- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Links
Images
Classifications
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M4/00—Electrodes
- H01M4/02—Electrodes composed of, or comprising, active material
- H01M4/04—Processes of manufacture in general
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M4/00—Electrodes
- H01M4/02—Electrodes composed of, or comprising, active material
- H01M4/36—Selection of substances as active materials, active masses, active liquids
- H01M4/58—Selection of substances as active materials, active masses, active liquids of inorganic compounds other than oxides or hydroxides, e.g. sulfides, selenides, tellurides, halogenides or LiCoFy; of polyanionic structures, e.g. phosphates, silicates or borates
- H01M4/583—Carbonaceous material, e.g. graphite-intercalation compounds or CFx
- H01M4/587—Carbonaceous material, e.g. graphite-intercalation compounds or CFx for inserting or intercalating light metals
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B32/00—Carbon; Compounds thereof
- C01B32/20—Graphite
- C01B32/205—Preparation
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M10/00—Secondary cells; Manufacture thereof
- H01M10/05—Accumulators with non-aqueous electrolyte
- H01M10/052—Li-accumulators
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
- Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
- Y02E60/10—Energy storage using batteries
Landscapes
- Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Inorganic Chemistry (AREA)
- Electrochemistry (AREA)
- General Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Geology (AREA)
- General Life Sciences & Earth Sciences (AREA)
- Life Sciences & Earth Sciences (AREA)
- Engineering & Computer Science (AREA)
- Manufacturing & Machinery (AREA)
- Carbon And Carbon Compounds (AREA)
- Battery Electrode And Active Subsutance (AREA)
- Inert Electrodes (AREA)
Abstract
【選択図】 図1
Description
該当せず。
該当せず。
発明の分野
本開示は、概して、炭素質材料の製造方法に関する。より詳細には、本開示は、電気化学的蓄電池における負極材料としての使用のための炭素粒子の製造方法に関する。
電池性能に対する要件は、それらの意図される用途に大きく依存する。例えば、ハイブリッド電気自動車での使用のための電池は、非常に長いライフサイクル、低コスト、高盛込密度(gravimetric density)及び高体積密度(volumetric density)を必要とし得るものであり、一方、携帯電話及びカムコーダーなどの携帯型デバイス用の電池は、軽量であるという追加の要件を有し得るものである。このような電池の構築のために使用される材料は、上述の要件を満たす電池能力において、重大な役割を果たす。
ここには、炭素粒子を製造する方法であって、前駆体材料を選択することと、前記前駆体材料を整粒する(sizing)ことと、前記前駆体材料を安定化させることと、前記前駆体材料を炭化させることと、前記前駆体材料を黒鉛化させる(graphitizing)こととを含み、前駆体材料は、約5重量%乃至約60重量%の揮発分含有量を有する方法が開示されている。
ここには、Liイオン電池中の負極材料としての使用に適切であり得る炭素粒子の製造についての方法論(methodologies)が開示されている。ここで説明される方法論は、初回クーロン効率及び充放電サイクル中の可逆容量が高められた炭素粒子の、さほど費用のかからない製造をもたらし得る。図1に示された本発明の或る実施形態100は、少なくとも、前駆体選択工程と、整粒工程と、安定化工程と、炭化工程と、黒鉛化工程とを含んでいる。これら処理工程が独立に行われることは理解されるべきであり、従って、これら工程の任意の組み合わせが企図され得る。或いは、このプロセスは、ここで説明される順序で行われ得る。
本発明を概略的に説明してきたが、以下の例は、本発明の特定の実施形態として挙げられており、その実施及び利点を説明するものである。これら例は、例証のみを目的として挙げられており、本明細書又は特許請求の範囲を何らかに限定するように意図されないことが理解される。
この例は、安定化工程での酸化剤として固体硝酸塩を使用する効果を説明する。石油生コークスが、前駆体材料として選択された。この石油コークスは、約71重量%の炭素含有量を有している。炭素含有量は、このコークスを、窒素ガス中で、2時間に亘り、1000℃で加熱することによって測定された。この例では、生コークスは、約9マイクロメートルの平均粒径(10%が3マイクロメートル未満であるが、90%が14マイクロメートル未満である)を有した微粉末へと粉砕及びミリングされた。
この例は、酸化剤として硝酸ナトリウムを使用し、これを例1と比べて比較的多量に使用したこと以外、例1と同様であった。まず、例1と同じ22.0gの石油コークス粉末が、1.7gのNaNO3と、5gの脱イオン水と、2gのアセトンとからなる硝酸ナトリウム(NaNO3)溶液と混ぜ合わされた。得られた混合物が、安定化及び炭化のために、例1と同じ方法で、乾燥及び熱処理された。
この例は、平均粒径がより大きかった以外、酸化剤及び量の点で例2と同じである。この例では、例1と同じ石油生コークスが使用された。まず、石油コークスが、約15マイクロメートルの平均粒径(10%が7マイクロメートル未満であり、90%が30マイクロメートル未満である)へとジェットミルされ、23.0gのミリングされた石油コークス粉末が、1.8gのNaNO3と、4gの脱イオン水と、2gのアセトンとからなる硝酸ナトリウム溶液と混ぜ合わされた。得られた混合物は、例1と同じ方法で、乾燥及び熱処理された。
この例は、安定化工程での酸化剤としての空気の使用を例証している。例3に挙げられたものと同じ100gのミリングされた石油コークス粉末が、8''径のガラス皿上に広げられ、1℃/分で250℃まで加熱され、3時間に亘ってこの温度に保持され、1℃/分で290℃まで加熱され、減圧(〜−18''Hg)下で、10時間に亘って290℃に保持された。減圧下での加熱は、生コークスの酸化をもたらした。結果、生コークス粒子は、不融性となり、続いての炭化及び黒鉛化工程の間、融合しなかった。
例4と同様に、例1のものと同じ100gのミリングされた石油コークスが、8''径のガラス皿上に広げられ、全ての工程(安定化、炭化及び黒鉛化)のために例4と同じ方法で熱処理された。この黒鉛粉末の試験結果も、表1に載せてある。
比較例1
この例は、生コークス粉末が、石油ピッチで被覆され、次に、熱処理されることで、例1と同様の電気化学的特性を持つ製品をつくることができることを示しているが、方法はより複雑である。
この例は、異なる石油コークスの効果を例示している。この例で使用される生石油コークスは、例1の71%に相当する約92%の炭素含有量を含有していた。この石油コークス粉末が窒素ガス流で迅速に加熱された際、それは焼結も発泡もしなかった。この例では、100グラムのミリングされた石油コークス粉末(平均粒径が約8マイクロメートル)が、8''径のガラス皿上に広げられ、1℃/分で250℃へと加熱されて、3時間に亘ってこの温度に保持され、1℃/分で290℃へと加熱されて、減圧(〜−18''Hg)下で、10時間に亘って290℃に保持された。
この例は、例1における、石油生コークスを用いた安定化工程の利点を説明している。100gの例1と同じ石油コークスが、5℃/分で800℃まで加熱されて、窒素中で、2時間に亘って800℃に保持され、続いて、室温まで冷却された。得られた粉末は焼結された。この硬い焼結材料は、再度粉砕しない限り、そのままでは使用できない。それ故に、この材料は、粉末としては試験できなかった。
Claims (25)
- 炭素粒子の製造方法であって、
(a)前駆体材料を選択することと、
(b)前記前駆体材料を整粒することと、
(c)前記前駆体材料を安定化させることと、
(d)前記前駆体材料を炭化させることと、
(e)前記前駆体材料を黒鉛化させることと
を含み、
前記前駆体材料は、約5重量%乃至約60重量%の揮発分含有量を有する方法。 - 請求項1記載の方法であって、前記前駆体材料は、約5重量%乃至約40重量%の揮発分含有量を有する方法。
- 請求項1記載の方法であって、前記前駆体材料は、炭素生成炭化水素である方法。
- 請求項1記載の方法であって、前記前駆体材料は、未か焼石油コークス、未か焼コールタールコークス、高分子量ピッチ、高分子量タール又はこれらの混合物である方法。
- 請求項1記載の方法であって、前記前駆体材料は生コークスである方法。
- 請求項5記載の方法であって、コークス原料は、常圧蒸留塔残渣、真空蒸留塔残渣、エチレン分解器残渣、流体接触分解器からのデカント若しくはスラリーオイル又はこれらの組み合わせである方法。
- 請求項1記載の方法であって、前記前駆体材料は、約1μm乃至約50μmの平均粒径へと整粒される方法。
- 請求項1記載の方法であって、前記前駆体材料は、約1μm乃至約30μmの平均粒径へと整粒される方法。
- 請求項1記載の方法であって、前記前駆体材料は、約1μm乃至約15μmの平均粒径へと整粒される方法。
- 請求項1記載の方法であって、前記前駆体材料の前記整粒は、機械的ミリング方法によって行われる方法。
- 請求項1記載の方法であって、前記安定化処理は、酸化剤存在下での前記前駆体材料の加熱を含んでいる方法。
- 請求項11記載の方法であって、前記前駆体材料は、約250℃乃至約350℃の温度へと加熱される方法。
- 請求項11記載の方法であって、前記酸化剤は、空気、酸素ガス、有機酸、無機酸、金属塩、金属酸化物、高原子価遷移金属酸化物又はこれらの組み合わせである方法。
- 請求項1記載の方法であって、前記前駆体材料の安定化度は、約0.1重量%乃至約20重量%である方法。
- 請求項14記載の方法であって、前記安定度は、安定化中の前記前駆体材料の正味の重量増加として測定される方法。
- 請求項1記載の方法であって、安定化後に、より大きな粒子及び硬い凝集塊を、前記前駆体材料から分離することを更に含んだ方法。
- 請求項1記載の方法であって、工程(b)は、工程(a)と(c)との間に行われる方法。
- 請求項1記載の方法であって、前記前駆体材料は、不活性環境において、約400℃乃至約1500℃の温度で炭化される方法。
- 請求項1記載の方法であって、炭化は、前記前駆体材料に、約80重量%を超える固定炭素含有量を与える方法。
- 請求項1記載の方法であって、前記前駆体材料は、約2000℃を超える温度で黒鉛化される方法。
- 請求項1記載の方法であって、工程(d)及び(e)は、工程(c)の後に行われる方法。
- 請求項1記載の方法であって、工程(e)後に、より大きな粒子及び硬い凝集塊を、前記前駆体材料から分離することを更に含んだ方法。
- 電極材料の製造方法であって、
(a)前駆体材料を選択することと、
(b)前記前駆体材料を整粒することと、
(c)前記前駆体材料を安定化させることと、
(d)前記前駆体材料を炭化させることと、
(e)前記前駆体材料を黒鉛化させることと
を含み、
前記電極材料は、約1μm乃至約50μmの平均粒径と、約80重量%を超える固定炭素含有量と、黒鉛構造とを有する方法。 - 約1μm乃至約50μmの平均粒径と、約0.1重量%乃至約10重量%の安定化度と、約80重量%を超える固定炭素含有量と、黒鉛構造とを有した炭素粒子。
- 炭素粒子の製造方法であって、
(a)前駆体材料を選択することと、
(b)前記前駆体材料を整粒することと、
(c)前記前駆体材料を安定化させることと、
(d)前記前駆体材料を黒鉛化させることと
を含み、
前記前駆体材料は、約5重量%乃至約60重量%の揮発分含有量を有する方法。
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US11/422,824 | 2006-06-07 | ||
US11/422,824 US7597999B2 (en) | 2006-06-07 | 2006-06-07 | Methods of preparing carbonaceous anode materials and using same |
PCT/US2007/069452 WO2007143388A1 (en) | 2006-06-07 | 2007-05-22 | Method of preparing carbonaceous anode materials and using same |
Publications (3)
Publication Number | Publication Date |
---|---|
JP2009539746A true JP2009539746A (ja) | 2009-11-19 |
JP2009539746A5 JP2009539746A5 (ja) | 2010-07-15 |
JP5638802B2 JP5638802B2 (ja) | 2014-12-10 |
Family
ID=38461954
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
JP2009514464A Expired - Fee Related JP5638802B2 (ja) | 2006-06-07 | 2007-05-22 | 炭素質負極材料の製造方法及びその使用方法 |
Country Status (8)
Country | Link |
---|---|
US (1) | US7597999B2 (ja) |
EP (1) | EP2025022A1 (ja) |
JP (1) | JP5638802B2 (ja) |
KR (1) | KR101425915B1 (ja) |
CN (1) | CN101461077B (ja) |
CA (1) | CA2652557C (ja) |
TW (1) | TWI419400B (ja) |
WO (1) | WO2007143388A1 (ja) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR101085048B1 (ko) | 2010-03-31 | 2011-11-21 | 한국화학연구원 | 개선된 핏치의 제조방법, 및 이를 이용한 석유화학 부산물로부터 고용량 금속-탄소 음극재료의 제조 방법 |
JP2014067625A (ja) * | 2012-09-26 | 2014-04-17 | Sanyo Electric Co Ltd | 非水電解質二次電池 |
Families Citing this family (21)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
TWI493780B (zh) * | 2008-03-31 | 2015-07-21 | 派諾得公司 | 用於電池的陽極粉末 |
WO2011099466A1 (ja) * | 2010-02-09 | 2011-08-18 | 住友大阪セメント株式会社 | 焼結体及びその製造方法 |
TW201140920A (en) * | 2010-04-08 | 2011-11-16 | Conocophillips Co | Methods of preparing carbonaceous material |
JP5728475B2 (ja) * | 2010-05-31 | 2015-06-03 | Jx日鉱日石エネルギー株式会社 | リチウムイオン二次電池負極材料用原料炭組成物 |
JP5528923B2 (ja) * | 2010-06-25 | 2014-06-25 | Jx日鉱日石エネルギー株式会社 | リチウムイオン二次電池負極材料用の原料炭組成物 |
CN102140254B (zh) * | 2011-03-10 | 2012-10-10 | 江苏国正新材料科技有限公司 | 一种高效改性沥青的制备方法 |
US9181134B1 (en) | 2011-04-27 | 2015-11-10 | Israzion Ltd. | Process of converting textile solid waste into graphite simple or complex shaped manufacture |
WO2014186550A1 (en) | 2013-05-17 | 2014-11-20 | Conocophillips Company | Electrically conductive proppant coating and related methods |
CN103325997B (zh) * | 2013-06-28 | 2016-03-30 | 马树华 | 用于锂离子动力电池负极的碳材料及其制备方法 |
CN104425821A (zh) * | 2013-09-11 | 2015-03-18 | 宁波杉杉新材料科技有限公司 | 一种锂离子电池石墨负极材料及其制备方法 |
CN105024075A (zh) * | 2014-12-18 | 2015-11-04 | 上海杉杉科技有限公司 | 快充石墨锂离子电池负极材料及其制备方法 |
CN105110325A (zh) * | 2015-08-25 | 2015-12-02 | 安徽工业大学 | 一种制备超级电容器用相互连接的且褶皱的石墨烯材料的方法 |
CN106486669A (zh) * | 2015-11-17 | 2017-03-08 | 上海杉杉科技有限公司 | 一种高放电倍率锂离子电池石墨负极材料及其制备方法 |
EP3580169A2 (en) * | 2017-02-08 | 2019-12-18 | National Electrical Carbon Products, Inc. | Carbon powders and methods of making same |
CN108822566B (zh) * | 2018-06-05 | 2020-08-04 | 广东石油化工学院 | 一种硅改性道路沥青路面养护剂及其制备方法 |
WO2021011650A1 (en) * | 2019-07-17 | 2021-01-21 | Phillips 66 Company | Electrode particles suitable for batteries |
US20210020939A1 (en) * | 2019-07-17 | 2021-01-21 | Phillips 66 Company | Anode particles suitable for batteries |
CN114097119A (zh) * | 2019-07-17 | 2022-02-25 | 菲利浦66公司 | 适用于电池的电极颗粒 |
CN110642244A (zh) * | 2019-10-08 | 2020-01-03 | 杭州高烯科技有限公司 | 一种石墨烯及氧化石墨烯的制备方法 |
JP7267509B2 (ja) * | 2020-06-23 | 2023-05-01 | 寧徳時代新能源科技股▲分▼有限公司 | 二次電池及び二次電池を含む装置 |
CN115611264A (zh) * | 2022-11-10 | 2023-01-17 | 泰安市法拉第能源科技有限公司 | 沥青基硬碳负极材料及制备方法、钠离子电池 |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH103922A (ja) * | 1996-06-14 | 1998-01-06 | Nippon Carbon Co Ltd | リチウム電池負極材料用炭素または黒鉛粉末 の製造方法 |
JPH10326611A (ja) * | 1997-03-28 | 1998-12-08 | Nippon Steel Corp | リチウム二次電池負極用炭素材料 |
JP2001023638A (ja) * | 1999-07-05 | 2001-01-26 | Sumitomo Metal Ind Ltd | リチウムイオン二次電池負極用黒鉛粉末の製造方法 |
JP2003142092A (ja) * | 2001-11-02 | 2003-05-16 | Nippon Carbon Co Ltd | 高性能リチウム二次電池負極材 |
JP2003297357A (ja) * | 2002-04-02 | 2003-10-17 | Nippon Steel Chem Co Ltd | リチウム二次電池負極材料とその製造方法 |
Family Cites Families (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4042486A (en) | 1974-06-24 | 1977-08-16 | Kureha Kagaku Kogyo Kabushiki Kaisha | Process for the conversion of pitch into crystalloidal pitch |
US4929404A (en) * | 1984-09-25 | 1990-05-29 | Mitsubishi Petrochemical Company Limited | Graphitic or carbonaceous moldings and processes for producing the same |
US4891203A (en) * | 1985-06-28 | 1990-01-02 | Union Carbide Corporation | Flake-like carbon bodies from semicoke |
JPS6479072A (en) | 1987-09-22 | 1989-03-24 | Petoca Ltd | Production of carbon-carbon composite material from pitch as matrix carbon precursor |
JPH08315817A (ja) | 1995-05-17 | 1996-11-29 | Sony Corp | 炭素負極材料の製造方法及び非水電解液二次電池 |
JP3193342B2 (ja) | 1997-05-30 | 2001-07-30 | 松下電器産業株式会社 | 非水電解質二次電池 |
JP2000086343A (ja) | 1998-09-09 | 2000-03-28 | Sec Corp | 炭素複合材料及びその製造方法 |
JP4945029B2 (ja) | 2001-03-06 | 2012-06-06 | 新日鐵化学株式会社 | リチウム二次電池負極用材料とその製造方法およびリチウム二次電池 |
TWI302761B (en) * | 2002-01-31 | 2008-11-01 | Conocophillips Co | Coated carbonaceous particles particularly useful as electrode materials in electrical storage cells, and methods of making the same |
US20030160215A1 (en) | 2002-01-31 | 2003-08-28 | Zhenhua Mao | Coated carbonaceous particles particularly useful as electrode materials in electrical storage cells, and methods of making the same |
US20040121122A1 (en) | 2002-12-20 | 2004-06-24 | Graftech, Inc. | Carbonaceous coatings on flexible graphite materials |
JP5153055B2 (ja) * | 2003-10-31 | 2013-02-27 | 昭和電工株式会社 | リチウム二次電池電極用炭素材料、その製造方法、電極ペースト、リチウム二次電池用電極及びリチウム二次電池 |
US20070092429A1 (en) * | 2005-10-24 | 2007-04-26 | Conocophillips Company | Methods of preparing carbon-coated particles and using same |
GB2432830A (en) | 2005-12-02 | 2007-06-06 | Morganite Elect Carbon | Formation of thermally anisotropic carbon material |
-
2006
- 2006-06-07 US US11/422,824 patent/US7597999B2/en not_active Expired - Fee Related
-
2007
- 2007-05-22 EP EP07762282A patent/EP2025022A1/en not_active Withdrawn
- 2007-05-22 CN CN2007800210277A patent/CN101461077B/zh not_active Expired - Fee Related
- 2007-05-22 KR KR1020087029849A patent/KR101425915B1/ko not_active IP Right Cessation
- 2007-05-22 CA CA2652557A patent/CA2652557C/en not_active Expired - Fee Related
- 2007-05-22 WO PCT/US2007/069452 patent/WO2007143388A1/en active Application Filing
- 2007-05-22 JP JP2009514464A patent/JP5638802B2/ja not_active Expired - Fee Related
- 2007-05-23 TW TW096118336A patent/TWI419400B/zh not_active IP Right Cessation
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH103922A (ja) * | 1996-06-14 | 1998-01-06 | Nippon Carbon Co Ltd | リチウム電池負極材料用炭素または黒鉛粉末 の製造方法 |
JPH10326611A (ja) * | 1997-03-28 | 1998-12-08 | Nippon Steel Corp | リチウム二次電池負極用炭素材料 |
JP2001023638A (ja) * | 1999-07-05 | 2001-01-26 | Sumitomo Metal Ind Ltd | リチウムイオン二次電池負極用黒鉛粉末の製造方法 |
JP2003142092A (ja) * | 2001-11-02 | 2003-05-16 | Nippon Carbon Co Ltd | 高性能リチウム二次電池負極材 |
JP2003297357A (ja) * | 2002-04-02 | 2003-10-17 | Nippon Steel Chem Co Ltd | リチウム二次電池負極材料とその製造方法 |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR101085048B1 (ko) | 2010-03-31 | 2011-11-21 | 한국화학연구원 | 개선된 핏치의 제조방법, 및 이를 이용한 석유화학 부산물로부터 고용량 금속-탄소 음극재료의 제조 방법 |
JP2014067625A (ja) * | 2012-09-26 | 2014-04-17 | Sanyo Electric Co Ltd | 非水電解質二次電池 |
Also Published As
Publication number | Publication date |
---|---|
CN101461077A (zh) | 2009-06-17 |
TW200810211A (en) | 2008-02-16 |
EP2025022A1 (en) | 2009-02-18 |
KR101425915B1 (ko) | 2014-08-12 |
CA2652557C (en) | 2012-03-13 |
US20070286792A1 (en) | 2007-12-13 |
JP5638802B2 (ja) | 2014-12-10 |
KR20090015110A (ko) | 2009-02-11 |
TWI419400B (zh) | 2013-12-11 |
WO2007143388A1 (en) | 2007-12-13 |
CN101461077B (zh) | 2012-08-08 |
US7597999B2 (en) | 2009-10-06 |
CA2652557A1 (en) | 2007-12-13 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
JP5638802B2 (ja) | 炭素質負極材料の製造方法及びその使用方法 | |
US20070092429A1 (en) | Methods of preparing carbon-coated particles and using same | |
KR100956251B1 (ko) | 전기 저장 전지의 전극 물질로서 특히 유용한 코팅된탄소성 입자 및 이의 제조 방법 | |
KR101380259B1 (ko) | 리튬 이온 전지용 전극 재료의 제조 방법 | |
TWI493780B (zh) | 用於電池的陽極粉末 | |
KR101380730B1 (ko) | 리튬 이온 전지용 전극 재료의 제조 방법 | |
KR20150134337A (ko) | 탄소재, 그 탄소재를 사용한 비수계 이차 전지 | |
JP2007039290A (ja) | 非水系二次電池用負極材料に適した炭素粉末 | |
TW201338253A (zh) | 非水電解質二次電池用碳質材料 | |
TW201705595A (zh) | 用於鋰離子電池組之陽極中的複合物粉末、用於製造複合物粉末的方法、及鋰離子電池組 | |
JP2018500742A (ja) | リチウムイオンバッテリのアノードにおいて使用するための複合粉末、このような複合粉末を調製する方法、及びこのような複合粉末を分析する方法 | |
KR20160065107A (ko) | 규소 함유 재료, 비수전해질 이차 전지용 부극, 비수전해질 이차 전지 및 그들의 제조 방법 | |
JP5737265B2 (ja) | 珪素酸化物及びその製造方法、負極、ならびにリチウムイオン二次電池及び電気化学キャパシタ | |
JP2024505607A (ja) | リチウム二次電池用負極活物質およびその製造方法並びにこれを用いて製造された負極を含むリチウム二次電池 | |
JP5212682B2 (ja) | リチウムイオン二次電池用負極材の製造方法 | |
KR101790699B1 (ko) | 화학적 활성화법으로 제조된 활성탄과 피치를 사용한 이차전지 음극의 제조 방법 | |
JP4488523B2 (ja) | 非水電解液二次電池、それに用いる炭素材料および該炭素材料の前駆体 | |
KR20200057468A (ko) | 이차전지 음극활물질 복합소재, 및 이의 제조 방법 | |
WO2020149252A1 (ja) | 人造黒鉛材料、人造黒鉛材料の製造方法、リチウムイオン二次電池用負極およびリチウムイオン二次電池 | |
JP2003100293A (ja) | 炭素材料及びその製造方法並びにその用途 | |
WO2020149251A1 (ja) | 人造黒鉛材料、人造黒鉛材料の製造方法、リチウムイオン二次電池用負極およびリチウムイオン二次電池 | |
JP2012174369A (ja) | リチウムイオン二次電池用負極およびリチウムイオン二次電池 | |
KR102334493B1 (ko) | 리튬 이온 이차 전지의 음극용 탄소 재료 및 그의 제조 방법, 및 그것을 이용한 음극 및 리튬 이온 이차 전지 | |
WO2023110903A1 (en) | Improved carbonaceous coating material for battery electrode materials | |
WO2023018545A1 (en) | Methods for preparing nano-ordered carbon anode materials for lithium-ion batteries |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
A521 | Written amendment |
Free format text: JAPANESE INTERMEDIATE CODE: A523 Effective date: 20100524 |
|
A524 | Written submission of copy of amendment under section 19 (pct) |
Free format text: JAPANESE INTERMEDIATE CODE: A524 Effective date: 20100524 |
|
A621 | Written request for application examination |
Free format text: JAPANESE INTERMEDIATE CODE: A621 Effective date: 20100524 |
|
A131 | Notification of reasons for refusal |
Free format text: JAPANESE INTERMEDIATE CODE: A131 Effective date: 20120828 |
|
A601 | Written request for extension of time |
Free format text: JAPANESE INTERMEDIATE CODE: A601 Effective date: 20121127 |
|
A602 | Written permission of extension of time |
Free format text: JAPANESE INTERMEDIATE CODE: A602 Effective date: 20121204 |
|
A521 | Written amendment |
Free format text: JAPANESE INTERMEDIATE CODE: A523 Effective date: 20130228 |
|
A131 | Notification of reasons for refusal |
Free format text: JAPANESE INTERMEDIATE CODE: A131 Effective date: 20130423 |
|
A601 | Written request for extension of time |
Free format text: JAPANESE INTERMEDIATE CODE: A601 Effective date: 20130723 |
|
A602 | Written permission of extension of time |
Free format text: JAPANESE INTERMEDIATE CODE: A602 Effective date: 20130730 |
|
A521 | Written amendment |
Free format text: JAPANESE INTERMEDIATE CODE: A523 Effective date: 20131023 |
|
A131 | Notification of reasons for refusal |
Free format text: JAPANESE INTERMEDIATE CODE: A131 Effective date: 20140107 |
|
A601 | Written request for extension of time |
Free format text: JAPANESE INTERMEDIATE CODE: A601 Effective date: 20140331 |
|
A602 | Written permission of extension of time |
Free format text: JAPANESE INTERMEDIATE CODE: A602 Effective date: 20140407 |
|
A711 | Notification of change in applicant |
Free format text: JAPANESE INTERMEDIATE CODE: A711 Effective date: 20140604 |
|
A521 | Written amendment |
Free format text: JAPANESE INTERMEDIATE CODE: A523 Effective date: 20140618 |
|
A01 | Written decision to grant a patent or to grant a registration (utility model) |
Free format text: JAPANESE INTERMEDIATE CODE: A01 Effective date: 20140924 |
|
A61 | First payment of annual fees (during grant procedure) |
Free format text: JAPANESE INTERMEDIATE CODE: A61 Effective date: 20141023 |
|
S111 | Request for change of ownership or part of ownership |
Free format text: JAPANESE INTERMEDIATE CODE: R313113 |
|
S531 | Written request for registration of change of domicile |
Free format text: JAPANESE INTERMEDIATE CODE: R313531 |
|
R350 | Written notification of registration of transfer |
Free format text: JAPANESE INTERMEDIATE CODE: R350 |
|
LAPS | Cancellation because of no payment of annual fees |