CN104549228A - 一种燃煤电厂低温脱硝催化剂及制备方法 - Google Patents

一种燃煤电厂低温脱硝催化剂及制备方法 Download PDF

Info

Publication number
CN104549228A
CN104549228A CN201510013205.8A CN201510013205A CN104549228A CN 104549228 A CN104549228 A CN 104549228A CN 201510013205 A CN201510013205 A CN 201510013205A CN 104549228 A CN104549228 A CN 104549228A
Authority
CN
China
Prior art keywords
temperature
low
catalyst
coal
sintering
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510013205.8A
Other languages
English (en)
Inventor
林琳
邵林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
State Grid Corp of China SGCC
State Grid Tianjin Electric Power Co Ltd
Original Assignee
State Grid Corp of China SGCC
State Grid Tianjin Electric Power Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by State Grid Corp of China SGCC, State Grid Tianjin Electric Power Co Ltd filed Critical State Grid Corp of China SGCC
Priority to CN201510013205.8A priority Critical patent/CN104549228A/zh
Publication of CN104549228A publication Critical patent/CN104549228A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种燃煤电厂低温脱硝催化剂及制备方法，催化剂包括按重量比例为1﹕1的催化剂载体Al2O3及添加物，添加物按重量份数比构成的组分为：MnO2：3.1-3.3份、MoO3：0.7-0.9份、WO3：1.1-1.3份、V2O5：70.0-80.0份、SiO2：15.0-20.0份。催化剂的制备方法包括：(1)按重量比例为1﹕1的催化剂载体Al2O3及添加物在360℃进行第一次定尺成型烧结；(2)对第一次烧结的初料在820℃进行第二次高温多孔烧结，降温得成品。本发明所得低温脱硝催化剂在100-140℃范围内连续使用一个月催化剂效果明显，且性能稳定，在标准流速下脱硝效率大于70％。

Description

一种燃煤电厂低温脱硝催化剂及制备方法
技术领域
本发明属于燃煤电厂烟气脱硝技术领域，尤其是一种燃煤电厂低温脱硝催化剂及制备方法。
背景技术
燃煤电厂目前大部分采用中温脱硝方案，即在尾部受热面空气预热器和省煤器之间喷入氨来达到脱硝的目的。还有少部分采用高温脱硝，即在燃烧区喷入尿素来完成脱硝工艺。以中温脱硝为例，存在着几个缺点：1、温度需相对准确，控制在310—340℃之间。2、烟气中含有大量的粉尘，易造成尾部受热面积灰和脱硝设备积灰使阻力增大。3、在此工况下脱硝易产生硫酸氢铵，是一种黏附性物质，容易造成堵塞，使阻力增大，催化剂失效，在中温段，使锅炉热效率降低。低温脱硝工艺，即在除尘器之后进行脱硝，具有几大优势：1、无粉尘干扰，或粉尘干扰较小。2、利用低温段脱硝，提高锅炉整体热效率。3、充分发挥催化剂性能。4、安装位置相对空间大。但目前低温脱硝催化剂研究和实用较少，所以迫切需研制一种适用于100—140℃下，具有稳定、高效催化性能的低温脱硝催化剂。
发明内容
本发明的目的是针对现有技术的不足，而提出一种燃煤电厂低温脱硝催化剂及制备方法。
本发明解决其技术问题是采取以下技术方案实现的：
一种燃煤电厂低温脱硝催化剂，包括按重量比例为1﹕1的催化剂载体Al2O3及添加物，其中，添加物按重量份数比构成的组分为：
而且，所述添加物按重量份数比构成的最佳组分为：
一种上述燃煤电厂低温脱硝催化剂的制备方法，包括步骤如下：
(1)按重量比例为1﹕1的催化剂载体Al2O3及添加物，添加物按重量份数比构成的如下组分，在360℃进行第一次定尺成型烧结；
(2)对第一次烧结的初料在820℃进行第二次高温多孔烧结，降温得成品。
而且，所述第二次烧结时，先在400℃以下缺氧烧结2小时，然后在820℃充氧烧结3小时候。
而且，所述降温得成品为，每小时降温梯度小于20℃，降至常温。
本发明的优点和积极效果是：
1、本发明的低温脱硝催化剂无明显的增加阻力的现象。
2、本发明的低温脱硝催化剂没有造成催化剂污堵和中毒的现象。
3、本发明的低温脱硝催化剂在100—140℃范围内有明显催化性能，催化性能在标准流速下脱硝效率大于70％。
3、本发明的低温脱硝催化剂在100—140℃，随着温度升高，脱硝效率增加。
4、本发明的低温脱硝催化剂在一个月内检验催化剂效果无明显变化，性能比较稳定。
具体实施方式
以下对本发明实施做进一步详述，以下实施例只是描述性的，不是限定性的，不能以此限定本发明的保护范围。
一种燃煤电厂低温脱硝催化剂，包括按重量份数比构成的如下组分：
作为催化剂载体的Al2O3 50份及添加物50份，其中，添加物按重量份数比构成的组分为：
在本发明的具体实施中，添加物按重量份数比构成的最佳组分为：
一种上述燃煤电厂低温脱硝催化剂的制备方法，包括步骤如下：
(1)按Al2O3质量一份和添加物一份，添加物按重量份数比构成的最佳组分为：
在360℃进行第一次定尺成型烧结；
(2)对第一次烧结的初料在820℃进行第二次高温多孔烧结，降温得成品。
在本发明的具体实施中，所述第二次烧结时，在400℃以下缺氧烧结2小时，在820℃充氧烧结3小时候。
在本发明的具体实施中，所述降温得成品为，每小时降温不大于20℃，降至常温。
所得低温脱硝催化剂在100—140℃范围内连续使用一个月催化剂效果明显，且性能稳定，在标准流速下脱硝效率大于70％。

Claims (5)

1.一种燃煤电厂低温脱硝催化剂，其特征在于包括按重量比例为1﹕1的催化剂载体Al2O3及添加物，其中，添加物按重量份数比构成的组分为：
2.根据权利要求1所述的燃煤电厂低温脱硝催化剂，其特征在于：所述添加物按重量份数比构成的最佳组分为：
3.一种上述燃煤电厂低温脱硝催化剂的制备方法，其特征在于包括步骤如下：
(1)按重量比例为1﹕1的催化剂载体Al2O3及添加物，添加物按重量份数比构成的如下组分，在360℃进行第一次定尺成型烧结；
(2)对第一次烧结的初料在820℃进行第二次高温多孔烧结，降温得成品。
4.根据权利要求3所述的燃煤电厂低温脱硝催化剂的制备方法，其特征在于：所述第二次烧结时，先在400℃以下缺氧烧结2小时，然后在820℃充氧烧结3小时候。
5.根据权利要求3所述的燃煤电厂低温脱硝催化剂的制备方法，其特征在于：所述降温得成品为，每小时降温梯度小于20℃，降至常温。
CN201510013205.8A 2015-01-12 2015-01-12 一种燃煤电厂低温脱硝催化剂及制备方法 Pending CN104549228A (zh)