WO2009000387A1 - Verfahren zum warmwalzen und zur wärmebehandlung eines bandes aus stahl - Google Patents
Verfahren zum warmwalzen und zur wärmebehandlung eines bandes aus stahl Download PDFInfo
- Publication number
- WO2009000387A1 WO2009000387A1 PCT/EP2008/004435 EP2008004435W WO2009000387A1 WO 2009000387 A1 WO2009000387 A1 WO 2009000387A1 EP 2008004435 W EP2008004435 W EP 2008004435W WO 2009000387 A1 WO2009000387 A1 WO 2009000387A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- strip
- cooling
- belt
- heating
- temperature
- Prior art date
Abstract
Description
Claims