WO2007105344A1 - 樹脂分散体、塗料、積層体及びその製造方法 - Google Patents
樹脂分散体、塗料、積層体及びその製造方法 Download PDFInfo
- Publication number
- WO2007105344A1 WO2007105344A1 PCT/JP2006/324090 JP2006324090W WO2007105344A1 WO 2007105344 A1 WO2007105344 A1 WO 2007105344A1 JP 2006324090 W JP2006324090 W JP 2006324090W WO 2007105344 A1 WO2007105344 A1 WO 2007105344A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- copolymer
- polymer
- propylene
- resin
- weight
- Prior art date
Abstract
Description
Claims