JP2013057162A - 部分配向ポリ(トリメチレンテレフタラート)糸 - Google Patents
部分配向ポリ(トリメチレンテレフタラート)糸 Download PDFInfo
- Publication number
- JP2013057162A JP2013057162A JP2012281245A JP2012281245A JP2013057162A JP 2013057162 A JP2013057162 A JP 2013057162A JP 2012281245 A JP2012281245 A JP 2012281245A JP 2012281245 A JP2012281245 A JP 2012281245A JP 2013057162 A JP2013057162 A JP 2013057162A
- Authority
- JP
- Japan
- Prior art keywords
- yarn
- partially oriented
- elongation
- break
- texturing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】ポリエステルポリマーから製造される部分配向糸であって、前述のポリマーは、繰返し単位の少なくとも85モル%がトリメチレン単位からなる少なくとも85モル%のポリ(トリメチレンテレフタラート)を含み、前述のポリマーは少なくとも0.70dl/gの固有粘度を有し、この部分配向糸は少なくとも110%の破断伸びを有する。さらに、部分配向糸の紡糸方法および部分配向フィード糸の連続延伸テキスチャリング方法。
【選択図】図5
Description
安定な部分配向ポリ(トリメチレンテレフタラート)糸が本発明により開発された。さらに、部分配向ポリ(トリメチレンテレフタラート)糸のフリクション仮撚りテキスチャリング方法も開発された。本発明は部分配向ポリ(トリメチレンテレフタラート)糸およびこのような糸のフリクション仮撚りテキスチャリング方法に関してこれまでに経験された問題を克服する。
以下の実施例で報告される部分配向ポリ(トリメチレンテレフタラート)糸の物理的性質は、Instron Corp.の引張試験機、モデルno.1122を用いて測定された。より具体的には、破断伸び、EB、およびテナシティはASTMD−2256にしたがって測定された。
実施例I−ポリマー調製
ポリ(トリメチレンテレフタラート)ポリマーを1,3−プロパンジオールおよびテレフタル酸ジメチルから、2容器方法で、最終ポリマーに対して60部/100万部(「ppm」)(マイクログラム/グラム)のチタン酸テトライソプロピル触媒、Tyzor(登録商標)TPT(イー・アイ・デュポン・ドゥ・ヌムール・アンド・カンパニー(Wilmington,DW))を用いて調製した。溶融テレフタル酸ジメチルを185℃でエステル交換反応容器内の1,3−プロパンジオールおよび触媒に加え、メタノールを除去しながら温度を210℃に上げた。二酸化チタンを、ポリマー中TiO2が0.3重量%となるように、1,3−プロパンジオール中20%のスラリとしてプロセスに加えた。得られた中間体を重縮合容器に移し圧力を1ミルバールに下げ温度を255℃に上げた。所望の溶融粘度に達したとき、圧力を上げポリマーを押出し、冷却し、そしてペレットにカットした。ペレットを、212℃で操作されるタンブルドライヤ中で固相重合して固有粘度を1.04dl/gとした。
糸を、慣用の再溶融1軸押出し方法および慣用のポリエステル繊維溶融紡糸(S−ラップ)方法を用いて、実施例Iで調製されたポリ(トリメチレンテレフタラート)ペレットから紡糸した。溶融紡糸プロセスの条件は以下の表IIに与えられている。ポリマーを表IIに記載されるような形状および直径をもつオリフィスを通して押出した。紡糸ブロックを、ポリマー温度が表IIに記載されたようになるのに必要な温度に保った。紡糸口金を出るフィラメントの流れを21℃の空気で冷却し、束に集め、紡糸仕上げを塗布し、さらにフィラメントをインターレースし収束した。部分配向ポリ(トリメチレンテレフタラート)糸の物理的性質はInstron Corp.引張試験機、モデルno.1122を用いて測定され、表IIIに記載されている。
この実施例は、本発明により製造された部分配向糸は後の延伸作業に有用であるということを示した。この実施例はさらに、フラットヤーン、すなわちこの例における糸がテキスチャを付与されなかったとき、糸は有用であることを示した。実施例II−A、II−C、II−DおよびII−Eで記載されたようにして製造された部分配向糸を、130℃のゴデット温度でBarmagの延伸巻取機、モデルDW48で延伸した。延伸速度、延伸倍率、およびInstronの引張試験機、モデル1122で測定された得られた延伸糸の物理的性質は以下の表IVに与えられる。実施例II−Dに記載されるようにして製造された部分配向糸は、表IVに報告されるように3種の異なる延伸倍率で延伸された。
この実施例は、本発明により製造される部分配向糸は後の延伸テキスチャリング作業に有用であるということを示した。この実施例はさらに、仮撚りテキスチャリング処理を用いて部分配向ポリ(トリメチレンテレフタラート)糸のテキスチャリングを成功させるのに必要な延伸テキスチャリングの処理条件を示した。図5に例示されるような装置を用いて、実施例II−AからII−Eで調製された部分配向糸の本発明によるフリクション仮撚りテキスチャリングをおこなった。糸を、ヒータを通過するときには約180℃の温度に加熱し、冷却プレートの上を通るときにはポリ(トリメチレンテレフタラート)のガラス転移温度より低い温度に冷却した。
Claims (25)
- 繰返し単位のトリメチレン単位からなるポリ(トリメチレンテレフタラート)を実質的に含むポリマーから製造される部分配向フィード糸の連続延伸テキスチャリング方法であって:
(a)前記部分−配向フィード糸を、
160℃と〜200℃の温度に設定されたヒータを通して供給する工程と;
(b)加熱された糸をフリクション仮撚り入れ装置に供給し、
これによって糸が、フリクション仮撚り入れ装置およびヒータを含むヒータまでの間の領域で46度から52度の撚り角度を有するように撚られる工程と;及び
(c)前記糸を巻取機に巻く工程と、
を含むことを特徴とする方法。 - 請求項1に記載の部分配向フィード糸の連続延伸テキスチャリング方法であって、
前記工程(a)のヒータが、180℃〜225℃の範囲の温度に設定され;
前記工程(a)後に、PPT糸が、PPTのガラス転移温度以下に冷却され;
PPTの延伸比が、約1.46〜1.71の範囲であり;
巻取り速度が400〜600 mpmの範囲であり;及び
ガイド−ディスク(guide−disc )
/ワーキングディスク(working disc)
/イグジットディスク(exit disc)比が1/3/1、1/4/1、1/5/1、及び1/7/1から選択される、ことを特徴とする方法。 - 撚り入れ装置が(ディスクタイプなどの)フリクションスピンドルであることを特徴とする請求項2に記載の方法。
- フリクションスピンドルが少なくとも1個の入口ガイドディスク、3から5個の作業ディスク、および1個の出口ガイドディスクを含むことを特徴とする請求項3に記載の方法。
- フリクションスピンドルが約0.75から1.0mmの間隔をもつ作業ディスクを含むことを特徴とする請求項3または4に記載の方法。
- 撚り入れ装置がクロスベルトであることを特徴とする請求項1に記載の方法または糸。
- 工程(a)の前に、糸を撚り遮断装置に通す工程をさらに含むことを特徴とする請求項1〜6のいずれかの項に記載の方法。
- ポリマーが少なくとも0.70dl/gの固有粘度を有し、および部分配向糸が少なくとも110%の破断伸びを有することを特徴とする請求項1〜7のいずれかの項に記載の方法。
- 破断伸びが少なくとも120%であることを特徴とする請求項1〜8のいずれかの項に記載の方法。
- 破断伸びが少なくとも130%であることを特徴とする請求項9に記載の方法。
- 破断伸びが180%までであることを特徴とする請求項1〜10のいずれかの項に記載の方法。
- 破断伸びが145%までであることを特徴とする請求項11に記載の方法。
- 固有粘度が少なくとも0.90dl/gであることを特徴とする請求項1〜12のいずれかの項に記載の方法。
- 延伸テキスチャード糸であって、
(a)ポリエステルポリマーから製造される部分配向糸であって:
前記ポリマーが、繰返し単位の少なくとも85モル%がトリメチレン単位からなる少なくとも85モル%のポリ(トリメチレンテレフタラート)を含み;
前記ポリマーが少なくとも0.70dl/gの固有粘度を有し;及び
前記部分配向糸が、少なくとも110〜180%の破断伸びを有することを特徴とする部分配向糸を、約160℃および200℃の間の温度にセットされたヒータを通して供給する工程と、
(b)糸が撚り入れ装置およびヒータを含むヒータまでの間の領域で約46度から約52度の撚り角度を有して撚られるように、糸を撚り入れ装置に供給する工程と、
(c)糸を巻取機に巻く工程と、をもつ部分配向糸の連続延伸テキスチャリングによって製造されることを特徴とする糸。 - 撚り入れ装置が(ディスクタイプなどの)フリクションスピンドルであることを特徴とする請求項14に記載の糸。
- フリクションスピンドルが少なくとも1個の入口ガイドディスク、3から5個の作業ディスク、および1個の出口ガイドディスクを含むことを特徴とする請求項15に記載の糸。
- フリクションスピンドルが約0.75から1.0mmの間隔をもつ作業ディスクを含むことを特徴とする請求項14に記載の糸。
- 撚り入れ装置がクロスベルトであることを特徴とする請求項14に記載の糸。
- 工程(a)の前に、糸を撚り遮断装置に通す工程をさらに含むことを特徴とする請求項14〜18のいずれかの項に記載の糸。
- ポリマーが少なくとも0.70dl/gの固有粘度を有し、および部分配向糸が少なくとも110%の破断伸びを有することを特徴とする請求項14〜19のいずれかの項に記載の糸。
- 破断伸びが少なくとも120%であることを特徴とする請求項14〜20のいずれかの項に記載の糸。
- 破断伸びが少なくとも130%であることを特徴とする請求項21に記載の糸。
- 破断伸びが180%までであることを特徴とする請求項14〜22のいずれかの項に記載の糸。
- 破断伸びが145%までであることを特徴とする請求項23に記載の糸。
- 固有粘度が少なくとも0.90dl/gであることを特徴とする請求項14〜24のいずれかの項に記載の糸。