GB2006242B - Polyester of 6 - hydroxy - 2 - naphthoic acid and para-hydroxy benzoic acid capable of readily undergoing melt processing - Google Patents

Polyester of 6 - hydroxy - 2 - naphthoic acid and para-hydroxy benzoic acid capable of readily undergoing melt processing

Info

Publication number
GB2006242B
GB2006242B GB7841144A GB7841144A GB2006242B GB 2006242 B GB2006242 B GB 2006242B GB 7841144 A GB7841144 A GB 7841144A GB 7841144 A GB7841144 A GB 7841144A GB 2006242 B GB2006242 B GB 2006242B
Authority
GB
United Kingdom
Prior art keywords
hydroxy
para
polyester
melt processing
benzoic acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB7841144A
Other languages
English (en)
Other versions
GB2006242A (en
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Celanese Corp
Original Assignee
Celanese Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Celanese Corp filed Critical Celanese Corp
Publication of GB2006242A publication Critical patent/GB2006242A/en
Application granted granted Critical
Publication of GB2006242B publication Critical patent/GB2006242B/en
Expired legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G63/00—Macromolecular compounds obtained by reactions forming a carboxylic ester link in the main chain of the macromolecule
    • C08G63/68—Polyesters containing atoms other than carbon, hydrogen and oxygen
    • C08G63/682—Polyesters containing atoms other than carbon, hydrogen and oxygen containing halogens
    • C08G63/6822—Polyesters containing atoms other than carbon, hydrogen and oxygen containing halogens derived from hydroxy carboxylic acids
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G63/00—Macromolecular compounds obtained by reactions forming a carboxylic ester link in the main chain of the macromolecule
    • C08G63/02—Polyesters derived from hydroxycarboxylic acids or from polycarboxylic acids and polyhydroxy compounds
    • C08G63/06—Polyesters derived from hydroxycarboxylic acids or from polycarboxylic acids and polyhydroxy compounds derived from hydroxycarboxylic acids
    • C08G63/065—Polyesters derived from hydroxycarboxylic acids or from polycarboxylic acids and polyhydroxy compounds derived from hydroxycarboxylic acids the hydroxy and carboxylic ester groups being bound to aromatic rings

Landscapes

  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Polyesters Or Polycarbonates (AREA)
  • Artificial Filaments (AREA)
  • Manufacture Of Macromolecular Shaped Articles (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
GB7841144A 1977-10-20 1978-10-19 Polyester of 6 - hydroxy - 2 - naphthoic acid and para-hydroxy benzoic acid capable of readily undergoing melt processing Expired GB2006242B (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US05/843,993 US4161470A (en) 1977-10-20 1977-10-20 Polyester of 6-hydroxy-2-naphthoic acid and para-hydroxy benzoic acid capable of readily undergoing melt processing

Publications (2)

Publication Number Publication Date
GB2006242A GB2006242A (en) 1979-05-02
GB2006242B true GB2006242B (en) 1982-04-28

Family

ID=25291500

Family Applications (1)

Application Number Title Priority Date Filing Date
GB7841144A Expired GB2006242B (en) 1977-10-20 1978-10-19 Polyester of 6 - hydroxy - 2 - naphthoic acid and para-hydroxy benzoic acid capable of readily undergoing melt processing

Country Status (12)

Country Link
US (1) US4161470A (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
JP (4) JPS5477691A (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
BE (1) BE871382A (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
BR (1) BR7806934A (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
CA (1) CA1120642A (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
DE (1) DE2844817A1 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
DK (1) DK466078A (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
FR (1) FR2406648A1 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
GB (1) GB2006242B (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
NL (1) NL184112C (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
NO (1) NO783543L (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
SE (1) SE7810921L (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)

Families Citing this family (314)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2960830D1 (en) * 1978-07-31 1981-12-03 Ici Plc Aromatic copolyesters capable of forming an anisotropic melt and shaped articles made thereof
US4224433A (en) * 1979-03-16 1980-09-23 Celanese Corporation Thermotropic polyesters of 2,6-dihydroxyanthraquinone
US4219461A (en) * 1979-04-23 1980-08-26 Celanese Corporation Polyester of 6-hydroxy-2-naphthoic acid, para-hydroxy benzoic acid, aromatic diol, and aromatic diacid capable of readily undergoing melt processing
US4256624A (en) * 1979-07-02 1981-03-17 Celanese Corporation Polyester of 6-hydroxy-2-naphthoic acid, aromatic diol, and aromatic diacid capable of undergoing melt processing
US4232144A (en) * 1979-09-17 1980-11-04 E. I. Du Pont De Nemours And Company Polyester which exhibits anisotropy in the melt containing p-oxybenzoyl units and 4-oxy-3'-carbonylbenzophenone units or methyl and chloro derivatives of said units
EP0030417B2 (en) * 1979-11-30 1994-03-30 Imperial Chemical Industries Plc Compositions of melt-processable polymers having improved processibility, and method of processing
US4299756A (en) * 1980-03-10 1981-11-10 Celanese Corporation Polyester of phenyl-4-hydroxybenzoic acid, aromatic diol, and aromatic diacid capable of forming an anisotropic melt
US4279803A (en) * 1980-03-10 1981-07-21 Celanese Corporation Polyester of phenyl-4-hydroxybenzoic acid and 4-hydroxybenzoic acid and/or 6-hydroxy-2-naphthoic acid capable of forming an anisotropic melt
EP0041327B1 (en) * 1980-05-30 1983-09-07 Imperial Chemical Industries Plc Improved melt spinning process
US4489190A (en) * 1980-06-11 1984-12-18 Celanese Corporation Blend of polyalkylene terephthalate and wholly aromatic polyester
US4267289A (en) * 1980-07-03 1981-05-12 Celanese Corporation Blend of wholly aromatic polyesters
US4337190A (en) * 1980-07-15 1982-06-29 Celanese Corporation Polyester of 6-hydroxy-2-naphthoic acid and meta-hydroxy benzoic acid capable of readily undergoing melt processing
DE3176201D1 (en) * 1980-07-16 1987-06-25 Ici Plc Shaped articles formed from polymers capable of exhibiting anisotropic melts
US4318842A (en) * 1980-10-06 1982-03-09 Celanese Corporation Polyester of 6-hydroxy-2-naphthoic acid, aromatic diol, and 1,4-cyclohexanedicarboxylic acid capable of undergoing melt processing
US4318841A (en) * 1980-10-06 1982-03-09 Celanese Corporation Polyester of 6-hydroxy-2-naphthoic acid, para-hydroxy benzoic acid, terephthalic acid, and resorcinol capable of readily undergoing melt processing to form shaped articles having increased impact strength
US4346209A (en) * 1980-11-19 1982-08-24 Celanese Corporation Solvent resistant halogenated aromatic polyester fibers and process therefor
US4335232A (en) * 1981-07-07 1982-06-15 E. I. Du Pont De Nemours And Company Optically anisotropic melt forming polyesters
US4429060A (en) 1981-07-13 1984-01-31 Celanese Corporation Lightweight high performance foams of thermotropic liquid crystal polymers comprising recurring 6-oxy-2-naphthoyl moieties
CA1194649A (en) * 1981-07-13 1985-10-01 Celanese Corporation High performance foams of thermotropic liquid crystal polymers
US4429061A (en) 1981-07-13 1984-01-31 Celanese Corporation Heat treated high performance foams of thermotropic liquid crystal polymers
US4355133A (en) * 1981-07-27 1982-10-19 Celanese Corporation Polyester of 6-hydroxy-2-naphthoic acid, 4-hydroxy benzoic acid, 1,4-cyclohexanedicarboxylic acid, and aromatic diol capable of readily undergoing melt processing to form articles possessing high impact properties
US4374228A (en) * 1981-08-03 1983-02-15 Fiber Industries, Inc. Wholly aromatic polyester capable of forming an anisotropic melt phase consisting essentially of para-oxybenzoyl moiety, bromo-substituted-para-oxybenzoyl moiety, and meta-oxybenzoyl moiety
US4384016A (en) * 1981-08-06 1983-05-17 Celanese Corporation Mutiaxially oriented high performance laminates comprised of uniaxially oriented sheets of thermotropic liquid crystal polymers
US4394498A (en) * 1981-08-24 1983-07-19 Celanese Corporation Method for providing particulates of liquid crystal polymers and particulates produced therefrom
US4370466A (en) * 1981-09-28 1983-01-25 E. I. Du Pont De Nemours And Company Optically anisotropic melt forming polyesters
JPS5853418A (ja) * 1981-09-28 1983-03-30 Teijin Ltd ポリエステルフイルムの製造方法
US4410683A (en) * 1981-12-09 1983-10-18 E. I. Du Pont De Nemours And Company Aromatic, melt-processible (co)polyesters
US4451611A (en) * 1981-12-15 1984-05-29 Celanese Corporation Process for forming blend of polyalkylene terephthalate and wholly aromatic polyester which exhibits an anisotropic melt phase
US4408022A (en) * 1981-12-15 1983-10-04 Celanese Corporation Blend of polyalkylene terephthalate and wholly aromatic polyester and process for producing the same
US4383105A (en) * 1981-12-28 1983-05-10 E. I. Du Pont De Nemours And Company Polyimide-esters and filaments
US4393191A (en) * 1982-03-08 1983-07-12 Celanese Corporation Preparation of aromatic polyesters by direct self-condensation of aromatic hydroxy acids
US4910057A (en) * 1982-04-02 1990-03-20 Hoechst Celanese Corporation Melt extruded elongated member suitable for improved service as a stiffening support in an optical fiber cable
US4395513A (en) * 1982-04-08 1983-07-26 Celanese Corporation High performance thermally stable poly(6-oxy-2-naphthoate)
EP0095865A3 (en) * 1982-06-01 1984-02-08 Celanese Corporation Thermoformed shaped articles of thermotropic liquid crystal polymers and methods of production thereof
CA1228957A (en) * 1982-06-21 1987-11-10 Norman S. Anderson Yarn which exhibits high tenacity comprised of thermotropic liquid crystalline polymer fibers, a reinforcing cord comprised thereof and a process of production thereof
US4457962A (en) * 1982-09-01 1984-07-03 Celanese Corporation Molded article comprised of a thermotropic liquid crystal line polymer with an inherently weak weld line incorporated therein
JPS5943021A (ja) * 1982-09-02 1984-03-09 Ueno Seiyaku Oyo Kenkyusho:Kk 芳香族（コ）ポリエステルの製法
JPS59120626A (ja) * 1982-12-27 1984-07-12 Sumitomo Chem Co Ltd 芳香族ポリエステルの製造方法
US4429105A (en) 1983-02-22 1984-01-31 Celanese Corporation Process for preparing a polyester of hydroxy naphthoic acid and hydroxy benzoic acid
JPS59213721A (ja) * 1983-05-19 1984-12-03 Mitsui Petrochem Ind Ltd 芳香族ポリエステル
EP0129372A3 (en) * 1983-06-20 1987-04-15 Imperial Chemical Industries Plc Improved optical fibre cable
JPS6040163A (ja) * 1983-07-27 1985-03-02 ヘキスト・セラニーズ・コーポレーション 電子部品の改良封入成形法
US4574066A (en) * 1984-02-27 1986-03-04 Celanese Corporation Process for the expeditious formation of a high strength shaped article of poly(6-oxy-2-naphthoate-4-oxybenzoate)
DE3407100A1 (de) * 1984-02-28 1985-08-29 Hoechst Ag, 6230 Frankfurt Verfahren zur herstellung von 6-acetoxy-2-naphthoesaeure
US6045906A (en) 1984-03-15 2000-04-04 Cytec Technology Corp. Continuous, linearly intermixed fiber tows and composite molded article thereform
JP2664406B2 (ja) * 1988-04-13 1997-10-15 ポリプラスチックス 株式会社 溶融時に光学的異方性を示すポリエステル樹脂及び樹脂組成物
US4567247A (en) * 1984-05-17 1986-01-28 Celanese Corporation Process for forming thermally stable thermotropic liquid crystalline polyesters of predetermined chain length utilizing aromatic hydroxyl monomer and/or aromatic amine monomer
US4612154A (en) * 1984-06-15 1986-09-16 E. I. Du Pont De Nemours And Company Spinning of certain high molecular weight anisotropic melt forming polyesters
US5143985A (en) * 1984-06-29 1992-09-01 Amoco Corporation Blends of a poly(aryl ether ketone) and a polyarylate
US4624872A (en) * 1984-08-13 1986-11-25 Celanese Corporation Liquid crystalline polymer substrates with orthogonal molecular orientation
US4581443A (en) * 1984-10-09 1986-04-08 Celanese Corporation Production of improved pellets from melt-processable polymer which is capable of forming and anisotropic melt
US4611025A (en) * 1985-04-04 1986-09-09 Akkapeddi Murali K Process for the production of thermoplastic compositions containing thermotropic oligomers and compositions produced by such process
EP0207644A1 (en) * 1985-06-06 1987-01-07 Celanese Corporation Fluid contactor elements of thermotropic liquid crystalline polymers
JP2505411B2 (ja) * 1986-03-24 1996-06-12 ポリプラスチックス 株式会社 溶融時に異方性を示す樹脂組成物
US4767183A (en) * 1986-05-12 1988-08-30 Westinghouse Electric Corp. High strength, heavy walled cable construction
JP2505429B2 (ja) * 1986-10-17 1996-06-12 ポリプラスチックス 株式会社 射出成型用組成物
US4871817A (en) * 1986-12-31 1989-10-03 General Electric Company Polyetherimide-liquid crystal polymer blends
EP0285554A1 (en) * 1987-03-19 1988-10-05 Maged A. Dr. Osman Linear rodlike polyesters
JPS63273636A (ja) * 1987-05-06 1988-11-10 Agency Of Ind Science & Technol 含フッ素共重合ポリエステル
US4835047A (en) * 1987-05-14 1989-05-30 Avraam Isayev Wholly aromatic polyester fiber-reinforced polyetherimide composite and process for preparing same
DE3884546T3 (de) * 1987-10-02 2000-03-23 Polyplastics Co. Ltd., Osaka Verfahren zur Oberflächenbehandlung von Gegenständen aus flüssigkristallinem Polyesterharz.
JPH01250410A (ja) * 1987-12-08 1989-10-05 Kuraray Co Ltd 高弾性率繊維の製造方法
US4942087A (en) * 1987-12-28 1990-07-17 Mitsui Petrochemical Industries, Ltd. Films of wholly aromatic polyester and processes for preparation thereof
JP2674062B2 (ja) * 1988-02-15 1997-11-05 東レ株式会社 高強度液晶ポリアリレート樹脂成形物の製法
JP2664400B2 (ja) * 1988-03-24 1997-10-15 ポリプラスチックス 株式会社 溶融時に異方性を示すポリエステル樹脂及び樹脂組成物
JPH07103232B2 (ja) * 1988-04-11 1995-11-08 工業技術院長 高弾性率ポリエステル成形品
JP2664404B2 (ja) * 1988-04-13 1997-10-15 ポリプラスチックス 株式会社 溶融時に光学的異方性を示すポリエステル樹脂及び樹脂組成物
JP2664405B2 (ja) * 1988-04-13 1997-10-15 ポリプラスチックス 株式会社 溶融時に光学的異方性を示すポリエステル樹脂及び樹脂組成物
US5003030A (en) * 1988-05-17 1991-03-26 Idemitsu Petrochemical Co., Ltd. Thermoplastic wholly aromatic copolyimide ester and process for producing the same
JPH0639533B2 (ja) * 1988-06-17 1994-05-25 株式会社クラレ 全芳香族ポリエステルフイルム及びその製造方法
FR2634215A1 (fr) * 1988-07-13 1990-01-19 Rhone Poulenc Chimie Compositions de moulage a base de polymeres thermotropes renforces par des charges minerales
JPH0791524B2 (ja) * 1988-07-20 1995-10-04 ポリプラスチックス株式会社 接着物
JP2590545B2 (ja) * 1988-09-17 1997-03-12 東レ株式会社 スクリーン紗及びその製法
JP2823873B2 (ja) * 1988-12-27 1998-11-11 ポリプラスチックス株式会社 流動性改良液晶性ポリエステル樹脂組成物
JPH02196819A (ja) * 1989-01-25 1990-08-03 Nippon Oil Co Ltd 全芳香族ポリエステル
US5409979A (en) * 1989-02-08 1995-04-25 Polyplastics Co., Ltd. Liquid-crystal polyester resin composition containing specified mold release agents
JPH02208317A (ja) * 1989-02-08 1990-08-17 Mitsubishi Gas Chem Co Inc 共重合ポリエステル
EP0417322B1 (en) * 1989-03-31 1996-01-17 Nippon Petrochemicals Company, Limited Molding method of magnetic disc substrate
USH1187H (en) 1989-08-28 1993-05-04 Shell Oil Company Polymer blends
FR2653436A1 (fr) * 1989-10-24 1991-04-26 Atochem Copolyesters aromatiques thermotropes et leur procede de preparation.
JP3086231B2 (ja) * 1989-11-01 2000-09-11 ポリプラスチックス株式会社 溶融時に異方性を示すポリエステル樹脂及び樹脂組成物
US5393848A (en) * 1990-01-16 1995-02-28 Hoechst Celanese Corp. Process for forming improved liquid crystalline polymer blends
DE4013574A1 (de) * 1990-04-27 1991-10-31 Hoechst Ag Flaechenhafter formkoerper und verfahren zu seiner herstellung
US5225457A (en) * 1990-06-05 1993-07-06 The Goodyear Tire & Rubber Company Reinforced polymer matrix and product containing micro and macro reinforcement
KR930005104B1 (ko) * 1990-08-30 1993-06-15 한국과학기술연구원 액정 폴리에스테르 펄프상 단섬유
US5135990A (en) * 1990-10-05 1992-08-04 General Electric Company Polyetherimide-liquid crystalline polymer blends
US5364905A (en) * 1991-04-26 1994-11-15 The Goodyear Tire & Rubber Company Process for the in-situ formation of reinforcing members in an elastomer and elastomer made thereby
US5563216A (en) * 1991-06-19 1996-10-08 Sumitomo Chemical Company, Limited Thermoplastic resin composition and preparation thereof
US5262473A (en) * 1991-11-29 1993-11-16 Enichem America Inc. Polymer molding compositions containing polycarbonates and polyesters and liquid crystalline polymers
US5366663A (en) * 1991-11-30 1994-11-22 Hoechst Ag Mixtures of liquid crystalline copolymers, polyether imides and compatibilizers and use thereof
JPH05230356A (ja) * 1991-11-30 1993-09-07 Hoechst Ag 液晶コポリマーおよびフッ素熱可塑性樹脂の混合物、ならびにその使用方法
US5227456A (en) * 1992-03-20 1993-07-13 Hoechst Celanese Corp. Wholly aromatic liquid crystalline polymers containing sulfonated ionic monomer units and laminates thereof
US5981007A (en) * 1992-03-31 1999-11-09 Foster-Miller, Inc. Extruded thermoplastic, liquid crystalline polymers and blends thereof having a planar morphology
JPH05339475A (ja) * 1992-04-08 1993-12-21 Toray Ind Inc 液晶性樹脂組成物
HK1007177A1 (en) * 1992-10-13 1999-04-01 Alliedsignal Inc. Entangled high strength yarn and fabric
US5851668A (en) * 1992-11-24 1998-12-22 Hoechst Celanese Corp Cut-resistant fiber containing a hard filler
US6162538A (en) * 1992-11-24 2000-12-19 Clemson University Research Foundation Filled cut-resistant fibers
JP3563752B2 (ja) * 1992-11-24 2004-09-08 エイチエヌエイ・ホールディングス・インコーポレーテッド 充填剤入り繊維
US5654045A (en) * 1992-12-21 1997-08-05 Hoechst Celanese Corp. Multiaxially reinforced LCP sheet
US5443783A (en) * 1993-03-23 1995-08-22 Hoechst Celanese Corp. Process for blow molding articles from liquid crystal polymers
ES2133554T3 (es) * 1993-05-07 1999-09-16 Sinco Ricerche Spa Composiciones de poliesteres adecuados para la fabricacion de fibras y peliculas con modulos de elasticidad elevados.
US5397502A (en) * 1993-06-10 1995-03-14 E. I. Du Pont De Nemours And Company Heat resistant liquid crsytalline polymers
US5472658A (en) * 1993-12-22 1995-12-05 Holechst Celanese Corporation Pre-stressing of heat treated liquid crystalline polymer fiber to improve modulus
TW340130B (en) * 1993-12-28 1998-09-11 Toray Industries Shaped article of liquid crystalline resin
US5830940A (en) * 1993-12-28 1998-11-03 Toray Industries, Inc. Shaped article of liquid crystalline polymer
DK63894A (da) * 1994-06-06 1996-01-08 Meadox Medicals Inc Kateter med stent samt fremgangsmåde til fremstilling af et sådant kateter med stent
EP0688812A1 (en) 1994-06-20 1995-12-27 Hoechst Celanese Corporation High barrier transparent films
JP2939477B2 (ja) 1994-08-16 1999-08-25 エイチエヌエイ・ホールディングス・インコーポレーテッド 液晶重合体−金属積層品および該積層品の製造法
US5705279A (en) * 1995-01-25 1998-01-06 Polyplastics Co. Ltd. Fibrillar copolyester having a large aspect ratio, production method for the same, and a resinous composite material containing the same as reinforcement
US5576358A (en) * 1995-02-03 1996-11-19 Alliedsignal Inc. Composition for use in friction materials and articles formed therefrom
JP2579742B2 (ja) * 1995-02-20 1997-02-12 ポリプラスチックス株式会社 射出成型用組成物
US5789042A (en) * 1995-03-28 1998-08-04 Hoechst Celanese Corporation Thin LCP film process
US7214847B1 (en) 1997-09-22 2007-05-08 Argentum Medical, L.L.C. Multilayer conductive appliance having wound healing and analgesic properties
US8801681B2 (en) 1995-09-05 2014-08-12 Argentum Medical, Llc Medical device
US8455710B2 (en) 1997-09-22 2013-06-04 Argentum Medical, Llc Conductive wound dressings and methods of use
US6087549A (en) * 1997-09-22 2000-07-11 Argentum International Multilayer laminate wound dressing
US5814094A (en) 1996-03-28 1998-09-29 Becker; Robert O. Iontopheretic system for stimulation of tissue healing and regeneration
US6861570B1 (en) * 1997-09-22 2005-03-01 A. Bart Flick Multilayer conductive appliance having wound healing and analgesic properties
TW413697B (en) 1995-12-15 2000-12-01 Toray Industries Liquid crystalline resin composition
US5633319A (en) 1996-01-16 1997-05-27 General Electric Company Compatibilized blends of polyetherimides and liquid crystalline polyesters
WO1998010926A1 (en) 1996-09-11 1998-03-19 Dupont Canada Inc. Heat exchangers containing liquid crystalline polymer layers
WO1998010927A1 (en) 1996-09-11 1998-03-19 Dupont Canada Inc. Polymeric multilayer heat exchangers containing a barrier layer
US6391754B1 (en) 1996-09-27 2002-05-21 Texas Instruments Incorporated Method of making an integrated circuit interconnect
IT1291674B1 (it) * 1997-04-28 1999-01-19 Sinco Eng Spa Resine poliestere aventi migliorate proprieta'
TR199902977T2 (xx) * 1997-06-06 2000-10-23 Michelin Recherche Et Technique S.A. Termotropik aromatik poliester (Amid) monofilaman
US5998804A (en) * 1997-07-03 1999-12-07 Hna Holdings, Inc. Transistors incorporating substrates comprising liquid crystal polymers
US6048922A (en) * 1997-08-20 2000-04-11 Eastman Chemical Company Process for preparing high strength fiber reinforced composites
US7101597B2 (en) 1997-09-10 2006-09-05 Boston Scientific Scimed, Inc. Medical devices made from polymer blends containing low melting temperature liquid crystal polymers
US6242063B1 (en) 1997-09-10 2001-06-05 Scimed Life Systems, Inc. Balloons made from liquid crystal polymer blends
US6284333B1 (en) 1997-09-10 2001-09-04 Scimed Life Systems, Inc. Medical devices made from polymer blends containing low melting temperature liquid crystal polymers
WO1999036606A1 (en) 1998-01-20 1999-07-22 Hna Holdings, Inc. Ballistic-resistant textile articles made from cut-resistant fibers
US6036711A (en) * 1998-02-18 2000-03-14 United States Surgical Corporation Reusable cannula
US6187437B1 (en) * 1998-09-10 2001-02-13 Celanese Acetate Llc Process for making high denier multilobal filaments of thermotropic liquid crystalline polymers and compositions thereof
US6204386B1 (en) 1998-11-05 2001-03-20 Arteva North America S.A.R.L. Method for esterification of carboxylic or polycarboxylic acid in the presence of supercritical fluids and catalysts therefor
US6379795B1 (en) 1999-01-19 2002-04-30 E. I. Du Pont De Nemours And Company Injection moldable conductive aromatic thermoplastic liquid crystalline polymeric compositions
US6364008B1 (en) 1999-01-22 2002-04-02 E. I. Du Pont De Nemours And Company Heat exchanger with tube plates
TWI230178B (en) 1999-05-13 2005-04-01 Sumitomo Chemical Co Liquid crystal polyester resin composition and molded article thereof
TW491879B (en) 1999-05-13 2002-06-21 Sumitomo Chemical Co Liquid crystal polyester resin composition and molded article
WO2000079206A1 (en) 1999-06-22 2000-12-28 Dupont Canada Inc. Heat exchanger formed from tubes joined by simultaneous extrusion thermal bonding
US6528164B1 (en) 1999-09-03 2003-03-04 Sumitomo Chemical Company, Limited Process for producing aromatic liquid crystalline polyester and film thereof
US6977103B2 (en) * 1999-10-25 2005-12-20 Boston Scientific Scimed, Inc. Dimensionally stable balloons
DE19961040A1 (de) * 1999-12-16 2001-06-21 Basf Ag Thermoplastische Formmassen mit verbessertem Verarbeitungsverhalten auf Basis von Polyarylenethersulfonen und Polyamiden
US6939940B2 (en) 2000-09-13 2005-09-06 The United States Of America As Represented By The Administrator Of The National Aeronautics And Space Administration Liquid crystalline thermosets from ester, ester-imide, and ester-amide oligomers
WO2002029347A2 (en) 2000-10-06 2002-04-11 E.I. Du Pont De Nemours And Company Heat exchanger made from bendable plastic tubing
JP3913527B2 (ja) * 2001-10-30 2007-05-09 ポリプラスチックス株式会社 全芳香族ポリエステルアミド及びポリエステルアミド樹脂組成物
JP3969171B2 (ja) 2001-11-12 2007-09-05 住友化学株式会社 液晶性ポリエステルおよびその製造方法
US6730377B2 (en) 2002-01-23 2004-05-04 Scimed Life Systems, Inc. Balloons made from liquid crystal polymer blends
US20050042496A1 (en) * 2002-02-13 2005-02-24 Bisara Mukesh K Method for manufacturing fuel cell separator plates under low shear strain
AU2003219894A1 (en) * 2002-02-26 2003-09-09 Uni-Pixel Displays, Inc. Enhancements to optical flat panel displays
JP2004013054A (ja) 2002-06-11 2004-01-15 Sumitomo Chem Co Ltd 高耐熱ラベル
US20040113129A1 (en) * 2002-07-25 2004-06-17 Waggoner Marion G. Static dissipative thermoplastic polymer composition
US20050082720A1 (en) * 2003-01-23 2005-04-21 Bloom Joy S. Moldings of liquid crystalline polymer powders
US20070225479A1 (en) * 2003-08-26 2007-09-27 General Electric Company Method of separating a polymer from a solvent
US6924350B2 (en) * 2003-08-26 2005-08-02 General Electric Company Method of separating a polymer from a solvent
US6949622B2 (en) * 2003-08-26 2005-09-27 General Electric Company Method of separating a polymer from a solvent
US20060089487A1 (en) * 2003-08-26 2006-04-27 Norberto Silvi Method of separating a polymer from a solvent
JP2005232210A (ja) * 2004-02-17 2005-09-02 Sumitomo Chemical Co Ltd 液晶ポリエステル樹脂組成物
JP2005272776A (ja) * 2004-03-26 2005-10-06 Polyplastics Co サーモトロピック液晶性ポリマーの製造方法
JP2006104305A (ja) * 2004-10-04 2006-04-20 Nippon Petrochemicals Co Ltd 固相重縮合方法、固相重縮合物および固相重縮合装置
US7288493B2 (en) * 2005-01-18 2007-10-30 Honeywell International Inc. Body armor with improved knife-stab resistance formed from flexible composites
US7379642B2 (en) 2005-01-18 2008-05-27 Adc Telecommunications, Inc. Low shrink telecommunications cable and methods for manufacturing the same
CA2538761A1 (en) * 2005-03-08 2006-09-08 Anthony Joseph Cesaroni Method for sealing heat exchanger tubes
US7547849B2 (en) 2005-06-15 2009-06-16 E.I. Du Pont De Nemours And Company Compositions useful in electronic circuitry type applications, patternable using amplified light, and methods and compositions relating thereto
US20070293109A1 (en) * 2005-06-16 2007-12-20 Ashok Bhatnagar Composite material for stab, ice pick and armor applications
CN101287581B (zh) 2005-10-12 2013-02-06 关西管道株式会社 封闭式管件的头部形成方法、封闭式管状容器及制造方法
US7601416B2 (en) * 2005-12-06 2009-10-13 Honeywell International Inc. Fragment and stab resistant flexible material with reduced trauma effect
JP5271479B2 (ja) * 2005-12-14 2013-08-21 上野製薬株式会社 液晶ポリエステル樹脂組成物
US20070202331A1 (en) * 2006-02-24 2007-08-30 Davis Gregory A Ropes having improved cyclic bend over sheave performance
US7642206B1 (en) 2006-03-24 2010-01-05 Honeywell International Inc. Ceramic faced ballistic panel construction
JP5132899B2 (ja) * 2006-06-26 2013-01-30 ポリプラスチックス株式会社 液晶性樹脂組成物
US8007202B2 (en) 2006-08-02 2011-08-30 Honeywell International, Inc. Protective marine barrier system
US7622405B1 (en) 2006-09-26 2009-11-24 Honeywell International Inc. High performance same fiber composite hybrids by varying resin content only
US8519053B2 (en) * 2006-10-02 2013-08-27 Armstrong World Industries, Inc. PVC/polyester binder for flooring
US20080081882A1 (en) * 2006-10-02 2008-04-03 Dong Tian Polyester binder for flooring products
US8652570B2 (en) * 2006-11-16 2014-02-18 Honeywell International Inc. Process for forming unidirectionally oriented fiber structures
US7762175B1 (en) 2006-11-30 2010-07-27 Honeywell International Inc. Spaced lightweight composite armor
US7794813B2 (en) * 2006-12-13 2010-09-14 Honeywell International Inc. Tubular composite structures
US20100203273A1 (en) * 2006-12-13 2010-08-12 Jhrg, Llc Anti-chafe cable cover
US8017529B1 (en) 2007-03-21 2011-09-13 Honeywell International Inc. Cross-plied composite ballistic articles
US7994074B1 (en) 2007-03-21 2011-08-09 Honeywell International, Inc. Composite ballistic fabric structures
US7993478B2 (en) 2007-03-28 2011-08-09 Honeywell International, Inc. Method to apply multiple coatings to a fiber web
KR101449981B1 (ko) 2007-06-03 2014-10-14 이머리스 피그먼츠 아이엔시 코팅된 칼슘 카보네이트를 포함하는 스펀레이드 섬유, 및 이를 제조하는 방법, 및 부직포 제품
US8475924B2 (en) * 2007-07-09 2013-07-02 E.I. Du Pont De Nemours And Company Compositions and methods for creating electronic circuitry
US20090017309A1 (en) * 2007-07-09 2009-01-15 E. I. Du Pont De Nemours And Company Compositions and methods for creating electronic circuitry
US8256019B2 (en) 2007-08-01 2012-09-04 Honeywell International Inc. Composite ballistic fabric structures for hard armor applications
US8258209B2 (en) * 2007-09-12 2012-09-04 Sumitomo Chemical Company, Limited Insulating resin composition and application thereof
JP5225653B2 (ja) * 2007-10-30 2013-07-03 上野製薬株式会社 液晶ポリエステルブレンド
US20110052913A1 (en) * 2008-01-21 2011-03-03 Mcamish Larry Monofilament fibers comprising at least one filler, and processes for their production
US20100035045A1 (en) 2008-01-21 2010-02-11 Imerys Pigments, Inc. Fibers comprising at least one filler and processes for their production
US20110059287A1 (en) * 2008-01-21 2011-03-10 Imerys Pigments, Inc. Fibers comprising at least one filler, processes for their production, and uses thereof
US7994075B1 (en) 2008-02-26 2011-08-09 Honeywell International, Inc. Low weight and high durability soft body armor composite using topical wax coatings
US8391658B2 (en) 2008-05-28 2013-03-05 Adc Telecommunications, Inc. Fiber optic cable with jacket embedded with reinforcing members
US8422843B2 (en) * 2008-03-28 2013-04-16 Adc Telecommunications, Inc. Multi-fiber fiber optic cable
WO2009136904A2 (en) 2008-03-31 2009-11-12 Sabic Innovative Plastics Ip B.V. Apparatus and method of separating a polymer from a solvent
US8275225B2 (en) * 2008-05-27 2012-09-25 Adc Telecommunications, Inc. Multi-jacketed fiber optic cable
WO2009154990A2 (en) * 2008-05-27 2009-12-23 Adc Telecommunications, Inc. Foamed fiber optic cable
AU2009260538B2 (en) 2008-05-28 2015-01-15 Adc Telecommunications, Inc. Fiber optic cable
JP5520468B2 (ja) * 2008-10-16 2014-06-11 古河電気工業株式会社 多層絶縁電線及びそれを用いた変圧器
JP5520493B2 (ja) 2008-10-20 2014-06-11 古河電気工業株式会社 多層絶縁電線及びそれを用いた変圧器
WO2010062646A1 (en) * 2008-10-28 2010-06-03 Adc Telecommunications, Inc. Flat drop cable
US20100193950A1 (en) * 2009-01-30 2010-08-05 E.I.Du Pont De Nemours And Company Wafer level, chip scale semiconductor device packaging compositions, and methods relating thereto
US9562744B2 (en) 2009-06-13 2017-02-07 Honeywell International Inc. Soft body armor having enhanced abrasion resistance
EP2474984A4 (en) 2009-09-02 2013-07-03 Furukawa Electric Co Ltd MULTILAYER INSULATED WIRE AND TRANSFORMER USING THE SAME
US8184935B2 (en) 2009-10-21 2012-05-22 Adc Telecommunications, Inc. Flat drop cable with center strength member
AU2010321868B2 (en) 2009-11-20 2014-12-11 Adc Telecommunications, Inc. Fiber optic cable assembly
AU2010321863B2 (en) 2009-11-20 2014-09-25 Adc Telecommunications, Inc. Fiber optic cable
WO2011097299A2 (en) * 2010-02-02 2011-08-11 Adc Telecommunications, Inc. Fiber optic cable bundle with staggered connectors
WO2011109498A2 (en) 2010-03-02 2011-09-09 Adc Telecommunications, Inc. Fiber optic cable assembly
US8915659B2 (en) 2010-05-14 2014-12-23 Adc Telecommunications, Inc. Splice enclosure arrangement for fiber optic cables
WO2011146720A2 (en) 2010-05-19 2011-11-24 Adc Telecommunications, Inc. Flat drop cable with medial bump
WO2011146717A2 (en) 2010-05-19 2011-11-24 Adc Telecommunications, Inc. Lashing together multiple fiber optic telecommunications cables
US9056950B2 (en) 2010-07-23 2015-06-16 Ticona Gmbh Composite polymeric articles formed from extruded sheets containing a liquid crystal polymer
JP2013533387A (ja) * 2010-07-23 2013-08-22 シスコム アドバンスド マテリアルズ 導電性金属でコーティングされた繊維、その調製のための連続的方法、およびその使用法
US8885998B2 (en) 2010-12-09 2014-11-11 Adc Telecommunications, Inc. Splice enclosure arrangement for fiber optic cables
EP2655846A1 (en) 2010-12-22 2013-10-30 Ticona LLC High temperature conduit having a complex, three-dimensional configuration
KR101305878B1 (ko) 2010-12-28 2013-09-09 도레이 카부시키가이샤 액정성 폴리에스테르 수지 조성물 및 그 제조 방법과 그로부터 이루어진 성형품
US8784683B2 (en) 2010-12-28 2014-07-22 Toray Industries, Inc. Liquid crystalline polyester composition, method of producing the same and molded product manufactured from the same
WO2012092505A1 (en) 2010-12-29 2012-07-05 Syscom Advanced Materials Metal and metallized fiber hybrid wire
KR101770826B1 (ko) * 2011-01-05 2017-08-23 심천 워트 어드밴스드 머티리얼즈 주식회사 섬유웹, 이의 제조방법 및 이를 구비하는 필터
FI20115099L (fi) * 2011-01-31 2012-08-01 Metso Fabrics Oy Kenkäpuristinhihna, menetelmä sen valmistamiseksi ja käyttö kenkäpuristimessa
US9739966B2 (en) 2011-02-14 2017-08-22 Commscope Technologies Llc Fiber optic cable with electrical conductors
EP2540778B1 (en) 2011-02-28 2020-01-22 Toray Industries, Inc. Liquid crystal polyester resin composition and metal composite molded article using same
EP2690140B1 (en) 2011-03-25 2016-11-16 Toray Industries, Inc. Thermoplastic resin composition and molded article using same
US9085672B2 (en) 2011-04-06 2015-07-21 Toray Industries, Inc. Liquid crystalline polyester composition and metal composite molded product using the same
US8781281B2 (en) 2011-07-21 2014-07-15 Adc Telecommunications, Inc. Drop cable with angled reinforcing member configurations
MX2014000631A (es) 2011-07-21 2014-04-30 Adc Telecommunications Inc Metodo para extruir un cable de bajada.
JP2014525498A (ja) 2011-08-29 2014-09-29 ティコナ・エルエルシー 高流動性液晶ポリマー組成物
US8778221B2 (en) 2011-08-29 2014-07-15 Ticona Llc Aromatic amide compound
WO2013032975A1 (en) 2011-08-29 2013-03-07 Ticona Llc Thermotropic liquid crystalline polymer with improved low shear viscosity
WO2013032977A1 (en) 2011-08-29 2013-03-07 Ticona Llc Heat-resistant liquid crystalline polymer composition having a low melting temperature
TW201313884A (zh) 2011-08-29 2013-04-01 Ticona Llc 液晶聚合物之固態聚合
US9045685B2 (en) 2011-08-29 2015-06-02 Ticona Llc Cast molded parts formed from a liquid crystalline polymer
TW201319118A (zh) 2011-08-29 2013-05-16 Ticona Llc 低熔融黏度液晶聚合物之熔融聚合
WO2013032978A1 (en) 2011-08-29 2013-03-07 Ticona Llc Method for minimizing process disruptions during formation of a liquid crystalline polymer
JP2014525501A (ja) 2011-08-29 2014-09-29 ティコナ・エルエルシー 高流動性液晶ポリマー組成物
US8852730B2 (en) 2011-08-29 2014-10-07 Ticona Llc Melt-extruded substrate for use in thermoformed articles
US20130052447A1 (en) 2011-08-29 2013-02-28 Ticona Llc Liquid Crystalline Polymer Composition Containing a Fibrous Filler
US9023452B2 (en) 2011-09-06 2015-05-05 Honeywell International Inc. Rigid structural and low back face signature ballistic UD/articles and method of making
US20130059496A1 (en) 2011-09-06 2013-03-07 Honeywell International Inc. Low bfs composite and process of making the same
US9023450B2 (en) 2011-09-06 2015-05-05 Honeywell International Inc. High lap shear strength, low back face signature UD composite and the process of making
US9567463B2 (en) 2011-09-30 2017-02-14 Basf Se High-strength blends based on polyarylene ethers
EP2574637A1 (de) 2011-09-30 2013-04-03 Basf Se Hochfeste Blends auf Basis von Polyarylenethern
KR102087451B1 (ko) 2011-09-30 2020-03-10 티코나 엘엘씨 액정 중합체를 위한 고상 중합 시스템
CN103906803B (zh) 2011-10-31 2016-05-25 提克纳有限责任公司 用于形成激光直接构建基材的热塑性组合物
TWI534253B (zh) 2011-11-15 2016-05-21 堤康那責任有限公司 具有改良可燃性效能之富含環烷之液晶聚合物組合物
WO2013074472A1 (en) 2011-11-15 2013-05-23 Ticona Llc Method of forming a liquid crystalline thermoplastic composition
KR101947215B1 (ko) 2011-11-15 2019-02-12 티코나 엘엘씨 미세 피치 전기 커넥터 및 그에 사용하기 위한 열가소성 조성물
TWI464244B (zh) 2011-11-15 2014-12-11 Ticona Llc 用於高壓電子組件之液晶聚合物組合物
TWI498351B (zh) 2011-11-15 2015-09-01 Ticona Llc 低環烷之液晶聚合物組合物
JP6294230B2 (ja) 2011-11-15 2018-03-14 ティコナ・エルエルシー コンパクトカメラモジュール
WO2013074467A1 (en) 2011-11-15 2013-05-23 Ticona Llc Low naphthenic liquid crystalline polymer composition for use in molded parts of a small dimensional tolerance
US9291433B2 (en) 2012-02-22 2016-03-22 Cryovac, Inc. Ballistic-resistant composite assembly
JP2013194225A (ja) * 2012-03-22 2013-09-30 Sumitomo Chemical Co Ltd 液晶ポリエステルフィルムの製造方法及び液晶ポリエステルフィルム
US9273418B2 (en) 2012-05-17 2016-03-01 Honeywell International Inc. Hybrid fiber unidirectional tape and composite laminates
CN104540923A (zh) 2012-06-27 2015-04-22 提克纳有限责任公司 超低粘度的液晶聚合物组合物
US10132010B2 (en) 2012-07-27 2018-11-20 Honeywell International Inc. UHMW PE fiber and method to produce
US9316802B2 (en) 2012-08-24 2016-04-19 Commscope Technologies Llc Optical fiber cable having reinforcing layer of tape heat-bonded to jacket
US8853342B2 (en) 2012-09-24 2014-10-07 Ticona Llc Crosslinkable liquid crystalline polymer
US8822628B2 (en) 2012-09-24 2014-09-02 Ticona Llc Crosslinkable liquid crystalline polymer
US9145519B2 (en) 2012-09-24 2015-09-29 Ticona Llc Crosslinkable aromatic polyester
WO2014052052A1 (en) 2012-09-27 2014-04-03 Ticona Llc Thermotropic liquid crystalline powder
WO2014052050A2 (en) 2012-09-27 2014-04-03 Ticona Llc Soluble aromatic polymer
US9145469B2 (en) 2012-09-27 2015-09-29 Ticona Llc Aromatic polyester containing a biphenyl chain disruptor
US20140099458A1 (en) 2012-10-05 2014-04-10 Ticona Llc Liquid Crystalline Composition with a Metallic Appearance
JP6462576B2 (ja) 2012-10-16 2019-01-30 ティコナ・エルエルシー 静電気防止液晶ポリマー組成物
US20140120282A1 (en) 2012-11-01 2014-05-01 Ticona Llc Multi-Layered Co-Injection Molded Article
WO2014074228A1 (en) 2012-11-09 2014-05-15 Ticona Llc Liquid crystalline polymer composition for melt-extruded sheets
WO2014074227A1 (en) 2012-11-09 2014-05-15 Ticona Llc Liquid crystalline polymer composition for films
WO2014081650A1 (en) 2012-11-21 2014-05-30 Ticona Llc Liquid crystalline polymer composition for melt-extruded substrates
US9355753B2 (en) 2012-12-05 2016-05-31 Ticona Llc Conductive liquid crystalline polymer composition
EP2935515B1 (en) 2012-12-19 2020-04-15 Ticona LLC Liquid crystalline composition having a dark black color
US20140178705A1 (en) 2012-12-20 2014-06-26 Ticona Llc Aromatic Polyester Coatings and Laminates
US11136445B2 (en) 2013-03-13 2021-10-05 Ticona Llc Liquid crystalline polymer composition
CN113912988A (zh) 2013-06-07 2022-01-11 提克纳有限责任公司 高强度热致液晶聚合物
US20150104165A1 (en) 2013-10-16 2015-04-16 Ticona Llc Polymer Composition for Use in a Compact Camera Module
WO2015059599A1 (en) 2013-10-21 2015-04-30 Ticona Gmbh Two component polyoxymethylene based systems
WO2015094486A1 (en) 2013-12-19 2015-06-25 Ticona Llc Liquid crystalline composition having a pearly luster
WO2015094805A1 (en) 2013-12-19 2015-06-25 Ticona Llc Polyarylene sulfide composition for use in forming a laser direct structured substrate
WO2015095035A1 (en) 2013-12-20 2015-06-25 Ticona Llc Metal detectable liquid crystalline polymer composition
JP2017513977A (ja) 2014-04-09 2017-06-01 ティコナ・エルエルシー 静電防止ポリマー組成物
KR102366736B1 (ko) 2014-04-09 2022-02-23 티코나 엘엘씨 카메라 모듈
WO2016003588A1 (en) 2014-07-01 2016-01-07 Ticona Llc Laser activatable polymer composition
WO2016028613A1 (en) 2014-08-21 2016-02-25 Ticona Llc Polyaryletherketone composition
CN106574184A (zh) 2014-08-21 2017-04-19 提克纳有限责任公司 包含聚芳基醚酮和低环烷液晶聚合物的组合物
US9909240B2 (en) 2014-11-04 2018-03-06 Honeywell International Inc. UHMWPE fiber and method to produce
CN107250209B (zh) 2015-02-26 2020-06-26 沙特基础工业全球技术公司 聚碳酸酯和液晶聚合物共混物
US10612189B2 (en) 2015-04-24 2020-04-07 Honeywell International Inc. Composite fabrics combining high and low strength materials
JP6905515B2 (ja) 2015-09-30 2021-07-21 セラニーズ・セールス・ジャーマニー・ゲーエムベーハー 低摩擦できしり音のないアセンブリ
JP6617626B2 (ja) * 2016-03-18 2019-12-11 東レ株式会社 液晶ポリエステルマルチフィラメントおよびその製造方法
US11352480B2 (en) 2016-03-18 2022-06-07 Ticona Llc Polyaryletherketone composition
US20170297295A1 (en) 2016-04-15 2017-10-19 Honeywell International Inc. Blister free composite materials molding
US10633535B2 (en) 2017-02-06 2020-04-28 Ticona Llc Polyester polymer compositions
CN111417681B (zh) 2017-12-05 2023-08-22 提克纳有限责任公司 用于摄像模组的芳族聚合物组合物
WO2019155419A1 (en) 2018-02-08 2019-08-15 Celanese Sales Germany Gmbh Polymer composite containing recycled carbon fibers
EP3773771B1 (en) 2018-03-29 2025-08-06 Atex Technologies, Inc. Small diameter, high strength, low elongation, creep resistant, abrasion resistant braided structure
JP7111502B2 (ja) * 2018-04-24 2022-08-02 上野製薬株式会社 機械強度および誘電特性に優れた液晶ポリエステル樹脂
JP7136636B2 (ja) * 2018-09-06 2022-09-13 ポリプラスチックス株式会社 全芳香族ポリエステル
JP2020083967A (ja) * 2018-11-20 2020-06-04 住友化学株式会社 芳香族ポリエステル及びその製造方法並びに組成物
JP6850320B2 (ja) * 2019-06-27 2021-03-31 デンカ株式会社 Ｌｃｐｔダイ押出未延伸フィルム、並びにこれを用いたフレキシブル積層体及びその製造方法
KR20220038094A (ko) 2019-07-17 2022-03-25 티코나 엘엘씨 초음파 프로브
WO2021025056A1 (ja) * 2019-08-06 2021-02-11 株式会社村田製作所 樹脂シート及び樹脂多層基板
US12209164B2 (en) 2019-09-10 2025-01-28 Ticona Llc Polymer composition and film for use in 5G applications
US12142820B2 (en) 2019-09-10 2024-11-12 Ticona Llc 5G system containing a polymer composition
US11917753B2 (en) 2019-09-23 2024-02-27 Ticona Llc Circuit board for use at 5G frequencies
US11646760B2 (en) 2019-09-23 2023-05-09 Ticona Llc RF filter for use at 5G frequencies
JP7339843B2 (ja) * 2019-10-21 2023-09-06 上野製薬株式会社 液晶ポリエステル樹脂
WO2021126743A1 (en) 2019-12-17 2021-06-24 Ticona Llc Three-dimensional printing system employing a thermotropic liquid crystalline polymer
CN115734798A (zh) 2020-04-28 2023-03-03 提克纳有限责任公司 微针组件
CN112812282A (zh) * 2020-12-28 2021-05-18 金发科技股份有限公司 一种液晶聚酯及其制备方法和应用
JP2024525233A (ja) 2021-07-16 2024-07-10 ビーエーエスエフ ソシエタス・ヨーロピア ポリフェニレンスルフィドを含む耐高温性を有する熱可塑性成形組成物
JP2024525803A (ja) 2021-07-16 2024-07-12 ビーエーエスエフ ソシエタス・ヨーロピア サーモトロピックなポリマーを含む耐高温性を有する熱可塑性成形組成物
KR20240120728A (ko) 2021-12-01 2024-08-07 티코나 엘엘씨 안테나 모듈
CN114853992B (zh) * 2022-04-26 2024-04-26 四川大学 可溶低介电常数低介电损耗阻燃全芳共聚酯及其制备方法和应用
DE202023106038U1 (de) 2023-10-18 2025-02-10 Lena Schindler Garn und textiles Flächengebilde für die Herstellung von Hitzeschutzbekleidung und Gießereibekleidung

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE344034C (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html) *
PH15509A (en) * 1974-05-10 1983-02-03 Du Pont Improvements in an relating to synthetic polyesters
US4083829A (en) * 1976-05-13 1978-04-11 Celanese Corporation Melt processable thermotropic wholly aromatic polyester
US4067852A (en) * 1976-05-13 1978-01-10 Celanese Corporation Melt processable thermotropic wholly aromatic polyester containing polybenzoyl units
US4184996A (en) * 1977-09-12 1980-01-22 Celanese Corporation Melt processable thermotropic wholly aromatic polyester

Also Published As

Publication number Publication date
BR7806934A (pt) 1979-07-03
GB2006242A (en) 1979-05-02
CA1120642A (en) 1982-03-23
JPH01306615A (ja) 1989-12-11
JPH01294767A (ja) 1989-11-28
NL184112B (nl) 1988-11-16
JPH0327643B2 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html) 1991-04-16
DE2844817C2 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html) 1989-04-27
FR2406648B1 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html) 1984-09-07
NO783543L (no) 1979-04-23
US4161470A (en) 1979-07-17
JPH0327585B2 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html) 1991-04-16
NL184112C (nl) 1989-04-17
DK466078A (da) 1979-04-21
NL7810508A (nl) 1979-04-24
DE2844817A1 (de) 1979-04-26
JPH0320337A (ja) 1991-01-29
FR2406648A1 (fr) 1979-05-18
JPS5477691A (en) 1979-06-21
JPS633888B2 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html) 1988-01-26
BE871382A (fr) 1979-04-19
JPH0329245B2 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html) 1991-04-23
SE7810921L (sv) 1979-04-21

Similar Documents

Publication Publication Date Title
GB2006242B (en) Polyester of 6 - hydroxy - 2 - naphthoic acid and para-hydroxy benzoic acid capable of readily undergoing melt processing
DE3169813D1 (en) Polyester of 6-hydroxy-2-naphthoic acid and metahydroxy benzoic acid capable of readily undergoing melt processing
DE3169703D1 (en) Polyester of 6-hydroxy-2-naphthoic acid, para-hydroxy benzoic acid, terephthalic acid and resorcinol capable of readily undergoing melt processing to form shaped articles having increased impact strength
DE3071547D1 (en) Polyester amides and adhesives therefrom
GB2042533B (en) Cyclohexylpyrimidines useful in liquid crystalline mixtures and display devices
JPS55110225A (en) Electrophoresis display unit and production thereof
IL53314A0 (en) Heat treated superalloy single crystal article and proces
GB2002504B (en) Process and apparatus or the continuous drying and/or granulating of loose material
JPS5517190A (en) Liquid crystal display and monitoring same
PH14312A (en) Benzeydryl-imidazole carboxylic acid derivatives and their use thereof
JPS55106221A (en) Pphydroxybenzoic acid* 1* 22bis*ppcarboxyphenoxy* ethane* polyester of terephthalic acid and hydroquinone which are able to form melttworkable anisotropic melt
EP0129395A3 (en) Anisotropic melt polyesters of 6-hydroxy-2-naphthoic acid
NO166336C (no) Krusende polyesterfilamenter og fremgangsmaate ved fremstilling derav
GB2077279B (en) High-solids polyesters process for their preparation and use thereof
JPS53124369A (en) Method of defrosting cooling element in showcase and apparatus therefor
DE3060934D1 (en) Polyester amides and their use as melt adhesives
JPS5483023A (en) Heat treatment of particulate material
JPS5670766A (en) Sweating promoting panel and its use
IL54629A0 (en) Heat treated superalloy single crystal article and proces
JPS53141252A (en) Benzoic acid derivative process for preparing same and medicine containing same
JPS5417998A (en) Polyester and its improvement
JPS544990A (en) Preparation of carbonic acid bissdiphenol ester of polyester diols* and its use for preparation of high segment polyester*polycarbonates
JPS5692918A (en) Rapidly crystallizable polyester composition and its manufacture
SG64685G (en) Substituted fluorophenols and their use in the preparation of liquid crystal esters
GB2063592B (en) Magnetic stirrer and drive circuit

Legal Events

Date Code Title Description
PE20 Patent expired after termination of 20 years

Effective date: 19981018