Classifications

• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61Q—SPECIFIC USE OF COSMETICS OR SIMILAR TOILETRY PREPARATIONS
  • A61Q11/00—Preparations for care of the teeth, of the oral cavity or of dentures; Dentifrices, e.g. toothpastes; Mouth rinses
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
  • A61K8/00—Cosmetics or similar toiletry preparations
  • A61K8/02—Cosmetics or similar toiletry preparations characterised by special physical form
  • A61K8/0241—Containing particulates characterized by their shape and/or structure
  • A61K8/027—Fibers; Fibrils
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
  • A61K8/00—Cosmetics or similar toiletry preparations
  • A61K8/18—Cosmetics or similar toiletry preparations characterised by the composition
  • A61K8/72—Cosmetics or similar toiletry preparations characterised by the composition containing organic macromolecular compounds
  • A61K8/73—Polysaccharides
  • A61K8/731—Cellulose; Quaternized cellulose derivatives
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61Q—SPECIFIC USE OF COSMETICS OR SIMILAR TOILETRY PREPARATIONS
  • A61Q17/00—Barrier preparations; Preparations brought into direct contact with the skin for affording protection against external influences, e.g. sunlight, X-rays or other harmful rays, corrosive materials, bacteria or insect stings
  • A61Q17/04—Topical preparations for affording protection against sunlight or other radiation; Topical sun tanning preparations
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61Q—SPECIFIC USE OF COSMETICS OR SIMILAR TOILETRY PREPARATIONS
  • A61Q19/00—Preparations for care of the skin
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08B—POLYSACCHARIDES; DERIVATIVES THEREOF
  • C08B1/00—Preparatory treatment of cellulose for making derivatives thereof, e.g. pre-treatment, pre-soaking, activation
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08B—POLYSACCHARIDES; DERIVATIVES THEREOF
  • C08B11/00—Preparation of cellulose ethers
  • C08B11/02—Alkyl or cycloalkyl ethers
  • C08B11/04—Alkyl or cycloalkyl ethers with substituted hydrocarbon radicals
  • C08B11/10—Alkyl or cycloalkyl ethers with substituted hydrocarbon radicals substituted with acid radicals
  • C08B11/12—Alkyl or cycloalkyl ethers with substituted hydrocarbon radicals substituted with acid radicals substituted with carboxylic radicals, e.g. carboxymethylcellulose [CMC]
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08B—POLYSACCHARIDES; DERIVATIVES THEREOF
  • C08B11/00—Preparation of cellulose ethers
  • C08B11/20—Post-etherification treatments of chemical or physical type, e.g. mixed etherification in two steps, including purification
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08B—POLYSACCHARIDES; DERIVATIVES THEREOF
  • C08B15/00—Preparation of other cellulose derivatives or modified cellulose, e.g. complexes
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08B—POLYSACCHARIDES; DERIVATIVES THEREOF
  • C08B37/00—Preparation of polysaccharides not provided for in groups C08B1/00 - C08B35/00; Derivatives thereof
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
  • D21H17/20—Macromolecular organic compounds
  • D21H17/21—Macromolecular organic compounds of natural origin; Derivatives thereof
  • D21H17/24—Polysaccharides
  • D21H17/25—Cellulose
  • D21H17/26—Ethers thereof
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61Q—SPECIFIC USE OF COSMETICS OR SIMILAR TOILETRY PREPARATIONS
  • A61Q19/00—Preparations for care of the skin
  • A61Q19/08—Anti-ageing preparations
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H21/00—Non-fibrous material added to the pulp, characterised by its function, form or properties; Paper-impregnating or coating material, characterised by its function, form or properties
  • D21H21/06—Paper forming aids
  • D21H21/10—Retention agents or drainage improvers
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H21/00—Non-fibrous material added to the pulp, characterised by its function, form or properties; Paper-impregnating or coating material, characterised by its function, form or properties
  • D21H21/14—Non-fibrous material added to the pulp, characterised by its function, form or properties; Paper-impregnating or coating material, characterised by its function, form or properties characterised by function or properties in or on the paper
  • D21H21/16—Sizing or water-repelling agents
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H21/00—Non-fibrous material added to the pulp, characterised by its function, form or properties; Paper-impregnating or coating material, characterised by its function, form or properties
  • D21H21/14—Non-fibrous material added to the pulp, characterised by its function, form or properties; Paper-impregnating or coating material, characterised by its function, form or properties characterised by function or properties in or on the paper
  • D21H21/18—Reinforcing agents
• • D—TEXTILES; PAPER
  • D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
  • D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
  • D21H21/00—Non-fibrous material added to the pulp, characterised by its function, form or properties; Paper-impregnating or coating material, characterised by its function, form or properties
  • D21H21/14—Non-fibrous material added to the pulp, characterised by its function, form or properties; Paper-impregnating or coating material, characterised by its function, form or properties characterised by function or properties in or on the paper
  • D21H21/18—Reinforcing agents
  • D21H21/20—Wet strength agents

Definitions

• the present invention relates to derivatized microfibrillar polysaccharide. More specifically, the present invention relates to microfibrillar polysaccharide stabilized by steric and/or electrostatic forces, where the electrostatic forces are provided by anionic charge, or by a combination of both anionic and cationic charge. BACKGROUND OF THE INVENTION Polysaccharides are often found in nature in forms having fibrous morphology.
• Polysaccharides which are not found in nature in fibrous form can often be transformed into fibrous morphologies using fiber spinning techniques. Whether the fibrous morphology is of natural or artificial origin, the polysaccharide will often be present such that the fibers can be reduced to fibrillar and microfibrillar sub-morphologies through the application of energy.
• Fibrillar and microfibrillar cellulose obtained in this manner have been considered for use in applications, including use as additives to aqueous-based systems in order to affect rheological properties, such as viscosity.
• the use level of these materials in aqueous systems is often on the order of about 2% by weight, below which these materials have a tendency to poorly occupy volume, and to exhibit gross inhomogeneities in distribution.
• Microfibrillated cellulose and its manufacture are discussed in U.S. Patent Nos. 4,500,546; 4,487,634; 4,483,743; 4,481,077; 4,481,076; 4,464,287; 4,452,722; 4,452,721; 4,378,381; 4,374,702; and 4,341,807, the disclosures of which are hereby incorporated by reference thereto.
• Nanofibrils are characterized in WO 98/02486 (PCT/FR97/01290), WO 98/02487 (PCT/FR97/01291), and WO 98/02499 (PCT/FR97/01297), the disclosures of which are hereby incorporated by reference.
• Nanofibrils are characterized as having diameters in the range of about 2 to about 10 nanometers.
• EP 845495 discusses cationic cellulose particulate which is characterized as insoluble, positively charged, and used in water treatment, specifically to treat water in a paper manufacturing plant. In paper making this cationic particulate is said to remove anionic trash from the water.
• the particles are obtained by milling, which is stated to reduce particle size uniformly such that particles are typically round as described by a length/diameter ratio of approximately 1.
• Particle size is stated to be 0.001 mm (i.e., 1 ⁇ m), and preferably 0.01 mm (10 ⁇ m)
• EP 859011 (“EP OH”) is directed to a process for obtaining cationic cellulose microfibrils or their soluble derivatives. The process is described as including making a cationic cellulose derivative and processing the derivative through a high pressure homogenizer to form transparent gels. The product can be dehydrated and rehydrated. Viscosity measurements are reported on the product at a concentration of 2% in water.
• EP '011 indicates that the degree of substitution ("DS") of the cellulose can range from 0.1 to 0.7, with a DS of between 0.2 and 0.7, 0.3 and 0.6, and 0.5 and 0.6 characterized as representing increasing orders of preference. The examples show cellulose with a DS ranging from a low of 0.24 up to 0.72.
• Gelling is reported to occur above a micro fibril concentration of 10 g/L, or above 1%, in water.
• EP '011 defines gelling as occurring when G' > G", where G' is the dynamic storage modulus and G" is the dynamic loss modulus.
• Microfibrillated chitosan is reported to form uniplanar, oriented sheets upon drying by H. Yokata, J. Polymer Sci., Part C: Polymer Letters, 24:423-425 (1986). This article mentions that at a level of 4% chitosan in water, a gel is formed having a viscosity of 26,600 cps (Brookfield, 20° C, rotor #7, lOrpm).
• the microfibrillated chitosan is made by homogenization of commercial chitosan flakes in a Gaulin homogenizer.
• the commercial chitosan is deacetylated using sodium hydroxide.
• JP 59 [1984]-84938 discusses a method for producing a chitosan suspension.
• Commercial chitosan separated and purified from crabs and lobsters is pulverized to pieces having maximum length of about 1-2 mm. The pieces are then suspended in water at up to 15% chitosan, and are run in multiple passes through a high pressure homogenizer at between 3,000 and 8,000 psi.
• microfibrillar polysaccharides whose viscosity- affecting properties are achieved without the presence of cationic functionalities, at least in part because of the general lack of suitability of cationic materials for use in foods. It would also be desirable to obtain microfibrillar polysaccharides that are capable of forming a gel at concentrations of 1% or less, thereby providing economy and ease of formulation, while still providing necessary rheological behavior and homogeneity of distribution.
• emulsion failure still takes place in such emulsions, either through density- driven separation, also referred to as creaming, or through gellation. It would accordingly be desirable to develop a material that could be added to emulsions to provide long-term stability.
• the present intention is directed to derivatized microfibrillar polysaccharide, methods for its production, and applications for its use.
• the derivatized microfibrillar polysaccharides is derivatized to contain substituents that provide electrostatic and/or steric functionality; where electrostatic functionality is present, it includes, but is not necessarily limited to, the presence of anionic charge.
• Polysaccharides suitable for use in the present invention include cellulose, hemicellulose, chitin, chitosan, guar gum, pectin, alginate, agar, xanthan, starch, amylose, amylopectin, alternan, gellan, mutan, dextran, pullulan, fructan, locust bean gum, carrageenan, glycogen, glycosaminoglycans, murein, bacterial capsular polysaccharides, and derivatives thereof. Mixtures of these may be employed.
• Preferred polysaccharides are cellulose, chitin, chitosan, pectin, agar, starch, carrageenan, and derivatives thereof, used singly or in combination, with cellulose being most preferred.
• the cellulose may be obtained from any available source, including, by way of example only, chemical pulps, mechanical pulps, thermal mechanical pulps, chemical-thermal mechanical pulps, recycled fibers, newsprint, cotton, soybean hulls, pea hulls, corn hulls, flax, hemp, jute, ramie, kenaf, manila hemp, sisal hemp, bagasse, corn, wheat, bamboo, velonia, bacteria, algae, fungi, microcrystalline cellulose, vegetables, and fruits.
• Preferred sources of cellulose include purified, optionally bleached wood pulps produced from sulfite, kraft, or prehydrolyzed kraft pulping processes; purified cotton linters; fruits; and vegetables.
• the derivatized microfibrillar polysaccharides that may be obtained using cellulose include, but are not limited to, hydroxyethyl cellulose, ethylhydroxyethyl cellulose, carboxymethylcellulose, carboxymethylhydroxyethyl cellulose, hydroxypropylhydroxyethyl cellulose, methyl cellulose, methylhydroxypropyl cellulose, methylhydroxyethyl cellulose, carboxymethylmethyl cellulose, hydrophobically modified carboxymethylcellulose, hydrophobically modified hydroxyethyl cellulose, hydrophobically modified hydroxypropyl cellulose, hydrophobically modified ethylhydroxyethyl cellulose, hydrophobically modified carboxymethylhydroxyethyl cellulose, hydrophobically modified hydroxypropylhydroxyethyl cellulose, hydrophobically modified methyl cellulose, hydrophobically modified methylhydroxypropylhydroxyethyl cellulose, hydrophobically modified methyl cellulose, hydrophobically modified methylhydroxypropyl cellulose
• the derivatized microfibrillar cellulose of the present invention may form a gel in water throughout the concentration range of between about 0.01 % and about 100%, or throughout the concentration range of between about 0.01 % and about 50 % in water, or at at least one point in the concentration range of from about 0.05 % up to about 0.99% in water.
• the derivatized microfibrillar cellulose of the present invention forms a gel in water at a concentration of about 0.95%.
• the derivatized microfibrillar polysaccharide may be used in the presence of a solvent, in which it is substantially insoluble.
• solvents include water, alcohol, and oil.
• the derivatized microfibrillar polysaccharides of the present invention may have a degree of substitution of less than about 0.5, less than about 0.35, less than about 0.2, less than about 0.18, or less than about 0.1.
• a preferred range for the degree of substitution is between about 0.02 and about 0.5, with a range of between about 0.05 and about 0.2 being more preferred.
• the degree of substitution representing those substituents which provide electrostatic functionality in the form of anionic charge is preferably least about 0.05.
• Anionic charge may be provided, for example, by carboxyl, sulfate, sulfonate, phosphonate, or phosphate groups, or combinations thereof. Where cationic charge is also present, both charges may be provided by the same groups or substituent (i.e., the substituent may be amphoteric or zwitterionic); or, the derivatized microfibrillar polysaccharide may be derivatized to contain both substituents that contain anionic charge and substituents that contain cationic charge.
• the derivatized microfibrillar polysaccharides of the present invention may be obtained by blending two or more separate derivatized microfibrillar polysaccharides, where at least one has been derivatized to provide anionic charge, and at least one other has been derivatized to provide anionic charge, cationic charge, or both.
• the derivatized microfibrillar polysaccharide of the present invention may have a molar substitution of less than about 3.0, or of less than about 1.5, or of less than about 1.0, or of less than about 0.5.
• the range of molar substitution may be from about 0.5 to about 3.0.
• Steric functionality may be provided, by way of non-limiting example, by hydroxyethyl groups, hydroxypropyl groups, methyl groups, ethyl groups; straight- or branched-chain alkyl, alkenyl, or alkynyl groups having from about 4 to about 30 carbons; and/or aryl, arylalkyl, arylalkenyl, cyclic, and herterocyclic hydrocarbons having from about 4 to about 30 carbons.
• the derivatized microfibrillar polysaccharide contains carboxymethylcellulose, and has a degree of substitution of less than about 0.35, or of less than about 2.0.
• the range of degree of substitution may be from about 0.02 to about 0.2, with a range of from about 0.10 to about 0.2 being preferred.
• the derivatized microfibrillar cellulose of the present invention may form a gel at a concentration of less than about 1% in water.
• the present invention is directed to a comestible composition of matter containing the derivatized microfibrillar polysaccharide of the present invention.
• the comestible composition of matter may, by way of non-limiting ex.ample, be a low fat, reduced fat, or fat-free food spread, such as a mayonnaise, or a salad dressing.
• the comestible composition may contain a pharmaceutically active ingredient.
• the derivatized microfibrillar polysaccharide may be used to provide or improve a controlled, sustained, or delayed release of a component of the comestible composition, including in particular a pharmaceutically active ingredient.
• the derivatized microfibrillar polysaccharides of the present invention may be used in non-comestible, spreadable compositions of matter, such as skin care lotions or creams, or sunscreen lotions or creams.
• the present invention is further directed to a paper composition containing the derivatized microfibrillar cellulose, and particularly, though not exclusively, microfibrillar carboxymethylcellulose.
• the derivatized microfibrillar polysaccharide may be produced by using a derivatizing step to treat a microfibrillar polysaccharide to obtain the derivatized microfibrillar polysaccharide.
• a derivatized polysaccharide may be microfibrillated to produce the derivatized microfibrillar polysaccharide.
• the steps of micro fibrillation and derivatization may take place at substantially the same time.
• cellulose is first derivatized with monochloroacetic acid or a salt thereof under alkaline conditions to produce carboxymethylcellulose; the carboxymethylcellulose is suspended in water; and the resulting suspension is homogenized to produce microfibrillated carboxymethylcellulose.
• the derivatizing step may include contacting a non-microfibrillar polysaccharide with a swelling agent, such as an anionic reagent, and may take place under alkaline conditions.
• a swelling agent such as an anionic reagent
• alkaline conditions may include contacting the cellulose with the anionic reagent in the presence of an alkaline reagent which is sodium hydroxide, an oxide or hydroxide of an alkali metal or alkaline earth metal, an alkali silicate, an alkali aluminate, an alkali carbonate, an amine, ammonium hydroxide, tetramethyl ammonium hydroxide, or combinations thereof.
• the derivatization may take place at high solids.
• Micro fibrillation may be accomplished by applying energy to a non-microfibrillar polysaccharide under conditions sufficient to produce microfibrillar polysaccharide.
• the non-microfibrillar may optionally be enzyme-treated before microfibrillizing. More specifically, microfibrillation may be accomplished using homogenization, pumping, mixing, heat, steam explosion, pressurization-depressurization cycle, impact, grinding, ultrasound, microwave explosion, milling, and combinations of these.
• the non-microfibrillar polysaccharide is passed through a homogenizer under conditions sufficient to produce microfibrillar cellulose; those conditions may include a pressure differential of at least about 3,000 psi, and passing the non- microfibrillar polysaccharide through the homogenizer at least three times.
• the method should be conducted to yield a derivatized microfibrillar polysaccharide that is substantially insoluble in the solvent of use. Water is a preferred solvent of use, but other solvents, including but not limited to alcohols and oils, are contemplated for various applications.
• the present invention extends to derivatized microfibrillar polysaccharide produced by the above methods.
• the present invention is directed to a method of modifying the rheological properties of a liquid composition of matter by incorporating the derivatized microfibrillar polysaccharides of the present invention into the liquid composition of matter.
• the derivatized microfibrillar polysaccharide may be incorporated into a water-containing system, where it may be used, for example, to provide scale control and/or corrosion control.
• the rheological properties which may be modified by the derivatized microfibrillar polysaccharide include viscosity, suspension stability, gel insensitivity to temperature, shear reversible gelation, yield stress, and liquid retention.
• Liquid compositions which may be Theologically modified include, as non- limiting examples, foods, pharmaceuticals, neutraceuticals, personal care products, fibers, papers, paints, coatings, and construction compositions. These include oral care products; creams or lotions for epidermal application (such as moisturizing, night, anti- age, or sunscreen creams or lotions); food spreads, including reduced fat, low fat, or fat free food spreads (such as mayonnaises); and drilling fluids.
• the present invention further extends to a method of improving the physical and or mechanical properties of a coating composition by incorporating, into the coating composition, an effective amount of the derivatized microfibrillar polysaccharide.
• the physical and/or mechanical properties that may be improved in this manner include film forming, leveling, sag resistance, strength, durability, dispersion, flooding, floating, and spatter.
• the present invention has particular utility in the field of paper manufacture and treatment.
• derivatized microfibrillar cellulose may be used to improve one or more of sizing, strength, scale control, drainage, dewatering, retention, clarification, formation, adsorbency, film formation, membrane formation, and polyelectrolyte complexation during paper manufacture.
• the derivatized microfibrillar cellulose may be used as a drainage aid and/or as a sizing agent.
• a polyelectrolyte complex containing the derivatized microfibrillar polysaccharide is also within the scope of the present invention.
• Microfibrillated carboxymethylcellulose is a particularly preferred embodiment for use in paper applications.
• the derivatized microfibrillar cellulose may be used, by way of further example, in a papermaking machine to increase the rate of drainage and/or dewatering during paper manufacture; for retention of organic and/or inorganic dispersed particles in a sheet of paper during its manufacture; to improve the uniformity of formation of a sheet of paper during its manufacture; and to improve the strength of a sheet of paper.
• the derivatized microfibrillar cellulose may be used in combination with any of the additives and performance enhancers conventionally used in paper manufacture, including cationic polyacrylamides; polydiallyldimethyl-ammonium chloride; cationic starch; derivatives of cellulose containing ammonium or mono-, di-, or trialkyl ammonium substituents; derivatives of guar gum containing ammonium or mono-, di-, or trialkyl ammonium substituents; resins formed by the reaction of amines and or polyamines with epichlorohydrin; aluminum salts; hydrolyzed or partially hydrolyzed aluminum salts; complexes of hydrolyzed or partially hydrolyzed aluminum salts with organic or inorganic species; at least one polymer of ethylene oxide, ethyleneimine, allylamine, or vinylamine; and, at least one copolymer or terpolymer of ethylene oxide, ethyleneimine, allylamine, or vinylamine; and combinations thereof.
• the particles so retained may include one or more of pulp fines, fillers, sizing agents, pigments, clays, detrimental organic particulate materials, and detrimental inorganic particulate materials.
• the stability of an emulsion, dispersion, or foam system may be improved by including, in the system, the derivatized microfibrillar polysaccharide of the present invention.
• the derivatized microfibrillar polysaccharide may be added to an existing system; added to a formulation which will be processed into such a system; or added during processing of such a formulation.
• a derivatized non-microfibrillated polysaccharide (where "non- microfibrillated” includes an incompletely microfibrillated polysaccharide) may be added to a formulation prior to completion of processing, and subsequent processing may then be conducted in a manner that will microfibrillate the polysaccharide.
• a microfibrillated polysaccharide may be added to the formulation, with subsequent processing conducted so as to derivatize the microfibrillated polysaccharide.
• both derivatization and microfibrillation may take place during processing.
• Systems which may be treated in this manner include water-in-oil and oil- in-water emulsions.
• the present invention also extends to emulsion, dispersion, and foam systems produced by the above methods; and, to emulsion, dispersion, or foam systems that contain the derivatized microfibrillar polysaccharide of the present invention.
• Figure 1 shows the dynamic mechanical spectra of Example 7, Sample 1.
• Figure 2 shows the dynamic mechanical spectra of Example 7, Sample 2.
• Figure 3 shows the dynamic mechanical spectra of Example 7, Sample 3.
• Figure 4 shows the dynamic mechanical spectra of Example 7, Sample 4.
• Figure 5 shows the dynamic mechanical spectra of Example 7, Sample 5.
• Figure 6 shows the dynamic mechanical spectra of Example 13, Sample 1.
• Figure 7 shows the dynamic mechanical spectra of Example 13, Sample 2.
• Figure 8 shows the dynamic mechanical spectra of Example 13, Sample 3.
• Figure 9 is a transmission electron micrograph of a sample microfibrillar carboxymethylcellulose prepared as in example 3 below, with a degree of substitution of about 0.17, negative stained with urinal acetate, at a magnification of 10,000X.
• DETAILED DESCRIPTION OF THE INVENTION The present invention comprises derivatized microfibrillar polysaccharide.
• Suitable polysaccharides for use in the present invention include, without limitation, cellulose, hemicellulose, chitin, chitosan, guar gum, pectin, alginate, agar, xanthan, starch, amylose, amylopectin, alternan, gellan, mutan, dextran, pullulan, fructan, locust bean gum, carrageenan, glycogen, glycosaminoglycans, murein, bacterial capsular polysaccharides, and derivatives thereof, with cellulose being prefened.
• the polysaccharide may be used as is, or spinning may be used to generate or improve fibrous structure.
• Cellulose is a preferred polysaccharide for use in the present invention.
• Sources of cellulose for use in this invention include the following: (a) wood fibers, such as from chemical pulps, mechanical pulps, thermal mechanical pulps, chemical-thermal mechanical pulps, recycled fibers, newsprint; (b) seed fibers, such as from cotton; (c) seed hull fiber, such as from soybean hulls, pea hulls, corn hulls; (d) bast fibers, such as from flax, hemp, jute, ramie, kenaf; (e) leaf fibers, such as from manila hemp, sisal hemp; (f) stalk or straw fibers, such as from bagasse, corn, wheat; (g) grass fibers, such as from bamboo; (h) cellulose fibers from algae, such as velonia; (i) bacteria or fungi; and (j) parenchymal cells, such as from vegetables and fruits, and in particular sugar beets, and citrus fruits such as lemons, limes, oranges, grapefruits.
• wood fibers such as from chemical pulps, mechanical
• Microcrystalline forms of these cellulose materials may also be used.
• Preferred cellulose sources are (1) purified, optionally bleached, wood pulps produced from sulfite, kraft (sulfate), or prehydrolyzed kraft pulping processes, (2) purified cotton linters, and (3) fruits and vegetables, in particular sugar beets and citrus fruits.
• the source of the cellulose is not limiting, and any source may be used, including synthetic cellulose or cellulose analogs.
• Cellulose is found in nature in several hierarchical levels of organization and orientation. Cellulose fibers comprise a layered secondary wall structure within which macrofibrils are arranged. Macrofibrils comprise multiple microfibrils which further comprise cellulose molecules arranged in crystalline and amorphous regions.
• Cellulose microfibrils range in diameter from about 5 to about 100 nanometers for different species of plant, and are most typically in the range of from about 25 to about 35 nanometers in diameter.
• the microfibrils are present in bundles which run in parallel within a matrix of amorphous hemicelluloses (specifically xyloglucans), pectinic polysaccharides, lignins, and hydroxyproline rich glycoproteins (includes extensin).
• Microfibrils are spaced approximately 3-4 nm apart with the space occupied by the matrix compounds listed above. The specific arrangement and location of the matrix materials and how they interact with the cellulose microfibrils is not yet fully known.
• polysaccharide microfibrils refer to small diameter, high length-to-diameter ratio substructures which are comparable in dimensions to those of cellulose microfibrils occurring in nature.
• polysaccharide microfibrils may have diameters in the range of about 20 to about 100 nanometers, combined with lengths providing high aspect ratios, such as in excess of 100, in excess of 500, or in excess of 1 ,000.
• microfibrils and micro fibrillation While the present specification and claims refer to microfibrils and micro fibrillation, the scope of the present invention also includes nanofibrils (cellulosic or otherwise), and the rheology modification, stabilization, and other properties that may be obtained with microfibrils by practicing the present invention may also be obtained using nanofibrils, either alone or in combination with microfibrils.
• fibers spun from polysaccharides can be derivatized and microfibrillated into fibrous structures having dimensions on the order of those found naturally in cellulose. Further background on the structure, functions, and biogenesis of native cellulose may be found in Haigler, C.H., Cellular Chemistry and Its Applications, Nevell, pp. 30-83 (1985), the entirety of which is hereby incorporated by reference.
• the derivatized microfibrillar polysaccharide of the present invention is characterized by being in microfibrillar form, and by the presence of substituents that provide steric and or electrostatic functionality.
• the amount of substituent present may be quantified by the degree of substitution, or DS, in the case of some anionic and cationic substituents, and by the molar substitution, or MS, in the case of steric substituents.
• the degree of substitution which will vary with the molecular weight of the polysaccharide, is the average number of substituted hydroxyl groups per anhydrosaccharide unit, while the molar substitution is the average number of substituent groups added per anhydrosaccharide unit.
• the DS and MS determine the solubility of the derivatized polysaccharide, and may be readily adjusted to obtain a derivatized polysaccharide that is substantially insoluble in the environment of use, whether aqueous or non-aqueous. While the environment of use will frequently be aqueous, the derivatized microfibrillar polysaccharides of the present invention have utility in applications having other solvents or liquid carriers, such as paints, coating, lacquers, oil-rich foods, inks (including but not limited to ink-jet inks), personal care products, cosmetics, and water-in-oil emulsions.
• solvents or liquid carriers such as paints, coating, lacquers, oil-rich foods, inks (including but not limited to ink-jet inks), personal care products, cosmetics, and water-in-oil emulsions.
• any suitable method may be used to obtain the derivatized microfibrillar polysaccharide.
• the steps of micro fibrillation and derivatization to impart steric and/or electrostatic functionality to the polysaccharide may be carried out separately or combined to arrive at the end result. Therefore, a non-microfibrillar polysaccharide starting material may either be derivatized with anionic groups, with both anionic and cationic groups, or with a blend or mixture of anionic groups and cationic groups, and then microfibrillated, or may first be microfibrillated and then derivatized.
• the starting material is microfibrillar polysaccharide
• the derivatizing step would be necessary
• the starting material is a polysaccharide that has already been properly derivatized with anionic or both anionic and cationic groups, only the microfibrillation step is required.
• the degree of substitution (for electrostatic derivatization), and/or of molar substitution (for steric derivatization), of the polysaccharide should be sufficiently low so that the derivatized microfibrillar polysaccharide will be substantially insoluble in the solvent or carrier that is present in the intended environment of use.
• the solvent or carrier will be water, and in such applications the degree of substitution and/or the molar substitution should be such that the derivatized microfibrillar polysaccharide is substantially insoluble in water.
• a polar solvent or carrier such as an alcohol
• a non-polar solvent or carrier such as an oil
• the degree of substitution and/or the molar substitution should be adjusted to obtain a derivatized microfibrillar polysaccharide that is substantially insoluble in the solvent or carrier used in the application of interest, which, for purposes of convenience, will hereafter be referred to as the "solvent of use”.
• the derivatized microfibrillar polysaccharide should be sufficiently insoluble in the environment of use to provide the desired properties in the intended application.
• substantially insoluble material may be confirmed by observation of a 1-5% suspension of the material in question in the solvent or carrier of use under a light microscope at sufficient magnification to see insoluble material.
• a size determination may be made by preparing a suspension of the material under consideration at approximately 0.1-0.01% in a liquid non-solvent which is effective in dispersing microfibrils. This suspension is then dried on a transmission electron microscope (TEM) grid, the sample is coated to protect it from electron beam damage, and examined at sufficient magnification and focus to observe structure in the 1-1000 nanometer range.
• TEM transmission electron microscope
• microfibrillar elements are present they can be detected under these conditions, and the combination of insolubility under the light microscope and microfibrillar structure under the TEM will indicate the presence of substantially insoluble microfibrillar material. See Figure 9 for an example transmission electron micrograph of a microfibrillar carboxymethylcellulose prepared as in example 3 below, having a DS of about 0.17
• substituteduents shall be used herein to mean chemical species that provide steric stabilization to the polysaccharide; chemical species that provide electrostatic functionality to the polysaccharide through .anionic charge; chemical species that provide electrostatic functionality to the polysaccharide through a combination of both anionic and cationic charge; and combinations of the foregoing.
• electrostatic means either anionic charge, or a combination of both anionic and cationic charge, whether as groups both present on a single substituent, or as groups provided separately on two or more substituents.
• “Derivatization” refers not only to chemical reactions resulting in covalent bonds, but to any process whereby the substituents become sufficiently associated with the polysaccharide to provide the rheological and other benefits of the present invention, and may include, for example, adsorption.
• references to the combination of both anionic and cationic charge on the polysaccharide include the use of substituents that contain both types of charge (i.e., amphoteric and/or zwitterionic substituents); the combined use of substituents which individually contain only anionic or only cationic charge, resulting in derivatized polysaccharide with a distribution of substituents that includes both anionic groups and cationic groups; and, blending of two or more derivatized polysaccharides where at least one derivatized polysaccharide includes at least anionic substituents and at least one other derivatized polysaccharide includes at least cationic substituents, resulting in a blend that contains both anionically derivatized polysaccharide and cationically derivatized polysaccharide.
• "derivatized” does not include the naturally- occurring, de minimis presence of groups that would only provide the steric and/or electrostatic functionality required by the present invention at concentrations higher than those found in nature.
• naturally-occurring cellulose may contain very low levels of anionic charge, which may still be present after micro fibrillation.
• microfibrillated cellulose is not "derivatized” as that term is used in the present application, both because its degree of substitution has not been changed from its natural state, and because the amount of charge present in such microfibrillated cellulose would not provide the benefits of the present invention.
• the sequence of steps used to arrive at the derivatized microfibrillar polysaccharide of the present invention is not critical.
• the starting material used to make the derivatized microfibrillar polysaccharide may be in microfibrillar or non-microfibrillar form.
• the starting material may aheady be derivatized with steric and/or electrostatic substituents, or not.
• substituents may be placed on the polysaccharide followed by microfibrillation, or the microfibrillation may be carried out first, followed by the placement of the substituents onto the resulting microfibrils. It is also acceptable to process polysaccharide into fibrils, place the substituents on the fibrils, and then further process the fibrils into microfibrils. Simil ⁇ irly, any non-microfibrillar form of polysaccharide which aheady contains such substituents may be processed into microfibrillar form. Moreover, derivatization and microfibrillation may be carried out simultaneously.
• polysaccharides will contain some quantity of both microfibrillar and non-microfibrillar structure both before and after processing, and that the ratio between the two structures may range from polysaccharide that is substantially completely microfibrillar, to polysaccharide that is substantially completely non-microfibrillar.
• microfibrillar “microfibrillated”, and the like include polysaccharides that are substantially completely microfibrillated, and those which may be substantially microfibrillated while containing minor but significant amounts of non-microfibrillar structure, provided the polysaccharide is sufficiently microfibrillated to confer the benefits afforded by the present invention.
• microfibrillation process generally requires less energy, and/or is more efficient, if the polysaccharide has already been derivatized. Without being bound by theory, this may be because the presence of the steric and/or electrostatic functionalities on the polysaccharide 'loosens' the structure of fibril bundles.
• microfibrillating a polysaccharide that has aheady been derivatized may result in a derivatized microfibrillar polysaccharide with relatively longer microfibrils as compared to effecting derivatization after microfibrillation. This is particularly significant because the energy required for microfibrillation can be significantly reduced by amounts of derivatization which are below the level that would render the resulting derivatized microfibrillar polysaccharide freely soluble in water.
• cellulose resulting in a DS on the order of 0.1 or 0.2 will 'loosen' the fibril bundles in cellulose enough to permit microfibrillation using conventional shearing devices such as a homogenizer, impingement mixer, or ultrasonicator.
• These low DS cellulose microfibrils have diameters on the order of 50 nanometers combined with lengths of up to 500 microns, resulting in aspect ratios in excess of 1,000. While the low DS allows microfibrillation, it is too low to allow the resulting material to be fully soluble in the solvent or carrier of use at the concentrations of interest.
• insoluble regions in the fibers may explain the data showing maximum gel formation at low DS's. These gels may be strengthened by weak association of the more hydrophobic unsubstituted regions.
• the stabilization or derivatization is accomplished by the generation or placement of substituents onto the fibril and/or micro fibril. It appears that the substituents become associated predominantly with the surface regions of the fibrils or microfibrils. Regardless of the precise mechanism, in functional terms micro fibril-micro fibril contact is inhibited by steric and/or electrostatic mechanisms or forces.
• the presence of the substituents also causes the microfibrils to occupy more volume than when they are not derivatized, possibly due to inhibition of contact along at least part of the length of the microfibrils. Rheological performance of the resulting derivatized microfibrillar polysaccharide is enhanced at low concentration since volume is better occupied and the materials are distributed more homogeneously.
• steric functionality or stabilization is provided by the formation of a protective barrier or sheath around a particle (such as a cellulose fibril or microfibril) to prevent flocculation.
• a particle such as a cellulose fibril or microfibril
• it may be achieved by a material, such as a polymer, being physically adsorbed on the surface of the particle, thereby preventing two particles from coming closer than a distance that is twice the sum of the radius of the particle and the thickness of the adsorbed layer.
• This interaction which as noted may be a polymer-polymer interaction, results in forces, such as osmotic and/or entropic forces, that repel the particles.
• a substituent used to provide the polysaccharide with steric functionality or stabilization may be neutral, anionic, cationic, amphiphilic, amphoteric, and/or zwitterionic.
• the surfaces of the derivatized microfibrils appear to have some areas free of the substituents such that some limited interaction between microfibrils still takes place. Limited interaction may even be necessary to facilitate network formation, and may be a cause of the rheological attributes of interest such as yield stress, shear reversible gelation, and insensitivity of the modulus to temperature.
• the length/diameter ratio, or aspect ratio, of the fibrils and microfibrils also contributes to the performance of the materials of the present invention.
• Any suitable process may be used to generate or place the substituents on the polysaccharide.
• the possible processes will generally be refened to collectively as "derivatization” herein; however, within the context of this invention, derivatization is used to mean any process which results in a polysaccharide (including fibrillar and microfibrillar polysaccharide) having the substituents sufficiently associated with the polysaccharide to provide the desired benefit(s), and includes not only chemical reactions resulting in covalent bonding, but also physical adsorption.
• Possible derivatization processes include any synthetic method(s) which may be used to associate the substituents with the polysaccharide. More generally, the stabilization or derivatization step may use any process or combination of processes which promote or cause the placement or generation of the substituents.
• the conditions for treating non-microfibrillar polysaccharide should generally include both alkalinity and swelling of the polysaccharide, in order to make the surface of the fibrils more accessible to the placement or generation of the substituents. Alkalinity and swelling may be provided by separate agents, or the same agent may both provide alkalinity and cause swelling of the polysaccharide.
• alkaline agents often serve multiple purposes, in that they may catalyze the reaction between the polysaccharide and the substituent, optionally de-protonate the derivative, and swell open the polysaccharide structure to allow access of the reagents to carry out the derivatization.
• Specific chemical methods which may be used to achieve the present invention include but are not limited to generation of anionic groups (such as carboxyl, sulfate, sulfonate, phosphonate, and/or phosphate); generation of both anionic and cationic groups (such as quaternary amine and/or amine); and generation of steric groups, on or near the surface of the particulate polysaccharide.
• Alkaline conditions are preferably obtained by using sodium hydroxide.
• any material that functions as a solvent for the polysaccharide of choice may be used, and alternative alkaline agents include alkali metal or alkaline earth metal oxides or hydroxides; alkali silicates; alkali aluminates; alkali carbonates; amines, including aliphatic hydrocarbon amines, especially tertiary amines; ammonium hydroxide; tetr.amethyl ammonium hydroxide; lithium chloride; N- methyl morpholine N-oxide; and the like.
• swelling agents may be added to increase access for derivatization. Interfibrillar and intercrystalline swelling agents are prefened, particularly swelling agents used at levels which give interfibrillar swelling, such as sodium hydroxide at an appropriately low concentration.
• derivatization of these fibrous polysaccharides be performed in a manner which limits the formation of microfibrils which are soluble in the intended end use composition, as these may not contribute significantly to the desired rheological performance. This typically limits the degree of derivatization which can be made where derivatization at higher levels would make the polysaccharide soluble in the end use composition. Specific limits may be readily determined based on the application in question, but as a matter of general guidance it is preferred that the degree of substitution (DS) be below about 0.5, or below about 0.35, or below about 0.2, or below about 0.18, or below about 0.1.
• the derivatization may be carried out in any suitable manner, including but not limited to suspension in water; in organic solvent, either alone or in mixtures with water; in solution; and in high solids, either with water alone or with water and a minor amount of organic solvent.
• high solids refers to a polysaccharide content of greater than about 25%.
• Optional derivatizations or functionalities which may also be placed on the polysaccharide include but are not limited to short chain aliphatic and other hydrophobic-type substitutions; oligomeric and polymeric substitutions; unch.arged substitutions, as for example short chain ethylene and propylene glycols; other associative-type functionality; surfactant-like functionality; methyl; ethyl; propyl; and combinations of these. These substitutions are optional in that they may not be intended for stabilization of the polysaccharide, and will instead provide additional functionality such as surface activity, emulsification power, adsorption characteristics, and the like.
• the method for processing a non-microfibrillar form of polysaccharide into the microfibrillar form may be carried out either before or after the derivatization reaction.
• the prefened method involves the use of a homogenizer on a dilute suspension of the non-microfibrillar polysaccharide in an aqueous medium.
• the aqueous medium optionally may have additives such as swelling agents, in particular interfibrillar and/or intercrystalline swelling agents, for example sodium hydroxide, to aid in improving the ease of micro fibril generation.
• a more prefened method of microfibrillation involves the use of mechanical energy on an aqueous suspension of derivatized polysaccharide which has not been dried.
• microfibrillation processes include, by way of non- limiting example, use of an impingement mixer; heat; steam explosion; pressurization- depressurization cycle; freeze-thaw cycle; impact; grinding (such as a disc grinder); pumping; mixing; ultrasound; microwave explosion; and milling. Combinations of these may also be used, such as milling followed by homogenization.
• any method of reducing particle size may be used, but methods for reducing particle size while preserving a high aspect ratio in the polysaccharide are prefened. As described previously, the degree of substitution of the polysaccharide also affects the ease of processing the polysaccharide to microfibrillar form.
• the process to generate the particulate may either be run by the consumer in the final application such that the particulate is generated in situ, or be run as described above in aqueous media, the material dehydrated, and the resulting particulate dried.
• the dried particulate of this invention hereafter refened to as the ready-to-gel or RTG form, can be rehydrated readily in polar solvents to obtain the desired rheological attributes. Dehydration can be accomplished by displacing water with less polar solvents and drying, and can be accelerated by protonation or shielding of charged groups if they are present.
• applications where the derivatized microfibrillar polysaccharide of the present invention have particular utility include those where the desired rheological attributes include at least one of yield stress, shear reversible gelation, and a modulus which is insensitive to temperature.
• the ability to provide the rheological attributes described herein also makes it possible to provide stabilization of mixtures of liquids and solids having different densities; gel-like properties, including mouth feel; pumpable gels; stabilization at elevated temperatures; and, control of hydration and diffusion.
• the utility of the present derivatized microfibrillar polysaccharides includes, without limitation, foods, personal care products, household products, pharmaceuticals, neutraceuticals, paper manufacture and treatment, coating compositions, water treatment, drilling fluids, agriculture, construction, .and spill control and/or recovery.
• the derivatized microfibrillar polysaccharides of the present invention may be useful as rheology modifiers; as stabilizers, such as by inhibiting creaming or settling in suspensions; and as non-digestable dietary fiber. They may also be used to control ice crystal growth during, for example, ice cream manufacture and storage.
• the derivatized microfibrillar polysaccharides may be used to stabilize emulsions, dispersions, suspensions, and foams, and may find use in creams, lotions, gels, and pastes, including those intended for epidermal application.
• sunscreens include sunscreens; moisturizing or anti- aging creams and lotions; cleaning soaps or gels; antiperspirants and deodorants, including those in stick, pump spray, aerosol, and roll-on form; fragrance releasing gels; lipsticks, lip glosses, and liquid makeup products; oral care products, including toothpastes, tooth polishing and whitening agents, and denture care products such as cleaners and adhesives, and further including use in sorbitol, sorbitol-water mixtures, and glycerol-water mixtures; products where controlled, sustained, or delayed release of an ingredient would be desirable; wound care products, such as ointments (including anesthetic, antiseptic, and antibiotic ointments), dressings, and products such as ostomy rings where good liquid retention is desirable; and absorbent products, such as diapers.
• ointments including anesthetic, antiseptic, and antibiotic ointments
• dressings include ostomy rings where good liquid retention is desirable
• absorbent products such
• the present invention may have particular utility, not only in personal care products but in other applications, with products dispersed by a pumping action.
• the shear- reversible gelation exhibited by the derivatized microfibrillar polysaccharide is well suited for pump dispensing, and may be advantageously combined with its ability to stabilize emulsions, dispersions, and foams to improve the uniform delivery of product.
• the rheological properties of the present derivatized microfibrillar polysaccharides, and their ability to stabilize emulsions, dispersions, and foams provide utility in areas such as detergents, shampoos, cleaners, and air fresheners.
• Specific examples include, without limitation, laundry products (including detergents, pre-spotting cleaners, and fabric treatment compositions, such as softeners); rug and upholstery shampoos; toilet bowl cleaners (particularly those dispensed in liquid or gel form); air fresheners; and general purpose cleaning agents, including liquids, gels, pastes, and foams used in cleaning and/or disinfecting household surfaces.
• the derivatized microfibrillar polysaccharides may have utility in controlled, sustained, or delayed release formulations; as disintegrants; as dietary fiber; in wound care, particularly in applications (such as ostomy rings) where liquid-holding ability is important; and as rheology modifiers.
• the derivatized microfibrillar polysaccharides of the present invention have utility in emulsion modification and/or stabilization; sizing; retention; clarification; absorbence; drainage; formation (such as by functioning as flocculation aids); deposit or scale control (by inhibiting the formation and/or growth of inorganic deposits); water treatment; dewatering; film and membrane formation; polyelectrolyte cross-linking; removal of detrimental organic and/or inorganic materials; in paper coatings; and in improving properties such as stiffness, wet strength, absorbancy, softness, toughness, tear resistance, and fold resistance.
• scale control refers to the prevention of calcium carbonate and calcium oxalate deposits forming during the pulping process.
• Scale control can be achieved by dispersion of salt crystals in the medium to prevent growth and deposition, inhibition of nucleation, or modification of the crystal growth mechanism to prevent the formation of crystal forms that will lead to deposits.
• derivatized microfibrillar cellulose having micron and smaller particle size, stabilized with appropriate functional groups, would serve to control scale deposit because such microcarriers inhibit the crystal growth which leads to deposition.
• cellulosic materials would be easier to recover from the pulping process due to their organic nature.
• Prefened functional groups would include phosphate/phosphonate groups, carboxylate groups, and sulfate/sulfonate groups.
• Alternative functional groups and appropriate use levels may be readily determined by those of ordinary skill in the art, based on the particular environment of use.
• the derivatized microfibrillar cellulose may also be used in a papermaking machine to increase the rate of drainage and/or dewatering during paper manufacture; to retain organic and/or inorganic dispersed particles (such as pulp fines, fillers, sizing agents, pigments, and/or clays); to retain detrimental organic and inorganic particulate materials; to improve the uniformity of formation of a sheet of paper; and to improve the strength of a sheet of paper.
• drainage aids are additives that increase the rate at which water is removed from a paper slurry on a paper machine. These additives increase machine capacity, and hence profitability, by allowing faster sheet formation.
• Anionically charged microfibrillar cellulosic derivatives are capable of greatly increasing drainage, either alone or in combination with other charged polymers.
• the derivatized microfibrillar cellulose of the present invention may also be used in coated papers, where cellulose derivatives may be used to control the rheology of the color coating and to provide water retention, thereby controlling the amount of liquid that permeates into the base sheet.
• the derivatized microfibrillar polysaccharides can provide rheology modification, improving properties such as spatter, leveling, sag resistance, flooding, and floating, and may have particular utility in gel paints. They may also improve pigment dispersion and/or stabilization, and function as charge control or flow control agents, including in inks, such as ink jet inks.
• the derivatized microfibrillar polysaccharides of the present invention can provide scale control, that is, inhibiting the formation and/or growth of inorganic deposits in aqueous systems; clarification; flocculation; sedimentation; coagulation; charge delivery; and softening.
• the present derivatized microfibrillar polysaccharides can provide rheology modification, reduce or prevent fluid loss, and improve secondary oil recovery.
• the derivatized microfibrillar polysaccharides of the present invention can be used in soil treatment, and may provide moisture retention, erosion resistance, frost resistance, and controlled, sustained, or delayed release of agricultural materials such as fertilizers, pesticides, fungicides, and herbicides. They may also be used for crop protection, such as to minimize or prevent frost damage.
• the derivatized microfibrillar polysaccharides can be used in dry wall muds, caulks, water-soluble adhesives, and board manufacture.
• the derivatized microfibrillar polysaccharides can be used for control and cleanup of liquid spills, as absorbents for oil; in general, as stabilizers for emulsions, dispersions, and foams (including but not limited to oil-in-water and water- in-oil emulsions); and for emulsification.
• Stability of commercial emulsions, such as paper size emulsions, is a recurring issue in industry.
• Cunent commercial emulsions include those which generally consist of an oil, waxy, or rosin phase dispersed in water.
• dispersions are generally stabilized by the addition of charged materials such as cationic starches, sodium lignin sulfonate, and aluminum sulfate. Such materials are generally added in amounts equal to about 10-20% by weight of the size component.
• the resulting dispersions are typically 0.2 to 2 micron particles, thought to be stabilized by charge repulsion, for example, with the positively charged starches on particle surfaces repelling each other.
• One cause of emulsion failure is density-driven separation. This can be limited by increasing viscosity, or internal structure within the fluid.
• an emulsion which maintains a viscosity of less than about 20 centipoise throughout a standard aging test might have its viscosity increased initially by as much as 100 centipoise through addition of a viscosifier to the formulation, and still be within acceptable commercial viscosity, provided that the viscosity did not then increase over time to exceed acceptable limits.
• One method to accomplish this result would be to use a viscosifying agent that does not cause a substantial increase in viscosity when first added to an emulsion formulation, but which does provide an increase in viscosity during normal processing of the emulsion formulation to produce the emulsion.
• a viscosifying agent that does not cause a substantial increase in viscosity when first added to an emulsion formulation, but which does provide an increase in viscosity during normal processing of the emulsion formulation to produce the emulsion.
• This can be accomplished by including, as an additive to the emulsion formulation, polysaccharide that has been derivatized as described herein but not yet microfibrillated.
• the shear will also microfibrillize the derivatized polysaccharide, resulting in the derivatized microfibrillar polysaccharide of the present invention, which will be present as part of the emulsion.
• the gel produced by the derivatized microfibrillar polysaccharide will then thin under shear stress but reform when shear stops.
• the insolubility of such low DS/MS polysaccharide may cause it to concentrate at the oil/water interface of oil-and-water emulsions, rather than the aqueous bulk phase, which may be desirable.
• the same result may be achieved by adding the derivatized microfibrillar polysaccharide of the present invention to an emulsion formulation, or to the final emulsion, or at any point during production of the emulsion.
• Further variations would include introducing derivatized polysaccharide that is only partially microfibrillated into the emulsion-making process at a point where subsequent processing would provide sufficient energy to complete the microfibrillation.
• the emulsion formulation may include a charged species that will adsorb onto the polysaccharide microfibrils, or such a species may be added during processing of the emulsion formulation, separately or in combination with the polysaccharide. Therefore, the derivatized microfibrillar polysaccharides of the present invention may serve as stabilizing additives to emulsions, with several process routes being available to accomplish this end result.
• the basic benefit of improved emulsion stability should be achieved by any procedure which has, as its final result, the presence of the derivatized microfibrillar polysaccharide of the present invention in the final emulsion.
• This improved emulsion stability may enable use of emulsion formulations which would not perform satisfactorily in the absence of the derivatized microfibrillar polysaccharide.
• Other benefits may include improved retention in paper, improved drainage of water from paper systems due to association of pulp and filler fines with the retained microfibrils, and resistance to emulsion breakage in the presence of high salt concentrations.
• the subject electrostatically derivatizedinaterials of this invention have also been discovered to provide rheology to aqueous systems over a wide pH range (namely from about 2.5 to 10 or higher) and ionic strength. This insensitivity to pH and ionic strength facilitates use in areas where low pH and high salt conditions exist, such as in personal care creams and lotions, food products, and the like.
• the derivatized microfibrillar polysaccharides of the present invention represent a vehicle for providing charge, whether anionic, cationic, or both, to a given environment. This may, as a representative example, have utility in water treatment, where charged particles are used to flocculate particulates and other contaminates.
• Example 1 Microfibrillated, Non-Derivatized Cellulose.
• Germaben® II biocide 17.50g 0.49 0.49
• IP A Isopropanol
• DI water Isopropanol (IP A) and DI water were charged to a nitrogen sparged, jacketed resin kettle equipped with an air driven stiner, stainless steel agitator, two pressure equalizing addition funnels, a reflux condenser, nitrogen inlet, vacuum line and thermocouple.
• Sulfate wood pulp (approximately 400 ⁇ m length) was added to the reactor and the mixture slurry was agitated for 10 minutes, after which the mixture was nitrogen sparged for 1 hour while cooling the slurry temperature to 15° C.
• the reactor was inerted.
• Aqueous 50% NaOH was slowly added to the reactor while maintaining the mixture slurry's temperature at about 15° C.
• the slurry was agitated for 1 hour after completion of caustic addition.
• Aqueous monochloroacetic acid (80% MCA) was slowly added to the reactor by funnel while maintaining reaction slurry temperature at about 15°C. After MCA addition, the reaction slurry was heated to 70° C and held for 1.5 hours. The reaction slurry was cooled below 30° C and glacial acetic acid was added to the reactor. The reaction mixture was then aspirator vacuum filtered with a sintered glass funnel and a rubber dam. The wetcake was slu ⁇ ied in 565g of 80% methanol for 15 minutes using an air driven stiner and a grounded stainless steel beaker and then aspirator vacuum filtered with a sintered glass funnel and a rubber dam. This was repeated two more times.
• the wetcake obtained from the previous three washes was slurried in lOOOg of pure methanol using an air driven stiner and a grounded stainless steel beaker for 15 minutes to dehydrate and then aspirator vacuum filtered with a sintered glass funnel and rubber dam.
• the final wetcake was dried in a Lab-Line fluidized bed dryer (model number 23852) for 35 minutes (air-dry for 5 minutes, heat- dry at 50° C for 10 minutes, and heat-dry at 70° C for an additional 20 minutes)
• the carboxymethylcellulose (CMC) product was ground using a Retsch Grinding Mill (model 2M1) with a 1mm screen. (Although the examples herein show washing of the product, the need for, or amount of, washing will depend on the intended application.)
• the container was closed and shaken to wet and disperse the CMC solids. The solids will settle if left standing, so the container was shaken just prior to pouring the slurry into the homogenizer.
• the suspension was processed in the homogenizer equipped with an agitated feed pot as follows: the homogenizer was turned on before the slurry was loaded. An 800 gram slurry was processed for about 20 minutes at about 3000 psi by recycling the discharged stream from the homogenizer to the feed pot. Pressure was monitored and appropriate adjustments made to the primary stage handwheel to keep the total pressure at about 3000 psi. After the processing was completed, the discharge tube was redirected so that the sample was collected and stored in a capped jar.
• Example 3 Preparation and Microfibrillation of Carboxymethylcellulose II (CMC II).
• IP A Isopropanol
• DI water DI water
• Sulfate wood pulp (approximately 400 ⁇ m length) was added to the reactor, the mixture slurry was agitated for 10 minutes, after which the mixture was nitrogen sparged for 1 hour while cooling the slurry temperature to 15° C.
• the reactor was inerted.
• Aqueous 50% NaOH was slowly added to the reactor maintaining the mixture slurry's temperature at about 15° C.
• the slurry was agitated for 1 hour after completion of caustic addition.
• Aqueous monochloroacetic acid (80% MCA) was slowly added to the reactor by funnel while maintaining reaction slurry temperature at about 15°C. After MCA addition, the reaction slurry was heated to about 70° C and held for 1.5 hours.
• the reaction slurry was cooled down to below 30° C and then aspirator vacuum filtered with a sintered glass funnel and a rubber dam.
• the wetcake was slurried in 565g of 80% methanol for 15 minutes using an air driven stiner and a grounded stainless steel beaker and then aspirator vacuum filtered with a sintered glass funnel and a rubber dam. This was repeated two more times.
• the wetcake obtained from the previous three washes was slurried in lOOOg of pure methanol using an air driven stiner and a grounded stainless steel beaker for 15 minutes to dehydrate and then aspirator vacuum filtered with a sintered glass funnel and rubber dam.
• the final wetcake was dried in a Lab-Line fluidized bed dryer (model number 23852) for 35 minutes (air-dry for 5 minutes, heat- dry at 50° C for 10 minutes, and heat-dry at 70° C for an additional 20 minutes).
• the carboxymethylcellulose (CMC) product was ground using a Retsch Grinding Mill (model 2M1) with a 1mm screen.
• Example 4 Preparation and Microfibrillation of Carboxymethylcellulose III (CMC III).
• Aqueous sodium monochloroacetate was prepared by mixing 80% MCA, 50% aqueous NaOH and DI water. This solution was slowly added to the reactor by addition funnel while maintaining reaction slurry temperature at about 15° C. After MCA addition, the reaction slurry was heated to about 70° C and held for 1.5 hours. The reaction slurry was cooled down to below 30° C and then aspirator vacuum filtered with a sintered glass funnel and a rubber dam. The wetcake was slurried in 565g of 80% methanol for 15 minutes using an air driven stiner and a grounded stainless steel beaker and then aspirator vacuum filtered with a sintered glass funnel and a rubber dam. This was repeated two more times.
• the wetcake obtained from the previous three washes was slurried in lOOOg of pure methanol using an air driven stiner and a grounded stainless steel beaker for 15 minutes to dehydrate and then aspirator vacuum filtered with a sintered glass funnel and rubber dam.
• the final wetcake was broken into small particles using a rubber spatula and then dried in the fluidized bed dryer for 35 minutes. (Air-dry for 5 minutes, heat-dry at 50 ° C for 10 minutes and heat-dry at 70° C for an additional 20 minutes)
• the product was ground using the Retsch mill with a 1mm screen.
• Example 5 CMC Preparation with Water Washing of Wetcake.
• Aqueous sodium monochloroacetate was prepared by mixing 80% MCA, 50% aqueous NaOH and DI water. This solution was slowly added to the reactor by addition funnel while maintaining reaction slurry temperature at about 15° C. After MCA addition, the reaction slurry was heated to about 70° C and held for 1.5 hours. The reaction slurry was cooled down to below 30° C and then aspirator vacuum filtered with a sintered glass funnel and a rubber dam. The wetcake was slurried in 650g of DI water for 15 minutes using an air driven stiner and a grounded stainless steel beaker and then aspirator vacuum filtered with a sintered glass funnel and a rubber dam. This was repeated one additional time.
• the wetcake obtained from the previous two washes was slurried in lOOOg DI water using an air driven stiner and a grounded stainless steel beaker for 15 minutes and then aspirator vacuum filtered with a sintered glass funnel and rubber dam.
• the final wetcake was dried in the fluidized bed dryer for 35 minutes (air-dry for 5 minutes, heat-dry at 50° C for 10 minutes and heat-dry at 70° C for an additional 20 minutes).
• the product was ground using the Retsch mill with a 1mm screen.
• the product was slurried in 3 liters of water for 15 minutes and filtered using a rubber dam. This slurry/filtration process was repeated three additional times. The final filter cake was dried in the fluidized bed dryer and ground in the Retsch mill using a 1 mm screen.
• Germaben® II biocide 4.01 grams 0.50%
• Example 2 Since the final slurry is 10% by weight of a 10% CMC slurry, the actual CMC level is the normal 1% by weight. Homogenization was performed as in Example 2 except that Sample #1 was processed for 25 minutes, and rheological testing was performed as in example 2.
• Example 7 Preparation of Ready-to-Gel Microfibrillated CMC.
• Gels were made as described in the slurry preparation and homogenization processing steps in Example 2 using CMC II as made in example 3 (DS about 0.16). The gels were then processed as follows (the following description pertains to Sample #1 in Table 11, and a similar procedure was used for all of the other samples): Approximately 2800 ml of isopropyl alcohol was added to a grounded 12 quart stainless steel (SS) beaker. The EPA was stined at the top speed of an overhead stiner driven by house air. A SS cowls blade on a SS shaft was used to stir the EPA. about 1400 grams of 1% CMC II gel was slowly added to the stirring EPA. The material ratio was 2 ml IPA/1 gram gel. It took about 5 minutes to add the gel to the EPA. The beaker was covered with plastic film and the slurry was stined for ten minutes.
• SS grounded 12 quart stainless steel
• the slurry was filtered through a synthetic straining cloth.
• the slurry was filtered using gravity.
• the slurry was covered with plastic film during the filtration to reduce EPA evaporation. Occasionally the gel on the cloth was stined with a plastic spatula to help speed filtration. When it appeared that the filtration had gone about as far as it could, the wet cake was transfened back to the 12 quart SS beaker.
• the dehydrated gels were examined by rehydration as follows: a premix of DI water and Germaben® II was prepared.
• Germaben® II biocide 4.00 grams 0.51%
• Example 8A Acid Process for Preparation of Ready-to-Gel Microfibrillar CMC.
• a gel as prepared in example 3 was acidified using HC1 to adjust the pH to about 2.7. The gel was centrifuged to remove about 60% of the water. The concentrated gel was then converted to RTG form by mixing with IPA equivalent to 2 times the weight of the gel, followed by filtration on a B ⁇ chner funnel and a second mix with another 2 times weight of EPA. The wet cake was dried in a vacuum oven.
• Example 8B Acid Process for Preparation of Ready-to-Gel Microfibrillar CMC.
• a second batch of gel as made in example 3 had its pH adjusted to about 2.7 with concentrated HC1.
• the sample was centrifuged .and about 62% of the water was removed.
• About 97g of concentrated gel was slurried with 150 ml EPA.
• the pH was adjusted to 7.0 during the stirring of the slurry by addition of a small amount of baking soda.
• the slurry was filtered on a B ⁇ chner funnel, and half of the wet cake (Sample A) was weighed into a crystallization dish for drying.
• Sample B the other half of the wet cake was reslurried in about 75 ml EPA.
• This wet cake was filtered on a Biichner funnel and was pressed with rubber dam to remove as much EPA as possible. Both wet cakes were dried to constant weight under vacuum, and the solids were ground up in a Waring blender.
• Sample A was mixed with water for a total solids level of 1%, and gelled quickly. The pH was about 5.8. Sample B gelled quickly when stined in water at a solids level of 1%.
• Isopropanol (602.8g) and DI water (86.4g) were charged to a nitrogen sparged, jacketed resin kettle equipped with an air driven stiner, stainless steel agitator, two pressure equalizing addition funnels, a reflux condenser, nitrogen inlet, vacuum line and thermocouple.
• Microfibrillated cellulose of Example 1 was vacuum filtered with a sintered glass funnel and a rubber dam.
• the wetcake was slurried in 565g of 80% isopropanol (EPA) for 15 minutes using an air driven stiner and a grounded stainless steel beaker and then aspirator vacuum filtered with a sintered glass funnel and a rubber dam. This was repeated two more times.
• EPA isopropanol
• the wetcake obtained from the previous three washes was slurried in lOOOg of pure EPA using an air driven stiner and a grounded stainless steel beaker for 15 minutes to dehydrate and then aspirator vacuum filtered with a sintered glass funnel and rubber dam.
• the resulting wet cake comprised of 36g microfibrillated cellulose, 228g IPA, and 36g DI water was added to the reactor, the mixture slurry was agitated for 10 minutes, after which the mixture was nitrogen sparged for 1 hour while cooling the slurry temperature to 15° C.
• the reactor was inerted.
• Aqueous 50% NaOH (10.52g) was slowly added to the reactor maintaining the mixture slurry's temperature at about 15° C.
• the slurry was agitated for 1 hour after completion of caustic addition.
• Aqueous monochloroacetic acid (7.26g of 80% aq MCA) was slowly added to the reactor by funnel while maintaining reaction slurry temperature at about 15° C.
• MCA addition the reaction slurry was heated to about 70° C and held for 1.5 hours.
• the reaction slurry was cooled down to below 30° C and then aspirator vacuum filtered with a sintered glass funnel and a rubber dam.
• the wetcake was slurried in 565g of 80% methanol for 15 minutes using an air driven stiner and a grounded stainless steel beaker and then aspirator vacuum filtered with a sintered glass funnel and a rubber dam. This was repeated two more times.
• the wetcake obtained from the previous three washes was slurried in lOOOg of pure methanol using an air driven stiner and a grounded stainless steel beaker for 15 minutes to dehydrate and then aspirator vacuum filtered with a sintered glass funnel and rubber dam.
• the final wetcake was dried in the fluidized bed dryer for 35 minutes (air-dry for 5 minutes, heat-dry at 50° C for 10 minutes and heat-dry at 70° C for an additional 20 minutes).
• the product was ground using the Retsch mill with a 1mm screen. DS of the resulting material was 0.14.
• CMC was produced as in example 3 using the cellulose source and recipe in Table 12.
• Example 2 Solka Floe (grade 300 FCC) obtained from Fiber Sales & Development Corp., Urbana, Ohio. (2) Bleached CTMP (Chemical Thermomechanical Pulp) Fluff obtained from SCA Graphic Sundsvall AB, Timra, Sweden Slurry preparation of the Solka Floe sample (Sample 2) was prepared as in Example 2. Homogenizer processing was performed as in Example 2, and rheological testing was performed as in Example 2.
• Example 11 Microfibrillation of CMC with Impingement Mixer.
• the samples used were 0.5%, 1.0% and 1.5% suspensions of low DS CMC prepared as in Example 3. Each slurry weighed a total of 100 grams. No Germaben® II biocide was used in the samples processed in the impingement mixer. The slurries were prepared by weighing the components into four ounce glass jars. The jars were capped and shaken to wet and disperse the CMC solids.
• Sample #1 (0,5%) Sample #2 (1.0%) Sample #3 (1.5%) CMC 0.50 grams 1.0 grams 1.5 grams DI water 99.5 grams 99.0 grams 98.5 grams
• a Microfluidics Corporation Model Ml 10 Series impingement mixer was flushed with DI water prior to use. The pressure was adjusted to the desired setting as the water was pumped. The impingement mixer was run such that the DI water was pumped until it was just at the bottom of the charge funnel. A heating bath used to control the temperature of the impingement mixer piping was set at 50° C.
• the sample jar was shaken again just before charging the sample funnel.
• the sample was charged into the funnel.
• An electric overhead stiner was in the sample funnel. This was turned on to help keep the CMC homogeneously suspended. After the first pass, the stiner is not needed.
• the sample was pumped through the microfluidizer ⁇ nd out into a collection jar. The material initially collected which contains the initial DI residue was discarded. Processing was then continued until the entire sample had been processed for 1 pass through the equipment.
• Example 12 Microfibrillated Hydrophobically Modified Carboxymethyl Cellulose (HMCMC)
• TSA Tert-butyl alcohol
• Hercules CMC 7H DS of about 0.7, 100 g
• the mixture was nitrogen sparged for 1 hour at 25 ° C.
• Aqueous NaOH 54 g of 7.5% NaOH was slowly added to the reactor maintaining the mixture slurry's temperature at about 25° C.
• the slurry cooled to about 15° C and was agitated for 1 hour at about 15° C.
• a 50% solution of cetyl glycidal ether (40 g of solution) was slowly added to the reactor by addition funnel while maintaining reaction slurry temperature at about 15° C.
• the reaction slurry was heated to about 80° C and held for 3.25 hours.
• the reaction slurry was cooled down to about 50° C and 9 g of 70% nitric acid was added.
• the mixture was cooled to about 30° C and then aspirator vacuum filtered with a sintered glass funnel and a rubber dam.
• the wetcake was slurried in 1000 g of 85% acetone for 15 minutes using an air driven stiner and a grounded stainless steel beaker and then aspirator vacuum filtered with a sintered glass funnel and a rubber dam. This was repeated two additional times.
• the wetcake obtained from the previous three washes was slurried in lOOOg of 100% acetone using an air driven stiner and a grounded stainless steel beaker for 15 minutes and then aspirator vacuum filtered with a sintered glass funnel and rubber dam.
• the final wetcake was dried in the fluidized bed dryer for 35 minutes. (Air-dry for 5 minutes, heat-dry at 50° C for 10 minutes and heat-dry at 70° C for an additional 20 minutes)
• the product was ground using the Retsch mill with a 1mm screen.
• the cetyl content of the resulting product was ⁇ 0.03 wt.%.
• the reaction slurry was then heated to about 90° C and maintained at 90° C with agitation for 30 minutes.
• the reaction slurry was cooled to about 50° C and 70% nitric acid was added.
• the reaction slurry was cooled to below 30° C and then aspirator vacuum filtered with a sintered glass funnel and a rubber dam.
• the wetcake was slurried in 600g of 80% acetone for 15 minutes using an air driven stiner and a grounded stainless steel beaker and then aspirator vacuum filtered with a sintered glass funnel and a rubber dam. This was repeated two additional times.
• the wetcake obtained from the previous three washes was slurried in 600g of 100% acetone water using an air driven stiner and a grounded stainless steel beaker for 15 minutes and then aspirator vacuum filtered with a sintered glass funnel and rubber dam.
• the final wetcake was dried in the fluidized bed dryer for 35 minutes (air-dry for 5 minutes, heat-dry at 50° C for 10 minutes and heat-dry at 70° C for an additional 20 minutes).
• the product was ground using the Retsch mill with a 1mm screen. Table 15 :HEC Recipes (all weights in grams)
• Drainage Aids in Paper Manufacture demonstrate the effectiveness of derivatized microfibrillar polysaccharide as a drainage- improvement aid.
• Drainage measurements were performed on a Canadian Standard Freeness (CSF) tester, using a bleached kraft pulp consisting of 70% hardwood and 30% softwood. All freeness testing was performed in hard water having a pH of 7.95-8.05, alkalinity of 50 ppm (as calcium carbonate), and hardness of 100 ppm (as calcium carbonate) using CSF.
• CSF Canadian Standard Freeness
• TAPPI method T 227 om-92 A pulp consistency of 0.3% was used. Higher CSF values indicate better (faster) drainage.
• Example 15 RTG CMC Sample Material and Hercules Reten® 1232 (R-1232).
• Example 16 RTG CMC Sample Material and Hercules Kymene® 557H resin (K-557H).
• Example 17 RTG CMC Material and Hercules Kymene 450 resin (K-450).
• the sample material extends the wet and dry strength activity of additives such as Hercules Kymene 557H or Kymene 450 resin.
• additives such as Hercules Kymene 557H or Kymene 450 resin.
• Example 20 Same as Example 18, using 66.0 g Precis ketene dimer, 1.5g of the sample material, 66.0g of 50% aluminum sulfate (18H 2 O) solution in water, and 166.5 g DI water.
• Example 20 Same as Example 18, using 66.0 g Precis ketene dimer, 1.5g of the sample material, 66.0g of 50% aluminum sulfate (18H 2 O) solution in water, and 166.5 g DI water.
• Example 21 Same as Example 18, using 66.0 g Precis ketene dimer; 1.5g of the sample material; 132.0g of a solution containing 25% (wt) aluminum sulfate (18H 2 O), deionized water, and sufficient alkalinity to raise the pH to 4.0; and 100.5 g DI water.
• Example 21 Same as Example 18, using 66.0 g Precis ketene dimer; 1.5g of the sample material; 132.0g of a solution containing 25% (wt) aluminum sulfate (18H 2 O), deionized water, and sufficient alkalinity to raise the pH to 4.0; and 100.5 g DI water.
• Example 21 Same as Example 18, using 66.0 g Precis ketene dimer; 1.5g of the sample material; 132.0g of a solution containing 25% (wt) aluminum sulfate (18H 2 O), deionized water, and sufficient alkalinity to raise the pH to 4.0; and 100.5 g DI water.
• Example 22 Same as Example 18, using 66.0 g Precis ketene dimer; 75. Og of a 2% solution of CMC 7M (DS of 0.7) (Hercules Incorporated, Wilmington DE) in deionized water; and 132.0g of a solution containing 25% (wt) aluminum sulfate (18H 2 O), deionized water, and sufficient alkalinity to raise the pH to 4.0; and 27.0 g DI water.
• CMC 7M DS of 0.7
• Example 18 the addition of low pH 50% alum solution gave an emulsion with poor stability, while similar recipes in Examples 18 and 20, made without alum or with alum whose pH had been raised to pH 4.0, gave good emulsions.
• Example 23 adding the microfibrillated gel without a second impingement mixer shearing as in Example 22 gave an emulsion which was not stable overnight, and thus could not be size tested the next day.
• Example 18 Example 20 Example 21 Example 22 Example 23
• Paperroaking The paper used in the sizing examples was made at pH 7 from a 75:25 blend of hardwood and softwood pulps beaten to a Canadian standard freeness of 525 and formed into sheets having a basis weight of 65.1 g/m 2 .
• Hercon 70, Hercon 79, and Hercon 115 sizing agents were all added at 0.06%, based on the pulp (conesponding to 1.2 pounds per ton).
• Laboratory water was used, having a hardness of 50 ppm, an alkalinity of 25 ppm, and a pH of 8.1 - 8.4.
• Example 28 use as fat replacer, viscosifier in food applications.
• Procedure 1 RTG Microfibrillated CMC prepared in example 7 above (DS about 0.16) was dispersed in water with agitation. Starch and maltodextrin were added with agitation. The mixture was heated to 80° - 90° C followed by cooling to 15° - 20° C. Egg yolk then vinegar were added. The product was then mixed by means of a colloid mill. This mixing consists of one pass through a Greerco colloid mill model W250V-B (Greerco Corp., Hudson, NH) with an emulsion rotor and stator at a 0.001 inch gap setting. The texture of this product is then evaluated after 24 hours.
• W250V-B Greerco Corp., Hudson, NH
• Procedure 2 to a 1% microfibrillated CMC gel as made in example 3 above (DS about 0.16) the balance of the water was added Starch and maltodextrin were then added with agitation. The mixture was heated to 80° - 90° C followed by cooling to 15° - 20° C. Egg yolk then vinegar were added. The product was then mixed by means of a colloid mill. The texture of this product is then evaluated after 24 hours.
• Procedure 3 starch and maltodextrin were added to water with agitation. The mixture was heated to 80° - 90° C followed by cooling to 15° - 20° C. Egg yolk then vinegar were added. The product is then mixed by means of a colloid mill. The texture of this product is then evaluated after 24 hours. Evaluation: viscosity was measured with a Brookfield (Model DV-II+), 20° C, helipath, 5 rpm spindle C, program S93.
• the appearance of the product containing either RTG Microfibrillated CMC or Microfibrillated CMC is that of a gel that holds its shape for a period of time when cut and does not synerese. When a portion of the product is lifted with a spoon or spatula, it does not appear to have stringiness of excessive tackiness; the texture is described as short.
• Example 29 use in personal care products.
• This example demonstrates the ability of the RTG CMC material to stabilize an oil in water emulsion, performing a role typically performed by surfactant/cosurfactant network- forming systems.
• the RTG CMC also is processed at room temperature, while typical surfactant/cosurfactant systems require heat.
• ant -age refers to that category of epidermal lotions and creams intended to contribute to a more youthful appearance by the user, such as by the reduction or removal of wrinkles.
• Part C was then added separately, mixing after addition of each part C ingredient.
• Part D was then added with vigorous agitation, which was continued until the mixture became smooth and homogeneous.
• Part E was then added, the mixture was cooled to 45 °C, and part F was added.

Landscapes

• Health & Medical Sciences (AREA)
• Chemical & Material Sciences (AREA)
• Life Sciences & Earth Sciences (AREA)
• General Health & Medical Sciences (AREA)
• Engineering & Computer Science (AREA)
• Organic Chemistry (AREA)
• Polymers & Plastics (AREA)
• Medicinal Chemistry (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Materials Engineering (AREA)
• Biochemistry (AREA)
• Public Health (AREA)
• Veterinary Medicine (AREA)
• Animal Behavior & Ethology (AREA)
• Birds (AREA)
• Dermatology (AREA)
• Epidemiology (AREA)
• Molecular Biology (AREA)
• Oral & Maxillofacial Surgery (AREA)
• Polysaccharides And Polysaccharide Derivatives (AREA)
• Paper (AREA)
• Cosmetics (AREA)
• General Preparation And Processing Of Foods (AREA)
• Jellies, Jams, And Syrups (AREA)
• Seasonings (AREA)
• Agricultural Chemicals And Associated Chemicals (AREA)

Priority Applications (11)

Applications Claiming Priority (2)

Publications (2)

Family

ID=22938284

Family Applications (1)

Country Status (19)

Cited By (65)

Families Citing this family (147)

Family Cites Families (43)

• 1999
  • 1999-02-10 US US09/248,246 patent/US6602994B1/en not_active Expired - Lifetime
• 2000
  • 2000-02-08 JP JP2000598543A patent/JP5238112B2/ja not_active Expired - Lifetime
  • 2000-02-08 IL IL13875100A patent/IL138751A0/xx unknown
  • 2000-02-08 ES ES00911740T patent/ES2396596T3/es not_active Expired - Lifetime
  • 2000-02-08 CA CA2327482A patent/CA2327482C/en not_active Expired - Lifetime
  • 2000-02-08 EP EP00911740A patent/EP1078008B1/en not_active Revoked
  • 2000-02-08 ID IDW20002313A patent/ID28502A/id unknown
  • 2000-02-08 CN CNB008005184A patent/CN100381469C/zh not_active Expired - Lifetime
  • 2000-02-08 HU HU0102765A patent/HUP0102765A2/hu unknown
  • 2000-02-08 BR BR0005116-0A patent/BR0005116A/pt not_active Application Discontinuation
  • 2000-02-08 DK DK00911740.9T patent/DK1078008T3/da active
  • 2000-02-08 TR TR2000/02813T patent/TR200002813T1/xx unknown
  • 2000-02-08 AU AU33590/00A patent/AU3359000A/en not_active Abandoned
  • 2000-02-08 NZ NZ507250A patent/NZ507250A/en unknown
  • 2000-02-08 PL PL00344839A patent/PL344839A1/xx unknown
  • 2000-02-08 KR KR1020007011213A patent/KR20010042551A/ko not_active Withdrawn
  • 2000-02-08 WO PCT/US2000/003319 patent/WO2000047628A2/en not_active Ceased
  • 2000-02-10 AR ARP000100591A patent/AR025822A1/es unknown
  • 2000-10-09 NO NO20005085A patent/NO20005085L/no not_active Application Discontinuation
• 2012
  • 2012-10-26 JP JP2012236999A patent/JP2013064134A/ja active Pending

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events