Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F2/00—Processes of polymerisation
  • C08F2/12—Polymerisation in non-solvents
  • C08F2/16—Aqueous medium
  • C08F2/22—Emulsion polymerisation
  • C08F2/24—Emulsion polymerisation with the aid of emulsifying agents
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
  • C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
  • C08F220/10—Esters
  • C08F220/12—Esters of monohydric alcohols or phenols
  • C08F220/14—Methyl esters, e.g. methyl (meth)acrylate
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
  • C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
  • C08F220/10—Esters
  • C08F220/20—Esters of polyhydric alcohols or phenols, e.g. 2-hydroxyethyl (meth)acrylate or glycerol mono-(meth)acrylate
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F236/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds
  • C08F236/02—Copolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds the radical having only two carbon-to-carbon double bonds
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F236/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds
  • C08F236/02—Copolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds the radical having only two carbon-to-carbon double bonds
  • C08F236/04—Copolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds the radical having only two carbon-to-carbon double bonds conjugated
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K3/00—Use of inorganic substances as compounding ingredients
  • C08K3/18—Oxygen-containing compounds, e.g. metal carbonyls
  • C08K3/20—Oxides; Hydroxides
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
  • C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
  • C08F220/10—Esters
  • C08F220/38—Esters containing sulfur
  • C08F220/382—Esters containing sulfur and containing oxygen, e.g. 2-sulfoethyl (meth)acrylate
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F222/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a carboxyl radical and containing at least one other carboxyl radical in the molecule; Salts, anhydrides, esters, amides, imides, or nitriles thereof
  • C08F222/10—Esters
  • C08F222/1006—Esters of polyhydric alcohols or polyhydric phenols
  • C08F222/102—Esters of polyhydric alcohols or polyhydric phenols of dialcohols, e.g. ethylene glycol di(meth)acrylate or 1,4-butanediol dimethacrylate
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F222/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a carboxyl radical and containing at least one other carboxyl radical in the molecule; Salts, anhydrides, esters, amides, imides, or nitriles thereof
  • C08F222/10—Esters
  • C08F222/1006—Esters of polyhydric alcohols or polyhydric phenols
  • C08F222/103—Esters of polyhydric alcohols or polyhydric phenols of trialcohols, e.g. trimethylolpropane tri(meth)acrylate

Definitions

• the present invention relates to an emulsion polymerization method using a reactive emulsifier, and to an aqueous polymer dispersion and a polymer film obtained thereby.
• the protection of objects includes anti-corrosion, anti-stain, waterproof, chemical-resistant, fire-resistant, pest repellent and antibacterial, etc.
• aesthetics include smoothing, glossing, coloring, pattern, design
• the creation of landscapes, etc., and the addition of functionality include the provision of performances such as adhesion, adhesion, water / oil repellency, light control, heat control, and adsorption.
• the emulsion polymerization method is an extremely effective method for industrial production of polymer dispersions, but the emulsifier (surfactant), which is an essential component, is present in the free state in the system.
• the emulsifier which is an essential component
• foam troubles may be caused and production efficiency may be reduced.
• the air bubbles generated in these steps remain until the polymer dispersion treatment step, the strength properties, protective properties, cosmetics, functional properties, etc. of the coating film are adversely affected, leading to a reduction in commercial value. There is a case.
• the wastewater load due to the outflow of the surfactant is also a problem.
• the reactive emulsifier When preparing a polymer dispersion by an emulsion polymerization method using a reactive emulsifier having a radical polymerizable group, the reactive emulsifier is used in the initial stage from the start of polymerization to form micelles and monomers as in the case of general surfactants. It contributes to solubilization and emulsification, and it is considered that the reactive emulsifier itself is copolymerized with monomers in the system and contributes to the stabilization of dispersion of polymer particles in the middle to late stages of polymerization.
• the reactive emulsifier has a reactive group because it has a function as an emulsifier in the emulsion polymerization process and is itself copolymerized with a monomer in the system and fixed to the polymer skeleton by a chemical bond.
• the amount of emulsifier (surfactant) present in the polymer dispersion in a free state is greatly reduced compared to the case where a conventional emulsifier is not used, eliminating the above-mentioned foam trouble, improving the water resistance of the coating film, and wastewater This contributes to reducing the load.
• the use of reactive emulsifiers greatly improved various problems caused by conventional emulsifiers, but the reaction rate of reactive emulsifiers in the system depends on the reactive emulsifier species, monomer species, polymerization conditions, etc. Since the (copolymerization ratio with the monomer) is low and many free emulsifiers remain in the system, there are cases in which such problems cannot be solved.
• the combination of the monomer used and the reactive emulsifier causes a decrease in monomer conversion, a change in molecular weight distribution (increase in polydispersity), an increase in the amount of oligomer, etc.
• Various physical properties of the polymer coating film may be reduced, and the use of reactive emulsifiers has not always sufficiently solved various practical problems.
• the use of reactive emulsifiers has not always sufficiently solved various practical problems.
• the amount of by-product oligomers increases during the emulsion polymerization process, it may be difficult to defoam the air bubbles generated in the polymerization process and subsequent processes using conventional antifoaming agents. It was.
• the polymer dispersion prepared by the emulsion polymerization method is usually used for i) coating film formation as a paint or a pressure-sensitive adhesive, or ii) solid polymer recovery using a precipitating agent, but each has the following problems. .
• the most important requirement for its use is to improve water resistance. Even when a reactive emulsifier is used, its own reaction rate (copolymerization rate with monomers) ) Is low, it may adversely affect the water resistance of the coating film. Specifically, when the coating film is brought into contact with water, or when the coating film is placed in water, a whitening (white turbidity) phenomenon of the coating film, a water absorption / swelling phenomenon, a decrease in adhesive strength, and the like may occur.
• the solid polymer is recovered from the dispersion or latex by a precipitation step such as a salting-out method or an acid precipitation method.
• the solid polymer is solidified by the free emulsifier or the precipitation step.
• the oligomers that were not obtained flowed into the aqueous waste liquid at the time of washing the solid polymer with water or the accompanying production line, and there was a concern that the waste water load increased in the factory waste water treatment process. Further, mixing of these free emulsifiers and oligomers into the recovered solid polymer due to insufficient washing with water can cause hue deterioration during heating of the polymer.
• the present invention has been made in view of the above, and improves the copolymerization ratio of the reactive emulsifier with the monomer, thereby eliminating foam troubles, further improving the water resistance of the coating film, and wastewater for solid polymer recovery.
• An object of the present invention is to provide an emulsion polymerization method using a reactive emulsifier capable of solving various problems such as load reduction, an aqueous polymer dispersion free from foam trouble, and a polymer film having improved water resistance. .
• the reaction rate of the reactive emulsifier in the system is low, and a large amount of free emulsifier remains in the system or undesired by-products.
• the waste water load due to the discharged liquid is greatly reduced, and when the polymer coating is brought into contact with water, or when the coating is placed in water, the whitening (white turbidity) of the coating, water absorption / swelling,
• the purpose is to suppress a decrease in adhesive strength.
• the emulsion polymerization method of the present invention is an emulsion polymerization method in which a monomer is emulsion-polymerized using a reactive emulsifier in the presence of a polymerization initiator in an aqueous medium, and in order to solve the above problems, a carbon-carbon
• One or more polymerizable unsaturated monomers X having at least one double bond in the molecule and at least a polymerizable group represented by any one of the following chemical formulas (1) to (3) in the molecule
• R 1 represents hydrogen or a methyl group
• n represents an integer of 1 to 5.
• the polyfunctional monomer Z1 or the hydrophilic monomer Z2 includes at least one group represented by any one of the following chemical formulas (4) to (6) as a polymerizable unsaturated group in the molecule. It is preferable to have.
• R 2 in the formula (4) and R 3 in the formula (6) each represent a hydrogen atom or a methyl group
• n in the formula (4) represents an integer of 1 to 5.
• polyfunctional monomer Z1 examples include ethylene glycol diacrylate, ethylene glycol dimethacrylate, trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, 1,6-hexanediol diacrylate, 1,3-butylene glycol dimethacrylate, One or more selected from the group consisting of allyl cyanurate, trimethallyl cyanurate, triallyl isocyanurate, trimethallyl isocyanurate, and octaallyl sucrose can be suitably used.
• hydrophilic monomer Z2 examples include hydroxyethyl acrylate, hydroxyethyl methacrylate, 2- (2-hydroxyethoxy) ethyl acrylate, 2- (2-hydroxyethoxy) ethyl methacrylate, hydroxypropyl acrylate, hydroxypropyl methacrylate, 2- (2-hydroxypropoxy) propyl acrylate, 2- (2-hydroxypropoxy) propyl methacrylate, hydroxyethyl allyl ether, hydroxypropyl allyl ether, 2- (2-hydroxyethoxy) ethyl allyl ether, 2- (2-hydroxypropoxy)
• One or more selected from the group consisting of propyl allyl ether and methoxylated derivatives thereof can be suitably used.
• the effect of the present invention is particularly remarkably obtained.
• the polymer dispersion of the present invention is obtained by the emulsion polymerization method of the present invention.
• the polymer film of the present invention is obtained by drying the polymer dispersion obtained by the above emulsion polymerization method.
• incompatibility of the monomer species and / or polymerization conditions may adversely affect the copolymerizability of the reactive emulsifier and the monomer.
• the amount of the free emulsifier in the system remains, or when the content of undesired by-products increases, the problems caused by these are solved. More specifically, the following effects can be obtained.
• the copolymerizability of the reactive emulsifier with various monomers is improved.
• the copolymerizability of styrene when a styrene monomer is copolymerized using a reactive emulsifier having no nonylphenol skeleton is greatly improved.
• water-based polymer dispersion of this invention obtained by the emulsion polymerization method of the said invention becomes a thing by which the bubble trouble was eliminated as above-mentioned.
• the polymer film of the present invention obtained from the aqueous polymer dispersion has greatly improved water resistance as described above.
• polymer dispersion the polymer aqueous dispersion obtained by the emulsion polymerization method
• polymer film refers to both a coating film in a state formed on the surface of a substrate and a film obtained by peeling it from the substrate.
• Polymerizable unsaturated monomer X used in the present invention is not particularly limited.
• methacrylic esters such as 2-ethylhexyl methacrylate, nonyl methacrylate, decyl methacrylate, undecyl methacrylate, lauryl methacrylate, tridecyl methacrylate, stearyl methacrylate, glycidyl methacrylate, acrylonitrile, methacrylonitrile, acrylamide
• Examples include methacrylamide, acrylic acid, methacrylic acid and the like.
• Aromatic monomers such as styrene, ⁇ -methylstyrene, vinyltoluene, dimethylstyrene, tert-butylstyrene, divinylbenzene, sodium styrenesulfonate, vinyl acetate, VeoVa® 9 (neononanoic acid vinyl ester, MOMENTIVE ), VeoVa (registered trademark) 10 (neodecanoic acid vinyl ester, MOMENTIVE), etc., vinyl chloride, vinylidene chloride, vinyl fluoride, vinylidene fluoride, trichloroethylene, tetrafluoroethylene, 2-chloropropene, 2 -Halogenated olefin monomers such as fluorinated propene and hexafluoropropene; conjugated diolefin monomers such as butadiene, isoprene and chloroprene; ethylene, maleic anhydride, male Methy
• These monomers may be used alone or in combination of two or more.
• acrylic acid esters, methacrylic acid esters, styrene, conjugated diolefin monomers and the like can be suitably used, and the effect of the present invention is remarkably exhibited particularly when styrene is used as one of the copolymerization monomers. .
• the reactive emulsifier Y used in the present invention has at least one polymerizable group represented by the following chemical formulas (1) to (3) in the molecule as described above, and in the formula (1), R 1 is hydrogen or Represents a methyl group, and n represents an integer of 1 to 5, preferably 1 to 3.
• the polymerizable group represented by the chemical formula (1) includes allyl group (2-propenyl group), methallyl group (2-methyl-2-propenyl group), isopropenyl group, 3-butenyl group, 3-methyl-3-butenyl group.
• the above-mentioned polymerizable group may be substituted on the aromatic group, for example, allylphenyl group, methallylphenyl group, isoallylphenyl group, allylalkylphenol group, methallylalkylphenol, isopropenylalkylphenol. Is an example of a polymerizable group that can be suitably used.
• the polymerizable group represented by the chemical formula (2) is a 1-propenyl group, and an aromatic group may be substituted with a 1-propenyl group, such as a 1-propenylphenyl group or a 1-propenylalkylphenyl group. Is an example of a polymerizable group that can be suitably used.
• the polymerizable group represented by the chemical formula (3) is derived from maleic acid or fumaric acid.
• the hydrophilic group of the reactive emulsifier Y may be nonionic, anionic, or cationic. Moreover, they can be mixed and used by arbitrary compounding ratios.
• Examples include the combined use of an anionic reactive emulsifier and a nonionic reactive emulsifier, and the combined use of a cationic reactive emulsifier and a nonionic reactive emulsifier.
• a nonionic hydrophilic group a polyoxyalkylene chain is preferable, but a polyoxyethylene chain is more preferable.
• Polyhydric alcohol is also a hydrophilic group that can be suitably used.
• Examples of the anionic hydrophilic group include sulfonate, carboxylate, sulfate ester salt, phosphate ester salt, and sulfosuccinate.
• As the cationic hydrophilic group a quaternary ammonium salt and an amine salt are preferable.
• reactive emulsifiers applicable to the present invention are shown below, but the reactive emulsifiers only need to satisfy the above requirements, and are not limited to the following examples.
• a reactive emulsifier having an anionic group introduced Nonionic reactive emulsifier obtained by adding alkylene oxide, alkyl glycidyl ether or phenyl glycidyl ether to allyl alcohol and a reactive emulsifier additionally introduced with an anionic group, described in JP-T-2005-536621 ; Addition of ⁇ -olefin epoxide or alkyl glycidyl ether to 3-methyl-3-buten-1-ol described in JP-A No. 2002-80506 and JP-A No.
• a reactive emulsifier incorporating a salt Nonionic reactive emulsifier in which an alkylene oxide chain is introduced into a reaction product of branched olefin oxide or internal olefin oxide and allyl alcohol or methallyl alcohol described in JP-A No. 2002-275115, and an oxyalkylene chain terminal
• a reactive emulsifier in which a sulfate ester salt is introduced After introducing an alkylene oxide chain into a reaction product of an ⁇ -olefin epoxide having 8 to 32 carbon atoms and allyl alcohol or methallyl alcohol described in JP-A-7-18809, a carboxylate group is introduced at the terminal.
• Reactive emulsifiers Nonionic reactive emulsifier obtained by adding alkylene oxide to propenyl nonylphenol described in JP-A-4-50204; Reactive emulsifiers obtained by adding an alkylene oxide to propenyl nonylphenol and then sulfate esterifying its oxyalkylene chain end as described in JP-A-4-53802; A reactive emulsifier obtained by adding a carboxylic acid salt after adding an alkylene oxide to propenyl nonylphenol, as described in JP-A-6-248005; Reactive emulsifiers obtained by adding alkylene oxide to propenyl nonylphenol and then phosphoric acid ester described in JP-A-4-550401; Reaction obtained by reacting a reaction product of maleic anhydride with 1,2-dihydroxyalkane or 1,2-dihydroxyalkane and alkylene oxide described in JP-A-2011-6684 and neutralizing with alkali Emulsifiers; After reacting male
• the resulting reactive emulsifier is also reacted with a reaction product of maleic anhydride and 1,2-dihydroxyalkane or 1,2-dihydroxyalkane and alkylene oxide, followed by addition of alkylene oxide, and then sulfate ester salt or A reactive emulsifier obtained by introducing a phosphate ester salt; A reactive emulsifier obtained by reacting maleic anhydride with a higher alcohol and then sulfonating as described in JP-A-58-45236.
• allyl alcohol derivatives are also examples of reactive emulsifiers that can be used in the present invention.
• a nonionic reactive emulsifier obtained by adding alkylene oxide to allyl alcohol, and the terminal is sulfated, sulfonated, ether carboxylated, phosphoric esterified, or a quaternary ammonium base is introduced at the terminal.
• ionic reactive emulsifiers obtained from the above are examples of reactive emulsifiers obtained from the above.
• the amount of the reactive emulsifier used in the emulsion polymerization method of the present invention is usually preferably 0.1 to 20% by weight, more preferably 0.2 to 10% by weight, based on the total monomer weight.
• Multifunctional monomer Z1 As the polyfunctional monomer Z1 having two or more polymerizable unsaturated groups in the molecule used in the present invention, a polyfunctional monomer having a molecular weight per functional group of less than 150 is preferable.
• the molecular weight per functional group is 150 or more, the effect of the polymer coating film on water resistance is poor, specifically, the effect of improving the copolymerization rate of the reactive emulsifier is poor, and the coating film is whitened (white turbidity). ) Insufficient effect in suppressing the phenomenon and water absorption / swelling phenomenon.
• this polyfunctional monomer is added in a large amount to compensate for the effect, the coating is less than when no polyfunctional monomer is added.
• the polyfunctional monomer Z1 preferably has at least one group represented by chemical formulas (4) to (6) in the molecule as a polymerizable unsaturated group.
• R 2 in the formula (4), R 3 in the formula (6) each represent a hydrogen or a methyl group.
• n represents an integer of 1 to 5, preferably 1 to 3.
• the polymerizable unsaturated group represented by the chemical formula (4) is an allyl group (2-propenyl group) or a methallyl group (2-methyl-2-propenyl group), specifically, triallyl isocyanurate, trimeta Allyl isocyanurate, triallyl cyanurate, trimethallyl cyanurate, diallylamine, triallylamine, diallyl adipate, diallyl carbonate, diallyldimethylammonium chloride, diallyl fumarate, diallyl isophthalate, diallyl malonate, diallyl oxalate, diallyl phthalate, Diallylpropyl isocyanurate, diallyl sebacate, diallyl succinate, diallyl terephthalate, diallyl tartrate, diallylbenzene, dimethallylbenzene, 2,6-diallylphenol, 2,6-dia Le phenol derivatives, 2,6-di-methallyl, 2,6
• the polymerizable unsaturated group represented by the chemical formula (5) is a 1-propenyl group, and specific examples thereof include di-1-propenylbenzene, di-1-propenylphenol and di-1-propenylphenol derivatives.
• the polymerizable unsaturated group represented by the chemical formula (6) is an acrylate group or a methacrylate group, and specific examples of the bifunctional monomer include ethylene glycol diacrylate, ethylene glycol dimethacrylate, diethylene glycol diacrylate, diethylene glycol dimethacrylate, and triethylene.
• Glycol diacrylate triethylene glycol dimethacrylate, polyethylene glycol diacrylate, polyethylene glycol dimethacrylate, propylene glycol diacrylate, propylene glycol dimethacrylate, dipropylene glycol diacrylate, dipropylene glycol dimethacrylate, tripropylene glycol diacrylate, tripropylene Glycol dimethacrylate, polypropylene glycol Diacrylate, polypropylene glycol dimethacrylate, 1,3-butylene glycol diacrylate, 1,3-butylene glycol dimethacrylate, 1,4-butanediol diacrylate, 1,4-butanediol dimethacrylate, 1,6-hexane Examples include diol diacrylate, 1,6-hexanediol dimethacrylate, other alkylene diol diacrylates, alkylene diol dimethacrylates, neopentyl glycol diacrylate, neopentyl glyco
• diols derived from hydrocarbons or diacrylates and dimethacrylates of alkylene oxide derivatives thereof can be used.
• the trifunctional monomer include trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, pentaerythritol triacrylate, pentaerythritol trimethacrylate, tris (acryloxyethyl) isocyanurate, and the like.
• examples of the tetrafunctional or higher functional monomer include pentaerythritol acrylate, pentaerythritol tetramethacrylate, dipentaerythritol polyacrylate, dipentaerythritol polymethacrylate, and octaallyl sucrose.
• the present invention it is preferable to use one selected from the above-mentioned bifunctional, trifunctional, or higher polyfunctional monomers, but it does not adversely affect the problems to be solved by the present invention. If it is in the range, two or more kinds can be used in combination.
• the polyfunctional monomer Z1 triallyl cyanurate, trialmethallyl cyanurate, triallyl isocyanurate, triallyl cyanurate, diallyl phthalate, diallyl isophthalate, diallyl Fumarate, diallyl malate, ethylene glycol diacrylate, ethylene glycol dimethacrylate, trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, 1,6-hexanediol diacrylate, 1,3-butylene glycol dimethacrylate, octaallyl sucrose Etc. are preferably used.
• the effect of the reactive emulsifier on improving the copolymerization rate will be poor, and the water resistance of the coating film will deteriorate, specifically the whitening (white turbidity) phenomenon of the coating film.
• it tends to promote water absorption / swelling phenomenon, and is not desirable from the viewpoint of foaming of polymer dispersion, deterioration of mechanical properties of coating film and reduction of adhesive strength.
• the addition amount of the polyfunctional monomer Z1 is larger than the above range and the Z1 / Y ratio is Z1 / Y> 1/3, the amount of aggregates is increased during emulsion polymerization, the solid content of the polymer dispersion is decreased, and the yield is increased. Deterioration and process delay due to clogging of filtration filter may occur, and compared with the case where this polyfunctional monomer is not added, the mechanical properties of the coating film and adhesive strength are greatly reduced. Or problems such as failure to create a good coating film.
• hydrophilic monomer Z2 The hydrophilic monomer Z2 having one polymerizable unsaturated group in the molecule used in the present invention has one polymerizable unsaturated group in the molecule, and the hydrophilic group is hydroxyethyl group, 2-hydroxyethoxy. It has an ethyl group, a hydroxypropyl group, a 2-hydroxypropoxypropyl group, a polyoxyethylene group, a polyoxypropylene group, a glyceryl group, a polyglyceryl group, or an alkoxylated derivative having 1 to 4 carbon atoms in the molecule. Examples thereof include hydrophilic monomers having a molecular weight of less than 250, and one or more of them can be selected and used.
• the average molecular weight of the hydrophilic monomer Z2 is preferably less than 250.
• the average molecular weight is 250 or more, the effect on the water resistance of the polymer coating film is poor.
• the copolymerization rate of the reactive emulsifier The effect for improvement is poor, and it is not desirable from the viewpoint of suppression of the whitening (white turbidity) phenomenon of the coating film and suppression of water absorption / swelling phenomenon.
• the amount of agglomerates increases during emulsion polymerization, causing problems such as a decrease in the solid content of the polymer dispersion, a decrease in yield, and a process delay due to clogging of the filtration filter.
• the hydrophilic monomer Z2 preferably has one group represented by the above chemical formulas (4) to (6) in the molecule as a polymerizable unsaturated group.
• hydrophilic monomer Z2 hydroxyethyl acrylate, hydroxyethyl methacrylate, 2- (2-hydroxyethoxy) ethyl acrylate, 2- (2-hydroxyethoxy) ethyl methacrylate, Hydroxypropyl acrylate, hydroxypropyl methacrylate, polyoxyethylene acrylate, polyoxyethylene methacrylate, or methoxy derivatives thereof are preferably used.
• the effects of the present invention are the polymerization unsaturated groups represented by the chemical formulas (1) to (3) of the reactive emulsifier Y and the polymerization of the hydrophilic monomer Z2 preferably represented by the chemical formulas (4) to (6).
• the amount of hydrophilic monomer Z2 added is greater than the above range and the Z2 / Y ratio is Z2 / Y> 1/1, the amount of aggregates increases during emulsion polymerization, the solid content of the polymer dispersion decreases, and the yield decreases. , Problems such as process delay due to clogging of the filtration filter may occur, and compared with the case where this hydrophilic monomer is not added, the mechanical properties of the coating film are greatly reduced and the adhesive strength is greatly reduced. Or troubles such as inability to create a good coating film.
• nonionic surfactant examples include polyoxyalkylene alkyl phenyl ether, polyoxyalkylene alkyl ether, polyoxyalkylene styrenated phenyl ether, polyoxyalkylene benzylated phenyl ether. , Polyoxyalkylene cumyl phenyl ether, fatty acid polyethylene glycol ether, polyoxyalkylene sorbitan fatty acid ester, sorbitan fatty acid ester, and the like.
• anionic surfactants include fatty acid soap, rosin acid soap, alkyl sulfonate, alkyl Aryl sulfonate, alkyl sulfate ester salt, alkyl sulfosuccinate, sulfate ester salt of nonionic surfactant having polyoxyalkylene chain, Phosphate ester salts, ether carboxylate, sulfosuccinic acid salts, and the like can be preferably used.
• cationic surfactant examples include stearyl trimethyl ammonium salt, cetyl trimethyl ammonium salt, lauryl trimethyl ammonium salt, dialkyl dimethyl ammonium salt, alkyl dimethyl benzyl ammonium salt, and alkyl dimethyl hydroxyethyl ammonium salt.
• a known protective colloid agent can be used in combination for the purpose of improving the polymerization stability during emulsion polymerization.
• protective colloid agents that can be used in combination include fully saponified polyvinyl alcohol (PVA), partially saponified PVA, hydroxyethyl cellulose, carboxymethyl cellulose, methyl cellulose, polyacrylic acid, polyvinyl pyrrolidone, and the like.
• the kind of polymerization initiator and the amount added are not particularly limited, but persulfates such as ammonium persulfate and potassium persulfate are desirable, and peroxides such as hydrogen peroxide and benzoyl peroxide are used. Can be used. Further, if necessary, as a redox polymerization initiator capable of starting a polymerization reaction at a low temperature, a reducing agent such as a persulfate and an alkali metal sulfite or bisulfite may be used in combination.
• the molecular weight regulator used in an emulsion polymerization process can be used suitably as needed in the range which does not have a bad influence with respect to the subject which should be solved by this invention.
• molecular weight modifiers include mercaptans such as n-dodecyl mercaptan, octyl mercaptan, t-butyl mercaptan, thioglycolic acid, thiomalic acid, thiosalicylic acid, sulfides such as diisopropylxanthogen disulfide, diethylxanthogen disulfide, diethylthiuram disulfide, and iodoform.
• halogenated hydrocarbons such as diphenylethylene, p-chlorodiphenylethylene, p-cyanodiphenylethylene, and ⁇ -methylstyrene dimer.
• the emulsion polymerization method applicable in the present invention is not particularly limited as long as it is a method in which the respective components used in the present invention are blended in an aqueous medium and emulsion polymerization is performed. Based on the batch polymerization method, the monomer dropping method, the emulsion dropping method, the seed polymerization method, the multistage polymerization method, the power feed polymerization method and the like classified based on the above.
• the polymer dispersion obtained by the emulsion polymerization method of the present invention is used for forming a coating film as a paint or an adhesive or recovering a solid polymer by a precipitating agent according to a conventional method. That is, a polymer film is obtained by drying the obtained polymer dispersion at room temperature or, if necessary, by heating.
• the solid polymer can be recovered by adding an acid or salt conventionally used as a precipitating agent, stirring, aggregating the polymer, and performing filtration or the like.
• part or % means “part by weight” or “% by weight”, respectively.
• Reactive emulsifier The reactive emulsifier that can be used in the present invention may be a commercial product or a prototype as long as it satisfies the requirements limited in the present invention. The example was used for the purpose of illustrating the effect. In addition, about what could not be obtained as a commercial item, the reactive emulsifier synthesize
• Reactive emulsifier [1] A reactive emulsifier having the following structural formula (AQUALON KH-10 manufactured by Daiichi Kogyo Seiyaku Co., Ltd.) was used.
• Reactive emulsifier [2] Reaction of 20 mole equivalent of ethylene oxide with potassium hydroxide as a catalyst to the reaction product of ⁇ -olefin epoxide having 12 and 14 carbon atoms and allyl alcohol which is a precursor of the reactive emulsifier [1] (before addition reaction of ethylene oxide)
• a nonionic reactive emulsifier [2] represented by the following structural formula was obtained.
• Reactive emulsifier [3] React the precursor of the reactive emulsifier [1] (before the ethylene oxide addition reaction) with the reaction product of ⁇ -olefin epoxide having 12 and 14 carbon atoms and allyl alcohol with 5 mole equivalent of ethylene oxide using potassium hydroxide as a catalyst. After that, a reactive emulsifier [3] represented by the following structural formula was obtained according to a known method (described in JP-A-7-18809).
• Reactive emulsifier [4] A 3 L stainless steel pressure reactor equipped with a stirrer, thermometer, nitrogen inlet tube, ethylene oxide inlet tube and having heating / cooling functions was added with 678 g (3 mol) of isopentadecene oxide, 174 g (3 mol) of allyl alcohol, and 30 g of sodium hydroxide was charged as a catalyst, and the atmosphere in the reactor was replaced with nitrogen, followed by reaction at 90 ° C. for 5 hours, and then at 130 ° C. and 0.25 MPa while sequentially introducing 1320 g (30 mol) of ethylene oxide. Thereafter, aging was performed by continuing stirring for 1 hour while maintaining the temperature.
• Reactive emulsifier [5] A 3L stainless steel pressure reactor equipped with a stirrer, thermometer, nitrogen inlet tube, ethylene oxide inlet tube and heating / cooling function was charged with 517 g (3 mol) of isoundecyl alcohol and 10 g of sodium hydroxide as a catalyst. After replacing the atmosphere in the reactor with nitrogen, 342 g (3 mol) of allyl glycidyl ether was charged at 90 ° C. and then aged at 90 ° C. for 5 hours, and then 1320 g (30 mol) of ethylene oxide at 130 ° C. and 0.25 MPa. ) Were sequentially introduced, followed by aging by continuing stirring for 1 hour while maintaining the temperature.
• Reactive emulsifier [6] A 3 L stainless steel pressure reactor equipped with a stirrer, thermometer, nitrogen introduction tube, alkylene oxides introduction tube and having heating and cooling functions was charged with 228 g (2 mol) of allyl alcohol and 14 g of potassium methoxide as a catalyst, Methanol was removed under reduced pressure. Thereafter, the reaction was carried out while sequentially introducing 464 g (8 mol) of propylene oxide while heating to 130 ° C., and then aging was carried out by continuing stirring for 1 hour while maintaining the temperature.
• Reactive emulsifier [7] In the production example of the reactive emulsifier [6], propylene oxide and phenyl glycidyl ether were changed to butylene oxide and 2-ethylhexyl glycidyl ether, respectively.
• Reactive emulsifier [8] A 3 L glass pressure reactor equipped with a stirrer, a thermometer, a reflux condenser, and a nitrogen introduction pipe and having a heating / cooling function was charged with 491 g (5 mol) of maleic anhydride and 290 g (5 mol) of allyl alcohol. The reaction was continued for 2 hours with stirring at 60 ° C., and then 930 g (5 mol) of lauryl alcohol, 15 g of paratoluenesulfonic acid, and 15 g of hydroquinone were added, and gradually removed up to 140 ° C. while removing the water produced while stirring. The mixture was heated to 5 hours and reacted for 5 hours to obtain allyl lauryl maleate.
• Reactive emulsifier [9] A 3 L glass pressure reactor equipped with a stirrer, a thermometer, a reflux condenser, and a nitrogen introduction pipe and having a heating / cooling function was charged with 294 g (3 mol) of maleic anhydride and 558 g (3 mol) of lauryl alcohol. To 80 ° C. for 2 hours with stirring. Subsequently, 1000 ml of heptane was added, and when the reaction crude product became uniform, it was cooled to room temperature. Then, after leaving still at room temperature for 5 hours, deposits were collect
• Reactive emulsifier A reactive emulsifier represented by the following structural formula (AQUALON BC-10 (Daiichi Kogyo Seiyaku Co., Ltd.)) was used.
• Reactive emulsifier A reactive emulsifier (HITENOL A-10 manufactured by Daiichi Kogyo Seiyaku Co., Ltd.) represented by the following structural formula was used.
• Reactive emulsifier [12] A 3 L stainless steel pressure reactor equipped with a stirrer, thermometer, nitrogen inlet tube, ethylene oxide inlet tube and heating / cooling function was added to 558 g (3 mol) of lauryl alcohol and 1.8 g of boron trifluoride ether as a catalyst. After replacing the atmosphere in the reactor with nitrogen, 426 g (3 mol) of glycidyl methacrylate was charged, and then aged at 80 ° C. for 5 hours, and then 1320 g (30 mol) of ethylene oxide at 130 ° C. and 0.25 MPa in order. After reacting while introducing, the mixture was aged by continuing stirring for 1 hour while maintaining the temperature.
• Reactive emulsifier [13] In the production example of the reactive emulsifier [5], the same procedure was followed except that allyl glycidyl ether was changed to vinyl benzyl glycidyl ether and isoundecyl alcohol was changed to lauryl alcohol.
• a reactor equipped with a stirrer, reflux condenser, thermometer, nitrogen inlet tube and dropping funnel was charged with 122 g of ion-exchanged water and 0.25 g of sodium bicarbonate, and stirring was continued while venting nitrogen.
• a part of 36 g of the previously prepared mixed monomer emulsion was charged and heated to 80 ° C.
• dissolved ammonium persulfate 0.5g in the ion-exchange water 20g was added as a polymerization initiator, and superposition
• 15 minutes after the addition of the polymerization initiator the remaining 324 parts of the mixed monomer emulsion was dropped and polymerized over 3 hours. Further, after aging for 2 hours in succession, the mixture was cooled and adjusted to pH 8 with aqueous ammonia to obtain a polymer dispersion for use in the evaluation experiment of the present invention.
• Example 2 Preparation of Styrene / Butyl Acrylate Polymer Dispersion
• Examples 2-1 to 2-8, Comparative Examples 2-1 to 2-11) Emulsification in the same manner as in Experiment 1 except that the monomer component in Experiment 1 was changed from methyl methacrylate and butyl acrylate to styrene and butyl acrylate, and the emulsifier and multifunctional monomer were changed to the conditions shown in Table 2. Polymerization was performed to obtain a polymer dispersion to be used in the evaluation experiment of the present invention.
• Example 3 Preparation of Styrene / Butadiene Dispersion
• Examples 3-1 to 3-9 Comparative Examples 3-1 to 3-7
• a reactor 60 g of ion-exchanged water was charged into a pressure-resistant glass bottle, specifically, an empty bottle for carbonated beverages, dissolved oxygen was removed with nitrogen gas, and the glass bottle was cooled in an ice-water bath.
• 0.12 g of naphthalene sulfonic acid holymarin condensate, 0.12 g of sodium carbonate and 0.12 g of dodecyl mercaptan are added, and the glass bottle is temporarily plugged with a rubber stopper, and the contents of the glass bottle are added.
• the bottle was opened, charged with 20 g of styrene and 0.12 g of potassium persulfate, and the glass bottle was temporarily plugged with a rubber stopper and allowed to cool in an ice-water bath.
• butadiene was introduced from a butadiene cylinder into a graduated sampling tube in a methanol dry ice bath, liquefied and weighed 20 g of butadiene was charged into a glass bottle using a syringe with a stopcock, and immediately covered with a predetermined metal crown.
• the bottle polymerization reactor was prepared by stoppering.
• the stoppered glass bottle was vigorously shaken to make the content liquid in the glass bottle milky.
• a glass bottle was set in a holder in a rotary polymerization tank for bottle polymerization adjusted to a water temperature of 50 ° C., polymerized at a rotation speed of 50 rpm for 20 hours, and emulsion polymerization was performed by a bottle polymerization method. Thereafter, the glass bottle is put into an ice-water bath, cooled, then opened, 0.12 g of p-tert-butylcatechol is added, and unreacted butadiene is distilled off by nitrogen gas bubbling in a fume hood. A polymer dispersion was obtained.
• Example 4 Preparation of Acrylonitrile / Butadiene / Styrene Resin
• Examples 4-1 to 4-8, Comparative Examples 4-1 to 4-8) A 0.75 L stainless steel pressure reactor equipped with a stirrer, thermometer, nitrogen inlet tube, and gas inlet tube, with heating and cooling functions, 100 g of ion-exchanged water, 0.5 g of naphthalenesulfonic acid polymarine condensate, sodium carbonate 0.5 g and 0.5 g of dodecyl mercaptan were charged, the emulsifier shown in Table 4 (3.0 g) was added, 0.3 g of potassium persulfate was further added, and the inside of the reactor was purged with nitrogen.
• a reactor having a stirrer, a reflux condenser, a thermometer, a nitrogen introduction tube, and a dropping funnel, and having a heating and cooling function, 64 g of polybutadiene dispersion prepared by the above operation in terms of solid content of 40%, ion Mixed monomer milk obtained by adding 36 g of exchanged water, then adding 75 g of styrene, 19 g of acrylonitrile, 100 g of ion exchanged water, and further adding the reactive emulsifier (1.9 g) and polyfunctional monomer shown in Table 4 and mixing and stirring them separately.
• Solid content 2 g of polymer dispersion was weighed into an aluminum cup, the solid content weight was determined from the weight of the residue after drying at 105 ° C. for 2 hours, and the solid content weight was expressed as% by weight of the dispersion weighed.
• Polymerization stability Agglomerates produced during the emulsion polymerization process were filtered with a 80 mesh wire mesh, and the filtration residue was washed with water and dried at 105 ° C. for 2 hours. The weight of the dispersion was based on the solid content of the dispersion. It is shown in wt%. In this measurement, the smaller the aggregate amount, the higher the polymerization stability in the emulsion polymerization step.
• Average particle diameter A part of the polymer dispersion was taken, and the particle diameter was measured with a dynamic light scattering particle size distribution measuring device (MICROTRAC UPA 9340, manufactured by Nikkiso Co., Ltd.).
• Copolymerization rate of reactive emulsifier A certain amount of polymer dispersion was weighed, and excess methanol was added. This methanol diluted solution was centrifuged and separated into a polymer and a supernatant. Then, the supernatant was recovered, and the emulsifier copolymerization ratio was measured from 1H-NMR measurement of the residue obtained after distillation under reduced pressure.
• Foaming property Take 100 ml of polymer dispersion and 100 ml of water in a 1 L graduated cylinder and adjust the temperature to 25 ° C. 2 (40-50 ⁇ m) was passed through nitrogen gas at 300 ml / min for 1 minute, then the nitrogen gas flow was stopped, and the bubble height (bubble amount) immediately thereafter was read as the bubble height (ml). Further, the bubble height (bubble amount) 5 minutes after stopping the nitrogen gas aeration was read as the bubble height (ml) after 5 minutes, and the bubble breakability (%) was determined by the following formula. In this case, the lower the foam height (ml) immediately after, and the lower the foam breakability (%), the lower the foamability of the polymer dispersion.
• Bubble breakability (%) Bubble height after 5 minutes (ml) / Immediately after bubble height (ml) x 100
• Filter filterability Gravity filtration of 80 g of the obtained polymer dispersion with a 200 mesh wire mesh, the time required for the filtration is measured, and the status of the aggregate residue remaining on the wire mesh is visually confirmed. The filter filterability was evaluated based on the criteria. In this measurement, the shorter the filtration time and the smaller the residue on the wire mesh, the higher the polymerization stability in the emulsion polymerization process, the higher the yield rate in commercial production, and the fewer troubles caused by clogging of the filtration filter. To do.
• the filtration time is within 15 seconds and no solid substance is seen on the wire mesh.
• the filtration time is less than 15 seconds, but a solid residue is slightly seen on the wire mesh.
• the filtration time is 15 More than 30 seconds and less than 30 seconds, solid residue can be seen on the wire mesh.
• Filtration time exceeds 30 seconds or clogging is observed, and many solid residue is seen on the wire mesh.
• Water whitening resistance test The obtained polymer dispersion was applied to a commercially available glass plate so as to have a film thickness of 120 ⁇ m (dry) and dried at 20 ° C. ⁇ 65% RH for 24 hours at 25 ° C. It was immersed in ion-exchanged water, a glass plate was placed on 16-point printed characters, and the number of days until the characters were not visible when the characters were seen through the polymer film was measured.
• Peeling state evaluation In the water whitening test, the state of the polymer film when 16-point characters disappeared was visually observed and evaluated based on the following criteria.
• the obtained polymer dispersion was applied to a commercially available glass plate so as to have a film thickness of 120 ⁇ m (dry), dried in an atmosphere of 20 ° C. ⁇ 65% RH for 24 hours, and the polymer film was carefully removed from the glass plate. It peeled off, the polymer film was cut out to the magnitude
• Water absorption rate (% by weight) ⁇ (polymer film weight after immersion ⁇ initial polymer film weight) / initial polymer film weight ⁇ ⁇ 100
• Polymer recovery rate After dewatering the agglomerated polymer obtained in the polymer recovery step, the polymer was dried under reduced pressure at 105 ° C. to determine the weight of the recovered polymer. Indicated.
• Total organic carbon (TOC) measurement Total waste water (including polymer wash water) obtained in the polymer recovery process is recovered, concentrated to 100 ml, and a portion of the waste water is collected, and total organic carbon meter TOC manufactured by Shimadzu Corporation -Total organic carbon (TOC) content (ppm) was measured using -VCPH.
• TOC Total organic carbon
• TOC value the smaller the TOC value, the smaller the amount of organic substances such as emulsifiers, unreacted monomers and oligomer components that flow into the wastewater, which means that the wastewater load in the polymer recovery process is reduced.
• the copolymerization ratio of the reactive emulsifier with the monomer is improved regardless of the reactive emulsifier species and the monomer species, and the foam trouble in the production process is eliminated. It can be seen that a highly stable polymer dispersion can be obtained and the wastewater load can be greatly reduced. It can also be seen that the polymer film obtained therefrom has solved the problems of whitening due to contact with water, water absorption and swelling.
• a reactor equipped with a stirrer, reflux condenser, thermometer, nitrogen inlet tube and dropping funnel was charged with 122 g of ion-exchanged water and 0.25 g of sodium bicarbonate, and stirring was continued while venting nitrogen.
• a part of 36 g of the previously prepared mixed monomer emulsion was charged and heated to 80 ° C.
• dissolved ammonium persulfate 0.5g in the ion-exchange water 20g was added as a polymerization initiator, and superposition
• 15 minutes after the addition of the polymerization initiator the remaining 324 parts of the mixed monomer emulsion was dropped and polymerized over 3 hours. Further, after aging for 2 hours in succession, the mixture was cooled and adjusted to pH 8 with aqueous ammonia to obtain a polymer dispersion for use in the evaluation experiment of the present invention.
• Example 6 Preparation of Styrene / Butyl Acrylate Polymer Dispersion
• Examples 6-1 to 6-7, Comparative Examples 6-1 to 6-9 The same operation as in Experiment 5 except that the monomer components methyl methacrylate and butyl acrylate in Experiment 5 were changed to styrene and butyl acrylate, and the reactive and polyfunctional monomers were changed to the conditions shown in Table 6.
• Emulsion polymerization was performed to obtain a polymer dispersion to be used for the evaluation experiment of the present invention.
• Example 7 Preparation of Styrene / Butadiene Dispersion
• Examples 7-1 to 7-10 Comparative Examples 7-1 to 7-6
• a reactor 60 g of ion-exchanged water was charged into a pressure-resistant glass bottle, specifically, an empty bottle for carbonated beverages, dissolved oxygen was removed with nitrogen gas, and the glass bottle was cooled in an ice-water bath.
• 0.12 g of naphthalene sulfonic acid holymarin condensate, 0.12 g of sodium carbonate and 0.12 g of dodecyl mercaptan are added, and the glass bottle is temporarily plugged with a rubber stopper, and the contents of the glass bottle are added.
• the bottle was opened, charged with 20 g of styrene and 0.12 g of potassium persulfate, and the glass bottle was temporarily plugged with a rubber stopper and allowed to cool in an ice-water bath.
• butadiene was introduced from a butadiene cylinder into a graduated sampling tube in a methanol dry ice bath, liquefied and weighed 20 g of butadiene was charged into a glass bottle using a syringe with a stopcock, and immediately covered with a predetermined metal crown.
• the bottle polymerization reactor was prepared by stoppering.
• the stoppered glass bottle was vigorously shaken to make the content liquid in the glass bottle milky.
• a glass bottle was set in a holder in a rotary polymerization tank for bottle polymerization adjusted to a water temperature of 50 ° C., polymerized at a rotation speed of 50 rpm for 20 hours, and emulsion polymerization was performed by a bottle polymerization method. Thereafter, the glass bottle is put into an ice-water bath, cooled, then opened, 0.12 g of p-tert-butylcatechol is added, and unreacted butadiene is distilled off by nitrogen gas bubbling in a fume hood. A polymer dispersion was obtained.
• the copolymerization rate of the reactive emulsifier with the monomer is improved regardless of the type of reactive emulsifier and the type of monomer, and the foam trouble in the production process is eliminated. It can be seen that a highly stable polymer dispersion can be obtained. It can also be seen that the polymer film obtained therefrom has solved the problems of whitening due to contact with water, water absorption and swelling.
• the water-based polymer dispersion obtained by the present invention has low foaming properties, and the polymer film obtained therefrom is excellent in water resistance, so that it is a building structure, residential interior / exterior, automobile, railway, various vehicles, ships, storage containers, electric machines. It can be suitably used as paints, coating materials, etc. used for electronic equipment, precision equipment, display equipment, metal products, resin products, furniture, leather products, textile products, and the like. Further, it can also be suitably used as an adhesive or pressure sensitive adhesive for paper, rubber, resin, leather, fiber, wood, metal, glass, ceramics and the like.

Landscapes

• Chemical & Material Sciences (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Organic Chemistry (AREA)
• Polymerisation Methods In General (AREA)
• Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)

Priority Applications (5)

Applications Claiming Priority (4)

Publications (1)

Family

ID=48043390

Family Applications (1)

Country Status (8)

Cited By (6)

Families Citing this family (16)

Citations (28)

Family Cites Families (9)

• 2012
  • 2012-09-19 IN IN3315CHN2014 patent/IN2014CN03315A/en unknown
  • 2012-09-19 KR KR1020147008654A patent/KR20140068136A/ko not_active Ceased
  • 2012-09-19 CN CN201280049309.9A patent/CN103906768A/zh active Pending
  • 2012-09-19 US US14/349,159 patent/US20140249272A1/en not_active Abandoned
  • 2012-09-19 JP JP2013537389A patent/JPWO2013051205A1/ja active Pending
  • 2012-09-19 WO PCT/JP2012/005946 patent/WO2013051205A1/ja not_active Ceased
  • 2012-09-19 EP EP12837696.9A patent/EP2765142A4/en not_active Withdrawn
  • 2012-09-25 TW TW101135081A patent/TW201331233A/zh unknown

Patent Citations (28)

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events