JP5530072B2 - 積層被覆物としての使用に適した生分解性ポリマーフィルムおよびシートならびにラップその他のパッケージング材料 - Google Patents
積層被覆物としての使用に適した生分解性ポリマーフィルムおよびシートならびにラップその他のパッケージング材料 Download PDFInfo
- Publication number
- JP5530072B2 JP5530072B2 JP2008064441A JP2008064441A JP5530072B2 JP 5530072 B2 JP5530072 B2 JP 5530072B2 JP 2008064441 A JP2008064441 A JP 2008064441A JP 2008064441 A JP2008064441 A JP 2008064441A JP 5530072 B2 JP5530072 B2 JP 5530072B2
- Authority
- JP
- Japan
- Prior art keywords
- biodegradable polymer
- soft
- hard
- film
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
特に、折り曲げたり、封止したり、または容易に閉止したり、基体に封止したりするために操作できるシートおよびフィルムに容易に形成可能な改良したバイオポリマーを提供することはパッケージング業界における進歩となるであろう。
さらに、現存するバイオポリマーに比べて広範な温度範囲にわたって温度安定性が高いシートおよびフィルムに容易に形成可能な改良された生分解性ポリマーを提供することはこの業界において進歩である。
このような、改良されたバイオポリマーを本明細書において開示する。
以下は原出願の国際出願日の請求の範囲である。
[特許請求の範囲]
[請求項1] 約10℃より高いガラス転移温度を有する少なくとも1種の硬質合成生分解性ポリマー;および
約0℃より低いガラス転移温度を有する少なくとも1種の軟質生分解性ポリマー;
を含んで構成される生分解性ポリマーブレンドであって、
前記ポリマーブレンドが押出成形シートおよびブロー成形フィルムのうち少なくとも1種への形成に適する、生分解性ポリマーブレンド。
[請求項2] 硬質生分解性ポリマーが、改質ポリエチレンテレフタレート、ポリエステルアミド、またはラクチドまたは炭素数4以下のヒドロキシ酸のうち少なくとも1種から形成される単位を有する脂肪族ポリエステルのうち少なくとも1種を含む、請求項1記載の生分解性ポリマーブレンド。
[請求項3] 硬質生分解性ポリマーが、ポリ乳酸;ポリ乳酸誘導体;テレフタレート基の一部がスルホン化されエチレン基の一部がアルキレンオキシド基またはポリアルキレンオキシド基のうち少なくとも1種で置換された改質ポリエチレンテレフタレート;グリコリド、ラクチドおよびε−カプロラクトンから形成された単位を含むターポリマー;または少なくとも1種の二酸、少なくとも1種のジオール、および少なくとも1種のアミノ酸から形成されたポリエステルアミド;のうち少なくとも1種を含む、請求項1記載の生分解性ポリマーブレンド。
[請求項4] 軟質生分解性ポリマーが、ラクチドまたは少なくとも5の炭素数を有するヒドロキシ酸のうち少なくとも1種から形成される単位を有する脂肪族ポリエステル;脂肪族ジオール、脂肪族二酸および芳香族二酸から形成される単位を有するポリエステル;またはコハク酸および脂肪族ジオールから形成される単位を有するポリエステル;のうち少なくとも1種を含む、請求項1記載の生分解性ポリマーブレンド。
[請求項5] 軟質生分解性ポリマーが、アジピン酸、ジアルキルテレフタレート、および少なくとも1種の脂肪族ジオールから形成される単位を有する脂肪族−芳香族コポリエステル;ポリカプロラクトン;ポリヒドロキシブチラート−ヒドロキシバレラートコポリマー;ポリブチレンスクシネート;ポリブチレンスクシネートアジペート;またはポリエチレンスクシネート;のうち少なくとも1種を含む、請求項1記載の生分解性ポリマーブレンド。
[請求項6] 軟質生分解性ポリマーが熱可塑性的処理可能性デンプンを含む請求項1記載の生分解性ポリマーブレンド。
[請求項7] 硬質生分解性ポリマーが生分解性ポリマーブレンドのうち約20〜約99重量%の範囲の濃度で含まれ、かつ軟質生分解性ポリマーが生分解性ポリマーブレンドのうち約1〜約80重量%の範囲の濃度で含まれる、請求項1記載の生分解性ポリマーブレンド。
[請求項8] 硬質生分解性ポリマーが生分解性ポリマーブレンドのうち約50〜約98重量%の範囲の濃度で含まれ、かつ軟質生分解性ポリマーが生分解性ポリマーブレンドのうち約2〜約50重量%の範囲の濃度で含まれる、請求項1記載の生分解性ポリマーブレンド。
[請求項9] 硬質生分解性ポリマーが生分解性ポリマーブレンドのうち約80〜約95重量%の範囲の濃度で含まれ、かつ軟質生分解性ポリマーが生分解性ポリマーブレンドのうち約5〜約20重量%の範囲の濃度で含まれる、請求項1記載の生分解性ポリマーブレンド。
[請求項10] 硬質生分解性ポリマーが約20℃より高いガラス転移温度を有する、請求項1記載の生分解性ポリマーブレンド。
[請求項11] 硬質生分解性ポリマーが約30℃より高いガラス転移温度を有する、請求項1記載の生分解性ポリマーブレンド。
[請求項12] 硬質生分解性ポリマーが約40℃より高いガラス転移温度を有する、請求項1記載の生分解性ポリマーブレンド。
[請求項13] 軟質生分解性ポリマーが約−10℃より低いガラス転移温度を有する、請求項1記載の生分解性ポリマーブレンド。
[請求項14] 軟質生分解性ポリマーが約−20℃より低いガラス転移温度を有する、請求項1記載の生分解性ポリマーブレンド。
[請求項15] 軟質生分解性ポリマーが約−30℃より低いガラス転移温度を有する、請求項1記載の生分解性ポリマーブレンド。
[請求項16] 少なくとも1種の非生分解性ポリマーをさらに含む、請求項1記載の生分解性ポリマーブレンド。
[請求項17] 少なくとも1種の粒子充填剤をさらに含む、請求項1記載の生分解性ポリマーブレンド。
[請求項18] 少なくとも1種の可塑化剤をさらに含む、請求項1記載の生分解性ポリマーブレンド。
[請求項19] 硬質ポリマーおよび軟質ポリマーのうち少なくとも1種が、1種以上のジイソシアネート連鎖延長剤を含む請求項1記載の生分解性ポリマーブレンド。
[請求項20] 生分解性ポリマーブレンドがシートまたはフィルムの形態を有する、請求項1記載の生分解性ポリマーブレンド。
[請求項21] シートまたはフィルムがパッキングラップとして使用するのに適した折れ固定性を有する請求項20記載の生分解性ポリマーブレンド。
[請求項22] シートまたはフィルムが少なくとも約100MPaのヤング率を有する、請求項20記載の生分解性ポリマーブレンド。
[請求項23] シートまたはフィルムが少なくとも約150MPaのヤング率を有する、請求項20記載の生分解性ポリマーブレンド。
[請求項24] シートまたはフィルムが少なくとも約200MPaのヤング率を有する、請求項20記載の生分解性ポリマーブレンド。
[請求項25] シートまたはフィルムが嵩高い手触りを増すためにテクスチャ化されている、請求項20記載の生分解性ポリマーブレンド。
[請求項26] シートまたはフィルムが少なくとも1部に印刷されている、請求項20記載の生分解性ポリマーブレンド。
[請求項27] シートまたはフィルムが少なくとも1種の付加的なシートまたはフィルムで積層される、請求項20記載の生分解性ポリマーブレンド。
[請求項28] シートまたはフィルムが製造されたモールド物品で積層される、請求項20記載の生分解性ポリマーブレンド。
[請求項29] 軟質ポリマーが合成ポリマーを含む、請求項1記載の生分解性ポリマーブレンド。
[請求項30] 約10℃より高いガラス転移温度を有する少なくとも1種の合成生分解性ポリマー;および
約0℃より低いガラス転移温度を有する少なくとも1種の合成生分解性ポリマー;
を含む生分解性ポリマーブレンドであって、
前記ポリマーブレンドが押出成形シートおよびブロー成形フィルムのうち少なくとも1種への形成に適する、生分解性ポリマーブレンド。
[請求項31] 約10℃より高いガラス転移温度を有する少なくとも1種の合成生分解性ポリマー;および
約0℃より低いガラス転移温度を有する少なくとも1種の生分解性ポリマー;
を含み、シートまたはフィルムの形態を有する生分解性ポリマーブレンドであって、
前記生分解性シートまたはフィルムがパッキングラップとしての使用に適する折れ固定性を有する、生分解性ポリマーブレンド。
約10℃より高いガラス転移温度を一般に有するポリマーとして特徴付けられる比較的硬質なポリマーは、生分解性ポリマーブレンドにおいて約20〜約99重量%の範囲の濃度を有すると好ましく、より好ましくは約50〜約98重量%であり、最も好ましくは約80%〜約95重量%である。
約0℃より低いガラス転移温度を有するポリマーとして特徴付けられる比較的軟質のポリマーは、生分解性ポリマーブレンドのうち、約1%〜約80重量%の濃度範囲を有すると好ましく、より好ましくは約2%〜約50重量%の範囲であり、最も好ましくは約5%〜約20重量%である。
本発明のこれらのおよび他の特徴は以下の記載からより充分に明らかになり、以下に説明した発明を実施することによりわかる。
本発明は、非ブレンドの生分解性ホモポリマーおよびコポリマーに比較して非常に改良された特性を有する生分解性ポリマーブレンドに関する。このような特性としては、改良された強度、可撓性、伸び率、および温度安定性を含む。さらに、このようなブレンドは、環境中に廃棄された際分解不可能であり、特別な処理なしでは容易に印刷できず、かつ固定された折れ特性に乏しい、従来のプラスチックより優れている。
本発明の範囲のバイオポリマーは、生物の作用を通して分解されるポリマーを含む。このようなポリマーはポリエステル、ポリエステルアミド、ポリカーボネート等、ある範囲の合成ポリマーを含む。生物分解反応は典型的に酵素触媒反応であり、かつ一般に水媒体中で生じる。蛋白質、セルロース、およびデンプン等の加水分解可能な結合を有する天然の巨大分子は一般に微生物の加水分解酵素により生物分解に感受性である。しかし、少しの人工的なポリマーも生分解性がある。ポリマーの親水性/疎水性の特性はこれらの生物分解能に非常に影響し、より極性のポリマーは一般により容易に生物分解可能である。生物分解能に影響する他の重要なポリマー特性は結晶化度および鎖自由度がある。
「硬質」と「軟質」ポリマー間の区別はある程度曖昧ではあるが、デンプンまたは他の水分感受性材料から製造したモールド物品における等積層コーティングとしての使用、またはラップまたは他のパッケージング材料としての使用のために適したフィルムまたはシートを製造することが目的である場合には特に、所望の性能基準を有するポリマーブレンドを得るために一緒にブレンドするポリマーを決定する際に有益な分類である。
ポリ乳酸は典型的には約59℃のガラス転移温度および約178℃の融点を有する。これは伸び率が低く、非常に硬い。
本発明にかかるポリマーブレンドの範囲内で使用される別の硬質ポリマーはCPLAとして知られている。これはPLAの誘導体であり、大日本インキ社から販売されている。2つのクラスのCPLAが販売されており、「CPLAハード」および「CPLAソフト」と呼ばれる。これらは両方共、本発明でいう「硬質」ポリマーである。CPLAハードは60℃のガラス転移温度を有するが、CPLAソフトは51℃のガラス転移温度を有する。
PACポリマー社は、ガラス転移温度が10〜28℃のポリエチレンカーボネート(PEC)を製造する。PECは本発明にかかるポリマーブレンドを製造するための硬質ポリマーである。
一般に、「軟質」すなわち低硬度であると特徴付けられるこれらのポリマーとしては典型的には約0℃より低いガラス転移温度を有するポリマーを含む。本発明の範囲内の軟質バイオポリマーは好ましくは約−10℃より低いガラス転移温度、より好ましくは約−20℃、最も好ましくは約−30℃を有する。前記範囲は、「軟質」ポリマーの「ガラス転移温度」が必ずしも明確な温度ではないがある範囲の温度にあることが多いという事実を光量に入れる試みである。
PESホモポリマーをエチレングリコールおよびコハク酸を反応させることによりかつ連鎖延長剤としてHMDIまたはジフェニルメタンジイソシアネートを使用することにより調製する。
スクシネートベース脂肪族ポリエステルを三井等圧、日本触媒、Cheil Synthetics、イーストマン化学、およびSunkyon Industruesも製造している。
所望の特性を付与するために、本発明の生分解性ポリマーブレンド内に数多くの任意成分が含まれる。
押出および/またはフィルムブロー、または、特に比較的硬質のポリマーブレンドの最終加工特性等のプロセスを改良するために、可塑化剤を添加することができる。硬質ポリマーブレンドは、製造中および製造後の、高温安定性、強度、低伸び率、高固定折れ性、「ブロッキング」抵抗性等の特性基準により決定される。このような場合、可塑化剤は、ポリマーブレンドが製造および/または特性基準を満たすことができるために必要である。
本発明で使用される任意の可塑化剤は、非制限的に大豆油、ヒマシ油、TWEEN20、TWEEN40、TWEEN60、TWEEN80、TWEEN85,ソルビタンモノラウレート、ソルビタンモノオレアート、ソルビタンモノパルミタート、ソルビタントリオレアート、ソルビタンモノステアラート、PEG、PEG誘導体、N,N−エチレンビスステアルアミド、N,N−エチレンビスオレアミド、ポリ(1,6−ヘキサメチレンアジペート)その他の適合性低分子量ポリマー等の重合性可塑化剤等を含む。
充填剤は任意の理由で添加され、非制限的に、ヤング率、折れの固定性、硬さの増加、コストおよび製造中の「ブロック」または自己接触に対するポリマーブレンドの傾向性の減少を含む。高アスペクト比を有する繊維のような充填剤は本発明のシートおよびフィルムの強度、破損エネルギー、折れ固定性を高める。本発明の範囲内の充填剤は一般にこれらの3つの分類に入る:(1)無機粒子充填剤、(2)繊維、(3)有機充填剤。
「粒子」または「微粒子充填剤」の用語は、種々の異なる形やアスペクト比の充填剤粒を包含するために広く解釈されるべきである。一般に、「粒子」は約10:1より小さいアスペクト比(すなわち長さ対厚さの比)を有する固体についていう。約10:1より大きいアスペクト比を有する固体は以下の議論により「繊維」として理解されるかもしれない。
ポリマーブレンドの物理特性を改良するために、広範な繊維を任意に使用可能である。前記充填剤同様、繊維は典型的に熱可塑性相とは別にこれと区別された固相を構成する。しかし、繊維の形のために、即ち、少なくとも約10:1より大きいアスペクト比を有するために、粒子充填剤よりも強度および靱性を付与することがより可能である。本発明において使用される「繊維」および「繊維材料」は共に無機繊維および有機繊維を含む。繊維は成形可能な材料に、可撓性、延性、曲げ性、凝集力、伸性、撓み性、靱性、折れ固定性、および破壊エネルギーを増加するために、ならびに得られたシートおよび物品の曲げ強度および引張強度を高めるために添加される。
本発明のポリマーブレンドは広範な有機充填剤を含むことができる。ポリマーブレンドおよび添加される有機充填剤の融点に依存して、有機充填剤は分離した粒子として残り、熱可塑性相と別の固相を構成してもよいし、あるいは部分的にまたは全体的に溶解して熱可塑性相と部分的にまたは完全に結合してもよい。
TPSに加えて、本発明のポリマーブレンドの範囲内で使用される他の天然ポリマーとしては、デンプンおよびセルロースの誘導体、蛋白質およびこの誘導体、多糖類ガムおよびその誘導体等その他の多糖類を含む。
デンプン誘導体の例としては、非制限的に改質デンプン、カチオン性デンプンおよびアニオン性デンプン、およびスターチアセタート、スターチヒドロキシエチルエーテル、アルキルスターチ、デキストリン、アミンスターチ、ホスフェートスターチおよびジアルデヒドスターチ等のデンプンエステルを含む。
適切な蛋白質ベースポリマーとしては例えばザイン(Zein:登録商標)(コーン由来プロルアミン)、コラーゲン(動物関連組織および骨から抽出される)およびこれらの誘導体(例えばゼラチンおよびグルー)、カゼイン(牛乳中の基本的な蛋白質)、ひまわり蛋白質、卵蛋白質、大豆蛋白質、野菜ゼラチン、グルテン、およびこれらの混合物または誘導体等を含む。
ポリマーブレンドの重要な特徴は一般的に生分解性であると考えられることであるが、生分解性ではない1種以上のポリマーが確実に本発明の範囲内にある。非生分解性ポリマーが一般的に優勢な連続相よりむしろ分散相を構成する場合、非生分解性ポリマー含有ポリマーブレンドは、少なくとも部分的には生分解性である。分解した場合、ポリマーブレンドは、後に非生分解性残渣が残り、これは非生分解性ポリマーの完全なフィルムおよびシートより優れている。
A.濃度範囲
ポリマーブレンド内の種々の成分濃度は、最終ブレンドの所望の物理的および機械的特性、特定のブレンドから製造されるべき物品の特性基準、所望の物品に製造するための製造やブレンドに使用されるプロセス装置、およびブレンド内の特別な成分を含む多くの要因に依存する。当業者は本発明に開示の特定の実施例等の開示から日常的な試験を通して種々の成分の濃度を選択し、最適化可能である。
前記範囲は、上記のような任意の添加成分を除いた硬質および軟質ポリマーのブレンドの観点において測定される。
ポリマーブレンドは所望の特性を有するように設計される。食事、他の消耗食物、特にファーストフード(例えばサンドイッチ、バーガー、デザート)を閉じ込めるために使用されるラップ等の「ラップ」として使用されることを意図したシートおよびフィルムの場合、折ったり、ラップしたり、他の操作により所望の方向にするために良好な「折れ固定」性を有するシートおよびフィルムを提供することが一般に望ましい。このようなラップは、自然に折りがもどったり、ラップが外れたりしないようにその方向を維持しようとし、数多くのプラスチックシートおよびフィルムについて生じる(例えばポリエチレン)。
本発明のポリマーブレンドを製造するために、熱可塑性組成物を製造する業界で知られている混合装置を使用することは本発明の範囲内である。本発明のブレンドを形成するために使用できる適当な混合装置の例としてはバス社(Buss Company)から販売される混練ブロックを有するメッシュスクリューを具えた二軸混練機、ブラベンダーミキサー、ゼイショーン(Theysohn)TSK 045コンパウンダ(これは同じ方向のシャフト回転を有する二軸エクストルーダであり、複数の加熱および処理領域を有する)、加熱可能なオーガースクリューを有するバスコニーダ(Buss Ko-Kneader)、ベーカーパーキンス MPC/V−30ダブルおよびシングルエクストルーダ、シングルまたはツインオーガーOMCエクストルーダ、モデルEPV/36Dエクストルーダ、BATTAGGIONME100直流スローミキサおよびHAAKEレオメックスエクストルーダを含む。
本発明の生分解性ブレンドおよびそれから得られる物品を形成するための、より具体的な組成物および処理条件を開示するために以下の実施例を示す。これらの実施例は本発明の生分解性ポリマーブレンドの種々の混合設計、およびブレンドを製造するための種々の方法およびこれから得られるシートおよびフィルムを製造するための種々の方法を含んでいる。
例1〜3
フィルムは以下の混合設計を有する生分解性ポリマーブレンドから製造され、前ポリマーブレンドの重量%で濃度を表す。
フィルムを以下の混合設計を有する生分解性ポリマーブレンドから製造した。その濃度は全ポリマーブレンドの重量%で表す。
例6
フィルムを以下の混合設計の生分解性ポリマーブレンドから製造した。その濃度は全ポリマーブレンドの重量%で表す。
例7
フィルムを以下の混合設計を有する生分解性ポリマーブレンドから製造した。その濃度は全ポリマーブレンドの重量%で表される。
フィルムを、以下の混合設計を有する生分解性ポリマーブレンドから製造した。その濃度は全ポリマーブレンドの重量%で表す。
結論として、本発明はパッキング材料としての使用に適した強度および可撓性を有するシートおよびフィルムに容易に形成可能な生分解性ポリマーを提供する。
また、基材を容易に閉じ込め封止するために折れたり、シールしたり、その他の操作が可能なシートおよびフィルムに容易に形成可能な生分解性ポリマーを提供する。
さらに、本発明は現存するバイオポリマーに比べて広い温度範囲にわたって高い熱安定性を有するシートおよびフィルムに容易に形成可能な生分解性ポリマーを提供する。
Claims (24)
- 生分解性ポリマーブレンドを含む食物ラップであって、
10℃より高いガラス転移温度を持ち、硬質および軟質の生分解性ポリマーの総合重量の20〜99重量%の量で含まれ、改質ポリエチレンテレフタレート;ポリエステルアミド;グリコリド、ラクチドおよびε−カプロラクトンから形成される単位を含むターポリマー;ポリアルキレンカーボネートのうち少なくとも1種からなる群より選択される、少なくとも1種の硬質の合成生分解性ポリマー、および
0℃より低いガラス転移温度を持ち、硬質および軟質の生分解性ポリマーの総合重量の1〜80重量%の量で含まれ、脂肪族ジオール、脂肪族二酸および芳香族二酸から形成される単位を含む脂肪族−芳香族コポリエステルを含有する、少なくとも1種の軟質の合成生分解性ポリマー
を含み、
ポリマーブレンドが、硬質または軟質の生分解性ポリマーのそれら自身によってのものよりも高い強度および/または伸びを持ち、およびシートまたはフィルムのうち少なくとも1種への形成に適する、食物ラップ。 - 軟質の合成生分解性ポリマーが、さらに、ポリヒドロキシバレラート、ポリカプロラクトン;ポリヒドロキシブチラート−ヒドロキシバレラートコポリマー;ポリブチレンスクシネート;またはポリブチレンスクシネートアジペートのうち少なくとも1種を含み、脂肪族−芳香族コポリエステルが、アジピン酸、ジアルキルテレフタレートおよび少なくとも1種の脂肪族ジオールから形成される単位を含む、請求項1に記載の食物ラップ。
- 硬質の合成生分解性ポリマーが硬質および軟質の生分解性ポリマーの総合重量の80〜95重量%の量で含まれ、かつ軟質の生分解性ポリマーが硬質および軟質の生分解性ポリマーの総合重量の5〜20重量%の量で含まれる、請求項1または2に記載の食物ラップ。
- 硬質の合成生分解性ポリマーが20℃より高いガラス転移温度を持つ、請求項1〜3のいずれか一項に記載の食物ラップ。
- 軟質の合成生分解性ポリマーが−10℃より低いガラス転移温度を持つ、請求項1〜4のいずれか一項に記載の食物ラップ。
- 生分解性ポリマーブレンドがさらに少なくとも1種の粒子充填剤を含み、粒子充填剤が少なくとも1種の無機充填剤粒子からなる、請求項1〜5のいずれか一項に記載の食物ラップ。
- 生分解性ポリマーブレンドがシートまたはフィルムの形態である、請求項1〜6のいずれか一項に記載の食物ラップ。
- シートまたはフィルムがパッケージングラップとしての使用に適した永久折れ目性を持つ、請求項7に記載の食物ラップ。
- シートまたはフィルムが少なくとも1種の付加的なシートまたはフィルムで積層されるか、または製造されたモールド物品に積層される、請求項8に記載の食物ラップ。
- 生分解性ポリマーブレンドを含む食物ラップであって、
10℃より高いガラス転移温度を持ち、硬質および軟質の生分解性ポリマーの総合重量の20〜99重量%の量で含まれ、改質ポリエチレンテレフタレート;ポリエステルアミド;ポリアルキレンカーボネートからなる群より選択される少なくとも1種の硬質の合成生分解性ポリマー、および
0℃より低いガラス転移温度を持ち、硬質および軟質の生分解性ポリマーの総合重量の1〜80重量%の量で含まれる、ポリブチレンスクシネート;ポリブチレンスクシネートアジペート;ポリエチレンスクシネート;脂肪族ジオール、脂肪族二酸および芳香族二酸から形成される単位を含むポリエステル;およびアジピン酸、ジアルキルテレフタレートおよび少なくとも1種の脂肪族ジオールから形成される単位を含む脂肪族−芳香族コポリエステルからなる群より選択され、前記ポリマーのいずれかが随意に1種以上のジイソシアネート連鎖延長剤を含む、少なくとも1種の軟質の合成生分解性ポリマー
を含み、
ポリマーブレンドがシートまたはフィルムのうち少なくとも1種への形成に適する、食物ラップ。 - 生分解性ポリマーブレンドが、少なくとも1種の天然のポリマーまたはその誘導体をさらに含む、請求項10に記載の食物ラップ。
- 硬質の合成生分解性ポリマーが硬質および軟質の生分解性ポリマーの総合重量の50〜98重量%の量で含まれ、かつ軟質の生分解性ポリマーが硬質および軟質の生分解性ポリマーの総合重量の2〜50重量%の量で含まれる、請求項10または11に記載の食物ラップ。
- 生分解性ポリマーブレンドが、少なくとも1種の無機充填剤粒子をさらに含む、請求項10〜12のいずれか一項に記載の食物ラップ。
- 生分解性ポリマーブレンドを含む食物ラップであって、
10℃より高いガラス転移温度を持ち、硬質および軟質の生分解性ポリマーの総合重量の20〜99重量%の量で含まれ、改質ポリエチレンテレフタレートからなる群より選択される少なくとも1種の硬質の合成生分解性ポリマー、および
0℃より低いガラス転移温度を持ち、および硬質および軟質の生分解性ポリマーの総合重量の1〜80重量%の量で含まれる、少なくとも1種の軟質の生分解性ポリマー
を含み、
ポリマーブレンドがシートまたはフィルムのうち少なくとも1種への形成に適する、食物ラップ。 - 軟質の生分解性ポリマーが、ポリヒドロキシバレラート、ポリカプロラクトン;ポリヒドロキシブチラート−ヒドロキシバレラートコポリマー;ポリブチレンスクシネート;ポリブチレンスクシネートアジペート;ポリエチレンスクシネート;脂肪族ジオール、脂肪族二酸および芳香族二酸から形成される単位を含むポリエステル;および熱可塑性加工デンプンからなる群より選択され、前記ポリマーのいずれかが随意に1種以上のジイソシアネート連鎖延長剤を含む、請求項14に記載の食物ラップ。
- 軟質の生分解性ポリマーがアジピン酸、ジアルキルテレフタレート、および少なくとも1種の脂肪族ジオールから形成される単位を含む少なくとも1種の脂肪族−芳香族コポリエステルからなる、請求項15に記載の食物ラップ。
- 生分解性ポリマーブレンドが、少なくとも1種の無機充填剤粒子をさらに含む、請求項14〜16のいずれか一項に記載の食物ラップ。
- 生分解性ポリマーブレンドから形成されるシートまたはフィルムを含む食物ラップであって、
10℃より高いガラス転移温度を持ち、硬質および軟質の生分解性ポリマーブレンドの20〜99重量%の量で含まれ、改質ポリエチレンテレフタレート;ポリエステルアミド;グリコリド、ラクチドおよびε−カプロラクトンから形成される単位を含むターポリマー;ポリアルキレンカーボネート;ポリ乳酸;ポリ乳酸誘導体;ラクチドまたは炭素数4以下のヒドロキシ酸のうち少なくとも1種から形成される単位を有する脂肪族ポリエステル:ポリヒドロキシブチラートのうち少なくとも1種からなる群より選択される、少なくとも1種の硬質の合成生分解性ポリマー、および
0℃より低いガラス転移温度を持ち、硬質および軟質の生分解性ポリマーブレンドの1〜80重量%の量で含まれる、少なくとも1種の軟質の生分解性ポリマー
を含み、
ポリマーブレンドが、各生分解性ポリマーのそれ自身によってのものよりも高い強度および/または伸びを持ち、
生分解性シートまたはフィルムが、所望の方向に折ったり、ラップしたりその他の操作を加えた際、シートまたはフィルムが実質的にその方向を維持するようにシートまたはフィルムが永久折れ目性を持つように、テクスチャ化されるか、または一定量で少なくとも1種の粒子充填剤を含む、食物ラップ。 - シートまたはフィルムが少なくともその1部に印刷を含む、請求項18に記載の食物ラップ。
- シートまたはフィルムが少なくとも1種の付加的なシートまたはフィルムで積層されるかまたは製造した成形品に積層される、請求項18または19に記載の食物ラップ。
- 生分解性ポリマーブレンドの使用であって、生分解性ポリマーブレンドが、
10℃より高いガラス転移温度を持ち、硬質および軟質の生分解性ポリマーの総合重量の20〜99重量%の量で含まれ、改質ポリエチレンテレフタレート;ポリエステルアミド;グリコリド、ラクチドおよびε−カプロラクトンから形成される単位を含むターポリマー;ポリアルキレンカーボネートのうち少なくとも1種からなる群より選択される、少なくとも1種の硬質の合成生分解性ポリマー、および
0℃より低いガラス転移温度を持ち、硬質および軟質の生分解性ポリマーの総合重量の1〜80重量%の量で含まれ、脂肪族ジオール、脂肪族二酸および芳香族二酸から形成される単位を含む脂肪族−芳香族コポリエステルを含有する、少なくとも1種の軟質の合成生分解性ポリマー
を含み、
前記ポリマーブレンドが、食物ラップとしてのシートまたはフィルムのうち少なくとも1種への形成について、硬質または軟質の生分解性ポリマーのそれら自身によってのものよりも高い強度および/または伸びを持ち、および適したものである、使用。 - 生分解性ポリマーブレンドの使用であって、生分解性ポリマーブレンドが、
10℃より高いガラス転移温度を持ち、硬質および軟質の生分解性ポリマーの総合重量の20〜99重量%の量で含まれ、改質ポリエチレンテレフタレート;ポリエステルアミド;およびポリアルキレンカーボネート;およびポリヒドロキシブチラートからなる群より選択される少なくとも1種の硬質の合成生分解性ポリマー、および
0℃より低いガラス転移温度を持ち、硬質および軟質の生分解性ポリマーの総合重量の1〜80重量%の量で含まれる、ポリブチレンスクシネート;ポリブチレンスクシネートアジペート;ポリエチレンスクシネート;脂肪族ジオール、脂肪族二酸および芳香族二酸から形成される単位を含むポリエステル;およびアジピン酸、ジアルキルテレフタレートおよび少なくとも1種の脂肪族ジオールから形成される単位を含む脂肪族−芳香族コポリエステルからなる群より選択され、前記ポリマーのいずれかが随意に1種以上のジイソシアネート連鎖延長剤を含む、少なくとも1種の軟質の合成生分解性ポリマー
を含み、
前記ポリマーブレンドが食物ラップとしてのシートまたはフィルムのうち少なくとも1種への形成に適する、使用。 - 生分解性ポリマーブレンドの使用であって、生分解性ポリマーブレンドが、
10℃より高いガラス転移温度を持ち、硬質および軟質の生分解性ポリマーの総合重量の20〜99重量%の量で含まれ、改質ポリエチレンテレフタレートより選択される少なくとも1種の硬質の合成生分解性ポリマー、および
0℃より低いガラス転移温度を持ち、および硬質および軟質の生分解性ポリマーの総合重量の1〜80重量%の量で含まれる、少なくとも1種の軟質の生分解性ポリマー
を含み、
ポリマーブレンドが食物ラップとしてのシートまたはフィルムのうち少なくとも1種への形成に適する、使用。 - 生分解性ポリマーブレンドから形成されるシートまたはフィルムの使用であって、生分解性ポリマーブレンドが、
10℃より高いガラス転移温度を持ち、硬質および軟質の生分解性ポリマーブレンドの20〜99重量%の量で含まれる、改質ポリエチレンテレフタレート;ポリエステルアミド;グリコリド、ラクチドおよびε−カプロラクトンから形成される単位を含むターポリマー;ポリアルキレンカーボネート;ポリ乳酸;ポリ乳酸誘導体;ラクチドまたは炭素数4以下のヒドロキシ酸のうち少なくとも1種から形成される単位を有する脂肪族ポリエステル:ポリヒドロキシブチラートのうち少なくとも1種からなる群より選択される、少なくとも1種の硬質の合成生分解性ポリマー、および
0℃より低いガラス転移温度を持ち、硬質および軟質の生分解性ポリマーブレンドの1〜80重量%の量で含まれる、少なくとも1種の軟質の生分解性ポリマー
を含み、
ポリマーブレンドが、各生分解性ポリマーのそれ自身によってのものよりも高い強度および/または伸びを持ち、
生分解性シートまたはフィルムが、所望の方向に折ったり、ラップしたりその他の操作を加えた際、食物ラップとしてのシートまたはフィルムが実質的にその方向を維持するようにシートまたはフィルムが永久折れ目性を持つように、テクスチャ化されるか、または一定量で少なくとも1種の粒子充填剤を含む、使用。