JP5686840B2 - 表面処理電解銅箔及びその表面処理銅箔を用いて得られる銅張積層板 - Google Patents
表面処理電解銅箔及びその表面処理銅箔を用いて得られる銅張積層板 Download PDFInfo
- Publication number
- JP5686840B2 JP5686840B2 JP2013091303A JP2013091303A JP5686840B2 JP 5686840 B2 JP5686840 B2 JP 5686840B2 JP 2013091303 A JP2013091303 A JP 2013091303A JP 2013091303 A JP2013091303 A JP 2013091303A JP 5686840 B2 JP5686840 B2 JP 5686840B2
- Authority
- JP
- Japan
- Prior art keywords
- copper foil
- electrolytic copper
- treated
- treated electrolytic
- clad laminate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
a)試料片の非測定面を試料台に密着させて固定する。
b)試料片の1cm角の範囲内において108μm×144μmの視野を6点選択して測定する。
c)6箇所の測定点から得られた値の平均値を試料の代表値として採用する。
この実施例では、各種添加剤濃度を表1に記載の濃度に調整した電解液7種類を用い、電解銅箔を作成した。具体的には、硫酸系銅電解液として、硫酸銅(試薬)と硫酸(試薬)とを純水に溶解し、銅濃度80g/L、フリー硫酸濃度140g/Lに調製し、基本溶液とした。そして、この基本溶液に、活性硫黄化合物のスルフォン酸塩としてMPS−Na又はSPS−Na、環状構造を持つ4級アンモニウム塩重合体としてDDAC重合体3種(センカ(株)製ユニセンス:FPA100L、FPA101L、FPA102L)及び塩酸を添加した。なお、用いたDDAC重合体の分子量はFPA100L<FPA101L<FPA102Lである。
そして、実施例1〜実施例11で得られたそれぞれの電解銅箔の両面に防錆処理を施した。ここでは以下に述べる条件の無機防錆を採用した。硫酸亜鉛浴を用い、フリー硫酸濃度70g/L、亜鉛濃度20g/Lとし、液温40℃、電流密度15A/dm2とした亜鉛防錆処理を施した。更に、前記亜鉛防錆を施した後に、電解でクロメート防錆処理を施した。このときの電解条件は、クロム酸濃度5.0g/L、pH 11.5、液温35℃、電流密度8A/dm2、電解時間5秒とした。
以降、表2、表3及び表4に記載の電解銅箔及び表面処理電解銅箔から得られたデータを用い、本件実施例と比較例に係る電解銅箔、表面処理電解銅箔を対比して説明する。
I 接着面
SWT うねりの頂点側を向いて形成されたサイドウォール
SWV うねりの谷側を向いて形成されたサイドウォール
W 配線
Claims (10)
- 電解銅箔の表面に防錆処理又はシランカップリング剤処理のいずれか一種以上を施した表面処理電解銅箔であって、
当該表面処理電解銅箔の絶縁層構成材料との接着面は、表面粗さ(Rzjis)が0.1μm〜1.0μmであり、且つ、光沢度[Gs(60°)]が400以上の電解銅箔の表面を用いて得られるものであり、
当該接着面の凹凸の最大高低差(PV)が、0.05μm〜1.5μmであることを特徴とする表面処理電解銅箔。 - 電解銅箔の表面に防錆処理又はシランカップリング剤処理のいずれか一種以上を施した表面処理電解銅箔であって、
当該表面処理電解銅箔の絶縁層との接着面が備える凹凸の最大高低差(PV)が0.05μm〜0.8μmであることを特徴とする表面処理電解銅箔。 - 当該接着面のうねりの最大高低差(Wmax)が0.05μm〜0.7μmである請求項1又は請求項2に記載の表面処理電解銅箔。
- 前記接着面のうねりの最大高低差(Wmax)と凹凸の最大高低差(PV)との比〔(Wmax)/(PV)〕が0.8以上である請求項3に記載の表面処理電解銅箔。
- 当該接着面の表面粗さ(RSm)が、0.1mmより大であることを特徴とする請求項1〜請求項4にいずれかに記載の表面処理電解銅箔。
- 前記接着面の表面粗さ(Rzjis)が、0.1μm〜1.0μmである請求項1〜請求項5のいずれかに記載の表面処理電解銅箔。
- 前記接着面は、電解銅箔の析出面側を用いて得られたものである請求項1〜請求項6のいずれかに記載の表面処理電解銅箔。
- 請求項1〜請求項7のいずれかに記載の表面処理電解銅箔と絶縁層構成材料とを張合わせて得られたことを特徴とする銅張積層板。
- 表面の銅を溶解除去した後に露出する絶縁層構成材料表面のうねりの高低差(Wmax)が0.05μm〜0.7μmである請求項8に記載の銅張積層板。
- 請求項8又は請求項9に記載の銅張積層板を用いて得られたことを特徴とするプリント配線板。