KR960024741A - 침상 전기전도성 산화주석 미세 입자 및 그의 제조방법 - Google Patents

침상 전기전도성 산화주석 미세 입자 및 그의 제조방법 Download PDF

Info

Publication number
KR960024741A
KR960024741A KR1019950056590A KR19950056590A KR960024741A KR 960024741 A KR960024741 A KR 960024741A KR 1019950056590 A KR1019950056590 A KR 1019950056590A KR 19950056590 A KR19950056590 A KR 19950056590A KR 960024741 A KR960024741 A KR 960024741A
Authority
KR
South Korea
Prior art keywords
fine particles
tin oxide
oxide fine
needle
antimony
Prior art date
Application number
KR1019950056590A
Other languages
English (en)
Other versions
KR100394889B1 (ko
Inventor
하루오 오꾸다
히데오 후따마따
히데오 다까하시
노리히꼬 사네후지
Original Assignee
아까자와 다까시
이시하라상교 가부시끼가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP03150695A external-priority patent/JP3515625B2/ja
Priority claimed from JP05649595A external-priority patent/JP3365883B2/ja
Priority claimed from JP18093795A external-priority patent/JP3609159B2/ja
Application filed by 아까자와 다까시, 이시하라상교 가부시끼가이샤 filed Critical 아까자와 다까시
Publication of KR960024741A publication Critical patent/KR960024741A/ko
Application granted granted Critical
Publication of KR100394889B1 publication Critical patent/KR100394889B1/ko

Abstract

본 발명은 0.005~1㎛의 평균직경, 0.05~10㎛의 평균길이 및 3이상의 종횡비를 가지는 침상 전기전도성 산화주석 미세 입자를 제공한다. 또한, 본 발명은 주석, 규소 및 알칼리 금속 할라이드를 함유하는 출발물질을 700~1200℃에서 연소시키고 연소 생성물에서 가용성 염을 제거함으로 이루어지는 침상 전기전도성 산화주석 미세 입자의 제조방법을 제공한다.

Description

침상 전기전도성 산화주석 미세 입자 및 그의 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제3도는 실시예 11에서 수득된 안티몬을 함유하는 침상의 전기 전도성 산화주석 미세 입자의 입자 형태를 보여주는 전자현미경 사진(×100,000)이다, 제4도는 비교예 5에서 수득된 전기전도성 미세 입자의 입자 형태를 보여주는 전자현미경 사진(×100,000)이다.

Claims (20)

  1. 주석, 규소 및 알칼리 금속 할라이드를 함유하는 출발물질을 700~1200℃에서 연소시키고 연소 생성물에서 가용성 염을 제거함으로 이루어지는 0.005~1㎛의 평균직경, 0.05~10㎛의 평균길이 및 3 이상의 종횡비를 가지는 침상 전기전도성 산화주석 미세 입자의 제조방법.
  2. 제1항에 있어서, SiO2를 기준으로 한 출발물질내 규소의 함량은 SnO2의 중량에 대하여 0.3~20%인 방법.
  3. 제1항에 있어서, 가용성 염의 제거는 연소 생성물을 무기산의 매질로 처리함으로써 수행되는 방법.
  4. 제1항에 있어서, 출발물질은 주석, 규소, 알칼리 금속 할라이드 및 부가적으로 안티몬을 함유하는 방법.
  5. 제4항에 있어서, Sb2O3를 기준으로 한 출발물질내 안티몬의 함량은 SnO2의 중량에 대하여 0.1~8%인 방법.
  6. 제4항에 있어서, SiO2를 기준으로 한 출발물질내 규소의 함량은 SnO2의 중량에 대하여 0.3~20%인 방법.
  7. 제4항에 있어서, 가용성 염의 제거는 연소 생성물을 무기산의 매질로 처리함으로써 수행되는 방법.
  8. 안티몬 화합물의 용액을 제1항의 침상 전기전도성 산화주석 미세 입자의 현탁액에 첨가하고, 중화를 수행하여 산화주석 미세 입자의 표면에 함수 산화 안티몬을 부착시킨 후, 여과 회수된 생성물을 700~1000℃에서 연소시킴으로 이루어지는 안티몬 함유 침상 전기전도성 산화주석 미세 입자의 제조방법.
  9. 제8항에 있어서, Sb2O3를 기준으로 한 부착 안티몬의 양은 SnO2의 중량에 대하여 0.1~20%인 방법.
  10. 0.005~1㎛의 평균직경, 0.05-10㎛의 평균길이 및 3 이상의 종횡비를 가지는 침상 전기전도성 산화주석 미세 입자.
  11. 제10항에 있어서, 10KΩ㎝ 이하의 분말 저항을 가지는 침상 전기전도성 산화주석 미세 입자.
  12. 제10항에 있어서, SiO2를 기준으로 한 규소의 함량은 SnO2의 중량에 대하여 0.1~10%인 침상 전기전도성 산화주석 미세 입자.
  13. 제10항에 있어서, 안티몬을 함유하는 침상 전기전도성 산화 주석 미세 입자.
  14. 제13항에 있어서, 1kΩ㎝ 이하의 분말 저항을 가지며, 80~90의 L*값을 가지는 침상 전기전도성 산화주석 미세 입자.
  15. 제13항에 있어서, Sb/Sn비를 기준으로 한 안티몬의 함량은 0.1/100~20/100인 침상 전기전도성 산화주석 미세 입자.
  16. 제13항에 있어서, SiO2를 기준으로 한 규소의 함량은 SnO2의 중량에 대하여 0.1~10%인 침상 전기전도성 산화주석 미세 입자.
  17. 제10항의 침상 전기전도성 산화주석 미세 입자를 수성 매질에 분산시킴으로서 수득한 수성 분산액.
  18. 제13항의 안티몬 함유 침상 전기전도성 산화주석 미세 입자를 수성 매질에 분산시킴으로써 수득한 수성 분산액.
  19. 고체물질을 기준으로 하여 100중량부의 수지 및 제10항의 침상 전기전도성 산화주석 미세 입자 3~200중량부를 함유하는 전기 전도성 조성물.
  20. 고체물질을 기준으로 하여 100중량부의 수지 및 제13항의 안티몬 함유 침상 전기전도성 산화주석 미세입자 3~200중량부를 함유하는 전기전도성 조성물.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019950056590A 1994-12-27 1995-12-26 침상 전기전도성 산화주석 미세입자 및 그의 제조방법 KR100394889B1 (ko)