KR20010080606A - 고무 조성물 - Google Patents
고무 조성물 Download PDFInfo
- Publication number
- KR20010080606A KR20010080606A KR1020017006633A KR20017006633A KR20010080606A KR 20010080606 A KR20010080606 A KR 20010080606A KR 1020017006633 A KR1020017006633 A KR 1020017006633A KR 20017006633 A KR20017006633 A KR 20017006633A KR 20010080606 A KR20010080606 A KR 20010080606A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- rubber
- polymer
- component
- diene
- Prior art date
Abstract
Description
◎ 제 1 단계 혼련 (B 형 밀폐혼련기, 온도는 혼련별 설정) | |
경과시간 | 조작 |
0 분 | 고무 투입 |
0 분 30 초 | 산화아연, 스테아르산 투입 |
1 분 00 초 | 실리카, 카본블랙, 실란 커플링제 투입 |
3 분 30 초 | 램을 올려 청소 |
4 분 00 초 | 배출 |
배출후 | 배합물 온도 측정후, 10 인치 롤로 분 배출/냉각 |
◎ 제 2 단계 혼련 (B 형 밀폐혼련기, 온도는 혼련별 설정) | |
0 분 | 제 1 단계 혼련 조성물, 노화방지제 투입 |
2 분 | 배출 |
배출후 | 배합물 온도 측정후, 10 인치 롤로 분 배출/냉각 |
◎ 제 3 단계 혼련 (10 인치 믹싱롤, 70 ℃ 설정) | |
0 분 | 제 2 단계 혼련 조성물 |
0 분 15 초 | 황, 가황 촉진제 투입 |
3 분 | 배출, 성형 |
Claims (15)
- (A-1) 공액 디엔계 고무상 중합체 또는 공액 디엔-스티렌계 고무상 공중합체로서, (1) 상기 고무상 중합체의 활성 말단을, 분자 중에 2 개 이상의 에폭시기를 갖는 다관능성 화합물과 반응시켜 얻은 변성 성분을 60 중량% 를 초과하여 함유하고, (2) 중합체의 분자량 분포 (Mw/Mn) 가 1.05 내지 3.0 이고 (3) 중합체의 중량평균분자량이 100,000 내지 2,000,000 인 디엔계 고무상 중합체로 이루어지는 (A) 100 중량부의 원료 고무,(B) 1 내지 100 중량부의 고무용 신전유(伸展油),(C) 25 내지 100 중량부의 보강성 실리카, 및(D) 1.0 내지 20 중량부의 가황제 및 가황 촉진제의 배합물;성분 (B), (C) 및 (D) 는 성분 (A) 100 중량부를 기준으로 한다.
- 제 1 항에 있어서, 상기 다관능성 화합물이 추가로 1 개 이상의 질소 함유기를 갖는 디엔계 중합체 고무 조성물.
- 제 1 항에 있어서, 상기 다관능성 화합물이 하기 일반식으로 표현되는 디엔계 중합체 고무 조성물:(식 중,R1및 R2는 탄소수 1 내지 10 의 탄화수소기, 또는 에테르 및 3 급 아민 중 1 종 이상의 기를 갖는 탄소수 1 내지 10 의 탄화수소기이고,R3및 R4는 수소, 탄소수 1 내지 20 의 탄화수소기, 또는 에테르기 및 3 급 아민 중 1 종 이상의 기를 갖는 탄소수 1 내지 20 의 탄화수소기이고,R5는 탄소수 1 내지 20 의 탄화수소기, 또는 에테르, 3 급 아민, 에폭시, 카르보닐, 할로겐 중 1 종 이상의 기를 갖는 탄소수 1 내지 20 의 탄화수소기이고, n 은 1 내지 6 이다).
- 제 3 항에 있어서, 상기 다관능성 화합물이 분자 중에 1 개 이상의 디글리시딜아미노기를 가지는 디엔계 중합체 고무 조성물.
- 제 1 항에 있어서, (A-1) 성분의 변성 성분 함유량이 크로마토그래피로 분석된 것인 디엔계 중합체 고무 조성물.
- 제 1 항에 있어서, (C) 성분의 중량에 대해 0.1 내지 20 중량% 의 (E) 유기 실란 커플링제를 추가로 함유하는 디엔계 중합체 고무 조성물.
- 제 1 항에 있어서, (F) 0.1 내지 100 중량부의 카본블랙을 추가로 함유하고, (C) 성분과 (F) 성분의 합계가 30 내지 150 중량부인 디엔계 중합체 고무 조성물.
- 제 7 항에 있어서, (F) 성분의 양이 0.1 중량부 이상 25 중량부 미만인 디엔계 중합체 고무 조성물.
- 제 1 항에 있어서, (A-1) 성분의 (2) 중합체의 분자량 분포 (Mw/Mn) 가 1.05 이상 2.2 미만인 디엔계 중합체 고무 조성물.
- 제 1 항에 있어서, (A) 성분이 15 내지 99 중량% 의 (A-1) 성분, 및 (A-2) 1 내지 85 중량% 의 (A-1) 성분 이외의 가황가능한 고무상 중합체로 이루어지는 디엔계 중합체 고무 조성물.
- 하기의 (A), (B) 및 (C) 로 이루어지는 초기 혼련 성분을 혼련 배출 온도가 135 내지 180 ℃ 로 되는 조건에서 1 회 이상 초기 혼련하고, 혼련 후의 바운드 러버량을 30 내지 70 중량% 로 하여 초기 혼련물을 얻고, 나아가 (A) 성분 100 중량부 당 (D) 를 상기 초기 혼련물에 첨가하고, 혼련 배출 온도가 120 ℃ 이하로 되도록 혼련하고 가황하여 얻어지는 디엔계 중합체 고무 가황물:(A-1) 공액 디엔계 고무상 중합체 또는 공액 디엔-스티렌계 고무상 공중합체로서, (1) 상기 고무상 중합체의 활성 말단을, 분자 중에 2 개 이상의 에폭시기를 갖는 다관능성 화합물과 반응시켜 얻은 변성 성분을 60 중량% 를 초과하여 함유하고, (2) 중합체의 분자량 분포 (Mw/Mn) 가 1.05 내지 3.0 이고 (3) 중합체의 중량평균분자량이 100,000 내지 2,000,000 인 디엔계 고무상 중합체로 이루어지는 (A) 100 중량부의 원료 고무,(B) 1 내지 100 중량부의 고무용 신전유(伸展油),(C) 25 내지 100 중량부의 보강성 실리카, 및(D) 1.0 내지 20 중량부의 가황제 및 가황 촉진제의 배합물.
- 제 11 항에 있어서, 상기 초기 혼련 성분이 추가로 (C) 성분의 중량에 대해 0.1 내지 20 중량% 의 (E) 유기 실란 커플링제, 및 (A) 성분 100 중량부 당 0.1 내지 100 중량부의 (F) 카본블랙 중 어느 1 개 이상을 함유하는 디엔계 중합체 고무 가황물.
- 제 11 항에 있어서, (A) 성분이 15 내지 99 중량% 의 (A-1) 성분, 및 (A-2) 1 내지 85 중량% 의 (A-1) 성분 이외의 가황가능한 고무상 중합체로 이루어지는 상기 디엔계 중합체 고무 가황물.
- 제 12 항에 있어서, (E) 성분의 양이 (C) 성분의 중량에 대해 0.1 중량% 이상 6 중량% 미만인 디엔계 중합체 고무 가황물.
- 제 11 항에 있어서, (C) 성분의 가열 감량 (Mo) 에 따라 하기 혼련 배출 온도 (Td) 로 되도록 초기 혼련을 실시하는 디엔계 중합체 고무 가황물:1) 1 % ≤Mo ≤4 % 의 경우, 135 ≤Td ≤180 ℃2) 4 % < Mo ≤6 % 의 경우, (15 ×Mo + 75) ℃ < Td ≤180 ℃3) 6 % < Mo ≤10 % 의 경우, 165 ℃ < Td ≤180 ℃