US20120060928A1 - Processes for preparing copper tin sulfide and copper zinc tin sulfide films - Google Patents

Processes for preparing copper tin sulfide and copper zinc tin sulfide films Download PDF

Info

Publication number
US20120060928A1
US20120060928A1 US13/319,900 US201013319900A US2012060928A1 US 20120060928 A1 US20120060928 A1 US 20120060928A1 US 201013319900 A US201013319900 A US 201013319900A US 2012060928 A1 US2012060928 A1 US 2012060928A1
Authority
US
United States
Prior art keywords
tin
copper
group
zinc
sulfur
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US13/319,900
Other languages
English (en)
Inventor
Lynda Kaye Johnson
Meijun Lu
John W. Catron, Jr.
Daniela Rodica Radu
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
EIDP Inc
Original Assignee
EI Du Pont de Nemours and Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by EI Du Pont de Nemours and Co filed Critical EI Du Pont de Nemours and Co
Priority to US13/319,900 priority Critical patent/US20120060928A1/en
Publication of US20120060928A1 publication Critical patent/US20120060928A1/en
Abandoned legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D11/00—Inks
    • C09D11/02—Printing inks
    • C09D11/03—Printing inks characterised by features other than the chemical nature of the binder
    • C09D11/037—Printing inks characterised by features other than the chemical nature of the binder characterised by the pigment
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L31/00—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof
    • H01L31/18—Processes or apparatus specially adapted for the manufacture or treatment of these devices or of parts thereof
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J2/00—Processes or devices for granulating materials, e.g. fertilisers in general; Rendering particulate materials free flowing in general, e.g. making them hydrophobic
    • B01J2/006—Coating of the granules without description of the process or the device by which the granules are obtained
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B82—NANOTECHNOLOGY
    • B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
    • B82Y30/00—Nanotechnology for materials or surface science, e.g. nanocomposites
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B19/00—Selenium; Tellurium; Compounds thereof
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G19/00—Compounds of tin
    • C01G19/006—Compounds containing, besides tin, two or more other elements, with the exception of oxygen or hydrogen
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/02—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition
    • C23C18/04—Pretreatment of the material to be coated
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/02—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition
    • C23C18/12—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition characterised by the deposition of inorganic material other than metallic material
    • C23C18/1204—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition characterised by the deposition of inorganic material other than metallic material inorganic material, e.g. non-oxide and non-metallic such as sulfides, nitrides based compounds
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/02—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition
    • C23C18/12—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition characterised by the deposition of inorganic material other than metallic material
    • C23C18/125—Process of deposition of the inorganic material
    • C23C18/1279—Process of deposition of the inorganic material performed under reactive atmosphere, e.g. oxidising or reducing atmospheres
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/02104—Forming layers
    • H01L21/02365—Forming inorganic semiconducting materials on a substrate
    • H01L21/02518—Deposited layers
    • H01L21/02521—Materials
    • H01L21/02551—Group 12/16 materials
    • H01L21/02557—Sulfides
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/02104—Forming layers
    • H01L21/02365—Forming inorganic semiconducting materials on a substrate
    • H01L21/02518—Deposited layers
    • H01L21/02521—Materials
    • H01L21/02551—Group 12/16 materials
    • H01L21/0256—Selenides
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/02104—Forming layers
    • H01L21/02365—Forming inorganic semiconducting materials on a substrate
    • H01L21/02518—Deposited layers
    • H01L21/02521—Materials
    • H01L21/02568—Chalcogenide semiconducting materials not being oxides, e.g. ternary compounds
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/02104—Forming layers
    • H01L21/02365—Forming inorganic semiconducting materials on a substrate
    • H01L21/02612—Formation types
    • H01L21/02614—Transformation of metal, e.g. oxidation, nitridation
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/02104—Forming layers
    • H01L21/02365—Forming inorganic semiconducting materials on a substrate
    • H01L21/02612—Formation types
    • H01L21/02617—Deposition types
    • H01L21/02623—Liquid deposition
    • H01L21/02628—Liquid deposition using solutions
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L31/00—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof
    • H01L31/0248—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof characterised by their semiconductor bodies
    • H01L31/0256—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof characterised by their semiconductor bodies characterised by the material
    • H01L31/0264—Inorganic materials
    • H01L31/032—Inorganic materials including, apart from doping materials or other impurities, only compounds not provided for in groups H01L31/0272 - H01L31/0312
    • H01L31/0324—Inorganic materials including, apart from doping materials or other impurities, only compounds not provided for in groups H01L31/0272 - H01L31/0312 comprising only AIVBVI or AIIBIVCVI chalcogenide compounds, e.g. Pb Sn Te
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
    • H01L31/00—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof
    • H01L31/04—Semiconductor devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation and specially adapted either for the conversion of the energy of such radiation into electrical energy or for the control of electrical energy by such radiation; Processes or apparatus specially adapted for the manufacture or treatment thereof or of parts thereof; Details thereof adapted as photovoltaic [PV] conversion devices
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2002/00—Crystal-structural characteristics
    • C01P2002/70—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data
    • C01P2002/72—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data by d-values or two theta-values, e.g. as X-ray diagram
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/01—Particle morphology depicted by an image
    • C01P2004/04—Particle morphology depicted by an image obtained by TEM, STEM, STM or AFM
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/60—Particles characterised by their size
    • C01P2004/62—Submicrometer sized, i.e. from 0.1-1 micrometer
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/60—Particles characterised by their size
    • C01P2004/64—Nanometer sized, i.e. from 1-100 nanometer
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E10/00—Energy generation through renewable energy sources
    • Y02E10/50—Photovoltaic [PV] energy

Definitions

  • This invention relates to processes for preparing films of CZTS and its selenium analogues on a substrate. Such films are useful in the preparation of photovoltaic devices. This invention also relates to processes for preparing coated substrates and for making photovoltaic devices.
  • Crystalline multinary-metal chalcogenide compositions containing only non-toxic and abundant elements are of particular interest in developing environmentally sustainable processes and devices.
  • Copper tin sulfide (Cu 2 SnS 3 or “CTS”) and copper zinc tin sulfide (Cu 2 ZnSnS 4 or “CZTS”) are particularly useful examples of this class of materials, and are of interest due to their potential applications as small band-gap semiconductors, as nonlinear materials, and as suitable candidates for photovoltaic cell materials.
  • Thin-film photovoltaic cells typically use semiconductors such as CdTe or copper indium gallium sulfide/selenide (CIGS) as an energy absorber material. Due to toxicity of cadmium and the limited availability of indium, alternatives are sought. CZTS possesses a band gap energy of about 1.5 eV and a large absorption coefficient (approx. 10 4 cm ⁇ 1 ), making it a promising CIGS replacement.
  • CZTS thin-films are illustrative of the general challenges that must be surmounted in making films of crystalline multinary-metal chalcogenide compositions.
  • Current techniques to make CZTS thin films e.g., thermal evaporation, sputtering, hybrid sputtering, pulsed laser deposition and electron beam evaporation
  • Electrochemical deposition is an inexpensive process, but compositional non-uniformity and/or the presence of secondary phases prevents this method from generating high-quality CZTS thin-films.
  • CZTS thin-films can also be made by the spray pyrolysis of a solution containing metal salts, typically CuCl, ZnCl 2 , and SnCl 4 , using thiourea as the sulfur source. This method tends to yield films of poor morphology, density and grain size. Photochemical deposition has also been shown to generate p-type CZTS thin films. However, the composition of the product is not well-controlled, and it is difficult to avoid the formation of impurities such as hydroxides. The synthesis of CZTS nanoparticles, which incorporate high-boiling amines as capping agents, has also been disclosed. The presence of capping agents in the nanoparticle layer may contaminate and lower the density of the annealed CZTS film.
  • metal salts typically CuCl, ZnCl 2 , and SnCl 4
  • One aspect of this invention is a process comprising:
  • a copper source selected from the group consisting of copper complexes of nitrogen-, oxygen-, carbon-, sulfur-, and selenium-based organic ligands, copper sulfides, copper selenides, and mixtures thereof;
  • a tin source selected from the group consisting of tin complexes of nitrogen-, oxygen-, carbon-, sulfur-, and selenium-based organic ligands, tin hydrides, tin sulfides, tin selenides, and mixtures thereof;
  • a zinc source selected from the group consisting of zinc complexes of nitrogen-, oxygen-, carbon-, sulfur-, and selenium-based organic ligands, zinc sulfides, zinc selenides, and mixtures thereof;
  • a chalcogen compound selected from the group consisting of: elemental S, elemental Se, CS 2 , CSe 2 , CSSe, R 1 S—Z, R 1 Se—Z, R 1 S—SR 1 , R 1 Se—SeR 1 , R 2 C(S)S—Z, R 2 C(Se)Se—Z, R 2 C(S)S—SC(S)R 2 , R 2 C(Se)Se—SeC(Se)R 2 , R 1 C(O)S—Z, and mixtures thereof, with each Z independently selected from the group consisting of: H, NR 4 4 , and SiR 5 3 ; wherein each R 1 and R 5 is independently selected from the group consisting of: hydrocarbyl and O-, N-, S-, halogen- and tri(hydrocarbyl)silyl-substituted hydrocarbyl; each R 2 is independently selected from the group consisting of hydrocarbyl, O-, N
  • At least one of the chalcogen compound and the tin source is a liquid at room temperature; and if the copper source is selected from copper sulfide and copper selenide, and the tin source is selected from tin sulfide and tin selenide, then the solvent is not hydrazine.
  • Another aspect of this invention is a photovoltaic device.
  • the terms “solar cell” and “photovoltaic cell” are synonymous unless specifically defined otherwise. These terms refer to devices that use semiconductors to convert visible and near-visible light energy into usable electrical energy.
  • band gap energy refers to the energy required to generate electron-hole pairs in a semiconductor material, which in general is the minimum energy needed to excite an electron from the valence band to the conduction band.
  • chalcogen refers to Group VIA elements
  • metal chalcogenides or “chalcogenides” refer to materials that comprise metals and Group VIA elements. Suitable Group VIA elements include sulfur, selenium and tellurium. Metal chalcogenides are important candidate materials for photovoltaic applications, since many of these compounds have optical band gap values well within the terrestrial solar spectra.
  • binary-metal chalcogenide refers to a chalcogenide composition comprising one metal.
  • ternary-metal chalcogenide refers to a chalcogenide composition comprising two metals.
  • quaternary-metal chalcogenide refers to a chalcogenide composition comprising three metals.
  • multinary-metal chalcogenide refers to a chalcogenide composition comprising two or more metals and encompasses ternary and quaternary metal chalcogenide compositions.
  • the terms “copper tin sulfide” and “CTS” refer to Cu 2 SnS 3 ; “copper tin selenide” and “CTSe” refer to Cu 2 SnSe 3 ; and “copper tin sulfide/selenide” and “CTS-Se” encompass all possible combinations of Cu 2 Sn(S,Se) 3 , including Cu 2 SnS 3 , Cu 2 SnSe 3 , and Cu 2 SnS x Se 3-x , where 0 ⁇ x ⁇ 3.
  • copper tin sulfide “copper tin selenide”, “copper tin sulfide/selenide”, “CTS”, “CTSe” and “CTS-Se” further encompass fractional stoichiometries, e.g., Cu 1.80 Sn 1.05 S 3 . That is, the stoichiometry of the elements can vary from a strictly 2:1:3 molar ratio.
  • copper zinc tin sulfide and “CZTS” refer to Cu 2 ZnSnS 4 ; copper zinc tin selenide and “CZTSe” refer to Cu 2 ZnSnSe 4 ; and copper zinc tin sulfide/selenide and “CZTS-Se” encompass all possible combinations of Cu 2 ZnSn(S,Se) 4 , including Cu 2 ZnSnS 4 , Cu 2 ZnSnSe 4 , and Cu 2 ZnSnS x Se 4-x , where 0 ⁇ x ⁇ 4.
  • CZTS copper zinc tin sulfide/selenide semiconductors with fractional stoichiometries, e.g., Cu 1.94 Zn 0.63 Sn 1.3 S 4 . That is, the stoichiometry of the elements can vary from a strictly 2:1:1:4 molar ratio. Materials designated as CTS-Se and CZTS-Se may also contain small amounts of other elements such as sodium. To date, the highest efficiencies have been measured for copper-poor CZTS-Se solar cells, where by “copper-poor” it is understood that the ratio Cu/(Zn+Sn) is less than 1.0. For high efficiency devices, a molar ratio of zinc to tin is greater than one is also desirable.
  • kesterite is commonly used to refer to materials belonging to the kesterite family of minerals and is also the common name of the mineral CZTS.
  • the term “kesterite” refers to crystalline compounds in either the I4- or I4-2m space groups having the nominal formula Cu 2 ZnSn(S—Se) 4 , and also “atypical kesterites” wherein zinc has replaced a fraction of the copper or copper has replaced a fraction of the zinc to give Cu c Zn z Sn(S—Se) 4 wherein c is greater than two and z is less than one; or c is less than two and z is greater than one.
  • the term “kesterite structure” refers to the structure of these compounds.
  • X-ray absorption spectroscopy reveals spectral features unique to the kesterite form and allows for determination of the ratio of Cu to Zn in the kesterite phase. This allows for the identification of atypical kesterite compositions, which are clearly distinguished from a mixture of separate sulfide phases producing the same elemental ratios in aggregate. Control of stoichiometry in this phase allows for control of electronic properties for improved performance in a photovoltaic device.
  • coherent domain size refers to the size of crystalline domains over which a defect-free, coherent structure may exist. The coherency comes from the fact that the three-dimensional ordering is not broken inside of these domains.
  • metal salts refers to compositions wherein metal cations and inorganic anions are joined by ionic bonding.
  • Relevant classes of inorganic anions comprise oxides, sulfides, carbonates, sulfates and halides.
  • metal complexes refers to compositions wherein a metal is bonded to a surrounding array of molecules or anions, typically called “ligands” or “complexing agents”.
  • ligands typically called “complexing agents”.
  • the atom within a ligand that is directly bonded to the metal atom or ion is called the “donor atom” and, herein, often comprises nitrogen, oxygen, selenium, or sulfur.
  • ligands are classified according to the “Covalent Bond Classification (CBC) Method” (Green, M. L. H. J. Organomet. Chem. 1995, 500, 127-148).
  • An “X-function ligand” is one which interacts with a metal center via a normal 2-electron covalent bond, composed of 1 electron from the metal and 1 electron from the X ligand.
  • Simple examples of X-type ligands include alkyls and thiolates.
  • nitrogen-, oxygen-, carbon-, sulfur-, and selenium-based organic ligands refers specifically to carbon-containing X-function ligands, wherein the donor atom comprises nitrogen, oxygen, carbon, sulfur, or selenium.
  • complexes of nitrogen-, oxygen-, carbon-, sulfur-, and selenium-based organic ligands refers to the metal complexes comprising these ligands.
  • hydrocarbyl group is a univalent group containing only carbon and hydrogen.
  • hydrocarbyl groups include unsubstituted alkyls, cycloalkyls, and aryl groups, including alkyl-substituted aryl groups.
  • Suitable hydrocarbyl groups and alkyl groups contain 1 to about 30 carbons, or 1 to 25, 1 to 20, 1 to 15, 1 to 10, 1 to 5, 1 to 4, or 1 to 2 carbons.
  • heteroatom-substituted hydrocarbyl is meant a hydrocarbyl group that contains one or more heteroatoms wherein the free valence is located on carbon, not on the heteroatom.
  • Examples include hydroxyethyl and carbomethoxyethyl.
  • Suitable heteroatom substituents include O-, N-, S-, halogen, and tri(hydrocarbyl)silyl.
  • all of the hydrogens may be substituted, as in trifluoromethyl.
  • tri(hydrocarbyl)silyl encompasses silyl substituents, wherein the substituents on silicon are hydrocarbyls.
  • O-, N-, S-, and Se-based functional groups univalent groups other than hydrocarbyl and substituted hydrocarbyl that comprise O-, N-, S-, or Se-heteroatoms, wherein the free valence is located on this heteroatom.
  • O-, N-, S-, and Se-based functional groups include alkoxides, amidos, thiolates, and selenolates.
  • One aspect of this invention is a process comprising:
  • a copper source selected from the group consisting of copper complexes of nitrogen-, oxygen-, carbon-, sulfur-, and selenium-based organic ligands, copper sulfides, copper selenides, and mixtures thereof;
  • a tin source selected from the group consisting of tin complexes of nitrogen-, oxygen-, carbon-, sulfur-, and selenium-based organic ligands, tin hydrides, tin sulfides, tin selenides, and mixtures thereof;
  • a zinc source selected from the group consisting of zinc complexes of nitrogen-, oxygen-, carbon-, sulfur-, and selenium-based organic ligands, zinc sulfides, zinc selenides, and mixtures thereof;
  • a chalcogen compound selected from the group consisting of: elemental S, elemental Se, CS 2 , CSe 2 , CSSe, R 1 S—Z, R 1 Se—Z, R 1 S—SR 1 , R 1 Se—SeR 1 , R 2 C(S)S—Z, R 2 C(Se)Se—Z, R 2 C(Se)S—Z, R 1 C(O)S—Z, R 1 C(O)Se—Z, and mixtures thereof, with each Z independently selected from the group consisting of: H, NR 4 4 , and SiR 5 3 ; wherein each R 1 and R 5 is independently selected from the group consisting of: hydrocarbyl and O-, N-, S-, halogen- and tri(hydrocarbyl)silyl-substituted hydrocarbyl; each R 2 is independently selected from the group consisting of hydrocarbyl, O-, N-, S-, Se-, halogen- and tri(
  • At least one of the chalcogen compound and the tin source is a liquid at room temperature; and if the copper source is selected from copper sulfide and copper selenide, and the tin source is selected from tin sulfide and tin selenide, then the solvent is not hydrazine.
  • the ratio of the total number of moles of the chalcogen compound, the sulfur- and selenium-based organic ligands, and the copper-, tin-, and zinc-sulfides and selenides to the total number of moles of the copper, tin and zinc complexes is at least about 1.
  • a chalcogen compound is present.
  • a zinc source is present.
  • elemental sulfur, elemental selenium, or a mixture of elemental sulfur and selenium is present, and the molar ratio of (S+Se) is about 0.2 to about 5, or about 0.5 to about 2.5, relative to the tin source.
  • the nitrogen-, oxygen-, carbon-, sulfur-, and selenium-based organic ligands are selected from the group consisting of: amidos; alkoxides; acetylacetonates; carboxylates; hydrocarbyls; O-, N-, S-, halogen- and tri(hydrocarbyl)silyl-substituted hydrocarbyls; thio- and selenolates; thio-, seleno-, and dithiocarboxylates; dithio-, diseleno-, and thioselenocarbamates; and dithioxanthogenates.
  • Suitable amidos include: bis(trimethylsilyl)amino, dimethylamino, diethylamino, diisopropylamino, N-methyl-t-butylamino, 2-(dimethylamino)-N-methylethylamino, N-methylcyclohexylamino, dicyclohexylamino, N-ethyl-2-methylallylamino, bis(2-methoxyethyl)amino, 2-methylaminomethyl-1,3-dioxolane, pyrrolidino, t-butyl-1-piperazinocarboxylate, N-methylanilino, N-phenylbenzylamino, N-ethyl-o-toluidino, bis(2,2,2-trifluoromethyl)amino, N-t-butyltrimethylsilylamino, and mixtures thereof.
  • Some ligands may chelate the metal center, and, in some cases, comprise more than one type of donor atom, e.g., the dianion of N-benzyl-2-aminoethanol is a suitable ligand comprising both amino and alkoxide groups.
  • Suitable alkoxides include: methoxide, ethoxide, n-propoxide, i-propoxide, n-butoxide, t-butoxide, neopentoxide, ethylene glycol dialkoxide, 1-methylcyclopentoxide, 2-fluoroethoxide, 2,2,2,-trifluoroethoxide, 2-ethoxyethoxide, 2-methoxyethoxide, 3-methoxy-1-butoxide, methoxyethoxyethoxide, 3,3-diethoxy-1-propoxide, 2-dimethylaminoethoxide, 2-diethylaminoethoxide, 3-dimethylamino-1-propoxide, 3-diethylamino-1-propoxide, 1-dimethylamino-2-propoxide, 1-diethylamino-2-propoxide, 2-(1-pyrrolidinyl)ethoxide, 1-ethyl-3-pyrrolidinoxide, 3-ace
  • acetylacetonate refers to the anion of 1,3-dicarbonyl compounds, A 1 C(O)CH(A 2 )C(O)A 1 , wherein each A 1 is independently selected from hydrocarbyl, substituted hydrocarbyl, and O-, S-, and N-based functional groups and each A 2 is independently selected from hydrocarbyl, substituted hydrocarbyl, halogen, and O-, S-, and N-based functional groups.
  • Suitable acetylacetonates include: 2,4-pentanedionate, 3-methyl-2-4-pentanedionate, 3-ethyl-2,4-pentanedionate, 3-chloro-2,4-pentanedionate, 1,1,1-trifluoro-2,4-pentanedionate, 1,1,1,5,5,5-hexafluoro-2,4-pentanedionate, 1,1,1,5,5,6,6,6,-octafluoro-2,4-hexanedionate, ethyl 4,4,4-trifluoroacetoacetate, 2-methoxyethylacetoacetate, methylacetoacetate, ethylacetoacetate, t-butylacetoacetate, 1-phenyl-1,3-butanedionate, 2,2,6,6-tetramethyl-3,5-heptanedionate, allyloxyethoxytrifluoroacetoacetate, 4,4,4-
  • Suitable carboxylates include: acetate, trifluoroacetate, propionate, butyrates, hexanoate, octanoate, decanoate, stearate, isobutyrate, t-butylacetate, heptafluorobutyrate, methoxyacetate, ethoxyacetate, methoxypropionate, 2-ethyl hexanoate, 2-(2-methoxyethoxy)acetate, 2-[2-(2-methoxyethoxy)ethoxy]acetate, (methylthio)acetate, tetrahydro-2-furoate, 4-acetyl butyrate, phenylacetate, 3-methoxyphenylacetate, (trimethylsilyl)acetate, 3-(trimethylsilyl)propionate, maleate, benzoate, acetylenedicarboxylate, and mixtures thereof.
  • Suitable hydrocarbyls include: methyl, ethyl, n-propyl, i-propyl, n-butyl, i-butyl, sec-butyl, t-butyl, n-pentyl, n-hexyl, n-heptyl, n-octyl, neopentyl, 3-methylbutyl, phenyl, benzyl, 4-t-butylbenzyl, 4-t-butylphenyl, p-tolyl, 2-methyl-2-phenylpropyl, 2-mesityl, 2-phenylethyl, 2-ethylhexyl, 2-methyl-2-phenylpropyl, 3,7-dimethyloctyl, allyl, vinyl, cyclopentyl, cyclohexyl, and mixtures thereof.
  • Suitable O-, N-, S-, halogen- and tri(hydrocarbyl)silyl-substituted hydrocarbyls include: 2-methoxyethyl, 2-ethoxyethyl, 4-methoxyphenyl, 2-methoxybenzyl, 3-methoxy-1-butyl, 1,3-dioxan-2-ylethyl, 3-trifluoromethoxyphenyl, 3,4-(methylenedioxy)phenyl, 2,4-dimethoxyphenyl, 2,5-dimethoxyphenyl, 3,4-dimethoxyphenyl, 2-methoxybenzyl, 3-methoxybenzyl, 4-methoxybenzyl, 3,5-dimethoxyphenyl, 3,5-dimethyl-4-methoxyphenyl, 3,4,5-trimethoxyphenyl, 4-methoxyphenethyl, 3,5-dimethoxybenzyl, 4-(2-tetrahydro-2H-pyranoxy)phenyl
  • Suitable thio- and selenolates include: 1-thioglycerol, phenylthio, ethylthio, methylthio, n-propylthio, i-propylthio, n-butylthio, i-butylthio, t-butylthio, n-pentylthio, n-hexylthio, n-heptylthio, n-octylthio, n-nonylthio, n-decylthio, n-dodecylthio, 2-methoxyethylthio, 2-ethoxyethylthio, 1,2-ethanedithiolate, 2-pyridinethiolate, 3,5-bis(trifluoromethyl)benzenethiolate, toluene-3,4-dithiolate, 1,2-benzenedithiolate, 2-dimethylaminoethanethiolate
  • Suitable thio-, seleno-, and dithiocarboxylates include: thioacetate, thiobenzoate, selenobenzoate, dithiobenzoate, and mixtures thereof.
  • Suitable dithio-, diseleno-, and thioselenocarbamates include: dimethyldithiocarbamate, diethyldithiocarbamate, dipropyldithiocarbamate, dibutyldithiocarbamate, bis(hydroxyethyl)dithiocarbamate, dibenzyldithiocarbamate, dimethyldiselenocarbamate, diethyldiselenocarbamate, dipropyldiselenocarbamate, dibutyldiselenocarbamate, dibenzyldiselenocarbamate, and mixtures thereof.
  • Suitable dithioxanthogenates include: methylxanthogenate, ethylxanthogenate, i-propylxanthogenate, and mixtures thereof.
  • suitable R 1 S— and R 1 Se— of R 1 S—Z and R 1 Se—Z are selected from the above list of suitable thio- and selenolates.
  • suitable R 1 S—SR 1 , R 1 Se—SeR 1 include: dimethyldisulfide, 2,2′-dipyridyldisulfide, di(2-thienyl)disulfide, bis(2-hydroxyethyl)disulfide, bis(2-methyl-3-furyl)disulfide, bis(6-hydroxy-2-naphthyl)disulfide, diethyldisulfide, methylpropyldisulfide, diallyldisulfide, dipropyldisulfide, isopropyldisulfide, dibutyldisulfide, sec-butyldisulfide, bis(4-methoxyphenyl)disulfide, dibenzyldisulfide, p-tolyldisulfide, phenylacetyldisulfide, tetramethylthiuram disulfide, t
  • suitable R 2 C(S)S—Z, R 2 C(Se)Se—Z, R 2 C(Se)S—Z, R 1 C(O)S—Z, and R 1 C(O)Se—Z are selected from the above lists of suitable thio-, seleno-, and dithiocarboxylates; suitable dithio-, diseleno-, and thioselenocarbamates; and suitable dithioxanthogenates.
  • Suitable NR 4 4 include: Et 2 NH 2 , Et 4 N, Et 3 NH, EtNH 3 , NH 4 , Me 2 NH 2 , Me 4 N, Me 3 NH, MeNH 3 , Pr 2 NH 2 , Pr 4 N, Pr 3 NH, PrNH 3 , Bu 3 NH, Me 2 PrNH, (i-Pr) 3 NH, and mixtures thereof.
  • Suitable SiR 5 3 include: SiMe 3 , SiEt 3 , SiPr 3 , SiBu 3 , Si(i-Pr) 3 , SiEtMe 2 , SiMe 2 (i-Pr), Si(t-Bu)Me 2 , Si(cyclohexyl)Me 2 , and mixtures thereof.
  • ligands and chalcogen compounds are commercially available or readily synthesized by the addition of an amine, alcohol, or alkyl nucleophile to CS 2 or CSe 2 or CSSe.
  • Components and by-products of the ink may be liquids at room temperature or at the heating temperature and coating temperature. In such cases, the ink need not comprise a solvent.
  • a chalcogen compound is present and is a liquid at room temperature.
  • the tin source is a liquid at room temperature.
  • a chalcogen compound is present and is a liquid at room temperature and the tin source is a liquid at room temperature.
  • a solvent is present and the boiling point of the solvent is greater than about 100° C. or 110° C. or 120° C. or 130° C. or 140° C. or 150° C. or 160° C. or 170° C. or 180° C. or 190° C. at atmospheric pressure. In some embodiments, the process is conducted at atmospheric pressure.
  • Suitable solvents include: aromatics, heteroaromatics, nitriles, amides, alcohols, pyrrolidinones, amines, and mixtures thereof.
  • Suitable heteroaromatics include pyridine and substituted pyridines.
  • Suitable amines include compounds of the form R 6 NH 2 , wherein each R 6 is independently selected from the group consisting of: O-, N-, S-, and Se-substituted hydrocarbyl.
  • the solvent comprises an amino-substituted pyridine.
  • the solvent comprises about 95 to about 5 wt %, or 90 to 10 wt %, or 80 to 20 wt %, or 70 to 30 wt %, or 60 to 40 wt %, based upon the total weight of the ink.
  • Suitable aromatic solvents include: benzene, toluene, ethylbenzene, chlorobenzene, o-xylene, m-xylene, p-xylene, mesitylene, i-propylbenzene, 1-chlorobenzene, 2-chlorotoluene, 3-chlorotoluene, 4-chlorotoluene, t-butylbenzene, n-butylbenzene, i-butylbenzene, s-butylbenzene, 1,2-dichlorobenzene, 1,3-dichlorobenzene, 1,4-dichlorobenzene, 1,3-diisopropylbenzene, 1,4-diisopropylbenzene, 1,2-difluorobenzene, 1,2,4-trichlorobenzene, 3-methylanisole, 3-chloroanisole, 3-phenoxytoluene, dipheny
  • Suitable heteroaromatic solvents include: pyridine, 2-picoline, 3-picoline, 3,5-lutidine, 4-t-butylpyridine, 2-aminopyridine, 3-aminopyridine, diethylnicotinamide, 3-cyanopyridine, 3-fluoropyridine, 3-chloropyridine, 2,3-dichloropyridine, 2,5-dichloropyridine, 5,6,7,8-tetrahydroisoquinoline, 6-chloro-2-picoline, 2-methoxypyridine, 3-(aminomethyl)pyridine, 2-amino-3-picoline, 2-amino-6-picoline, 2-amino-2-chloropyridine, 2,3-diaminopyridine, 3,4-diaminopyridine, 2-(methylamino)pyridine, 2-dimethylaminopyridine, 2-(aminomethyl)pyridine, 2-(2-aminoethyl)pyridine, 2-methoxypyridine, 2-butoxy
  • Suitable nitrile solvents include: acetonitrile, 3-ethoxypropionitrile, 2,2-diethoxypropionitrile, 3,3-diethoxypropionitrile, diethoxyacetonitrile, 3,3-dimethoxypropionitrile, 3-cyanopropionaldehyde dimethylacetal, dimethylcyanamide, diethylcyanamide, diisopropylcyanamide, 1-pyrrolidinecarbonitrile, 1-piperidinecarbonitrile, 4-morpholinecarbonitrile, methylaminoacetonitrile, butylaminoacetonitrile, dimethylaminoacetonitrile, diethylaminoacetonitrile, N-methyl-beta-alaninenitrile, 3,3′-iminopropionitrile, 3-(dimethylamino)propionitrile, 1-piperidinepropionitrile, 1-pyrrolidinebutyronitrile, propionitrile, butyronitrile, valeronitrile, isovaleronit
  • Suitable amide solvents include: N,N-diethylnicotinamide, N-methylnicotinamide, N,N-dimethylformamide, N,N-diethylformamide, N,N-diisopropylformamide, N,N-dibutylformamide, N,N-dimethylacetamide, N,N-diethylacetamide, N,N-diisopropylacetamide, N,N-dimethylpropionamide, N,N-diethylpropionamide, N,N,2-trimethylpropionamide, acetamide, propionamide, isobutyramide, trimethylacetamide, nipecotamide, N,N-diethylnipecotamide, and mixtures thereof.
  • Suitable alcohol solvents include: methoxyethoxyethanol, methanol, ethanol, isopropanol, 1-butanol, 2-pentanol, 2-hexanol, 2-octanol, 2-nonanol, 2-decanol, 2-dodecanol, ethylene glycol, 1,3-propanediol, 2,3-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,7-heptanediol, 1,8-octanediol, cyclopentanol, cyclohexanol, cyclopentanemethanol, 3-cyclopentyl-1-propanol, 1-methylcyclopentanol, 3-methylcyclopentanol, 1,3-cyclopentanediol, 2-cyclohexylethanol, 1-cyclohexylethanol, 2,3-dimethylcyclohexanol,
  • Suitable pyrrolidinone solvents include: N-methyl-2-pyrrolidinone, 5-methyl-2-pyrrolidinone, 3-methyl-2-pyrrolidinone, 2-pyrrolidinone, 1,5-dimethyl-2-pyrrolidinone, 1-ethyl-2-pyrrolidinone, 1-(2-hydroxyethyl)-2-pyrrolidinone, 5-methoxy-2-pyrrolidinone, 1-(3-aminopropyl)-2-pyrrolidinone, and mixtures thereof.
  • Suitable amine solvents include: butylamine, hexylamine, octylamine, 3-methoxypropylamine, 2-methylbutylamine, isoamylamine, 1,2-dimethylpropylamine, hydrazine, ethylenediamine, 1,3-diaminopropane, 1,2-diaminopropane, 1,2-diamino-2-methylpropane, 1,3-diaminopentane, 1,1-dimethylhydrazine, N-ethylmethylamine, diethylamine, N-methylpropylamine, diisopropylamine, dibutylamine, triethylamine, N-methylethylenediamine, N-ethylethylenediamine, N-propylethylenediamine, N-isopropylethylenediamine, N,N′-dimethylethylenediamine, N,N-dimethylethylenediamine, N,N′-diethylethylened
  • the ink comprises up to about 10 wt % or 7.5 wt % or 5 wt % or 2.5 wt % or 1 wt % of one or more additives selected from the group consisting of: dispersants, surfactants, polymers, binders, ligands, capping agents, defoamers, thickening agents, corrosion inhibitors, plasticizers, and dopants.
  • Suitable dopants include sodium and alkali-containing compounds selected from the group consisting of: alkali compounds comprising nitrogen-, oxygen-, carbon-, sulfur-, or selenium-based organic ligands, alkali sulfides, alkali selenides, and mixtures thereof.
  • the dopant comprises an alkali-containing compound selected from the group consisting of: alkali-compounds comprising amidos; alkoxides; acetylacetonates; carboxylates; hydrocarbyls; O-, N-, S-, halogen-, and tri(hydrocarbyl)silyl-substituted hydrocarbyls; thio- and selenolates; thio-, seleno-, and dithiocarboxylates; dithio-, diseleno-, and thioselenocarbamates; and dithioxanthogenates.
  • alkali-containing compound selected from the group consisting of: alkali-compounds comprising amidos; alkoxides; acetylacetonates; carboxylates; hydrocarbyls; O-, N-, S-, halogen-, and tri(hydrocarbyl)silyl-substituted hydrocarbyls; thi
  • the ink comprises one or more binders or surfactants selected from the group consisting of: decomposable binders; decomposable surfactants; cleavable surfactants; surfactants with a boiling point less than about 250° C.; and mixtures thereof.
  • Suitable decomposable binders include: homo- and co-polymers of polyethers; homo- and co-polymers of polylactides; homo- and co-polymers of polycarbonates; homo- and co-polymers of poly[3-hydroxybutyric acid]; homo- and co-polymers of polymethacrylates; and mixtures thereof.
  • the molar ratio of copper to tin is about 2:1 in the ink. In other embodiments, zinc is present in the ink and the molar ratio of copper to zinc to tin is about 2:1:1 in the ink.
  • Preparing the ink typically comprises mixing the components (i)-(v) by any conventional method. If one or more of the copper-, tin-, zinc-, or chalcogen sources is a liquid at room temperature or at the processing temperatures, the use of a separate solvent is optional. Otherwise, a solvent is used.
  • the ink is a solution; in other embodiments, the ink is a suspension or dispersion.
  • the preparation is conducted under an inert atmosphere, taking precautions to protect the reaction mixtures from air and light.
  • the ink is prepared at low temperatures, e.g., when low boiling point and/or highly reactive reagents such as CS 2 and ZnEt 2 are utilized. In such cases, the ink is typically stirred for 48 hours or longer at room temperature prior to heat processing. In some embodiments, the ink is prepared at about 20-100° C., e.g., when the reagents are solids or have high boiling points and/or when one or more of the solvents is a solid at room temperature, e.g., 2-aminopyridine or 3-aminopyridine. In some embodiments, all of the ink components are added together at room temperature.
  • elemental chalcogen is added last, following the mixing of all the other components for about half an hour at room temperature.
  • the components are added consecutively.
  • all of the reagents except copper can be mixed and heated at about 100° C. prior to addition of the copper source, or all of the reagents except tin can be mixed and heated at about 100° C. prior to the addition of the tin source.
  • each ink comprising a complete set of reagents, e.g., each ink comprises at least a zinc source, a copper source, and a tin source for inks useful for forming CZTS-Se.
  • the two or more inks can then be combined following mixing or following heat-processing. This method is especially useful for controlling stoichiometry and obtaining CTS-Se or CZTS-Se of high purity, as prior to mixing, separate films from each ink can be coated, annealed, and analyzed by XRD. The XRD results can guide the selection of the type and amount of each ink to be combined.
  • an ink yielding an annealed film of CZTS-Se with traces of copper sulfide and zinc sulfide can be combined with an ink yielding an annealed film of CZTS-Se with traces of tin sulfide, to form an ink that yields an annealed film comprising only CZTS-Se, as determined by XRD.
  • the ink has been heat-processed at a temperature of greater than about 100° C. or 110° C. or 120° C. or 130° C. or 140° C. or 150 C.° or 160° C. or 170° C. or 180° C. or 190° C. before coating on the substrate.
  • Suitable heating methods include conventional heating and microwave heating.
  • this heat-processing step aids the formation of CZTS-Se, with XAS analysis of films formed from heat-processed inks indicating the presence of kesterite upon heating the films at heating temperatures as low as 120° C.
  • This optional heat-processing step is typically carried out under an inert atmosphere.
  • the ink produced at this stage can be stored for extended periods (e.g., a couple of months) without any noticeable decrease in efficacy.
  • the substrate can be rigid or flexible.
  • the substrate comprises in layered sequence: (i) a base film; and (ii) optionally, an electrically conductive coating.
  • the base film is selected from the group consisting of: glass, metals, and polymeric films.
  • Suitable electrically conductive coatings include: metal conductors, transparent conducting oxides, and organic conductors.
  • a sodium compound e.g., NaF, Na 2 S, or Na 2 Se.
  • the substrate comprises material selected from the group consisting of metal foils, plastics, polymers, metalized plastics, glass, solar glass, low-iron glass, green glass, soda-lime glass, steel, stainless steel, aluminum, ceramics, metal plates, metalized ceramic plates, and metalized polymer plates.
  • the ink is disposed on a substrate to provide a coated substrate by any of a variety of solution-based coating and printing techniques, including spin-coating, spray-coating, dip-coating, rod-coating, drop-cast coating, roller coating, slot-die coating, draw-down coating, ink-jet printing, contact printing, gravure printing, flexographic printing, and screen printing.
  • the coating can be dried by evaporation, by applying vacuum, by heating, or by combinations thereof.
  • the substrate and disposed ink are heated at a temperature from 80-350° C., or 100-300° C., or 120-250° C., or 150-190° C.
  • the drying step can be a separate, distinct step, or can occur as the substrate and precursor ink are heated in an annealing step.
  • CZTS-Se is formed during this heating step, with XAS analysis indicating the presence of kesterite.
  • heated layers comprising CTS-Se or CZTS-Se are formed at heating temperatures as low as 120° C.
  • the heated layers comprise CZTS-Se wherein the Cu/Zn ratio of kesterite is approximately 2/1, falling in the range of about 1.6 ⁇ Cu/Zn ⁇ 3.1. In some embodiments, the heated layers comprise CZTS-Se wherein the Cu/Zn ratio of the kesterite is greater than about 3.1.
  • the heated layers comprise CZTS-Se wherein the Cu/Zn ratio of the kesterite is less than about 1.6. In yet other embodiments, the heated layers comprise CZTS-Se wherein the coherent domain size of the kesterite is 2-30 nm.
  • the coated substrate comprises one or more copper compounds selected from the group consisting of binary copper chalcogenides, binary copper oxides, and CTS-Se, and one or more tin compounds selected from the group consisting of binary tin chalcogenides, binary tin oxides, and CTS-Se, wherein the chalcogenides comprise sulfides, selenides or mixtures thereof.
  • the molar ratio of copper to tin in the coated substrate is about 2:1.
  • the coated substrate further comprises one or more zinc compounds selected from the group consisting of binary zinc chalcogenides, ZnO, and CZTS-Se, wherein the chalcogenides comprise sulfides, selenides or mixtures thereof.
  • the molar ratio of copper to zinc to tin is about 2:1:1. In other embodiments, the molar ratio of copper to (zinc plus tin) is less than one, and the molar ratio of zinc to tin is greater than one.
  • the process further comprises an annealing step in which the coated substrate is heated at about 350-800° C., or 400-650° C., or 450-600° C., or 450-525° C.
  • the annealing comprises one or more of thermal processing, rapid thermal processing (RTP), rapid thermal annealing (RTA), pulsed thermal processing (PTP), laser beam exposure, heating via IR lamps, electron beam exposure, pulsed electron beam processing, and heating via microwave irradiation.
  • RTP refers to a technology that can be used in place of standard furnaces and involves single wafer processing, fast heating and cooling rates, thermal nonequilibrium and controlled ambient.
  • RTA is a subset of RTP, which consists of unique heat treatments for different effects, including activation of dopants, changing substrate interfaces, densifying and changing states of films, repairing damage, and moving dopants.
  • Rapid thermal anneals are performed using either lamp-based heating, a hot chuck, or a hot plate.
  • PTP involves thermally annealing structures at extremely high power densities for periods of very short duration, resulting, for example, in defect reduction.
  • pulsed electron beam processing uses pulsed high energy electron beam with short pulse duration. Pulsed processing is useful for processing thin films on temperature-sensitive substrates. The duration of the pulse is so short that little energy is transferred to the substrate, leaving the substrate undamaged.
  • the annealing step can be carried out under an inert atmosphere, provided that the ratio of the total number of moles of the chalcogen compound, the sulfur- and selenium-based organic ligands, and the copper-, tin- and zinc-sulfides and selenides to the total number of moles of the copper, tin and zinc complexes is at least about 1.
  • the annealing step is carried out in an atmosphere comprising an inert gas and reactive component selected from the group consisting of: selenium vapor, sulfur vapor, hydrogen, hydrogen sulfide, hydrogen selenide, and mixtures thereof.
  • At least a portion of the chalcogen can be exchanged (e.g., S can be replaced by Se) by conducting the annealing step in the presence of selenium vapor or hydrogen selenide.
  • annealings are conducted under a combination of atmospheres, e.g., a first annealing is carried out under an inert atmosphere and a second annealing is carried out in an atmosphere comprising an inert gas and a reactive component as described above.
  • CTS-Se and/or CZTS-Se can be formed in high yield during the annealing step, as determined by XRD or XAS.
  • annealed films consist essentially of CTS-Se or CZTS-Se, according to XRD analysis.
  • the coherent domain size of the CTS-Se or CZTS-Se is greater than about 30 nm, or greater than 40, 50, 60, 70, 80, 90 or 100 nm, as determined by XRD.
  • the molar ratio of copper to tin is about 2:1 in the annealed film.
  • the molar ratio of copper to zinc to tin is about 2:1:1 in the annealed film. In other embodiments, the molar ratio of copper to (zinc plus tin) is less than one, and a molar ratio of zinc to tin is greater than one in the annealed film comprising CZTS-Se.
  • films of varying thickness can be coated in a single-coating step.
  • the coating thickness can also be increased by repeating the coating and drying steps.
  • the annealed film typically has an increased density and/or reduced thickness versus that of the wet precursor layer.
  • the film thicknesses of the dried and annealed coatings are 0.1-200 microns, or 0.1-100 microns, or 0.1-50 microns, or 0.1-25 microns, or 0.1-10 microns, or 0.5-5 microns.
  • the coating thickness can be increased by repeating the coating and drying steps. These multiple coatings can be conducted with the same ink formulation or with different ink formulations. As described above, wherein two or more inks were mixed, the coating of multiple layers with different inks can be used to fine-tune stoichiometry and purity of the CTS-Se and CZTS-Se films by fine tuning Cu to Sn and Cu to Zn to Sn ratios.
  • the coated substrate can be dried and then a second coating can be applied and coated by spin-coating.
  • the spin-coating step can wash organics out of the first coating.
  • the coated film can be soaked in a solvent and then the solvent removed by spin-coating.
  • Suitable solvents for washing include hydrocarbyls.
  • binary sulfides and other impurities can be removed by etching using techniques known in the art, such as those used for CIGS films.
  • One aspect of this invention provides a process for manufacturing thin-film photovoltaic cells comprising CZTS-Se.
  • a typical photovoltaic cell includes a substrate, a back contact layer (e.g., molybdenum), an absorber layer (also referred to as the first semiconductor layer), a buffer layer (also referred to as the second semiconductor layer), and a top contact layer.
  • the photovoltaic cell can also include an electrical contact of electrode pad on the top contact layer, and an anti-reflective (AR) coating on the front (light-facing) surface of the substrate to enhance the transmission of light into the semiconductor layer.
  • AR anti-reflective
  • the process provides a electronic device and comprises depositing one or more layers in layered sequence onto the annealed coating of the substrate.
  • the layers can be selected from the group consisting of: conductors, semiconductors, and dielectrics.
  • the process provides a photovoltaic device and comprises depositing the following layers in layered sequence onto the annealed coating of the substrate having an electrically conductive layer present: (i) a buffer layer; (ii) a transparent top contact layer, and (iii) optionally, an antireflective layer.
  • the process provides a photovoltaic device and comprises disposing one or more layers selected from the group consisting of buffer layers, top contact layers, electrode pads, and antireflective layers onto the annealed CZTS-Se film.
  • layers selected from the group consisting of buffer layers, top contact layers, electrode pads, and antireflective layers onto the annealed CZTS-Se film.
  • construction and materials for these layers are analogous to those of a CIGS photovoltaic cell.
  • Suitable substrate materials for the photovoltaic cell substrate are as described above and below.
  • the photovoltaic cell substrate can also comprise an interfacial layer to promote adhesion between the substrate material and metal layer.
  • Suitable interfacial layers can comprise metals (e.g., V, W, Cr), glass, or compounds of nitrides, oxides, and/or carbides.
  • interfacial layers are derived from adhesion promoters.
  • Suitable adhesion promoters comprise siloxy-substituted sulfur compounds, including thiols, sulfides, disulfides, tetrasulfides, and polysulfides.
  • adhesion promoters are selected from the group consisting of: bis[m-(2-triethoxysilylethyl)tolyl]polysulfide, bis[3-triethoxysilyl]propyl]disulfide, bis[3-triethoxysilyl]propyl]tetrasulfide, and 2,2-dimethoxy-1-thia-2-silacyclopentane.
  • Typical photovoltaic cell substrates are glass or plastic, coated on one side with a conductive material, e.g., a metal.
  • the substrate is molybdenum-coated glass.
  • Useful analytical techniques for characterizing the composition of the CTS-Se and CZTS-Se layers of the present invention include XRD (X-Ray Diffraction) and XAS.
  • SLG slides were treated with 3-(mercaptopropyl)-trimethoxysilane. ⁇ 100 mL of 3-(mercaptopropyl)-trimethoxysilane and ⁇ 1 mL of 2-(2-methoxyethoxy)acetic acid were mixed in a glass bottle in the drybox. SLG slides and Mo-patterned SLG slides were soaked in this solution for more than 24 hr. Next, the slides were soaked in methylene chloride for ⁇ 0.5 hr, rinsed with MeOH, and then dried with a wipe.
  • Annealing of Coated Substrates in a Tube Furnace were carried out either under a nitrogen, nitrogen/sulfur, or nitrogen/selenium atmosphere.
  • Annealings under a nitrogen atmosphere were carried out in either a single-zone Lindberg/Blue (Ashville, N.C.) tube furnace equipped with an external temperature controller and a one-inch quartz tube, or in a Lindberg/Blue three-zone tube furnace (Model STF55346C) equipped with a three-inch quartz tube.
  • a gas inlet and outlet were located at opposite ends of the tube, and the tube was purged with nitrogen while heating and cooling.
  • the coated substrates were placed on quartz plates inside of the tube.
  • Annealings under a nitrogen/sulfur atmosphere were carried out in the single-zone furnace in the one-inch tube.
  • a 3-inch long ceramic boat was loaded with 2.5 g of elemental sulfur and placed near the nitrogen inlet, outside of the direct heating zone.
  • the coated substrates were placed on quartz plates inside the tube.
  • annealings were carried out under a nitrogen/sulfur atmosphere, unless noted otherwise.
  • Rapid Thermal Annealing A MILA-5000 Infrared Lamp Heating System by ULVAC-RICO Inc. (Methuen, Mass.) was used for heating and the system was cooled using a Polyscience (Niles, Ill.) recirculating bath held at 15° C. Samples were heated under nitrogen purge as follows: 20° C. for 10 min; ramp to 400° C. in 1 min; hold at 400° C. for 2 min; cool to 20° C. during ⁇ 30 min.
  • Substrates for photovoltaic devices were prepared by coating a SLG substrate with a 500 nm layer of patterned molybdenum using a Denton Sputtering System. Deposition conditions were: 150 watts of DC Power, 20 sccm Ar, and 5 mT pressure. Cadmium Sulfide Deposition. 12.5 mg CdSO 4 (anhydrous) was dissolved in a mixture of nanopure water (34.95 mL) and 28% NH 4 OH (4.05 mL). Then a 1 mL aqueous solution of 22.8 mg thiourea was added rapidly to form the bath solution.
  • the bath solution was poured into a double-walled beaker (with 70° C. water circulating between the walls), which contained the samples to be coated.
  • the solution was continuously stirred with a magnetic stir bar. After 23 minutes, the samples were taken out, rinsed with and then soaked in nanopure water for an hour. The samples were dried under a nitrogen stream and then annealed under a nitrogen atmosphere at 200° C. for 2 minutes. Insulating ZnO and AZO Deposition.
  • a transparent conductor was sputtered on top of the CdS with the following structure: 50 nm of insulating ZnO (150 W RF, 5 mTorr, 20 sccm) followed by 500 nm of Al-doped ZnO using a 2% Al 2 O 3 , 98% ZnO target (75 or 150 W RF, 10 mTorr, 20 sccm).
  • ITO Transparent Conductor Deposition 50 nm of insulating ZnO (150 W RF, 5 mTorr, 20 sccm) followed by 500 nm of Al-doped ZnO using a 2% Al 2 O 3 , 98% ZnO target (75 or 150 W RF, 10 mTorr, 20 sccm).
  • a transparent conductor was sputtered on top of the CdS with the following structure: 50 nm of insulating ZnO [100 W RF, 20 mTorr (19.9 mTorr Ar+0.1 mTorr O 2 )] followed by 250 nm of ITO [100 W RF, 12 mTorr (12 mTorr Ar+5 ⁇ 10 ⁇ 6 Torr O 2 )].
  • the sheet resistivity of the resulting ITO layer is around 30 ohms per square.
  • Deposition of Silver Lines Silver was deposited at 150 WDC, SmTorr, 20 sccm Ar, with a target thickness of 750 nm.
  • XAS Analysis XANES spectroscopy at the Cu, Zn and Sn K-edges were carried out at the Advanced Photon Source at the Argonne National Laboratory. Data were collected in fluorescence geometry at beamline 5BMD, DND-CAT. Thin film samples were presented to the incident x-ray beam as made. An Oxford spectroscopy-grade ion chamber was used to determine the X-ray incident intensity (I 0 ). The I 0 detector was filled with 570 Torr of N 2 and 20 Torr of Ar. The fluorescence detector was a Lytle Cell filled with Xe installed perpendicular to the beam propagation direction. Data were collected from 8879 eV to 9954 eV for the Cu edge.
  • the high final energy was used in order to capture a portion of the Zn edge in the same data set, to allow edge step ratio determination as an estimate of Cu:Zn ratio in the film.
  • the Zn edge data were collected over the range 9557 eV to 10,404 eV.
  • Sn edge data covered the range of 29,000 eV to 29,750 eV.
  • the data energy scales were calibrated based on data from metal reference foils collected prior to sample data collection. A second order background was subtracted and the spectra were normalized.
  • the diffractometer was equipped with automatic variable anti-scatter and divergence slits, X′Celerator RTMS detector, and Ni filter.
  • the radiation was CuK(alpha) (45 kV, 40 mA).
  • Data were collected at room temperature from 4 to 120°. 2-theta; using a continuous scan with an equivalent step size of 0.02°; and a count time of from 80 sec to 240 sec per step in theta-theta geometry.
  • Thin film samples were presented to the X-ray beam as made.
  • MDI/Jade software version 9.1 was used with the International Committee for Diffraction Data database PDF4+ 2008 for phase identification and data analysis. IV Analysis.
  • the excitation light source was a xenon arc lamp with wavelength selection provided by a monochrometer in conjunction with order sorting filters.
  • Optical bias was provided by a broad band tungsten light source focused to a spot slightly larger than the monochromatic probe beam. Measurement spot sizes were approximately 1 mm ⁇ 2 mm.
  • OBIC Analysis Optical beam induced current measurements were determined with a purpose-constructed apparatus employing a focused monochromatic laser as the excitation source.
  • the excitation beam was focused to a spot ⁇ 100 microns in diameter.
  • the excitation spot was rastered over the surface of the test sample while simultaneously measuring photocurrent so as to build a map of photocurrent vs position for the sample.
  • the resulting photocurrent map characterizes the photoresponse of the device vs. position.
  • the apparatus can operate at various wavelengths via selection of the excitation laser. Typically, 440, 532 or 633 nm excitation sources were employed.
  • Zinc diethyldithiocarbamate (0.5919 g, 1.635 mmol), copper(II) dimethyldithiocarbamate (0.9930 g, 3.267 mmol), and di-n-butyltinsulfide (0.4506 g, 1.701 mmol) were placed in a 40 mL amber vial equipped with a stir bar. 4-t-Butylpyridine (4.4144 g) was added, and the resulting mixture was stirred well. Next, 0.0520 g (1.621 mmol) of elemental sulfur was added. The reaction mixture was stirred for ⁇ 12 hr at room temperature and then ⁇ 40 hr at a first heating temperature of 105° C.
  • a SLG slide was coated via drop-coating according to the following procedure: While being maintained at 105° C. with stirring, a small portion of the formulation was drawn into a pipette and then spread uniformly onto the substrate, which was also heated to 105° C. The coating on the SLG slide was then dried in the drybox by raising the temperature of the hotplate from 105° C. to 170° C. for 0.5 h. The dried sample was annealed under a nitrogen/sulfur atmosphere at 550° C. for 1 hr. Analysis of the annealed sample by XRD and XAS confirmed the presence of CZTS.
  • Example 1 was repeated using pyridine or toluene or 3-aminopyridine in place of 4-t-butylpyridine, with the second heating temperature of ⁇ 105° C., 105° C., and 170° C., respectively.
  • the annealing temperature/time was 400°/0.5 h for the sample prepared in pyridine; 500°/0.5 h for the toluene sample; and 550° C./1 h for the 3-aminopyridine sample.
  • Analysis of the annealed samples by XRD and XAS also confirmed the presence of CZTS.
  • Example 1 was repeated with annealing carried out under a nitrogen atmosphere by RTA. Analysis of the annealed sample by XRD also confirmed the presence of CZTS.
  • Example 1 was repeated, but the formulation was deposited on a Mo-patterned SLG slide. Also, the temperature of the hotplate was raised from 105 to 180° C. over the course of 2 hr, and the coating was annealed at 550° C. for 0.5 hr. Cadmium sulfide, insulating ZnO and AZO, and silver lines were deposited. Analysis by OBIC at 440 nm and 633 nm showed photoresponses greater than 5 and 0.75 micro-Amp, respectively, adjacent to the silver line.
  • the reaction mixture was stirred for ⁇ 12 hr at room temperature and then ⁇ 40 hr at a first heating temperature of 105° C. Next, the reaction mixture was stirred for ⁇ 8 hr at a second heating temperature of 110° C.
  • An untreated glass slide was coated via drop-coating in a manner similar to described above in Example 1. The coated substrate was then placed on a hot plate and heated to 120° C. for ⁇ 0.5 hr. The coated substrate was allowed to remain on the hotplate as it cooled to room temperature. The coated substrate was annealed in the tube furnace at 500° C. under a nitrogen/sulfur atmosphere for 0.5 hr. Analysis of the annealed sample by XRD confirmed the presence of CZTS. Spectrophotometric measurements showed a bandgap at 110 nm ( ⁇ 1.13 eV) for a 4 micron-thick film.
  • Example 2 was repeated using 2-aminopyridine in place of pyridine, with the second heating temperature about 190° C., a drying temperature of 170° C., and an annealing temperature of 550° C. for 1 hr. Analysis of the annealed sample by XRD and XAS also confirmed the presence of CZTS.
  • Example 2 was repeated using no additional solvent and the solution was stirred at room temperature for several days without heating prior to coating.
  • the coating was produced via blade-coating, with both the formulation and substrate initially at room temperature.
  • the thickness of the coating was controlled by placing 0.003 feeler stock on either side of the area to be coated, and a thicker piece of feeler stock was used as the blade.
  • the drying temperature was 110° C. for ⁇ 0.5 hr, and the annealing temperature was 550° C. for 0.5 hr.
  • Analysis of the annealed sample by XRD and XAS also confirmed the presence of CZTS. Spectrophotometric measurements showed a bandgap at 850 nm ( ⁇ 1.45 eV) for an ⁇ 5 micron-thick film.
  • Example 2 was repeated, but the formulation was deposited on a Mo-patterned SLG slide. Cadmium sulfide and insulating ZnO and AZO were deposited. Analysis by OBIC at 440 nm showed a photoresponse greater than 0.2 micro-Amp. Also, IV analysis showed diode-like behavior, with V oc of 78 mV, J SC of 0.119 mA/cm 2 , FF of 23.6%, and efficiency of 0.002%.
  • a formulation was prepared according to the procedure of Example 1, using zinc methoxyethoxide (0.8184 mmol), copper(I) acetate (1.636 mmol), di-n-butyltinsulfide (0.8276 mmol), 2-mercaptoethanol (3.426 mmol), and sulfur (0.7795 mmol) in diethylnicotinamide (1.0871 g).
  • the reaction mixture was stirred for ⁇ 12 hr at room temperature and then ⁇ 40 hr at 105° C. Next, the reaction mixture was stirred ⁇ 8 hr at 190° C.
  • An untreated glass slide was coated via drop-coating according to the procedure of Example 1, and then dried at 170-190° C. on the hotplate in the drybox. Annealing was carried out at 550° C. for 30 min in a nitrogen/sulfur atmosphere. Analysis of the annealed sample by XRD confirmed the presence of CZTS.
  • Example 3 was repeated using 4-t-butylpyridine, 1,2,4-trichlorobenzene, or 3-methoxypropionitrile as the solvent.
  • the temperature of the second heating step was 160-190° C., 190° C., and 150° C., respectively for these solvents.
  • Analysis of the annealed samples by XRD confirmed the presence of CZTS.
  • Example 3 was also repeated using zinc methoxyethoxide (0.8829 mmol), copper(I) acetate (1.518 mmol), di-n-butyltinsulfide (0.8884 mmol), 2-mercaptoethanol (3.673 mmol), and sulfur (0.8045 mmol) in 2- or 3-aminopyridine (1.0314 g), and a second heating temperature of 170° C. CZTS was detected in both the dried and the annealed samples by XAS.
  • a formulation was prepared according to the procedure of Example 4 using zinc methoxyethoxide (0.2385 g, 0.271 mmol); 1.4965 g of a 10-12 wt % solution (0.545 mmol assuming 11 wt %) of copper(II) methoxyethoxyethoxide in methoxyethoxyethanol; 0.1218 g (0.272 mmol) of di-n-butylbis(1-thioglycerol)tin; 0.1326 g (1.697 mmol) of 2-mercaptoethanol; and 0.0089 g (0.278 mmol) of elemental sulfur.
  • a coating on treated glass was dried at 120° C. for 0.5 hr and then annealed under a nitrogen/sulfur atmosphere at 650° C. for 30 min. Analysis of the annealed sample by XRD and XAS confirmed the presence of CZTS.
  • a coating on glass was annealed under a nitrogen/sulfur atmosphere at 550° C. for 30 min. Analysis by XRD and XAS confirmed the presence of CZTS.
  • Example 6 was repeated, but the formulation was deposited on a Mo-patterned SLG substrate. Cadmium sulfide and insulating ZnO and AZO were deposited. Analysis by OBIC at 440 nm showed a photoresponse greater than 0.1 micro-Amp adjacent. Analysis of the sample via EQE demonstrated that the PV device exhibited a photoresponse consistent with the semiconductor absorber having a band gap energy of 1.53+/ ⁇ 0.04 eV, consistent with the absorber being assigned as CZTS.
  • Formulations were prepared according to the procedure of Example 1 using 0.2952 g (0.816 mmol) of zinc diethyldithiocarbamate, 0.4960 g (1.632 mmol) of copper(II) dimethyldithiocarbamate, 0.2696 g (0.851 mmol) of tin(II) acetylacetonate, and 0.2469 g (1.838 mmol) of (ethylthio)trimethylsilane. After being thoroughly mixed, the reaction mixture was divided into thirds and placed in three 4 mL vials equipped with stir bars. One of these vials was used for Example 7 and received no additional reagents.
  • the second heating temperature was 110° C.
  • two SLG slides were drop-coated according to the procedure of Example 1, both coatings were dried at 120° C. and one of these coatings was annealed at 400° C.
  • Another vial was used for Example 8, and 0.0082 g of elemental sulfur (1 equiv) was added to the vial.
  • the second heating temperature was 110° C.
  • a coating was prepared on a SLG slide with drying temperature at 120° C.
  • the annealing temperature was 400° C.
  • the formulation of Example 9 was analogous to that of Example 8, except that 2-aminopyridine was used as the solvent.
  • the second heating temperature was 190° C.
  • the drying temperature was 170-190° C.
  • the annealing temperature was 550° C.
  • CZTS was detected in all of the annealed samples and the dried sample of Example 7 by XRD and/or XAS.
  • a formulation was prepared according to the procedure of Example 1 using 0.1768 g (0.820 mmol) of zinc methoxyethoxide, 0.2047 g (1.630 mmol) of copper(II) methoxide, 0.4004 g (0.911 mmol) of bis[bis(trimethysilyl)amino]tin(II), 0.8990 g (6.692 mmol) of ethylthiotrimethylsilane, 0.0259 g (0.808 mmol) of elemental sulfur, and 0.4700 g of 3,5-lutidine.
  • the second heating temperature was 165° C.
  • the formulation was coated on an untreated glass slide and dried at 170° C.
  • the coating was annealed at 550° C. for 30 min, and was then analyzed by XRD, which indicated kesterite as the predominant component and a trace amount of covelite (CuS).
  • a formulation was prepared according to the procedure of Example 1 using 0.1754 g (0.814 mmol) of zinc methoxyethoxide, 0.2055 g (1.636 mmol) of copper(II) methoxide, 0.3983 g (0.906 mmol) of bis[bis(trimethysilyl)amino]tin(II), 0.5226 g (6.69 mmol) of 2-mercaptoethanol, 0.0258 g (0.804 mmol) of elemental sulfur and 0.9520 g of 3,5-lutidine.
  • the second heating temperature was 165° C.
  • the formulation was drop-cast onto two untreated slides and two treated slides.
  • the two coatings on the untreated slides were dried at 210° C., and the two coatings on the treated slides were dried at 250° C.
  • One of the coatings on an untreated slide was annealed at 550° C. for 1 hr, and one of the coatings on a treated slide was annealed at 550° C. for 0.5 hr.
  • the coatings were analyzed by XAS, and the presence of CZTS was confirmed in the annealed coatings.
  • Example 12 According to the procedure of Example 1, the formulation of Example 12 was prepared using 0.1829 g (0.849 mmol) of zinc methoxyethoxide, 0.2110 g (1.680 mmol) of copper(II) methoxide, 0.2299 g (0.868 mmol) of di-n-butyltin sulfide, 0.4085 g (5.23 mmol) of 2-mercaptoethanol, and 0.916 g of 4-t-butylpyridine. The second heating temperature was 190° C.
  • Example 13 According to the procedure of Example 1, the formulation of Example 13 was prepared using 0.1830 g (0.849 mmol) of zinc methoxyethoxide, 0.1947 g (1.550 mmol) of copper(II) methoxide, 0.2440 g (0.921 mmol) of di-n-butyltin sulfide, 0.4049 g (5.18 mmol) of 2-mercaptoethanol, 0.792 mmol of sulfur, and 0.926 g of 4-t-butylpyridine. The second heating temperature was 190° C.
  • Each formulation was drop-cast onto two untreated glass slides and the coatings were dried at 170° C.
  • One coating of each formulation was then annealed at 550° C. for 0.5 hr.
  • the coatings were analyzed by XAS, and the presence of CZTS was confirmed in the annealed coatings.
  • Example 15 According to the procedure of Example 1, the formulation of Example 15 was prepared using 0.0.2312 g (0.821 mmol) of zinc 2,4-pentanedionate monohydrate, 0.1999 g (1.631 mmol) of copper(I) acetate, 0.3885 g (0.901 mmol) of di-n-butyltin bis(acetylacetonate), 1.0881 g (4.89 mmol) of diethyldithiocarbamic acid diethylammonium salt, 0.0264 g (0.823 mmol) of elemental sulfur, and 1.433 g of 4-t-butylpyridine.
  • the second heating temperature was 190° C.
  • the formulation was drop-coated onto untreated glass, dried at 180° C., and annealed at 550° C. for 0.5 hr. Analysis by XAS confirmed the presence of CZTS in the annealed sample.
  • Example 16 According to the procedure of Example 1, the formulation of Example 16 was prepared using 0.851 mmol of zinc diethyldithiocarbamate, 1.595 mmol of copper(II) dimethyldithiocarbamate, 0.949 mmol of tin(II) sulfide, 0.823 mmol of elemental sulfur, and 2.895 g of N-methyl-2-pyrrolidinone.
  • the second heating temperature was at 170-190° C.
  • the formulation was drop-coated onto two untreated glass slides, the coatings were dried at 180° C. and then one of the coatings was annealed at 550° C. for 1 hr.
  • Analysis by XRD and XAS confirmed the presence of CZTS in the annealed sample; XAS analysis confirmed the presence of CZTS in the dried (un-annealed) sample.
  • Example 16 using 3-amino-pyridine as the solvent without the addition of elemental sulfur was spun-coated to give a third layer.
  • the substrate was heated at 105° C. for several hr and then for 20-30 min at 220° C., then cooled to room temperature.
  • the substrate was annealed for 90 min under a nitrogen/sulfur atmosphere at 550° C. Analysis by XRD confirmed the presence of CZTS.
  • a coated substrate was prepared analogously to that of Example 17 except that the third layer was not applied.
  • the substrate was annealed for 90 min under a nitrogen/selenium atmosphere.
  • XRD analysis indicated the presence of CZTS-Se, with sulfur partially (67.8%) replaced with selenium.
  • Example 16 The formulation of Example 16 using 2-aminopyridine as the solvent and without the addition of elemental sulfur was spun-coated onto a treated SLG substrate. The substrate was then heated at 105° C. for at least 2 hr, cooled to room temperature, heated to 170° C. for 70 min, and cooled to room temperature. Next, a formulation analogous to that used for Example 1, except with only 2.2 g of 4-t-butylpyridine, was spun on top of the first coating. The substrate was heated at 105° C. for several hr, then at 170° C. for 20 min, and cooled to room temperature. After annealing by RTA under nitrogen, XRD indicated the presence of CZTS. The substrate was then annealed in a furnace under a selenium/nitrogen atmosphere for 90 min at 550° C. XRD indicated the presence of CZTS-Se, with sulfur partially (67.1%) replaced with selenium.
  • Zinc sulfide (0.915 mmol), copper(II) sulfide (1.539 mmol), and tin(II) sulfide (0.884 mmol) were placed in a 40 mL amber vial equipped with a stir bar. 3-Methoxypropylamine (0.893 g) was added, and the resulting mixture was stirred well. Next, 0.798 mmol of elemental sulfur was added. The reaction mixture was stirred for ⁇ 12 hr at room temperature and then ⁇ 48 hr at 105° C. The formulation was then drop-coated onto a treated SLG slide according to procedure of Example 1. The coating was then dried in the drybox by raising the temperature of the hotplate from 105° C. to 170° C. for 0.5 hr. The coating was annealed at 550° C. for 0.5 hr. Analysis of the annealed sample by XAS confirmed the presence of CZTS.
  • Formulation and coating was analogous to that of Example 1, except that no zinc compound was used in the formulation.
  • the coated substrate was annealed under selenium/nitrogen vapor for 90 min at 550° C.
  • the XRD analysis indicated the presence of CTS-Se, with sulfur partially (71.4%) replaced with selenium and with an average grain size of greater than 100 nm.
  • Example 16 was repeated using 4-t-butylpyridine as the solvent and tin(II) selenide in place of tin(II) sulfide.
  • the XRD analysis indicated the presence of CTS-Se, with sulfur partially (76.8%) replaced with selenium and with an average grain size of 35.2 nm

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Physics & Mathematics (AREA)
  • Condensed Matter Physics & Semiconductors (AREA)
  • General Physics & Mathematics (AREA)
  • Organic Chemistry (AREA)
  • Computer Hardware Design (AREA)
  • Power Engineering (AREA)
  • Microelectronics & Electronic Packaging (AREA)
  • Manufacturing & Machinery (AREA)
  • Materials Engineering (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Inorganic Chemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Electromagnetism (AREA)
  • Metallurgy (AREA)
  • Mechanical Engineering (AREA)
  • Thermal Sciences (AREA)
  • Nanotechnology (AREA)
  • Wood Science & Technology (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Composite Materials (AREA)
  • Photovoltaic Devices (AREA)
  • Inks, Pencil-Leads, Or Crayons (AREA)
  • Manufacture Of Metal Powder And Suspensions Thereof (AREA)
  • Application Of Or Painting With Fluid Materials (AREA)
  • Paints Or Removers (AREA)
  • Liquid Deposition Of Substances Of Which Semiconductor Devices Are Composed (AREA)
US13/319,900 2009-05-21 2010-05-21 Processes for preparing copper tin sulfide and copper zinc tin sulfide films Abandoned US20120060928A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US13/319,900 US20120060928A1 (en) 2009-05-21 2010-05-21 Processes for preparing copper tin sulfide and copper zinc tin sulfide films

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
US18018109P 2009-05-21 2009-05-21
US18017909P 2009-05-21 2009-05-21
US18018609P 2009-05-21 2009-05-21
US18018409P 2009-05-21 2009-05-21
US13/319,900 US20120060928A1 (en) 2009-05-21 2010-05-21 Processes for preparing copper tin sulfide and copper zinc tin sulfide films
PCT/US2010/035810 WO2010135667A1 (fr) 2009-05-21 2010-05-21 Procédés pour préparer des films de sulfure de cuivre et d'étain et de sulfure de cuivre, de zinc et d'étain

Publications (1)

Publication Number Publication Date
US20120060928A1 true US20120060928A1 (en) 2012-03-15

Family

ID=42797237

Family Applications (2)

Application Number Title Priority Date Filing Date
US13/319,819 Expired - Fee Related US9112094B2 (en) 2009-05-21 2010-05-21 Copper tin sulfide and copper zinc tin sulfide ink compositions
US13/319,900 Abandoned US20120060928A1 (en) 2009-05-21 2010-05-21 Processes for preparing copper tin sulfide and copper zinc tin sulfide films

Family Applications Before (1)

Application Number Title Priority Date Filing Date
US13/319,819 Expired - Fee Related US9112094B2 (en) 2009-05-21 2010-05-21 Copper tin sulfide and copper zinc tin sulfide ink compositions

Country Status (7)

Country Link
US (2) US9112094B2 (fr)
EP (3) EP2432840A1 (fr)
JP (3) JP2012527401A (fr)
KR (3) KR20120036872A (fr)
CN (3) CN102439098A (fr)
TW (1) TW201107241A (fr)
WO (3) WO2010135667A1 (fr)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20120061790A1 (en) * 2010-09-09 2012-03-15 International Business Machines Corporation Structure and Method of Fabricating a CZTS Photovoltaic Device by Electrodeposition
US20120255488A1 (en) * 2011-04-07 2012-10-11 Dynamic Micro Systems, Semiconductor Equipment Gmbh Methods and apparatuses for roll-on coating
US20130224902A1 (en) * 2012-02-24 2013-08-29 Industry-Academic Cooperation Foundation, Yeungnam University Method of manufacturing photovoltaic cell
US20140096826A1 (en) * 2012-10-04 2014-04-10 International Business Machines Corporation Solution processing of kesterite semiconductors
US20140273333A1 (en) * 2013-03-13 2014-09-18 Intermolecular Inc. Methods for fabricating ZnOSe alloys
US20160133768A1 (en) * 2013-08-01 2016-05-12 Lg Chem, Ltd. Ink composition for manufacturing light absorption layer of solar cells and method of manufacturing thin film using the same
US9601642B1 (en) * 2014-09-29 2017-03-21 EWHA University—Industry Collaboration Foundation CZTSe-based thin film and method for preparing the same, and solar cell using the same
US10340402B2 (en) 2014-11-13 2019-07-02 Lg Chem, Ltd. Method of preparing metal chalcogenide nanoparticles and method of producing light absorption layer thin film based thereon
US11162024B2 (en) 2016-03-18 2021-11-02 Osaka University Semiconductor nanoparticles and method of producing semiconductor nanoparticles

Families Citing this family (88)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
BRPI1011655A2 (pt) * 2009-05-26 2019-09-24 Purdue Research Foundation uso de lcat para tratar anemia e disfunção de glóbulos vermelhos
US8277894B2 (en) * 2009-07-16 2012-10-02 Rohm And Haas Electronic Materials Llc Selenium ink and methods of making and using same
US8308973B2 (en) * 2009-07-27 2012-11-13 Rohm And Haas Electronic Materials Llc Dichalcogenide selenium ink and methods of making and using same
US20110094557A1 (en) * 2009-10-27 2011-04-28 International Business Machines Corporation Method of forming semiconductor film and photovoltaic device including the film
US10147604B2 (en) 2009-10-27 2018-12-04 International Business Machines Corporation Aqueous-based method of forming semiconductor film and photovoltaic device including the film
US8119506B2 (en) * 2010-05-18 2012-02-21 Rohm And Haas Electronic Materials Llc Group 6a/group 3a ink and methods of making and using same
WO2011146115A1 (fr) 2010-05-21 2011-11-24 Heliovolt Corporation Précurseur liquide pour dépôt de séléniure de cuivre et procédé pour sa préparation
WO2012023973A2 (fr) 2010-08-16 2012-02-23 Heliovolt Corporation Précurseur liquide pour le dépôt du séléniure d'indium et procédé de préparation correspondant
JP6064314B2 (ja) * 2010-11-29 2017-01-25 株式会社リコー 金属酸化物薄膜形成用塗布液、金属酸化物薄膜の製造方法、及び電界効果型トランジスタの製造方法
JP5278778B2 (ja) * 2011-01-18 2013-09-04 株式会社豊田中央研究所 カルコゲナイト系化合物半導体及びその製造方法
WO2012100139A2 (fr) * 2011-01-21 2012-07-26 Regents Of The University Of Minnesota Chalcogénures métalliques et procédés de préparation et d'utilisation de ces derniers
TR201809809T4 (tr) * 2011-02-02 2018-07-23 Advenira Entpr Inc Solüsyon ile türetilen nanokompozit prekursör solüsyonlar.
US10131793B2 (en) 2011-02-02 2018-11-20 Advenira Enterprises, Inc. Modified hybrid sol-gel solutions and compositions formed from such solutions
WO2012112491A1 (fr) * 2011-02-15 2012-08-23 Purdue Research Foundation Conversion d'énergie par effet thermoélectrique basée sur du czts (cuivre-zinc-étain-soufre) nanostructuré
JP5774727B2 (ja) * 2011-02-18 2015-09-09 ユニバーシティ オブ ワシントン スルー イッツ センター フォー コマーシャリゼーション Ｉ２−ｉｉ−ｉｖ−ｖｉ４及びｉ２−（ｉｉ、ｉｖ）−ｉｖ−ｖｉ４半導体フィルムを含む半導体フィルムを形成する方法
US8501526B2 (en) 2011-04-22 2013-08-06 Alliance For Sustainable Energy, Llc Synthesizing photovoltaic thin films of high quality copper-zinc-tin alloy with at least one chalcogen species
WO2012148198A2 (fr) * 2011-04-28 2012-11-01 주식회사 엘지화학 Nouveau composé semi-conducteur et son utilisation
EP2703344B1 (fr) * 2011-04-28 2016-08-31 LG Chem, Ltd. Nouveau composé semi-conducteur et son utilisation
US8771555B2 (en) 2011-05-06 2014-07-08 Neo Solar Power Corp. Ink composition
EP2708496B1 (fr) * 2011-05-13 2018-02-28 LG Chem, Ltd. Nouveau semi-conducteur composé et son utilisation
KR101431771B1 (ko) * 2011-05-13 2014-08-19 주식회사 엘지화학 신규한 화합물 반도체 및 그 활용
CN103534201B (zh) * 2011-05-13 2016-10-19 Lg化学株式会社 新的化合物半导体及其用途
CN103502143B (zh) * 2011-05-13 2016-01-20 Lg化学株式会社 新的化合物半导体及其用途
JP5788832B2 (ja) * 2011-06-06 2015-10-07 トヨタ自動車株式会社 ソルボサーマル法を用いるＣｕ，Ｚｎ，Ｓｎ及びＳを含有する硫化物系化合物半導体ナノ粒子の製造方法
JP5922348B2 (ja) * 2011-07-25 2016-05-24 京セラ株式会社 半導体層の製造方法、光電変換装置の製造方法および半導体層形成用液
WO2013015745A1 (fr) * 2011-07-25 2013-01-31 Nanyang Technological University Couche mince de cu-zn-sn-s/se et ses procédés de fabrication
JP5536153B2 (ja) * 2011-09-16 2014-07-02 新日光能源科技股▲ふん▼有限公司 カルコゲナイド半導体膜の形成方法及び光起電力装置
WO2013047461A1 (fr) * 2011-09-30 2013-04-04 凸版印刷株式会社 Encre pour former un film mince semi-conducteur composite et son procédé de fabrication
KR101311030B1 (ko) * 2011-11-24 2013-09-24 연세대학교 산학협력단 Ｃｚｔｓ 박막용 하이브리드 잉크
JP2013115235A (ja) * 2011-11-29 2013-06-10 Toyota Central R&D Labs Inc 光電素子及びその製造方法
JP5776993B2 (ja) * 2011-11-30 2015-09-09 株式会社村田製作所 化合物半導体超微粒子の製造方法
CN104136375B (zh) * 2011-12-22 2016-09-28 西安大略大学 含铜纳米晶及其制备方法
JP2013136481A (ja) * 2011-12-28 2013-07-11 Toyota Motor Corp Ｃｚｔｓ系化合物半導体及び光電変換素子
TWI460869B (zh) * 2011-12-30 2014-11-11 Ind Tech Res Inst 太陽能電池光吸收層之製法
US20130217211A1 (en) * 2012-02-21 2013-08-22 Aqt Solar, Inc. Controlled-Pressure Process for Production of CZTS Thin-Films
JP5752624B2 (ja) * 2012-03-09 2015-07-22 トヨタ自動車株式会社 Ｃｚｔｓ化合物半導体の製造方法
EP2647675A2 (fr) * 2012-04-02 2013-10-09 Neo Solar Power Corp. Procédé de formation d'une encre
EP2647595A2 (fr) * 2012-04-03 2013-10-09 Neo Solar Power Corp. Composition d'encre, film semi-conducteur à base de chalcogénure, dispositif photovoltaïque et procédés pour former ceux-ci
KR101298026B1 (ko) * 2012-04-13 2013-08-26 한국화학연구원 태양전지 광활성층의 제조방법
US8586457B1 (en) * 2012-05-17 2013-11-19 Intermolecular, Inc. Method of fabricating high efficiency CIGS solar cells
US9105797B2 (en) 2012-05-31 2015-08-11 Alliance For Sustainable Energy, Llc Liquid precursor inks for deposition of In—Se, Ga—Se and In—Ga—Se
EP2674964B1 (fr) * 2012-06-14 2014-10-29 Suntricity Cells Corporation Solution de précurseur pour former un film mince à semi-conducteurs sur la base de CIS, CIGS ou CZTS
TWI586773B (zh) * 2012-07-26 2017-06-11 東京應化工業股份有限公司 光吸收層形成用塗佈液之製造方法
US8987590B2 (en) 2012-08-01 2015-03-24 International Business Machines Corporation Thin film solar cells
WO2014025176A1 (fr) * 2012-08-09 2014-02-13 한국에너지기술연구원 Cellule solaire cigs à substrat flexible ayant un procédé d'alimentation en na amélioré et son procédé de fabrication
CN102790130B (zh) * 2012-08-09 2015-08-05 中国科学院长春应用化学研究所 一种吸光层薄膜的制备方法
CN103779433B (zh) * 2012-10-22 2016-09-21 中物院成都科学技术发展中心 一种铜铟镓硒薄膜预制层及其制备方法
KR101389832B1 (ko) * 2012-11-09 2014-04-30 한국과학기술연구원 구리인듐셀레늄（ｃｉｇｓ） 또는 구리아연주석황（ｃｚｔｓ）계 박막형 태양전지 및 그의 제조방법
CN103094422A (zh) * 2013-01-29 2013-05-08 电子科技大学 铜锌锡硫硒薄膜制备中的掺杂工艺
KR20140097981A (ko) 2013-01-29 2014-08-07 주식회사 엘지화학 태양전지용 금속 나노 입자의 제조 방법, 그 금속 나노 입자를 포함하는 잉크 조성물 및 이를 사용한 박막의 제조 방법
JP5884945B2 (ja) * 2013-03-07 2016-03-15 株式会社村田製作所 化合物半導体超微粒子、超微粒子薄膜及び光電変換デバイス
CN103214901B (zh) * 2013-04-08 2014-11-12 无锡舒玛天科新能源技术有限公司 一种制备铜铟镓硒墨水的方法
JP5835265B2 (ja) * 2013-04-11 2015-12-24 株式会社豊田中央研究所 光電変換材料及びその製造方法
KR101406704B1 (ko) 2013-04-18 2014-06-12 한국에너지기술연구원 동시진공증발공정 기반의 CZTSe 광흡수층 제조방법
US9634161B2 (en) 2013-05-01 2017-04-25 Delaware State University Nanoscale precursors for synthesis of Fe2(Si,Ge)(S,Se)4 crystalline particles and layers
CN104151932A (zh) * 2013-05-13 2014-11-19 中原工学院 柔性或薄膜太阳能电池用喷墨打印机墨水及其制备方法
JP6012866B2 (ja) * 2013-06-03 2016-10-25 東京応化工業株式会社 錯体およびその溶液の製造方法、太陽電池用光吸収層の製造方法および太陽電池の製造方法
JP2015002269A (ja) * 2013-06-14 2015-01-05 株式会社豊田中央研究所 光吸収体及び光電変換素子
JP6281835B2 (ja) * 2013-09-06 2018-02-21 国立大学法人 宮崎大学 太陽電池用化合物半導体ナノ粒子の作製方法
CN103560165A (zh) * 2013-09-12 2014-02-05 北京工业大学 一种硫醇基墨水制备Cu2ZnSn(S,Se)4太阳能电池吸收层薄膜的方法
WO2015039106A2 (fr) * 2013-09-16 2015-03-19 Wake Forest University Films polycristallins comprenant un chalcogénure de cuivre, de zinc et d'étain et procédés pour le fabriquer
EP3116019A4 (fr) * 2014-03-14 2017-03-22 Tokyo Ohka Kogyo Co., Ltd. AGENT DE RÉGULATION DE CROISSANCE CRISTALLINE, PROCÉDÉ PERMETTANT DE FORMER DES MICROPARTICULES SEMI-CONDUCTRICES DE TYPE p OU UN FILM DE MICROPARTICULES SEMI-CONDUCTRICES DE TYPE p, COMPOSITION PERMETTANT DE FORMER UNE COUCHE DE TRANSPORT DE TROUS ET PHOTOPILE
CN103923515A (zh) * 2014-04-10 2014-07-16 北京工业大学 一种可用于制备Cu2ZnSnS4太阳能电池吸收层薄膜的墨水的配制方法
JP2015202979A (ja) * 2014-04-14 2015-11-16 学校法人中部大学 前駆体膜の作製方法
CN103928575A (zh) * 2014-04-29 2014-07-16 中国科学院长春应用化学研究所 一种吸光层薄膜、其制备方法和铜基薄膜太阳能电池
CN104037267B (zh) * 2014-06-30 2016-07-06 电子科技大学 一种对铜锌锡硒薄膜太阳能电池吸收层改性的方法
JP6404068B2 (ja) * 2014-10-01 2018-10-10 国立研究開発法人産業技術総合研究所 酸化物前駆体材料
CN104701138A (zh) * 2015-03-08 2015-06-10 北京工业大学 一种CZTS(Se)纳米晶薄膜的制备方法
CN104993016B (zh) * 2015-06-10 2017-01-11 中南大学 一种贵金属纳米晶负载铜锌锡硫薄膜的制备方法
CN104876195B (zh) * 2015-06-17 2017-01-25 许昌学院 一种常温原位控制合成硒硫铜三元化合物的化学方法
CN105355720B (zh) * 2015-12-03 2017-02-01 华东师范大学 一种制备铜锡硫薄膜太阳能电池吸收层的方法
CN105615174B (zh) * 2016-03-17 2018-02-02 杨祖发 一种具有充电功能的太阳伞
JP6464215B2 (ja) * 2016-03-18 2019-02-06 国立大学法人大阪大学 半導体ナノ粒子およびその製造方法
CN106098841B (zh) * 2016-06-28 2017-12-12 南安泉鸿孵化器管理有限公司 一种铜锌锡硫光电纤维的制备方法
CN106098814A (zh) * 2016-07-01 2016-11-09 福建师范大学 一种氧化物纳米颗粒制备太阳能电池吸收层CTSSe薄膜的方法
CN106118242A (zh) * 2016-07-28 2016-11-16 Tcl集团股份有限公司 一种喷墨打印用的量子点油墨及其制备方法
US11087976B2 (en) * 2016-10-07 2021-08-10 Haldor Topsøe A/S Kesterite material of CZTS, CZTSe or CZTSSe type
CN106449812B (zh) * 2016-11-15 2020-06-30 云南师范大学 溅射锡靶和硫化铜靶制备铜锡硫薄膜电池的方法
CN107634107B (zh) * 2017-08-30 2019-03-26 中建材（合肥）新能源有限公司 一种增强光吸收效率型纳米光伏材料的制备方法
CN108807145B (zh) * 2018-06-05 2020-08-11 南京邮电大学 一种制备高效铜铟硒和铜铟镓硒薄膜太阳能电池的方法
AT521545A1 (de) * 2018-08-09 2020-02-15 Ait Austrian Inst Tech Gmbh Suspension zur herstellung einer halbleiterschicht
PL241410B1 (pl) * 2019-02-11 2022-09-26 Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie Sposób wytwarzania proszkowego kesterytu typu Cu<sub>₂</sub>SnZnS<sub>₄</sub>
PL241416B1 (pl) * 2019-02-11 2022-09-26 Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie Sposób wytwarzania proszkowego kesterytu typu Cu₂SnZnS₄, przeznaczonego do produkcji warstw czynnych w cienkowarstwowych ogniwach fotowoltaicznych
CN109979645B (zh) * 2019-03-29 2020-11-10 合肥工业大学 一种p型硫化铜透明导电薄膜及制备方法
CN111554760B (zh) * 2020-05-15 2022-06-17 南京邮电大学 铜锌锡硫薄膜太阳能电池的前驱体溶液及其制备方法与应用
KR102443380B1 (ko) * 2020-11-24 2022-09-19 한국과학기술연구원 전기화학적 질소환원을 위한 다중공 금속황화물 나노입자의 제조방법 및 이에 따라 제조된 다중공 금속황화물 나노입자
CN112892224B (zh) * 2021-01-15 2022-05-13 东华大学 一种MoS2/CNT复合膜的制备方法和应用
WO2023215849A2 (fr) * 2022-05-06 2023-11-09 Electroninks Incorporated Compositions d'encre conductrice comprenant des complexes d'or

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4030987A (en) * 1975-03-08 1977-06-21 Kabushiki Kaisha Japan Metal Finishing Company Zinc plating method
US5877559A (en) * 1995-06-12 1999-03-02 Nitto Denko Corporation Film carrier for fine-pitched and high density mounting and semiconductor device using same
US20050118364A1 (en) * 2001-12-24 2005-06-02 Guise Richard J. Tubular member having an anti-galling coating
US20090205714A1 (en) * 2006-05-24 2009-08-20 Kuehnlein Holger Metal Plating Composition and Method for the Deposition of Copper-Zinc-Tin Suitable for Manufacturing Thin Film Solar Cell

Family Cites Families (26)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5100471A (en) * 1990-06-27 1992-03-31 Xerox Corporation Liquid ink compositions
JPH08316507A (ja) * 1995-05-12 1996-11-29 Yazaki Corp 薄膜太陽電池及びその製造方法
US6126740A (en) * 1995-09-29 2000-10-03 Midwest Research Institute Solution synthesis of mixed-metal chalcogenide nanoparticles and spray deposition of precursor films
DE19921515A1 (de) * 1999-05-10 2000-11-30 Ist Inst Fuer Solartechnologie Dünnschichtsolarzelle auf der Basis der Ia/IIIb/VIa- Verbindungshalbleiter und Verfahren zu ihrer Herstellung
US6875661B2 (en) * 2003-07-10 2005-04-05 International Business Machines Corporation Solution deposition of chalcogenide films
US7691294B2 (en) * 2005-03-04 2010-04-06 Inktec Co., Ltd. Conductive inks and manufacturing method thereof
KR100727434B1 (ko) * 2005-03-04 2007-06-13 주식회사 잉크테크 투명 은 잉크 조성물 및 이를 이용한 박막 형성방법
RU2388774C2 (ru) * 2005-03-04 2010-05-10 Инктек Ко., Лтд. Проводящие чернила и способ их получения
GB2429838B (en) * 2005-08-12 2011-03-09 Nanoco Technologies Ltd Nanoparticles
JP2007048680A (ja) * 2005-08-12 2007-02-22 Mitsubishi Paper Mills Ltd 光電変換材料、半導体電極並びにそれを用いた光電変換素子
KR100768341B1 (ko) 2005-11-09 2007-10-17 주식회사 나노신소재 금속성 잉크, 그리고 이를 이용한 전극형성방법 및 기판
WO2007092606A2 (fr) * 2006-02-09 2007-08-16 Qd Vision, Inc. affichages comprenant des nanocristaux semi-conducteurs et leurs procEdes de fabrication
US7494841B2 (en) * 2006-05-12 2009-02-24 International Business Machines Corporation Solution-based deposition process for metal chalcogenides
US9105776B2 (en) * 2006-05-15 2015-08-11 Stion Corporation Method and structure for thin film photovoltaic materials using semiconductor materials
GB2438452B (en) * 2006-05-24 2010-12-15 Nokia Corp Portable telecommunications apparatus
KR101252005B1 (ko) * 2006-06-22 2013-04-08 삼성전자주식회사 나노결정 입자를 함유하는 박막 및 그의 제조방법
US7638356B2 (en) * 2006-07-11 2009-12-29 The Trustees Of Princeton University Controlled growth of larger heterojunction interface area for organic photosensitive devices
WO2008018718A1 (fr) * 2006-08-07 2008-02-14 Inktec Co., Ltd. Procédé pour la préparation de nanoparticules d'argent et compositions d'encre d'argent les contenant
JP5309521B2 (ja) * 2006-10-11 2013-10-09 三菱マテリアル株式会社 電極形成用組成物及びその製造方法並びに該組成物を用いた電極の形成方法
WO2008154524A2 (fr) * 2007-06-08 2008-12-18 Robert Stancel Ensemble de connexion électrique montable par la tranche
JP5773646B2 (ja) * 2007-06-25 2015-09-02 キユーデイー・ビジヨン・インコーポレーテツド ナノ材料を被着させることを含む組成物および方法
JP4783908B2 (ja) * 2007-07-18 2011-09-28 株式会社豊田中央研究所 光電素子
JP2009105130A (ja) * 2007-10-22 2009-05-14 Canon Inc 光起電力素子の製造方法
EP2067525A1 (fr) * 2007-12-04 2009-06-10 Sony Corporation Procédé de préparation d'un film nanoparticulaire ayant des ions métalliques incorporés
WO2010095608A1 (fr) * 2009-02-20 2010-08-26 株式会社豊田中央研究所 Sulfure et élément photoélectrique
WO2010098369A1 (fr) * 2009-02-27 2010-09-02 国立大学法人名古屋大学 Nanoparticules semi-conductrices et leur procédé de production

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4030987A (en) * 1975-03-08 1977-06-21 Kabushiki Kaisha Japan Metal Finishing Company Zinc plating method
US5877559A (en) * 1995-06-12 1999-03-02 Nitto Denko Corporation Film carrier for fine-pitched and high density mounting and semiconductor device using same
US20050118364A1 (en) * 2001-12-24 2005-06-02 Guise Richard J. Tubular member having an anti-galling coating
US20090205714A1 (en) * 2006-05-24 2009-08-20 Kuehnlein Holger Metal Plating Composition and Method for the Deposition of Copper-Zinc-Tin Suitable for Manufacturing Thin Film Solar Cell

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
Tanaka et al., "Preparation of Cu2ZnSnS4 thin films by sulfurizing sol-gel deposited precursors", Solar Energy Materials & Solar Cells 91, pp. 1199-1201, 2007. *

Cited By (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9041141B2 (en) 2010-09-09 2015-05-26 International Business Machines Corporation Structure and method of fabricating a CZTS photovoltaic device by electrodeposition
US8426241B2 (en) * 2010-09-09 2013-04-23 International Business Machines Corporation Structure and method of fabricating a CZTS photovoltaic device by electrodeposition
US8790956B2 (en) 2010-09-09 2014-07-29 International Business Machines Corporation Structure and method of fabricating a CZTS photovoltaic device by electrodeposition
US20120061790A1 (en) * 2010-09-09 2012-03-15 International Business Machines Corporation Structure and Method of Fabricating a CZTS Photovoltaic Device by Electrodeposition
US20120255488A1 (en) * 2011-04-07 2012-10-11 Dynamic Micro Systems, Semiconductor Equipment Gmbh Methods and apparatuses for roll-on coating
US8739728B2 (en) * 2011-04-07 2014-06-03 Dynamic Micro Systems, Semiconductor Equipment Gmbh Methods and apparatuses for roll-on coating
US20130224902A1 (en) * 2012-02-24 2013-08-29 Industry-Academic Cooperation Foundation, Yeungnam University Method of manufacturing photovoltaic cell
US9076917B2 (en) * 2012-02-24 2015-07-07 Industry-Academic Cooperation Foundation, Yeungnam University Method of manufacturing photovoltaic cell
US20150144177A1 (en) * 2012-10-04 2015-05-28 International Business Machines Corporation Solution processing of kesterite semiconductors
US20140096826A1 (en) * 2012-10-04 2014-04-10 International Business Machines Corporation Solution processing of kesterite semiconductors
US9252304B2 (en) * 2012-10-04 2016-02-02 International Business Machines Corporation Solution processing of kesterite semiconductors
US8980682B2 (en) * 2013-03-13 2015-03-17 Intermolecular, Inc. Methods for fabricating ZnOSe alloys
US20140273333A1 (en) * 2013-03-13 2014-09-18 Intermolecular Inc. Methods for fabricating ZnOSe alloys
US20160133768A1 (en) * 2013-08-01 2016-05-12 Lg Chem, Ltd. Ink composition for manufacturing light absorption layer of solar cells and method of manufacturing thin film using the same
US9876131B2 (en) * 2013-08-01 2018-01-23 Lg Chem, Ltd. Ink composition for manufacturing light absorption layer of solar cells and method of manufacturing thin film using the same
US9601642B1 (en) * 2014-09-29 2017-03-21 EWHA University—Industry Collaboration Foundation CZTSe-based thin film and method for preparing the same, and solar cell using the same
US10340402B2 (en) 2014-11-13 2019-07-02 Lg Chem, Ltd. Method of preparing metal chalcogenide nanoparticles and method of producing light absorption layer thin film based thereon
US10418498B2 (en) 2014-11-13 2019-09-17 Lg Chem, Ltd. Method of preparing metal chalcogenide nanoparticles and method of producing light absorption layer thin film based thereon
US11162024B2 (en) 2016-03-18 2021-11-02 Osaka University Semiconductor nanoparticles and method of producing semiconductor nanoparticles
US11788003B2 (en) 2016-03-18 2023-10-17 Osaka University Semiconductor nanoparticles and method of producing semiconductor nanoparticles

Also Published As

Publication number Publication date
JP2012527402A (ja) 2012-11-08
WO2010135622A1 (fr) 2010-11-25
US20120061628A1 (en) 2012-03-15
EP2432842A1 (fr) 2012-03-28
TW201107241A (en) 2011-03-01
EP2432841A1 (fr) 2012-03-28
CN102439098A (zh) 2012-05-02
JP2012527401A (ja) 2012-11-08
US9112094B2 (en) 2015-08-18
CN102439097A (zh) 2012-05-02
JP2012527523A (ja) 2012-11-08
KR20120036872A (ko) 2012-04-18
EP2432840A1 (fr) 2012-03-28
KR20120030434A (ko) 2012-03-28
WO2010135667A1 (fr) 2010-11-25
WO2010135665A1 (fr) 2010-11-25
CN102439096A (zh) 2012-05-02
KR20120028933A (ko) 2012-03-23

Similar Documents

Publication Publication Date Title
US9112094B2 (en) Copper tin sulfide and copper zinc tin sulfide ink compositions
US8366975B2 (en) Atypical kesterite compositions
US20140144500A1 (en) Semiconductor inks films, coated substrates and methods of preparation
US20130233202A1 (en) Inks and processes for preparing copper indium gallium sulfide/selenide coatings and films
US9105796B2 (en) CZTS/Se precursor inks and methods for preparing CZTS/Se thin films and CZTS/Se-based photovoltaic cells
US20130264526A1 (en) Molecular precursors and processes for preparing copper indium gallium sulfide/selenide coatings and films
US20150118144A1 (en) Dispersible metal chalcogenide nanoparticles
US20130221489A1 (en) Inks and processes to make a chalcogen-containing semiconductor
TWI431073B (zh) 硒／１ｂ族油墨及其製造及使用方法
JP4536443B2 (ja) カルコゲニド（ｃｈａｌｃｏｇｅｎｉｄｅ）皮膜の溶液堆積
KR101840303B1 (ko) 셀레늄/1ｂ족/3ａ족 잉크, 및 그의 제조방법 및 사용방법
TWI432532B (zh) 硒油墨及其製造及使用方法
US20140048137A1 (en) Process for preparing coated substrates and photovoltaic devices
US20130292800A1 (en) Processes for preparing copper indium gallium sulfide/selenide films
Valls et al. Easy and low-cost aqueous precipitation method to obtain Cu2ZnSn (S, Se) 4 thin layers
Prabeesh et al. Influence of thiourea in the precursor solution on the structural, optical and electrical properties of CZTS thin films deposited via spray coating technique
Gupta et al. Evaluating the role of precursor concentration in facile conformal coating of sub-micrometer thick Cu2ZnSnS4 films using non-toxic ethanol based solutions
TW201401344A (zh) 半導體膜之製備

Legal Events

Date Code Title Description
STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION