JP4965555B2 - ヒートセット型光学フィルム - Google Patents
ヒートセット型光学フィルム Download PDFInfo
- Publication number
- JP4965555B2 JP4965555B2 JP2008505460A JP2008505460A JP4965555B2 JP 4965555 B2 JP4965555 B2 JP 4965555B2 JP 2008505460 A JP2008505460 A JP 2008505460A JP 2008505460 A JP2008505460 A JP 2008505460A JP 4965555 B2 JP4965555 B2 JP 4965555B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- stretching
- tddr
- refractive index
- runway
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
この出願は、「光学フィルム(Heat Setting Optical Films)ヒートセット工程」と題する米国特許仮出願第60/669865号(2005年4月8日出願)から優先の利益を請求する非暫定的出願である。
本開示は、光学フィルムを作製するヒートセット工程、並びにこれらの工程で作製されるフィルムに関する。
h(s)=(h(L’)−h(L’’))(1−(s−L’)/(L’’ −L’))α+h(L’’)
(式中、αは、L’からL’’に厚さが減少するテーパの正の比率である)で与えられる。
x/x0=(1/4)(y/x0)2+1である。
Δnyz=Δnyz(U=0)X(1−U)
(式中、Δnyzは、値のUのMD方向(すなわち、y方向)とND方向(すなわち、z方向)の屈折率の差であり、Δnyz(U=0)は、MDDRが延伸全体を通して1に保持されることを除き理想的に延伸されたフィルムのその屈折率である)により、y(MD)とz(ND)の間で合致した屈折率レベルを推測するため使用されてよい。この関係は、様々な光学フィルムに使用されるポリエステル系(PEN、PET及びPEN又はPETのコポリマーを含む)について正当に予測することわかっている。これらのポリエステル系において、Δnyz(U=0)は、典型的に差Δnxy(U=0)の約1/2、又はそれより多い量で、2つの面内方向、MD(y軸)とTD(x軸)の屈折差である。Δnxy(U=0)の典型的な値は、633ナノメートルで約0.26までの範囲にわたる。Δnyz(U=0)の典型的な値は、633ナノメートルで約0.15までの範囲にわたる。例えば、90/10coPEN、すなわち、約90%のPEN様繰返し単位と10%のPET様繰返し単位を含むコポリエステルは、633ナノメートルで典型的な値約0.14の高い伸びを有する。633ナノメートルで0.02、0.01及び0.003のΔnyzの相当値を備える実際のフィルム延伸比により測定した0.75、0.88及び0.97のU値を有するこの90/10coPENを含むフィルムが、本明細書に記載した方法により作製されている。
d(x/x1)/d(y/x1)=tan(θ)
(式中、tan(θ)は、発散角θの接線であり、yは、所定のx座標に対応する右境界軌道上の対向する点の現状位置のy座標である)。次に、微分式を、例えば、TDDRの履歴に沿って1から最大目標値まで1/tan(θ)を積分することにより解き、解析又は数式によるいずれかで右境界軌道の完全な座標の組{(x、y)}を得ることができる。
±(x)/(x1)=(1/4)(x1/x0)(y/x1)2+1
(式中、x1/x0は、換算入口離隔距離として定義される)。上記式が完全な一軸延伸を備えた放物線状走路を要求する場合、量x0は、2つの対向する走路の離隔距離の半分に相当する。換算入口離隔距離、x1/x0は、一軸状態からの軌道の偏位を表す。1つの実施形態において、主延伸領域の2つの対向する走路間の距離は、上述したように調節でき、軌道の操作を可能にし、1と異なるU及びFの値を備える(以下で記載する)。これらの軌道を形成する他の方法も使用されてよく、それらには、例えば、走路形状制御ユニットを使用し、又は目標の軌道を有する固定形状を選定することにより軌道の形状を操作することが含まれてよい。
F=1/(MDDRxTDDR1/2)として書き表わされる。
MDDR>1/(FmaxxTDDR1/2)
ここで、Fmaxは、1を超える任意の好ましいレベルで選択されてよい。例えば、上記したように、Fは、2、1.5、1.2又は1.1となるよう選択されてよい。
MDDR<1/(FminxTDDR1/2)
ここで、延伸比が2になった後の延伸の最終部分については、Fminは、0.9以上である。
x1/x0=(F2(TDDR)-1)/(TDDR-1)により関連付けられる。
MDDR=(TDDR(x1/x0)+(1−x1/x0))-1/2
±(x)/(x1)=(1/4)(x1/x0)(y/x1)2+1
に相当する関数型を有する走路を備える初期延伸領域を有し,次に、
±(x)/(x2)=(1/4)(x2/x0)((y−A)/x2)2+1
(式中、x1とx2は異なり、Aは、軌道の結合を可能とする垂直移動に相当する)に相当する関数型を有する走路を備える後部延伸領域を有してよい。任意の数の放物線状セグメントが、このようにして一体にされてよい。
((TDDR)(MDDR))-4+((TDDR)(MDDR))2−(TDDR)-2−(MDDR)-2−sin2(θ)((TDDR)(MDDR))-2=0
(式中、MDDRは、発散角のコサインである)。本開示のこの任意の方法は、次に境界軌道のこの部類を明示する。
相対複屈折=|ny-nz|/|nx-nu|
(式中、nuは2つの類似屈折率nyとnzの平均であり、差の絶対値が用いられる)で与えられる。相対複屈折は、フィルムの一軸特性が増すにつれて減少する。
ほぼ正確な一軸フィルムを作製する2つの方法を使用し、2つのポリエステル系構成体を例示する。最初の実施例の組としては、図7を参照にして本明細書に記載したようなバッチテンター工程により作製されたPET外側表面薄層を備える多層光学フィルム(MOF)が挙げられる。第2の実施例の組は、米国特許第6,939,499号、同第6,916,440号、同第6,949,212号及び同第6,936,209号に記載されたもの等の放物線状テンター工程により作製されたPEN外側表面薄層を備えるMOFを含む。
PET表面薄層を備えるMOFフィルムを、図7に記載したバッチテンター工程を使用し高度に延伸した(実施例1〜7)。延伸後のPET表面薄層の屈折率発現をメトリコンプリズムカップラー(Metricon Prism Coupler)を用い「上端」と「下端」側の平均値を使用し測定した。外側PET層が極端に薄いため、反射強度対入射角のプロットでシャープなひざよりむしろ波結合モードが観察された。精度を改善するため、屈折率は、最初の観察モードの前端の位置と同程度に一様に測定された。これは、特定環境下で調和した波モードとかなり一致するが、他の環境下でのnxの過小評価につながってもよい。nyとnzは、典型的にもっと小さいシャープな指数を有する。再度、強度低下の前端を使用した。
PEN表面薄層を備える多層光学フィルム(MOF)を放物線状テンター工程を使用し高度に延伸した。フィルムは、連続最終フィルムの単一MDレーンから使用し、初期状態の再現性を向上させた。延伸行程後PEN表面薄層の屈折率発現を、メトリコンプリズムカップラー(Metricon Prism Coupler)を使用し「上端」と「下端」側の平均を用いて計量した。PET実施例に関して、波モードと強度ひざの前端を使用した屈折率測定法を再度使用した。
コポリエステル実施例10
PENとPETの組成物中間体であるコポリエステルが、85モル%のPEN(約0.5の固有粘度(IV)を有する)と15モル%のPET(約0.8の固有粘度(IV)を有する)のペレット混合物を押出成形機に投入することにより形成された。これらは、押出成形時、その場でエステル交換し、キャストされ、いわゆる85/15coPENを含む透明で未配向のキャストウェブを形成した。この材料を含むフィルムは、多層光学フィルム、例えば反射偏光子フィルムの複屈折層として使用されてよい。
85/15coPENを形成し、実施例10と同じやり方で延伸した。この材料を含むフィルムは、多層光学フィルム、例えば反射偏光子フィルムの複屈折層として使用することが可能である。
比較例1
多層光学フィルム-PEN/CoPEN5545HD/CoPEN7525HD反射偏光子
多層反射偏光子フィルムを、ポリエチレンナフタレートから作製された第1光学層、コポリエチレンナフタレート(CoPEN5545HD)から作製された第2光学層、及びより高Tgのコポリエチレンナフタレート(CoPEN7525HD)から作製された表面薄層又は非光学層で構成した。
多層光学フィルム-CoPEN9010/CoPEN−tbia/CoPEN−tbia反射偏光子
多層反射偏光子フィルムを、コポリエチレンナフタレート(CoPEN9010)から作製された第1光学層、コポリエチレンナフタレート(CoPEN−tbia)から作製された第2光学層、及びコポリエチレンナフタレート(CoPEN−tbia)から作製された表面薄層又は非光学層で構成した。
多層光学フィルム-PEN/CoPEN5050HH/SA115反射偏光子フィルム
多層反射偏光子フィルムを、ポリエチレンナフタレートから作製された第1光学層、コポリエチレンナフタレート(CoPEN5050HH)から作製された第2光学層、及びイーストマンケミカル社(Eastman Chemical CO.)から商標名「SA115」のもとで市販のシクロ脂肪族ポリエステル/ポリカーボネートブレンドから作製された表面薄層又は非光学層で構成した。
多層光学フィルム-CoPEN9010/SA115/SA115反射偏光子フィルム
多層反射偏光子フィルムを、ポリエチレンナフタレート(CoPEN9010)から作製された第1光学層、及びイーストマンケミカル社(Eastman Chemical CO.)からシリーズ商標名「SA115」のもとで市販のシクロ脂肪族ポリエステル/ポリカーボネートブレンドから作製された第2光学層及び表面薄層で構成した。
PENの製造
第1光学層を形成するため使用したポリエチレンナフタレート(PEN)は、以下の原料、ジメチルナフタレンジカルボキシレート(136kg)、エチレングリコール(73kg)、酢酸マンガン(II)(27g)、酢酸コバルト(II)(27g)、及び酢酸アンチモン(III)(48g)をバッチ反応器に投入し,合成した。0.2MPa(2気圧(1,520トル又は2x105N/m2))の圧力下、この混合物を254℃に加熱し、同時にメタノール(エステル交換反応副生成物)を除去した。35kgのメタノールを除去後、トリエチルホスホノアセテート(49g)を反応器に投入し、圧力を0.13kPa(1トル(131N/m2))まで徐々に下げ、同時に290℃に加熱した。固有粘度0.48dL/g(フェノール/o−ジクロロベンゼン(60/40重量%)中で測定)を有するポリマーが製造されるまで縮合反応副生成物であるエチレングリコールを連続的に除去した。
第1光学層を形成するため使用したコポリエチレンナフタレート(CoPEN9010)は、以下の原料、ジメチルナフタレンジカルボキシレート126kg、ジメチルテレフタレート11kg、エチレングリコール75kg、酢酸マンガン27g、酢酸コバルト27g、及び三酢酸アンチモン48gをバッチ反応器に投入し,合成した。0.2MPa(2気圧(2x105N/m2))の圧力下、この混合物を254℃に加熱し、同時にメタノールを除去した。36kgのメタノールを除去後、トリエチルホスホノアセテート49gを反応器に投入し、次に、圧力を0.13kPa(1トル)まで徐々に下げ、同時に290℃に加熱した。フェノール/o−ジクロロベンゼン(60/40重量%)中で測定した固有粘度0.50dL/gを有するポリマーが製造されるまで縮合反応副生成物であるエチレングリコールを連続的に除去した。
第2光学層を形成するため使用したコポリエチレン−ヘキサメチレンナフタレートポリマー(CoPEN5545HD)は、以下の原料、ジメチル2,6−ナフタレンジカルボキシレート(88.5kg)、ジメチルテレフタレート(57.5kg)、1,6−ヘキサンジオール(4.7kg)、エチレングリコール(81kg)、トリメチロールプロパン(239g)、酢酸コバルト(II)(15g)、酢酸亜鉛(22g)、及び酢酸アンチモン(III)(51g)をバッチ反応器に投入し,合成した。混合物を、0.2MPa(2気圧(2x105N/m2))の圧力で温度254℃まで加熱し、反応させ、同時にメタノール反応生成物を除去した。反応を完結し、メタノール(約39.6kg)を除去後、トリエチルホスホノアセテート(37g)を反応器に投入し、圧力を0.13kPa(1トル(263N/m2))まで下げ、同時に290℃に加熱した。フェノールとo−ジクロロベンゼンの60/40重量%混合物中で測定した固有粘度0.56dL/gを有するポリマーが製造されるまで縮合副生成物であるエチレングリコールを連続的に除去した。この方法で製造したCoPEN5545HDポリマーは、示差走査熱量計により温度上昇速度20℃/分で測定したとき94℃のガラス転移温度(Tg)を有した。CoPEN5545HDポリマーは、632ナノメートルで1.612の屈折率を有した。
第2光学層を形成するため使用したコポリエチレン−ヘキサメチレンナフタレートポリマー(CoPEN7525HD)は、以下の原料、ジメチル2,6−ナフタレンジカルボキシレート(114.8kg)、ジメチルテレフタレート(30.4kg)、1,6−ヘキサンジオール(5.9kg)、エチレングリコール(75kg)、トリメチロールプロパン(200g)、酢酸コバルト(II)(15g)、酢酸亜鉛(22g)、及び酢酸アンチモン(III)(51g)をバッチ反応器に投入し,合成した。混合物を、0.2MPa(2気圧(2x105N/m2))の圧力で温度254℃まで加熱し、反応させ、同時にメタノール反応生成物を除去した。反応を完結し、メタノール(約39.6kg)を除去後、トリエチルホスホノアセテート(37g)を反応器に投入し、圧力を0.13kPa(1トル(263N/m2))まで下げ、同時に290℃に加熱した。フェノールとo−ジクロロベンゼンの60/40重量%混合物中で測定した固有粘度0.52dl/gを有するポリマーが製造されるまで縮合副生成物であるエチレングリコールを連続的に除去した。この方法で製造したCoPEN7525HDポリマーは、示差走査熱量計により温度上昇速度20℃/分で測定したとき102℃のガラス転移温度(Tg)を有した。CoPEN7525HDポリマーは、632ナノメートルで1.624の屈折率を有した。
第2光学層を形成するため使用したコポリエチレン−ヘキサメチレンナフタレートポリマー(CoPEN5050HH)は、以下の原料、ジメチル2,6−ナフタレンジカルボキシレート(80.9kg)、ジメチルテレフタレート(64.1kg)、1,6−ヘキサンジオール(15.45kg)、エチレングリコール(75.4kg)、トリメチロールプロパン(2kg)、酢酸コバルト(II)(25g)、酢酸亜鉛(40g)、及び酢酸アンチモン(III)(60g)をバッチ反応器に投入し,合成した。混合物を、0.2MPa(2気圧(2x105N/m2))の圧力で温度254℃まで加熱し、反応させ、同時にメタノール反応生成物を除去した。反応を完結し、メタノール(約42.4kg)を除去後、トリエチルホスホノアセテート(55g)を反応器に投入し、圧力を0.13kPa(1トル(263N/m2))まで下げ、同時に290℃に加熱した。フェノールとo−ジクロロベンゼンの60/40重量%混合物中で測定した固有粘度0.55dl/gを有するポリマーが製造されるまで縮合副生成物であるエチレングリコールを連続的に除去した。この方法で製造したCoPEN5050HHポリマーは、示差走査熱量計により温度上昇速度20℃/分で測定したとき85℃のガラス転移温度(Tg)を有した。CoPEN5050HHポリマーは、632ナノメートルで1.601の屈折率を有した。
CoPEN−tbiaポリマーの合成を以下の材料、ジメチル2,6−ナフタレンジカルボキシレート(47.3kg)、ジメチルテレフタレート(18.6kg)、1,4−シクロヘキサンジメタノール(40.5kg)、ネオペンチルグリコール(15kg)、エチレングリコール(41.8kg)、トリメチロールプロパン(2kg)、酢酸コバルト(II)(36.3g)、酢酸亜鉛(50g)、及び酢酸アンチモン(III)(65g)を投入したバッチ反応器で行った。混合物を、0.2MPa(2気圧(2x105N/m2))の圧力で温度254℃まで加熱し、反応させ、同時にメタノール反応生成物を除去した。
以下に、本願発明に関連する発明の実施の形態を列挙する。
実施形態1
光学フィルムを作製する方法であって、
複屈折を発現できる高分子材料を含んでなるフィルム(32)を供給し、
前記フィルム(32)を実質的に一軸配向し、及び
前記配向フィルム(32)をヒートセットする、
ことを含む光学フィルム作製方法。
実施形態2
前記配向フィルム(32)が、約0.2に等しいか又は約0.2を超える範囲の一軸特性度Uを示す、実施形態1に記載の方法。
実施形態3
前記配向フィルム(32)が、約0.7に等しいか又は約0.7を超える範囲の一軸特性度Uを示す、実施形態1に記載の方法。
実施形態4
前記ヒートセット工程が、前記フィルム(32)を、該少なくとも1つの高分子材料のガラス転移温度を超え及びその高分子材料の融点未満の温度に加熱することを含んでなる、実施形態1に記載の方法。
実施形態5
前記ヒートセット工程が、前記フィルム(32)を約1秒〜約10分の間加熱することを含んでなる、実施形態1に記載の方法。
実施形態6
前記ヒートセット工程が、前記フィルム(32)を、該各高分子材料のガラス転移温度を超え及び該各高分子材料の融点未満の温度に加熱することを含んでなる、実施形態1に記載の方法。
実施形態7
前記フィルム(32)を実質的に一軸配向する前記行程を第1温度で実施し、及び
前記ヒートセット工程において、前記フィルム(32)を前記第1温度よりも高い第2温度に加熱する、実施形態1に記載の方法。
実施形態8
複屈折を発現できる前記高分子材料が、ポリエチレンナフタレート、ポリエチレンテレフタレート、ポリプロピレン、及びシンジオタクチックポリスチレンから成る群から選択される、実施形態1に記載の方法。
実施形態9
複屈折を発現できる前記高分子材料が、ポリエステルを含む、実施形態1に記載の方法。
実施形態10
複屈折を発現できる前記高分子材料が、半結晶質高分子を含む、実施形態1に記載の方法。
実施形態11
前記フィルム(32)が、更にポリエステル/ポリカーボネートブレンドをむ、実施形態1に記載の方法。
実施形態12
前記配向光学フィルム(32)が、反射偏光子である、実施形態1に記載の工程により作製される光学フィルム(32)。
実施形態13
前記配向光学フィルム(32)が、多層反射偏光子又は拡散反射偏光子である、実施形態12に記載の工程により作製される光学フィルム(32)。
実施形態14
前記配向光学フィルム(32)が、補償素子である、実施形態1に記載の工程により作製される光学フィルム(32)。
実施形態15
フィルム(32)を供給する前記行程が、フィルムひと巻きを供給する、実施形態1に記載の方法。
実施形態16
フィルム(32)を供給する前記行程が、押出成形機から前記フィルム(32)を供給することを含んでなる、実施形態1に記載の方法。
実施形態17
フィルム(32)を供給する前記行程が、延伸方向の初期屈折率、前記延伸方向と直交する面内方向の初期屈折率及び厚さ方向の初期屈折率を有するフィルム(32)を供給し、並びに
前記ヒートセット工程が、前記延伸方向と直交する前記面内方向の前記初期屈折率より大きい前記延伸方向と直交する前記面内方向の最終屈折率をもたらす、実施形態1に記載の方法。
実施形態18
前記ヒートセット工程が、前記厚さ方向の前記初期屈折率より大きい前記厚さ方向の最終屈折率をもたらす、実施形態17に記載の方法。
実施形態19
フィルム(32)を供給する前記行程が、延伸方向の初期屈折率、前記延伸方向と直交する面内方向の初期屈折率及び厚さ方向の初期屈折率を有するフィルム(32)を供給し、並びに
前記ヒートセット工程が、前記厚さ方向の前記初期屈折率より大きい前記厚さ方向の最終屈折率をもたらす、実施形態1に記載の方法。
実施形態20
フィルム(32)を供給する前記行程が、延伸方向と直交する面内方向の初期屈折率と厚さ方向の初期屈折率との初期差を有するフィルム(32)を供給し、及び
前記ヒートセット工程が、前記延伸方向と直交する前記面内方向の最終屈折率と前記厚さ方向の最終屈折率の最終差をもたらし、前記最終差が、前記初期差未満である、実施形態1に記載の方法。
実施形態21
フィルム(32)を供給する前記行程が、延伸方向の初期屈折率、前記延伸方向と直交する面内方向の初期屈折率及び厚さ方向の初期屈折率を有するフィルム(32)を供給し、及び
前記ヒートセット工程が、前記延伸方向の前記初期屈折率より大きい前記延伸方向の最終屈折率をもたらす、実施形態1に記載の方法。
実施形態22
フィルム(32)を供給する前記行程が、延伸方向の初期屈折率と延伸方向と直交する面内方向の初期屈折率との初期差を有するフィルム(32)を供給し、また
前記ヒートセット工程が、前記延伸方向の最終屈折率と前記延伸方向と直交する前記面内方向の最終屈折率との初期差をもたらし、前記最終差が前記初期差未満である、実施形態1に記載の方法。
実施形態23
前記フィルム(32)を実質的に一軸配向する前記行程が、前記フィルム(32)の非連続部分をテンター装置で延伸することを含む、実施形態1に記載の方法。
実施形態24
前記フィルム(32)を実質的に一軸配向する前記行程が、前記フィルム(32)を横方向に延伸することを含む、実施形態1に記載の方法。
実施形態25
更に、前記配向フィルム(32)を冷却することを含む、実施形態1に記載の方法。
実施形態26
前記フィルム(32)が、複数個の層を含み、及び
前記フィルム(32)が、複数個の層を含み、及び
前記ヒートセット工程が、隣接した層間の接着を増加させる、実施形態1に記載の方法。
実施形態27
前記フィルム(32)が、有意なひずみ誘起結晶化が発生する延伸比であるひずみ誘起結晶点を有し、及び
前記フィルム(32)を実質的に配向にする前記行程が、前記ひずみ誘起結晶点より大きい延伸比で前記フィルム(32)を延伸することを含む、実施形態1に記載の方法。
実施形態28
前記フィルム(32)を実質的に一軸配向する前記行程が、前記フィルム(32)を第1延伸比で延伸方向に延伸することを含み、また
前記ヒートセット工程が、前記フィルム(32)を前記前記第1延伸比より大きい第2延伸比で前記延伸方向に延伸することを含む、実施形態1に記載の方法。
実施形態29
前記フィルム(32)を実質的に一軸配向する前記行程が、前記フィルム(32)を第1延伸比で延伸方向に延伸することを含み、また
前記ヒートセット工程が、前記フィルム(32)を前記前記第1延伸比より小さい第2延伸比で前記延伸方向に延伸することを含む、実施形態1に記載の方法。
実施形態30
前記フィルム(32)を実質的に一軸配向する前記行程が、前記フィルム(32)を第1延伸比で延伸方向に延伸することを含み、また
前記ヒートセット工程が、前記フィルム(32)を前記前記第1延伸比にほぼ等しい第2延伸比で前記延伸方向に延伸することを含む、実施形態1に記載の方法。
実施形態31
前記フィルム(32)が、初期密度を備え、また
前記ヒートセット工程が、前記初期密度より大きい最終密度を有する前記フィルム(32)を生成する、実施形態1に記載の方法。
実施形態32
フィルム(32)を供給する前記行程が、層の少なくとも1つが非晶質材料を含む複数個の層を有するフィルム(32)を供給することを含み、また
前記ヒートセット工程が、前記非晶質材料を含む前記層の非晶質特性を保持することを含む、実施形態1に記載の方法。
実施形態33
前記非晶質材料が、ポリカーボネート又はポリカーボネートとコポリエステルのブレンドを含む、実施形態32に記載の方法。
実施形態34
更に、第2ヒートセット工程を含む、実施形態1に記載の方法。
実施形態35
フィルム(32)を加工する方法であって、
フィルム(32)を機械方向に沿って搬送すると同時に前記フィルム(32)の対向する端部部分を保持する工程、
前記対向する端部部分を広がった曲線状経路に沿って移動することにより前記フィルム(32)を延伸して延伸フィルム(32)を形成する工程、及び
前記延伸フィルム(32)をヒートセット工程を含む方法。
実施形態36
前記広がった経路が、実質的に放物線状である、実施形態35に記載の方法。
実施形態37
前記ヒートセット工程が、前記フィルム(32)を、そのフィルムの少なくとも1つの高分子構成成分のTgを超える温度に加熱することを含む、実施形態35に記載の方法。
実施形態38
前記ヒートセット工程が、前記フィルム(32)を、そのフィルムのすべての高分子構成成分のTgを超える温度に加熱する、実施形態35に記載の方法。
実施形態39
前記ヒートセット工程が、前記フィルム(32)を、前記フィルム(32)のTgと融点の間の温度に加熱することを含む、実施形態35に記載の方法。
実施形態40
前記フィルム(32)の延伸工程は、前記フィルム(32)を、4を超過する延伸比まで延伸することを含む、実施形態35に記載の方法。
実施形態41
実施形態35に記載の工程により作製されるフィルム(32)。
実施形態42
33%を超える結晶化度を有するポリエチレンテレフタレートを含む光学フィルム(32)。
実施形態43
36%を超える結晶化度を有するポリエチレンテレフタレートを含む、実施形態42に記載の前記光学フィルム(32)。
実施形態44
39%を超える結晶化度を有するポリエチレンテレフタレートを含む、実施形態42に記載の前記光学フィルム(32)。
実施形態45
28%を超える結晶化度を有するポリエチレンナフタレート(napthalate)を含む光学フィルム(32)。
実施形態46
30%を超える結晶化度を有するポリエチレンナフタレート(napthalate)を含む、実施形態45に記載の前記光学フィルム(32)。
実施形態47
48%を超える結晶化度を有するポリエチレンナフタレート(napthalate)を含む、実施形態45に記載の前記光学フィルム(32)。
Claims (1)
- フィルム(32)を加工する方法であって、
延伸方向の初期屈折率、前記延伸方向と直交する面内方向の初期屈折率及び厚さ方向の初期屈折率を有するポリエステルフィルム(32)を機械方向に沿って搬送すると同時に前記フィルム(32)の対向する端部部分を保持する工程、
前記対向する端部部分を広がった、曲線状の経路に沿って移動することにより前記フィルム(32)を延伸して延伸フィルム(32)を形成する工程、及び
前記延伸フィルム(32)をヒートセット工程を含み、前記ヒートセット工程が、前記延伸方向と直交する前記面内方向の前記初期屈折率より大きい前記延伸方向と直交する前記面内方向の延伸フィルムの最終屈折率をもたらす、方法。