WO2016133364A1 - 봉지 필름 - Google Patents

봉지 필름 Download PDF

Info

Publication number
WO2016133364A1
WO2016133364A1 PCT/KR2016/001608 KR2016001608W WO2016133364A1 WO 2016133364 A1 WO2016133364 A1 WO 2016133364A1 KR 2016001608 W KR2016001608 W KR 2016001608W WO 2016133364 A1 WO2016133364 A1 WO 2016133364A1
Authority
WO
WIPO (PCT)
Prior art keywords
encapsulation
layer
resin
film
encapsulation film
Prior art date
Application number
PCT/KR2016/001608
Other languages
English (en)
French (fr)
Inventor
김현석
유현지
문정옥
양세우
Original Assignee
주식회사 엘지화학
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 엘지화학 filed Critical 주식회사 엘지화학
Priority to US15/309,376 priority Critical patent/US20170077450A1/en
Priority to CN201680001681.0A priority patent/CN106463622B/zh
Priority to JP2016563443A priority patent/JP6580592B2/ja
Publication of WO2016133364A1 publication Critical patent/WO2016133364A1/ko

Abstract

본 출원은 봉지 필름, 이를 포함하는 유기전자장치 및 이를 이용한 유기전자장치의 제조 방법에 관한 것으로서, 외부로부터 유기전자장치로 유입되는 수분 또는 산소를 효과적으로 차단할 수 있고, 취급성 및 가공성 등 기계적 특성이 우수한 봉지 필름 및 이를 포함하는 유기전자장치를 제공한다.

Description

봉지 필름
관련 출원들과의 상호 인용　
본 출원은 2015년 02월 17일자 한국 특허 출원 제10-2015-0024423호에 기초한 우선권의 이익을 주장하며, 해당 한국 특허 출원의 문헌에 개시된　모든 내용은 본 명세서의 일부로서 포함된다.
기술분야
본 출원은 봉지 필름, 이를 포함하는 유기전자장치 및 이를 이용한 유기전자장치의 제조방법에 관한 것이다.
유기전자장치(OED; organic electronic device)는 정공 및 전자를 이용하여 전하의 교류를 발생하는 유기 재료층을 포함하는 장치를 의미하며, 그 예로는, 광전지 장치(photovoltaic device), 정류기(rectifier), 트랜스미터(transmitter) 및 유기발광다이오드(OLED; organic light emitting diode) 등을 들 수 있다.
상기 유기전자장치 중 유기발광다이오드(OLED: Organic Light Emitting Didoe)는 기존 광원에 비하여, 전력 소모량이 적고, 응답 속도가 빠르며, 표시장치 또는 조명의 박형화에 유리하다. 또한, OLED는 공간 활용성이 우수하여, 각종 휴대용 기기, 모니터, 노트북 및 TV에 걸친 다양한 분야에서 적용될 것으로 기대되고 있다.
OLED의 상용화 및 용도 확대에 있어서, 가장 주요한 문제점은 내구성 문제이다. OLED에 포함된 유기재료 및 금속 전극 등은 수분 등의 외부적 요인에 의해 매우 쉽게 산화된다. 따라서, OLED를 포함하는 제품은 환경적 요인에 크게 민감하다. 이에 따라 OLED 등과 같은 유기전자장치에 대한 외부로부터의 산소 또는 수분 등의 침투를 효과적으로 차단하기 위하여 다양한 방법이 제안되어 있다.
본 출원은 외부로부터 유기전자장치로 유입되는 수분 또는 산소를 효과적으로 차단할 수 있는 구조의 형성이 가능하고, 취급성 및 가공성 등 기계적 특성이 우수한 봉지 필름을 제공한다.
본 출원은 봉지 필름에 관한 것이다. 상기 봉지 필름은 예를 들면, OLED 등과 같은 유기전자장치를 봉지 또는 캡슐화하는 것에 적용될 수 있다.
본 명세서에서, 용어 「유기전자장치」는 서로 대향하는 한 쌍의 전극 사이에 정공 및 전자를 이용하여 전하의 교류를 발생하는 유기재료층을 포함하는 구조를 갖는 물품 또는 장치를 의미하며, 그 예로는, 광전지 장치, 정류기, 트랜스미터 및 유기발광다이오드(OLED) 등을 들 수 있으나, 이에 제한되는 것은 아니다. 본 출원의 하나의 예시에서 상기 유기전자장치는 OLED일 수 있다.
예시적인 봉지 필름(10)은 도 1에 나타난 바와 같이 순차로 형성된 보호층(13), 메탈층(12) 및 봉지층(11)을 포함할 수 있다. 상기에서 보호층은 자성체를 포함할 수 있다. 상기 봉지층은 점착제 조성물 또는 접착제 조성물을 포함할 수 있다. 본 출원은, 상기와 같이, 보호층, 메탈층 및 봉지층이 일체로 제공되는 봉지 필름에 관한 것이다. 상기 자성체가 보호층에 포함될 경우, 일체화된 봉지 필름에 대해 자력에 의한 공정이 가능해지고, 이에 따라 공정의 편의가 도모되고 생산성이 향상된다. 하나의 예시에서, 자성체는 자성을 갖는 한 그 종류는 특별히 제한되지 않고, 당업계의 공지의 재료일 수 있다. 예를 들어, 자성체는 Fe3O4, Fe2O3, MnFe2O4, BaFe12O19, SrFe12O19, CoFe2O4, Fe, CoPt, 및 FePt로 이루어진 군으로부터 선택된 1 이상일 수 있다. 자성체는 분말형태로 보호층의 수지 성분과 함께 보호층을 구성할 수 있다. 또한, 본 출원의 구체예에서, 상기 자성체는 수지 성분 100 중량부에 대하여 20 내지 400 중량부, 50 내지 400 중량부, 60 내지 350 중량부, 70 내지 300 중량부, 또는 80 내지 250 중량부로 포함될 수 있다. 상기 자성체가 상기 수치 이상 포함됨으로써, 충분한 자력으로 자석에 의해서 필름이 고정될 수 있고, 이에 따라 필름을 고정하기 위해서 추가 공정이 필요하지 않아 생산성이 향상된다.
본 출원은 상기 보호층은 열전도성 필러를 추가로 포함할 수 있다. 본 출원은 열전도성 필러를 포함함으로써, 메탈층 접합 공정 시 접합계면에서 발생된 열을 보다 빨리 방출시킬 수 있다. 또한 유기전자장치 동작 중 축적되는 열을 신속히 외부로 방출시키고, 이에 따라 유기전자장치 자체의 온도는 더욱 낮게 유지시킬 수 있고, 크랙 및 결함 발생은 감소된다. 하나의 예시에서, 상기 보호층의 열전도도는 0.5 W/mK 이상, 0.7 W/mK 이상, 1 W/mK 이상, 2 W/mK 이상, 또는 3 W/mK 이상일 수 있고, 상한은 특별히 한정되지 않으나 100 W/mK 이하일 수 있다. 열전도성 필러는 당업계의 공지의 재료일 수 있고, 예를 들어, 산화알루미늄, 산화마그네슘, 산화칼슘, 탄산칼슘, 질화붕소, 질화알루미늄, 탄화규소 및 수산화알루미늄으로 이루어진 군으로부터 선택된 1 이상을 포함할 수 있다. 상기 열전도성 필러는 보호층을 구성하는 수지성분 100 중량부에 대하여 200 내지 1500 중량부 또는 300 내지 1400 중량부로 포함될 수 있다.
하나의 예시에서, 보호층은 25℃에서 0.01MPa 내지 500MPa의 인장 탄성률을 가질 수 있다. 전술한 바와 같이, 필름이 보호층, 메탈층 및 봉지층의 일체로 제공될 경우, 고온 공정에서 패널의 휨이 발생할 수 있고, 각층의 얼라인 오차가 발생되는 문제가 있다. 그러나, 본 출원은 상기 보호층의 인장 탄성률의 범위를 상기와 같이 제어함으로써, 상기 문제를 해결할 수 있다. 상기 인장 탄성률의 측정은 당업계의 공지의 방법으로 수행할 수 있다. 예를 들어, 상기 보호층의 두께를 80 ㎛로 제조하고, 제조된 보호층을 제조 시의 코팅 방향을 길이 방향으로 하여, 50 mm×10 mm(길이×폭)의 크기로 재단하여 시편을 제조한 후에, 상기 시편을 길이 방향으로 25 mm만 남도록 양 끝을 테이핑 하였다. 이어서, 테이핑 부분을 잡아 25℃에서 1 mm/min의 속도로 인장하면서, 인장탄성률을 측정하였다. 하나의 예시에서, 상기 보호층의 인장 탄성률은 25℃에서 0.01MPa 내지 500MPa, 0. 1MPa 내지 450MPa, 0.5MPa 내지 400MPa 또는 1MPa 내지 350MPa의 범위 내에 있을 수 있다. 본 출원의 보호층은 선팽창계수가 60 ppm/K 이상 또는 100 ppm/K 이상일 수 있고, 500 ppm/K 이하일 수 있는데, 상기 보호층은 선팽창계수가 높을지라도, 상기와 같이 낮은 인장 탄성률을 가짐으로써, 봉지 필름이 유기전자장치에 적용될 경우, 고온에서 봉지필름의 수축 또는 팽창에도 불구하고, 봉지 필름을 구성하는 각 층의 단차를 최소화하고 패널 휨을 방지할 수 있다.
하나의 예시에서, 본 출원의 보호층 및 메탈층은 하기 일반식 1을 만족할 수 있다.
[일반식 1]
Tp / Tm ≥ 1
상기 일반식 1에서, Tp는 보호층의 두께이고, Tm은 메탈층의 두께이다. 상기와 같이 메탈층의 두께에 대한 보호층의 두께의 비율(Tp / Tm)은 1이상, 1.3이상, 1.5이상, 1.8이상, 2이상 또는 2.1 이상일 수 있다. 상기 보호층의 두께는 40㎛ 내지 400㎛, 50㎛ 내지 380㎛, 55㎛ 내지 350㎛, 60㎛ 내지 330㎛, 70㎛ 내지 300㎛ 또는 80㎛ 내지 280㎛의 범위 내에 있을 수 있다. 또한, 메탈층의 두께는 10㎛ 내지 100㎛, 11㎛ 내지 90㎛, 12㎛ 내지 80㎛, 13㎛ 내지 70㎛, 14㎛ 내지 60㎛, 15㎛ 내지 50㎛ 또는 16㎛ 내지 45㎛의 범위 내에 있을 수 있다. 본 출원은, 보호층의 두께를 상기 수치 이상으로 제어함으로써, 유기전자장치 제조 공정 중 외부 충격에 의한 유기전자소자의 손상 등을 방지할 수 있다. 또한, 본 출원은 보호층의 두께를 상기 수치 이하로 제어함으로써, 상기 필름에 높은 자성을 구현할 수 있다. 또한, 본 출원은 상기 메탈층의 두께를 상기 수치 이하로 제어함으로써, 플랙서블한 특성을 갖는 유기전자장치를 제공할 수 있다. 이에 따라, 상기와 같이 플랙서블 디스플레이에 적용 가능하도록 유연성이 있으면서, 유기전자장치 제조 공정 중 외부로부터 찍힘 등의 손상을 방지할 수 있는 봉지 필름을 제공하기 위해, 메탈층의 두께와 보호층의 두께는 상기 일반식 1의 두께 비율을 만족할 수 있다. 다만, 보호층의 두께가 일정 범위 이상으로 두꺼워지면, 공정 중 소자의 손상 방지는 방지할 수 있지만, 고온에서 유기전자장치의 휨이 발생할 수 있다. 따라서, 보호층의 두께는 400㎛ 이하일 수 있다. 또한, 봉지필름의 보호층이 전술한 바와 같이 상기 인장 탄성률 범위를 만족함으로써, 본 출원은 소자의 손상을 방지할 뿐만 아니라 패널의 휨 발생을 방지하고, 유기전자장치의 얼라인 오차를 최소화하며, 플랙서블 디스플레이에 적용될 수 있는 유기전자장치 봉지 필름을 제공할 수 있다.
본 출원의 구체예에서, 보호층은 메탈층이 습기와의 접촉 시 부식을 방지해주고 공정중의 접힘이나 꺾임 등에 의한 손상을 방지할 수 있다.
하나의 예시에서, 상기 보호층은 수지 성분을 포함할 수 있다. 상기 보호층을 구성하는 소재는 특별히 제한되지 않는다. 하나의 예시에서, 상기 보호층을 구성하는 수지 성분으로서, 폴리오가노실록산, 폴리이미드, 스티렌계 수지 또는 엘라스토머, 폴리올레핀계 수지 또는 엘라스토머, 폴리옥시알킬렌계 수지 또는 엘라스토머, 폴리에스테르계 수지 또는 엘라스토머, 폴리염화비닐계 수지 또는 엘라스토머, 폴리카보네이트계 수지 또는 엘라스토머, 폴리페닐렌설파이드계 수지 또는 엘라스토머, 폴리아미드계 수지 또는 엘라스토머, 아크릴레이트계 수지 또는 엘라스토머, 에폭시계 수지 또는 엘라스토머, 실리콘계 수지 또는 엘라스토머, 및 불소계 수지 또는 엘라스토머로 이루어진 군으로부터 선택된 1 이상을 포함할 수 있으나 이에 한정되는 것은 아니다. 상기 수지 성분은 유리전이온도가 0℃ 미만, -10℃ 미만 또는 -30℃ 미만, -50℃ 미만 또는 -60℃ 미만일 수 있다. 상기에서 유리전이온도란, 약 조사량 1J/cm2 이상의 자외선을 조사한 후의 유리전이온도; 또는 자외선 조사 이후 열경화를 추가로 진행한 후의 유리전이온도를 의미할 수 있다.
본 출원의 구체예에서, 상기 봉지 필름의 메탈층은 투명할 수 있고, 불투명할 수 있다. 한편, 본 명세서에서 용어 메탈층은 무기층과 동일한 의미로 사용될 수 있다. 상기 메탈층은 박막의 메탈 포일(Metal foil) 또는 고분자 기재층에 메탈이 증착되어 있을 수 있다. 상기 고분자 기재층은 전술한 보호층일 수 있다. 메탈층은 열전도성을 가지며, 수분 차단성을 가지는 물질이라면 제한 없이 사용될 수 있다. 메탈층은 금속, 산화금속, 질화금속, 탄화금속, 옥시질화금속, 옥시붕화금속, 및 그의 배합물 중에서 어느 하나를 포함할 수 있다. 예컨대, 메탈층은 하나의 금속에 1 이상의 금속 원소 또는 비금속원소가 첨가된 합금을 포함할 수 있고, 예를 들어, 철-니켈 합금 또는 스테인레스 스틸(SUS)을 포함할 수 있다. 또한, 하나의 예시에서 메탈층은 구리, 알루미늄 니켈, 산화실리콘, 산화알루미늄, 산화티타늄, 산화인듐, 산화 주석, 산화주석인듐, 산화탄탈룸, 산화지르코늄, 산화니오븀, 및 그들의 배합물을 포함할 수 있다. 메탈층은 전해, 압연, 가열증발, 전자빔 증발, 스퍼터링, 반응성 스퍼터링, 화학기상증착, 플라즈마 화학기상증착 또는 전자 사이클로트론 공명 소스 플라즈마 화학기상 증착 수단에 의해 증착될 수 있다. 본 출원의 일 실시예에서, 메탈층은 반응성 스퍼터링에 의해 증착될 수 있다.
바람직하게, 메탈층은 50W/mK 이상, 60W/mK 이상, 70 W/mK 이상, 80 W/mK 이상, 90 W/mK 이상, 100 W/mK 이상, 110 W/mK 이상, 120 W/mK 이상, 130 W/mK 이상, 140 W/mK 이상, 150 W/mK 이상, 200 W/mK 이상 또는 250 W/mK 이상의 열전도도를 갖을 수 있다. 이와 같이 높은 열전도도를 가짐으로써, 메탈층 접합 공정시 접합계면에서 발생된 열을 보다 빨리 방출시킬 수 있다. 또한 높은 열전도도는 유기전자장치 동작 중 축적되는 열을 신속히 외부로 방출시키고, 이에 따라 유기전자장치 자체의 온도는 더욱 낮게 유지시킬 수 있고, 크랙 및 결함 발생은 감소된다.
본 명세서에서 용어 「열전도도」란 물질이 전도에 의해 열을 전달할 수 있는 능력을 나타내는 정도이며, 단위는 W/mK로 나타낼 수 있다. 상기 단위는 같은 온도와 거리에서 물질이 열전달하는 정도를 나타낸 것으로서, 거리의 단위(미터)와 온도의 단위(캘빈)에 대한 열의 단위(와트)를 의미한다.
또한, 메탈층은 25℃에서 10,000MPa 내지 250,000MPa, 20,000MPa 내지 240,000MPa 또는 30,000MPa 내지 230,000MPa 의 인장 탄성률을 가질 수 있다. 메탈층이 상기 인장 탄성률 범위로 제어됨으로써, 본 출원은 패널의 휨 발생을 방지하고, 유기전자장치의 얼라인 오차를 최소화하며, 플랙서블 디스플레이에 적용될 수 있는 유기전자장치 봉지 필름을 제공할 수 있다.
하나의 예시에서, 상기 봉지 필름은 봉지층을 포함할 수 있다. 하나의 예시에서, 상기 봉지층은 단일층 혹은 2 이상의 다층 구조일 수 있다. 2 이상의 층이 봉지층을 구성할 경우, 상기 봉지층의 각 층의 조성은 동일하거나 상이할 수 있다. 하나의 예시에서, 상기 봉지층은 점착제 조성물을 포함하는 점착제층일 수 있다. 또한, 상기 봉지층은 접착제 조성물을 포함하는 접착제층일 수 있다.
본 발명의 구체예에서, 봉지층은 봉지 수지를 포함할 수 있다. 상기 봉지 수지는 유리전이온도가 0℃ 미만, -10℃ 미만 또는 -30℃ 미만, -50℃ 미만 또는 -60℃ 미만일 수 있다. 상기에서 유리전이온도란, 약 조사량 1J/cm2 이상의 자외선을 조사한 후의 유리전이온도; 또는 자외선 조사 이후 열경화를 추가로 진행한 후의 유리전이온도를 의미할 수 있다.
하나의 예시에서, 상기 봉지 수지는 스티렌계 수지 또는 엘라스토머, 폴리올레핀계 수지 또는 엘라스토머, 기타 엘라스토머, 폴리옥시알킬렌계 수지 또는 엘라스토머, 폴리에스테르계 수지 또는 엘라스토머, 폴리염화비닐계 수지 또는 엘라스토머, 폴리카보네이트계 수지 또는 엘라스토머, 폴리페닐렌설파이드계 수지 또는 엘라스토머, 탄화수소의 혼합물, 폴리아미드계 수지 또는 엘라스토머, 아크릴레이트계 수지 또는 엘라스토머, 에폭시계 수지 또는 엘라스토머, 실리콘계 수지 또는 엘라스토머, 불소계 수지 또는 엘라스토머 또는 이들의 혼합물 등을 포함할 수 있다.
상기에서 스티렌계 수지 또는 엘라스토머로는, 예를 들면, 스티렌-에틸렌-부타디엔-스티렌 블록 공중합체(SEBS), 스티렌-이소프렌-스티렌 블록 공중합체(SIS), 아크릴로니트릴-부타디엔-스티렌 블록 공중합체(ABS), 아크릴로니트릴-스티렌-아크릴레이트 블록 공중합체(ASA), 스티렌-부타디엔-스티렌 블록 공중합체(SBS), 스티렌계 단독 중합체 또는 이들의 혼합물이 예시될 수 있다. 상기 올레핀계 수지 또는 엘라스토머로는, 예를 들면, 고밀도폴리에틸렌계 수지 또는 엘라스토머, 저밀도폴리에틸렌계 수지 또는 엘라스토머, 폴리프로필렌계 수지 또는 엘라스토머 또는 이들의 혼합물이 예시될 수 있다. 상기 엘라스토머로는, 예를 들면, 에스터계 열가소성 엘라스토머, 올레핀계 엘라스토머, 실리콘계 엘라스토머, 아크릴계 엘라스토머 또는 이들의 혼합물 등을 사용할 수 있다. 그 중 올레핀계 열가소성 엘라스토머로서 폴리부타디엔 수지 또는 엘라스토머 또는 폴리이소부틸렌 수지 또는 엘라스토머 등이 사용될 수 있다. 상기 폴리옥시알킬렌계 수지 또는 엘라스토머로는, 예를 들면, 폴리옥시메틸렌계 수지 또는 엘라스토머, 폴리옥시에틸렌계 수지 또는 엘라스토머 또는 이들의 혼합물 등이 예시될 수 있다. 상기 폴리에스테르계 수지 또는 엘라스토머로는, 예를 들면, 폴리에틸렌 테레프탈레이트계 수지 또는 엘라스토머, 폴리부틸렌 테레프탈레이트계 수지 또는 엘라스토머 또는 이들의 혼합물 등이 예시될 수 있다. 상기 폴리염화비닐계 수지 또는 엘라스토머로는, 예를 들면, 폴리비닐리덴 클로라이드 등이 예시될 수 있다. 상기 탄화수소의 혼합물로는, 예를 들면, 헥사트리아코탄(hexatriacotane) 또는 파라핀 등이 예시될 수 있다. 상기 폴리아미드계 수지 또는 엘라스토머로는, 예를 들면, 나일론 등이 예시될 수 있다. 상기 아크릴레이트계 수지 또는 엘라스토머로는, 예를 들면, 폴리부틸(메타)아크릴레이트 등이 예시될 수 있다. 상기 에폭시계 수지 또는 엘라스토머로는, 예를 들면, 비스페놀 A 형, 비스페놀 F 형, 비스페놀 S 형 및 이들의 수첨가물 등의 비스페놀형; 페놀노볼락형이나 크레졸노볼락형 등의 노볼락형; 트리글리시딜이소시아누레이트형이나 히단토인형 등의 함질소 고리형; 지환식형; 지방족형; 나프탈렌형, 비페닐형 등의 방향족형; 글리시딜에테르형, 글리시딜아민형, 글리시딜에스테르형 등의 글리시딜형; 디시클로펜타디엔형 등의 디시클로형; 에스테르형; 에테르에스테르형 또는 이들의 혼합물 등이 예시될 수 있다. 상기 실리콘계 수지 또는 엘라스토머로는, 예를 들면, 폴리디메틸실록산 등이 예시될 수 있다. 또한, 상기 불소계 수지 또는 엘라스토머로는, 폴리트리플루오로에틸렌 수지 또는 엘라스토머, 폴리테트라플루오로에틸렌 수지 또는 엘라스토머, 폴리클로로트리플루오로에틸렌 수지 또는 엘라스토머, 폴리헥사플루오로프로필렌수지 또는 엘라스토머, 폴리플루오린화비닐리덴, 폴리플루오린화비닐, 폴리플루오린화에틸렌프로필렌 또는 이들의 혼합물 등이 예시될 수 있다.
상기 나열한 수지 또는 엘라스토머는, 예를 들면, 말레산무수물 등과 그라프트되어 사용될 수도 있고, 나열된 다른 수지 또는 엘라스토머 내지는 수지 또는 엘라스토머를 제조하기 위한 단량체와 공중합되어 사용될 수도 있으며, 그 외 다른 화합물에 의하여 변성시켜 사용할 수도 있다. 상기 다른 화합물의 예로는 카르복실-말단 부타디엔-아크릴로니트릴 공중합체 등을 들 수 있다.
하나의 예시에서 상기 봉지층은 봉지 수지로서 상기 언급한 종류 중에서 올레핀계 엘라스토머, 실리콘계 엘라스토머 또는 아크릴계 엘라스토머 등을 포함할 수 있지만, 이에 제한되는 것은 아니다.
본 발명의 일구체예에서, 상기 봉지 수지는 올레핀계 수지일 수 있다. 하나의 예시에서, 상기 올레핀계 수지는 디엔 및 하나의 탄소-탄소 이중결합을 포함하는 올레핀계 화합물의 공중합체일 수 있다. 여기서, 올레핀계 화합물은 이소부틸렌, 프로필렌 또는 에틸렌 등을 포함할 수 있고, 디엔은 상기 올레핀계 화합물과 중합 가능한 단량체일 수 있으며, 예를 들어, 1-부텐, 2-부텐, 이소프렌 또는 부타디엔 등을 포함할 수 있다. 즉, 본 발명의 봉지 수지는 예를 들면, 이소부틸렌 단량체의 단독 중합체; 이소부틸렌 단량체와 중합 가능한 다른 단량체를 공중합한 공중합체; 또는 이들의 혼합물 등을 사용할 수 있다. 하나의 예시에서, 하나의 탄소-탄소 이중결합을 포함하는 올레핀계 화합물 및 디엔의 공중합체는 부틸 고무일 수 있다. 상기와 같이 특정 수지를 사용함에 따라, 본 출원에서 구현하고자 하는 수분 차단성을 만족시킬 수 있다. 또한, 본 출원은 기존의 이소부틸렌 중합체가 수분 투과도가 낮은 반면, 내열성이 낮기 때문에 봉지층에 특정 가교 구조를 구현하여 내습성과 내열성을 개선시킬 수 있다.
봉지층에서 상기 수지 또는 엘라스토머 성분은 점착제 조성물이 필름 형상으로 성형이 가능한 정도의 중량평균분자량(Mw: Weight Average Molecular Weight)을 가질 수 있다. 예를 들면, 상기 수지 또는 엘라스토머는 약 10만 내지 200만, 10만 내지 150만 또는 10만 내지 100만 정도의 중량평균분자량을 가질 수 있다. 본 명세서에서 용어 중량평균분자량은, GPC(Gel Permeation Chromatograph)로 측정한 표준 폴리스티렌에 대한 환산 수치를 의미한다. 다만, 상기 언급된 중량평균분자량을 상기 수지 또는 엘라스토머 성분이 반드시 가져야 하는 것은 아니다. 예를 들어, 수지 또는 엘라스토머 성분의 분자량이 필름을 형성할 정도의 수준이 되지 않는 경우에는 별도의 바인더 수지가 점착제 조성물에 배합될 수 있다.
또 다른 구체예에서, 본 출원에 따른 봉지 수지는 경화성 수지일 수 있다. 본 발명에서 사용할 수 있는 경화성 수지의 구체적인 종류는 특별히 제한되지 않으며, 예를 들면, 이 분야에서 공지되어 있는 다양한 열경화성 또는 광경화성 수지를 사용할 수 있다. 용어 「열경화성 수지」는, 적절한 열의 인가 또는 숙성(aging) 공정을 통하여, 경화될 수 있는 수지를 의미하고, 용어 「광경화성 수지」는 전자기파의 조사에 의하여 경화될 수 있는 수지를 의미한다. 또한, 상기 경화성 수지는 열경화와 광경화의 특성을 모두 포함하는 듀얼 경화형 수지일 수 있다.
본 출원에서 경화성 수지의 구체적인 종류는 전술한 특성을 가지는 것이라면, 특별히 제한되지 않는다. 예를 들면, 경화되어 접착 특성을 나타낼 수 있는 것으로서, 글리시딜기, 이소시아네이트기, 히드록시기, 카르복실기 또는 아미드기 등과 같은 열경화 가능한 관능기를 하나 이상 포함하거나, 혹은 에폭사이드(epoxide)기, 고리형 에테르(cyclic ether)기, 설파이드(sulfide)기, 아세탈(acetal)기 또는 락톤(lactone)기 등과 같은 전자기파의 조사에 의해 경화 가능한 관능기를 하나 이상 포함하는 수지를 들 수 있다. 또한, 상기와 같은 수지의 구체적인 종류에는, 아크릴 수지, 폴리에스테르 수지, 이소시아네이트 수지 또는 에폭시 수지 등이 포함될 수 있으나, 이에 제한되는 것은 아니다.
본 출원에서는 상기 경화성 수지로서, 방향족 또는 지방족; 또는 직쇄형 또는 분지쇄형의 에폭시 수지를 사용할 수 있다. 본 발명의 일 구현예에서는 2개 이상의 관능기를 함유하는 것으로서, 에폭시 당량이 180 g/eq 내지 1,000 g/eq인 에폭시 수지를 사용할 수 있다. 상기 범위의 에폭시 당량을 가지는 에폭시 수지를 사용하여, 경화물의 접착 성능 및 유리전이온도 등의 특성을 효과적으로 유지할 수 있다. 이와 같은 에폭시 수지의 예에는, 크레졸 노볼락 에폭시 수지, 비스페놀 A형 에폭시 수지, 비스페놀 A형 노볼락 에폭시 수지, 페놀 노볼락 에폭시 수지, 4관능성 에폭시 수지, 비페닐형 에폭시 수지, 트리 페놀 메탄형 에폭시 수지, 알킬 변성 트리 페놀 메탄 에폭시 수지, 나프탈렌형 에폭시 수지, 디시클로펜타디엔형 에폭시 수지 또는 디시클로펜타디엔 변성 페놀형 에폭시 수지의 일종 또는 이종 이상의 혼합을 들 수 있다.
본 출원에서는, 경화성 수지로서 분자 구조 내에 환형 구조를 포함하는 에폭시 수지를 사용할 수 있으며, 방향족기(예를 들어, 페닐기)를 포함하는 에폭시 수지를 사용할 수 있다. 에폭시 수지가 방향족기를 포함할 경우, 경화물이 우수한 열적 및 화학적 안정성을 가지면서, 낮은 흡습량을 나타내어 유기전자장치 봉지 구조의 신뢰성을 향상시킬 수 있다. 본 발명에서 사용할 수 있는 방향족기 함유 에폭시 수지의 구체적인 예로는, 비페닐형 에폭시 수지, 디시클로펜타디엔형 에폭시 수지, 나프탈렌형 에폭시 수지, 디시클로펜타디엔 변성 페놀형 에폭시 수지, 크레졸계 에폭시 수지, 비스페놀계 에폭시 수지, 자일록계 에폭시 수지, 다관능 에폭시 수지, 페놀 노볼락 에폭시 수지, 트리페놀메탄형 에폭시 수지 및 알킬 변성 트리페놀메탄 에폭시 수지 등의 일종 또는 이종 이상의 혼합일 수 있으나, 이에 제한되는 것은 아니다.
본 출원에서 또한, 상기 에폭시 수지로서, 실란 변성 에폭시 수지, 또는 방향족기를 가지는 실란 변성 에폭시 수지를 사용할 수 있다. 이와 같이 실란으로 변성되어 구조적으로 실란기를 가지는 에폭시 수지를 사용할 경우, 유기전자장치의 유리 기판 또는 기판 무기재 등과의 접착성을 극대화시키고, 또한 수분 배리어성이나 내구성 및 신뢰성 등을 향상시킬 수 있다. 본 발명에서 사용할 수 있는 상기와 같은 에폭시 수지의 구체적인 종류는 특별히 제한되지 않고, 이와 같은 수지는 예를 들면, 국도 화학 등과 같은 구입처로부터 용이하게 입수할 수 있다.
또한, 본 출원의 봉지층은 봉지 수지와 상용성이 높고, 상기 봉지 수지와 함께 특정 가교 구조를 형성할 수 있는 활성 에너지선 중합성 화합물을 포함할 수 있다.
예를 들어, 본 출원의 봉지층은 봉지 수지와 함께 활성 에너지선의 조사에 의해 중합될 수 있는 다관능성의 활성 에너지선 중합성 화합물을 포함할 수 있다. 상기 활성 에너지선 중합성 화합물은, 예를 들면, 활성에너지선의 조사에 의한 중합 반응에 참여할 수 있는 관능기, 예를 들면, 아크릴로일기 또는 메타크릴로일기 등과 같은 에틸렌성 불포화 이중결합을 포함하는 관능기, 에폭시기 또는 옥세탄기 등의 관능기를 2개 이상 포함하는 화합물을 의미할 수 있다.
다관능성의 활성에너지선 중합성 화합물로는, 예를 들면, 다관능성 아크릴레이트(MFA; Multifunctional acrylate)를 사용할 수 있다.
또한, 상기 활성 에너지선의 조사에 의해 중합될 수 있는 다관능성의 활성 에너지선 중합성 화합물은 하기 화학식 1을 만족할 수 있다. 또한, 상기 활성 에너지선 중합성 화합물은 봉지 수지 100 중량부에 대하여 5 중량부 내지 30 중량부, 5 중량부 내지 25 중량부, 8 중량부 내지 20 중량부, 10 중량부 내지 18 중량부 또는 12 중량부 내지 18 중량부로 포함될 수 있다.
[화학식 1]
Figure PCTKR2016001608-appb-I000001
상기 화학식 1에서, R1은 수소 또는 탄소수 1 내지 4의 알킬기이고, n은 2 이상의 정수이며, X는 탄소수 3 내지 30의 직쇄, 분지쇄 또는 고리형 알킬기로부터 유도된 잔기를 나타낸다. 상기에서, X가 고리형 알킬기로부터 유도된 잔기인 경우, X는 예를 들어 탄소수 3 내지 30, 탄소수 6 내지 28, 탄소수 8 내지 22, 또는 탄소수 12 내지 20의 고리형 알킬기로부터 유도된 잔기일 수 있다. 또한, X가 직쇄형 알킬기로부터 유도된 잔기인 경우, X는 탄소수 3 내지 30, 탄소수 6 내지 25, 또는 탄소수 8 내지 20의 직쇄 알킬기로부터 유도된 잔기일 수 있다. 또한, X가 분지쇄형 알킬기로부터 유도된 잔기인 경우, X는 탄소수 3 내지 30, 탄소수 5 내지 25, 또는 탄소수 6 내지 20의 분지쇄 알킬기로부터 유도된 잔기일 수 있다.
본 명세서에서 용어 「알킬기로부터 유도된 잔기」란, 특정 화합물의 잔기로서, 알킬기로 구성된 것을 의미할 수 있다. 하나의 예시에서, 상기 화학식 1에서, n이 2인 경우, 상기 X는 알킬렌기일 수 있다. 또한, n이 3 이상인 경우 X는 알킬기의 2 이상의 수소가 탈리되어 상기 화학식 1의 (메타)아크로일기에 결합되어 있을 수 있다.
본 명세서에서 용어 「알킬기」는, 특별히 달리 규정하지 않는 한, 탄소수 1 내지 30, 탄소수 1 내지 25, 탄소수 1 내지 20, 탄소수 1 내지 16, 탄소수 1 내지 12, 탄소수 1 내지 8 또는 탄소수 1 내지 4의 알킬기를 의미할 수 있다. 상기 알킬기는 직쇄형, 분지쇄형 또는 고리형 구조를 가질 수 있으며, 임의적으로 하나 이상의 치환기에 의해서 치환되어 있을 수 있다.
또한, 본 명세서에서 용어 「알킬렌기」 또는 「알킬리덴기」는, 특별히 달리 규정하지 않는 한, 탄소수 2 내지 30, 탄소수, 2 내지 25, 탄소수, 2 내지 20, 탄소수 2 내지 16, 탄소수 2 내지 12, 탄소수 2 내지 10 또는 탄소수 2 내지 8의 알킬렌기 또는 알킬리덴기를 의미할 수 있다. 상기 알킬렌기 또는 알킬리덴기는, 직쇄, 분지쇄 또는 고리형일 수 있다. 또한, 상기 알킬렌기 또는 알킬리덴기는 임의적으로 하나 이상의 치환기에 이해 치환될 수 있다.
본 명세서에서 용어 「알콕시기」는, 특별히 달리 규정하지 않는 한, 탄소수 1 내지 20, 탄소수 1 내지 16, 탄소수 1 내지 12, 탄소수 1 내지 8 또는 탄소수 1 내지 4의 알콕시기를 의미할 수 있다. 상기 알콕시기는, 직쇄, 분지쇄 또는 고리형일 수 있다. 또한, 상기 알콕시기는 임의적으로 하나 이상의 치환기에 이해 치환될 수 있다.
상기 활성 에너지선의 조사에 의해 중합될 수 있는 다관능성의 활성 에너지선 중합성 화합물은 상기 화학식 1을 만족하는 한, 제한없이 사용될 수 있다. 예를 들어, 상기 화합물은 1,4-부탄디올 디(메타)아크릴레이트, 1,3-부틸렌 글리콜 디(메타)아크릴레이트, 1,6-헥산디올 디(메타)아크릴레이트, 1,8-옥탄디올 디(메타)아크릴레이트, 1,12-도데세인디올(dodecanediol) 디(메타)아크릴레이트, 네오펜틸글리콜 디(메타)아크릴레이트, 디시클로펜타닐(dicyclopentanyl) 디(메타)아크릴레이트, 시클로헥산-1,4-디메탄올 디(메타)아크릴레이트, 트리시클로데칸디메탄올(메타)디아크릴레이트, 디메틸롤 디시클로펜탄 디(메타)아크릴레이트, 네오펜틸글리콜 변성 트리메틸프로판 디(메타)아크릴레이트, 아다만탄(adamantane) 디(메타)아크릴레이트, 트리메틸롤프로판 트리(메타)아크릴레이트 또는 이들의 혼합물을 포함할 수 있다.
다관능성의 활성에너지선 중합성 화합물로는, 예를 들면, 분자량이 1,000 미만이며, 관능기를 2개 이상 포함하는 화합물을 사용할 수 있다. 이 경우, 분자량은 중량평균분자량 또는 통상적인 분자량을 의미할 수 있다. 상기 다관능성의 활성에너지선 중합성 화합물에 포함되는 고리 구조는 탄소환식 구조 또는 복소환식 구조; 또는 단환식 또는 다환식 구조의 어느 것이어도 된다.
본 출원의 구체예에서, 봉지층은 라디칼 개시제를 추가로 포함할 수 있다. 라디칼 개시제는 광개시제 또는 열개시제일 수 있다. 광개시제의 구체적인 종류는 경화 속도 및 황변 가능성 등을 고려하여 적절히 선택될 수 있다. 예를 들면, 벤조인계, 히드록시 케톤계, 아미노 케톤계 또는 포스핀 옥시드계 광개시제 등을 사용할 수 있고, 구체적으로는, 벤조인, 벤조인 메틸에테르, 벤조인 에틸에테르, 벤조인 이소프로필에테르, 벤조인 n-부틸에테르, 벤조인 이소부틸에테르, 아세토페논, 디메틸아니노 아세토페논, 2,2-디메톡시-2-페닐아세토페논, 2,2-디에톡시-2-페닐아세토페논, 2-히드록시-2-메틸-1-페닐프로판-1온, 1-히드록시시클로헥실페닐케톤, 2-메틸-1-[4-(메틸티오)페닐]-2-몰포리노-프로판-1-온, 4-(2-히드록시에톡시)페닐-2-(히드록시-2-프로필)케톤, 벤조페논, p-페닐벤조페논, 4,4'-디에틸아미노벤조페논, 디클로로벤조페논, 2-메틸안트라퀴논, 2-에틸안트라퀴논, 2-t-부틸안트라퀴논, 2-아미노안트라퀴논, 2-메틸티오잔톤(thioxanthone), 2-에틸티오잔톤, 2-클로로티오잔톤, 2,4-디메틸티오잔톤, 2,4-디에틸티오잔톤, 벤질디메틸케탈, 아세토페논 디메틸케탈, p-디메틸아미노 안식향산 에스테르, 올리고[2-히드록시-2-메틸-1-[4-(1-메틸비닐)페닐]프로판논] 및 2,4,6-트리메틸벤조일-디페닐-포스핀옥시드 등을 사용할 수 있다.
라디칼 개시제는 활성에너지선 중합성 화합물 100 중량부에 대하여 0.2 중량부 내지 20 중량부, 0.5 내지 18 중량부, 1 내지 15 중량부, 또는 2 중량부 내지 13 중량부의 비율로 포함될 수도 있다. 이를 통해 활성에너지선 중합성 화합물의 반응을 효과적으로 유도하고, 또한 경화 후에 잔존 성분으로 인해 봉지층 조성물의 물성이 악화되는 것을 방지할 수 있다.
하나의 예시에서, 봉지층은 열경화성 화합물을 추가로 포함할 수 있다. 열경화성 화합물은 전술한 다관능성 아크릴레이트를 포함할 수 있다. 이러한 다관능성 아크릴레이트는 전술한 열라디칼 개시제 또는 경화제에 의해 가교될 수 있다.
본 출원의 구체예에서, 봉지 필름의 봉지층은 봉지 수지의 종류에 따라서, 경화제를 추가로 포함할 수 있다. 예를 들어, 전술한 봉지 수지와 반응하여, 가교 구조 등을 형성할 수 있는 경화제를 추가로 포함할 수 있다.
경화제는, 봉지 수지 또는 그 수지에 포함되는 관능기의 종류에 따라서 적절한 종류가 선택 및 사용될 수 있다.
하나의 예시에서 봉지 수지가 에폭시 수지인 경우, 경화제로는, 이 분야에서 공지되어 있는 에폭시 수지의 경화제로서, 예를 들면, 아민 경화제, 이미다졸 경화제, 페놀 경화제, 인 경화제 또는 산무수물 경화제 등의 일종 또는 이종 이상을 사용할 수 있으나, 이에 제한되는 것은 아니다.
하나의 예시에서 상기 경화제로는, 상온에서 고상이고, 융점 또는 분해 온도가 80℃ 이상인 이미다졸 화합물을 사용할 수 있다. 이러한 화합물로는, 예를 들면, 2-메틸 이미다졸, 2-헵타데실 이미다졸, 2-페닐 이미다졸, 2-페닐-4-메틸 이미다졸 또는 1-시아노에틸-2-페닐 이미다졸 등이 예시될 수 있으나, 이에 제한되는 것은 아니다,
경화제의 함량은, 조성물의 조성, 예를 들면, 봉지 수지의 종류나 비율에 따라서 선택될 수 있다. 예를 들면, 경화제는, 봉지 수지 100 중량부에 대하여, 1 중량부 내지 20 중량부, 1 중량부 내지 10중량부 또는 1 중량부 내지 5 중량부로 포함할 수 있다. 그렇지만, 상기 중량 비율은, 봉지 수지 또는 그 수지의 관능기의 종류 및 비율, 또는 구현하고자 하는 가교 밀도 등에 따라 변경될 수 있다.
봉지 수지가 활성 에너지선의 조사에 의해 경화될 수 있는 수지인 경우, 개시제로는, 예를 들면, 양이온 광중합 개시제를 사용할 수 있다.
양이온 광중합 개시제로는, 오늄 염(onium salt) 또는 유기금속염(organometallic salt) 계열의 이온화 양이온 개시제 또는 유기 실란 또는 잠재성 황산(latent sulfonic acid) 계열이나 비이온화 양이온 광중합 개시제를 사용할 수 있다. 오늄염 계열의 개시제로는, 디아릴이오도늄 염(diaryliodonium salt), 트리아릴술포늄 염(triarylsulfonium salt) 또는 아릴디아조늄 염(aryldiazonium salt) 등이 예시될 수 있고, 유기금속 염 계열의 개시제로는 철 아렌(iron arene) 등이 예시될 수 있으며, 유기 실란 계열의 개시제로는, o-니트릴벤질 트리아릴 실리 에테르(o-nitrobenzyl triaryl silyl ether), 트리아릴 실리 퍼옥시드(triaryl silyl peroxide) 또는 아실 실란(acyl silane) 등이 예시될 수 있고, 잠재성 황산 계열의 개시제로는 α-설포닐옥시 케톤 또는 α-히드록시메틸벤조인 설포네이트 등이 예시될 수 있으나, 이에 제한되는 것은 아니다.
하나의 예시에서 양이온 개시제로는, 이온화 양이온 광중합 개시제를 사용할 수 있다.
하나의 예시에서, 봉지층은 점착 부여제를 추가로 포함할 수 있으며, 상기 점착 부여제는 바람직하게 수소화된 환형 올레핀계 중합체일 수 있다. 점착 부여제로는, 예를 들면, 석유 수지를 수소화하여 얻어지는 수소화된 석유 수지를 사용할 수 있다. 수소화된 석유 수지는 부분적으로 또는 완전히 수소화될 수 있으며, 그러한 수지들의 혼합물일 수도 있다. 이러한 점착 부여제는 점착제 조성물과 상용성이 좋으면서도 수분 차단성이 우수하고, 유기 휘발 성분이 낮은 것을 선택할 수 있다. 수소화된 석유 수지의 구체적인 예로는, 수소화된 테르펜계 수지, 수소화된 에스테르계 수지 또는 수소화된 다이사이클로펜타디엔계 수지 등을 들 수 있다. 상기 점착 부여제의 중량평균분자량은 약 200 내지 5,000 일 수 있다. 상기 점착 부여제의 함량은 필요에 따라 적절하게 조절할 수 있다. 예를 들면, 점착 부여제의 함량은 후술하는 겔 함량 등을 고려하여 선택될 수 있고, 하나의 예시에 따르면, 점착제 조성물의 고형분 100 중량부 대비 5 중량부 내지 100 중량부, 8 내지 95 중량부, 10 중량부 내지 93 중량부 또는 15 중량부 내지 90 중량부의 비율로 포함될 수 있다.
봉지층은, 필요한 경우에, 수분 흡착제를 추가로 포함할 수 있다. 본 명세서에서 용어 「수분 흡착제(moisture absorbent)」는, 예를 들면, 후술하는 봉지 필름으로 침투한 수분 내지는 습기와의 화학적 반응을 통해 상기를 제거할 수 있는 물질을 의미할 수 있다. 본 발명의 봉지층이 수분 흡착제를 포함할 경우, 필름으로 형성 시, 후술하는 광투과도을 만족시키지 못할 수 있지만, 그 대신 우수한 수분 차단성을 구현할 수 있다. 구체적으로, 상기 봉지층은 필름으로 형성 시, 유기전자장치를 봉지하는 것에 적용될 수 있다. 이 경우, 상기 봉지층은 수분 흡착제를 포함하지 않거나 소량 포함하여, 전면 발광(top emission)형 유기전자장치의 봉지에 적용되거나; 또는 수분 흡착제를 포함하여 우수한 수분 차단성을 나타내어, 배면 발광(bottom emission)형의 유기전자장치의 봉지에 적용될 수 있으나, 이에 한정되는 것은 아니다.
예를 들어, 수분 흡착제는 봉지층 또는 봉지 필름 내에 고르게 분산된 상태로 존재할 수 있다. 여기서 고르게 분산된 상태는 봉지층 또는 봉지 필름의 어느 부분에서도 동일 또는 실질적으로 동일한 밀도로 수분 흡착제가 존재하는 상태를 의미할 수 있다. 상기에서 사용될 수 있는 수분 흡착제로는, 예를 들면, 금속 산화물, 황산염 또는 유기 금속 산화물 등을 들 수 있다. 구체적으로, 상기 황산염의 예로는, 황산마그네슘, 황산나트륨 또는 황산니켈 등을 들 수 있으며, 상기 유기 금속 산화물의 예로는 알루미늄 옥사이드 옥틸레이트 등을 들 수 있다. 상기에서 금속산화물의 구체적인 예로는, 오산화인(P2O5), 산화리튬(Li2O), 산화나트륨(Na2O), 산화바륨(BaO), 산화칼슘(CaO) 또는 산화마그네슘(MgO) 등을 들 수 있고, 금속염의 예로는, 황산리튬(Li2SO4), 황산나트륨(Na2SO4), 황산칼슘(CaSO4), 황산마그네슘(MgSO4), 황산코발트(CoSO4), 황산갈륨(Ga2(SO4)3), 황산티탄(Ti(SO4)2) 또는 황산니켈(NiSO4) 등과 같은 황산염, 염화칼슘(CaCl2), 염화마그네슘(MgCl2), 염화스트론튬(SrCl2), 염화이트륨(YCl3), 염화구리(CuCl2), 불화세슘(CsF), 불화탄탈륨(TaF5), 불화니오븀(NbF5), 브롬화리튬(LiBr), 브롬화칼슘(CaBr2), 브롬화세슘(CeBr3), 브롬화셀레늄(SeBr4), 브롬화바나듐(VBr3), 브롬화마그네슘(MgBr2), 요오드화바륨(BaI2) 또는 요오드화마그네슘(MgI2) 등과 같은 금속할로겐화물; 또는 과염소산바륨(Ba(ClO4)2) 또는 과염소산마그네슘(Mg(ClO4)2) 등과 같은 금속염소산염 등을 들 수 있으나, 이에 제한되는 것은 아니다. 봉지층에 포함될 수 있는 수분 흡착제로는 상술한 구성 중 1 종을 사용할 수도 있고, 2 종 이상을 사용할 수도 있다. 하나의 예시에서 수분 흡착제로 2 종 이상을 사용하는 경우 소성돌로마이트(calcined dolomite) 등이 사용될 수 있다.
이러한 수분 흡착제는 용도에 따라 적절한 크기로 제어될 수 있다. 하나의 예시에서 수분 흡착제의 평균 입경이 10 내지 15000 nm 정도로 제어될 수 있다. 상기 범위의 크기를 가지는 수분 흡착제는 수분과의 반응 속도가 너무 빠르지 않아 보관이 용이하고, 봉지하려는 소자에 손상을 주지 않고, 효과적으로 수분을 제거할 수 있다.
수분 흡착제의 함량은, 특별히 제한되지 않고, 목적하는 차단 특성을 고려하여 적절하게 선택될 수 있다.
봉지층은 필요한 경우, 수분 차단제를 또한 포함할 수 있다. 본 명세서에서 용어 「수분 차단제(moisture blocker)」는, 수분과의 반응성이 없거나 낮으나, 수분 내지는 습기의 필름 내에서의 이동을 차단하거나 방해할 수 있는 물질을 의미할 수 있다. 수분 차단제로는, 예를 들면, 클레이, 탈크, 침상 실리카, 판상 실리카, 다공성 실리카, 제올라이트, 티타니아 또는 지르코니아 중 1 종 또는 2 종 이상을 사용할 수 있다. 또한, 수분 차단제는 유기물의 침투가 용이하도록 유기 개질제 등에 의하여 표면 처리가 될 수 있다. 이러한 유기 개질제로는, 예를 들면, 디메틸 벤질 수소화 탈로우 4차 암모늄(dimethyl benzyl hydrogenatedtallow quaternaty ammonium), 디메틸 수소화 탈로우 4차 암모늄(dimethyl dihydrogenatedtallow quaternary ammonium), 메틸 탈로우 비스-2-하이드록시에틸 4차 암모늄(methyl tallow bis-2-hydroxyethyl quaternary ammonium), 디메틸 수소화 탈로우 2-에틸헥실 4차 암모늄(dimethyl hydrogenatedtallow 2-ethylhexyl quaternary ammonium), 디메틸 탈수소화 탈로우 4차 암모늄(dimethyl dehydrogenated tallow quaternary ammonium) 또는 이들의 혼합물인 유기 개질제 등이 사용될 수 있다.
수분 차단제의 함량은, 특별히 제한되지 않고, 목적하는 차단 특성을 고려하여 적절하게 선택될 수 있다.
봉지층에는 상술한 구성 외에도 용도 및 후술하는 봉지 필름의 제조 공정에 따라 다양한 첨가제가 포함될 수 있다. 예를 들어, 봉지층은 경화성 물질, 가교제 또는 필러 등을 목적하는 물성에 따라 적정 범위의 함량으로 포함할 수 있다.
본 출원의 구체예에서, 상기 봉지층은 전술한 바와 같이 단층 구조로 형성될 수 있고, 또한 2 이상의 층으로 형성될 수 있다. 예를 들어, 봉지 필름은 전술한 봉지층을 포함하는 제1층 및 점착성 수지 또는 접착성 수지를 포함하는 제2층을 포함할 수 있다. 상기 제2층에 포함되는 점착성 수지 또는 접착성 수지는 전술한 봉지 수지와 동일하거나 상이할 수 있으며, 통상의 기술자가 목적하는 바에 따라 적절하게 선택할 수 있다. 또한, 상기 제1층 및 제2층은 각각 수분 흡착제를 포함하거나 포함하지 않을 수 있다.
본 출원의 구체예에서, 상기 제1층 또는 제2층은 전술한 수지 이외에 다른 구성, 예를 들면, 전술한 활성 에너지선 중합성 화합물, 열경화성 화합물, 라디칼 개시제, 점착 부여제, 수분 흡착제, 수분차단제, 분산제 또는 실란 화합물 등을 포함할 수 있으며, 제1층과 제2층의 구성은 서로 동일하거나 상이할 수 있다. 또한, 제2층은 경화성 물질, 경화제 또는 필러 등을 목적하는 물성에 따라 적정 범위의 함량으로 포함할 수 있다. 한편, 상기 수분 흡착제의 함량은, 상기 봉지 필름이 유기전자소자의 봉지에 적용되는 점을 고려할 때, 소자의 손상 등을 고려하여 제어할 수 있다. 예를 들어, 소자와 접촉하는 층에 소량의 수분 흡착제를 구성하거나, 수분 흡착제를 포함하지 않을 수 있다. 하나의 예시에서, 소자와 접촉하는 제2층은 봉지 필름이 함유하는 수분 흡착제 전체 질량에 대해서 0 내지 20%의 수분 흡착제를 포함할 수 있다. 또한, 소자와 접촉하지 않는 제1층은 봉지 필름이 함유하는 수분 흡착제 전체 질량에 대해서 80 내지 100%의 수분 흡착제를 포함할 수 있다.
제1층과 추가적으로 적층되는 제2층의 적층 순서는 특별히 한정되지 않으며, 제1층 상에 제2층이 형성될 수 있고, 반대로 제2층 상에 제1층이 형성될 수 있다. 또한, 봉지층은 3개 이상의 층으로 구성될 수 있으며, 예를 들면, 상기 제1층이 2 이상의 층으로 포함되거나, 상기 제2층이 2 이상의 층으로 포함될 수 있다.
또한, 본 발명에 따른 봉지 필름은 100 ㎛ 두께로 제조된 상태에서, 상기 필름의 두께 방향에 대하여 측정한 투습도(Water Vapor Transmission Rate)가 100℉ 및 100%의 상대 습도 하에서 50 g/m2·day 이하, 40 g/m2·day 이하, 30 g/m2·day 이하, 20 g/m2·day 이하 또는 10 g/m2·day 이하일 수 있다. 이러한 투습도를 가지도록 메탈층 및 봉지층의 조성이나 가교 조건 등을 조절하여, 전자 장치의 봉지 또는 캡슐화 구조에 적용되었을 때에 외부로부터 침투하는 수분이나 산소 등을 효과적으로 차단하여 소자를 안정적으로 보호할 수 있는 봉지 또는 캡슐화 구조를 구현할 수 있다. 상기 투습도는 낮을수록 우수한 수분 차단성을 나타낼 수 있는 것이므로, 그 하한은 특별히 한정되지 않으나, 예를 들어, 0 g/m2·day 일 수 있다.
봉지 필름은, 기재 필름 또는 이형 필름(이하, 「제 1 필름」이라 칭하는 경우가 있다.)을 추가로 포함하고, 상기 봉지층이 상기 기재 또는 이형 필름상에 형성되어 있는 구조를 가질 수 있다. 상기 구조는 또한 상기 보호층 상에 형성된 기재 또는 이형 필름(이하, 「제 2 필름」이라 칭하는 경우가 있다.)을 추가로 포함할 수 있다.
본 출원에서 사용할 수 있는 상기 제 1 필름의 구체적인 종류는 특별히 한정되지 않는다. 본 출원에서는 상기 제 1 필름으로서, 예를 들면, 이 분야의 일반적인 고분자 필름을 사용할 수 있다. 본 출원에서는, 예를 들면, 상기 기재 또는 이형 필름으로서, 폴리에틸렌테레프탈레이트 필름, 폴리테트라플루오르에틸렌 필름, 폴리에틸렌 필름, 폴리프로필렌 필름, 폴리부텐 필름, 폴리부타디엔 필름, 염화비닐 공중합체 필름, 폴리우레탄 필름, 에틸렌-비닐 아세테이트 필름, 에틸렌-프로필렌 공중합체 필름, 에틸렌-아크릴산 에틸 공중합체 필름, 에틸렌-아크릴산 메틸 공중합체 필름 또는 폴리이미드 필름 등을 사용할 수 있다. 또한, 본 출원의 상기 기재 필름 또는 이형 필름의 일면 또는 양면에는 적절한 이형 처리가 수행되어 있을 수도 있다. 기재 필름의 이형 처리에 사용되는 이형제의 예로는 알키드계, 실리콘계, 불소계, 불포화에스테르계, 폴리올레핀계 또는 왁스계 등을 사용할 수 있고, 이 중 내열성 측면에서 알키드계, 실리콘계 또는 불소계 이형제를 사용하는 것이 바람직하지만, 이에 제한되는 것은 아니다.
본 출원에서 상기와 같은 기재 필름 또는 이형 필름(제 1 필름)의 두께는 특별히 한정되지 않고, 적용되는 용도에 따라서 적절히 선택될 수 있다. 예를 들면, 본 출원에서 상기 제 1 필름의 두께는 10 ㎛ 내지 500 ㎛, 바람직하게는 20 ㎛ 내지 200 ㎛ 정도일 수 있다. 상기 두께가 10 ㎛ 미만이면 제조 과정에서 기재 필름의 변형이 쉽게 발생할 우려가 있고, 500 ㎛를 초과하면, 경제성이 떨어진다.
본 출원의 봉지 필름에 포함되는 봉지층의 두께는 특별히 제한되지 않고, 상기 필름이 적용되는 용도를 고려하여 하기의 조건에 따라 적절하게 선택할 수 있다. 봉지층의 두께는 5 ㎛ 내지 200 ㎛, 바람직하게는 5 ㎛ 내지 100 ㎛ 정도일 수 있다. 봉지층의 두께가 5 ㎛ 미만일 경우 충분한 수분차단 능력을 발휘할 수 없으며, 200 ㎛ 초과할 경우 공정성을 확보하기가 어려우며, 수분 반응성으로 인하여 두께 팽창이 커서 유기발광소자의 증착막에 손상을 입힐 수 있으며 경제성이 떨어진다.
본 출원은 또한 봉지 필름의 제조 방법에 관한 것이다. 예시적인 봉지 필름은, 상기 봉지층을 필름 또는 시트 형상으로 성형하는 것을 포함할 수 있다.
하나의 예시에서 상기 방법은, 전술한 봉지층을 구성하는 성분을 포함하는 코팅액을 기재 또는 이형 필름 상에 시트 또는 필름 형상으로 적용하고, 상기 적용된 코팅액을 건조하는 것을 포함할 수 있다.
코팅액은, 예를 들면, 상기 기술한 각 봉지층의 성분을 적절한 용매에 용해 또는 분산시켜 제조할 수 있다. 하나의 예시에서 상기 봉지층은, 필요한 경우 상기 수분 흡착제 또는 필러를 용매에 용해 또는 분산시키고, 분쇄한 후에 분쇄된 상기 수분 흡착제 또는 필러를 봉지 수지와 혼합하는 것을 포함하는 방식으로 제조할 수 있다.
코팅액 제조에 사용되는 용제의 종류는 특별히 한정되지 않는다. 다만, 용제의 건조 시간이 지나치게 길어지거나, 혹은 고온에서의 건조가 필요할 경우, 작업성 또는 봉지 필름의 내구성 측면에서 문제가 발생할 수 있으므로, 휘발 온도가 150°C 이하인 용제를 사용할 수 있다. 필름 성형성 등을 고려하여, 상기 범위 이상의 휘발 온도를 가지는 용제를 소량 혼합하여 사용할 수 있다. 용제로는, 메틸에틸케톤(MEK), 아세톤, 톨루엔, 디메틸포름아미드(DMF), 메틸셀로솔브(MCS), 테트라히드로퓨란(THF), 자일렌 또는 N-메틸피롤리돈(NMP) 등의 일종 또는 이종 이상이 예시될 수 있으나, 이에 제한되는 것은 아니다.
상기 코팅액을 기재 또는 이형 필름에 적용하는 방법은 특별히 한정되지 않으며, 예를 들면, 나이프 코트, 롤 코트, 스프레이 코트, 그라비어 코트, 커튼 코트, 콤마 코트 또는 립 코트 등과 같은 공지의 코팅 방식을 적용할 수 있다.
적용된 코팅액을 건조하여, 용제를 휘발시키고 봉지층을 형성할 수 있다. 상기 건조는, 예를 들면, 70°C 내지 150°C의 온도에서 1분 내지 10분 동안 수행될 수 있다. 상기 건조의 조건은, 사용된 용제의 종류를 고려하여 변경될 수 있다.
각각의 제1층 및 제2층을 적층하는 방법도 특별히 한정되지 않는다. 예를 들면, 별도의 이형 필름에 형성된 제1층 및 제2층을 서로 합판하여 다층 구조의 봉지 필름을 형성할 수도 있으며, 제1층 위에 바로 제2층을 형성할 수도 있으며, 그 반대로 제조할 수도 있다.
건조에 이어서 봉지층 상에 메탈층 및 보호층을 형성할 수 있다. 메탈층을 형성하는 방법은 당업계의 공지의 기술을 사용하여 형성할 수 있다. 예를 들어, 메탈층은 메탈 포일(metal foil)로 형성되거나 보호층에 메탈이 증착되어 형성될 수 있다. 예를 들어, 메탈층은 전해 또는 압연의 방식으로 제조될 수 있다.
본 출원은 또한 유기전자장치에 관한 것이다. 상기 유기전자장치는, 도 2에 도시된 바와 같이, 기판(21); 상기 기판(21) 상에 형성된 유기전자소자(22); 및 상기 유기전자소자(22)를 봉지하는 전술한 봉지필름(10)을 포함할 수 있다. 상기 봉지 필름은 유기전자소자의 전면, 예를 들면 상부 및 측면을 모두 봉지하고 있을 수 있다. 상기 봉지 필름은 점착제 조성물 또는 접착제 조성물을 가교된 상태로 함유하는 봉지층을 포함할 수 있다. 또한, 상기 봉지층이 유기전자소자의 전면에 접촉하도록 유기전자장치가 형성되어 있을 수 있다.
상기에서 유기전자소자는 예를 들면, 유기발광소자일 수 있다.
또한, 본 발명은 유기전자장치의 제조 방법에 관한 것이다. 상기 유기전자장치는 예를 들면, 상기 봉지 필름을 사용하여 제조할 수 있다.
상기 봉지층은, 유기전자장치에서 우수한 수분 차단 특성을 나타내면서 상기 기판과 메탈층을 효율적으로 고정 및 지지하는 구조용 봉지층으로서 형성될 수 있다.
또한, 상기 봉지층은, 전면 발광(top emission) 또는 배면 발광(bottom emission) 등의 유기전자장치의 형태와 무관하게 안정적인 봉지층으로 형성될 수 있다.
본 명세서 용어 봉지층은 유기전자소자의 상부 및 측면을 모두 커버하는 점착제를 의미할 수 있다.
상기 유기전자장치의 제조를 위해서는 예를 들면, 상부에 유기전자소자가 형성된 기판에 전술한 봉지 필름이 상기 유기전자소자를 커버하도록 적용하는 단계; 및 상기 봉지 필름을 경화하는 단계를 포함할 수 있다. 상기 봉지 필름의 경화 단계는 봉지층의 경화를 의미한다.
본 명세서에서 용어 「경화」란 가열 또는 UV 조사 공정 등을 거쳐 본 발명의 점착제 조성물이 가교 구조를 형성하여 점착제의 형태로 제조하는 것을 의미할 수 있다. 또는, 접착제 조성물을 접착제 형태로 제조하는 것을 의미할 수 있다.
구체적으로, 기판으로 사용되는 글라스 또는 고분자 필름상에 진공 증착 또는 스퍼터링 등의 방법으로 투명 전극을 형성하고, 상기 투명전극상에 예를 들면, 정공 수송층, 발광층 및 전자 수송층 등으로 구성되는 발광성 유기 재료의 층을 형성한 후에 그 상부에 전극층을 추가로 형성하여 유기전자소자를 형성할 수 있다. 이어서, 상기 공정을 거친 기판의 유기전자소자의 전면을, 상기 봉지 필름의 봉지층이 덮도록 위치시킨다.
본 출원의 봉지 필름은, OLED 등과 같은 유기전자장치의 봉지 또는 캡슐화에 적용될 수 있다. 상기 필름은 또한 외부로부터 유기전자장치로 유입되는 수분 또는 산소를 효과적으로 차단할 수 있는 구조의 형성이 가능하고, 취급성 및 가공성 등 기계적 특성이 우수하다.
도 1은 본 출원의 하나의 예시에 따른 봉지 필름을 나타내는 단면도이다.
도 2는 본 출원의 하나의 예시에 따른 유기전자장치를 나타내는 단면도이다.
[부호의 설명]
10: 봉지 필름
11: 봉지층
12: 메탈층
13: 보호층
21: 기판
22: 유기전자소자
이하 본 발명에 따르는 실시예 및 본 발명에 따르지 않는 비교예를 통하여 본 발명을 보다 상세히 설명하나, 본 발명의 범위가 하기 제시된 실시예에 의해 제한되는 것은 아니다.
실시예 1
봉지층 용액의 제조
봉지수지로서 부틸 고무 50g (BR068, EXXON), 점착 부여제로서 수첨 탄화수소수지 24g (Eastotac H-100L), 단관능성 아크릴레이트 2-(2-Ethoxyethoxy)ethyl Acrylate 15g, 다관능성의 활성 에너지선 중합성 화합물로서 트리메티롤프로판 트리아크릴레이트 10g 및 라디칼 개시제로서 2,2-디메톡시-1,2-디페닐에탄-1-온 1g (Irgacure651, Ciba)을 투입하고, 톨루엔으로 고형분이 15 중량% 정도가 되도록 희석하여 코팅 용액을 제조하였다.
보호층 및 메탈층의 제조
Dow corning사의 Sylgard 184(폴리디메틸실록산)를 주제와 경화제가 100:20의 중량비율로 되도록 혼합하고 자성체로서 스트론튬 페라이트 (Sigma Aldrich사)를 상기 주제 100중량부 대비 50 중량부로 추가로 혼합하여 보호층용 코팅액을 제조하고, 상기 코팅액을 50㎛의 알루미늄 필름 상에 100㎛의 두께로 코팅하였다.
봉지 필름의 제조
상기 준비된 봉지층 용액을 이형 PET의 이형면에 도포하고 100℃ 오븐에서 15분간 건조하여 두께 50㎛의 봉지층을 형성하고 이를 다시 상기 알루미늄 필름과 합판하여 봉지필름을 제조하였다. 제조된 필름에 자외선을 2 J/cm2 조사한 샘플에 대하여 물성을 측정한다.
실시예 2
자성체를 수지성분 100중량부 대비 100 중량부로 포함한 것을 제외하고는 실시예 1과 동일한 방법으로 봉지 필름을 제조하였다.
실시예 3
자성체를 수지성분 100중량부 대비 300 중량부로 포함한 것을 제외하고는 실시예 1과 동일한 방법으로 봉지 필름을 제조하였다.
실시예 4
자성체를 수지성분 100중량부 대비 30 중량부로 포함한 것을 제외하고는 실시예 1과 동일한 방법으로 봉지 필름을 제조하였다.
비교예 1
보호층에 자성체를 투입하지 않은 것을 제외하고 실시예 1과 동일한 방법으로 봉지 필름을 제조하였다.
실험예 1 - 자성에 의한 유지력 평가
실시예 및 비교예를 통해 제조된 봉지 필름의 자성에 의한 유지력을 하기와 같이 평가하였다. 상기 보호층, 메탈층 및 봉지층을 50 × 10 mm의 크기로 재단하여 시편을 제조한 후에, 상기 시편의 보호층을 SUS 시트 상에 10 × 10 mm 면적이 겹치도록 위치시켰다. 이어서, 이를 90도로 세워 100g의 무게의 추를 연결하여 24시간 동안 유지력을 평가하여 밀린거리를 측정하였다.
부착여부 밀린 거리(mm)
실시예 1 O 2
실시예 2 O 1
실시예 3 O 0
실시예 4 O 10
비교예 1 X -

Claims (17)

  1. 자성체를 포함하는 보호층; 상기 보호층 상에 형성된 메탈층; 및 상기 메탈층 상에 형성된 봉지층을 포함하는 유기전자소자 봉지 필름.
  2. 제 1 항에 있어서, 보호층 및 메탈층은 하기 일반식 1을 만족하는 봉지 필름:
    [일반식 1]
    Tp / Tm ≥ 1
    상기 일반식 1에서, Tp는 보호층의 두께이고, Tm은 메탈층의 두께이다.
  3. 제 1 항에 있어서, 보호층의 두께는 40 내지 400㎛의 범위 내에 있는 봉지 필름.
  4. 제 1 항에 있어서, 메탈층의 두께는 10 내지 100㎛의 범위 내에 있는 봉지 필름.
  5. 제 1 항에 있어서, 보호층은 25℃에서 0.01MPa 내지 500MPa의 인장 탄성률을 가지는 봉지 필름.
  6. 제 1 항에 있어서, 보호층은 폴리오가노실록산, 폴리이미드, 스티렌계 수지 또는 엘라스토머, 폴리올레핀계 수지 또는 엘라스토머, 폴리옥시알킬렌계 수지 또는 엘라스토머, 폴리에스테르계 수지 또는 엘라스토머, 폴리염화비닐계 수지 또는 엘라스토머, 폴리카보네이트계 수지 또는 엘라스토머, 폴리페닐렌설파이드계 수지 또는 엘라스토머, 폴리아미드계 수지 또는 엘라스토머, 아크릴레이트계 수지 또는 엘라스토머, 에폭시계 수지 또는 엘라스토머, 실리콘계 수지 또는 엘라스토머, 및 불소계 수지 또는 엘라스토머로 이루어진 군으로부터 선택된 1 이상인 수지성분을 포함하는 봉지 필름.
  7. 제 6 항에 있어서, 자성체는 수지성분 100 중량부에 대하여 50 내지 400 중량부로 포함되는 봉지 필름.
  8. 제 1 항에 있어서, 자성체는 Fe3O4, Fe2O3, MnFe2O4, BaFe12O19, SrFe12O19, CoFe2O4, Fe, CoPt, 및 FePt로 이루어진 군으로부터 선택된 1 이상을 포함하는 봉지 필름.
  9. 제 1 항에 있어서, 메탈층은 금속, 산화금속, 질화금속, 탄화금속, 옥시질화금속, 옥시붕화금속, 및 그의 배합물 중 어느 하나를 포함하는 봉지 필름.
  10. 제 1 항에 있어서, 메탈층은 알루미늄, 구리, 니켈, 산화실리콘, 산화알루미늄, 산화티타늄, 산화인듐, 산화 주석, 산화주석인듐, 산화탄탈룸, 산화지르코늄, 산화니오븀, 및 그들의 배합물 중 어느 하나를 포함하는 봉지 필름.
  11. 제 1 항에 있어서, 봉지층은 단일층 혹은 2 이상의 층으로 형성되어 있는 봉지 필름.
  12. 제 1 항에 있어서, 봉지층은 봉지 수지를 포함하는 봉지 필름.
  13. 제 12 항에 있어서, 봉지층은 활성 에너지선 중합성 화합물을 추가로 포함하는 봉지 필름.
  14. 제 1 항에 있어서, 봉지층은 수분 흡착제를 포함하는 봉지 필름.
  15. 기판; 기판 상에 형성된 유기전자소자; 및 상기 유기전자소자를 봉지하는 제 1 항에 따른 봉지 필름을 포함하는 유기전자장치.
  16. 제 15 항에 있어서, 봉지 필름의 봉지층이 유기전자소자의 전면을 커버하고 있는 유기전자장치.
  17. 상부에 유기전자소자가 형성된 기판에 제 1 항에 따른 봉지 필름이 상기 유기전자소자를 커버하도록 적용하는 단계; 및 상기 봉지 필름을 경화하는 단계를 포함하는 유기전자장치의 제조 방법.
PCT/KR2016/001608 2015-02-17 2016-02-17 봉지 필름 WO2016133364A1 (ko)