JP6992818B2 - 全固体電池 - Google Patents
全固体電池 Download PDFInfo
- Publication number
- JP6992818B2 JP6992818B2 JP2019552367A JP2019552367A JP6992818B2 JP 6992818 B2 JP6992818 B2 JP 6992818B2 JP 2019552367 A JP2019552367 A JP 2019552367A JP 2019552367 A JP2019552367 A JP 2019552367A JP 6992818 B2 JP6992818 B2 JP 6992818B2
- Authority
- JP
- Japan
- Prior art keywords
- negative electrode
- active material
- electrode active
- solid
- solid electrolyte
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
正極11は、正極活物質粒子を含んでいる。好ましく用いられる正極活物質粒子としては、例えば、ナシコン型構造を有するリチウム含有リン酸化合物粒子、オリビン型構造を有するリチウム含有リン酸化合物粒子、リチウム含有層状酸化物粒子、スピネル型構造を有するリチウム含有酸化物粒子等が挙げられる。好ましく用いられるナシコン型構造を有するリチウム含有リン酸化合物の具体例としては、Li3V2(PO4)3等が挙げられる。好ましく用いられるオリビン型構造を有するリチウム含有リン酸化合物の具体例としては、Li3Fe2(PO4)3、LiMnPO4等が挙げられる。好ましく用いられるリチウム含有層状酸化物粒子の具体例としては、LiCoO2,LiCo1/3Ni1/3Mn1/3O2等が挙げられる。好ましく用いられるスピネル型構造を有するリチウム含有酸化物の具体例としては、LiMn2O4,LiNi0.5Mn1.5O4、Li4Ti5O12等が挙げられる。なかでも、下記の負極活物質及びガーネット型固体電解質を用いる本実施形態においては、LiCoO2,LiCo1/3Ni1/3Mn1/3O2等のリチウム含有層状酸化物がより好ましく用いられる。なお、これらの正極活物質粒子のうちの1種のみを用いてもよいし、複数種類を混合して用いてもよい。
負極12は、負極活物質層を有している。負極活物質層は、LISICON型の結晶構造を有する酸化物を60体積%以上含む。負極活物質層は、LISICON型の結晶構造を有する酸化物を65体積%以上含むことが好ましく、70体積%以上含むことがより好ましい。負極活物質層は、例えば、LISICON型の結晶構造を有する酸化物のみにより構成されていてもよい。
固体電解質層13は、ガーネット型の結晶構造を有する酸化物及びLISICON型の結晶構造を有する酸化物の少なくとも一方を固体電解質として含む。
次に、全固体電池1の製造方法の一例について説明する。
〔固体電解質粉末の作製〕
水酸化リチウム一水和物(LiOH・H2O)、酸化ガリウム(Ga2O3)、酸化アルミニウム(Al2O3)、水酸化ランタン(La(OH)3)、酸化ジルコニウム(ZrO2)を含む原料を、固体電解質の組成が下記の表1に示す組成となるように秤量した。次に、水を添加し、100mlのポリエチレン製ポリポットに封入して、ポット架上で150rpm、16時間回転させ、原料を混合した。なお、また、Li源である水酸化リチウム一水和物(LiOH・H2O)は焼結時のLi欠損を考慮し、狙い組成に対し、3質量%過剰に仕込んだ。
水酸化リチウム一水和物(LiOH・H2O)、五酸化バナジウム(V2O5)を、負極活物質粉末の組成が下記の表1に示す組成となるように秤量した。次に、水を添加し、100mlのポリエチレン製ポリポットに封入して、ポット架上で150rpm、16時間回転させ、原料を混合した。
上記作製の負極活物質粉末と導電助剤としてのAgとにアルコール、バインダを加え、混練することで、負極合材ペーストを調製した。この負極合材ペーストを上記作製の焼結タブレットの上に塗布し、乾燥させた。その後、400℃に加熱し、バインダを除去した後に、750℃~800℃で3時間熱処理することで焼結タブレットの一方の主面上に負極活物質層を形成した。
〔固体電解質粉末の作製〕
比較例1と同様にして固体電解質粉末を作製した。
水酸化リチウム一水和物(LiOH・H2O)、五酸化バナジウム(V2O5)、酸化ケイ素(SiO2)を、負極活物質の組成が下記の表1に示す組成となるように秤量したこと以外は、比較例1と同様にして負極活物質粉末を作製した。
比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
比較例1と同様にして固体電解質粉末を作製した。
水酸化リチウム一水和物(LiOH・H2O)、五酸化バナジウム(V2O5)、酸化ゲルマニウム(GeO2)を、負極活物質の組成が下記の表1に示す組成となるように秤量したこと以外は、比較例1と同様にして負極活物質粉末を作製した。
比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
比較例1と同様にして固体電解質粉末を作製した。
水酸化リチウム一水和物(LiOH・H2O)、五酸化バナジウム(V2O5)、酸化チタン(TiO2)を、負極活物質の組成が下記の表1に示す組成となるように秤量したこと以外は、比較例1と同様にして負極活物質粉末を作製した。
比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
比較例1と同様にして固体電解質粉末を作製した。
水酸化リチウム一水和物(LiOH・H2O)、五酸化バナジウム(V2O5)、酸化リン(P2O5)を、負極活物質の組成が下記の表1に示す組成となるように秤量したこと以外は、比較例1と同様にして負極活物質粉末を作製した。
比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
比較例1と同様にして固体電解質粉末を作製した。
水酸化リチウム一水和物(LiOH・H2O)、酸化アルミニウム(Al2O3)、五酸化バナジウム(V2O5)、酸化ケイ素(SiO2)を、負極活物質の組成が下記の表1に示す組成となるように秤量したこと以外は、比較例1と同様にして負極活物質粉末を作製した。
比較例1と同様にして全固体電池を作製した。
実施例1~実施例12及び比較例1において作製した全固体電池に対して、0.05Itに相当する電流密度で電位範囲0.3V~3.0V(vs.Li/Li+)で定電流放電試験を行った。その結果、求められた初期可逆電気量を負極活物質の質量で除算することにより、初期可逆容量を算出した。また、負極活物質中のVが2電子反応進行した際の容量を理論容量とし、上記初期可逆容量を理論容量で除算することで利用率を算出した。
〔固体電解質粉末の作製〕
水酸化リチウム一水和物(LiOH・H2O)、酸化ゲルマニウム(GeO2)、酸化アルミニウム(Al2O3)、酸化リン(P2O5)を、固体電解質の組成が下記の表2に示す組成となるように秤量したこと以外は、実施例4と同様にして負極活物質粉末を作製した。
実施例4と同様にして負極活物質粉末を作製した。
比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
水酸化リチウム一水和物(LiOH・H2O)、水酸化ランタン(La(OH)3)、酸化チタン(TiO2)を、固体電解質の組成が下記の表2に示す組成となるように秤量したこと以外は、実施例4と同様にして負極活物質粉末を作製した。
実施例4と同様にして負極活物質粉末を作製した。
比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
水酸化リチウム一水和物(LiOH・H2O)、水酸化ランタン(La(OH)3)、酸化ジルコニウム(ZrO2)、酸化タンタル(Ta2O5)を、固体電解質の組成が下記の表2に示す組成となるように秤量したこと以外は、比較例1と同様にして負極活物質粉末を作製した。
実施例4と同様にして負極活物質粉末を作製した。
比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
水酸化リチウム一水和物(LiOH・H2O)、酸化アルミニウム(Al2O3)、水酸化ランタン(La(OH)3)、酸化ジルコニウム(ZrO2)を、固体電解質の組成が下記の表2に示す組成となるように秤量したこと以外は、比較例1と同様にして負極活物質粉末を作製した。
実施例4と同様にして負極活物質粉末を作製した。
比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
水酸化リチウム一水和物(LiOH・H2O)、酸化ガリウム(Ga2O3)、酸化スカンジウム(Sc2O3)、水酸化ランタン(La(OH)3)、酸化ジルコニウム(ZrO2)を、固体電解質の組成が下記の表2に示す組成となるように秤量したこと以外は、比較例1と同様にして負極活物質粉末を作製した。
実施例4と同様にして負極活物質粉末を作製した。
比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
水酸化リチウム一水和物(LiOH・H2O)、水酸化ランタン(La(OH)3)、酸化ジルコニウム(ZrO2)、酸化ニオブ(Nb2O5)を、固体電解質の組成が下記の表2に示す組成となるように秤量したこと以外は、比較例1と同様にして負極活物質粉末を作製した。
実施例4と同様にして負極活物質粉末を作製した。
比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
水酸化リチウム一水和物(LiOH・H2O)、酸化アルミニウム(Al2O3)、水酸化ランタン(La(OH)3)、酸化ジルコニウム(ZrO2)、酸化ニオブ(Nb2O5)を、固体電解質の組成が下記の表2に示す組成となるように秤量したこと以外は、比較例1と同様にして負極活物質粉末を作製した。
実施例4と同様にして負極活物質粉末を作製した。
比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
水酸化リチウム一水和物(LiOH・H2O)、酸化アルミニウム(Al2O3)、水酸化ランタン(La(OH)3)、酸化ジルコニウム(ZrO2)、酸化ビスマス(Bi2O3)を、固体電解質の組成が下記の表2に示す組成となるように秤量したこと以外は、比較例1と同様にして負極活物質粉末を作製した。
実施例4と同様にして負極活物質粉末を作製した。
比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
水酸化リチウム一水和物(LiOH・H2O)、酸化ゲルマニウム(GeO2)、酸化リン(P2O5)を、固体電解質の組成が下記の表2に示す組成となるように秤量したこと以外は、比較例1と同様にして負極活物質粉末を作製した。
実施例4と同様にして負極活物質粉末を作製した。
比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
水酸化リチウム一水和物(LiOH・H2O)、酸化ケイ素(SiO2)、酸化リン(P2O5)を、固体電解質の組成が下記の表2に示す組成となるように秤量したこと以外は、比較例1と同様にして負極活物質粉末を作製した。
実施例4と同様にして負極活物質粉末を作製した。
比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
水酸化リチウム一水和物(LiOH・H2O)、五酸化バナジウム(V2O5)、酸化ケイ素(SiO2)を、固体電解質の組成が下記の表2に示す組成となるように秤量したこと以外は、比較例1と同様にして負極活物質粉末を作製した。
実施例4と同様にして負極活物質粉末を作製した。
比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
水酸化リチウム一水和物(LiOH・H2O)、酸化ガリウム(Ga2O3)、酸化アルミニウム(Al2O3)、水酸化ランタン(La(OH)3)、酸化ジルコニウム(ZrO2)、五酸化バナジウム(V2O5)、酸化ケイ素(SiO2)、酸化ホウ素(B2O3)を、固体電解質の組成が下記の表2に示す組成となるように秤量したこと以外は、比較例1と同様にして負極活物質粉末を作製した。
実施例4と同様にして負極活物質粉末を作製した。
比較例1と同様にして全固体電池を作製した。
実施例13~実施例22及び比較例2、比較例3において作製した全固体電池に対しても実施例1等と同様の評価を行い、初期可逆容量及び利用率を算出した。
〔固体電解質粉末の作製〕
実施例4と同様にして固体電解質粉末を作製した。
実施例4と同様にして負極活物質粉末を作製した。
導電助剤を用いなかったこと以外は、比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
実施例19と同様にして固体電解質粉末を作製した。
実施例19と同様にして負極活物質粉末を作製した。
導電助剤を用いなかったこと以外は、比較例1と同様にして全固体電池を作製した。
実施例23~実施例24において作製した全固体電池に対しても実施例1等と同様の評価を行い、初期可逆容量及び利用率を算出した。
〔固体電解質粉末の作製〕
実施例23と同様にして固体電解質粉末を作製した。
実施例4と同様にして負極活物質粉末を作製した。
負極活物質及び導電助剤の配合割合を表4に示す割合としたこと以外は、比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
実施例23と同様にして固体電解質粉末を作製した。
実施例25と同様にして負極活物質粉末を作製した。
焼結助剤としてLi3BO3を用い、負極活物質、導電助剤及び焼結助剤の配合割合を表4に示す割合としたこと以外は、比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
実施例23と同様にして固体電解質粉末を作製した。
実施例25と同様にして負極活物質粉末を作製した。
導電助剤としてカーボンナノファイバー(VGCF(登録商標))を用い、負極活物質、導電助剤及び焼結助剤の配合割合を表4に示す割合としたこと以外は、比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
実施例23と同様にして固体電解質粉末を作製した。
実施例25と同様にして負極活物質粉末を作製した。
負極活物質、導電助剤及び焼結助剤の配合割合を表4に示す割合としたこと以外は、実施例27と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
実施例23と同様にして固体電解質粉末を作製した。
実施例25と同様にして負極活物質粉末を作製した。
焼結助剤としてB2O3を用い、負極活物質、導電助剤及び焼結助剤の配合割合を表4に示す割合としたこと以外は、比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
実施例23と同様にして固体電解質粉末を作製した。
実施例25と同様にして負極活物質粉末を作製した。
焼結助剤としてLiBO2を用い、負極活物質、導電助剤及び焼結助剤の配合割合を表4に示す割合としたこと以外は、比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
実施例23と同様にして固体電解質粉末を作製した。
実施例25と同様にして負極活物質粉末を作製した。
焼結助剤としてLi2.4Al0.2BO3を用い、負極活物質、導電助剤及び焼結助剤の配合割合を表4に示す割合としたこと以外は、比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
実施例23と同様にして固体電解質粉末を作製した。
実施例25と同様にして負極活物質粉末を作製した。
焼結助剤としてLi2.2C0.8B0.2O3を用い、負極活物質、導電助剤及び焼結助剤の配合割合を表4に示す割合としたこと以外は、比較例1と同様にして全固体電池を作製した。
〔固体電解質粉末の作製〕
実施例23と同様にして固体電解質粉末を作製した。
実施例25と同様にして負極活物質粉末を作製した。
焼結助剤としてLi4B2O5を用い、負極活物質、導電助剤及び焼結助剤の配合割合を表4に示す割合としたこと以外は、比較例1と同様にして全固体電池を作製した。
実施例25~実施例33において作製した全固体電池に対しても実施例1等と同様の評価を行い、初期可逆容量及び利用率を算出した。
Claims (4)
- 正極と、
負極活物質層を有する負極と、
前記正極と前記負極活物質層との間に設けられた固体電解質層と、
を備える全固体電池であって、
前記負極活物質層は、負極活物質として、LISICON型の結晶構造を有する酸化物を、60体積%以上含み、
前記負極活物質としての前記LISICON型の結晶構造を有する酸化物が5価のVを含み、
前記固体電解質層は、ガーネット型の結晶構造を有する酸化物及びLISICON型の結晶構造を有する酸化物の少なくとも一方を固体電解質として含み、
前記負極活物質層は、導電助剤をさらに含む、全固体電池。 - 前記負極活物質層に含まれるLISICON型の結晶構造を有する酸化物は、化学式(Li[3-ax+(5-b)y]Ax)(V(1-y)By)O4(Aは、Na、K、Mg、Ca、Al、Ga、Zn、Fe、Cr及びCoからなる群から選ばれた少なくとも一種の元素であり、Bは、Zn、Al、Ga、Si、Ge、Sn、P、As、Ti、Mo、W、Fe、Cr及びCoからなる群から選ばれた少なくとも一種の元素であり、0≦x≦1.0、0≦y≦0.6、aはAの価数、bはBの価数である。)で表される酸化物である、請求項1に記載の全固体電池。
- 前記化学式において、0≦x≦0.2、0.1≦y≦0.4である、請求項2に記載の全固体電池。
- 前記負極活物質層は、焼結助剤をさらに含む、請求項1~3のいずれか一項に記載の全固体電池。