WO2005051858A1 - Substrat transparent utilisable alternativement ou cumulativement pour le controle thermique, le blindage electromagnetique et le vitrage chauffant. - Google Patents
Substrat transparent utilisable alternativement ou cumulativement pour le controle thermique, le blindage electromagnetique et le vitrage chauffant. Download PDFInfo
- Publication number
- WO2005051858A1 WO2005051858A1 PCT/FR2004/050614 FR2004050614W WO2005051858A1 WO 2005051858 A1 WO2005051858 A1 WO 2005051858A1 FR 2004050614 W FR2004050614 W FR 2004050614W WO 2005051858 A1 WO2005051858 A1 WO 2005051858A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- functional
- layer
- zno
- layers
- stack
- Prior art date
Abstract
Description
Claims