FR2846332A1 - Copolymeres transparents a blocs polyamides et blocs polyethers - Google Patents
Copolymeres transparents a blocs polyamides et blocs polyethers Download PDFInfo
- Publication number
- FR2846332A1 FR2846332A1 FR0213218A FR0213218A FR2846332A1 FR 2846332 A1 FR2846332 A1 FR 2846332A1 FR 0213218 A FR0213218 A FR 0213218A FR 0213218 A FR0213218 A FR 0213218A FR 2846332 A1 FR2846332 A1 FR 2846332A1
- Authority
- FR
- France
- Prior art keywords
- blocks
- polyamide
- polyether
- acid
- copolymers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
La présente invention concerne des copolymères à blocs polyamides et blocs polyéthers dans lesquels:les blocs polyamides sont des copolyamides aliphatiques,les blocs polyéthers sont constitués essentiellement de PTMG de masse molaire moyenne en nombre Mn comprise entre 200 et 1000,la dureté Shore D est supérieure ou égale à 40.Ces copolymères sont utiles pour fabriquer de nombreux objets et en particulier des chaussures de sport.
Description
COPOLYM RES TRANSPARENTS BLOCS POLYAMIDES ET BLOCS
POLYETHERS
[Domaine de l'invention] La présente invention concerne des copolymères transparents à blocs polyamides et blocs polyéthers. Ils sont aussi appelés polyéther blocs amides (PEBA), ce sont des élastomères thermoplastiques. Ils sont appelés aussi polyamides élastomères. Ces copolymères sont utiles pour fabriquer de 10 nombreux objets et en particulier des chaussures de sport. La transparence des copolymères de la présente invention est mesurée sur des feuilles de 2mm d'épaisseur. [L'art antérieur et le problème technique] 15 De nombreuses demandes de brevet décrivent des copolymères à blocs
polyamides et blocs polyéthers.
US 4820796 décrit des copolymères à blocs polyamides et blocs polyéthers dont les blocs polyamides sont en PA 6 (polyamide 6 ou 20 polycaprolactame) et les blocs polyéthers en PTMG (polytetraméthylène glycol ou polyoxytetraméthylène glycol ou encore polytetrahydrofuranne) de masse molaire moyenne en nombre Mn comprise entre 680 et 4040. Ils ont une
transparence insuffisante.
US 5280087 décrit des copolymères à blocs polyamides et blocs 25 polyéthers dont les blocs polyamides sont en PA 6 (polyamide 6 ou polycaprolactame) et les blocs polyéthers en PTMG (polytetraméthylène glycol ou polyoxytetraméthylène glycol ou encore polytetrahydrofuranne) de masse molaire moyenne en nombre Mn comprise entre 1000 et 2000. Ils ont une
transparence insuffisante.
On a maintenant trouvé de nouveaux copolymères à blocs polyamides et blocs polyéthers tels que leurs blocs polyamides sont des copolyamides et leurs blocs polyéthers sont en PTMG de masse molaire moyenne en nombre Mn comprise entre 200 et 1000. Ces copolymères sont particulièrement transparents au sens de l'invention. Avantageusement leur dureté Shore D est supérieure ou égale à 40. Au contact de l'humidité ou de l'eau ils ont une faible
reprise en eau ce qui permet de bonnes propriétés mécaniques.
L'art antérieur a déjà décrit des copolymères à blocs polyamides et blocs polyéthers dont les blocs polyamide sont en copolyamide mais ils sont toujours
associés à des blocs polyéthers hydrophiles.
La demande de brevet JP 05 078477 A publiée le 30 mars 1993 décrit des copolymères à blocs polyamides et blocs polyéthers ayant des blocs en 10 copolyamide mais les blocs polyéthers sont un mélange de PTMG et de PEG (polyethylène glycol ou polyoxyethylène glycol) contenant entre 30 et 99% en poids de PEG. La masse molaire moyenne en nombre Mn du PTMG est comprise entre 1000 et 2000. La masse molaire moyenne en nombre Mn du PEG est comprise entre 1000 et 2020. Ils sont utilisés pour rendre des résines 15 antistatiques. Il est écrit aussi qu'ils ont d'excellentes propriétés de perméabilité
à la vapeur d'eau.
La demande de brevet WO 99-33659 décrit une structure multichouche comprenant un matériau recouvert par un copolymère à blocs polyamides et blocs hydrophiles, ledit copolymère ayant une température de fusion inférieure 20 à 1350C et de préférence comprise entre 90 et 1350C. Les blocs polyamides sont de faible masse ou sont des copolyamides. Les blocs hydrophiles du copolymère sont des polyéthers ayant au moins 50 % en poids de motifs: C2H40 La quantité de blocs polyéthers du copolymère représente 10 à 40 % en poids du copolymère. Le matériau de cette structure multicouche est du papier, du carton, un non tissé de fibres de cellulose, un non tissé à base de fibres de polyoléfine ou un tissu choisi parmi le coton, le polyamide ou le polyester. La demande de brevet EP 1046675 décrit des copolymères à blocs polyamides et blocs polyéthers similaires à ceux de la structure décrite plus haut dans la structure selon WO 99-33659. Ils sont utiles comme additifs dans
des polymères thermoplastiques pour les rendre antistatiques.
[Brève description de l'invention]
La présente invention concerne des copolymères à blocs polyamides et blocs polyéthers dans lesquels: les blocs polyamides sont des copolyamides aliphatiques, les blocs polyéthers sont constitués essentiellement de PTMG de masse molaire moyenne en nombre Mn comprise entre 200 et 1000,
la dureté Shore D est supérieure ou égale à 40.
L'invention concerne aussi les objets fabriqués avec ces copolymères.
On peut les fabriquer par injection, moulage, extrusion et en général selon les techniques de transformation de polymères thermoplastiques. Par exemple des feuilles de 0,5 à 3 mm d'épaisseur sont utiles pour faire des semelles de
chaussures de sport.
[Description détaillée de l'invention]
Les copolymères à blocs polyamides et blocs polyéthers en général résultent de la copolycondensation de séquences polyamides à extrémités 25 réactives avec des séquences polyéthers à extrémités réactives, telles que, entre autres: 1) Séquences polyamides à bouts de chaîne diamines avec des
séquences polyoxyalkylènes à bouts de chaînes dicarboxyliques.
2) Séquences polyamides à bouts de chaînes dicarboxyliques avec 30 des séquences polyoxyalkylènes à bouts de chaînes diamines obtenues par cyanoéthylation et hydrogénation de séquences
polyoxyalkylène alpha-oméga dihydroxylées aliphatiques appelées polyétherdiols.
3) Séquences polyamides à bouts de chaînes dicarboxyliques avec des polyétherdiols, les produits obtenus étant, dans ce cas particulier, des polyétheresteramides. Les séquences polyamides à bouts de chaînes dicarboxyliques proviennent par exemple de la condensation de précurseurs de polyamides en
présence d'un diacide carboxylique limiteur de chaîne.
Les séquences polyamides à bouts de chaînes diamines proviennent par 10 exemple de la condensation de précurseurs de polyamides en présence d'une
diamine limiteur de chaîne.
Les polymères à blocs polyamides et blocs polyéthers peuvent aussi comprendre des motifs répartis de façon aléatoire. Ces polymères peuvent être préparés par la réaction simultanée du polyéther et des précurseurs des blocs
1 5 polyamides.
Par exemple, on peut faire réagir du polyétherdiol, des précurseurs de
polyamide et un diacide limiteur de chaîne. On obtient un polymère ayant essentiellement des blocs polyéthers, des blocs polyamides de longueur très variable, mais aussi les différents réactifs ayant réagi de façon aléatoire qui 20 sont répartis de façon aléatoire (statistique) le long de la chaîne polymère.
On peut aussi faire réagir du polyétherdiamine, des précurseurs de
polyamide et un diacide limiteur de chaîne. On obtient un polymère ayant essentiellement des blocs polyéthers, des blocs polyamides de longueur très variable, mais aussi les différents réactifs ayant réagi de façon aléatoire qui 25 sont répartis de façon aléatoire (statistique) le long de la chaîne polymère.
Dans la présente invention les séquences polyamides résultent: a) soit de la condensation d'au moins un acide alpha oméga aminocarboxylique (ou un lactame), au moins une diamine aliphatique et au moins un diacide carboxylique aliphatique, b) soit de la condensation d'au moins deux acides alpha oméga aminocarboxyliques ou d'au moins deux lactames ayant de 6 à 12 atomes de carbone ou d'un lactame et d'un acide aminocarboxylique n'ayant pas le même nombre d'atomes de carbone,
c) soit de la condensation d'une diamine aliphatique avec un diacide carboxylique aliphatique et au moins un autre monomère choisi parmi les 5 diamines aliphatiques différentes de la précédente et les diacides aliphatiques différents du précédent.
Les blocs polyamides sont obtenus en présence d'un diacide ou d'une
diamine limiteur de chaîne si on veut des blocs polyamides à extrémités acides ou amines. Si les précurseurs comprennent déjà un diacide ou une diamine il 10 suffit par exemple de l'utiliser en excès.
A titre d'exemple d'acide alpha omega amino carboxylique aliphatique on
peut citer les acides aminocaproques, amino-7-heptano'que, amino11undécanoque et amino-12-dodécanoque.
A titre d'exemple de lactame on peut citer le caprolactame, 15 l'oenantholactame et le lauryllactame.
A titre d'exemple de diamines aliphatiques on peut citer l'hexaméthylènediamine, la dodécaméthylènediamine et la
triméthylhexaméthylène diamine.
A titre d'exemple de diacides aliphatiques on peut citer les acides 20 butane-diolque, adipique, azélaque, subérique, sébacique, dodécanedicarboxylique, les acides gras dimérisés (ces acides gras dimérisés ont de préférence une teneur en dimère d'au moins 98%; de préférence ils sont hydrogénés; ils sont commercialisés sous la marque "PRIPOL" par la société
"UNICHEMA", ou sous la marque EMPOL par la société HENKEL).
La masse molaire moyenne en nombre Mn des séquences polyamides
peut être comprise entre 500 et 10000 et de préférence entre 500 et 4500.
S'agissant des blocs polyamide de type b) les proportions en poids des monomères peuvent être telles que l'un représente 50 à 75% de l'ensemble des
monomères du bloc polyamide.
A titre d'exemple de blocs polyamides on peut citer: Les blocs 6 / 11 / 12 qui résultent de la condensation du caprolactame, de l'acide amino-1 1undecanoque et du lauryllactame. Les proportions en poids pouvant être respectivement 10 à 20 / 20 à 40 / 50 à 80. La masse molaire moyenne en nombre Mn de ces blocs polyamide peut être comprise entre 500
et 4200.
On peut encore citer les blocs 6 / 12 qui résultent de la condensation du 5 caprolactame et du lauryllactame. Les proportions en poids peuvent être de 18 à 45% de caprolactame pour respectivement 55 à 82% de lauryllactame. La masse molaire moyenne en nombre Mn de ces blocs polyamide peut être
comprise entre 1000 et 3000.
Les blocs polyéthers peuvent représenter 5 à 85 % en poids du copolymère à blocs polyamides et polyéthers. Les blocs polyéthers sont constitués de motifs tétrahydrofurane qui conduit aux enchaînements polytétraméthylène glycol aussi appelé PTMG qu'on peut représenter par la formule:
HO CH2CH2CH2CH2-0OH
On ne sortirait pas du cadre de l'invention si les blocs polyéthers contenaient de faibles proportions d'autres oxydes d'alkylènes pourvu que les propriétés du copolymère de l'invention soient conservées. On entend par 20 faibles proportions une proportion en poids de l'ordre de 5% au plus. De même
le copolymère de l'invention peut contenir d'autres polyéthers que le PTMG pourvu que les propriétés du copolymère de l'invention soient conservées. On entend par faibles proportions une proportion en poids de l'ordre de 5% au plus.
La quantité de blocs polyéthers dans ces copolymères à blocs 25 polyamides et blocs polyéthers est avantageusement de 10 à 70% en poids du
copolymère et de préférence de 35 à 60%.
Les blocs polyétherdiols sont soit utilisés tels quels et copolycondensés avec des blocs polyamides à extrémités carboxyliques, soit ils sont aminés pour être transformés en polyéther diamines et condensés avec des blocs 30 polyamides à extrémités carboxyliques. Par simplification on conserve
l'appellation de bloc PTMG pour les blocs polyéthers provenant du polytetraméthyleneglycol (polyétherdiol) dont on a remplacé les extrémités OH par des fonctions NH2 puis qu'on a condensé avec les blocs polyamides. Ils peuvent être aussi mélangés avec des précurseurs de polyamide et un limiteur 5 de chaîne diacide pour faire les polymères à blocs polyamides et blocs polyéthers ayant des motifs répartis de façon statistique.
La masse Mn des séquences polyéthers est comprise
avantageusement entre 300 et 700.
S'agissant de la dureté shore D, elle est comprise entre 40 et 70.
On peut aussi caractériser les copolymères de l'invention par leur
viscosité intrinsèque. Ces polymères à blocs polyamides et blocs polyéthers qu'ils proviennent de la copolycondensation de séquences polyamides et polyéthers préparées auparavant ou d'une réaction en une étape présentent, par exemple, une viscosité intrinsèque entre 0,8 et 2,5 mesurée dans le 15 métacrésol à 2500 C pour une concentration initiale de 0,8 g/100 mi.
S'agissant de leur préparation les copolymères de l'invention peuvent être préparés par tout moyen permettant d'accrocher les blocs polyamide et les blocs polyéthers. En pratique, on utilise essentiellement deux procédés l'un dit 20 en 2 étapes, l'autre en une étape. Dans le procédé en deux étapes on fabrique d'abord les blocs polyamides puis dans une deuxième étape on accroche les blocs polyamides et les blocs polyéthers. Dans le procédé en une étape on mélange les précurseurs de polyamide, le limiteur de chaînes et le polyéther; on obtient alors un polymère ayant essentiellement des blocs polyéthers, des blocs 25 polyamides de longueur très variable, mais aussi les différents réactifs ayant réagi de façon aléatoire qui sont répartis de façon aléatoire (statistique) le long de la chaîne polymère. Que ce soit en une ou deux étapes il est avantageux d'opérer en présence d'un catalyseur. On peut utiliser les catalyseurs décrits dans les brevets US 4 331 786, US 4 115 475, US 4 195 015, US 4 839 441, 30 US 4 864 014, US 4 230 838 et US 4 332 920. Dans le procédé en une étape on fabrique aussi des blocs polyamide, c'est pourquoi on a écrit au début de ce paragraphe que les copolymères de l'invention pouvaient être préparés par tout moyen d'accrocher les blocs polyamides et les blocs polyéthers. Des procédés de préparation de ces copolymères sont aussi décrits dans la demande de
brevet WO 99-33659 et la demande de brevet EP 1046675.
On décrit maintenant en détail les procédés de préparation dans 5 lesquels les blocs polyamides sont à extrémités carboxyliques et le polyéther est un polyétherdiol.
Le procédé en 2 étapes consiste d'abord à préparer les blocs polyamides à extrémités carboxyliques par condensation des précurseurs de polyamide en présence d'un diacide carboxylique limiteur de chaîne puis dans 10 une deuxième étape à ajouter le polyéther et un catalyseur. Si les précurseurs de polyamide ne sont que des lactames ou des acides alpha oméga aminocarboxyliques, on ajoute un diacide carboxylique. Si les précurseurs comprennent déjà un diacide carboxylique on l'utilise en excédent par rapport à la stoechiométrie des diamines. La réaction se fait habituellement entre 180 et 15 300'C, de préférence 200 à 2901C la pression dans le réacteur s'établit entre 5 et 30 bars, on la maintient environ 2 à 3 heures. On réduit lentement la pression en mettant le réacteur à l'atmosphère puis on distille l'eau excédentaire par
exemple une heure ou deux.
Le polyamide à extrémités acide carboxylique ayant été préparé on 20 ajoute ensuite le polyéther et un catalyseur. On peut ajouter le polyéther en une ou plusieurs fois, de même pour le catalyseur. Selon une forme avantageuse.on ajoute d'abord le polyéther, la réaction des extrémités OH du polyéther et des extrémités COOH du polyamide commence avec formations de liaison ester et élimination d'eau; On élimine le plus possible l'eau du milieu réactionnel par 25 distillation puis on introduit le catalyseur pour achever la liaison des blocs polyamides et des blocs polyéthers. Cette deuxième étape s'effectue sous agitation de préférence sous un vide d'au moins 6 mm Hg (800 Pa) à une température telle que les réactifs et les copolymères obtenus soient à l'état fondu. A titre d'exemple cette température peut être comprise entre 100 et 30 400'C et le plus souvent 200 et 3000C. La réaction est suivie par la mesure du couple de torsion exercée par le polymère fondu sur l'agitateur ou par la mesure de la puissance électrique consommée par l'agitateur. La fin de la réaction est déterminée par la valeur du couple ou de la puissance cible. Le catalyseur est défini comme étant tout produit permettant de faciliter la liaison des blocs polyamide et des blocs polyéther par estérification. Le catalyseur est avantageusement un dérivé d'un métal (M) choisi dans le groupe formé par le titane, le zirconium et 1' hafnium. A titre d'exemple de dérivé on peut citer les tétraalcoxydes qui répondent à la formule générale M(OR)4, dans laquelle M représente le titane, le zirconium ou 1' hafnium et les R, identiques ou différents, désignent des
radicaux alcoyles, linéaires ou ramifiés, ayant de 1 à 24 atomes de carbone.
Les radicaux alcoyles en C1 à C24 parmi lesquels sont choisis les radicaux R des tétraalcoxydes utilisés comme catalyseurs dans le procédé suivant l'invention sont par exemple tels que méthyle, éthyle, propyl, isopropyl, butyle, éthylhexyl, décyl, dodécyl, hexadodécyl. Les catalyseurs préférés sont les tétraalcoxydes pour lesquels les radicaux R, identiques ou différents, sont 15 des radicaux alcoyles en C1 à C8. Des exemples de tels catalyseurs sont notamment Zr (OC2H5)4, Zr (O-isoC3H7)4, Zr(OC4H9)4, Zr(OC5H1 1)4,
Zr(OC6H13)4, Hf(OC2H5)4, Hf(OC4H9)4, Hf(O-isoC3H7)4.
Le catalyseur utilisé dans ce procédé suivant l'invention peut consister uniquement en un ou plusieurs des tétraalcoxydes de formule M(OR)4 définis 20 précédemment. Il peut encore être formé par l'association d'un ou plusieurs de ces tétraalcoxydes avec un ou plusieurs alcoolates alcalins ou alcalino-terreux de formule (R1O)pY dans laquelle R1 désigne un reste hydrocarboné, avantageusement un reste alcoyle en C1 à C24, et de préférence en C1 à C8, Y représente un métal alcalin ou alcalino- terreux et p est la valence de Y. Les 25 quantités d'alcoolate alcalin ou alcalino-terreux et de tétraalcoxydes de zirconium ou d'hafnium que l'on associe pour constituer le catalyseur mixte peuvent varier dans de larges limites. On préfère toutefois utiliser des quantités d'alcoolate et de tétraalcoxydes telles que la proportion molaire d'alcoolate soit
sensiblement égale à la proportion molaire de tétraalcoxyde.
La proportion pondérale de catalyseur, c'est-à-dire du ou des tétraalcoxydes lorsque le catalyseur ne renferme pas d'alcoolate alcalin ou
alcalino-terreux ou bien de l'ensemble du ou des tétraalcoxydes et du ou des alcoolates alcalins ou alcalino-terreux lorsque le catalyseur est formé par l'association de ces deux types de composés, varie avantageusement de 0,01 à 5 % du poids du mélange du polyamide dicarboxylique avec le 5 polyoxyalcoylène glycol, et se situe de préférence entre 0,05 et 2 % de ce poids.
A titre d'exemple d'autres dérivés, on peut citer aussi les sels du métal (M) en particulier les sels de (M) et d'un acide organique et les, sels complexes entre l'oxyde de (M) et/ou l'hydroxyde de (M) et un acide organique. 10 Avantageusement l'acide organique peut être l'acide formique, l'acide acétique, I'acide propionique, l'acide butyrique, l'acide valérique, l'acide caproque, l'acide caprylique, I'acide lauryque, I'acide myristique, I'acide palmitique, I'acide stéarique, l'acide oléique, I'acide linoléique, I'acide linolénique, l'acide cyclohexane carboxylique, l'acide phénylacétique, I'acide benzoque, l'acide 15 salicylique, I'acide oxalique, I'acide malonique, I'acide succinique, I'acide glutarique, l'acide adipique, l'acide maléique, l'acide fumarique, l'acide phtalique et l'acide crotonique. Les acides acétique et propionique sont particulièrement préférés. Avantageusement M est le zirconium. Ces sels peuvent s'appeler sels de zirconyle. La demanderesse sans être liée par cette explication pense que 20 ces sels de zirconium et d'un acide organique ou les sels complexes cités plus haut libèrent ZrO++ au cours du procédé. On utilise le produit vendu sous le nom d'acétate de zirconyle. La quantité à utiliser est la même que pour les
dérivés M(OR)4.
Ce procédé et ces catalyseurs sont décrits dans les brevets 25 US 4,332, 920, US 4,230,838, US 4,331,786, US 4,252,920, JP 07145368A, JP
06287547A, et EP 613919.
S'agissant du procédé en une étape on mélange tous les réactifs utilisés dans le procédé en deux étapes c'est-à-dire les précurseurs de polyamide, le diacide carboxylique limiteur de chaîne, le polyéther et le 30 catalyseur. Il s'agit des même réactifs et du même catalyseur que dans le procédé en deux étapes décrit plus haut. Si les précurseurs de polyamide ne
sont que des lactames il est avantageux d'ajouter un peu d'eau.
il Le copolymère a essentiellement les mêmes blocs polyéthers, les mêmes blocs polyamides, mais aussi une faible partie des différents réactifs ayant réagi de façon aléatoire qui sont répartis de façon statistique le long de la
chaîne polymère.
On ferme et on chauffe le réacteur sous agitation comme dans la
première étape du procédé en deux étapes décrit plus haut. La pression s'établit entre 5 et 30 bars. Quand elle n'évolue plus, on met le réacteur sous pression réduite tout en maintenant une agitation vigoureuse des réactifs fondus. La réaction est suivie comme précédemment pour le procédé en deux 10 étapes.
Le catalyseur utilisé dans le procédé en une étape est de préférence un sel du métal (M) et d'un acide organique ou un sel complexe entre l'oxyde de
(M) et/ou l'hydroxyde de (M) et un acide organique.
On peut ajouter dans les copolymères de l'invention des colorants, des
pigments, des charges, des anti UV, des antioxydants.
[Exemples]
Exemple 1
Synthèse d'un 6/ 11 / 12 - PTMG o la séquence PA est de 4000 g.molet de composition 6 / 11 / 12: 10 / 30 / 60 et o le polyéther est le PTMG de
Mn 650.
Les monomères suivants sont introduits dans un autoclave équipé d'un agitateur: 2.49 kg de Lactame 6, 7.5 kg d'amino 11, 15 kg de Lactame 12 et 0.96 kg d'acide adipique. Le mélange ainsi formé est mis sous atmosphère inerte et chauffé jusqu'à ce que la température atteigne 280 OC et 25.5 bars de pression. Après un maintien de 3h, on effectue ensuite une opération de 30 détente de 2h pour revenir à la pression atmosphérique. Le polytétraméthylène glycol de masse 650 g.mol-1 (4 kg) et Zr(OBu)4 (30 g) sont ensuite ajoutés dans le réacteur pour terminer la polymérisation à 240 OC sous pression absolue de 8 mbars (soit 800 Pa). Le produit final a une viscosité inhérente de 1.5 dl/g et un MFI (235 C / 2.16 kg) de 6.15 g/10 mn. Le moulage par injection de plaques 100*100*2 mm confirme la transparence du produit avec une transmission à 460 nm de 68 %, à 560 nm de 78 % et à 700 nm de 85 %, ainsi qu'une opacité d'environ 13 %.
Exemple 2
Synthèse d'un 6 / 12 - PTMG o la séquence PA est de 1300 g.mol-1 et
de composition 6 / 12: 20 / 80 et o le polyéther est le PTMG de Mn 650.
Les monomères suivants sont introduits dans un autoclave équipé d'un agitateur: 3.60 kg de Lactame 6, 14.40 kg de Lactame 12 et 2.32 kg d'acide adipique. Le mélange ainsi formé est mis sous atmosphère inerte et chauffé jusqu'à ce que la température atteigne 280 C et 22 bars de pression. Après un maintien de 3h, on effectue ensuite une opération de détente de 2h pour revenir 15 à la pression atmosphérique. Le polytétraméthylène glycol de masse 650 g.mol1 (9.8 kg) et Zr(OBu)4 (60 g) sont ensuite ajoutés dans le réacteur pour terminer la polymérisation à 240 C sous pression absolue de 13 mbars (1300 Pa). Le produit final a une viscosité inhérente de 1.5 dl/g et un MFI (235 C / 1 kg) de 10.5 g/10mn. Le moulage par injection de plaques 100*100*2 mm confirme la 20 transparence du produit avec une transmission à 460 nm de 66 %, à 560 nm de
77 % et à 700 nm de 84 %, ainsi qu'une opacité d'environ 12 %.
Claims (7)
1 Copolymères à blocs polyamides et blocs polyéthers dans lesquels: les blocs polyamides sont des copolyamides aliphatiques, les blocs polyéthers sont constitués essentiellement de PTMG de masse molaire moyenne en nombre Mn comprise entre 200 et 1000,
la dureté Shore D est supérieure ou égale à 40.
2 Copolymères selon la revendication 1 dans lesquels les blocs polyamides résultent de la condensation d'au moins un acide alpha oméga aminocarboxylique (ou un lactame), au moins une diamine aliphatique et au
moins un diacide carboxylique aliphatique.
3 Copolymères selon la revendication 1 dans lesquels les blocs polyamides résultent de la condensation d'au moins deux acides alpha oméga aminocarboxyliques ou d'au moins deux lactames ayant de 6 à 12 atomes de carbone ou d'un lactame et d'un acide aminocarboxylique n'ayant pas le même
nombre d'atomes de carbone.
4 Copolymères selon la revendication 1 dans lesquels les blocs
polyamides résultent de la condensation d'une diamine aliphatique avec un diacide carboxylique aliphatique et au moins un autre monomère choisi parmi les diamines aliphatiques différentes de la précédente et les diacides 25 aliphatiques différents du précédent.
Copolymères selon l'une quelconque des revendications
précédentes dans lesquels la masse molaire moyenne en nombre Mn des séquences polyamides est comprise entre 500 et 10000. 30 6 Copolymères selon la revendication 5 dans lesquels la masse molaire moyenne en nombre Mn des séquences polyamides est comprise
entre 500 et 4500.
7 Copolymères selon l'une quelconque des revendications
précédentes dans lesquels la masse Mn des séquences polyéthers est
comprise avantageusement entre 300 et 700.
8 Copolymères selon l'une quelconque des revendications 10 précédentes dans lesquels la dureté Shore D est comprise entre 40 et 70.
9 Objets fabriqués avec les copolymères selon l'une quelconque
des revendications précédentes.