WO2013066629A1 - Methylene beta-ketoester monomers, methods for making methylene beta-ketoester monomers, polymerizable compositions and products formed therefrom - Google Patents

Methylene beta-ketoester monomers, methods for making methylene beta-ketoester monomers, polymerizable compositions and products formed therefrom Download PDF

Info

Publication number
WO2013066629A1
WO2013066629A1 PCT/US2012/060837 US2012060837W WO2013066629A1 WO 2013066629 A1 WO2013066629 A1 WO 2013066629A1 US 2012060837 W US2012060837 W US 2012060837W WO 2013066629 A1 WO2013066629 A1 WO 2013066629A1
Authority
WO
WIPO (PCT)
Prior art keywords
alkyl
heterocyclyl
halo
aryl
cycloalkyl
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2012/060837
Other languages
English (en)
French (fr)
Inventor
Bernard Miles Malofsky
Adam Gregg Malofsky
Tanmoy Dey
Jeffrey M. Sullivan
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sirrus Inc
Original Assignee
Bioformix LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bioformix LLC filed Critical Bioformix LLC
Priority to US14/352,406 priority Critical patent/US9527795B2/en
Priority to EP12846728.9A priority patent/EP2768872B1/en
Priority to MX2014004781A priority patent/MX360463B/es
Priority to CA2853079A priority patent/CA2853079A1/en
Priority to JP2014537249A priority patent/JP2014534969A/ja
Publication of WO2013066629A1 publication Critical patent/WO2013066629A1/en
Anticipated expiration legal-status Critical
Priority to US15/363,169 priority patent/US20170073438A1/en
Priority to US15/661,893 priority patent/US10414839B2/en
Ceased legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
    • C08F222/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a carboxyl radical and containing at least one other carboxyl radical in the molecule; Salts, anhydrides, esters, amides, imides, or nitriles thereof
    • C08F222/10—Esters
    • C08F222/12—Esters of phenols or saturated alcohols
    • C08F222/14—Esters having no free carboxylic acid groups, e.g. dialkyl maleates or fumarates
    • C—CHEMISTRY; METALLURGY
    • C07—ORGANIC CHEMISTRY
    • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
    • C07C45/00—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds
    • C07C45/61—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds by reactions not involving the formation of >C = O groups
    • C07C45/67—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds by reactions not involving the formation of >C = O groups by isomerisation; by change of size of the carbon skeleton
    • C07C45/68—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds by reactions not involving the formation of >C = O groups by isomerisation; by change of size of the carbon skeleton by increase in the number of carbon atoms
    • C07C45/72—Preparation of compounds having >C = O groups bound only to carbon or hydrogen atoms; Preparation of chelates of such compounds by reactions not involving the formation of >C = O groups by isomerisation; by change of size of the carbon skeleton by increase in the number of carbon atoms by reaction of compounds containing >C = O groups with the same or other compounds containing >C = O groups
    • C07C45/75—Reactions with formaldehyde
    • C—CHEMISTRY; METALLURGY
    • C07—ORGANIC CHEMISTRY
    • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
    • C07C49/00—Ketones; Ketenes; Dimeric ketenes; Ketonic chelates
    • C07C49/76—Ketones containing a keto group bound to a six-membered aromatic ring
    • C07C49/794—Ketones containing a keto group bound to a six-membered aromatic ring having unsaturation outside an aromatic ring
    • C—CHEMISTRY; METALLURGY
    • C07—ORGANIC CHEMISTRY
    • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
    • C07C49/00—Ketones; Ketenes; Dimeric ketenes; Ketonic chelates
    • C07C49/76—Ketones containing a keto group bound to a six-membered aromatic ring
    • C07C49/794—Ketones containing a keto group bound to a six-membered aromatic ring having unsaturation outside an aromatic ring
    • C07C49/796—Ketones containing a keto group bound to a six-membered aromatic ring having unsaturation outside an aromatic ring polycyclic
    • C—CHEMISTRY; METALLURGY
    • C07—ORGANIC CHEMISTRY
    • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
    • C07C49/00—Ketones; Ketenes; Dimeric ketenes; Ketonic chelates
    • C07C49/76—Ketones containing a keto group bound to a six-membered aromatic ring
    • C07C49/794—Ketones containing a keto group bound to a six-membered aromatic ring having unsaturation outside an aromatic ring
    • C07C49/798—Ketones containing a keto group bound to a six-membered aromatic ring having unsaturation outside an aromatic ring containing rings other than six-membered aromatic rings
    • C—CHEMISTRY; METALLURGY
    • C07—ORGANIC CHEMISTRY
    • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
    • C07C49/00—Ketones; Ketenes; Dimeric ketenes; Ketonic chelates
    • C07C49/76—Ketones containing a keto group bound to a six-membered aromatic ring
    • C07C49/80—Ketones containing a keto group bound to a six-membered aromatic ring containing halogen
    • C—CHEMISTRY; METALLURGY
    • C07—ORGANIC CHEMISTRY
    • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
    • C07C67/00—Preparation of carboxylic acid esters
    • C07C67/03—Preparation of carboxylic acid esters by reacting an ester group with a hydroxy group
    • C—CHEMISTRY; METALLURGY
    • C07—ORGANIC CHEMISTRY
    • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
    • C07C67/00—Preparation of carboxylic acid esters
    • C07C67/30—Preparation of carboxylic acid esters by modifying the acid moiety of the ester, such modification not being an introduction of an ester group
    • C—CHEMISTRY; METALLURGY
    • C07—ORGANIC CHEMISTRY
    • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
    • C07C69/00—Esters of carboxylic acids; Esters of carbonic or haloformic acids
    • C07C69/52—Esters of acyclic unsaturated carboxylic acids having the esterified carboxyl group bound to an acyclic carbon atom
    • C07C69/604—Polycarboxylic acid esters, the acid moiety containing more than two carboxyl groups
    • C—CHEMISTRY; METALLURGY
    • C07—ORGANIC CHEMISTRY
    • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
    • C07C69/00—Esters of carboxylic acids; Esters of carbonic or haloformic acids
    • C07C69/66—Esters of carboxylic acids having esterified carboxylic groups bound to acyclic carbon atoms and having any of the groups OH, O—metal, —CHO, keto, ether, acyloxy, groups, groups, or in the acid moiety
    • C07C69/73—Esters of carboxylic acids having esterified carboxylic groups bound to acyclic carbon atoms and having any of the groups OH, O—metal, —CHO, keto, ether, acyloxy, groups, groups, or in the acid moiety of unsaturated acids
    • C07C69/738—Esters of keto-carboxylic acids or aldehydo-carboxylic acids
    • C—CHEMISTRY; METALLURGY
    • C07—ORGANIC CHEMISTRY
    • C07D—HETEROCYCLIC COMPOUNDS
    • C07D307/00—Heterocyclic compounds containing five-membered rings having one oxygen atom as the only ring hetero atom
    • C07D307/02—Heterocyclic compounds containing five-membered rings having one oxygen atom as the only ring hetero atom not condensed with other rings
    • C07D307/34—Heterocyclic compounds containing five-membered rings having one oxygen atom as the only ring hetero atom not condensed with other rings having two or three double bonds between ring members or between ring members and non-ring members
    • C07D307/38—Heterocyclic compounds containing five-membered rings having one oxygen atom as the only ring hetero atom not condensed with other rings having two or three double bonds between ring members or between ring members and non-ring members with substituted hydrocarbon radicals attached to ring carbon atoms
    • C07D307/40—Radicals substituted by oxygen atoms
    • C07D307/46—Doubly bound oxygen atoms, or two oxygen atoms singly bound to the same carbon atom
    • C—CHEMISTRY; METALLURGY
    • C07—ORGANIC CHEMISTRY
    • C07D—HETEROCYCLIC COMPOUNDS
    • C07D307/00—Heterocyclic compounds containing five-membered rings having one oxygen atom as the only ring hetero atom
    • C07D307/02—Heterocyclic compounds containing five-membered rings having one oxygen atom as the only ring hetero atom not condensed with other rings
    • C07D307/34—Heterocyclic compounds containing five-membered rings having one oxygen atom as the only ring hetero atom not condensed with other rings having two or three double bonds between ring members or between ring members and non-ring members
    • C07D307/38—Heterocyclic compounds containing five-membered rings having one oxygen atom as the only ring hetero atom not condensed with other rings having two or three double bonds between ring members or between ring members and non-ring members with substituted hydrocarbon radicals attached to ring carbon atoms
    • C07D307/54—Radicals substituted by carbon atoms having three bonds to hetero atoms with at the most one bond to halogen, e.g. ester or nitrile radicals
    • C—CHEMISTRY; METALLURGY
    • C07—ORGANIC CHEMISTRY
    • C07D—HETEROCYCLIC COMPOUNDS
    • C07D333/00—Heterocyclic compounds containing five-membered rings having one sulfur atom as the only ring hetero atom
    • C07D333/02—Heterocyclic compounds containing five-membered rings having one sulfur atom as the only ring hetero atom not condensed with other rings
    • C07D333/04—Heterocyclic compounds containing five-membered rings having one sulfur atom as the only ring hetero atom not condensed with other rings not substituted on the ring sulphur atom
    • C07D333/06—Heterocyclic compounds containing five-membered rings having one sulfur atom as the only ring hetero atom not condensed with other rings not substituted on the ring sulphur atom with only hydrogen atoms, hydrocarbon or substituted hydrocarbon radicals, directly attached to the ring carbon atoms
    • C07D333/22—Radicals substituted by doubly bound hetero atoms, or by two hetero atoms other than halogen singly bound to the same carbon atom
    • C—CHEMISTRY; METALLURGY
    • C07—ORGANIC CHEMISTRY
    • C07D—HETEROCYCLIC COMPOUNDS
    • C07D333/00—Heterocyclic compounds containing five-membered rings having one sulfur atom as the only ring hetero atom
    • C07D333/02—Heterocyclic compounds containing five-membered rings having one sulfur atom as the only ring hetero atom not condensed with other rings
    • C07D333/04—Heterocyclic compounds containing five-membered rings having one sulfur atom as the only ring hetero atom not condensed with other rings not substituted on the ring sulphur atom
    • C07D333/06—Heterocyclic compounds containing five-membered rings having one sulfur atom as the only ring hetero atom not condensed with other rings not substituted on the ring sulphur atom with only hydrogen atoms, hydrocarbon or substituted hydrocarbon radicals, directly attached to the ring carbon atoms
    • C07D333/24—Radicals substituted by carbon atoms having three bonds to hetero atoms with at the most one bond to halogen, e.g. ester or nitrile radicals
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
    • C08F116/00—Homopolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an alcohol, ether, aldehydo, ketonic, acetal or ketal radical
    • C08F116/36—Homopolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an alcohol, ether, aldehydo, ketonic, acetal or ketal radical by a ketonic radical
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
    • C08F128/00—Homopolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a bond to sulfur or by a heterocyclic ring containing sulfur
    • C08F128/06—Homopolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a bond to sulfur or by a heterocyclic ring containing sulfur by a heterocyclic ring containing sulfur
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
    • C08F20/00—Homopolymers and copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride, ester, amide, imide or nitrile thereof
    • C08F20/02—Monocarboxylic acids having less than ten carbon atoms, Derivatives thereof
    • C08F20/10—Esters
    • C08F20/12—Esters of monohydric alcohols or phenols
    • C08F20/14—Methyl esters, e.g. methyl (meth)acrylate
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
    • C08F20/00—Homopolymers and copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride, ester, amide, imide or nitrile thereof
    • C08F20/02—Monocarboxylic acids having less than ten carbon atoms, Derivatives thereof
    • C08F20/10—Esters
    • C08F20/26—Esters containing oxygen in addition to the carboxy oxygen
    • C08F20/28—Esters containing oxygen in addition to the carboxy oxygen containing no aromatic rings in the alcohol moiety
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
    • C08F20/00—Homopolymers and copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride, ester, amide, imide or nitrile thereof
    • C08F20/02—Monocarboxylic acids having less than ten carbon atoms, Derivatives thereof
    • C08F20/10—Esters
    • C08F20/26—Esters containing oxygen in addition to the carboxy oxygen
    • C08F20/30—Esters containing oxygen in addition to the carboxy oxygen containing aromatic rings in the alcohol moiety
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
    • C08F20/00—Homopolymers and copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride, ester, amide, imide or nitrile thereof
    • C08F20/02—Monocarboxylic acids having less than ten carbon atoms, Derivatives thereof
    • C08F20/10—Esters
    • C08F20/38—Esters containing sulfur
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
    • C08F20/00—Homopolymers and copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride, ester, amide, imide or nitrile thereof
    • C08F20/62—Monocarboxylic acids having ten or more carbon atoms; Derivatives thereof
    • C08F20/68—Esters
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
    • C08F22/00—Homopolymers and copolymers of compounds having one or more unsaturated aliphatic radicals each having only one carbon-to-carbon double bond, and at least one being terminated by a carboxyl radical and containing at least one other carboxyl radical in the molecule; Salts, anhydrides, esters, amides, imides or nitriles thereof
    • C08F22/10—Esters
    • C08F22/12—Esters of phenols or saturated alcohols
    • C08F22/20—Esters containing oxygen in addition to the carboxy oxygen
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
    • C08F24/00—Homopolymers and copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a heterocyclic ring containing oxygen
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
    • C08F28/00—Homopolymers and copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a bond to sulfur or by a heterocyclic ring containing sulfur
    • C08F28/06—Homopolymers and copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a bond to sulfur or by a heterocyclic ring containing sulfur by a heterocyclic ring containing sulfur
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/01—Use of inorganic substances as compounding ingredients characterized by their specific function
    • C08K3/013—Fillers, pigments or reinforcing additives
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/0008—Organic ingredients according to more than one of the "one dot" groups of C08K5/01 - C08K5/59
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L21/00—Compositions of unspecified rubbers
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L33/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Compositions of derivatives of such polymers
    • C08L33/04—Homopolymers or copolymers of esters
    • C08L33/14—Homopolymers or copolymers of esters of esters containing halogen, nitrogen, sulfur, or oxygen atoms in addition to the carboxy oxygen
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L33/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Compositions of derivatives of such polymers
    • C08L33/04—Homopolymers or copolymers of esters
    • C08L33/14—Homopolymers or copolymers of esters of esters containing halogen, nitrogen, sulfur, or oxygen atoms in addition to the carboxy oxygen
    • C08L33/16—Homopolymers or copolymers of esters containing halogen atoms
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L35/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a carboxyl radical, and containing at least one other carboxyl radical in the molecule, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Compositions of derivatives of such polymers
    • C08L35/02—Homopolymers or copolymers of esters
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D129/00—Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an alcohol, ether, aldehydo, ketonic, acetal, or ketal radical; Coating compositions based on hydrolysed polymers of esters of unsaturated alcohols with saturated carboxylic acids; Coating compositions based on derivatives of such polymers
    • C09D129/12—Homopolymers or copolymers of unsaturated ketones
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D133/00—Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Coating compositions based on derivatives of such polymers
    • C09D133/04—Homopolymers or copolymers of esters
    • C09D133/14—Homopolymers or copolymers of esters of esters containing halogen, nitrogen, sulfur or oxygen atoms in addition to the carboxy oxygen
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D133/00—Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Coating compositions based on derivatives of such polymers
    • C09D133/04—Homopolymers or copolymers of esters
    • C09D133/14—Homopolymers or copolymers of esters of esters containing halogen, nitrogen, sulfur or oxygen atoms in addition to the carboxy oxygen
    • C09D133/16—Homopolymers or copolymers of esters containing halogen atoms
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D135/00—Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a carboxyl radical, and containing at least another carboxyl radical in the molecule, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Coating compositions based on derivatives of such polymers
    • C09D135/02—Homopolymers or copolymers of esters
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D141/00—Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a bond to sulfur or by a heterocyclic ring containing sulfur; Coating compositions based on derivatives of such polymers
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D4/00—Coating compositions, e.g. paints, varnishes or lacquers, based on organic non-macromolecular compounds having at least one polymerisable carbon-to-carbon unsaturated bond ; Coating compositions, based on monomers of macromolecular compounds of groups C09D183/00 - C09D183/16
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J133/00—Adhesives based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Adhesives based on derivatives of such polymers
    • C09J133/04—Homopolymers or copolymers of esters
    • C09J133/06—Homopolymers or copolymers of esters of esters containing only carbon, hydrogen and oxygen, the oxygen atom being present only as part of the carboxyl radical
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J133/00—Adhesives based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Adhesives based on derivatives of such polymers
    • C09J133/04—Homopolymers or copolymers of esters
    • C09J133/14—Homopolymers or copolymers of esters of esters containing halogen, nitrogen, sulfur or oxygen atoms in addition to the carboxy oxygen
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J133/00—Adhesives based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Adhesives based on derivatives of such polymers
    • C09J133/04—Homopolymers or copolymers of esters
    • C09J133/14—Homopolymers or copolymers of esters of esters containing halogen, nitrogen, sulfur or oxygen atoms in addition to the carboxy oxygen
    • C09J133/16—Homopolymers or copolymers of esters containing halogen atoms
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J135/00—Adhesives based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a carboxyl radical, and containing at least another carboxyl radical in the molecule, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Adhesives based on derivatives of such polymers
    • C09J135/02—Homopolymers or copolymers of esters
    • C—CHEMISTRY; METALLURGY
    • C07—ORGANIC CHEMISTRY
    • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
    • C07C2601/00—Systems containing only non-condensed rings
    • C07C2601/12—Systems containing only non-condensed rings with a six-membered ring
    • C07C2601/14—The ring being saturated
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P20/00—Technologies relating to chemical industry
    • Y02P20/10—Process efficiency

Definitions

  • the invention relates to a new class of methylene beta-ketoester monomers, to methods of producing or synthesizing such monomers, and to the use and application of such monomers as commercial products and compositions, including, for example, monomer-based products (e.g., inks, adhesives, coatings, sealants or reactive molding) and polymer-based products (e.g., fibers, films, sheets, medical polymers, composite polymers and surfactants).
  • monomer-based products e.g., inks, adhesives, coatings, sealants or reactive molding
  • polymer-based products e.g., fibers, films, sheets, medical polymers, composite polymers and surfactants.
  • the new monomers relate to a platform of methylene beta-ketoester monomers having the general structural formula:
  • Products produced with such monomers include, for example, polymerizable compositions and polymers formed therefrom, e.g., inks, adhesives, coatings, sealants, reactive moldings, fibers, films, sheets, medical polymers, composite polymers and surfactants.
  • Methylene malonate monomers have been disclosed for example in U.S.
  • Patent Nos. U.S. Patent Nos. 2,313,501 ; 2,330,033; 3,221,745; 3,523,097; 3,557,185; 3,758,550; 3,975,422; 4,049,698; 4,056,543; 4,160,864; 4,931,584; 5,142,098;
  • methylene malonates have the potential to form the basis of a large-scale platform of raw materials useful in a wide variety of chemical products.
  • methylene beta-ketoester monomers and their associated monomeric and polymeric -based products would be useful in industrial, consumer, and medical applications.
  • methylene beta-ketoester monomers would provide a benefit over other monomers in that the incorporation of a ketone group adjacent to the active methylene group reduces the susceptibility of degradation of the monomer upon utilization or further functionalization.
  • methylene beta-ketoester monomers and their products can be produced via sustainable routes as well as be designed to be environmentally benign, biologically benign and as such many of the products can be generally regarded as "green.”
  • the invention provides a methylene beta-ketoester monomer having a structure: wherein Ri and R 2 are independently C 1 -C 15 alkyl, C 2 -Ci 5 alkenyl, halo-(Ci- Ci 5 alkyl), C 3 -C 6 cycloalkyl, halo-(C 3 -C 6 cycloalkyl), heterocyclyl, heterocyclyl-(Ci- Ci 5 alkyl), aryl, aryl-(Cl-C15 alkyl), heteroaryl or heteroaryl-(Ci-Ci 5 alkyl), or alkoxy -(Cl-15 alkyl), each of which may be optionally substituted by C 1 -C 15 alkyl, halo-(Ci- Ci 5 alkyl), C 3 -C 6 cycloalkyl, halo-(C 3 -C 6 cycloalkyl), heterocyclyl, heterocyclyl-(Ci- Ci 5 alkyl)
  • heterocyclyl heterocyclyl, heterocyclyl-(Ci-Ci 5 alkyl), aryl, aryl -(C 1 -C 15 alkyl), heteroaryl, Ci- Ci 5 alkoxy, C 1 -C 15 alkylthio, hydroxyl, nitro, azido, cyano, acyloxy, carboxy, or ester.
  • the invention provides a method of making a methylene beta-ketoester monomer comprising: a) reacting a beta-ketoester reactant having the structural formula:
  • Ri and R 2 are independently Q-Q5 alkyl, C 2 -C 15 alkenyl, halo-(Ci-Ci 5 alkyl), C 3 -C 6 cycloalkyl, halo-(C 3 -C 6 cycloalkyl), heterocyclyl, heterocyclyl-(Ci-Ci 5 alkyl), aryl, aryl-(Cl-C15 alkyl), heteroaryl or heteroaryl-(Cr Ci 5 alkyl), or alkoxy -(Cl-15 alkyl), each of which may be optionally substituted by C 1 -C 15 alkyl, halo-(C Ci 5 alkyl), C 3 -C 6 cycloalkyl, halo-(C 3 -C 6 cycloalkyl), heterocyclyl, heterocyclyl-(Ci-Ci 5 alkyl), aryl, aryl -(Q-Q5 alkyl), heteroaryl, Cp Ci 5 alkyl
  • heterocyclyl heterocyclyl, heterocyclyl-(Ci-Ci 5 alkyl), aryl, aryl -(C 1 -C 15 alkyl), heteroaryl, Ci- Ci 5 alkoxy, C 1 -C 15 alkylthio, hydroxyl, nitro, azido, cyano, acyloxy, carboxy, or ester.
  • the methods of the invention herein include the step of isolating the methylene beta-ketoester by: i. contacting the reaction complex, or a portion thereof, with an energy transfer means to produce a vapor phase including the methylene beta- ketoester monomer; and
  • the methods of the invention herein include isolating the methylene beta-ketoester by: i. heating the reaction complex, or a portion thereof, to a temperature between about 130°C and about 300°C to produce a vapor phase including the methylene beta-ketoester monomer; and ii. collecting the methylene beta-ketoester monomer from the vapor phase.
  • the methods of the invention are performed under reaction conditions of: a) an initiating temperature of between about 60 °C and about 130 °C; b) atmospheric pressure.
  • the invention provides a method of preparing a methylene beta- ketoester monomer comprising: a) reacting a beta-ketoester reactant having the structural formula:
  • reaction complex under suitable reaction conditions for sufficient time with a source of formaldehyde, optionally in the presence of an acidic or basic catalyst, and optionally in the presence of an acidic or non-acidic solvent, to form a reaction complex; b) contacting the reaction complex, or a portion thereof, with an energy transfer means at a temperature between about 150°C and about 300°C to provide the reaction complex, or portion thereof, as a vapor phase; and c) isolating a methylene beta-ketoester monomer from the reaction complex or portion thereof, wherein the methylene beta-ketoester monomer has the structural formula:
  • Ri and R 2 are independently C 1 -C 15 alkyl, C 2 -Ci 5 alkenyl, halo-(Ci-Cis alkyl), C 3 -C 6 cycloalkyl, halo-(C 3 -C 6 cycloalkyl), heterocyclyl, heterocyclyl-(Ci-Ci 5 alkyl), aryl, aryl-(Cl-C15 alkyl), heteroaryl or heteroaryl-(Ci- Ci 5 alkyl), or alkoxy -(Cl-15 alkyl), each of which may be optionally substituted by C1-C15 alkyl, halo-(Ci-Ci 5 alkyl), C 3 -C 6 cycloalkyl, halo-(C 3 -C 6 cycloalkyl), heterocyclyl, heterocyclyl-(Ci-Ci 5 alkyl), aryl, aryl -(C 1 -C 15 alkyl),
  • the invention provides a polymerizable composition comprising a methylene beta-ketoester monomer of the invention.
  • the polymerizable composition is capable of bonding glass to a substrate in a time period of less than about 90 seconds, less than about 60 seconds, less than about 30 seconds, or less than about 15 seconds.
  • the polymerizable composition comprising a methylene beta-ketoester monomer further comprises at least one additive selected from the group consisting of an acidic stabilizer, a free radical stabilizer, a sequestering agent, a cure accelerator, a rheology modifier, a plasticizing agent, a thixo tropic agents, a natural rubber, a synthetic rubbers, a filler agent and a reinforcing agent.
  • at least one additive selected from the group consisting of an acidic stabilizer, a free radical stabilizer, a sequestering agent, a cure accelerator, a rheology modifier, a plasticizing agent, a thixo tropic agents, a natural rubber, a synthetic rubbers, a filler agent and a reinforcing agent.
  • the invention provides an adhesive product comprising a methylene beta-ketoester monomer of the invention.
  • the adhesive products have a shelf life of at least one year.
  • the invention provides a polymer formed by polymerization of one or more methylene beta-ketoester monomers or a polymerizable composition thereof.
  • the polymers of the invention are useful as a sealant, a coating, a textile fiber, a water-treatment polymer, an ink carrier, a paint carrier, a packaging film, a molding, a medical polymer, a polymer film, a polymer fiber, or a polymer sheet.
  • the polymers of the invention have repeat units of the formula:
  • R and R' are independently C 1 -C 15 alkyl, C 2 -C 15 alkenyl, halo-(Ci-Cis alkyl), C 3 -C 6 cycloalkyl, halo-(C 3 -C 6 cycloalkyl), heterocyclyl, heterocyclyl-(Ci-Ci 5 alkyl), aryl, aryl-(Cl-C15 alkyl), heteroaryl or heteroaryl-(Ci-Ci 5 alkyl), or alkoxy -(Cl-15 alkyl), each of which may be optionally substituted by C 1 -C 15 alkyl, halo-(Ci-Cis alkyl), C 3 -C 6 cycloalkyl, halo-(C 3 -C 6 cycloalkyl), heterocyclyl, heterocyclyl-(Ci-Ci 5 alkyl), aryl, aryl -(C 1 -C 15 alkyl), heteroaryl
  • the invention provides an oligomeric complex prepared by reacting a beta-ketoester with a source of formaldehyde; optionally in the presence of heat transfer agent; optionally in the presence of an acidic or basic catalyst; and optionally in the presence of an acidic or non-acidic solvent.
  • the oligomeric complex has between 2 and 12 repeat units having the structural formula:
  • R and R' are independently C 1 -C 15 alkyl, C2-C 15 alkenyl, halo-(Ci-Cis alkyl), C 3 -C 6 cycloalkyl, halo-(C 3 -C 6 cycloalkyl), heterocyclyl, heterocyclyl-(Ci-Ci 5 alkyl), aryl, aryl-(Cl-C15 alkyl), heteroaryl or heteroaryl-(Ci-Ci 5 alkyl), or alkoxy -(Cl-15 alkyl), each of which may be optionally substituted by C 1 -C 15 alkyl, halo-(Ci-Cis alkyl), C3-C6 cycloalkyl, halo-(C3-C6 cycloalkyl), heterocyclyl, heterocyclyl-(Ci-Ci 5 alkyl), aryl, aryl -(C 1 -C 15 alkyl), heteroaryl, C 1 -
  • the invention provides a methylene beta-ketoester monomer prepared according to the methods of the invention.
  • Figures 1 and 2 depict NMR spectra demonstrating evidence of a methylene beta-ketoester reaction product formed by the reaction of ethyl 4,4-dimethyl-3- oxopentanoate and formaldehyde.
  • Figures 3 and 4 depict NMR spectra demonstrating evidence of a methylene beta-ketoester reaction product formed by the reaction of ethyl 3-oxo-3- phenylpropanoate with formaldehyde.
  • Figure 5 depicts an NMR spectrum demonstrating evidence of a methylene beta-ketoester reaction product formed by the reaction of ethyl 3-oxo-hexanoate with formaldehyde.
  • Figure 6 depicts an NMR spectrum demonstrating evidence of a methylene beta-ketoester reaction product formed by the reaction of ethyl 3-oxobutanoate with formaldehyde.
  • Figure 7 depicts an NMR spectrum demonstrating evidence of a methylene beta-ketoester reaction product formed by the reaction of methyl 3-oxobuanoate with formaldehyde.
  • Figure 8 depicts an NMR spectrum demonstrating evidence of a methylene beta-ketoester reaction product formed by the reaction of ethyl 4-methyl-3- oxopentanoate with formaldehyde.
  • Figure 9 depicts an NMR spectrum demonstrating evidence of a methylene beta-ketoester reaction product formed by the reaction of ethyl 3-oxopenanoate with formaldehyde.
  • the present invention provides new and nonobvious improvements and modifications in the use and application of the Knoevenagel reaction in order to produce methylene beta-ketoester monomers:
  • beta-ketoester refers to a compound having the core formula— -C(0)-CH 2 -C(0)0 .
  • the term "monofunctional" refers to a methylene beta- ketoester or a beta-ketoester having only one core formula.
  • difunctional refers to a methylene beta-ketoester or a beta-ketoester having two core formulas.
  • multifunctional refers to a methylene beta-ketoester or a beta-ketoester having two or more core formulas. Thus the term multifunctional encompasses the term difunctional.
  • reaction complex refers to the materials which result after reacting a beta-ketoester starting material with a source of formaldehyde.
  • reaction complexes may comprise, without limitation, methylene beta-ketoester monomers, oligomeric complexes, irreversible complex impurities, starting materials, or latent acid- forming impurities.
  • reaction vessel refers to any container in which the reactants, solvents, catalysts or other materials may be combined for reaction.
  • Such reaction vessels can be made of any material known to one of skill in the art such as metal, ceramic or glass.
  • vapor phase refers to a gaseous phase which may comprise, without limitation, vaporized methylene beta-ketoester monomer, vaporized starting materials; vaporized solvents, or vaporized impurities.
  • the term “recovering” or “obtaining” or “isolating” refers to the removal of the monomer from the reaction mixture, vapor phase, or condensed vapor phase by one of the methods described herein, although the desired product may not be in a purified form.
  • the term “crack” is also used to indicate
  • methylene beta-ketoester monomer may be obtained by "cracking" an oligomeric complex found in the reaction complex.
  • sterically hindered refers to a compound in which the size of groups within the molecule prevents chemical reactions that are observed in related smaller molecules.
  • volatile and “non-volatile” refers to a compound which is capable of evaporating readily at normal temperatures and pressures, in the case of volatile; or which is not capable of evaporating readily at normal temperatures and pressures, in the case of non- volatile.
  • energy transfer means refers to a means which is capable of volatizing a reaction complex, usually by, but not limited to, rapidly heating the reaction complex to temperatures from about 150°C to about 300°C.
  • energy transfer means include, but are not limited to, heat transfer agents, heat transfer surfaces, lasers, and sources of radiation.
  • heat transfer agent refers to a material which is capable of achieving a high temperature and transferring that temperature to a reaction mixture.
  • heat transfer agents are typically able to reach temperatures from about 150°C to about 300°C and include, but are note limited to silica, silicone oil, mineral oil, a petroleum based heat transfer oil or a synthetic chemical based heat transfer oil.
  • the heat transfer agent can be pre-formed reaction complex.
  • pre-formed reaction complex refers to a reaction complex as defined herein which is prepared by reacting step (a) as described herein in advance of the vaporization step (b).
  • Such pre-formed reaction complexes can be formed up to a year, up to six months, up to 3 months, up to 1 month, up to 2 weeks, up to 1 week, up to 3 days, or up to 1 day in advance of the vaporization step (b).
  • the vaporization step (b) is performed on a newly prepared reaction complex.
  • the pre-formed reaction complex can refer to an oligomeric complex as defined herein.
  • substantially absence refers to a reaction mixture comprising less than 1% by weight of the particular component as compared to the total reaction mixture.
  • a "substantial absence” refers to less than 0.7%, less than 0.5%, less than 0.4%m less than 0.3%, less than 0.2% or less than 0.1% by weight of the of the particular component as compared to the total reaction mixture. In certain other embodiments, a "substantial absence” refers to less than 1.0%, less than 0.7%, less than 0.5%, less than 0.4%m less than 0.3%, less than 0.2% or less than 0.1% by volume of the of the particular component as compared to the total reaction mixture.
  • the term "stabilized,” e.g., in the context of “stabilized” molecules of the invention or compositions comprising same, refers to the tendency of the molecules of the invention (or their compositions) to substantially not polymerize with time, to substantially not harden, form a gel, thicken, or otherwise increase in viscosity with time, and/or to substantially show minimal loss in cure speed (i.e., cure speed is maintained) with time.
  • shelf-life e.g., as in the context of the molecules of the invention having an improved “shelf-life,” refers to the molecules of the invention which are stabilized for a given period of time, e.g., 1 month, 6 months, or even 1 year or more.
  • Methylene beta-ketoester monomers in accordance with the present invention may be made by a modified Knoevenagel condensation reaction of a beta-ketoester with formaldehyde under suitable reaction conditions.
  • the general reaction scheme is provided below.
  • the invention provides a methylene beta-ketoester monomer having the structural formula:
  • Ri and R 2 are independently C 1 -C 15 alkyl, C 2 -Ci 5 alkenyl, halo-(Ci-Ci 5 alkyl), C 3 -C 6 cycloalkyl, halo-(C 3 -C 6 cycloalkyl), heterocyclyl, heterocyclyl-(Ci-Ci 5 alkyl), aryl, aryl-(Cl-C15 alkyl), heteroaryl or heteroaryl-(Ci- Ci 5 alkyl), or alkoxy -(Cl-15 alkyl), each of which may be optionally substituted by C1-C15 alkyl, halo-(Ci-Ci 5 alkyl), C 3 -C 6 cycloalkyl, halo-(C 3 -C 6 cycloalkyl), heterocyclyl, heterocyclyl-(Ci-Ci 5 alkyl), aryl, aryl -(C 1 -C 15 alkyl
  • the invention provides a methylene beta-ketoester monomer having the structural formula:
  • Ri and R 2 are independently Ci-C 6 alkyl, halo-(Ci-C 6 alkyl), C 3 -C 6 cycloalkyl, heterocyclyl, heterocyclyl-(Ci-C 6 alkyl), aryl, aryl-(Cl-C6 alkyl), heteroaryl or heteroaryl-(Ci-C 6 alkyl), each of which may be optionally substituted by halo or Ci-C 6 alkoxy.
  • the invention provides a methylene beta-ketoester monomer having the structural formula:
  • Ri and R 2 are independently Ci-C 6 alkyl or aryl.
  • the reaction for making methylene beta-ketoester monomers of the invention includes at least two basic reactants: a beta-ketoester precursor and a source of formaldehyde.
  • Beta-ketoester precursors in accordance with exemplary embodiments disclosed herein include beta-ketoesters able to undergo a condensation reaction at the alpha carbon.
  • Beta-ketoester precursors include, but are not limted to, molecules having the structural formula:
  • Ri and R 2 are independently C 1 -C 15 alkyl, C 2 -Ci 5 alkenyl, halo-(Ci-Cis alkyl), C 3 -C 6 cycloalkyl, halo-(C 3 -C 6 cycloalkyl), heterocyclyl, heterocyclyl-(Ci-Ci 5 alkyl), aryl, aryl-(Cl-C15 alkyl), heteroaryl or heteroaryl-(Ci- Ci 5 alkyl), or alkoxy -(Cl-15 alkyl), each of which may be optionally substituted by C1-C15 alkyl, halo-(Ci-Ci 5 alkyl), C 3 -C 6 cycloalkyl, halo-(C 3 -C 6 cycloalkyl), heterocyclyl, heterocyclyl-(Ci-Ci 5 alkyl), aryl, aryl -(C 1 -C 15 alkyl),
  • heterocyclyl heterocyclyl, heterocyclyl-(Ci-Ci 5 alkyl), aryl, aryl -(C 1 -C 15 alkyl), heteroaryl, Ci- Ci 5 alkoxy, C 1 -C 15 alkylthio, hydroxyl, nitro, azido, cyano, acyloxy, carboxy, or ester.
  • the present invention contemplates the following specifically identified beta-ketoester precursors: ethyl 4,4-dimethyl-3- oxopentanoate, ethyl 3-oxo-3-phenylpropanoate, ethyl 3-oxohexanoate, ethyl 3- oxobutanoate, methyl 3-oxobuanoate, ethyl 4-methyl-3-oxopentanoate, and ethyl 3- oxopenanoate among others.
  • the beta-ketoester precursor may be derived or obtained from any source, including any commercial source, derived from nature, other compounds, synthesized by other processes, etc.
  • the beta-ketoester precursors are obtained from "green" sources.
  • the beta-ketoester precursors can be derived from biological sources, such as via fermentation production systems whereby microorganisms generate the beta-ketoester precursors is direct metabolic by-products of fermentation— or whereby the microorganisms generate metabolic by- products of fermentation that can be then converted inexpensively to the desired beta- ketoester precursors.
  • fermentation production systems are well-known in the art and may utilize either— or both— microorganisms derived from nature or engineered microorganisms that are specifically designed to produce the desired beta- ketoester precursors products, e.g., recombinant or engineered Escherichia coli.
  • the beta-ketoester precursor is reacted with a source of formaldehyde.
  • a source of formaldehyde may be synthesized, derived from another chemical species (e.g., paraformaldehyde), or obtained from nature or from some other suitable source.
  • the formaldehyde is introduced in the form of a gas.
  • formaldehyde and paraformaldehyde are readily available, which may include, for example, trioxane and formalin (e.g., aqueous formaldehyde).
  • the source of formaldehyde may be paraformaldehyde, formalin or gaseous formaldehyde.
  • the formaldehyde is obtained from paraformaldehyde.
  • the source of formaldehyde is paraformaldehyde that is thermally degraded to formaldehyde in the reaction vessel. It is envisioned that other means of providing formaldehyde to the reaction vessel may be utilized, for example, a stream of gaseous formaldehyde.
  • the methods of preparing the methylene beta- ketoester takes place in the presence of a suitable catalyst.
  • a suitable catalyst it is envisioned that certain reactions may not required the presence of a catalyst.
  • the catalysts that may be used include, but are not limited to, basic catalysts such as potassium acetate, sodium acetate, zinc acetate, zinc diacetate dihydrate, aluminum acetate, calcium acetate, magnesium acetate, magnesium oxide, copper acetate, lithium acetate, aluminum oxide, or zinc oxide.
  • basic catalysts such as potassium acetate, sodium acetate, zinc acetate, zinc diacetate dihydrate, aluminum acetate, calcium acetate, magnesium acetate, magnesium oxide, copper acetate, lithium acetate, aluminum oxide, or zinc oxide.
  • the catalysts include, but are not limited to, acidic catalysts such as paratoluene sulfonic acid, dodecylbenzene sulfonic acid, boron trifluoride, zinc perchlorate, sulfated zirconium oxide, sulfated titanium oxide, lithium chloride, boron trifluoride etherate, ferric sulfate, zirconium oxychloride, cupric chloride, titanium tetrachloride, or zinc chloride.
  • acidic catalysts such as paratoluene sulfonic acid, dodecylbenzene sulfonic acid, boron trifluoride, zinc perchlorate, sulfated zirconium oxide, sulfated titanium oxide, lithium chloride, boron trifluoride etherate, ferric sulfate, zirconium oxychloride, cupric chloride, titanium tetrachloride, or zinc chloride.
  • Still other exemplary catalysts are heterogeneous catalysts. Still other exemplary catalysts are enzyme catalysts.
  • An exemplary enzyme is Novozym ® 435 available from Novozyme. Novozym 435 is an immobilized granulate, non-specific lipase particularly useful for ester production.
  • Neutral catalysts can also include silica and other insoluble surface-active agents.
  • amphoteric catalysts can include, but are not limited to, aluminum oxide, aluminum acetate, zinc acetate, magnesium acetate, and zinc oxide.
  • the present inventors have surprisingly and unexpectedly found that no catalyst is required to conduct the synthesis reaction of the invention.
  • the reaction can be conducted with all of the reactants added to the reaction vessel at the start of the reaction prior to adding heat.
  • the source of formaldehyde in this embodiment is preferably solid
  • This reaction surprisingly can be run rapidly and in a continuous mode and unexpectedly avoids the formation of— or substantially minimizes the formation of— deleterious side products, unwanted polymerization complexes and degradation of the monomer products.
  • the present invention contemplates that the synthesis reaction include an acidic or non-acidic solvent, or optionally no solvent at all.
  • Non-acidic solvents can include, but are not limited to, tetrahydrofuran, chloroform, dichloromethane, toluene, heptane, ethyl acetate, n-butyl acetate, dibutyl ether and hexane.
  • Acidic solvents can include, but are not limited to acetic acid and propionic acid.
  • the acidic solvent is added just prior to recovery.
  • optionally no solvent is needed.
  • This zero- solvent approach will not only decrease the overall cost of production but will also help to lessen any negative impact on the environment caused by the methods of the invention, i.e., provides an environmentally-friendly approach to the synthesis of 2- methylene-l,3-disubstituted-propane-l,3-diones.
  • An advantage of this condition is the avoidance or minimization of the formation of impurities, e.g., ketals and other latent acid- forming species.
  • the present inventors have surprisingly and unexpectedly found that the synthesis reaction of the invention may be conducted in the absence of both a solvent and a catalyst.
  • the reaction can be conducted with all of the reactants added to the reaction vessel at the start of the reaction prior to adding heat and in the absence of a solvent.
  • the source of formaldehyde in this embodiment is preferably solid paraformaldehyde, and is added along with the other reactants, including the malonic ester, prior to adding heat.
  • This reaction surprisingly can be run rapidly and in a continuous mode and unexpectedly avoids the formation of— or substantially minimizes the formation of— deleterious side products, unwanted polymerization complexes and degradation of the monomer products.
  • Certain embodiments of the present invention provide monomers that are amenable to anionic polymerization. Therefore, to prevent unwanted polymerization and extend shelf life, certain exemplary embodiments include suitable acidic stabilizers, for example, trifluoromethane sulfonic acid, maleic acid, methane sulfonic acid, difluoro acetic acid, trichloroacetic acid, phosphoric acid, dichloro acetic acid, chlorodifluoro or like acid.
  • Acidic stabilizers can include any material which can be added to the monomer or polymer compositions to extend shelf-life, e.g., by up to, for example, 1 year or more.
  • Such acidic stabilizers may have a pKa in the range of, for example, between about -15 to about 5, or between about -15 to about 3, or between about -15 to about 1, or between -2 to about between about -2 to about 2, or between about 2 to about 5, or between about 3 to about 5.
  • the starting precursor is reacted with paraformaldehyde in the presence of a catalyst (e.g., zinc acetate dehydrate) at 60 °C -130 °C (e.g., 100 °C) for at least about 30 minutes.
  • a catalyst e.g., zinc acetate dehydrate
  • the resulting intermediate material e.g., oligomeric complex
  • the resulting crude monomer is then purified, for example by distillation, fractional distillation or other separation methods.
  • reaction complex For a typical lab scale reaction: a 3-neck 250 mL round bottom reaction flask was equipped with an overhead stirrer, a heating mantle, and a temperature probe connected to a temperature controller. The reaction flask was adequately vented to the back of the hood to reduce the possibility of pressure build-up. The beta-ketoester (precursor), paraformaldehyde (1.8 equiv) and zinc acetate (0.001 equiv) were added to the reaction flask. The contents of the flask were mixed for approximately 2 minutes prior to the application of heat. After the initial mixing period the temperature controller was set to 100 °C. The heterogeneous reaction mixture was allowed to heat with the temperature for dissolution and onset of exotherm being noted. Once a rapid increase in temperature was observed, heating was discontinued. Once the exotherm subsided, the heating mantle was immediately removed and the reaction mixture (herein "reaction complex”) was allowed to cool to room
  • a 4-neck suitable round bottom flask was equipped with a mechanical stirrer, heating mantle, a thermocouple connected to a temperature controller, an addition funnel, a Claisen adapter, and a vacuum adapter connected to a receiver one-neck round bottom flask which was placed in an ice-bath.
  • the system was evacuated to low pressure (1- 250 mmHg).
  • the oligomeric mixture was added to the addition funnel.
  • the reaction flask was then applied via the connected heating mantle to 150-270 °C. Once the temperature inside the flask reached the desired range, a drop-wise addition of the oligomer (reaction complex) to reaction flask was started.
  • the addition rate was maintained so that the set temperature was maintained in the desired range.
  • the heating mantle was turned off and the system was allowed to cool to room temperature, at this point the system was opened to atmospheric pressure. An aliquot was then taken for analysis and the remaining cracked distillate was either distilled further via fractional distillation to improve purity or placed in a refrigerator.
  • This general reaction scheme was utilized to provide the examples provided herein. Due to the wide variety of example obtained, it is envisioned that this general reaction scheme can be utilized to provide a wide array of methylene beta-ketoester monomers as set forth herein. Further, it is envisioned that modifications can be made to this general reaction scheme in order to improve efficiencies and purity of the product obtained.
  • the invetion provides a method of preparing methylene beta- ketoester monomers according to the reaction scheme disclosed herein.
  • the method for preparing the methylene beta-ketoester monomers comprises: a) reacting a beta-ketoester reactant having the structural formula:
  • the reaction may be initiated at temperatures between about 60 °C to about 130 °C, at atmospheric pressure. It is contemplated that the reaction conditions may be modified depending on the source of formaldehyde. For example, when paraformaldehyde is utilized within the reaction vessel, the initial temperature must be high enough to make free formaldehyde available for the reaction. If another source of formaldehyde is utilized, those having skill in the art will appreciate that the reaction conditions may be modified accordingly. Exemplary sources include paraformaldehyde, formalin, trioxane, gaseous formaldehyde, or any reaction or process in which formaldehyde is liberated.
  • the methylene beta-ketoester monomer may be isolated from the reaction complex by contacting the reaction complex, or a portion thereof, with an energy transfer means to produce a vapor phase including the methylene beta- ketoester monomer; and collecting the methylene beta-ketoester monomer from the vapor phase.
  • the methylene beta-ketoester monomer may be isolated from the reaction complex immediately, or the reaction complex may be stored, preferably refrigerated, until a later time.
  • the reaction complex is not acid stabilized prior to isolating the methylene beta-ketoester monomer.
  • the reaction complex may be heated to a vapor phase and condensed in order to isolate the methylene beta-ketoester monomer.
  • the reaction complex may be heated to a temperature between about 130 °C and about 300 °C.
  • the reaction complex, or a portion thereof may come in contact with an energy transfer means in order to facilitate isolation of the monomer.
  • the reaction complex, or portion thereof may be vaporized in a very short time, for example less than 15 minutes, preferably less than 1 minute, more preferably less than 30 seconds, and less than 1 second. Certain exemplary embodiments contemplate vaporizing the reaction complex in a continuous manner as it is formed during the reaction step.
  • Exemplary energy transfer means include a heat transfer agent, a heat exchanger, a laser, microwave energy, sonic energy, electromagnetic energy, and a source of radiation, or any combination thereof.
  • the energy transfer means operates to quickly vaporize the reaction complex (or portion thereof) to permit isolation of the monomer product.
  • an oligomeric complex may be formed, and the energy transfer means is utilized to "crack" or depolymerize the oligomer to allow isolation of the monomer.
  • the oligomeric complex may include oligomers of 2-12 units able to provide monomer product upon crack.
  • the heat transfer agent is a heated inert gas, one or more metal beads, one or more glass beads, one or more porcelain beads, sand, silica, silicone oil, mineral oil, a petroleum based heat transfer oil, a synthetic chemical based heat transfer oil, or a pre-formed portion of the reaction complex.
  • the heat exchanger is a shell and tube heat exchanger, a plate heat exchanger, and adiabatic wheel heat exchanger, a finned pipe heat exchanger, a plate fin heat exchanger, or a scraped surface heat exchanger.
  • the vapor phase of the reaction complex is condensed, and the condensate is subject to one or more further separation processes.
  • the separation process may include any of simple distillation, fractional distillation, flash distillation, steam distillation, vacuum distillation, short path distillation, thin-film distillation, reactive distillation, pervaporation, extractive distillation, flash evaporation, rotary evaporation, liquid/liquid extraction, centrifuging, or any combination thereof, and other techniques known to those having skill in the art.
  • the methylene beta-ketoester monomers of the invention can be incorporated into any number of compositions and products including but not limited to reactive monomer-based compositions, reactive oligomer-based compositions and reactive polymer-based compositions.
  • Exemplary compositions can be analyzed by placing a drop of a monomer composition on a substrate (for example a glass slide or 4"xl" polycarbonate sample). Another glass slide or piece of polycarbonate is pressed on top over the monomer- covered area. The time is then immediately recorded from pressing the top-slide till the two slides are bonded tightly.
  • the exemplary composition is capable of bonding glass to a substrate in less than about 90 seconds, less than about 60 seconds, less than about 30 seconds or less than about 15 seconds.
  • the exemplary composition is capable of bonding polycarbonate to a substrate in less than about 90 seconds, less than about 60 seconds, less than about 45 seconds or less than about 30 seconds.
  • exemplary compositions can be analyzed by mixing 0.5 ml of monomer with 0.3 ml of 3% tertiary butyl ammonium fluoride (TBAF) in Dibutyl Phthalate solution. The time is recorded from adding the TBAF solution till the mixture become solid with vigorous stirring or mixing. In such embodiments, said composition solidifies upon addition of 3% tertiary butyl ammonium fluoride (TBAF) in Dibutyl Phthalate solution in less than about 15 seconds, less than about 10 seconds, or less than about 7 seconds.
  • TBAF tertiary butyl ammonium fluoride
  • the exemplary compositions can be analyzed by placing 0.5 ml of monomer into a test tube and cap with a cork stopper and keeping the test tubes containing monomers at 25°C, or in ovens at 55°C or 82°C.
  • the storage stability test is performed at atmospheric pressure. Time is recorded when the monomer became a gel or solid.
  • said composition remains stable at 25°C and at atmospheric pressure for more than 10 days, more than 15 days, more than 20 days, more than 25 days or more than 30 days.
  • said composition remains stable at 82°C and at atmospheric pressure for more than about 2 hours, more than about 3 hours, or more than about 4 hours.
  • compositions include, but are not limited to an adhesive, a coating, a sealant, a composite, or a surfactant.
  • polymer products include, but are not limited to, a sealant, a thermal barrier coating, a textile fiber, a water-treatment polymer, an ink carrier, a paint carrier, a packaging film, a molding, a medical polymer, a polymer film, a polymer fiber or a polymer sheet.
  • the exemplary compositions may be formulated to include one or more materials to extend the shelf-life as well as control the onset of cure of the materials.
  • the compositions are formulated such that the composition is stable for at least 1 month, or for at least 2 months, or for at least 3 months, or for at least 4 months, or for at least 5 months, or for at least 5-10 months, or for at least 10-20 months, or for at least 20-30 months.
  • the adhesive composition comprising the methylene beta-ketoester monomers or other commercial compositions or products, are stable for at least one year.
  • Such formulation materials include acidic stabilizer, volatile acid stabilizers, acidic gases, free radical stabilizers, sequestering agents, cure accelerators and rheology modifiers.
  • Exemplary embodiments contemplate any suitable acidic stabilizer known in the art, including, for example, trifluoromethane sulfonic acid, maleic acid, methane sulfonic acid, difluoro acetic acid, trichloroacetic acid, phosphoric acid, dichloroacetic acid, chlorodifluoro or like acid.
  • Acidic stabilizers can include any material which can be added to the monomer or polymer compositions to extend shelf-life, e.g., by up to, for example, 1 year or more.
  • Such acidic stabilizers may have a pKa in the range of, for example, between about -15 to about 5, or between about -15 to about 3, or between about -15 to about 1, or between -2 to about between about -2 to about 2, or between about 2 to about 5, or between about 3 to about 5.
  • Volatile acid stabilizers include any material which can be added to the monomer or polymer compositions to extend shelf-life and stabilize the vapor phase above the composition upon storage, e.g., acidic gases. Such volatile acid stabilizers may have a boiling point, for example, less than about 200°C; less than about 170°C; or less than about 130°C.
  • Acidic gases include any gaseous material which can be added to the monomer or polymer compositions to extend shelf-life and stabilize the vapor phase above the composition upon storage.
  • Such acid gases can include, but are not limited to, S0 2 or BF 3 .
  • such acidic stabilizer can be present in a concentration of about 0.1 ppm to about 100 ppm; about 0.1 ppm to about 25 ppm; or about 0.1 ppm to about 15 ppm.
  • Free radical stabilizers can include any material capable of stabilizing or inhibiting free radical polymerization of the material upon standing.
  • the free radical stabilizers are phenolic free radical stabilizers such as, HQ (hydroquinone), MEHQ (methyl- hydroquinone), BHT (butylated hydroxtoluene) and BHA (butylated hydroxyanisole).
  • the free radical stabilizers are present in a concentration of 0.1 ppm to 10,000 ppm; 0.1 ppm to 3000 ppm; or 0.1 ppm to 1500 ppm.
  • the free radical stabilizers are present in a concentration of 0.1 ppm to 1000 ppm; 0.1 ppm to 300 ppm; or 0.1 ppm to 150 ppm.
  • Sequestering agents include any material capable of enhancing the bonding of materials containing acid salts such as paper or wood.
  • sequestering agents include, but are not limited to crown ethers, silyl crowns, calixarenes and
  • Sequestering agents also enhance the utility of surface accelerators that are acid salts applied to surfaces to control the rate of cure of the materials.
  • Cure accelerators include any material capable of speeding the rate of cure of the methylene beta-ketoester monomers. Cure accelerators also include any material capable of speeding the cure through volume of the applied composition. Such cure accelerators include but are not limited to sodium or potassium acetate; acrylic, maleic or other acid salts of sodium, potassium lithium copper and cobalt; salts such as tetrabutyl ammonium fluoride, chloride, or hydroxide; or chemically basic materials such as amines and amides, or salts of polymer bond acids, benzoate salts, 2,4-pentanedionate salts, sorbate salts , or propionate salts. Such cure accelerators can be added directly to the exemplary compositions or applied to the material to be bonded prior to addition of the composition.
  • Rheology modifiers include any material which can modify the viscosity of the exemplary compositions as well as thixotropic properties for greater utility in certain applications.
  • Rheology modifiers include, but are not limited to,
  • the exemplary compositions may include tougheners.
  • tougheners include, but are not limited to, acrylic rubbers; polyester urethanes; ethylene-vinyl acetates; fluorinated rubbers; isoprene-acrylonitrile polymers;
  • the tougheners include those disclosed in U.S. Pat. No.
  • the toughener is an elastomeric polymer which is a copolymer of methyl acrylate and ethylene, manufactured by DuPont, under the name of VAMAC, such as VAMAC N123 and VAMAC B-124.
  • VAMAC N123 and VAMAC B-124 are reported by DuPont to be a master batch of
  • the toughener may be the DuPont materials called VAMAC B-124, N123., VAMAC G, VAMAC VMX 1012 or VCD 6200.
  • the toughener may be a rubber toughening component having (a) reaction products of the combination of ethylene, methyl acrylate and monomers having carboxylic acid cure sites, (b) dipolymers of ethylene and methyl acrylate, and combinations of (a) and (b), which once the reaction products and/or dipolymers are formed are then substantially free of processing aids, such as the release agents octadecyl amine (reported by DuPont to be available commercially from Akzo Nobel under the tradename ARMEEN 18D), complex organic phosphate esters (reported by DuPont to be available commercially from R.T.
  • processing aids such as the release agents octadecyl amine (reported by DuPont to be available commercially from Akzo Nobel under the tradename ARMEEN 18D), complex organic phosphate est
  • Vanderbilt Co., Inc. under the tradename VANFRE VAM stearic acid and/or polyethylene glycol ether wax
  • anti-oxidants such as substituted diphenyl amine (reported by DuPont to be available commercially from Uniroyal Chemical under the tradename
  • compositions containing methylene beta-ketoester monomer may also optionally include other additives, such as plasticizing agents, thixotropic agents, natural or synthetic rubbers, filler agents, and reinforcing agents, etc.
  • additives are well known to those skilled in the art.
  • the exemplary compositions containing methylene beta-ketoester monomer may optionally include at least one plasticizing agent that imparts flexibility to the polymer formed from the methylene beta-ketoester monomer.
  • the plasticizing agent preferably contains little or no moisture and should not significantly affect the stability or polymerization of the monomer.
  • plasticizers are useful in polymerized compositions to be used in any application in which flexibility of the adhesive or polymer product is desirable.
  • plasticizers include, without limitation, acetyl tributyl citrate, dimethyl sebacate, triethyl phosphate, tri (2-ethylhexyl)phosphate, tri (p- cresyl) phosphate, glyceryl triacetate, glyceryl tributyrate, diethyl sebacate, dioctyl adipate, isopropyl myristate, butyl stearate, lauric acid, trioctyl trimellitate, dioctyl glutarate, and mixtures thereof.
  • Preferred plasticizers are tributyl citrate and acetyl tributyl citrate.
  • suitable plasticizers include polymeric plasticizers, such as polyethylene glycol (PEG) esters and capped PEG esters or ethers, polyester glutarates and polyester adipates.
  • plasticizing agents in amounts less than about 60 weight %, or less than about 50 weight %, or less than about 30 weight %, or less than about 10 weight %, or less than about 5 weight %, or less than about 1 weight % or less, provides increased film strength (e.g., toughness) of the polymerized monomer over polymerized monomers not having plasticizing agents.
  • compositions containing methylene beta-ketoester monomer may also optionally include at least one thixotropic agent, i.e., the property of exhibiting a high fluidity during deformation by force of a sprayer, roller or trowel, but losing the fluidity when left at rest.
  • thixotropic agents are known to the skilled artisan and include, but are not limited to, silica gels such as those treated with a silyl isocyanate. Examples of suitable thixotropic agents are disclosed in, for example, U.S. Pat. Nos.: 4,720,513 or 4,510,273, the disclosures of which are hereby incorporated in their entireties.
  • the exemplary compositions containing methylene beta-ketoester monomer may also optionally include at least one natural or synthetic rubber to impart impact resistance, which is preferable especially for industrial compositions of the present invention.
  • Suitable rubbers are known to the skilled artisan. Such rubbers include, but are not limited to, dienes, styrenes, acrylonitriles, and mixtures thereof. Examples of suitable rubbers are disclosed in, for example, U.S. Pat. Nos. 4,313,865 and 4,560,723, the disclosures of which are hereby incorporated in their entireties.
  • compositions containing methylene beta-ketoester monomer may also optionally comprise one or more other reinforcing agents (e.g., fibrous reinforcements) other than natural or synthetic rubber to impart impact resistance and/or to impart structural strength or to provide shape or form.
  • suitable fibrous reinforcement include PGA microfibrils, collagen microfibrils, cellulosic microfibrils, and olefinic microfibrils.
  • the compositions may also contain colorants such as dyes, pigments, and pigment dyes.
  • suitable colorants include 6-hydroxy-5-[(4- sulfophenyl)axo]-2-naphthalene-sulfonic acid (FD+C Yellow No. 6); 9-(o- carboxyphenyl)-6-hydroxy-2,4,5,7-tetraiodo-3H-xanthen-3-one monohydrate (FD+C Red No. 3); and 2-(l,3-dihydro-3-oxo-5-sulfo-2H-indol-2-ylidene)-2,3-dihydro-3- oxo-lH-indo le-5-sulfonic acid (FD+C Blue No. 2), wherein the suitable colorant should not destabilize the monomer.
  • compositions containing methylene beta-ketoester monomer may also optionally include at least one thickening agent.
  • suitable thickeners include, for example, polycyanoacrylates, polylactic acid, poly-l,4-dioxa-2-one, polyoxalates, polyglycolic acid, lactic-glycolic acid copolymers, polycaprolactone, lactic acid- caprolactone copolymers, poly-3-hydroxybutyric acid, polyorthoesters, polyalkyl acrylates, copolymers of alkylacrylate and vinyl acetate, polyalkyl methacrylates, and copolymers of alkyl methacrylates and butadiene.
  • alkyl methacrylates and acrylates are poly(2-ethylhexyl methacrylate) and poly(2-ethylhexyl acrylate), also poly(butylmethacrylate) and poly(butylacrylate), also copolymers of various acrylate and methacrylate monomers, such as poly(butylmethacrylate-co- methylacrylate).
  • difunctional monomeric cross-linking agents may be added to the monomer compositions of this invention.
  • crosslinking agents are known.
  • U.S. Pat. No. 3,940,362 to Overhults which is hereby incorporated in its entirety by reference, discloses such crosslinking agents.
  • compositions and additives contemplated herein include additional stabilizers, accelerators, plasticizers, fillers, opacifiers, inhibitors, thixotrophy conferring agents, dyes, fluorescence markers, thermal degradation reducers, adhesion promoters, thermal resistance conferring agents and combinations thereof, and the like, some of which are exemplified by U.S. Pat. Nos. 5,624,669; 5,582,834;
  • composition is a monomer-based composition (e.g. , inks, adhesives, coatings, sealants or reactive molding) or a polymer-based
  • composition e.g., fibers, films, sheets, medical polymers, composite polymers and surfactants
  • one having ordinary skill in the art will have the knowledge and skill by which to formulate such compositions and/or products without undue experimentation having suitable amounts, levels and combinations of the above types of additives and components.
  • polymerizable compositions may be formulated to include additives such as acidic stabilizers, a free radical stabilizers, a sequestering agents, a cure accelerators, rheology modifiers, a plasticizing agents, a thixotropic agents, natural rubbers, synthetic rubbers, filler agents, reinforcing agents and the like.
  • additives are provided at levels sufficient to achieve the desired results which can readily be determined by those having skill in the art.
  • an acidic stabilizer is present in a concentration of about 0.1 ppm to about 100 ppm, about 0.1 ppm to about 25 ppm, or about 0.1 ppm to about 15 ppm, by weight of the composition.
  • a free radical stabilizer is present in a concentration selected from about 0.1 ppm to about 10000 ppm, about 0.1 ppm to about 3000 ppm, about 0.1 ppm to 1500 ppm, about 0.1 ppm to about 1000 ppm, about 0.1 ppm to about 300 ppm, or about 0.1 ppm to about 150 ppm, by weight of the composition.
  • a sequestering agent such as a crown ether, a silyl crown, a calixarene, a polyethylene glycol, or a combination thereof may be utilized.
  • a cure accelerator such as sodium acetate, potassium acetate, tetrabutyl ammonium fluoride, tetrabutyl ammonium chloride, tetrabutyl ammonium hydroxide, a benzoate salt, a 2,4-pentanedionate salt, a sorbate salt, and a propionate salt, may be utilized.
  • a rheology modifier such as
  • hydroxyethylcellulose ethyl hydroxyethylcellulose, methylcellulose, a polymeric thickener, and pyrogenic silica, may be utilized.
  • Exemplary polymerizable compositions are stable at 25°C and at atmospheric pressure for more than 10 days, more than 15 days, more than 20 days, more than 25 days, or more than 30 days. Certain exemplary embodiments may exhibit a shelf life of up to one year, or up to two years. Certain exemplary embodiments may be tested for stability at elevated temperature, e.g., 82°C, at atmospheric pressure. Certain exemplary embodiments may exhibit elevated temperature stability for more than 2 hours.
  • Certain exemplary embodiments disclosed herein relate to polymers and polymer products formed by polymerization of the polymerizable compositions comprising the methylene beta-ketoester monomers.
  • Polymers and polymer products envisioned include coatings, paints, fibers, composites, textile fibers, water-treatment polymers, ink carriers, paint carriers, packaging films, moldings, medical polymers, polymer films, polymer fibers, polymer sheets, and the like.
  • the methylene beta-ketoester monomers are capable of supporting a vast array of products due to the activity of the methylene group and the ability to vary the functional groups R, R as shown in the structure of the repeating unit:
  • R and R' are independently C 1 -C 15 alkyl, C2-C 15 alkenyl, halo-(Ci-Cis alkyl), C 3 -C 6 cycloalkyl, halo-(C 3 -C 6 cycloalkyl), heterocyclyl, heterocyclyl-(Ci-Ci 5 alkyl), aryl, aryl-(Cl-C15 alkyl), heteroaryl or heteroaryl-(Ci-Ci 5 alkyl), or alkoxy -(Cl-15 alkyl), each of which may be optionally substituted by C 1 -C 15 alkyl, halo-(Ci-Cis alkyl), C 3 -C 6 cycloalkyl, halo-(C 3 -C 6 cycloalkyl), heterocyclyl, heterocyclyl-(Ci-Ci 5 alkyl), aryl, aryl -(C 1 -C 15 alkyl), heteroaryl, C
  • the reaction of the precursor beta-ketoester with the source of formaldehyde may result in an oligomeric complex which is subsequently cracked to obtain the desired methylene beta-ketoester monomer.
  • Certain oligomeric complexes are capable of being efficiently vaporized or "cracked" into high purity monomers of 2- methylene-l,3-disubstituted-propane-l,3-dione by rapid vaporization as described herein.
  • the invention provides an oligomeric complex prepared by reacting a l,3-disubstituted-propane-l,3-dione with a source of formaldehyde; optionally in the presence of heat transfer agent; optionally in the presence of an acidic or basic catalyst; and optionally in the presence of an acidic or non-acidic solvent.
  • the oligomeric complex comprises between 2 and 12 repeat units that are able to yield monomer upon cracking
  • the invention further provides an oligomeric complex prepared by reacting a l,3-disubstituted-propane-l,3-dione with a source of formaldehyde in a substantial absence of acidic solvent; optionally in the presence of heat transfer agent; optionally in the presence of an acidic or basic catalyst; and optionally in the presence of a non- acidic solvent.
  • the substantial absence of acidic solvent represents less than 1.0%, less than 0.5%, less than 0.2% or less than 0.1% by weight acidic solvent as compared to the total composition of the reaction mixture.
  • a 250 mL round bottom flask was equipped with a heating mantle, an overhead stirrer equipped with a teflon paddle, a thermocouple and an outlet adapter with attached rubber tubing vented to the back of the hood.
  • the round bottom flask was placed on a heating mantle.
  • a 50 g sample of ethyl pivaloylacetate (i.e., 4,4- dimethyl-3-oxopentanoate), 4.8 g of paraformaldehyde and 0.06 g of zinc acetate were added to the round bottom flask to form a heterogeneous mixture. After 2 minutes of mixing the temperature was set to 100 °C and heating was started.
  • a 4-neck 250 mL round bottom flask was fitted with a mechanical stirrer, an addition funnel, a thermocouple attached to a temperature controller, a Claisen distillation head, vacuum adapater connected to a one-neck 100 mL round bottom flask placed in an ice bath.
  • the system was evacuated to 100 mmHg after which heat was then applied via a heating mantle.
  • the set temperature reached 190 °C
  • the oligomer was slowly added to the hot cracking flask.
  • the resulting crude monomer was simultaneously cracked and distilled to the recieving flask. During the distillation phase an average head temperature of 155 °C was observed.
  • the heat source was turned off and the system was allowed to cool to room temperature.
  • the crude pale green monomer was then analyzed by 1 H and 13 C NMR. The following monomer was obtained.
  • Figures 1 and 2 show the 1H, 13 C, and DEPT-135 NMR spectra of the isolation step ("crack") in this reaction. Peaks at 5.6 and 6.3 ppm in the 1 H and 126 ppm in the
  • Figures 3 and 4 show peaks at 6.1 and 6.7 ppm in the 1H NMR spectrum and a peak at 131 ppm in the 13 C NMR spectrum corresponding to the geminal CH 2 peak and a quaternary peak at 142 ppm, which are consistent with the product.
  • Example 3 Reaction of ethyl 3-oxohexanoate with formaldehyde:
  • Figure 5 shows the 1H NMR spectrum. Peaks at 6.25 and 6.35 ppm are consistent with the geminal CH 2 of the product.
  • Figure 6 shows the H NMR spectrum. The two small peaks at 6.4 and 6.5 ppm are consistent with the geminal CH 2 of the product.
  • Example 5 Reaction of methyl 3-oxobuanoate with formaldehyde:
  • Figure 7 shows the 1 H NMR spectrum. The peaks at 6.4 and 6.5 ppm are consistent with the geminal CH 2 of the product
  • Figure 8 shows the 1H NMR spectrum. The peaks at 6.15 and 6.35 ppm are consistent with the geminal CH 2 of the product.
  • Example 7 Reaction of ethyl 3-oxopenanoate with formaldehyde: The reaction scheme disclosed herein was performed using ethyl 3- oxopenanoate and formaldehyde (obtained from paraformaldehyde). The following monomer was obtained.
  • Figure 9 shows the 1H NMR spectrum. The peaks at 6.3 and 6.4 ppm are consistent with the geminal CH 2 of the product.
  • reaction scheme disclosed herein is performed using an appropriate beta- ketoester reactant and a source of formaldehyde to obtain the following monomers.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Health & Medical Sciences (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Wood Science & Technology (AREA)
  • Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
  • Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
  • Adhesives Or Adhesive Processes (AREA)
  • Phenolic Resins Or Amino Resins (AREA)
  • Polyesters Or Polycarbonates (AREA)
  • Low-Molecular Organic Synthesis Reactions Using Catalysts (AREA)
  • Paints Or Removers (AREA)
  • Inks, Pencil-Leads, Or Crayons (AREA)
  • Sealing Material Composition (AREA)
  • Wrappers (AREA)
  • Polymerisation Methods In General (AREA)
  • Macromonomer-Based Addition Polymer (AREA)
PCT/US2012/060837 2010-10-20 2012-10-18 Methylene beta-ketoester monomers, methods for making methylene beta-ketoester monomers, polymerizable compositions and products formed therefrom Ceased WO2013066629A1 (en)

Priority Applications (7)

Application Number Priority Date Filing Date Title
US14/352,406 US9527795B2 (en) 2011-10-19 2012-10-18 Methylene beta-ketoester monomers, methods for making methylene beta-ketoester monomers, polymerizable compositions and products formed therefrom
EP12846728.9A EP2768872B1 (en) 2011-10-19 2012-10-18 Methods for making methylene beta-ketoester monomers
MX2014004781A MX360463B (es) 2011-10-19 2012-10-18 Monomeros de beta-cetoester de metileno, procedimientos de fabricación de monomeros de beta-cetoester de metileno, composiciones polimerizables y productos formados a partir de las mismas.
CA2853079A CA2853079A1 (en) 2011-10-19 2012-10-18 Methylene beta-ketoester monomers, methods for making methylene beta-ketoester monomers, polymerizable compositions and products formed therefrom
JP2014537249A JP2014534969A (ja) 2011-10-19 2012-10-18 メチレンβ−ケトエステルモノマー、メチレンβ−ケトエステルモノマーを製造するための方法、これらから作られる重合可能な組成物および製品
US15/363,169 US20170073438A1 (en) 2011-10-19 2016-11-29 Polymers including a methylene beta-ketoester and products formed therefrom
US15/661,893 US10414839B2 (en) 2010-10-20 2017-07-27 Polymers including a methylene beta-ketoester and products formed therefrom

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
US201161549152P 2011-10-19 2011-10-19
US201161549104P 2011-10-19 2011-10-19
US201161549092P 2011-10-19 2011-10-19
US61/549,092 2011-10-19
US61/549,104 2011-10-19
US61/549,152 2011-10-19

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
US14/868,795 Continuation-In-Part US9828324B2 (en) 2010-10-20 2015-09-29 Methylene beta-diketone monomers, methods for making methylene beta-diketone monomers, polymerizable compositions and products formed therefrom

Related Child Applications (2)

Application Number Title Priority Date Filing Date
US14/352,406 A-371-Of-International US9527795B2 (en) 2011-10-19 2012-10-18 Methylene beta-ketoester monomers, methods for making methylene beta-ketoester monomers, polymerizable compositions and products formed therefrom
US15/363,169 Division US20170073438A1 (en) 2010-10-20 2016-11-29 Polymers including a methylene beta-ketoester and products formed therefrom

Publications (1)

Publication Number Publication Date
WO2013066629A1 true WO2013066629A1 (en) 2013-05-10

Family

ID=48141622

Family Applications (3)

Application Number Title Priority Date Filing Date
PCT/US2012/060840 Ceased WO2013059479A2 (en) 2010-10-20 2012-10-18 Methylene beta-diketone monomers, methods for making methylene beta-diketone monomers, polymerizable compositions and products formed therefrom
PCT/US2012/060830 Ceased WO2013059473A2 (en) 2011-10-19 2012-10-18 Multifunctional monomers, methods for making multifunctional monomers, polymerizable compositions and products formed therefrom
PCT/US2012/060837 Ceased WO2013066629A1 (en) 2010-10-20 2012-10-18 Methylene beta-ketoester monomers, methods for making methylene beta-ketoester monomers, polymerizable compositions and products formed therefrom

Family Applications Before (2)

Application Number Title Priority Date Filing Date
PCT/US2012/060840 Ceased WO2013059479A2 (en) 2010-10-20 2012-10-18 Methylene beta-diketone monomers, methods for making methylene beta-diketone monomers, polymerizable compositions and products formed therefrom
PCT/US2012/060830 Ceased WO2013059473A2 (en) 2011-10-19 2012-10-18 Multifunctional monomers, methods for making multifunctional monomers, polymerizable compositions and products formed therefrom

Country Status (6)

Country Link
US (7) US9221739B2 (enExample)
EP (6) EP3517523A1 (enExample)
JP (3) JP2014534969A (enExample)
CA (3) CA2853079A1 (enExample)
MX (3) MX360463B (enExample)
WO (3) WO2013059479A2 (enExample)

Cited By (28)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2831185A4 (en) * 2012-03-30 2016-01-27 Sirrus Inc INK AND COATING FORMULATIONS AND POLYMERIZABLE SYSTEMS FOR THE PRODUCTION OF SAID FORMULATIONS
US9249265B1 (en) 2014-09-08 2016-02-02 Sirrus, Inc. Emulsion polymers including one or more 1,1-disubstituted alkene compounds, emulsion methods, and polymer compositions
WO2016040014A1 (en) 2014-09-08 2016-03-17 Sirrus, Inc. Solution polymers including one or more 1,1-disubstituted alkene compounds, solution polymerization methods, and polymer compositions
US9315597B2 (en) 2014-09-08 2016-04-19 Sirrus, Inc. Compositions containing 1,1-disubstituted alkene compounds for preparing polymers having enhanced glass transition temperatures
US9416091B1 (en) 2015-02-04 2016-08-16 Sirrus, Inc. Catalytic transesterification of ester compounds with groups reactive under transesterification conditions
US9512058B2 (en) 2011-10-19 2016-12-06 Sirrus Inc. Multifunctional monomers, methods for making multifunctional monomers, polymerizable compostions and products formed thereform
US9518001B1 (en) 2016-05-13 2016-12-13 Sirrus, Inc. High purity 1,1-dicarbonyl substituted-1-alkenes and methods for their preparation
US9522381B2 (en) 2013-01-11 2016-12-20 Sirrus, Inc. Method to obtain methylene malonate via bis(hydroxymethyl) malonate pathway
US9567475B1 (en) 2016-06-03 2017-02-14 Sirrus, Inc. Coatings containing polyester macromers containing 1,1-dicarbonyl-substituted 1 alkenes
US9617354B2 (en) 2015-06-01 2017-04-11 Sirrus, Inc. Electroinitiated polymerization of compositions having a 1,1-disubstituted alkene compound
US9617377B1 (en) 2016-06-03 2017-04-11 Sirrus, Inc. Polyester macromers containing 1,1-dicarbonyl-substituted 1 alkenes
US9683147B2 (en) 2015-05-29 2017-06-20 Sirrus, Inc. Encapsulated polymerization initiators, polymerization systems and methods using the same
US9752059B2 (en) 2012-11-16 2017-09-05 Sirrus, Inc. Plastics bonding systems and methods
DE102017204525A1 (de) 2016-03-23 2017-09-28 Basf Se Verbundfolienlaminate für flexible Verpackungen
US9828324B2 (en) 2010-10-20 2017-11-28 Sirrus, Inc. Methylene beta-diketone monomers, methods for making methylene beta-diketone monomers, polymerizable compositions and products formed therefrom
WO2018086860A1 (en) 2016-11-09 2018-05-17 Basf Se Polyurethane-vinyl hybrid polymers, methods of making them and their use
US10047192B2 (en) 2012-06-01 2018-08-14 Sirrus, Inc. Optical material and articles formed therefrom
US10196481B2 (en) 2016-06-03 2019-02-05 Sirrus, Inc. Polymer and other compounds functionalized with terminal 1,1-disubstituted alkene monomer(s) and methods thereof
WO2019137853A1 (en) 2018-01-09 2019-07-18 Basf Se Compositions comprising polymerizable vinyl compounds, inorganic or organic fillers and their use
US10414839B2 (en) 2010-10-20 2019-09-17 Sirrus, Inc. Polymers including a methylene beta-ketoester and products formed therefrom
US10428177B2 (en) 2016-06-03 2019-10-01 Sirrus, Inc. Water absorbing or water soluble polymers, intermediate compounds, and methods thereof
US10501400B2 (en) 2015-02-04 2019-12-10 Sirrus, Inc. Heterogeneous catalytic transesterification of ester compounds with groups reactive under transesterification conditions
CN110903194A (zh) * 2019-12-11 2020-03-24 南京恒道医药科技有限公司 连续制备伏立康唑中间体2-氟-3-氧戊酸乙酯的方法
US10607910B2 (en) 2012-11-30 2020-03-31 Sirrus, Inc. Composite compositions for electronics applications
WO2020123579A1 (en) 2018-12-11 2020-06-18 Sirrus, Inc. Polymerization of 1,1-dicarbonyl 1-alkenes
WO2020123581A1 (en) 2018-12-11 2020-06-18 Sirrus, Inc. Emulsion polymers of 1,1-dicarbonyl 1-alkenes of controlled particle size
DE102019219214A1 (de) 2018-12-17 2020-06-18 Basf Se Zusammensetzungen, die multifunktionelle Vinylverbindungen in Miniemulsion umfassen, und ihre Verwendung als Vernetzer für Polymere
US10913875B2 (en) 2012-03-30 2021-02-09 Sirrus, Inc. Composite and laminate articles and polymerizable systems for producing the same

Families Citing this family (46)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9144796B1 (en) 2009-04-01 2015-09-29 Johnson Matthey Public Limited Company Method of applying washcoat to monolithic substrate
EP3445830A1 (en) 2016-04-21 2019-02-27 Zephyros Inc. Malonates and derivatives for in-situ films
WO2017210084A1 (en) 2016-06-03 2017-12-07 Sirrus, Inc. Water absorbing or water soluble polymers, intermediate compounds, and methods thereof
JP2019517599A (ja) * 2016-06-03 2019-06-24 シラス・インコーポレイテッド 末端１，１−二置換アルケンモノマーによって官能化されたポリマー及びその他の化合物ならびにその方法
JP2019522064A (ja) * 2016-06-03 2019-08-08 シラス・インコーポレイテッド 吸水性または水溶性ポリマー、中間化合物、及びそれらの方法
US11078376B2 (en) 2016-07-26 2021-08-03 Ppg Industries Ohio, Inc. Polyurethane coating compositions containing 1,1-di-activated vinyl compounds and related coatings and processes
US11634524B2 (en) 2016-07-26 2023-04-25 Ppg Industries Ohio, Inc. Acid-catalyzed curable coating compositions containing 1,1 di-activated vinyl compounds and related coatings and processes
CN109641237B (zh) 2016-07-26 2021-11-30 Ppg工业俄亥俄公司 含有1,1-二-活化的乙烯基化合物的酸催化的可固化涂料组合物和相关的涂料和方法
WO2018022810A1 (en) 2016-07-26 2018-02-01 Ppg Industries Ohio, Inc. Curable compositions containing 1,1-di-activated vinyl compounds and related coatings and processes
EP3491057B1 (en) 2016-07-26 2022-11-09 PPG Industries Ohio, Inc. Particles having surfaces functionalized with 1,1-di-activated vinyl compounds
CN109642098B (zh) 2016-07-26 2022-02-11 Ppg工业俄亥俄公司 包含1,1-二活化的乙烯基化合物的可电沉积的涂料组合物
ES2932659T3 (es) * 2016-07-26 2023-01-23 Ppg Ind Ohio Inc Composiciones curables multicapa que contienen productos de compuestos vinílicos 1,1-diactivados y procesos relacionados
WO2018022785A1 (en) 2016-07-26 2018-02-01 Ppg Industries Ohio, Inc. Three-dimensional printing processes using 1,1-di-activated vinyl compounds
WO2018053503A1 (en) 2016-09-19 2018-03-22 Zephyros, Inc. Malonate and cyanoacrylate adhesives for joining dissimilar materials
US11999866B2 (en) 2016-09-19 2024-06-04 Zephyros, Inc. Polymalonate and cyanoacrylate based surface concrete sealers
US10934411B2 (en) 2016-09-30 2021-03-02 Ppg Industries Ohio, Inc. Curable compositions containing 1,1-di-activated vinyl compounds that cure by pericyclic reaction mechanisms
CN113249041B (zh) * 2017-05-18 2023-08-15 纳美仕有限公司 树脂组合物
JP7663319B2 (ja) 2017-06-02 2025-04-16 アルケマ フランス 硬化性組成物及びその使用
CN107225048B (zh) * 2017-07-01 2019-07-12 山东金城柯瑞化学有限公司 煤炭浮选剂
US20200368997A1 (en) 2017-09-13 2020-11-26 Zephyros, Inc. Composite structures for localized stiffening
JP6427848B1 (ja) * 2017-10-17 2018-11-28 ナミックス株式会社 樹脂組成物
JPWO2019088102A1 (ja) 2017-10-31 2020-12-03 ナミックス株式会社 樹脂組成物
WO2019129572A1 (en) * 2017-12-27 2019-07-04 Basf Se A composition, its preparation method, and the use of the composition in construction application
EP3724242A1 (en) * 2018-01-12 2020-10-21 Sirrus, Inc. Emulsion polymers crosslinked with compounds containing two or more dicarbonyl-substituted 1 alkene units
KR102540734B1 (ko) 2018-02-01 2023-06-08 삼성디스플레이 주식회사 유기발광표시장치 및 그의 제조방법
JP2021512139A (ja) * 2018-04-03 2021-05-13 シラス・インコーポレイテッド エステル交換条件下で反応性の基を有するエステル化合物の不均一触媒によるエステル交換
US11028294B2 (en) 2018-08-10 2021-06-08 International Business Machines Corporation Armonk, New York Acrylate-cyanoacrylate monomers
WO2020068916A1 (en) 2018-09-26 2020-04-02 Swimc Llc Curable coating compositions
JP7343912B2 (ja) 2018-10-05 2023-09-13 ナミックス株式会社 樹脂組成物
US12146014B2 (en) 2018-10-09 2024-11-19 Namics Corporation Curing agent composition for curing 2-methylene-1,3-dicarbonyl compound
CN112969756A (zh) 2018-11-15 2021-06-15 株式会社日本触媒 丙烯酸类树脂组合物、交联体和交联体的制造方法
JP7219594B2 (ja) * 2018-11-15 2023-02-08 株式会社日本触媒 粘着剤組成物、及びそれを含む物品並びに粘着製品の製造方法
CN113348157A (zh) * 2019-01-29 2021-09-03 株式会社日本触媒 养护剂、具有覆膜的水泥类结构体的制造方法、水泥类成形体的收缩减少方法和干燥抑制方法以及抑制劣化因子侵入水泥类结构体的方法
WO2020167621A1 (en) 2019-02-14 2020-08-20 Sirrus, Inc. Particles encapsulated with dicarbonyl-substituted-1- alkenes
US12479947B2 (en) 2019-07-19 2025-11-25 Arkema France Curable compositions useful for obtaining non-sensitizing cured products
WO2021075206A1 (ja) 2019-10-18 2021-04-22 ナミックス株式会社 重合性組成物及びそれを用いる硬化性樹脂組成物
CN111044647A (zh) * 2019-12-20 2020-04-21 广电计量检测(合肥)有限公司 一种检测水体中直链烷基苯的样品前处理和定量分析方法
WO2021150844A1 (en) 2020-01-24 2021-07-29 Sirrus, Inc. Compositions containing 1,1-disubstituted activated alkenes useful in additive manufacturing and articles formed therefrom
WO2021162938A1 (en) 2020-02-10 2021-08-19 Sirrus, Inc. Copolymers of dicarbonyl substituted-1-alkene and olefins and methods to make them
EP4122963A4 (en) * 2020-03-18 2024-04-24 Namics Corporation PHOTO-CURING RESIN COMPOSITION
WO2021231288A1 (en) 2020-05-15 2021-11-18 Nippon Shokubai Co., Ltd. Improved dicarbonyl substituted-1-alkene compositions
WO2021252594A1 (en) 2020-06-11 2021-12-16 Nippon Shokubai Co., Ltd. Polyesters prepared from 1,1-diester-1-alkenes containing a strong acid and stabilizer
US20240140903A1 (en) * 2020-12-17 2024-05-02 The Royal Institution For The Advancement Of Learning / Mcgill University Chemical additives and their use thereof for modifying mechanical properties of pvc and preventing the formation of surface defects during pvc calendering
WO2023149445A1 (ja) * 2022-02-07 2023-08-10 ナミックス株式会社 液状重合性組成物及びそれを用いる硬化性樹脂組成物
JPWO2023149444A1 (enExample) 2022-02-07 2023-08-10
EP4286677A1 (en) 2022-06-02 2023-12-06 Linde GmbH Method of operating an internal combustion engine and corresponding arrangement

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB432628A (en) * 1933-12-23 1935-07-23 John David Kendall Improvements in or relating to the production of compounds containing an ethylenic linkage, or a polymethine chain
US4049698A (en) * 1976-08-05 1977-09-20 Eastman Kodak Company Process for producing methylene malonic esters
US4728701A (en) * 1983-09-19 1988-03-01 Jarvis Marvin A Process for the polymerization of acrylates
US20040220060A1 (en) * 2000-06-22 2004-11-04 Bartley Stuart L Acylatign agents and dispersants for lubricating oil and fuels
US7659423B1 (en) * 2006-04-18 2010-02-09 Loctite (R&D) Limited Method of preparing electron deficient olefins in polar solvents
US20100286433A1 (en) * 2009-05-07 2010-11-11 Malofsky Bernard M Methylidene malonate process
US20110015406A1 (en) * 2008-03-18 2011-01-20 Mitsui Chemicals Agro, Inc. Method for producing fluorine-containing acylacetic acid derivative, method for producing fluorine-containing pyrazolecarboxylic acid ester derivative, and method for producing fluorine-containing pyrazolecarboxylic acid derivative

Family Cites Families (268)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2277479A (en) * 1938-08-13 1942-03-24 Gen Electric Acetoacetic ester-formaldehyde resins
US2230033A (en) * 1939-01-04 1941-01-28 James W Hackett Foot exerciser
US2245567A (en) 1939-06-23 1941-06-17 Eastman Kodak Co Manufacture of unsaturated ketones
US2313501A (en) 1939-08-15 1943-03-09 Eastman Kodak Co Process for preparing methylene dialkyl malonates
US2212506A (en) 1939-08-15 1940-08-27 Eastman Kodak Co Preparation of methylene dialkyl malonates
US2330033A (en) 1939-11-16 1943-09-21 Gen Electric Method of preparing methylene malonic esters
US2403791A (en) 1939-11-16 1946-07-09 Gen Electric Interpolymers of a methylene malonic ester and an unsaturated alkyd resin
US2569767A (en) * 1946-05-27 1951-10-02 L D Caulk Company Dental material and method
US2730457A (en) 1953-06-30 1956-01-10 Ncr Co Pressure responsive record materials
US3042710A (en) 1960-10-03 1962-07-03 Borden Co Ethenoid carbonyl compounds
DE1569968B1 (de) 1960-10-19 1969-11-06 Eastman Kodak Co Verwendung von hochgereinigten monomeren Estern der Methylenmalonsaeure als autopolymerisierbare Klebstoffe
US3197318A (en) 1960-11-07 1965-07-27 Borden Co 2-methylenemalonic acid ester contact adhesive compositions
GB965767A (en) 1960-11-17 1964-08-06 Hoyt Harrison Todd Method of fusing materials to metal surfaces
FR1290837A (fr) 1960-12-23 1962-04-20 Air Liquide Nouveaux polymères anthraquinoniques réducto-oxydables, leurs procédés de préparation et leur application à la fabrication de l'eau oxygénée
GB975733A (en) 1961-12-18 1964-11-18 Ici Ltd Process for preventing haze formation in fermented beverages
US3203915A (en) 1962-07-02 1965-08-31 Dal Mon Research Co Oxygen convertible polymeric compositions
US3221745A (en) 1962-09-12 1965-12-07 Eastman Kodak Co Method of bonding body tissue together using methylenemalonic acid esters
US3427250A (en) 1963-03-25 1969-02-11 Polaroid Corp Microscopic capsules and process for their preparation
US3489663A (en) 1965-10-19 1970-01-13 Owens Illinois Inc Electrolytic polymerization
US3557185A (en) 1967-03-06 1971-01-19 Toa Gosei Chem Ind Stabilized alpha-cyanoacrylate adhesive compositions
US4105688A (en) 1968-05-09 1978-08-08 Lonza, Ltd. Process for the production of malonic acid dinitrile and purification thereof
US3595869A (en) 1968-05-15 1971-07-27 Merck & Co Inc Process for preparing a diastereomer of an optically active ester or amide of (cis-1,2-epoxypropyl)-phosphonic acid
US3591676A (en) 1968-11-01 1971-07-06 Eastman Kodak Co Surgical adhesive compositions
DE2027502C3 (de) 1970-05-29 1980-06-19 Schering Ag, 1000 Berlin Und 4619 Bergkamen Verfahren zur Herstellung von Cyanacrylsäureestern
US3677989A (en) 1970-06-16 1972-07-18 Union Carbide Corp Ethylene/acrylic acid copolymer emulsions
DE2042610C3 (de) 1970-08-27 1979-03-15 Wacker-Chemie Gmbh, 8000 Muenchen Verfahren zur Herstellung von Methylenmalonester
US3940362A (en) 1972-05-25 1976-02-24 Johnson & Johnson Cross-linked cyanoacrylate adhesive compositions
US3975422A (en) 1972-11-21 1976-08-17 Johnson & Johnson Preparation of bis (2-cyanoacrylate)monomers
US3923836A (en) * 1973-07-18 1975-12-02 Smithkline Corp Chroman and chromene compounds
US3973438A (en) 1973-08-21 1976-08-10 Westinghouse Electric Corporation Composition for forming thermo-particulating coating which protects electrical apparatus
US4079058A (en) 1973-08-29 1978-03-14 Dynamit Nobel Ag Process of performing cyclization reactions using benzyl or pyridylamino malonic acid derivatives
CH582655A5 (enExample) 1973-10-18 1976-12-15 Lonza Ag
US3945891A (en) 1974-06-20 1976-03-23 Fmc Corporation Distillation process for purification of triaryl phosphate esters
US3966562A (en) 1974-07-31 1976-06-29 Agency Of Industrial Science & Technology Multi-stage flash distillation plant
US4018656A (en) 1974-09-03 1977-04-19 Bechtel International Corporation Thermal softening and distillation by regenerative method
US4004984A (en) 1975-02-07 1977-01-25 Aktiebolaget Atomenergi Distillation plant
US4148693A (en) 1975-02-26 1979-04-10 Williamson William R Horizontal cylindrical distillation apparatus
US3978422A (en) 1975-02-28 1976-08-31 Alpha Engineering Corporation Broadband automatic gain control amplifier
US3995489A (en) 1975-04-15 1976-12-07 Westinghouse Electric Corporation Malonic acid derivative composition for forming thermoparticulating coating
US4046943A (en) 1975-04-15 1977-09-06 Westinghouse Electric Corporation Malonic acid derivative composition for forming thermoparticulating coating
US4001345A (en) 1975-06-02 1977-01-04 Ppg Industries, Inc. Distillation of methylchloroform
SU614742A3 (ru) 1975-06-02 1978-07-05 Динамит Нобель Аг (Фирма) Способ получени с - с диалкиловых эфиров малоновой кислоты
US4036985A (en) 1975-07-16 1977-07-19 Jose Amato Mono substituted malonic acid diamides and process of preparing them
US4083751A (en) 1975-08-11 1978-04-11 Occidental Petroleum Corporation Continuous feed pyrolysis chamber for decomposing solid waste
DE2647452A1 (de) 1975-11-07 1977-05-18 Ciba Geigy Ag Neue hydroxybenzylmalonsaeure-derivate
US4282067A (en) 1976-04-28 1981-08-04 Jerome Katz Apparatus for high volume distillation of liquids
US4186060A (en) 1976-04-28 1980-01-29 Fogel S J Method and apparatus for high volume distillation of liquids
US4186058A (en) 1976-04-28 1980-01-29 Fogel S J Method and apparatus for high volume distillation of liquids
US4035243A (en) 1976-04-28 1977-07-12 Jerome Katz Method and apparatus for high volume distillation of liquids
US4319964A (en) 1976-04-28 1982-03-16 Jerome Katz Apparatus for high volume distillation of liquids
US4154914A (en) 1976-05-01 1979-05-15 Toyo Seal Kogyo Kabushiki Kaisha (Toyo Seal Industries Co., Ltd.) Process for producing acrylic rubber by copolymerizing acrylic ester and malonic acid derivative having active methylene group
US4224112A (en) 1976-06-11 1980-09-23 Phillips Petroleum Company Recovery of 1,1-dihydroheptafluorobutanol from water by distillation
US4236975A (en) 1976-06-11 1980-12-02 Phillips Petroleum Company Recovery of methyl heptafluorobutyrate from water by distillation
US4229263A (en) 1976-06-11 1980-10-21 Phillips Petroleum Company Recovery of methyl heptafluorobutyrate from methanol by distillation
US4080238A (en) 1976-07-14 1978-03-21 Pratt & Lambert, Inc. One-liquid cold setting adhesive with encapsulated catalyst initiator
US4118422A (en) 1976-08-23 1978-10-03 Texaco Development Corp. Polyols from 2,3-morpholinediones
US4056543A (en) 1976-09-07 1977-11-01 Eastman Kodak Company Process of preparing substituted acrylates
US4160864A (en) 1976-09-07 1979-07-10 Eastman Kodak Company Adhesive compositions comprising methyl allyl methylenemalonate
US4282071A (en) 1977-04-25 1981-08-04 The Dow Chemical Company Anhydrous separation of volatile aluminum chloride complex from an ethylbenzene production stream by distillation
EP0002260B1 (de) 1977-12-02 1982-07-14 Ciba-Geigy Ag Malonsäurederivate von sterisch gehinderten Piperidinen, Verfahren zu ihrer Herstellung und mit ihnen stabilisiertes organisches Material
US4176012A (en) 1978-01-10 1979-11-27 Bryant Jeffrey J Adjacent loop distillation
US4243493A (en) 1978-02-03 1981-01-06 Mannesmannrohren-Werke A.G. Process for transportation and distillation of petroleum with methanol
US4256908A (en) 1978-07-03 1981-03-17 Ube Industries, Ltd. Process for preparing diesters of malonic acid
JPS5647471A (en) 1979-09-28 1981-04-30 Japan Synthetic Rubber Co Ltd Instantaneous adhesive composition
JPS5667383A (en) 1979-11-08 1981-06-06 Mitsui Petrochem Ind Ltd Thixotropic agent
US4440601A (en) 1980-01-28 1984-04-03 Jerome Katz Method and apparatus for high volume fractional distillation of liquids
US4291171A (en) 1980-08-20 1981-09-22 The United States Of America As Represented By The Secretary Of The Navy Esters of 2-fluoro-2,2-dinitroethylmalonate and 2,2-dinitropropylmalonate
DE3105718A1 (de) 1981-02-17 1982-09-02 Hoechst Ag, 6000 Frankfurt Fuer lebensmittel, insbesondere wurstwaren, geeignete rauchdurchlaessige schlauchhuelle mit einer klebenaht und verfahren zu ihrer herstellung
US4329479A (en) 1981-04-07 1982-05-11 Nihon Nohyaku Co., Ltd. Process for producing 1,3-dithiol-2-ylidene malonic acid dialkyl esters
US4450067A (en) 1981-04-30 1984-05-22 Mobil Oil Corporation Distillation-induced extraction process
US4897473A (en) 1981-05-01 1990-01-30 Union Carbide Chemicals And Plastics Company Inc. Homologation of carbonyloxy containing compounds
US4444928A (en) 1981-08-14 1984-04-24 Ciba-Geigy Corporation Polymeric malonic acid derivatives
JPS5867647A (ja) 1981-10-15 1983-04-22 Ube Ind Ltd マロン酸ジエステルの製造法
US4440910A (en) 1982-01-18 1984-04-03 Loctite Corporation Toughened cyanoacrylates containing elastomeric rubbers
GB2115031B (en) 1982-01-29 1985-09-18 Andres Galvez Figari Cast floors
JPS597193A (ja) 1982-07-02 1984-01-14 Shionogi & Co Ltd マロニルメチル基の異性化方法
EP0103233B1 (en) 1982-08-31 1987-11-25 Daikin Kogyo Co., Ltd. A method to trap the enolate ion of the malonic acid or its derivatives
US4411740A (en) 1982-09-20 1983-10-25 Dow Corning Corporation Separation of chlorosilanes by extractive distillation
DE3241512A1 (de) 1982-11-10 1984-05-10 Bayer Ag, 5090 Leverkusen Substituierte malonsaeurediamide, verfahren zu ihrer herstellung und ihre verwendung als schaedlingsbekaempfungsmittel
FR2540739A1 (fr) 1983-02-11 1984-08-17 Elf France Dispositif et installations pour la distillation par evaporation en couches minces, en particulier pour hydrocarbures, et procede de mise en oeuvre de ce dispositif
US4517105A (en) 1983-03-07 1985-05-14 Aluminum Company Of America Metalworking lubricant composition containing a novel substituted malonic acid diester
AT379602B (de) * 1983-07-11 1986-02-10 Vianova Kunstharz Ag Verfahren zur herstellung von vernetzungskomponenten fuer lackbindemittel
US4503074A (en) 1983-08-08 1985-03-05 Merck & Co., Inc. Halogenated geminal diesters
US4767503A (en) 1983-08-29 1988-08-30 Allied Corporation Removal of light impurities from caprolactam by distillation with water
US4560723A (en) 1983-11-14 1985-12-24 Minnesota Mining And Manufacturing Company Cyanoacrylate adhesive composition having sustained toughness
AT380008B (de) 1983-12-23 1986-03-25 Chemie Linz Ag Verfahren zur herstellung von mono- oder biscarbonylverbindungen
DE3400401A1 (de) 1984-01-07 1985-08-22 Bayer Ag, 5090 Leverkusen Substituierte malonsaeurederivate, verfahren zu ihrer herstellung und ihre verwendung als schaedlingsbekaempfungsmittel
US4720543A (en) 1985-06-06 1988-01-19 Georgetown University 1a-7-substituted derivatives of mitomycin and uses thereof
US4613658A (en) 1985-10-15 1986-09-23 University Of Southern Mississippi Vinyl monomers capable of forming side-chain liquid crystalline polymers and the resulting polymers
US4724053A (en) 1985-12-20 1988-02-09 Polaroid Corporation, Patent Dept. Method for the electropolymerization of conductive polymers
CA1222845A (en) * 1986-02-06 1987-06-09 Progressive Chemical Research Ltd. Silicone-sulfone and silicone-fluorocarbon-sulfone gas permeable contact lenses and compositions thereof
US5292937A (en) 1986-03-31 1994-03-08 Rhone-Poulenc Inc. Use of malonic acid derivative compounds for retarding plant growth
JPS62260879A (ja) 1986-05-07 1987-11-13 Matsumoto Seiyaku Kogyo Kk 接着剤組成物
US4783242A (en) 1986-05-22 1988-11-08 The Dow Chemical Company Distillation system and process
IT1196500B (it) 1986-07-16 1988-11-16 Eniricerche Spa Derivati dell'acido malonico e metodi per la loro sintesi
JPS6342135A (ja) 1986-08-08 1988-02-23 Shinkawa Ltd ワイヤボンデイング方法
JPS63159385A (ja) 1986-08-29 1988-07-02 Nippon Nohyaku Co Ltd マロン酸誘導体及びその製法並びにその用途
US5446195A (en) 1986-09-02 1995-08-29 West Point Pepperell Water-soluble active methylenes as formaldehyde scavengers
HU197574B (en) 1986-10-09 1989-04-28 Chinoin Gyogyszer Es Vegyeszet Process for production of derivatives of 3,7-dihydro-3-methil-7-//1,2,4-oxadiasole/-3-il/alkylenil/-1h-purin-2,6-dion and medical compositions containing these substances
US4736056A (en) 1986-12-15 1988-04-05 Smith Oliver W Process for the production of malonic acid derivative compounds
JPH087443B2 (ja) * 1986-12-29 1996-01-29 凸版印刷株式会社 高解像度ポジ型放射線感応性レジスト
FR2611705B1 (fr) 1987-03-05 1989-07-13 Union Pharma Scient Appl Procede de preparation de monesters ou diesters de l'acide endoethano-9, 10 dihydro-9, 10 anthracene bicarboxylique-11, 11, nouveaux monesters ou diesters ainsi prepares et utilisation de ceux-ci pour la preparation de methylenemalonates symetriques ou asymetriques
US4828882A (en) 1987-03-16 1989-05-09 Canadian Patents & Developments Limited Particle encapsulation technique
DE3733552A1 (de) 1987-10-03 1989-04-13 Herberts Gmbh Kathodisch abscheidbares waessriges elektrotauchlack-ueberzugsmittel und dessen verwendung
US5021486A (en) 1989-03-21 1991-06-04 Ciba-Geigy Corporation Hindered amine-substituted malonic acid derivatives of s-triazine
JPH02281013A (ja) 1989-04-24 1990-11-16 Cemedine Co Ltd ジケトン化合物系共重合体
DE3934190A1 (de) 1989-10-13 1991-04-18 Basf Ag Malonsaeurefarbstoffe und deren polykondensationsprodukte
DE4009621A1 (de) 1990-03-26 1991-10-02 Henkel Kgaa (alpha) -cyanacrylatklebstoffzusammensetzungen
US5284987A (en) 1990-06-15 1994-02-08 Amoco Corporation Preparation of a dimethyltetralin in a distillation reactor
US5227027A (en) 1990-08-23 1993-07-13 Topper Robert T High efficiency water distillation apparatus using a heat pump system and process for use thereof
US5064507A (en) 1990-09-27 1991-11-12 Allied-Signal Inc. Distillation process for recovery of high purity phenol
MX9200216A (es) 1991-01-21 1992-08-01 Lonza Ag Procedimiento para la preparacion de anhidrido de acido malonico.
DE4114733A1 (de) 1991-05-06 1992-11-12 Huels Chemische Werke Ag Verfahren zur herstellung von substituierten malonesteraniliden und malonsaeure-monoaniliden
JPH0517723A (ja) 1991-07-10 1993-01-26 Three Bond Co Ltd 接着剤組成物
US5259835A (en) 1991-08-29 1993-11-09 Tri-Point Medical L.P. Wound closure means and method using flowable adhesive
US5391624A (en) 1992-02-10 1995-02-21 S. C. Johnson & Son, Inc. Thermosettable compositions
US5624669A (en) 1993-03-31 1997-04-29 Tri-Point Medical Corporation Method of hemostatic sealing of blood vessels and internal organs
US5328687A (en) 1993-03-31 1994-07-12 Tri-Point Medical L.P. Biocompatible monomer and polymer compositions
US5567761A (en) 1993-05-10 1996-10-22 Guertin Bros. Coatings And Sealants Ltd. Aqueous two-part isocyanate-free curable, polyurethane resin systems
KR970010594B1 (ko) 1993-10-16 1997-06-28 한국과학기술연구원 말론산 유도체의 백금착화합물 및 그 제조방법
AU672337B2 (en) 1993-10-27 1996-09-26 Nippon Paint Co., Ltd. Curable resin composition for coating uses
DE4408248A1 (de) 1994-03-11 1995-09-14 Hoechst Ag Physiologisch verträgliche und physiologisch abbaubare Kohlenhydrat-Mimetika, ein Verfahren zur Herstellung und ihre Verwendung
EP0671409A3 (de) 1994-03-11 1996-06-12 Hoechst Ag Malonsäurederivate mit antiadhäsiven Eigenschaften.
CA2193968A1 (en) 1994-06-28 1996-01-11 Jeffrey G. Clark Ph-modified biocompatible monomer and polymer compositions
US5550172A (en) 1995-02-07 1996-08-27 Ethicon, Inc. Utilization of biocompatible adhesive/sealant materials for securing surgical devices
DE19508049C2 (de) 1995-02-23 1997-02-06 Schering Ag Verwendung von Methylenmalondiesterderivaten zur Herstellung von gasenthaltenden Mikropartikeln
JPH08231564A (ja) * 1995-02-28 1996-09-10 Nippon Shokubai Co Ltd リン酸エステルおよびその製造方法並びにリン酸エステル重合体
US5614650A (en) 1995-03-07 1997-03-25 Sandler; Stanley R. Zirconium compounds of sulfonic acids
US5928611A (en) 1995-06-07 1999-07-27 Closure Medical Corporation Impregnated applicator tip
DE19541213A1 (de) 1995-11-04 1997-05-07 Rwe Dea Ag Verfahren zur chemischen Umsetzung von Stoffen in einer Reaktionskolonne
JPH09258448A (ja) * 1996-03-19 1997-10-03 Fujitsu Ltd レジスト組成物及びそれを用いた半導体装置製造方法
EP0808822B1 (en) 1996-05-22 2001-10-04 Nippon Paint Co., Ltd. Method for preparing malonate group-containing acrylate monomers
DE19623142A1 (de) 1996-06-10 1997-12-11 Huels Chemische Werke Ag Enantiomerenangereicherte, durch einen tertiären Kohlenwasserstoffrest substituierte Malonsäuremonoester sowie deren Herstellung
DE19629372A1 (de) 1996-07-20 1998-01-22 Degussa Verfahren zur Herstellung von Malonsäure oder einem Salz derselben
FR2755136B1 (fr) 1996-10-25 1999-01-22 Virsol Procede de preparation de nanoparticules de methylidene malonate, nanoparticules contenant eventuellement une ou plusieurs molecules biologiquement actives et compositions pharmaceutiques les contenant
DE19704449A1 (de) 1997-02-06 1998-08-13 Huels Chemische Werke Ag Verfahren zur Herstellung von Malonsäure und Alkylmalonsäuren
US6238896B1 (en) 1997-02-20 2001-05-29 Mitsubishi Rayon Co., Ltd. Process for producing malonic acid derivatives
DE19711762A1 (de) 1997-03-21 1998-09-24 Huels Chemische Werke Ag Verfahren zur Herstellung von Bishydroxymethylverbindungen
DE19724074C2 (de) 1997-06-07 2000-01-13 Metallgesellschaft Ag Verfahren zur Hochtemperatur-Kurzzeit-Destillation von Rückstandsölen
WO1999001420A1 (en) 1997-07-03 1999-01-14 Taito Co., Ltd. Process for the preparation of 2-aminomalonic acid derivatives and intermediates used in the process
AU8502798A (en) 1997-07-21 1999-02-10 Aguila Technologies, Inc. Semiconductor flip-chip package and method for the fabrication thereof
BR9704357A (pt) 1997-08-13 1999-05-11 Trikem Sa Processo para produção de acido malônico e de ésteres de acido malônico
US6353268B1 (en) 1997-08-22 2002-03-05 Micron Technology, Inc. Semiconductor die attachment method and apparatus
FR2774096B1 (fr) 1998-01-29 2000-04-07 Virsol Nouveaux copolymeres tensioactifs a base de methylidene malonate
US6291703B1 (en) 1998-02-09 2001-09-18 Ciba Specialty Chemicals Corporation Preparation of substituted hydroxyhydrocinnamate esters by continuous transesterification using reactive distillation
FR2775284B1 (fr) * 1998-02-20 2000-04-21 Rhodia Chimie Sa Procede de preparation de composes cetoniques aromatiques
WO1999046619A1 (en) 1998-03-09 1999-09-16 Corning Incorporated Optical waveguide having non absorbing cladding region
FR2778100B1 (fr) 1998-04-29 2001-05-04 Virsol Nouvelles microspheres a base de poly(methylidene malonate), leur procede de preparation et compositions pharmaceutiques les contenant
CN1299293A (zh) * 1998-04-30 2001-06-13 科乐医药有限公司 具有聚合试剂和/或生物活性物质的黏合剂涂药器
US6512023B1 (en) 1998-06-18 2003-01-28 Closure Medical Corporation Stabilized monomer adhesive compositions
JP2000019936A (ja) 1998-07-06 2000-01-21 Central Glass Co Ltd ホログラムの作製方法およびその装置
US6632518B1 (en) 1998-10-14 2003-10-14 E. I. Du Pont De Nemours And Company Fluoropolymer film structures and laminates produced therefrom
CN1156505C (zh) 1998-12-07 2004-07-07 拜尔公司 含有分散的反应性或二次交联聚氨酯的水性聚氨酯分散体的凝聚方法和用该方法制备的产品及其用途
WO2000040571A1 (en) 1999-01-02 2000-07-13 Aventis Pharma Deutschland Gmbh Novel malonic acid derivatives, processes for their preparation, their use and pharmaceutical compositions containing them (inhibition of factor xa activity)
JP2000199936A (ja) * 1999-01-06 2000-07-18 Konica Corp 熱現像感光材料
FR2788516B1 (fr) 1999-01-14 2001-04-06 Virsol Procede de preparation de polymere de methylidene malonate
FR2789314B1 (fr) 1999-02-09 2001-04-27 Virsol Materiau de suture de plaies a base de methylidene malonate
US6197482B1 (en) 1999-05-14 2001-03-06 Eastman Kodak Company Polymer overcoat for imaging elements
IL146775A0 (en) 1999-05-27 2002-07-25 Tno Method for the purification of a liquid by membrane distillation, in particular for the production of desalinated water from seawater or brackish water or process water
US6210474B1 (en) 1999-06-04 2001-04-03 Eastman Kodak Company Process for preparing an ink jet ink
US6225038B1 (en) 1999-11-04 2001-05-01 Eastman Kodak Company Thermally processable imaging element
US6245933B1 (en) 1999-11-19 2001-06-12 Closure Medical Corporation Transesterification method for making cyanoacrylates
DE19959587B4 (de) 1999-12-10 2006-08-24 Lurgi Lentjes Ag Verfahren zur schonenden Kurzzeit-Destillation von Rückstandsölen
US6183593B1 (en) 1999-12-23 2001-02-06 Closure Medical Corporation 1,1-disubstituted ethylene adhesive compositions containing polydimethylsiloxane
AUPQ540200A0 (en) 2000-02-02 2000-02-24 Aquadyne Incorporated Water distillation systems
EP1254105A1 (de) 2000-02-10 2002-11-06 Lonza AG Verfahren zur herstellung von alkoxymalonsäuredinitrilen
US6541656B2 (en) 2000-02-10 2003-04-01 Nippon Shokubai Company, Ltd. Process for producing α, β-unsaturated carboxylic acid esters and catalyst for use in such process
EP1127884A1 (en) 2000-02-26 2001-08-29 Aventis Pharma Deutschland GmbH Novel malonic acid derivatives, processes for their preparation, their use as inhibitor of factor XA activity and pharmaceutical compositions containing them
WO2002006368A2 (en) 2000-07-14 2002-01-24 Metabolix, Inc. Polyurethanes obtained from hydroxyalkanoates and isocyanates
US20040005314A1 (en) 2001-07-27 2004-01-08 Enrique Escandon Apo-2l receptor agonist and cpt-11 synergism
FR2812551B1 (fr) 2000-08-07 2003-03-28 Virsol Forme pharmaceutique comprenant un materiau support a base de methylidene malonate et un facteur de regulation cellulaire
ES2233544T3 (es) 2000-10-17 2005-06-16 Societe De Technologie Michelin Procedimiento de preparacion de un elastomero dienico por polimerizacion anionica.
US6545097B2 (en) 2000-12-12 2003-04-08 Scimed Life Systems, Inc. Drug delivery compositions and medical devices containing block copolymer
US20020151629A1 (en) 2001-02-08 2002-10-17 Buffkin Halbert C. Protective coating
US7450290B2 (en) 2001-06-25 2008-11-11 University Of Washington Electropolymerization of enhanced electrochromic (EC) polymer film
JP3976663B2 (ja) 2001-11-01 2007-09-19 横浜ゴム株式会社 １液湿気硬化型ウレタン樹脂組成物
US6896838B2 (en) 2001-11-21 2005-05-24 Closure Medical Corporation Halogenated polymeric containers for 1, 1-disubstituted monomer compositions
US6767980B2 (en) 2002-04-19 2004-07-27 Nippon Shokubai Co., Ltd. Reactive diluent and curable resin composition
US6794515B2 (en) 2002-05-15 2004-09-21 Genzyme Corporation Synthesis of 2-alkylcysteine via substituted thiazoline amide
US7629416B2 (en) 2002-08-12 2009-12-08 Exxonmobil Chemical Patents Inc. Plasticized polyolefin compositions
WO2004035540A1 (ja) 2002-10-18 2004-04-29 Meiji Seika Kaisha, Ltd. マロン酸モノエステルおよびその製造方法
US7056540B2 (en) 2002-10-29 2006-06-06 Council Of Scientific And Industrial Research Enzymatic process for the preparation of optically active alcohols from ketones using tuberous root Daucus carota
US6826341B2 (en) 2002-11-04 2004-11-30 Fitel Usa Corp. Systems and methods for reducing splice loss in optical fibers
WO2004076601A1 (ja) 2002-12-26 2004-09-10 Matsushita Electric Industrial Co., Ltd. 金属加工用水溶性潤滑剤、その使用に適した金属加工方法及び金属加工装置
DE10308504A1 (de) * 2003-02-26 2004-09-09 Basf Ag Enzymatische Herstellung von (Meth)acrylsäureestern
EP1475367B1 (de) 2003-05-08 2010-07-07 Bayer MaterialScience AG Verfahren zur Destillation eines Gemisches isomerer Diisocyanatodiphenylmethane
US6767857B1 (en) 2003-05-29 2004-07-27 Fina Technology, Inc. Process for forming a Ziegler-Natta catalyst system having a controlled morphology
GB0317268D0 (en) 2003-07-23 2003-08-27 Viral Asa A Compounds
WO2005012427A1 (ja) 2003-08-04 2005-02-10 Zeon Corporation 重合性組成物及びそれを用いてなる成形体
US7226957B1 (en) 2003-11-03 2007-06-05 University Of Iowa Research Foundation Method for producing polymers with controlled molecular weight and end group functionality using photopolymerization in microemulsions
JP2005170803A (ja) 2003-12-08 2005-06-30 Daicel Chem Ind Ltd 新規なマロン酸モノメチル誘導体とその製造法
US20050228074A1 (en) 2004-04-05 2005-10-13 Bridgestone Corporation Amphiphilic polymer micelles and use thereof
US7170188B2 (en) 2004-06-30 2007-01-30 Intel Corporation Package stress management
US7305850B2 (en) 2004-07-23 2007-12-11 Velocys, Inc. Distillation process using microchannel technology
CA2574113C (en) 2004-07-23 2014-02-18 Anna Lee Tonkovich Distillation process using microchannel technology
US8119214B2 (en) 2004-09-01 2012-02-21 Appleton Papers Inc Encapsulated cure systems
US9598527B2 (en) 2004-09-01 2017-03-21 Ppg Industries Ohio, Inc. Polyurethanes, articles and coatings prepared therefrom and methods of making the same
US7371804B2 (en) 2004-09-07 2008-05-13 Ophthonix, Inc. Monomers and polymers for optical elements
US8075906B2 (en) 2005-02-01 2011-12-13 Boston Scientific Scimed, Inc. Medical devices having polymeric regions with copolymers containing hydrocarbon and heteroatom-containing monomeric species
US7603889B2 (en) 2005-04-01 2009-10-20 MEAS France System for monitoring and controlling unit operations that include distillation
WO2007018736A2 (en) 2005-07-22 2007-02-15 Appleton Papers Inc. Encapsulated structural adhesive
US7919543B2 (en) 2005-08-16 2011-04-05 Electronics For Imaging, Inc. Inkjet inks, methods for applying inkjet ink, and articles printed with inkjet inks
DE602006012593D1 (de) 2005-08-24 2010-04-15 Nippon Catalytic Chem Ind Durch Radiation vernetzbare Zusammensetzungen und daraus hergestelte vernetzte Produkte
US7771567B2 (en) 2005-09-02 2010-08-10 Rives Michael L Salt water distillation system
US20070092483A1 (en) 2005-10-21 2007-04-26 Pollock Polymer Group Surgical adhesive compostion and process for enhanced tissue closure and healing
US7626477B2 (en) 2005-11-28 2009-12-01 General Electric Company Cold mass cryogenic cooling circuit inlet path avoidance of direct conductive thermal engagement with substantially conductive coupler for superconducting magnet
US8113895B2 (en) 2005-12-16 2012-02-14 Yoshihiro Watanabe Article such as surfboard and production method thereof
CA2644172A1 (en) 2006-04-07 2007-10-18 E.I. Du Pont De Nemours And Company Processes for chemical synthesis of lipochitooligosaccharides
WO2007120630A2 (en) 2006-04-10 2007-10-25 Abm Associates Llc Activated anaerobic adhesive and use thereof
WO2007139116A1 (ja) 2006-05-29 2007-12-06 Denki Kagaku Kogyo Kabushiki Kaisha クロス共重合体の製造方法、得られるクロス共重合体、及びその用途
EP2452962B1 (en) 2006-08-16 2017-03-22 Asahi Kasei Kabushiki Kaisha Block copolymer or hydrogenated product thereof
US8332435B2 (en) 2006-10-03 2012-12-11 Salesforce.Com, Inc. Method and system for customizing a user interface to an on-demand database service
FR2907131B1 (fr) 2006-10-12 2008-11-21 Commissariat Energie Atomique Procede de formation de films organiques sur des surfaces conductrices ou semi-conductrices de l'electricite a partir de solutions aqueuses en deux etapes
EP1927477B1 (en) 2006-11-30 2009-03-18 FUJIFILM Corporation Ink composition for inkjet-recording and method for inkjet-recording
JP2008174494A (ja) 2007-01-19 2008-07-31 Nippon Shokubai Co Ltd メチレンマロン酸組成物およびその安定化方法
JP2008189776A (ja) 2007-02-02 2008-08-21 Fujifilm Corp 活性放射線硬化型重合性組成物、インク組成物、インクジェット記録方法、印刷物、平版印刷版の作製方法、及び平版印刷版
US8110251B2 (en) 2007-02-06 2012-02-07 Glumetrics, Inc. Method for polymerizing a monomer solution within a cavity to generate a smooth polymer surface
JP5243072B2 (ja) 2007-03-30 2013-07-24 富士フイルム株式会社 インク組成物、並びに、それを用いた画像記録方法及び画像記録物
US8168213B2 (en) 2007-05-15 2012-05-01 Boston Scientific Scimed, Inc. Medical devices having coating with improved adhesion
US7742670B2 (en) 2007-10-01 2010-06-22 Corning Cable Systems Llc Index-matching gel for nanostructure optical fibers and mechanical splice assembly and connector using same
KR20090064862A (ko) 2007-12-17 2009-06-22 광주과학기술원 피리딘을 기능성 그룹으로 함유한 스티렌 유도체의 음이온중합 방법
US8138610B2 (en) 2008-02-08 2012-03-20 Qimonda Ag Multi-chip package with interconnected stacked chips
JP2009192309A (ja) 2008-02-13 2009-08-27 Shinko Electric Ind Co Ltd 半導体検査装置
KR101215459B1 (ko) 2008-03-27 2012-12-26 도쿄 프린팅 잉크 엠에프지. 캄파니 리미티드 에칭 레지스트용 잉크젯 잉크 조성물
US8318060B2 (en) 2008-07-22 2012-11-27 University Of New Hampshire Microencapsulation of amines
GB2463065B (en) * 2008-09-01 2012-11-07 Loctite R & D Ltd Transferable curable non-liquid film on a release substrate
EP2344207B1 (en) 2008-09-22 2013-12-25 Boston Scientific Neuromodulation Corporation Implantable or insertable medical devices
DE102009000861A1 (de) 2009-02-13 2010-08-19 Henkel Ag & Co. Kgaa Verfahren zur Herstellung von Cyanacrylsäureestern
US8106234B2 (en) 2009-05-07 2012-01-31 OptMed, Inc Methylidene malonate process
US7829738B1 (en) 2009-05-19 2010-11-09 Nalco Company Production of N,N-dialklylaminoethyl (meth)acrylates
SG176270A1 (en) 2009-05-29 2012-01-30 Jx Nippon Oil & Energy Corp Isobutylene-based polymer and method for producing same
DE102009027545A1 (de) 2009-07-08 2011-02-03 Henkel Ag & Co. Kgaa Verfahren zur Herstellung von Cyanacrylsäureestern in Gegenwart von Übergangsmetall-Katalysatoren
JP5671302B2 (ja) 2009-11-10 2015-02-18 富士フイルム株式会社 インプリント用硬化性組成物、パターン形成方法およびパターン
JPWO2011070739A1 (ja) 2009-12-07 2013-04-22 住友ベークライト株式会社 半導体封止用エポキシ樹脂組成物、その硬化体及び半導体装置
JP2011122005A (ja) 2009-12-08 2011-06-23 Sony Corp 反射防止フィルム及びその製造方法、並びに紫外線硬化性樹脂材料組成物塗液
EP3195858B1 (en) 2010-04-03 2019-08-07 Praful Doshi Medical devices including medicaments and methods of making and using same
EP2585422B1 (en) 2010-06-23 2018-01-10 Total Research & Technology Feluy Dehydration of alcohols on poisoned acidic catalysts
US8554938B2 (en) 2010-08-31 2013-10-08 Millind Mittal Web browser proxy-client video system and method
CN105949358A (zh) 2010-10-20 2016-09-21 瑟拉斯公司 基本不含杂质的亚甲基丙二酸酯的合成
WO2013059479A2 (en) 2011-10-19 2013-04-25 Bioformix Inc. Methylene beta-diketone monomers, methods for making methylene beta-diketone monomers, polymerizable compositions and products formed therefrom
US9249265B1 (en) 2014-09-08 2016-02-02 Sirrus, Inc. Emulsion polymers including one or more 1,1-disubstituted alkene compounds, emulsion methods, and polymer compositions
US9505943B2 (en) 2010-12-20 2016-11-29 Dsm Ip Assets B.V. Aqueous bio-renewable vinyl polymer composition
US20130019520A1 (en) 2011-02-02 2013-01-24 Brown University Methods of Making Fatty Acids and Fatty Acid Alkyl Esters
CN102901754A (zh) 2011-07-27 2013-01-30 中国科学院电子学研究所 基于电聚合分子印迹技术的双参数复合微传感器及制备法
EP2831185B1 (en) 2012-03-30 2019-09-25 Sirrus, Inc. Ink and coating formulations and polymerizable systems for producing the same
CA2869112A1 (en) 2012-03-30 2013-10-03 Bioformix Inc. Composite and laminate articles and polymerizable systems for producing the same
US9181365B2 (en) 2012-03-30 2015-11-10 Sirrus, Inc. Methods for activating polymerizable compositions, polymerizable systems, and products formed thereby
US10047192B2 (en) 2012-06-01 2018-08-14 Sirrus, Inc. Optical material and articles formed therefrom
WO2013184255A1 (en) 2012-06-04 2013-12-12 Biosynthetic Technologies, Llc Processes for preparing estolide base oils and lubricants that include transesterification
EP2909364B1 (en) 2012-10-19 2019-09-25 The Colorado State University Research Foundation Electropolymerization of a coating onto an electrode material
EP2920231B1 (en) 2012-11-16 2020-05-06 Sirrus, Inc. Plastics bonding systems and methods
CN105164797B (zh) 2012-11-30 2019-04-19 瑟拉斯公司 用于电子应用的复合组合物
WO2014110388A1 (en) 2013-01-11 2014-07-17 Bioformix Inc. Method to obtain methylene malonate via bis(hydroxymethyl) malonate pathway
US9334430B1 (en) 2015-05-29 2016-05-10 Sirrus, Inc. Encapsulated polymerization initiators, polymerization systems and methods using the same
US9217098B1 (en) 2015-06-01 2015-12-22 Sirrus, Inc. Electroinitiated polymerization of compositions having a 1,1-disubstituted alkene compound
DE102017204525A1 (de) 2016-03-23 2017-09-28 Basf Se Verbundfolienlaminate für flexible Verpackungen
EP3445830A1 (en) 2016-04-21 2019-02-27 Zephyros Inc. Malonates and derivatives for in-situ films
US20180010014A1 (en) 2016-07-11 2018-01-11 Zephyros, Inc. Compositions for adhesive applications
US11078376B2 (en) 2016-07-26 2021-08-03 Ppg Industries Ohio, Inc. Polyurethane coating compositions containing 1,1-di-activated vinyl compounds and related coatings and processes
WO2018022810A1 (en) 2016-07-26 2018-02-01 Ppg Industries Ohio, Inc. Curable compositions containing 1,1-di-activated vinyl compounds and related coatings and processes
CN109642098B (zh) 2016-07-26 2022-02-11 Ppg工业俄亥俄公司 包含1,1-二活化的乙烯基化合物的可电沉积的涂料组合物
ES2932659T3 (es) 2016-07-26 2023-01-23 Ppg Ind Ohio Inc Composiciones curables multicapa que contienen productos de compuestos vinílicos 1,1-diactivados y procesos relacionados
CN109641237B (zh) 2016-07-26 2021-11-30 Ppg工业俄亥俄公司 含有1,1-二-活化的乙烯基化合物的酸催化的可固化涂料组合物和相关的涂料和方法
WO2018022785A1 (en) 2016-07-26 2018-02-01 Ppg Industries Ohio, Inc. Three-dimensional printing processes using 1,1-di-activated vinyl compounds
EP3491057B1 (en) 2016-07-26 2022-11-09 PPG Industries Ohio, Inc. Particles having surfaces functionalized with 1,1-di-activated vinyl compounds
WO2018053503A1 (en) 2016-09-19 2018-03-22 Zephyros, Inc. Malonate and cyanoacrylate adhesives for joining dissimilar materials
US11999866B2 (en) 2016-09-19 2024-06-04 Zephyros, Inc. Polymalonate and cyanoacrylate based surface concrete sealers
JP2019537527A (ja) 2016-11-09 2019-12-26 ビーエーエスエフ ソシエタス・ヨーロピアＢａｓｆ Ｓｅ ポリウレタン−ビニルハイブリッドポリマー、それらの製造方法およびそれらの使用

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB432628A (en) * 1933-12-23 1935-07-23 John David Kendall Improvements in or relating to the production of compounds containing an ethylenic linkage, or a polymethine chain
US4049698A (en) * 1976-08-05 1977-09-20 Eastman Kodak Company Process for producing methylene malonic esters
US4728701A (en) * 1983-09-19 1988-03-01 Jarvis Marvin A Process for the polymerization of acrylates
US20040220060A1 (en) * 2000-06-22 2004-11-04 Bartley Stuart L Acylatign agents and dispersants for lubricating oil and fuels
US7659423B1 (en) * 2006-04-18 2010-02-09 Loctite (R&D) Limited Method of preparing electron deficient olefins in polar solvents
US20110015406A1 (en) * 2008-03-18 2011-01-20 Mitsui Chemicals Agro, Inc. Method for producing fluorine-containing acylacetic acid derivative, method for producing fluorine-containing pyrazolecarboxylic acid ester derivative, and method for producing fluorine-containing pyrazolecarboxylic acid derivative
US20100286433A1 (en) * 2009-05-07 2010-11-11 Malofsky Bernard M Methylidene malonate process

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
REDDY ET AL.: "An easy-to-use heterogeneous promoted zirconia catalyst for Knoevenagel condensation in liquid phase under solvent-free conditions", JOURNAL OF MOLECULAR CATALYSIS A: CHEMICAL, vol. 258, 2006, pages 302 - 307, XP005652133 *
See also references of EP2768872A4 *

Cited By (53)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10414839B2 (en) 2010-10-20 2019-09-17 Sirrus, Inc. Polymers including a methylene beta-ketoester and products formed therefrom
US9828324B2 (en) 2010-10-20 2017-11-28 Sirrus, Inc. Methylene beta-diketone monomers, methods for making methylene beta-diketone monomers, polymerizable compositions and products formed therefrom
US9512058B2 (en) 2011-10-19 2016-12-06 Sirrus Inc. Multifunctional monomers, methods for making multifunctional monomers, polymerizable compostions and products formed thereform
US9969822B2 (en) 2011-10-19 2018-05-15 Sirrus, Inc. Multifunctional monomers, methods for making multifunctional monomers, polymerizable compositions and products formed therefrom
US9527795B2 (en) 2011-10-19 2016-12-27 Sirrus, Inc. Methylene beta-ketoester monomers, methods for making methylene beta-ketoester monomers, polymerizable compositions and products formed therefrom
EP2831185A4 (en) * 2012-03-30 2016-01-27 Sirrus Inc INK AND COATING FORMULATIONS AND POLYMERIZABLE SYSTEMS FOR THE PRODUCTION OF SAID FORMULATIONS
EP3848402A1 (en) * 2012-03-30 2021-07-14 Sirrus, Inc. Ink and coating formulations and polymerizable systems for producing the same
US10913875B2 (en) 2012-03-30 2021-02-09 Sirrus, Inc. Composite and laminate articles and polymerizable systems for producing the same
US9523008B2 (en) 2012-03-30 2016-12-20 Sirrus, Inc. Ink coating formulations and polymerizable systems for producing the same
US10047192B2 (en) 2012-06-01 2018-08-14 Sirrus, Inc. Optical material and articles formed therefrom
US9752059B2 (en) 2012-11-16 2017-09-05 Sirrus, Inc. Plastics bonding systems and methods
US10607910B2 (en) 2012-11-30 2020-03-31 Sirrus, Inc. Composite compositions for electronics applications
US9522381B2 (en) 2013-01-11 2016-12-20 Sirrus, Inc. Method to obtain methylene malonate via bis(hydroxymethyl) malonate pathway
US10086355B2 (en) 2013-01-11 2018-10-02 Sirrus, Inc. Method to obtain methylene malonate via bis(hydroxymethyl) malonate pathway
US9969819B2 (en) 2014-09-08 2018-05-15 Sirrus, Inc. Pressure sensitive adhesive including a 1,1-disubstituted alkene compound
US9315597B2 (en) 2014-09-08 2016-04-19 Sirrus, Inc. Compositions containing 1,1-disubstituted alkene compounds for preparing polymers having enhanced glass transition temperatures
US9249265B1 (en) 2014-09-08 2016-02-02 Sirrus, Inc. Emulsion polymers including one or more 1,1-disubstituted alkene compounds, emulsion methods, and polymer compositions
US11021617B2 (en) 2014-09-08 2021-06-01 Sirrus, Inc. Polymers including one or more 1,1-disubstituted alkene compounds and polymer compositions thereof
US9676875B2 (en) 2014-09-08 2017-06-13 Sirrus, Inc. Solution polymers including one or more 1,1-disubstituted alkene compounds, solution polymerization methods, and polymer compositions
US10308802B2 (en) 2014-09-08 2019-06-04 Sirrus, Inc. Polymers including one or more 1,1-disubstituted alkene compounds and polymer compositions thereof
US9790295B2 (en) 2014-09-08 2017-10-17 Sirrus, Inc. Compositions containing 1,1-disubstituted alkene compounds for preparing polymers having enhanced glass transition temperatures
US9637564B2 (en) 2014-09-08 2017-05-02 Sirrus, Inc. Emulsion polymers including one or more 1,1-disubstituted alkene compounds, emulsion methods, and polymer compositions
US9890227B1 (en) 2014-09-08 2018-02-13 Sirrus, Inc. Compositions containing 1,1-di-substituted alkene compounds for preparing polymers having enhanced glass transition temperatures
US10184073B2 (en) 2014-09-08 2019-01-22 Sirrus, Inc. Emulsion including polymers containing a 1,1-disubstituted alkene compound, adhesives, coatings, and methods thereof
US10167348B2 (en) 2014-09-08 2019-01-01 Sirrus, Inc. Solution polymers formed from methylene malonate monomers, polymerization, and solution polymer products
US10519257B2 (en) 2014-09-08 2019-12-31 Sirrus, Inc. Compositions containing 1,1-di-carbonyl-substituted alkene compounds for preparing polymers having enhanced glass transition temperatures
EP3789408A1 (en) 2014-09-08 2021-03-10 Sirrus, Inc. Solution polymers including one or more 1,1-disubstituted alkene compounds, solution polymerization methods, and polymer compositions
WO2016040014A1 (en) 2014-09-08 2016-03-17 Sirrus, Inc. Solution polymers including one or more 1,1-disubstituted alkene compounds, solution polymerization methods, and polymer compositions
US10081685B2 (en) 2014-09-08 2018-09-25 Sirrus, Inc. Emulson polymers including one or more 1,1-disubstituted alkene compounds, emulson methods, and polymer compositions
US9416091B1 (en) 2015-02-04 2016-08-16 Sirrus, Inc. Catalytic transesterification of ester compounds with groups reactive under transesterification conditions
US9938223B2 (en) 2015-02-04 2018-04-10 Sirrus, Inc. Catalytic transesterification of ester compounds with groups reactive under transesterification conditions
US10501400B2 (en) 2015-02-04 2019-12-10 Sirrus, Inc. Heterogeneous catalytic transesterification of ester compounds with groups reactive under transesterification conditions
US10087272B2 (en) 2015-05-29 2018-10-02 Sirrus, Inc. Encapsulated polymerization initiators, polymerization systems and methods using the same
US9683147B2 (en) 2015-05-29 2017-06-20 Sirrus, Inc. Encapsulated polymerization initiators, polymerization systems and methods using the same
US9617354B2 (en) 2015-06-01 2017-04-11 Sirrus, Inc. Electroinitiated polymerization of compositions having a 1,1-disubstituted alkene compound
DE102017204525A1 (de) 2016-03-23 2017-09-28 Basf Se Verbundfolienlaminate für flexible Verpackungen
US9518001B1 (en) 2016-05-13 2016-12-13 Sirrus, Inc. High purity 1,1-dicarbonyl substituted-1-alkenes and methods for their preparation
US9617377B1 (en) 2016-06-03 2017-04-11 Sirrus, Inc. Polyester macromers containing 1,1-dicarbonyl-substituted 1 alkenes
US9567475B1 (en) 2016-06-03 2017-02-14 Sirrus, Inc. Coatings containing polyester macromers containing 1,1-dicarbonyl-substituted 1 alkenes
US10428177B2 (en) 2016-06-03 2019-10-01 Sirrus, Inc. Water absorbing or water soluble polymers, intermediate compounds, and methods thereof
US10196481B2 (en) 2016-06-03 2019-02-05 Sirrus, Inc. Polymer and other compounds functionalized with terminal 1,1-disubstituted alkene monomer(s) and methods thereof
US10150886B2 (en) 2016-06-03 2018-12-11 Sirrus, Inc. Coatings containing polyester macromers containing 1,1-dicarbonyl-substituted 1 alkenes
US9718989B1 (en) 2016-06-03 2017-08-01 Sirrus, Inc. Coatings containing polyester macromers containing 1,1-dicarbonyl-substituted 1 alkenes
US10087283B2 (en) 2016-06-03 2018-10-02 Sirrus, Inc. Polyester macromers containing 1,1-dicarbonyl-substituted 1 alkenes
US9745413B1 (en) 2016-06-03 2017-08-29 Sirrus, Inc. Polyester macromers containing 1,1-dicarbonyl-substituted 1 alkenes
US10894856B2 (en) 2016-11-09 2021-01-19 Basf Se Polyurethane-vinyl hybrid polymers, methods of making them and their use
WO2018086860A1 (en) 2016-11-09 2018-05-17 Basf Se Polyurethane-vinyl hybrid polymers, methods of making them and their use
WO2019137853A1 (en) 2018-01-09 2019-07-18 Basf Se Compositions comprising polymerizable vinyl compounds, inorganic or organic fillers and their use
WO2020123581A1 (en) 2018-12-11 2020-06-18 Sirrus, Inc. Emulsion polymers of 1,1-dicarbonyl 1-alkenes of controlled particle size
WO2020123579A1 (en) 2018-12-11 2020-06-18 Sirrus, Inc. Polymerization of 1,1-dicarbonyl 1-alkenes
DE102019219214A1 (de) 2018-12-17 2020-06-18 Basf Se Zusammensetzungen, die multifunktionelle Vinylverbindungen in Miniemulsion umfassen, und ihre Verwendung als Vernetzer für Polymere
CN110903194A (zh) * 2019-12-11 2020-03-24 南京恒道医药科技有限公司 连续制备伏立康唑中间体2-氟-3-氧戊酸乙酯的方法
CN110903194B (zh) * 2019-12-11 2022-02-25 南京恒道医药科技有限公司 连续制备伏立康唑中间体2-氟-3-氧戊酸乙酯的方法

Also Published As

Publication number Publication date
EP2768917A4 (en) 2016-10-05
WO2013059473A2 (en) 2013-04-25
JP2014532625A (ja) 2014-12-08
WO2013059479A3 (en) 2013-07-11
US20170050914A1 (en) 2017-02-23
US9221739B2 (en) 2015-12-29
US20140329980A1 (en) 2014-11-06
MX2014004780A (es) 2015-03-20
CA2853068A1 (en) 2013-04-25
US20180327525A1 (en) 2018-11-15
MX2014004782A (es) 2015-03-20
EP3293216A1 (en) 2018-03-14
JP2014534969A (ja) 2014-12-25
MX370256B (es) 2019-12-09
US9512058B2 (en) 2016-12-06
MX360463B (es) 2018-11-05
MX2014004781A (es) 2015-03-20
US20140275400A1 (en) 2014-09-18
US20140288230A1 (en) 2014-09-25
EP2768897A2 (en) 2014-08-27
CA2853079A1 (en) 2013-05-10
JP6267643B2 (ja) 2018-01-24
EP2768872A1 (en) 2014-08-27
EP3517523A1 (en) 2019-07-31
MX360462B (es) 2018-11-05
EP2768897B1 (en) 2019-01-23
EP2768917A2 (en) 2014-08-27
EP2768897A4 (en) 2015-08-12
EP2768872B1 (en) 2017-11-22
CA2853073A1 (en) 2013-04-25
US10611861B2 (en) 2020-04-07
US9527795B2 (en) 2016-12-27
EP3339301A3 (en) 2018-08-08
WO2013059473A3 (en) 2015-06-25
US20170073438A1 (en) 2017-03-16
EP2768917B1 (en) 2018-12-05
US10604601B2 (en) 2020-03-31
EP2768872A4 (en) 2015-08-26
JP2015517973A (ja) 2015-06-25
US9969822B2 (en) 2018-05-15
EP3339301A2 (en) 2018-06-27
US20180346615A1 (en) 2018-12-06
WO2013059479A2 (en) 2013-04-25

Similar Documents

Publication Publication Date Title
EP2768872B1 (en) Methods for making methylene beta-ketoester monomers
EP2630116B1 (en) Synthesis of methylene malonates using rapid recovery in the presence of a heat transfer agent
US9828324B2 (en) Methylene beta-diketone monomers, methods for making methylene beta-diketone monomers, polymerizable compositions and products formed therefrom
US10414839B2 (en) Polymers including a methylene beta-ketoester and products formed therefrom

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12846728

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 14352406

Country of ref document: US

ENP Entry into the national phase

Ref document number: 2014537249

Country of ref document: JP

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: MX/A/2014/004781

Country of ref document: MX

ENP Entry into the national phase

Ref document number: 2853079

Country of ref document: CA

NENP Non-entry into the national phase

Ref country code: DE

REEP Request for entry into the european phase

Ref document number: 2012846728

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 2012846728

Country of ref document: EP