WO2006038532A1 - ポリオレフィン微多孔膜 - Google Patents

ポリオレフィン微多孔膜 Download PDF

Info

Publication number
WO2006038532A1
WO2006038532A1 PCT/JP2005/018013 JP2005018013W WO2006038532A1 WO 2006038532 A1 WO2006038532 A1 WO 2006038532A1 JP 2005018013 W JP2005018013 W JP 2005018013W WO 2006038532 A1 WO2006038532 A1 WO 2006038532A1
Authority
WO
WIPO (PCT)
Prior art keywords
mass
microporous membrane
less
polyolefin microporous
plasticizer
Prior art date
Application number
PCT/JP2005/018013
Other languages
English (en)
French (fr)
Inventor
Masahiro Ohashi
Hiroshi Sogo
Original Assignee
Asahi Kasei Chemicals Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=36142608&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=WO2006038532(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Asahi Kasei Chemicals Corporation filed Critical Asahi Kasei Chemicals Corporation
Priority to CN2005800332684A priority Critical patent/CN101031421B/zh
Priority to EP05788195A priority patent/EP1787805B1/en
Priority to AT05788195T priority patent/ATE534513T1/de
Priority to US11/664,276 priority patent/US20080193833A1/en
Priority to JP2006539252A priority patent/JP4711965B2/ja
Publication of WO2006038532A1 publication Critical patent/WO2006038532A1/ja
Priority to US14/280,431 priority patent/US9741989B2/en
Priority to US15/628,348 priority patent/US10384426B2/en

Abstract

　本発明は、二層以上の積層フィルムを含むポリオレフィン微多孔膜であって、少なくとも片側の表面層は厚さが０．２μｍ以上５μｍ以下であり、かつ無機粒子を含み、少なくとも一層はポリエチレンを含み、透気度が５０秒／１００ｃｃ以上１０００秒／１００ｃｃ以下、突刺強度が３．０Ｎ/２０μｍ以上である、ポリオレフィン微多孔膜を提供する。  

Description

明 細 書
ポリオレフイン微多孔膜
技術分野
[0001] 本発明は、ポリオレフイン微多孔膜、特にリチウムイオン電池用セパレータ、精密濾 過膜、コンデンサー用セパレータ、燃料電池用材料に好適なポリオレフイン微多孔膜 に関する。
背景技術
[0002] ポリオレフイン微多孔膜は、精密濾過膜、電池用セパレータ、コンデンサー用セパ レータ、燃料電池用材料などに使用されており、特にリチウムイオン電池用セパレー タとして使用されている。近年、リチウムイオン電池は、携帯電話、ノート型パーソナ ルコンピュータなどの小型電子機器に用いられ、さらには電気自動車、小型バイクな どへの応用も図られている。
[0003] リチウムイオン電池用セパレータにはポリエチレン微多孔膜が使用されている。その 理由はポリエチレン微多孔膜が透過性に優れているとともに、電池の安全性確保の ために、 130°Cから 150°Cでポリマーを溶融させて連通孔を閉塞し、電流をシャットダ ゥンする機能を有するからである。シャットダウンとは、微多孔膜の孔が溶融した榭脂 によって閉塞され、膜の電気抵抗が増大することにより、リチウムイオンの流れを遮断 する現象である。微多孔膜を電池セパレータとして使用する場合、安全性確保の観 点にお ヽてはシャットダウン温度ができるだけ低 、ことが望まし 、。さらにセパレータ の機能として、孔閉塞後もフィルム形状を維持し、電極間の絶縁性を保持する必要も ある。つまり、セパレータのシャットダウン後、さらに電池の温度が上がると、セパレー タの流動化が始まり、電気抵抗が低下し、電流が復帰する。この温度をショート温度と よぶ。そのためショート温度が高いことが望ましい。
[0004] 小型電子機器の高機能化に伴 、、リチウムイオン電池の単位体積あたりの高容量 化が要求されている。それに伴い、高温でより高い安全性も必要となってくる。例えば 電池の異常発熱を想定した高温時にもさらなる安全性を保ち、同時に高温での特性 も維持することが求められている。高容量ィ匕を達成するためには、いかにセパレータ を薄膜ィ匕して電極を詰め込むかが解決策である。電極を詰め込むと電池内が密に充 填された状態となるため、電解液の含浸性の悪さが問題となる。また電池部材を捲回 するときにはセパレータにより強度な機械的負荷力 Sかかるので、セパレータが薄膜ィ匕 されたときでも、高い機械強度が必要となる。さらに電極が密に充填された状態で電 池の出力特性も向上させる必要があるため、セパレータの高い透過性も必要となって くる。そのため上述の機能を併せ持ち、かつセパレータの電解液の含浸性、機械強 度、透過性、および電池に用いたときの高温保存特性を兼ね備えたセパレータの開 発が課題となっていた。
[0005] 特許文献 1には、二種以上の積層シート製品において、セパレータとして高い耐熱 温度を発現することを目的に、第二種層に充填材を高い含有率で含有させることを 特徴とする技術を開示している。しかし、この文献に記載されている技術では、薄膜 化が困難であり、電池の単位体積あたりの高容量ィ匕を達成することが難しい。また特 許文献 1の実施例では二枚の 40メッシュの金網を通して押出して大きな凝集物を除 去している。この方法ではメッシュを通り抜ける凝集物が存在するため、通り抜けた凝 集物が存在する個所は、機械強度が弱ぐピンホールが発生しやすい。また、凝集物 を取り除いているために、局所的に組成の不均一が生じやすい問題がある。そのた め、膜の均一性向上が課題となる。
[0006] 特許文献 2には、ポリオレフイン系榭脂と無機粉体とで構成される無機質含有多孔 膜の層と、ポリオレフイン系榭脂 100質量％とで構成される有機質多孔膜の層を交互 に積層されたセパレータが開示されている。この文献では、含浸性およびシャットダウ ン特性と耐熱性を達成している。しかし、無機質含有膜は 10〜20 mであり、また有 機質多孔膜は無機質含有多孔膜をアルカリ溶液等で抽出除去して得られる。そのた め、これ以上の薄膜化は困難であり、電池の単位体積あたりの高容量化を達成する ことが難しい。また有機質多孔膜は気孔率の高い膜しか作製できないので、膜強度 は低くなる傾向になる。さらに特許文献 2の実施例では、無機質含有多孔膜と有機質 多孔膜を重ね合わせてセパレータを作製しているので、セパレータの層間が密着し ておらず、電池を作製する際にセパレータがずれるという問題点がある。
[0007] 特許文献 1 :特許第 2108985号公報 特許文献 2：特開 2001— 266828号公報
発明の開示
発明が解決しょうとする課題
[0008] 本発明の目的は、透過性、電解液の含浸性に優れ、より薄い薄膜ィ匕が可能であり、 薄膜ィ匕したときにも機械強度が高ぐ電池に用いる際の高温保存特性にも優れた、リ チウムイオン電池用セパレータ、精密濾過膜、セパレータ、燃料電池用材料に好適 なポリオレフイン微多孔膜を提供することである。
課題を解決するための手段
[0009] 本発明者らは、鋭意研究を重ねた結果、二層以上の積層フィルムの表面層の組成 と膜構成、無機粒子の分散方法を検討し、上記課題を解決することを見いだし、本発 明を完成するに至った。
すなわち、本発明は以下の通りである。
(1)二層以上の積層フィルムを含むポリオレフイン微多孔膜であって、
少なくとも片側の表面層は厚さが 0. 2 m以上 5 m以下であり、かつ無機粒子を 含み、少なくとも他の一層はポリエチレンを含み、
透気度が 50秒 ZlOOcc以上 1000秒 ZlOOcc以下、突刺強度が 3. 0N/20 μ m 以上である、ポリオレフイン微多孔膜。
(2)三層以上の積層フィルムを含む、（1)に記載のポリオレフイン微多孔膜。
(3)少なくとも片側の厚さが 0. 2 m以上 5 m以下である表面層が、無機粒子含有 率 5質量％以上 60質量％以下、かつポリプロピレン含有率 5質量％以上 95質量％ 以下である、（1)又は（2)に記載のポリオレフイン微多孔膜。
(4)少なくとも片側の厚さが 0. 2 m以上 5 m以下である表面層が、無機粒子含有 率 5質量％以上 60質量％以下、ポリプロピレン含有率 5質量％以上 90質量％以下、 かつポリエチレン含有率 5質量％以上 90質量％以下である、（1)又は（2)に記載の ポリオレフイン微多孔膜。
(5)少なくとも片側の厚さが 0. 2 m以上 5 m以下である表面層が、無機粒子含有 率 5質量％以上 60質量％以下、ポリプロピレン含有率 20質量％以上 90質量％以下 、かつポリエチレン含有率 5質量0 /0以上であり、少なくとも他の一層力 ポリエチレン を 30質量％以上含み、無機粒子を含まない、（1)又は（2)に記載のポリオレフイン微 多孔膜。
(6)全体の膜厚が 2 μ m以上 50 μ m以下である、（1)〜（5)の 、ずれかに記載のポリ ォレフィン微多孔膜。
(7)全体の膜厚が 5 μ m以上 30 μ m以下である、（1)〜（5)の 、ずれかに記載のポリ ォレフィン微多孔膜。
(8) MD方向と TD方向の破断強度の比が 0. 1以上 8. 0以下である、（1)〜（7)のい ずれかに記載のポリオレフイン微多孔膜。
(9)無機粒子がケィ素、アルミニウム、及びチタンのいずれか一つの酸化物あるいは 窒化物である、 (1)〜（8)のいずれかに記載のポリオレフイン微多孔膜。
(10)ポリオレフイン榭脂、無機粒子、可塑剤を式（1)の関係を満たす範囲で混練す る工程を経て得られる、 (1)〜（9)のいずれか〖こ記載のポリオレフイン微多孔膜。
0. 6≤可塑剤重量 Z (可塑剤吸油量 X無機粒子重量 X可塑剤密度） X 100≤l . 2 (1)
(11)共押出法により積層されたシートを形成し、二軸延伸を施し、可塑剤を抽出して 得られる、（1)〜（10)のいずれかに記載のポリオレフイン微多孔膜。
( 12) ( 1)〜（ 11)の 、ずれかに記載のポリオレフイン微多孔膜を用 、たリチウムィォ ン電池用セパレータ。
発明を実施するための最良の形態
[0010] 以下、本発明のポリオレフイン微多孔膜、およびその製造方法を説明する。
本発明は二層以上の積層フィルムを含むポリオレフイン微多孔膜であり、好ましくは 三層である。生産性の観点から、表面層の二層が同一の組成で、中間層が異なる組 成の二種三層構造がより好まし 、。
[0011] 表面層は、電解液の含浸性、電池に用いたときの高温保存特性のために無機粒子 を含有し、また透過性、機械強度を両立するために、膜厚を薄くする必要がある。ま た中間層は、透過性、シャットダウン特性を付与するためにポリエチレンを含有する 必要がある。
表面層において、無機粒子の含有率は 5質量％以上 60質量％以下が好ましぐよ り好ましくは 10質量％以上 50%質量以下、さらに好ましくは 20質量％以上 40%質 量以下である。無機粒子の含有率は、電解液の含浸性、電池の高温保存特性の観 点から 5質量％以上が好ましぐ機械強度および膜成形の観点力 60質量％以下が 好ましい。
[0012] このとき使用する無機粒子としては、ケィ素、アルミニウム、及びチタンの 、ずれか 一つの酸ィ匕物あるいは窒化物が好ましぐ例えばシリカ、アルミナが好適である。より 好ましくは、ポリオレフインの可塑剤への分散性の観点力 表面を疎水処理した無機 粒子である。また、本発明に使用する無機粒子は、使用する可塑剤に対する吸油量 力 150ml/ 1 OOg以上力 S好まし <、より好まし < it 150ml/ 1 OOg以上 1000ml/ 100 g以下である。さらに好ましくは 150mlZl00g以上 500mlZl00g以下である。吸油 量が 150mlZl00g以上の場合、無機粒子を溶融混練、押出しシートィ匕すると、シー ト中に凝集物が生じに《高倍率の延伸が可能であり、高強度かつ薄膜を達し得る。 また lOOOmlZlOOg以下の場合、無機粒子の嵩密度が大きいために生産時におけ る扱 、が容易であることにカ卩え、凝集物が生じにくい。
[0013] 本発明のポリオレフイン微多孔膜をセパレータとして用いる電池の高温保存特性お よび高耐熱特性をさらに向上させるために、表面層には 5質量％以上 95質量％以下 のポリプロピレンを含有することが好ましい。より好ましくは 5質量％以上 90質量％以 下、さらに好ましくは 20質量％以上 90質量％以下、最も好ましくは 30質量％以上 80 質量％以下である。
また、表面層にはポリプロピレン以外にポリエチレンなどのポリオレフイン類を使用 することもできる。この際、ポリオレフイン類は単独でもポリプロピレンと混合して使用し ても良い。セパレータを 20 m以下と薄膜ィ匕する観点から、シャットダウン機能を有 する層を厚くすることが好ましぐ全層がシャットダウン機能を有することが最も好まし い。そのため表面層にはポリエチレンを含有することが好ましい。この場合、表面層と 中間層のシャットダウン温度の差を 10°C未満にすることが好ましぐ表面層には 5質 量％以上 90質量％以下のポリエチレンを含有することが好ましい。
[0014] このとき使用するポリプロピレンとしては、ホモポリマー、ランダムコポリマー、ブロック コポリマー等が挙げられ、一種類または二種類以上を混合して使用することができる 。また重合触媒にも特に制限はなぐチーグラー ·ナッタ系触媒やメタ口セン系触媒な どが挙げられる。また立体規則性にも特に制限はなぐァイソタクチックやシンジォタ クチックゃァタクチックを使用することができる。
このとき使用するポリエチレンとしては、高密度、中密度または低密度ポリエチレン が挙げられ、一種類あるいは二種類以上を混合して使用できる。また重合触媒にも 特に制限はなく、チーグラー ·ナッタ系触媒やフィリップス系触媒やメタ口セン系触媒 などが挙げられる。機械強度の観点から、高密度ポリエチレンが好ましい。また機械 強度と高透過性を両立させる観点から、ポリエチレンの粘度平均分子量は 10万以上 1200万以下が好ましぐより好ましくは 20万以上 300万以下、さらに好ましくは 20万 以上 200万以下、最も好ましくは 20万以上 100万以下である。
[0015] 本発明における少なくとも片側の表面層の厚さは 0. 2 m以上 5 m以下である。
好ましくは 0. 5 μ m以上 3 μ m以下である。電解液の含浸性、膜の均一性の点力 0 . 2 μ m以上であり、透過性、機械強度の点から 5 μ m以下である。
本発明における他の一層とは、厚さが 0. 2 m以上 5 m以下である表面層以外 の層をいう。例えばポリオレフイン微多孔膜が三層の場合は中間層、または中間層と 厚さが 0. 2 μ m以上 5 μ m以下である表面層とは異なる表面層となる。他の一層はポ リエチレンを必須成分として含む。他の一層におけるポリエチレンの割合は、透過性 、シャットダウン温度の観点から、好ましくは 5質量％以上、さらに好ましくは 30質量 %以上、より好ましくは 50質量％以上、最も好ましくは 80質量％である。必要に応じ て、他の一層にはシャットダウン特性、機械強度を損なわない範囲で、無機粒子が含 まれていてもよい。
[0016] さらに本発明の効果を損なわない範囲で、ポリオレフイン組成物には酸ィ匕防止剤、 核剤などの添加剤を適量添加してもよ 、。
本発明のポリオレフイン微多孔膜は、例えばポリオレフイン樹脂と無機粒子、可塑剤
、あるいはポリオレフイン樹脂と可塑剤を溶融混練し、押出成形、延伸、可塑剤抽出、 熱処理の工程によって製造される。
[0017] 本発明にお 、てポリオレフイン樹脂と無機粒子と可塑剤を溶融混練する方法は、あ らカじめポリオレフイン樹脂と無機粒子と可塑剤をヘンシェルミキサー等で所定の割 合で事前混練する工程を経て、該混練物を押出機に投入し、加熱溶融させながら任 意の比率で可塑剤を導入し、さらに混練することが挙げられる。具体的には、ポリオレ フィン榭脂と無機粒子と以下の範囲で指定される添加量の可塑剤とをヘンシェルミキ サ一等で事前混練したものを二軸押出機に投入し、所定可塑剤添加量の残り分をサ イドフイードすることができる。このような方法によって、無機粒子の分散性がより良好 なシートを得ることができ、無機粒子を含む層が高倍率の延伸で破膜することなく実 施することができる。
[0018] 具体的にはポリオレフイン樹脂と無機粒子と可塑剤を式（1)の範囲の量で事前混 練する。
0. 6≤可塑剤重量 Z (可塑剤吸油量 X無機粒子重量 X可塑剤密度） X 100≤l. 2 (1)
0. 6以上の場合、無機粒子が適度に可塑剤を保持しポリオレフイン樹脂との嵩密 度の差力 、さくなるために均一に分散する。 1. 2以下の場合、大量の可塑剤中に無 機粒子を混練することによる無機粒子の凝集を防ぐことができる。さらに好ましい条件 は 0. 7以上 1. 0以下である。最終的に添加する混練物の割合が上記の範囲内であ れば、押出機等を用いてポリオレフイン榭脂、無機粒子、可塑剤を一度に混練しても 、無機粒子の分散性の良好なシートを得ることができる。
溶融混練には、一軸押出機や二軸押出機などを用いる方法が挙げられる。溶融混 練の温度は 160°C以上 300°C以下が好ましい。
[0019] 可塑剤は、ポリオレフインと混合した際に、その融点以上において相溶することので きる有機化合物が望ましい。このような可塑剤として、例えば流動パラフィンやバラフ インワックスなどの炭化水素類、ジ 2—ェチルへキシルフタレート、ジヘプチルフタ レート、ジブチルフタレートなどのフタル酸エステル類、その他、セバシン酸エステル 類、ステアリン酸エステル類、アジピン酸エステル類、リン酸エステル類が挙げられる 。これらの可塑剤を単独で使用しても、 2種以上混合して使用してもカゝまわない。可 塑剤の溶融混練される全混合物中に占める割合は、 20質量％以上 80質量％以下 が好ましい。
[0020] 押出成形は、スリットダイや Tダイなどのシートダイ力 押出しキャストロールなどで 冷却する方法や、インフレーション法により行い、これによりゲルシートを得ることがで きる。本発明のポリオレフイン微多孔膜は、それぞれの押出機力も各層を構成するゲ ルシートを一体ィ匕させて一つのダイで共押出する方法、各層を構成するゲルシートを 重ね合わせて熱融着する方法のいずれでも作製できる。共押出法の方が、高い層間 接着強度を得やすく、層間に連通孔を形成しやす!ヽために高透過性を維持しやすく 、生産性にも優れているためにより好ましい。
延伸としては、高機械強度、縦横の物性バランスに優れるので、二軸延伸が好まし い。好ましくは同時二軸延伸、逐次二軸延伸である。延伸温度は、好ましくは 100°C 以上から 135°C以下である。延伸倍率は、膜強度の観点で好ましくは面積倍率で 3 倍以上から 200倍以下である。
[0021] 可塑剤の抽出は膜を抽出溶媒に浸漬することにより行い、その後膜を十分乾燥さ せる。抽出溶媒は、ポリオレフイン、無機粒子に対して貧溶媒であり、かつ可塑剤に 対しては良溶媒であり、沸点がポリオレフインの融点よりも低いことが望ましい。このよ うな抽出溶媒として、例えば塩化メチレン、 1,1,1—トリクロロェタンなどの塩素系溶剤 、メチルェチルケトン、アセトンなどのケトン類、ヒドロフルォロカーボン、ヒドロフルォロ エーテル、環状ヒドロフルォロカーボン、ペルォロカーボン、ペルフルォロエーテルな どのハロゲン系有機溶剤、ジェチルエーテルゃテトラヒドロフランなどのエーテル類、 n—へキサン、シクロへキサンなどの炭化水素類、メタノール、イソプロピルアルコー ルなどのアルコール類が挙げられる。またこれらの抽出溶媒を二種類以上使用しても よい。この中では特に塩化メチレンが好ましい。
[0022] また可塑剤の抽出後には、膜厚、透気度などの膜物性の調整のため必要に応じて 延伸を加えてもよい。該抽出後の延伸は一軸延伸、同時二軸延伸、逐次二軸延伸 が挙げられ、好ましくは同時二軸延伸、逐次二軸延伸である。延伸温度は、好ましく は 100°C以上から 135°C以下である。延伸倍率は、好ましくは面積倍率で 1倍を越え て 10倍以下である。
熱処理は、高温雰囲気下での膜収縮を低減するために、例えばテンター、ー軸延 伸機、あるいは両方を用いて、 100°C以上ポリエチレンの融点以下の温度範囲で、 幅方向、長さ方向、あるいは両方向にその収縮応力を緩和することにより行う。 [0023] 上記のように作製したポリオレフイン微多孔膜は、各層とも孔が三次元的に入り組ん でいる三次元網目構造をとつていることが好ましい。このとき、その三次元網目構造 が各層でつながつていることが好ましい。三次元網目構造とは、表面が葉脈状であり 、任意の三次元座標軸方向からの断面の膜構造力スポンジ状である構造である。葉 脈状とはフイブリルが網状構造を形成して 、る状態である。これらは走査型電子顕微 鏡で表面および断面を観察することにより確認できる。三次元網目構造のフィブリル 径は 0. 01 μ m以上 0. 3 μ m以下であることが好ましぐ走査型電子顕微鏡で観察 できる。
[0024] 本発明のポリオレフイン微多孔膜は、表面層の厚さを調整し、かつ無機粒子を配合 することで、透過性、機械強度、電解液の含浸性に優れ、ショート温度が高ぐ他の 一層にポリエチレンを含有することで、シャットダウン温度が低いという特徴をもつ。表 面層にポリプロピレンを含有することにより、高温保存特性および高耐熱特性をさら に向上させることができる。
[0025] 本発明のポリオレフイン微多孔膜は、好ましくは以下の膜物性を示す。
(1)二層以上の積層フィルムで構成される微多孔膜全体における膜厚は、電池の絶 縁不良防止の点から 2 μ m以上 50 μ m以下が好ましい。より好ましくは 5 μ m以上 30 μ m以下、さらに好ましくは 7 μ m以上 25 μ m以下である。
(2)表面層の膜厚は、 0. 2 m以上 5 m以下である。より好ましくは 0. 5 m以上 3 μ m以" hである。
(3)透気度は、機械強度、自己放電の点から 50秒 ZlOOcc、電池のサイクル特性、 レート特性の点から 1000秒 ZlOOcc以下である。好ましくは 70秒 ZlOOcc以上 80 0秒 ZlOOcc以下、より好ましくは 100秒 ZlOOcc以上 600秒 ZlOOcc以下である。
(4)突刺強度は、電池の組立の点から 3. 0N/20 m以上である。好ましくは 4. ON/ 20 μ m以上である。
[0026] (5)破断強度は、電池の^ &立の点から MD方向、 TD方向ともに 500kg/cm2以上、 MD方向と TD方向の破断強度の比は 0. 1以上 8. 0以下が好ましい。より好ましくは 0. 1以上 5.0以下、さらに好ましくは 0. 5以上 2. 0以下である。
(6)電解液含浸性は、例えば ImolZLの六フッ化リン酸リチウム溶液 (溶媒:プロピレ ンカーボネート）を用いた場合、透明化するまでの時間は短いほど好ましい。具体的 には 30秒以下が好ましぐより好ましくは 20秒以下、更に好ましくは 10秒以下である
(7)下記の試験方法 (8)に記す高温保存特性は 70%以上であり、より好ましくは 75 %以上である。高温保存特性が 70%未満では、高温時の電池特性が低下する。高 温保存特性は 60°C、 7日間保存したときの容量維持率力も求める。
[0027] 次に実施例によって本発明をさらに詳細に説明するが、本発明は下記実施例に限 定されるものではない。実施例において示される試験方法は次の通りである。
(1)膜厚 m)
ダイヤルゲージ (尾崎製作所：商標、 PEACOCK No. 25)にて測定した。 MD10 mm X TDlOmmのサンプルを切り出し、格子状に 9箇所（3点 X 3点）の膜厚を測定 した。得られた平均値を膜厚 ( μ m)とした。
(2) 表面層の膜厚 （ m)
走査型電子顕微鏡の断面観察、もしくは剥離が可能な場合にはこの層を剥離させ て上記（1)の方法により、膜厚を測定した。
(3) 透気度 （秒 ZlOOcc)
JIS P— 8117に準拠し、ガーレー式透気度計 (東洋精機製作所 (株)製「G— B2」 (商標)）で測定した。
[0028] (4) 突刺強度 (ΝΖ20 /ζ πι)
カトーテック製 KES— G5ハンディー圧縮試験器を用いて、針先端の曲率半径 0. 5 mm、突刺速度 2mmZsecの条件で突刺試験を行うことにより、最大突刺荷重として 生の突刺強度 (N)が得られる。これに 20 ( μ m) Z膜厚 ( μ m)を乗じることにより 20 μ m膜厚換算突刺強度 (NZ20 μ m)を算出した。
(5) MD方向の破断強度と TD方向の破断強度の比 A
引張試験機（島津製作所製オートグラフ AG— A型)を用いて、以下の条件で破断 強度を測定した。
サンプノレ开状 ： サンプノレ長 X サンプノレ幅 = 100 mm X 10 mm チャック間距離 ： 50 mm 引張速度 ： 200 mm/min
次に上記方法で MD、 TD方向のサンプル破断時の強度を求めて、次式で A値を計 昇した。
A = (MD方向の破断強度) / (TD方向の破断強度）
[0029] (6)可塑剤吸油量 （mlZlOOg)
FRONTEX S410可塑剤吸油量測定器を用いて測定を行った。無機粒子 5gを 投入し、混練しながら可塑剤を滴下した。混練時のトルクが上昇し、最大トルクの 70 %に減少するときの可塑剤添加量 (ml)を求め、それと無機粒子重量 (g)より、次式を 用いて計算した。
可塑剤吸油量 (ml/100g) =可塑剤添加量/無機粒子重量 X 100
(7)電解液の含浸性
電解液として ImolZLの六フッ化リン酸リチウム溶液 (溶媒:プロピレンカーボネート )を使用し、グローブボックス内で該電解液を微多孔膜に滴下した。 30秒後に電解液 の液滴と微多孔膜が接している面の 80%以上が透明であった場合を含浸性が良好 (〇）と判定し、 80%未満であった場合を含浸性が十分ではな 、（ X )と判定した。
[0030] (8)高温保存特性 (%)
(a)正極の作製
正極活物質としてリチウムコバルト複合酸ィ匕物 LiCoOを 92. 2重量0 /0、導電材とし
2
てリン片グラフアイトとアセチレンブラックをそれぞれ 2. 3重量％、バインダーとしてポ リフッ化ビ-リデン（PVdF) 3. 2重量0 /0を N メチルピロリドン（NMP)中に分散させ てスラリーを作製する。このスラリーを正極集電体となる厚さ 20 mのアルミニウム箔 の片面にダイコーターで塗布し、 130°Cで 3分間乾燥後、ロールプレス機で圧縮成形 する。このとき、正極の活物質塗布量は 250g/m2、活物質嵩密度は 3. 00g/cm3 になるようにする。これを面積 2. 00cm2の円形に打ち抜く。
(b)負極の作製
負極活物質として人造グラフアイト 96. 9重量％、バインダーとしてカルボキシメチル セルロースのアンモ-ゥム塩 1. 4重量0 /0とスチレン ブタジエン共重合体ラテックス 1 . 7重量％を精製水中に分散させてスラリーを作製する。このスラリーを負極集電体と なる厚さ 12 /z mの銅箔の片面にダイコーターで塗布し、 120°Cで 3分間乾燥後、ロー ルプレス機で圧縮成形する。このとき、負極の活物質塗布量は 106gZm2、活物質 嵩密度は 1. 35g/cm3になるようにする。これを面積 2. 05cm2の円形に打ち抜く。
[0031] (c)簡易電池組立
ポリオレフイン微多孔膜、正極、負極、電解液 (ImolZLの六フッ化リン酸リチウム溶 液 (溶媒：エチレンカーボネート Zェチルメチルカーボネート = 1Z2)をアルミニウム およびステンレス製のセル内に組み込んで、簡易リチウムイオン電池を作製する。 (d)高温保存特性評価
上記のように組み立てた簡易電池を 25°C雰囲気下、 3mA (約 0. 5C)の電流値で 電池電圧 4. 2Vまで充電し、到達後 4. 2Vを保持するようにして電流値を 3mAから 絞り始めるという方法で、合計 6時間の充電を行う。そして 3mAの電流値で電池電圧 3. OVまで放電する。
次に 25°C雰囲気下、 6mA (約 1. OC)の電流値で電池電圧 4. 2Vまで充電し、到 達後 4. 2Vを保持するようにして電流値を 6mAから絞り始めるという方法で、合計 3 時間充電を行う。そして 6mAの電流値で電池電圧 3. OVまで放電する。このときの 放電容量を A(mAh)とする。
次に 25°C雰囲気下、 6mA (約 1. OC)の電流値で電池電圧 4. 2Vまで充電し、到 達後 4. 2Vを保持するようにして電流値を 6mAから絞り始めるという方法で、合計 3 時間充電を行う。充電状態に保持したセルを 60°C雰囲気下で 7日間保存する。その 後セルを取り出し 25°C雰囲気下、 6mAの電流値で電池電圧 3. OVまで放電する。 次に 25°C雰囲気下、 6mA (約 1. OC)の電流値で電池電圧 4. 2Vまで充電し、到達 後 4. 2Vを保持するようにして電流値を 6mAから絞り始めるという方法で、合計 3時 間充電を行う。そして 6mAの電流値で電池電圧 3. OVまで放電する。このときの放 電容量を B (mAh)とする。 Bの Aに対する比率から、容量維持率を高温保存特性とし て算出する。
[0032] 本発明を実施例に基づいて説明する。
[実施例 1]
表面層の原料として、ポリプロピレン (密度 0. 90、粘度平均分子量 30万） 32質量 部、シリカ（吸油量 200ml/100g) 8質量部、核剤としてビス（P ェチルベンジリデン )ソルビトールを 2質量部、酸ィ匕防止剤としてテトラキスー [メチレン一（3 '、 5 '—ジー t ーブチルー 4 'ーヒドロキシフエ-ル）プロピオネート]メタンを 0. 3質量部、可塑剤とし て、流動ノ ラフィン（37. 78。Cにおける動粘度 75. 90cSt、密度 0. 868)を 12質量 部加えた後、ミキサーで攪拌し原料を調製した。中間層の原料として、高密度ポリエ チレン (密度 0. 95、粘度平均分子量 25万) 40質量部、酸化防止剤としてテトラキス —[メチレン一（3 '、 5，ージ tーブチルー 4 'ーヒドロキシフエ-ル）プロピオネート]メ タンを 0. 3質量部配合し原料を調製した。各配合物は 2台の口径 25mm、 L/D=4 8の二軸押出機フィーダ一を介して投入した。さらに表面層には流動パラフィン 48質 量部、中間層には 60質量部をサイドフィードでそれぞれの押出機に注入し、両表面 層、中間層の押出量がそれぞれ、 1時間当たり 5kg、 15kgになるように調整し、 200 °C、 200rpmの条件で混練した後、押出機先端に取り付けた共押出（二種三層）が 可能な Tダイ力も押出した。ただちに 25°Cに冷却したキャストロールで冷却固化させ 、厚さ 1.5mmのシートを成形した。このシートを同時二軸延伸機で 124°Cの条件で 7 X 7倍に延伸した後、塩化メチレンに浸漬して、流動パラフィンを抽出除去後乾燥し、 テンター延伸機により 125°Cの条件で横方向に 1. 5倍延伸した。その後、この延伸 シートを 130°Cで 7%幅方向に緩和して熱処理を行い、表面層の二層が同一の組成 で、中間層が異なる組成の二種三層構造を有する微多孔膜を得た。得られた微多孔 膜の物性を表 1に示す。
[実施例 2]
表面層の原料として、ポリプロピレンの代わりに高密度ポリエチレン (密度 0. 95、粘 度平均分子量 25万)を用いた以外は実施例 1と同様に微多孔膜を作製した。作製し た微多孔膜の物性を表 1に示す。
[実施例 3]
表面層の原料として、ポリプロピレン (密度 0. 90、粘度平均分子量 30万） 36質量 部、シリカ（吸油量 200ml/100g) 4質量部、可塑剤として流動パラフィンを 6質量部 加えた後、ミキサーで攪拌し原料を調製し、さらに表面層には流動パラフィン 54質量 部をサイドフィードで押出機に注入した以外は実施例 1と同様に微多孔膜を作製した 。作製した微多孔膜の物性を表 1に示す。
[0034] [実施例 4]
シートの厚さを 0. 9mmとした以外は実施例 1と同様に微多孔膜を作製した。作製 した微多孔膜の物性を表 1に示す。
[実施例 5]
シートの厚さを 3. Ommとした以外は実施例 1と同様に微多孔膜を作製した。作製 した微多孔膜の物性を表 1に示す。
[実施例 6]
表面層の押出量を 1時間当たり 2. 5kgとした以外は実施例 1と同様に微多孔膜を 作製した。作製した微多孔膜の物性を表 1に示す。
[実施例 7]
表面層の押出量を 1時間当たり 10kgとした以外は実施例 1と同様に微多孔膜を作 製した。作製した微多孔膜の物性を表 1に示す。
[0035] [実施例 8]
表面層の原料として、ポリプロピレン (密度 0. 90、粘度平均分子量 30万） 24質量 部、シリカ（吸油量 200ml/100g) 16質量部、可塑剤として流動パラフィンを 20質量 部加えた後、ミキサーで攪拌し原料を調製し、さらに表面層には流動パラフィン 40質 量部をサイドフィードで押出機に注入した以外は実施例 1と同様に微多孔膜を作製し た。作製した微多孔膜の物性を表 1に示す。
[実施例 9]
表面層の原料として、ポリプロピレン (密度 0. 90、粘度平均分子量 30万） 25質量 部、高密度ポリエチレン (密度 0. 95、粘度平均分子量 25万） 7質量部、シリカ（吸油 量 200ml/100g) 8質量部とした以外は実施例 1と同様に微多孔膜を作製した。作製 した微多孔膜の物性を表 1に示す。
[0036] [実施例 10]
表面層の原料として、ポリプロピレン (密度 0. 90、粘度平均分子量 30万） 32質量 部、アルミナ（吸油量 180ml/100g) 8質量部、可塑剤として流動パラフィンを 10質量 部加えた後、ミキサーで攪拌し原料を調製し、さらに表面層には流動パラフィン 50質 量部をサイドフィードで押出機に注入した以外は実施例 1と同様に微多孔膜を作製し た。作製した微多孔膜の物性を表 1に示す。
[実施例 11]
中間層の原料として、高密度ポリエチレン (密度 0. 95、粘度平均分子量 25万） 36 質量部、シリカ（吸油量 200ml/100g)4質量部、可塑剤として流動パラフィンを 6質 量部加えた後、ミキサーで攪拌し原料を調製し、さらに中間層には流動パラフィン 54 質量部をサイドフィードで押出機に注入した以外は、実施例 1と同様に微多孔膜を作 製した。作製した微多孔膜の物性を表 1に示す。
[実施例 12]
Tダイの形状を変更することで、二層積層フィルム構造のポリオレフイン微多孔膜を 作製した。無機粒子を含む層の原料として、ポリプロピレン (密度 0. 90、粘度平均分 子量 30万） 32質量部、シリカ（吸油量 200ml/100g) 8質量部、核剤としてビス — ェチルベンジリデン)ソルビトールを 2質量部、酸ィ匕防止剤としてテトラキスー [メチレ ン 3 '、5 '—ジー t ブチル 4 ' ヒドロキシフエ-ル）プロピオネート]メタンを 0. 3質量部、可塑剤として、流動パラフィン（37. 78°Cにおける動粘度 75. 90cSt)を 1 2質量部加えた後、ミキサーで攪拌し原料を調製した。他の一層の原料として、高密 度ポリエチレン (密度 0. 95、粘度平均分子量 25万) 40質量部、酸化防止剤としてテ トラキスー [メチレン一（3 '、 5，ージ tーブチルー 4 'ーヒドロキシフエ-ル）プロピオ ネート]メタンを 0. 3質量部配合し原料を調製した。各配合物は 2台の口径 25mm、 L ZD = 48の二軸押出機フィーダ一を介して投入した。さらに無機粒子を含む層には 流動パラフィン 48質量部、他の一層には 60質量部をサイドフィードでそれぞれの押 出機に注入し、無機粒子を含む層、他の一層の押出量がそれぞれ、 1時間当たり 2. 5kg、 17. 5kgになるように調整し、 200°C、 200rpmの条件で混練した後、押出機 先端に取り付けた共押出（二種二層）が可能な Tダイ力 押出した。それ以外は実施 例 1と同様に微多孔膜を作製した。得られた微多孔膜の物性を表 1に示す。なお高 温保存特性評価では、無機粒子を含む層を正極側に接するように、簡易電池を組み 立てた。
[実施例 13] 表面層の原料として、ポリプロピレン (密度 0. 90、粘度平均分子量 30万） 12質量 部、シリカ（吸油量 200ml/100g) 28質量部とした以外は実施例 1と同様に微多孔膜 を作製した。しかし、延伸時に表面層が破膜して、微多孔膜を安定して作製すること ができな力つた。破膜して！/、な 、部分で測定した物性を表 1に示す。
[実施例 14]
表面層の原料として、ポリプロピレン (密度 0. 90、粘度平均分子量 30万） 32質量 部、シリカ（吸油量 200ml/100g) 5質量部、可塑剤として流動パラフィンを 8質量部 加えた後、ミキサーで攪拌し原料を調製し、さらに表面層には流動パラフィン 52質量 部をサイドフィードで押出機に注入した以外は実施例 1と同様に微多孔膜を作製した 。しかし、延伸時に表面層が破膜して、微多孔膜を安定して作製することができなか つた。破膜して ヽな!ヽ部分で測定した物性を表 1に示す。
[0038] [比較例 1]
表面層の原料として、ポリプロピレン (密度 0. 90、粘度平均分子量 30万）を 40質 量部にし、シリカを添加しな力つた以外は、実施例 1と同様に微多孔膜を作製した。 作製した微多孔膜の物性を表 1に示すが、透気度が高く電解液の含浸性が不十分 であった。
[比較例 2]
表面層、中間層の押出量がそれぞれ、 1時間当たり 10kg、 5kgになるように調整し た以外は、実施例 1と同様に微多孔膜を作製した。作製した微多孔膜の物性を表 1 に示す力 透気度が 1000秒 ZlOOccを超えた。
[0039] [比較例 3]
表面層の原料として、ポリプロピレン (密度 0. 90、粘度平均分子量 30万） 32質量 部、シリカ（吸油量 200ml/100g) 8質量部、核剤としてビス（P—ェチルベンジリデン )ソルビトールを 2質量部、酸ィ匕防止剤としてテトラキスー [メチレン一（3 '、 5 '—ジー t ーブチルー 4 'ーヒドロキシフエ-ル）プロピオネート]メタンを 0. 3質量部、可塑剤とし て、流動パラフィン（37. 78°Cにおける動粘度 75. 90cSt)を 12質量部加えた後、ミ キサ一で攪拌し原料を調製した。中間層の原料として、高密度ポリエチレン (密度 0. 95、粘度平均分子量 25万) 40質量部、酸ィ匕防止剤としてテトラキスー [メチレン一（3 '、 5，ージ—tーブチルー 4 'ーヒドロキシフエ-ル）プロピオネート]メタンを 0. 3質量 部配合し原料を調製した。各配合物は 2台の口径 25mm、 LZD=48の二軸押出機 フィーダ一を介して投入した。さらに表面層には流動パラフィン 48質量部、中間層に は 60質量部をサイドフィードでそれぞれの押出機に注入し、表面層、中間層の押出 量がそれぞれ、 1時間当たり 2kg、 6kgになるように調整し、 200°C、 200rpmの条件 で混練した後、押出機先端に取り付けた共押出（2種 3層）が可能な Tダイ力 押出し た。ただちに 25°Cに冷却したキャストロールで冷却固化させ、厚さ 0. 25mmのシート を成形した。このシートを一軸延伸機で 124°Cの条件で 6倍に延伸した後、この延伸 フィルムを塩化メチレンに浸漬し、流動パラフィンを抽出除去後乾燥し、微多孔膜を 得た。得られた微多孔膜の物性を表 1に示すが、突刺強度が 3. 0ΝΖ20 ;ζ ΐη未満で めつに。
[表 1-1]
全体の 無機粒子を含 無機粒子を含 式 1 透気度 突刺強度 破断強度の比 電解液の fei )皿保 7子 膜厚 む表面層の膜 む層の無機粒 (sec/1 OOcc) (Ν/20μ m) (MD/TD) 含浸性 特性 m) 厚 （ im) 子の含有量 (%)
(wt%)
実施例 1 20 2 20 0. 9 430 5. 2 0. 8 〇 77 実施例 2 20 2 20 0. 9 210 5. 4 1. 1 〇 71 実施例 3 20 2 10 0. 9 460 5. 1 0. 8 〇 76 実施例 4 10 1 20 0. 9 290 7. 3 1. 3 〇 77 実施例 5 40 5 20 0. 9 720 4. 3 0. 7 〇 76 実施例 6 20 1 20 0. 9 320 5. 2 0. 8 〇 77 実施例 7 20 4 20 0. 9 630 4. 8 1. 0 〇 76
〕 s〕〔2l3004-
全体の 無機粒子を含 無機粒子を含 式 透気度 突刺強度 破断強度の比 雹解液の 皿保チ 膜厚 む表面層の膜 む層の無機粒 含浸性 特性
厚 子の含有量 実施例 〇 実施例 〇 実施例 1 0 20 2 20 0. 480 4. 4 0. 8 ο 75 実施例 表面層 〇 中間層 実施例 ο 実施例 1 3 20 2 70 0. 2 380 θ ο 76 実施例 - 〇
〕 s〕 〔1l2004- 全体の 無機粒子を含 無機粒子を含 式 1 透気度 突刺強度 破断強度の比 電解液の / m ¾ 7子 膜厚 む表面層の膜 む層の無機粒 (sec/1 OOcc) (N/20 μ m) (MD/TD) 含浸性 特性
(yUm) 厚 m) 子の含有量 (%)
(wt%)
比較例 1 20 2 0 - 1010 5. 2 0. 8 X 72 比較例 2 20 8 20 0. 9 1020 5. 5 0. 8 〇 75 比較例 3 40 5 20 0. 9 260 2. 8 10. 6 〇 75
実施例 1 3 1 4は表面層が破膜しなかった部分を測定
産業上の利用可能性
本発明のポリオレフイン微多孔膜は、精密濾過膜、電池用セパレータ、コンデンサ ー用セパレータ、燃料電池用材料などに使用でき、特にリチウムイオン電池用セパレ ータとに好適である。

Claims

請求の範囲
[1] 二層以上の積層フィルムを含むポリオレフイン微多孔膜であって、
少なくとも片側の表面層は厚さが 0. 2 m以上 5 m以下であり、かつ無機粒子を 含み、少なくとも他の一層はポリエチレンを含み、
透気度が 50秒 ZlOOcc以上 1000秒 ZlOOcc以下、突刺強度が 3. 0N/20 μ m 以上である、ポリオレフイン微多孔膜。
[2] 三層以上の積層フィルムを含む、請求項 1記載のポリオレフイン微多孔膜。
[3] 少なくとも片側の厚さが 0. 2 m以上 5 m以下である表面層が、無機粒子含有率
5質量％以上 60質量％以下、かつポリプロピレン含有率 5質量％以上 95質量％以 下である、請求項 1又は 2に記載のポリオレフイン微多孔膜。
[4] 少なくとも片側の厚さが 0. 2 m以上 5 m以下である表面層が、無機粒子含有率
5質量％以上 60質量％以下、ポリプロピレン含有率 5質量％以上 90質量％以下、か つポリエチレン含有率 5質量％以上 90質量％以下である、請求項 1又は 2に記載の ポリオレフイン微多孔膜。
[5] 少なくとも片側の厚さが 0. 2 m以上 5 m以下である表面層が、無機粒子含有率
5質量％以上 60質量％以下、ポリプロピレン含有率 20質量％以上 90質量％以下、 かつポリエチレン含有率 5質量％以上であり、少なくとも他の一層が、ポリエチレンを
30質量％以上含み、無機粒子を含まない、請求項 1又は 2に記載のポリオレフイン微 多孔膜。
[6] 全体の膜厚が 2 μ m以上 50 μ m以下である、請求項 1〜5のいずれ力 1項に記載 のポリオレフイン微多孔膜。
[7] 全体の膜厚が 5 μ m以上 30 μ m以下である、請求項 1〜5のいずれ力 1項に記載 のポリオレフイン微多孔膜。
[8] MD方向と TD方向の破断強度の比が 0. 1以上 8. 0以下である、請求項 1〜7のい ずれ力 1項に記載のポリオレフイン微多孔膜。
[9] 無機粒子がケィ素、アルミニウム、及びチタンの!/、ずれか一つの酸化物ある!/、は窒 化物である、請求項 1〜8のいずれか 1項に記載のポリオレフイン微多孔膜。
[10] ポリオレフイン榭脂、無機粒子、可塑剤を式（1)の関係を満たす範囲で混練するェ 程を経て得られる、請求項 1〜9のいずれか 1項に記載のポリオレフイン微多孔膜。
0. 6≤可塑剤重量 Z (可塑剤吸油量 X無機粒子重量 X可塑剤密度） X 100≤l . 2 (1)
[11] 共押出法により積層されたシートを形成し、二軸延伸を施し、可塑剤を抽出して得 られる、請求項 1〜10のいずれか 1項に記載のポリオレフイン微多孔膜。
[12] 請求項 1〜11のいずれか 1項に記載のポリオレフイン微多孔膜を用いたリチウムィ オン電池用セパレータ。
PCT/JP2005/018013 2004-10-01 2005-09-29 ポリオレフィン微多孔膜 WO2006038532A1 (ja)