機株式会社 炭化珪素エピタキシャルウエハ、炭化珪素エピタキシャルウエハの製造方法、電力変換装置
RU2716866C1 (ru) * 2019-06-06 2020-03-17 Публичное Акционерное Общество "Электровыпрямитель" Способ роста эпитаксиальных слоев карбида кремния р-типа проводимости с малой плотностью базальных дислокаций
CN110281142A (zh) * 2019-06-20 2019-09-27 山东大学 金刚石籽晶制备方法、金刚石籽晶及单晶
JP6791348B2 (ja) * 2019-12-24 2020-11-25 住友電気工業株式会社 炭化珪素エピタキシャル基板および炭化珪素半導体装置の製造方法
JP6973600B2 (ja) * 2019-12-24 2021-12-01 住友電気工業株式会社 炭化珪素エピタキシャル基板および炭化珪素半導体装置の製造方法
CN113122147B (zh) * 2019-12-31 2024-03-12 安集微电子科技（上海）股份有限公司 一种化学机械抛光液及其使用方法
KR102229588B1 (ko) 2020-05-29 2021-03-17 에스케이씨 주식회사 웨이퍼의 제조방법, 에피택셜 웨이퍼의 제조방법, 이에 따라 제조된 웨이퍼 및 에피택셜 웨이퍼
JP7610934B2 (ja) * 2020-07-21 2025-01-09 三菱電機株式会社 炭化珪素エピタキシャルウエハの製造方法
CN112259451B (zh) * 2020-09-22 2022-11-29 山东天岳先进科技股份有限公司 一种碳化硅晶片的位错识别方法及碳化硅晶片与应用
KR102283879B1 (ko) 2021-01-14 2021-07-29 에스케이씨 주식회사 탄화규소 웨이퍼의 제조방법, 탄화규소 웨이퍼 및 웨이퍼 제조용 시스템
KR102321229B1 (ko) * 2021-03-30 2021-11-03 주식회사 쎄닉 탄화규소 웨이퍼 및 이를 적용한 반도체 소자
CN113594027A (zh) * 2021-07-27 2021-11-02 兰州大学 一种腐蚀4h-碳化硅表面的方法
JP7285890B2 (ja) 2021-08-04 2023-06-02 株式会社レゾナック ＳｉＣエピタキシャルウェハ及びＳｉＣエピタキシャルウェハの製造方法
JP7183358B1 (ja) * 2021-08-04 2022-12-05 昭和電工株式会社 ＳｉＣエピタキシャルウェハ及びＳｉＣエピタキシャルウェハの製造方法
CN119764220B (zh) * 2024-12-27 2025-11-18 中国电子科技集团公司第五十五研究所 一种降低碳化硅外延材料缺陷数量的方法

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1895573A1 (en) * 2005-04-22 2008-03-05 Bridgestone Corporation Silicon carbide single-crystal wafer and process for producing the same
WO2009035095A1 (ja) * 2007-09-12 2009-03-19 Showa Denko K.K. エピタキシャルＳｉＣ単結晶基板及びエピタキシャルＳｉＣ単結晶基板の製造方法

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4238357B2 (ja) 2003-08-19 2009-03-18 独立行政法人産業技術総合研究所 炭化珪素エピタキシャルウエハ、同ウエハの製造方法及び同ウエハ上に作製された半導体装置
JP4581081B2 (ja) 2004-03-25 2010-11-17 独立行政法人産業技術総合研究所 エピタキシャルウエハ作製時に用いる炭化珪素平滑化基板の作製方法、炭化珪素基板表面の平滑化及びＳｉＣエピタキシャル成長に用いる装置
US20080261401A1 (en) * 2004-04-08 2008-10-23 Ii-Vi Incorporated Chemical-Mechanical Polishing of Sic Surfaces Using Hydrogen Peroxide or Ozonated Water Solutions in Combination with Colloidal Abrasive
EP1752567B1 (en) * 2004-05-27 2011-09-14 Bridgestone Corporation Process for producing wafer of silicon carbide single-crystal
EP1619276B1 (en) * 2004-07-19 2017-01-11 Norstel AB Homoepitaxial growth of SiC on low off-axis SiC wafers
JP2007182330A (ja) * 2004-08-24 2007-07-19 Bridgestone Corp 炭化ケイ素単結晶ウェハ及びその製造方法
JP4987792B2 (ja) 2008-04-17 2012-07-25 新日本製鐵株式会社 エピタキシャル炭化珪素単結晶基板の製造方法

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1895573A1 (en) * 2005-04-22 2008-03-05 Bridgestone Corporation Silicon carbide single-crystal wafer and process for producing the same
WO2009035095A1 (ja) * 2007-09-12 2009-03-19 Showa Denko K.K. エピタキシャルＳｉＣ単結晶基板及びエピタキシャルＳｉＣ単結晶基板の製造方法

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN106233430A (zh) * 2014-04-18 2016-12-14 国立研究开发法人产业技术综合研究所 碳化硅外延晶片及其制造方法
CN106233430B (zh) * 2014-04-18 2019-08-06 国立研究开发法人产业技术综合研究所 碳化硅外延晶片及其制造方法

Also Published As

Publication number Publication date
KR20120101097A (ko) 2012-09-12
EP2514857A1 (en) 2012-10-24
JP4887418B2 (ja) 2012-02-29
KR101377813B1 (ko) 2014-03-25
CN102656297A (zh) 2012-09-05
US20120280254A1 (en) 2012-11-08
WO2011074453A1 (ja) 2011-06-23
JP2011121847A (ja) 2011-06-23
EP2514857A4 (en) 2013-08-07
EP2514857B1 (en) 2018-02-21

Similar Documents

Publication Publication Date Title
CN102656297B (zh) SiC外延晶片及其制造方法
JP5076020B2 (ja) ＳｉＣエピタキシャルウェハ
CN102576666B (zh) SiC外延晶片及其制造方法
CN103765559B (zh) SiC外延晶片及其制造方法
JP6122704B2 (ja) ＳｉＣエピタキシャルウェハ及びその製造方法
JP5384714B2 (ja) ＳｉＣエピタキシャルウェハ及びその製造方法
JP5304713B2 (ja) 炭化珪素単結晶基板、炭化珪素エピタキシャルウェハ、及び薄膜エピタキシャルウェハ
TWI875904B (zh) Ｉｉｉ族氮化物單晶基板及其製造方法
JPWO2009150896A1 (ja) シリコンエピタキシャルウェーハ及びその製造方法
JP7632731B2 (ja) 炭化ケイ素エピタキシャル基板
JP5604577B2 (ja) ＳｉＣエピタキシャルウェハ
WO2021200203A1 (ja) ダイヤモンド結晶基板と、ダイヤモンド結晶基板の製造方法
JP5124690B2 (ja) ＳｉＣエピタキシャルウェハ

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
CP01 Change in the name or title of a patent holder

Address after: Tokyo, Japan

Patentee after: Lishennoco Co.,Ltd.

Address before: Tokyo, Japan

Patentee before: Showa electrical materials Co.,Ltd.

CP01 Change in the name or title of a patent holder
TR01 Transfer of patent right

Effective date of registration: 20230516

Address after: Tokyo, Japan

Patentee after: Showa electrical materials Co.,Ltd.

Address before: Tokyo, Japan

Patentee before: SHOWA DENKO Kabushiki Kaisha

TR01 Transfer of patent right