WO2006016618A1 - フッ化ビニリデン系樹脂フィルム - Google Patents

フッ化ビニリデン系樹脂フィルム Download PDF

Info

Publication number
WO2006016618A1
WO2006016618A1 PCT/JP2005/014684 JP2005014684W WO2006016618A1 WO 2006016618 A1 WO2006016618 A1 WO 2006016618A1 JP 2005014684 W JP2005014684 W JP 2005014684W WO 2006016618 A1 WO2006016618 A1 WO 2006016618A1
Authority
WO
WIPO (PCT)
Prior art keywords
vinylidene fluoride
fluoride resin
methacrylic
weight
film
Prior art date
Application number
PCT/JP2005/014684
Other languages
English (en)
French (fr)
Inventor
Kazuhito Wada
Yukihiro Shimamoto
Original Assignee
Kaneka Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kaneka Corporation filed Critical Kaneka Corporation
Priority to JP2006531696A priority Critical patent/JP4958552B2/ja
Priority to US11/659,633 priority patent/US7452602B2/en
Priority to EP20050770467 priority patent/EP1798253B8/en
Publication of WO2006016618A1 publication Critical patent/WO2006016618A1/ja
Priority to US12/287,992 priority patent/US8303875B2/en

Abstract

　透明性、耐候性、耐薬品性、耐折曲げ割れ性および成形性に優れたフッ化ビニリデン系樹脂フィルムおよびフッ化ビニリデン系樹脂多層フィルムを提供する。フィルム成形時に、溶融状態のフッ化ビニリデン系樹脂をロールまたは金属ベルトに挟み込んで成形することにより、ポリフッ化ビニリデンの平均球晶直径が微小化され、上記特性を有するフッ化ビニリデン系樹脂フィルムおよびフッ化ビニリデン系樹脂多層フィルムを得ることができる。                                                                                     

Description

明 細 書
フッ化ビニリデン系樹脂フィルム
技術分野
[0001] 本発明は、優れた透明性を有するフッ化ビ-リデン系榭脂フィルムおよびフッ化ビ
-リデン系榭脂多層フィルムに関する。
背景技術
[0002] 耐候性ゃ耐薬品性に優れ、溶融成形が可能であるフッ化ビ-リデン系榭脂は、簡 易倉庫のテントやトラック用幌布等の表面保護フィルムとして、また、電照式看板や建 材、 自動車の外装フィルムの保護フィルムとして広く使用されている。近年、塗装代 替としてプラスチック成形品の表面にフッ化ビ -リデン系榭脂およびアクリル系榭脂を 積層したフィルムを加飾する方法が注目されている。保護フィルムや加飾フィルムは 、基材の表面に接着されて使用されるため、基材の表面に施した印刷や模様が鮮明 に見える透明性が要求されている。しかし、フッ化ビ-リデン系榭脂は結晶性榭脂で あり、結晶化速度が大きいため、透明性を満足させることは非常に困難であった。
[0003] これまでに、フィルムの薄膜ィ匕 (特許文献 1参照）、フッ化ビ -リデン系榭脂への他 モノマーの共重合 (特許文献 2参照）、メタクリル系樹脂との混合 (特許文献 3参照）、 等の方法が提案されているが、これらの方法により得られるフィルムは、要求される透 明性を満足できていない。
[0004] さらに、フッ化ビニリデン系榭脂フィルムの加工時の成形条件 (例えば、吐出速度、 引取速度、滞留時間、ダイス温度と冷媒温度の差、等)を制御することにより、ポリフッ 化ビ-リデンの球晶半径を小さくし、透明性を改善する方法 (特許文献 4参照）が提 案されているが、装置上の限界から平均球晶半径を 0. 5 m未満に抑制することが 困難であり、さらなる透明'性の向上が求められていた。
[0005] 他方、さらにメタクリル系榭脂組成物と共押出成形されたフッ化ビニリデン系榭脂多 層フィルム力 巿場において強い関心を持たれている。具体的な例としては、基材の 劣化防止、美観の維持などのために、プラスチック，金属，木材などの種々の材料に ラミネートする保護フィルム、また、自動車内外装部品にラミネートする塗装，メツキ代 替フィルムの用途などがあげられる。さらに、今後、環境問題力も塗装，メツキ工程か ら排出される有害物質の規制が強化されると予測されるため、これらの代替品として フィルムが注目されている。これらのフィルムに対しての要求特性として、耐折曲げ割 れ性および成形性が挙げられて!/、る。
特許文献 1 :特開昭 57— 187248号
特許文献 2：特開昭 64— 8665号
特許文献 3：特開平 5— 50566号
特許文献 4：特開平 6 - 80794号
発明の開示
発明が解決しょうとする課題
[0006] したがって、透明性、耐候性、耐薬品性、耐折曲げ割れ性および成形性に優れた フッ化ビ-リデン系榭脂フィルムおよびフッ化ビ-リデン系榭脂多層フィルムが求めら れていた。
課題を解決するための手段
[0007] そこで、本発明者らは鋭意検討した結果、溶融押出されたフッ化ビ-リデン系榭脂 をロールまたは金属ベルトで挟み込むことで、加圧しながら冷却することにより、著し く透明性が向上することを見出し、本発明に至った。
[0008] すなわち、本発明は、
ポリフッ化ビ-リデンの平均球晶直径が 1. 0 m未満であるフッ化ビ-リデン系榭脂 フィルム (請求項 1)、
曇価が 1%未満である請求項 1記載のフッ化ビニリデン系榭脂フィルム (請求項 2)、 口ールまたは金属ベルトに挟み込んで成形されてなる、請求項 1および 2に記載のフ ッ化ビ二リデン系榭脂フィルム (請求項 3)、
フッ化ビ-リデン榭脂が、フッ化ビ-リデン系榭脂（D) 50〜99. 9重量部およびメタク リル系榭脂組成物（C) O. 1〜50重量部からなる組成物である、請求項 1〜3のいず れかに記載のフッ化ビ-リデン榭脂フィルム (請求項 4)、
表面層を形成する請求項 1〜4のいずれかに記載のフッ化ビニリデン榭脂層と、メタ クリル系榭脂組成物（C)層とからなる、フッ化ビ-リデン系榭脂多層フィルム (請求項 フッ化ビ-リデン榭脂層とメタクリル系榭脂組成物 (C)とが共押出成形されてなる、請 求項 5に記載フッ化ビニリデン系榭脂多層フィルム (請求項 6)、
メタクリル系榭脂組成物 (C)が、
メタクリル酸エステル系重合体 (A)をアクリル酸エステル系架橋弾性体粒子 (B)の存 在下において重合することにより得られるメタクリル系榭脂組成物であって、
(1)メタクリル酸エステル系重合体 (A)力 メタクリル酸アルキルエステル 50〜 100重 量％、およびアクリル酸アルキルエステル 0〜50重量％を含む単量体混合物を重合 すること〖こより得られ、
(2)アクリル酸エステル系架橋弾性体粒子（B) ί アクリル酸アルキルエステル 50〜 100重量％ぉよびメタクリル酸アルキルエステル 50〜0重量％を含む単量体混合物 (b)および、 1分子あたり 2個以上の非共役二重結合を有する多官能性単量体を共 重合することにより得られ、
(3)アクリル酸エステル系架橋弾性体粒子 (B)の含有量が 5〜45重量％であり、 かつ、
(4)メタクリル系榭脂組成物（C) 100重量部に対して、一般式（1)で示す紫外線吸収 剤 0. 01〜30重量部を共重合してなることを特徴とするメタクリル系榭脂組成物であ る、
請求項 4記載のフッ化ビ-リデン系榭脂フィルムまたは請求項 5または 6記載のフッ化 ビ-リデン系榭脂多層フィルム
[化 1]
Figure imgf000005_0001
[0010] (式中、 Xは Hまたはハロゲン、 Rは H、メチルまたは炭素数 4〜6の t—アルキル基、
1
Rは直鎖または枝分かれ鎖状の炭素数 2〜： LOのアルキレン基、 Rは Hまたはメチル
2 3
である。 ) (請求項 7)、
請求項 1〜7のいずれかに記載のフッ化ビ-リデン系榭脂フィルムまたはフッ化ビ-リ デン系榭脂多層フィルムを積層した積層品（請求項 8)および
射出成形により製造される請求項 8記載の積層品 (請求項 9)
に関する。
発明の効果
[0011] 本発明のフッ化ビ-リデン系榭脂フィルムおよびフッ化ビ-リデン系榭脂多層フィル ムは、ロールまたは金属ベルトに挟み込んで、加圧しながら冷却することにより、透明 性の問題点を解決しつつ、フィルムの必要特性である耐候性、耐薬品性、耐折曲げ 割れ性および成形性に優れる。
図面の簡単な説明
[0012] [図 1]実施例 1の透過型電子顕微鏡観察写真 (倍率 10000倍）；黒色に見える層（表 面層）がフッ化ビニリデン系榭脂層であり、図 2に見られるような球晶構造は認められ ないく検出限界 0. 1 /ζ πι>。
[図 2]比較例 1の透過型電子顕微鏡観察写真 (倍率 10000倍）；黒色に見える層（表 面層）がフッ化ビ-リデン系榭脂層であり、全体に平均直径 3. O /z mの球晶が認めら れる。
符号の説明
[0013] 1 フッ化ビニリデン系榭脂層
2 メタクリル系榭脂組成物層
発明を実施するための最良の形態
[0014] 本発明におけるフッ化ビニリデン系榭脂フィルムとは、ポリフッ化ビニリデンの平均 球晶直径が、 1. O /z m未満であるフッ化ビ-リデン系榭脂フィルムである。好ましくは 、 0. 6 m未満であり、より好ましくは、検出限界である 0. 1 μ m未満である。ポリフッ 化ビニリデンの平均球晶直径が 1. O /z m以上では、得られるフッ化ビニリデン系榭脂 フィルムの透明性が満足できな 、傾向がある。
[0015] なお、本発明におけるポリフッ化ビ-リデンの平均球晶直径 Dは、透過型電子顕微
0
鏡観察法またはレーザー小角散乱法により測定した値である。
[0016] 本発明における過型電子顕微鏡観察法では、フッ化ビ-リデン系榭脂フィルムに 対し、凍結超薄切片法により試料調整した後、透過型電子顕微鏡（日本電子 (株)製 、 JEM— 1200EX)を用いて、カロ速電圧 80kVにて、 10000倍で観察した際のポリフ ッ化ビユリデンの結晶直径を測定した <検出限界: 0. 1 /ζ πι>。平均結晶直径は、 電子顕微鏡観察写真中の球晶 50個に関して、ノギスを用い、該球晶直径を測定し、 その平均値を採用した。
本発明におけるレーザー小角散乱法では、ポリフッ化ビ-リデン榭脂フィルムを 45度 ずつずらして 8枚重ねあわせて測定試料を作成した後、レーザー光源として He— Ne ガスレーザー（ネオアーク（株）、 NEO— 15MS ; 15mV、 632. 8nm)および PDA検 出器 (浜松ホトニタス (株)製、フォトダイオードアレイ S6494— 128)を用いて、小角 光散乱測定を行った。得られた散乱ベクトル 散乱強度チャートにおいて、散乱強 度極大値の散乱ベクトル Q (nm_1)をカーブフィッティングから求め、 R =4. 09/ max 0
Q の計算式により、平均球晶半径 Rを算出した。この場合、平均球晶直径としては max 0
、 Rを 2倍した値を採用する。
0
[0017] なお、後述するフッ化ビ-リデン系榭脂多層フィルムに関しては、クロ口ホルムに浸 積することにより、アクリル系榭脂組成物 (C)層を溶解させ、フッ化ビ-リデン系榭脂 層 (フィルム)を取り出し、小角光散乱測定の資料とした。
[0018] 本発明におけるフッ化ビ-リデン系榭脂フィルムとは、曇価が 1%以下である。好ま しくは 0. 9%以下、さらに好ましくは 0. 8%以下である。ポリフッ化ビ-リデンの曇価 力 1%を超えると、得られるフッ化ビ-リデン系榭脂フィルムの透明性が満足できない 傾向がある。なお、曇価は、 JIS K6714に準じて、温度 23°C± 2°C、湿度 50% ± 5 %の条件下にて測定した値である。メタクリル系榭脂組成物（C)との多層フィルムに おいては、フィルム全層の曇価もポリフッ化ビ-リデン系榭脂層の曇価とほとんど違わ な 、ために、曇価はフィルム全層につ 、て測定した。
[0019] 本発明におけるフッ化ビ-リデン系榭脂フィルムは、押出機より吐出された直後の 溶融状態にあるフッ化ビ-リデン榭脂を、ロールまたは金属ベルトに挟み込んで加圧 しながら冷却して成形する方法により得られたものである。溶融状態にあるフッ化ビニ リデン榭脂を挟み込まずにロールまたは金属ベルトに接触させるだけで、冷却した場 合には、平均球晶直径を 1. 0 m未満とすることができず、得られたフィルムの透明 性を満足できない。また、溶融状態にあるフッ化ビ-リデン榭脂をロールまたは金属 ベルトに挟み込んで成形することにより、平均球晶直径を小さくできるば力りでなぐ 表面を平滑にすることもできる。
[0020] 本発明のロールまたは金属ベルトによる挟み込み成形においては、ロールまたは 金属ベルトの温度を 10°C〜100°Cに保持することが好ましぐ 20°C〜60°Cがより好 ましい。ロールまたは金属ベルトの温度が 100°C超であれば、得られたフィルムの透 明性が悪ィ匕する傾向にあり、 10°C未満では卷取り時にフィルムにシヮが入る等の不 具合を生ずる可能性がある。
[0021] また、フッ化ビ-リデン系榭脂組成物およびメタクリル系榭脂組成物 (C)を共押出 成形する場合には、ロールまたは金属ベルトの温度は、フッ化ビ-リデン榭脂組成物 側を 10°C〜80°Cに、メタクリル系榭脂組成物（C)側を 10°C〜100°Cに保持すること が好まし!/ヽ。さらに、フッ化ビニリデン系榭脂組成物側およびメタクリル系榭脂組成物
(C)側のロールまたは金属ベルトの温度に差異を設けることにより、フッ化ビ-リデン 系榭脂 (D)の透明性および、メタクリル系榭脂組成物 (C)の卷取り時の不具合改善 を両立することができる。
[0022] 本発明のロールまたは金属ベルトによる挟み込み成形においては、押出機のダイ スのリップからロールまたは金属ベルトに接触するまでの距離力 300mm以下であ ることが好ましぐ 250mm以下であることがより好ましい。接触するまでの距離を 300 mm以下とすることにより、溶融榭脂を挟み込むまでの時間を短縮し、挟み込みによ る効果を大きくすることができる。
[0023] 本発明にお 、て用いられるロールまたは金属ベルトの表面粗度は、平均表面粗さ として 0. 5 m以下であることが好ましぐ 0. 2 m以下であることがより好ましい。口 ールまたは金属ベルトの平均表面粗さが 0. 5 μ m以下であれば、得られたフィルム が平滑化され、透明性をより高くすることができる。 [0024] 本発明において用いられるロールの材質は特に限定されないが、シリコンまたは金 属であることが好ましい。
[0025] 本発明におけるフッ化ビ-リデン系榭脂（D)は、フッ化ビ-リデン単独重合体、フッ 化ビ-リデンを構成単位として 70モル％以上含有する共重合体、さらには、これら重 合体の混合物であっても構わな 、。フッ化ビ-リデンと共重合される単量体としては、 エチレン、プロピレン、四フッ化工チレン、六フッ化プロピレン、三フッ化工チレン、三 フッ化塩ィ匕エチレン、フッ化ビュル等があげられ、これらの単量体は単独で使用して もよぐまたは 2種以上を併用してもよい。
[0026] これらのフッ化ビ -リデン系榭脂の融点は、 145〜180°Cの範囲にある力 本発明 におけるフッ化ビ-リデン系榭脂（D)としては、 165°C以上であることが好ましい。フ ッ化ビ -リデン系榭脂（D)の融点が 165°C以上であれば、インサート成形、インモー ルド成形、熱ロールによるラミネーシヨン成形などの 2次加工後の透明性の悪ィ匕を防 ぐことができる。
[0027] 本発明におけるフッ化ビ-リデン系榭脂フィルムは、フッ化ビ-リデン系榭脂（D)の みで形成されていてもよいが、透明性および、メタクリル系榭脂組成物 (C)または積 層対象物との接着性の点から、フッ化ビ-リデン系榭脂 (D) 50〜99. 9重量部およ びメタクリル系榭脂組成物（C) 0. 1〜50重量部力 なる組成物力 形成されることが 好ましい。より好ましくはフッ化ビ-リデン系榭脂（D) 60〜99. 9重量部およびメタタリ ル系榭脂組成物（C) O. 1〜40重量部、さらに好ましくはフッ化ビ-リデン系榭脂（D) 70-99. 9重量部およびメタクリル系榭脂組成物（C) O. 1〜30重量部である。メタク リル系榭脂組成物 (C)が 0. 1重量部以上含有されることにより、透明性および接着 性を向上することができる。フッ化ビ-リデン系榭脂 (D)が 50重量部未満では、耐薬 品性が低下する傾向がある。
[0028] 本発明におけるメタクリル系榭脂組成物（C)は、特に限定されるものではな 、が、メ タクリル酸エステル系重合体 (A)をアクリル酸エステル系架橋弾性体粒子 (B)の存在 下において重合することにより得られる多層構造重合体が好ましい。さらに、メタタリ ル酸エステル系重合体 (A)およびアクリル酸エステル系架橋弾性体粒子 (B)は、組 成として下記の範囲であることがより好まし 、。 [0029] 本発明におけるメタクリル系榭脂組成物（C)は、メタクリル酸エステル系重合体 (A) 、アクリル酸エステル系架橋弾性体粒子 (B)さらに、メタクリル酸エステル系重合体（ A)と順次段階的に重合するような 3層構造重合体であっても力まわない。
[0030] 本発明におけるメタクリル酸エステル系重合体 (A)は、メタクリル酸アルキルエステ ル 50〜100重量0 /0およびアクリル酸アルキルエステル 0〜50重量％を含む単量体 混合物を、少なくとも 1段以上で重合させてなるものである。より好ましくは、メタクリル 酸アルキルエステル 60〜100重量。 /0、およびアクリル酸アルキルエステル 0〜40重 量％である。アクリル酸アルキルエステルが 50重量％を超えると、得られるメタクリル 系榭脂組成物から形成しうるフィルムの耐熱性および表面硬度が低下する傾向があ る。
[0031] 本発明におけるメタクリル酸エステル系重合体 (A)を構成するメタクリル酸アルキル エステルは、重合反応性やコストの点から、アルキル基の炭素数が 1〜 12であるもの が好ましぐ直鎖状でも分岐状でもよい。その具体例としては、例えば、メタクリル酸メ チル、メタクリル酸ェチル、メタクリル酸プロピル、メタクリル酸 n—ブチル、メタクリル酸 イソプチル、メタクリル酸 t—ブチル等があげられる。これらの単量体は単独で使用し てもよく、また、 2種以上を併用してもよい。
[0032] 本発明におけるメタクリル酸エステル系重合体 (A)を構成するアクリル酸アルキル エステルは、重合反応性やコストの点力 アルキル基の炭素数が 1〜 12であるものが 好ましぐ直鎖状でも分岐状でもよい。その具体例としては、例えば、アクリル酸メチ ル、アクリル酸ェチル、アクリル酸プロピル、アクリル酸 n—ブチル、アクリル酸イソブチ ル、アクリル酸 tーブチル、アクリル酸 2—ェチルへキシル、アクリル酸 n—ォクチル 等があげられる。これらの単量体は、単独で使用してもよぐ 2種以上を併用してもよ い。
[0033] 本発明のメタクリル酸エステル系重合体 (A)においては、必要に応じて、メタクリル 酸アルキルエステルおよびアクリル酸アルキルエステルに対し共重合可能なェチレ ン系不飽和単量体を共重合してもかまわな 、。これらの共重合可能なエチレン系不 飽和単量体としては、例えば、塩化ビニル、臭化ビュル等のハロゲンィ匕ビニル、アタリ 口-トリル、メタタリ口-トリル等のシアン化ビュル、蟻酸ビュル、酢酸ビュル、プロピオ ン酸ビュル等のビュルエステル、スチレン、ビュルトルエン、 α—メチルスチレン等の 芳香族ビュル誘導体、塩ィ匕ビユリデン等のハロゲンィ匕ビユリデン、アクリル酸、アタリ ル酸ナトリウム、アクリル酸カルシウム等のアクリル酸およびその塩、アクリル酸 ーヒ ドロキシェチル、アクリル酸ジメチルアミノエチル、アクリル酸グリシジル、アクリルアミド 、 Ν—メチロールアクリルアミド等のアクリル酸アルキルエステル誘導体、メタクリル酸 、メアクリル酸ナトリウム、メタアクリル酸カルシウム等のメタクリル酸およびその塩、メタ クリルアミド、メタクリル酸 j8—ヒドロキシェチル、メタクリル酸ジメチルアミノエチル、メ タクリル酸グリシジル等のメタクリル酸アルキルエステル誘導体等があげられる。これ らの単量体は、単独で使用してもよぐ 2種以上を併用してもよい。
[0034] 本発明におけるアクリル酸エステル系架橋弾性体粒子 (B)は、アクリル酸アルキル エステル 50〜100重量0 /0およびメタクリル酸アルキルエステル 50〜0重量0 /0を含む 単量体混合物 (b)および、 1分子あたり 2個以上の非共役二重結合を有する多官能 性単量体からなる混合物を、少なくとも 1段以上で共重合させてなるものである。単量 体混合物（b)は、より好ましくは、アクリル酸アルキルエステル 60〜： LOO重量0 /0およ びメタクリル酸アルキルエステル 40〜0重量0 /0である。メタクリル酸アルキルエステル が 50重量％を超えると、得られるメタクリル系榭脂組成物カゝら形成しうるフィルムの耐 折曲げ割れ性が低下する傾向がある。
[0035] 本発明のアクリル酸エステル系架橋弾性体粒子 (B)にお 、ては、必要に応じて、メ タクリル酸アルキルエステルおよびアクリル酸アルキルエステルと共重合可能なェチ レン系不飽和単量体を共重合してもかまわな 、。
[0036] 本発明におけるアクリル酸エステル系架橋弾性体粒子 (B)は、 1分子あたり 2個以 上の非共役な反応性二重結合を有する多官能性単量体が共重合されているため、 得られる重合体が架橋弾性を示す。また、アクリル酸エステル系架橋弾性体粒子 (B )の重合時に反応せずに残った一方の反応性官能基 (二重結合)がグラフト交叉点と なって、一定割合のメタクリル酸エステル系共重合体 (A)力 アクリル酸エステル系 架橋弾性体粒子 (B)にグラフト化される。このことにより、アクリル酸エステル系架橋 弾性体粒子 (B) 1S メタクリル酸エステル系共重合体 (A)中に不連続かつ均一に分 散する。 [0037] 本発明において用いられる多官能性単量体としては、ァリルメタタリレート、ァリルァ クリレ一ト、トリァリルシアヌレ一ト、トリアリルイソシァヌレ一ト、ジァリルフタレ一ト、ジァ リノレマレート、ジビ-ノレアジペート、ジビュルベンゼンエチレングリコールジメタクリレ ート、ジビュルベンゼンエチレングリコールジアタリレート、ジエチレングリコールジメタ クリレ一ト、ジエチレングリコ一ルジアタリレ一ト、トリエチレングリコ一ルジメタクリレ一ト 、トリエチレングリコールジアタリレート、トリメチロールプロパントリメタタリレート、トリメ チロールプロパントリアタリレート、テトラメチロールメタンテトラメタタリレート、テトラメチ 口ールメタンテトラアタリレート、ジプロピレングリコ ルジメタクリレートおよびジプロピ レングリコールジアタリレート等があげられる。これらは、単独で使用してもよぐ 2種以 上を併用してもよい。
[0038] 本発明のアクリル酸エステル系架橋弾性体粒子 (B)における多官能性単量体の添 加量は、前記単量体混合物 (b) 100重量部に対して、 0. 05〜20重量部が好ましく 、 0. 1〜： LO重量部がより好ましい。多官能性単量体の添加量が 0. 05重量部未満で は、メタクリル系榭脂組成物カゝら形成しうるフィルムの耐衝撃性および耐折曲げ割れ 性が低下する傾向があり、 20重量部を超えても、耐衝撃性および耐折曲げ割れ性が 低下する傾向がある。
[0039] 本発明のアクリル酸エステル系架橋弾性体粒子 (B)で用いられるアクリル酸アルキ ルエステル、メタクリル酸アルキルエステルおよび、これらと共重合可能なエチレン系 不飽和単量体の具体例は、前記メタクリル酸エステル系重合体 (A)に使用したもの があげられる。
[0040] 本発明におけるアクリル酸エステル系架橋弾性体粒子 (B)の含有量は、メタクリル 系榭脂組成物（C)全体を 100重量％とした場合に、 5〜45重量％が好ましぐ 10〜 40重量％がより好ましぐ 15〜35重量％がさらに好ましい。アクリル酸エステル系架 橋弾性体粒子 (B)の含有量が 5重量％未満では、得られるメタクリル系榭脂組成物 力 形成しうるフィルムの耐衝撃性および耐折曲げ割れ性が低下する傾向にあり、 4 5重量％を超えると、フィルムの硬度および成形性が低下する傾向にある。
[0041] 本発明おけるメタクリル系榭脂組成物 (C)は、一般式（1)で示す紫外線吸収剤を 共重合してなるメタクリル系榭脂組成物であることが、さらに好まし 、。 [0042] [化 2]
Figure imgf000013_0001
[0043] (式中、 Xは Hまたはハロゲン、 Rは H、メチルまたは炭素数 4〜6の t—アルキル基、
1
Rは直鎖または枝分かれ鎖状の炭素数 2〜： LOのアルキレン基、 Rは Hまたはメチル
2 3
である。 )
本発明における一般式（1)で示す紫外線吸収剤は、 2- (2'—ヒドロキシ— 5 '—メ タクリロイルォキシェチルフエ-ル） 2H—ベンゾトリアゾール類であり、 2— (2'—ヒ ドロキシ— 5，—アタリロイルォキシェチルフエ-ル）—2H ベンゾトリァゾール、 2- ( 2'ーヒドロキシ 5 '—メタクリロイルォキシェチルフエニル） 2H べンゾトリァゾー ル、 2— (2'—ヒドロキシ一 5 '—メタクリロイルォキシェチルフエ-ル） 5 クロ口一 2 H ベンゾトリァゾール、 2- (2'—ヒドロキシ一 5 '—メタクリロイルォキシプロピルフエ -ル） 2H ベンゾトリァゾール、 2— (2，一ヒドロキシ一 5，一メタクリロイルォキシェ チル— 3，—t—ブチルフエ-ル）—2H ベンゾトリアゾール等が挙げられる。より好ま しくは、コストおよび取り扱い性から、 2- (2，一ヒドロキシ一 5，一メタクリロイルォキシ ェチルフエ-ル） 2H—ベンゾトリアゾールである。
[0044] 本発明における一般式（1)で示す紫外線吸収剤の共重合比率は、メタクリル系榭 脂組成物（C) 100重量部に対して、 0. 01〜30重量部が好ましぐ 0. 01〜25重量 部がより好ましぐ 0. 01〜20重量部がさらに好ましぐ 0. 05〜20重量部が特に好ま しい。一般式（1)で示す紫外線吸収剤の共重合比率が 0. 01重量部未満では、得ら れるメタクリル系榭脂組成物力 形成しうるフィルムの耐候性が低下する傾向にあり、 50重量部を超えると、フィルムの耐衝撃性および耐折曲げ割れ性が低下する傾向に ある。 [0045] 本発明における一般式（1)で示す紫外線吸収剤の共重合は、メタクリル系榭脂組 成物（C)の 、ずれの層にお 、て共重合されて 、ても構わな 、が、メタクリル酸エステ ル系共重合体 (A)ばかりではなぐアクリル酸エステル系架橋弾性体粒子 (B)に共 重合されて ヽることが好ましぐ紫外線吸収剤はメタクリル系榭脂組成物（C)全体に 均一に共重合されることがより好ましい。
[0046] 本発明におけるメタクリル系榭脂組成物 (C)の製造方法は特に限定されず、公知 の乳化重合法、乳化 懸濁重合法、懸濁重合法、塊状重合法または溶液重合法が 適用可能であるが、乳化重合法が特に好ましい。
[0047] 本発明における一般式（1)で示す紫外線吸収剤の共重合方法も特に限定されず、 メタクリル系榭脂組成物 (C)の製造中に共重合することが好ま 、。共重合方法とし ては、公知の乳化重合法、乳化 懸濁重合法、懸濁重合法、塊状重合法または溶 液重合法が適用可能であるが、乳化重合法が特に好ましい。
[0048] 本発明のアクリル酸エステル系架橋弾性体粒子 (B)の重合における開始剤として は、公知の有機系過酸ィ匕物、無機系過酸化物、ァゾィ匕合物などの開始剤を使用す ることができる。具体的には、例えば、 t プチルノヽイド口パーオキサイド、 1, 1, 3, 3 ーテトラメチルブチルノヽイド口パーオキサイド、スクシン酸パーオキサイド、パーォキシ マレイン酸 t ブチルエステル、クメンハイド口パーオキサイド、ベンゾィルパーォキサ イド等の有機過酸化物や、過硫酸カリウム、過硫酸ナトリウム等の無機過酸化物、さら にァゾビスイソプチ口-トリル等の油溶性開始剤も使用される。これらは単独で用いて もよぐ 2種以上併用してもよい。これらの開始剤は、亜硫酸ナトリウム、チォ硫酸ナト リウム、ナトリウムホルムアルデヒドスルフォキシレート、ァスコルビン酸、ヒドロキシァセ トン酸、硫酸第一鉄、硫酸第一鉄とエチレンジァミン四酢酸 2ナトリウムの錯体なとの 還元剤と組み合わせた通常のレドックス型開始剤として使用してもよい。
[0049] 前記有機系過酸化物は、重合系にそのまま添加する方法、単量体に混合して添加 する方法、乳化剤水溶液に分散させて添加する方法など、公知の添加法で添加する ことができるが、透明性の点から、単量体に混合して添加する方法あるいは乳化剤水 溶液に分散させて添加する方法が好まし 、。
[0050] また、前記有機系過酸化物は、重合安定性、粒子径制御の点から、 2価の鉄塩等 の無機系還元剤および Zまたはホルムアルデヒドスルホキシル酸ソーダ、還元糖、ァ スコルビン酸等の有機系還元剤と組み合わせたレドックス系開始剤として使用するの が好ましい。
[0051] 前記乳化重合に使用される界面活性剤にも特に限定はなぐ通常の乳化重合用の 界面活性剤であれば使用することができる。具体的には、例えばアルキルスルフォン 酸ナトリウム、アルキルベンゼンスルフォン酸ナトリウム、ジォクチルスルフォコハク酸 ナトリウム、ラウリル硫酸ナトリウム、脂肪酸ナトリウム等の陰イオン性界面活性剤や、 アルキルフエノール類、脂肪族アルコール類とプロピレンオキサイド、エチレンォキサ イドとの反応生成物等の非イオン性界面活性剤等が示される。これらの界面活性剤 は単独で用いてもよぐ 2種以上併用してもよい。更に要すれば、アルキルアミン塩等 の陽イオン性界面活性剤を使用してもよ!、。
[0052] 得られたメタクリル系榭脂組成物（C)ラテックスは、通常の凝固、洗浄および乾燥の 操作により、または、スプレー乾燥、凍結乾燥などによる処理により、榭脂組成物が分 離、回収される。
[0053] 本発明のフッ化ビ-リデン系榭脂組成物 (フッ化ビ-リデン系榭脂 (D)または、フッ 化ビ-リデン系榭脂 (D)およびメタクリル系榭脂組成物 (C) )には、着色のために無 機系顔料または有機系染料を、熱や光に対する安定性を更に向上させるために抗 酸化剤、熱安定剤、紫外線吸収剤、紫外線安定剤などを、あるいは、抗菌、脱臭剤、 滑剤等を、単独または 2種以上組み合わせて添加してもよ ヽ。
[0054] 本発明のフッ化ビ-リデン系榭脂組成物 (フッ化ビ-リデン系榭脂 (D)または、フッ 化ビ-リデン系榭脂（D)およびメタクリル系榭脂組成物（C) )には、必要に応じて、ポ リグルタルイミド、無水ダルタル酸ポリマー、ラタトン環化メタクリル系榭脂、メタクリル系 榭脂、ポリエチレンテレフタレート榭脂、ポリブチレンテレフタレート榭脂等を配合する ことも可能である。ブレンドの方法は特に限定されず、公知の方法を用いることができ る。
[0055] 本発明のフッ化ビニリデン系榭脂フィルムの厚みは、 1〜300 μ mが好ましぐ 5〜2 00 μ mがより好ましい。フィルムの厚みが 1 μ m未満ではフィルムの加工性が低下す る傾向があり、 300 /z mを超えると、得られるフィルムの透明性が低下する傾向がある [0056] 本発明のフッ化ビ-リデン系榭脂フィルムは、 目的に応じて、フィルムの積層成形 や、二軸延伸によるフィルムの改質も可能である。
[0057] 本発明のフッ化ビニリデン系榭脂フィルムは、フッ化ビニリデン系榭脂 (フッ化ビニリ デン系榭脂 (D)または、フッ化ビ-リデン系榭脂 (D)およびメタクリル系榭脂組成物 力もなる組成物）力も形成されてなるフィルムであってもよ 、が、耐候性 (特に紫外線 防御能）、コスト、成形性および積層対象物との接着性の点から、表面層を形成する 上記フッ化ビ-リデン系榭脂層と、メタクリル系榭脂組成物 (C)層とからなるフッ化ビ -リデン系榭脂多層フィルムが好まし 、。
[0058] 本発明における表面層を形成する上記フッ化ビニリデン系榭脂層と、メタクリル系榭 脂組成物 (C)層とからなるフッ化ビ-リデン系榭脂多層フィルムの製造方法としては 、特に限定されないが、通常の積層方法を適用することができる。積層方法の具体例 としては、例えば、（i)上記フッ化ビ-リデン系榭脂フィルムと、別途溶融押出等により 製造されたメタクリル系榭脂組成物 (C)フィルムとを、接着剤を用いて貼り合わせる方 法、両フィルムの積層面を加熱した後に圧着させる方法、等、（ii)フッ化ビ-リデン系 榭脂層とメタクリル系榭脂組成物 (C)層とを共押出する方法、等があげられる。
[0059] これらの中でも、上記フッ化ビ-リデン系榭脂組成物とメタクリル系榭脂組成物（C) との共押出法が、フッ化ビ-リデン系榭脂層とメタクリル系榭脂組成物 (C)層との接 着性確保、多層フィルム製造時のフィルムへの熱履歴制御の容易さの点から、好まし い。
[0060] 本発明にお 、て、フッ化ビ -リデン系榭脂およびメタクリル系榭脂組成物（C)力もな るフッ化ビ-リデン系榭脂多層フィルムの場合、フッ化ビ-リデン系榭脂層の厚みは 1 〜50 μ m、メタクリル系榭脂組成物（C)層の厚みは 20〜200 μ mが好ましい。フッ 化ビ-リデン系榭脂層の厚みが 1 μ m未満では、充分な耐候性が得られない傾向が あり、 50 mを超えるとコスト的に不利になる傾向がある。メタクリル系榭脂組成物（C )層の厚みが 20 m未満では、フィルム卷取り時にシヮが入り易くなる傾向があり、 2 00 μ mを超えると 2次カ卩ェ性がし難くなる傾向がある。
[0061] 本発明のフッ化ビ-リデン系榭脂多層フィルムにおいても、ポリフッ化ビ-リデンの 平均球晶直径が、 1. 0 m未満であり、好ましくは 0. 6 m未満であり、より好ましく は検出限界である 0.： m未満である。ポリフッ化ビ-リデンの平均球晶直径が 1. 0 μ m以上では、得られるフッ化ビ-リデン系榭脂多層フィルムの透明性が満足できな い傾向がある。
[0062] 本発明のフッ化ビ-リデン系榭脂多層フィルムにおいても、曇価は 1%以下であり、 好ましくは 0. 9%以下、さらに好ましくは 0. 8%以下である。ポリフッ化ビ-リデン榭 脂多層フィルムの曇価が 1%を超えると、得られるフッ化ビ-リデン系榭脂多層フィル ムの透明性が満足できない傾向がある。
[0063] 本発明のフッ化ビニリデン系榭脂組成物より得られたフッ化ビニリデン系榭脂フィル ムまたはフッ化ビ-リデン系榭脂多層フィルムは、必要に応じて、公知の方法によりフ イルム表面の光沢を低減させることができる。例えば、メタクリル系榭脂組成物（C)に 無機充填剤または架橋性高分子粒子を混練する方法等で実施することが可能であ る。また、得られるフィルムをエンボスカ卩ェにより、フィルム表面の光沢を低減させるこ とも可能である。
[0064] 本発明のフッ化ビ-リデン系榭脂フィルムまたは多層フィルムは、金属、プラスチッ クなどに積層して用いることができる。フィルムの積層方法としては、積層成形や、鋼 板などの金属板に接着剤を塗布した後、金属板にフィルムを載せて乾燥させ貼り合 わせるウエットラミネートや、ドライラミネート、ェクストル一ジョン (押出）ラミネート、ホッ トメルトラミネートなどがあげられる。
[0065] プラスチック部品にフィルムを積層する方法としては、フィルムを金型内に配置して おき、射出成形にて榭脂を充填するインサート成形またはラミネートインジェクション プレス成形や、フィルムを予備成形した後に金型内に配置し、射出成形にて榭脂を 充填するインモールド成形などがあげられる。
[0066] 本発明のメタクリル系榭脂組成物カゝら得られるフィルム積層品は、自動車内装材， 自動車外装材などの塗装代替用途、窓枠、浴室設備、壁紙、床材などの建材用部 材、 日用雑貨品、家具や電気機器のハウジング、ファクシミリなどの OA機器のハウジ ング、電気または電子装置の部品などに使用することができる。また、成形品としては 、照明用レンズ、自動車ヘッドライト、光学レンズ、光ファイノく、光ディスク、液晶用導 光板、液晶用フィルム、滅菌処理の必要な医療用品、電子レンジ調理容器、家電製 品のハウジング、玩具またはレクリェーション品目などに使用することができる。
実施例
[0067] 次に、本発明を実施例に基づき、さらに詳細に説明するが、本発明はこれらの実施 例のみに限定されるものではない。
[0068] なお、以下の実施例および比較例で測定した物性の各測定方法は、次のとおりで ある。
[0069] (電子顕微鏡観察による結晶性の評価）
得られたフィルムに対し、凍結超薄切片法により試料調整した後、透過型電子顕微 鏡（日本電子（株）製、 JEM— 1200EX)を用いて、カロ速電圧 80kVにて、 10000倍 で観察した際のポリフッ化ビ-リデンの結晶直径を測定したく検出限界は、 0. l ^ m >。結晶直径は、電子顕微鏡観察写真中の球晶 10個に関して、ノギスを用い、該直 径を測定し、その平均値を平均球晶直径とした。
[0070] (レーザー小角散乱法による結晶性の評価）
得られたフィルムをクロ口ホルムに浸漬し、ベース榭脂層を溶解して得たポリフツイ匕 ビ-リデンフィルムを 45度ずつずらして 8枚重ねあわせて測定試料を作成した後、レ 一ザ一光源として He— Neガスレーザー（ネオアーク（株）、 NEO— 15MS； 15mV、 632. 8nm)および PDA検出器 (浜松ホトニタス (株)製、フォトダイオードアレイ S649 4— 128)を用いて、小角光散乱測定を行った。散乱強度極大値の散乱ベクトル Q max
(nm 1)をカーブフィッティングから求め、次式より平均球晶半径 Rを算出した。
0
R (平均球晶半径） =4. 09/Q
0 max
(重合転化率の評価）
得られたメタクリル系榭脂組成物（C)ラテックスを、熱風乾燥機内にて 120°Cにて 1 時間乾燥して固形成分量を求め、重合転化率 (％) = 100 X固形成分量 Z仕込み 単量体の式により、重合転ィ匕率 (％)を算出した。
[0071] (透明性の評価）
得られたフィルムの透明性は、 JIS K6714に準じて、温度 23°C± 2°C、湿度 50% ± 5%の条件下にて、曇価 (ヘイズ)を測定した。 [0072] (耐薬品性の評価）
フィルム上にキシレンを一滴垂らし、フィルムの変化を目視で評価した。
〇：変化が認められない。
X：滴下跡が認められる。
[0073] (耐折曲げ割れ性の評価）
得られたフィルムを 1回 180度折り曲げて、折り曲げ部の変化を目視で評価した。 〇：割れが認められない
X：割れが認められる。
[0074] (成形性の評価）
フィルム成形を 3時間連続して行い、その運転状況を観察し、以下の基準により評 価をした。
〇：フィルムの厚みが均一で、切れずに成形できる。
X：フィルムの厚みが不均一またはフィルム切れが発生する。
(紫外線吸収剤のブリード性の評価）
フィルム成形を 3時間連続して行い、冷却ロールへの付着状況を観察し、以下の基 準により評価をした。
〇：冷却ロールへの付着が認められな!/、。
X：冷却ロールへの付着が認められる。
[0075] また、製造例、実施例および比較例中の「部」は重量部、「％」は重量％を表す。ま た、略号はそれぞれ下記の物質を表す。
PVDF- 1： SOLEF1010 (SOLVAY社製、 PVDFホモポリマー）
PVDF- 2： SOLEF1008 (SOLVAY社製、 PVDFホモポリマー）
PVDF- 3： SOLEF11010 (SOLVAY社製、 PVDFコーポリマー）
BA:アクリル酸ブチル
MMA：メタクリル酸メチル
CHP：クメンハイド口パーオキサイド
A1MA：メタクリル酸ァリル RUVA: 2- (2'—ヒドロキシ一 5'—メタクリロイルォキシェチルフエニル） 2— H— ベンゾトリアゾール（大塚化学 (株）製、 RUVA— 93)
(製造例 1)メタクリル系榭脂組成物の製造
攪拌機付き 8L重合装置に、以下の物質を仕込んだ。
脱イオン水 200部
ジォクチルスルフォコハク酸ナトリウム 0. 25部
ソディウムホルムアルデヒドスルフォキシレート 0. 15部
エチレンジァミン四酢酸— 2—ナトリウム 0. 001部
硫酸第一鉄 0. 00025部
重合機内を窒素ガスで充分に置換し実質的に酸素のない状態とした後、内温を 60 °Cにし、表 1中（1)に示した単量体混合物（B) <すなわち、 BA90%および MMA1 0%からなる単量体混合物 100部に対し A1MA1部および CHP0. 2部からなる単量 体混合物 30部、および RUVA0. 6部〉を 10部 Z時間の割合で連続的に添加し、 添加終了後、さらに 0. 5時間重合を継続し、アクリル酸エステル系架橋弾性体粒子（ B)を得た。重合転化率は 99. 5%であった。
[0076] その後、ジォクチルスルフォコハク酸ナトリウム 0. 05部を仕込んだ後、内温を 60°C にし、表 1中（1)に示した単量体混合物（A) <すなわち、 BA10%および MMA90 %からなる単量体混合物 100部に対し tDMO. 5部および CHP0. 5部からなる単量 体混合物 70部、および RUVA1. 4部〉を 10部 Z時間の割合で連続的に添加し、さ らに 1時間重合を継続し、メタクリル系榭脂組成物（C)を得た。重合転化率は 98. 5 %であった。得られたラテックスを塩ィ匕カルシウムで塩析、凝固し、水洗、乾燥して榭 脂粉末 (1)を得た。さらに、 40ミリ φベント付き単軸押出機（田端機械工業 (株)製、 H V-40- 28)を用いてシリンダ温度を 240°Cに設定して溶融混練を行い、ペレツトイ匕 した。
[0077] [表 1] メタクリル系樹脂組成物 （C)
( 1 ) (2) (3 ) (4) (5) (6) (7 ) 初期ジォクチルスルフォ
(部） 0.25 0.25 0.25 0.25 0.25 0.25 0.25 コハク酸ナドゾゥム量
重量部 30 20 30 30 30 30 50
BA ( %) 90 90 90 90 90 10 90 アクリル酸
エステル系 MMA (%) 10 10 10 10 10 90 10 架橋弾性体 AIMA (部） 1 3 1 1 1 1 1 粒子 (B) CHP (部） 0.2 0.2 0.2 0.5 0.2 0.2 0.2
RUVA (部） 0.6 0.4 0 10.5 0.6 0.6 1 重量部 70 80 70 70 70 70 50
BA (%) 10 10 10 10 80 10 10 メタクリル酸 MMA (%) 90 90 90 90 20 90 90 エステル系
重合体 （ tDM
A) (部) 0.5 0.5 0.5 0.5 0.5 0.5 0.5
CHP (部） 0.5 0.5 0.5 1 0.5 0.5 0.5
RUVA (部） 1.4 1 .6 0 24.5 1 .4 1.4 1 重合転化率 (%) 98.5 98.7 98.6 凝集 98.9 98.5 98.4
[0078] (製造例 2〜7)
単量体混合物（B)または単量体混合物 (A)の単量体組成を表 1のように変更した 以外は、製造例 1と同様に重合を行い、凝固、水洗、乾燥して樹脂粉末 (2)〜（7)を 得、さらに溶融混練を行い、ペレツトイ匕した。ただし、製造例 (4)では重合中にラテツ タスが凝集したため、榭脂粉体 (4)が得られず、ペレツトイ匕およびフィルム化ができず 、フィルム物性を評価できな力つた。
[0079] また、製造例 (3)は、得られた榭脂粉末 (3)に紫外線吸収剤として構造式 (2)で示 されるチヌビン P (チバスペシャルケミカル社製）を 2部ブレンドして力 溶融混練を行 い、ペレット化した。
[0080] [化 3]
Figure imgf000021_0001
[0081] (製造例 8)
PVDF- 1 · 98部および製造例（1)で作製した榭脂粉末（1) 2部を、ヘンシェルミキ サ一でブレンドし、 40ミリ φベント付き単軸押出機（田端機械工業 (株)製、 HV— 40 - 28)を用いてシリンダ温度を 240°Cに設定して溶融混練を行 、、ペレツトイ匕した。
[0082] (製造例 9)
PVDF- 1 ·45部と製造例（1)で作製した榭脂粉末（1) 55部に変更した以外は、 製造例 10と同様にヘンシェルミキサーでブレンドし、 40ミリ φベント付き単軸押出機（ 田端機械工業 (株)製、 HV— 40— 28)を用いてシリンダ温度を 240°Cに設定して溶 融混練を行い、ペレツトイ匕した。
[0083] (製造例 10)
PVDF- 1 · 98部と製造例（2)で作製した榭脂粉末 (2) 2部に変更した以外は、製 造例 10と同様にヘンシェルミキサーでブレンドし、 40ミリ φベント付き単軸押出機（田 端機械工業 (株)製、 HV— 40— 28)を用いてシリンダ温度を 240°Cに設定して溶融 混練を行い、ペレツトイ匕した。
[0084] (製造例 11)
PVDF- 1 ·45部と製造例 (3)で作製した榭脂粉末 (3) 55部に、紫外線吸収剤とし て構造式（2)で示されるチヌビン Ρ (チバスペシャルケミカル社製）を 2部ブレンドして から、製造例 10と同様にヘンシェルミキサーでブレンドし、 40ミリ φベント付き単軸押 出機を用いてシリンダ温度を 240°Cに設定して溶融混練を行 、、ペレツトイ匕した。
[0085] (実施例 1〜8、比較例 1〜4)
製造例（1)で得られたメタクリル系榭脂組成物をベース榭脂とし、表 2に示す榭脂 組成を表面層榭脂として、 2種 2層 Tダイ (フィードブロック方式)付き押出機（60mm 押出機 2基)を用いて、ダイス温度 240°Cで成形し、表 2に示す温度条件に制御した 金属ロールに挟み込んで、厚み 60 m (ベース榭脂層 53 mおよび表層榭脂層 7 μ m)のフィルムを得た。
[0086] 得られたフィルムを用いた種々の特性を評価し、その結果を表 2に示した。
[0087] [表 2]
Figure imgf000023_0001
[0088] 実施例 1および比較例 1の透過型電子顕微鏡での観察写真（10000倍)を図 1およ び 2に示した。
[0089] なお、実施例 1および比較例 1に関しては、レーザー小角散乱法によるポリフッ化ビ 二リデンの平均結晶半径 Rを測定したが、実施例 1では散乱強度が弱く検出されず
0
、球晶の生成は認められな力つた力 比較例 1では R = 1. 48 m (平均球晶直径と
0
しては 2. 96 μ m)であった。
[0090] (実施例 9〜13)
製造例で得られた表 3に示すメタクリル系榭脂組成物をベース榭脂とし、 PVDF- 1を表面層榭脂として、 2種 2層 Tダイ (フィードブロック方式)付き押出機（60mm押出 機 2基)を用いて、ダイス温度 240°Cで成形し、表 3に示す温度条件のロールに挟み 込んで、厚み 60 m (ベース榭脂層 53 mおよび表層榭脂層 7 m)のフィルムを 得た。
[0091] 得られたフィルムを用いた種々の特性を評価し、その結果を表 3に示した。
[0092] [表 3]
実施例 比較例
1 9 10 11 12 13 1
PVDF-1 PVDF-1 PVDF-1 PVDF-1 PVDF-1 PVDF-1 PVDF-1 表面層樹脂 フッ化ビニリデン系樹脂（D)
100部 100部 100部 100部 100部 100部 100部
(1) (2) (3) (5) (6) (7) (1) ベ一ス樹脂 メタクリル系樹脂組成物（C)
100部 100部 100部 100部 100部 100部 100部
〔〕¾£Je0093ゝ^n〜
両面 両面 両 网面 ί^ιέι ]¾]面
挟み込み口- -ル 未使用 使用 使用 使用 使用 使用 使用
表層樹脂側温度 (°c) 30 30 30 30 30 30
ベ一ス樹脂側温度 (°c) 30 30 30 30 30 30 ― 平均 透過型電子顕微鏡 10000倍で <0.1 <0.1 <0.1 <0.1 <0.1 ぐ 0.1 3.0 球晶直径 観察く検出限界 :0. 1 m>
透明性（％) 0.7 0.7 0.7 0.7 0.7 0.7 5.5 耐薬品性 〇 O o 〇 ο 〇 〇 フィルム
耐折リ曲げ割れ性 〇 X 〇 〇 特性 O 〇 〇
成形性 o O 〇 X Ο X 〇 ブリ一ド性 O O X 〇 Ο 〇 〇
*) 製造例（ は、乳化重合時にラテックスが凝集した為、樹脂粉体 が得られず、フィルムを作製することができなかった。
Figure imgf000025_0001

Claims

請求の範囲
[1] ポリフッ化ビ-リデンの平均球晶直径が 1. 0 m未満である、フッ化ビ -リデン系榭 脂フィルム。
[2] 曇価が 1%未満である、請求項 1記載のフッ化ビ-リデン系榭脂フィルム。
[3] ロールまたは金属ベルトに挟み込んで成形されてなる、請求項 1または 2に記載の フッ化ビニリデン系榭脂フィルム。
[4] フッ化ビ -リデン系榭脂が、フッ化ビ-リデン系榭脂（D) 50〜99. 9重量部およびメ タクリル系榭脂組成物（C) O. 1〜50重量部力もなる組成物である、請求項 1〜3のい ずれかに記載のフッ化ビ-リデン系榭脂フィルム。
[5] 表面層を形成する請求項 1〜4のいずれかに記載のフッ化ビニリデン榭脂層と、メタ クリル系榭脂組成物（C)層とからなる、フッ化ビ-リデン系榭脂多層フィルム。
[6] フッ化ビ-リデン榭脂層とメタクリル系榭脂組成物 (C)とが共押出成形されてなる、 請求項 5に記載フッ化ビ-リデン系榭脂多層フィルム。
[7] メタクリル系榭脂組成物 (C)が、
メタクリル酸エステル系重合体 (A)をアクリル酸エステル系架橋弾性体粒子 (B)の存 在下において重合することにより得られるメタクリル系榭脂組成物であって、
(1)メタクリル酸エステル系重合体 (A)力 メタクリル酸アルキルエステル 50〜 100重 量％、およびアクリル酸アルキルエステル 0〜50重量％を含む単量体混合物を重合 すること〖こより得られ、
(2)アクリル酸エステル系架橋弾性体粒子（B) ί アクリル酸アルキルエステル 50〜 100重量％ぉよびメタクリル酸アルキルエステル 50〜0重量％を含む単量体混合物 (b)および、 1分子あたり 2個以上の非共役二重結合を有する多官能性単量体を共 重合することにより得られ、
(3)アクリル酸エステル系架橋弾性体粒子 (B)の含有量が 5〜45重量％であり、 かつ、
(4)メタクリル系榭脂組成物（C) 100重量部に対して、一般式（1)で示す紫外線吸収 剤 0. 01〜30重量部を共重合してなることを特徴とするメタクリル系榭脂組成物であ る、 請求項 4記載のフッ化ビ-リデン系榭脂フィルムまたは請求項 5または 6記載のフッ化 ビ-リデン系榭脂多層フィルム。
[化 1]
Figure imgf000027_0001
(式中、 Xは Hまたはハロゲン、 Rは H、メチルまたは炭素数 4〜6の t—アルキル基、
1
Rは直鎖または枝分かれ鎖状の炭素数 2〜： LOのアルキレン基、 Rは Hまたはメチル
2 3
である。 )
[8] 請求項 1〜7の 、ずれかに記載のフッ化ビ-リデン系榭脂フィルムまたはフッ化ビ- リデン系榭脂多層フィルムを積層した、積層品。
[9] 射出成形により製造されてなる、請求項 8記載の積層品。
PCT/JP2005/014684 2004-08-11 2005-08-10 フッ化ビニリデン系樹脂フィルム WO2006016618A1 (ja)