WO2000070694A1 - Mit metalloxiden beschichtete lithium-mischoxid-partikel - Google Patents
Mit metalloxiden beschichtete lithium-mischoxid-partikel Download PDFInfo
- Publication number
- WO2000070694A1 WO2000070694A1 PCT/EP2000/003682 EP0003682W WO0070694A1 WO 2000070694 A1 WO2000070694 A1 WO 2000070694A1 EP 0003682 W EP0003682 W EP 0003682W WO 0070694 A1 WO0070694 A1 WO 0070694A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- lithium
- oxide particles
- mixed oxide
- coated
- metal
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
- C01G53/00—Compounds of nickel
- C01G53/40—Nickelates
- C01G53/42—Nickelates containing alkali metals, e.g. LiNiO2
- C01G53/44—Nickelates containing alkali metals, e.g. LiNiO2 containing manganese
- C01G53/50—Nickelates containing alkali metals, e.g. LiNiO2 containing manganese of the type [MnO2]n-, e.g. Li(NixMn1-x)O2, Li(MyNixMn1-x-y)O2
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M4/00—Electrodes
- H01M4/02—Electrodes composed of, or comprising, active material
- H01M4/13—Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
- H01M4/131—Electrodes based on mixed oxides or hydroxides, or on mixtures of oxides or hydroxides, e.g. LiCoOx
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09C—TREATMENT OF INORGANIC MATERIALS, OTHER THAN FIBROUS FILLERS, TO ENHANCE THEIR PIGMENTING OR FILLING PROPERTIES ; PREPARATION OF CARBON BLACK ; PREPARATION OF INORGANIC MATERIALS WHICH ARE NO SINGLE CHEMICAL COMPOUNDS AND WHICH ARE MAINLY USED AS PIGMENTS OR FILLERS
- C09C3/00—Treatment in general of inorganic materials, other than fibrous fillers, to enhance their pigmenting or filling properties
- C09C3/06—Treatment with inorganic compounds
- C09C3/063—Coating
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M4/00—Electrodes
- H01M4/02—Electrodes composed of, or comprising, active material
- H01M4/36—Selection of substances as active materials, active masses, active liquids
- H01M4/362—Composites
- H01M4/366—Composites as layered products
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01D—COMPOUNDS OF ALKALI METALS, i.e. LITHIUM, SODIUM, POTASSIUM, RUBIDIUM, CAESIUM, OR FRANCIUM
- C01D15/00—Lithium compounds
- C01D15/02—Oxides; Hydroxides
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
- C01G51/00—Compounds of cobalt
- C01G51/40—Cobaltates
- C01G51/42—Cobaltates containing alkali metals, e.g. LiCoO2
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/80—Particles consisting of a mixture of two or more inorganic phases
- C01P2004/82—Particles consisting of a mixture of two or more inorganic phases two phases having the same anion, e.g. both oxidic phases
- C01P2004/84—Particles consisting of a mixture of two or more inorganic phases two phases having the same anion, e.g. both oxidic phases one phase coated with the other
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M10/00—Secondary cells; Manufacture thereof
- H01M10/05—Accumulators with non-aqueous electrolyte
- H01M10/052—Li-accumulators
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M4/00—Electrodes
- H01M4/02—Electrodes composed of, or comprising, active material
- H01M4/36—Selection of substances as active materials, active masses, active liquids
- H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
- H01M4/50—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of manganese
- H01M4/505—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of manganese of mixed oxides or hydroxides containing manganese for inserting or intercalating light metals, e.g. LiMn2O4 or LiMn2OxFy
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M4/00—Electrodes
- H01M4/02—Electrodes composed of, or comprising, active material
- H01M4/36—Selection of substances as active materials, active masses, active liquids
- H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
- H01M4/52—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of nickel, cobalt or iron
- H01M4/525—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of nickel, cobalt or iron of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
- Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
- Y02E60/10—Energy storage using batteries
Definitions
- the invention relates to coated lithium mixed oxide particles for improving the high-temperature properties of electrochemical cells.
- the principle of operation of the lithium-ion battery is based on the fact that both the cathode and the anode materials can reversibly intercalate lithium ions. I.e. during charging, the lithium ions migrate out of the cathode, diffuse through the electrolyte and are intercalated in the anode. The same process takes place in the opposite direction when unloading. Because of this mode of operation, these batteries are also called “rocking chairs” or lithium-ion batteries.
- the resulting voltage of such a cell is determined by the lithium intercalation potentials of the electrodes.
- cathode materials that intercalate lithium ions at very high potentials and anode materials that intercalate lithium ions at very low potentials (vs. Li / Li + ).
- Cathode materials that meet these requirements are LiCo0 2 and LiNi0 2 , which have a layer structure, and LiMn 2 0 4 , which has a cubic spatial network structure. These compounds deintercalate lithium ions at potentials around 4V (vs Li / Li + ).
- certain carbon compounds such as. B. Graphite the requirement of low potential and high capacity.
- LiCo0 2 , LiNi0 2 and LiMn 2 0 4 are discussed and used for 4V cathodes.
- Mixtures are used as the electrolyte which, in addition to a conductive salt, also contain aprotic solvents.
- the most commonly used solvents are ethylene carbonate (EC), propylene carbonate (PC), dimethyl carbonate (DMC), diethyl carbonate (DEC) and ethyl methyl carbonate (EMC).
- EC ethylene carbonate
- PC propylene carbonate
- DMC dimethyl carbonate
- DEC diethyl carbonate
- EMC ethyl methyl carbonate
- LiPF 6 is used almost without exception.
- Graphite is usually used as the anode.
- Cathode materials especially the lithium manganese spinel
- lithium manganese spinel is for the cathode
- a disadvantage of the spinel is its lower capacity and its insufficient high-temperature storage capacity and the associated poor cycle stability at high temperatures. The reason for this is considered to be the solubility of the divalent manganese in the electrolyte (Solid State Ionics 69 (1994) 59; J. Power Sources 66 (1997) 129; J. Electrochem. Soc. 144 (1997) 2178).
- the manganese is present in two oxidation states, namely trivalent and tetravalent.
- the LiPF 6 -containing electrolyte always contains water impurities. This water reacts with the conductive salt LiPF 6 to form LiF and acidic components, eg HF.
- One way to increase the stability of the spinel at high temperatures is to dope it.
- part of the manganese ions can be replaced by other, for example trivalent, metal cations.
- Antonini et al. report that spinels doped with gallium and chromium (e.g.
- Li 1.02 Gao . o 25 C-ro . o 25 Mn 1.95 ⁇ 4 ) at 55 ° C show satisfactory storage and cycle stability (J. Electrochem. Soc, 145 (1998) 2726).
- a layer for example a lithium borate glass (Solid State Ionics 104 (1997) 13).
- a spinel is placed in a methanolic solution of H 3 B0 3 , LiBO 2 * 8H 2 0 and LiOH * H 2 0 given and stirred at 50-80 ° C until the solvent has completely evaporated.
- the powder is then heated to 600-800 ° C to ensure the conversion into the borate. This improves the shelf life at high temperatures. However, no improved cycle stability was found.
- WO 98/02930 undoped spinels are treated with alkali metal hydroxide solutions.
- the treated spinel is then heated in a CO 2 atmosphere in order to convert the adhering hydroxides into the corresponding carbonates.
- the spinels modified in this way show improved high-temperature shelf life as well as improved cycle stability at high temperatures.
- the cathode and / or anode is coated in such a way that the active material is pasted onto the current conductor together with binder and a conductive material. Then a paste consisting of the
- Coating material, binder and / or solvent applied to the electrode Inorganic and / or organic materials which can be conductive are named as coating materials, e.g. B. Al 2 0 3 , nickel, graphite, LiF, PVDF etc. Lithium-ion batteries that contain electrodes coated in this way show high voltages and capacities as well as improved safety characteristics (EP 836238).
- the electrode paste (cathode material: lithium manganese spinel) is first produced and applied to the current conductor. Then the protective layer, consisting of a metal oxide and binder, is pasted onto the electrode.
- Metal oxides used are, for example, aluminum oxide, titanium oxide and zirconium oxide.
- JP 08236114 likewise first produces the electrode, preferably LiNi 0 5 C0 0.5 O 2 as the active material, and then one Oxide layer applied by sputtering, vacuum evaporation or CVD.
- JP 09147916 a protective layer consisting of solid oxide particles, for example MgO, CaO, SrO, Zr0 2 , Al 2 0 3 Si0 2 , and a polymer is applied to the side of the current collector that contains the electrode.
- a protective layer consisting of solid oxide particles, for example MgO, CaO, SrO, Zr0 2 , Al 2 0 3 Si0 2 , and a polymer is applied to the side of the current collector that contains the electrode.
- JP 09165984 Another way is described in JP 09165984.
- the lithium manganese spinel which is coated with boron oxide, serves as the cathode material. This coating is created during the spinel synthesis.
- a lithium, manganese and boron compound are calcined in an oxidizing atmosphere.
- the boron oxide-coated spinels obtained in this way show no manganese dissolution at high voltages.
- JP 08250120 is used for coating with sulfides, selenides and tellurides
- the object of the present invention is to provide electrode materials which do not have the disadvantages of the prior art and which have improved storage stability and cycle stability at high temperatures, in particular at temperatures above room temperature.
- the object according to the invention is achieved by lithium mixed oxide particles which are coated with one or more metal oxides.
- the invention also relates to a method for coating the lithium mixed oxide particles and the use in electrochemical cells, batteries and secondary lithium batteries.
- the present invention relates to undoped and doped mixed oxides as cathode materials selected from the group Li (MnMe z ) 2 0 4 , Li (CoMe z ) 0 2 , Li (Ni 1 - x - y Co x Me y ) 0 2 , where Me is at least is a metal cation from the groups Ila, lila, IVa, Ilb, Illb, IVb, VIb, Vllb, VIII of the periodic table.
- Particularly suitable metal cations are copper, silver, nickel, magnesium, zinc, aluminum, iron, cobalt, chromium, titanium and zircon, and also lithium for the spinel compounds.
- the present invention also relates to other lithium intercalation and insertion compounds which are suitable for 4V cathodes with improved high-temperature properties, in particular at temperatures above room temperature, their production and use, in particular as cathode material in electrochemical cells.
- the lithium mixed oxide particles are coated with metal oxides in order to obtain improved storage stability and cyclability at high temperatures (above room temperature).
- metal oxides in particular oxides or mixed oxides of Zr, Al, Zn, Y, Ce, Sn, Ca, Si, Sr, Mg and Ti and mixtures thereof, for example ZnO, CaO, SrO, Si0 2 , CaTi0 3 , are suitable as coating materials.
- Particle has some advantages over the coating of the electrode strips. If the electrode material is damaged, a large part of the active material can attack the coated tapes, while these undesired reactions remain highly localized when the individual particles are coated.
- the coating process achieves layer thicknesses between 0.03 ⁇ m and 5 ⁇ m. Preferred layer thicknesses are between 0.05 ⁇ m and 3 ⁇ m.
- the lithium mixed oxide particles can be coated one or more times.
- the coated lithium mixed oxide particles can be processed with the usual carriers and auxiliaries to 4V cathodes for lithium-ion batteries.
- the coating is carried out at the supplier so that the battery manufacturer does not have to make the process changes necessary for the coating.
- the undesirable reactions of the electrode material with the electrolyte are strongly inhibited, and thus an improvement in the shelf life and cycle stability at higher temperatures is achieved.
- the cathode material according to the invention can be used in secondary lithium-ion batteries with common electrolytes.
- electrolytes with conductive salts selected from the group LiPF 6 , LiBF 4 , LiCI0 4 , LiAsF 6 , LiCF 3 S0 3 , LiN (CF 3 S0 2 ) 2 or LiC (CF 3 S0 2 ) 3 and mixtures thereof are suitable.
- the electrolytes can too contain organic isocyanates (DE 199 44 603) to reduce the water content.
- the electrolytes can also contain organic alkali salts (DE 199 10 968) as an additive.
- Alkali borates of the general formula are suitable
- R 1 and R 2 are the same or different
- each individually or jointly having the meaning of an aromatic or aliphatic carbon, dicarbon or sulfonic acid radical, or in each case individually or jointly meaning an aromatic ring from the group consisting of phenyl, naphthyl and anthracenyl or phenanthrenyl, which can be unsubstituted or substituted one to four times by A or shark, or in each case individually or jointly the meaning of a heterocyclic aromatic ring from the group pyridyl, pyrazyl or bipyridyl, which is unsubstituted or mono- to triple by A or shark may be substituted, or in each case individually or jointly, have the meaning of an aromatic hydroxy acid from the group of aromatic hydroxy-carboxylic acids or aromatic hydroxy-sulfonic acids, which may be unsubstituted or substituted one to four times by A or shark, and
- A is alkyl with 1 to 6 carbon atoms, which can be halogenated one to three times.
- Alkaline alcoholates of the general formula are also suitable Li + OR " , in which R has the meaning of an aromatic or aliphatic carbon, dicarbon or sulfonic acid residue, or
- aromatic hydroxy acid from the group of aromatic hydroxy-carboxylic acids or aromatic hydroxy-sulfonic acids, which can be unsubstituted or substituted one to four times by A or shark,
- a alkyl with 1 to 6 carbon atoms which can be halogenated one to three times.
- R 1 and R 2 are the same or different, optionally connected directly to one another by a single or double formation, each individually or jointly the meaning of an aromatic Rings from the group phenyl, naphthyl, anthracenyl or
- Phenanthrenyl which is unsubstituted or one to six times by alkyl
- Alkyl (Ci to C 6 ), alkoxy groups (d to C 6 ) or halogen (F, Cl, Br) can be substituted,
- R 3 -R 6 can each have the following meaning individually or in pairs, optionally directly linked to one another by a single or double bond:
- alkyl (d to C 6 ), alkyloxy (d to C 6 ) or halogen (F, Cl, Br)
- Phenyl, naphthyl, anthracenyl or phenanthrenyl which can be unsubstituted or monosubstituted to sixfold substituted by alkyl (d to C 6 ), alkoxy groups (d to C 6 ) or halogen (F, Cl, Br),
- Pyridyl, pyrazyl or pyrimidyl which can be unsubstituted or mono- to tetrasubstituted by alkyl (d to C 6 ), alkoxy groups (d to C 6 ) or halogen (F, Cl, Br),
- the end product is isolated can be contained in the electrolyte.
- electrolytes can be compounds of the following formula (DE 199 41 566)
- A N, P, P (O), O, S, S (O), S0 2 , As, As (O), Sb, Sb (O)
- A can be enclosed in different positions in R 1 , R 2 and / or R 3 ,
- Kt can be enclosed in a cyclic or heterocyclic ring
- the groups bound to Kt can be the same or different
- D + selected from the group of alkali metals in a polar organic solvent with a salt of the general formula
- Kt, A, R 1 , R 2 , R 3 , k, I, x and y have the meaning given above and
- R 1 to R 5 are the same or different, optionally connected directly to one another by a single or double formation, each individually or jointly the meaning
- alkyl or alkoxy radical (d to C 8 ) which can be partially or completely substituted by F, Cl, Br,
- an aromatic ring from the group phenyl, naphthyl, anthracenyl or phenanthrenyl, optionally bonded via oxygen, which may be unsubstituted or monosubstituted to sixfold substituted by alkyl (d to C 8 ) or F, Cl, Br an aromatic heterocyclic ring, optionally bonded via oxygen, from the group pyridyl, pyrazyl or pyrimidyl, which may be unsubstituted or substituted one to four times by alkyl (d to C 8 ) or F, Cl, Br and
- R 6 to R 8 are the same or different, optionally connected directly to one another by a single or double bond, each individually or jointly the meaning
- a hydrogen or the meaning as R 1 to R 5 prepared by reacting a corresponding boron or phosphorus-Lewis acid solvency adduct with a lithium or tetraalkylammonium imide, methanide or triflate can be used.
- borate salts (DE 199 59 722) of the general formula
- M is a metal ion or tetraalkylammonium ion
- R 1 to R 4 may be the same or different, optionally by means of a single or double bond directly bonded alkoxy or carboxy radicals (CC 8 ).
- These borate salts are prepared by reacting lithium tetraalcoholate borate or a 1: 1 mixture of lithium alcoholate with a boric acid ester in an aprotic solvent with a suitable hydroxyl or carboxyl compound in a ratio of 2: 1 or 4: 1.
- cathode materials in particular materials with a layer structure (for example Li (CoMe z ) 0 2 or Li (Ni 1. X - y Co x Me y ) 0 2 ) and spinels (for example Li (MnMe z ) 2 0 4 ) suspended in polar organic solvents such as alcohols, aldehydes, halides or ketones, spinels also in water and placed in a reaction vessel.
- polar organic solvents such as alcohols, aldehydes, halides or ketones
- spinels also in water and placed in a reaction vessel.
- the materials can also be suspended in non-polar organic solvents, such as cycloalkanes or aromatics.
- the reaction vessel can be heated and is equipped with a stirrer. The reaction solution is heated to temperatures between 10 and 100 ° C, depending on the boiling point of the solvent.
- Soluble metal salts selected from the group of zirconium, aluminum, zinc, yttrium, cerium, tin, calcium, silicon, strontium, titanium and magnesium salts and their mixtures, which are in organic solvents, are used as the coating solution , or water are soluble. Acids, bases or water are suitable as the hydrolysis solution, depending on the solvent used for the coating solution.
- the coating solution and the hydrolysis solution are slowly metered in.
- the dosing quantities and speeds depend on the desired layer thicknesses and the metal salts used.
- the hydrolysis solution is added in excess.
- the solution is filtered off and the powder obtained is dried.
- the dried powder In order to ensure complete conversion into the metal oxide, the dried powder must still be calcined.
- the powder is heated to 400 ° C. to 1000 ° C., preferably 700 to 850 ° C., and kept at this temperature for 10 minutes to 5 hours, preferably 20 to 60 minutes.
- the particles can be coated one or more times. If desired, the first coating can be carried out with a metal oxide and the next coatings with the oxides of other metals.
- Tetrapropyl orthozirconate (26.58 g), which is dissolved in ethanol (521.8 ml), serves as the coating solution.
- Water (14.66 g) is used as the hydrolysis solution. Both solutions are slowly added. The addition of zirconium propylate is complete after approx. 6.5 hours. To ensure that the hydrolysis reaction also takes place quantitatively, water (36.4 g) is added for the further hydrolysis for a further 16.2 hours.
- the ethanolic solution is filtered off and the powder obtained is dried at about 100.degree. To ensure complete conversion into the Zr0 2 , the dried powder must still be calcined. After drying, the powder is therefore heated to 800 ° C. and kept at this temperature for 30 minutes.
- Electrolyte mixed (LP600 Selectipur ® from Merck, EC: DEC: PC 2: 1: 3 1M LiPF 6 ).
- the aluminum bottles are then sealed gas-tight. These preparations are all carried out in an argon-flushed glove box.
- the bottles prepared in this way are then removed from the glove box and stored in a drying cabinet at 80 ° C. for 6 or 13 days.
- the aluminum bottles cooled to room temperature are reinserted into the glove box and opened there.
- the electrolyte is filtered off and the amount of manganese dissolved in the electrolyte is determined quantitatively by means of ICP-OES.
- Table 1 compares the analytical results of the uncoated and coated lithium manganese spinels.
- the cathode powder is mixed well with 15% conductive carbon black and 5% PVDF (binder material).
- the paste thus produced is applied to an aluminum mesh, which serves as a current conductor, and dried overnight at 175 ° C. under an argon atmosphere and under reduced pressure.
- the dried electrode is introduced into the glove box flushed with argon and the measuring cell is installed.
- Lithium metal serves as the counter and reference electrode.
- LP 50 Selectipur ® from Merck is used as the electrolyte (1 M LiPF 6 in EC: EMC 50: 50% by weight).
- the measuring cell with the electrodes and the electrolyte is placed in a steel container, which is sealed gas-tight.
- the cell produced in this way is removed from the glove box and placed in a climatic cabinet which is set to 60 ° C. After connecting the measuring cell to one
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Electrochemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- General Chemical & Material Sciences (AREA)
- Composite Materials (AREA)
- Inorganic Chemistry (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Battery Electrode And Active Subsutance (AREA)
- Secondary Cells (AREA)
- Inorganic Compounds Of Heavy Metals (AREA)
- Compounds Of Iron (AREA)
Priority Applications (6)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
AU47512/00A AU4751200A (en) | 1999-05-15 | 2000-04-25 | Lithium-mixed oxide particles coated with metal-oxides |
KR1020017014531A KR20020013887A (ko) | 1999-05-15 | 2000-04-25 | 금속 옥사이드로 피복된 리튬 혼합된 옥사이드 입자 |
BR0010566-0A BR0010566A (pt) | 1999-05-15 | 2000-04-25 | Partìculas misturadas de óxido de lìtio revestidas |
EP00929419A EP1188196A1 (de) | 1999-05-15 | 2000-04-25 | Mit metalloxiden beschichtete lithium-mischoxid-partikel |
CA002373756A CA2373756A1 (en) | 1999-05-15 | 2000-04-25 | Coated lithium mixed oxide particles |
JP2000619043A JP2003500318A (ja) | 1999-05-15 | 2000-04-25 | 金属酸化物で被覆されたリチウム混合酸化物粒子 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE19922522A DE19922522A1 (de) | 1999-05-15 | 1999-05-15 | Beschichtete Lithium-Mischoxid-Partikel und deren Verwendung |
DE19922522.2 | 1999-05-15 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2000070694A1 true WO2000070694A1 (de) | 2000-11-23 |
Family
ID=7908244
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2000/003682 WO2000070694A1 (de) | 1999-05-15 | 2000-04-25 | Mit metalloxiden beschichtete lithium-mischoxid-partikel |
Country Status (10)
Country | Link |
---|---|
EP (1) | EP1188196A1 (ja) |
JP (1) | JP2003500318A (ja) |
KR (1) | KR20020013887A (ja) |
CN (1) | CN1350706A (ja) |
AU (1) | AU4751200A (ja) |
BR (1) | BR0010566A (ja) |
CA (1) | CA2373756A1 (ja) |
DE (1) | DE19922522A1 (ja) |
RU (1) | RU2001132863A (ja) |
WO (1) | WO2000070694A1 (ja) |
Cited By (13)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2001291518A (ja) * | 2000-03-13 | 2001-10-19 | Samsung Sdi Co Ltd | リチウム二次電池用正極活物質及びその製造方法 |
US6749965B1 (en) * | 1999-02-10 | 2004-06-15 | Samsung Sdi Co., Ltd. | Positive active material for lithium secondary batteries and method of preparing the same |
US7138209B2 (en) | 2000-10-09 | 2006-11-21 | Samsung Sdi Co., Ltd. | Positive active material for rechargeable lithium battery and method of preparing same |
US7566479B2 (en) | 2003-06-23 | 2009-07-28 | Lg Chem, Ltd. | Method for the synthesis of surface-modified materials |
WO2012035211A1 (fr) * | 2010-09-17 | 2012-03-22 | Commissariat A L'energie Atomique Et Aux Energies Alternatives | Accumulateur au lithium tout solide et procédé de fabrication d'un tel accumulateur |
US8236449B2 (en) | 2005-07-11 | 2012-08-07 | Panasonic Corporation | Lithium ion secondary battery with improved electrode stability and safety |
WO2018149834A1 (de) | 2017-02-17 | 2018-08-23 | Evonik Degussa Gmbh | Mit aluminiumoxid und titandioxid umhüllte lithium-mischoxidpartikel und verfahren zu deren herstellung |
US10611931B2 (en) | 2015-08-28 | 2020-04-07 | Dupont Electronics, Inc. | Electrically conductive adhesives |
WO2021037904A1 (en) | 2019-08-27 | 2021-03-04 | Evonik Operations Gmbh | Mixed lithium transition metal oxide containing pyrogenically produced zirconium-containing oxides |
WO2021037900A1 (en) | 2019-08-27 | 2021-03-04 | Evonik Operations Gmbh | Mixed lithium transition metal oxide coated with pyrogenically produced zirconium-containing oxides |
US10967428B2 (en) | 2015-08-28 | 2021-04-06 | Dupont Electronics, Inc. | Coated copper particles and use thereof |
EP4002519A1 (en) | 2020-11-11 | 2022-05-25 | Evonik Operations GmbH | Transition metal oxide particles encapsulated in nanostructured lithium titanate or lithium aluminate, and the use thereof in lithium ion batteries |
WO2023232596A1 (en) | 2022-06-03 | 2023-12-07 | Evonik Operations Gmbh | Cathode active material particles encapsulated in pyrogenic, nanostructured magnesium oxide, and methods of making and using the same |
Families Citing this family (71)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6489060B1 (en) * | 1999-05-26 | 2002-12-03 | E-One Moli Energy (Canada) Limited | Rechargeable spinel lithium batteries with greatly improved elevated temperature cycle life |
JP4938919B2 (ja) * | 2000-01-14 | 2012-05-23 | ソニー株式会社 | 二次電池 |
DE10014884A1 (de) * | 2000-03-24 | 2001-09-27 | Merck Patent Gmbh | Beschichtete Lithium-Mischoxid-Partikel und ein Verfahren zu deren Herstellung |
EP1205998A2 (de) | 2000-11-10 | 2002-05-15 | MERCK PATENT GmbH | Elektrolyte |
DE10055811A1 (de) | 2000-11-10 | 2002-05-29 | Merck Patent Gmbh | Tetrakisfluoroalkylborat-Salze und deren Verwendung als Leitsalze |
KR100399642B1 (ko) | 2001-10-24 | 2003-09-29 | 삼성에스디아이 주식회사 | 리튬 이차 전지용 양극 활물질 및 그 제조방법 |
JP4307962B2 (ja) * | 2003-02-03 | 2009-08-05 | 三洋電機株式会社 | 非水電解質二次電池 |
JP2004311408A (ja) * | 2003-03-25 | 2004-11-04 | Nichia Chem Ind Ltd | 非水電解質二次電池用正極活物質および非水電解質二次電池 |
TWI286849B (en) | 2003-03-25 | 2007-09-11 | Nichia Corp | Positive electrode active material for nonaqueous electrolyte secondary battery and nonaqueous electrolyte secondary battery |
US8153295B2 (en) | 2003-07-17 | 2012-04-10 | Gs Yuasa International Ltd. | Positive electrode active material and its manufacturing method, positive electrode for lithium secondary cell using same, and lithium secondary cell |
CN100442577C (zh) * | 2003-07-17 | 2008-12-10 | 株式会社杰士汤浅 | 正极活性物质及其制造方法、以及锂二次电池的正极和锂二次电池 |
JP5036121B2 (ja) * | 2003-08-08 | 2012-09-26 | 三洋電機株式会社 | 非水電解質二次電池 |
JP4424949B2 (ja) * | 2003-09-09 | 2010-03-03 | 三洋電機株式会社 | 非水電解質二次電池 |
JP4967217B2 (ja) * | 2003-12-08 | 2012-07-04 | 日本電気株式会社 | 二次電池用正極活物質、それを用いた二次電池用正極および二次電池 |
JP4798962B2 (ja) * | 2004-05-06 | 2011-10-19 | 日本電工株式会社 | リチウムマンガン複合酸化物及びその製造方法 |
JP2005339886A (ja) * | 2004-05-25 | 2005-12-08 | Sanyo Electric Co Ltd | 非水電解質二次電池 |
JP4887671B2 (ja) * | 2004-06-17 | 2012-02-29 | トヨタ自動車株式会社 | リチウム二次電池と該電池に備えられる正極及びその製造方法 |
JP4683527B2 (ja) * | 2004-07-22 | 2011-05-18 | 日本化学工業株式会社 | 改質リチウムマンガンニッケル系複合酸化物、その製造方法、リチウム二次電池正極活物質及びリチウム二次電池 |
JP2006114256A (ja) * | 2004-10-12 | 2006-04-27 | Toyota Motor Corp | 二次電池用正極及びその利用 |
JP4721729B2 (ja) | 2004-11-12 | 2011-07-13 | 三洋電機株式会社 | 非水電解質二次電池 |
JP4841133B2 (ja) | 2004-11-16 | 2011-12-21 | 三洋電機株式会社 | 非水電解質二次電池 |
US10454106B2 (en) | 2004-12-31 | 2019-10-22 | Iucf-Hyu (Industry-University Cooperation Foundation Hanyang University) | Double-layer cathode active materials for lithium secondary batteries, method for preparing the active materials, and lithium secondary batteries using the active materials |
JP5196621B2 (ja) * | 2005-06-27 | 2013-05-15 | 一般財団法人電力中央研究所 | 常温溶融塩を用いたリチウムイオン二次電池およびその製造方法 |
CN100426562C (zh) * | 2005-09-14 | 2008-10-15 | 松下电器产业株式会社 | 非水电解质二次电池 |
JP5076332B2 (ja) * | 2006-03-06 | 2012-11-21 | ソニー株式会社 | 正極活物質の製造方法、および非水電解質二次電池の製造方法 |
EP2012380B1 (en) | 2006-03-15 | 2011-06-29 | Sumitomo Chemical Company, Limited | Positive electrode active material powder |
US8080335B2 (en) * | 2006-06-09 | 2011-12-20 | Canon Kabushiki Kaisha | Powder material, electrode structure using the powder material, and energy storage device having the electrode structure |
JP5077131B2 (ja) | 2007-08-02 | 2012-11-21 | ソニー株式会社 | 正極活物質、並びにそれを用いた正極、および非水電解質二次電池 |
JP2009064576A (ja) * | 2007-09-04 | 2009-03-26 | Toyota Motor Corp | 正極活物質およびリチウム二次電池 |
JP5189384B2 (ja) * | 2008-02-29 | 2013-04-24 | 株式会社日立製作所 | リチウム二次電池 |
JP2009263176A (ja) * | 2008-04-25 | 2009-11-12 | Kanto Denka Kogyo Co Ltd | マグネシウムアルミニウム複合酸化物表面被覆スピネル型マンガン酸リチウム及びその製造方法、並びにそれを使用する正極活物質及び非水電解質電池 |
KR101875954B1 (ko) * | 2008-07-15 | 2018-07-06 | 다우 글로벌 테크놀로지스 엘엘씨 | 전지 전극용 무기 결합제 및 이의 수계 공정 |
KR101623963B1 (ko) * | 2008-08-04 | 2016-05-24 | 소니 가부시끼가이샤 | 정극 활물질 및 그것을 이용한 정극과 비수 전해질 2차 전지 |
WO2011052607A1 (ja) * | 2009-10-29 | 2011-05-05 | Agcセイミケミカル株式会社 | リチウムイオン二次電池用正極材料の製造方法 |
JP5747457B2 (ja) * | 2010-01-06 | 2015-07-15 | 三洋電機株式会社 | リチウム二次電池 |
JP5382061B2 (ja) | 2010-06-22 | 2014-01-08 | 日亜化学工業株式会社 | 非水電解液二次電池用正極組成物及び該正極組成物を用いた正極スラリー |
WO2012115263A1 (ja) * | 2011-02-25 | 2012-08-30 | 三洋電機株式会社 | 非水電解液二次電池 |
KR101288973B1 (ko) * | 2011-05-04 | 2013-07-24 | 삼성전자주식회사 | 전극활물질, 그 제조방법 및 이를 채용한 전극 및 리튬전지 |
KR20130050161A (ko) * | 2011-11-07 | 2013-05-15 | 삼성에스디아이 주식회사 | 전극활물질, 그 제조방법 및 이를 채용한 전극 및 리튬전지 |
CN104247101A (zh) * | 2012-04-11 | 2014-12-24 | 旭硝子株式会社 | 锂离子二次电池用正极活性物质 |
CN104350636B (zh) | 2012-07-09 | 2017-11-03 | 株式会社Lg 化学 | 用于高电压的正极活性材料和包含其的锂二次电池 |
KR101596272B1 (ko) * | 2013-01-03 | 2016-02-22 | 주식회사 엘지화학 | 리튬 복합 전이금속 산화물 제조용 장치, 이를 이용하여 제조된 리튬 복합 전이금속 산화물, 및 그 제조방법 |
US20160056469A1 (en) * | 2013-03-28 | 2016-02-25 | Sanyo Electric Co., Ltd. | Positive electrode for nonaqueous electrolyte secondary battery, method for manufacturing positive electrode for nonaqueous electrolyte secondary battery, and nonaqueous electrolyte secondary battery |
WO2015004705A1 (ja) * | 2013-07-08 | 2015-01-15 | 株式会社 日立製作所 | リチウムイオン二次電池用正極活物質 |
WO2015025844A1 (ja) | 2013-08-23 | 2015-02-26 | 日本電気株式会社 | リチウム鉄マンガン系複合酸化物およびそれを用いたリチウムイオン二次電池 |
KR101665766B1 (ko) | 2013-09-30 | 2016-10-12 | 주식회사 엘지화학 | 이차전지용 양극활물질 및 이의 제조 방법 |
KR101607013B1 (ko) | 2013-09-30 | 2016-03-28 | 주식회사 엘지화학 | 이차전지용 양극활물질 코팅 용액과 이의 제조 방법 |
KR101636148B1 (ko) | 2013-09-30 | 2016-07-04 | 주식회사 엘지화학 | 이차전지용 양극활물질, 이의 제조 방법 및 이를 포함하는 리튬 이차전지용 양극 |
WO2015065098A2 (ko) * | 2013-10-31 | 2015-05-07 | 주식회사 엘지화학 | 양극 활물질, 이의 제조방법, 및 이를 포함하는 리튬 이차전지 |
CN105449196B (zh) * | 2014-08-28 | 2019-01-08 | 宁德时代新能源科技股份有限公司 | 复合正极活性物质及锂离子二次电池 |
US10847788B2 (en) | 2015-02-20 | 2020-11-24 | Nec Corporation | Lithium-iron-manganese-based composite oxide and lithium-ion secondary battery using same |
WO2017102550A1 (en) * | 2015-12-18 | 2017-06-22 | Basf Se | Non-aqueous electrolytes for lithium-ion batteries comprising asymmetric borates |
US11942632B2 (en) * | 2016-10-06 | 2024-03-26 | Lg Energy Solution, Ltd. | Positive electrode active material particle including core containing lithium cobalt oxide and shell containing composite metal oxide and preparation method thereof |
CA3042432A1 (en) * | 2016-11-14 | 2018-05-17 | Lilac Solutions, Inc. | Lithium extraction with coated ion exchange particles |
CN108110311B (zh) * | 2016-11-25 | 2021-05-14 | 深圳新宙邦科技股份有限公司 | 一种锂离子电池 |
KR102448302B1 (ko) * | 2017-04-28 | 2022-09-29 | 삼성전자주식회사 | 복합양극활물질, 이를 채용한 양극과 리튬전지 및 그 제조방법 |
JP7187123B2 (ja) * | 2017-05-01 | 2022-12-12 | テイカ株式会社 | 蓄電デバイス用ガス発生抑制剤およびこの蓄電デバイス用ガス発生抑制剤を用いた蓄電デバイス用正極および蓄電デバイス |
US11253848B2 (en) | 2017-08-02 | 2022-02-22 | Lilac Solutions, Inc. | Lithium extraction with porous ion exchange beads |
KR20230026524A (ko) * | 2017-11-13 | 2023-02-24 | 더 리전츠 오브 더 유니버시티 오브 콜로라도, 어 바디 코퍼레이트 | 혼합 금속 산화물 상 박막 코팅 |
CN108091848A (zh) * | 2017-12-12 | 2018-05-29 | 桑顿新能源科技有限公司 | 一种碳包覆的介孔硅基负极材料及其制备方法 |
CN108134073B (zh) * | 2017-12-25 | 2020-02-18 | 桑德新能源技术开发有限公司 | 一种三元正极材料及其制备方法 |
CN112041470A (zh) | 2018-02-28 | 2020-12-04 | 锂莱克解决方案公司 | 用于提取锂的具有颗粒捕集器的离子交换反应器 |
CN108832093B (zh) * | 2018-06-12 | 2020-06-26 | 桑德新能源技术开发有限公司 | 一种复合正极材料、制备方法及锂离子电池 |
CN110002546B (zh) * | 2019-02-19 | 2022-06-17 | 江苏海普功能材料有限公司 | 一种活化(Cu-Fe-Ce)/Al2O3纳米粒子电极的制备及其应用 |
CN110104739B (zh) * | 2019-05-27 | 2022-02-11 | 中国华能集团清洁能源技术研究院有限公司 | 一种用于处理工业循环冷却水高效电极及其制备方法 |
JP2023514803A (ja) | 2020-01-09 | 2023-04-11 | ライラック ソリューションズ,インク. | 望ましくない金属を分離するための方法 |
WO2021220875A1 (ja) * | 2020-04-27 | 2021-11-04 | パナソニックIpマネジメント株式会社 | 非水電解質二次電池用正極活物質、及び非水電解質二次電池 |
KR20230023714A (ko) | 2020-06-09 | 2023-02-17 | 리락 솔루션즈, 인크. | 스케일런트의 존재 하에서의 리튬 추출 |
EP4247759A1 (en) | 2020-11-20 | 2023-09-27 | Lilac Solutions, Inc. | Lithium production with volatile acid |
WO2022226219A1 (en) | 2021-04-23 | 2022-10-27 | Lilac Solutions, Inc. | Ion exchange devices for lithium extraction |
CN113373443B (zh) * | 2021-05-20 | 2022-09-06 | 浙江锋锂新能源科技有限公司 | 一种气液混合处理锂金属表面的方法及锂金属电池 |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0511632A1 (en) * | 1991-04-30 | 1992-11-04 | Sony Corporation | Nonaqueous electrolyte secondary battery |
JPH08236114A (ja) * | 1995-02-27 | 1996-09-13 | Sanyo Electric Co Ltd | リチウム二次電池 |
EP0789410A1 (en) * | 1996-02-02 | 1997-08-13 | Matsushita Electric Industrial Co., Ltd. | Batteries and a manufacturing method of postitive active material for the batteries |
WO1997049136A1 (en) * | 1996-06-14 | 1997-12-24 | N.V. Union Miniere S.A. | Electrode material for rechargeable batteries and process for the preparation thereof |
EP0997956A1 (en) * | 1998-10-27 | 2000-05-03 | Toda Kogyo Corporation | Manganese oxide, lithium manganese complex oxide and cobalt-coated lithium manganese complex oxide; and preparation processes thereof |
-
1999
- 1999-05-15 DE DE19922522A patent/DE19922522A1/de not_active Withdrawn
-
2000
- 2000-04-25 CA CA002373756A patent/CA2373756A1/en not_active Abandoned
- 2000-04-25 CN CN00807605A patent/CN1350706A/zh active Pending
- 2000-04-25 AU AU47512/00A patent/AU4751200A/en not_active Abandoned
- 2000-04-25 EP EP00929419A patent/EP1188196A1/de not_active Ceased
- 2000-04-25 JP JP2000619043A patent/JP2003500318A/ja active Pending
- 2000-04-25 KR KR1020017014531A patent/KR20020013887A/ko not_active Application Discontinuation
- 2000-04-25 WO PCT/EP2000/003682 patent/WO2000070694A1/de not_active Application Discontinuation
- 2000-04-25 BR BR0010566-0A patent/BR0010566A/pt not_active Application Discontinuation
- 2000-04-25 RU RU2001132863/09A patent/RU2001132863A/ru not_active Application Discontinuation
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0511632A1 (en) * | 1991-04-30 | 1992-11-04 | Sony Corporation | Nonaqueous electrolyte secondary battery |
JPH08236114A (ja) * | 1995-02-27 | 1996-09-13 | Sanyo Electric Co Ltd | リチウム二次電池 |
EP0789410A1 (en) * | 1996-02-02 | 1997-08-13 | Matsushita Electric Industrial Co., Ltd. | Batteries and a manufacturing method of postitive active material for the batteries |
WO1997049136A1 (en) * | 1996-06-14 | 1997-12-24 | N.V. Union Miniere S.A. | Electrode material for rechargeable batteries and process for the preparation thereof |
EP0997956A1 (en) * | 1998-10-27 | 2000-05-03 | Toda Kogyo Corporation | Manganese oxide, lithium manganese complex oxide and cobalt-coated lithium manganese complex oxide; and preparation processes thereof |
Non-Patent Citations (2)
Title |
---|
AMATUCCI G G ET AL: "Surface treatments of Li1+xMn2-xO4 spinels for improved elevated temperature performance", SOLID STATE IONICS,NL,NORTH HOLLAND PUB. COMPANY. AMSTERDAM, vol. 104, no. 1-2, 1 December 1997 (1997-12-01), pages 13 - 25, XP004126247, ISSN: 0167-2738 * |
PATENT ABSTRACTS OF JAPAN vol. 1997, no. 01 31 January 1997 (1997-01-31) * |
Cited By (19)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6749965B1 (en) * | 1999-02-10 | 2004-06-15 | Samsung Sdi Co., Ltd. | Positive active material for lithium secondary batteries and method of preparing the same |
USRE43276E1 (en) | 2000-03-13 | 2012-03-27 | Samsung Sdi Co., Ltd. | Positive active material for rechargeable lithium battery and method of preparing same |
JP4574877B2 (ja) * | 2000-03-13 | 2010-11-04 | 三星エスディアイ株式会社 | リチウム二次電池用正極活物質及びその製造方法 |
JP2001291518A (ja) * | 2000-03-13 | 2001-10-19 | Samsung Sdi Co Ltd | リチウム二次電池用正極活物質及びその製造方法 |
US7138209B2 (en) | 2000-10-09 | 2006-11-21 | Samsung Sdi Co., Ltd. | Positive active material for rechargeable lithium battery and method of preparing same |
US8007941B2 (en) | 2000-10-09 | 2011-08-30 | Samsung Sdi Co., Ltd. | Positive active material for rechargeable lithium battery and method of preparing same |
US8034486B2 (en) | 2000-10-09 | 2011-10-11 | Samsung Sdi Co., Ltd. | Positive active material for rechargeable lithium battery and method of preparing same |
US7566479B2 (en) | 2003-06-23 | 2009-07-28 | Lg Chem, Ltd. | Method for the synthesis of surface-modified materials |
US8236449B2 (en) | 2005-07-11 | 2012-08-07 | Panasonic Corporation | Lithium ion secondary battery with improved electrode stability and safety |
FR2965106A1 (fr) * | 2010-09-17 | 2012-03-23 | Commissariat Energie Atomique | Electrode pour accumulateur au lithium tout solide et procede de realisation d'une telle electrode |
WO2012035211A1 (fr) * | 2010-09-17 | 2012-03-22 | Commissariat A L'energie Atomique Et Aux Energies Alternatives | Accumulateur au lithium tout solide et procédé de fabrication d'un tel accumulateur |
US9105903B2 (en) | 2010-09-17 | 2015-08-11 | Commissariat A L'energie Atomique Et Aux Energies Alternatives | All-solid-state lithium battery, and production method therefor |
US10611931B2 (en) | 2015-08-28 | 2020-04-07 | Dupont Electronics, Inc. | Electrically conductive adhesives |
US10967428B2 (en) | 2015-08-28 | 2021-04-06 | Dupont Electronics, Inc. | Coated copper particles and use thereof |
WO2018149834A1 (de) | 2017-02-17 | 2018-08-23 | Evonik Degussa Gmbh | Mit aluminiumoxid und titandioxid umhüllte lithium-mischoxidpartikel und verfahren zu deren herstellung |
WO2021037904A1 (en) | 2019-08-27 | 2021-03-04 | Evonik Operations Gmbh | Mixed lithium transition metal oxide containing pyrogenically produced zirconium-containing oxides |
WO2021037900A1 (en) | 2019-08-27 | 2021-03-04 | Evonik Operations Gmbh | Mixed lithium transition metal oxide coated with pyrogenically produced zirconium-containing oxides |
EP4002519A1 (en) | 2020-11-11 | 2022-05-25 | Evonik Operations GmbH | Transition metal oxide particles encapsulated in nanostructured lithium titanate or lithium aluminate, and the use thereof in lithium ion batteries |
WO2023232596A1 (en) | 2022-06-03 | 2023-12-07 | Evonik Operations Gmbh | Cathode active material particles encapsulated in pyrogenic, nanostructured magnesium oxide, and methods of making and using the same |
Also Published As
Publication number | Publication date |
---|---|
CA2373756A1 (en) | 2000-11-23 |
CN1350706A (zh) | 2002-05-22 |
EP1188196A1 (de) | 2002-03-20 |
BR0010566A (pt) | 2002-02-19 |
DE19922522A1 (de) | 2000-11-16 |
RU2001132863A (ru) | 2003-08-10 |
JP2003500318A (ja) | 2003-01-07 |
AU4751200A (en) | 2000-12-05 |
KR20020013887A (ko) | 2002-02-21 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2000070694A1 (de) | Mit metalloxiden beschichtete lithium-mischoxid-partikel | |
DE10014884A1 (de) | Beschichtete Lithium-Mischoxid-Partikel und ein Verfahren zu deren Herstellung | |
EP3429000B1 (en) | Modified positive active material and preparation method therefor, and electrochemical energy storage device | |
EP2717364B1 (en) | Use of a positive electrode material for a sulfide-based solid electrolyte battery and sulfide-based solid electrolyte battery with such positive electrode material | |
US20230077131A1 (en) | Positive electrode material, preparation method therefor, and lithium ion secondary battery | |
EP1087452A2 (de) | Beschichtete Lithium-Mischoxid-Partikel und deren Verwendung II | |
DE19615686A1 (de) | Lithiummanganoxid-Einfügungsverbindungen, Verfahren zu ihrer Herstellung sowie deren Verwendung in Akkumulatoren | |
DE112012004372T5 (de) | Sekundärbatterie mit nicht wässrigem elektrolyten und verfahren zur herstellung der selben | |
WO2000055935A1 (de) | Anwendung von additiven in elektrolyten für elektrochemische zellen | |
DE112013000854T5 (de) | Sulfidfestkörperelektrolytmaterial, Batterie und Herstellungsverfahren für das Sulfidfestkörperelektrolytmaterial | |
CN105900266B (zh) | 电极及非水电解质电池 | |
DE112012002265T5 (de) | Festkörperbatteriesystem und Herstellungsverfahren einer regenerierbaren Festkörpersekundärbatterie | |
DE102014223147A1 (de) | Chromdotiertes Lithium-Titanat als Kathodenmaterial | |
DE112013007268T5 (de) | Beschichtete lithiumreiche Schichtoxide und ihre Vorbereitung | |
US11735728B2 (en) | Cathode active material for non-aqueous electrolyte secondary battery and method of manufacturing cathode active material for non-aqueous electrolyte secondary battery | |
EP3678236A1 (en) | Positive electrode active material for lithium secondary batteries, positive electrode for lithium secondary batteries, and lithium secondary battery | |
CN109428066A (zh) | 核壳材料及其制备方法、锂离子电池负极材料及锂离子电池 | |
DE102020123448A1 (de) | Kathodenaktives Material für Lithium-Sekundärbatterie und Verfahren zur Herstellung desselben | |
DE112017007079T5 (de) | Verfahren zum stabilisieren von lithiumtitanatoxid (lto) durch elektrolytvorbehandlung | |
DE112019007641T5 (de) | Positives aktivmaterial, positive elektrode, nichtwässriger-elektrolyt-energiespeicher vorrichtung, verfahren zum herstellen eines positiven aktivmaterials, verfahren zum herstellen einer positiven elektrode, und verfahren zum herstellen einer nichtwässriger-elektrolyt-energiespeichervorrichtung | |
DE102015115120A1 (de) | Sekundärbatterie mit nichtwässrigem elektrolyt | |
DE102004008397B4 (de) | Positives aktives Elektrodenmaterial, Verfahren zur Herstellung eines positiven aktiven Elektrodenmaterials und Lithium-Sekundärzelle | |
EP4145555A1 (en) | Positive electrode material and battery | |
Huiyong et al. | Influence of Sc3+ on LiMn2O4 cathode materials at elevated temperature | |
US20240170718A1 (en) | Solid electrolyte material and battery including the same |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
WWE | Wipo information: entry into national phase |
Ref document number: 00807605.7 Country of ref document: CN |
|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): AE AL AM AT AU AZ BA BB BG BR BY CA CH CN CR CU CZ DE DK DM EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR LR LS LT LU LV MA MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): GH GM KE LS MW SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG |
|
DFPE | Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101) | ||
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
WWE | Wipo information: entry into national phase |
Ref document number: 2000929419 Country of ref document: EP |
|
ENP | Entry into the national phase |
Ref document number: 2373756 Country of ref document: CA Ref document number: 2373756 Country of ref document: CA Kind code of ref document: A Ref document number: 2000 619043 Country of ref document: JP Kind code of ref document: A |
|
WWE | Wipo information: entry into national phase |
Ref document number: 1020017014531 Country of ref document: KR Ref document number: 09959983 Country of ref document: US |
|
WWP | Wipo information: published in national office |
Ref document number: 1020017014531 Country of ref document: KR |
|
WWP | Wipo information: published in national office |
Ref document number: 2000929419 Country of ref document: EP |
|
REG | Reference to national code |
Ref country code: DE Ref legal event code: 8642 |
|
WWR | Wipo information: refused in national office |
Ref document number: 2000929419 Country of ref document: EP |
|
WWW | Wipo information: withdrawn in national office |
Ref document number: 2000929419 Country of ref document: EP |
|
WWW | Wipo information: withdrawn in national office |
Ref document number: 1020017014531 Country of ref document: KR |