TW201639973A - 覆銀銅粉及使用其之銅糊、導電性塗料、導電性片、以及覆銀銅粉之製造方法 - Google Patents
覆銀銅粉及使用其之銅糊、導電性塗料、導電性片、以及覆銀銅粉之製造方法 Download PDFInfo
- Publication number
- TW201639973A TW201639973A TW104135570A TW104135570A TW201639973A TW 201639973 A TW201639973 A TW 201639973A TW 104135570 A TW104135570 A TW 104135570A TW 104135570 A TW104135570 A TW 104135570A TW 201639973 A TW201639973 A TW 201639973A
- Authority
- TW
- Taiwan
- Prior art keywords
- silver
- copper powder
- group
- coated copper
- coated
- Prior art date
Abstract
本發明提供一種能夠使銅粉彼此之接點增多而確保優異之導電性、且較佳地用於導電性糊或電磁波屏蔽等用途之覆銀銅粉。
本發明之覆銀銅粉1呈現樹枝狀形狀，該樹枝狀形狀具有直線成長之主幹2與自該主幹2分支出之多個枝3，主幹2及枝3係平板狀銅粒子集合而構成，該平板狀銅粒子係根據掃描式電子顯微鏡(SEM)觀察而求出之剖面平均厚度為0.02μm~5.0μm者，於該銅粒子之表面被覆有銀，該覆銀銅粉1之平均粒徑(D50)為1.0μm~100μm，並且銅粒子之相對於平板狀面為垂直方向之最大高度，為該平板狀面之水平方向之最大長度的1/10以下。
Description
本發明係關於一種表面被覆有銀之銅粉(覆銀銅粉)，並且關於用作導電性糊等之材料且能夠改善導電性之具有新穎形狀的覆銀銅粉及使用其之銅糊、導電性塗料、導電性片、以及該覆銀銅粉之製造方法。
於形成電子機器中之配線層或電極等時，多使用如樹脂型糊或燒成型糊、電磁波屏蔽塗料之類的使用銀粉或覆銀銅粉等金屬填料之糊劑或塗料。將銀粉或覆銀銅粉之金屬填料糊塗佈或印刷於各種基材上，進行加熱硬化或加熱燒成之處理，而形成作為配線層或電極等之導電膜。
例如樹脂型導電性糊係由金屬填料與樹脂、硬化劑、溶劑等構成，將其印刷於導電體電路圖案或端子上，於100℃~200℃加熱硬化而成為導電膜，形成配線或電極。關於樹脂型導電性糊，由於熱硬化型樹脂受熱而硬化收縮，因此將金屬填料壓接而使之相互接觸，藉此金屬填料彼此重疊，結果形成電性連接之電流通路。該樹脂型導電性糊於200℃以下之硬化溫度下進行處理，因此用於印刷配線板等使用不耐熱材料之基板。
另一方面，燒成型導電性糊係由金屬填料與玻璃、溶劑等構
成，將其印刷於導電體電路圖案或端子上，於600℃~800℃加熱燒成，而成為導電膜，形成配線或電極。燒成型導電性糊藉由較高溫度下之處理而使金屬填料彼此燒結，從而確保導通性。如此，該燒成型導電性糊由於在較高之燒成溫度進行處理，故而有無法用於如使用樹脂材料的印刷配線基板之問題，但由於金屬填料以高溫處理之方式進行燒結，故而能夠實現低電阻。因此，燒成型導電性糊被用於積層陶瓷電容器之外部電極等。
另一方面，電磁波屏蔽被用來防止自電子機器產生電磁雜訊，尤其近年來，電腦或手機之殼體變為樹脂製，因此為了確保殼體之導電性，提出有利用蒸鍍法或濺鍍法形成較薄之金屬皮膜之方法、或者塗佈導電性塗料之方法、於所需部位貼附導電性片而屏蔽電磁波之方法等。其中，多採用使金屬填料分散於樹脂中並進行塗佈之方法、或使金屬填料分散於樹脂中並加工成片狀再將其貼附於殼體之方法，該等方法於加工步驟中無需特殊設備，自由度優異。
然而，上述使金屬填料分散於樹脂中而進行塗佈之情形或加工成片狀之情形時，由於金屬填料於樹脂中之分散狀態不一致，故而為了取得電磁波屏蔽效率，提高金屬填料之填充率等方法成為必須。然而，於該情形時，因大量金屬填料之添加而導致產生片材重量變重、且樹脂片之可撓性受損等問題。因此，例如於專利文獻1中，為了解決該等問題而提出有使用平板狀金屬填料之方法，藉此，能夠形成電磁波屏蔽效果優異、可撓性亦良好之較薄片材。
此處，為了製作平板狀銅粉，例如專利文獻2中揭示有獲得適合用作導電性糊之填料的薄片狀銅粉之方法。具體而言，以平均粒徑0.5
~10μm之球狀銅粉作為原料，使用球磨機或振磨機，利用磨機內所裝填之介質的機械能而機械性地加工成平板狀。
又，例如專利文獻3中揭示有關於導電性糊用銅粉末、詳細而言作為通孔用及外部電極用銅糊可獲得高性能之圓盤狀銅粉末及其製造方法的技術。具體而言，於介質攪拌磨機投入粒狀霧化銅粉末，使用直徑1/8~1/4英吋之鋼球作為粉碎介質，添加以重量計相對於銅粉末為0.5~1%之脂肪酸，於空氣中或惰性氣體環境中進行粉碎，藉此加工成平板狀。
另一方面，作為該等導電性糊或電磁波屏蔽用所使用之金屬填料，多採用銀粉，但隨著低成本化之潮流，存在使用覆銀銅粉之傾向，該覆銀銅粉係藉由於較銀粉廉價之銅粉之表面塗覆銀而減少銀使用量者。
作為於銅粉表面被覆銀之方法，存在藉由置換反應而於銅表面被覆銀之方法、與於含還原劑之無電解鍍敷溶液中被覆銀之方法。
關於藉由置換反應而被覆銀之方法，利用於溶液中銅溶出時產生之電子而將銀離子還原，藉此於銅表面形成銀之被膜。例如專利文獻4中揭示有藉由向存在銀離子之溶液中投入銅粉，從而利用銅與銀離子之置換反應而於銅表面形成銀之被膜的製造方法。然而，利用該置換反應之方法中，一旦於銅表面形成銀之被膜，則銅之溶解不會再進行，因此存在無法控制銀之被覆量之問題。
為了解決該問題，有於含還原劑之無電解鍍敷液被覆銀之方法。例如專利文獻5中提出有藉由使銅粉與硝酸銀於溶存有還原劑之溶液中進行反應而製造被覆銀之銅粉的方法。
另外，作為銅粉，已知有呈“被稱為枝晶(dendrite)狀”
之樹枝狀析出的電解銅粉，由於形狀為樹枝狀，故而具有表面積較大之特徵。如此藉由為枝晶狀之形狀，當將其用於導電膜等時，該枝晶之枝重合，易實現導通，又，與球狀粒子相比，粒子彼此之接點數變多，因此具有能夠減少導電性糊等中之導電性填料之量的優點。例如於專利文獻6及7中提出有於呈枝晶狀銅粉之表面被覆有銀之覆銀銅粉。
具體而言，專利文獻6及7中揭示有如下之枝晶，其特徵為以自主軸分支出之長枝作為基於枝晶狀而進一步成長者，該覆銀銅粉與先前之樹枝狀結晶相比粒子彼此之接點變多，藉此導通性提高，若用於導電性糊等，則即便減少導電性粉末之量而亦能夠提高導電性。
另一方面，專利文獻8中指出，於將樹枝狀銅粉用作導電性糊或電磁波屏蔽用樹脂等之金屬填料之情形時，若該金屬填料為呈樹枝狀延伸之形狀，則樹枝狀銅粉彼此會超出所需地相互纏繞，因此易發生凝集，又，流動性下降而非常難以操作，從而降低生產性。再者，專利文獻8中揭示，為了提高電解銅粉本身之強度，於用以使電解銅粉析出之電解液之硫酸銅水溶液中添加鎢酸鹽，藉此能夠提高電解銅粉本身之強度，使樹枝不易折斷，實現高強度。
如此，將樹枝狀銅粉用作導電性糊等之金屬填料並非易事，此亦導致糊劑之導電性不易獲得改善。
為了確保導電性，具有三維形狀之樹枝狀形狀者與粒狀者相比易確保接點，可期待確保作為導電性糊或電磁波屏蔽之較高導電性。然而，先前之呈枝晶狀形狀之覆銀銅粉，由於為特徵在於自主軸分支出之長枝的枝晶，且為細長枝狀之形狀，故而若自確保接點之方面考慮則結構簡
單，對使用更少覆銀銅粉且有效確保接點之形狀而言並非是理想形狀。
[專利文獻1]日本特開2003-258490號公報
[專利文獻2]日本特開2005-200734號公報
[專利文獻3]日本特開2002-15622號公報
[專利文獻4]日本特開2000-248303號公報
[專利文獻5]日本特開2006-161081號公報
[專利文獻6]日本特開2013-89576號公報
[專利文獻7]日本特開2013-100592號公報
[專利文獻8]日本特開2011-58027號公報
本發明係鑒於上述實際情況而提出者，其目的在於提供一種能夠使銅粉彼此之接點增多而確保優異之導電性、且較佳地用於導電性糊或電磁波屏蔽等用途之覆銀銅粉。
本發明人等為了解決上述課題，反覆進行努力研究。結果發現，藉由為下述覆銀銅粉，銅粉彼此之接點變多而表現出優異之導電性，從而完成本發明，上述覆銀銅粉呈現具有主幹與自該主幹分支出之多個枝的樹枝狀形狀，主幹及枝係特定剖面平均厚度之平板狀銅粒子集合而構成，於該銅粒子之表面被覆有銀，抑制相對於平板狀面為垂直方向之成長。即，本發明提供以下者。
(1)本發明之第1發明係一種覆銀銅粉，其呈現樹枝狀形
狀，該樹枝狀形狀具有直線成長之主幹與自該主幹分支出之多個枝，上述主幹及上述枝係平板狀銅粒子集合而構成，該平板狀銅粒子係根據掃描式電子顯微鏡(SEM)觀察而求出之剖面平均厚度為0.02μm~5.0μm者，於該銅粒子之表面被覆有銀，該覆銀銅粉之平均粒徑(D50)為1.0μm~100μm，上述銅粒子之相對於平板狀面為垂直方向之最大高度，為該平板狀面之水平方向之最大長度的1/10以下。
(2)關於本發明之第2發明，如第1發明之覆銀銅粉，其中，銀被覆量相對於經銀被覆之覆銀銅粉整體之質量100%，為1質量%~50質量%。
(3)關於本發明之第3發明，如第1或第2發明之覆銀銅粉，其體密度為0.5g/cm3~5.0g/cm3之範圍。
(4)關於本發明之第4發明，如第1至第3發明中任一項之覆銀銅粉，其BET比表面積值為0.2m2/g~5.0m2/g。
(5)本發明之第5發明係一種金屬填料，其以整體之20質量%以上之比例含有第1至第4發明中任一項之覆銀銅粉。
(6)本發明之第6發明係一種導電性糊，係使第5發明之金屬填料與樹脂混合而成。
(7)本發明之第7發明係一種電磁波屏蔽用導電性塗料，係使用第5發明之金屬填料而成。
(8)本發明之第8發明係一種電磁波屏蔽用導電性片，係使用第5發明之金屬填料而成。
(9)本發明之第9發明係一種覆銀銅粉之製造方法，係製
造第1至第4發明之覆銀銅粉之方法，具有藉由電解法使銅粉自電解液析出至陰極上之步驟、與對該銅粉被覆銀之步驟，使上述電解液含有銅離子、1種以上之下述式(1)所表示之具有啡結構之化合物、及1種以上之非離子界面活性劑，從而進行電解，
[式(1)中，R1、R2、R3、R4、R6、R7、R8、R9分別各自為：選自由氫、鹵素、胺基、OH、=O、CN、SCN、SH、COOH、COO鹽、COO酯、SO3H、SO3鹽、SO3酯、苯磺酸及C1~C8烷基所組成之群中之基，R5為選自由氫、鹵素、胺基、OH、-O、CN、SCN、SH、COOH、COO鹽、COO酯、SO3H、SO3鹽、SO3酯、苯磺酸、低級烷基及芳基所組成之群中之基，A-為鹵化物陰離子]。
(10)本發明之第10發明係一種覆銀銅粉之製造方法，係製造如第1至第4發明之覆銀銅粉之方法，具有藉由電解法使銅粉自電解液析出至陰極上之步驟、與對該銅粉被覆銀之步驟，使上述電解液含有銅離子、1種以上之下述式(2)所表示之具有偶氮苯結構之化合物、及1種以上之非離子界面活性劑，從而進行電解，
[式(2)中，R1、R2、R3、R4、R5、R6、R7、R8、R9、R10分別各自為：選自由氫、鹵素、胺基、OH、=O、CN、SCN、SH、COOH、COO鹽、COO酯、SO3H、SO3鹽、SO3酯、苯磺酸、低級烷基及芳基所組成之群中之基]。
(11)本發明之第11發明係一種覆銀銅粉之製造方法，係製造第1至第4發明之覆銀銅粉之方法，具有藉由電解法使銅粉自電解液析出至陰極上之步驟、與對該銅粉被覆銀之步驟，使上述電解液含有銅離子、1種以上之下述式(3)所表示之具有啡結構與偶氮苯結構之化合物、及1種以上之非離子界面活性劑，從而進行電解，
[式(3)中，R1、R2、R4、R5、R6、R7、R8、R9、R10、R11、R12、R13分別各自為：選自由氫、鹵素、胺基、OH、=O、CN、SCN、SH、COOH、COO鹽、COO酯、SO3H、SO3鹽、SO3酯、苯磺酸及C1~C8烷基所組成之群中之基，R3為選自由氫、鹵素、胺基、OH、=O、CN、SCN、SH、COOH、COO鹽、COO酯、SO3H、SO3鹽、SO3酯、苯磺酸、低級烷基及芳基所組成之群中之基，A-為鹵化物陰離子]。
(12)本發明之第12發明係一種覆銀銅粉之製造方法，係製造第1至第4發明之覆銀銅粉之方法，具有藉由電解法使銅粉自電解液析出至陰極上之步驟、與對該銅粉被覆銀之步驟，使上述電解液含有銅離子、選自由下述式(1)所表示之具有啡結構之化合物、下述式(2)所表示之具有偶氮苯結構之化合物、及下述式(3)所表示之具有啡結構與偶氮苯結構之化合物所組成之群中之2種以上、以及1種以上之非離子界面活性劑，從而進行電解，
[式(1)中，R1、R2、R3、R4、R6、R7、R8、R9分別各自為：選自由氫、鹵素、胺基、OH、=O、CN、SCN、SH、COOH、COO鹽、COO酯、SO3H、
SO3鹽、SO3酯、苯磺酸及C1~C8烷基所組成之群中之基，R5為選自由氫、鹵素、胺基、OH、-O、CN、SCN、SH、COOH、COO鹽、COO酯、SO3H、SO3鹽、SO3酯、苯磺酸、低級烷基及芳基所組成之群中之基，A-為鹵化物陰離子]，
[式(2)中，R1、R2、R3、R4、R5、R6、R7、R8、R9、R10分別各自為：選自由氫、鹵素、胺基、OH、=O、CN、SCN、SH、COOH、COO鹽、COO酯、SO3H、SO3鹽、SO3酯、苯磺酸、低級烷基及芳基所組成之群中之基]，
[式(3)中，R1、R2、R4、R5、R6、R7、R8、R9、R10、R11、R12、R13分別各自為：選自由氫、鹵素、胺基、OH、=O、CN、SCN、SH、COOH、COO鹽、COO酯、SO3H、SO3鹽、SO3酯、苯磺酸及C1~C8烷基所組成之群中之基，R3為選自由氫、鹵素、胺基、OH、=O、CN、SCN、SH、COOH、COO鹽、COO酯、SO3H、SO3鹽、SO3酯、苯磺酸、低級烷基及芳基所組成之群中之基，A-為鹵化物陰離子]。
根據本發明之覆銀銅粉，能夠確保較多之接點，並且能夠獲得較大之接觸面積，確保優異之導電性，且防止凝集，從而可較佳地用於導電性糊或電磁波屏蔽等用途。
1‧‧‧(樹枝狀)覆銀銅粉
2‧‧‧主幹
3、3a、3b‧‧‧枝
4‧‧‧相對於平板狀面為水平方向(X-Y方向)之最大長度
5‧‧‧相對於平板狀面(X-Y面)為垂直方向之最大高度
圖1係示意性地表示樹枝狀覆銀銅粉之具體形狀之圖。
圖2係示意性地表示樹枝狀覆銀銅粉之具體形狀之圖。
圖3係表示藉由掃描式電子顯微鏡(SEM)以倍率5,000倍觀察作為先前例之銀被覆前之樹枝狀銅粉時之觀察影像的照片圖。
圖4係表示藉由掃描式電子顯微鏡(SEM)以倍率1,000倍觀察銀被覆前之樹枝狀銅粉時之觀察影像的照片圖。
圖5係表示藉由掃描式電子顯微鏡(SEM)以倍率1,000倍觀察樹枝狀覆銀銅粉時之觀察影像的照片圖。
圖6係表示藉由掃描式電子顯微鏡(SEM)以倍率1,000倍觀察樹枝狀
覆銀銅粉時之觀察影像的照片圖。
以下，針對本發明之覆銀銅粉之具體實施形態(以下稱為「本實施形態」)，一面參照圖式一面進行詳細說明。再者，本發明並不限定於以下之實施形態，可於不變更本發明之要旨之範圍進行各種變化。又，本說明書中，「X~Y」(X、Y為任意數值)之表述意指「X以上且Y以下」。
《1.樹枝狀覆銀銅粉》
關於本實施形態之覆銀銅粉，於使用掃描式電子顯微鏡(SEM)觀察時，呈現樹枝狀形狀(以下亦將本實施形態之覆銀銅粉稱為「樹枝狀覆銀銅粉」)，該樹枝狀形狀具有直線成長之主幹與自該主幹分支出之多個枝，該主幹及枝係由具有特定剖面平均厚度之平板狀銅粒子集合而構成，於該等平板狀銅粒子之表面被覆有銀。
具體而言，本實施形態之樹枝狀覆銀銅粉中，該主幹及枝係“根據SEM觀察而求出之剖面平均厚度為0.02μm~5.0μm之平板狀銅粒子”集合而構成，該覆銀銅粉之平均粒徑(D50)為1.0μm~100μm。並且，該樹枝狀覆銀銅粉之特徵在於：平板狀銅粒子之相對於其平板狀面為垂直方向之高度，為水平方向上之最大長度的1/10以下，抑制朝垂直方向之成長而具有平滑面。
本實施形態之樹枝狀覆銀銅粉1例如可藉由如下方式製作：將陽極與陰極浸漬於含銅離子之硫酸酸性之電解液中，通入直流電流而進行電解，藉此使銅粉析出至陰極上，對所獲得之銅粉之表面被覆銀，
該製作方法詳見下文。
圖1及圖2係示意性地表示本實施形態之樹枝狀覆銀銅粉之具體形狀之圖。如圖1所示，該樹枝狀覆銀銅粉1呈現具有直線成長之主幹2與自該主幹2分支出之多個枝3的樹枝狀形狀。再者，樹枝狀覆銀銅粉1中之枝3不僅指自主幹2分支出之枝3a、3b，還包括進而自該枝3a、3b分支出之枝。
並且，如上所述，主幹2及枝3係平板狀銅粒子集合而構成，該平板狀銅粒子係根據SEM觀察而求出之剖面平均厚度為0.02μm~5.0μm者。關於此種平板狀銅粒子之形成，如下所述，認為於電解析出銅粉時，電解液中所添加之特定添加劑吸附於銅粒子表面，藉此抑制成長，其結果成長為平板狀。再者，藉由對上述平板狀銅粒子之表面被覆銀而構成覆銀銅粉1。
然而，若銅粉亦沿例如圖2所示之相對於平板狀面之垂直方向(圖2中之Z方向)成長，則儘管分別成長為枝的銅粒子本身為平板狀、但會形成銅粒子亦沿垂直方向以突起之方式成長的銅粉。再者，圖2係表示水平於平板狀面之方向(平板方向)與垂直於該平板狀面之方向的圖，所謂平板方向係指X-Y方向，所謂垂直方向係指Z方向。
此處，圖3係表示對銀被覆前之樹枝狀銅粉，藉由SEM(倍率5,000倍)觀察亦相對於平板狀面沿垂直方向成長之銅粉時之觀察影像之一例的照片圖。該照片圖所示之樹枝狀銅粉形狀如下：銅粒子相對於平板狀面沿垂直方向成長而形成突起，又，一部分之平板狀面彎折而在垂直方向具有高度。
若如圖3之照片圖所示般銅粒子沿垂直方向成長，則例如於將基於該銅粉所製作之覆銀銅粉用在導電性糊或導電塗料等用途時，因該銅粒子沿垂直方向成長而導致銅粉成為大體積，因此無法獲得填充密度，從而產生無法充分確保導電性之問題。
相對於此，關於本實施形態之覆銀銅粉1，抑制相對於平板狀面為垂直方向之成長，從而成為具有大致平滑之面之銅粉。具體而言，如圖2所示，覆銀銅粉1中，相對於平板狀面為垂直方向之最大高度(圖2中之符號「5」)，為平板狀面之水平方向之長軸之最大長度(圖2中之符號「4」)的1/10以下。再者，所謂相對於平板狀面為垂直方向之最大高度5，並非平板狀面之厚度，而是例如於平板狀面形成有突起之情形時意指該突起之高度，即以平板狀之「面」為基準而與厚度方向相反之方向的“高度”。又，所謂相對於平板狀面為水平方向之最大長度4，意指平板狀面之長軸長度。
此處，圖4係表示如下觀察影像之一例的照片圖：藉由SEM(倍率1,000倍)對銀被覆前之樹枝狀銅粉觀察時之觀察影像，即相對於平板狀面為垂直方向之成長得以抑制的平板狀之樹枝狀銅粉之觀察影像。又，圖5係表示如下觀察影像之一例的照片圖：藉由SEM(倍率1,000倍)觀察對圖4所示之垂直方向之成長得以抑制之樹枝狀銅粉被覆銀所獲得之樹枝狀覆銀銅粉時之觀察影像。又，同樣地，圖6係表示如下觀察影像之一例的照片圖：藉由SEM(倍率1,000倍)觀察對垂直方向上之成長得以抑制之樹枝狀銅粉被覆銀所獲得之樹枝狀覆銀銅粉之另一部位時之觀察影像。如該等照片圖所示，可知相對於平板狀面為垂直方向上之成長得以抑
制，而成為具有大致平滑之面之樹枝狀且平板狀的銅粉。
藉由為上述垂直方向之成長得以抑制的平板之覆銀銅粉1，能夠確保銅粉彼此之接觸面積較大。並且，藉由該接觸面積變大，能夠實現低電阻、即高導電率。藉此，導電性更優異，又，能夠將該導電性維持於良好狀態，可較佳地用於導電性塗料或導電性糊之用途。又，樹枝狀覆銀銅粉1為平板狀銅粒子集合而構成，藉此亦能夠有助於配線材等之薄型化。
如上所述，樹枝狀覆銀銅粉1中，構成主幹2及枝3之被覆有銀之平板狀銅粒子1，其剖面平均厚度為0.02μm~5.0μm。關於被覆有銀之平板狀銅粒子之剖面平均厚度，較薄者更能發揮作為平板之效果。即，由剖面平均厚度為5.0μm以下之被覆有銀之平板狀銅粒子構成主幹2及枝3，藉此能夠確保銅粒子彼此、及由此構成之樹枝狀覆銀銅粉1彼此之接觸面積較大。
再者，被覆有銀之平板狀銅粒子之剖面平均厚度越薄，則樹枝狀覆銀銅粉1彼此接觸時之接點數越少。若被覆有銀之銅粒子之剖面平均厚度為0.02μm以上，則能夠確保充足之接點數，更佳為0.2μm以上，藉此能夠增加接點數．
又，關於本實施形態之樹枝狀覆銀銅粉1，其平均粒徑(D50)為1.0μm~100μm。平均粒徑可藉由變更下述電解條件而控制。又，視需要追加利用噴射磨機、樣品磨機(sample mill)、旋風磨機(cyclone mill)、珠磨機等機械粉碎或壓碎，藉此能夠進一步調整為所需大小。再者，平均粒徑(D50)可藉由例如雷射繞射散射式粒度分佈測定法進行測定。
此處，例如於專利文獻1中亦指出，成為樹枝狀覆銀銅粉之問題點，可列舉如下情況：於用作導電性糊或電磁波屏蔽用樹脂等之金屬填料時，由於樹脂中之金屬填料為呈樹枝狀延伸之形狀，故而樹枝狀銅粉彼此相互纏繞而發生凝集，於樹脂中分散不均。又，該凝集導致糊劑黏度上升，從而於藉由印刷而形成配線時出現問題。發生該等情況之原因在於樹枝狀覆銀銅粉之形狀(粒徑)較大，為了有效利用樹枝狀形狀並且解決該問題，必須減小樹枝狀覆銀銅粉之形狀。然而，若過度減小樹枝狀覆銀銅粉之粒徑，則無法確保該樹枝狀形狀。因此，為了確保樹枝狀形狀之效果，即，藉由為三維形狀而使表面積增大、成形性或燒結性優異、或經由枝狀部位牢固連結而能夠以較高強度成形的效果，樹枝狀覆銀銅粉必須為規定以上之大小。
就該方面而言，關於本實施形態之樹枝狀覆銀銅粉1，藉由其平均粒徑為1.0μm~100μm，使表面積增大，能夠確保良好之成形性或燒結性。進而，該樹枝狀覆銀銅粉1由於不僅為樹枝狀形狀，並且主幹2及枝3係由平板狀銅粒子1之集合體構成，故而藉由樹枝狀之三維效果、與構成該樹枝狀形狀之銅粒子1為平板狀之效果，能夠確保銅粉彼此有更多之接點。
關於製作平板狀覆銀銅粉之方法，如專利文獻2或專利文獻3之記載，揭示有利用機械方法成形為平板狀之方法。關於該機械方法，例如於將球狀銅粉成形為平板狀之情形時，必須於機械加工時防止銅氧化，因此添加脂肪酸，於空氣中或非活性氣體環境中進行粉碎，藉此加工成平板狀。然而，存在無法完全防止氧化之情況，或存在加工時所添加之脂肪
酸於糊化時對分散性造成影響之情況，因此必須於加工結束後將其去除，但該脂肪酸有時因機械加工時之壓力而牢固地固著於銅表面，從而產生無法完全去除之問題，於用作導電性糊或電磁波屏蔽用樹脂等之金屬填料時，氧化被膜或脂肪酸之附著會變成電阻變大之原因。
相對於此，本實施形態之樹枝狀覆銀銅粉1能夠於不進行機械加工之情況下直接藉由電解進行成長，而形成平板形狀，因此不會發生迄今為止於機械方法中成為問題之氧化問題或因脂肪酸殘留所引起之問題，成為表面狀態良好之銅粉，導電性成為極良好之狀態，於用作導電性糊或電磁波屏蔽用樹脂等之金屬填料時能夠實現低電阻。再者，有關該樹枝狀覆銀銅粉1之製造方法於下文詳細說明。
又，為了進一步實現低電阻，金屬填料之填充率成為問題。為了進一步提高填充率，平板狀之樹枝狀覆銀銅粉必須具有平滑性。即，關於本實施形態之樹枝狀覆銀銅粉1之形態，藉由相對於平板狀面為垂直方向之最大高度，為相對於平板狀面為水平方向之最大長度的1/10以下，而平滑性變高，填充率上升，並且銅粉彼此之面的接點增多，因此能夠進一步實現低電阻。
《2.銀被覆量》
本實施形態之樹枝狀覆銀銅粉1如上所述係由剖面平均厚度為0.02μm~5.0μm之平板狀且表面被覆有銀之銅粒子構成為樹枝狀而成者。以下關於對覆銀銅粉之表面之銀被覆進行說明。
本實施形態之樹枝狀覆銀銅粉1係對銀被覆前之樹枝狀銅粉，較佳為以相對於經銀被覆之該覆銀銅粉整體之質量100%為1質量%~
50質量%之比例被覆銀而成者，銀之厚度(被覆厚度)為0.1μm以下、較佳為0.05μm以下之極薄被膜。因此，樹枝狀覆銀銅粉1形成保持原本銀被覆前之樹枝狀銅粉形狀之形狀。因此，被覆銀前之銅粉之形狀、與對銅粉被覆銀後之覆銀銅粉之形狀兩者均具有樹枝狀之形狀。
樹枝狀覆銀銅粉1中之銀之被覆量如上所述，相對於經銀被覆之該覆銀銅粉1整體之質量100%，較佳為1質量%~50質量%之範圍。關於銀之被覆量，就成本觀點而言較佳為儘可能較少，但若過少，則無法確保於銅粉表面形成均勻之銀被膜，導致導電性下降。因此，作為銀之被覆量，相對於經銀被覆之該覆銀銅粉1整體之質量100%，較佳為1質量%以上，更佳為2質量%以上，進而較佳為5質量%以上。
另一方面，若銀之被覆量變多，則就成本觀點而言欠佳，又，若銅粉表面被覆有超出所需之銀，則存在構成樹枝狀覆銀銅粉1之銅粒子之表面之微細凸部消失之可能性。因此，作為銀之被覆量，相對於經銀被覆之該覆銀銅粉1整體之質量100%，較佳為50質量%以下，更佳為20質量%以下，進而較佳為10質量%以下。
又，本實施形態之樹枝狀覆銀銅粉1中，樹枝狀銅粉之表面所被覆之銀的平均厚度為0.001μm~0.1μm左右，較佳為0.005μm~0.02μm。若銀之被覆厚度平均未達0.001μm，則無法確保於銅粉表面均勻被覆有銀，又，成為導電性下降之原因。另一方面，若銀之被覆厚度平均超過0.1μm，則就成本觀點而言欠佳。
如此，樹枝狀銅粉之表面所被覆之銀之平均厚度為0.1μm以下，與構成銀被覆前之樹枝狀銅粉之平板狀銅粒子之剖面平均厚度(0.02
μm~5.0μm)相比較小。因此，於使用銀被覆樹枝狀銅粉之表面之前後，平板狀銅粒子之剖面平均厚度不會發生實質性變化。
作為樹枝狀覆銀銅粉1之體密度，並無特別限定，較佳為0.5g/cm3~5.0g/cm3之範圍。若體密度未達0.5g/cm3，則存在無法充分確保覆銀銅粉1彼此之接點之可能性。另一方面，若體密度超過5.0g/cm3，則樹枝狀覆銀銅粉1之平均粒徑亦變大，如此表面積變小而存在成形性或燒結性變差之情況。
又，關於本實施形態之樹枝狀覆銀銅粉1，並無特別限定，較佳為其BET比表面積之值為0.2m2/g~5.0m2/g。若BET比表面積值未達0.2m2/g，則存在被覆有銀之銅粒子無法成為如上所述之目標形狀之情況，存在無法獲得較高導電性之情況。另一方面，若BET比表面積值超過5.0m2/g，則存在樹枝狀覆銀銅粉1之表面的銀披覆不均勻而無法獲得較高導電性之可能性。又，構成覆銀銅粉1之銅粒子變得過細，從而存在覆銀銅粉成為細鬚狀之狀態、導電性下降之情況。再者，BET比表面積可依據JIS Z8830：2013進行測定。
再者，利用電子顯微鏡觀察時，只要如上所述之形狀之樹枝狀覆銀銅粉於所獲得之覆銀銅粉中占特定比例，則即便混合其以外之形狀之覆銀銅粉，亦能夠獲得與僅由該樹枝狀覆銀銅粉構成之銅粉相同之效果。具體而言，於利用電子顯微鏡(例如500倍~20,000倍)觀察時，只要上述形狀之樹枝狀覆銀銅粉於全部覆銀銅粉中占80個數%以上、較佳為90個數%以上之比例，則亦可包含其他形狀之覆銀銅粉。
《3.覆銀銅粉之製造方法》
其次，對本實施形態之樹枝狀覆銀銅粉1之製造方法進行說明。以下，首先，說明構成樹枝狀覆銀銅粉之樹枝狀銅粉之製造方法，繼而，說明對樹枝狀銅粉被覆銀而獲得樹枝狀覆銀銅粉之方法。
<3-1.銅粉之製造方法>
本實施形態之樹枝狀銅粉例如可使用含有銅離子之硫酸酸性溶液作為電解液，藉由特定電解法而製造。
電解時，例如於以金屬銅作為陽極(anode)、以不鏽鋼板或鈦板等作為陰極(cathode)所設置之電解槽中，收容上述含有銅離子之硫酸酸性之電解液，對該電解液以特定電流密度進行直流電流之通電，藉此實施電解處理。藉此，隨著通電而能夠使微細之樹枝狀銅粉析出(電析)至陰極上。尤其於本實施形態中，藉由於含有成為銅離子源之水溶性銅鹽之硫酸酸性之電解液中添加特定添加劑、非離子界面活性劑及氯化物離子，能夠析出平板狀銅粒子集合而構成的平板狀之樹枝狀銅粉。
(1)銅離子
水溶性銅鹽係供給銅離子之銅離子源，例如可列舉硫酸銅五水合物等硫酸銅、硝酸銅等，並無特別限定。又，亦可使氧化銅溶解於硫酸溶液而製成硫酸酸性溶液。作為電解液中之銅離子濃度，可設為1g/L~20g/L左右，較佳設為5g/L~10g/L左右。
(2)硫酸
硫酸係用以製備硫酸酸性之電解液者。作為電解液中之硫酸濃度，以游離硫酸濃度計，可設為20g/L~300g/L左右，較佳設為50g/L~150g/L左右。該硫酸濃度會對電解液之導電率造成影響，因此會對陰極上所獲
得之銅粉之均勻性造成影響。
(3)添加劑
作為添加劑，可使用選自由具有啡結構之化合物、具有偶氮苯結構之化合物、及具有啡結構與偶氮苯結構之化合物所組成之群中之任一種以上之化合物，或將選自該群中之分子結構不同之2種以上之化合物併用。本實施形態中，藉由將上述添加劑與後述非離子界面活性劑一併添加至電解液中，能夠製造相對於平板狀面為垂直方向之成長得以抑制之銅粉、即具有平滑面之銅粉。
作為選自由具有啡結構之化合物、具有偶氮苯結構之化合物、具有啡結構與偶氮苯結構之化合物所組成之群中之添加劑於電解液中之濃度，以所添加之化合物之總量計，較佳設為1~1000mg/L左右。
(具有啡結構之化合物)
具有啡結構之化合物可以下述式(1)表示。本實施形態中，可含有1種或2種以上之下述式(1)所表示之具有啡結構之化合物作為添加劑。
此處，式(1)中，R1、R2、R3、R4、R6、R7、R8、R9分別各自為：選自由氫、鹵素、胺基、OH、=O、CN、SCN、SH、COOH、COO鹽、
COO酯、SO3H、SO3鹽、SO3酯、苯磺酸及C1~C8烷基所組成之群中之基。又，R5為選自由氫、鹵素、胺基、OH、-O、CN、SCN、SH、COOH、COO鹽、COO酯、SO3H、SO3鹽、SO3酯、苯磺酸、低級烷基及芳基所組成之群中之基。又，A-為鹵化物陰離子。
具體而言，作為具有啡結構之化合物，例如可列舉：5-甲基啡-5-鎓、銅綠菌素B(Aeruginosin B)、銅綠菌素A(Aeruginosin A)、5-乙基啡-5-鎓、3,7-二胺基-5-苯基啡-5-鎓、5-乙基啡-5-鎓、5-甲基啡-5-鎓、3-胺基-5-苯基-7-(二乙胺基)啡-5-鎓、2,8-二甲基-3,7-二胺基-5-苯基啡-5-鎓、1-甲氧基-5-甲基啡-5-鎓、3-胺基-7-(二甲胺基)-1,2-二甲基-5-(3-磺酸根基苯基)啡-5-鎓、1,3-二胺基-5-甲基啡-5-鎓、1,3-二胺基-5-苯基啡-5-鎓、3-胺基-7-(二乙胺基)-2-甲基-5-苯基啡-5-鎓、3,7-雙(二乙胺基)-5-苯基啡-5-鎓、2,8-二甲基-3,7-二胺基-5-(4-甲基苯基)啡-5-鎓、3-(甲基胺基)-5-甲基啡-5-鎓、3-羥基-7-(二乙胺基)-5-苯基啡-5-鎓、5-氮鎓啡(azonia phenazine)、1-羥基-5-甲基啡-5-鎓、4H,6H-5-苯基-3,7-二氧雜啡-5-鎓、苯胺基阿朴藏紅(anilino-aposafranine)、酚藏紅、中性紅等。
(具有偶氮苯結構之化合物)
具有偶氮苯結構之化合物可以下述式(2)表示。本實施形態中，可含有1種或2種以上之下述式(2)所表示之具有偶氮苯結構之化合物作為添加劑。
此處，式(2)中，R1、R2、R3、R4、R5、R6、R7、R8、R9、R10分別各自為：選自由氫、鹵素、胺基、OH、=O、CN、SCN、SH、COOH、COO鹽、COO酯、SO3H、SO3鹽、SO3酯、苯磺酸、低級烷基及芳基所組成之群中之基。
具體而言，作為具有偶氮苯結構之化合物，例如可列舉：偶氮苯、4-胺基偶氮苯-4'-磺酸、4-(二甲胺基)-4'-(三氟甲基)偶氮苯、C.I.酸性紅13、汞橙(mercury orange)、2',4'-二胺基-5'-甲基偶氮苯-4-磺酸鈉、甲基紅、甲基黃、甲基橙、偶氮苯-2,4-二胺、茜素黃GG、4-二甲胺基偶氮苯、橙I、柳氮磺胺吡啶(salazosulfapyridine)、4-(二乙胺基)偶氮苯、橙OT、3-甲氧基-4-胺基偶氮苯、4-胺基偶氮苯、N,N,2-三甲基偶氮苯-4-胺、4-羥基偶氮苯、蘇丹I、4-胺基-3,5-二甲基偶氮苯、N,N-二甲基-4-[(喹啉-6-基)偶氮]苯胺、鄰胺基偶氮甲苯、茜素黃R、4'-(胺基磺醯基)-4-羥基偶氮苯-3-羧酸、剛果紅、活性紅、間胺黃(metanil yellow)、橙II、分散橙3、C.I.直接橙39、2,2'-二羥基偶氮苯、偶氮苯-4,4'-二醇、萘紅、5-苯基偶氮苯-2-醇、2,2'-二甲基偶氮苯、C.I.媒染黃(C.I.mordant yellow)12、媒染黃10、酸性黃、分散藍、新型黃RMF(new yellow RMF)、Bistramine棕G等。
(具有啡結構與偶氮苯結構之化合物)
具有啡結構與偶氮苯結構之化合物可以下述式(3)表示。本實施形態中，可含有1種或2種以上之下述式(3)所表示之具有啡結構與偶氮苯結構之化合物作為添加劑。
此處，式(3)中，R1、R2、R4、R5、R6、R7、R8、R9、R10、R11、R12、R13分別各自為：選自由氫、鹵素、胺基、OH、=O、CN、SCN、SH、COOH、COO鹽、COO酯、SO3H、SO3鹽、SO3酯、苯磺酸及C1~C8烷基所組成之群中之基。又，R3為選自由氫、鹵素、胺基、OH、=O、CN、SCN、SH、COOH、COO鹽、COO酯、SO3H、SO3鹽、SO3酯、苯磺酸、低級烷基及芳基所組成之群中之基。又，A-為鹵化物陰離子。
具體而言，作為具有啡結構與偶氮苯結構之化合物，例如可列舉：3-(二乙胺基)-7-[(4-羥基苯基)偶氮]-2,8-二甲基-5-苯基啡-5-鎓、3-[[4-(二甲胺基)苯基]偶氮]-7-(二乙胺基)-5-苯基啡-5-鎓、傑納斯綠(Janus green)B、3-胺基-7-[{2,4-二胺基苯基)偶氮]-2,8-二甲基-5-苯基啡-5-鎓、2,8-二甲基-3-胺基-5-苯基-7-(2-羥基-1-萘基偶氮)啡-5-鎓、3-[[4-(二甲胺基)苯基]偶
氮]-7-(二甲胺基)-5-苯基啡-5-鎓、3-胺基-7-[[4-(二甲胺基)苯基]偶氮]-5-苯基啡-5-鎓、2-(二乙胺基)-7-[4-(甲基炔丙基胺基)苯基偶氮]-9-苯基-9-氮鎓-10-氮雜蒽、2-(二乙胺基)-7-[4-(甲基4-戊炔基胺基)苯基偶氮]-9-苯基-9-氮鎓-10-氮雜蒽、2-(二乙胺基)-7-[4-(甲基2,3-二羥基丙基胺基)苯基偶氮]-9-苯基-9-氮鎓-10-氮雜蒽等。
(4)界面活性劑
作為界面活性劑，含有非離子界面活性劑。本實施形態中，藉由將非離子界面活性劑與上述添加劑一併添加至電解液中，能夠製造相對於平板狀面為垂直方向之成長得以抑制之銅粉、即具有平滑面之銅粉。
作為非離子界面活性劑，可單獨使用1種或將2種以上併用，電解液中之濃度以總量計可設為1~10000mg/L左右。
作為非離子界面活性劑之數量平均分子量，並無特別限定，較佳為100~200000，更佳為200~15000，進而較佳為1000~10000。若為數量平均分子量未達100之界面活性劑，則存在析出非樹枝狀之微細電解銅粉之可能性。另一方面，若為數量平均分子量超過200000之界面活性劑，則存在析出平均粒徑較大之電解銅粉而僅獲得比表面積未達0.2m2/g之樹枝狀銅粉之可能性。再者，本實施形態中，數量平均分子量係設為藉由以四氫呋喃(THF)為溶劑之凝膠滲透層析法(GPC)所求出之聚苯乙烯換算之分子量。
作為非離子界面活性劑之種類，並無特別限定，較佳為具有醚基之界面活性劑，例如可列舉：聚乙二醇、聚丙二醇、聚伸乙基亞胺、
普朗尼克(Pluronic)型界面活性劑、Tetronic型界面活性劑、聚氧乙二醇-甘油醚、聚氧乙二醇-二烷基醚、聚氧乙烯聚氧丙烯二醇-烷基醚、芳香族醇烷氧基化物、下述(x)式所表示之高分子化合物等，該等非離子界面活性劑可單獨使用1種或將2種以上併用。
更具體而言，作為聚乙二醇，可使用例如下述式(i)所表示者。
-(CH2CH2O)n1-················(i)
(式(i)中，n1表示1~120之整數)
又，作為聚丙二醇，可使用例如下述式(ii)所表示者。
(式(ii)中，n1表示1~90之整數)
又，作為聚伸乙基亞胺，可使用例如下述式(iii)所表示者。
-(CH2CH2NH)n1-················(iii)
(式(iii)中，n1表示1~120之整數)
又，作為普朗尼克型界面活性劑，可使用例如下述式(iv)所表示者。
HO-(C2H4O)l2-(C3H6O)m2-(C2H4O)n2-H················(iv)
(式(iv)中，n2及l2表示1~30之整數，m2表示10~100之整數)
又，作為Tetronic型界面活性劑，可使用例如下述式(v)
所表示者。
(式(v)中，n3表示1~200之整數，m3表示1~40之整數)
又，作為聚氧乙二醇-甘油醚，可使用例如下述式(vi)所表示者。
(式(vi)中，n4、m4及l4分別表示1~200之整數)
又，作為聚氧乙二醇-二烷基醚，可使用例如下述式(vii)所表示者。
R1O-(C2H4O)n5-OR2················(vii)
(式(vii)中，R1及R2表示氫原子或碳數1~5之低級烷基，n5表示2~200之整數)
又，作為聚氧乙烯聚氧丙烯二醇-烷基醚，可使用例如下述式(viii)所表示者。
R3O-(C2H4O)m6(C2H4O)n6-H················(viii)
(式(viii)中，R3表示氫原子或碳數1~5之低級烷基，m6或n6表示2~100之整數)
又，作為芳香族醇烷氧基化物，可使用例如下述式(ix)所
表示者。
C6H5(CH2)m7O(CH2CH2O)n7H················(ix)
(式(ix)中，m7表示1~5之整數，n7表示1~120之整數)
又，可使用下述(x)式所表示之高分子化合物。
(式(x)中，R1表示碳數5~30之高級醇之殘基、具有碳數1~30之烷基之烷基苯酚之殘基、具有碳數1~30之烷基之烷基萘酚之殘基、碳數3~25之脂肪醯胺之殘基、碳數2~5之烷基胺之殘基、或羥基。又，R2及R3表示氫原子或甲基。又，m及n表示1~100之整數)
(5)氯化物離子
關於氯化物離子，可藉由於電解液中添加鹽酸、氯化鈉等供給氯化物離子之化合物(氯化物離子源)而含有。氯化物離子與上述添加劑或非離子界面活性劑一併有助於所析出之銅粉之形狀控制。作為電解液中之氯化物離子濃度，並無特別限定，可設為1mg/L~500mg/L左右。
關於本實施形態之樹枝狀銅粉1之製造方法，例如使用如上所述之組成之電解液而進行電解，藉此於陰極上析出生成銅粉而製造。作為電解方法，可使用公知方法。例如作為電流密度，於使用硫酸酸性之電解液進行電解時，較佳設為3A/dm2~30A/dm2之範圍，一面攪拌電解液一面通電。又，作為電解液之液溫(浴溫)，可設為例如20℃~60℃左右。
<3-2.銀之被覆方法(覆銀銅粉之製造)>
本實施形態之樹枝狀覆銀銅粉1可藉由使用例如還原型無電解鍍敷法
或置換型無電解鍍敷法，於利用上述電解法所製作之樹枝狀銅粉之表面被覆銀而製造。
特別關於本實施形態之樹枝狀覆銀銅粉1，於銀被覆前之樹枝狀銅粉中具有“相對於平板狀面為垂直方向之成長得以抑制”之平滑面，藉此於該銅粉之表面被覆銀時，可使銀更均勻地被覆。
為了於樹枝狀銅粉之表面被覆均勻厚度之銀，較佳為於鍍銀前進行清洗，可使樹枝狀銅粉分散於清洗液中，一面攪拌一面進行清洗。作為該清洗處理，較佳為於酸性溶液中進行，更佳為使用亦用於後述還原劑之多元羧酸。洗淨後，對樹枝狀銅粉適當反覆進行過濾-分離、與水洗，使樹枝狀銅粉分散於水中而製成水性漿料。再者，關於過濾-分離、與水洗，只要使用公知方法即可。
具體而言，於利用還原型無電解鍍敷法被覆銀之情形時，藉由將樹枝狀銅粉洗淨後所獲得之水性漿料中添加還原劑與銀離子溶液，可使銀被覆於樹枝狀銅粉之表面。此處，藉由於水性漿料中預先添加還原劑並使之分散後，於含有該還原劑與樹枝狀銅粉之水性漿料連續地添加銀離子溶液，可使銀更均勻地被覆於樹枝狀銅粉之表面。
作為還原劑，可使用各種還原劑，較佳為無法使銅之錯離子還原之還原力較弱之還原劑。作為該弱還原劑，可使用還原性有機化合物，例如可使用碳水化合物類、多元羧酸及其鹽、醛類等。更具體而言，可列舉：葡萄糖(glucose)、乳酸、草酸、酒石酸、蘋果酸、丙二酸、乙醇酸、酒石酸鈉鉀、福馬林等。
於含樹枝狀銅粉之水性漿料添加還原劑後，較佳為進行攪拌
等以使還原劑充分地分散。又，為了將水性漿料調整為所需之PH值，可適當添加酸或鹼。進而，亦可藉由添加醇等水溶性有機溶劑而促進作為還原劑之還原性有機化合物之分散。
作為連續地添加之銀離子溶液，可使用公知之鍍銀液，其中，較佳為使用硝酸銀溶液。又，硝酸銀溶液易引起錯合反應，因此更佳為以氨性硝酸銀溶液之形式添加。再者，關於氨性硝酸銀溶液所使用之氨，可添加於硝酸銀溶液，或可預先與還原劑一併添加至水性漿料並使之分散，或可以與硝酸銀溶液分開之另一氨溶液之形式，和硝酸銀溶液同時添加於水性漿料，只要採用包括該等方法之組合在內之任一方法即可。
於將銀離子溶液添加至例如含有樹枝狀銅粉與還原劑之水性漿料時，較佳為以相對較慢之速度緩慢添加，藉此能夠於樹枝狀銅粉之表面形成均勻厚度之銀被膜。又，為了提高被膜厚度之均勻性，更佳為將添加速度設為固定。進而，亦可以如下方式進行：預先將所添加之還原劑等利用其他溶液調整，並且與銀離子溶液一併緩慢地追加添加至水性漿料。
如此，對添加有銀離子溶液等之水性漿料進行過濾、分離，加以水洗，然後使之乾燥，藉此能夠獲得樹枝狀之覆銀銅粉1。作為該等過濾以後之處理手段，並無特別限定，只要採用公知方法即可。
另一方面，關於以置換型無電解鍍敷法被覆銀之方法，利用銅與銀之離子化傾向之不同，藉由於溶液中銅溶解時產生之電子，使溶液中之銀離子還原而析出至銅表面。因此，置換型之無電解鍍銀液只要以成為銀離子源之銀鹽、錯合劑及傳導鹽作為主要成分而構成，即能夠進行銀被覆，但為了更均勻地被覆銀，視需要可添加界面活性劑、光澤劑、結晶
調整劑、pH調整劑、沈澱防止劑、穩定劑等。本實施形態之覆銀銅粉之製造中，該鍍敷液並無特別限定。
更具體而言，作為銀鹽，可使用硝酸銀、碘化銀、硫酸銀、甲酸銀、乙酸銀、乳酸銀等，可使之與分散於水性漿料中之樹枝狀銅粉進行反應。作為鍍敷液中之銀離子濃度，可設為1g/L~10g/L左右。
又，錯合劑係與銀離子形成錯合物，作為代表性者，可使用檸檬酸、酒石酸、乙二胺四乙酸、氮基三乙酸等、或乙二胺、甘胺酸、乙內醯脲、吡咯啶酮、琥珀醯亞胺等含N化合物、羥基亞乙基二膦酸、胺基三亞甲基膦酸、巰基丙酸、硫甘醇、硫半卡肼等。作為鍍敷液中之錯合劑之濃度，可設為10g/L~100g/L左右。
又，作為傳導鹽，可使用硝酸、硼酸、磷酸等無機酸，檸檬酸、順丁烯二酸、酒石酸、苯二甲酸等有機酸，或該等之鈉、鉀、銨鹽等。作為鍍敷液中之傳導鹽濃度，可設為5g/L~50g/L左右。
關於對樹枝狀銅粉之表面被覆銀時之被覆量之控制，例如可藉由改變置換型無電解鍍敷液之銀投入量而進行控制。又，為了提高被膜厚度之均勻性，較佳為將添加速度設為固定。
如此，對反應結束後之漿料進行過濾、分離，加以水洗，其後使之乾燥，藉此可獲得樹枝狀之覆銀銅粉。作為該等過濾以後之處理手段，並無特別限定，只要採用公知方法即可。
《4.導電性糊、電磁波屏蔽用導電性塗料、導電性片之用途》
本實施形態之樹枝狀覆銀銅粉1如上所述係具有主幹2與多個枝3之樹枝狀覆銀銅粉，主幹2及自該主幹2分支出之多個枝3係“剖面平均厚
度為0.02μm~5.0μm之平板狀且表面被覆有銀”之銅粒子集合而構成。又，該樹枝狀覆銀銅粉之平均粒徑(D50)為1.0μm~100μm。關於上述樹枝狀覆銀銅粉1，藉由為樹枝狀之形狀而使表面積增大，成形性或燒結性優異，又，藉由為樹枝狀且由具有特定剖面平均厚度之平板狀銅粒子構成，能夠確保較多之接點數，發揮優異之導電性。
並且，該樹枝狀覆銀銅粉1中，銅粒子之相對於平板狀面為垂直方向之最大高度，為該平板狀面之水平方向之最大長度的1/10以下，朝垂直方向之成長得以抑制而具有平滑面。藉由上述樹枝狀覆銀銅粉1，能夠進一步增加銅粉彼此之接點，提高導電性。
又，根據上述具有特定結構之樹枝狀覆銀銅粉1，即便於製成銅糊等之情形時，亦能夠抑制凝集，實現於樹脂中之均勻分散，又，能夠抑制因糊劑黏度上升等所引起之印刷性不良等。因此，樹枝狀覆銀銅粉1可較佳地用於導電性糊或導電塗料等用途。
例如關於導電性糊(銅糊)，可藉由包含本實施形態之樹枝狀銅粉1作為金屬填料(銅粉)，與黏合劑樹脂、溶劑、進而視需要之抗氧化劑或偶合劑等添加劑進行混練而製作。
本實施形態中，上述樹枝狀覆銀銅粉1係以於金屬填料中成為20質量%以上、較佳為30質量%以上、更佳為50質量%以上之量之比例的方式構成。若將金屬填料中樹枝狀覆銀銅粉1之比例設為20質量%以上，則例如於將該金屬填料用於銅糊之情形時，能夠均勻分散於樹脂中，又，能夠防止糊劑黏度過度上升而產生印刷性不良。又，藉由為由平板狀之微細銅粒子之集合體所構成之樹枝狀覆銀銅粉1，能夠發揮作為導電性糊之優
異導電性。
再者，作為金屬填料，只要以如上所述般使樹枝狀覆銀銅粉1成為20質量%以上之量的比例方式含有即可，另外亦可混合例如1μm~20μm左右之球狀銅粉等。
具體而言，作為黏合劑樹脂，並無特別限定，可使用環氧樹脂、酚樹脂等。又，作為溶劑，可使用乙二醇、二乙二醇、三乙二醇、甘油、萜品醇等有機溶劑。又，作為該有機溶劑之添加量，並無特別限定，可以成為適於網版印刷或分注器印刷等導電膜形成方法之黏度之方式，並考慮到樹枝狀覆銀銅粉1之粒度而調整添加量。
進而，亦可添加其他樹脂成分以調整黏度。例如可列舉以乙基纖維素為代表之纖維素系樹脂等，以溶解於萜品醇等有機溶劑之有機媒劑之形式添加。再者，關於該樹脂成分之添加量，必須抑制於無損燒結性之程度，較佳為設為整體之5質量%以下。
又，作為添加劑，為了改善燒成後之導電性，可添加抗氧化劑等。作為抗氧化劑，並無特別限定，例如可列舉羥基羧酸等。更具體而言，較佳為檸檬酸、蘋果酸、酒石酸、乳酸等羥基羧酸，尤佳為對被覆有銀之銅的吸附力較高之檸檬酸或蘋果酸。作為抗氧化劑之添加量，考慮到抗氧化效果或糊劑黏度等，可設為例如1~15質量%左右。
其次，關於電磁波屏蔽用材料，於利用本實施形態之樹枝狀覆銀銅粉1作為金屬填料之情形時，亦不限於在特別之限定條件下使用，可採用通常方法，例如可將金屬填料與樹脂混合使用。
例如作為用於形成電磁波屏蔽用導電性片之電磁波屏蔽層
之樹脂，並無特別限定，可適當使用先前所用之氯乙烯樹脂、乙酸乙烯酯樹脂、二氯亞乙烯樹脂、丙烯酸樹脂、聚胺酯(polyurethane)樹脂、聚酯樹脂、烯烴樹脂、氯化烯烴樹脂、聚乙烯醇系樹脂、醇酸樹脂、酚樹脂等由各種聚合物及共聚物構成之熱塑性樹脂、熱硬化性樹脂、放射線硬化型樹脂等。
作為製造電磁波屏蔽材之方法，例如可藉由如下方式製造：使如上所述之金屬填料與樹脂分散或溶解於溶劑而製成塗料，將該塗料塗佈或印刷於基材上，藉此形成電磁波屏蔽層，乾燥至表面固化之程度。又，亦可將金屬填料用於導電性片之導電性接著劑層。
又，於利用本實施形態之覆銀銅粉1作為金屬填料而製作電磁波屏蔽用導電性塗料之情形時，亦不限於在特別之限定條件下使用，可採用通常方法，例如將金屬填料與樹脂及溶劑加以混合，進而視需要混合抗氧化劑、增黏劑、沈澱防止劑等，進行混練，藉此可用作導電性塗料。
關於此時所使用之黏合劑樹脂及溶劑，亦並無特別限定，可利用先前使用之氯乙烯樹脂、乙酸乙烯酯樹脂、丙烯酸樹脂、聚酯樹脂、氟樹脂、矽樹脂或酚樹脂等。又，關於溶劑，亦可利用先前使用之異丙醇等醇類、甲苯等芳香族烴類、乙酸甲酯等酯類、甲基乙基酮等酮類等。又，關於作為添加劑之抗氧化劑，亦可利用先前使用之脂肪醯胺、高級脂肪酸胺、苯二胺衍生物、鈦酸酯系偶合劑等。
[實施例]
以下，一併揭示實施例與比較例而更具體地說明本發明，但本發明並不受以下實施例之任何限定。
<評價方法>
針對下述實施例及比較例中所獲得之銅粉，藉由以下方法，進行形狀之觀察、平均粒徑之測定、比表面積等之測定。
(形狀之觀察)
藉由掃描式電子顯微鏡(日本電子股份有限公司製造，JSM-7100F型)，於特定倍率之視域中任意觀察20處，觀察該視域內所含之覆銀銅粉。
(平均粒徑之測定)
關於所獲得之覆銀銅粉之平均粒徑(D50)，使用雷射繞射-散射法粒度分佈測定器(日機裝股份有限公司製造，HRA9320 X-100)進行測定。
(BET比表面積)
關於BET比表面積，使用比表面積-細孔分佈測定裝置(Quantachrome公司製造，QUADRASORB SI)進行測定。
(電阻率值測定)
關於被膜之電阻率值，使用低電阻率計(三菱化學股份有限公司製造，Loresta-GPMCP-T600)，藉由四端子法測定片材電阻值，另一方面，藉由表面粗糙度形狀測定器(東京精密股份有限公司製造，SURFCOM130A)測定被膜之膜厚，用片材電阻值除以膜厚，藉此求出電阻率值。
(電磁波屏蔽特性)
關於電磁波屏蔽特性之評價，針對各實施例及比較例中所獲得之試樣，使用頻率1GHz之電磁波，測定其衰減率而評價。具體而言，將未使用樹枝狀覆銀銅粉之比較例2之情況的等級設為『△』，將差於該比較例2之等級的情況設為『×』，將優於該比較例2之等級的情況設為『○』，將更
優異之情形設為『◎』而進行評價。
又，為了亦對電磁波屏蔽之可撓性進行評價，將所製作之電磁波屏蔽彎折，確認電磁波屏蔽特性是否變化。
[實施例1]
<樹枝狀銅粉之製造>
於容量100L之電解槽中，使用電極面積為200mm×200mm之鈦製電極板作為陰極，使用電極面積為200mm×200mm之銅製電極板作為陽極，向該電解槽中裝入電解液，對其以直流電流通電而使銅粉析出至陰極板。
此時，作為電解液，使用銅離子濃度為15g/L、硫酸濃度為100g/L之組成者。又，對該電解液以電解液中之氯化物離子(氯離子)濃度成為50mg/L之方式添加鹽酸溶液(和光純藥工業股份有限公司製造)。又，於該電解液，以電解液中之濃度成為100mg/L之方式添加作為添加劑之具有啡結構之化合物即番紅(關東化學工業股份有限公司製造)，進而，以電解液中之濃度成為500mg/L之方式添加作為非離子界面活性劑之分子量1000之聚乙二醇(PEG)(和光純藥工業股份有限公司製造)。
繼而，對調整為上述濃度之電解液，一面使用泵而使之以15L/min之流量循環，一面將溫度維持於25℃，以陰極之電流密度成為10A/dm2之方式通電，從而使銅粉析出至陰極板上。
使用刮板，將析出至陰極板上之電解銅粉機械性地刮落至電解槽之槽底而回收，將所回收之銅粉用純水洗淨後，裝入減壓乾燥器進行乾燥。
<藉由還原法之樹枝狀覆銀銅粉之製造>
繼而，使用利用上述方法所製作之銅粉而製作覆銀銅粉。
即，將所獲得之銅粉100g於3%酒石酸水溶液中攪拌約1小時後，進行過濾、水洗，使之分散於2升之離子交換水中。於其中添加酒石酸6g、葡萄糖6g、乙醇60ml，進而添加28%氨水60ml並攪拌，其後，將“於4.5升離子交換水溶解有硝酸銀70g”之水溶液、“於900ml離子交換水溶解有葡萄糖30g、酒石酸30g及乙醇300ml”之水溶液、以及28%氨水300ml分別歷時60分鐘緩慢添加。再者，此時之浴溫為25℃。
各水溶液之添加結束後，對粉末進行過濾、水洗，通入乙醇而使之乾燥，結果獲得於銅粉表面被覆有銀之覆銀銅粉。藉由SEM於倍率5,000倍之視域觀察所獲得之覆銀銅粉，結果至少90個數%以上之覆銀銅粉為表面均勻被覆有銀之平板狀銅粒子密集、集合而呈現樹枝狀形狀之樹枝狀覆銀銅粉。又，回收該樹枝狀覆銀銅粉，測定銀被覆量，結果銀被覆量相對於該覆銀銅粉整體之質量100%為30.5質量%。
又，針對所獲得之樹枝狀覆銀銅粉，藉由SEM進行觀察，並測定平板狀銅粒子之剖面平均厚度、以及該樹枝狀覆銀銅粉之相對於平板狀面沿垂直方向成長之最大長度與相對於平板狀面為水平方向之長軸長度的比。結果構成所獲得之樹枝狀覆銀銅粉之銅粒子為剖面平均厚度2.6μm之平板狀。又，該樹枝狀覆銀銅粉之平均粒徑(D50)為47.7μm。並且，該覆銀銅粉自平板狀面沿垂直方向成長之最大長度與水平於平板狀面之方向(平板方向)之最大長度的比(垂直方向長度/平板方向長軸長度)以平均計為0.062。
又，所獲得之樹枝狀覆銀銅粉之體密度為2.9g/cm3。又，BET比表面積為1.13m2/g。
根據該實施例1之結果可知，藉由於電解液中添加具有啡結構之化合物與非離子界面活性劑而製作樹枝狀電解銅粉，對所獲得之銅粉之表面被覆銀，能夠製作朝垂直方向之成長得以抑制之平板狀之樹枝狀覆銀銅粉。
[實施例2]
<樹枝狀銅粉之製造>
於電解液中以氯化物離子濃度成為150mg/L之方式添加鹽酸溶液(和光純藥工業股份有限公司製造)，又，以電解液中之濃度成為150mg/L之方式添加作為添加劑之具有偶氮苯結構之化合物即甲基橙(關東化學工業股份有限公司製造)。進而，對電解液以電解液中之濃度成為700mg/L之方式添加作為非離子界面活性劑之分子量1000之聚氧乙烯聚氧丙烯丁醚(日油股份有限公司製造，商品名：Unilube 50MB-11)。除此以外，於與實施例1相同之條件下進行電解處理，製作樹枝狀銅粉。
<藉由還原法之樹枝狀覆銀銅粉之製造>
繼而，對所獲得之樹枝狀銅粉，以與實施例1相同之步驟於其表面被覆銀，結果獲得於樹枝狀銅粉之表面被覆有銀之覆銀銅粉。
藉由SEM於倍率5,000倍之視域觀察所獲得之覆銀銅粉，結果至少90個數%以上之覆銀銅粉為表面被覆有銀之平板狀銅粒子密集、集合而呈現樹枝狀形狀之樹枝狀覆銀銅粉。又，回收該樹枝狀覆銀銅粉，測定銀被覆量，結果銀被覆量相對於該覆銀銅粉整體之質量100%為30.1質
量%。
又，針對所獲得之樹枝狀覆銀銅粉，藉由SEM進行觀察，並測定平板狀銅粒子之剖面平均厚度、以及該樹枝狀覆銀銅粉之相對於平板狀面沿垂直方向成長之最大長度與相對於平板狀面為水平方向之長軸長度的比。結果構成所獲得之樹枝狀覆銀銅粉之銅粒子為剖面平均厚度1.8μm之平板狀。又，該樹枝狀覆銀銅粉之平均粒徑(D50)為36.6μm。並且，該覆銀銅粉自平板狀面沿垂直方向成長之最大長度與水平於平板狀面之方向(平板方向)之最大長度的比(垂直方向長度/平板方向長軸長度)以平均計為0.036。
又，所獲得之樹枝狀覆銀銅粉之體密度為2.2g/cm3。又，BET比表面積為1.24m2/g。
根據該實施例2之結果可知，藉由於電解液中添加具有偶氮苯結構之化合物與非離子界面活性劑而製作樹枝狀電解銅粉，對所獲得之銅粉之表面被覆銀，能夠製作朝垂直方向之成長得以抑制之平板狀之樹枝狀覆銀銅粉。
[實施例3]
<樹枝狀銅粉之製造>
於電解液中以氯化物離子濃度成為80mg/L之方式添加鹽酸溶液(和光純藥工業股份有限公司製造)，又，以電解液中之濃度成為600mg/L之方式添加作為添加劑之具有啡結構與偶氮苯結構之化合物即傑納斯綠B(關東化學工業股份有限公司製造)。進而，對電解液以電解液中之濃度成為1000mg/L之方式添加作為非離子界面活性劑之分子量3000之聚氧乙烯
聚氧丙烯丁醚(日油股份有限公司製造，商品名：Unilube 50MB-72)。除此以外，於與實施例1相同之條件下進行電解處理，製作樹枝狀銅粉。
<藉由置換法之樹枝狀覆銀銅粉之製作>
繼而，使用所獲得之樹枝狀銅粉100g，藉由置換型無電解鍍敷液而於該銅粉表面形成銀被覆。
作為置換型無電解鍍敷液，使用於離子交換水1升溶解有硝酸銀25g、檸檬酸20g及乙二胺10g之組成溶液，向該溶液中投入樹枝狀銅粉100g，攪拌45分鐘而進行反應。此時之浴溫為30℃。
反應結束後，對粉末進行過濾、水洗，通入乙醇而使之乾燥，結果獲得於樹枝狀銅粉之表面被覆有銀之覆銀銅粉。藉由SEM於倍率5,000倍之視域觀察所獲得之覆銀銅粉，結果至少90個數%以上之覆銀銅粉為表面均勻被覆有銀之平板狀銅粒子密集、集合而呈現樹枝狀形狀之樹枝狀覆銀銅粉。又，回收該樹枝狀覆銀銅粉，測定銀被覆量，結果銀被覆量相對於該覆銀銅粉整體之質量100%為10.6質量%。
又，針對所獲得之樹枝狀覆銀銅粉，藉由SEM進行觀察，並測定平板狀銅粒子之剖面平均厚度、以及該樹枝狀覆銀銅粉之相對於平板狀面沿垂直方向成長之最大長度與相對於平板狀面為水平方向之長軸長度的比。結果構成所獲得之樹枝狀覆銀銅粉之銅粒子為剖面平均厚度1.2μm之平板狀。又，該樹枝狀覆銀銅粉之平均粒徑(D50)為32.9μm。並且，該覆銀銅粉自平板狀面沿垂直方向成長之最大長度與水平於平板狀面之方向(平板方向)之最大長度的比(垂直方向長度/平板方向長軸長度)以平均計為0.024。
又，所獲得之樹枝狀覆銀銅粉之體密度為1.9g/cm3。又，BET比表面積為1.89m2/g。
根據該實施例3之結果可知，藉由於電解液中添加具有啡結構與偶氮苯結構之化合物、及非離子界面活性劑而製作樹枝狀電解銅粉，對所獲得之銅粉之表面被覆銀，能夠製作朝垂直方向之成長得以抑制之平板狀之樹枝狀覆銀銅粉。
[實施例4]
<樹枝狀銅粉之製造>
於電解液中以氯化物離子濃度成為100mg/L之方式添加鹽酸溶液(和光純藥工業股份有限公司製造)，又，以電解液中之濃度成為150mg/L之方式添加作為添加劑之具有偶氮苯結構之化合物即甲基橙(關東化學工業股份有限公司製造)，進而以電解液中之濃度成為100mg/L之方式添加作為添加劑之具有啡結構與偶氮苯結構之化合物即傑納斯綠B(關東化學工業股份有限公司製造)。又，對電解液以電解液中之濃度成為1000mg/L之方式添加作為非離子界面活性劑之分子量600之聚乙二醇(PEG)(和光純藥工業股份有限公司製造)，進而以電解液中之濃度成為1000mg/L之方式添加作為非離子界面活性劑之分子量3000之聚氧乙烯聚氧丙烯丁醚(日油股份有限公司製造，商品名：Unilube 50MB-72)，除此以外，於與實施例1相同之條件下進行電解處理，製作樹枝狀銅粉。
<藉由還原法之樹枝狀覆銀銅粉之製造>
繼而，對所獲得之樹枝狀銅粉，以與實施例1相同之步驟於其表面被覆銀，結果獲得於樹枝狀銅粉之表面被覆有銀之覆銀銅粉。
藉由SEM於倍率5000倍之視域觀察所獲得之覆銀銅粉，結果至少90個數%以上之覆銀銅粉為由表面被覆有銀之平板狀銅粒子密集、集合而呈現樹枝狀形狀之樹枝狀覆銀銅粉。又，回收該樹枝狀覆銀銅粉，測定銀被覆量，結果銀被覆量相對於該覆銀銅粉整體之質量100%為30.8質量%。
又，針對所獲得之樹枝狀覆銀銅粉，藉由SEM進行觀察，並測定平板狀銅粒子之剖面平均厚度、以及該樹枝狀覆銀銅粉之相對於平板狀面沿垂直方向成長之最大長度與相對於平板狀面為水平方向之長軸長度的比。結果構成所獲得之樹枝狀覆銀銅粉之銅粒子為剖面平均厚度0.4μm之平板狀。又，該樹枝狀覆銀銅粉之平均粒徑(D50)為18.5μm。並且，該覆銀銅粉自平板狀面沿垂直方向成長之最大長度與水平於平板狀面之方向(平板方向)之最大長度的比(垂直方向長度/平板方向長軸長度)以平均計為0.056。
又，所獲得之樹枝狀覆銀銅粉之體密度為1.1g/cm3。又，BET比表面積為2.16m2/g。
根據該實施例4之結果可知，藉由混合添加具有偶氮苯結構之化合物、及具有啡結構與偶氮苯結構之化合物作為添加劑，進而添加2種以上之非離子界面活性劑而製作樹枝狀電解銅粉，對所獲得之銅粉之表面被覆銀，能夠製作朝垂直方向之成長得以抑制之平板狀之樹枝狀覆銀銅粉。
[實施例5]
對實施例1中所獲得之比表面積為1.13m2/g之樹枝狀覆銀銅粉55質
量份混合酚樹脂(群榮化學股份有限公司製造，PL-2211)15質量份、丁基賽路蘇(關東化學股份有限公司製造，鹿特級)10質量份，使用小型捏合機(日本精機製作所製造，No Bubbling Kneader NBK-1)，以1200rpm混練3分鐘，反覆進行3次該混練，藉此實現糊化。利用金屬刮漿板將所獲得之導電糊劑印刷於玻璃上，於大氣環境中分別在150℃、200℃進行30分鐘之硬化。
藉由硬化所獲得之被膜之電阻率值分別為26.5×10-6Ω．cm(硬化溫度150)、3.6×10-6Ω．cm(硬化溫度200℃)。
[實施例6]
對實施例2中所獲得之比表面積為1.24m2/g之樹枝狀覆銀銅粉55質量份混合酚樹脂(群榮化學股份有限公司製造，PL-2211)15質量份、丁基賽路蘇(關東化學股份有限公司製造，鹿特級)10質量份，使用小型捏合機(日本精機製作所製造，No Bubbling Kneader NBK-1)，以1200rpm混練3分鐘，反覆進行3次該混練，藉此實現糊化。利用金屬刮漿板將所獲得之導電糊劑印刷於玻璃上，於大氣環境中分別在150℃、200℃進行30分鐘之硬化。
藉由硬化所獲得之被膜之電阻率值分別為28.3×10-6Ω．cm(硬化溫度150℃)、4.4×10-6Ω．cm(硬化溫度200℃)。
[實施例7]
對實施例4中所獲得之比表面積為2.16m2/g之樹枝狀覆銀銅粉55質量份混合酚樹脂(群榮化學股份有限公司製造，PL-2211)15質量份、丁基賽路蘇(關東化學股份有限公司製造，鹿特級)10質量份，使用小型捏
合機(日本精機製作所製造，No Bubbling Kneader NBK-1)，以1200rpm混練3分鐘，反覆進行3次該混練，藉此實現糊化。利用金屬刮漿板將所獲得之導電糊劑印刷於玻璃上，於大氣環境中分別在150℃、200℃進行30分鐘之硬化。
藉由硬化所獲得之被膜之電阻率值分別為31.2×10-6Ω．cm(硬化溫度150℃)、4.9×10-6Ω．cm(硬化溫度200℃)。
[實施例8]
將實施例1中所獲得之比表面積為1.13m2/g之覆銀銅粉、與實施例2中所獲得之比表面積為1.24m2/g之覆銀銅粉此等兩種不同之覆銀銅粉，以50：50之比例混合，對所獲得之覆銀銅粉55質量份(合計量)混合酚樹脂(群榮化學股份有限公司製造，PL-2211)15質量份、丁基賽路蘇(關東化學股份有限公司製造，鹿特級)10質量份，使用小型捏合機(日本精機製作所製造，No Bubbling Kneader NBK-1)，以1200rpm混練3分鐘，反覆進行3次該混練，藉此實現糊化。利用金屬刮漿板將所獲得之導電糊劑印刷於玻璃上，於大氣環境中分別在150℃、200℃進行30分鐘之硬化。
藉由硬化所獲得之被膜之電阻率值分別為28.9×10-6Ω．cm(硬化溫度150℃)、3.1×10-6Ω．cm(硬化溫度200℃)。
[實施例9]
使實施例1中所獲得之比表面積為1.13m2/g之樹枝狀覆銀銅粉分散於樹脂中而製成電磁波屏蔽材。
即，對實施例1中所獲得之樹枝狀覆銀銅粉40g分別混合氯乙烯樹脂100g與甲基乙基酮200g，使用小型捏合機，以1200rpm混練
3分鐘，反覆進行3次該混練，藉此實現糊化。於糊化時，覆銀銅粉未發生凝集而均勻分散於樹脂中。使用梅爾棒(Meyer bar)將其塗佈於厚度100μm之由透明聚對苯二甲酸乙二酯片構成之基材上，加以乾燥而形成厚度25μm之電磁波屏蔽層。
關於電磁波屏蔽特性，使用頻率1GHz之電磁波，測定其衰減率，藉此進行評價。將特性評價之結果示於表1。
[實施例10]
使實施例2中所獲得之比表面積為1.24m2/g之樹枝狀覆銀銅粉分散於樹脂而製成電磁波屏蔽材。
即，對實施例2中所獲得之樹枝狀覆銀銅粉40g分別混合氯乙烯樹脂100g與甲基乙基酮200g，使用小型捏合機，以1200rpm混練3分鐘，反覆進行3次該混練，藉此實現糊化。糊化時，覆銀銅粉未發生凝集而均勻分散於樹脂中。使用梅爾棒將其塗佈於厚度100μm之由透明聚對苯二甲酸乙二酯片構成之基材上，加以乾燥而形成厚度25μm之電磁波屏蔽層。
關於電磁波屏蔽特性，使用頻率1GHz之電磁波，測定其衰減率，藉此進行評價。將特性評價之結果示於表1。
[實施例11]
使實施例4中所獲得之比表面積為2.16m2/g之樹枝狀覆銀銅粉分散於樹脂中而製成電磁波屏蔽材。
即，對實施例4中所獲得之樹枝狀覆銀銅粉40g分別混合氯乙烯樹脂100g與甲基乙基酮200g，使用小型捏合機，以1200rpm混練
3分鐘，反覆進行3次該混練，藉此實現糊化。糊化時，銅粉未發生凝集而均勻分散於樹脂中。使用梅爾棒將其塗佈於厚度100μm之由透明聚對苯二甲酸乙二酯片構成之基材上，加以乾燥而形成厚度25μm之電磁波屏蔽層。
關於電磁波屏蔽特性，使用頻率1GHz之電磁波，測定其衰減率，藉此進行評價。將特性評價之結果示於表1。
[比較例1]
於實施例1之條件中，不添加作為添加劑之具有啡結構之化合物即番紅、與作為非離子界面活性劑之分子量1000之聚乙二醇(PEG)，除此以外，於同一條件下使銅粉析出至陰極板上。並且，繼而，於與實施例1同一條件下，對所獲得之銅粉之表面被覆銀而獲得覆銀銅粉。
藉由上述利用掃描式電子顯微鏡(SEM)之方法觀察所獲得之覆銀銅粉之形狀，結果所獲得之覆銀銅粉儘管呈現樹枝狀之形狀，但為粒狀銅粒子集合而成，並非平板狀之樹枝狀覆銀銅粉。又，所獲得之覆銀銅粉之比表面積為0.14m2/g，銀被覆量相對於該覆銀銅粉整體之質量100%為30.4質量%。
繼而，對所製作之樹枝狀覆銀銅粉55質量份混合酚樹脂(群榮化學股份有限公司製造，PL-2211)15質量份、丁基賽路蘇(關東化學股份有限公司製造，鹿特級)10質量份，使用小型捏合機(日本精機製作所製造，No Bubbling Kneader NBK-1)，以1200rpm混練3分鐘，反覆進行3次該混練，藉此實現糊化。利用金屬刮漿板將所獲得之導電糊劑印刷於玻璃上，於大氣環境中分別在150℃、200℃進行30分鐘之硬化。
藉由硬化所獲得之被膜之電阻率值分別為165×10-6Ω．cm(硬化溫度150℃)，45.2×10-6Ω．cm(硬化溫度200℃)。
[比較例2]
使比較例1中所獲得之覆銀銅粉分散於樹脂而製成電磁波屏蔽材。
即，於實施例1中不添加作為添加劑之番紅與非離子界面活性劑，對於此條件下所獲得之比較例1之樹枝狀覆銀銅粉40g分別混合氯乙烯樹脂100g與甲基乙基酮200g，使用小型捏合機，以1200rpm混練3分鐘，反覆進行3次該混練，藉此實現糊化。糊化時，覆銀銅粉未發生凝集而均勻分散於樹脂中。使用梅爾棒將其塗佈於厚度100μm之由透明聚對苯二甲酸乙二酯片構成之基材上，加以乾燥而形成厚度25μm之電磁波屏蔽層。
關於電磁波屏蔽特性，使用頻率1GHz之電磁波，測定其衰減率，藉此進行評價。將特性評價之結果示於表1。
1‧‧‧(樹枝狀)覆銀銅粉
2‧‧‧主幹
3,3a、3,3b‧‧‧枝
Claims (12)
- 一種覆銀銅粉，其呈現樹枝狀形狀，該樹枝狀形狀具有直線成長之主幹與自該主幹分支出之多個枝，上述主幹及上述枝係平板狀銅粒子集合而構成，該平板狀銅粒子係根據掃描式電子顯微鏡(SEM)觀察而求出之剖面平均厚度為0.02μm~5.0μm者，於該銅粒子之表面被覆有銀，該覆銀銅粉之平均粒徑(D50)為1.0μm~100μm，上述銅粒子之相對於平板狀面為垂直方向之最大高度，為該平板狀面之水平方向之最大長度的1/10以下。
- 如申請專利範圍第1項之覆銀銅粉，其中，銀被覆量相對於經銀被覆之覆銀銅粉整體之質量100%為1質量%~50質量%。
- 如申請專利範圍第1項之覆銀銅粉，其體密度為0.5g/cm3~5.0g/cm3之範圍。
- 如申請專利範圍第1項之覆銀銅粉，其BET比表面積值為0.2m2/g~5.0m2/g。
- 一種金屬填料，其以整體之20質量%以上之比例含有申請專利範圍第1至4項中任一項之覆銀銅粉。
- 一種導電性糊，係使申請專利範圍第5項之金屬填料與樹脂混合而成。
- 一種電磁波屏蔽用導電性塗料，係使用申請專利範圍第5項之金屬填料而成。
- 一種電磁波屏蔽用導電性片，係使用申請專利範圍第5項之金屬填料而成。
- 一種覆銀銅粉之製造方法，係製造申請專利範圍第1至4項中任一項之覆銀銅粉之方法，其具有藉由電解法使銅粉自電解液析出至陰極上之步驟、與對該銅粉被覆銀之步驟，使上述電解液含有銅離子、1種以上之下述式(1)所表示之具有啡結構之化合物、及1種以上非離子界面活性劑，從而進行電解，
- 一種覆銀銅粉之製造方法，係製造申請專利範圍第1至4項中任一項 之覆銀銅粉之方法，其具有藉由電解法使銅粉自電解液析出至陰極上之步驟、與對該銅粉被覆銀之步驟，使上述電解液含有銅離子、1種以上之下述式(2)所表示之具有偶氮苯結構之化合物、及1種以上非離子界面活性劑，從而進行電解，
- 一種覆銀銅粉之製造方法，係製造申請專利範圍第1至4項中任一項之覆銀銅粉之方法，其具有藉由電解法使銅粉自電解液析出至陰極上之步驟、與對該銅粉被覆銀之步驟， 使上述電解液含有銅離子、1種以上之下述式(3)所表示之具有啡結構與偶氮苯結構之化合物、及1種以上非離子界面活性劑，從而進行電解，
- 一種覆銀銅粉之製造方法，係製造申請專利範圍第1至4項中任一項之覆銀銅粉之方法，其具有藉由電解法使銅粉自電解液析出至陰極上 之步驟、與對該銅粉被覆銀之步驟，使上述電解液含有銅離子、選自由下述式(1)所表示之具有啡結構之化合物、下述式(2)所表示之具有偶氮苯結構之化合物、及下述式(3)所表示之具有啡結構與偶氮苯結構之化合物所組成之群中之2種以上、以及1種以上非離子界面活性劑，從而進行電解，