JP2001146419A - 熱分解法により得られた広い表面積の酸化アルミニウムおよびその使用 - Google Patents
熱分解法により得られた広い表面積の酸化アルミニウムおよびその使用Info
- Publication number
- JP2001146419A JP2001146419A JP2000272066A JP2000272066A JP2001146419A JP 2001146419 A JP2001146419 A JP 2001146419A JP 2000272066 A JP2000272066 A JP 2000272066A JP 2000272066 A JP2000272066 A JP 2000272066A JP 2001146419 A JP2001146419 A JP 2001146419A
- Authority
- JP
- Japan
- Prior art keywords
- surface area
- aluminum oxide
- pyrolysis
- oxide obtained
- industry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
ェット用紙またはインクジェットフィルムへの使用の際
にインクを迅速に吸収し、色に高度な明るさを与えるた
めに、簡単に分散可能な充填剤が必要とされる。 【解決手段】 熱分解法により得られた広い表面積の酸
化アルミニウムにおいて、BETによる比表面積が11
5m2/gを上廻り、シアーズ数が8ml/2gを上廻
る。
Description
られた酸化アルミニウム、その製造法ならびにその使用
に関する。
クジェット用紙またはインクジェットフィルムへの使用
の際にインクを迅速に吸収し、色に高度な明るさを与え
るために、簡単に分散可能な充填剤が必要とされる。
載された課題が課された。
れた酸化アルミニウムに関し、この酸化アルミニウム
は、相応する刷毛塗り用塗料受容体における酸化アルミ
ニウムの性質によって、この特殊な酸化アルミニウムを
含有する前記媒体上にインクジェットプリンターによっ
て塗布されるインクが極めて高度な色の明るさおよび色
の忠実さを再現する状態にある。
えば、紙、シート、物質等)で常用されているようなイ
ンク受容層の製造の際の前記酸化アルミニウムの使用に
関する。
115m2/gを上廻り、シアーズ数が8ml/2gを
上廻ることによって特徴付けられている、熱分解法によ
り得られた広い表面積の酸化アルミニウムである。
ルミニウムは、秤量分16gを用いて測定された粉末の
ジブチルフタレート吸収量が測定不可能である(最終点
での検出なし)ことによって特徴付けられている。
アルミニウムは、フレーム酸化または好ましくはフレー
ム加水分解の方法により製造されてよく、この場合出発
材料としては、蒸発可能なアルミニウム化合物、好まし
くは塩化物が利用される。
ト媒体中のインク吸収物質としての本発明による酸化ア
ルミニウムの使用である。
材料として、触媒活性の物質として、分散液を製造する
ための出発物質として、研磨材料として(CMPの使
用)、セラミックの基材として、電子工業において、化
粧品工業において、シリコーン工業およびゴム工業にお
ける添加剤として、液状系のレオロジーの調整のため、
耐熱安定化のため、ラッカー工業においての広い表面積
の本発明による酸化アルミニウムの使用である。
られた本発明による酸化アルミニウムは、次の性質を有
する:ポイント活字の良好な光学的密度および分解能、
高いインク吸収量、迅速なインク乾燥時間、滲み(イン
クの互いの中への滲入)、乾燥後の良好な水安定性、色
の移動なし、長時間後のインクの破壊なし。
ニウム(Aluminiumoxid)Cおよびエーロジル(Aerosi
l)MOX 170、)と比較して、本発明による酸化
アルミニウムは、インクジェット媒体受容層の製造の際
に単独ならびに別の充填剤との組合せで極めて良好な性
質を示す。この酸化アルミニウムは、よりいっそう高度
な色の明るさおよび色の濃さを示す。この性質は、特に
写真のような写実性を再現するために使用されるインク
受容層の場合に必要とされる。また、水および光に対す
る耐候性は向上されており、このことは、屋外での使用
の際に有利である。
アルミニウム320kg/h(AlCl3)を水素10
0Nm3/hおよび空気450Nm3/hと一緒に燃焼さ
せる。
レーム反応後に濾過装置またはサイクロン中で同時に生
成された塩酸ガスと分離し、この場合には、引続きなお
付着するHCl痕跡を湿った空気を用いて高められた温
度での処理によって除去する。
法酸化アルミニウムは、第1表に示された物理化学的特
性データを有する。第1表中には、比較のためにデグッ
サ−ヒュルス社(Degussa-Huels)社/フランクフルト
(Frankfurt)の商業的に入手可能な熱分解法酸化アル
ミニウムのデータが一緒に記載されている。(商品名Al
uminiumoxid C)
特許第0717008号明細書に記載されている。
99 30質量部(Clariant)、サイパーナート(Sipe
rnat)310 80質量部(沈降珪酸、Degussa-Huels
AG)および熱分解法により得られた上記の酸化物それぞ
れ20質量部を使用する。固体含量を18%に調節す
る。この水性分散液をディスソルバーを用いて3000
rpmで30分間攪拌する。この刷毛塗り用塗料を異形
成形されたドクターブレードを用いて原紙70g/m2
上に塗布する。刷毛塗り用塗料を熱風で乾燥させる。塗
装質量は、乾燥状態で10g/m2である。
オール(Mowiol)28−99 35質量部(Clariant)
および熱分解法により得られた上記の酸化物それぞれ1
00質量部を使用する。固体含量を15%に調節する。
この分散液を均質化する。この刷毛塗り用塗料を異形成
形されたドクターブレードを用いて厚さ100μmのポ
リエステルフィルム上に塗布する。刷毛塗り用塗料を熱
風で乾燥させる。湿式膜厚は、120μmである。
オール(Mowiol)5−88 70質量部(Clariant)、
PVP/VA W−735 20質量部(ポリビニルピ
ロリドン−ポリビニルアセテート共重合体、ISP)、
ポリビニルピロリドン K−30 10部(ISP)お
よび熱分解法により得られた上記の酸化物それぞれ50
部を使用する。
り用塗料を異形成形されたドクターブレードを用いて8
0μmの湿式膜厚で厚さ100μmのポリエステルフィ
ルム上に塗布する。刷毛塗り用塗料を熱風で乾燥させ
る。
ム Alu 130の使用技術的利点を示す。
ウム130とともに、なお酸化アルミニウムC(Alumin
iumoxid C)およびMOX 170(双方ともDegussa-H
uels AG Frankfurt)を使用する。
は、ポリビニルアルコール(固体、略符号PVA) Cl
ariant社のモヴィオール(Mowiol)28−99の(PV
Aに対して)10%の水溶液である。
Bを生成する。この溶液にサイパーナート(Sipernat)
310 80質量部(沈降珪酸、Degussa-Huels AG)お
よびそれぞれ熱分解法により得られた酸化物を刷毛塗り
用塗料Cの形成のために添加する。この刷毛塗り用塗料
は、固体に対してサイパーナート(Sipernat)3108
0部と熱分解法酸化物20部とPVA30部の質量比を
有する。全固体含量は、18%である。
て3000rpmで30分間分散させる。引続き、刷毛
塗り用塗料を異形成形されたドクターブレードを用いて
原紙70g/m2上に塗布し、熱風で乾燥させる。塗装
質量は、乾燥状態で10g/m2である。
0dpi)を有するエプソンスタイラスカラー(Epson
Stylus Colour)800上で試験する。
よる酸化アルミニウム130とともに、なお酸化アルミ
ニウムCおよびMOX170(双方ともDegussa-Huels
AG Frankfurt)を使用する。
性分散液を得る。これは、回転子−固定子系(Ultra-Tu
rrax)を使用しながら30分間の分散時間で二重壁容器
(水冷で)中で行なわれる。酢酸0.5%の質量分を有
する、(固体に対して)25%の分散液(w=0.2
5)を得る。
ニルアルコール(固体、略符号PVA) Clariant社の
モヴィオール(Mowiol)40−88の(PVAに対し
て)8%の水溶液である。
液Bを生成する。この溶液Bにそれぞれ種々の金属酸化
物分散液を添加し、刷毛塗り用塗料Cを形成させる。刷
毛塗り用塗料Cは、固体物質に対して熱分解法酸化物1
00部とPVA25部との質量比を有する。全固体含量
は、15%である。この刷毛塗り用塗料を異形成形され
たドクターブレードを用いて厚さ100μmのポリエス
テルフィルム上に塗布し、熱風で乾燥させる。湿式膜厚
は、120μmである。
用いた場合には、付着する被膜を製造することは不可能
であった。この混合酸化物のためには、この含量を固体
物質の割合に対してエーロジル100部対PVA40部
の比になるまで高めなければならない。
よる酸化アルミニウム130とともに、なお酸化アルミ
ニウムCおよびMOX170(双方ともDegussa-Huels
AG Frankfurt)を使用する。
ール(固体、略符号PVA)4−88の(PVAに対し
て)20%の水溶液である。
ビニルアセテートとからなる共重合体(略符号PVP/
VA)の(共重合体に対して)50%の水溶液である。
ン(略符号PVP)の(PVPに対して)20%の水溶
液である。
割合で混合し(固体に対してPVA70質量部:PVP
/VA20部:PVP10部)、水で希釈し、したがっ
てそれぞれ金属酸化物50部の添加の際に、20%の全
固体含量を有する刷毛塗り用塗料を得る。この分散液
を、適当な分散装置、例えば回転子−固定子系を有する
ヤンケウントクンケル社(Janke und Kunkel)のウルト
ラ−ターラックス(Ultra-Turrax)を用いて10000
rpmで30分間分散させる。刷毛塗り用塗料を異形成
形されたドクターブレードを用いて80μmの湿式膜厚
で厚さ100μmのポリエステルフィルム上に塗布し、
熱風で乾燥させる。
xid CおよびAerosil MOX 170、双方ともDegussa-Hu
els AG)と比較して、本発明による酸化アルミニウム
は、単独ならびに別の充填剤との組合せでインクジェッ
ト受容層の製造の際に極めて良好な性質を示す。この酸
化アルミニウムは、高度な色の明るさおよび色の濃さを
示す。この性質は、特に写真のような写実性を再現する
ために使用されるインク受容層の場合に必要とされる。
また、水および光に対する耐候性は向上されており、こ
のことは、屋外での使用の際に有利である。
Claims (5)
- 【請求項1】 熱分解法により得られた広い表面積の酸
化アルミニウムにおいて、BETによる比表面積が11
5m2/gを上廻り、シアーズ数が8ml/2gを上廻
ることを特徴とする、熱分解法により得られた広い表面
積の酸化アルミニウム。 - 【請求項2】 秤量分16gを用いて測定された粉末の
ジブチルフタレート吸収量が測定不可能である(最終点
での検出なし)、請求項1記載の熱分解法により得られ
た酸化アルミニウム。 - 【請求項3】 フレーム酸化または好ましくはフレーム
加水分解の方法により製造され、この場合出発材料とし
ては、蒸発可能なアルミニウム化合物、好ましくは塩化
物が利用される、請求項1または2記載の熱分解法によ
り得られた酸化アルミニウム。 - 【請求項4】 インクジェット媒体中のインク吸収物質
としての請求項1記載の広い表面積の酸化アルミニウム
の使用。 - 【請求項5】 充填剤として、担持材料として、触媒活
性の物質として、分散液を製造するための出発物質とし
て、研磨材料として(CMPの使用)、セラミックの基
材として、電子工業において、化粧品工業において、シ
リコーン工業およびゴム工業における添加剤として、液
状系のレオロジーの調整のため、耐熱安定化のため、ラ
ッカー工業においての請求項1記載の広い表面積の酸化
アルミニウムの使用。