JPWO2011013691A1 - 積層鋼板 - Google Patents
積層鋼板 Download PDFInfo
- Publication number
- JPWO2011013691A1 JPWO2011013691A1 JP2011524803A JP2011524803A JPWO2011013691A1 JP WO2011013691 A1 JPWO2011013691 A1 JP WO2011013691A1 JP 2011524803 A JP2011524803 A JP 2011524803A JP 2011524803 A JP2011524803 A JP 2011524803A JP WO2011013691 A1 JPWO2011013691 A1 JP WO2011013691A1
- Authority
- JP
- Japan
- Prior art keywords
- wire
- laminated
- steel sheet
- steel plate
- core layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
[積層鋼板の構成]
初めに、図1を参照しながら、本発明の第1の実施形態に係る積層鋼板の全体構成について説明する。図1は、本実施形態に係る積層鋼板1の全体構成の一例を示す断面図である。
まず、図1、図2A及び図2Bを参照しながら、本実施形態に係る網状の線材群11の構成について詳細に説明する。図2A及び図2Bは、本実施形態に係る網状の線材群11の構成の一例を示す図であり、図2Aは平面図を示し、図2Bは断面図を示している。
軽量化可能な目開きを確保しても、網状の線材群を構成する線材の引張強度が601MPa以上であれば、コア層の強度は確保される。その結果、積層鋼板を曲げや絞りなど強加工に供した後も、コア層は破壊することなく健全に維持される。線材の引張強度は1000MPa以上であることが好ましく、2000MPa以上であることがさらに好ましく、この範囲で上記の効果が確保されるとともに、衝撃吸収能も得られる。一方、せん断や曲げ加工性からは、線材の引張強度は6000MPa以下であることが好ましい。線材の引張強度が6000MPaを超えるとコア層のせん断抵抗が大きくなり、積層鋼板を曲げ加工する際に、表層や表層と接着層との間の接合層の各々に加わる曲げ力やせん断力が増加し、表層破壊や接着層での剥離・破壊が生じやすくなる。
線材の直径(線径)dは、特に限定されず、積層鋼板1の用途に応じて必要とされる剛性や耐衝撃性の観点から、必要とされるコア層10の厚み以下であればよく、用途ごとに優先させる積層鋼板1の特性(板密度、剛性、耐衝撃性等)に応じて適宜決定することができる。例えば、積層鋼板1の板密度が特に重要な場合には、網状の線材群11の目開き、コア層10の目標とする板密度ρ目標に応じて、下記(1)式及び(2)式から線径dを決定することができる。また、積層鋼板1の耐衝撃性が特に重要な場合には、耐衝撃性の支配因子である塑性変形域の曲げモーメントMp目標に応じて、下記(3)式及び(2)式から線径dを決定することができる。
ρ目標>7.8×(1−Vair)×n ・・・(1)
Vair=w2/(w+d)2 ・・・(2)
Mp目標<1/4σYs[(ts+tc)2−tc 2]+1/8(1−Vair)σYc ・・・(3)
(上記(1)〜(3)式で、ρ目標はコア層10の目標板密度、Vairはコア層10中の空孔115部分の体積、nは網状の線材群11の積層枚数、wは網状の線材群11の目開き、Mp目標は目標曲げモーメント、σYsは表層鋼板5の降伏強度、σYcはコア層10の降伏強度、tsは表層鋼板5の厚み、tcはコア層10の厚み、dは網状の線材群11の線径を示す。)
本実施形態に係る積層鋼板1では、網状の線材群11の目開きwが、表層鋼板5の厚みtsの10倍以下であることが必要である。このように、網状の線材群11の目開きwを表層鋼板5の厚みtsの10倍以下としたのは、以下に説明する本発明者の検討によるものである。コア層10の母材である線材と表層鋼板5との引張強度比が1/50(引張強度の大きい方を分母とした値)以下となるようなコア層10を有する積層鋼板1を引張変形させた場合を想定する。この場合に、コア層10に存在する空孔115の一辺の長さ(目開きw)を表層鋼板5の厚みの10倍超とすると、表層鋼板1のうち空孔115上に位置する部分に応力が集中し、早期に表層鋼板5が破断してしまうことがFEM(有限要素法)解析により判明した。表層鋼板5において、コア層10の空孔115上に位置する部分と、線材(縦線111及び横線113)上に位置する部分とでは、実質上の鋼板厚みが異なる。そのため、空孔115上に位置する部分の強度(引張強度や降伏強度)の方が、線材上に位置する部分の強度よりも小さくなる。その結果、積層鋼板1に引張変形や圧縮変形などが加わると、表層鋼板5の中でも強度が低い空孔115上に位置する部分に応力が集中し、破断伸びが減少し、これにより加工性が低下してしまう。
網状の線材群11の形成方法については、上述した線材の引張強度及び目開きの条件を満足するものであれば、織り方や編み方などは特に制限されず、例えば、正方目、ひし形、亀甲状等の矩形目などのいずれでもよい。正方目の網状の線材群11としては、織網状の線材群、クリンプ網状の線材群などがある。織網状の線材群の具体例としては、平織り、綾織、たたみ織り、たたみ綾織り等が挙げられる。また、クリンプ網状の線材群の具体例としては、クリンプ織り、ロッククリンプ織り、ダブルクリンプ織り、フラットクリンプ織り、トンキャップスクリーン織り、スロットスクリーン織り等が挙げられる。また、網状の線材群11の形成方法としては、織りや編みではなくても、溶接等の固相接合によっても構わない。すなわち、縦線111と横線113とを溶接等の固相接合により接合し、網状に形成してもよい。さらに、網状の線材群11の織り方としては、2次元織りではなく、3次元の立体織りにしてもよい。
図3は、本実施形態に係る網状の線材群の変形例の構成を示す平面図である。本実施形態では、以下に説明する網状の線材群11による表層鋼板5の拘束効果を効率よく発現させるために、図3に示した網状の線材群11’のように、縦線111と横線113とからなる正方目の網状の線材群に、縦線111及び横線113の方向に対して45°の方向の斜め方向の織り(線)117が加えられていることが特に好ましい。
EI=(1/12)Es[(ts+tc)3−tc 3]+1/12Ectc 3 ・・・(4)
(上記(4)式において、EIは積層鋼板1の剛性、Esは表層鋼板5のヤング率、Ecは、コア層10のヤング率、tsは表層鋼板5の厚み、tcはコア層10の厚みを示す。)
上述したように、本実施形態に係るコア層10に含まれる網状の線材群11は、1枚であっても、2枚以上積層されていてもよい。また、1種以上の網状の線材群11が2次元にランダムに配列してもよい。なお、2枚以上積層する場合は、樹脂シート13が2つの網状の線材群11の間に積層されている場合も含まれる。特に、本実施形態では、コア層10の等方性を増加させるために、コア層10にn層(nは2以上)の網状の線材群11を積層する場合、各層の網状の線材群11を形成する線材の方向を、隣接する層の網状の線材群11間で360/3n°以上360/n°以下の角度ずつ一定方向にずらして、各層の網状の線材群11を積層することも可能である。このような積層方法を例示すると、最下層の網状の線材群11に対し、その上層の各網状の線材群11を45°ずつ回転させて4層積層する方法などがある。等方性を増加させる観点からは、網状の線材群11の層数nを大きくして、網状の線材群11を微細な角度ずつ(360/3n°〜360/n°ずつ)回転させて積層することが好ましい。一方、経済的合理性の観点からは層の数に上限を定めた方が好ましい。したがって、積層する網状の線材群11の数は、2層以上20層以下であることが好ましい。なお、2枚以上の網状の線材群11を積層する場合に、回転せずに各網状の線材群が平行になるようにしてもよい。
本実施形態においては、網状を形成する線材は、引張強度が601MPa以上であればよく、以下の金属系、無機系、有機系線材が考えられる。中でもコア層と表層間の変形挙動を類似させ、曲げなどの大変形を与えた際に、コア層と表層とがより一体となって変形するため、金属系線材がより好ましい。この観点から最も好ましいのは、鋼線である。金属系線材としては、炭素含有量が0.24%以上の炭素鋼、オーステナイト、フェライト系ステンレス鋼などの鋼線、銅、真鍮、青銅、燐青銅などの銅系線材、ニッケル、ニッケル・銅、ニッケル・クロム、ニッケル・クロム・モリブデン合金などのニッケル線材、チタン線材、アルミニウム線材などがある。なお、鉄系線材の場合は、亜鉛メッキ、Niメッキ、真鍮メッキ、銅メッキなどの公知のメッキを施していてもよい。また、無機系線材としては、PAN系、ピッチ系の炭素繊維、ガラス繊維、アルミナ繊維、炭化珪素繊維等の無機繊維などがある。さらに、有機系線材としては、アラミド繊維、ポリアリレート繊維、高強度ポリオレフィン繊維(例えば高重合度ポリエチレン繊維と呼ばれる高強度繊維等)の高強力高ジュラス有機繊維があげられる。
本実施形態における網状の線材群11として、鋼線を用いる場合、その炭素含有量は、0.24質量%以上であることが好ましい。鋼線の炭素含有量を0.24質量%以上とすることにより、鋼線の引張強度を確保することができる。例えば、コア層10内の鋼線密度を必要とされる板密度(コア層10内における鋼線の質量比)まで低下させても、積層鋼板1を加工するときや加工後の製品として必要とされるコア層10の網状の線材群11の引張強度及び降伏強度を確保することができる。このため、積層鋼板1の剛性や耐衝撃性を高く保ちつつ、積層鋼板1を十分に軽量化することが可能となる。
次に、本実施形態に係る樹脂シート13の構成について説明する。本実施形態に係る樹脂シート13の基材としては、樹脂種を特に制限するものではなく、熱可塑性樹脂、熱硬化性樹脂、ゴム状弾性体からなる樹脂シート、あるいはこれらの1種又は2種類以上の混合物を使用することができる。具体的には、樹脂シート13の樹脂種としては、例えば、ポリスチレン、ポリメチルメタクリレート、硬質、軟質塩化ビニル、高密度、低密度もしくはリニア低密度ポリエチレン、ポリプロピレン等の汎用ビニル系樹脂シート、アイオノマー、ポリオレフィン系エラストマー、スチレン系エラストマー等のエラストマー系樹脂シート、ポリカーボネート、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリアリレート等のポリエステル樹脂シート、6ナイロン、66ナイロン、12ナイロン等のポリアミド樹脂シート、ポリイミド樹脂シート、ポリエステルカーボネート樹脂シート、ポリフェニレンエーテル等の縮重合系熱可塑性樹脂シート、エポキシ樹脂、フェノール樹脂、ユリア樹脂、ポリエステルメラミン系樹脂等の熱硬化樹脂シート等、及びこれらの混合物を挙げることができる。また、樹脂シート13のシート成形性や耐衝撃性等を改質する目的で、ポリスチレン、ポリメチルメタクリレート、硬質、軟質塩化ビニル等のハロゲン化ビニル樹脂、高密度、低密度もしくはリニア低密度ポリエチレン、ポリプロピレン、アモルファスポリオレフィン等の汎用ビニル系樹脂、アイオノマー、エチレン−プロピレン共重合体、エチレン−ブテン共重合体、エチレン−酢酸ビニル共重合体等のポリオレフィン系エラストマー、スチレン系エラストマー等のエラストマー系樹脂、ポリカーボネート等の縮重合体を上述した樹脂に混合することもできる。
本実施形態に係る表層鋼板5としては、特に限定はされないが、具体的には、例えば、ブリキ、薄錫めっき鋼板、電解クロム酸処理鋼板(ティンフリースチール)、ニッケルめっき鋼板等の缶用鋼板や、溶融亜鉛めっき鋼板、溶融亜鉛−鉄合金めっき鋼板、溶融亜鉛−アルミニウム−マグネシウム合金めっき鋼板、溶融アルミニウム−シリコン合金めっき鋼板、溶融鉛−錫合金めっき鋼板等の溶融めっき鋼板や、電気亜鉛めっき鋼板、電気亜鉛−ニッケルめっき鋼板、電気亜鉛−鉄合金めっき鋼板、電気亜鉛−クロム合金めっき鋼板等の電気めっき鋼板等の表面処理鋼板、冷延鋼板、熱延鋼板、ステンレス鋼板等を使用することができる。また、表層鋼板5は、塗装鋼板、プリント鋼板、フィルムラミネート鋼板等の表面処理鋼板であってもよい。
次に、本実施形態における樹脂シート13と表層鋼板5又は網状の線材群11との接合について説明する。
次に、本実施形態においては、網状の線材群11と表層鋼板5とを直接接合する場合もあり得ることから、本実施形態における網状の線材群11と表層鋼板5との接合について説明する。まず、網状の線材群11と表層鋼板5との好適な密着力は、ピール強度によって評価することができるが、本実施形態における網状の線材群11と表層鋼板5とは、5N/cm以上のピール強度で接合されることが好ましい。ピール強度が5N/cm未満では、積層鋼板1の曲げ変形や引張変形の際に、コア層10の両面の表層鋼板5が一体となって変形せず、積層鋼板1の剛性や耐衝撃性を発現させることができないおそれがある。積層鋼板1の曲げ変形時のせん断によるコア層10両面の表層鋼板のずれを小さくするために、ピール強度を25N/cm以上とすることがより好ましく、40N/cm以上とすることがさらに好ましく、60N/cm以上とすることがさらに一層好ましい。なお、ピール強度は、JIS Z0238のTピール試験により評価することができる。
本実施形態に係る積層鋼板1の厚みは特に制限されず、目的とする特性に応じて適宜変更することが可能である。例えば、積層鋼板1の特性として剛性や耐衝撃性を優先させたい場合には、選択する網状の線材群11の構成(線材の線径、目開き、降伏強度等)に応じて、それぞれ、上記(3)式又は(4)式等によって、積層鋼板1の厚みを決定することができる。
D=1/3[(E1−E2)(y1−ye)3+(E2−E3)(y2−ye)3+E1ye 3+E3(h−ye)3]・・・(5)
ye=[(e1−E2)y1 2+(E2−E3)y2 2+E3h2]/[2((E1−E2)y1+(E2−E3)y2+E3h)]・・・(6)
ρ=[7.8(h−y2+y1)+ρコア層(y2−y1)]/h・・・(7)
(上記(5)〜(7)式において、E1は下面側の表層鋼板5Aのヤング率であり、E2はコア層10のヤング率であり、E3は上面側の表層鋼板5Bのヤング率であり、y1は表層鋼板5の厚みであり、y2はy1+コア層10の厚みであり、yeは中立軸のy座標であり、hはy2+上面側の表層鋼板5Aの厚み、ρコア層はコア層密度である。)
続いて、上述したような構成を有する積層鋼板1の製造方法について詳細に説明する。
(1)炭素含有量が0.24質量%以上の鋼線を用いて網状の線材群11を製造する。
(2)コア層10(1枚又は2枚以上の網状の線材群11、1枚又は2枚以上の樹脂シート13)の両面に必要に応じて接合材(接着剤、ブレーズ剤等)を塗布する。そして、例えば、図1に示した構造を有するコア層10を形成しようとする場合は、表層鋼板5A、樹脂シート13、網状の線材群11、樹脂シート13、網状の線材群11、樹脂シート13、表層鋼板5Bの順に積層し、常温もしくは加熱しながら加圧する。
次に、図6を参照しながら、本発明の第2の実施形態に係る積層鋼板の全体構成について説明する。図6は、本実施形態に係る積層鋼板2の全体構成の一例を示す断面図である。
次に、図7を参照しながら、本発明の第3の実施形態に係る積層鋼板の全体構成について説明する。図7は、本実施形態に係る積層鋼板3の全体構成の一例を示す断面図である。
以上説明したような本発明の第1〜第3実施形態に係る積層鋼板は、軽量で、剛性、耐衝撃性が高く、かつ、加工性にも優れ、曲げ加工、絞り加工等の強加工を行っても加工後の耐熱形状安定性に優れるものとなる。また、上述した各実施形態に係る積層鋼板では、コア層10が網状の線材群11の他に、樹脂シート13を有することにより、制振性能をも向上させることができる。従って、本発明の第1〜第3の実施形態に係る積層鋼板は、自動車用、家電用、家具用、OA機器などの部材用に利用でき、特に、絞り加工、曲げ加工、プロファイリング加工等の強加工によって成形した後に塗装するシート部品用の鋼板として好適に使用することができる。
本実施例及び比較例では、表1に示す表層鋼板、表2に示す金網(網状の線材群)、表3に示す樹脂シートを使用して積層鋼板を製造した。ここで、表3のPET系アロイは、PET(RN163:東洋紡績製)/アイオノマー(ハイミラン1706:三井デシュポン製)/エチレン系ゴム(EBM2401P:JSR製)の質量比が、80質量部/10質量部/10質量部からなるアロイである。また、表3に示した本実施例及び比較例で使用した発泡体(発泡シート)は、PET系アロイ及びナイロンシートに20MPa、32℃の超臨界CO2を含侵した後、圧力を解放し、それぞれ260℃、240℃に加熱して発泡させた。そして、加熱後、0℃まで冷却し、気泡の成長を停止させることにより、表3に示した発泡シートを得た。なお、超臨界CO2の含浸時間、加熱時間及び冷却速度を調整することにより、発泡シートの発泡率及び発泡径を制御した。また、表2の「織り」における「平織り+45°」とは、平織りの金網に、縦線及び横線の方向に対して45°の方向の斜め線を織り込んだものを示している。
次に、表2に示す金網を表3に示す樹脂シートで包埋した樹脂中に包埋された金網を得た。具体的には、まず、金網の0.55倍の厚みを有する樹脂シートの片面に下記表4に示す接着剤をコートした。次いで、樹脂シートの接着剤をコートした面が金網と接触するようにして、金網の両面に当該樹脂シートを積層し、所定温度(樹脂シートがPET系アロイの場合は260℃、樹脂シートがナイロンの場合は240℃)及び所定圧力(10kgf/cm2〜40kgf/cm2(0.98MPa〜2.92MPa))で圧着することにより、下記の表4に示した樹脂中に包埋された金網No.1−15を得た。なお、樹脂中に包埋された金網No.1−No.15のうち、複数の金網を使用したものについては、まず、上述のようにして1枚の金網を樹脂シートで包埋した樹脂中に包埋された金網を作製した。そして、得られた樹脂中に包埋された金網の表面に接着剤をコートし、各樹脂中に包埋された金網の接着剤コート面が接触するように積層し、加熱圧着して複数の金網が積層された樹脂中に包埋された金網(No.3−No.6、No.9、No.12)を得た。
本実施例における積層鋼板の具体的な製造方法としては、まず、表1に示す300mm×300mmの鋼板の片面に表5に示す接着剤をコートした。そして、接着剤が、上述したようにして得られた樹脂中に包埋された金網と接触するように、鋼板、樹脂中に包埋された金網、鋼板の順に積層して積層体を得た。次に、上記の所定温度(樹脂シートがPET系アロイの場合は260℃、樹脂シートがナイロンの場合は240℃)まで加温した。次いで、所定厚みのシムを用いて積層体の四方を囲み、圧着力10kgf/cm2〜40kgf/cm2(0.98MPa〜2.92MPa)で2分間加熱圧着した後、室温まで冷却して、表6に示した実施例No.1〜No.25の各積層鋼板を得た。
表2に示す金網No.1の両面に、表3に示す接着剤をコートした後、当該金網の両面に表1に示す表層鋼板No.1を積層し、表6に示す実施例No.1と同一の条件で熱圧着することにより、比較例No.1の積層鋼板を得た。
まず、板厚2.1mmの引張強度980MPaの高強度鋼板をパンチング加工し、直径2.0mmの円形孔を付与した(開孔率66%)。そして、パンチング加工後の加工板を、表5に示す樹脂中に包埋された金網No.1と同様にしてPET系アロイ発泡シートに包埋した。そして、その後は実施例No.1と同様の条件により、当該樹脂中に包埋された加工板をコア層とした比較例No.2の積層鋼板を得た。
炭素含有量が最も低い金網No.10を包埋した比較例No.3の積層鋼板を、実施例No.1と同様の手順により得た。また、目開きが最も大きい金網No.11を包埋した比較例No.4の積層鋼板を実施例No.1と同様の手順により得た。
ガラス短繊維入りナイロンシート(厚み:1.3mm、ガラス繊維30質量%含有、引張強度:34MPa)を実施例No.1と同様に表層鋼板1間に積層して比較例5の積層鋼板を得た。また、PET系アロイ発泡シートを実施例1と同様に表層鋼板1間に積層して比較例6の積層鋼板を得た。
コア層として1mmの厚みのPP発泡シートを使用し、接着層として0.05mmの厚みの酸変性PPを使用して実施例1と同様の手順により比較例7の積層鋼板を得た。
上述したようにして得られた各実施例の積層鋼板からASTM D−790に準じて試験片(25mm×150mm)を切り出し、支点間距離を50mm、速度を5mm/minに設定して3点曲げ試験を実施した。このとき、実施例No.1−No.19、No.22−No.24では、試験片の長手方向及び幅方向が最下層金網の正方格子の方向と一致するように試験片を切り出した。また、実施例No.20、No.21では、試験片の長手方向及び幅方向が最下層金網の正方格子の対角線の方向と一致するように試験片を切り出した。
M=Pl/4b ・・・(ii)
<1.軽量性の評価>
各々の積層鋼板の板密度ρを(iii)式により算出した。
Wp=ρstp ・・・(v)
(v)式で算出した積層鋼板の単位面積当たりの質量Wと同一質量を有する鋼板単独の剛性Dpを(vi)式により算出した。また、(vi)式で求めた剛性Dpと積層鋼板の剛性Dとの比(D/Dp)を算出し、積層鋼板の剛性を評価した。ここで、D/Dp>1である場合は、鋼板単独の場合と比較して合理的に剛性が増大していると評価する。
実施例No.22−No.24の積層鋼板に対して破断するまで曲げを継続し、破断時の撓み量を測定し、測定された撓み量を用いて積層鋼板の延性を評価した。ここで、撓み量が大きいほど延性が高いと評価するものとする。なお、撓み量の測定は、荷重点の移動距離により測定した。
ハット曲げ試験片の断面を目視ならびに実体顕微鏡で観察して、表層鋼板の剥離、表層鋼板の破壊や座屈およびコア層への陥入、コア層の破損、座屈の有無を検査した。ここで、すべて異常がない場合には加工健全性に優れると評価した。また、当該加工片を180℃に加熱したオーブンに装入し、30分保持後、オーブンから取り出し、室温まで冷却した。そして、加工後における表層鋼板の剥離、コア層の破壊、流れなどの加熱形状健全性を評価した。ここで、すべて異常がない場合には、加熱形状健全性に優れると評価した。
上述したようにして測定した2次共振周波数での損失係数に基づき、実施例No.1−No.24の積層鋼板の制振性を評価した。なお、損失係数が大きいほど制振特性が良好であると判断するものとする。
以上の評価結果を下記表7に示す。
M(実施例No.1)=1/4(Ts((ts+tc)2−tc 2))−Tc(tc 2)) ・・(viii)
5(5A,5B) (表層)鋼板
10 コア層
11 網状の線材群
13 樹脂シート
111 縦線
113 横線
115 空孔(網目)
117 斜め方向の織り(線)
ts 表層鋼板の厚み
tc コア層の厚み
wL,wH 目開き
p (メッシュ)ピッチ
d 線径
Claims (13)
- 線材を用いて網状に形成した線材群と樹脂シートとを備えたコア層と、前記コア層の両面に接合された鋼板とを有し、
前記線材の引張強度が601MPa以上であり、かつ、前記線材群の目開きが前記鋼板の厚みの10倍以下であることを特徴とする、積層鋼板。 - 前記線材の引張強度が、1000MPa以上であることを特徴とする、請求項1に記載の積層鋼板。
- 前記線材群の目開きが、前記鋼板の厚みの3.5倍以下であることを特徴とする、請求項1に記載の積層鋼板。
- 前記線材群の目開きが、前記鋼板の厚みの0.1倍以上であることを特徴とする、請求項1に記載の積層鋼板。
- 前記線材群の目開きが、前記鋼板の厚みの0.5倍以上1倍以下であることを特徴とする、請求項3に記載の積層鋼板。
- 前記樹脂シートの基材が、発泡体であることを特徴とする、請求項1に記載の積層鋼板。
- 前記コア層と前記鋼板とが接着剤を用いて接合され、
前記接着剤と前記鋼板とのせん断密着強度が30N/cm2以上であり、
前記接着剤の100℃〜160℃での貯蔵弾性率G’が、0.05MPa以上100MPa以下であることを特徴とする、請求項1に記載の積層鋼板。 - 前記線材群は、縦線及び横線に対して斜め方向に織りが加えられていることを特徴とする、請求項1に記載の積層鋼板。
- 前記線材群は、正方目の網であり、
前記斜め方向は、前記縦線及び前記横線の方向に対して45°の方向であることを特徴とする、請求項7に記載の積層鋼板。 - 前記コア層が、n(nは2以上の整数)層の積層された前記線材群からなり、
各層の前記線材群を形成する前記線材の方向を、隣接する層の前記線材群間で360/3n°以上360/n°以下の角度ずつ一定方向にずらして、各層の前記線材群が積層されることを特徴とする、請求項1に記載の積層鋼板。 - 前記コア層は、2層〜20層の積層された前記線材群からなることを特徴とする、請求項10に記載の積層鋼板。
- 前記コア層は、3枚以上の前記線材群を有しており、
3枚以上の前記線材群から任意に選択された隣り合う2枚の前記線材群のうち、前記コア層の厚み方向の中央位置に対して、より遠い側に配置された前記線材群の目開きが、より近い側に配置された前記線材群の目開きよりも小さいことを特徴とする、請求項1に記載の積層鋼板。 - 前記コア層は、複数の前記線材群を有しており、
前記複数の線材群が互いに固相接合または織り込みにより接合されていることを特徴とする、請求項1に記載の積層鋼板。