RU2007120390A - Модифицированные материалы носителей для катализаторов - Google Patents
Модифицированные материалы носителей для катализаторов Download PDFInfo
- Publication number
- RU2007120390A RU2007120390A RU2007120390/04A RU2007120390A RU2007120390A RU 2007120390 A RU2007120390 A RU 2007120390A RU 2007120390/04 A RU2007120390/04 A RU 2007120390/04A RU 2007120390 A RU2007120390 A RU 2007120390A RU 2007120390 A RU2007120390 A RU 2007120390A
- Authority
- RU
- Russia
- Prior art keywords
- catalyst
- less
- procatalyst
- carrier material
- clause
- Prior art date
Abstract
1. Способ получения алкенилалканоатов, включающий:введение исходного сырья, содержащего этилен, уксусную кислоту и кислородсодержащий газ, в контакт с катализатором или прокатализатором, полученным на материале носителя, с образованием винилацетата, где перед добавлением палладийсодержащего и золотосодержащего каталитических компонентов материал носителя модифицируют в результате добавления раствора предшественника модификатора к материалу носителя, где материал носителя выбирают из диоксида циркония, титаносиликата или цирконосиликата.2. Способ по п.1, где перед добавлением каталитических компонентов модифицированный материал носителя подвергают прокаливанию.3. Способ по п.1 или 2, где соотношение этилацетата и винилацетата составляет величину, меньшую приблизительно 800 ч./млн.4. Способ по п.1 или 2, где соотношение этилацетата и полученного алкенилалканоата составляет величину, меньшую приблизительно 250 ч./млн.5. Способ по п.1 или 2, где катализатор или прокатализатор содержит калиевый активатор.6. Способ по п.1 или 2, где катализатор или прокатализатор характеризуется селективностью получения СО, меньшей приблизительно 9,0%.7. Способ по п.6, где катализатор или прокатализатор характеризуется селективностью получения СО, меньшей приблизительно 9,0%, при степени превращения О45%.8. Способ по п.7, где соотношение этилацетата и винилацетата составляет величину, меньшую приблизительно 800 ч./млн, и где катализатор или прокатализатор характеризуется селективностью получения СО, меньшей приблизительно 9,0%.9. Способ по п.8, где соотношение этилацетата и винилацетата составляет величину, меньшую приблизительно 800 ч./млн, и �
Claims (30)
1. Способ получения алкенилалканоатов, включающий:
введение исходного сырья, содержащего этилен, уксусную кислоту и кислородсодержащий газ, в контакт с катализатором или прокатализатором, полученным на материале носителя, с образованием винилацетата, где перед добавлением палладийсодержащего и золотосодержащего каталитических компонентов материал носителя модифицируют в результате добавления раствора предшественника модификатора к материалу носителя, где материал носителя выбирают из диоксида циркония, титаносиликата или цирконосиликата.
2. Способ по п.1, где перед добавлением каталитических компонентов модифицированный материал носителя подвергают прокаливанию.
3. Способ по п.1 или 2, где соотношение этилацетата и винилацетата составляет величину, меньшую приблизительно 800 ч./млн.
4. Способ по п.1 или 2, где соотношение этилацетата и полученного алкенилалканоата составляет величину, меньшую приблизительно 250 ч./млн.
5. Способ по п.1 или 2, где катализатор или прокатализатор содержит калиевый активатор.
6. Способ по п.1 или 2, где катализатор или прокатализатор характеризуется селективностью получения СО2, меньшей приблизительно 9,0%.
7. Способ по п.6, где катализатор или прокатализатор характеризуется селективностью получения СО2, меньшей приблизительно 9,0%, при степени превращения О2 45%.
8. Способ по п.7, где соотношение этилацетата и винилацетата составляет величину, меньшую приблизительно 800 ч./млн, и где катализатор или прокатализатор характеризуется селективностью получения СО2, меньшей приблизительно 9,0%.
9. Способ по п.8, где соотношение этилацетата и винилацетата составляет величину, меньшую приблизительно 800 ч./млн, и где катализатор или прокатализатор характеризуется селективностью получения СО2, меньшей приблизительно 9,0%, при степени превращения О2 45%.
10. Способ по п.6, где соотношение этилацетата и винилацетата составляет величину, меньшую приблизительно 250 ч./млн, и где катализатор или прокатализатор характеризуется селективностью получения СО2, меньшей приблизительно 9,0%.
11. Способ по п.10, где соотношение этилацетата и винилацетата составляет величину, меньшую приблизительно 250 ч./млн, и где катализатор или прокатализатор характеризуется селективностью получения СО2, меньшей приблизительно 9,0%, при степени превращения О2 45%.
12. Способ по п.1 или 2, где раствор предшественника модификатора содержит ниобий, титан, магний или их комбинации.
13. Способ по п.1 или 2, где после добавления каталитических компонентов материал носителя подвергают прокаливанию.
14. Способ по п.1 или 2, где материал носителя представляет собой слоистый материал носителя.
15. Способ получения катализатора или прокатализатора, подходящего для получения алкенилалканоатов, включающий:
импрегнирование материала носителя водным раствором предшественника модификатора;
импрегнирование модифицированного материала водным раствором предшественника каталитического компонента и
восстановление предшественника каталитического компонента в результате введения материала носителя в контакт с восстанавливающей средой,
где материал носителя выбирают из диоксида циркония, титаносиликата или цирконосиликата.
16. Способ по п.15, дополнительно включающий прокаливание модифицированного материала носителя в невосстанавливающей атмосфере перед импрегнированием водным раствором предшественника каталитического компонента.
17. Способ по п.15 или 16, где стадия прокаливания модифицированного материала носителя включает прокаливание при температуре от приблизительно 300°С до приблизительно 700°С.
18. Способ по п.15 или 16, где первая стадия импрегнирования включает импрегнирование материала носителя модификатором в количестве от приблизительно 0,1 до приблизительно 4,0% при расчете на массу материала носителя.
19. Способ по п.15 или 16, где водный раствор предшественника каталитического компонента содержит золото, палладий или их комбинацию.
20. Способ по п.15 или 16, где атомное отношение между золотом и палладием находится в диапазоне от приблизительно 0,3 до приблизительно 0,90.
21. Способ по п.15 или 16, где раствор предшественника модификатора содержит барий, магний, церий, калий, кальций, ниобий, тантал, титан, иттрий, стронций, цирконий, лантан, празеодим, ванадий, молибден, рубидий или их бинарные комбинации.
22. Способ по п.21, где раствор предшественника модификатора содержит ниобий, титан, магний, цирконий или их комбинации.
23. Способ по п.22, где раствор предшественника модификатора содержит ниобий, титан, магний или их комбинации.
24. Способ по п.21, где раствор предшественника модификатора содержит хлорид, нитрат, оксалат, лактат или их комбинации.
25. Способ по п.15 или 16, где материал носителя представляет собой слоистый материал носителя.
26. Способ по п.15 или 16, дополнительно включающий прокаливание после импрегнирования модифицированного материала носителя раствором предшественника каталитического компонента.
27. Способ по п.15 или 16, дополнительно включающий введение катализатора или прокатализатора в контакт с активатором.
28. Способ по п.15 или 16, дополнительно включающий введение ацетата щелочного металла в контакт с материалом носителя в количестве приблизительно от 10 до 70 г на один 1 л катализатора.
29. Способ по п.28, где стадия введения в контакт каталитического компонента включает введение в контакт от приблизительно 1 до приблизительно 10 г палладия на 1 л катализатора и от приблизительно 0,5 до приблизительно 10 г золота на 1 л катализатора, при этом количество золота находится от приблизительно 10 до приблизительно 125% при расчете на массу палладия.
30. Катализатор или прокатализатор, полученные в соответствии со способом по пп.15-29.