TW308582B - - Google Patents
Download PDFInfo
- Publication number
- TW308582B TW308582B TW084101658A TW84101658A TW308582B TW 308582 B TW308582 B TW 308582B TW 084101658 A TW084101658 A TW 084101658A TW 84101658 A TW84101658 A TW 84101658A TW 308582 B TW308582 B TW 308582B
- Authority
- TW
- Taiwan
- Prior art keywords
- bao
- cao
- mgo
- sro
- glass
- Prior art date
Description
經濟部中央標準局貝工消费合作社印製 306582 五、發明説明(I ) 本發明体關於H4 59酸_坡瑀,特別使用6:平板顯示器 元件中 發明背f : 板顯示器廣為 < 們憋到闕趣,例如藥紀型電腦,μ及 資訊Μ及娛樂應用之大型組件:φ·板顯不器 '項特殊型式 為液晶顯示器' 液晶顯不器(LCDs )為中.板顯示器?1;卩丨:,其砍靠外界光 源照明顯#
Dumbaugh , Jr .之美_第4824808號專利列舉出LCD基 Μ玻瑀四項主要特性 第 坡璃必需為非刻意地添加鹼金晒氧(t物W防止鹼 金藝由基板遷柊至半導體陣列之可能; 第二,破璃基板必需有充份池(b學W又性κ承受tft陣 列沉檳處埋過程中所使闬之ib學藥劑; 第ΐ ,在玻瑀與TFT陣列中所存在的之間膨漲保數不相 匹配必需維持為相當低,甚至於在基板邂理過程溫度增加 時:以坟 第四,玻璃必蔣能狗Μ相當高品質薄Η型式而價格相 當低地製造出;即其並ί、需要廣泛之δΗ磨以及抛光Κ確保 所需要之表面修整 最後.項要求為最難達成,因為其需要 '個Η狀坡璃 處埋過程以製造出大體t完整之破瑀Η 0前使用溢流 问Τ7拉引Μ狀醺理法 該處理法已擷不於DockertY之美國 第3338696號專利W及Dockerty之美國第3682609號專利」 本紙張尺度逋用中國國家梂準(CNS ) A4规格(210X297公釐) 午 -------------裝------訂------- 、 ί (請先閲讀背面之注f項再填寫本頁) A7 B7 經濟部中央標準局負工消費合作社印裝 五、發明説明(·2 ) 遺處埋法需要S液相線溫度F具有非常高黏滯係數之坡璃 以坆畏期例如30天之德定性Μ防止在熔融以及成形溫度F 形成析晶現象」
Corning Code 7059坡瑀目前被使用来製造LCDs .該 玻璃以重量百'分比表示S含大約50% Si〇2 15% B2〇3 , 10 % Al2 〇3 ,M .¾ 24% BaO,名義上並不含鹼金嗎氧〇:物,Μ及 線性熱膨漲數CTE( 25-300 Γ )為46X10- V η Μ坆Γ土液相 纈溫度Κ黏滯丨系數超過60000 Pa ( 600000泊丨..坡瑀高液相 線黏滯係數能夠經由溢流向F拉引Η狀處埋法使其被抽拉 為Η狀,丨s是其相當低應變點(93 c m適當處理a-S1元 ί牛K坆不適用poiy-si/c件:1 因此,廣泛丨日並不成功之研究已指引發展出之玻瑀將 ?ί 含後:項要求,# 閱美國第 4409337,4824808,5116788, 及5116789號専利 原先埴些坡瑀ti破使用來製造多矽元 件而後其能夠_由溢流问F拉引Μ狀處埋法形成Μ吠 其線性熱膨漲ί系數與矽非常匹配。 冃前庄液晶技術中項前進技術稱為"晶Μ在玻璃t." (COG )¾進 步強調要求基Η玻璃之熱膨漲谣數與砂非常 接近因此原先LCDTt件並不需要將驅動器晶Η裝置於基 板玻璃上相反方地,矽晶片相隔遙遠地装置著並利用柔 軟的接線遵接至LCD基板電路由於LCD元件技術改春以及 rt丨牛變為較大,該柔軟之接線按裝由於價格以及不確定之 可靠性因素則變為不可接受:該情況將促使採用矽晶Η帶 狀自動接合(TAB )在該處理過程中矽晶片以及電子連接 本紙張尺度逋用中國國家標準(CNS > A4規格(210X25»7公釐) ------Γ——,--^------^-----'10 / f (請先閲讀背面之注$項再填寫本頁) 五、發明説明(3 ) A7 B7 經濟部中央標準局員工消费合作社印袋 晶Η均裝置於承載_帶丨:,其Η次組件地自接按装於LCD * H h ,Μ及埋接至LCD電路而完成 當改菩吋靠性K及提 供半導體允許之密度達到大約為200微米之間距時TAB價格 將降低:f過COG將因該. 項因素而對TAB而提供熨進 '步 改菩:因此當LCD_t[:;件尺寸_以及品質要求提時H些7_c件 需要作COG並需要使用集體電路矽晶Η :碁於這些埋由,基 Μ玻璃線性熱膨漲係數必需與矽非常接近,即玻璃線性熱 膨漲係數(0-300Γ )應界於31-44x10- 7 /(、,最好界於32-40 Χ10- 7 溢流向Τ'拉引Η狀處理法在液相線所需要之高黏滯係 數,600000泊(60000 Pas )與poly-Si元件所需要數項其他 持性同時地具有為相當難以達成1此注意到其他形成Η 狀處理過程,其黏滯因素並非如此_卜分重要_其®含浮式 處理法Μ及再抽拉處理法 浮式處理法包含抽拉出埋纊Η狀坡瑀於瑢融金圈表面 h ,例如為熔融之錫 與熔融金驅接觸之表1«丨在抽拉過程 中並未暴露出,Μ坆因ffi丨相當光滑W及沒有缺陷。其只需 要庄個表面作修整本發明主要目的在5彳提供苹板Μ作 為顯示器ίί ί牛之用,特刖是晶Η之LCD元件另外 _目標在於提供異於溢流向F拉引Η狀處理法,例如浮 式處埋法所製造出之平板 發明大要: 本發明主要在於1鋁矽酸鹽玻璃特別使用作為平板 顯示器之平板,其具有應變點溫度高於640t’,CTEsS 31-57 本紙張尺度適用中國國家揉率(CNS > A4規格(210X297公釐) 請k. 閲 面 之 注
I 頁 裝 訂 線 6 4 305582 經濟部中央揉準局貞工消费合作社印製 五、發明説明(牛) χΐϋ- 7 / r、範圍内,在浸人95Γ 5%重量比HC1水溶液F 24小時 後重星損失為小K 20mg/cm2 ,其名親h並沒有鹼金屬氧化 物,其組成份Μ氧丨b物重最Θ分比為計尊基準包含49-67% Sl〇2 ,至少 6% Al2〇3 , Al2〇3為 6-14%加上.55-67% Si〇2M 及 AI2O3 為 16-23% 加上 49-58% S1O2, S1O2+AI2O3 > 68%, 0-15% B2O3 ,至少 種鹼土金屬氧化物由〇-21%63〇,0-15% SrO, 0-18% CaO, 0-8* MgO標示比例中選取出Μ及 BaO+CaO+SrO+MgO 為 12-30%_: 本發明製造平板顯不器玻璃平板之方法Q含熔融鋁矽 酸鹽玻璃原料,其組成份Μ氧化物重虽&分比為計算基準, 包含 49-67* Si〇2 ,至少 6* Αΐ2〇3 , ΑΙ2Ο3為 6-14%加上 55 -67% S1O2M 及 ΑΙ2Ο3 為 16-23% 加上 49-58* Sl〇2, Sl〇2 + AI2O3 > 68%, 0-15% B2O3,至少一棰鹼土金靨氧化物由 0-21* BaO, 0-15* SrO, 0-18% CaO, 0-8¾ MgO標示比例 中選取出Μ及BaO+CaO+SrO+MgO為12-301M及由熔融物抽 拉出熔融玻璃薄Μ。 本發明亦憤期使鋁矽酸豔玻璃具有之應變點高於640 Γ ,在浸人951之5%重鼉比HC1水溶液下24小時後重量損失 為小於20mg/cm2 ,CTE界於31-57x10— 7之間,其名義h並沒 有鹼金驅氧ib物,其組成份Μ氧化物重量百分比為計算基 準包含 49-67% Si〇2 ,全少 6% ΑΙ2Ο3 , ΑΙ2Ο3 為 6-14%加 h 55-67* S1O2M 及 AI2O3 為 16-23* 加上 49-58* Si〇2, S1O2 +AI2O3 > 68*, 0-15% B2O3,至少--種鹼土金_氧化物由 0-21% BaO, 0-15¾ SrO, 0-18* CaO, 0-8% MgO檷示比例 本紙張尺度遑用中國國家標準(CNS ) A4規格(210X297公釐) η ------,——^--裝------訂-----^1線 (請先閲讀背面之注##項再填寫本頁) 經濟部中央橾率局貝工消费合作社印装 A7 B7 五、發明説明(宁) 中選取出 Μ 及 BaO+CaO+SrO+MgO為 12-30%‘: 詳細說明: 本發明起源於對平板顯示器平板之需求,該平板能夠 賴由一種方法製造出,而該方法並+會增加溢流向F拉引 處理法之要求。特別是,其將避免在液相線溫度F超過 60000Pas ( 600000泊)非常高黏浦丨系數之要求。 同時,必需符台·些其他之要求 這些S含玻璃應變 點溫度高於640_(〕,良好之化學跗久性,f含_金靨Μ及受 控制之熱膨漲係數(CTE > 我們發琨這些要求由名義上不含驗金圈is矽酸鹽玻璃 族屬來達成,其組成份Μ氧化物為基準計算E要包含49-67 % Sl〇2 ,至少 6% Al2〇3 , Al2〇3為 6-14%加 t: 55-67% Si〇2 Μ 及 Al2〇3為 16-23%加 h 49-58* S1O2 , S1O2+AI2O3 > 68V. 0-15* B2O3,至少·種鐮土金靨氧化物由0-21%BaO,0-15% SrO, 0-18% CaO, 0-8% MgO標示比例中選取出以及 BaO+CaO+SrO+MgO為 12-30%〇 為了得到具有所需要化學,成肜,Μ及物理特性之組嫌 則必需遵從特定之組成份,如F面所說明
Si〇2以及Α12 〇3為形成玻戚之氧化物。基於該目的Μ 及產生所需要之高應變點至少需要49% Sl〇2以及6% Al2〇3 :當Si〇2含量大於67%以及Al2〇3含量大於23S時玻璃之熔 融寒為困難
Sl〇2以及Α12 〇3亦對玻璃耐久性有所Μ連在瑄一方 面Sl〇2M及Al2〇3含鼉為相互闞埋的 Al2〇3含量在6-14% 本紙張尺度逋用中國國家揉準(CNS > Α4规格(2丨ΟΧ297公着) -------------.——裝------訂-----丨線 (請先閲讀背面之注項再填寫本頁) 3 3 經濟部中央標率局負工消费合作社印裝 A7 B7 五、發明説明(έ ) 範園内Si〇2含量必需至少為55% ,Μ及饅好為至少60% ,Μ產 生所需要之化學耐久性:Al2〇3含量在16-23%範圍内,Sl〇2 含最可低至49%以遝到適當之耐久'性 SlOi‘ +Α12〇3總含量 應該大於68%以得到所需要之附久性 b2〇3將使玻璃软化,即降低熔融溫度K及使熔融變得 容易:不過,其將降低應變點Μ及對耐久性有所危害,特別 是在大數量時。因此,& 〇3含量應不超過15% ,以及最好不 超過8% 當肿晶Μ將裝置於玻璃上,CTE必需為31-44x10- 7 / Γ , BaO最好維持低含最。其他鹼土金鼷氧化物以及/或Α12 〇3 能夠被替代。 通常,_ 土金麵將使CTE增加,其排列顒序為Ba>Sr>Ca> Mg, BaO具有最佳效果Μ & MgO為最小效果 除:Γ上述所提及之組成份,亦可考鼸·些附加上之組 成份這些組成份包含 Ti〇2 , Zr〇2 , ZnO, La2 〇3 , Ta2 〇5 , Nb2 〇5 以坆Y2〇3 最好瑄些氧化物存在量不超過5%重量比,因為 其將增加密度Μ及降低應變點通常,將會得到-呰益處 例如折射率或耐久性 鹼金屬Μ及鹵化物將危害液晶,因此需沏以避免,除非 為不可遴免之雑質。 -般接受之化學耐久性量測為玻璃試樣浸漬於951C之 5%重量比HC1水溶液中歷時24小時後之重量損失。作為本 發明用途,重鼉損失必需小於20mg/cm2 ,最好小於5mg/cm2 , 最佳情況為低於lmg/cm2 本紙張尺度適用中國國家揉準(CNS > A4规格(2丨0X 297公釐) 9 --------------^------1T-----|-丨.^ (請先閲讀背面之注項再填寫本頁) 9 7 經濟部中央樣準局貝工消费合作社印製 808582_B7_ 五、發明説明(η ) 有兩踊熱膝漲係數值與顯示器玻璃板相闞缠,特別是 LCD元件 .涸數值主要決定於Code 7059坡璃,其庄業界 已荽為標準 該玻瑀CTE為46x10- 7 /10 ,Μ及CTE範圍為44-57x10- 7 /Γ視為相容的 最好在45-50x10- 7 /10範圍内 我們發現兩棰鋁矽酸種類AM及Β之CTE數值在該範園 該棰類之玻璃組成份Μ氧化物重量百分比為計算檷準, 將包含 A B Sl〇2 50-57 55-67 A12 03 16-22 6-14 B203 0-5. i ) 0-7.5 MgO 0,5-3 0-6.5 CaO 1-12. 5 0-18.5 SrO 0.5-15 0-15.5 BaO 1-21 1-9.5 MgO+CaO+SrO+BaO 一 16.5-28 其他CTE大小主要決定於需要與矽匹配,因而允許直接 與晶Η壤接矽CTE值為36x10- 7 /V 因此坡璃板CTE範圍 為 31-44x10- 7 /1、,最好為 32-40x10- 7 / ·(、_ 為」’使CTE值在這些範圍内,我們發琨兩棰鋁矽酸鹽種 類CM及D將符合該要求該棰類玻璃組成份κ氧化物重量 百分比為計算基準,包含:
C D
Si〇2 49-58 57-66 本紙張尺度逋用中國國家橾準(CNS > A4规格(210X 297公釐) /c? ------------:——^------1T------ 一 (請先聞讀背面之注^^項再填寫本頁) 丄Ο 8 Α7 Β7 經濟部中央樣準局舅工消費合作社印装 五、發明説明(分) Α12 〇3 17.5-23 8-14 Β2〇3 0-14.5 0-13 MgO 0-8 0-4,5 CaO 0-9 0-9 SrO 0.4-13.5 0.5-15. BaO 0-21 2-21
HgO+CaO+SrO+BaO 13-28 另外…方面,本發明考嗛-棰製造LCD元件平板之方法 ,其II由熔融上面所敘述之坡璃,利用例如浮式處理法由熔 融物形成片狀玻璃,再加Μ抽拉或滾壓,M ft將片狀玻瑀切 剳為平板大小' 具體實拖例說明: 表I記錄.·些玻璃組成份:·組成份以氧i'b物重量份數 宋表示,列例說明本發明玻璃組成份·些參數:各個成份 總和非常接近1〇〇,並且稍低於1(3〇 ,其由於省略澄清劑例如 As 2 〇3 因此貿際上表列之數值可視為重量丙分比: 實際原料能夠包含所需要之氧化物:其亦能夠包含其 他化合物,當其與其他原料成份熔融在·起時,其將轉化為 所需要之氧fb物並呈適當之比例例如CaC〇3以及BaC〇3能 夠分別提供作為CaO以及BaO之來源 Μ這些組成份為主之玻璃原料被混合°原料被攬伴混 合在起以得到均質的熔融,Μ及再注人至甶金坩堝·:’放 置蓋子後,坩堝被移入至溫度為1650(、高溫埔中’為了確 霣使玻璃形成而沒有夾雜物以及條痕,實施_個步嫌之溶 本紙張尺度適用中國國家標率(CNS ) Α4说格(210X297公釐) ----------^--裝------訂------.線 、+' (請先閲讀背面之注$項再填寫本頁) Α7 __—_Β7 五、發明説明(3) 融操作。原料苜先加以熔融歷時16小時以及加以报拌.,而 後Μ细束之流動注人至清水池中Μ形成微细分離之玻璃顆 粒該處理過程在玻璃業界稱為Μ淌凝"(dirigaging卜在 第二步猓中,微细分離玻璃顆粒(在乾燥後)M 165〇t再加 以熔融歷時4小時1融物以兩個方向加以攬拌,即順時鐘 Μ及逆時鐘方向熔融物而後被注人至不鏽鋼板上Μ形成 玻璃板其尺寸大約為18"χ6"χ0. 5" 這些玻璃板被立即移 入操作溫度為725Τ'之退火埔中 必需說明L·述說明R表示霣驗室之搡作過程 而本發 明玻璃能夠使用大型已商業化之破璃熔融以及成形設備加 Κ熔融Μ及成形·假如餺要,能夠添加‘般常用數量之澄 清劑例如砷以及銻之氧化物:_ 表I亦列舉一些玻璃業界傳統量測技術所測定出化學 Μ及物理特性之鼉測值。在溫度0-3001C範園内之線性熱 瞭漲係數Κ Χ10- 7 / C表示:软化點(S . Ρ .)及應變點(St. Ρ > M C表示,Μ及經由纖維延伸來澜定出在HCl* _久性評 定是藉由浸潰於95〇溫度F 5%重量比HC1水溶液24小時後 測定重量損失(mg/cm2 > „ ^ 裝 訂 線 、·-- (請先閲讀背面之注$項再填寫本頁) 經濟部中央橾準局貝工消费合作社印製 本紙張尺度適用中國國家橾率(CNS ) A*»规格(210X297公釐) 1^ 五、發明説明() A7 B7 經濟部中央標準局貝工消費合作社印製
Sl〇2 A1203 B203 MgO CaO SrO BaO CTE St -P. S.P. Dur . S1O2 Al2 〇3 B2 〇3 MgO CaO SrO BaO CTE St S.P. Dur . 1 2 3 4 5 65 65.4 50,6 65 55.7 8.2 13 22.1 8.1 13.6 7.8 - 6.0 5.8 5.1 3.1 - - 0.3 3.0 - - — 13 7.1 13 0.4 12.8 - 5.2 2.2 20 /7 8.2 2.2 9.3 38.6 38.9 41.3 48.5 46·8 692 810 719 669 662 1016 985 1003 1093 913 6 64.7 8.0 5.7 12.9 7.7 49.4 710 980 2.73 0,03 6.65 0.69 0.22 0.01 7 8 9 10 1 L 12 50 3 49 9 65 3 61.2 50 3 50 20 1 21 8 8 0 13.3 21 5 21 0.6 0.6 6.4 0.4 5.9 5.9 2 0.3 - 8 0.5 12.6 5 20.9 20.5 7.0 2 48.7 43.5 44.9 43 734 750 714 674 9 5.8 7 0.6 9 0.4 4 20.2 4 43.6 744 1008 1013 993 928 1012 4.9 5.4 0.01 0*07 5 3.1 9.2 13 2.2 51.3 728 972 240 I „ n 裝 訂 線 (請先閲讀背面之注^^項再填寫本頁) 本紙張尺度逋用中國國家梂準(CNS > A4说格(21OX297公釐)/3 13 2 A7 ____B7 五、發明説明⑴*·) 表IA記錄相同Z玻璃組成份,但是K氧化物莫_百分
比表示。 表 IA 1 2 3 4 5 6 Si〇2 72.43 80.13 63.56 68.05 64.03 75.05 a1203 5.33 9.38 16.36 5.02 9.20 5.48 B2 〇3 7.52 0.00 6.48 5.28 5.04 0.00 MgO 5.16 0.00 0.00 0.39 5.12 0.00 CaO 0.00 0.00 0.00 20.19 8,72 7.09 SrO 8.39 0.28 9.33 0,00 3,49 8.67 BaO 0.97 9.93 4*04 0.90 4.18 3.51 7 8 9 10 11 12 S1O2 63.65 62.03 7 3.34 61.56 62.46 56.70 AI2O3 14.96 15.94 5.27 10.57 15.70 14.39 B2O3 0.67 0.00 0.00 0.00 0.00 0.00 MgO 1.23 11.05 9.90 0.33 10.76 15.59 CaO 8.63 0.42 0.00 18.83 0.81 3.72 SrO 0.27 0.34 8.20 0.00 0.26 8.42 BaO 10.35 9.97 3.09 8.54 9.82 0.95 I. I 1 ~裝·~ ^ ~~ —訂 Μ 線 (請先閲讀背面之注$項再填寫本頁) 鯉濟部中央樣準局只工消費合作社印製 上述玻璃之測試說明出組成份仔细之控制必需實拖於 配製破瑀過程Μ產生具有本發明數項特性。組成份1,4以 及9十分類似,除了組成份1具有較多SrO含量,組成份具有 較多CaO含悬,以及組成份9不含B2〇3而BaO含量鵂多。組成 份1,4,9為依序地増高,組成份1為勉強地可接受" 本紙張尺度逍用中國國家梂準(CNS ) A4規格(210X297公釐) I斗 丄4 308582 $ 五、發明説明(θ) 比較亦列舉說明各種氧it物含鼉對耐久性之影響:因 此,比較組成份11M及12顯示出鹼土金腦氧化物之替代對 耐久性有非常大之影# 同時,比較組成份1以及6顯示省 略B2 〇3增多鹼土金驅氧化物將有較佳之影響。 如先前所說明,優先使用CTE範画而與code 7059玻璃 相匹配為45-50x10· 7/1〇。鋁矽酸鹽種類A义B卞坡璃具 有之CTE在該範園内,Μ及其組成份Μ氧化物重量丙分比 為計算摞準,包含:
Af B, Si〇2 50-57 55-67 Al2 〇3 16-20 6-<13 B2〇3 0-5.5 0-7.5 MgO 2-2.75 2-6.5 CaO l-<7 0*17 . SrO 0.5-15 0-14. BaO 1-21 2-9.5 表II揭示於該棰類範園内範例性之組成份。組成份13 ,14以及15為棰類Α1之範例,同時16,17W ft 18為種類Β1之 範例。 --------------裝------訂------線 ί 邮 (請先閲讀背面之注意Ϋ項再填寫本頁) 經濟部中央標準局貝工消費合作社印製 本紙張尺度逋用中团國家梯準(CNS ) A4规格(210X 297公釐) (5* 丄5 A7 B7 五、發明説明(丨3 )
表 II 丄3 14 15 16 17 18 Sl〇2 56. 1 52. 9 53. 7 65. 5 56. 6 66 . 9 A1203 17.0 18.2 18. 0 3 ‘ 1 1丄. 2 6 . 1 B203 - 2. 0 4. 7 ~ Ί · 4 - MgO 2. 3 2. 4 2 . 4 6. 1 2. 2 6 · 2 CaO 6. 8 6 . 9 6 . 5 5 . 2 2. 1 - SrO 5 5. 1 5, 1 12· 9 12. 0 13. 3 BaO 12· 9 12. 6 9 · 6 2. 2 8. 7 7 . 5 CTE 43. 3 48. 4 45. 3 48. 1 47. 3 45. 5 Strain 718 695 677 693 650 699 HC1 0. 08 0. 62 1.9 0. 03 0. 3 0· 01 Density 2. 31 2· 80 2. 70 2. 70 2· 72 2. 73 使用於δθ之玻璃板ft先採用CTE範画已說明為32-40X 10-7 /r 鋁δ々酸鹽棰類c1及沪中之玻瑀具有CTES在該範 圍内Μ及組成份Μ氧化物重量百分比為計算標準,包含: ------------裝------訂----- (請先閲讀背面之注項再填寫本頁) 經濟部中央揉率局貝工消費合作社印製
Cf D' S1O2 54-57 55-65.5 Αΐ2 〇3 17.5-23 8-13 Β2〇3 5-15 4-13 MgO 2-2.75 2-3.5 CaO 1·5-<7 0-6.5 SrO 2-6 0-13 BaO 0.5-9.5 2-21 本紙張尺度逋用中困國家梂準(CNS > Α4规格(210X 297公釐) 五 、發明説明(丨 A7 B7 丄6 2 表1II渴示出這些棰類範例性組成份,,C 份19,20及21為範例’同時D,棰類M.組成份22 例。 f棰類 ,23¾ 表 III 19 20 21 22 23 24 Sl〇2 56 .6 55.5 56.2 64.6 65 64.3 Al2 〇3 22 4 18.4 22.9 12.9 8.2 13 B2〇3 7 8 9.3 5.9 4.4 7.8 4.4 MgO 2 3 2.3 2.4 2.2 3.1 2.2 CaO 3 4 6.9 4.9 6.3 - 6.3 SrO 4 9 5.0 5.0 0.8 13 1.2 BaO 2 6 2.6 2.7 8.8 2.2 8.7 CTE 32 2 40 35.4 38.8 38.6 38.8 經濟部中央標準局貝工消费合作社印裝
Strain 692 666 706 683 692 686 HC1 1.8 2.6 0.8 0.02 2.7 0.02
Density 2.52 2.54 2.56 2.55 2.54 2.56 在本發明優先使用之實施例中,平板顯示器之玻瑀平 板之應變點大於660η K及在先前所說明之HC1測試中重量 損失小於lmg/cm2 我們發琨在兩種鋁矽酸鹽種類之玻璃 符合«先使用之品質。E及F兩棰組成份Μ氧化物Μ量百分 比為計蓴基準,包含: 本紙張尺度適用中國國家梂率(CNS > Α4規格(210X297公釐) 1*7 ---------,--^------^------ h.~' (請先閲讀背面之注$項再填寫本頁) A7 B7 五、發明説明(γ) 經濟部中央標準局貝工消費合作社印製 E F Sl〇2 54-58 55-6 7 Al2 〇3 16- 23 6-14 B2 〇3 0-6 0-7 . 5 MgO 2- 4.5 0-7 CaO 1- 12.5 0-18.5 SrO 2.5-15.5 0-15 BaO 0 - -14.5 1-21 MgO+CaO+SrO+BaO 15-27 18-28 表IVE及IVF揭示出每-種類代表性範例R氧丨b物重量 百分比為分析《準之組成份Μ及相闞特性 : 表 IVE 25 26 2Ί 28 29 30 Sl〇2 55.16 56.95 56.7 57.63 58.19 54.69 Α1;Ϊ 〇3 18.19 16.81 22.63 19.21 19.43 17.79 B2 〇3 0,95 0 0.997 5.3 3 5,3 5 0.94 MgO 2.23 2.25 2.31 2.6 2.67 2.17 CaO 1.46 4.7 6.7 8.63 8.7 6 1.39 SrO 13,06 4.82 4*86 5 . 5 5.61 14.25 BaO 8*94 14.47 5.77 1.09 0 8.7 6 CTE 45.4 46.8 41.8 42 4丄 46.8 Strain 731 724 748 684 688 722 HC1 0.07 4 0.06 0.57 0.16 0-48 0.11 Density 2.7 9 2.429 2.676 2.579 2-564 2.819 ------------,——^------ΐτ------Λ / ί (請先閲讀背面之注$項再填寫本頁) 本紙張尺度適用中國國家橾準(CNS ) A4規格(21 OX 297公釐) 18 2 A7 B7 五、發明説明(lb) 經濟部中央梯準局貝工消费合作社印製 表 IVF 31 32 33 34 35 36 Sl〇2 55.7 55.53 56.9 65.49 66.93 66.85 A12 03 13.6 13.3 13.03 8.14 6.1 6.23 B2 〇3 5.1 3.2 7.3 0 0 0 MgO 3 2.27 2.2 6.08 6.23 0.13 CaO Ί Λ 4.08 0 5.16 0 5.69 SrO 5.2 12.59 11.9 12.92 13.26 13.29 BaO 9.3 9.03 8,7 2.22 7.48 7.8 CTE 46.8 50.2 45 48.1 45*5 50.9 Strain 662 675 662 693 699 699 HC1 0.22 0.076 0.31 0.03 0.0134 0*0058 Density 2.79 2.429 2.676 2.579 2.564 2.819 另外 -棰構成破璃板®先使用實施例 ,其密度小於2 . 5 公克/立方公分c 符合該要求之坡璃為種類G ,其組成份範 圍Η氧化物為分析基準 ,包含: Sx〇2 54.8 -57 AI2 〇3 16.8 -21.8 B2〇3 0 -14 MgO 2.2-2.5 CaO 1.5 -9.5 SrO 4.5-5.5 BaO 0.1 -14.5 MgO+CaO+SrO+BaO 12.5-27 --------------裝------訂------—.線—ί (請先閲讀背面之注f項再填寫本頁) 本紙張尺度適用中國國家梂準(CNS > A4規格(210X297公釐) \〇1 • 19 3 3〇β583 A7 B7 五、發明説明(丨η) 表V揭示出代表性範例以氧ib物垂量百分比為分析基 準之組成份Μ及相關特性: 37 38 39 -40 41 42 Si〇2 55. 9 56. 08 56 .95 56. 14 56 . 6 56. 72 Al2 〇3 21. 7 3 16. 98 16, .81 21. 1 16. 92 19. 04 B2〇3 · 9. 76 0 0 1. 06 0. 99 9 · 73 MgO 2 . 45 2. 28 2 .25 2· 28 2. 31 2. 37 CaO 2· 36 6 . 78 4 • 7 5. 59 9 . 4 6. 95 SrO 5. 13 5 4 .82 4. 84 4 . 78 5 . 07 BaO 2. 67 12. 86 14 .47 8. 99 8. 91 0· 12 CTE 31. 2 48. 3 46 ,8 43 . 6 49 · 3 37 * 6 Strain 680 718 724 73 7 710 670 HC1 3. 36 0♦ 08 0 • 06 0· 27 0· 15 4. 15 Density 2, 496 2. 312 2 • 429 2* 467 2 . 265 2. 494 本發 明另外 * itti 範例 性 X作實拖 例為 : CTE為32-40x10- 7之鋁矽酸鹽玻璃以及鋁矽酸鹽棰類 主要包含: a. 54-57% S1O2, 17.5-23% AI2O3, 5-15% B2O3 , 2-2.75% MgO, 1.5-<7% CaO, 2-6% SrOft 0.5-9.5% BaO, 經濟部中央棣準局貝工消費合作社印製 --------------餐------1T-----id (請先閲讀背面之注$項再填寫本頁)
b. 57-65.5% S1O2, 8-13% AI2O3, 4-13 B2〇3, 2-3.5% MgO, 0-6.5% CaO, 0-13% SrOft 2-21% BaO CTE為4 5-50x10-7之鋁矽酸鹽坡璃M及鋁矽酸鹽種類 主要包含: a. 50-57% S1O2 , 16-20% AI2O3, 0-5.5% Ba〇3, 2- 本紙張尺度逋用中國國家梂準(CNS ) A4说格(210X297公釐) 20 4 A7 B7 五、發明説明(\《) 2.75% MgO., 1-<7% CaO, 0.5-15% SrO^ 1-21% BaO, b. 55-67% S1O2 , 6-<13% AI2O3, 0-7.5 B2 0:i , 2-6.5% MgO, 0-17.5% CaO, 0-14.5% SrO及 2-9.5% BaO: -------------裝------訂------,線 / { ~ (請先閲讀背面之注^^項再填寫本頁) 經濟部中央標準局貝工消費合作社印製 本紙張尺度適用中國國家梂準(CNS ) A4規格(210X 297公釐) 1/
Claims (1)
- 經濟部中央標準局貞工消費合作社印裂 ^0.6583 b8 C8 _ D8 々、申請專利範圍 1 - 棰鋁的酸鹽坡璃,其應變點高於640彳?,tt浸漬於95Γ 5%重量比HC1水溶液24小時後重量損失小於20mg/cm2 ,CTE 界31與57x10- 7 / Γ ,名義t:不含鹼金屬氧化物K及其組 成份Μ氧ib物重量吞分比為計算基準®含49-67% Si〇2 ,至 少 6% Al2〇3 ,當 55-67% Si02時 Al2〇3為 6-14%以及當 49-58% Sl〇2時 AI2O3為 16 — 23%,Si〇2+Al2〇3>68%, 0-15% B2O3 ,Μ 及至少一棰鹼土金喔氧化物由依所顯示比例之0-21% BaO , 0-15* Sr0,0-18* CaO,0-8% MgO種類中選取出从及 12-30% BaO+CaO+SrO+MgO 2. 依據申請專利範圃第1項鋁矽醃鹽玻璃,其CTE在31-44X 10-7广P範圍内K及由鋁69酸鹽破璃細分類屮選取出,其組 成份Μ氧化物靈最百分比為計算基準包含 a. 49-67% S1O2, 17.5-23% Al2〇3, 0 -14.5% B203 , 0-8% MgO, 0-9% CaO, 0.4-13.5% SrO, 0-21% BaO,i皮璃 包含至少-棰鹼土金矚氧化物為所顯示之比例以ft BaO + CaO+SrO+MgO缌含 II 為 13-28%, b. 57-66% S1O2 , 8-14% AI2O3 , 0 — 13% B2O3 , 0-4.5% MgO, 0-9% CaO, 0.5-13% SrO, 2-21% BaO 3. 依據申請專利範園第1項鋁矽酸鹽玻璃,其CTE在44~57x 10- 7广(、範圍内Μ及由鋁矽酸鹽玻璃细分類中S取出,其組 成份Μ氧化物重量ft分比為計算基準包含 a. 50-57% S1O2, 16-22% AI2O3, 0-5.5% B2〇3, 0.5 一3% MgO, 1-12.5% CaO, 0.5-15% SrO, 1-21% BaO, b. 55-67% S1O2 , 6-14% AI2O3 , 0-7.5% B2〇3 , 0- 本紙張尺度逋用中國國家梯準(CNS ) A4规格(210X 297公釐) I--------·:1 裝------訂-----^~'線—· (請先Μ讀背面之注$項再填寫本頁) 經濟部中央標準局貝工消費合作社印製 S0.6$83 b8 C8 D8六、申請專利範圍 6.5% MgO, 0-18.5% CaO, 0-15.5% SrO, 1-9.5% BaO,W 及 MgO+CaO+SrO+BaO總含量為 16.5-28% 4 .依據申請專利範圍第1項鋁矽酸鹽坡瑀,其應變點大於 660ΐ:’ Μ及庄浸漬於95Γ 5¾重量比HC1水溶液24小時後重壘 損失小於Img/cm2 Μ及由鋁矽酸玻璃刖分類中選取出,其 組成份Μ氧化物重屋百分比為計算基準包含 a. 54-58% S1O2 , 16-23% AI2O3 , 0—6% B2O3, 2-4.5% MgO, 1-12.5% CaO, 2.5-15.5% Sr〇K 0-14.5% BaO, MgO +CaO+SrO+BaO為 15-27%, b. 55-67% S1O2 , 6-14% AI2O3, 0-7.5% Bz〇3, 0-7% MgO , 0-18.5% CaO , 0-15% SrO , 1- 21% BaO,MgO+CaO+SrO +BaO為 18-28% 5 .依據申請專利範園第 1項鋁矽酸鹽坡璃,其密度小於2 . 5 公萣/立方公分Μ及組成份包含54 · 8-57% Si〇2 , 16.8-21 · 8% AI2O3, 0-14% B2O3, 2.2-2.5% MgO, 1.5-9.5% CaO, 4.5- 5 :5% SrO, 0.1-14.5% BaO, MgO+CaO+SrO+BaO為 12.5 — 27%.:· (請先閲讀背面之注意事項再填寫本頁) -裝. 訂 本紙張度適用中國國家揉率(CNS > A4規格(210 X 297公釐) >3