WO2004013925A1 - Perovskite-based fuel cell electrode and membrane - Google Patents

Perovskite-based fuel cell electrode and membrane Download PDF

Info

Publication number
WO2004013925A1
WO2004013925A1 PCT/GB2003/003344 GB0303344W WO2004013925A1 WO 2004013925 A1 WO2004013925 A1 WO 2004013925A1 GB 0303344 W GB0303344 W GB 0303344W WO 2004013925 A1 WO2004013925 A1 WO 2004013925A1
Authority
WO
WIPO (PCT)
Prior art keywords
value
membrane
fuel
layer
anode
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/GB2003/003344
Other languages
English (en)
French (fr)
Inventor
John Thomas Sirr Irvine
Shanwen Tao
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
University of St Andrews
Original Assignee
University of St Andrews
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by University of St Andrews filed Critical University of St Andrews
Priority to AU2003248994A priority Critical patent/AU2003248994B2/en
Priority to US10/523,093 priority patent/US7504172B2/en
Priority to EP03766465.3A priority patent/EP1532710B1/en
Priority to DK03766465.3T priority patent/DK1532710T3/en
Priority to ES03766465.3T priority patent/ES2598356T3/es
Priority to CA2493029A priority patent/CA2493029C/en
Priority to JP2004525554A priority patent/JP4961614B2/ja
Publication of WO2004013925A1 publication Critical patent/WO2004013925A1/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/42—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on chromites
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
    • B01D53/22—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols by diffusion
    • B01D53/228—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols by diffusion characterised by specific membranes
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/016—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on manganites
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/86—Inert electrodes with catalytic activity, e.g. for fuel cells
    • H01M4/88—Processes of manufacture
    • H01M4/8878—Treatment steps after deposition of the catalytic active composition or after shaping of the electrode being free-standing body
    • H01M4/8882—Heat treatment, e.g. drying, baking
    • H01M4/8885—Sintering or firing
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/86—Inert electrodes with catalytic activity, e.g. for fuel cells
    • H01M4/90—Selection of catalytic material
    • H01M4/9016—Oxides, hydroxides or oxygenated metallic salts
    • H01M4/9025—Oxides specially used in fuel cell operating at high temperature, e.g. SOFC
    • H01M4/9033—Complex oxides, optionally doped, of the type M1MeO3, M1 being an alkaline earth metal or a rare earth, Me being a metal, e.g. perovskites
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M8/00—Fuel cells; Manufacture thereof
    • H01M8/10—Fuel cells with solid electrolytes
    • H01M8/12—Fuel cells with solid electrolytes operating at high temperature, e.g. with stabilised ZrO2 electrolyte
    • H01M8/124—Fuel cells with solid electrolytes operating at high temperature, e.g. with stabilised ZrO2 electrolyte characterised by the process of manufacturing or by the material of the electrolyte
    • H01M8/1246—Fuel cells with solid electrolytes operating at high temperature, e.g. with stabilised ZrO2 electrolyte characterised by the process of manufacturing or by the material of the electrolyte the electrolyte consisting of oxides
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3205—Alkaline earth oxides or oxide forming salts thereof, e.g. beryllium oxide
    • C04B2235/3208—Calcium oxide or oxide-forming salts thereof, e.g. lime
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3205—Alkaline earth oxides or oxide forming salts thereof, e.g. beryllium oxide
    • C04B2235/3213—Strontium oxides or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3205—Alkaline earth oxides or oxide forming salts thereof, e.g. beryllium oxide
    • C04B2235/3215—Barium oxides or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3224—Rare earth oxide or oxide forming salts thereof, e.g. scandium oxide
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3224—Rare earth oxide or oxide forming salts thereof, e.g. scandium oxide
    • C04B2235/3225—Yttrium oxide or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3224—Rare earth oxide or oxide forming salts thereof, e.g. scandium oxide
    • C04B2235/3227—Lanthanum oxide or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C04B2235/3241—Chromium oxides, chromates, or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3262—Manganese oxides, manganates, rhenium oxides or oxide-forming salts thereof, e.g. MnO
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3262—Manganese oxides, manganates, rhenium oxides or oxide-forming salts thereof, e.g. MnO
    • C04B2235/3265—Mn2O3
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3262—Manganese oxides, manganates, rhenium oxides or oxide-forming salts thereof, e.g. MnO
    • C04B2235/3267—MnO2
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/74—Physical characteristics
    • C04B2235/76—Crystal structural characteristics, e.g. symmetry
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/74—Physical characteristics
    • C04B2235/76—Crystal structural characteristics, e.g. symmetry
    • C04B2235/761—Unit-cell parameters, e.g. lattice constants
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/74—Physical characteristics
    • C04B2235/76—Crystal structural characteristics, e.g. symmetry
    • C04B2235/768—Perovskite structure ABO3
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/86—Inert electrodes with catalytic activity, e.g. for fuel cells
    • H01M2004/8678—Inert electrodes with catalytic activity, e.g. for fuel cells characterised by the polarity
    • H01M2004/8684—Negative electrodes
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M8/00—Fuel cells; Manufacture thereof
    • H01M8/10—Fuel cells with solid electrolytes
    • H01M8/12—Fuel cells with solid electrolytes operating at high temperature, e.g. with stabilised ZrO2 electrolyte
    • H01M2008/1293—Fuel cells with solid oxide electrolytes
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
    • Y02E60/30—Hydrogen technology
    • Y02E60/50—Fuel cells
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P70/00—Climate change mitigation technologies in the production process for final industrial or consumer products
    • Y02P70/50—Manufacturing or production processes characterised by the final manufactured product

Definitions

  • the present invention relates to fuel cell electrodes, and more particularly to electrodes suitable for use in solid oxide fuel cells (SOFCs) .
  • SOFCs solid oxide fuel cells
  • the present invention provides a novel material suitable for use in a solid oxide fuel cell, especially in an anode thereof, wherein the material is of an, optionally doped, double perovskite oxide material having the general formula I: wherein Ln is selected from Y, La and a Lanthanide series element, or a combination of these and X also represents an element occupying the A site of a perovskite oxide and is selected from Sr, Ca and Ba, and Z 1 and Z 2 represent different elements occupying the B site of a perovskite oxide and are selected from Cr, Mn, Mg and Fe, and wherein a has a value from 0 to 1, preferably, 0.7 to 1.0, b has a value of from 1 to 0, preferably 0.3 to 0, and each of c and d has a value of from 0.25 to 0.75, provided that a + b has a value of 1, and c + d, has a value of 1, and wherein e has a value of from 0.8 to
  • the Z 1 and Z 2 , elements are preferably present in substantially equivalent amounts, they can nevertheless depart to some extent from exactly equivalent amounts. Also it is possible for the A site in the perovskite material (occupied by Ln and X) , and/or the B site in the perovskite material (occupied by Z 1 and Z 2 ) , to be somewhat depleted (e ⁇ 1 and f ⁇ 1) without disrupting the crystal structure thereof and significantly degrading the properties of the anode. Similarly, although g normally has a value of 3, some crystal defects in relation to the O sites are also acceptable.
  • 0 site deficiency (g ⁇ 3) is acceptable and indeed may be useful in that it allows for 0 atom mobility between different 0 sites within the crystal lattice of the material.
  • a limited degree of excess 0 atoms (g > 3) is also acceptable in at least some circumstances.
  • novel double perovskite materials provided by the present invention can be used in the production of anodes for use in SOFCs and which have significantly improved electrochemical performance, electrical and catalytic properties when compared with anodes of previously known materials, when used with methane fuel, whilst avoiding the particular problems and disadvantages of previously proposed electrodes such as Ni-YSZ. More particularly it has been found that they are chemically redox stable, which may significantly decrease the volume instability during redox cycling that causes degradation.
  • novel materials of the present invention are particularly valuable for use as anodes in SOFCs, they also have other applications in SOFCs including as one or more of: anode functional layer, cathode functional layer, cathode, and interconnector .
  • a functional layer indicates a thin electroactive layer provided between the electrode current collector (anode or cathode) and the electrolyte; or possibly between the anode or cathode current collector and another functional layer, for the purposes of protecting the electrode itself from degradation (typically due to interfacial reaction) , and/or enhancing catalytic activity and/or enhancing the performance characteristics (e.g. reducing polarisation resistance) .
  • a functional layer could have a thickness of from 1 to 50 ⁇ m, preferably 20 to 30 ⁇ m.
  • the functional layer may moreover be substantially solid or have more or less greater porosity, for example, up to 70% porosity, preferably from 30 to 60% porosity, conveniently from 40 to 50% porosity.
  • interconnector indicates a component used for connecting together the electrodes of neighbouring cells in an assembly of a plurality of cells connected together in series.
  • the materials are preferably made with high density (i.e. low porosity, preferably not more than 1 % porosity, advantageously zero continuous porosity) in order to make them substantially gas-impermeable.
  • materials of the present invention can, surprisingly, be used as both anodes and cathodes.
  • This makes it possible to produce a cell with the same anode and cathode electrodes whereby it is possible to operate the cell using either electrode as cathode and anode, and even to reverse operation of the cell when required, for example, in a reversible fuel cell application (in which energy can be stored temporarily by applying a voltage to the electrodes), by changing the cell connections so that the anode becomes the cathode and vice versa.
  • Z 1 and Z 2 represent Cr and Mn, respectively.
  • X represents Sr.
  • the double perovskite materials used in accordance with the present invention may nevertheless also be doped to some extent i.e. any one or more of the A and B sites which would otherwise be occupied by Ln, X, Z 1 and Z z , may be replaced to a limited degree by one or more suitable dopant elements in order to improve still further electrical and/or catalytic properties .
  • Suitable dopants at the B sites i.e. replacing either or both of some Z 1 and some Z 2 sites, for improving electrical conductivity include V, Fe, Cu, Co, Ti, Nb, Mo, Ru and Ni, whilst suitable dopants for improving catalytic activity include Pd, Ce, Ni, Ru and Mg.
  • the dopant should not occupy more than 20% of the B sites of the double perovskite oxide. Where there is used a dopant, this is preferably present at a level of not more than 20%, preferably from 5 to 20%.
  • novel materials of the present invention may be used with various different electrolytes.
  • they have been found to be compatible and suitable for use with yttria stabilised zirconia (YSZ) electrolyte which exhibits good thermal and chemical stability.
  • YSZ yttria stabilised zirconia
  • double perovskite indicates a material in which the B sites in the crystal lattice structure of said material are populated by comparable substantial amounts of two different elements, with not less than 25%, preferably not less than 30% of the B sites populated by said two different elements.
  • the invention encompasses materials in which one of the elements can occupy as many as 75% of the B sites, and the other as few as 25%, substantial amounts of each one (at least 25%, preferably at least 30%) are present, and the relative amounts (3:1 or less) are comparable - unlike in a doped material in which the elements are in a relative ratio of at least 4:1 and often 10:1 or more.
  • the B sites could also be occupied by a third element (Z3) present in an amount of at least 30%, which is comparable to that of the first two elements. Whilst such a material could be described as a triple perovskite, it should be understood ⁇ to be also encompassed within the "double perovskites" of the present invention. Again the term “triple” reflects composition at the B-site rather than a specific type of structural ordering.
  • Preferred materials provided by the present invention are those in which in general formula I, each of c and d has a value of at least 0.4. Desirably, in general formula I, a has a value of from 0.7 to 0.9, most preferably from 0.72 to 0.85.
  • novel materials of the present invention may be prepared by any suitable method known in the art. In general two or more compounds consisting essentially of the required metallic elements in suitable proportions, in the form of suitable oxides or salts with nitric acids, are brought together into intimate admixture with heat treatment.
  • One convenient method comprises a solid state reaction in which dry oxides and/or carbonates (or other salts such as acetates, oxalates etc) of the metal elements are mixed together and fired at a high temperature, typically of the order of 1000 to 1400°C.
  • Another convenient method comprises combustion synthesis in which a solution of salts such as nitrates of the required metal elements in suitable proportions, in aqueous ethylene glycol, from which solution water is progressively removed to yield a gel which can be burnt to provide a char. Firing of the char at high temperature, typically above 1100°C, then yields the double- perovskite form of the material.
  • the electrode In order to make the material suitable for use as a fuel cell electrode, it is necessary for it to be in a relatively porous form which presents a relatively large surface area for chemical interactions to take place at.
  • the electrode Preferably the electrode should have a porosity value of at least 20%, preferably from 30 to 60% advantageously from 40 to 50%, typically around 50%.
  • porous forms of the novel double perovskite material may be obtained by the addition of pore-forming agents (PFAs) .
  • the PFAs could be one or more of carbon and organic materials, such as PVB (polyvinyl butyral) , PEG (polyethylene glycol) , terpineol, ethyl cellulose etc.
  • novel materials of the present invention may be used in various forms and configurations of SOFCs. Thus they may be used as anode and/or cathode, and/or functional layer, in planar or tubular SOFC or SOFC rolls.
  • novel materials of the invention are substantially compatible with various electrolytes used in SOFCs, including in particular doped ceria and especially perovskites such as Sr- and Mg-doped LaGa0 3 etc, as well as undoped ceria.
  • the present invention provides a SOFC having an electrode or functional layer of a novel material according to the present invention.
  • the present invention provides a SOFC having an anode of a novel material according to the present invention.
  • SOFCs using or containing an anode of the present invention may be used to oxidise any fuel appropriate for fuel cell use either directly or after at least partial reformation.
  • fuels include hydrogen; hydrogen; a hydrocarbon fuel compound such as methane, ethane, propane, or butane; a hydrocarbon based fuel compound such as methanol or ethanol; and a non- hydrocarbon hydride fuel compound such as ammonia, hydrogen sulphide; as well as mixtures of such compounds such as LPG, gasoline, diesel, biogas, biofuel, kerosene, or JP8 .
  • the present invention provides a method of oxidising a fuel in an SOFC, comprising the steps of: a) providing an SOFC having an anode of the novel material of the present invention; and b) applying a voltage to said SOFC so as to oxidize said f el . It is also possible in at least some cases to use the new double perovskite materials provided by the present invention, in fuel cell cathodes, ' and accordingly the present invention also extends to a fuel cell cathode comprising a substantially porous body of a double perovskite according to the present invention. This provides the opportunity to use the same material as both cathode and anode in a SOFC with clear advantages with regard to compatibility issues.
  • the invention provides a novel material suitable for use in an anode in a solid oxide fuel cell, wherein the material is of an, optionally doped, double perovskite oxide material having the general formula I: wherein Ln is selected from Y, La and a Lanthanide series element, or a combination of these and X represents an optional second element occupying the A site of a perovskite oxide and is selected from Sr, Ca and Ba, and Z 1 and Z 2 represent different elements occupying the B site of a perovskite oxide and are selected from Cr, Mn and Fe, and wherein a has a value from 0.7 to 1.0, b has a value of from 0.3 to 0, and each of c and d has a value of from 0.25 to 0.75, provided that a + b has a value of 1, and c + d, has a value of not less than 0.8, and wherein e has a value of from 0.8 to 1.
  • Ln is selected from Y, La and a Lan
  • novel double perovskite materials of the present invention may also be used in mixed-conducting ceramic membranes as a syngas reactor membrane or as a protective layer on the natural gas side of a syngas reactor membrane layer of another material (which typically comprises a dense layer of lanthanum strontium-iron-cobalt oxide) or a related composition.
  • Such ceramic membranes are useful for partial oxidation of natural gas into synthesis gas, often referred to as syngas .
  • Syngas can be used to make liquid diesel and other transportation fuels, as well as chemicals for the petrochemical, rubber, plastics, and fertilizer industries.
  • Hydrogen can also be separated from the gas and used as an energy source or by a refinery to produce cleaner, higher- performance gasoline.
  • the unique approach of the MIEC (mixed ionic/electronic conducting) membrane technology allows the integration of oxygen separation, steam- and C0 2 - reforming, and partial oxidation of methane into a single process.
  • the technology substantially reduces the energy and capital cost associated with conventional syngas production.
  • the MIEC membrane technology can also help to reduce N0 X emissions by using nitrogen oxides as an oxygen source.
  • the energy contained in the oxygen-depleted air stream can be recovered through the generation of power and steam.
  • the present invention provides a mixed ionic/electronic conducting membrane comprising a layer of a novel double perovskite material according to the present invention.
  • said layer comprises a protective layer on at least one side of a mixed ionic/electronic conducting ceramic membrane, and especially one suitable for use in a syngas reactor.
  • a protective layer would generally have a thickness of from 1 to 200 ⁇ m, preferably, from 20 to70 ⁇ m.
  • the membrane consists essentially of a novel double perovskite material according to the present invention, the membrane would generally have a thickness of from 10 to 500 ⁇ m, preferably from 20 tolOO ⁇ m.
  • Such mixed ionic/electronic conducting membranes are also suitable for use in separating oxygen from air for various purposes, e.g. for the production of (substantially pure) oxygen gas, or for use directly in reactions with other materials (e.g. with methane in syngas production).
  • the perovskite material should be made with high density (i.e. low porosity, preferably not more than 1 % porosity, advantageously zero continuous porosity) in order to make them substantially gas-impermeable.
  • Such membranes may be self supporting or supported on a porous metal or ceramic or metal/ceramic composite, support.
  • Figs. 1, 3 and 4 are graphs showing measurement of various electrical properties obtained using anodes of the invention.
  • Fig. 2 is a schematic drawing of the principal parts of an electrochemical cell of the invention in sectional elevation; and
  • Fig. 2A is an underside plan view of the cell of Fig.2; and Fig. 5 is a schematic sectional view of an SOFC.
  • Example 1 Preparation of Double Perovskite Material La 2 0 3 (4.8873g), SrC0 3 (1.4763g), Cr 2 0 3 (1.5199g) and Mn0 2 (1.7388g) in powder form were mixed together in an agate mortar. The mixed powders were transferred into a zirconia container, with addition some acetone or ethanol and ball- milled for 15 minutes twice, and then left for 10 hours in a fume cupboard to evaporate the organic component.
  • the dried powders were then subjected to a series of high temperature firing and intermediate grinding cycles using a muffle furnace, as follows: 1. 12 hours at 1400°C
  • Example 2 Preparation of Double Perovskite Material La 2 0 3 (4.8873g), SrC0 3 (1.4763g) and MnC0 3 (2.299g) were dissolved in dilute nitric acid (40 mis 4 N) and heated to 80°C with stirring until a solution is obtained. Then 8.0028g Cr (N0 3 ) 3 -9H 2 0 was dissolved into the solution. 25ml pure ethyl glycol was then added into the mixed nitrate solution and stirred at 80°C for 2 hours. The obtained gel was transferred into a porcelain container and heated on a hot plate until firing into char. The char was further heated at 1100 to 1400°C to obtain the perovskite oxide having the composition Lao.-75Sro.25Cro.5Mno.5O3.
  • the double perovskite material of Example 1 (0.45g) was mixed with 0.05g carbon (graphite) and 5ml ethanol .
  • the mixture was ground in an agate mortar or ball-milled for 30 minutes to form a slurry.
  • the slurry was painted or screen-printed onto an 8mol%Y 2 0 3 stabilised zirconia (YSZ) 2 cm diameter disc with 2 mm thickness.
  • the anode supported on the YSZ electrolyte was then fired from room temperature heating up at 5°C/min up to 1100°C, held at 1100°C for 4 hours, and then cooled down to room temperature at 5°C/min.
  • the thickness of the anode so obtained is about 30-100 ⁇ m with an area of 1cm 2 .
  • a small amount of gold paste was partially coated onto the anode (ca. 50% coverage) and fired at 900°C for 30 minutes using a 5°C/min heating up and cooling down rate in the range from 300°C to 900°C, to ensure better electronic contact for testing purposes.
  • Platinum paste Engelhard Clal 6082
  • the anode obtained in Example 3 was mounted in a solid oxide fuel cell configured in the form of a 0.2mm thick layer of YSZ electrolyte.
  • La 0 .8Sro.2Mn0 3 (LSM) was coated onto the other side of the YSZ sheet to provide a cathode.
  • the slurry composition used in the production of the cathode was 0.45g Lao. 8 Sro. 2 Mn0 3 , 0.05g graphite and 5ml ethanol .
  • a thin layer platinum paste (see Example 3) was coated onto the LSM and fired at 900 °C for 30 minutes with 5°C/min heating up and cooling down rates above 300°C to provide a cathode current collector.
  • Figure 1 shows the performance of the cell using the double perovskite oxide Lao.-75Sro.25Cro.5Mno.5O3 anode of Example 3, when supplied with various different fuels: wet H , wet 5%H 2 or wet and pure CH 4 , at 900°C. While the open circuit voltages (OCVs) for wet 5%H 2 and wet H 2 were close to the value predicted by the Nerst equation, 0.95 and 1.09V at 900°C, the OCV for wet and unhumidified cylinder CH 4 was 0.87 and 086V respectively, which is slightly lower than that for wet 5%H 2 .
  • OCVs open circuit voltages
  • the maximum power densities were higher for wet H 2 than wet 5%H 2 , with values of 0.34W cm -2 and 0.17W cm -2 - respectively.
  • the maximum power density for wet methane was about 0.1W cm -2 at 0.53V, which is slightly lower than that for wet 5%H 2 .
  • Example 3 The properties of the anode of Example 3 were examined by means of a three-electrode configuration test cell illustrated schematically in Figs. 2 and 2A, which show a disc shaped electrolyte 1 with an annular anode 2 on one face 3 and an annular cathode 4 and a central disc-form reference electrode 5 on the opposite face 6.
  • the electrolyte was sintered 8mol%Y 2 0 3 stabilized Zr0 2 (YSZ) pellet with 2mm thickness and 20mm diameter.
  • An anode with a thickness of about 50 ⁇ m was deposited onto the YSZ electrolyte using an ethanol-based slurry and firing typically at 1000 to 1300°C.
  • Fig. 3 shows the potential and current change at 925 °C under operation using wet CH 4 as fuel at 0.4V bias. No significant performance degradation was observed during four hours operation although a trace amount of carbon was observed after the fuel cell performance in wet CH 4 and cooling down in the same atmosphere.
  • Example 6 Preparation and use of Modified Anode
  • a thin film interface of Ce 0 . 8 Gdo. 2 ⁇ 2 (CGO) prepared by a sol-gel process, was applied between the YSZ electrode and the anode.
  • Anode polarisation resistance was further decreased with such a thin layer (5 ⁇ m) of CGO deposited between the YSZ electrolyte and LSCM anode as shown in Fig. 4.
  • the polarization resistances in wet 5%H 2 and wet H 2 were about 0.62 ⁇ cm -2 and 0.25 ⁇ cm -2 , respectively.
  • the anode polarization in wet H 2 at 925°C is comparable to that of the conventional Ni-YSZ cermet anode at 1000 °C.
  • novel perovskite material of Example 1 involves using this material as a thin functional layer, approximately 20-50 microns thick, which is electrochemically active, on top of a conducting support such as a nickel zirconia cermet or on a porous steel current collector support, and in either case below a dense ( ⁇ 2% porosity) YSZ electrolyte.
  • a conducting support such as a nickel zirconia cermet or on a porous steel current collector support, and in either case below a dense ( ⁇ 2% porosity) YSZ electrolyte.
  • a double perovskite LSCM material prepared according to Example 1 is used in a composite multi-layered anode structure with a pure nickel current collector layer, an LSCM outer functional layer, and a series of progressively graded Ni-LSCM cermet intermediate layers, as follows:
  • Example 8 Preparation and use of Interconnector Mix the stoichiometric ratios (as in Example 1) of La 2 0 3 , SrC ⁇ 3 , Cr 2 ⁇ 3 and Mn 2 ⁇ 3 together, add some acetone, ball-mill in a zirconia container with zirconia balls for 30 minutes. Fire at 1200°C for 20 hours twice with ball-milling with acetone for 30 minutes . after each firing, then dry press into 30mm diameter pellets, and finally fire at 1500°C for 36 hours. This provides a pellet with relative density of approximately 94% (i.e. 6% porosity). Typically lanthanum strontium chromite would require 1600°C heat treat treatment to achieve similar densification.
  • Fig. 5 shows schematically an SOFC generator 7 of the the invention for generating electricity from fuel gas .
  • the generator 7 comprises a tubular SOFC element 8 mounted in a chamber 9 and having an outer tubular anode 10 and an inner tubular cathode 11 with an electrolyte 12 therebetween, the anode, cathode and electrolyte being of the same materials as those in the example illustrated in Fig.2.
  • An air inlet tube 13 is provided for introducing pre-heated air 14 into the interior 15 of the SOFC element 8, and a fuel gas supply pipe 16 provided for feeding pre-heated fuel gas 17 into the chamber 9 around the anode 10.
  • Electrical connections 18 are connected to the cathode 11 and anode 10 for connection of the generator 7 to an electrical load in use of the generator.
  • Exhaust gases 19 comprising spent air, unused fuel, and oxidation products, are vented from the chamber 9 by an exhaust pipe 20, although it is generally preferred that spent air 21 is exhausted separately from the unused fuel gas, via a separate

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Manufacturing & Machinery (AREA)
  • Ceramic Engineering (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Materials Engineering (AREA)
  • Electrochemistry (AREA)
  • Organic Chemistry (AREA)
  • Structural Engineering (AREA)
  • Sustainable Energy (AREA)
  • Physics & Mathematics (AREA)
  • Sustainable Development (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Thermal Sciences (AREA)
  • Analytical Chemistry (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Inert Electrodes (AREA)
  • Fuel Cell (AREA)
  • Inorganic Compounds Of Heavy Metals (AREA)
  • Compositions Of Oxide Ceramics (AREA)
PCT/GB2003/003344 2002-08-01 2003-07-31 Perovskite-based fuel cell electrode and membrane Ceased WO2004013925A1 (en)

Priority Applications (7)

Application Number Priority Date Filing Date Title
AU2003248994A AU2003248994B2 (en) 2002-08-01 2003-07-31 Perovskite-based fuel cell electrode and membrane
US10/523,093 US7504172B2 (en) 2002-08-01 2003-07-31 Perovskite-based fuel cell electrode and membrane
EP03766465.3A EP1532710B1 (en) 2002-08-01 2003-07-31 Perovskite-based fuel cell electrode and membrane
DK03766465.3T DK1532710T3 (en) 2002-08-01 2003-07-31 PEROVSKIT-BASED FUEL CELL ELECTRODE AND MEMBRANE
ES03766465.3T ES2598356T3 (es) 2002-08-01 2003-07-31 Electrodo de pila de combustible a base de perovskita y membrana
CA2493029A CA2493029C (en) 2002-08-01 2003-07-31 Perovskite-based fuel cell electrode and membrane
JP2004525554A JP4961614B2 (ja) 2002-08-01 2003-07-31 ペロブスカイトベースの燃料電池電極および膜

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GBGB0217794.7A GB0217794D0 (en) 2002-08-01 2002-08-01 Fuel cell electrodes
GB0217794.7 2002-08-01

Publications (1)

Publication Number Publication Date
WO2004013925A1 true WO2004013925A1 (en) 2004-02-12

Family

ID=9941494

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/GB2003/003344 Ceased WO2004013925A1 (en) 2002-08-01 2003-07-31 Perovskite-based fuel cell electrode and membrane

Country Status (10)

Country Link
US (1) US7504172B2 (enExample)
EP (1) EP1532710B1 (enExample)
JP (1) JP4961614B2 (enExample)
CN (1) CN1322625C (enExample)
AU (1) AU2003248994B2 (enExample)
CA (1) CA2493029C (enExample)
DK (1) DK1532710T3 (enExample)
ES (1) ES2598356T3 (enExample)
GB (1) GB0217794D0 (enExample)
WO (1) WO2004013925A1 (enExample)

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1294670C (zh) * 2004-03-03 2007-01-10 哈尔滨工业大学 一种镓酸镧基固体氧化物燃料电池用正极材料的制备方法
WO2007004684A1 (ja) * 2005-06-30 2007-01-11 Tokyo Institute Of Technology 酸素過剰型金属酸化物及び酸素貯蔵又は酸素選択膜用セラミックスと該金属酸化物を用いる方法及び装置
WO2007093759A1 (en) * 2006-02-14 2007-08-23 Rolls-Royce Plc A solid oxide fuel cell module with multilayered anode
JP2008529226A (ja) * 2005-02-02 2008-07-31 テクニカル ユニバーシティ オブ デンマーク 可逆式固体酸化物型燃料電池を製造する方法
WO2008145145A1 (en) * 2007-05-31 2008-12-04 Elcogen As Method for the preparation of a solid oxide fuel cell single cell and the named cell
WO2009025553A1 (en) 2007-08-22 2009-02-26 Stichting Energieonderzoek Centrum Nederland Electrode for fixed oxide reactor and fixed oxide reactor
US7745031B2 (en) 2004-06-10 2010-06-29 Technical University Of Denmark Solid oxide fuel cell
RU2424604C1 (ru) * 2007-05-31 2011-07-20 Элкоген Ас Способ изготовления одиночного твердооксидного топливного элемента
US9263758B2 (en) 2005-08-31 2016-02-16 Technical University Of Denmark Reversible solid oxide fuel cell stack and method for preparing same
CN113299960A (zh) * 2021-05-17 2021-08-24 深圳大学 一种乙烯与电能共生型固体氧化物燃料电池及其制备方法
CN115939472A (zh) * 2022-11-25 2023-04-07 中国科学院宁波材料技术与工程研究所 一种抗积碳固体氧化物燃料电池及其制备方法

Families Citing this family (47)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR100543979B1 (ko) * 2003-11-21 2006-01-20 한국표준과학연구원 나노 크기의 세공을 갖는 강자기성 망간 산화물 막과 이의제조방법
EP1716076B1 (en) * 2004-01-23 2017-03-15 Very Small Particle Company Pty Ltd Method for making metal oxides
JP4788274B2 (ja) * 2005-10-03 2011-10-05 株式会社村田製作所 Ｃｔｒ特性を有する酸化物導電体磁器および抵抗体
AT9543U1 (de) 2006-07-07 2007-11-15 Plansee Se Verfahren zur herstellung einer elektrisch leitfähigen schicht
JP5361143B2 (ja) * 2007-05-29 2013-12-04 新光電気工業株式会社 固体酸化物型燃料電池およびその製造方法
US20090017341A1 (en) * 2007-07-09 2009-01-15 Uchicago Argonne, Llc Air electrode composition for intermediate temperature electrochemical devices
CN100459250C (zh) * 2007-10-11 2009-02-04 北京科技大学 一种用于固体氧化物燃料电池的缺位掺杂阳极材料
JP5226290B2 (ja) * 2007-12-19 2013-07-03 国立大学法人東京工業大学 固体酸化物型電池
JP5689790B2 (ja) * 2008-04-03 2015-03-25 サッチェム，インコーポレイテッド ジカルボン酸オニウムを用いた先進セラミック粉末の調製方法
CN102119134B (zh) * 2008-06-13 2015-02-11 塞瑞斯知识产权有限公司 用于沉积陶瓷膜的方法
KR101213060B1 (ko) 2009-03-12 2012-12-17 한창산업 주식회사 고체산화물 연료전지용 공기극 물질
CN101789501B (zh) * 2010-01-22 2011-12-28 清华大学 用于固体氧化物电解池阴极的钙钛矿粉体材料的制备方法
DE102010027645A1 (de) * 2010-07-19 2012-01-19 Forschungszentrum Jülich GmbH CO2 tolerantes, gemischt leitendes Oxid und dessen Anwendung für die Wasserstoffabtrennung
TWI416787B (zh) 2010-07-23 2013-11-21 Iner Aec Executive Yuan 固態氧化物燃料電池之多孔金屬基板結構及其之製作方法
TWI411154B (zh) 2010-07-23 2013-10-01 Iner Aec Executive Yuan 一種用於固態氧化物燃料電池之雙層陽極-金屬基板結構及其製作方法
JP5204816B2 (ja) * 2010-08-11 2013-06-05 株式会社ノリタケカンパニーリミテド 酸素分離膜エレメント及びその製造方法
JP5737954B2 (ja) * 2011-01-07 2015-06-17 国立大学法人茨城大学 バナデート系複合酸化物の製造方法
WO2012145072A1 (en) 2011-04-22 2012-10-26 Topera, Inc. Basket style cardiac mapping catheter having a flexible electrode assembly for detection of cardiac rhythm disorders
JP5717067B2 (ja) * 2011-04-22 2015-05-13 独立行政法人物質・材料研究機構 中低温で動作する固体酸化物燃料電池用複合カソード材料、固体酸化物燃料電池用複合カソード及び固体酸化物燃料電池用電解質−複合カソード構造体の製造方法
FR2981508B1 (fr) * 2011-10-12 2013-11-15 Areva Electrode pour cellule electrochimique et procede de fabrication d'une telle electrode
EP2621006B1 (en) 2012-01-26 2016-10-26 Institute of Nuclear Energy Research Atomic Energy Council An anode on a pretreated substrate for improving redox-stablility of solid oxide fuel cell and the fabrication method thereof
JP5746309B2 (ja) * 2012-12-17 2015-07-08 サムソン エレクトロ−メカニックス カンパニーリミテッド． 固体酸化物燃料電池の電極用ペースト、これを用いる固体酸化物燃料電池およびその製造方法
KR20150126835A (ko) * 2013-01-30 2015-11-13 가부시키가이샤 산도쿠 양극 촉매 및 기기
CN103149256A (zh) * 2013-02-27 2013-06-12 上海大学 由SrNiFeO3修饰玻碳电极的电化学传感器及其对H2O2的测定方法
US9809453B2 (en) 2013-03-15 2017-11-07 Lg Fuel Cell Systems, Inc. Catalysts for hydrocarbon reforming
JP5603515B1 (ja) * 2013-08-23 2014-10-08 日本碍子株式会社 空気極材料及び固体酸化物型燃料電池
GB2522522B (en) * 2014-11-27 2018-01-24 Ceres Ip Co Ltd Structure
CN104458859A (zh) * 2014-12-12 2015-03-25 上海大学 La0.88Sr0.12MnO3纳米纤维修饰的碳糊电极及其制备方法和应用
CN104779398A (zh) * 2015-04-27 2015-07-15 上海邦民新能源科技有限公司 固体氧化物燃料电池阳极材料及具有其的阳极
KR101905953B1 (ko) * 2015-05-15 2018-10-10 세종대학교산학협력단 삼중층 페로브스카이트 공기극 촉매 및 이를 구비하는 전기화학소자
CN105449227B (zh) * 2016-01-02 2018-07-06 红河学院 一种层状钙钛矿燃料电池阴极材料及其制备方法
CN106835206B (zh) * 2017-01-03 2018-10-02 北京科技大学 一种铬酸镧基惰性阳极的制备方法及应用
JP6844440B2 (ja) * 2017-06-16 2021-03-17 日本製鉄株式会社 水素の製造方法
CN107293718B (zh) * 2017-06-26 2020-05-26 合肥国轩高科动力能源有限公司 R2-xMxEMnO6改性镍锰酸锂材料及制备、应用
CN107352587B (zh) * 2017-06-29 2018-10-23 宁波吉电鑫新材料科技有限公司 一种电场调控选择结晶合成双钙钛矿钠离子电池负极材料及其制备方法
CN107265502B (zh) * 2017-06-29 2018-10-23 宁波吉电鑫新材料科技有限公司 一种电场调控选择结晶合成双钙钛矿钾离子电池负极材料及其制备方法
CN107285390B (zh) * 2017-06-29 2018-11-09 宁波吉电鑫新材料科技有限公司 一种电场调控选择结晶合成双钙钛矿锂离子电池负极材料及其制备方法
US11843123B2 (en) * 2018-03-02 2023-12-12 Northwestern University Cobalt-substituted perovskite compounds for solid oxide electrochemical cells
CN109921043B (zh) * 2019-02-26 2021-10-08 五邑大学 一种b掺杂钙钛矿类氧化物的电催化剂及其制备方法
CN109809486A (zh) * 2019-03-26 2019-05-28 暨南大学 一种向KNbO3钙钛矿中掺杂Ba和Ni离子的方法
CN109913900A (zh) * 2019-04-18 2019-06-21 北京理工大学 一种具有高催化活性的用于co2电解的soec阴极材料
JP7360276B2 (ja) 2019-08-30 2023-10-12 太陽誘電株式会社 固体酸化物型燃料電池およびその製造方法
JP7377051B2 (ja) * 2019-10-07 2023-11-09 太陽誘電株式会社 固体酸化物型燃料電池およびその製造方法
CN110668804A (zh) * 2019-10-17 2020-01-10 江苏科技大学 一种固体氧化物燃料电池用陶瓷连接体材料及其制备方法
JP7484048B2 (ja) 2020-03-10 2024-05-16 太陽誘電株式会社 固体酸化物型燃料電池およびその製造方法
CN113800908A (zh) * 2021-08-26 2021-12-17 桂林理工大学 中介电常数双钙钛矿微波介质陶瓷材料及其制备方法
KR102454622B1 (ko) * 2022-01-20 2022-10-17 주식회사 에코나인 이중 페로브스카이트 또는 삼중 페로브스카이트 구조를 갖는 산화방지제

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH01200560A (ja) * 1988-02-05 1989-08-11 Mitsubishi Heavy Ind Ltd 電極材料
JPH02236959A (ja) * 1989-03-09 1990-09-19 Mitsubishi Heavy Ind Ltd 電極材料
EP0411547A1 (en) 1989-07-31 1991-02-06 Tonen Corporation Lanthanum chromite-based complex oxides and uses thereof
US5686198A (en) 1996-02-29 1997-11-11 Westinghouse Electric Corporation Low cost stable air electrode material for high temperature solid oxide electrolyte electrochemical cells

Family Cites Families (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2810104B2 (ja) * 1989-04-28 1998-10-15 日本碍子株式会社 セラミックス電極及びこれを有する燃料電池
JPH0317958A (ja) * 1989-06-14 1991-01-25 Agency Of Ind Science & Technol 固体電解質型燃料電池用空気極材料および固体電解質型燃料電池
JPH0317959A (ja) * 1989-06-14 1991-01-25 Agency Of Ind Science & Technol 固体電解質型燃料電池用空気極材料および固体電解質型燃料電池
JP2946053B2 (ja) * 1990-06-16 1999-09-06 工業技術院長 円筒型固体電解質燃料電池並びに平板型固体電解質燃料電池
JPH0644991A (ja) * 1992-07-27 1994-02-18 Ngk Insulators Ltd 固体電解質型燃料電池用インターコネクターの製造方法
JPH0927330A (ja) * 1995-07-11 1997-01-28 Tokyo Gas Co Ltd 固体電解質燃料電池の燃料極
JP2001196069A (ja) * 1999-11-01 2001-07-19 Mitsubishi Heavy Ind Ltd 燃料電池
JP4379987B2 (ja) * 1999-11-30 2009-12-09 トヨタ自動車株式会社 燃料電池の制御装置
US6537465B2 (en) * 2000-12-29 2003-03-25 Praxair Technology, Inc. Low pressure steam purged chemical reactor including an oxygen transport membrane
GB0125276D0 (en) * 2001-10-20 2001-12-12 Strathclyde Improvements in fuel cells related devices

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH01200560A (ja) * 1988-02-05 1989-08-11 Mitsubishi Heavy Ind Ltd 電極材料
JPH02236959A (ja) * 1989-03-09 1990-09-19 Mitsubishi Heavy Ind Ltd 電極材料
EP0411547A1 (en) 1989-07-31 1991-02-06 Tonen Corporation Lanthanum chromite-based complex oxides and uses thereof
US5686198A (en) 1996-02-29 1997-11-11 Westinghouse Electric Corporation Low cost stable air electrode material for high temperature solid oxide electrolyte electrochemical cells

Non-Patent Citations (11)

* Cited by examiner, † Cited by third party
Title
J. LIU ET AL., ELECTROCHEMICAL AND SOLID-STATE LETTERS, vol. 5, 2002, pages A122 - A125
MORI MASASHI ET AL: "Control of the thermal expansion of strontium-doped lanthanum chromite perovskites by b-site doping for high-temperature solid oxide fuel cell separators", J AM CERAM SOC;JOURNAL OF THE AMERICAN CERAMIC SOCIETY APRIL 2001, vol. 84, no. 4, April 2001 (2001-04-01), pages 781 - 786, XP002263206 *
P. VERNOUX ET AL., J. ELECTROCHEM. SOC., vol. 145, 1998, pages 3487 - 3492
PALMA J ET AL: "PEROVSKITE-TYPE (LA,SR)(MN,CR)O3 COMPOUNDS AS CANDIDATES FOR SOFC CATHODES", PROCEEDINGS OF THE INTERNATIONAL SYMPOSIUM ON SOLID OXIDE FUEL CELLS. ATHENS, JULY 2 - 5, 1991, LUXEMBURG, EEC, LU, vol. SYMP. 2, 2 July 1991 (1991-07-02), pages 537 - 544, XP000546146, ISBN: 92-826-2556-7 *
PALMA, PROCEEDINGS OF THE INTERNATIONAL SYMPOSIUM ON SOLID OXIDE FUEL CELLS, 2 July 1991 (1991-07-02), pages 537 - 544
PATENT ABSTRACTS OF JAPAN vol. 013, no. 496 (E - 843) 9 November 1989 (1989-11-09) *
PATENT ABSTRACTS OF JAPAN vol. 014, no. 550 (E - 1009) 6 December 1990 (1990-12-06) *
RASIT KOC ET AL: "STRUCTURAL, SINTERING AND ELECTRICAL PROPERTIES OF THE PEROVSKITE-TYPE (LA,SR)(CR,MN)O3", EXTENDED ABSTRACTS, FALL MEETING, HOLLYWOOD, ELECTROCHEMICAL SOCIETY, VOL. 89/2 (1989), P. 799, ISSN: 0160-4619, XP000276907 *
VERNOUX PHILIPPE ET AL: "Catalytic and electrochemical properties of doped lanthanum chromites as new anode materials for solid oxide fuel cells", J AM CERAM SOC;JOURNAL OF THE AMERICAN CERAMIC SOCIETY OCTOBER 2001, vol. 84, no. 10, October 2001 (2001-10-01), pages 2289 - 2295, XP002263207 *
VERNOUX: "Catalytic and electrochemical properties of doped lanthanum chromites as new anode materials for solid oxide fuel cells", J. AM. CERAM. SOC., vol. 84, no. 10, October 2001 (2001-10-01), pages 2289 - 2295, XP002263207
WANG Z M ET AL: "The effect of average A-site cation radius on TC in perovskite manganites", JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, ELSEVIER SCIENCE PUBLISHERS, AMSTERDAM, NL, vol. 234, no. 2, September 2001 (2001-09-01), pages 213 - 217, XP004300664, ISSN: 0304-8853 *

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1294670C (zh) * 2004-03-03 2007-01-10 哈尔滨工业大学 一种镓酸镧基固体氧化物燃料电池用正极材料的制备方法
US7745031B2 (en) 2004-06-10 2010-06-29 Technical University Of Denmark Solid oxide fuel cell
US7601183B2 (en) 2005-02-02 2009-10-13 Technical University Of Denmark Method for producing a reversible solid oxide fuel cell
JP2008529226A (ja) * 2005-02-02 2008-07-31 テクニカル ユニバーシティ オブ デンマーク 可逆式固体酸化物型燃料電池を製造する方法
WO2007004684A1 (ja) * 2005-06-30 2007-01-11 Tokyo Institute Of Technology 酸素過剰型金属酸化物及び酸素貯蔵又は酸素選択膜用セラミックスと該金属酸化物を用いる方法及び装置
US9263758B2 (en) 2005-08-31 2016-02-16 Technical University Of Denmark Reversible solid oxide fuel cell stack and method for preparing same
WO2007093759A1 (en) * 2006-02-14 2007-08-23 Rolls-Royce Plc A solid oxide fuel cell module with multilayered anode
WO2008145145A1 (en) * 2007-05-31 2008-12-04 Elcogen As Method for the preparation of a solid oxide fuel cell single cell and the named cell
RU2424604C1 (ru) * 2007-05-31 2011-07-20 Элкоген Ас Способ изготовления одиночного твердооксидного топливного элемента
WO2009025553A1 (en) 2007-08-22 2009-02-26 Stichting Energieonderzoek Centrum Nederland Electrode for fixed oxide reactor and fixed oxide reactor
CN113299960A (zh) * 2021-05-17 2021-08-24 深圳大学 一种乙烯与电能共生型固体氧化物燃料电池及其制备方法
CN113299960B (zh) * 2021-05-17 2022-12-20 深圳大学 一种乙烯与电能共生型固体氧化物燃料电池及其制备方法
CN115939472A (zh) * 2022-11-25 2023-04-07 中国科学院宁波材料技术与工程研究所 一种抗积碳固体氧化物燃料电池及其制备方法

Also Published As

Publication number Publication date
GB0217794D0 (en) 2002-09-11
AU2003248994A1 (en) 2004-02-23
JP2005535084A (ja) 2005-11-17
CA2493029C (en) 2012-05-08
AU2003248994B2 (en) 2008-12-18
CN1672284A (zh) 2005-09-21
CN1322625C (zh) 2007-06-20
ES2598356T3 (es) 2017-01-27
US20050266297A1 (en) 2005-12-01
EP1532710A1 (en) 2005-05-25
US7504172B2 (en) 2009-03-17
CA2493029A1 (en) 2004-02-12
JP4961614B2 (ja) 2012-06-27
EP1532710B1 (en) 2016-08-17
DK1532710T3 (en) 2016-12-05

Similar Documents

Publication Publication Date Title
CA2493029C (en) Perovskite-based fuel cell electrode and membrane
JP2005535084A5 (enExample)
CN104078687B (zh) 含有碱金属或碱土金属元素的固体氧化物燃料电池的阳极材料及其制备方法和用途
US9252447B2 (en) Composite anode for a solid oxide fuel cell with improved mechanical integrity and increased efficiency
Taillades et al. Intermediate temperature anode‐supported fuel cell based on BaCe0. 9Y0. 1O3 electrolyte with novel Pr2NiO4 cathode
JP3317523B2 (ja) 固体電解質型燃料電池
CN101295791B (zh) 一种中、低温固体氧化物燃料电池三元复合阴极材料
CN105981207A (zh) 电化学能量转换装置、电池及其负极侧材料
Rostaghi Chalaki et al. LaFe0. 6Co0. 4O3 promoted LSCM/YSZ anode for direct utilization of methanol in solid oxide fuel cells
Panthi et al. Direct methane operation of a micro-tubular solid oxide fuel cell with a porous zirconia support
Sivtsev et al. Microtubular solid oxide fuel cells with a two-layer LSCF/BSCFM5 cathode
JP2001527277A (ja) 固体酸化物燃料電池の空気電極組成物
CA2136680A1 (en) Fuel cells and process for the production of the anode
JP2007066813A (ja) 燃料電池用の電極およびこれを用いた固体電解質型燃料電池
CN105130426A (zh) 一种高温化学稳定的sofc钙钛矿阳极材料及其制备方法
WO2009025553A9 (en) Electrode for fixed oxide reactor and fixed oxide reactor
US7758992B2 (en) Copper-substituted perovskite compositions for solid oxide fuel cell cathodes and oxygen reduction electrodes in other electrochemical devices
CN114630811A (zh) 电极材料、其生产方法及其用途
Jasinski et al. Single Chamber Solid Oxide Fuel Cell—Investigation of Cathodes
Rainwater Electrical Properties of BaZr0. 1Ce0. 7Y0. 1Yb0. 1O3-[delta] and Its Application in Intermediate Temperature Solid Oxide Fuel Cells
KR20240073589A (ko) 루들스덴 포퍼 구조의 화합물을 포함하는 고체산화물 공전해 셀용 공기극, 이를 포함하는 고체산화물 공전해 셀 및 고체산화물 공전해 셀의 제조방법
Bian 3D Engineered Electrodes for Intermediate Temperature Solid Oxide Fuel Cell
KR20250150790A (ko) 연속합성 반응(In-situ Process)을 통해 만들어진 복합 전해질층을 포함하는 고체산화물 연료전지 단위셀의 제조방법
JPH08264187A (ja) 固体電解質型燃料電池
KR20250115817A (ko) 고체산화물 전지용 공기극 구조 및 이의 제조방법

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ OM PH PL PT RO RU SD SE SG SK SL TJ TM TN TR TT TZ UA UG US UZ VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 2493029

Country of ref document: CA

REEP Request for entry into the european phase

Ref document number: 2003766465

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 2003766465

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 2004525554

Country of ref document: JP

WWE Wipo information: entry into national phase

Ref document number: 10523093

Country of ref document: US

Ref document number: 20038184885

Country of ref document: CN

Ref document number: 2003248994

Country of ref document: AU

WWP Wipo information: published in national office

Ref document number: 2003766465

Country of ref document: EP