WO2005019376A1 - 酸窒化物蛍光体と発光器具 - Google Patents

酸窒化物蛍光体と発光器具 Download PDF

Info

Publication number
WO2005019376A1
WO2005019376A1 PCT/JP2004/012135 JP2004012135W WO2005019376A1 WO 2005019376 A1 WO2005019376 A1 WO 2005019376A1 JP 2004012135 W JP2004012135 W JP 2004012135W WO 2005019376 A1 WO2005019376 A1 WO 2005019376A1
Authority
WO
WIPO (PCT)
Prior art keywords
phosphor
light
oxynitride
oxynitride phosphor
elements
Prior art date
Application number
PCT/JP2004/012135
Other languages
English (en)
French (fr)
Inventor
Naoto Hirosaki
Original Assignee
National Institute For Materials Science
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by National Institute For Materials Science filed Critical National Institute For Materials Science
Priority to US10/561,264 priority Critical patent/US20070018567A1/en
Priority to KR1020067000302A priority patent/KR101102304B1/ko
Priority to DE112004001533.2T priority patent/DE112004001533B4/de
Priority to CN2004800240601A priority patent/CN1839193B/zh
Priority to JP2005513337A priority patent/JP5035818B2/ja
Publication of WO2005019376A1 publication Critical patent/WO2005019376A1/ja
Priority to US12/078,822 priority patent/US8007684B2/en
Priority to US13/064,465 priority patent/US8147718B2/en
Priority to US13/344,187 priority patent/US8394295B2/en

Abstract

本発明は、従来の希土類付活サイアロン蛍光体より高い発光輝度を有する酸窒化物蛍光体を提供することにある。その解決手段は、酸窒化物蛍光体の材料設計を一般式ＭＡ１（Ｓｉ6-zＡｌz）Ｎ10-zＯz（ただし、ＭはＬａ、Ｃｅ、Ｐｒ、Ｎｄ、Ｓｍ、Ｅｕ、Ｇｄ、Ｔｂ、Ｄｙ、Ｈｏ、Ｅｒ、Ｔｍ、Ｙｂ、Ｌｕから選ばれる１種または２種以上の元素）で示されるＪＥＭ相を主成分として生成せしめ、これによって例えば、蛍光スペクトル最大発光波長が４２０ｎｍ以上５００ｎｍ以下、励起スペクトル最大励起波長が２５０ｎｍ以上４００ｎｍ以下の高輝度の酸窒化物蛍光体を提供しうるものである。

Description

酸窒化物蛍光体と発光器具 技術分野
本発明は、 J EM相を主体とするシリ コン酸窒化物蛍光体とその用途に関する。 さらに詳細には、 該用途は、 該蛍光体の有する性質、 すなわち 4 2 0 n m以上の 波長の蛍光を発光する特性を利用した照明器具、 画像表示装置の発光器具に関す る。
明 背景技術
蛍光体は、 蛍光表示管 （VF D) 、 フィールドェミ ッショ ンディスプレイ （F 書
ED) 、 プラズマディスプレイパネル （PD P) 、 陰極線管 （CRT) 、 白色発 光ダイオード （L ED) などに用いられている。 これらのいずれの用途において も、 蛍光体を発光させるためには、 蛍光体を励起するためのエネルギーを蛍光体 に供給する必要があり、 蛍光体は真空紫外線、 紫外線、 電子線、 青色光などの高 いエネルギーを有した励起源により励起されて、 可視光線を発する。 従って、 蛍 光体は前記のような励起源に曝される結果、 蛍光体の輝度が低下するという問題 があり、 従来のケィ酸塩蛍光体、 リン酸塩蛍光体、 アルミン酸塩蛍光体、 硫化物 蛍光体などの蛍光体より輝度低下の少ない蛍光体として、 サイアロン蛍光体が提 案されている。 このサイアロン蛍光体の製造方法と しては、 例えば、 窒化ケィ素 （S i 3N4) 、 窒化アルミニウム （A 1 N) 、 酸化ユーロピウム （E u 203) を所定のモル比と なるように混合し、 1気圧 （0. 1 MP a ) の窒素中において 1 7 0 0 °Cの温度 で 1時間保持してホッ トプレス法により焼成して製造することが従来から行なわ れている （例えば、 特許文献 1参照） 。 この手法で得られる Euイオンを付活し た αサイアロンは、 4 50から 50 0 nmの青色光で励起されて 5 5 0から 6 0 0 nmの黄色の光を発する蛍光体となることが報告されている。 しかしながら、 紫外 L E Dや紫外線ランプなどの紫外線を励起源とする用途には、 4 0 0 nm以 下の波長で効率よく励起される蛍光体が求められていた。 また、 黄色だけでなく 青や緑色に発光する蛍光体も求められていた。 さらに、 発光輝度がより高い蛍光 体が求められていた。 特許文献 1 ； 特開 2 00 2— 3 6 3 5 5 4号公報 発明の開示
発明が解決しよう とする課題
本発明の目的は、 従来の希土類付活サイアロン蛍光体より高い発光輝度を有す る酸窒化物蛍光体を提供することにある。 課題を解決するための手段
本発明者らにおいては、 かかる状況の下で、 M、 S i、 A 1、 0、 Nの元素 （た だし、 Mは L a、 C e、 P r、 N d、 Sm、 E u、 G d、 T b、 D y、 H o、 E r、 Tm、 Y b、 L uから選ばれる 1種または 2種以上の元素） を含有する蛍光 体について鋭意研究を重ねた結果、 特定の組成領域範囲および結晶相を有するも のは、 紫外線で励起され高い輝度の発光を有する蛍光体となることを見出した。 すなわち、 一般式 MA 1 (S i 6 zA 1 z) Nio-zOz (ただし、 Mは L a、 C e、 P r、 N d、 Sm、 E u、 G d、 T b、 D y、 H o、 E r、 Tm、 Y b、 L u力 ら 選ばれる 1種または 2種以上の元素） で示される組成を有してなる J EM相は、 紫外線の照射によって励起され、 高い輝度の発光を有する蛍光体となることを見 出したものである。
J EM相は、 J e k a b s G r i n s らによって希土類金属によって安定化 された α—サイァロンを調整するプロセスにおいて生成することが確認された新 規な窒素富化物質であって、 その詳細は、 この出願前すでに学術文献 （非特許文 献 1参照） 等に詳しく報告されている。 この報告によると、 J EM相は、 前示一 般式で示される.組成よりなる結晶相であって、 特有な原子配列構造を有する、 z をパラメータとする耐熱性に優れた物質であり、 その特徴は、 下記表 1 (前記非 特許文献第 2 0 0 3ページに掲載されている T a b I e 3に同じ） に記載されて いるように特有な空間群と、 原子の占めるサイ トとその座標とによって特徴づけ られる特有な結晶構造、 原子配列構造を有してなる物質であると定義される。 非特許文献 1； J e k a b s G r i n s ほ力 3名" J o u r n a l o f M a t e r i a l s C h e m i s t r y" 1 9 9 5年、 5卷、 1 1月号、 2 0 0 1〜 2 0 0 6ぺージ 表 1 ；
Figure imgf000004_0001
すなわち、 表 1によって示される J EM相は、 （ 1 ) 特定の P b c n空間群 （S p a c e g r o u p) 、 （ 2) 格子定数 ( a = 9. 4 2 2 5、 b = 9. 7 5 6 1、 c = 8. 9 3 6 2 A) 、 および （ 3) 特定の原子サイ トと原子座標によって 特徴づけられる物質であるが、 その構成成分とする L nや固溶量 τが変化するこ とによって表 1中の格子定数は変化するが、 （ 1 ) P b c η空間群で示される結 晶構造と （ 3) 原子が占めるサイ トとその座標によって与えられる原子位置は変 わることはない。 表 1に記載されているようにこれらの基本的データが与えられれば、 当該物質 の結晶構造はこれによって一義的に決定され、 その結晶構造の有する X線回折強 度 （X線回折チヤ一ト） をこのデータに基づいて計算することができる。 そして、 測定した X線回折結果と計算した回折データとがー致したときに当該結晶構造が 同じものと特定することができる。 表 1は、 その意味で J EM層を特定する上において基準となるもので重要であ る。 この表 1に基づく物質の同定方法については、 後述実施例 1において具体的 に述べる。 .ここでは、 概略的な説明に留める。 なお、 表 1において、 サイ トの記 号は空間群の対称性を示す記号である。 座標は X、 y、 zの格子に対して 0から 1の値をとる。 また、 Mは S i または A 1 で、 Xは Oまたは Nを示している。 なお、 この J EM相は、 サイアロンの研究過程において確認された経緯からも、 専ら耐熱特性についての研究報告が主で、 蛍光体と して使用することについては これまで検討されたことはなかった。
J EM相が、 紫外線または電子線で励起され高い輝度の発光を有する蛍光体と し て使用し得ることについては、本発明者らにおいて初めて見いだしたものである。 そしてこの知見を、本発明者らは、 さらに発展させ、鋭意研究した結果、以下（ 1 ) 〜 （2 9) に記載する構成を講ずることによって特定波長領域で輝度特性に優れ た特有な発光現象があることを知見したものである。 本発明は、 前記した知見に基づく一連の研究の結果なされたものであって、 こ れによって高輝度発光する酸窒化物蛍光体および蛍光体を利用した照明器具、 画 像表示装置の発光器具を提供することに成功したものである。
( 1 ) 一般式 MA 1 ( S i 6·ζΑ 1 ζ) Ν10-ζΟ: (ただし、 Mは L a、 C e、 P r、 N d、 S m、 E u、 G d、 T b、 D y、 H o、 E r、 Tm、 Y b、 L u力 ら選ば れる 1種または 2種以上の元素） で示される . EM相を主成分とする酸窒化物蛍 光体。
( 2 ) J EM相を母体結晶と し、 Mi (ただし、 M lは C e , P r、 N d、 S ra
E u、 G d、 T b、 D v、 H o、 E r、 Tm、 L uから選ばれる 1種また は 2種以上の元素） を発光中心とすることを特徴とする前記 （ 1 ) 項に記載の酸 窒化物蛍光体。
( 3 ) 少なく とも L aおよび Mi の元素 （ただし， Mi は C e、 P r、 N d、 S m、 E u、 G d、 T b、 D y、 H o、 E r、 Tm、 Y b、 L uから選ばれる 1種 または 2種以上の元素） を含有することを特徴とする前記 （ 1 ) 項ないし （ 2 ) 項のいずれか 1項に記載の酸窒化物蛍光体。
(4) 少なく とも C eを含有することを特徴とする前記 （ 1 ) 項ないし （3) 項のいずれか 1項に記載の酸窒化物蛍光体。
(5) 少なく とも E uを含有することを特徴とする前記 （ 3) 項に記載の酸窒 化物蛍光体。
(6 ) 少なく とも T bを含有することを特徴とする前記 （ 3) 項に記載の酸窒 化物蛍光体。
( 7) 少なく とも C e と T bを含有することを特徴とする前記 （3) 項に記載の 酸窒化物蛍光体。
( 8 ) M、 S i 、 A 1、 0、 Nの元素 （ただし、 Mは L a、 C e、 P r、 N d、 Sm、 E u、 G d、 T b、 D y、 H o、 E r、 Tm、 Y b、 L u力 ら選ばれる 1 種または 2種以上の元素） を含有し、 組成式 Ma S i bA 1 cOd e (式中、 a=l と する） で示され、
b = ( 6 - z ) X f ( i )
c = ( 1 + z ) X g (ii)
d = z X h (iii)
e = ( 1 0 - z ) X i (iv)
0. 1 ≤ z ≤ 3 · · · · (v)
0. 7≤ f ≤ 1. 3 (vi)
0. 7≤ g ≤ 3 (vii)
0. 7≤ h ≤ 3 (viii)
0. 7≤ i ≤ 1. 3 (ix) 、
以上の条件を全て満たす組成であることを特徴とする酸窒化物蛍光体
( 9) f = g = h = i = j = 1であることを特徴とする前記 （8) 項に記載の 酸窒化物蛍光体。
( 1 0) z = 1であることを特徴とする前記 （8) 項ないし （ 9) 項のいずれ か 1項に記載の酸窒化物蛍光体。 ( 1 1 ) Mが C eであることを特徴とする前記 （ 8 ) 項ないし （ 1 0) 項のい ずれか 1項に記載の酸窒化物蛍光体。
( 1 2) Mが L a と C eの 2元素を少なく とも含有することを特徴とする前記 ( 8) 項ないし （ 1 0) 項のいずれか 1項に記載の酸窒化物蛍光体。
( 1 3) Mが L a と E uの 2元素を少なく とも含有することを特徴とする前記 (8) 項ないし （ 1 0) 項のいずれか 1項に記載の酸窒化物蛍光.体。
( 1 4) Mが L a と T bの 2元素を少なく とも含有することを特徴とする前記 ( 8) 項ないし （ 1 0) 項のいずれか 1項に記載の酸窒化物蛍光体。
( 1 5) Mが L a、 C e、 T bの 3元素を少なく とも含有することを特徴とす る前記 （8) 項、 （9) 項、 （ 1 0) 項、 （ 1 2) 項、 （ 1 4) 項のいずれか 1 項に記載の酸窒化物蛍光体。
( 1 6) L a と C eの 2元素を少なく とも含有し、 L a と C eの含有比 （組成 中の原子の数の比） が 0. C eノ L a ≤ 1 0 であることを特徴とす る前記 （ 1 ) 項、 （2) 項、 （ 3) 項、 （4) 項、 （ 7) 項、 （8) 項、 （9) 項、 （ 1 0) 項、 （ 1 1 ) 項、 （ 1 2 ) 項のいずれか 1項に記載の酸窒化物蛍光 体。
( 1 7) L a と E uの 2元素を少なく とも含有し、 L a と E uの含有比 （組成 中の原子の数の比） が 0. 0 0 1≤ E u/L a ≤ 1 である.ことを特徴とす る前記 （ 1 ) 項、 （ 2) 項、 （ 3) 項、 （ 5) 項、 （ （8) 項、 （9) 項、 （ 1 0) 項、 （ 1 3) 項のいずれか 1項に記載の酸窒化物蛍光体。
( 1 8 ) L a と T bの 2元素を少なく とも含有し、 L a と T bの含有比 （組成 中の原子の数の比） が 0. T b /L a 1 0であることを特徴とする 前記 （ 1 ) 項、 （2) 項、 （3 ) 項、 （6) 項、 （ 7) 項、 （8) 項、 （9) 項、
( 1 0) 項、 （ 1 4) 項、 （ 1 5 ) 項のいずれか 1項に記載の酸窒化物蛍光体。
( 1 9) L a、 C e、 T bの 3元素を少なく とも含有し、 L a、 C e , T bの 含有比 （組成中の原子の数の比） が 0. 0 1≤ (C e +T b) /L a ≤ 1 0 であることを特徴とする前記 （ 1 ) 項、 （2) 項、 （ 3) 項、 （6) 項、 （ 7) 項、 （8) 項、 （ 9) 項、 （ 1 0) 項、 （ 1 4) 項、 （ 1 5 ) 項のいずれか 1項 に記載の酸窒化物蛍光体。
(2 0) 蛍光スぺク トルにおいて、 最大発光波長が 4 2 0 nm以上 5 0 0 nm 以下であり、 励起スぺク トルにおいて最大励起波長が 2 5 0 n m以上 4 0 0 n m 以下であることを特徴とする前記 （4) 項、 （ 1 1 ) 項、 （ 1 2) 項、 （ 1 6) 項のいずれか 1項に記載の酸窒化物蛍光体。
(2 1 ) 蛍光スぺク トルにおいて、 最大発光波長が 4 8 0 n m以上 5 6 0 n m 以下であり、 励起スぺク トルにおいて最大励起波長が 2 0 0 n m以上 3 0 0 n m 以下であることを特徴とする前記 （6) 項、 （6) 項、 （ 1 4) 項、 （ 1 5) 項、
( 1 8) 項、 （ 1 9) 項のいずれか 1項に記載の酸窒化物蛍光体。
(2 2) J EM相と他の結晶相あるいはアモルファス相との混合物から構成さ れ、 J EM相の含有量が 5 0質量％以上であることを特徴とする前記 （ 1 ) 項な いし （ 2 1 ) 項のいずれか 1項に記載の酸窒化物蛍光体。
(2 3) 発光光源と蛍光体から構成される照明器具において、 少なく とも前記 ( 1 ) 項ないし （ 2 2) 項のいずれか 1項に記載の蛍光体を用いることを特徴と する照明器具。
(24) 該発光光源が 3 3 0〜 4 2 0 n mの波長の光を発する L E Dであるこ とを特徴とする前記 （ 2 3) 項に記載の照明器具。
(2 5) 該発光光源が 3 3 0〜 4 2 0 n mの波長の光を発する L E Dであり、 前記 （2 2) 項のいずれか 1項に記載の蛍光体と、 3 3 0〜 4 2 0 n mの励起光 にょり 5 2 0 11 !11以上5 7 0 11 m以下の波長の光を発する緑色蛍光体と、 3 3 0 〜4 20 nmの励起光により 5 7 0 n m以上 7 0 0 n m以下の光を発する赤色蛍 光体とを用いることにより、 赤、 緑、 青色の光を混ぜて白色光を発することを特 徴とする前記 （2 3) 項または （24) 項のいずれか 1項に記載の照明器具。
(2 6) 該発光光源が 3 3 0〜 4 2 0 n mの波長の光を発する L E Dであり、 前記 （ 1 ) 項ないし （ 2 2) 項のいずれか 1項に記載の蛍光体と、 3 30〜4 2 0 nmの励起光により 5 5 0 nm以上 6 0 0 n m以下の波長の光.を発する黄色蛍 光体とを用いることにより、 黄色と青色の光を混ぜて白色光を発することを特徴 とする前記 （ 2 3) 項または （ 2 4) 項のいずれか 1項に記載の照明器具。
(2 7) 該黄色蛍光体が E uを固溶させた C a— αサイアロンであることを特 徴とする前記 （2 6) 項に記載の照明器具。
(2 8) 励起源と蛍光体から構成される画像表示装置において、 少なく とも前 記 （ 1 ) 項ないし （2 2 ) 項のいずれか 1項に記載の蛍光体を用いることを特徴 とする画像表示装置。 画像表示装置が、 蛍光表示管 （VF D)、 フィールドエミ ッショ ンディ
G スプレイ （F ED)、 プラズマディスプレイパネル （PD P)、 陰極線管 （CRT) のいずれかであることを特徴とする前記 （2 8 ) 項に記載の画像表示装置。 発明の効果
本発明の製造方法により得られるサイアロン蛍光体は、 従来のサイアロン蛍光 体に比し、 高い輝度を示し、 励起源に曝されても材料劣化や、 輝度の低下が少な い。 そのため、 VFD、 F ED, PD P、 CRT, 白色 L E Dなどの用途に好適 であり、 この種分野における材料設計において、 新規性のある有用な材料を提供 するものである。 図面の簡単な説明
図 1 ；本発明の酸窒化物 （実施例 1 ) の X線回折チャートを示す図である。 図 2 ；本発明の酸窒化物 （実施例 1 ) の励起 ·発光スぺク トルを示す図である。 図 3 ；本発明の酸窒化物 （実施例 3) の励起 ·発光スぺク トルを示す図である。 図 4 ；本発明の酸窒化物 （実施例 5) の励起 ·発光スぺク トルを示す図である。 図 5 ；本発明の酸窒化物 （実施例 8) の励起 ·発光スぺク トルを示す図である。 図 6 ；本発明の酸窒化物の （実施例 1 4〜 2 4 ) の発光スぺク トル
図 7 ； 本発明による照明器具 （L ED照明器具） の概略図。 .
図 8 ； 本発明による画像表示装置 （プラズマディスプレイパネル） の概略図。 符号の説明 ；
1 ；本発明の赤色蛍光体 （実施例 1 ) と黄色蛍光体との混合物、 または本発明 の赤色蛍光体 （実施例 1 ) と青色蛍光体と緑色蛍光体との混合物。 ·
2 ， L E Dチップ。
3 、 4 ；導電性端子。
5 ワイヤーボンド。
6 樹脂層。
7 容 ¾5。
8 本発明の赤色蛍光体 （実施例 1 )。
9 緑色蛍光体。
1 0 ； 青色蛍光体。
1 1 、 1 2、 1 3 ; 紫外線発光セル。
1 4、 1 5、 1 6、 1 7 ;
1 8、 1 9 ;誘電体層。
2 0
2 1 2 2 ； ガラス基板。 発明を実施するための最良の形態
以下、 本発明の実施の態様を以下実施例に基づいて詳しく説明する。 本発明の蛍光体は、 一般式 MA 1 ( S i 6·ΖΑ 1 ζ) 10·ζΟζ (ただし、 Μは L a、 C e、 P r、 N d、 Sm、 E u、 G d、 T b、 D y、 H o、 E r、 Tm、 Y b、 L uから選ばれる 1種または 2種以上の元素） で示される J EM相を主成分と し て含んでなるものである。 本発明では、 蛍光発光の点からは、 その酸窒化物蛍光 体の構成成分たる J EM相は、 高純度で極力多く含むこと、 できれば単相から構 成されていることが望ましいが、 特性が低下しない範囲内で他の結晶相あるいは アモルファス相との混合物から構成することもできる。 この場合、 J EM相の含 有量が 5 0質量％以上であることが高い輝度を得るために望ましい。 本発明にお いて主成分とする範囲は、 J EM相の含有量が少なく とも 5 0質量％以上である。
J EM相を生成するには、 一般式 MA 1 ( S i 6·ΖΑ 1 ζ) Ν10.ζΟζにおける Μと して L a、 C e、 P r、 N d、 Sm、 E u、 G d、 T b、 D y、 H o、 E r、 Tm、 Y b、 L uから選ばれる 1種または 2種以上の元素を含んでいることが必 要である。 なかでも、 L a、 C e、 N dが J EM相を形成する組成範囲が広いの で好ましい。
J EM相を母体結晶と し、 Mi (ただし、 Miは C e , P r、 N d、 Sm、 E u、 G d、 T b、 D y、 H o、 E r、 Tm、 Y b、 L uから選ばれる 1種または 2種 以上の元素の混合物） 元素を J EM母体に固溶させることによって、 これらの元 素が発光中心として働き、 蛍光特性を発現する。 ただし、 母体形成のための元素 と発光中心の元素が同一のことも可能である。 C eの J EM相はこれにあたり、 発光中心 （M を添加することなく C eの J EM相単独で輝度が高い蛍光体とな り得る。
L aを J EM相形成のための主元素と して用いると輝度の高い蛍光体が得られ るので好ましい。 この場合、 少なく とも L aおよび Miの元素 （ただし， Miは C e、 P r、 N d、 Sm、 E u、 G d、 T b、 D y、 H o、 E r、 Tm、 Y b、 L uから選ばれる 1種または 2種以上の混合物） を含有し J EM相を形成する組成 が選ばれる。 特に、 L aの J EM相を母体結晶として、 （ 1 ) C eを発光中心と する蛍光体、 （2) E uを発光中心とする蛍光体、 （ 3) T bを発光中心とする 蛍光体、 （4) C e と T bを含み T bを発光中心とする蛍光体は輝度が高く、 組 成により様々な色の発光をするので、 用途により適宜組み合わせ、 選ぶことがで さる。 本発明では J EM相の結晶構造を持つ M (ただし Mは、 L a、 C e、 P r、 N d、 Sm、 E u、 G d、 T b、 D y、 H o、 E r、 Tm、 Y b、 L uから選ばれ る 1種または 2種以上の元素） 、 S i 、 A l 、 0、 Nから構成される物質で有れ ば組成の種類を特に規定しないが、 次の組成で J EIV [相の含有割合が高く、 輝度 が高い蛍光体が得られる。
S M、 S i 、 A l 、 0、 Nの元素 （ただし、 Mは L a 、 C e 、 P r 、 N d、 S m、 E u、 G d、 T b、 D y、 H o、 E r、 Tm、 Y b、 L uから選ばれる 1種また は 2種以上の元素） から構成され、 その組成は組成式 MaS i bA l cOdNeで示さ れる。 組成式はその物質を構成する原子数の比であり、 a、 b、 c、 d、 eに任 意の数をかけた物も同一の組成である。 従って、 本発明では a=l となるように a、 b、 c、 d、 eを計算し直したものに対して以下の条件を決める。
本発明では、 b、 c、 d、 e、 f の値は、
b = ( 6 - z ) X f (i)
c = ( 1 + z ) X g (ii)
d = z X h (iii)
e = ( 1 0 - z ) X i (iv)
0. 1 ≤ z ≤ 3 (v)
0. 7 ≤ f ≤ 1 . 3 (vi)
0. 7 ≤ g ≤ 3 (vii)
0. 7 ≤ h ≤ 3 (viii)
0. 7 ≤ i ≤ 1 . 3 (ix) 、
の条件を全て満たす値から選ばれる。 ここに、 f 、 g、 h、 i 、 j は、 J EMの一般式、
MA 1 ( S i 6 zA 1 z) N10 zOz
からのずれを表している。 式中、 a値は金属元素 M (ただし、 Mは L a、 C e、 P r 、 N d、 S m、 E u、 G d、 T b、 D y、 H o E r、 Tm、 Y b、 L u力 ら選ばれる 1種または 2種以上の元素） の含有量であり 蛍光体中に含まれるこ れらの元素の総量である。 本発明では a値は 1 とする。 b値は、 S i の含有量であり、 b = ( 6 — z ) X f で与えられる。
ただし、 z、 f は、 0. 1 ≤ z ≤ 3 , 0. 7 ≤ f I . 3で示される量 である。 好ましくは f = lがよい。 b値がこの値の範囲外では安定な J EM相が 生成しないため発光強度が低下する c値は、 A 1 の含有量であり、 c = ( 1 + z ) X gで与えられる。
ただし、 z、 f は、 0. 1 ≤ z ≤ 3 , 0. 7 ≤ g 3で示される量であ る。 好ましくは g = lがよい。 b値がこの値の範囲外では安定な J EM相が生成 しないため発光強度が低下する。 d値は、 Oの含有量であり、 d == z X hで与えられる。
ただし、 z、 つは、 0. 1 ≤ z ≤ 3 , 0. 7 ≤ h ≤ 3で示される量であ る。 好ましくは h = lがよい。 b値がこの値の範囲外では安定な J EM相が生成 しないため発光強度が低下する。 e値は、 Nの含有量であり、 e = ( 1 0 - z ) X iで与えられる。
ただし、 z、 i は、 0. 1 z ≤ 3 , 0. 7≤ i ≤ 1. ·3で示される量 である。 好ましくは i = lがよい。 b値がこの値の範囲外では安定な J EM相が 生成しないため発光強度が低下する。 以上の組成範囲で高輝度の発光を示す蛍光体が得られるが、 特に輝度が高いの は、
( 1 ) Mが C eである組成、
( 2 ) Mが L a と C eの 2元素を少なく とも含有する組成であり、 中でも L a と C eの含有比 （組成中の原子の数の比） が 0. 0 1≤ C e /L a ≤ 1 0 で ある組成、
( 3 ) Mが L a と E uの 2元素を少なく とも含有する組成であり、 中でも L a と E uの含有比 （組成中の原子の数の比） が 0. 00 1 ≤ E u/L a ≤ 1 で ある組成、
( 4 ) Mが L a と T bの 2元素を少なく とも含有する組成であり、 中でも L a と T bの含有比 （組成中の原子の数の比） が 0. 0 1≤ T b/L a ≤ 1 0であ る組成、
( 5 ) Mが L a、 C e、 T bの 3元素を少なく とも含有する組成'、
であり、
その中でも L a、 C e、 T bの 3元素を少なく とも含有し、 L a、 C e， T bの 含有比 （組成中の原子の数の比） が 0. 0 1 ≤ (C e +T b) /L a ≤ 1 0 である組成、
の何れかの組成を選択することによって一層発光強度の高い蛍光体とすることが できる。 本発明の蛍光体は、 蛍光体を構成する組成の違いにより励起スぺク トルと蛍光 スペク トルが異なり、 これを適宜選択組み合わせることによって、 さまざまな発 光スぺク トルを有してなるものに任意に設定することができる。 その態様は、 用途に基づいて必要とされるスぺク トルに設定すればよい。
C e J £^1相ゃし a J EM相に C eを付活したものにおいては、 最大発光波長が 4 2 O nm以上 5 0 O nm以下であり、 励起スぺク トルにおいて最大励起波長が 2 5 0 nm以上 4 0 O n m以下である紫外線で励起されて青色の光を発光する蛍 光体を得ることができる。 また、 L a J EM相に Tbを付活したものにおいては、 最大発光波長が 4 8 0 nm以上 5 6 O nm以下であり、 励起スぺク トルにおいて最大励起波長が 2 0 0 nm以上 3 0 0 n m以下である紫外線で励起されて緑色の光を発光する蛍光体を 得ることができる。
：0 本発明では、 結晶相と して J EM相の単相から構成されることが望ましいが、 特性が低下しない範囲内で他の結晶相あるいはアモルファス相との混合物から構 成することもできる。 この場合、 J EM相の含有量が 5 0質量％以上であること が高い輝度を得るために望ましい。 本発明において主成分とする範囲は、 前述したように、 J EM相の含有量が少 なく とも 5 0質量。 /0以上である。 J EM相の含有量の割合は、 X線回折測定を行 い、 それぞれの相の最強ピークの強さの比から求めることができる。 本発明の蛍光体を電子線で励起する用途に使用する場合は、 導電性を持つ無機 物質を混合することにより蛍光体に導電性を付与することができる。 導電性を持 つ無機物質としては、 Z n、 A l 、 G a、 I n、 S nから選ばれる 1種または 2 種以上の元素を含む酸化物、 酸窒化物、 または窒化物、 あるいはこれらの混合物 を挙げることができる。 本発明の製造方法により得られる酸窒化物蛍光体は、 従来のサイアロン蛍光体 より高い輝度を示し、励起源に曝された場合の蛍光体の輝度の低下が少ないので、 VFD、 F ED、 PD P、 CRT, 白色 L E Dなどに好適に有する酸窒化物蛍光 体である。 本発明の照明器具は、 少なく とも発光光源と本発明の蛍光体を用いて構成され る。 照明器具としては、 L ED照明器具、 蛍光ランプなどがある。 例えば、 L E D照明器具は、 本発明の蛍光体を用い、 この蛍光体を先行文献、 例えば日本特許 公報の特開平 5— 1 5 2 6 0 9、 特開平 7— 9 9 3 4 5、 特許公報第 2 9 2 7 2 7 9号など、 に記載されているような公知の手法、 手段を適用して製造すること ができる。 この場合、 発光光源は 1 0 0〜 5 0 0 n mの波長の光を発するものが 望ましく、 中でも 3 3 0〜4 2 0 n mの紫外 （または紫） L ED発光素子が好ま しい。 これらの発光素子と しては、 G a Nや I n G a Nなどの窒化物半導体からなるも のがあり、 組成を調整することにより、 所定の波長の光を発する発光光源となり 得る。 照明器具において本発明の蛍光体を単独で使用する方法のほかに、 他の発光特 性を持つ蛍光体と併用することによって、 所望の色を発する照明器具を構成する ことができる。 この一例として、 3 3 0〜 4 2 0 nmの紫外 L EDあるいは紫 L ED発光素子と この波長で励起され 5 2 0 nra以上 5 7 0 n m以下の波長の光を発する緑色蛍光 体と、 5 70 nm以上 7 00 n m以下の光を発する赤色蛍光体と本発明の蛍光体 W 2
との組み合わせがある このような緑色蛍光体と しては B a M g A l 1 0O 1 7 ： E u、 Mnを、 赤色蛍 光体と しては Y 2O 3 ： E uを挙げることができる。 この構成では、 L E Dが発する紫外線が蛍光体に照射されると、 赤、 緑、 青の 3色の光が発せられ、 これの混合により 白色の照明器具となる。 別の手法と して、 3 3 0〜 4 2 0 n mの紫外 L E Dあるいは紫 L E D発光素子 とこの波長で励起されて 5 5 0 nm以上 6 0 0 n m以下の波長に発光ピークを持 つ黄色蛍光体および本発明の蛍光体との組み合わせがある。 このような黄色蛍光体と しては、 特許公報第 2 9 2 7 2 7 9号に記載の （Y、 G d) 2 (A l 、 G a ) 501 2 : C eゃ特開 2 0 0 2— 3 6 3 5 5 4に記載の α 一サイアロン ： E u系を挙げることができる。 なかでも E uを固溶させた C a - α -サイアロンが発光輝度が高いのでよい。 この構成では、 L EDが発する紫外あ るいは紫光が蛍光体に照射されると、 青、 黄の 2色の光が発せられ、 これらの光 が混合されて白色または赤みがかった電球色の照明器具となる。 本発明の画像表示装置は少なく も励起源と本発明の蛍光体で構成され、 蛍光表 示管 （VFD)、 フィールドェミッションディスプレイ （F ED)、 プラズマディ スプレイパネル （PD P)、 陰極線管 （CRT) などがある。 本発明の蛍光体は、 1 0 0〜 1 9 0 n mの真空紫外線、 1 9 0〜 3 8 0 n mの紫外線、 電子線などの 励起で発光することが確認されており、 これらの励起源と本発明の蛍光体との組 み合わせで、 上記のような画像表示装置を構成することができる。 次に本発明を具体的実施例によってさらに詳しく説明するが、 これはあくまで も本発明を容易に理解するための一助として開示したものであって、 本発明は、 これらの実施例に限定されるものではない。 実施例 1 ；
組成式 L a 0.2 C e o.s S i 5A 12θ1.5Ν8.7で示される化合物 （表 3に原料粉末の 混合組成、 表 4にパラメータ、 表 5に反応後の計算組成を示す） を得るべく、 平 均粒径 0. 、 酸素含有量 0. 9 3重量％、 α型含有量 9 2 %の'窒化ケィ素 粉末と窒化アルミニウム粉末と酸化ランタンと酸化セリ ウムとを、 各々 4 8. 6 6重量％、 1 7. 0 6重量％、 2 7. 1 2重量0 /。、 7. 1 6重量％となるように 秤量し、 η—へキサンを用いて湿式ボールミルにより 2時間混合した。 ロータリーエバポレータにより η—へキサンを除去し、 得られた混合物を、 金型 を用いて 2 0MP aの圧力を加えて成形し、 直径 1 2 mm、 厚さ 5 mmの成形体 と した この成形体を窒化ホウ素製のるつぼに入れて黒鉛抵抗加熱方式の電気炉にセッ ト した。 焼成の操作は、 まず、 拡散ポンプにより焼成雰囲気を真空とし、 室温から
8 0 0°Cまで毎時 5 0 0°Cの速度で加熱し、 8 0 0°Cで純度が 9 9. 9 9 9体積％ の窒素を導入して圧力を 1 MP a とし、 毎時 5 00°Cで 1 7 0 0°Cまで昇温し、 1 7 0 0°Cで 2時間保持して行った。 焼成後、 得られた焼結体の構成結晶を以下のような手順によって同定した結果、 J EM相であると判定された。 先ず、 合成した試料をメノウの乳鉢を用いて粉末 に粉砕し、 C uの Κ α線を用いた粉末 X線回折測定を行った。 その結果、 得られたチャートは図 1に示すパターンを示した。 これを指数付け した結果、 下記の表 2に示す結果が得られた。 表 2から求めた格子定数は、 （a = 9. 4 3 04 A, b = 9. 7 6 8 9 A, c = 8. 9 3 8 6 A) であった。 この格子定数と表 1に示す原子座標を用いて、 リ一トベルト解析計算ソフ ト (R I E T AN— 2 0 0 0、 泉富士夫作、 朝倉書店、 粉末 X線解析の実際） によ り X線回折図形シミユ レーシヨンを行ったところ、 実験で得られた X線回折図と 一致した。 これらの結果から、 実施例 1の物質は J EM相であると判定された。すなわち、 図 1に示すように J EM相が主成分で、 j3サイアロンが副生成物である混合物で ることが確認された。 それぞれの相の最強ピークは 8 3 と 1 5であり、 これから 求めた J EM相の割合は 8 5 %であった。 この粉末に、 波長 3 6 5 nmの光を発するランプで照射した結果、 青色に発光 することを確認した。 この粉末の発光スペク トルおよび励起スペク トル （図 2) を蛍光分光光度計を用いて測定した結果、 この粉末は 3 6 5 nmに励起スぺク ト ルのピークがあり 3 6 5 n mの紫外光励起による発光スぺク トルにおいて、 44 7 nmの青色光にピークがある蛍光体であることが分かった。 ピークの発光強度は、 1 7 8 7カウントであった。 なおカウント値は測定装置 や条件によって変化するため単位は任意単位である。 すなわち、 同一条件で測定 した本実施例および比較例内でしか比較できない。 電子線励起によるこの粉末の発光特性を、 力ソードルミネッセンス （C L) 検 知器を備えた S EMで観察した。 この装置は、 電子線を照射して発生する可視光 を光ファイバ一を通して装置の外に設置されたホ トマルチプライヤに誘導するこ とにより、電子線で励起して発する光の発光スぺク トルを測定できる装置である。 この蛍光体は電子線で励起されて 4 3 0 n mの波長の青色発光を示すことが確 された。 表 2 ；
Figure imgf000016_0001
実施例 2〜 1 2 ；
表 3、 表 4、 表 5に示す組成の他は実施例 1 と同様の手法で酸窒化物粉末を作 成したところ、 表 6の実施例 2〜 1 2に示すように紫外線で励起される輝度が高 い蛍光体が得られた。 実施例 3 (C e iS i 5A 12θι.5Ν8.7) は、 希土類として C eだけを含むもので あり、 図 3に示すスペク トルを示し、 4 6 8 n mの青色発光する蛍光体が得られ た。 実施例 5 (L a o.sE U 0.2S i 5A 12Oi.5N8.7) は、 E uを発光中心とするも のであり、 図 4に示すスペク トルを示し、 5 1 0〜 5 5 0 n mの緑色発光する蛍 光体が得られた。 実施例 8 (L a 0.5T b 0.5S i 5A 12Οι.5Ν8.7) は、 T bを発光中心とするもの であり、 図 5に示すスペク トルを示し、 緑色発光する蛍光体が得られた。 比較例 1 3 ;
表 3に示す組成のほかは実施例 1 と同様の手法で酸窒化物粉末を作成した。
J EM含有率の高いものが得られたが、 比較例 1 3に例示するように輝度が高い 蛍光体は得られなかった。 表 3 ；
Figure imgf000017_0001
表 4 ：
Figure imgf000017_0002
表 5 ；
生成物組成 (原子％)
Si La Ce Eu Tb Al o N 実施例 1 27.523 4.4037 1.1009 0 0 11.009 8.2569 47.706
2 27.523 0 0 5.5046 0 11.009 8.2569 47.706
3 27.523 0 5.5046 0 0 11.009 8.2569 47.706
4 27.523 2.7523 2.7523 0 0 11.009 8.2569 47.706
5 27.523 4.4037 0 1.1009 0 11.009 8.2569 47.706
6 27.523 2.7523 0 2.7523 0 11.009 8.2569 47.706
7 27.523 4.4037 0 0 1.009 11.009 8.2569 47.706
8 27.523 2.7523 0 0 2.7523 11.009 8.2569 47.706
9 27.778 4.4444 1.1111 0 0 11.111 5.5556 50
10 27.778 4.4444 0 1.1111 0 11.111 5.5556 50
11 27.778 4.4444 0 0 1.1111 11.111 5.5556 50
12 27.778 4.4444 0.5556 0 0.5556 11.111 5.5556 50
27.523 5.5046 0 0 0 11.009 8.2569 47.706 表 6 ；
Figure imgf000018_0001
実施例 1 4〜 3 2 ；
原料粉末は、窒化ケィ素粉末（平均粒径 0. 5 in、酸素含有量 0. 9 3重量％、 ひ型含有量 9 2%)、 窒化アルミニウム粉末 （比表面積 3. 3m2Zg、 酸素含有 量 0. 7 9 %)、 酸化ランタン粉末 （純度 9 9. 9 %)、 酸化ユーロピウム粉末 （純 度 9 9. 9 %)、 酸化アルミニウム粉末 （純度 9 9. 9 %)、 さらに、 金属ランタ ン （純度 9 9. 9%) をアンモニア中で窒化して合成した窒化ランタン粉末、 金 属セリ ゥムをアンモニア中で窒化して合成した窒化セリ ゥム粉末、 及び金属ユー 口ピウムをアンモニア中で窒化して合成した窒化ユーロピウム粉末、 以上の粉末 を用いた。 これらの原料粉末を表 7に示す組成となるように枰量し、 メノゥ乳棒と乳鉢で 3 0分間混合を行なった後に、 得られた混合物を、 5 00 mのふるいを通して 窒化ホウ素製のるつぼに自然落下させて、 るつぼに粉末を充填した。 粉体の嵩密 度 （体積充填率） は約 2 0〜 3 0 %であった。 嵩密度を 3 0 %以下の状態に保持したのは、 原料粉末の周りに自由な空間があ ると次の焼成工程で、 反応生成物が自由な空間に結晶成長することにより結晶同 士の接触が少なくなり、 これによつて、 表面欠陥の少ない結晶を合成することが 出来るためである。 作製する試料に窒化ランタン粉末、 窒化セリ ウム粉末、 窒化 ユーロピウム粉末が含まれる場合は、 粉末の枰量、 混合、 充填の各工程は全て、 水分 1 p p m以下酸素 1 p p m以下の窒素雰囲気を保持することができるグロ一 ブボックス中で操作を行った。 この混合粉末を窒化ホウ素製のるつぼに入れて黒鉛抵抗加熱方式の電気炉にセ ッ トした。 焼成の操作は、 まず、 拡散ポンプにより焼成雰囲気を真空とし、 室温 から 8 0 0 °Cまで毎時 5 0 0 °Cの速度で加熱し、 8 0 0 °(：で純度が9 9 . 9 9 9 体積％の窒素を導入して圧力を I M P a とし、 毎時 5 0 0。Cで 1 9 0 0。Cまで昇 温し、 1 9 0 0 °Cで 2時間保持して行った。 焼成後、 この得られた焼成体を粗粉 砕の後、 窒化ケィ素焼結体製のるつぼと乳鉢を用いて手で粉砕し、 3 0 μ ηιの目 のふるいにかけて粉末を得た。この合成した粉末をメノゥの乳鉢を用いて粉碎し、 C uの K a線を用いた粉末 X線回折測定を行った。 その結果、 全ての試料で主成 分は J E M相であり、 その含有割合は 5 0 %以上であった。 この粉末の発光スぺク トルおょぴ励起スぺク トルを蛍光分光光度計を用いて 測定した結果を表 8に示す。 実施例 1 4〜 2 4に関しては発光スベタ.トルを図 6 に示す。 蛍光測定の結果、 4 0 0〜 5 4 0 n mの波長にピークを持つ青色あるい は緑色の発色を示す蛍光体であることが分かった。 表 7 原料組成 (重量％)
Si3N4 La203 Ce02 Eu203 Al203 LaN CeN EuN AIN
実施例 14 48.85 33.35 0.69 17.12
' 15 48.85 33.69 0.34 17.12
16 48.85 33.92 0.1 1 17.12
17 48.85 33.99 0.34 17.12
18 48.85 34.02 0.01 17.12
19 48.82 33.33 0.74 17.12
20 48.83 33.68 0.37 17.12
21 48.84 33.91 0.12 17.12
22 48.85 33.99 0.04 17.12
23 48.85 34.02 0.01 17.12
24 48.84 32.89 1.14 17.12
25 59.13 31.26 0.97 8.64
26 54.16 1 1.43 20.5 12.94
27 49.19 22.84 9.76 17.24
28 59.09 31.23 1.05 8.63
29 54.1 1 1 1.42 20.48 1.05 12.94
30 49.15 22.83 9.75 1.05 17.23
31 44.19 33.18 1.1 1 21.52
32 39.25 33.15 1.1 1 3.56 22.93 表 8 ；
Figure imgf000020_0001
次ぎに、 不発明の窒化物からなる蛍光体を用いた照明器具について説明する。 図 7に、 照明器具としての白色 L E Dの概略構造図を示す。 発光素子として 40 5 nmの紫 L ED 2を用い、本発明の実施例 24の蛍光体と、 a。. 75 E U 0. 25 S Ϊ 8. 6 2 5 A 13. 3 7 5 O ^ 125N14. g 75の組成を持つ C &
-α-サイアロン： E u系の黄色蛍光体とを樹脂層に分散させて L E D 2上にかぶ せた構造とする。 導電性端子に電流を流すと、 該 LED 2は 405 n mの光を発 し、 この光で青色蛍光体および黄色蛍光体が励起されて青色および黄色の光を発 し、 黄色および青色が混合されて白色の光を発する照明装置として機能する。 上記配合とは異なる配合設計によって作製した照明装置を示す。 先ず、 発光素 子として 380 nmの紫外 L EDを用い、 本発明の実施例 24の蛍光体と、 緑色 蛍光体 （Β &Μ8 Α 1 1 ()Ο17 : Ε ι、 Μη) と、 赤色蛍光体 （ L a 2 Ο , S ： E u) を樹脂層に分散させて紫外 L ED上にかぶせた構造とする。 導電性端子に電 流を流すと、 L EDは 380 nmの光を発し、 この光で赤色蛍光体と緑色蛍光体 と青色蛍光体が励起されて赤色と緑色と青色の光を発する。 これらの光が混合さ れて白色の光を発する照明装置として機能する。 次ぎに、 本発明の蛍光体を用いた画像表示装置の設計例について説明する。 図
8は、画像表示装置としてのプラズマディスプレイパネルの原理的概略図である。 本発明の実施例 24の赤色蛍光体と緑色蛍光体 （Z n 2 S i 04 ： Mn) および青 色蛍光体 （B a Mg A l 1 C)O 1 7 : E u) がそれぞれのセル 1 1、 1 2、 1 3の 内面に塗布されている。 電極 1 4、 1 5、 1 6、 1 7に通電するとセル中で X e 放電により真空紫外線が発生し、 これにより蛍光体が励起されて、 赤、 緑、 青の 可視光を発し、 この光が保護層 2 0、 誘電体層 1 9、 ガラス基板 2 2を介して外 側から観察され、 画像表示と して機能する。 また、 本発明の蛍光体は、 電子線を照射すると青色ないし緑色に発光すること から、 CRTゃフィールドエミッションディスプレイ用の蛍光体として機能する。 以上述べたように、 本発明は、 これまでなかった新規な組成の蛍光体とその製 造方法を提供するものであり、 これによつて、 高輝度、 劣化のない優れた蛍光体 を提供するものである。 産業上の利用可能性
近年、 蛍光体とその利用に大きな関心が集まっている。 本発明.の窒化物蛍光体 は、 従来のサイアロンや酸窒化物蛍光体より高輝度発光し、 励起源に曝されたも 蛍光体の輝度低下、 材料劣化の少ない特性を有し、 VFD、 F ED, PD P、 C RT、 白色 L EDなどに好適に使用される新規な窒化物蛍光体である。 今後、 各 種表示装置をはじめ、 照明器具等における材料設計において、 大いに利用される ことが期待される。

Claims

請 求 の 範 囲
1. —般式 MA 1 ( S i 6-zA 1 z) Nio-zOz (ただし、 Mは L a、 C e、 P r、 N d、 Sm、 E u、 G d、 T b、 D y、 H o、 E r、 Tm、 Y b、 L uから選ば れる 1種または 2種以上の元素） で示される J EM相を主成分として含有してい ることを特徴とする酸窒化物蛍光体。
2. J EM相を母体結晶とし、 Mi (ただし、 Miは C e， P r '、 N d
E u、 G d、 T b、 D y、 H o、 E r、 Tm、 Y b、 L uから選ばれる
は 2種以上の元素） を発光中心と してなることを特徴と している請求項
載の酸窒化物蛍光体。
3. 少なく とも L aおよび Miの元素 （ただし， Miは C e、 P r、 N d、 S m、 E u、 G d、 T b、 D y、 H o、 E r、 Tm、 Y b、 L uから選ばれる 1種また は 2種以上の元素） を含有することを特徴とする請求項 1項ないし 2項のいずれ か 1項に記載の酸窒化物蛍光体。
4. 少なく とも C eを含有することを特徴とする請求項 1項ないし 3項のいず れか 1項に記載の酸窒化物蛍光体。
5. 少なく とも E uを含有することを特徴とする請求項 3項に記載の酸窒化物 蛍光体。
6. 少なく とも T bを含有することを特徴とする請求項 3項に'記載の酸窒化物 蛍光体。
7. 少なく とも C e と T bを含有することを特徴とする請求項 3項に記載の酸 窒化物蛍光体。
8. M、 S i 、 A l 、 0、 Nの元素 （ただし、 Mは L a、 C e、 P r、 N d、 Sm、 E u、 G d、 T b、 D y、 H o、 E r、 Tm、 Y b、 L uから選ばれる 1 種または 2種以上の元素） を含有し、 組成式 MaS i bA 1 cOdNe (式中、 a=l と する） で示され、
b = ( 6 - z ) X f (i)
c = ( 1 + z ) X g (ii)
d = z X h (iii)
e = ( 1 0 - z ) X i (iv)
0. 1≤ z ≤ 3 (v)
0. 7≤ f ≤ 1. 3 (vi)
0. 7≤ g ≤ 3 (vii)
0. 7≤ h ≤ 3 (viii)
0. 7≤ i ≤ 1. 3 (ix) 、
以上の条件を全て満たす組成であることを特徴とする酸窒化物蛍光体。
9. f = g = h = i = lであることを特徴とする請求項 8項に記載の酸窒化物 蛍光体。
1 0. z = lであることを特徴とする請求項 8項ないし 9のいずれか 1項に記載 の酸窒化物蛍光体。
1 1. Mが C eであることを特徴とする請求項 8項ないし 1 0のいずれか 1項 に記載の酸窒化物蛍光体。
1 2. Mが L a と C eの 2元素を少なく とも含有することを特徴とする請求項 8項ないし 1 0のいずれか 1項に記載の酸窒化物蛍光体。
1 3. Mが L a と E uの 2元素を少なく とも含有することを特徴とする請求項 8項ないし 1 0のいずれか 1項に記載の酸窒化物蛍光体。
1 4. Mが L a と T bの 2元素を少なく とも含有することを特徴とする請求項 8項ないし 1 0のいずれか 1項に記載の酸窒化物蛍光体。
1 5. Mが L a、 C e、 T bの 3元素を少なく とも含有することを特徴とする 請求項 8項、 9項、 1 0項、 1 2項、 1 4項のいずれか 1項に記載の酸窒化物蛍 光体。
1 6. L a と C eの 2元素を少なく とも含有し、 L a と C eの含有比 （組成中 の原子の数の比） が 0. 0 1 ≤ C e /L a ≤ 1 0 であることを特徴とする 請求項 1項、 2項、 3項、 4項、 7項、 8項、 9項、 1 0項、 1.1項、 1 2項の いずれか 1項に記載の酸窒化物蛍光体。
1 7. L a と E uの 2元素を少なく とも含有し、 L a と E uの含有比 （組成中 の原子の数の比） が 0. 0 0 1≤ E u /L a ≤ 1 であることを特徴とする 請求項 1項、 2項、 3項、 5項、 8項、 9項、 1 0項、 1 3項のいずれか 1項に 記載の酸窒化物蛍光体。
1 8. L a と T bの 2元素を少なく とも含有し、 & と丁 15の含有比 （組成中 の原子の数の比） が 0. 0 1≤ T b / L a ≤ 1 0であることを特徴とする請 求項 1項、 2項、 3項、 6項、 7項、 8項、 9項、 1 0項、 1 4項 1 5項のいず れか 1項に記載の酸窒化物蛍光体。
1 9. L a、 C e、 T bの 3元素を少なく とも含有し、 L a、 C e , T bの含 有比 （組成中の原子の数の比） が 0. 0 1≤ (C e +T b) /L a で あることを特徴とする請求項 1項、 2項、 3項、 6項、 7項、 8'項、 9項、 1 0 項、 1 4項、 1 5項のいずれか 1項に記載の酸窒化物蛍光体。
2 0. 蛍光スぺク トルにおいて、 最大発光波長が 4 2 0 nm以上 5 00 nm以 下であり、 励起スぺク トルにおいて最大励起波長が 2 5 0 1111以上4 0 0 1 111以 下であることを特徴とする請求項 4項、 1 1項、 1 2項、 1 6項のいずれか 1項 に記載の酸窒化物蛍光体。
2 1. 蛍光スぺク トルにおいて、 最大発光波長が 4 8 0 11111以上5 6 0 11111以 下であり、 励起スぺク トルにおいて最大励起波長が 2 0 0 nm以上 3 0 0 n m以 下であることを特徴とする請求項 6項、 7項、 1 4項、 1 5項、 1 8項、 1 9項 のいずれか 1項に記載の酸窒化物蛍光体。
2 2. J EM相と他の結晶相あるいはアモルファス相との混合物から構成され、 J EM相の含有量が 5 0質量％以上であることを特徴とする請求項 1項ないし 2 1項のいずれか 1項に記載の酸窒化物蛍光体。
2 3. 発光光源と蛍光体から構成される照明器具において、 少なく とも請求項 1項ないし 2 2項のいずれか 1項に記載の蛍光体を用いることを特徴とする照明 器具。
24. 該発光光源が 3 3 0〜 4 20 n mの波長の光を発する L E Dであること を特徴とする請求項 2 3項に記載の照明器具。
2 5. 該発光光源が 3 3 0〜4 2 0 nmの波長の光を発する L EDであり、 請 求項 1項ないし 2 2項のいずれか 1項に記載の蛍光体と、 3 3 0〜 4 20 n mの 励起光により 5 2 0 nm以上 5 7 0 n m以下の波長の光を発する緑色蛍光体と、
3 3 0〜 4 2 0 n mの励起光により 5 7 0 n m以上 70 0 nm以下の光を発する 赤色蛍光体とを用いることにより、 赤、 緑、 青色の光を混ぜて白色光を発するこ とを特徴とする請求項 2 3項または 24項のいずれか 1項に記載の照明器具。
2 6. 該発光光源が 3 3 0〜4 2 0 n mの波長の光を発する L E Dであり、 請 求項 1項ないし 2 2項のいずれか 1項に記載の蛍光体と、 3 3 0〜4 2 0 nmの 励起光により 5 5 0 n m以上 6 0 0 n m以下の波長の光を発する黄色蛍光体とを 用いることにより、 黄色と青色の光を混ぜて白色光を発することを特徴とする請 求項 2 3項または 2 4項のいずれか 1項に記載の照明器具。 該黄色蛍光体が E uを固溶させた C a—ひサイアロンであることを特徴 とする請求項 2 6項に記載の照明器具。
2 8. 励起源と蛍光体から構成される画像表示装置において、 少なく とも請求 項 1項ないし 2 2項のいずれか 1項に記載の蛍光体を用いることを特徴とする画 像表示装置。
2 9. 画像表示装置が、 蛍光表示管 （V F D)、 フィールドエミ ッションデイス プレイ （F ED)、 プラズマディスプレイパネル （PD P)、 陰極線管 （CRT) のいずれかであることを特徴とする請求項 2 8項に記載の画像表示装置。
PCT/JP2004/012135 2003-08-22 2004-08-18 酸窒化物蛍光体と発光器具 WO2005019376A1 (ja)