DE976043C - Verfahren zur Herstellung von Faeden od. dgl. aus Polymerisaten des Acrylnitrils - Google Patents
Verfahren zur Herstellung von Faeden od. dgl. aus Polymerisaten des AcrylnitrilsInfo
- Publication number
- DE976043C DE976043C DEP6409A DEP0006409A DE976043C DE 976043 C DE976043 C DE 976043C DE P6409 A DEP6409 A DE P6409A DE P0006409 A DEP0006409 A DE P0006409A DE 976043 C DE976043 C DE 976043C
- Authority
- DE
- Germany
- Prior art keywords
- threads
- production
- acrylonitrile polymers
- draft
- strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
(WiGBl. S. 175)
AUSGEGEBEN AM 31. JANUAR 1963
P
640p VIIa/
29
a
des Acrylnitrils
Zusatz zum Patent 974
Gegenstand des Hauptpatentes 974749 ist ein Verfahren zur Herstellung von Fäden od. dgl.
aus Polymerisaten des Acrylnitrils, bei welchem eine Lösung des Polymerisates nach dem Trockenspinnverfahren
mit einem Schachtverzug von mehr als 1:3 versponnen und nach Entfernen der Hauptmenge
des Lösungsmittels vorzugsweise bei einer Temperatur unter ioo° C auf etwa das 2- bis
4fache verstreckt wird. Bereits bei dieser mäßigen Kaltverstreckung der Fäden erhält man, wie im
Hauptpatent näher ausgeführt, Fäden von kleinerem Denier, als aus denselben Düsen nach den
bisher bekannten Verfahren (kleiner Verzug, hohe Verstreckung) hergestellt werden konnten.
Die Erfindung schlägt nun vor, die mit Hochverzug gesponnenen Fäden oder Fadenbündel bei
Temperaturen zwischen 100 und etwa 300 C unterhalb des Zersetzungspunktes auf das 4- bis 1 of ache
zu verstrecken. Hierdurch ist es nicht nur möglich, aus den üblichen Spinndüsen Fäden von bisher
unerreichter Feinheit zu erhalten, sondern diese Fäden besitzen auch eine größere Reißfestigkeit als
die nach den bisher üblichen Verfahren hergestellten.
In der nachfolgenden Tabelle zeigt die erste Zeile die Eigenschaften der nach den bekannten
Verfahren aus Polyacrylnitril in Dimethylformamidlösung gesponnenen Fäden; die zweite Zeile
209 765/20
gibt die entsprechenden Daten für Hochverzugfaden, nach dem Verfahren des Hauptpatentes, wobei
die Werte für Verzug und Verstreckung gegenüber der ersten Zeile vertauscht sind, so daß vergleichbare
Fäden von gleichem Denier erhalten werden. In der letzten Zeile sind die Werte für
Hochverzugfäden angeführt, die bei gleichem Verzug wie für Zeile 2 bei höherer Temperatur hochverstreckt
sind. Die erste Spalte gibt den Verzug, die zweite die Verstreckung und die dritte die
Strecktemperatur an. Die nächsten zwei Spalten nennen die Eigenschaften der so erhaltenen Fäden,
und zwar das Schrumpfvermögen bei spannungsfreiem Erhitzen, den Titer, die Festigkeit in
Reißkilometern und die Dehnung. In der letzten Spalte ist die nach dem spannungsfreien Ausschrumpfen
der Fäden, durch 15- bis ßominutiges
Auskochen in Wasser resultierende Dehnung angegeben. Hierbei wird zugleich die Festigkeit noch
um 2 bis 4Rkm für die Fäden der ersten zwei
und um 4 bis 6 Rkm für die Fäden der letzten Zeile erhöht.
*5 Nr· | Schachtverzug | Verstreckung | Streck temperatur °C |
Schrumpfung % |
Titer den |
Rkm | VoI vor Heißb |
dehnung nach ehandlung |
I 2 ao 3 |
I =3 ι :8 ι :8 |
ι :8 ι :3 ι : 10 |
ISO IOO 150 |
5 bis 10 10 bis 30 3 bis 8 |
2,5 2,5 O,7 |
35 bis 40 25 bis 30 45 bis 50 |
12 20 IO |
18 bis 22 20 bis 40 14 bis 16 |
Die Tabelle zeigt, daß die nach dem erfindüngsgemäßen Verfahren hergestellten. 0,7-den-Fäden
neben einer für die üblichen textlien Zwecke durchaus genügenden Dehnbarkeit eine um etwa 3o°/0
gegenüber den bisher bekannten Fäden, und um etwa 75% gegenüber den Hochverzugfäden des
Hauptpatentes höhere Festigkeit besitzen. Es ist nach dem erfindungsgemäßen Verfahren sogar möglieh,
mit üblichen Spinndüsen Fäden von 0,5 den und etwa 55 Rkm Festigkeit zu erzeugen.
Gemäß dem Verfahren des Hauptpatentes wird eine 25°/0ige Lösung von Polyacrylnitril in Dimethylformamid
durch eine 18-Loch-Düse mit 0,3 mm Lochdurchmesser in einen beheizten
Schacht bei einem Verzug von 1:10 (Abzugsgeschwindigkeit
420 m je Minute) gesponnen und aufgespult. Diese Hochverzugfäden werden mit Hilfe einer Streckvorrichtung, z. B. beheizten Walzen,
sofort oder zu einem späteren Zeitpunkt bei 1500 C Temperatur auf das 7- bis 8fache verstreckt.
Nach der Verstreckung beträgt def Einzeltiter 0,7 den, die Festigkeit 4,5 g/den und die Dehnung
io°/0. Werden die Fäden mit Wasser von Siedehitze
30 Minuten gewaschen, so erhöht sich die Dehnung auf 15% bei geringer Zunahme der
Festigkeit.
Die so hergestellten Fäden sind schrumpffrei und können sowohl als Seide weiterverarbeitet werden,
oder sie können mit einer Schneidmaschine in Stapel geschnitten und als Faser verwandt werden.
Claims (1)
- Patentanspruch:Verfahren zur Herstellung vqn Fäden od.dgl. aus Polymerisaten des Acrylnitrils nach Patent 974749, dadurch gekennzeichnet, daß die mit Hochverzug gesponnenen Fäden oder Fadenbündel bei Temperaturen zwischen 100 und etwa 300 C unterhalb des Zersetzungspunktes auf das 4- bis iofache verstreckt werden.In Betracht gezogene Druckschriften: Britische Patentschrift Nr. 585 368; USA.-Patentschriften Nr. 2404714, 2445042; Zeitschrift »Silk and Rayon«, Januar 1949, Aufsatz von A.J.Hall, »Hinter den Kulissen der neuen Vinyon-N-Fasern«.© 209765/20 1.65