KR910004684A - 열가소성 올레핀 중합체 및 이의 제조 방법 - Google Patents
열가소성 올레핀 중합체 및 이의 제조 방법 Download PDFInfo
- Publication number
- KR910004684A KR910004684A KR1019900013007A KR900013007A KR910004684A KR 910004684 A KR910004684 A KR 910004684A KR 1019900013007 A KR1019900013007 A KR 1019900013007A KR 900013007 A KR900013007 A KR 900013007A KR 910004684 A KR910004684 A KR 910004684A
- Authority
- KR
- South Korea
- Prior art keywords
- polymer
- mpa
- alpha
- propylene
- component
- Prior art date
Abstract
내용 없음.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (20)
- a) (i) 일반식 H2C=CHR(여기서, R은 H또는 C2-6직쇄 또는 측쇄 알킬이다)을 갖고 85중량%이상의 프로필렌을 함유하며 아이소택틱 지수가 75보다 큰 알파-올레핀 하나 이상과 프로필렌의 공중합체, (ii) 아이소택틱 지수가 75보다 큰 폴리부텐-1, (iii) 밀도가 0.95g/㎤이상인 에틸렌 단독중합체 또는 에틸렌과 밀도가 0.915g/㎤이상인 C3-8알파-올레핀의 공중합체, (iv) 아이소택틱 지수가 85보다 큰 프로필렌의 단독중합체 10내지 90부(열가소성 올레핀 중합체를 기준으로 함)와 혼합된 중합체 분획(i), (ii)또는 (iii), 또는 이들 중합체 분획만의 혼합물 또는 아이소택틱 지수가 85보다 큰 프로필렌의 단독중합체 10내지 90부(열가소성 올레핀 중합체를 기준으로 함)와 혼합된 이들 중합체 분획의 혼합물로 구성된 그룹중에서 선택된 결정성 중합체 분획 60내지 약 85부, b) 실질적으로 성분 c)를 제조하는 데 사용되는 알파-올레핀 또는 2개의 알파-올레핀이 사용될 경우 최대량으로 존재하는 알파-올레핀 단위로 구성된, 실온에서 크실렌에 불용성이며 반-결정성, 저밀도인 기본적으로 선형인 공중합체 분획 약 1내지 15부, 및 c) 디엔 1내지 10%또는 일반식 H2C=CHR (여기서, R은 상기에서 정의한 바와 동일하다)의 상이한 알파-올레핀 터모노머 1내지 20%를 갖거나 갖지 않는, 경우에 따라 터모노머로서 존재하는 알파-올레핀을 제외한 알파-올레핀 약 30내지 약 80중량%를 함유하고 실온에서 크실렌에 가용성인, 프로필렌 및 일반식 H2C=CHR(여기서, R은 상기에서 정의한 바와 동일하다)의 알파-올레핀의 비결정성 공중합체 분획 약 10내지 39부[여기서, 성분 a), b) 및 c)의 총량은 100부이다]를 포함하고, 1000MPa 이하 내지 150MPa의 굴곡 모듈러스, 7MPa보다 큰 인장 강도, -18℃에서 유연 충격 파단을 일으키게 하는 충격 강도 및 200%이상의 파단점 신장률을 가짐을 특징으로 하는 열가소성 올레핀 중합체.
- 제1항에 있어서, 성분 a)가 (i)인 중합체.
- 제1항에 있어서, 성분 a)가 (ii)인 중합체.
- 제1항에 있어서, 성분 a)가 (iii)인 중합체.
- 제2항에 있어서, (i)이 프로필렌 및 에틸렌의 공중합체인 중합체.
- 제2항에 있어서, (i)의 아이소택틱 지수가 90보다 큰 중합체.
- 제3항에 있어서, (ii)의 아이소택틱 지수가 85보다 큰 중합체.
- 제4항에 있어서, (iii)이 에틸렌과 1내지 10%의 알파-올레핀의 공중합체인 중합체.
- 제4항에 있어서, (iii)이 에틸렌과 부텐-1의 공중합체인 중합체.
- 제4항에 있어서, (iii)이 에틸렌의 단독중합체인 중합체.
- 제1항에 있어서, 성분a)가, 아이소택틱 지수가 85보다 큰 프로필렌의 단독중합체 10내지 90부(열가소성 올레핀 중합체를 기준으로 함)과 혼합된 (i)인 중합체.
- 제1항에 있어서, 굴곡 모듈러스가 150내지 700MPa이고, 인장 강도가 10MPa보다 크고, 파단점 신장율이 500%보다 크고, 충격 강도가 바람직하게는 -29℃에서 유연 충격 파단을 일으키게 하는 정도인 중합체.
- 제1항에 있어서, 굴곡 모듈러스가 500내지 700MPa이고, 인장 강도가 13MPa보다 크며, 파단점 신장율이 500%보다 큰 중합체.
- 제1항에 있어서, 평균 직경이 250내지 7000μ이고, 유동능이 30초 미만이고, 용적 밀도(압축됨)가 0.4g/cc 이상인 구형 입자 형태로 존재하는 중합체.
- 제2항에 있어서, 굴곡 모듈러스가 150내지 700MPa이고, 인장 강도가 10MPa보다 크고, 파단점 신장율이 500%보다 크고, 충격 강도가 바람직하게는 -29℃에서 유연 충격 파단을 일으키게 하는 정도인 중합체.
- 제2항에 있어서, 굴곡 모듈러스가 500내지 700MPa이고, 인장 강도가 13MPa보다 크고, 파단점 신장율이 500%보다 큰 중합체.
- 제2항에 있어서, 평균 직경이 250내지 7000μ이고, 유동능이 30초 미만이고, 용적 밀도(압축됨)가 0.4g/cc 보다 큰 구형 입자 형태로 존재하는 중합체.
- 모든 중합 반응 단계에서 트리알킬알루미늄 화합물, 전자 공여체, 및 티탄의 할라이드 또는 할로겐-알코올레이트 및 무수 마그네슘 클로라이드상에 지지된 전자-공여체 화합물을 함유하는 고체 촉매 성분(이 성분은 100㎡/g미만의 표면적, 약 0.2내지 0.4cc/g의 다공성, 공극의 500%이상이 100°A보다 큰 반경을 갖는 공극 용적 분포를 갖고, 33.5°와 35°의 2v의 각 사이에서 최대 강도를 갖는 할로를 나타내는 마그네슘 클로라이드 리플렉션을 나타내며 14.95°의 2v에서 리플렉션을 나타내지 않는 X-선 스펙트럼을 갖는다)을 포함하는 촉매를 사용하여, 성분 a)를 하나 이상의 제1단계에서 제조하고 성분 b)및 c)를 하나 이상의 제2단계에서 제조하는, 선행의 중합 반응에서 생성된 중합체 물질의 존재하에서 후속적인 중합 반응을 수행하는 두 단계 이상의 연속 중합반응을 포함함을 특징으로 하여, 제1항의 열가소성 올레핀 중합체를 제조하는 방법.
- 제18항에 있어서, 성분 a)의 중합 반응을 액체 단량체중에서 수행하고 성분 b)및 c)의 중합 반응을 기체상에서 수행하는 방법.
- 제18항에 있어서, 중합 반응을 기체상에서 수행하는 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.