WO2004050972A1 - 立体織物およびその製造方法 - Google Patents
立体織物およびその製造方法 Download PDFInfo
- Publication number
- WO2004050972A1 WO2004050972A1 PCT/JP2003/015345 JP0315345W WO2004050972A1 WO 2004050972 A1 WO2004050972 A1 WO 2004050972A1 JP 0315345 W JP0315345 W JP 0315345W WO 2004050972 A1 WO2004050972 A1 WO 2004050972A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- yarn
- surface layer
- woven fabric
- dimensional
- Prior art date
Abstract
Description
Claims