CN100338252C - 镀锌钢板 - Google Patents
镀锌钢板 Download PDFInfo
- Publication number
- CN100338252C CN100338252C CNB038020459A CN03802045A CN100338252C CN 100338252 C CN100338252 C CN 100338252C CN B038020459 A CNB038020459 A CN B038020459A CN 03802045 A CN03802045 A CN 03802045A CN 100338252 C CN100338252 C CN 100338252C
- Authority
- CN
- China
- Prior art keywords
- phase
- coating
- quality
- steel plate
- application
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
Description
序号 | 热浸镀锌层的组成(质量%) | 表面粗糙度 | 鲜映性 | 备注 | |||||||||||
Mg | Al | Si | Ca | Be | Ti | Cu | Ni | Co | Cr | Mn | Ra | Wca | |||
1 | 3 | 11 | 0.15 | 0.35 | 0.42 | 3 | 本发明例 | ||||||||
2 | 3 | 11 | 0.15 | 0.98 | 0.77 | 3 | ″ | ||||||||
3 | 3 | 11 | 0.15 | 1.21 | 1.06 | 2 | 比较例 | ||||||||
4 | 3 | 11 | 0.15 | 1.10 | 0.73 | 2 | ″ | ||||||||
5 | 3 | 11 | 0.15 | 0.88 | 0.91 | 2 | ″ | ||||||||
6 | 3 | 11 | 0.15 | 0.05 | 0.55 | 0.49 | 3 | 本发明例 | |||||||
7 | 3 | 11 | 0.15 | 0.05 | 0.95 | 0.78 | 3 | ″ | |||||||
8 | 3 | 11 | 0.15 | 0.05 | 1.32 | 1.13 | 2 | 比较例 | |||||||
9 | 3 | 11 | 0.15 | 0.03 | 0.47 | 0.64 | 3 | 本发明例 | |||||||
10 | 3 | 11 | 0.15 | 0.03 | 0.96 | 0.77 | 3 | ″ | |||||||
11 | 3 | 11 | 0.15 | 0.03 | 1.27 | 1.08 | 2 | 比较例 | |||||||
12 | 3 | 11 | 0.15 | 0.03 | 0.39 | 0.45 | 3 | 本发明例 | |||||||
13 | 3 | 11 | 0.15 | 0.03 | 0.92 | 0.76 | 3 | ″ | |||||||
14 | 3 | 11 | 0.15 | 0.03 | 1.40 | 1.12 | 2 | 比较例 | |||||||
15 | 3 | 11 | 0.15 | 0.31 | 0.43 | 0.51 | 3 | 本发明例 | |||||||
16 | 3 | 11 | 0.15 | 0.31 | 0.97 | 0.78 | 3 | ″ | |||||||
17 | 3 | 11 | 0.15 | 0.31 | 1.27 | 1.15 | 2 | 比较例 | |||||||
18 | 3 | 11 | 0.15 | 0.03 | 0.57 | 0.63 | 3 | 本发明例 | |||||||
19 | 3 | 11 | 0.15 | 0.03 | 0.96 | 0.78 | 3 | ″ | |||||||
20 | 3 | 11 | 0.15 | 0.03 | 1.27 | 1.09 | 2 | 比较例 | |||||||
21 | 3 | 11 | 0.15 | 0.04 | 0.41 | 0.53 | 3 | 本发明例 | |||||||
22 | 3 | 11 | 0.15 | 0.04 | 0.96 | 0.77 | 3 | ″ | |||||||
23 | 3 | 11 | 0.15 | 0.04 | 1.28 | 1.17 | 2 | 比较例 | |||||||
24 | 3 | 11 | 0.15 | 0.03 | 0.52 | 0.46 | 3 | 本发明例 | |||||||
25 | 3 | 11 | 0.15 | 0.03 | 0.97 | 0.78 | 3 | ″ | |||||||
26 | 3 | 11 | 0.15 | 0.03 | 1.33 | 1.15 | 2 | 比较例 | |||||||
27 | 3 | 11 | 0.15 | 0.03 | 0.38 | 0.44 | 3 | 本发明例 | |||||||
28 | 3 | 11 | 0.15 | 0.03 | 0.93 | 0.78 | 3 | ″ | |||||||
29 | 3 | 11 | 0.15 | 0.03 | 1.41 | 1.11 | 2 | 比较例 | |||||||
30 | 4 | 8 | 0.25 | 0.38 | 0.43 | 3 | 本发明例 | ||||||||
31 | 5 | 10 | 0.3 | 0.45 | 0.57 | 3 | ″ | ||||||||
32 | 6 | 4 | 0.12 | 0.52 | 0.61 | 3 | ″ | ||||||||
33 | 5 | 15 | 1.5 | 0.64 | 0.49 | 3 | ″ | ||||||||
34 | 1 | 2 | 0.06 | 0.76 | 0.52 | 3 | ″ | ||||||||
35 | 3 | 19 | 0.5 | 0.81 | 0.60 | 3 | ″ | ||||||||
36 | 3 | 6 | 0.005 | 0.39 | 0.42 | 3 | ″ | ||||||||
37 | 3 | 11 | 0.15 | 0.0002 | 0.44 | 0.56 | 3 | ″ | |||||||
38 | 3 | 11 | 0.15 | 0.003 | 0.57 | 0.61 | 3 | ″ | |||||||
39 | 3 | 11 | 0.15 | 0.0003 | 0.51 | 0.48 | 3 | ″ |
序号 | 热浸镀锌层的组成(质量%) | 表面粗糙度 | 涂敷后耐蚀性 | 鲜映性 | 备注 | |||||||||||
Mg | Al | Si | Ca | Be | Ti | Cu | Ni | Co | Cr | Mn | Ra | Wca | ||||
1 | 3 | 11 | 0.15 | 0.05 | 0.7 | 0.6 | 5 | 3 | 本发明例 | |||||||
2 | 3 | 11 | 0.15 | 0.03 | 0.7 | 0.6 | 5 | 3 | ″ | |||||||
3 | 3 | 11 | 0.15 | 0.03 | 0.7 | 0.6 | 5 | 3 | ″ | |||||||
4 | 3 | 11 | 0.15 | 0.01 | 0.7 | 0.6 | 5 | 3 | ″ | |||||||
5 | 3 | 11 | 0.15 | 0.05 | 0.7 | 0.6 | 5 | 3 | ″ | |||||||
6 | 3 | 11 | 0.15 | 0.31 | 0.7 | 0.6 | 5 | 3 | ″ | |||||||
7 | 3 | 11 | 0.15 | 0.03 | 0.7 | 0.6 | 5 | 3 | ″ | |||||||
8 | 3 | 11 | 0.15 | 0.01 | 0.7 | 0.6 | 5 | 3 | ″ | |||||||
9 | 3 | 11 | 0.15 | 0.08 | 0.7 | 0.6 | 5 | 3 | ″ | |||||||
10 | 3 | 11 | 0.15 | 0.04 | 0.7 | 0.6 | 5 | 3 | ″ | |||||||
11 | 3 | 11 | 0.15 | 0.01 | 0.7 | 0.6 | 5 | 3 | ″ | |||||||
12 | 3 | 11 | 0.15 | 0.05 | 0.7 | 0.6 | 5 | 3 | ″ | |||||||
13 | 3 | 11 | 0.15 | 0.03 | 0.7 | 0.6 | 5 | 3 | ″ | |||||||
14 | 3 | 11 | 0.15 | 0.01 | 0.7 | 0.6 | 5 | 3 | ″ | |||||||
15 | 3 | 11 | 0.15 | 0.03 | 0.7 | 0.6 | 5 | 3 | ″ | |||||||
16 | 3 | 11 | 0.15 | 0.01 | 0.7 | 0.6 | 5 | 3 | ″ | |||||||
17 | 3 | 11 | 0.15 | 0.1 | 0.7 | 0.6 | 5 | 3 | ″ | |||||||
18 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
19 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
20 | 3 | 11 | 0.15 | 0.02 | 0.2 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
21 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
22 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
23 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
24 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
25 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
26 | 3 | 11 | 0.15 | 0.02 | 0.2 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
27 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
28 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
29 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
30 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
31 | 3 | 11 | 0.15 | 0.02 | 0.2 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
32 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
33 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ |
序号 | 热浸镀锌层的组成(质量%) | 表面粗糙度 | 涂敷后耐蚀性 | 鲜映性 | 备注 | |||||||||||
Mg | Al | Si | Ca | Be | Ti | Cu | Ni | Co | Cr | Mn | Ra | Wca | ||||
34 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | 本发明例 | ||||||
35 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
36 | 3 | 11 | 0.15 | 0.2 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
37 | 3 | 11 | 0.15 | 0.2 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
38 | 3 | 11 | 0.15 | 0.2 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
39 | 3 | 11 | 0.15 | 0.2 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
40 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
41 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
42 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
43 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
44 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
45 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | ||||||
46 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | |||||
47 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | |||||
48 | 3 | 11 | 0.15 | 0.02 | 0.2 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | |||||
49 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | |||||
50 | 3 | 11 | 0.15 | 0.02 | 0.02 | 0.02 | 0.2 | 0.02 | 0.02 | 0.02 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ |
51 | 4 | 8 | 0.25 | 0.02 | 0.2 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | |||||
52 | 5 | 10 | 0.3 | 0.02 | 0.2 | 0.02 | 0.7 | 0.6 | 5 | 3 | ″ | |||||
53 | 6 | 4 | 0.12 | 0.02 | 0.02 | 0.02 | 0.7 | 0.6 | 4 | 3 | ″ | |||||
54 | 5 | 15 | 1.5 | 0.02 | 0.02 | 0.02 | 0.7 | 0.6 | 4 | 3 | ″ | |||||
55 | 1 | 2 | 0.06 | 0.02 | 0.02 | 0.02 | 0.7 | 0.6 | 4 | 3 | ″ | |||||
56 | 3 | 11 | 0.15 | 0.4 | 0.4 | 3 | 3 | 比较例 | ||||||||
57 | 0 | 0.2 | 0 | 0.7 | 0.6 | 1 | 3 | ″ | ||||||||
58 | 3 | 20 | 0.6 | 0.02 | 0.7 | 0.6 | 3 | 3 | ″ | |||||||
59 | 0.1 | 5 | 0 | 0.7 | 0.6 | 2 | 3 | ″ | ||||||||
60 | 3 | 6 | 0.005 | 0.7 | 0.6 | 3 | 3 | 比较例 | ||||||||
61 | 3 | 11 | 0.15 | 0.0002 | 0.7 | 0.6 | 4 | 3 | 本发明例 | |||||||
62 | 3 | 11 | 0.15 | 0.003 | 0.7 | 0.6 | 4 | 3 | ″ | |||||||
63 | 3 | 11 | 0.15 | 0.0003 | 0.7 | 0.6 | 4 | 3 | ″ | |||||||
64 | 3 | 11 | 0.15 | 0.0002 | 0.003 | 0.7 | 0.6 | 4 | 3 | ″ | ||||||
65 | 3 | 11 | 0.15 | 0.0002 | 0.0003 | 0.7 | 0.6 | 4 | 3 | ″ | ||||||
66 | 3 | 11 | 0.15 | 0.003 | 0.0003 | 0.7 | 0.6 | 4 | 3 | ″ |
Claims (6)