JP4902545B2 - 導電性複合繊維及びその製造方法 - Google Patents
導電性複合繊維及びその製造方法 Download PDFInfo
- Publication number
- JP4902545B2 JP4902545B2 JP2007540945A JP2007540945A JP4902545B2 JP 4902545 B2 JP4902545 B2 JP 4902545B2 JP 2007540945 A JP2007540945 A JP 2007540945A JP 2007540945 A JP2007540945 A JP 2007540945A JP 4902545 B2 JP4902545 B2 JP 4902545B2
- Authority
- JP
- Japan
- Prior art keywords
- conductive
- fiber
- conductive layer
- polymer
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
0≦|φ1−φ2|≦1.1 (I)
1.8≦DT≦4.5 (II)
50≦DE≦90 (III)
(但し、上記式中、φ1はポリエステル系ポリマー(A)のSP値[(cal/cm3)1/2]、φ2はポリエステル系ポリマー(B)のSP値[(cal/cm3)1/2]、DTは繊維強度(cN/dtex)、DEは伸度(%)を意味する。)
3≦N≦8 (IV)
25≦S≦45 (V)
1.0×109≦E’≦6.0×109 (VI)
(但し、上記式中、Nは導電層の露出部の数、Sは繊維の表面全体に占める導電層の表面露出面積割合(%)、E’は10Hz、100℃における貯蔵弾性率(Pa)を意味する。)
(1)上記(A)の溶融ポリマー液と(B)の溶融ポリマー液を合流して複合紡糸口金より溶融吐出する。
(2)吐出された溶融ポリマーを、一旦ガラス転移点未満の温度に冷却する。
(3)次いで加熱装置内を走行させて延伸熱処理する。
(4)その後に油剤を付与する。
(5)3000m/分以上の速度で巻き取る。
(6)上記(1)〜(3)を、吐出糸条が最初にローラーあるいはガイドに接する以前に行う。
B:保護ポリマー層
1.8≦DT≦4.5 (II)
50≦DE≦90 (III)
(但し、上記式中、DTは繊維強度(cN/dtex)、DEは伸度(%)を意味する。)
0≦|φ1−φ2|≦1.1 (I)
(但し、上記式中、φ1はポリエステル系ポリマー(A)のSP値[(cal/cm3)1/2]、φ2はポリエステル系ポリマー(B)のSP値[(cal/cm3)1/2]を意味する。)
3≦N≦8 (IV)
25≦S≦45 (V)
1.0×109≦E’≦6.0×109 (VI)
(但し、上記式中、Nは導電層の露出部の数、Sは繊維の表面全体に占める導電層の表面露出面積割合(%)、E’は10Hz、100℃における貯蔵弾性率(Pa)を意味する。)
(a)単に紡糸しただけの未延伸繊維をそのまま導電性繊維として使用する方法。
(b)紡糸した繊維を一旦ボビンに巻き取り、そしてそれを延伸する方法。
(c)吐出した繊維を第一ローラーで集束し、巻き取ることなく直ちに延伸する、いわゆる紡糸直結延伸する方法。
(1)上記(A)の溶融ポリマー液と(B)の溶融ポリマー液を合流して複合紡糸口金より溶融吐出する。
(2)吐出された溶融ポリマーを、一旦ガラス転移点未満の温度に冷却する。
(3)次いで加熱装置内を走行させて延伸熱処理する。
(4)その後に油剤を付与する。
(5)3000m/分以上の速度で巻き取る。
(6)上記(1)〜(3)を、吐出糸条が最初にローラーあるいはガイドに接する以前に行う。
1×106<R0<9×109 (7)
0≦|log(R1/R0)|<2 (8)
1≦DEd≦20 (9)
上記式中、R0は0HL(洗濯未処理)の糸抵抗値(Ω/cm・f)、R1は100HL後(洗濯100回後)の糸抵抗値(Ω/cm・f)、DEdは限界伸度(糸抵抗値が1012Ω/cm・fに達する時の伸度(%))を表す。
電圧電流計法により、平行クリップ電極にセットされた導電性繊維(単繊維)試料に、直流電圧25〜500Vを印可し、その電圧とその時の試料に流れる電流値からオームの法則により求めた。また、本発明で規定される電気抵抗値は100V印可時で求めたものである。
繊維の除電性能評価は、導電性繊維を布帛中に含有せしめたときの布帛の摩擦における帯電電荷量の測定をもって行なった。すなわち、JIS−1094に準じて測定した。測定は22℃、相対湿度40%の部屋に24時間放置し、同室内にて行なった。
JIS−1013Lに準ずる。繊維長10cm、伸長速度100%/分、常温で測定。
導電性繊維を布帛中に含有し、硫酸3重量%水溶液中に布帛を24時間浸け、その後24時間自然乾燥させて、水洗し、導電性繊維の強度を測定した。
A:強度保持率95%以上
B:強度保持率70%以上95%未満
C:強度保持率70%未満
強度保持率={(処理前強度−処理後強度)/処理前強度}×100}
動的粘弾性の測定により求められる。
装置:DVE−14 FTレオスペクトラー(UBM製)
測定条件:繊維長1cm、周波数10Hz、変位5μm、
昇温速度3℃/分(−100〜250℃)
電圧電流計法により、平行クリップ電極にセットされた導電性繊維(単繊維)試料に、直流電圧25〜500Vを印可し、その電圧とその時の試料に流れる電流値からオームの法則により求めた。また、本発明で規定される電気抵抗値は100V印可時で求めたものである。
強伸度測定器にて伸長した糸の抵抗値を測定する。
抵抗値の測定は上記に準ずる。
SP値=ρΣG/Mにより計算した値。
G:原子および原子団の凝集エネルギー定数 M:構造単位の分子量
繊維断面の電子顕微鏡写真(×2000倍)から任意の10個の繊維断面を選び、その平均値を求める。
遠心沈降法により測定した一次平均粒子径を意味する。
導電ポリマー層(A)用の成分として、導電性カーボンブラックを25重量%含有したポリブチレンテレフタレート(PBT:融点225℃)を用い、保護ポリマー層(B)用の成分として平均粒子径0.4μmの酸化チタンを0.5重量%含有するポリエチレンテレフタレート(PET:融点255℃)を用い、複合比率10/90(重量%)、4芯芯鞘の芯露出型断面で複合紡糸し、4本の複合フィラメントの集合体からなり、その合計繊度が22dtexの導電性複合マルチフィラメントを得た。紡糸方法として、上記(A)の溶融物と(B)の溶融物を合流して複合紡糸口金より溶融吐出し、吐出された溶融ポリマーを、一旦ガラス転移点未満の温度に冷却し、次いで加熱装置内を走行させて延伸熱処理し、その後に油剤を付与し、そして3500m/分の速度で巻き取る方法を用い、上記吐出糸条が最初にローラーあるいはガイドに接する以前に上記延伸熱処理を行った。なお、上記冷却方法として、25℃の冷却風を0.5m/秒の速度でノズル直下の繊維に吹き当てた。また、延伸熱処理方法として、ノズル直下1.5mの位置に、直径3cm、長さ1mの加熱チューブを設け、チューブ内を180℃に保つ方法を用いた。繊維化工程性は良好で問題なかった。この導電性複合繊維の構成および繊維化条件を纏めて表1に示す。またこの導電性繊維の断面形状に関する値を表3に示す。
保護ポリマー層(B)として、表1の実施例2〜4に示すものを使用し、そして導電ポリマー層の露出部の数を実施例5に示した個数にする以外はそれぞれ実施例1と同様に実施し、導電性繊維を得た。いずれも耐酸性及び電気性能も良好であった。評価結果を表1及び表2に示す。またこれらの導電性繊維の断面形状に関する値等を表3に示す。
導電ポリマー層(A)、保護ポリマー層(B)を表1に示すポリマーを用いて実施例1と同様にして実施したが、比較例1、2は耐酸性、比較例2、3は導電層と保護ポリマー層との剥離により繊維化工程性が不良であった。
導電ポリマー層の露出部の数を変更すること以外は実施例1と同様の条件で実施したが、実施例6は電気特性、実施例7は耐酸性が不十分であった。
繊維断面を図1とし、導電層の位置を動かすか、あるいは導電層比率を変更することにより1個の導電層の露出長を表2に示す数字に変更した以外は実施例1と同様の条件で実施したが、実施例8は電気特性が不十分で、実施例9は毛羽断糸が発生した。
紡糸・延伸条件を、紡糸速度1000m/分で紡糸後、ホットローラー(HR)とコールドローラー(CR)の間にホットプレート(HP)を設置した延伸装置を用い、CRの表面速度をHRの表面速度の2.8倍とし、HRの表面温度を80℃、HRとCRの間に設置したHPを120℃の条件で延伸して、延伸後22dtexとなる吐出量に設定し、伸度を40%にする以外は実施例1と同様にして実施したが、電気特性の耐久性に劣る結果しか得られなかった。
紡糸・延伸条件として、紡糸速度3800m/分で巻取り(延伸なし)、伸度および強度をそれぞれ120%及び1.5cN/dtexとした以外は実施例1と同様にして実施したが、電気特性の耐久性に劣る結果が得られた。
導電ポリマー層(A)は鞘成分として、導電性カーボンブラックを25重量%含有したポリブチレンテレフタレート(PBT:融点225℃)を用い、保護ポリマー層(B)は芯成分として平均粒子径0.4μmの酸化チタンを0.5重量%含有するポリエチレンテレフタレート(PET:融点255℃)を用い、複合比率(鞘/芯)15/85(重量%)、芯鞘型断面(単芯)で複合紡糸し、4本の複合フィラメントの集合体からなり、その合計繊度が22dtexの導電性複合マルチフィラメントを得た。紡糸方法としては、実施例1と同様の方法を用いた。繊維化工程性は良好で問題なかった。この導電性複合繊維の構成および評価結果を纏めて表4に示す。この導電性複合繊維は表面全面を導電層が覆っていた。
導電層(A)と保護ポリマー層(B)がそれぞれ鞘と芯を形成し、その比を表4の実施例11〜13に示す値とする以外は実施例10と同様に繊維化し性能評価に供した。その結果、得られた導電性繊維及びこれを用いた織物評価ともに良好であった。すなわち導電層の重量比率が15重量%〜50重量%の範囲では製糸性、性能とも良好であることが確認された。これらの導電性複合繊維において、何れも、繊維表面は導電層により完全に覆われていた。
導電層(A)と保護ポリマー層(B)がそれぞれ鞘と芯を形成し、その比を表4の実施例14に示す値とする以外は実施例10と同様に繊維化し性能評価に供した。その結果、得られた導電性繊維及びこれを用いた織物評価ともに実施例10の繊維に比べて性能が低かった。また、繊維表面の導電層の被覆状態が不均一であり、導電層により覆われておらずに、芯成分の保護層が露出している部分も見られた。
紡糸速度1000m/分で紡糸した後、ホットローラー(HR)とコールドローラー(CR)の間にホットプレート(HP)を設置した延伸装置を用い、HR温度80℃、ホットプレート温度120℃で、延伸倍率2.8倍で延伸した以外は実施例10と同様に繊維化し性能評価に供した。その結果、得られた導電性繊維及びこれを用いた織物評価ともに実施例10の繊維に比べて性能が低かった。
紡糸速度を3800m/分とし、延伸熱処理を行わなかった以外は実施例10と同様に繊維化し性能評価に供した。その結果、製糸性は不良であり、得られた導電性繊維及びこれを用いた織物評価ともに実施例10の繊維に比べて性能が低かった。
Claims (10)
- 導電性カーボンブラックを23〜33重量%含有する融点が200℃以上のポリエステル系ポリマー(A)からなる導電層と、融点が210℃以上のポリエステル系ポリマー(B)からなる保護層とからなる導電性複合繊維であって、下記式(I)〜(III)を満足することを特徴する導電性複合繊維。
0≦|φ1−φ2|≦1.1 (I)
1.8≦DT≦4.5 (II)
50≦DE≦90 (III)
式中、φ1はポリエステル系ポリマー(A)のSP値[(cal/cm3)1/2]、φ2はポリエステル系ポリマー(B)のSP値[(cal/cm3)1/2]、DTは繊維強度(cN/dtex)、DEは伸度(%)を意味する。 - 下記式(IV)〜(VI)を満足する請求項1記載の導電性複合繊維。
3≦N≦8 (IV)
25≦S≦45 (V)
1.0×109≦E’≦6.0×109 (VI)
式中、Nは導電層の露出部の数、Sは繊維の表面全体に占める導電層の表面露出面積割合(%)、E’は10Hz、100℃における貯蔵弾性率(Pa)を意味する。 - 繊維軸に直角な方向での繊維断面における導電層の形状において、繊維表面露出部の長さ(L1)に対する導電層厚み(D1)の比(D1/L1)が0.15〜1.0である請求項2記載の導電性複合繊維。
- 導電層の断面形状が両面凸型の凸レンズの断面形状に類似した形状であり、繊維に占める導電層の重量割合が5〜15重量%の範囲である請求項2又は3に記載の導電性複合繊維。
- 導電層を鞘成分とし保護層を芯成分とする芯鞘型複合繊維であって、複合繊維に占める導電層の重量割合が15〜50重量%である請求項1記載の導電性複合繊維。
- 導電層を構成するポリエステル系ポリマー(A)がポリブチレンテレフタレート系の樹脂であり、かつ保護層を構成するポリエステル系ポリマー(B)がポリエチレンテレフタレート系の樹脂である請求項1〜5のいずれか記載の導電性複合繊維。
- 保護層を形成するポリエステル系ポリマー(B)が、平均粒径0.01〜1μmの無機微粒子を0.05〜10重量%の割合で含有する請求項1〜6のいずれか記載の導電性複合繊維。
- 請求項1〜7のいずれかに記載の導電性複合繊維を3〜6本束ねてなるマルチフィラメントであって、該マルチフィラメントの合計繊度が10〜40dtexであるマルチフィラメント。
- 請求項1〜7のいずれかに記載の導電性複合繊維が、経糸または緯糸として間隔をおいて打ち込まれた織物からなる防塵衣。
- 導電性カーボンブラックを23〜33重量%含有する融点が200℃以上のポリエステル系ポリマー(A)と融点が210℃以上のポリエステル系ポリマー(B)を複合紡糸して導電性複合繊維を製造する方法において、以下の(1)〜(5)をその順序で、かつ下記(6)を満足するように実施することを特徴とする導電性複合繊維の製造方法。
(1)上記(A)の溶融ポリマー液と(B)の溶融ポリマー液を合流して複合紡糸口金より溶融吐出する。
(2)吐出された溶融ポリマーを、一旦ガラス転移点未満の温度に冷却する。
(3)次いで加熱装置内を走行させて延伸熱処理する。
(4)その後に油剤を付与する。
(5)3000m/分以上の速度で巻き取る。
(6)上記(1)〜(3)を、吐出糸条が最初にローラーあるいはガイドに接する以前に行う。