RU2007119381A - Изделие производства и способ анодного нанесения покрытия из оксидной керамики на алюминий и/или титан - Google Patents
Изделие производства и способ анодного нанесения покрытия из оксидной керамики на алюминий и/или титан Download PDFInfo
- Publication number
- RU2007119381A RU2007119381A RU2007119381/02A RU2007119381A RU2007119381A RU 2007119381 A RU2007119381 A RU 2007119381A RU 2007119381/02 A RU2007119381/02 A RU 2007119381/02A RU 2007119381 A RU2007119381 A RU 2007119381A RU 2007119381 A RU2007119381 A RU 2007119381A
- Authority
- RU
- Russia
- Prior art keywords
- water
- titanium
- anodizing solution
- product
- aluminum
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D11/00—Electrolytic coating by surface reaction, i.e. forming conversion layers
- C25D11/02—Anodisation
- C25D11/04—Anodisation of aluminium or alloys based thereon
- C25D11/06—Anodisation of aluminium or alloys based thereon characterised by the electrolytes used
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D11/00—Electrolytic coating by surface reaction, i.e. forming conversion layers
- C25D11/02—Anodisation
- C25D11/024—Anodisation under pulsed or modulated current or potential
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D11/00—Electrolytic coating by surface reaction, i.e. forming conversion layers
- C25D11/02—Anodisation
- C25D11/026—Anodisation with spark discharge
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D11/00—Electrolytic coating by surface reaction, i.e. forming conversion layers
- C25D11/02—Anodisation
- C25D11/04—Anodisation of aluminium or alloys based thereon
- C25D11/06—Anodisation of aluminium or alloys based thereon characterised by the electrolytes used
- C25D11/08—Anodisation of aluminium or alloys based thereon characterised by the electrolytes used containing inorganic acids
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D11/00—Electrolytic coating by surface reaction, i.e. forming conversion layers
- C25D11/02—Anodisation
- C25D11/26—Anodisation of refractory metals or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
- C25D5/18—Electroplating using modulated, pulsed or reversing current
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
- C25D5/60—Electroplating characterised by the structure or texture of the layers
- C25D5/615—Microstructure of the layers, e.g. mixed structure
- C25D5/617—Crystalline layers
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
- C25D5/627—Electroplating characterised by the visual appearance of the layers, e.g. colour, brightness or mat appearance
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
- Y10T428/12611—Oxide-containing component
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
- Y10T428/12611—Oxide-containing component
- Y10T428/12618—Plural oxides
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12736—Al-base component
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12736—Al-base component
- Y10T428/12743—Next to refractory [Group IVB, VB, or VIB] metal-base component
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12771—Transition metal-base component
- Y10T428/12806—Refractory [Group IVB, VB, or VIB] metal-base component
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/31504—Composite [nonstructural laminate]
- Y10T428/3154—Of fluorinated addition polymer from unsaturated monomers
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/31504—Composite [nonstructural laminate]
- Y10T428/3154—Of fluorinated addition polymer from unsaturated monomers
- Y10T428/31544—Addition polymer is perhalogenated
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/31504—Composite [nonstructural laminate]
- Y10T428/31652—Of asbestos
- Y10T428/31663—As siloxane, silicone or silane
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Electrochemistry (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Engineering & Computer Science (AREA)
- Crystallography & Structural Chemistry (AREA)
- Inorganic Chemistry (AREA)
- Chemical Treatment Of Metals (AREA)
- Other Surface Treatments For Metallic Materials (AREA)
- Application Of Or Painting With Fluid Materials (AREA)
- Coating By Spraying Or Casting (AREA)
Claims (43)
1. Способ формирования защитного покрытия на поверхности изделия из алюминия, алюминиевого сплава, титана или титанового сплава, включающий в себя
A) обеспечение раствора для анодирования, образованного водой, фосфорсодержащей кислотой и/или солью и одним или более дополнительными компонентами, выбранными из группы, состоящей из
a) водорастворимых комплексных фторидов,
b) водорастворимых комплексных оксифторидов,
c) вододиспергируемых комплексных фторидов, и
d) вододиспергируемых комплексных оксифторидов
элементов, выбранных из группы, состоящей из Ti, Zr, Hf, Sn, Al, Ge и B и их смесей;
B) обеспечение катода в контакте с упомянутым раствором для анодирования;
C) размещение изделия из алюминия, алюминиевого сплава, титана или титанового сплава в качестве анода в упомянутом растворе для анодирования; и
D) пропускание тока между анодом и катодом через упомянутый раствор для анодирования в течение времени, эффективного для формирования защитного покрытия на по меньшей мере одной поверхности изделия.
2. Способ по п.1, в котором изделие содержит преимущественно титан.
3. Способ по п.1, в котором изделие содержит преимущественно алюминий, а защитное покрытие является преимущественно диоксидом титана.
4. Способ по п.1, в котором защитное покрытие содержит преимущественно оксиды Ti, Zr, Hf, Sn, Ge и/или B.
5. Способ по п.1, в котором защитное покрытие образовано преимущественно диоксидом титана.
6. Способ по п.1, в котором упомянутый ток является постоянным током со средним напряжением не более 200 В.
7. Способ по п.1, в котором во время этапа (D) упомянутое защитное покрытие формируют при скорости по меньшей мере 1 мкн толщины в минуту.
8. Способ по п.1, в котором упомянутый ток является постоянным током или переменным током.
9. Способ по п.1, в котором упомянутый раствор для анодирования содержит воду, фосфорсодержащую кислоту и водорастворимые и/или вододиспергируемые комплексные фториды Ti и/или Zr.
10. Способ по п.1, в котором раствор для анодирования имеет pH 1-6.
11. Способ по п.1, в котором раствор для анодирования приготавливают с использованием комплексного фторида, выбранного из группы, состоящей из H2TiF6, H2ZrF6, H2HfF6, H2GeF6, H2SnF6, H3AlF6, HBF4 и их солей и смесей.
12. Способ по п.11, в котором раствор для анодирования дополнительно содержит HF или ее соль.
13. Способ по п.1, в котором раствор для анодирования дополнительно содержит хелатообразующий агент.
14. Способ по п.1, в котором упомянутая фосфорсодержащая кислота и/или соль присутствует в концентрации, измеренной как P, от 0,01 до 0,25 М.
15. Способ формирования защитного покрытия на поверхности металлического изделия, образованного преимущественно алюминием или титаном, включающий в себя
A) обеспечение раствора для анодирования, образованного водой, фосфорсодержащей кислородсодержащей кислотой и/или солью и водорастворимым комплексным фторидом и/или оксифторидом элемента, выбранного из группы, состоящей из Ti, Zr и их комбинаций;
B) обеспечение катода в контакте с упомянутым раствором для анодирования;
C) размещение металлического изделия, образованного преимущественно алюминием или титаном, в качестве анода в упомянутом растворе для анодирования; и
D) пропускание постоянного тока или переменного тока между анодом и катодом в течение времени, эффективного для формирования защитного покрытия, содержащего оксиды Ti и/или Zr, на по меньшей мере одной поверхности металлического изделия.
16. Способ по п.15, в котором раствор для анодирования приготавливают с использованием комплексного фторида, содержащего анион, содержащий по меньшей мере 4 атома фтора и по меньшей мере один атом, выбранный из группы, состоящей из Ti, Zr и их комбинаций.
17. Способ по п.15, в котором раствор для анодирования приготавливают с использованием комплексного фторида, выбранного из группы, состоящей из H2TiF6, H2ZrF6 и их солей и смесей.
18. Способ по п.15, в котором упомянутый комплексный фторид вводят в раствор для анодирования в концентрации по меньшей мере 0,01 М.
19. Способ по п.15, в котором постоянный ток имеет среднее напряжение не более 250 вольт.
20. Способ по п.15, в котором раствор для анодирования дополнительно содержит хелатообразующий агент.
21. Способ по п.15, в котором раствор для анодирования содержит по меньшей мере один комплексный оксифторид, полученный объединением по меньшей мере одного комплексного фторида по меньшей мере одного элемента, выбранного из группы, состоящей из Ti и Zr, и по меньшей мере одного соединения, которое является оксидом, гидроксидом, карбонатом или алкоголятом по меньшей мере одного элемента, выбранного из группы, состоящей из Ti, Zr, Hf, Sn, B, Al и Ge.
22. Способ по п.15, в котором раствор для анодирования имеет pH от 2 до 6.
23. Способ формирования защитного покрытия на изделии, имеющем по меньшей мере одну металлическую поверхность, образованную титаном, титановым сплавом, алюминием или алюминиевым сплавом, включающий в себя
A) обеспечение раствора для анодирования, причем упомянутый раствор для анодирования был приготовлен растворением водорастворимого комплексного фторида и/или оксифторида элемента, выбранного из группы, состоящей из Ti, Zr, Hf, Sn, Ge, B и их комбинаций, и кислоты и/или соли, которая содержит фосфор, в воде;
B) обеспечение катода в контакте с упомянутым раствором для анодирования;
C) размещение упомянутой металлической поверхности, образованной титаном, титановым сплавом, алюминием или алюминиевым сплавом, в качестве анода в упомянутом растворе для анодирования; и
D) пропускание постоянного тока или переменного тока между анодом и катодом в течение времени, эффективного для формирования защитного покрытия на упомянутой металлической поверхности изделия.
24. Способ по п.23, в котором pH раствора для анодирования регулируют, используя аммиак, амин, гидроксид щелочного металла или их смесь.
25. Способ по п.23, в котором упомянутая фосфорсодержащая кислота и/или соль присутствуют в концентрации, измеренной как P, от 0,01 до 0,25 М.
26. Способ по п.23, в котором раствор для анодирования дополнительно содержит хелатообразующий агент.
27. Способ по п.23, в котором для приготовления упомянутого раствора для анодирования дополнительно используют по меньшей мере одно соединение, которое является оксидом, гидроксидом, карбонатом или алкоголятом по меньшей мере одного элемента, выбранного из группы, состоящей из Ti, Zr, Si, Hf, Sn, B, Al и Ge.
28. Способ по п.23, в котором защитное покрытие содержит преимущественно оксиды Ti, Zr, Hf, Sn, Ge и/или B.
29. Способ по п.23, в котором для приготовления раствора для анодирования используют одно или более из H2TiF6, солей H2TiF6, H2ZrF6 и солей H2ZrF6.
30. Способ по п.27, в котором для приготовления раствора для анодирования используют основный карбонат циркония.
31. Способ по п.23, в котором упомянутый один или более водорастворимых комплексных фторидов является комплексным фторидом титана, а ток является постоянным током.
32. Изделие производства, содержащее
a) подложку, имеющую по меньшей мере одну поверхность, содержащую достаточно алюминия и/или титана для того, чтобы действовать в качестве анода при пиковых напряжениях по меньшей мере 300 В;
b) сцепленный защитный слой, преимущественно содержащий по меньшей мере один оксид элементов, выбранных из группы, состоящей из Ti, Zr, Hf, Ge, B и их смесей, связанный с упомянутой по меньшей мере одной поверхностью; упомянутый защитный слой также содержит фосфор в количествах, измеренных как P, менее 10%.
33. Изделие по п.32, в котором сцепленный защитный слой образован преимущественно диоксидом титана.
34. Изделие по п.32, в котором сцепленный защитный слой образован смесью диоксида титана и оксида циркония.
35. Изделие по п.32, дополнительно содержащее слой краски, нанесенный на сцепленный защитный слой.
36. Изделие по п.32, причем это изделие производства представляет собой автомобильный колесный диск, образованный преимущественно алюминием.
37. Изделие по п.36, в котором сцепленный защитный слой образован преимущественно диоксидом циркония.
38. Изделие по п.36, дополнительно содержащее по меньшей мере один слой краски, нанесенный на защитный слой.
39. Изделие по п.38, в котором упомянутый по меньшей мере один слой краски содержит прозрачное покрытие.
40. Изделие по п.32, причем это изделие производства образовано преимущественно титаном.
41. Изделие по п.33, причем это изделие производства представляет собой составную конструкцию, имеющую первую часть, образованную преимущественно алюминием, и вторую часть, образованную преимущественно титаном.
42. Способ формирования защитного покрытия на изделии, имеющем по меньшей мере одну поверхность, содержащую алюминий и/или титан, причем этот способ включает в себя
A) обеспечение раствора для анодирования, образованного водой, фосфорсодержащей кислотой и/или солью и одним или более дополнительными компонентами, выбранными из группы, состоящей из
a) водорастворимых и/или вододиспергируемых комплексных фторидов элементов, выбранных из группы, состоящей из Ti, Zr, Hf, Sn, Al, Ge и B;
b) водорастворимых и/или вододиспергируемых солей циркония и кислородсодержащей кислоты;
c) водорастворимых и/или вододиспергируемых солей ванадия и кислородсодержащей кислоты;
d) водорастворимых и/или вододиспергируемых солей титана и кислородсодержащей кислоты;
e) водорастворимых и/или вододиспергируемых солей ниобия;
f) водорастворимых и/или вододиспергируемых солей молибдена;
g) водорастворимых и/или вододиспергируемых солей марганца; и
h) водорастворимых и/или вододиспергируемых солей вольфрама;
B) обеспечение катода в контакте с упомянутым раствором для анодирования;
C) размещение изделия, имеющего по меньшей мере одну поверхность, содержащую алюминий и/или титан, в качестве анода в упомянутом растворе для анодирования; и
D) пропускание тока между анодом и катодом через упомянутый раствор для анодирования в течение времени, эффективного для формирования защитного покрытия на по меньшей мере одной поверхности изделия.
43. Способ по п.42, в котором pH составляет 2-6, и раствор для анодирования дополнительно содержит водорастворимые и/или вододиспергируемые фториды и/или гидроксиды щелочного металла.