JP2008519681A - 被覆された金属表面の補修コーティングの製造方法 - Google Patents
被覆された金属表面の補修コーティングの製造方法 Download PDFInfo
- Publication number
- JP2008519681A JP2008519681A JP2007540563A JP2007540563A JP2008519681A JP 2008519681 A JP2008519681 A JP 2008519681A JP 2007540563 A JP2007540563 A JP 2007540563A JP 2007540563 A JP2007540563 A JP 2007540563A JP 2008519681 A JP2008519681 A JP 2008519681A
- Authority
- JP
- Japan
- Prior art keywords
- siloxane
- coating
- group
- composition
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、
A1)活性化組成物、不動態化組成物、リン酸塩処理組成物、チタン化合物またはジルコニウム化合物あるいはその両者を含む組成物および後すすぎ組成物などの前処理組成物、
A2)プライマー、ウェットプライマー、溶接プライマー、e−コート、粉末コート、ベースコートおよびクリアコートなどの有機組成物、ならびに
A3)シラン、シラノール、シロキサンおよびポリシロキサンから選択される、少なくとも1種のケイ素化合物を含む溶液または分散液である組成物を含むケイ素化合物:
の群より選択される少なくとも1種の組成物を用いて適用、少なくとも1種の耐食コーティングAを用いて被覆される、少なくとも1種の金属表面上の補修コーティングを製造する方法に関するものであるが、
少なくとも1種の耐食コーティングAは、領域Zにおいて少なくとも部分的に除去されており、
少なくとも1種のケイ素化合物を含む薄層(thin)耐食コーティングBは、少なくとも1種のシラン、少なくとも1種のシラノール、少なくとも1種のシロキサン、少なくとも1種のポリシロキサンまたはこれらの混合物(=シロキサン組成物)を含む溶液または分散液を用いて領域Zの少なくとも一部に適用される。この組成物は、溶液、分散液、あるいは同時に溶液であると共に分散液である。
本明細書において、「シラン」または「シロキサン」という用語は、多くの状況において、「シラン、シラノール、シロキサンおよび同等の化学的性質を有するポリシロキサンおよびこれらの反応生成物および誘導体から選択される、少なくとも1種のケイ素化合物」を意味するものとするが、これは、多くの状況下において、シランからシラノールへ、シラノールからシロキサンへ、シロキサンからポリシロキサンへの連続反応およびこれらのいずれかの組み合わせが存在するからである。本発明の優先権を主張する出願であるUS SN 10/985,652、対応する優先出願DE 1020050155573.1、DE 102005015575.8およびDE 102005015576.6、ならびに既述の3件のドイツ国特許出願に関連する、対応PCT出願の内容、とりわけ、種々の組成物、添加される種々の化合物、種々の製造段階、生成される種々のコーティング、実施例、比較例、ならびに効果、特性および実験結果といったものは、本願明細書において明確に援用される。
本発明は、耐食性を有するとともに、さらにその表面に次のコーティングを塗布するにあたり良好な接着性を示すコーティングを生み出す、被覆された金属表面のコーティングの修復に用いる修復コーティング方法に関するものである。
3−グリシドキシアルキルトリアルコキシシラン、
3−メタクリルオキシアルキルトリアルコキシノシラン、
3−(トリアルコキシシリル)アルキル−コハク酸−シラン、
アミノアルキルアミノアルキルアルキルジアルコキシシラン、
ベータ−(3,4−エポキシシクロアルキル)アルキルトリアルコキシシラン、
(3,4−エポキシシクロアルキル)アルキルトリアルコキシシラン、
ビス(トリアルコキシシリルアルキル)アミン、
ビス(トリアルコキシシリル)エタン、
(3,4−エポキシシクロアルキル)トリアルコキシシラン、
ガンマ−アミノアルキルトリアルコキシシラン、
ガンマ−メタクリルオキシアルキルトリアルコキシシラン、
ガンマ−ウレイドアルキルトリアルコキシシラン、
グリシドキシアルキルトリアルコキシシラン、
N−2−アミノアルキル−3−アミノプロピルトリアルコキシシラン、
N−(3−トリアルコキシシリル)アルキル)アルキレンジアミン、
N−ベータ−(アミノアルキル)−ガンマ−アミノアルキルトリアルコキシシラン、
N−(ガンマ−トリアルコキシシリルアルキル)ジアルキレントリアミン、
ポリアミノアルキルアルキルジアルコキシシラン、
トリ−(3−トリアルコキシシリル)アルキル)イソシアヌレート、
(ウレイドプロピルトリアルコキシ)シラン、
ビニルトリアセトキシシラン、
ならびに、その対応するシラノール、シロキサン、ポリシロキサン、これらの誘導体および反応生成物。
3−(アミノプロピル)シラントリオール、
3−グリシドキシプロピルトリエトキシシラン、
3−グリシドキシプロピルトリメトキシシラン、
3−グリシジルオキシプロピルトリエトキシシラン、
3−メタクリルオキシプロピルトリエトキシシラン、
3−メタクリルオキシプロピルトリメトキシシラン、
3−(トリエトキシシリル)プロピル−コハク酸−シラン、
アミノエチルアミノプロピルメチルジエトキシシラン、
アミノエチルアミノプロピルメチルジメトキシシラン、
アミノプロピルトリアルコキシシラン、
ベータ−(3,4−エポキシシクロへキシル)エチルトリエトキシシラン、
ベータ−(3,4−エポキシシクロへキシル)エチルトリメトキシシラン、
ベータ−(3,4−エポキシシクロへキシル)メチルトリエトキシシラン、
ベータ−(3,4−エポキシシクロへキシル)メチルトリメトキシシラン、
ビス−1,2−(トリエトキシシリル)エタン、
ビス−1,2−(トリメトキシシリル)エタン、
(3,4−エポキシシクロへキシル)プロピルトリエトキシシラン、
(3,4−エポキシシクロへキシル)プロピルトリメトキシシラン、
ビス−(トリエトキシシリルプロピル)アミン、
ビス−(トリメトキシシリルプロピル)アミン、
(3,4−エポキシブチル)トリエトキシシラン、
(3,4−エポキシブチル)トリメトキシシラン、
ガンマ−アミノプロピルトリエトキシシラン、
ガンマ−アミノプロピルトリメトキシシラン、
ガンマ−メタクリルオキシプロピルトリエトキシシラン、
ガンマ−メタクリルオキシプロピルトリメトキシシラン、
ガンマ−ウレイドプロピルトリアルコキシシラン、
N−2−アミノエチル−3−アミノプロピルトリエトキシシラン、
N−2−アミノエチル−3−アミノプロピルトリメトキシシラン、
N−2−アミノメチル−3−アミノプロピルトリエトキシシラン、
N−2−アミノメチル−3−アミノプロピルトリメトキシシラン、
N−(3−(トリメトキシシリル)プロピル)エチレンジアミン、
N−ベータ−(アミノエチル)−ガンマ−アミノプロピルトリエトキシシラン、
N−ベータ−(アミノエチル)−ガンマ−アミノプロピルトリメトキシシラン、
N−(ガンマ−トリエトキシシリルプロピル)ジエチレントリアミン、
N−(ガンマ−トリメトキシシリルプロピル)ジエチレントリアミン、
N−(ガンマ−トリエトキシシリルプロピル)ジメチレントリアミン、
N−(ガンマ−トリメトキシシリルプロピル)ジメチレントリアミン、
ポリアミノアルキルエチルジアルコキシシラン、
ポリアミノアルキルメチルジアルコキシシラン、
トリ−(3−(トリエトキシシリル)プロピル)イソシアヌレート、
トリ−(3−(トリメトキシシリル)プロピル)イソシアヌレート、
ビニルトリアセトキシシラン、
ならびに、その対応するシラノール、シロキサン、ポリシロキサン、これらの誘導体および反応生成物。
溶液および分散液であり、少なくとも1種の部分的に加水分解されたシラン、少なくとも1種の完全に加水分解されたシラン、少なくとも1種のオリゴマーシロキサン、少なくとも1種のポリマーシロキサン、少なくとも1種のポリシロキサン、またはこれらの混合物の含有量を含むものである。より好ましくは、これらの組成物は少なくとも1種のオリゴマーシロキサンおよび少なくとも1種のポリマーシロキサンの含有量を含んでいる。より高い粘度が要求される場合には、有機モノマー、有機オリゴマー、有機ポリマーの群から選択される、少なくとも1種の化合物、ベントナイト、耐火粘土、カオリナイトおよびゼオライトといった粘土または粘土様物質、いずれかのホウ酸塩、例えばナノ結晶質SiO2などのいずれかの酸化物、いずれかの有機物質、またはセルロース、アクリレート(メタクリレート)、単糖類(多糖類)、でんぷんおよびポリシロキサンをベースとする有機物質を含むいずれかの混合物などの微結晶質ケイ酸塩など、少なくとも1種の増粘剤、を添加しても構わない。
溶液および分散液であり、例えばアミノ基、エポキシ基、グリシドキシ基、ヒドロキシ基、イソシアナト基、メルカプト基、(メタ)アクリレート基、(ポリ)硫黄基、チオール基、ウレイド基、ビニル基およびビニルベンゼン基から選択される少なくとも1種の基を有する、少なくとも1種の有機ケイ素化合物の含有量、ならびに、一分子あたりに少なくとも二つ以上のシリル基を有する、少なくとも1種の多官能性ケイ素化合物を含むものである。より好ましくは、これらの組成物は(a)少なくとも1種の有機ケイ素化合物の成分であって、例えばアミノ基、エポキシ基、グリシドキシ基、ヒドロキシ基、イソシアナト基、メルカプト基、(メタ)アクリレート基、(ポリ)硫黄基、チオール基、ウレイド基、ビニル基およびビニルベンゼン基から選択される、少なくとも1種の基を、容量として0.1〜120g/Lの範囲内、より好ましくは0.12または0.5〜80g/Lの範囲内、さらにより好ましくは0.15〜50g/Lまたは1〜50g/Lまたは0.2〜5g/Lまたは0.5〜1.5g/Lの範囲内、例えば、各々が約0.1、0.2、0.3、0.4、0.5、0.6、0.7、0.8、0.9、1、1.2、1.4、1.6、1.8、2、2.5、3、4、5、6、8、10、12、14、16、18、20、22、24、26、28、30、32、34、36、38、40、42、44、46、48、50、52、54、56、58、60、62、64、66、68、70、72、74、76、78、80、82、84、86、88、90、92、94、96、98、100、102、104、106、108、110、112、114、116または118g/L、ならびに、(b)少なくとも二つ以上のシリル基を有する、少なくとも1種の多官能性ケイ素化合物の成分であって、0.1〜120g/Lの範囲内、より好ましくは0.12〜80g/Lの範囲内、または0.5〜〜80g/Lの範囲内、さらにより好ましくは0.15〜50g/Lまたは1〜50g/Lまたは0.2〜5g/Lまたは0.5〜1.5g/Lの範囲内、例えば、各々が約0.1、0.2、0.3、0.4、0.5、0.6、0.7、0.8、0.9、1、1.2、1.4、1.6、1.8、2、2.5、3、4、5、6、8、10、12、14、16、18、20、22、24、26、28、30、32、34、36、38、40、42、44、46、48、50、52、54、56、58、60、62、64、66、68、70、72、74、76、78、80、82、84、86、88、90、92、94、96、98、100、102、104、106、108、110、112、114、116または118g/L、を示す水溶液または分散液であることがより好ましい。
(a)モノマー、オリゴマー、ポリマー、コポリマー、ブロックコポリマー、またはこれらのいずれかの混合物であって、好ましくは、各々は以下をベースとする:
アクリル、ブタジエン、エポキシ、エチレン、メラミン、メタクリル、ポリカーボネート、ポリエステル、ポリエーテル、ポリウレタン、スチレン、ビニルまたはこれらのいずれかの混合物、
(b)あるいは、コポリマー、好ましくは以下をベースとする:
アクリル−ポリエステル−ポリウレタン コポリマー、
アクリル−ポリエステル−ポリウレタン−スチレン コポリマー、
アクリル酸エステル、
アクリル酸エステル−メタクリル酸エステル、任意に遊離酸またはアクリロニトリルと共に、
エチレン−アクリル混合物
エチレン−アクリル コポリマー
エチレン−アクリル−ポリエステル コポリマー
エチレン−アクリル−ポリウレタン コポリマー
エチレン−アクリル−ポリエステル−ポリウレタン コポリマー
エチレン−アクリル−ポリエステル−ポリウレタン−スチレン コポリマー
エチレン−アクリル−スチレン コポリマー
メラミン−ホルムアルデヒド樹脂と結合した遊離のカルボキシル基を有するポリエステル樹脂、
アクリレートおよびスチレンをベースとする合成樹脂混合物および/またはコポリマー、
スチレン−ブタジエンをベースとする合成樹脂混合物および/またはコポリマー、
アクリレートおよびエポキシドをベースとする合成樹脂混合物および/またはコポリマー、
カルボキシル基を含むアクリル修飾ポリエステルをベースとして、メラミン−ホルムアルデヒドおよびエチレン−アクリル コポリマーと合わせたもの、
ポリカーボネート−ポリウレタン、
ポリエステル−ポリウレタン、
スチレン、
スチレン−酢酸ビニル、
酢酸ビニル、
ビニルエステル、
ビニルエーテル、
またはこれらのいずれかの混合物、あるいは、(a)および(b)のいずれかの混合物。
アセチルアセトネート、
アセトアセテート、
ジ−n−アルコキシ−ビスアルキル アセトアセテート、
ヒドロキシアルキレンジアミン トリアセテート、
トリアルカノアミン、
トリアルキレンテトラミン アルカリ金属乳酸塩、
アルカノールアミン、
アルキル アセタトアセテート、
アルキレンジアミン テトラアセテート
アンモニウム乳酸塩、
クエン酸塩、
ジアルキルクエン酸塩、
ジアルキルエステル−クエン酸塩、
ジアルキレントリアミン、
ジイソアルコキシビスアルキル アセトアセテート、
ジイソプロポキシビスアルキル、
あるいは、これらのいずれかの混合物。
以下のセクションでは、可能となる方法のバリエーション、組成物のバリエーションおよびこれに関連する効果のいくつかを示すことを主眼とした具体的な実施例および比較例をより詳しく記載するが、これらにより本発明が限定されるということではない。
各テストに対し、溶融亜鉛メッキ鋼を原料とした、リン酸亜鉛コーティング、ならびにリン酸亜鉛コーティング上にe−コートの電気塗装を有する15枚の金属シートを使用した。リン酸亜鉛コーティングの厚さは約6μm、e−コートの厚さは約20μmであった。このように被覆された各金属シートの中央部において、これらのコーティングに砂やすりをかけることにより、加工のない(むき出しの)金属表面がシートの中央部で確認されたが、このシートの薄層金属表面もまた砂やすりをかけたことにより除去されていた。次に、やすりがけの直後に、繊維や綿毛を放出しない清潔な雑巾に純水を浸み込ませて湿った状態とした。この湿った清潔な雑巾を使用して、全除去領域Zに沿ってふき取って、埃ならびにやすりがけにより残存した微粒子部分を完全に清掃した。次に、別の清潔な雑巾でこれらの領域を乾かすことによって、水膜が全く残存しないか、あるいは非常に微量の薄い水膜のみが残存した。次に清掃の直後に、シロキサン組成物を除去領域Zに塗布して、製造したての清潔な除去領域上にコーティングBを作製した。
Claims (32)
- A1)活性化組成物、不動態化組成物、リン酸塩処理組成物、チタン化合物またはジルコニウム化合物あるいはその両者を含む組成物および後すすぎ組成物などの前処理組成物、
A2)プライマー、ウェットプライマー、溶接プライマー、e−コート、粉末コート、ベースコートおよびクリアコートなどの有機組成物、ならびに
A3)シラン、シラノール、シロキサンおよびポリシロキサンから選択される、少なくともとも1種のケイ素化合物を含む溶液または分散液であるケイ素化合物を含む組成物
からなる群より選択される少なくとも1種の組成物を用いて塗布される、少なくとも1種の耐食コーティングAにより被覆された、少なくとも1種の金属表面上の補修コーティングを製造する方法において、
少なくとも1種の耐食コーティングAは、領域Zにおいて少なくとも部分的に除去されており、
少なくとも1種のケイ素化合物を含む薄層耐食コーティングBを、少なくとも1種のシラン、少なくとも1種のシラノール、少なくとも1種のシロキサン、少なくとも1種のポリシロキサンまたはこれらの混合物を含む溶液または分散液(=シロキサン組成物)を用いて領域Zの少なくとも一部に塗布する方法。 - シロキサン組成物の薄膜Bが、直径または厚さが10μm以下の粒子、繊維、綿毛片ならびに傷を生じるその他の物質を含まずに塗布される、請求項1に記載の方法。
- シロキサン組成物の薄膜Bが、0.005〜40μmの範囲の湿潤膜厚で塗布される、請求項1に記載の方法。
- シロキサン組成物の薄膜Bが、0.001〜3μmの範囲の乾燥膜厚で塗布される、請求項1に記載の方法。
- シロキサン組成物の薄膜Bを塗布し、次に、例えば5〜300℃の範囲の温度で乾燥させる、請求項1に記載の方法。
- 薄膜Bをシロキサン組成物を用いて塗布し、例えば室温での自然乾燥により、被覆された金属基体を加熱することにより、熱風により加熱することにより、高温ガス流を用いて吹き付けまたは加熱を行なうことにより、または、これらのいずれかの組み合わせにより乾燥させる、請求項1に記載の方法。
- シロキサン組成物の薄膜Bを、シロキサン組成物を収容及び分配する器具の接触によって塗布する、請求項1に記載の方法。
- シロキサン組成物の薄膜Bを、例えば噴霧缶を用いてシロキサン組成物を噴霧することによって塗布する、請求項1に記載の方法。
- シロキサン組成物の薄膜Bを、シロキサン組成物用の貯蔵室を備えた器具を使用することによって塗布する、請求項1に記載の方法。
- シロキサン組成物の薄膜Bを、刷毛、スポンジ、タンポン、スティック、またはゲルパックのような器具を使用することによって塗布する、請求項1に記載の方法。
- シロキサン組成物の薄膜Bを、貯蔵室から器具の作業表面へと、シロキサン組成物を移送する能力を有する膜またはその他の多孔質材を有する貯蔵室を備えた器具を使用することによって塗布する、請求項1に記載の方法。
- シロキサン組成物が、20℃における測定で1〜250mPa・sの範囲の粘度を有する、請求項1に記載の方法。
- シロキサン組成物が、ペーストである、請求項1に記載の方法。
- シロキサン組成物を、鉄、鋼、亜鉛メッキまたは亜鉛合金メッキされた鋼、アルミニウム、アルミニウム合金、マグネシウム合金、チタン、チタン合金、あるいはこれらのいずれかの組み合わせである、少なくとも1種の金属表面に塗布する、請求項1に記載の方法。
- 表面に少なくとも2種の異なる材料を現す、少なくとも1つの部分の少なくとも1つの表面であって、少なくとも1種の金属材で作られる、プラスチック材の薄片、マルチレイヤー、シートまたはコンポーネントなどの少なくとも1種のプラスチック材で作られる、少なくとも1種のガラス材で作られる、少なくとも1種のセラミック材で作られる、少なくとも1種の木材で作られる、あるいはこれらのいずれかの混合物で作られる表面に対して、シロキサン組成物を塗布する、請求項1に記載の方法。
- シロキサン組成物を、少なくとも1種のシートの少なくとも1つの金属表面、少なくとも1種の複雑に形成された部分、少なくとも1つの非常に大きな部分、あるいはこれらの混合物に対して塗布する、請求項1に記載の方法。
- シロキサン組成物を、コイル、金属シート、車体、自動車の部品、航空機の機体、船舶、海洋器材、鉄道車両、あるいはそれらの部品のいずれか、建築物、家具、機器または装置の部品あるいは構成部品の、少なくとも1種の金属表面に対して、製造中または損傷後あるいは長期間使用後のいずれかに塗布する、請求項1に記載の方法。
- 少なくとも1種の耐食コーティングAが、研削、研磨、サンドブラストまたは塗膜剥離によって、あるいはこれらのいずれかの組み合わせによって、領域Zにおいて少なくとも部分的に除去されている、請求項1に記載の方法。
- 少なくとも1種の耐食コーティングCを薄膜B上に塗布し、その際、コーティングCは、プライマー、ウェットプライマー、e−コート、粉末コート、ベースコートまたはクリアコートなどの有機組成物によって、あるいは、薄膜B用と同一または異なるシロキサン組成物を含むコーティングによって、あるいは、このような組成物の継続的な塗布によって生成され、ここで、少なくとも1種のコーティングCは、被覆された金属部品の大部分または全ての表面上に任意に塗布されてよい、請求項1に記載の方法。
- 耐食コーティングA、B、Cまたはこれらのいずれかの組み合わせの生成に用いるシロキサン組成物が、シラン、シラノール、シロキサンおよびポリシロキサンの群から選択される、少なくとも1種のケイ素化合物を含む溶液または分散液である、請求項1に記載の方法。
- 耐食コーティングA、B、Cまたはこれらのいずれかの組み合わせの生成に用いるシロキサン組成物が、少なくとも1種の部分的に加水分解されたシラン、少なくとも1種の完全に加水分解されたシラン、少なくとも1種のオリゴマーシロキサン、少なくとも1種のポリマーシロキサン、少なくとも1種のポリシロキサン、またはこれらの混合物の含分を含む溶液または分散液である、請求項1に記載の方法。
- 耐食コーティングA、B、Cまたはこれらのいずれかの組み合わせの生成に用いるシロキサン組成物が、例えばアミノ基、エポキシ基、グリシドキシ基、ヒドロキシ基、イソシアナト基、メルカプト基、(メタ)アクリレート基、(ポリ)硫黄基、チオール基、ウレイド基、ビニル基およびビニルベンゼン基から選択される少なくとも1種の基を有する、少なくとも1種の有機ケイ素化合物の成分、ならびに、一分子あたりに少なくとも2つのシリル基を有する、少なくとも1種の多官能性ケイ素化合物を含む溶液または分散液である、請求項1に記載の方法。
- 耐食コーティングA、B、Cまたはこれらのいずれかの組み合わせの生成に用いるシロキサン組成物が、シラン、シラノール、シロキサンおよびポリシロキサンから選択される、少なくとも1種のケイ素化合物、ならびに、有機モノマー、有機オリゴマー、有機ポリマー、有機コポリマー、有機ブロックコポリマーまたはこれらのいずれかの混合物である、少なくとも1種の有機化合物の含分を含む溶液または分散液である、請求項1に記載の方法。
- 耐食コーティングA、B、Cまたはこれらのいずれかの組み合わせの生成に用いるシロキサン組成物が、シラン、シロキサンおよびポリシロキサンから選択される、少なくとも1種のケイ素化合物、ならびに、酢酸、氷酢酸、その他の炭酸、硫酸、塩酸、硝酸、フッ酸、いずれかのリンを有する酸、またはこれらのいずれかの混合物などの、少なくとも1種の酸の含分を含む溶液または分散液である、請求項1に記載の方法。
- 耐食コーティングA、B、Cまたはこれらのいずれかの組み合わせの生成に用いるシロキサン組成物が、シラン、シロキサンおよびポリシロキサンから選択される、少なくとも1種のケイ素化合物、ならびに、メタノール、エタノール、プロパノールまたはこれらのいずれかの混合物などの、アルコールなどの、少なくとも1種の有機溶媒の含分を含む溶液または分散液である、請求項1に記載の方法。
- 耐食コーティングA、B、Cまたはこれらのいずれかの組み合わせの生成に用いるシロキサン組成物が、シラン、シラノール、シロキサンおよびポリシロキサンから選択される、少なくとも1種のケイ素化合物、ならびに、チタン、ハフニウム、ジルコニウム、アルミニウムまたはホウ素、あるいはこれらのいずれかの混合物を含む、少なくとも1種の化合物の含分を含む溶液または分散液である、請求項1に記載の方法。
- 耐食コーティングA、B、Cまたはこれらのいずれかの組み合わせの生成に用いるシロキサン組成物が、シラン、シラノール、シロキサンおよびポリシロキサンから選択される、少なくとも1種のケイ素化合物、ならびに、粒径が1ミクロン未満の粒子、界面活性剤、染料、蛍光剤、殺生物剤、pH調節剤、キレート、熱的な影響による化学的架橋に好適な架橋剤、光開始剤およびゲル生成用の物質の群から選択される、少なくとも1種の添加剤の含分を含む溶液または分散液である、請求項1に記載の方法。
- 耐食コーティングA、B、Cの生成に用いるシロキサン組成物が、シラン、シラノール、シロキサンおよびポリシロキサンから選択される、少なくとも1種のケイ素化合物、ならびに、硝酸塩、亜硝酸塩またはグアニジン化合物などの、少なくとも1種の窒素を有する剤の含分を含む溶液または分散液である、請求項1に記載の方法。
- 耐食コーティングA、B、Cまたはこれらのいずれかの組み合わせの生成に用いるシロキサン組成物が、アミノ基、エポキシ基、グリシドキシ基、イソシアナト基、メルカプト基、(メタ)アクリレート基、(ポリ)硫黄基、ウレイド基、ビニル基およびビニルベンゼン基よりなる群から選択される、少なくとも1種の官能基を有しているシラン、シラノール、シロキサンおよびポリシロキサンから選択される、少なくとも1種のケイ素化合物を含む溶液または分散液である、請求項1に記載の方法。
- 器具が、シラン、シラノール、シロキサンおよびポリシロキサンから選択される、少なくとも1種のケイ素化合物を含む溶液または分散液である組成物を収容及び分配する、請求項1に記載の方法への適用に好適な器具。
- 器具が、シラン、シラノール、シロキサンおよびポリシロキサンから選択される、少なくとも1種のケイ素化合物を含む溶液または分散液である組成物を収容する貯蔵室を有する噴霧缶、噴霧器またはスティックである、請求項1に記載の方法への適用に好適な器具。
- 器具が、シラン、シラノール、シロキサンおよびポリシロキサンから選択される、少なくとも1種のケイ素化合物を含む組成物であるペーストを収容し、ならびに、その器具が、被覆されるべき表面に接触させた時にペーストの一部を送出または放出する、請求項1に記載の方法への適用に好適な器具。