US20090196812A1 - Catalysts, Systems and Methods Utilizing Non-Zeolitic Metal-Containing Molecular Sieves Having the CHA Crystal Structure - Google Patents

Catalysts, Systems and Methods Utilizing Non-Zeolitic Metal-Containing Molecular Sieves Having the CHA Crystal Structure Download PDF

Info

Publication number
US20090196812A1
US20090196812A1 US12/361,980 US36198009A US2009196812A1 US 20090196812 A1 US20090196812 A1 US 20090196812A1 US 36198009 A US36198009 A US 36198009A US 2009196812 A1 US2009196812 A1 US 2009196812A1
Authority
US
United States
Prior art keywords
catalyst
sapo
nox
ppm
mixture
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US12/361,980
Other languages
English (en)
Inventor
Ivor Bull
Gerald S. Koermer
Ahmad Moini
Signe Unverricht
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BASF Corp
Original Assignee
BASF Catalysts LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BASF Catalysts LLC filed Critical BASF Catalysts LLC
Priority to US12/361,980 priority Critical patent/US20090196812A1/en
Priority to PCT/US2009/032610 priority patent/WO2009099937A1/en
Priority to JP2010545198A priority patent/JP2011510899A/ja
Priority to CN2009801121392A priority patent/CN101983103A/zh
Priority to ARP090100315A priority patent/AR071555A1/es
Priority to BRPI0906992-5A priority patent/BRPI0906992B1/pt
Assigned to BASF CATALYSTS LLC reassignment BASF CATALYSTS LLC ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: BULL, IVOR
Publication of US20090196812A1 publication Critical patent/US20090196812A1/en
Priority to US13/214,391 priority patent/US10105649B2/en
Priority to US13/214,445 priority patent/US8617474B2/en
Priority to JP2014043814A priority patent/JP2014139440A/ja
Assigned to BASF CORPORATION reassignment BASF CORPORATION CHANGE OF NAME (SEE DOCUMENT FOR DETAILS). Assignors: BASF CATALYSTS LLC
Priority to US16/129,053 priority patent/US20190015783A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
    • B01D53/34—Chemical or biological purification of waste gases
    • B01D53/92—Chemical or biological purification of waste gases of engine exhaust gases
    • B01D53/94—Chemical or biological purification of waste gases of engine exhaust gases by catalytic processes
    • B01D53/9404—Removing only nitrogen compounds
    • B01D53/9409—Nitrogen oxides
    • B01D53/9413—Processes characterised by a specific catalyst
    • B01D53/9418—Processes characterised by a specific catalyst for removing nitrogen oxides by selective catalytic reduction [SCR] using a reducing agent in a lean exhaust gas
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
    • B01D53/34—Chemical or biological purification of waste gases
    • B01D53/92—Chemical or biological purification of waste gases of engine exhaust gases
    • B01D53/94—Chemical or biological purification of waste gases of engine exhaust gases by catalytic processes
    • B01D53/9445—Simultaneously removing carbon monoxide, hydrocarbons or nitrogen oxides making use of three-way catalysts [TWC] or four-way-catalysts [FWC]
    • B01D53/945—Simultaneously removing carbon monoxide, hydrocarbons or nitrogen oxides making use of three-way catalysts [TWC] or four-way-catalysts [FWC] characterised by a specific catalyst
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
    • B01D53/34—Chemical or biological purification of waste gases
    • B01D53/92—Chemical or biological purification of waste gases of engine exhaust gases
    • B01D53/94—Chemical or biological purification of waste gases of engine exhaust gases by catalytic processes
    • B01D53/9459—Removing one or more of nitrogen oxides, carbon monoxide, or hydrocarbons by multiple successive catalytic functions; systems with more than one different function, e.g. zone coated catalysts
    • B01D53/9477—Removing one or more of nitrogen oxides, carbon monoxide, or hydrocarbons by multiple successive catalytic functions; systems with more than one different function, e.g. zone coated catalysts with catalysts positioned on separate bricks, e.g. exhaust systems
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J29/00—Catalysts comprising molecular sieves
    • B01J29/82—Phosphates
    • B01J29/84—Aluminophosphates containing other elements, e.g. metals, boron
    • B01J29/85—Silicoaluminophosphates [SAPO compounds]
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/50—Catalysts, in general, characterised by their form or physical properties characterised by their shape or configuration
    • B01J35/56—Foraminous structures having flow-through passages or channels, e.g. grids or three-dimensional monoliths
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
    • B01J35/61—Surface area
    • B01J35/615—100-500 m2/g
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
    • B01J35/61—Surface area
    • B01J35/617—500-1000 m2/g
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
    • B01J37/02—Impregnation, coating or precipitation
    • B01J37/024—Multiple impregnation or coating
    • B01J37/0246—Coatings comprising a zeolite
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
    • F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
    • F01N3/00—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust
    • F01N3/08—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous
    • F01N3/10—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust
    • F01N3/18—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust characterised by methods of operation; Control
    • F01N3/20—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust characterised by methods of operation; Control specially adapted for catalytic conversion ; Methods of operation or control of catalytic converters
    • F01N3/2066—Selective catalytic reduction [SCR]
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2251/00—Reactants
    • B01D2251/20—Reductants
    • B01D2251/206—Ammonium compounds
    • B01D2251/2062—Ammonia
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2251/00—Reactants
    • B01D2251/20—Reductants
    • B01D2251/206—Ammonium compounds
    • B01D2251/2067—Urea
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2255/00—Catalysts
    • B01D2255/10—Noble metals or compounds thereof
    • B01D2255/102—Platinum group metals
    • B01D2255/1021—Platinum
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2255/00—Catalysts
    • B01D2255/20—Metals or compounds thereof
    • B01D2255/207—Transition metals
    • B01D2255/20715—Zirconium
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2255/00—Catalysts
    • B01D2255/20—Metals or compounds thereof
    • B01D2255/207—Transition metals
    • B01D2255/20738—Iron
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2255/00—Catalysts
    • B01D2255/20—Metals or compounds thereof
    • B01D2255/207—Transition metals
    • B01D2255/20761—Copper
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2255/00—Catalysts
    • B01D2255/50—Zeolites
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2255/00—Catalysts
    • B01D2255/50—Zeolites
    • B01D2255/502—Beta zeolites
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2255/00—Catalysts
    • B01D2255/50—Zeolites
    • B01D2255/504—ZSM 5 zeolites
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2255/00—Catalysts
    • B01D2255/90—Physical characteristics of catalysts
    • B01D2255/915—Catalyst supported on particulate filters
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2255/00—Catalysts
    • B01D2255/90—Physical characteristics of catalysts
    • B01D2255/92—Dimensions
    • B01D2255/9207—Specific surface
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J2229/00—Aspects of molecular sieve catalysts not covered by B01J29/00
    • B01J2229/10—After treatment, characterised by the effect to be obtained
    • B01J2229/18—After treatment, characterised by the effect to be obtained to introduce other elements into or onto the molecular sieve itself
    • B01J2229/186—After treatment, characterised by the effect to be obtained to introduce other elements into or onto the molecular sieve itself not in framework positions
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J29/00—Catalysts comprising molecular sieves
    • B01J29/005—Mixtures of molecular sieves comprising at least one molecular sieve which is not an aluminosilicate zeolite, e.g. from groups B01J29/03 - B01J29/049 or B01J29/82 - B01J29/89
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
    • F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
    • F01N2610/00—Adding substances to exhaust gases
    • F01N2610/02—Adding substances to exhaust gases the substance being ammonia or urea
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
    • F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
    • F01N2610/00—Adding substances to exhaust gases
    • F01N2610/08—Adding substances to exhaust gases with prior mixing of the substances with a gas, e.g. air
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02C—CAPTURE, STORAGE, SEQUESTRATION OR DISPOSAL OF GREENHOUSE GASES [GHG]
    • Y02C20/00—Capture or disposal of greenhouse gases
    • Y02C20/10—Capture or disposal of greenhouse gases of nitrous oxide (N2O)
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02T—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO TRANSPORTATION
    • Y02T10/00—Road transport of goods or passengers
    • Y02T10/10—Internal combustion engine [ICE] based vehicles
    • Y02T10/12—Improving ICE efficiencies

Definitions

  • Embodiments of the invention relate to catalysts comprising non-zeolitic metal containing molecular sieves that have the CHA framework or crystal structure, methods for their manufacture and use, and exhaust gas treatment systems containing such catalysts.
  • Three Way Catalysts are designed to remove NOx from the exhaust of vehicles equipped with a gasoline engine.
  • the nitrogen oxides react with the unburned hydrocarbons or CO in such a way that the oxygen of NOx is consumed for the oxidation of the unburned hydrocarbons or CO yielding nitrogen, carbon dioxide and water.
  • Three-way catalysts cannot be used for the treatment of exhaust from lean burn and diesel engines because of the low NOx conversion in the presence of oxygen.
  • NOx storage and reduction which requires alternating lean and rich operating periods of the engine.
  • the nitrogen oxides will be adsorbed in the form of nitrates.
  • the nitrates are reduced to nitrogen by reaction with the hydrocarbons contained in the exhaust.
  • a second type of technology for the reduction of NOx in diesel engines involves Selective Catalytic Reduction (SCR) of NOx.
  • SCR Selective Catalytic Reduction
  • a first type of SCR involves hydrocarbon SCR (HC SCR), which involves the use of a hydrocarbon such as diesel fuel as a reducing agent to reduce NOx in the diesel engine exhaust gas stream.
  • HC SCR hydrocarbon SCR
  • the applicability of HC SCR for diesel engines does not appear to be viable because most of catalysts suitable for HC-SCR show a very narrow temperature window where a useful NOx reduction can be obtained. See, for example, Ishihara et. al., Ind. Eng. Chem. Res ., Vol. 36, No. 1, 1997, in which conversion of NOx using Cu-SAPO-34 and hydrocarbons was observed to be less than 70% at about 400° C. and less than about 20% at 200° C.
  • a second type of SCR involves ammonia SCR.
  • Selective Catalytic Reduction using ammonia or ammonia precursor as reducing agent is believed to be the most viable technique for the removal of nitrogen oxides from the exhaust of diesel vehicles.
  • the nitrogen oxides are mainly composed of NO (>90%), so the SCR catalyst favors the conversion of NO and NH 3 into nitrogen and water.
  • Two major challenges in developing catalysts for the automotive application of the ammonia SCR process are to provide a wide operating window for SCR activity, including low temperatures of from 200° C. and higher and improvement of the catalyst's hydrothermal stability for temperatures above 500° C.
  • hydrothermal stability refers to retention of a material's capability to catalyze the SCR of NOx, with a preference for the retention to be at least 85% of the material's NOx conversion ability prior to hydrothermal aging.
  • the emissions from vehicles are measured using standardized engine or vehicle test cycles, in which speed and load are varied to simulate actual driving conditions.
  • the ECE test cycle which is also referred to as UDC, represents urban driving under low speed and load, and the Extra Urban Driving Cycle (EUDC) involves higher speeds.
  • Most test cycles include a cold-start portion.
  • the Euro 3 test cycle includes the ECE+EUDC cycles, and includes evaluation of emissions when the catalyst at temperatures as low as 150° C. for a significant portion of the drive cycle. Thus, low temperature NOx conversion is of great interest.
  • Zeolites are aluminosilicate crystalline materials having rather uniform pore sizes which, depending upon the type of zeolite and the type and amount of cations included in the zeolite lattice, typically range from about 3 to 10 Angstroms in diameter. Both synthetic and natural zeolites and their use in promoting certain reactions, including the selective reduction of nitrogen oxides with ammonia in the presence of oxygen, are well known in the art.
  • Metal-promoted zeolite catalysts including, among others, iron-promoted and copper-promoted zeolite catalysts, where, for instance, the metal is introduced via ion-exchange, for the selective catalytic reduction of nitrogen oxides with ammonia are known.
  • Iron-promoted zeolite beta has been an effective catalyst for the selective reduction of nitrogen oxides with ammonia.
  • hydrothermal conditions such as reduction of NOx from gas exhaust at temperatures exceeding 500° C.
  • the activity of many metal-promoted zeolites, such as Cu and Fe versions of ZSM-5 and Beta begins to decline. This decline in activity is believed to be due to destabilization of the zeolite such as by dealumination and consequent loss of metal-containing catalytic sites within the zeolite.
  • aspects of the invention are directed to a metal-loaded non-zeolitic molecular sieve having the CHA structure and effective to selectively reduce nitrogen oxides with ammonia in the presence of oxygen, methods for the manufacture of such catalysts, catalyst composites comprising such molecular sieves, and exhaust gas treatment systems and methods incorporating such catalysts.
  • the catalyst may be part of an exhaust gas treatment system used to treat exhaust gas streams, especially those emanating from gasoline or diesel engines.
  • One embodiment of the present invention pertains to metal-loaded non-zeolitic molecular sieves having the CHA structure and their application in exhaust gas systems such as those designed to reduce nitrogen oxides.
  • novel metal-loaded non-zeolitic molecular sieve catalysts having the CHA structure are provided which exhibit improved NH 3 SCR of NOx.
  • the non-zeolitic molecular sieve catalysts made in accordance with one or more embodiments of the present invention provide a catalyst material which exhibits excellent hydrothermal stability and high catalytic ability over a wide temperature range.
  • non-zeolitic molecular sieve catalysts materials according to embodiments of the present invention offer improved low temperature activity and hydrothermal stability.
  • a comprises a Cu-loaded non-zeolitic molecular sieve having the CHA crystal structure having a Cu loading so that the catalyst is effective to selectively reduce nitrogen oxides with ammonia in the presence of oxygen in an exhaust gas stream at 200° C. when the catalyst has been deposited on a honeycomb substrate having a cell density of 400 cpsi at a loading between 2 and 2.5 g/in 3 and tested at a space velocity of 80,000 hr ⁇ 1 where the feed stream comprises a mixture of 10% O 2 , 5% H 2 O, 500 ppm NO and 500 ppm NH 3 to provide at least 80% NOx conversion.
  • the first embodiment is directed to a catalyst exhibiting excellent NOx conversion at 200° C., and it is not limited by a particular loading.
  • the recitation of “when the catalyst has been deposited on a honeycomb substrate having a cell density of 400 cpsi at a loading between 2 and 2.5 g/in 3 and tested at a space velocity of 80,000 hr ⁇ 1 where the feed stream comprises a mixture of 10% O 2 , 5% H 2 O, 500 ppm NO and 500 ppm NH 3 ” in the claims is provided as testing parameters to provide clarity when a non-zeolitic molecular sieve having the CHA crystal structure has a copper loading that results in at least 80% conversion at 200° C.
  • the non-zeolitic molecular sieve comprises Cu-SAPO-34 and the catalyst is effective to provide at least about 85% NOx conversion in the exhaust gas stream at 200° C. In a third embodiment, the catalyst is effective to provide at least about 90% NOx conversion in the exhaust gas stream at 200° C.
  • the Cu-SAPO-34 material upon hydrothermal aging in 10% steam at 850° C. and 6 hours, retains at least 85% on a percentage basis of the NOx conversion at 200° C.
  • the Cu-SAPO-34 material upon hydrothermal aging in 10% steam at 900° C. and 1 hour, retains at least 90% of the NOx conversion on a percentage basis at 200° C.
  • the Cu-SAPO-34 material upon hydrothermal aging in 10% steam at 900° C. and 1 hour, retains at least 95% of the NOx conversion on a percentage basis at 200° C.
  • the catalyst is effective to reduce NOx so that that ratio of NOx to N 2 O in the gas stream after passing through the catalyst is greater than 2.5. In an eighth embodiment, the catalyst is effective to reduce NOx so that that ratio of NOx to N 2 O in the gas stream after passing through the catalyst is greater than 5.
  • the catalyst is effective to make less than 10 ppm N 2 O over the temperature range of 200° C. to 450° C. In a tenth embodiment, the catalyst is effective to make less than 5 ppm N 2 O over the temperature range of 200° C. to 450° C.
  • the catalyst contains a secondary metal; b) the secondary metal comprises zirconium; the catalyst contains in the range of about 2 weight percent and 4 weight percent Cu.
  • a process for manufacturing Cu-SAPO-34 comprises mixing a neutral, nitrogen-containing organic template, an alumina source, a silica source and a phosphorous source in a gel mixture; heating the gel to less than about 200° C. for at least about 12 hours to form crystalline SAPO-34; filtering and washing the crystalline SAPO-34; calcining the crystalline SAPO-34; and ion exchanging the crystalline SAPO-34 with a copper salt to provide Cu-SAPO-34.
  • the eleventh embodiment may include one or more of the following process variants: the template comprises morpholine and the heating temperature is less than about 185° C. and the heating time is at least about 24 hours; the copper salt comprises copper acetate; after ion exchanging the crystalline SAPO-34 with a copper salt to provide Cu-SAPO-34, Cu-SAPO-34 is washed to provide a filtrate having a conductivity less than about 600 ⁇ Scm ⁇ 1 , or less than about 400 ⁇ Scm ⁇ 1 , or less than about 200 ⁇ Scm ⁇ 1; calcining the washed Cu-SAPO-34 material at a temperature less than about 600° C.; and/or the crystalline material has a crystal size having 90% of the crystals less than 20 microns, or less than 15 microns
  • a catalyst is provided made by the process for manufacturing described in the eleventh embodiment and the variants described above.
  • a catalyst composite including a catalyst of any of embodiments 1-11 above.
  • a catalyst composite comprises a honeycomb substrate having a catalyst of any of embodiments 1-10 and 12 deposited on a honeycomb substrate as a washcoat at a loading in the range of about 0.5 g/in 3 and 3.5 g/in 3 .
  • the honeycomb can be a wall flow substrate or a flow through substrate.
  • the honeycomb substrate is a flow through substrate
  • at least a portion of the flow through substrate is coated with a washcoat containing Pt and a metal-loaded non-zeolitic molecular sieve to oxidize ammonia in the exhaust gas stream.
  • at least a portion of a wall flow substrate is coated with a washcoat containing Pt and a metal-loaded non-zeolitic molecular sieve to oxidize ammonia in the exhaust gas stream.
  • an exhaust gas treatment system includes a catalyst of embodiments 1-10, or 12-16 and a second catalyst such as an oxidation catalyst.
  • the catalyst of any of claims 1 - 10 is combined with a metal containing zeolitic SCR catalyst.
  • Another aspect of the invention pertains to process for the reduction of oxides of nitrogen contained in a gas stream in the presence of oxygen comprising contacting the gas stream with a Cu-loaded non-zeolitic molecular sieve as described in any of the previously described embodiments 1-10 or 12-17.
  • FIGS. 1A , 1 B, and 1 C are schematic depictions of three exemplary embodiments of the emissions treatment system of the invention.
  • FIG. 2 is a graph depicting nitrogen oxides removal efficiency (%), and N 2 O generated (ppm) as a function of reaction temperatures for a Cu-SAPO34 catalyst containing 3.31 wt % CuO prepared according to the methods of Example 1;
  • FIG. 3 is a graph depicting nitrogen oxides removal efficiency (%), and N 2 O generated (ppm) as a function of reaction temperatures for aged versions of the Cu-SAPO34 catalyst containing 3.31 wt % CuO prepared according to the methods of Example 1;
  • FIG. 4 is a graph depicting nitrogen oxides removal efficiency (%), ammonia consumption (%) and N 2 O generated (ppm) as a function of reaction temperature for a Cu-SAPO34 catalyst containing 3.18 wt % CuO prepared according to the methods of Example 2;
  • FIG. 5 is a graph depicting nitrogen oxides removal efficiency (%) and N 2 O generated (ppm) as a function of aging temperature for a CuSAPO-44 catalyst containing 3.78 wt % CuO prepared according to the methods of Example 3;
  • FIG. 6 is a graph depicting nitrogen oxides removal efficiency (%) and N 2 O generated (ppm) as a function of aging temperature for a Cu-SAPO34 catalyst prepared according to the methods of Example 4;
  • FIG. 7 is a graph depicting nitrogen oxides removal efficiency (%) and N 2 O generated (ppm) as a function of aging temperature for a Cu-SAPO34 catalyst prepared according to the methods of Example 11;
  • FIG. 8 is a graph depicting nitrogen oxides removal efficiency (%) and N 2 O generated (ppm) as a function of aging temperature for a Cu-SAPO34 catalyst prepared according to the methods of Example 12;
  • FIG. 9 is a graph depicting nitrogen oxides removal efficiency (%) and N 2 O generated (ppm) as a function of aging temperature for a Cu-SAPO34 catalyst prepared according to the methods of Example 13;
  • FIG. 10 is a graph depicting nitrogen oxides removal efficiency (%) and N 2 O generated (ppm) as a function of aging temperature for a Cu-SAPO34 catalyst prepared according to the methods of Example 14.
  • metal-loaded, non-zeolitic molecular sieves having the CHA structure are provided.
  • non zeolitic molecular sieve refers to corner sharing tetrahedral frameworks where at least a portion of the tetrahedral sites are occupied by an element other than silicon or aluminum.
  • fresh refers to an as manufactured catalyst that has not been hydrothermally aged. Any non-aluminosilicate composition having the CHA framework structure (as defined by the International Zeolite Association) comprising at least one T element which is not Si or Al and exhibits improved NH 3 SCR or NOx can be utilized according to embodiments of the present invention.
  • Non-limiting examples of such molecular sieves include aluminophosphates and metal-aluminophosphates, wherein metal could include silicon, copper, zinc or other suitable metals.
  • Specific non-limiting examples include SAPO-34, SAPO-44, and SAPO-47.
  • Especially suitable materials are those which couple excellent hydrothermal stability indicated by minimal loss of activity upon aging with improved catalytic activity compared to Fe-beta zeolite catalyst materials.
  • Materials according to embodiments of the invention exhibit high catalytic NOx conversion performance and over a wide temperature range and low N 2 O make. More specifically, Cu-SAPO-34 materials exhibit high NOx conversion for fresh and aged samples under extreme temperature conditions and at high space velocities of 80,000 h ⁇ 1 .
  • the wide temperature range includes low temperature, for example, temperatures as low as 200° C.
  • Cu-SAPO-34 materials are provided that exhibit at least about 75%, more specifically, at least about 80%, still more specifically at least about 85%, and in highly specific embodiments at least about 90% NOx conversion when fresh and hydrothermally aged in 10% steam for at least 1 hour, 3 hours and 6 hours at temperatures of at least about 800° C., at least about 850° C., and at least about 900° C.
  • materials in accordance with embodiments of the invention exhibit the NOx conversions noted above when hydrothermally aged in 10% steam for up to at least 3 hours and up to 6 hours at each of 800° C. and 850° C.
  • materials that have been hydrothermally aged in 10% steam at 900° C. for 1 hour exhibit NOx conversions of at least 80%, 85% and 90%.
  • the fresh and hydrothermally aged NOx conversion of Cu-SAPO-34 materials exhibit better NOx conversion than Cu CHA zeolitic molecular sieves (e.g. Cu SSZ-13) for both fresh and hydrothermally aged materials aged and tested under similar conditions.
  • the NOx conversion performance of Cu-SAPO-34 materials provided herein exhibit at least about 5% (e.g., 85% versus 80%), 10% (e.g. 90% versus 80%), 15% (e.g. 95% versus 80%) or 20% (e.g.
  • Cu-SAPO-34 materials are provided that exhibit extremely low N 2 O make for fresh and hydrothermally aged samples over a temperature range of 200° C. to 450° C.
  • the N 2 O make over the temperature range of 200° C. to 450° C. is less than about 10 ppm, less than 9 ppm, less than about 8 ppm, less than 7 ppm, less than about 5 ppm, less than about 4 ppm, less than about 3 ppm, and less than about 2 ppm.
  • a Cu-SAPO34 slurry is prepared by mixing 90 g of Cu-SAPO34, as described in detail below, with 215 mL of deionized water. The mixture is ball-milled for 11 hours to obtain a slurry which comprises 90% particles smaller than 10 ⁇ m. 15.8 g of zirconyl acetate in dilute acetic acid (containing 30% ZrO 2 ) is added into the slurry with agitation.
  • the slurry is coated onto 1′′ Diameter ⁇ 3′′ Long (1′′ D ⁇ 3′′ L) cellular ceramic cores, having a cell density of 400 cpsi (cells per square inch) and a wall thickness of 6.5 mil.
  • the coated cores are dried at 110° C. for 3 hours and calcined at 400° C. for 1 hour.
  • the coating process is repeated at least once to obtain a target washcoat loading of 2.4 g/in 3 . This provides a sample similar to catalytic articles that are used in automobiles.
  • Nitrogen oxides selective catalytic reduction (SCR) efficiency and selectivity of a fresh (as made) catalyst core are measured by adding a feed gas mixture of 500 ppm of NO, 500 ppm of NH 3 , 10% O 2 , 5% H 2 O, balanced with N 2 to a steady state reactor containing a 1′′D ⁇ 3′′L catalyst core.
  • the washcoated core is shaped into a square cross section wrapped with a ceramic insulation mat and placed inside an Inconel reactor tube heated by an electrical furnace.
  • the gases, O 2 (from air), N 2 and H 2 O are preheated in a preheater furnace before entering the reactor.
  • the reactive gases NO and NH 3 are introduced between the preheater furnace and the reactor.
  • the catalyst is coated on the aforementioned 400 cpsi (cells per square inch) core to target a loading between 2 and 2.5 g/in 3 .
  • the reaction is carried at a space velocity of 80,000 hr ⁇ 1 across a 150° C. to 460° C. temperature range (space velocity as determined at 32° F.). Space velocity is defined as the gas flow rate comprising the entire reaction mixture divided by the geometric volume of the catalyst core.
  • Hydrothermal stability of the catalyst is measured by hydrothermal aging of a fresh catalyst core in the presence of 10% H 2 O (remainder air; space velocity at 32° F. h ⁇ 1 4000 h ⁇ 1 ) one of the following conditions, 750° C. for 25 hours, 800° C. for 50 hours, 850° C. for 6 and 10 hours and 900° C. for 1 hour followed by measurement of the nitrogen oxides SCR efficiency and selectivity by the same process, as outlined above, for the SCR evaluation on a fresh catalyst core.
  • H 2 O residual air
  • Cu-SAPO34 materials are provided herein having a SiO 2 content in the range of about 10 to 25 wt. %, more specifically in the range of about 12 to 20 wt. % and most specifically in the range of about 15 to 19 wt. %, as measured by X-ray fluorescence (XRF).
  • the fresh SAPO-34 or Cu-SAPO-34 materials have a BET surface area in the range of about 300 to 600 m 2 /g., preferably greater than 350 m 2 /g, in the range of 375 m 2 /g to 600 m 2 /g.
  • the Cu-SAPO34 materials after ion exchange, have a conductivity sufficiently low, for example less than 600 ⁇ Scm ⁇ 1 , more specifically, less than 400 ⁇ Scm ⁇ 1 , and less than about 200 ⁇ Scm ⁇ 1 , so that conductivity the solution or filtrate containing the crystalline material that is substantially free of non-exchanged metal.
  • the conductivity of the filtrate can be measured by a conductivity meter (Newport Electronics, Model DP-03, Santa Anna, Ca).
  • the Cu content of the Cu-SAPO34 materials on a CuO basis as measured by Inductively Coupled Plasma (ICP) analysis is in the range of about 1% to 5%, more specifically in the range of about 2% to about 4%, and even more specifically in the range of about 2.5% to about 3.5%.
  • ICP Inductively Coupled Plasma
  • a neutral, nitrogen-containing organic template e.g., morpholine
  • suitable alumina, silica and phosphorous source materials are mixed together to form a gel mixture. Thereafter, the gel is heated to temperature of less than about 200° C., more specifically, less than about 185° C.
  • the heating at a suitable temperature for example about 170° C. is performed for at least about 12 hours, at least about 24 hours, or at least about 48 hours.
  • the mixture is then cooled, filtered and washed. Thereafter, ion exchange is performed sing a suitable copper salt, such as copper sulfate, copper nitrate or copper acetate.
  • a suitable copper salt such as copper sulfate, copper nitrate or copper acetate.
  • ion exchange crystalline material is washed until the conductivity of the filtrate is sufficiently low. Thereafter, the material is calcined at a temperature less than about 650° C., specifically less than 600° C., and more preferably less than 550° C.
  • the crystalline material made by the method has a crystal size having 90% of the crystals less than about 20 microns, and in specific embodiments, 90% of the crystals are less than about 15 microns. More details of the process of synthesizing Cu-SAPO-34 materials are provided in the Examples. In accordance with one or more embodiments, Cu-SAPO-34 catalysts materials are provided that are made by the methods of manufacturing described above.
  • loaded refers to the extra framework occupation of metals within the porous network of the molecular sieve.
  • the extra framework species resides in the channels, cavities, cages and/or the exterior surfaces of the molecular sieves.
  • Metals could be in one of several forms, including, but not limited to, ions, oxides, and oxycations.
  • the structural integrity of the zeolite or catalyst is enhanced by the presence of the metal in the molecular sieve.
  • a second metal further improves the catalytic properties of a catalytic article including a Cu-SAPO-34 molecular sieve.
  • An example of such a second metal includes zirconium, which may improve washcoat properties such as adhesion or porosity, and may improve the NOx conversion activity of the Cu-SAPO-34 material and resistance to degradation by hydrothermal aging.
  • a wide variety of material parameters including, but not limited to silicon content, the particular metal loaded, the metal loading quantity, the oxidation state of the metal, crystal size, surface area, overall composition of the non zeolitic molecular sieve, structural defects and others, may be independent or interdependent in their effect on hydrothermal stability and NOx conversion performance. Accordingly, in order to obtain an SCR catalyst material that exhibits excellent fresh and aged NOx conversion performance, it will be appreciated that changing one parameter such as the metal loading, crystal size and/or surface area may improve NOx conversion performance, but may negatively impact other material properties.
  • non-zeolitic molecular sieve material a wide variety of processing parameters to manufacture the non-zeolitic molecular sieve material, including but not limited to the hydrothermal synthesis conditions such as temperature, time, pH, specific reactants and material properties of the specific reactants can have an impact on the fresh and/or aged NOx conversion performance of the final material.
  • hydrothermal synthesis conditions such as temperature, time, pH, specific reactants and material properties of the specific reactants
  • material properties of the specific reactants can have an impact on the fresh and/or aged NOx conversion performance of the final material.
  • the metal e.g., Cu, Fe, or Co
  • the particular metal salt, the pH of the loading conditions during ion exchange, and direct incorporation of the metal to the molecular sieve during hydrothermal synthesis of the molecular sieve provides yet another set of variables to consider in the manufacture of a metal loaded molecular sieve for use as an SCR catalyst for the abatement of nitrogen oxides. Obtaining an excellent material for SCR performance is not a straightforward endeavor.
  • Metal-loaded non-zeolitic molecular sieve catalysts having the CHA structure in accordance with one or more embodiments of the invention can be utilized in catalytic processes which involve oxidizing and/or hydrothermal conditions, for example, in temperatures in excess of about 600° C., for example, above about 800° C. and in the presence of up to about 10% water vapor. More specifically, it has been found that metal-loaded non-zeolitic molecular sieve catalysts having the CHA structure which have been prepared in accordance with embodiments of the invention have increased hydrothermal stability compared to Fe Beta zeolites.
  • Metal-loaded non-zeolitic molecular sieve catalysts having the CHA structure prepared in accordance with embodiments of the invention yield improved activity in the selective catalytic reduction of NOx with ammonia, especially when operated under high temperatures of at least about 600° C., for example, about 800° C. and higher, and high water vapor environments of up to about 10% or more.
  • Embodiments of this invention also pertain to a process for abatement of NOx in an exhaust gas stream generated by an internal combustion engine utilizing metal-loaded non-zeolitic molecular sieve catalysts having the CHA structure.
  • Other embodiments pertain to SCR catalysts comprising metal-loaded non-zeolitic molecular sieves having the CHA structure, and exhaust gas treatment systems incorporating metal-loaded non-zeolitic molecular sieves having the CHA structure.
  • Still other embodiments pertain to ammonia oxidation (AMOX) catalysts and exhaust gas treatment systems incorporating AMOX catalyst comprising metal-loaded non-zeolitic molecular sieve catalysts having the CHA structure.
  • AMOX ammonia oxidation
  • catalysts and systems utilize metal-loaded non-zeolitic molecular sieves having the CHA structure having ion-exchanged metal which do not exhibit significant hydrothermal degradation of the catalysts when aged under high temperatures of at least about 600° C., for example, about 800° C. and higher, and high water vapor environments of about 10% or more.
  • no significant hydrothermal degradation of the catalyst material is exhibited by retaining at least about 85% of the fresh NOx conversion, retaining at least about 90% of the fresh NOx conversion and at least about 95% of the fresh NOx conversion when hydrothermally aged for temperatures of at least about 800° C. and 850° C. for times of 6 and 10 hours using the testing conditions described above, and 900° C.
  • retention of NOx conversion means the percentage NOx conversion of an aged sample divided by the percentage NOx conversion of a fresh sample.
  • the retention of NOx conversion occurs at temperatures in the range of 200° C. to 450° C.
  • the metal-loaded non-zeolitic molecular sieves having the CHA structure operate within a low temperature window.
  • the DOC will tend to activate for both low temperature light-off and HC fuel burning.
  • the SCR catalyst can maintain its ability to operate at low temperatures. Since the oxidation catalysts will lose their ability to oxidize NO to NO 2 , it is useful to provide an SCR catalyst that can treat NO as effectively as NO 2 .
  • Metal-loaded non-zeolitic molecular sieves having the CHA structure produced in accordance with embodiments of the invention have the ability to reduce NO with NH 3 at low temperatures
  • Another feature of the catalysts according to one or more embodiments of the present invention is that they can achieve a high conversion of NOx to nitrogen by ammonia SCR that is independent of NOx specification, i.e. the NO:NO 2 ratio. It is well known in the art that NO 2 is more reactive than NO and that the presence of NO 2 in an ammonia SCR catalyst feed stream improves NOx conversion. The optimal NO:NO 2 ratio for many catalysts is about 1:1.
  • the catalysts according to one or more embodiments of the present invention provide additional flexibility for treating the pollutants from a diesel engine exhaust stream.
  • the SCR catalyst can be in the form of self supporting catalyst particles or as a honeycomb monolith formed of the SCR catalyst composition.
  • the SCR catalyst composition is disposed as a washcoat or as a combination of washcoats on a ceramic or metallic substrate, for example, a honeycomb flow through substrate.
  • the SCR catalyst is formed from a metal-loaded non-zeolitic molecular sieves having the CHA structure.
  • such SCR catalyst compositions are deposited at a concentration of at least about 0.5 g/in 3 , for example, about 1.3 g/in 3 , about 2.4 g/in 3 or higher such as 5 g/in 3 to ensure that the desired NOx reduction is achieved and to secure adequate durability of the catalyst over extended use.
  • SCR catalyst is used herein in a broader sense to mean a selective catalytic reduction in which a catalyzed reaction of nitrogen oxides with a reductant occurs to reduce the nitrogen oxides.
  • reductant or “reducing agent” is also broadly used herein to mean any chemical or compound tending to reduce NOx at elevated temperatures.
  • the reducing agent is ammonia, specifically an ammonia precursor, i.e., urea.
  • the catalyst compositions are disposed on a substrate.
  • the substrate may be any of those materials typically used for preparing catalysts, and will usually comprise a ceramic or metal honeycomb structure. Any suitable substrate may be employed, such as a monolithic substrate of the type having fine, parallel gas flow passages extending therethrough from an inlet or an outlet face of the substrate, such that passages are open to fluid flow therethrough (referred to as honeycomb flow through substrates).
  • honeycomb flow through substrates honeycomb flow through substrates.
  • the passages which are essentially straight paths from their fluid inlet to their fluid outlet, are defined by walls on which the catalytic material is disposed as a washcoat so that the gases flowing through the passages contact the catalytic material.
  • the flow passages of the monolithic substrate are thin-walled channels, which can be of any suitable cross-sectional shape and size such as trapezoidal, rectangular, square, sinusoidal, hexagonal, oval, circular, etc.
  • Such structures may contain from about 60 to about 400 or more gas inlet openings (i.e., cells) per square inch of cross section.
  • the substrate can also be a wall-flow filter substrate, where the channels are alternately blocked, allowing a gaseous stream entering the channels from one direction (inlet direction), to flow through the channel walls and exit from the channels from the other direction (outlet direction).
  • AMOX and/or SCR catalyst composition can be coated on the flow through or wall-flow filter. If a wall flow substrate is utilized, the resulting system will be able to remove particulate matter along with gaseous pollutants.
  • the wall-flow filter substrate can be made from materials commonly known in the art, such as cordierite, aluminum titanate or silicon carbide. It will be understood that the loading of the catalytic composition on a wall flow substrate will depend on substrate properties such as porosity and wall thickness, and typically will be lower than loading on a flow through substrate.
  • the ceramic substrate may be made of any suitable refractory material, e.g., cordierite, cordierite-alumina, silicon nitride, zircon mullite, spodumene, alumina-silica magnesia, zircon silicate, sillimanite, a magnesium silicate, zircon, petalite, alpha-alumina, an aluminosilicate, and the like.
  • suitable substrates are cordierite substrates available from Corning, Inc. and aluminum titanate substrates available from NGK
  • the substrates useful for the catalysts of embodiments of the present invention may also be metallic in nature and be composed of one or more metals or metal alloys.
  • the metallic substrates may be employed in various shapes such as corrugated sheet or monolithic form.
  • Suitable metallic supports include the heat resistant metals and metal alloys such as titanium and stainless steel as well as other alloys in which iron is a substantial or major component.
  • Such alloys may contain one or more of nickel, chromium and/or aluminum, and the total amount of these metals may advantageously comprise at least 15 wt. % of the alloy, e.g., 10-25 wt. % of chromium, 3-8 wt. % of aluminum and up to 20 wt. % of nickel.
  • the alloys may also contain small or trace amounts of one or more other metals such as manganese, copper, vanadium, titanium, and the like.
  • the surface or the metal substrates may be oxidized at high temperatures, e.g., 1000° C. and higher, to improve the resistance to corrosion of the alloys by forming an oxide layer on the surfaces of the substrates. Such high temperature-induced oxidation may enhance the adherence of the refractory metal oxide support and catalytically promoting metal components to the substrate.
  • one or both of the metal-loaded non-zeolitic molecular sieves having the CHA structure compositions may be deposited on an open cell foam substrate.
  • substrates are well known in the art, and are typically formed of refractory ceramic or metallic materials.
  • washcoats of metal-loaded non-zeolitic molecular sieves having the CHA structure can be prepared using a binder.
  • a ZrO 2 binder derived from a suitable precursor such as zirconyl acetate or any other suitable zirconium precursor such as zirconyl nitrate.
  • zirconyl acetate binder provides a catalytic coating that remains homogeneous and intact after thermal aging, for example, when the catalyst is exposed to high temperatures of at least about 600° C., for example, about 800° C. and higher, and high water vapor environments of about 10% or more.
  • binders include, but are not limited to, alumina and silica.
  • Alumina binders include aluminum oxides, aluminum hydroxides, and aluminum oxyhydroxides.
  • Aluminum salts and colloidal forms of alumina many also be used.
  • Silica binders include various forms of SiO 2 , including colloidal silica.
  • binder compositions may include any combination of zirconia, alumina, and silica.
  • metal-loaded non-zeolitic molecular sieves having the CHA structure can be used as an ammonia oxidation catalyst.
  • Such AMOX catalysts are useful in exhaust gas treatment systems including an SCR catalyst.
  • a gaseous stream containing oxygen, nitrogen oxides and ammonia can be sequentially passed through first and second catalysts, the first catalyst favoring reduction of nitrogen oxides and the second catalyst favoring the oxidation or other decomposition of excess ammonia.
  • the first catalysts can be a SCR catalyst comprising a zeolite and the second catalyst can be an AMOX catalyst comprising a molecular sieve.
  • ammonia is added to the gaseous stream containing the nitrogen oxides and the gaseous stream is then contacted with a suitable catalyst at elevated temperatures in order to catalyze the reduction of nitrogen oxides with ammonia.
  • gaseous streams for example, the products of combustion of an internal combustion engine or of a gas-fueled or oil-fueled turbine engine, often inherently also contain substantial amounts of oxygen.
  • a typical exhaust gas of a turbine engine contains from about 2 to 15 volume percent oxygen and from about 20 to 500 volume parts per million nitrogen oxides, the latter normally comprising a mixture of NO and NO 2 .
  • an oxygen-containing gas usually air, may be introduced between the first catalyst zone and the second catalyst zone, in order to insure that adequate oxygen is present in the second catalyst zone for the oxidation of residual or excess ammonia.
  • Metal-promoted zeolites have been used to promote the reaction of ammonia with nitrogen oxides to form nitrogen and H 2 O selectively over the competing reaction of oxygen and ammonia.
  • the catalyzed reaction of ammonia and nitrogen oxides is therefore sometimes referred to as the selective catalytic reduction (“SCR”) of nitrogen oxides or, as sometimes herein, simply as the “SCR process”.
  • SCR selective catalytic reduction
  • Such channeling is of particular concern when utilizing catalysts comprising monolithic honeycomb-type carriers comprising refractory bodies having a plurality of fine, parallel gas flow paths extending therethrough because, unlike the case of beds of particulate catalyst, there is no opportunity for gas mixing between channels.
  • metal-loaded non-zeolitic molecular sieves having the CHA structure can be formulated to favor either (1) the SCR process, i.e., the reduction of nitrogen oxides with ammonia to form nitrogen and H 2 O, or (2) the oxidation of ammonia with oxygen to form nitrogen and H 2 O.
  • the SCR process i.e., the reduction of nitrogen oxides with ammonia to form nitrogen and H 2 O
  • the oxidation of ammonia with oxygen to form nitrogen and H 2 O.
  • U.S. Pat. No. 5,516,497 teaches iron and copper loading levels on zeolites other than copper silicoaluminophosphate to obtain selectivity for an SCR reaction and selectivity of the catalyst for the oxidation of ammonia by oxygen at the expense of the SCR process, thereby improving ammonia removal.
  • metal loading can be tailored to obtain selectivity for SCR reactions and oxidation of ammonia by oxygen and to provide exhaust gas treatment systems utilizing both types of catalyst.
  • the above principles are utilized by providing a staged or two-zone catalyst in which a first catalyst zone with metal-loaded non-zeolitic molecular sieves having the CHA structure, that promotes SCR followed by a second catalyst zone comprising a metal-loaded non-zeolitic molecular sieves having the CHA structure and/or a precious metal component that promotes oxidation of ammonia.
  • the resultant catalyst composition thus has a first (upstream) zone which favors the reduction of nitrogen oxides with ammonia, and a second (downstream) zone which favors the oxidation of ammonia.
  • the oxidation of residual ammonia by oxygen is favored by the downstream or second catalyst zone.
  • the quantity of ammonia in the gaseous stream discharged from the catalyst is thereby reduced or eliminated.
  • the first zone and the second zones can be on a single catalyst substrate or as separate substrates.
  • metal-loaded non-zeolitic molecular sieves having the CHA structure SCR catalysts can be disposed on a wall-flow filter or catalyzed soot filter. Washcoats comprising metal-loaded non-zeolitic molecular sieves having the CHA structure can be coated on a porous filter to provide for soot combustion, SCR and AMOX functions.
  • the catalyst comprises a precious metal component, i.e., a platinum group metal component.
  • a precious metal component i.e., a platinum group metal component.
  • AMOX catalysts typically include a platinum component.
  • Suitable precious metal components include platinum, palladium, rhodium and mixtures thereof.
  • the several components (for example, metal-loaded non-zeolitic molecular sieves having the CHA structure and precious metal component) of the catalyst material may be applied to the refractory carrier member, i.e., the substrate, as a mixture of two or more components or as individual components in sequential steps in a manner which will be readily apparent to those skilled in the art of catalyst manufacture.
  • a typical method of manufacturing a catalyst according to an embodiment of the present invention is to provide the catalyst material as a coating or layer of washcoat on the walls of the gas-flow passages of a suitable carrier member. This may be accomplished by impregnating a fine particulate refractory metal oxide support material, e.g., gamma alumina, with one or more catalytic metal components such as a precious metal, i.e., platinum group, compound or other noble metals or base metals, drying and calcining the impregnated support particles and forming an aqueous slurry of these particles.
  • a fine particulate refractory metal oxide support material e.g., gamma alumina
  • one or more catalytic metal components such as a precious metal, i.e., platinum group, compound or other noble metals or base metals
  • Particles of the bulk metal-loaded non-zeolitic molecular sieves having the CHA structure may be included in the slurry.
  • Activated alumina may be thermally stabilized before the catalytic components are dispersed thereon, as is well known in the art, by impregnating it with, e.g., a solution of a soluble salt of barium, lanthanum, zirconium, rare earth metal or other suitable stabilizer precursor, and thereafter drying (e.g., at 110° C. for one hour) and calcining (e.g., at 550° C. for one hour) the impregnated activated alumina to form a stabilizing metal oxide dispersed onto the alumina.
  • Base metal catalysts may optionally also have been impregnated into the activated alumina, for example, by impregnating a solution of a base metal nitrate into the alumina particles and calcining to provide a base metal oxide dispersed in the alumina particles.
  • the carrier may then be immersed into the slurry of impregnated activated alumina and excess slurry removed to provide a thin coating of the slurry on the walls of the gas-flow passages of the carrier.
  • the coated carrier is then dried and calcined to provide an adherent coating of the catalytic component and, optionally, the metal-loaded non-zeolitic molecular sieves having the CHA structure material, to the walls of the passages thereof.
  • One or more additional layers may be provided on the carrier. After each layer is applied, or after a number of desired layers are applied, the carrier is then dried and calcined to provide a finished catalyst member in accordance with one embodiment of the present invention.
  • the alumina or other support particles impregnated with the precious metal or base metal component may be mixed with bulk or supported particles of the metal-loaded non-zeolitic material having the CHA structure in an aqueous slurry, and this mixed slurry of catalytic component particles and metal-loaded non-zeolitic molecular sieves having the CHA structure material particles may be applied as a coating to the walls of the gas-flow passages of the carrier.
  • the exhaust gas stream can be contacted with a catalyst prepared in accordance with embodiments of the present invention.
  • catalysts comprising metal-loaded non-zeolitic molecular sieves having the CHA structure made in accordance with embodiments of the present invention are well suited to treat the exhaust of engines, including diesel engines.
  • the metal-loaded non-zeolitic molecular sieves having the CHA structure can be used in combination with other metal containing zeolitic SCR catalysts such as Beta zeolite (e.g., Fe Beta), zeolite Y, and ZSM5.
  • a metal-loaded non-zeolitic molecular sieve having the CHA structure can be physically mixed with a metal containing zeolitic SCR catalyst, or alternatively, they can be in separate washcoats.
  • the separate washcoats containing different catalysts can be provided in a layered structure, or alternatively, the different catalysts can be arranged in an upstream/downstream relationship on a substrate.
  • a metal-loaded non-zeolitic molecular sieve combined with FeBeta may provide a catalyst in which FeBeta exhibits excellent high temperature performance, while the metal-loaded non-zeolitic molecular sieve exhibits excellent low temperature performance, providing a wide range of operation.
  • FIGS. 1A , 1 B and 1 C Exemplary embodiments of emission treatment systems are shown in FIGS. 1A , 1 B and 1 C.
  • One embodiment of the inventive emissions treatment system denoted as 1 A is schematically depicted in FIG. 1A .
  • the exhaust containing gaseous pollutants (including unburned hydrocarbons, carbon monoxide and NOx) and particulate matter, is conveyed from the engine 19 to a position downstream in the exhaust system where a reductant, i.e., ammonia or an ammonia-precursor, is added to the exhaust stream.
  • the reductant is injected as a spray via a nozzle (not shown) into the exhaust stream.
  • Aqueous urea shown on one line 25 can serve as the ammonia precursor which can be mixed with air on another line 26 in a mixing station 24 .
  • Valve 23 can be used to meter precise amounts of aqueous urea which are converted in the exhaust stream to ammonia.
  • the exhaust stream with the added ammonia is conveyed to the SCR catalyst substrate 12 (also referred to herein including the claims as “the first substrate”) containing metal-loaded non-zeolitic molecular sieves having the CHA structure in accordance with one or more embodiments.
  • the NOx component of the exhaust stream is converted through the selective catalytic reduction of NOx with NH 3 to N 2 and H 2 O.
  • excess NH 3 that emerges from the inlet zone can be converted through oxidation by a downstream ammonia oxidation catalyst (not shown) also containing metal-loaded non-zeolitic molecular sieves having the CHA structure to convert the ammonia to N 2 and H 2 O.
  • the first substrate is typically a flow through monolith substrate.
  • FIG. 1B An alternative embodiment of the emissions treatment system, denoted as 11 B is depicted in FIG. 1B which contains a second substrate 27 interposed between the NH 3 injector and the first substrate 12 .
  • the second substrate is coated with an SCR catalyst composition which may be the same composition as is used to coat the first substrate 12 or a different composition.
  • SCR catalyst compositions that are used to coat the substrate can be selected to optimize NOx conversion for the operating conditions characteristic of that site along the exhaust system.
  • the second substrate can be coated with an SCR catalyst composition that is better suited for higher operating temperatures experienced in upstream segments of the exhaust system, while another SCR composition can be used to coat the first substrate (i.e., the inlet zone of the first substrate) that is better suited to cooler exhaust temperatures which are experienced in downstream segments of the exhaust system.
  • an SCR catalyst composition that is better suited for higher operating temperatures experienced in upstream segments of the exhaust system
  • another SCR composition can be used to coat the first substrate (i.e., the inlet zone of the first substrate) that is better suited to cooler exhaust temperatures which are experienced in downstream segments of the exhaust system.
  • the second substrate 27 can either be a honeycomb flow through substrate, an open cell foam substrate or a honeycomb wall flow substrate.
  • the system can remove greater than 80% of the particulate matter including the soot fraction and the SOF.
  • an oxidation catalyst upstream of the site of ammonia/ammonia precursor injection.
  • an oxidation catalyst is disposed on a catalyst substrate 34 .
  • the emissions treatment system 11 C is provided with the first substrate 12 and optionally includes a second substrate 27 .
  • the exhaust stream is first conveyed to the catalyst substrate 34 where at least some of the gaseous hydrocarbons, CO and particulate matter are combusted to innocuous components.
  • a significant fraction of the NO of the NOx component of the exhaust is converted to NO 2 . Higher proportions of NO 2 in the NOx component facilitate the reduction of NOx to N 2 and H 2 O on the SCR catalyst(s) located downstream.
  • the first substrate 12 could be a catalyzed soot filter, and the SCR catalyst could be disposed on the catalyzed soot filter.
  • the second substrate 27 comprising an SCR catalyst may be located upstream from catalyst substrate 34 .
  • Testing of catalyst samples to determine the SCR performance of catalysts and/or to compare the performance to other catalysts can be completed as follows.
  • the catalyst samples are slurried and washcoated, as described below onto a monolithic core.
  • the size of the core is trimmed to give a square of 144 cells (at 400 cpsi) by three inches in length.
  • the sample is loaded into a tubular flow reactor and tested for catalytic activity.
  • the flow rate is set so that the space velocity over the sample is approximately 80,000 h ⁇ 1, which is defined by the geometric volume of the sample with respect to the total volume of gas flow.
  • the testing consists of flowing a simulated diesel exhaust gas mixture over the catalyst and measuring the NOx and NH 3 conversions, as well as N 2 O make.
  • the simulated gas mixture consisted of 10% O 2 , 5% H 2 O, 500 ppm NO and 500 ppm NH 3 .
  • the testing procedure equilibrates the catalyst at several steady state temperature points, and measures the resulting conversions.
  • the steady state temperature points chosen for testing and comparison for the samples herein were 200° C., 250° C., 300° C. and 450° C.
  • the high temperature stability is measured by treating the catalysts at temperatures of 850° C. for 6 h with a flow of air and steam (10 vol %).
  • samples can be aged above 600° C., more particularly, above 700° C. for times longer than 6 hrs, and more particularly, for longer 24 hrs etc.
  • 6,914,030 discloses a method of synthesizing pure phase CHA framework type silicoaluminophosphate molecular sieves having relatively low silicon content using synthesis templates that contain at least one dimethylamino moiety, selected from one or more of N,N-dimethylethanolamine, N,N-dimethylpropanolamine, N,N-dimethylbutanolamine, N,N-dimethylheptanolamine, N,N-dimethylhexanolamine, N,N-dimethylethylenediamine, N,N-dimethylbutylenediamine, N,N-dimethylheptylenediamine, N,N-dimethylhexylenediamine 1-dimethylamino-2-propanol, N,N-dimethylethylamine, N,N-dimethylpropylamine, N,N-dimethylpentylamine, N,N-dimethylhexylamine and N,N-di
  • U.S. Pat. No. 7,247,287 discloses the synthesis of silicoaluminophosphate molecular sieves having the CHA framework type employing a template having the formula: R 1 R 2 N—R 3 wherein R 1 and R 2 are independently selected from the group consisting of alkyl groups having from 1 to 3 carbon atoms and hydroxyalkyl groups having from 1 to 3 carbon atoms and R 3 is selected from the group consisting of 4- to 8-membered cycloalkyl groups, optionally substituted by 1 to 3 alkyl groups having from 1 to 3 carbon atoms; and 4- to 8-membered heterocyclic groups having from 1 to 3 heteroatoms, said heterocyclic groups being optionally substituted by 1 to 3 alkyl groups having from 1 to 3 carbon atoms and the heteroatoms in said heterocyclic groups being selected from the group consisting of O, N, and S.
  • the template is selected from N,N-dimethyl-cyclohexylamine, N,N-dimethyl-methyl-cyclohexylamine, N,N-dimethyl-cyclopentylamine, N,N-dimethyl-methyl-cyclopentylamine, N,N-dimethyl-cycloheptylamine, N,N-dimethyl-methylcycloheptylamine, and most preferably is N,N-dimethyl-cyclohexylamine.
  • the synthesis can be effected with or without the presence of fluoride ions and can produce CHA framework type silicoaluminophosphates with a low Si/Al ratio. Alternative synthesis conditions and routes are of course within the scope of the present invention.
  • a SAPO-34 was prepared from a gel composition of 1.0 Al 2 O 3 :1.06 P 2 O 5 :1.08 SiO 2 :2.09 R:66H 2 O.
  • a reaction mixture was formed by combining 1.54 kg of 85 wt. % orthophosphoric acid with a mixture of 920 g of a pseudoboehmite alumina (Catapal B) in 1.8 kg of deionized water. Then a further 1 kg of deionized water was added. The mixture was stirred until homogeneous. To this mixture was added a mixture containing 409 g of fumed silica (Aerosil-200), 1.16 kg morpholine (Aldrich, 99%) and 1.5 kg deionized water.
  • the silica-containing mixture was added slowly with stirring and stirred until homogeneous. A further 2.5 kg of deionized water was added and the mixture was stirred until homogenous.
  • the resulting gel was transferred to 5 gallon autoclave where it was aged at 38° C. for 24 hours. This was then heated in the autoclave for 24 hours at 200° C.
  • the crystalline product was recovered via filtration and was washed to a conductivity lower than 200 ⁇ Scm ⁇ 1 . Washing the crystalline product after ion exchange in this manner so that conductivity is sufficiently low, that is below 200 ⁇ Scm ⁇ 1 , results in a crystalline material that is substantially free of non-exchanged metal.
  • the sample was dried before calcining at 540° C. for 4 hours.
  • the crystalline product had an X-ray powder diffraction pattern indicating that it was SAPO-34, a non-zeolitic molecular sieve with the chabazite topology.
  • the composition of the solids product was established to be 0.19 wt % C, 49.63 wt % Al 2 O 3 , 26.92 wt % P 2 O 5 , and 23.14 wt % SiO 2 .
  • An NH 4 -form of SAPO-34 was prepared by exchanging 350 g of the calcined SAPO-34 in a solution of ammonium nitrate (1750 g 54 wt % ammonium nitrate mixed with 1750 g of deionized water).
  • the pH was adjusted to 3 by addition of ammonium hydroxide prior to heating the solution to 80° C.
  • the exchange was carried out by agitating the slurry at 80° C. for 1 hour, during which the pH was between 2.57 and 3.
  • the solid was then filtered on a Buchner filter and washed until the filtrate had a conductivity lower than 200 ⁇ Scm ⁇ 1 .
  • the powder was then dried for 16 hours before carrying out the above ammonium exchange process for a total of two exchanges.
  • a Cu-SAPO34 powder catalyst was prepared by mixing 350 g of NH 4 + -form SAPO-34, with 1.31 L of a copper(II) sulfate solution of 1.0 M.
  • An ion-exchange reaction between the NH 4 + -form SAPO-34 and the copper ions was carried out by agitating the slurry at 70° C. for 1 hour. The pH was between 2.9 and 3.2 during the reaction. The resulting mixture was then filtered, washed until the filtrate had a conductivity lower than 200 ⁇ Scm ⁇ 1 , which indicated that substantially no soluble or free copper remained in the sample, and the washed sample was dried at 90° C.
  • the above process including the ion-exchange, filtering, washing and drying was repeated to give a total of 2 exchanges.
  • the pH of the second exchange was between 2.9 and 3.1 during the reaction.
  • the obtained Cu-SAPO34 catalyst comprised CuO at 3.31% by weight, as determined by ICP analysis.
  • the BET surface area of this sample as prepared was 417 m 2 /g.
  • the BET surface area of this sample after aging at 800° C. in 10% steam for 50 hours was 406 m 2 /g.
  • a Cu-SAPO34 slurry was prepared by mixing 90 g of Cu-SAPO34, as described above, with 215 mL of deionized water. The mixture was ball-milled for 11 hours to obtain a slurry which comprised 90% particles smaller than 10 ⁇ m. 15.8 g of zirconyl acetate in dilute acetic acid (containing 30% ZrO 2 ) was added into the slurry with agitation.
  • the slurry was coated onto 1′′D ⁇ 3′′L cellular ceramic cores, having a cell density of 400 cpsi (cells per square inch) and a wall thickness of 6.5 mil.
  • the coated cores were dried at 110° C. for 3 hours and calcined at 400° C. for 1 hour. The coating process was repeated once to obtain a target washcoat loading of 2.4 g/in 3 .
  • Nitrogen oxides selective catalytic reduction (SCR) efficiency and selectivity of a fresh catalyst core was measured by adding a feed gas mixture of 500 ppm of NO, 500 ppm of NH 3 , 10% O 2 , 5% H 2 O, balanced with N 2 to a steady state reactor containing a 1′′D ⁇ 3′′L catalyst core.
  • the washcoated core is shaped into a square cross section wrapped with a ceramic insulation mat and placed inside an Inconel reactor tube heated by an electrical furnace.
  • the gases, O 2 (from air), N2 and H 2 O are preheated in a preheater furnace before entering the reactor.
  • the reactive gases NO and NH3 are introduced between the preheater furnace and the reactor.
  • the catalyst is coated on the aforementioned 400 cpsi (cells per square inch) core to target a loading between 2 and 2.5 g/in 3 .
  • the reaction was carried at a space velocity of 80,000 hr ⁇ 1 across a 150° C. to 460° C. temperature range. Space velocity is defined as the gas flow rate comprising the entire reaction mixture divided by the geometric volume of the catalyst core.
  • Hydrothermal stability of the catalyst was measured by hydrothermal aging of a fresh catalyst core in the presence of 10% H 2 O at one of the following conditions, 750° C. for 25 hours, 800° C. for 50 hours, and 850° C. for 6 hours followed by measurement of the nitrogen oxides SCR efficiency and selectivity by the same process, as outlined above, for the SCR evaluation on a fresh catalyst core.
  • the standard test of an aged catalyst evaluates a catalyst aged at 800° C. for 50 hrs.
  • FIG. 2 is a graph showing the NOx conversion and N 2 O make or formation versus temperature for the fresh sample and the sample aged at 800° C.
  • the fresh NOx conversion at 200° C. is about 72%
  • the NOx conversion for the aged sample at 200° C. is 87%
  • FIG. 3 is a graph showing the NOx Conversion and N 2 O formation versus aging temperatures for the aged samples.
  • the NOx conversion at 200° C. for the sample aged 750° C. was 90% and for the sample aged at 850° C. was about 80%.
  • the N 2 O make for the fresh sample at 200° C. was 1 ppm, and the maximum value over the range of 200° C. to 450° C. was 3 ppm.
  • the N 2 O make at 200° C. was 4 ppm, and the maximum value over the range of 200° C. to 450° C. was 5 ppm.
  • the NH 4 + -form of SAPO-34 was formed using the same hydrothermal synthesis and ammonium exchange conditions detailed in example 1.
  • a Cu-SAPO34 powder catalyst was prepared by mixing 320 g of NH 4 + -form SAPO-34 with 1.28 L of a copper(II) acetate monohydrate solution of 0.5 M. The pH was between 4.0 and 4.3 during the reaction. An ion-exchange reaction between the NH4 + -form SAPO-34 and the copper ions was carried out by agitating the slurry at 70° C. for 1 hour. The resulting mixture was then filtered, washed until the filtrate had a conductivity lower than 200 ⁇ Scm ⁇ 1 , which indicated that substantially no soluble or free copper remained in the sample, and the washed sample was dried at 90° C. The obtained Cu-SAPO34 catalyst comprised CuO at 3.18% by weight. The BET surface area of this sample as prepared was 307 m 2 /g. The BET surface area of this sample after aging at 850° C. in 10% steam for 6 hours was 303 m 2 /g.
  • FIG. 4 is a graph showing the NOx conversion and N 2 O make or formation versus temperature for this sample.
  • the NOx conversion for a fresh sample at 200° C. was 79%, and for sample aged at 850° C. for 10 hours was about 68%. While the NOx conversion of this sample was not as high as Examples 1, 11 and 12, similar to Example 4 below, the fresh surface area was relatively low at 307 m 2 /g, and the surface area when aged at 850° C. was 303 m 2 /g. It is unclear if the lower NOx conversion was due to surface area or if other factors affected NOx performance.
  • a SAPO-44 was prepared from a gel composition of 1.0 Al 2 O 3 :1.0 P 2 O 5 :1.0 SiO 2 :1.9 R:63 H 2 O.
  • a reaction mixture was formed by combining 1.54 kg of 85 wt. % orthophosphoric acid with a mixture of 971 g of a pseudoboehmite alumina (Catapal B) in 4 kg of deionized water. The mixture was stirred until homogeneous. To this mixture was added a mixture containing 399.6 g of fumed silica (Aerosil-200), 1.25 kg cyclohexylamine (Aldrich, 99%) and 2.66 kg deionized water.
  • the silica-containing mixture was added slowly with stirring and stirred until homogeneous.
  • the resulting gel was transferred to 5 gallon autoclave where it was heated in the autoclave for 48 hours at 190° C.
  • the crystalline product was recovered via filtration and was washed to a conductivity lower than 200 ⁇ Scm ⁇ 1 .
  • the sample was dried before calcining at 600° C. for 4 hours.
  • the crystalline product had an X-ray powder diffraction pattern indicating that it was SAPO-44, a non-zeolitic molecular sieve with the chabazite topology.
  • the composition of the solids product was established to be 42.51 wt % Al 2 O 3 , 35.93 wt % P205, and 21.17 wt % SiO 2 .
  • An NH 4 -form of SAPO-44 was prepared by exchanging 350 g of the calcined SAPO-44 in a solution of ammonium nitrate (1750 g 54 wt % ammonium nitrate mixed with 1750 g of deionized water). The pH was adjusted to 3 by addition of ammonium hydroxide prior to heating the solution to 80° C. The exchange was carried out by agitating the slurry at 80° C. for 1 hour, during which the pH was between 2.57 and 3. The solid was then filtered on a Buchner filter and washed until the filtrate had conductivity lower than 200 ⁇ Scm ⁇ 1 . The powder was then dried for 16 hours before carrying out the above ammonium exchange process for a total of two exchanges.
  • a CuSAPO-44 catalyst comprising 3.78% CuO by weight was prepared by the same process as that in Example 1. The pH of both exchanges were between 2.6 and 2.7 throughout the exchange. Using the procedure in Example 1, 300 grams of CuSAPO-44 at 3.78% CuO by weight was prepared.
  • FIG. 5 is a graph showing the NOx Conversion and N 2 O formation versus aging temperatures for this sample.
  • a SAPO-34 was prepared from a gel composition of 1.0 Al 2 O 3 :1.06 P 2 O 5 :1.08 SiO 2 :2.09 R:66 H 2 O.
  • a reaction mixture was formed by combining 1.54 kg of 85 wt. % orthophosphoric acid with a mixture of 920 g of a pseudoboehmite alumina (Catapal B) in 1.8 kg of deionized water. Then a further 1 kg of deionized water was added. The mixture was stirred until homogeneous. To this mixture was added a mixture containing 1022.5 g of colloidal silica (Ludox AS40), 1.16 kg morpholine (Aldrich, 99%) and 886.5 g deionized water.
  • the silica-containing mixture was added slowly with stirring and stirred until homogeneous. A further 2.5 kg of deionized water was added and the mixture was stirred until homogenous.
  • the resulting gel was transferred to 5 gallon autoclave where it was aged at 38° C. for 24 hours. This was then heated in the autoclave for 24 hours at 200° C.
  • the crystalline product was recovered via filtration and was washed to a conductivity lower than 200 ⁇ Scm ⁇ 1 .
  • the sample was dried before calcining at about 640° C. for 4 hours.
  • An NH 4 -form of SAPO-34 was prepared by exchanging 350 g of the calcined SAPO-34 in a solution of ammonium nitrate (1750 g 54 wt % ammonium nitrate mixed with 1750 g of deionized water). The pH was adjusted to 4 by addition of ammonium hydroxide prior to heating the solution to 80° C. The exchange was carried out by agitating the slurry at 80° C. for 1 hour. The solid was then filtered on a Buchner filter and washed until the filtrate had a conductivity lower than 200 ⁇ Scm ⁇ 1 . The powder was then dried for 16 hours before carrying out the above ammonium exchange process for a total of two exchanges.
  • a Cu-SAPO34 powder catalyst was prepared by mixing 350 g of NH 4 -form SAPO-34, with 1.31 L of a copper(II) sulfate solution of 1.0 M.
  • An ion-exchange reaction between the NH 4 + -form SAPO-34 and the copper ions was carried out by agitating the slurry at 70° C. for 1 hour.
  • the resulting mixture was then filtered, washed until the filtrate had a conductivity of lower than 200 ⁇ Scm ⁇ 1 , which indicated that substantially no soluble or free copper remained in the sample, and the washed sample was dried at 90° C.
  • the above process including the ion-exchange, filtering, washing and drying was repeated to give a total of 2 exchanges.
  • the pH of both exchanges were between 2.8 and 3.2 throughout the exchange.
  • the obtained Cu-SAPO34 catalyst comprised CuO at 3.71% by weight, as determined by ICP analysis.
  • the BET surface area of this sample as prepared was 309 m 2 /g.
  • the BET surface area of this sample after aging at 800° C. in 10% steam for 50 hours was 264 m 2 /g.
  • FIG. 6 is a graph showing the NOx Conversion and N 2 O formation versus aging temperatures for this sample.
  • the NOx conversion at 200° C. for the fresh sample was about 49% and for the sample at 800° C. was about 22%. While it is not entirely understood why this sample exhibited poorer NOx conversion than the others, it is noted that the fresh surface area of this sample was on the low end of the samples tested at 309 m 2 /g, and the aged surface area at 800° C. was at 264 m 2 /g.
  • a SAPO-34 is prepared from a gel composition of 1.0 Al 2 O 3 :1.06 P 2 O 5 :1.08 SiO 2 :1.05 (TEA) 2 O:66 H 2 O.
  • a reaction mixture is formed by combining 1.54 kg of 85 wt. % orthophosphoric acid with a mixture of 920 g of a pseudoboehmite alumina (Catapal B) in 1.8 kg of deionized water. Then a further 1 kg of deionized water is added. The mixture is stirred until homogeneous.
  • An NH 4 -form of SAPO-34 is prepared by exchanging 350 g of the calcined SAPO-34 in a solution of ammonium nitrate (1750 g 54 wt % ammonium nitrate mixed with 1750 g of deionized water). The pH is adjusted to 4 by addition of ammonium hydroxide prior to heating the solution to 80° C. The exchange is carried out by agitating the slurry at 80° C. for 1 hour. The solid is then filtered on a Buchner filter and washed until the filtrate had a conductivity lower than 200 ⁇ Scm ⁇ 1 . The powder is then dried for 16 hours before carrying out the above ammonium exchange process for a total of two exchanges.
  • a Cu-SAPO34 powder catalyst is prepared by mixing 350 g of NH4+-form SAPO-34, with 1.31 L of a copper(II) sulfate solution of 1.0 M.
  • An ion-exchange reaction between the NH4+-form SAPO-34 and the copper ions is carried out by agitating the slurry at 70° C. for 1 hour.
  • the resulting mixture is then filtered, washed until the filtrate had a conductivity of lower than 200 ⁇ Scm ⁇ 1 , which indicated that substantially no soluble or free copper remained in the sample, and the washed sample is dried at 90° C.
  • the above process including the ion-exchange, filtering, washing and drying is repeated to give a total of 2 exchanges.
  • a SAPO-34 is prepared from a gel composition of 1.0 Al 2 O 3 :1.06 P2O5:1.08 SiO2:2.09 i-PrNH2:66 H 2 O.
  • a reaction mixture is formed by combining 1.54 kg of 85 wt. % orthophosphoric acid with a mixture of 920 g of a pseudoboehmite alumina (Catapal B) in 1.8 kg of deionized water. Then a further 1 kg of deionized water is added. The mixture is stirred until homogeneous.
  • An NH4-form of SAPO-34 is prepared by exchanging 350 g of the calcined SAPO-34 in a solution of ammonium nitrate (1750 g 54 wt % ammonium nitrate mixed with 1750 g of deionized water). The pH is adjusted to 4 by addition of ammonium hydroxide prior to heating the solution to 80° C. The exchange is carried out by agitating the slurry at 80° C. for 1 hour. The solid is then filtered on a Buchner filter and washed until the filtrate had a conductivity lower than 200 ⁇ Scm ⁇ 1. The powder is then dried for 16 hours before carrying out the above ammonium exchange process for a total of two exchanges.
  • a Cu-SAPO34 powder catalyst is prepared by mixing 350 g of NH4+-form SAPO-34, with 1.31 L of a copper(II) sulfate solution of 1.0 M.
  • An ion-exchange reaction between the NH4+-form SAPO-34 and the copper ions is carried out by agitating the slurry at 70° C. for 1 hour.
  • the resulting mixture is then filtered, washed until the filtrate had a conductivity of lower than 200 ⁇ Scm ⁇ 1 , which indicated that substantially no soluble or free copper remained in the sample, and the washed sample is dried at 90° C.
  • the above process including the ion-exchange, filtering, washing and drying is repeated to give a total of 2 exchanges.
  • a SAPO-34 is prepared from a gel composition of 1.0 Al 2 O 3 :1.06 P2O5:1.08 SiO2:1.05 (Pr2NH): 0.53 (TEA)2O:66 H 2 O.
  • a reaction mixture is formed by combining 1.54 kg of 85 wt. % orthophosphoric acid with a mixture of 920 g of a pseudoboehmite alumina (Catapal B) in 1.8 kg of deionized water. Then a further 1 kg of deionized water is added. The mixture is stirred until homogeneous.
  • An NH4-form of SAPO-34 is prepared by exchanging 350 g of the calcined SAPO-34 in a solution of ammonium nitrate (1750 g 54 wt % ammonium nitrate mixed with 1750 g of deionized water). The pH is adjusted to 4 by addition of ammonium hydroxide prior to heating the solution to 80° C. The exchange is carried out by agitating the slurry at 80° C. for 1 hour. The solid is then filtered on a Buchner filter and washed until the filtrate had a conductivity lower than 200 ⁇ Scm ⁇ 1 . The powder is then dried for 16 hours before carrying out the above ammonium exchange process for a total of two exchanges.
  • a Cu-SAPO34 powder catalyst is prepared by mixing 350 g of NH4+-form SAPO-34, with 1.31 L of a copper(II) sulfate solution of 1.0 M.
  • An ion-exchange reaction between the NH4+-form SAPO-34 and the copper ions is carried out by agitating the slurry at 70° C. for 1 hour.
  • the resulting mixture is then filtered, washed until the filtrate had a conductivity of lower than 200 ⁇ Scm ⁇ 1 , which indicated that substantially no soluble or free copper remained in the sample, and the washed sample is dried at 90° C.
  • the above process including the ion-exchange, filtering, washing and drying is repeated to give a total of 2 exchanges.
  • a SAPO-34 is prepared from a gel composition of 1.0 Al2O3:1.06 P2O5:1.08 SiO2:2.09 Pr2NH:66 H 2 O.
  • a reaction mixture is formed by combining 1.54 kg of 85 wt. % orthophosphoric acid with a mixture of 920 g of a pseudoboehmite alumina (Catapal B) in 1.8 kg of deionized water. Then a further 1 kg of deionized water is added. The mixture is stirred until homogeneous. To this mixture is added a mixture containing 409 g of fumed silica (Aerosil-200), 1.19 kg dipropylamine (Aldrich, 99%) and 1.5 kg deionized water.
  • the silica-containing mixture is added slowly with stirring and stirred until homogeneous.
  • a further 2.5 kg of deionized water is added and the mixture is stirred until homogenous.
  • a portion of the resulting gel is transferred to 5 gallon autoclave where it is aged at 38° C. for 24 hours. This is then heated in the autoclave for 24 hours at 200° C.
  • the crystalline product is recovered via filtration and is washed to a conductivity lower than 200 ⁇ Scm ⁇ 1 .
  • the sample is dried before calcining at 540° C. for 4 hours.
  • An NH4-form of SAPO-34 is prepared by exchanging 350 g of the calcined SAPO-34 in a solution of ammonium nitrate (1750 g 54 wt % ammonium nitrate mixed with 1750 g of deionized water). The pH is adjusted to 4 by addition of ammonium hydroxide prior to heating the solution to 80° C. The exchange is carried out by agitating the slurry at 80° C. for 1 hour. The solid is then filtered on a Buchner filter and washed until the filtrate had a conductivity lower than 200 ⁇ Scm ⁇ 1. The powder is then dried for 16 hours before carrying out the above ammonium exchange process for a total of two exchanges.
  • a Cu-SAPO34 powder catalyst is prepared by mixing 350 g of NH4+-form SAPO-34, with 1.31 L of a copper(II) sulfate solution of 1.0 M.
  • An ion-exchange reaction between the NH4+-form SAPO-34 and the copper ions is carried out by agitating the slurry at 70° C. for 1 hour.
  • the resulting mixture is then filtered, washed until the filtrate had a conductivity of lower than 200 ⁇ Scm ⁇ 1 , which indicated that substantially no soluble or free copper remained in the sample, and the washed sample is dried at 90° C.
  • the above process including the ion-exchange, filtering, washing and drying is repeated to give a total of 2 exchanges.
  • a SAPO-34 is prepared from a gel composition of 1.0 Al2O3:1.06 P2O5:1.08 SiO2:1.05 Pr2NH:1.05 DEA:66 H 2 O.
  • a reaction mixture is formed by combining 1.54 kg of 85 wt. % orthophosphoric acid with a mixture of 920 g of a pseudoboehmite alumina (Catapal B) in 1.8 kg of deionized water. Then a further 1 kg of deionized water is added. The mixture is stirred until homogeneous.
  • An NH4-form of SAPO-34 is prepared by exchanging 350 g of the calcined SAPO-34 in a solution of ammonium nitrate (1750 g 54 wt % ammonium nitrate mixed with 1750 g of deionized water). The pH is adjusted to 4 by addition of ammonium hydroxide prior to heating the solution to 80° C. The exchange is carried out by agitating the slurry at 80° C. for 1 hour. The solid is then filtered on a Buchner filter and washed until the filtrate had a conductivity lower than 200 ⁇ Scm ⁇ 1 . The powder is then dried for 16 hours before carrying out the above ammonium exchange process for a total of two exchanges.
  • a Cu-SAPO34 powder catalyst is prepared by mixing 350 g of NH4+-form SAPO-34, with 1.31 L of a copper(II) sulfate solution of 1.0 M.
  • An ion-exchange reaction between the NH4+-form SAPO-34 and the copper ions is carried out by agitating the slurry at 70° C. for 1 hour.
  • the resulting mixture is then filtered, washed until the filtrate had a conductivity of lower than 200 ⁇ Scm ⁇ 1, which indicated that substantially no soluble or free copper remained in the sample, and the washed sample is dried at 90° C.
  • the above process including the ion-exchange, filtering, washing and drying is repeated to give a total of 2 exchanges.
  • a SAPO-34 is prepared from a gel composition of 1.0 Al 2 O3:1.06 P2O5:1.08 SiO2:1.05 Pr3N:0.53 (TEA)2O:66 H2O.
  • a reaction mixture is formed by combining 1.54 kg of 85 wt. % orthophosphoric acid with a mixture of 920 g of a pseudoboehmite alumina (Catapal B) in 1.8 kg of deionized water. Then a further 1 kg of deionized water is added. The mixture is stirred until homogeneous.
  • An NH4-form of SAPO-34 is prepared by exchanging 350 g of the calcined SAPO-34 in a solution of ammonium nitrate (1750 g 54 wt % ammonium nitrate mixed with 1750 g of deionized water). The pH is adjusted to 4 by addition of ammonium hydroxide prior to heating the solution to 80° C. The exchange is carried out by agitating the slurry at 80° C. for 1 hour. The solid is then filtered on a Buchner filter and washed until the filtrate had a conductivity lower than 200 ⁇ Scm ⁇ 1. The powder is then dried for 16 hours before carrying out the above ammonium exchange process for a total of two exchanges.
  • a Cu-SAPO34 powder catalyst is prepared by mixing 350 g of NH4+-form SAPO-34, with 1.31 L of a copper(II) sulfate solution of 1.0 M.
  • An ion-exchange reaction between the NH4+-form SAPO-34 and the copper ions is carried out by agitating the slurry at 70° C. for 1 hour.
  • the resulting mixture is then filtered, washed until the filtrate had a conductivity of lower than 200 ⁇ Scm ⁇ 1, which indicated that substantially no soluble or free copper remained in the sample, and the washed sample is dried at 90° C.
  • the above process including the ion-exchange, filtering, washing and drying is repeated to give a total of 2 exchanges.
  • a SAPO-34 was prepared from a gel composition of 1.0 Al 2 O 3 :0.85 P2O5:0.60 SiO2:3.0 R:32 H2O.
  • a reaction mixture was prepared by mixing 45 kg of DI water and 18.76 kg of phosphoric acid. This was followed by the addition of 10.80 kg of Catapal B alumina to the acid solution over 45 minutes. The alumina digestion was continued for 2 hrs with intensive stirring. Then 22.74 kg of Morpholine was added over a period of 60 minutes. An additional 0.3 kg of water was used at this stage. Upon addition of Morpholine, the temperature rose to approx. 46° C. The slurry was cooled down to approx. 28° C. before the next addition. Then, 7.76 kg of Ludox AS 40 colloidal silica was added, as well as an additional 0.50 kg of DI water. The resulting gel was transferred to a 30 gallon reactor and an additional 2.20 kg of DI water was added.
  • the reactor temperature was ramped up to 170° C. within 8 hours, and held at this temperature for 48 hours.
  • the crystalline product was recovered via filtration and was washed to a conductivity lower than 200 ⁇ Scm ⁇ 1.
  • This product was calcined at 540° C. for 6 hours.
  • the crystalline product had an X-ray powder diffraction pattern indicating that it was SAPO-34, a non-zeolitic molecular sieve with the chabazite topology.
  • the product consisted of crystals in the 3 to 10 ⁇ m range.
  • the elemental analysis of the calcined product showed 15.5% SiO2, 40.3% Al 2 O 3 , and 44.2% P2O5.
  • the BET surface area was 583 m2/g.
  • An NH4-form of SAPO-34 was prepared by exchanging 400 g of the calcined SAPO-34 in a solution of ammonium nitrate (2000 g 60 wt % ammonium nitrate mixed with 2000 g of deionized water). The exchange was carried out by agitating the slurry at 80° C. for 1 hour, with the initial pH adjusted to 3.0-3.5 using NH4OH. The solid was then filtered and washed until the filtrate had a conductivity lower than 200 ⁇ Scm ⁇ 1.
  • a Cu-SAPO34 powder catalyst was prepared by ion exchange of the NH4+-form SAPO-34 with a copper (II) acetate solution.
  • the latter solution was prepared by dissolving 63.48 g of copper (II) acetate (Aldrich) in 1590 g DI water.
  • the solution was heated to 70° C., and 400 g NH4-SAPO-34 was then added.
  • the pH was measured to be 4.49 at 70° C. No adjustment was made to the pH. This was allowed to react at 70° C. for one hour.
  • the final pH of the slurry was determined to be 4.03 at 79° C.
  • the resulting mixture was then filtered, washed until the filtrate had a conductivity lower than 200 ⁇ Scm ⁇ 1, which indicated that substantially no soluble or free copper remained in the sample, and the washed sample was dried at 90° C.
  • the obtained Cu-SAPO34 catalyst had a copper content of 2.71% by weight, expressed at CuO, as determined by ICP analysis.
  • This Cu-SAPO-34 sample had a BET surface area of 486 m2/g.
  • Two separate samples obtained were hydrothermally aged at 850° C. for 6 hours and 900° C. for 1 hour. After aging, the powder in 10% steam at 850° C. for 6 hours, it had a BET surface area of 550 m2/g.
  • FIG. 7 is a graph showing the NOx Conversion and N2O formation versus aging temperatures for this sample.
  • the NOx conversion at 200° C. for the fresh sample was 90% and for the sample aged at 850° C., the NOx conversion was 93%, and for the sample age at 900° C., the NOx conversion was 90%.
  • the N2O make for the fresh sample at 200° C. was 0.4 ppm, and the maximum value over the range of 200° C. to 450° C. was 2 ppm. For the sample aged at 850° C. the N2O make at 200° C.
  • a large scale preparation of SAPO-34 was carried out in a similar fashion as that described in Example 11.
  • the primary difference was the quantities of the ingredients, which were as follows: 3,433 kg DI water, 1,582 kg H3PO4, 970 kg Catapal B alumina, 1,910 kg Morpholine, 657 kg Ludox AS-40, and an additional 630 kg DI water for rinsing and flushing throughout the process.
  • the reactor temperature was ramped up to 169° C. within 8 hours. It was held in the 168-171° C. range for 48.5 hours.
  • the X-ray diffraction pattern identified the product as SAPO-34, with a small amount (less than 5%) of a secondary phase with the sodalite structure.
  • the calcined powder had a BET surface area of 550 m2/g.
  • An NH4-form of SAPO-34 was prepared by exchanging 400 g of the calcined SAPO-34 in a solution of ammonium nitrate (2000 g 60 wt % ammonium nitrate mixed with 2000 g of deionized water). The exchange was carried out by agitating the slurry at 80° C. for 1 hour, with the initial pH adjusted to 3.0-3.5 using NH4OH. The solid was then filtered and washed until the filtrate had a conductivity lower than 200 ⁇ Scm ⁇ 1 .
  • a Cu-SAPO34 powder catalyst was prepared by ion exchange of the NH4+-form SAPO-34 with a copper (II) acetate solution.
  • the latter solution was prepared by dissolving 63.48 g of copper (II) acetate (Aldrich) in 1590 g DI water.
  • the solution was heated to 70° C., and 400 g NH 4 -SAPO-34 was then added.
  • the pH was measured to be 4.57 at 66° C. No adjustment was made to the pH. This was allowed to react at 70° C. for one hour.
  • the final pH of the slurry was determined to be 4.14 at 74° C.
  • the resulting mixture was then filtered, washed until the filtrate had a conductivity lower than 200 ⁇ Scm ⁇ 1 , which indicated that substantially no soluble or free copper remained in the sample, and the washed sample was dried at 90° C.
  • the obtained Cu-SAPO34 catalyst had a copper content 2.72% by weight, expressed at CuO, as determined by ICP analysis.
  • This Cu-SAPO-34 sample had a BET surface area of 462 m2/g. After aging the powder in 10% steam at 850° C. for 6 hours, it had a BET surface area of 527 m2/g.
  • FIG. 8 is a graph showing the NOx Conversion and N2O formation versus aging temperatures for this sample.
  • a fresh sample showed NOx conversion at 200° C. of 88%, and NOx conversion at 200° C. for the sample aged at 850° C. was 89%.
  • the N2O make for the fresh sample at 200° C. was 0.2 ppm, and the maximum value over the range of 200° C. to 450° C. was 2 ppm.
  • the N2O make at 200° C. was 2 ppm, and the maximum value over the range of 200° C. to 450° C. was 3 ppm.
  • a SAPO-34 was prepared from a gel composition of 1.0 Al 2 O 3 :0.93 P2O5:0.96 SiO2:3.0 R:32H2O.
  • a reaction mixture was prepared by mixing 37 kg of DI water and 17.65 kg of phosphoric acid. This was followed by the addition of 9.18 kg of Catapal B alumina to the acid solution over 30 minutes. The alumina digestion was continued for 2 hrs with intensive stirring. Then 19.24 kg of Morpholine was added over a period of 15 minutes. An additional 0.3 kg of water was used at this stage. Upon addition of Morpholine, the temperature rose to approx. 75° C. The slurry was cooled down to approx. 38° C. before the next addition. Then, 10.53 kg of Ludox AS 40 colloidal silica was added, as well as an additional 0.52 kg of DI water. The resulting gel was transferred to a 30 gallon reactor and an additional 2.5 kg of DI water was added.
  • the reactor temperature was ramped up to 170° C. within 8 hours, and held at this temperature for 48 hours.
  • the crystalline product was recovered via filtration and was washed to a conductivity lower than 200 ⁇ Scm ⁇ 1 .
  • This product was calcined at 540° C. for 6 hours.
  • the crystalline product had an X-ray powder diffraction pattern indicating that it was SAPO-34, a non-zeolitic molecular sieve with the chabazite topology.
  • the product consisted of crystals in the 3 to 10 ⁇ m range.
  • the elemental analysis of the calined product showed 18.4% SiO 2 , 40.8% Al 2 O 3 , and 40.8% P2O5.
  • the calcined powder had a BET surface area of 382 m2/g. After aging the powder in 10% steam at 900° C. for 1 hour, it had a BET surface area of 344 m2/g.
  • An NH4-form of SAPO-34 was prepared by exchanging 274 g of the calcined SAPO-34 in a solution of ammonium nitrate (1370 g 60 wt % ammonium nitrate mixed with 1370 g of deionized water). The exchange was carried out by agitating the slurry at 80° C. for 1 hour, with the initial pH adjusted to 3.0-3.5 using NH4OH. The solid was then filtered and washed until the filtrate had a conductivity lower than 200 ⁇ Scm ⁇ 1.
  • a Cu-SAPO34 powder catalyst was prepared by ion exchange of the NH4+-form SAPO-34 with a copper (II) acetate solution.
  • the latter solution was prepared by dissolving 31.74 g of copper (II) acetate (Aldrich) in 795 g DI water.
  • the solution was heated to 70° C., and 200 g NH4-SAPO-34 was then added.
  • the pH was measured to be 4.53 at the beginning. No adjustment was made to the pH. This was allowed to react at 70° C. for one hour.
  • the final pH of the slurry was determined to be 4.02.
  • the resulting mixture was then filtered, washed until the filtrate had a conductivity lower than 200 ⁇ Scm ⁇ 1 , which indicated that substantially no soluble or free copper remained in the sample, and the washed sample was dried at 90° C.
  • the obtained Cu-SAPO34 catalyst had a copper content 2.89% by weight, expressed at CuO, as determined by ICP analysis.
  • FIG. 9 is a graph showing the NOx Conversion and N2O formation versus aging conditions for this sample.
  • the fresh sample exhibited NOx conversion of greater than 85% and nearly 90% at 200° C. and higher over the range of 200° C. to 450° C.
  • the N2O make for the fresh sample at 200° C. was 0.3 ppm, and the maximum value over the range of 200° C. to 450° C. was 2 ppm.
  • the N2O make at 200° C. was 3 ppm, and the maximum value over the range of 200° C. to 450° C. was 3 ppm.
  • a SAPO-34 was prepared from a gel composition of 1.0 Al 2 O 3 :0.93 P2O5:0.96 SiO2:3.0 R:32 H 2 O.
  • a reaction mixture was prepared by mixing 37 kg of DI water and 17.65 kg of phosphoric acid. This was followed by the addition of 9.18 kg of Catapal B alumina to the acid solution over 30 minutes. The alumina digestion was continued for 2 hrs with intensive stirring. Then 19.24 kg of Morpholine was added over a period of 15 minutes. An additional 0.3 kg of water was used at this stage. Upon addition of Morpholine, the temperature rose to approx. 75° C. The slurry was cooled down to approx. 38° C. before the next addition. Then, 10.53 kg of Ludox AS 40 colloidal silica was added, as well as an additional 0.52 kg of DI water. The resulting gel was transferred to a 30 gallon reactor and an additional 2.5 kg of DI water was added.
  • the reactor temperature was ramped up to 170° C. within 8 hours, and held at this temperature for 48 hours.
  • the crystalline product was recovered via filtration and was washed to a conductivity lower than 200 ⁇ Scm ⁇ 1 .
  • This product was calcined at 540° C. for 6 hours.
  • the crystalline product had an X-ray powder diffraction pattern indicating that it was SAPO-34, a non-zeolitic molecular sieve with the chabazite topology.
  • the product consisted of crystals in the 3 to 10 ⁇ m range.
  • the elemental analysis of the calcined product showed 18.4% SiO2, 40.8% Al 2 O 3 , and 40.8% P2O5.
  • the calcined powder had a BET surface area of 382 m2/g. After aging the powder in 10% steam at 900° C. for 1 hour, it had a BET surface area of 344 m2/g.
  • An NH4-form of SAPO-34 was prepared by exchanging 274 g of the calcined SAPO-34 in a solution of ammonium nitrate (1370 g 60 wt % ammonium nitrate mixed with 1370 g of deionized water). The exchange was carried out by agitating the slurry at 80° C. for 1 hour, with the initial pH adjusted to 3.0 using NH4OH. The final pH was 2.45. The solid was then filtered and washed until the filtrate had a conductivity lower than 200 ⁇ Scm ⁇ 1.
  • a Cu-SAPO34 powder catalyst was prepared by ion exchange of the NH4+-form SAPO-34 with a copper (II) acetate solution.
  • the latter solution was prepared by dissolving 15.87 g of copper (II) acetate (Aldrich) in 795 g DI water.
  • the solution was heated to 70° C., and 200 g NH4-SAPO-34 was then added.
  • the pH was measured to be 4.51 at the beginning. No adjustment was made to the pH. This was allowed to react at 70° C. for one hour.
  • the resulting mixture was then filtered, washed until the filtrate had a conductivity lower than 200 ⁇ Scm ⁇ 1 , which indicated that substantially no soluble or free copper remained in the sample, and the washed sample was dried at 90° C.
  • the obtained Cu-SAPO34 catalyst had a copper content 1.93% by weight, expressed at CuO, as determined by ICP analysis.
  • This Cu-SAPO-34 sample had a BET surface area of 337 m2/g. After aging the powder in 10% steam at 900° C. for 1 hour, it had a BET surface area of 295 m2/g.
  • FIG. 10 is a graph showing the NOx conversion and N2O formation for the aged sample.
  • a NOx conversion analysis for a fresh sample was not conducted.
  • the NOx conversion at 200° C. was at least about 75%, and the conversion in the range of 250° C. to 450° C. was greater than 85%.
  • the N2O make of the aged sample was 2.6 ppm at 200° C. and the maximum value over the range of 200° C. to 450° C. 3 ppm.
  • Cu-SAPO-34 materials in accordance with embodiment of the present invention exhibit excellent NOx conversion for fresh and aged samples exceeding 80%, 85% and 90%, with a NOx conversion retention after aging of at least 85%, at least 90% and at least 95% after aging at either 850° C. for 6 hours or 900° C. for 1 hour.
  • the ratio of NOx (with NOx referring to NO and NO 2 ) in an exhaust gas stream after passing through the catalyst to N2O in the gas stream after passing through the Cu-SAPO-34 catalyst material is less than great than 2.5:1, more specifically 5:1, and even more specifically
  • a zeolitic CuCHA catalyst comprising 3.36% CuO by weight was prepared as follows followed by an incipient wetness impregnation.
  • a zeolitic CuCHA powder catalyst was prepared by mixing 17 Kg of commercially available NH4+-form CHA zeolite, having a silica/alumina mole ratio of 30, with 68 L of a copper(II) sulfate solution of 1.0 M. The pH was adjusted to 3.5 with nitric acid. An ion-exchange reaction between the NH4+-form CHA and the copper ions was carried out by agitating the slurry at 80° C. for 1 hour. The resulting mixture was then filtered and air-dried.
  • a CuCHA slurry was prepared by mixing 90 g of CuCHA, as described above, with 215 mL of deionized water. The mixture was ball-milled. 15.8 g of zirconyl acetate in dilute acetic acid (containing 30% ZrO2) was added into the slurry with agitation.
  • the slurry was coated onto 1′′D ⁇ 3′′L cellular ceramic cores, having a cell density of 400 cpsi (cells per square inch) and a wall thickness of 6.5 mil.
  • the coated cores were dried at 110° C. for 3 hours and calcined at 400° C. for 1 hour.
  • the coating process was repeated once to obtain a target washcoat loading of 2.4 g/in3.
  • a copper sulfate solution comprised of 1.64 g of copper sulfate pentahydrate and 105 mL of deionized water.
  • the impregnated sample was dried at 90° C. and calcined at 640° C. for 6 hours.
  • a Cu/Y zeolite powder catalyst was prepared having silica/alumina mole ratio of ⁇ 5 as described further below.
  • a Cu/Y powder catalyst was prepared by mixing 500 g of NH4+-form Zeolite Y, having a silica/alumina mole ratio of 5, with 2500 mL of a copper(II) sulfate solution of 0.1 M. The pH was between 2.9 and 3.3. An ion-exchange reaction between the NH4+-form Y zeolite and the copper ions was carried out by agitating the slurry at 80° C. for 1 hour. The resulting mixture was then filtered, washed with deionized water and dried at 90° C. The above process including the ion-exchange, filtering, washing and drying was repeated for a total of 5 exchanges where pH was similar to above. The resulting Cu Zeolite Y product was then calcined at 640° C. in air for 16 hours. The obtained Cu Zeolite Y catalyst comprised CuO at 4.60% by weight.
  • the Cu/Y slurry was prepared by mixing 200 g of Cu/Y, as described above, with 400 mL of deionized water. The mixture was milled by passing twice through an Eigermill to obtain a slurry which comprised 90% particles smaller than 8 ⁇ m. 8.7 g of zirconyl acetate in dilute acetic acid (containing 30% ZrO2) was added into the slurry with agitation.
  • the slurry was coated onto 1′′D ⁇ 3′′L cellular ceramic cores, having a cell density of 400 cpsi (cells per square inch) and a wall thickness of 6.5 mil. Two coats were required to obtain a target washcoat loading of 1.6 g/in3.
  • the coated cores were dried at 90° C. for 3 hours, and the cores were calcined at 450° C. for 1 hour after the second drying step.
  • hydrothermal aging and SCR evaluation are the same as outlined in Example 1, except aging at was performed 750° C. for 25 hours.
  • a Cu/Beta powder catalyst was prepared having silica/alumina mole ratio is 35 using a procedure similar to the sample prepared in comparative EXAMPLE 15.
  • the hydrothermal aging and SCR evaluation are the same as outlined in Example 1.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Health & Medical Sciences (AREA)
  • Combustion & Propulsion (AREA)
  • Organic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Biomedical Technology (AREA)
  • Environmental & Geological Engineering (AREA)
  • Analytical Chemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • General Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Toxicology (AREA)
  • Catalysts (AREA)
  • Exhaust Gas Treatment By Means Of Catalyst (AREA)
  • Silicates, Zeolites, And Molecular Sieves (AREA)
  • Exhaust Gas After Treatment (AREA)
US12/361,980 2008-01-31 2009-01-29 Catalysts, Systems and Methods Utilizing Non-Zeolitic Metal-Containing Molecular Sieves Having the CHA Crystal Structure Abandoned US20090196812A1 (en)

Priority Applications (10)

Application Number Priority Date Filing Date Title
US12/361,980 US20090196812A1 (en) 2008-01-31 2009-01-29 Catalysts, Systems and Methods Utilizing Non-Zeolitic Metal-Containing Molecular Sieves Having the CHA Crystal Structure
BRPI0906992-5A BRPI0906992B1 (pt) 2008-01-31 2009-01-30 “processo para sintetizar cu-sapo-34 e para reduzir óxidos de nitrogênio contidos em uma corrente gasosa na presença de oxigênio, catalisador de peneira molecular não zeolítica, compósito de catalisador, e, sistemas de tratamento de gás de escapamento e de tratamento de emissão”
JP2010545198A JP2011510899A (ja) 2008-01-31 2009-01-30 Ｃｈａ結晶構造を有する分子篩を含む非沸石系金属を利用する触媒、システム、および方法
CN2009801121392A CN101983103A (zh) 2008-01-31 2009-01-30 利用具有cha晶体结构的非沸石的含金属分子筛的催化剂、系统和方法
ARP090100315A AR071555A1 (es) 2008-01-31 2009-01-30 Catalizadores, sistemas y metodos en los que se utilizan tamices moleculares no zeoliticos que contienen metales con la estructura cristalina cha
PCT/US2009/032610 WO2009099937A1 (en) 2008-01-31 2009-01-30 Catalysts, systems and methods utilizing non-zeolitic metal-containing molecular sieves having the cha crystal structure
US13/214,391 US10105649B2 (en) 2008-01-31 2011-08-22 Methods utilizing non-zeolitic metal-containing molecular sieves having the CHA crystal structure
US13/214,445 US8617474B2 (en) 2008-01-31 2011-08-22 Systems utilizing non-zeolitic metal-containing molecular sieves having the CHA crystal structure
JP2014043814A JP2014139440A (ja) 2008-01-31 2014-03-06 Ｃｈａ結晶構造を有する分子篩を含む非沸石系金属を利用する触媒、システム、および方法
US16/129,053 US20190015783A1 (en) 2008-01-31 2018-09-12 Methods Utilizing Non-Zeolitic Metal-Containing Molecular Sieves Having The CHA Crystal Structure

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US2494608P 2008-01-31 2008-01-31
US12/361,980 US20090196812A1 (en) 2008-01-31 2009-01-29 Catalysts, Systems and Methods Utilizing Non-Zeolitic Metal-Containing Molecular Sieves Having the CHA Crystal Structure

Related Child Applications (2)

Application Number Title Priority Date Filing Date
US13/214,391 Division US10105649B2 (en) 2008-01-31 2011-08-22 Methods utilizing non-zeolitic metal-containing molecular sieves having the CHA crystal structure
US13/214,445 Division US8617474B2 (en) 2008-01-31 2011-08-22 Systems utilizing non-zeolitic metal-containing molecular sieves having the CHA crystal structure

Publications (1)

Publication Number Publication Date
US20090196812A1 true US20090196812A1 (en) 2009-08-06

Family

ID=40931892

Family Applications (4)

Application Number Title Priority Date Filing Date
US12/361,980 Abandoned US20090196812A1 (en) 2008-01-31 2009-01-29 Catalysts, Systems and Methods Utilizing Non-Zeolitic Metal-Containing Molecular Sieves Having the CHA Crystal Structure
US13/214,391 Active US10105649B2 (en) 2008-01-31 2011-08-22 Methods utilizing non-zeolitic metal-containing molecular sieves having the CHA crystal structure
US13/214,445 Active US8617474B2 (en) 2008-01-31 2011-08-22 Systems utilizing non-zeolitic metal-containing molecular sieves having the CHA crystal structure
US16/129,053 Abandoned US20190015783A1 (en) 2008-01-31 2018-09-12 Methods Utilizing Non-Zeolitic Metal-Containing Molecular Sieves Having The CHA Crystal Structure

Family Applications After (3)

Application Number Title Priority Date Filing Date
US13/214,391 Active US10105649B2 (en) 2008-01-31 2011-08-22 Methods utilizing non-zeolitic metal-containing molecular sieves having the CHA crystal structure
US13/214,445 Active US8617474B2 (en) 2008-01-31 2011-08-22 Systems utilizing non-zeolitic metal-containing molecular sieves having the CHA crystal structure
US16/129,053 Abandoned US20190015783A1 (en) 2008-01-31 2018-09-12 Methods Utilizing Non-Zeolitic Metal-Containing Molecular Sieves Having The CHA Crystal Structure

Country Status (6)

Country Link
US (4) US20090196812A1 (ja)
JP (2) JP2011510899A (ja)
CN (1) CN101983103A (ja)
AR (2) AR071555A1 (ja)
BR (1) BRPI0906992B1 (ja)
WO (1) WO2009099937A1 (ja)

Cited By (62)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090285737A1 (en) * 2007-02-27 2009-11-19 Basf Catalysts Llc Copper CHA Zeolite Catalysts
US20100092362A1 (en) * 2007-03-26 2010-04-15 Pq Corporation High silica chabazite for selective catalytic reduction, methods of making and using same
CN101797518A (zh) * 2010-04-14 2010-08-11 太原理工大学 一种柴油机车尾气净化整体式催化剂的制备方法
US20110118108A1 (en) * 2009-11-19 2011-05-19 Ibiden Co., Ltd. Honeycomb structural body and manufacturing method of honeycomb structural body
US20110165051A1 (en) * 2009-12-18 2011-07-07 Basf Corporation Process Of Direct Copper Exchange Into Na+-Form Of Chabazite Molecular Sieve, And Catalysts, Systems And Methods
US20110165052A1 (en) * 2009-12-18 2011-07-07 Basf Corporation Process for Preparation of Copper Containing Molecular Sieves With the CHA Structure, Catalysts, Systems and Methods
US20110207598A1 (en) * 2009-12-18 2011-08-25 Jgc Catalysts And Chemicals Ltd. Metal-supported crystalline silica aluminophosphate catalyst and process for producing the same
US20120020875A1 (en) * 2009-01-22 2012-01-26 Mitsubishi Plastics, Inc. Catalyst for reducing nitrogen oxides and method for producing the same
US20120058018A1 (en) * 2010-09-02 2012-03-08 Ibiden Co., Ltd. Silico-alumino phosphate, honeycomb structural body and exhaust gas conversion apparatus
WO2012059145A1 (en) * 2010-11-02 2012-05-10 Haldor Topsøe A/S Method for the preparation of a catalysed particulate filter and catalysed particulate filter
WO2012059144A1 (en) * 2010-11-02 2012-05-10 Haldor Topsøe A/S Method for the preparation of a catalysed particulate filter and catalysed particulate filter
EP2463028A1 (en) * 2010-12-11 2012-06-13 Umicore Ag & Co. Kg Process for the production of metal doped zeolites and zeotypes and application of same to the catalytic removal of nitrogen oxides
WO2012080318A1 (de) * 2010-12-16 2012-06-21 Umicore Ag & Co. Kg Kupfer-chabazit-basierter katalysator mit verbesserter katalytischer aktivitaet zur reduktion von stickoxiden
WO2012138405A1 (en) * 2011-04-08 2012-10-11 Johnson Matthey Public Limited Company Catalysts for the reduction of ammonia emission from rich-burn exhaust
US20120269719A1 (en) * 2011-04-18 2012-10-25 Pq Corporation Large crystal, organic-free chabazite, methods of making and using the same
US20120301381A1 (en) * 2007-04-26 2012-11-29 Johnson Matthey Public Limited Company Transition metal/zeolite scr catalysts
GB2497656A (en) * 2011-12-12 2013-06-19 Johnson Matthey Plc Substrate monolith comprising SCR catalyst and trap for gas phase PGM
US8617474B2 (en) 2008-01-31 2013-12-31 Basf Corporation Systems utilizing non-zeolitic metal-containing molecular sieves having the CHA crystal structure
US20140010722A1 (en) * 2011-03-08 2014-01-09 Mitsubishi Plastics, Inc. Catalyst, device for removing nitrogen oxide, and system for removing nitrogen oxide
US8667785B2 (en) 2011-12-12 2014-03-11 Johnson Matthey Public Limited Company Catalysed substrate monolith
US8668891B2 (en) 2011-12-12 2014-03-11 Johnson Matthey Public Limited Company Exhaust system for a lean-burn IC engine comprising a PGM component and a SCR catalyst
US20140112835A1 (en) * 2011-08-18 2014-04-24 Ibiden Co., Ltd. Honeycomb structure, method for producing same, exhaust gas purification device and silicoaluminophosphate particles
US8735311B2 (en) 2007-02-27 2014-05-27 Basf Corporation Copper CHA zeolite catalysts
EP2746224A1 (en) * 2011-08-18 2014-06-25 Ibiden Co., Ltd Silicoaluminophosphate particles, honeycomb structure, method for producing same, and exhaust gas purification device
WO2014160293A1 (en) * 2013-03-14 2014-10-02 Basf Corporation Selective catalytic reduction catalyst systems
WO2014160289A1 (en) * 2013-03-14 2014-10-02 Basf Corporation Selective catalytic reduction catalyst system
US8883119B2 (en) 2009-11-24 2014-11-11 Basf Se Process for the preparation of zeolites having CHA structure
US8987161B2 (en) 2010-08-13 2015-03-24 Ut-Battelle, Llc Zeolite-based SCR catalysts and their use in diesel engine emission treatment
US9005559B2 (en) 2011-10-06 2015-04-14 Johnson Matthey Public Limited Company Oxidation catalyst for internal combustion engine exhaust gas treatment
US20150118134A1 (en) * 2012-04-27 2015-04-30 Haldor Topsøe A/S Method and system for the purification of exhaust gas from an internal combustion engine
JP2015093209A (ja) * 2013-11-08 2015-05-18 トヨタ自動車株式会社 排ガス浄化用触媒
EP2659975A4 (en) * 2010-12-27 2015-06-17 Mitsubishi Plastics Inc CATALYST FOR REMOVING NITROGEN OXIDE
GB2522527A (en) * 2013-12-02 2015-07-29 Johnson Matthey Plc Mixed template synthesis of high silica Cu-CHU
CN105008048A (zh) * 2013-03-13 2015-10-28 巴斯夫公司 稳定的金属交换的sapo材料
US9242239B2 (en) 2011-04-08 2016-01-26 Johnson Matthey Public Limited Company Catalysts for the reduction of ammonia emission from rich-burn exhaust
US9259684B2 (en) 2011-12-12 2016-02-16 Johnson Matthey Public Limited Company Exhaust system for a lean-burn internal combustion engine including SCR catalyst
US9321009B2 (en) 2009-04-03 2016-04-26 Basf Corporation Emissions treatment system with ammonia-generating and SCR catalysts
CN105688980A (zh) * 2016-03-10 2016-06-22 镇江翰宏新材料科技有限公司 一种分子筛负载scr催化剂的制备方法
US9410463B2 (en) * 2011-08-18 2016-08-09 Ibiden Co., Ltd. Composite particles, honeycomb structure, method for manufacturing honeycomb structure, and exhaust gas purifying apparatus
US20160230631A1 (en) * 2015-02-11 2016-08-11 GM Global Technology Operations LLC Selective catalytic reduction device
US9527751B2 (en) 2011-11-11 2016-12-27 Basf Se Organotemplate-free synthetic process for the production of a zeolitic material of the CHA-type structure
US9670415B2 (en) 2011-09-06 2017-06-06 Basf Se Synthesis of zeolitic materials using N,N-dimethyl organotemplates
EP3060339A4 (en) * 2013-10-24 2017-06-28 W.R. Grace & CO. - CONN. Method for synthesizing silicoaluminophosphate-34 molecular sieves
US9782761B2 (en) 2013-10-03 2017-10-10 Ford Global Technologies, Llc Selective catalytic reduction catalyst
EP2995367B1 (en) 2009-04-17 2017-12-20 Johnson Matthey Public Limited Company Small pore molecular sieve supported copper catalysts durable against lean/rich aging for the reduction of nitrogen oxides
US9895660B2 (en) 2014-04-07 2018-02-20 Haldor Topsoe A/S Method for producing metal exchanged microporous materials by solid-state ion exchange
US9914114B2 (en) 2014-04-07 2018-03-13 Haldor Topsoe A/S Method for producing metal exchanged metallo-aluminophosphates by solid-state ion exchange at low temperatures
GB2521576B (en) * 2012-10-18 2018-06-27 Johnson Matthey Plc Close-coupled SCR system
CN109081360A (zh) * 2017-06-13 2018-12-25 中国石油化工股份有限公司 分子筛scm-14、其合成方法及其用途
CN109250728A (zh) * 2017-07-12 2019-01-22 中国科学院大连化学物理研究所 Cu-SAPO分子筛合成方法及合成的Cu-SAPO分子筛和应用
CN110392606A (zh) * 2017-02-22 2019-10-29 巴斯夫公司 用于减少氮氧化物的废气处理催化剂
US10570802B2 (en) * 2015-07-09 2020-02-25 Umicore Ag & Co. Kg System for the removal of particulate matter and noxious compounds from engine exhaust gas
GB2577001A (en) * 2016-04-11 2020-03-11 Johnson Matthey Plc Method of coating a substrate with a particle stabilized foam
EP2567081B1 (en) 2010-05-05 2020-07-08 BASF Corporation Integrated scr and amox catalyst systems
CN113318782A (zh) * 2021-05-28 2021-08-31 江西农业大学 一种富锰的Mn-SAPO-18分子筛催化剂的制备方法及其用途
CN113766973A (zh) * 2019-05-15 2021-12-07 株式会社Acr 催化剂、催化剂产品以及催化剂的制造方法
CN113856749A (zh) * 2021-08-26 2021-12-31 中汽研（天津）汽车工程研究院有限公司 一种钐基cha分子筛催化剂及应用
CN114177935A (zh) * 2021-10-14 2022-03-15 凯龙蓝烽新材料科技有限公司 一种用于柴油车尾气净化的scr催化剂
US11305266B2 (en) * 2020-01-03 2022-04-19 Hyundai Motor Company Catalyst and manufacturing method thereof
US11590482B1 (en) * 2011-06-17 2023-02-28 Johnson Matthey Public Limited Company Alumina binders for SCR catalysts
CN115739174A (zh) * 2022-11-15 2023-03-07 昆明理工大学 一种抗水热稳定性脱硝催化剂及其制备方法和应用、整体式催化剂及其应用
CN115739172A (zh) * 2022-12-02 2023-03-07 润和科华催化剂(上海)有限公司 一种协同脱除n2o和no的催化剂及其制备方法

Families Citing this family (73)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2464478A (en) 2008-10-15 2010-04-21 Johnson Matthey Plc Aluminosilicate zeolite catalyst and use thereof in exhaust gas after-treatment
KR101477338B1 (ko) 2008-12-24 2014-12-29 바스프 코포레이션 촉매된 ｓｃｒ 필터 및 하류 ｓｃｒ 촉매를 사용한 배출물 처리 시스템 및 방법
DE102009040352A1 (de) 2009-09-05 2011-03-17 Johnson Matthey Catalysts (Germany) Gmbh Verfahren zur Herstellung eines SCR aktiven Zeolith-Katalysators sowie SCR aktiver Zeolith-Katalysator
BR112012008847A2 (pt) * 2009-10-14 2019-09-24 Basf Corp peneira molecular de levinita contendo cobre, catalisador, processo para a preparação de qualquer peneira molecular de levinita contendo cobre, usa de catalisador, sistema de tratamento de gás de descarga, e, método paea seletivamente reduzir óxidos de nitrogênio
GB2475740B (en) * 2009-11-30 2017-06-07 Johnson Matthey Plc Catalysts for treating transient NOx emissions
EP2335810B1 (de) * 2009-12-11 2012-08-01 Umicore AG & Co. KG Selektive katalytische Reduktion von Stickoxiden im Abgas von Dieselmotoren
US9352307B2 (en) 2010-04-08 2016-05-31 Basf Corporation Cu-CHA/Fe-MFI mixed zeolite catalyst and process for the treatment of NOx in gas streams
MX360154B (es) * 2010-04-08 2018-10-24 Basf Se Catalizador de zeolita mixta de cu-cha/fe-mfi y proceso para tratar nox en corriente de gas usando el mismo.
FR2962923B1 (fr) 2010-07-22 2015-01-02 Peugeot Citroen Automobiles Sa Composition catalytique et dispositif de traitement des gaz comprenant une telle composition
US8617502B2 (en) 2011-02-07 2013-12-31 Cristal Usa Inc. Ce containing, V-free mobile denox catalyst
US9409787B2 (en) 2011-06-27 2016-08-09 Mitsubishi Plastics, Inc. Transition-metal-containing zeolite
JP6320918B2 (ja) * 2011-07-27 2018-05-09 ジョンソン、マッセイ、パブリック、リミテッド、カンパニーＪｏｈｎｓｏｎ Ｍａｔｔｈｅｙ Ｐｕｂｌｉｃ Ｌｉｍｉｔｅｄ Ｃｏｍｐａｎｙ 低リンチャバサイト
US8789356B2 (en) * 2011-07-28 2014-07-29 Johnson Matthey Public Limited Company Zoned catalytic filters for treatment of exhaust gas
WO2013024548A1 (ja) * 2011-08-18 2013-02-21 イビデン株式会社 ハニカム構造体及びその製造方法、排ガス浄化装置並びにシリコアルミノホスフェート粒子
JPWO2013024547A1 (ja) * 2011-08-18 2015-03-05 イビデン株式会社 ハニカム構造体及びその製造方法、排ガス浄化装置並びにシリコアルミノホスフェート粒子
JP5573799B2 (ja) * 2011-09-06 2014-08-20 トヨタ自動車株式会社 排ガス浄化触媒およびそれを含む排ガス浄化触媒システム
WO2013035054A1 (en) * 2011-09-06 2013-03-14 Basf Se Synthesis of zeolitic materials using n,n-dimethyl organotemplates
US9999877B2 (en) 2011-10-05 2018-06-19 Basf Se Cu-CHA/Fe-BEA mixed zeolite catalyst and process for the treatment of NOx in gas streams
JP2014530097A (ja) * 2011-10-05 2014-11-17 ビーエーエスエフ ソシエタス・ヨーロピアＢａｓｆ Ｓｅ ガス流中のＮＯｘを処理するためのＣｕ−ＣＨＡ／Ｆｅ−ＢＥＡ混合ゼオライト触媒および方法
US8956992B2 (en) * 2011-10-27 2015-02-17 GM Global Technology Operations LLC SCR catalysts preparation methods
US20120258032A1 (en) * 2011-11-02 2012-10-11 Johnson Matthey Public Limited Company Catalyzed filter for treating exhaust gas
RU2612697C2 (ru) * 2011-11-11 2017-03-13 Басф Се Способ, не использующий органический шаблон, для получения цеолитного материала, обладающего структурой типа сна
US9981256B2 (en) 2011-12-02 2018-05-29 Pq Corporation Stabilized microporous crystalline material, the method of making the same, and the use for selective catalytic reduction of NOx
JP6104270B2 (ja) 2011-12-02 2017-03-29 ピーキュー コーポレイション 安定化したミクロポーラス結晶性材料、その製造方法およびＮＯｘの選択触媒還元のための使用方法
RU2017146613A (ru) * 2012-01-31 2018-10-17 Джонсон Мэтти Паблик Лимитед Компани Каталитические смеси
US20150273446A1 (en) * 2012-10-03 2015-10-01 Ibiden Co., Ltd. Honeycomb structure
EP2908946B1 (en) * 2012-10-19 2020-09-09 BASF Corporation 8-ring small pore molecular sieve as high temperature scr catalyst
JP2014122142A (ja) * 2012-12-21 2014-07-03 Mitsubishi Plastics Inc 遷移金属含有ゼオライト、及びその製造方法
FR3011487B1 (fr) 2013-10-07 2017-07-21 Peugeot Citroen Automobiles Sa Dispositif de traitement des gaz d’echappement
US20150231617A1 (en) * 2014-02-19 2015-08-20 Ford Global Technologies, Llc Fe-SAPO-34 CATALYST FOR USE IN NOX REDUCTION AND METHOD OF MAKING
JPWO2015146482A1 (ja) * 2014-03-26 2017-04-13 三菱樹脂株式会社 遷移金属含有ゼオライトの製造方法、及び該方法により得られる遷移金属ゼオライト、並びに該ゼオライトを用いた排ガス浄化処理用触媒
US10118166B2 (en) * 2014-06-06 2018-11-06 Uop Llc Zeolitic materials with modified surface composition, crystal structure, crystal size, and/or porosity, methods for making the same, and methods for converting oxygenates to olefins via reactions catalyzed by the same
CN104028299B (zh) * 2014-06-19 2016-05-18 中国石油大学(北京) 一种fcc再生烟气脱硝用铜基微孔复合分子筛基催化剂、制备方法及其用途
EP2985068A1 (de) 2014-08-13 2016-02-17 Umicore AG & Co. KG Katalysator-System zur Reduktion von Stickoxiden
JP6723223B2 (ja) * 2014-08-22 2020-07-15 ダブリュー・アール・グレース・アンド・カンパニー−コーンＷ Ｒ Ｇｒａｃｅ ＆ Ｃｏ−Ｃｏｎｎ モノイソプロパノールアミンを用いたシリコアルミノホスフェート−３４モレキュラーシーブの合成方法
CN104289115B (zh) * 2014-08-25 2016-06-01 南京工业大学 一种高硅cha型ssz-13分子筛膜的制备方法
CN104722331B (zh) * 2014-12-13 2017-02-01 济南大学 一种Cu‑SAPO‑44微孔分子筛的制备方法及其作为NH3‑SCR催化剂的应用
CN104549228A (zh) * 2015-01-12 2015-04-29 国家电网公司 一种燃煤电厂低温脱硝催化剂及制备方法
US10850267B2 (en) 2015-01-30 2020-12-01 Dalian Institute Of Chemical Physics, Chinese Academy Of Sciences Preparation method for metal-modified SAPO molecular sieve
CN105251530A (zh) * 2015-10-12 2016-01-20 华中科技大学 一种氟化氢改性一步法合成Cu-SAPO-34分子筛催化剂的制备方法
CN105233858A (zh) * 2015-10-21 2016-01-13 南京理工大学 一种均匀负载的铈基分子筛催化剂、制备方法及其用途
BR112018009908B1 (pt) * 2015-11-17 2021-11-30 Basf Corporation Composição de catalisador, artigo de catalisador, métodos para reduzir seletivamente óxidos de nitrogênio e para preparar uma composição de catalisador, e, sistema para tratamento de gás de escape
EP3205398A1 (en) 2016-02-12 2017-08-16 Hyundai Motor Company Method for preparing zeolite catalyst
US10343925B2 (en) 2016-02-12 2019-07-09 Hyundai Motor Company Method for preparing zeolite catalyst
WO2017213022A1 (ja) * 2016-06-07 2017-12-14 日揮触媒化成株式会社 高耐水熱性チャバザイト型ゼオライトおよびその製造方法
CN109562363B (zh) * 2016-06-13 2022-02-25 巴斯夫公司 催化剂复合材料及其在选择性催化还原NOx中的应用
KR101982040B1 (ko) 2016-06-21 2019-05-24 삼성전기주식회사 팬-아웃 반도체 패키지
EP3357558B1 (de) 2017-02-03 2019-06-26 Umicore Ag & Co. Kg Katalysator zur reinigung der abgase von dieselmotoren
WO2019042884A1 (de) 2017-08-31 2019-03-07 Umicore Ag & Co. Kg Verwendung eines palladium-platin-zeolith-basierten katalysators als passiver stickoxid-adsorber zur abgasreinigung
EP3450015A1 (de) 2017-08-31 2019-03-06 Umicore Ag & Co. Kg Palladium-zeolith-basierter passiver stickoxid-adsorber-katalysator zur abgasreinigung
EP3450016A1 (de) 2017-08-31 2019-03-06 Umicore Ag & Co. Kg Palladium-zeolith-basierter passiver stickoxid-adsorber-katalysator zur abgasreinigung
EP3449999A1 (de) 2017-08-31 2019-03-06 Umicore Ag & Co. Kg Passiver stickoxid-adsorber
US11141717B2 (en) 2017-08-31 2021-10-12 Umicore Ag & Co. Kg Palladium/zeolite-based passive nitrogen oxide adsorber catalyst for purifying exhaust gas
US10711674B2 (en) 2017-10-20 2020-07-14 Umicore Ag & Co. Kg Passive nitrogen oxide adsorber catalyst
CN109856313A (zh) * 2017-11-30 2019-06-07 中国科学院大连化学物理研究所 一种选择性还原脱硝催化剂的耐低温水热稳定性评价方法
WO2019134958A1 (de) 2018-01-05 2019-07-11 Umicore Ag & Co. Kg Passiver stickoxid-adsorber
US10898889B2 (en) 2018-01-23 2021-01-26 Umicore Ag & Co. Kg SCR catalyst and exhaust gas cleaning system
US10456746B2 (en) * 2018-02-12 2019-10-29 GM Global Technology Operations LLC Selective catalytic reduction filter for reducing nitrous oxide formation and methods of using the same
CN109126862A (zh) * 2018-08-20 2019-01-04 中国汽车技术研究中心有限公司 一种加快合成cha结构分子筛的方法及其催化剂在nh3-scr反应中的应用
EP3613503A1 (en) 2018-08-22 2020-02-26 Umicore Ag & Co. Kg Passive nitrogen oxide adsorber
EP3616792A1 (de) 2018-08-28 2020-03-04 Umicore Ag & Co. Kg Stickoxid-speicherkatalysator
US11439952B2 (en) 2018-11-16 2022-09-13 Umicore Ag & Co. Kg Low temperature nitrogen oxide adsorber
WO2020144195A1 (de) 2019-01-08 2020-07-16 Umicore Ag & Co. Kg Passiver stickoxid-adsorber mit oxidationskatalytisch aktiver funktion
EP3695902B1 (de) 2019-02-18 2021-09-01 Umicore Ag & Co. Kg Katalysator zur reduktion von stickoxiden
CN110227540B (zh) * 2019-05-10 2020-09-08 四川大学 Afi-cha混晶分子筛及以其为载体的nh3-scr催化剂以及它们的制备方法
EP3824988A1 (en) 2019-11-20 2021-05-26 UMICORE AG & Co. KG Catalyst for reducing nitrogen oxides
CN112827507B (zh) * 2019-11-22 2023-08-11 中冶京诚工程技术有限公司 铜锌离子交换分子筛scr催化剂及其制备方法和应用
EP3885040A1 (de) 2020-03-24 2021-09-29 UMICORE AG & Co. KG Ammoniakoxidationskatalysator
EP3978100A1 (de) 2020-09-30 2022-04-06 UMICORE AG & Co. KG Bismut enthaltender gezonter dieseloxidationskatalysator
JP2023542828A (ja) 2020-09-30 2023-10-12 ユミコア・アクチエンゲゼルシャフト・ウント・コムパニー・コマンディットゲゼルシャフト ディーゼル酸化触媒を含有するビスマット
WO2022079141A1 (en) 2020-10-14 2022-04-21 Umicore Ag & Co. Kg Passive nitrogen oxide adsorber
CN112371163B (zh) * 2020-11-12 2022-03-29 中国科学院长春应用化学研究所 一种脱硝催化剂及其制备方法
EP4063003A1 (en) 2021-03-23 2022-09-28 UMICORE AG & Co. KG Filter for the aftertreatment of exhaust gases of internal combustion engines

Citations (68)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4220632A (en) * 1974-09-10 1980-09-02 The United States Of America As Represented By The United States Department Of Energy Reduction of nitrogen oxides with catalytic acid resistant aluminosilicate molecular sieves and ammonia
US4297328A (en) * 1979-09-28 1981-10-27 Union Carbide Corporation Three-way catalytic process for gaseous streams
US4440871A (en) * 1982-07-26 1984-04-03 Union Carbide Corporation Crystalline silicoaluminophosphates
US4544538A (en) * 1982-07-09 1985-10-01 Chevron Research Company Zeolite SSZ-13 and its method of preparation
US4567029A (en) * 1983-07-15 1986-01-28 Union Carbide Corporation Crystalline metal aluminophosphates
US4735930A (en) * 1986-02-18 1988-04-05 Norton Company Catalyst for the reduction of oxides of nitrogen
US4735927A (en) * 1985-10-22 1988-04-05 Norton Company Catalyst for the reduction of oxides of nitrogen
US4753927A (en) * 1983-08-12 1988-06-28 Immunetech Pharmaceuticals Method of blocking immune complex binding to immunoglobulin Fc receptors
US4861743A (en) * 1987-11-25 1989-08-29 Uop Process for the production of molecular sieves
US4867954A (en) * 1988-04-07 1989-09-19 Uop Catalytic reduction of nitrogen oxides
US4874590A (en) * 1988-04-07 1989-10-17 Uop Catalytic reduction of nitrogen oxides
US4961917A (en) * 1989-04-20 1990-10-09 Engelhard Corporation Method for reduction of nitrogen oxides with ammonia using promoted zeolite catalysts
US5024981A (en) * 1989-04-20 1991-06-18 Engelhard Corporation Staged metal-promoted zeolite catalysts and method for catalytic reduction of nitrogen oxides using the same
US5041270A (en) * 1986-10-17 1991-08-20 Kabushiki Kaisha Toyota Chuo Kenkyusho Method of purifying exhaust gases
US5096684A (en) * 1989-03-31 1992-03-17 Elf France Process for the synthesis of precursors of molecular sieves of the silicoaluminophosphate type, precursors obtained and their application to obtaining the said molecular sieves
US5147949A (en) * 1988-03-29 1992-09-15 Exxon Chemical Patents Inc. Polymerization process using a silica gel supported metallocene-alumoxane catalyst
US5233117A (en) * 1991-02-28 1993-08-03 Uop Methanol conversion processes using syocatalysts
US5313792A (en) * 1991-09-20 1994-05-24 Toyota Jidosha Kabushiki Kaisha Exhaust gas purification apparatus for an internal combustion engine
US5417949A (en) * 1993-08-25 1995-05-23 Mobil Oil Corporation NOx abatement process
US5477014A (en) * 1989-07-28 1995-12-19 Uop Muffler device for internal combustion engines
US5589147A (en) * 1994-07-07 1996-12-31 Mobil Oil Corporation Catalytic system for the reducton of nitrogen oxides
US5589149A (en) * 1993-11-09 1996-12-31 Union Carbide Chemicals & Plastics Technology Corporation Process for absorption of mercaptans
US5733837A (en) * 1993-05-10 1998-03-31 Sakai Chemical Industry Co., Ltd. Catalyst for catalytic reduction of nitrogen oxides
US5884473A (en) * 1995-06-23 1999-03-23 Ngk Insulators, Ltd. System for exhaust gas purification and method for exhaust gas purification using said system
US6139808A (en) * 1996-12-20 2000-10-31 Ngk Insulators, Ltd. Catalyst for exhaust gas purification and system for exhaust gas purification
US6162415A (en) * 1997-10-14 2000-12-19 Exxon Chemical Patents Inc. Synthesis of SAPO-44
US6171556B1 (en) * 1992-11-12 2001-01-09 Engelhard Corporation Method and apparatus for treating an engine exhaust gas stream
US20010038812A1 (en) * 1992-11-19 2001-11-08 Yavuz Bulent O. Zeolite-containing oxidation catalyst and method of use
US6316683B1 (en) * 1999-06-07 2001-11-13 Exxonmobil Chemical Patents Inc. Protecting catalytic activity of a SAPO molecular sieve
US20010043896A1 (en) * 2000-03-01 2001-11-22 Rainer Domesle Catalyst for purifying the exhaust gases of diesel engines, and process for the preparation thereof
US20020016252A1 (en) * 1997-10-09 2002-02-07 Ngk Insulators, Ltd. Adsorbent for exhaust gas purification
US6350298B1 (en) * 1998-10-30 2002-02-26 The Boc Group, Inc. Adsorbents and adsorptive separation process
US6376562B1 (en) * 1998-12-24 2002-04-23 Korea Advanced Institute Of Science And Technology Hybrid catalyst for hydrocarbon synthesis via hydrogenation of carbon dioxide
US6395674B1 (en) * 1999-06-07 2002-05-28 Exxon Mobil Chemical Patents, Inc. Heat treating a molecular sieve and catalyst
US20020084223A1 (en) * 2000-12-28 2002-07-04 Feimer Joseph L. Removal of sulfur from naphtha streams using high silica zeolites
US6503863B2 (en) * 1999-06-07 2003-01-07 Exxonmobil Chemical Patents, Inc. Heat treating a molecular sieve and catalyst
US20030069449A1 (en) * 2001-08-30 2003-04-10 Zones Stacey I. Small crystallite zeolite CHA
US6569394B2 (en) * 1998-11-25 2003-05-27 Siemens Aktiengesellschaft Catalyst body and process for breaking down nitrogen oxides
US6576203B2 (en) * 1998-06-29 2003-06-10 Ngk Insulators, Ltd. Reformer
US6606856B1 (en) * 2000-03-03 2003-08-19 The Lubrizol Corporation Process for reducing pollutants from the exhaust of a diesel engine
US6685905B2 (en) * 2001-12-21 2004-02-03 Exxonmobil Chemical Patents Inc. Silicoaluminophosphate molecular sieves
US6696032B2 (en) * 2001-11-29 2004-02-24 Exxonmobil Chemical Patents Inc. Process for manufacturing a silicoaluminophosphate molecular sieve
US6696063B1 (en) * 1998-12-30 2004-02-24 Applied Research Systems Ars Holding N.V. Treatment of HIV-associated dysmorphia/dysmetabolic syndrome (HADDS) with or without lipodystrophy
US20040082466A1 (en) * 2001-11-30 2004-04-29 Guang Cao Method of synthesizing molecular sieves
US20040098973A1 (en) * 2002-11-21 2004-05-27 Tennison Paul Joseph Exhaust gas aftertreatment systems
US20040166035A1 (en) * 2001-07-25 2004-08-26 Naomi Noda Honeycomb structural body for exhaust emission control and honeycomb catalyst body for exhaust emission control
US20040171476A1 (en) * 2003-02-27 2004-09-02 In-Sik Nam Zeolite catalyst and preparation process for NOx reduction
US20040209760A1 (en) * 2003-04-17 2004-10-21 Ict Co., Ltd. Exhaust gas purifying catalyst and process for purifying exhaust gas by use of the catalyst
US20050031514A1 (en) * 2003-08-05 2005-02-10 Engelhard Corporation Catalyzed SCR filter and emission treatment system
US20050096214A1 (en) * 2001-03-01 2005-05-05 Janssen Marcel J. Silicoaluminophosphate molecular sieve
US6974889B1 (en) * 1998-07-29 2005-12-13 Exxonmobil Chemical Patents Inc. Processes for manufacture of molecular sieves
US20060039843A1 (en) * 2004-08-23 2006-02-23 Engelhard Corporation Zone coated catalyst to simultaneously reduce NOx and unreacted ammonia
US7014827B2 (en) * 2001-10-23 2006-03-21 Machteld Maria Mertens Synthesis of silicoaluminophosphates
US20060115403A1 (en) * 2004-11-29 2006-06-01 Chevron U.S.A. Inc. Reduction of oxides of nitrogen in a gas stream using high-silics molecular sieve CHA
US7094389B2 (en) * 2003-12-23 2006-08-22 Exxonmobil Chemical Patents Inc. Chabazite-containing molecular sieve, its synthesis and its use in the conversion of oxygenates to olefins
US20060228283A1 (en) * 2005-02-28 2006-10-12 Catalytic Solutions, Inc. Catalyst and method for reducing nitrogen oxides in exhaust streams with hydrocarbons or alcohols
US20070000243A1 (en) * 2005-06-30 2007-01-04 General Electric Company Conversion system for reducing NOx emissions
US20070043249A1 (en) * 2005-08-18 2007-02-22 Guang Cao Synthesis of molecular sieves having the chabazite framework type and their use in the conversion of oxygenates to olefins
US7182927B2 (en) * 2001-09-07 2007-02-27 Engelhard Corporation Hydrothermally stable metal promoted zeolite beta for NOx reduction
US20070149385A1 (en) * 2005-12-23 2007-06-28 Ke Liu Catalyst system for reducing nitrogen oxide emissions
US20070286798A1 (en) * 2006-06-09 2007-12-13 Guang Cao Treatment of CHA-type molecular sieves and their use in the conversion of oxygenates to olefins
US20080241060A1 (en) * 2007-03-26 2008-10-02 Hong-Xin Li Novel microporous crystalline material comprising a molecular sieve or zeolite having an 8-ring pore opening structure and methods of making and using same
US20080317999A1 (en) * 2007-01-31 2008-12-25 Joseph Patchett Gas Catalysts Comprising Porous Wall Honeycombs
US20090048095A1 (en) * 2007-08-13 2009-02-19 Hong-Xin Li Novel iron-containing aluminosilicate zeolites and methods of making and using same
US20090060809A1 (en) * 2005-03-30 2009-03-05 Sued-Chemie Catalysts Japan, Inc. Ammonia Decomposition Catalyst and Process for Decomposition of Ammonia Using the Catalyst
US7601662B2 (en) * 2007-02-27 2009-10-13 Basf Catalysts Llc Copper CHA zeolite catalysts
US20100092362A1 (en) * 2007-03-26 2010-04-15 Pq Corporation High silica chabazite for selective catalytic reduction, methods of making and using same
US20100290963A1 (en) * 2007-04-26 2010-11-18 Johnson Matthey Public Limited Company Transition metal / zeolite scr catalysts

Family Cites Families (43)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE394541C (de) 1922-10-24 1924-04-22 Gutberlet & Co A Seitenziehmarke fuer Druckpressen, Falzmaschinen u. dgl.
US3346328A (en) 1967-03-30 1967-10-10 Francis J Sergeys Method of treating exhaust gases
JPS51147470A (en) 1975-06-12 1976-12-17 Toa Nenryo Kogyo Kk A process for catalytic reduction of nitrogen oxides
JPS60125250A (ja) 1983-12-08 1985-07-04 Shiyuuichi Kagawa 窒素酸化物の接触分解触媒及びその使用方法
US5011667A (en) 1988-09-08 1991-04-30 Engelhard Corporation Self-bound sodium chabazite aggregates and methods for preparation thereof
JP2557712B2 (ja) * 1988-12-27 1996-11-27 株式会社豊田中央研究所 排気ガス浄化方法
JP2533371B2 (ja) * 1989-05-01 1996-09-11 株式会社豊田中央研究所 排気ガス浄化用触媒
JPH0557194A (ja) 1991-07-06 1993-03-09 Toyota Motor Corp 排気ガス浄化用触媒の製造方法
JP3303341B2 (ja) 1992-07-30 2002-07-22 三菱化学株式会社 ベータ型ゼオライトの製造方法
ATE191060T1 (de) 1992-11-19 2000-04-15 Engelhard Corp Anwendung und gerät zur behandlung eines maschinenabgas-stroms
JPH07155614A (ja) * 1993-12-07 1995-06-20 Toyota Motor Corp 排気ガス浄化用触媒の製造方法
JPH07232035A (ja) 1994-02-21 1995-09-05 Toray Ind Inc 窒素酸化物の浄化方法および浄化装置
US6133185A (en) 1995-11-09 2000-10-17 Toyota Jidosha Kabushiki Kaisha Exhaust gas purifying catalyst
JPH11179158A (ja) 1997-10-15 1999-07-06 Ngk Insulators Ltd 小細孔多孔体を含む自動車排ガス浄化用の吸着材及び吸着体、これを用いた排ガス浄化システム及び排ガス浄化方法
WO1999056859A1 (en) 1998-05-07 1999-11-11 Engelhard Corporation Catalyzed hydrocarbon trap and method using the same
JP3580163B2 (ja) 1998-06-04 2004-10-20 トヨタ自動車株式会社 内燃機関の排気浄化装置
US6826906B2 (en) * 2000-08-15 2004-12-07 Engelhard Corporation Exhaust system for enhanced reduction of nitrogen oxides and particulates from diesel engines
JP3571642B2 (ja) 2000-11-16 2004-09-29 トヨタ自動車株式会社 排気浄化装置用の還元剤
DE10059520A1 (de) 2000-11-30 2001-05-17 Univ Karlsruhe Verfahren zur Abtrennung von Zeolith-Kristallen aus Flüssigkeiten
CN100375741C (zh) * 2001-09-12 2008-03-19 旭化成化学株式会社 生产内酰胺的方法
US20030133925A1 (en) * 2001-09-28 2003-07-17 Shawar Ribhi M. Monobactam compositions and methods of use thereof
WO2003059849A1 (en) 2002-01-03 2003-07-24 Exxonmobil Chemical Patents Inc. Stabilisation of acid catalysts
JP2003290629A (ja) 2002-04-02 2003-10-14 Nissan Motor Co Ltd 排ガス浄化システム
EP1876247B1 (en) * 2002-07-08 2013-03-27 BASF Corporation Metal compound removal
JP2005514319A (ja) * 2002-10-24 2005-05-19 エクソンモービル・ケミカル・パテンツ・インク 酸触媒の安定化
JP4300862B2 (ja) 2002-11-11 2009-07-22 トヨタ自動車株式会社 内燃機関の排気浄化装置
CN1246223C (zh) 2003-09-03 2006-03-22 中国石油化工股份有限公司 合成硅磷铝分子筛的方法
JP2005177570A (ja) 2003-12-17 2005-07-07 Ne Chemcat Corp 高温特性に優れるｓｃｒ触媒
JP4427356B2 (ja) 2004-02-27 2010-03-03 東京濾器株式会社 窒素酸化物浄化用触媒システム及び窒素酸化物浄化方法
PL1774145T3 (pl) 2004-07-26 2009-03-31 Dow Global Technologies Inc Ulepszony, katalizowany filtr sadzy
JP4745968B2 (ja) 2004-07-29 2011-08-10 エヌ・イーケムキャット株式会社 低温特性に優れる脱硝触媒
JP2006089300A (ja) * 2004-09-21 2006-04-06 Nippon Gas Gosei Kk Ｓａｐｏ−３４の製造方法、および、プロパンを主成分とする液化石油ガスの製造方法
CN101111667B (zh) * 2004-12-17 2010-05-12 臼井国际产业株式会社 柴油发动机的排放气体用电气式处理方法及其装置
US7918991B2 (en) 2005-04-27 2011-04-05 W. R. Grace & Co.-Conn. Compositions and processes for reducing NOx emissions during fluid catalytic cracking
WO2007004774A1 (en) 2005-07-06 2007-01-11 Heesung Catalysts Corporation An oxidation catalyst for nh3 and an apparatus for treating slipped or scrippedd nh3
US7576031B2 (en) 2006-06-09 2009-08-18 Basf Catalysts Llc Pt-Pd diesel oxidation catalyst with CO/HC light-off and HC storage function
CN101121532A (zh) 2006-08-08 2008-02-13 中国科学院大连化学物理研究所 一种小孔磷硅铝分子筛的金属改性方法
US7998423B2 (en) 2007-02-27 2011-08-16 Basf Corporation SCR on low thermal mass filter substrates
US20090196812A1 (en) 2008-01-31 2009-08-06 Basf Catalysts Llc Catalysts, Systems and Methods Utilizing Non-Zeolitic Metal-Containing Molecular Sieves Having the CHA Crystal Structure
US8151558B2 (en) 2008-01-31 2012-04-10 Caterpillar Inc. Exhaust system implementing SCR and EGR
US8293199B2 (en) 2009-12-18 2012-10-23 Basf Corporation Process for preparation of copper containing molecular sieves with the CHA structure, catalysts, systems and methods
US9120056B2 (en) 2010-02-16 2015-09-01 Ford Global Technologies, Llc Catalyst assembly for treating engine exhaust
US8101146B2 (en) 2011-04-08 2012-01-24 Johnson Matthey Public Limited Company Catalysts for the reduction of ammonia emission from rich-burn exhaust

Patent Citations (73)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4220632A (en) * 1974-09-10 1980-09-02 The United States Of America As Represented By The United States Department Of Energy Reduction of nitrogen oxides with catalytic acid resistant aluminosilicate molecular sieves and ammonia
US4297328A (en) * 1979-09-28 1981-10-27 Union Carbide Corporation Three-way catalytic process for gaseous streams
US4544538A (en) * 1982-07-09 1985-10-01 Chevron Research Company Zeolite SSZ-13 and its method of preparation
US4440871A (en) * 1982-07-26 1984-04-03 Union Carbide Corporation Crystalline silicoaluminophosphates
US4567029A (en) * 1983-07-15 1986-01-28 Union Carbide Corporation Crystalline metal aluminophosphates
US4753927A (en) * 1983-08-12 1988-06-28 Immunetech Pharmaceuticals Method of blocking immune complex binding to immunoglobulin Fc receptors
US4735927A (en) * 1985-10-22 1988-04-05 Norton Company Catalyst for the reduction of oxides of nitrogen
US4735930A (en) * 1986-02-18 1988-04-05 Norton Company Catalyst for the reduction of oxides of nitrogen
US5041270A (en) * 1986-10-17 1991-08-20 Kabushiki Kaisha Toyota Chuo Kenkyusho Method of purifying exhaust gases
US4861743A (en) * 1987-11-25 1989-08-29 Uop Process for the production of molecular sieves
US5147949A (en) * 1988-03-29 1992-09-15 Exxon Chemical Patents Inc. Polymerization process using a silica gel supported metallocene-alumoxane catalyst
US4874590A (en) * 1988-04-07 1989-10-17 Uop Catalytic reduction of nitrogen oxides
US4867954A (en) * 1988-04-07 1989-09-19 Uop Catalytic reduction of nitrogen oxides
US5096684A (en) * 1989-03-31 1992-03-17 Elf France Process for the synthesis of precursors of molecular sieves of the silicoaluminophosphate type, precursors obtained and their application to obtaining the said molecular sieves
US4961917A (en) * 1989-04-20 1990-10-09 Engelhard Corporation Method for reduction of nitrogen oxides with ammonia using promoted zeolite catalysts
US5024981A (en) * 1989-04-20 1991-06-18 Engelhard Corporation Staged metal-promoted zeolite catalysts and method for catalytic reduction of nitrogen oxides using the same
US5516497A (en) * 1989-04-20 1996-05-14 Engelhard Corporation Staged metal-promoted zeolite catalysts and method for catalytic reduction of nitrogen oxides using the same
US5477014A (en) * 1989-07-28 1995-12-19 Uop Muffler device for internal combustion engines
US5233117A (en) * 1991-02-28 1993-08-03 Uop Methanol conversion processes using syocatalysts
US5313792A (en) * 1991-09-20 1994-05-24 Toyota Jidosha Kabushiki Kaisha Exhaust gas purification apparatus for an internal combustion engine
US6171556B1 (en) * 1992-11-12 2001-01-09 Engelhard Corporation Method and apparatus for treating an engine exhaust gas stream
US20010038812A1 (en) * 1992-11-19 2001-11-08 Yavuz Bulent O. Zeolite-containing oxidation catalyst and method of use
US5733837A (en) * 1993-05-10 1998-03-31 Sakai Chemical Industry Co., Ltd. Catalyst for catalytic reduction of nitrogen oxides
US5417949A (en) * 1993-08-25 1995-05-23 Mobil Oil Corporation NOx abatement process
US5589149A (en) * 1993-11-09 1996-12-31 Union Carbide Chemicals & Plastics Technology Corporation Process for absorption of mercaptans
US5589147A (en) * 1994-07-07 1996-12-31 Mobil Oil Corporation Catalytic system for the reducton of nitrogen oxides
US5884473A (en) * 1995-06-23 1999-03-23 Ngk Insulators, Ltd. System for exhaust gas purification and method for exhaust gas purification using said system
US6139808A (en) * 1996-12-20 2000-10-31 Ngk Insulators, Ltd. Catalyst for exhaust gas purification and system for exhaust gas purification
US20020016252A1 (en) * 1997-10-09 2002-02-07 Ngk Insulators, Ltd. Adsorbent for exhaust gas purification
US6162415A (en) * 1997-10-14 2000-12-19 Exxon Chemical Patents Inc. Synthesis of SAPO-44
US6319487B1 (en) * 1997-10-14 2001-11-20 Exxon Mobil Chemical Patents Inc. Synthesis of SAPO-44
US6576203B2 (en) * 1998-06-29 2003-06-10 Ngk Insulators, Ltd. Reformer
US6974889B1 (en) * 1998-07-29 2005-12-13 Exxonmobil Chemical Patents Inc. Processes for manufacture of molecular sieves
US6350298B1 (en) * 1998-10-30 2002-02-26 The Boc Group, Inc. Adsorbents and adsorptive separation process
US6569394B2 (en) * 1998-11-25 2003-05-27 Siemens Aktiengesellschaft Catalyst body and process for breaking down nitrogen oxides
US6376562B1 (en) * 1998-12-24 2002-04-23 Korea Advanced Institute Of Science And Technology Hybrid catalyst for hydrocarbon synthesis via hydrogenation of carbon dioxide
US6696063B1 (en) * 1998-12-30 2004-02-24 Applied Research Systems Ars Holding N.V. Treatment of HIV-associated dysmorphia/dysmetabolic syndrome (HADDS) with or without lipodystrophy
US6503863B2 (en) * 1999-06-07 2003-01-07 Exxonmobil Chemical Patents, Inc. Heat treating a molecular sieve and catalyst
US6395674B1 (en) * 1999-06-07 2002-05-28 Exxon Mobil Chemical Patents, Inc. Heat treating a molecular sieve and catalyst
US6316683B1 (en) * 1999-06-07 2001-11-13 Exxonmobil Chemical Patents Inc. Protecting catalytic activity of a SAPO molecular sieve
US20010043896A1 (en) * 2000-03-01 2001-11-22 Rainer Domesle Catalyst for purifying the exhaust gases of diesel engines, and process for the preparation thereof
US6606856B1 (en) * 2000-03-03 2003-08-19 The Lubrizol Corporation Process for reducing pollutants from the exhaust of a diesel engine
US20020084223A1 (en) * 2000-12-28 2002-07-04 Feimer Joseph L. Removal of sulfur from naphtha streams using high silica zeolites
US20050096214A1 (en) * 2001-03-01 2005-05-05 Janssen Marcel J. Silicoaluminophosphate molecular sieve
US20040166035A1 (en) * 2001-07-25 2004-08-26 Naomi Noda Honeycomb structural body for exhaust emission control and honeycomb catalyst body for exhaust emission control
US6709644B2 (en) * 2001-08-30 2004-03-23 Chevron U.S.A. Inc. Small crystallite zeolite CHA
US20030069449A1 (en) * 2001-08-30 2003-04-10 Zones Stacey I. Small crystallite zeolite CHA
US7182927B2 (en) * 2001-09-07 2007-02-27 Engelhard Corporation Hydrothermally stable metal promoted zeolite beta for NOx reduction
US7014827B2 (en) * 2001-10-23 2006-03-21 Machteld Maria Mertens Synthesis of silicoaluminophosphates
US6696032B2 (en) * 2001-11-29 2004-02-24 Exxonmobil Chemical Patents Inc. Process for manufacturing a silicoaluminophosphate molecular sieve
US20040082466A1 (en) * 2001-11-30 2004-04-29 Guang Cao Method of synthesizing molecular sieves
US6685905B2 (en) * 2001-12-21 2004-02-03 Exxonmobil Chemical Patents Inc. Silicoaluminophosphate molecular sieves
US20040098973A1 (en) * 2002-11-21 2004-05-27 Tennison Paul Joseph Exhaust gas aftertreatment systems
US20040171476A1 (en) * 2003-02-27 2004-09-02 In-Sik Nam Zeolite catalyst and preparation process for NOx reduction
US7049261B2 (en) * 2003-02-27 2006-05-23 General Motors Corporation Zeolite catalyst and preparation process for NOx reduction
US20040209760A1 (en) * 2003-04-17 2004-10-21 Ict Co., Ltd. Exhaust gas purifying catalyst and process for purifying exhaust gas by use of the catalyst
US20050031514A1 (en) * 2003-08-05 2005-02-10 Engelhard Corporation Catalyzed SCR filter and emission treatment system
US7229597B2 (en) * 2003-08-05 2007-06-12 Basfd Catalysts Llc Catalyzed SCR filter and emission treatment system
US7094389B2 (en) * 2003-12-23 2006-08-22 Exxonmobil Chemical Patents Inc. Chabazite-containing molecular sieve, its synthesis and its use in the conversion of oxygenates to olefins
US20060039843A1 (en) * 2004-08-23 2006-02-23 Engelhard Corporation Zone coated catalyst to simultaneously reduce NOx and unreacted ammonia
US20060115403A1 (en) * 2004-11-29 2006-06-01 Chevron U.S.A. Inc. Reduction of oxides of nitrogen in a gas stream using high-silics molecular sieve CHA
US20060228283A1 (en) * 2005-02-28 2006-10-12 Catalytic Solutions, Inc. Catalyst and method for reducing nitrogen oxides in exhaust streams with hydrocarbons or alcohols
US20090060809A1 (en) * 2005-03-30 2009-03-05 Sued-Chemie Catalysts Japan, Inc. Ammonia Decomposition Catalyst and Process for Decomposition of Ammonia Using the Catalyst
US20070000243A1 (en) * 2005-06-30 2007-01-04 General Electric Company Conversion system for reducing NOx emissions
US20070043249A1 (en) * 2005-08-18 2007-02-22 Guang Cao Synthesis of molecular sieves having the chabazite framework type and their use in the conversion of oxygenates to olefins
US20070149385A1 (en) * 2005-12-23 2007-06-28 Ke Liu Catalyst system for reducing nitrogen oxide emissions
US20070286798A1 (en) * 2006-06-09 2007-12-13 Guang Cao Treatment of CHA-type molecular sieves and their use in the conversion of oxygenates to olefins
US20080317999A1 (en) * 2007-01-31 2008-12-25 Joseph Patchett Gas Catalysts Comprising Porous Wall Honeycombs
US7601662B2 (en) * 2007-02-27 2009-10-13 Basf Catalysts Llc Copper CHA zeolite catalysts
US20080241060A1 (en) * 2007-03-26 2008-10-02 Hong-Xin Li Novel microporous crystalline material comprising a molecular sieve or zeolite having an 8-ring pore opening structure and methods of making and using same
US20100092362A1 (en) * 2007-03-26 2010-04-15 Pq Corporation High silica chabazite for selective catalytic reduction, methods of making and using same
US20100290963A1 (en) * 2007-04-26 2010-11-18 Johnson Matthey Public Limited Company Transition metal / zeolite scr catalysts
US20090048095A1 (en) * 2007-08-13 2009-02-19 Hong-Xin Li Novel iron-containing aluminosilicate zeolites and methods of making and using same

Cited By (127)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8404203B2 (en) 2007-02-27 2013-03-26 Basf Corporation Processes for reducing nitrogen oxides using copper CHA zeolite catalysts
US9839905B2 (en) 2007-02-27 2017-12-12 Basf Corporation Copper CHA zeolite catalysts
US11845067B2 (en) 2007-02-27 2023-12-19 Basf Corporation Copper CHA zeolite catalysts
US10654031B2 (en) 2007-02-27 2020-05-19 Basf Corporation Copper CHA zeolite catalysts
US8735311B2 (en) 2007-02-27 2014-05-27 Basf Corporation Copper CHA zeolite catalysts
US9162218B2 (en) 2007-02-27 2015-10-20 Basf Corporation Copper CHA zeolite catalysts
US9138732B2 (en) 2007-02-27 2015-09-22 Basf Corporation Copper CHA zeolite catalysts
US11529619B2 (en) 2007-02-27 2022-12-20 Basf Corporation Copper CHA zeolite catalysts
US20090285737A1 (en) * 2007-02-27 2009-11-19 Basf Catalysts Llc Copper CHA Zeolite Catalysts
US9656254B2 (en) 2007-02-27 2017-05-23 Basf Corporation Copper CHA zeolite catalysts
US20100092362A1 (en) * 2007-03-26 2010-04-15 Pq Corporation High silica chabazite for selective catalytic reduction, methods of making and using same
US10384162B2 (en) * 2007-03-26 2019-08-20 Pq Corporation High silica chabazite for selective catalytic reduction, methods of making and using same
US11478748B2 (en) 2007-04-26 2022-10-25 Johnson Matthey Public Limited Company Transition metal/zeolite SCR catalysts
US20120301381A1 (en) * 2007-04-26 2012-11-29 Johnson Matthey Public Limited Company Transition metal/zeolite scr catalysts
US8906820B2 (en) * 2007-04-26 2014-12-09 Johnson Matthey Public Limited Company Transition metal/zeolite SCR catalysts
US8617474B2 (en) 2008-01-31 2013-12-31 Basf Corporation Systems utilizing non-zeolitic metal-containing molecular sieves having the CHA crystal structure
US10105649B2 (en) 2008-01-31 2018-10-23 Basf Corporation Methods utilizing non-zeolitic metal-containing molecular sieves having the CHA crystal structure
CN103801392A (zh) * 2009-01-22 2014-05-21 三菱树脂株式会社 氮氧化物净化用催化剂及其制造方法
US20120020875A1 (en) * 2009-01-22 2012-01-26 Mitsubishi Plastics, Inc. Catalyst for reducing nitrogen oxides and method for producing the same
US20130005563A1 (en) * 2009-01-22 2013-01-03 Mitsubishi Plastics, Inc. Catalyst for reducing nitrogen oxides and method for producing the same
US20160082425A1 (en) * 2009-01-22 2016-03-24 Mitsubishi Plastics, Inc. Catalyst for reducing nitrogen oxides and method for producing the same
US9662611B2 (en) 2009-04-03 2017-05-30 Basf Corporation Emissions treatment system with ammonia-generating and SCR catalysts
US9321009B2 (en) 2009-04-03 2016-04-26 Basf Corporation Emissions treatment system with ammonia-generating and SCR catalysts
US9358503B2 (en) 2009-04-03 2016-06-07 Basf Corporation Emissions treatment system with ammonia-generating and SCR catalysts
US10124292B2 (en) 2009-04-03 2018-11-13 Basf Corporation Emissions treatment system with ammonia-generating and SCR catalysts
EP2995367B1 (en) 2009-04-17 2017-12-20 Johnson Matthey Public Limited Company Small pore molecular sieve supported copper catalysts durable against lean/rich aging for the reduction of nitrogen oxides
EP2338858A1 (en) * 2009-11-19 2011-06-29 Ibiden Co., Ltd. Honeycomb structural body and manufacturing method of honeycomb structural body
US20110118108A1 (en) * 2009-11-19 2011-05-19 Ibiden Co., Ltd. Honeycomb structural body and manufacturing method of honeycomb structural body
US8883119B2 (en) 2009-11-24 2014-11-11 Basf Se Process for the preparation of zeolites having CHA structure
US9895684B2 (en) 2009-11-24 2018-02-20 Basf Se Process for the preparation of zeolites having CHA structure
US8293198B2 (en) 2009-12-18 2012-10-23 Basf Corporation Process of direct copper exchange into Na+-form of chabazite molecular sieve, and catalysts, systems and methods
US20110165051A1 (en) * 2009-12-18 2011-07-07 Basf Corporation Process Of Direct Copper Exchange Into Na+-Form Of Chabazite Molecular Sieve, And Catalysts, Systems And Methods
US20110207598A1 (en) * 2009-12-18 2011-08-25 Jgc Catalysts And Chemicals Ltd. Metal-supported crystalline silica aluminophosphate catalyst and process for producing the same
US8293199B2 (en) 2009-12-18 2012-10-23 Basf Corporation Process for preparation of copper containing molecular sieves with the CHA structure, catalysts, systems and methods
US20110165052A1 (en) * 2009-12-18 2011-07-07 Basf Corporation Process for Preparation of Copper Containing Molecular Sieves With the CHA Structure, Catalysts, Systems and Methods
CN101797518A (zh) * 2010-04-14 2010-08-11 太原理工大学 一种柴油机车尾气净化整体式催化剂的制备方法
EP2567081B1 (en) 2010-05-05 2020-07-08 BASF Corporation Integrated scr and amox catalyst systems
US9403156B2 (en) 2010-08-13 2016-08-02 Ut-Battelle, Llc Zeolite-based SCR catalysts and their use in diesel engine emission treatment
US8987161B2 (en) 2010-08-13 2015-03-24 Ut-Battelle, Llc Zeolite-based SCR catalysts and their use in diesel engine emission treatment
US8808633B2 (en) * 2010-09-02 2014-08-19 Ibiden Co., Ltd. Silico-alumino phosphate, honeycomb structural body and exhaust gas conversion apparatus
US20120058018A1 (en) * 2010-09-02 2012-03-08 Ibiden Co., Ltd. Silico-alumino phosphate, honeycomb structural body and exhaust gas conversion apparatus
WO2012059145A1 (en) * 2010-11-02 2012-05-10 Haldor Topsøe A/S Method for the preparation of a catalysed particulate filter and catalysed particulate filter
WO2012059144A1 (en) * 2010-11-02 2012-05-10 Haldor Topsøe A/S Method for the preparation of a catalysed particulate filter and catalysed particulate filter
RU2572610C2 (ru) * 2010-11-02 2016-01-20 Хальдор Топсеэ А/С Способ получения катализируемого сажевого фильтра и катализируемый сажевый фильтр
CN103328098A (zh) * 2010-11-02 2013-09-25 赫多特普索化工设备公司 制造催化微粒过滤器的方法及催化微粒过滤器
JP2014508630A (ja) * 2010-11-02 2014-04-10 ハルドール・トプサー・アクチエゼルスカベット 触媒化微粒子フィルターの製造方法及び触媒化微粒子フィルター
US9339844B2 (en) 2010-11-02 2016-05-17 Haldor Topsoe A/S Method for the preparation of a catalysed particulate filter and catalysed particulate filter
RU2564854C2 (ru) * 2010-11-02 2015-10-10 Хальдор Топсеэ А/С Способ получения катализируемого сажевого фильтра
JP2014508631A (ja) * 2010-11-02 2014-04-10 ハルドール・トプサー・アクチエゼルスカベット 触媒化微粒子フィルターの製造方法及び触媒化粒子フィルター
EP3401009A1 (en) * 2010-11-02 2018-11-14 Umicore Ag & Co. Kg Method for the preparation of a catalysed particulate filter
CN103384564A (zh) * 2010-11-02 2013-11-06 赫多特普索化工设备公司 制造催化微粒过滤器的方法及催化微粒过滤器
US9346018B2 (en) 2010-11-02 2016-05-24 Haldor Topsoe A/S Method for the preparation of a catalysed particulate filter and catalysed particulate filter
EP2463028A1 (en) * 2010-12-11 2012-06-13 Umicore Ag & Co. Kg Process for the production of metal doped zeolites and zeotypes and application of same to the catalytic removal of nitrogen oxides
WO2012076648A1 (en) * 2010-12-11 2012-06-14 Umicore Ag & Co. Kg Process for the production of metal doped zeolites and zeotypes and application of same to the catalytic remediation of nitrogen oxides
US8865120B2 (en) 2010-12-11 2014-10-21 Umicore Ag & Co., Kg Process for the production of metal doped zeolites and zeotypes and application of same to the catalytic remediation of nitrogen oxides
WO2012080318A1 (de) * 2010-12-16 2012-06-21 Umicore Ag & Co. Kg Kupfer-chabazit-basierter katalysator mit verbesserter katalytischer aktivitaet zur reduktion von stickoxiden
KR101849068B1 (ko) 2010-12-16 2018-04-17 우미코레 아게 운트 코 카게 질소 산화물의 환원을 위한 촉매 활성이 개선된 구리/카바자이트계 촉매
US8821820B2 (en) 2010-12-16 2014-09-02 Umicore Ag & Co. Kg Copper/chabazite-based catalyst with improved catalytic activity for reduction of nitrogen oxides
EP2659975A4 (en) * 2010-12-27 2015-06-17 Mitsubishi Plastics Inc CATALYST FOR REMOVING NITROGEN OXIDE
US20140010722A1 (en) * 2011-03-08 2014-01-09 Mitsubishi Plastics, Inc. Catalyst, device for removing nitrogen oxide, and system for removing nitrogen oxide
US9242239B2 (en) 2011-04-08 2016-01-26 Johnson Matthey Public Limited Company Catalysts for the reduction of ammonia emission from rich-burn exhaust
KR102047049B1 (ko) * 2011-04-08 2019-11-20 존슨 맛쎄이 퍼블릭 리미티드 컴파니 과농-연소 배기가스로부터 암모니아 배출의 감소를 위한 촉매
KR20140032398A (ko) * 2011-04-08 2014-03-14 존슨 맛쎄이 퍼블릭 리미티드 컴파니 과농-연소 배기가스로부터 암모니아 배출의 감소를 위한 촉매
RU2593293C2 (ru) * 2011-04-08 2016-08-10 Джонсон Мэтти Паблик Лимитед Компани Катализаторы для уменьшения выбросов аммиака с выхлопными газами от сжигания богатой топливной смеси
WO2012138405A1 (en) * 2011-04-08 2012-10-11 Johnson Matthey Public Limited Company Catalysts for the reduction of ammonia emission from rich-burn exhaust
US20120269719A1 (en) * 2011-04-18 2012-10-25 Pq Corporation Large crystal, organic-free chabazite, methods of making and using the same
US11590482B1 (en) * 2011-06-17 2023-02-28 Johnson Matthey Public Limited Company Alumina binders for SCR catalysts
US9410463B2 (en) * 2011-08-18 2016-08-09 Ibiden Co., Ltd. Composite particles, honeycomb structure, method for manufacturing honeycomb structure, and exhaust gas purifying apparatus
US9284874B2 (en) 2011-08-18 2016-03-15 Ibiden Co., Ltd. Silicoaluminophosphate particles, honeycomb structure, method for manufacturing the same and exhaust gas purifying apparatus
EP2746224A1 (en) * 2011-08-18 2014-06-25 Ibiden Co., Ltd Silicoaluminophosphate particles, honeycomb structure, method for producing same, and exhaust gas purification device
EP2746224A4 (en) * 2011-08-18 2015-04-29 Ibiden Co Ltd SILICOALUMINOPHOSPHATE PARTICLES, HONEYCOMB STRUCTURE, PROCESS FOR PRODUCING THE SAME, AND EXHAUST GAS PURIFICATION DEVICE
US20140112835A1 (en) * 2011-08-18 2014-04-24 Ibiden Co., Ltd. Honeycomb structure, method for producing same, exhaust gas purification device and silicoaluminophosphate particles
US9670415B2 (en) 2011-09-06 2017-06-06 Basf Se Synthesis of zeolitic materials using N,N-dimethyl organotemplates
US9005559B2 (en) 2011-10-06 2015-04-14 Johnson Matthey Public Limited Company Oxidation catalyst for internal combustion engine exhaust gas treatment
US9868115B2 (en) 2011-10-06 2018-01-16 Johnson Matthey Public Limited Company Oxidation catalyst for internal combustion engine exhaust gas treatment
US9527751B2 (en) 2011-11-11 2016-12-27 Basf Se Organotemplate-free synthetic process for the production of a zeolitic material of the CHA-type structure
US9333461B2 (en) 2011-12-12 2016-05-10 Johnson Matthey Public Limited Company Substrate monolith comprising SCR catalyst
US8667785B2 (en) 2011-12-12 2014-03-11 Johnson Matthey Public Limited Company Catalysed substrate monolith
GB2497656A (en) * 2011-12-12 2013-06-19 Johnson Matthey Plc Substrate monolith comprising SCR catalyst and trap for gas phase PGM
US9597661B2 (en) 2011-12-12 2017-03-21 Johnson Matthey Public Limited Company Catalysed substrate monolith
US9046022B2 (en) 2011-12-12 2015-06-02 Johnson Matthey Public Limited Company Catalysed substrate monolith
GB2497656B (en) * 2011-12-12 2015-09-16 Johnson Matthey Plc Substrate monolith comprising SCR catalyst
US8668891B2 (en) 2011-12-12 2014-03-11 Johnson Matthey Public Limited Company Exhaust system for a lean-burn IC engine comprising a PGM component and a SCR catalyst
US9259684B2 (en) 2011-12-12 2016-02-16 Johnson Matthey Public Limited Company Exhaust system for a lean-burn internal combustion engine including SCR catalyst
US8986635B2 (en) 2011-12-12 2015-03-24 Johnson Matthey Public Limited Company Exhaust system for a lean-burn IC engine comprising a PGM component and a SCR catalyst
US20150118134A1 (en) * 2012-04-27 2015-04-30 Haldor Topsøe A/S Method and system for the purification of exhaust gas from an internal combustion engine
US9561468B2 (en) * 2012-04-27 2017-02-07 Haldor Topsoe A/S Method and system for the purification of exhaust gas from an internal combustion engine
US9855528B2 (en) 2012-04-27 2018-01-02 Haldor Topsoe A/S System for the purification of exhaust gas from an internal combustion engine
GB2521576B (en) * 2012-10-18 2018-06-27 Johnson Matthey Plc Close-coupled SCR system
US9931620B2 (en) 2013-03-13 2018-04-03 Basf Corporation Stabilized metal-exchanged SAPO material
CN105008048A (zh) * 2013-03-13 2015-10-28 巴斯夫公司 稳定的金属交换的sapo材料
US9802182B2 (en) 2013-03-13 2017-10-31 Basf Corporation Stabilized metal-exchanged SAPO material
US9017626B2 (en) 2013-03-14 2015-04-28 Basf Corporation Selective catalytic reduction catalyst system
WO2014160289A1 (en) * 2013-03-14 2014-10-02 Basf Corporation Selective catalytic reduction catalyst system
CN105188924A (zh) * 2013-03-14 2015-12-23 巴斯夫公司 选择性催化还原催化剂系统
WO2014160292A1 (en) * 2013-03-14 2014-10-02 Basf Corporation Selective catalytic reduction catalyst system
WO2014160293A1 (en) * 2013-03-14 2014-10-02 Basf Corporation Selective catalytic reduction catalyst systems
US9468915B2 (en) 2013-03-14 2016-10-18 Basf Corporation Selective catalytic reduction catalyst system
US10512901B2 (en) 2013-03-14 2019-12-24 Basf Corporation Selective catalytic reduction catalyst system
CN105026038A (zh) * 2013-03-14 2015-11-04 巴斯夫公司 选择性催化还原催化剂系统
US9782761B2 (en) 2013-10-03 2017-10-10 Ford Global Technologies, Llc Selective catalytic reduction catalyst
EP3060339A4 (en) * 2013-10-24 2017-06-28 W.R. Grace & CO. - CONN. Method for synthesizing silicoaluminophosphate-34 molecular sieves
JP2015093209A (ja) * 2013-11-08 2015-05-18 トヨタ自動車株式会社 排ガス浄化用触媒
GB2522527B (en) * 2013-12-02 2018-01-24 Johnson Matthey Plc Mixed template synthesis of high silica Cu-CHA
GB2522527A (en) * 2013-12-02 2015-07-29 Johnson Matthey Plc Mixed template synthesis of high silica Cu-CHU
US11207666B2 (en) 2013-12-02 2021-12-28 Johnson Matthey Public Limited Company Mixed template synthesis of high silica Cu-CHA
US9895660B2 (en) 2014-04-07 2018-02-20 Haldor Topsoe A/S Method for producing metal exchanged microporous materials by solid-state ion exchange
US9914114B2 (en) 2014-04-07 2018-03-13 Haldor Topsoe A/S Method for producing metal exchanged metallo-aluminophosphates by solid-state ion exchange at low temperatures
US20160230631A1 (en) * 2015-02-11 2016-08-11 GM Global Technology Operations LLC Selective catalytic reduction device
US9850797B2 (en) * 2015-02-11 2017-12-26 GM Global Technology Operations LLC Selective catalytic reduction device
US10577999B2 (en) * 2015-07-09 2020-03-03 Umicore Ag & Co. Kg System for the removal of particulate matter and noxious compounds from engine exhaust gas
US10570802B2 (en) * 2015-07-09 2020-02-25 Umicore Ag & Co. Kg System for the removal of particulate matter and noxious compounds from engine exhaust gas
CN105688980A (zh) * 2016-03-10 2016-06-22 镇江翰宏新材料科技有限公司 一种分子筛负载scr催化剂的制备方法
GB2577001A (en) * 2016-04-11 2020-03-11 Johnson Matthey Plc Method of coating a substrate with a particle stabilized foam
US11618014B2 (en) 2016-04-11 2023-04-04 Johnson Matthey Public Limited Company Method of coating a substrate with a particle stabilized foam
GB2577001B (en) * 2016-04-11 2020-09-23 Johnson Matthey Plc Method of coating a substrate with a particle stabilized foam
EP3585516A4 (en) * 2017-02-22 2020-08-19 BASF Corporation EMISSION TREATMENT CATALYST FOR THE REMOVAL OF NITROGEN OXIDES
CN110392606A (zh) * 2017-02-22 2019-10-29 巴斯夫公司 用于减少氮氧化物的废气处理催化剂
CN109081360A (zh) * 2017-06-13 2018-12-25 中国石油化工股份有限公司 分子筛scm-14、其合成方法及其用途
CN109250728A (zh) * 2017-07-12 2019-01-22 中国科学院大连化学物理研究所 Cu-SAPO分子筛合成方法及合成的Cu-SAPO分子筛和应用
CN113766973A (zh) * 2019-05-15 2021-12-07 株式会社Acr 催化剂、催化剂产品以及催化剂的制造方法
US11305266B2 (en) * 2020-01-03 2022-04-19 Hyundai Motor Company Catalyst and manufacturing method thereof
CN113318782A (zh) * 2021-05-28 2021-08-31 江西农业大学 一种富锰的Mn-SAPO-18分子筛催化剂的制备方法及其用途
CN113856749A (zh) * 2021-08-26 2021-12-31 中汽研（天津）汽车工程研究院有限公司 一种钐基cha分子筛催化剂及应用
CN114177935A (zh) * 2021-10-14 2022-03-15 凯龙蓝烽新材料科技有限公司 一种用于柴油车尾气净化的scr催化剂
CN115739174A (zh) * 2022-11-15 2023-03-07 昆明理工大学 一种抗水热稳定性脱硝催化剂及其制备方法和应用、整体式催化剂及其应用
CN115739172A (zh) * 2022-12-02 2023-03-07 润和科华催化剂(上海)有限公司 一种协同脱除n2o和no的催化剂及其制备方法

Also Published As

Publication number Publication date
AR106797A2 (es) 2018-02-21
CN101983103A (zh) 2011-03-02
AR071555A1 (es) 2010-06-30
US8617474B2 (en) 2013-12-31
JP2014139440A (ja) 2014-07-31
BRPI0906992B1 (pt) 2018-04-03
JP2011510899A (ja) 2011-04-07
WO2009099937A1 (en) 2009-08-13
US20190015783A1 (en) 2019-01-17
US20110300042A1 (en) 2011-12-08
US20110300028A1 (en) 2011-12-08
US10105649B2 (en) 2018-10-23
BRPI0906992A2 (pt) 2015-07-21

Similar Documents

Publication Publication Date Title
US20190015783A1 (en) Methods Utilizing Non-Zeolitic Metal-Containing Molecular Sieves Having The CHA Crystal Structure
US11845067B2 (en) Copper CHA zeolite catalysts
US11311867B2 (en) Copper and iron co-exchanged chabazite catalyst
US8404203B2 (en) Processes for reducing nitrogen oxides using copper CHA zeolite catalysts
CA2961232A1 (en) Emissions treatment systems with twc catalysts and scr-hct catalysts
KR20110082603A (ko) 낮은 알루미나에 대한 실리카 비를 갖는 캐버자이트 제올라이트 촉매
US9931620B2 (en) Stabilized metal-exchanged SAPO material
KR20190027392A (ko) 선택적 접촉 환원 물품 및 시스템
WO2017109705A1 (en) Process for preparing iron(iii)-exchanged zeolite composition

Legal Events

Date Code Title Description
AS Assignment

Owner name: BASF CATALYSTS LLC, NEW JERSEY

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:BULL, IVOR;REEL/FRAME:022585/0824

Effective date: 20090305

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION

AS Assignment

Owner name: BASF CORPORATION, NEW JERSEY

Free format text: CHANGE OF NAME;ASSIGNOR:BASF CATALYSTS LLC;REEL/FRAME:035711/0619

Effective date: 20100401