WO2006035822A1 - ハニカム構造体 - Google Patents

ハニカム構造体 Download PDF

Info

Publication number
WO2006035822A1
WO2006035822A1 PCT/JP2005/017868 JP2005017868W WO2006035822A1 WO 2006035822 A1 WO2006035822 A1 WO 2006035822A1 JP 2005017868 W JP2005017868 W JP 2005017868W WO 2006035822 A1 WO2006035822 A1 WO 2006035822A1
Authority
WO
WIPO (PCT)
Prior art keywords
catalyst
porous ceramic
cam structure
porosity
layer
Prior art date
Application number
PCT/JP2005/017868
Other languages
English (en)
French (fr)
Inventor
Kazushige Ohno
Hiroki Sato
Masayuki Hayashi
Kazutake Ogyu
Original Assignee
Ibiden Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ibiden Co., Ltd. filed Critical Ibiden Co., Ltd.
Priority to EP05787923A priority Critical patent/EP1795262B1/en
Priority to AT05787923T priority patent/ATE456397T1/de
Priority to JP2006537776A priority patent/JP5142529B2/ja
Priority to DE602005019182T priority patent/DE602005019182D1/de
Publication of WO2006035822A1 publication Critical patent/WO2006035822A1/ja
Priority to US11/496,431 priority patent/US7731774B2/en

Abstract

本発明は、全体の気孔に対する気孔径が１０μｍ以下の細孔の割合や気孔率に応じ、圧力損失が増大しないように触媒担体や触媒を担持させることができ、かつ、触媒機能を充分に果たすことが可能なハニカム構造体を提供することを目的とするものであり、本発明のハニカム構造体は、壁部を隔てて長手方向に貫通する複数のセルのいずれか一方の端部が封止されてなる多孔質セラミック部材が接着剤層を介して複数個接着され、前記壁部に触媒担持層が付着したハニカム構造体であって、前記多孔質セラミック部材の全気孔容積に対する気孔径１０μｍ以下の気孔容積の割合をＸ１（％）、気孔率をＹ１（％）、前記触媒担持層の重量をＺ１（ｇ／ｌ）とした際、これらＸ１、Ｙ１、Ｚ１は、下記の（１）、（２）式を満たすことを特徴とする。 Ｘ１≦２０－Ｚ１／１０・・・（１） Ｙ１≧３５＋７Ｚ１／４０・・・（２） （但し、２０≦Ｚ１≦１５０）

Description

ノヽニカム構造体
技術分野
[0001] 本発明は、ディーゼルエンジン等の内燃機関カゝら排出される排気ガス中のパティキュ レート等を除去するフィルタや、触媒担体等として用いられるハニカム構造体に関す る。
背景技術
[0002] バス、トラック等の車両や建設機械等の内燃機関力も排出される排気ガス中に含有さ れるスス等のパティキュレートが環境や人体に害を及ぼすことが最近問題となってい る。
そこで、排気ガス中のパティキュレートを捕集して、排気ガスを浄ィ匕するフィルタとして 多孔質セラミック力 なるハ-カム構造体を用いたものが種々提案されて 、る。
[0003] 従来、この種のハニカム構造体として、特許文献 1には、隔壁を隔てて長手方向に延 びる多数の貫通孔のいずれか一方の端部が封止されて多数のセルが形成された多 孔質コ一ディエライトからなるフィルタであって、
上記フィルタ（多孔質コーディエライト）の細孔分布力 細孔径 10 μ m未満の細孔容 積:全細孔容積の 15%以下、細孔径 10〜50 mの細孔容積:全容積の 75%以上 、細孔径 50 mを超える細孔容積:全細孔容積の 10%以下としたフィルタが開示さ れている。
[0004] 特許文献 1には、その効果として、パティキュレートの捕集効率が高ぐ細孔へのパテ ィキュレートの目詰まりによる圧力損失の増大を防止することができることが記載され ている。
また、特許文献 1の段落番号 [0026]には、細孔径 10 m未満の細孔容積が全細孔 容積の 15%を超えると、フィルタに触媒を付着させる際に、触媒による細孔の目詰ま りにより、圧力損失の増大を生じてしまうことが記載されて 、る。
[0005] 特許文献 2には、特許文献 1と同様の構造を有し、隔壁にパティキュレートを酸ィ匕除 去するための触媒を付着した排ガス浄ィ匕フィルタであって、 気孔率が 55〜80%、平均細孔径が 30〜50 μ m、細孔径 100 μ m以上の細孔容積 が全体の 5%以下のものが開示されている。
[0006] この特許文献 2には、隔壁内部までパティキュレートを侵入させることができ、触媒反 応面積が大きぐ破損、溶損を抑制することができ、高捕集効率のものであることが記 載さている。
[0007] 特許文献 1 :特開 2002— 219319号公報
特許文献 2：特開 2002— 357114号公報
発明の開示
発明が解決しょうとする課題
[0008] 特許文献 1には、気孔率、気孔径の関係についての記載がある力 触媒担持量につ いての記載がされておらず、また、特許文献 2には、平均細孔径と細孔径 100 m以 上と細孔径の大き 、ものの割合が記載されて 、るが、細孔径の小さなものにっ 、て は記載されていな力つた。
課題を解決するための手段
[0009] 本願発明者は、触媒担持層の量に着目したところ、同じ気孔径、気孔率であっても、 触媒担持層の量によっては、細孔に目詰まりが生じる場合があることを見出し、更に 鋭意研究を進めたところ、触媒機能を充分に果たすことができる触媒担持量と、その 量の触媒を担持した際に、圧力損失が増大しないような、フィルタ (ハ-カム構造体） の気孔径、気孔率との関係を見出し、本発明を完成させるに至った。
[0010] すなわち、第一の本発明のハ-カム構造体は、壁部を隔てて長手方向に貫通する 複数のセルのいずれか一方の端部が封止されてなる多孔質セラミック部材が接着剤 層を介して複数個接着され、上記壁部に触媒担持層が付着したハ-カム構造体で あって、
上記多孔質セラミック部材の全気孔容積に対する気孔径 10 μ m以下の気孔容積の 割合を X (%)、気孔率を Y (%)、上記触媒担持層の重量を Z (gZDとした際、これ ら X、 Y、 Zは、下記の（1)、（2)式を満たすことを特徴とする。
X≤20— Z /10· · · (1)
Υ≥35 + 7Ζ /40· · · (2) (但し、 20≤Z≤150)
なお、上記触媒担持層の重量∑ェは、上記ハ-カム構造体のみかけ体積 1リットルあた りの重量 (g)である。
[0011] 第二の本発明のハ-カム構造体は、壁部を隔てて長手方向に貫通する複数のセル のいずれか一方の端部が封止され、上記壁部に触媒担持層が付着した多孔質セラ ミック力 なるハ-カム構造体であって、
上記多孔質セラミックの全気孔容積に対する気孔径 10 μ m以下の気孔容積の割合 を X (%)、気孔率を Y (%)、上記触媒担持層の重量を Z (gZDとした際、これら X
2 2 2 2
、 Y 、 Zは、下記の（3)、（4)式を満たすことを特徴とする。
2 2
X≤20-Ζ Ζ10· · · (3)
2 2
Υ≥35 + 7Ζ /40· · · (4)
2 2
(但し、 20≤Ζ≤150)
2
なお、上記触媒担持層の重量 Ζは、上記ハ-カム構造体のみかけ体積 1リットルあた
2
りの重量 (g)である。
[0012] 第一の本発明のハ-カム構造体は、炭化珪素質セラミック力 なることが望ましぐ第 二の本発明のハ-カム構造体は、コーディエライトからなることが望ましい。
なお、以下においては、第一の本発明のハ-カム構造体のような、多孔質セラミック 部材が接着剤層を介して複数個組み合わされた構造を有するハ-カム構造体を集 合体型ハ-カム構造体ともいい、一方、第二の本発明のハ-カム構造体のような、全 体が一体として形成された構造を有するハニカム構造体を一体型ハニカム構造体と もいう。また、一体型ハニカム構造体と集合体型ハニカム構造体とを特に区別する必 要がない場合には、単にハ-カム構造体という。
発明の効果
[0013] 第一の本発明のハ-カム構造体によれば、触媒担持層の量と、多孔質セラミック部 材の気孔径、気孔率との関係を上記のように規定したので、第一の本発明のハ-カ ム構造体は、上記触媒担持層に触媒を担持させることにより、触媒機能を充分に果 たすことができ、触媒付与後の圧力損失の増大を防止することができる。
[0014] 第二の本発明のハ-カム構造体によれば、触媒担持層の量と、多孔質セラミックの気 孔径、気孔率との関係を上記のように規定したので、第二の本発明のハ-カム構造 体は、上記触媒担持層に触媒を担持させることにより、触媒機能を充分に果たすこと 力 Sでき、触媒付与後の圧力損失の増大を防止することができる。
発明を実施するための最良の形態
[0015] 第一の本発明のハ-カム構造体は、壁部を隔てて長手方向に貫通する複数のセル のいずれか一方の端部が封止されてなる多孔質セラミック部材が接着剤層を介して 複数個接着され、上記壁部に触媒担持層が付着したハ-カム構造体であって、 上記多孔質セラミック部材の全気孔容積に対する気孔径 10 μ m以下の気孔容積の 割合を X (%)、気孔率を Y (%)、上記触媒担持層の重量を Z (gZDとした際、これ ら X、 Y、 Zは、下記の（1)、 （2)式を満たすことを特徴とするハ-カム構造体。 X≤20— Z /10· · · (1)
Υ≥35 + 7Ζ /40· · · (2)
(但し、 20≤Z≤150)
[0016] 図 1は、第一の本発明に係るハ-カム構造体を模式的に示す斜視図であり、図 2 (a) は、図 1に示したハ-カム構造体を構成する多孔質セラミック部材の斜視図であり、 ( b)は、（a)に示した多孔質セラミック部材の A— A線断面図である。
[0017] 図 1に示すように、第一の本発明のハ-カム構造体は、集合型のハ-カム構造体 10 であり、炭化珪素等力もなる多孔質セラミック部材 20が、接着剤層 11を介して複数個 組み合わされて円柱状のセラミックブロック 15を構成し、このセラミックブロック 15の周 囲にシール材層（コート層） 12が形成されている。
[0018] 図 1に示した第一の本発明のハ-カム構造体 10では、セラミックブロックの形状は円 柱状である力 本発明において、セラミックブロックは、柱状であれば円柱状に限定さ れることはなぐ例えば、楕円柱状や角柱状等任意の形状のものであってもよい。
[0019] 多孔質セラミック部材 20は、図 2 (a)、 (b)に示したように、長手方向に多数のセル 21 が並設され、セル 21同士を隔てるセル壁 (壁部） 23がフィルタとして機能するようにな つている。即ち、多孔質セラミック部材 20に形成されたセル 21は、図 2 (b)に示したよ うに、排気ガスの入口側又は出口側の端部のいずれかが封止材 22により目封じされ 、一のセル 21に流入した排気ガスは、必ずセル 21を隔てるセル壁 23を通過した後、 他のセル 21から流出するようになって!/、る。
[0020] 第一の本発明のハ-カム構造体は、主として多孔質セラミック力もなり、その材料とし ては、例えば、窒化アルミニウム、窒化ケィ素、窒化ホウ素、窒化チタン等の窒化物 セラミック、炭化珪素、炭化ジルコニウム、炭化チタン、炭化タンタル、炭化タンダステ ン等の炭化物セラミック、アルミナ、ジルコユア、コージユライト、ムライト、シリカ等の酸 化物セラミック等を挙げることができる。また、ハ-カム構造体 10は、シリコンと炭化珪 素との複合体、チタン酸アルミニウムと 、つた 2種類以上の材料力も形成されて 、るも のであってもよい。シリコンと炭化珪素との複合体を用いる場合には、シリコンを全体 の 0〜45重量％となるように添加することが望まし!/、。
上記多孔質セラミックの材料としては、耐熱性が高ぐ機械的特性に優れ、かつ、熱 伝導率も高い炭化珪素質セラミックが望ましい。なお、炭化珪素質セラミックとは、炭 化珪素が 60wt%以上のものをいうものとする。
[0021] 第一の本発明のハ-カム構造体 10は、触媒担持層が付着したハ-カム構造体であ り、該触媒担持層に触媒を担持させる。
上記触媒としては特に限定されな 、が、パティキュレートの燃焼の活性ィ匕エネルギー を低下させパティキュレートを燃えやすくするものや、 CO、 HC及び NOx等の排気ガ ス中の有害なガス成分を浄ィ匕することができるもの等が望ましぐ例えば、白金、パラ ジゥム、ロジウム等の貴金属等を挙げることができる。なかでも、白金、パラジウム、口 ジゥム力もなる、いわゆる三元触媒が望ましい。また、貴金属に加えて、アルカリ金属 (元素周期表 1族)、アルカリ土類金属 (元素周期表 2族)、希土類元素 (元素周期表 3族）、遷移金属元素等を担持させてもよい。
[0022] このようなハ-カム構造体 10に触媒担持層が付着し、該触媒担持層に触媒が担持さ れることにより、ハ-カム構造体 10は、排気ガス中のパティキュレートを捕集するフィ ルタとして機能するとともに、排気ガスに含有される CO、 HC及び NOx等を浄化する ための触媒コンバータとして機能する。
[0023] また、ハ-カム構造体 10の触媒担持層に触媒を付着させる際には、予めその表面を アルミナ等の触媒担持層で被覆した後に、上記触媒を付着させることが望ましい。こ れにより、比表面積を大きくして、触媒の分散度を高め、触媒の反応部位を増やすこ とができる。また、触媒担持層によって触媒金属のシンタリングを防止することができ るので、触媒の耐熱性も向上する。
[0024] 上記触媒担持層としては、例えば、アルミナ、チタ-ァ、ジルコユア、シリカ、セリア等 の酸ィ匕物セラミックが挙げられる。
[0025] 第一の本発明では、多孔質セラミック部材の全気孔容積に対する気孔径 10 m以 下の気孔容積の割合を X (%)、気孔率を Y (%)、上記触媒担持層の重量を Z (g
ZDとした際、これら X、 Y、 Zは、下記の（1)、（2)式を満たすことを特徴とする。
X ≤20— Z /10 · · · ( 1)
Υ ≥35 + 7Ζ /40 · · · (2)
(但し、 20≤Z ≤150)
[0026] 上記（1)、 （2)式となるように、触媒担持層の量に従って、多孔質セラミック部材の気 孔径ゃ気孔率を調整することによって、排ガスの浄ィ匕等の機能を充分に果たしなが ら、圧力損失の上昇を防止することができるハ-カム構造体を提供することができる。
[0027] X力 Z /10を超えた場合には、多孔質セラミック部材 20を構成する壁部の全 気孔容積に対する気孔径 10 μ m以下の細孔の気孔容積の割合が触媒担持層の付 着量に対して多くなるので、細孔に触媒担持層が付着することによる圧力損失が大き くなりやすい。
なお、この明細書において、セル壁とは、セルを隔てる部分をいい、壁部とは、セル 壁を含む多孔質セラミック部材 20の全体をいうものとする。
[0028] また、 Y力 S35 + 7Z Z40よりも小さい場合には、気孔自体の容積が触媒担持層の付 着量に比べて少ないので、細孔に触媒担持層が付着することにより気孔の容積が減 少し、圧力損失が大きくなりやすい。
[0029] 多孔質セラミック部材 20の気孔率 Yは特に限定されないが、望ましい下限は 38. 5
%であり、望ましい上限は 75%である。 38. 5%未満であると、触媒担持層を付着さ せた際に、ハ-カム構造体 10が目詰まりを起こしやすぐ圧損が高くなる。一方、 75
%を超えると、ハ-カム構造体 10の強度が低下して容易に破壊されることがある。
[0030] 多孔質セラミック部材 20の気孔率 Yの下限は、 40%がより望ましぐ多孔質セラミツ ク部材 20の気孔率の上限は、 65%がより望ましい。 [0031] 触媒担持層の量 (Z^は、 20〜150gZlである。触媒担持層の量を、上記範囲とする ことにより、触媒を良好に分散させることができ、かつ、圧力損失の上昇を防止するこ とがでさる。
[0032] ハ-カム構造体 10の平均気孔径の望ましい下限は 10 μ mであり、望ましい上限は 5 0 mである。平均気孔径が 10 m未満であると、触媒担持層付着後の圧損が高く なり、一方、平均気孔径が 50 mを超えると、パティキュレートが気孔を通り抜けてし まい、該パティキュレートを捕集することができず、フィルタとして機能しないことがある なお、上記気孔率は、例えば、水銀圧入法、アルキメデス法及び走査型電子顕微鏡 (SEM)による測定等の従来公知の方法により測定することができる。
[0033] ハ-カム構造体 10を製造する際に使用するセラミックの粒径としては特に限定されな いが、後の焼成工程で収縮が少ないものが望ましぐ例えば、 0. 3〜50 /ζ πι程度の 平均粒径を有する粉末 100重量部と、 0. 1〜1. 0 m程度の平均粒径を有する粉 末 5〜65重量部とを組み合わせたものが望ましい。
上記粒径のセラミック粉末を配合し、混合することで、気孔率や気孔径が 10 m以下 の細孔の割合をある程度制御することができる。
[0034] 多孔質セラミック部材 20を構成する封止材 22と壁部 23とは、同じ多孔質セラミックか らなることがより望ましい。これにより、両者の密着強度を高くすることができるとともに 、封止材 22の気孔率を壁部 23と同様に調整することで、壁部 23の熱膨張率と封止 材 22の熱膨張率との整合を図ることができ、製造時や使用時の熱応力によって封止 材 22と壁部 23との間に隙間が生じたり、封止材 22や封止材 22に接触する部分の壁 部 23にクラックが発生したりすることを防止することができる。なお、壁部は、セル 21 同士を隔てるセル壁及び外周部分の両方を意味するものとする。
[0035] 封止材 22の厚さは特に限定されないが、例えば、封止材 22が多孔質炭化珪素から なる場合には、 l〜20mmであることが望ましぐ 3〜： LOmmであることがより望ましい
[0036] セル壁 23の厚さは特に限定されないが、望ましい下限は 0. 1mmであり、望ましい上 限は 0. 6mmである。 0. 1mm未満であると、ハ-カム構造体 10の強度が充分でな いことがある。 0. 6mmを超えると、圧力損失が高くなる。
[0037] 本発明のハ-カム構造体 10において、接着剤層 11は、多孔質セラミック部材 20間 に形成され、複数個の多孔質セラミック部材 20同士を結束する接着剤 (又は、シー ル材）として機能するものであり、一方、シール材層 12は、ハ-カムブロック 15の外周 面に形成され、ハ-カム構造体 10を内燃機関の排気通路に設置した際、ハ-カムブ ロック 15の外周面力もセルを通過する排気ガスが漏れ出すことを防止するためのシ ール材として、また、ハ-カムブロック 15の外周形状を整えると共に強度を向上させ るための補強材として機能するものである。
なお、多孔質セラミック部材 10において、接着剤層 11とシール材層 12とは、同じ材 料力もなるものであってもよぐ異なる材料からなるものであってもよい。さらに、接着 剤層 11及びシール材層 12が同じ材料カゝらなるものである場合、その材料の配合比 は同じであってもよぐ異なっていてもよい。また、緻密質でも、多孔質でもよい。
[0038] 接着材層 11及びシール材層 12を構成する材料としては特に限定されず、例えば、 無機バインダーと有機バインダーと無機繊維及び/又は無機粒子とからなるもの等 を挙げることができる。
[0039] 上記無機バインダーとしては、例えば、シリカゾル、アルミナゾル等を挙げることがで きる。これらは、単独で用いてもよぐ 2種以上を併用してもよい。上記無機バインダー のなかでは、シリカゾノレが望ましい。
[0040] 上記有機バインダーとしては、例えば、ポリビュルアルコール、メチルセルロース、ェ チルセルロース、カルボキシメチルセルロース等を挙げることができる。これらは、単 独で用いてもよぐ 2種以上を併用してもよい。上記有機バインダーのなかでは、カル ボキシメチルセルロースが望まし 、。
[0041] 上記無機繊維としては、例えば、シリカ アルミナ、ムライト、アルミナ、シリカ等のセラ ミックファイバ一等を挙げることができる。これらは、単独で用いてもよぐ 2種以上を併 用してもよい。上記無機繊維のなかでは、シリカ アルミナファイバーが望ましい。
[0042] 上記無機粒子としては、例えば、炭化物、窒化物等を挙げることができ、具体的には 、炭化珪素、窒化珪素、窒化硼素等力 なる無機粉末等を挙げることができる。これ らは、単独で用いてもよぐ 2種以上を併用してもよい。上記無機粒子のなかでは、熱 伝導性に優れる炭化珪素が望ま ヽ。
[0043] さらに、シール材層ゃ接着剤層を形成するために用いるペーストには、必要に応じて 酸化物系セラミックを成分とする微小中空球体であるバルーンや、球状アクリル粒子 、グラフアイト等の造孔剤を添加してもよい。
上記バルーンとしては特に限定されず、例えば、アルミナバルーン、ガラスマイクロバ ルーン、シラスバルーン、フライアッシュバルーン（FAバルーン）、ムライトバルーン等 を挙げることができる。これらのなかでは、アルミナバルーンが望ましい。
[0044] 上記触媒担持層に触媒が担持された本発明のハ-カム構造体は、従来公知の触媒 付 DPF (ディーゼル ·パティキュレート ·フィルタ）と同様のガス浄ィ匕装置として機能す るものである。従って、ここでは、本発明の一体型ハ-カム構造体が触媒担持体とし ても機能する場合の詳し 、説明を省略する。
[0045] 次に本発明のハ-カム構造体の製造方法の一例について説明する。
まず、上述したようなセラミックを主成分とする原料ペーストを用いて押出成形を行い
、四角柱形状のセラミック成形体を作製する。
[0046] 上記原料ペーストとしては特に限定されないが、製造後のハ-カム構造体の気孔率 力 5〜75%となるものが望ましぐ例えば、上述したようなセラミック力もなる粉末 に、バインダー及び分散媒液等を加えたものを挙げることができる。
[0047] 上記セラミック粉末の粒径は特に限定されないが、後の焼成工程で収縮の少ないも のが好ましぐ例えば、 0. 3〜50 111程度の平均粒径を有する粉末100重量部と0.
1〜1. 0 m程度の平均粒径を有する粉末 5〜65重量部とを組み合わせたものが好 ましい。
多孔質セラミック部材の気孔径等を調節するためには、焼成温度を調節する必要も あるが、セラミック粉末の粒径を調節することにより、気孔径を調節することができる。
[0048] 上記バインダーとしては特に限定されず、例えば、メチルセルロース、カルボキシメチ ルセルロース、ヒドロキシェチルセルロース、ポリエチレングリコール、フエノール榭脂 、エポキシ榭脂等を挙げることができる。
上記バインダーの配合量は、通常、セラミック粉末 100重量部に対して、 1〜： LO重量 部程度が望ましい。 [0049] 上記分散媒液としては特に限定されず、例えば、ベンゼン等の有機溶媒、メタノール 等のアルコール、水等を挙げることができる。
上記分散媒液は、上記原料ペーストの粘度が一定範囲内となるように適量配合され る。
[0050] これらセラミック粉末、バインダー及び分散媒液は、アトライター等で混合し、ニーダ 一等で充分に混練した後、押出成形される。
[0051] また、上記原料ペーストには、必要に応じて成形助剤を添加してもよい。
上記成形助剤としては特に限定されず、例えば、エチレングリコール、デキストリン、 脂肪酸石鹼、ポリビニルアルコール等を挙げることができる。
[0052] さらに、上記原料ペーストには、必要に応じて酸化物系セラミックを成分とする微小中 空球体であるバルーンや、球状アクリル粒子、グラフアイト等の造孔剤を添加してもよ い。
上記バルーンとしては特に限定されず、例えば、アルミナバルーン、ガラスマイクロバ ルーン、シラスバルーン、フライアッシュバルーン（FAバルーン）、ムライトバルーン等 を挙げることができる。これらのなかでは、アルミナバルーンが望ましい。
[0053] 次に、上記セラミック成形体を、マイクロ波乾燥機、熱風乾燥機、誘電乾燥機、減圧 乾燥機、真空乾燥機、凍結乾燥機等を用いて乾燥させ、セラミック乾燥体とする。次 いで、入口側セル群の出口側の端部、及び、出口側セル群の入口側の端部に、封 止材となる封止材ペーストを所定量充填し、セルを目封じする。
[0054] 上記封止材ペーストとしては特に限定されないが、後工程を経て製造される封止材 の気孔率が 30〜75%となるものが望ましぐ例えば、上記原料ペーストと同様のもの を用いることができる。
[0055] 次に、上記封止材ペーストが充填されたセラミック乾燥体に対して、所定の条件で脱 脂（例えば、 200〜500°C)、焼成（例えば、 1400〜2300°C)を行うことにより、多孔 質セラミック力 なり、その全体が一の焼結体力 構成された多孔質セラミック部材 20 を製造することができる。
上記セラミック乾燥体の脱脂及び焼成の条件は、従来から多孔質セラミックからなる フィルタを製造する際に用いられている条件を適用することができる。 [0056] また、本発明のハ-カム構造体では、次に、多孔質セラミック部材 20の側面に、接着 材層 11となる接着剤ペーストを均一な厚さで塗布して接着剤ペースト層を形成し、こ の接着剤ペースト層の上に、順次他の多孔質セラミック部材 20を積層する工程を繰 り返し、所定の大きさの多孔質セラミック部材集合体を作製する。
なお、上記接着剤ペーストを構成する材料としては、既に説明しているのでここでは その説明を省略する。
[0057] 次に、この多孔質セラミック部材集合体を加熱して接着剤ペースト層を乾燥、固化さ せて接着材層 11とする。
次に、ダイヤモンドカッター等を用い、多孔質セラミック部材 20が接着材層 11を介し て複数個接着された多孔質セラミック部材集合体に切削加工を施し、円柱形状のセ ラミックブロック 15を作製する。
[0058] そして、ハ-カムブロック 15の外周に上記シール材ペーストを用いてシール材層 12 を形成することで、多孔質セラミック部材 20が接着材層 11を介して複数個接着され た円柱形状のセラミックブロック 15の外周部にシール材層 12が設けられたノヽ-カム 構造体 10を製造することができる。
[0059] 本発明は、触媒担持層が形成されてなるが、この触媒担持層には、貴金属等の触媒 が付与されることが望ましい。
[0060] なお、こののち、触媒を担持するが、上記集合体を製作する前でも力まわない。
上記セラミック焼成体の表面にアルミナ力 なる触媒担持層を形成する方法としては
、例えば、アルミナ粉末を含有する溶液をセラミック焼成体に含浸させて加熱する方 法等を挙げることができる。
[0061] その後に、更に、 Ce (NO )等の希土類元素等を含有する金属化合物の溶液をセラ
3 3
ミック焼成体に含浸させてもよ 、。
なお、アルミナ粉末を作る際に、 Ce (NO )等の希土類元素等を含有する金属化合
3 3
物の溶液と、 Al (NO ) 等のアルミニウムを含有する金属化合物の溶液を混ぜて、予
3 3
め、混在させ、アルミナ、セリアが混在する粉末を粉砕して、担持させてもよい。
上記アルミナ膜に触媒を付与する方法としては、例えば、ジニトロジアンミン白金硝酸 溶液（[Pt (NH ) (NO ) ]HNO )等をセラミック焼成体に含浸させて加熱する方法 等を挙げることができる。
[0062] 第一の本発明のハ-カム構造体の用途は特に限定されないが、車両の排気ガス浄 化装置に用いることが望ましい。下記する第二の本発明のハ-カム構造体も同様で ある。
図 3は、本発明のハ-カム構造体が設置された車両の排気ガス浄ィ匕装置の一例を模 式的に示した断面図である。
[0063] 図 3に示したように、排気ガス浄化装置 70は、主に、ハ-カム構造体 10、ハ-カム構 造体 10の外方を覆うケーシング 71、ハ-カム構造体 10とケーシング 71との間に配 置される保持シール材 72から構成されており、ケーシング 71の排気ガスが導入され る側の端部には、エンジン等の内燃機関に連結された導入管 74が接続されており、 ケーシング 71の他端部には、外部に連結された排出管 75が接続されている。なお、 図 6中、矢印は排気ガスの流れを示している。
[0064] このような構成力もなる排気ガス浄ィ匕装置 70では、エンジン等の内燃機関から排出さ れた排気ガスは、導入管 74を通ってケーシング 71内に導入され、入口側セル力ゝらハ 二カム構造体内に流入し、壁部を通過して、この壁部でパティキュレートが捕集され て浄化された後、出口側セル力もハ-カム構造体外に排出され、排出管 75を通って 外部へ排出されることとなる。また、ハ-カム構造体には、触媒が付着しており、 CO、 HC及び NOx等の排気ガス中の有害なガス成分を浄ィ匕することができる。
[0065] また、排気ガス浄ィ匕装置 70では、ハ-カム構造体の壁部に大量のパティキュレート が堆積し、圧力損失が高くなると、ハ-カム構造体の再生処理が行われる。
上記再生処理では、ポストインジェクション方式を用いてパティキュレートを燃焼除去 してもよいし、更にハ-カム構造体の前に触媒担持層及び触媒層を形成し、その反 応熱を利用してもよい。また、図示しない加熱手段を用いて加熱されたガスをハ-カ ム構造体のセルの内部へ流入させることで、ハ-カム構造体を加熱し、壁部に堆積し たパティキュレートを燃焼除去してもよ 、。
触媒を付着させた本発明のハ-カム構造体では、触媒の種類等により、通常の温度 より低い温度でパティキュレートを燃焼除去することが可能となる。
[0066] 次に、第二の本発明について説明する。 第二の本発明のハ-カム構造体は、壁部を隔てて長手方向に貫通する複数のセル のいずれか一方の端部が封止され、上記壁部に触媒担持層が付着した多孔質セラ ミック力 なるハ-カム構造体であって、
上記多孔質セラミックの全気孔容積に対する気孔径 10 μ m以下の気孔容積の割合 を X (%)、気孔率を Y (%)、上記触媒担持層の重量を Z (gZDとした際、これら X
2 2 2 2
、 Y、 Zは、下記の（3)、（4)式を満たすことを特徴とするハ-カム構造体。
2 2
X≤20-Ζ Ζ10· · · (3)
2 2
Υ≥35 + 7Ζ /40· · · (4)
2 2
(但し、 20≤Ζ≤150)
2
[0067] 図 4 (a)は、第二の本発明のハ-カム構造体の別の一例である一体型ハ-カム構造 体の具体例を模式的に示した斜視図であり、（b)は、その B— B線断面図である。
[0068] 図 4 (a)に示したように、本発明のハ-カム構造体 30は、多数のセル 31がセル壁 (壁 部） 33を隔てて長手方向に並設された多孔質セラミック力 なる円柱状のセラミックブ ロック 35からなる。なお、壁部は、セル 41を隔てるセル壁及び外周部分の両方を意 味するものとする。
[0069] 第二の本発明のハ-カム構造体 30では、セラミックブロック 35は、図 3 (b)に示したよ うに、セル 31の端部の!/、ずれかが封止材 32により封止されて!/、る。
即ち、本発明のハ-カム構造体 30のセラミックブロック 35では、一方の端部で所定 のセル 31が封止材 32により封止され、セラミックブロック 35の他方の端部では、封止 材 32により封止されていないセル 31が封止材 32により封止されている。
[0070] この場合、一のセル 31に流入した排気ガスは、必ずセル 31を隔てるセル壁 33を通 過した後、他のセル 31から流出されるようになっており、これらのセル 31同士を隔て る壁部 33を粒子捕集用フィルタとして機能させることができる。
また、図 3には示していないが、セラミックブロック 35の周囲には、図 1に示したハ-カ ム構造体 10と同様に、シール材層が形成されて 、てもよ!/、。
[0071] 上記ハ-カム構造体を構成する多孔質セラミックとしては特に限定されず、例えば、 コージエライト、アルミナ、シリカ、ムライト、ジルコ-ァ、イットリア等の酸ィ匕物セラミック 、炭化珪素、炭化ジルコニウム、炭化チタン、炭化タンタル、炭化タングステン等の炭 化物セラミック、窒化アルミニウム、窒化珪素、窒化ホウ素、窒化チタン等の窒化物セ ラミック等が挙げられる。
[0072] これらのなかでは、コージエライト等の酸ィ匕物セラミックが好ましい。安価に製造するこ とができるとともに、比較的熱膨張係数が小さぐ例えば、本発明のハ-カム構造体を 上記ハ-カムフィルタとして使用して 、る途中に破壊されるおそれが小さ 、からであ る。
[0073] 図 4に示した第二の本発明のハ-カム構造体 30では、セラミックブロック 35の形状は 円柱状である力 本発明において、セラミックブロックは、柱状であれば円柱状に限 定されることはなく、例えば、楕円柱状や角柱状等任意の形状のものであってもよい
[0074] 第二の本発明のハ-カム構造体 30は、触媒担持層が付着し、該触媒担持層に触媒 が担持されるように構成されたノ、二カム構造体である。
上記触媒としては特に限定されな 、が、パティキュレートの燃焼の活性ィ匕エネルギー を低下させるものや、 CO、 HC及び NOx等の排気ガス中の有害なガス成分を浄ィ匕 することができるもの等が望ましぐ例えば、白金、パラジウム、ロジウム等の貴金属等 を挙げることができる。なかでも、白金、パラジウム、ロジウムからなる、いわゆる三元 触媒が望ましい。また、貴金属に加えて、アルカリ金属 (元素周期表 1族）、アルカリ 土類金属 (元素周期表 2族)、希土類元素 (元素周期表 3族)、遷移金属元素等を担 持させてもよい。
[0075] このようなハ-カム構造体 30は、排気ガス中の CO、 HC及び NOx等を浄化すること ができる。
このようなハ-カム構造体 30の触媒担持層に触媒が担持されることで、ハ-カム構造 体 10は、排気ガス中のパティキュレートを捕集するフィルタとして機能するとともに、 排気ガスに含有される CO、 HC及び NOx等を浄ィ匕するための触媒コンバータとして 機能する。
[0076] セラミックブロック 35に上記触媒を付着させる際には、上述のように、予めその表面を アルミナ等の触媒担持層で被覆した後に、上記触媒を付着させることが望ましい。こ れにより、比表面積を大きくして、触媒の分散度を高め、触媒の反応部位を増やすこ とができる。また、触媒担持層によって触媒金属のシンタリングを防止することができ るので、触媒の耐熱性も向上する。
[0077] 上記触媒担持層としては、例えば、アルミナ、チタ-ァ、ジルコユア、シリカ、セリア等 の酸ィ匕物セラミックが挙げられる。
[0078] また、上記触媒担持層に触媒が担持されることにより、触媒上で酸化反応等が進行 し、反応熱が発生するため、ハ-カム構造体 10の温度を上昇させることができる。
[0079] 第二の本発明では、多孔質セラミックの全気孔容積に対する気孔径 10 μ m以下の 気孔容積の割合を X (%)、気孔率を Y (%)、上記触媒担持層の重量を Z
2 2 2 (gZDと した際、これら X、 Y、 Zは、下記の（3)、（4)式を満たすことを特徴とするハ-カム
2 2 2
構造体である。
X≤20-Ζ /ΙΟ· · · (3)
2 2
Υ≥35 + 7Ζ /40· · · (4)
2 2
(但し、 20≤Ζ≤150)
2
[0080] 上記（3)、 （4)式となるように、触媒担持層の量に従って、多孔質セラミック部材の気 孔径ゃ気孔率を調整することによって、排ガスの浄ィ匕等の機能を充分に果たしなが ら、圧力損失の上昇を防止できるハ-カム構造体を提供することができる。
[0081] X力 Ζ /10を超えた場合には、セラミックブロック 35を構成する壁部の全気孔
2 2
容積に対する気孔径 10 μ m以下の細孔の気孔容積の割合が触媒担持層の付着量 に対して多くなるので、細孔に触媒担持層が付着することによる圧力損失が大きくな りやすい。
[0082] また、 Y力 S35 + 7Z Z40よりも小さい場合には、気孔自体の容積が触媒担持層の付
2 2
着量に比べて少ないので、細孔に触媒担持層が付着することにより気孔の容積が減 少し、圧力損失が大きくなりやすい。
[0083] セラミックブロック 35の気孔率 Yは特に限定されないが、望ましい下限は 38. 5%で
2
あり、望ましい上限は 75%である。 38. 5%未満であると、触媒担持層を付着させた 際に、セラミックブロック 35が目詰まりを起こしやすぐ圧損が高くなる。一方、 75%を 超えると、セラミックブロック 35の強度が低下して容易に破壊されることがある。
[0084] セラミックブロック 35の気孔率 Yの下限は、 40%力 り望ましく、セラミックブロック 35 の気孔率の上限は、 65%がより望ましい。
[0085] 触媒担持層の量 (Z )は、 20〜150gZlである。触媒担持層の量を、上記範囲とする
2
ことにより、触媒を良好に分散させることができ、かつ、圧力損失の上昇を防止するこ とがでさる。
[0086] セラミックブロック 35の平均気孔径の望ましい下限は 10 μ mであり、望ましい上限は 50 ;ζ ΐηである。 10 /z m未満であると、触媒担持層を付着させることが難しくなり、一方 、 50 mを超えると、パティキュレートが気孔を通り抜けてしまい、該パティキュレート を捕集することができず、フィルタとして機能しな 、ことがある。
なお、上記気孔率は、例えば、水銀圧入法、アルキメデス法及び走査型電子顕微鏡 (SEM)による測定等の従来公知の方法により測定することができる。
[0087] セラミックブロック 35を封止材の材料、セル壁の厚さ、シール材層の材料、セルの大 きさ、種類等に関しては、第一の本発明と同様であるので、ここでは、詳しい説明を省 略する。
[0088] 次に、第二の本発明のハ-カム構造体の製造方法の一例について説明する。
まず、上述したようなセラミックを主成分とする原料ペーストを用いて押出成形を行い 、セラミックブロックとなる円柱形状のセラミック成形体を作製する。この際、成形体の 形状が円柱で、寸法が第一の本発明と比べて大きい他は、第一の本発明と同様の バインダー、分散媒等を用い、同様の方法で成形体を製造するので、ここでは、その 詳しい説明を省略する。
[0089] 次に、第一の本発明と同様に、上記セラミック成形体を、マイクロ波乾燥機、熱風乾 燥機、誘電乾燥機、減圧乾燥機、真空乾燥機、凍結乾燥機等を用いて乾燥させ、セ ラミック乾燥体とする。次いで、入口側セル群の出口側の端部、及び、出口側セル群 の入口側の端部に、封止材となる封止材ペーストを所定量充填し、セルを目封じする その後、第一の本発明と同様に、脱脂、焼成を行うことによりセラミックブロックを製造 し、壁部に触媒担持層を付着させ、触媒を担持する。
実施例
[0090] 以下に実施例を掲げ、本発明を更に詳しく説明するが、本発明はこれら実施例のみ に限定されるものではない。
[0091] (実施例 1)
平均粒径 22 mの α型炭化珪素粉末 7000重量部と、平均粒径 0. 5 mの α型炭 化珪素粉末 3000重量部とを湿式混合し、得られた混合物 10000重量部に対して、 有機バインダー（メチルセルロース）を 570重量部、水を 1770重量部加えて混練して 混合組成物を得た。
次に、上記混合組成物に可塑剤 (日本油脂社製 ュニループ）を 330重量部、潤滑 剤として（グリセリン)を 150重量部加えてさらに混練した後、押出成形を行い、図 2に 示した角柱形状の生成形体を作製した。
[0092] 次に、マイクロ波乾燥機等を用いて上記生成形体を乾燥させ、セラミック乾燥体とし た後、上記生成形体と同様の組成の封止材ペーストを所定のセルに充填した。
次いで、再び乾燥機を用いて乾燥させた後、 400°Cで脱脂し、常圧のアルゴン雰囲 気下 2200°C、 3時間で焼成を行うことにより、気孔率 Y力 2%、平均気孔径が 11 m、全気孔容積に対する気孔径 10 m以下の気孔容積の割合を X力 13%、その 大きさが 34. 3mm X 34. 3mm X 150mm、セル 21の数が 28個 Zcm2実質的に全 ての壁部 23の厚さが 0. 30mmの炭化珪素焼結体からなる一体型ハ-カム構造体 2 0を製造した。
[0093] 繊維長 0. 2mmのアルミナファイバー 30重量％、平均粒径 0. 6 mの炭化珪素粒 子 21重量％、シリカゾル 15重量％、カルボキシメチルセルロース 5. 6重量％、及び 、水 28. 4重量％を含む耐熱性の接着剤ペーストを用いて多孔質セラミック部材 20 を多数接着させ、続いて、ダイヤモンドカッターを用いて切断することにより、円柱状 のセラミックブロック 15を作製した。
[0094] 次に、無機繊維としてアルミナシリケートからなるセラミックファイバー（ショット含有率： 3%、繊維長： 0. 1〜： L00mm) 23. 3重量％、無機粒子として平均粒径 0. 3 mの 炭化珪素粉末 30. 2重量％、無機バインダーとしてシリカゾル (ゾル中の SiOの含有
2 率： 30重量％) 7重量％、有機バインダーとしてカルボキシメチルセルロース 0. 5重 量0 /0及び水 39重量％を混合、混練してシール材ペーストを調製した。
[0095] 次に、上記シール材ペーストを用いて、セラミックブロック 15の外周部に厚さ 0. 2mm のシール材ペースト層を形成した。そして、このシール材ペースト層を 120°Cで乾燥 して、直径 143. 8mm X長さ 150mmの円柱状の集合体型ハ-カム構造体 10を製 •laし 7こ。
[0096] 次に、 γ —アルミナを、水と分散剤である硝酸溶液と混合し、さらにボールミルで 90 min_ 1で 24時間粉砕して、平均粒径 2 mのアルミナスラリーを調製し、次に、得ら れたスラリー中にハ-カム構造体を浸し、引き上げた後、 200°Cで乾燥させた。 上記工程をアルミナ層（触媒担持層）が 20gZLの量に達するまで繰り返し、 600°C で焼成した。
[0097] 次に、白金濃度 4. 53重量％のジニトロジアンミン白金硝酸（[Pt (NH ) (NO ) ]H
3 2 2 2
NO )を蒸留水で希釈し、上記希土類酸ィ匕物含有アルミナ層が形成された上記セラ
3
ミック焼成体を浸漬した後、 110°Cで 2時間、窒素雰囲気中 500°Cで 1時間加熱して 、上記セラミック焼成体の表面に、平均粒子直径 2nmの白金触媒を 5gZL担持させ 、触媒を担持したハニカム構造体の製造を終了した。
[0098] (実施例 2〜10、比較例 1〜8)
成形体を作製する際、表 1に示したような各成分を混合して混合組成物を形成し、押 出成形により成形体を作製したほかは、実施例 1と同様にしてハ-カム構造体 10を 製造し、得られたノヽ-カム構造体 10に表 2に記載の量の触媒担持層を付着させ、触 媒を担持させた。なお、白金触媒の量は、 5gZLで一定である。
また、実施例 3〜10、比較例 3〜6では、気孔を形成するための造孔剤として、表 1に 記載の平均粒子径を有するアクリル粒子を添加している。
[0099] [表 1]
Figure imgf000020_0002
Figure imgf000020_0003
Figure imgf000020_0005
Figure imgf000020_0004
Figure imgf000020_0006
Figure imgf000020_0001
(評価）
(1)気孔率等の測定
触媒担持層及び触媒を付着させる前に、水銀圧入法によるポロシメーター（島津製 作所社製、オートポア III 9420)を用い、水銀圧入法により細孔直径 0.1 360 mの範囲で細孔分布を測定した。
上記測定により得られた多孔質セラミック部材 20の全気孔容積に対する気孔径 10 m以下の気孔容積の割合 X (%)、気孔率 Y (%)及びこれらと触媒担持層の量 Z
1 1 2
(g/1)の値に基づき計算した（1)式、（2)式の値を表 2に示す。
[0101] (2)圧力損失の測定
触媒担持層及び触媒を付着させる前後で、各実施例及び比較例に係るハニカム構 造体をエンジンの排気通路に配設し、空気を 750m3Zhrの速度で流してハ-カム構 造体の圧力損失を測定した。その結果を表 2及び図 5に示した。表 2では、触媒担持 層等を付着させる前をコート前、触媒担持層を付着させた後をコート後と記載してい る。
[0102] [表 2]
Figure imgf000021_0001
[0103] 表 2及び図 5に示したように、上記（3)式及び (4)式の関係を満たす各実施例に係る 集合体型ハニカム構造体は、触媒担持層を付着する前後で圧力損失は余り変化し ておらず、触媒担持層付着後もその値は、 12. 5〜13. OkPaの範囲に入っており、 その値は、低い。一方、上記（3)式及び (4)式の関係を満たしていない各比較例に 係るハ-カム構造体は、触媒担持層を付着させることにより、圧力損失が 13. 0より大 きくなつており、初期の圧力損失が高くなることからフィルタとしての使用が難しいこと がわカゝる。
図面の簡単な説明
[0104] [図 1]第一の本発明のハ-カム構造体の一例を模式的に示した斜視図である。
[図 2] (a)は、第一の本発明のハ-カム構造体を構成する多孔質セラミック部材を模 式的に示した斜視図であり、（b)は、その A— A線断面図である。
[図 3]本発明のハ-カム構造体が設置された車両の排気ガス浄化装置の一例を模式 的に示した断面図である。
[図 4] (a)は、第二の本発明のハ-カム構造体を模式的に示した断面図であり、 (b) は、その B— B線断面図である。
[図 5]実施例及び比較例に係る結果を示したグラフである。
符号の説明
[0105] 10、 30 ハ-カム構造体
11 接着剤層
12 シール材層
15 セラミックブロック
20 多孔質セラミック部材
21、 31 セノレ
22 封止材
23、 33 壁咅
35 セラミックブロック

Claims

請求の範囲
[1] 壁部を隔てて長手方向に貫通する複数のセルのいずれか一方の端部が封止されて なる多孔質セラミック部材が接着剤層を介して複数個接着され、前記壁部に触媒担 持層が付着したノヽ-カム構造体であって、
前記多孔質セラミック部材の全気孔容積に対する気孔径 10 μ m以下の気孔容積の 割合を X (%)、気孔率を Y (%)、前記触媒担持層の重量を Z (gZDとした際、 これら X、 Y、 Zは、下記の（1)、（2)式を満たすことを特徴とするハ-カム構造体。 X≤20— Z /10· · · (1)
Υ≥35 + 7Ζ /40· · · (2)
(但し、 20≤Z≤150)
[2] 前記ハ-カム構造体は、炭化珪素質セラミック力 なる請求項 1に記載のハ-カム構 造体。
[3] 壁部を隔てて長手方向に貫通する複数のセルのいずれか一方の端部が封止され、 前記壁部に触媒担持層が付着した多孔質セラミック力 なるハ-カム構造体であつ て、
前記多孔質セラミックの全気孔容積に対する気孔径 10 μ m以下の気孔容積の割合 を X (%)、気孔率を Y (%)、前記触媒担持層の重量を Z (gZDとした際、
2 2 2
これら X、 Y、 Zは、下記の（3)、（4)式を満たすことを特徴とするハ-カム構造体。
2 2 2
X≤20-Ζ Ζ10· · · (3)
2 2
Υ≥35 + 7Ζ /40· · · (4)
2 2
(但し、 20≤Ζ≤150)
2
[4] 前記ハ-カム構造体は、コーディエライトからなる請求項 3に記載のハ-カム構造体
PCT/JP2005/017868 2004-09-30 2005-09-28 ハニカム構造体 WO2006035822A1 (ja)