JP2019202934A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2019202934A5 JP2019202934A5 JP2019162190A JP2019162190A JP2019202934A5 JP 2019202934 A5 JP2019202934 A5 JP 2019202934A5 JP 2019162190 A JP2019162190 A JP 2019162190A JP 2019162190 A JP2019162190 A JP 2019162190A JP 2019202934 A5 JP2019202934 A5 JP 2019202934A5
- Authority
- JP
- Japan
- Prior art keywords
- chemically strengthened
- strengthened glass
- glass according
- zro
- cao
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Links
- ODINCKMPIJJUCX-UHFFFAOYSA-N calcium monoxide Chemical compound [Ca]=O ODINCKMPIJJUCX-UHFFFAOYSA-N 0.000 claims 16
- CPLXHLVBOLITMK-UHFFFAOYSA-N magnesium oxide Chemical compound [Mg]=O CPLXHLVBOLITMK-UHFFFAOYSA-N 0.000 claims 16
- GEIAQOFPUVMAGM-UHFFFAOYSA-N oxozirconium Chemical compound [Zr]=O GEIAQOFPUVMAGM-UHFFFAOYSA-N 0.000 claims 16
- 239000005345 chemically strengthened glass Substances 0.000 claims 15
- 229910018072 Al 2 O 3 Inorganic materials 0.000 claims 8
- 229910018068 Li 2 O Inorganic materials 0.000 claims 8
- 229910004298 SiO 2 Inorganic materials 0.000 claims 8
- IATRAKWUXMZMIY-UHFFFAOYSA-N strontium oxide Inorganic materials [O-2].[Sr+2] IATRAKWUXMZMIY-UHFFFAOYSA-N 0.000 claims 8
- QVQLCTNNEUAWMS-UHFFFAOYSA-N barium oxide Inorganic materials [Ba]=O QVQLCTNNEUAWMS-UHFFFAOYSA-N 0.000 claims 6
- XLOMVQKBTHCTTD-UHFFFAOYSA-N zinc monoxide Chemical compound [Zn]=O XLOMVQKBTHCTTD-UHFFFAOYSA-N 0.000 claims 4
- 239000011521 glass Substances 0.000 claims 3
- 229910010413 TiO 2 Inorganic materials 0.000 claims 2
- 239000000203 mixture Substances 0.000 claims 2
- 239000005341 toughened glass Substances 0.000 claims 2
- 238000004031 devitrification Methods 0.000 claims 1
- 239000011159 matrix material Substances 0.000 claims 1
Claims (13)
- 酸化物基準のモル百分率表示で、ＳｉＯ２を５４〜６２％、Ａｌ２Ｏ３を１２〜２０％、Ｂ２Ｏ３を０．５〜５％、Ｐ２Ｏ５を０〜４％、Ｌｉ２Ｏを５〜１６％、Ｎａ２Ｏを５〜１４％、Ｋ２Ｏを０〜２％、ＭｇＯを０〜１０％、ＣａＯを０〜１％、ＳｒＯを０〜１％、ＢａＯを０〜１％、ＺｎＯを０〜５％、ＴｉＯ２を０〜１％、ＺｒＯ２を０〜４％を含有し、
ＳｉＯ２、Ａｌ２Ｏ３、Ｂ２Ｏ３、Ｐ２Ｏ５、Ｌｉ２Ｏ、Ｎａ２Ｏ、Ｋ２Ｏ、ＭｇＯ、ＣａＯ、ＳｒＯ、ＢａＯ及びＺｒＯ２の各成分の酸化物基準のモル百分率表示による含有量を用いて、下記式に基づき算出されるＸの値が４００００以上である化学強化用ガラス。
Ｘ＝ＳｉＯ２×３２９＋Ａｌ２Ｏ３×７８６＋Ｂ２Ｏ３×６２７＋Ｐ２Ｏ５×（−９４１）＋Ｌｉ２Ｏ×９２７＋Ｎａ２Ｏ×４７．５＋Ｋ２Ｏ×（−３７１）＋ＭｇＯ×１２３０＋ＣａＯ×１１５４＋ＳｒＯ×７３３＋ＺｒＯ２×５１．８ - ＳｉＯ２、Ａｌ２Ｏ３、Ｂ２Ｏ３、Ｐ２Ｏ５、Ｌｉ２Ｏ、Ｎａ２Ｏ、Ｋ２Ｏ、ＭｇＯ、ＣａＯ、ＳｒＯ、ＢａＯ及びＺｒＯ２の各成分の酸化物基準のモル百分率表示による含有量を用いて、下記式に基づき算出されるＹの値が０．７以上である、請求項１に記載の化学強化用ガラス。
Ｙ＝ＳｉＯ２×０．００８８４＋Ａｌ２Ｏ３×０．０１２０＋Ｂ２Ｏ３×（−０．００３７３）＋Ｐ２Ｏ５×０．０００６８１＋Ｌｉ２Ｏ×０．００７３５＋Ｎａ２Ｏ×（−０．００２３４）＋Ｋ２Ｏ×（−０．００６０８）＋ＭｇＯ×０．０１０５＋ＣａＯ×０．００７８９＋ＳｒＯ×０．００７５２＋ＢａＯ×０．００４７２＋ＺｒＯ２×０．０２０２ - 酸化物基準のモル百分率表示によるＬｉ ２ Ｏの含有量が１３％以下である、請求項１または２に記載の化学強化用ガラス。
- 酸化物基準のモル百分率表示によるＡｌ ２ Ｏ ３ の含有量が１３％以上である、請求項１〜３のいずれか１項に記載の化学強化用ガラス。
- 失透温度Ｔが、粘度が１０４ｄＰａ・ｓとなる温度Ｔ４以下である請求項１〜４のいずれか１項に記載の化学強化用ガラス。
- 破壊靭性値が０．７ＭＰａ・ｍ１／２以上である請求項１〜５のいずれか１項に記載の化学強化用ガラス。
- ヤング率が７４ＧＰａ以上である請求項１〜６のいずれか１項に記載の化学強化用ガラス。
- 表面圧縮応力（ＣＳ）が４５０ＭＰａ以上の化学強化ガラスであって、
前記化学強化ガラスの母組成が、酸化物基準のモル百分率表示で、ＳｉＯ２を５４〜６２％、Ａｌ２Ｏ３を１２〜２０％、Ｂ２Ｏ３を０．５〜５％、Ｐ２Ｏ５を０〜４％、Ｌｉ２Ｏを５〜１６％、Ｎａ２Ｏを５〜１４％、Ｋ２Ｏを０〜２％、ＭｇＯを０〜１０％、ＣａＯを０〜１％、ＳｒＯを０〜１％、ＢａＯを０〜１％、ＺｎＯを０〜５％、ＴｉＯ２を０〜１％、ＺｒＯ２を０〜４％を含有し、
前記化学強化ガラスの母組成におけるＳｉＯ２、Ａｌ２Ｏ３、Ｂ２Ｏ３、Ｐ２Ｏ５、Ｌｉ２Ｏ、Ｎａ２Ｏ、Ｋ２Ｏ、ＭｇＯ、ＣａＯ、ＳｒＯ、ＢａＯ及びＺｒＯ２の各成分の酸化物基準のモル百分率表示による含有量を用いて、下記式に基づき算出されるＸの値が４００００以上である化学強化ガラス。
Ｘ＝ＳｉＯ２×３２９＋Ａｌ２Ｏ３×７８６＋Ｂ２Ｏ３×６２７＋Ｐ２Ｏ５×（−９４１）＋Ｌｉ２Ｏ×９２７＋Ｎａ２Ｏ×４７．５＋Ｋ２Ｏ×（−３７１）＋ＭｇＯ×１２３０＋ＣａＯ×１１５４＋ＳｒＯ×７３３＋ＺｒＯ２×５１．８ - 前記化学強化ガラスの応力プロファイル中で応力がゼロになる部分のガラス表面からの深さ（ＤＯＬ）から２０μｍガラス表面側の深さにおける圧縮応力値ＣＳＤＯＬ−２０を用いて下記式により算出されるΔＣＳＤＯＬ−２０（単位：ＭＰａ／μｍ）が０．４以上である請求項８に記載の化学強化ガラス。
ΔＣＳＤＯＬ−２０＝ＣＳＤＯＬ−２０／２０ - 前記ΔＣＳＤＯＬ−２０（単位：ＭＰａ／μｍ）が４．０以下である請求項８または９に記載の化学強化ガラス。
- 板厚ｔが２ｍｍ以下である請求項８〜１０のいずれか１項に記載の化学強化ガラス。
- ガラス表面から１００μｍの深さの部分の圧縮応力値（ＣＳ１００）が１５ＭＰａ以上である請求項８〜１１のいずれか１項に記載の化学強化ガラス。
- 前記ＣＳ１００と板厚ｔ（ｍｍ）の二乗との積（ＣＳ １００ ×ｔ２）が１２０ＭＰａ・ｍｍ２以下である請求項１２に記載の化学強化ガラス。