WO2006103960A1 - アレルゲン失活剤 - Google Patents

アレルゲン失活剤 Download PDF

Info

Publication number
WO2006103960A1
WO2006103960A1 PCT/JP2006/305415 JP2006305415W WO2006103960A1 WO 2006103960 A1 WO2006103960 A1 WO 2006103960A1 JP 2006305415 W JP2006305415 W JP 2006305415W WO 2006103960 A1 WO2006103960 A1 WO 2006103960A1
Authority
WO
WIPO (PCT)
Prior art keywords
allergen
house dust
titanium oxide
treating agent
present
Prior art date
Application number
PCT/JP2006/305415
Other languages
English (en)
French (fr)
Inventor
Shinichi Nagai
Takashi Sugiyama
Original Assignee
Fumakilla Limited
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fumakilla Limited filed Critical Fumakilla Limited
Priority to US11/885,644 priority Critical patent/US10226543B2/en
Priority to CN2006800096597A priority patent/CN101146886B/zh
Priority to EP20060729404 priority patent/EP1882727B1/en
Publication of WO2006103960A1 publication Critical patent/WO2006103960A1/ja

Abstract

　pHの変動による性能の低下が少なく、アレルゲンを吸着除去できるだけではなく、アレルゲン自体を失活除去できるアレルゲン失活剤を提供する。ならびにハウスダストの効果的な除去を可能にする、染みの発生などの使用上の問題もない、ハウスダスト処理剤、スプレーおよびシートを提供する。  

Description

明 細 書
アレルゲン失活剤
技術分野
[0001] 本発明は、ハウスダスト中のアレルゲンに作用するアレルゲン失活剤に関し、さらに アレルゲンが失活したハウスダストを凝集 '除去しやすくするハウスダスト処理剤に関 する。
背景技術
[0002] 室内には、ダニの死骸や糞、花粉、塵埃、繊維屑など、種々のハウスダストが存在 する。一般に、電気掃除機などを用いて掃除が行われるが、例えば、カーペット、ソフ ァー、寝具などにからみついた細かいハウスダストは、電気掃除機などをかけただけ では充分に除去することができない。し力しながら、喘息、皮膚炎、花粉症などの種 々のアレルギー疾患は、ハウスダストに含まれるアレルゲン、主としてダニアレルゲン や花粉により発症することが知られており、従って、アレルゲンの失活およびハウスダ ストの除去は重要である。
[0003] アレルゲンを効果的に除去する技術としては、例えば、水膨潤性粘土、ポリビュル アルコールなどで処理する技術 (例えば、特許文献 1および 2参照）、カオリン、タルク などの無機粉体で処理する技術 (特許文献 3参照）などが知られている。これらはい ずれも、使用する各成分によりアレルゲンを吸着して除去するものである。また、タン ニン酸やアルコール、塩化ベンザルコニゥムで処理する技術など（特許文献 4〜7参 照）が知られており、これらはアレルゲンを変性失活して除去するものである。
特許文献 1 :特開 2000— 16941号公報
特許文献 2 :特開 2002— 128680号公報
特許文献 3 :特開 2002— 167332号公報
特許文献 4：特公平 2— 16731号公報
特許文献 5：特開 2000— 63207号公報
特許文献 6 :特開 2000— 264837号公報
特許文献 7：特開 2001— 335474号公報 発明の開示
発明が解決しょうとする課題
[0004] し力しながら、前記のようなアレルゲンを吸着して除去する技術の中には、高 pHで はその吸着性が低下する傾向があった。また、前記のアレルゲンを変性失活させて 除去する技術に使用される成分の中には被処理物に染みができるなど、使用性に問 題のあるものもあった。また、上記いずれの技 テもハウスダストの除去効果としては未 だ充分なものではなった。
[0005] 従って、本発明は、 pHの変動による性能の低下が少なぐアレルゲンを吸着除去で きるだけではなぐアレルゲン自体を失活除去できるアレルゲン失活剤を提供するこ とを目的とする。本発明はまた、ハウスダストの効果的な除去を可能にする、染みの 発生などの使用上の問題もない、ハウスダスト処理剤、スプレーおよびシートを提供 することを目的とする。
課題を解決するための手段
[0006] すなわち、本発明は、
〔1〕光触媒機能を持つ酸化チタンを含有するアレルゲン失活剤；
〔2〕前記〔1〕記載のアレルゲン失活剤およびポリアクリル酸ナトリウムを含有するハウ スダスト処理剤；
〔3〕前記〔2〕記載のハウスダスト処理剤をスプレー容器に充填してなるハウスダスト処 理用スプレー；
〔4〕前記〔2〕記載のハウスダスト処理剤をシート材に含浸してなるハウスダスト処理用 シート；
〔5〕アレルゲンを失活させるための、光触媒機能を持つ酸化チタンの使用；ならびに 〔6〕水、低級アルコールまたはその混合物に光触媒機能を持つ酸化チタンおよびポ リアクリル酸ナトリウムを分散する工程を含む、ハウスダスト処理剤の製造方法 に関する。
発明の効果
[0007] 本発明により、 pHの変動による性能の低下が少なぐアレルゲンを吸着除去できる だけではなぐアレルゲン自体を失活除去できるアレルゲン失活剤を提供することが できる。また、本発明により、ハウスダストの効果的な除去を可能にする、染みの発生 などの使用上の問題もない、ハウスダスト処理剤、スプレーおよびシートを提供するこ とができる。
図面の簡単な説明
[0008] [図 1]標準ダストの実体顕微鏡写真 (倍率 50倍)である。
[図 2]吸着 ·凝集性が認められなレ、状態を示す実体顕微鏡写真 (倍率 50倍)である。
[図 3]吸着 ·凝集性が認められる状態を示す実体顕微鏡写真 (倍率 50倍)である。 発明を実施するための最良の形態
[0009] 本発明のアレルゲン失活剤は、光触媒機能を持つ酸化チタンを含有することを一 つの特徴とする。かかる特徴を有することにより、酸化チタンの持つアレルゲン吸着 能を利用してアレルゲンを吸着して除去できるだけではなぐ酸化チタンの光触媒機 能によりアレルゲン自体を失活させて除去できるという効果が奏される。また、本発明 のアレルゲン失活剤に含有される酸化チタンは金属酸化物であるがゆえに、経時的 に変色することなぐ従来、問題であった染みなどが生じにくい。
[0010] 本発明のアレルゲン失活剤の失活対象となるアレルゲンとしては、ダニの死骸や糞
、花粉などが挙げられる。
[0011] 本明細書において、「光触媒機能」とは、光エネルギーによって発現する酸化力を 利用して有機物などを分解できる能力をいう。酸化チタンが光触媒機能を有するか 否かは、例えば、メチレンブルーの退色が酸化チタンによって生じるか否かで確認す ること力 Sできる。具体的には、酸化チタンをメチレンブルー水溶液に添加し、光照射を 行ないながら、メチレンブルーの退色の程度を目視することで確認することができる。
[0012] 本発明に使用される酸化チタンの結晶型には、アナタース型とルチル型があるが、 アレルゲン失活性の観点から、アナタース型が好ましレ、。
[0013] 本発明に使用される酸化チタンの一次粒子の平均粒子径は、特に限定されないが 、アレルゲン失活性の観点から、 l〜200nmが好ましぐ l〜30nmがより好ましぐ 5〜2 Onmがさらに好ましレ、。酸化チタンの平均粒子径が力かる範囲であれば、アレルゲン 失活剤のアレルゲンの失活'除去効果が高まると共に、その分散安定性が高まる傾 向が見られるので好ましい。酸化チタンの一次粒子の平均粒子径は、例えば、数百 n m程度であれば電子顕微鏡により測定することができ、それ以下であれば、 X線解析 の測定結果から、当該分野で公知の Scherrerの式を用いて結晶子径として測定する こと力 Sできる。酸化チタンの一次粒子の平均粒子径の調整は、例えば、酸化チタンの 焙焼によって容易に行うことができる。なお、酸化チタンは、平均粒子径の異なる 1種 または 2種以上のものを混合して用いることもできる。
[0014] 本発明のアレルゲン失活剤中の酸化チタンの含有量は、本発明の効果が奏される 限り特に限定されないが、 0.005〜100重量％が好ましぐ 0.01〜20重量％がより好ま しい。
[0015] アレルゲン失活剤に使用される溶剤としては、水、低級アルコールまたはその混合 物が好適である。水としては、例えば、精製水などを用いることができる。低級アルコ ールの炭素数は、酸化チタンの分散安定性の観点から、 1〜5であることが好ましぐ 1 〜4であることがより好ましぐ 2であることがさらに好ましい。したがって、低級アルコー ルのなかでは、エタノールが好適である。
[0016] 溶剤として水と低級アルコールの混合液を使用する場合、水：低級アルコールの重 量比は、ハウスダスト処理剤の乾燥性および使用性を高める観点、ならびに引火性 を低減させるとともに刺激性を和らげる観点から、 50： 50〜80： 20であることが好ましく 、 60 : 40〜70 : 30であることがより好ましい。
[0017] 本発明のアレルゲン失活剤には、酸化チタンの分散性の向上の観点から、分散剤 を適量で含有させてもよい。分散剤の量は、その種類などによって異なるので一概に は決定することができないため、その種類などに応じて、本発明の目的が阻害されな い範囲内で調整することが好ましい。
[0018] 本発明のアレルゲン失活剤にはさらに、消臭剤、殺虫剤、殺ダニ剤、忌避剤、殺菌 剤、防黴防腐剤、帯電防止剤、光沢剤、安定化剤、香料、 pH調整剤、風合向上剤な どの添加剤を適量で含有させてもよい。添加剤の量は、その種類などによって異なる ので一概には決定することができないため、その種類などに応じて、本発明の目的が 阻害されない範囲内で調整することが好ましい。
[0019] 本発明のアレルゲン失活剤は、例えば、酸化チタンを前記溶剤に分散させることに より調製して使用することもできるし、酸化チタンそのものをアレルゲン失活剤として 使用することちできる。
[0020] 本発明のアレルゲン失活剤は幅広レ、 pHにおいてその効果を奏することができるが 、アレルゲン失活作用の維持の観点から、 pHは好ましくは 4〜9である。
[0021] 以下、前記アレルゲン失活剤を含有する本発明のハウスダスト処理剤、スプレーな らびにシートについて順に説明する。
[0022] (1)処理剤
本発明のハウスダスト処理剤の処理対象としては、一般的にハウスダストと称される ものであれば特に限定されなレ、が、ダニの死骸や糞、花粉などのアレルゲンを含む ハウスダストに対して優れた除去効果を奏し、ダニの死骸や糞などのダニアレルゲン を含むハウスダストに対して特に優れた除去効果を奏する。
[0023] 本発明のハウスダスト処理剤は、そのものとしても使用可能であるが、後述のスプレ 一やシートの調製に好適に用いられる。
[0024] ハウスダスト処理剤に含まれるアレルゲン失活剤の含有量は、本発明の効果が奏さ れる限り特に限定されなレ、が、酸化チタンの溶剤への充分な分散性を確保し、ならび に充分なハウスダストの除去効果を発揮させる観点から、酸化チタンとして、好ましく は 0.005〜20重量％、より好ましくは 0.01〜1重量％、さらに好ましくは 0.01〜0.2重量 %である。
[0025] ハウスダスト処理剤は、さらにポリアクリル酸ナトリウムを含有する。該成分を含有さ せることで、さらに、例えば、ハウスダストを凝集して、電気掃除機などにより除去しや すくなるという効果が奏される。
[0026] 本発明に使用されるポリアクリル酸ナトリウムの重量平均分子量は、好ましくは 200
X 104〜2000 X 104であり、より好ましくは 500 X 104〜1000 X 104である。
[0027] 本発明のハウスダスト処理剤中のポリアクリル酸ナトリウムの含有量は、特に限定さ れるものではないが、好ましくは 0.0001〜5重量％、より好ましくは 0.0005〜1重量％、 さらに好ましくは 0.0005〜 1重量％である。
[0028] ハウスダスト処理剤に使用される溶剤としては、アレルゲン失活剤に含有されている 水、低級アルコールまたはその混合物をハウスダスト処理剤の溶剤としてもよぐまた 、新たな水、低級アルコールまたはその混合物をハウスダスト処理剤の溶剤としても よい。水としては、アレルゲン失活剤と同様に、精製水などを用いることができる。低 級アルコールの炭素数は、アレルゲン失活剤と同様に、酸化チタンの分散安定性の 観点から、 1〜5であることが好ましぐ 1〜4であることがより好ましぐ 2であることがさら に好ましい。したがって、低級アルコールのなかでは、エタノールが好適である。
[0029] 溶剤として水と低級アルコールの混合液を使用する場合、水：低級アルコールの重 量比は、ハウスダスト処理剤の乾燥性および使用性を高める観点、ならびに引火性 を低減させるとともに刺激性を和らげる観点から、 50： 50〜80： 20であることが好ましく 、 60 : 40〜70 : 30であることがより好ましい。
[0030] ハウスダスト処理剤における水と低級アルコールとの合計含有量は、酸化チタンの 分散安定性、ハウスダスト処理剤の乾燥性および使用性を考慮して決定される。前 記水と低級アルコールとの合計含有量は、通常、酸化チタン、ポリアクリル酸ナトリウ ム、添加剤および消臭成分との残部であることが好ましレ、。
[0031] 本発明のハウスダスト処理剤には、例えば、分散剤、殺虫剤、殺ダニ剤、忌避剤、 殺菌剤、防黴防腐剤、帯電防止剤、光沢剤、安定化剤、香料、 pH調整剤、風合向上 剤などの添加剤を適量で含有させてもよい。添加剤の量は、その種類などによって 異なるので一概には決定することができないため、その種類などに応じて、本発明の 目的が阻害されない範囲内で調整することが好ましい。
[0032] 本発明のハウスダスト処理剤には、さらに消臭成分を含有させるのが好ましい。該 成分を含有させることで、さらに、例えば、ヒトの皮脂や汗に由来する臭いの除去効 果をも発揮させることができる。
[0033] 消臭成分としては、特に限定されるものではなレ、が、例えば、緑茶、柿、竹、ツバキ 、バラ、キク、マツ、スギ、ォォバコ、サトウキビ、モウソゥチタなどの植物抽出物、ロー ズ油、ラベンダー油、ベルガモット油、ビターアーモンド油、カナンガ油、カシア油、シ ダーウッド油、シナモン油、シトロネラ油、レモン油、ライム油、ナツメグ油、ペパーミン ト油、アビエス油、パイン油、スターァニス油、テレビン油、べチバー油、ユーカリ油、 ローズマリー油、ヒノキ油などの植物精油、ァネトール、シトロネラール、シトラール、リ モネン、シネオール、 ひ一ビネン、テルピノレンなどの植物精油由来成分、メチノレメタ タリレート、ェチルメタタリレート、ラウリノレメタタリレート、ステアリルメタタリレート、ピル ビン酸ェチル、ピルビン酸エステル、マレイン酸ジメチル、ベタインなどの消臭成分な どが挙げられる。前記のような臭いの除去効果に優れることから、緑茶、柿、竹などの 植物抽出物が好適である。
[0034] 本発明のハウスダスト処理剤中の消臭成分の含有量は、本発明の効果が奏される 限り特に限定されないが、充分な臭いの除去効果を発揮させる観点から、好ましくは 0.01〜10重量％、より好ましくは 0.05〜2重量％である。
[0035] ハウスダスト処理剤としては、例えば、酸化チタンを 0·01〜0·2重量％、ポリアクリノレ 酸ナトリウムを 0.0005〜0.01重量％、添加剤を0.01〜5重量％、エタノールを 20〜50 重量％、水を残部として含有してなるハウスダスト処理剤が特に好適である。
[0036] 本発明のハウスダスト処理剤は、前記各成分を適宜混合することにより得られる。酸 化チタンは一般的に水に分散しにくいので、通常、水、低級アルコールまたはその混 合物に分散剤を添加して攪拌して分散液として調製するのが好ましい。
[0037] 本発明のハウスダスト処理剤は幅広い ρΗにおいてその効果を奏することができるが 、アレルゲン失活作用の維持の観点から、 ρΗは好ましくは 4〜9である。
[0038] (2)スプレー
本発明のスプレーは、前記ハウスダスト処理剤を公知のスプレー容器に充填してな るものであり、好ましい態様のハウスダスト処理剤を充填してなるものがより好適であ る。
[0039] スプレー容器の種類には特に限定がないが、使用時の簡便性の観点から、例えば 、トリガー式スプレー容器、ポンプ式スプレー容器、蓄圧式スプレー容器などが好まし レ、。スプレー容器の内容量は、使用性などの観点から、通常、好ましくは 10〜 1000m L程度、より好ましくは 30〜750mL程度、さらに好ましくは 50〜500mL程度である。
[0040] 前記ハウスダスト処理剤のスプレー容器への充填は、公知の方法に従って行うこと ができる。
[0041] (3)シート
本発明のシートは、前記ハウスダスト処理剤を公知のシート材料に含浸させてなる ものであり、好ましい態様のハウスダスト処理剤を含浸させてなるものがより好適であ る。
[0042] なお、前記ハウスダスト処理剤の特に好適な態様におけるエタノールの含有量は 20 〜50重量％であるが、シートの調製に前記ハウスダスト処理剤を用いる場合、特に好 適な態様におけるエタノールの含有量はフローリングワックスへの影響などを考慮す ると、 1〜50重量％である。
[0043] シートの形状としては、特に限定されるものではなレ、が、通常、縦 150〜200mm、横 2 00〜300mm、厚さ 0.05〜lmm程度の大きさを有するものが好適である。かかるシート は、単層からなるものであっても、同一若しくは異なる材料 *材質からなる層を積層し てなるものであってもよレ、。
[0044] 前記シート材料としては、特に限定されるものではなぐ例えば、不織布、編織布、 紙などが挙げられるが、強度が高ぐ低コストであり、 目付の調整が容易であるなどの 観点から、不織布が好適である。これらのシート材料は、公知の方法に従って製造す ること力 Sできる。また、市販のものが入手可能であれば、それを用いてもよい。
[0045] 例えば、シート材料として好適に使用される前記不織布は、ケミカルボンド法、サー マルボンド法、スパンレース法、スパンボンド法、ニードルパンチ法などの公知の方法 により製造すること力 Sできる。また、その材質としては、特に限定されるものではないが 、例えば、ポリプロピレン、ポリエチレン、ポリエステル、アクリル、レーヨン、コットン、パ ルプなどが挙げられる。不織布の材質としては、ハウスダスト処理剤を含浸させ易い こと力 、レーヨンまたはパルプが好適であり、強度を保つという観点から、ポリエチレ ンまたはポリエステルが好適である。さらに、両方の観点から、それぞれにおいて好 適な材料として例示されたものを適当な割合で混紡したものがより好適である。
[0046] なお、不織布の目付、すなわち、単位面積当りの繊維重量としては、通常、 30〜80 g/m2程度が好適である。
[0047] 前記ハウスダスト処理剤のシート材料への含浸は、公知の方法に従って行うことが できる。例えば、前記好適な範囲の目付を有する不織布からなるシート材料に対し前 記ハウスダスト処理剤を含浸させる場合、シート材料を目付の 2〜3倍量程度の前記 ハウスダスト処理剤に浸漬して、該シート材料に前記ハウスダスト処理剤を含浸させ るのが好適である。すなわち、 目付が 50g/m2である場合、不織布からなるシート材料 lm2当たり 100〜150gの前記ハウスダスト処理剤を含浸させるのが好適である。
[0048] 本発明のハウスダスト処理剤及びスプレーは、例えば、電気掃除機によって掃除し ようとする対象である室内のカーペット、ソファー、寝具などに散布などにより適用して 用レ、られる。かかる場合、適用直後に、好ましくは数分間から数時間そのまま放置し た後に、電気掃除機により通常通り前記対象の掃除を行うことで、アレルゲンを効果 的に失活することができ、またハウスダストを効果的に除去することができる。また、例 えば、寝具などを屋外に干す場合に、該寝具などに適用して用いることもできる。そ の場合、一定時間干した後、室内に取り込む際に、ハタキゃ手で叩くことでハウスダ ストを効果的に除去することができる。通常、干した寝具などを叩くと付着したハウス ダストが細かく砕け、ますますとれ難くなる場合があるが、本発明のハウスダスト処理 剤などを予め適用しておけ
ば、ハウスダストが凝集され、効果的な除去が可能となる。
[0049] なお、ハウスダスト処理剤は、その散布などが容易でないことから、スプレーとして用 レ、るのが好適である。また、スプレーは、アレルゲンの失活作用およびハウスダストの 除去効果を充分に発揮させる観点から、酸化チタンを均一に分散させた状態で用い るのが好適である。従って、通常、対象への適用前にスプレーをよく振って用いるの が好ましい。さらに、その適用時には、対象のスプレー適用部分が濡れているため、 適用後一定時間をおき充分に乾燥させた後、掃除などを行うのが好ましい。なお、本 発明のハウスダスト処理剤など力 緑茶、柿、竹などの植物抽出物などからなる消臭 成分を含有してなる場合、アレルゲンを効果的に失活でき、ノ、ウスダストを効果的に 除去できると共に、前記したような臭いを効果的に除去することができる。
[0050] 一方、本発明のシートは、ハウスダストが溜まっている部分、例えば、寝具などの表 面や、室内電灯のかさ、窓枠、床などを拭くのに好適に使用される。通常、かかる部 分を水拭きした場合、例えば、ハウスダストが濡れるだけで、拭きとることは困難であ る力 本発明のシートによれば、アレルゲンを効果的に失活させると共にハウスダスト を凝集させて効果的に除去することができる。また、前記のような消臭成分が含有さ れておれば、前記したような臭いを効果的に除去することもできる。
実施例 [0051] 実施例:!〜 5および比較例:!〜 3 アレルゲン失活剤の調製
表 1に示す酸化チタン A〜F、シリカまたはタルクを表 2に示す配合に従って各成分 を混合し、試験液 1〜5 (実施例:!〜 5)および比較試験液 1〜3 (比較例:!〜 3)を得た
[0052] なお、酸化チタン、シリカまたはタルクは、常温の水に攪拌下、少量ずつ添加するこ とにより、水に分散させた。また、使用した酸化チタンの光触媒機能を確認するため、 酸化チタン O.lgをメチレンブルー水溶液（0.1重量％) lOOmLに添加攪拌し、得られた 分散液をスポイトで採取してその一滴をスライドグラス上にのせ、光照射（ブラックライ ト、紫外線強度 1000 μ \νん m2)を行ないながら、メチレンブルーの退色の程度を肉眼 で観察したところ、光照射開始から 1時間後に、酸化チタン A〜Eを分散させた分散液 の色は青色から無色透明に変化し、一方酸化チタン Fを分散させた分散液の色は青 色から変化しなかった。従って、酸化チタン A〜Eは光触媒機能を有し、一方、酸化チ タン Fは光触媒機能を有していなかった。
[0053] [表 1]
Figure imgf000011_0001
[0054] [表 2]
Figure imgf000011_0002
試験例 1 アレルゲン失活作用の評価
前記試験液:!〜 5及び比較試験液:!〜 3のアレルゲン失活作用を、アレルゲンとし てダニアレルゲンを用い、以下の方法に従って評価した。
[0056] Dfb抗原〔ダニ虫体粗抗原；ササら（Sasa, M. et al., Jpn. J. Exp. Med., 40: p367- 38 2， 1970)の方法により得た〕を PBSに対し 20 /i g/mLの濃度となるように溶解して調製 した抗原液 1 mLに、 0.15mLの試験液 1〜 5及び比較試験液 1〜 3をそれぞれ添カロし た。なお、陰性対照では、それらの試験液の代わりに同量の水を添加した。室温で蛍 光灯（36W X 8)の下、 2時間維持した後、各試験液によるアレルゲン失活作用の程度 をマイティーチエッカー（ダニアレルゲン検知用キット：シントーファイン社製）により測 定した。
[0057] マイティーチエッカーによれば、被検液中の、アレルゲンとして作用し得るダニァレ ルゲン Der2 (主要アレルゲンの 1つ）量を、モノクローナル抗体を用いた水平展開方 式により測定することができるので、各試験液によるアレルゲン失活作用の程度は、 各試験液のアレルゲンの失活作用を表すものと考えられる。
[0058] マイティーチエッカーによるダニアレルゲン量の判定基準を以下の表 3に、また、該 判定基準に基づく各試験液によるアレルゲン失活作用の程度の判定結果を表 4に示 す。
[0059] [表 3]
Figure imgf000012_0001
[0060] [表 4]
Figure imgf000012_0002
表 4より、試験液:!〜 5のアレルゲン失活作用の程度は比較試験液 1〜3および陰 性対照に比べ高レ、ことがわかる。比較試験液に使用した成分は従来のアレルゲン除 去技術に使用された成分である。表 4の結果は、これらの成分に比べ、本発明で使 用される酸化チタンのダニアレルゲンの失活作用の程度が特に優れることを示す。 [0062] 試験例 2 アレルゲン失活作用における光の影響
前記試験液 1のアレルゲン失活作用が光によりどのような影響を受けるかを確認す るため、光条件を変更する以外は試験例 1と同様に、アレルゲン失活作用の程度を 評価した。対照として、比較試験液 1を使用した。その結果を表 5に示す。
[0063] [表 5]
Figure imgf000013_0001
[0064] 表 5より、試験液 1のアレルゲン失活作用の程度は強い光が当たることにより一層向 上し、一方、比較試験液 1のアレルゲン失活作用の程度は光条件によらず低いまま であった。
[0065] 試験例 3 アレルゲン失活作用における pHの影響
前記試験液 1のアレルゲン失活作用が pHによりどのような影響を受けるかを確認す るため、試験前に乳酸または炭酸ナトリウムを用レ、て試験液の pHを調整する以外は 試験例 1と同様に、アレルゲン失活作用の程度を評価した。その結果を表 6に示す。 なお、試験液 1の試験前の pHは 6であった。
[0066] [表 6]
Figure imgf000013_0002
[0067] 表 6より、試験液 1のアレルゲン失活作用の程度は pHによらず維持されることがわか る。
[0068] 実施例 6および比較例 4〜： 11 ハウスダスト処理剤の調製
表 7に示す配合に従って各成分を混合し、試験液 6 (実施例 6)および比較試験液 4 〜11 (比較例4〜11)を得た。なお、表 7における単位は gである。
[0069] [表 7] 実施例 比 K例
6 4 5 6 7 8 9 10 1 1
K化チタン A 0. 18 0. 18 0. 18 0. 13 0. 18 0. 18 0. 18 0. 18 0. 8
本'リ 7クリ A¾ナトリウム 0. 0045 一 - 一 - 一 - 一 一
7ルキ'ン酸ナトリウム 一 0. 0045 O. 09 一 一 一 一 一 一
Λ* イショテ'ンノ ン 一 一 一 0. 0045 Q. 45 一 一 一 一
木 ' i m- 一 一 - - 一 0. 0045 0. 45 一 一
一 ■ - - - 一 - 一 0. Q04S 0. 45
水 Z70 270 210 270 270 270 270 270 270
Iタ ル 180 I SO I 8Q 180 180 180 180 180 180
[0070] 試験例 4 アレルゲン失活作用の評価
試験液 6および比較試験液 4〜： 11について試験例 1と同様にアレルゲン失活作用 を評価した。その結果を表 8に示す。
[0071] 試験例 5 ハウスダスト凝集効果の評価
直径 9cmのプラスチックシャーレに、塵埃として標準ダスト〔コットンリンタ、（財）日本 空気清浄協会製〕 10mgを入れ、市販のハンドスプレー容器に充填してなる試験液 6 または比較試験液 4〜： 11を 0.7mL標準ダストめがけて噴霧した。室温にて乾燥させた 後、実体顕微鏡 (Nikon製;拡大倍率 50倍）にて顕鏡し、以下の評価基準に従って、 標準ダストの吸着、凝集の程度を観察した。なお、対照として、プラスチックシャーレ に標準ダストを入れただけのもの、試験液の代わりに水を噴霧したものを同様に観察 した。その結果を表 8に示す。
[0072] 〈標準ダストの吸着 ·凝集性〉
〇：吸着 ·凝集性有り
X：吸着 ·凝集性無し
[0073] なお、標準ダストの吸着'凝集性を評価する上では、対照の場合を標準ダストの吸 着-凝集性なしとして、標準ダストの吸着 ·凝集状態を観察することにより評価した。ま た、標準ダストの実体顕微鏡写真を図 1に、各評価 (それぞれ Xおよび〇）の実体顕 微鏡写真を図 2および 3に示す。
[0074] [表 8]
Figure imgf000014_0001
表 8の結果より、凝集剤としてアルギン酸ナトリウム、ノ レイショデンプン、ポリビュル アルコールまたはメチルセルロースを使用した比較試験液において、配合割合が約 0 .001重量％ (比較例 4、 6、 8および 10)では、標準ダストに対して吸着 ·凝集性が認め られず（図 2)、標準ダストに対する吸着 ·凝集性を発揮するため配合割合を高めると（ 比較例 5、 7、 9および 11)、酸化チタンのアレルゲン失活作用を阻害した。これに対 して、ポリアクリル酸ナトリウム（実施例 6)では、約 0.001重量％という低濃度でさえ、標 準ダストに対する吸着 ·凝集性が認められ（図 3)、アレルゲン失活作用をも阻害しな かった。
産業上の利用可能性
本発明によれば、アレルゲンの効果的な失活を可能にするアレルゲン失活剤、ハウ スダストの効果的な除去を可能にするハウスダスト処理剤、スプレーならびにシートを 提供すること力 Sできる。

Claims

請求の範囲
[1] 光触媒機能を持つ酸化チタンを含有するアレルゲン失活剤。
[2] 水、低級アルコールまたはその混合物をさらに含有する請求項 1記載のアレルゲン 失活剤。
[3] 請求項 1または 2記載のアレルゲン失活剤およびポリアクリル酸ナトリウムを含有す るハウスダスト処理剤。
[4] 請求項 3記載のハウスダスト処理剤をスプレー容器に充填してなるハウスダスト処理 用スプレー。
[5] 請求項 3記載のハウスダスト処理剤をシート材に含浸してなるハウスダスト処理用シ ート。
[6] アレルゲンを失活させるための、光触媒機能を持つ酸化チタンの使用。
[7] 水、低級アルコールまたはその混合物に光触媒機能を持つ酸化チタンおよびポリ アクリル酸ナトリウムを分散する工程を含む、ハウスダスト処理剤の製造方法。
PCT/JP2006/305415 2005-03-25 2006-03-17 アレルゲン失活剤 WO2006103960A1 (ja)