WO2010084526A1 - 非水電解質二次電池及びその製造方法 - Google Patents

非水電解質二次電池及びその製造方法 Download PDF

Info

Publication number
WO2010084526A1
WO2010084526A1 PCT/JP2009/000238 JP2009000238W WO2010084526A1 WO 2010084526 A1 WO2010084526 A1 WO 2010084526A1 JP 2009000238 W JP2009000238 W JP 2009000238W WO 2010084526 A1 WO2010084526 A1 WO 2010084526A1
Authority
WO
WIPO (PCT)
Prior art keywords
positive electrode
current collector
electrolyte secondary
secondary battery
battery
Prior art date
Application number
PCT/JP2009/000238
Other languages
English (en)
French (fr)
Inventor
上田敦史
村岡芳幸
Original Assignee
パナソニック株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by パナソニック株式会社 filed Critical パナソニック株式会社
Priority to US12/529,094 priority Critical patent/US8389161B2/en
Priority to PCT/JP2009/000238 priority patent/WO2010084526A1/ja
Priority to KR1020097013706A priority patent/KR101154771B1/ko
Priority to JP2009519726A priority patent/JPWO2010084526A1/ja
Priority to CN200980000100A priority patent/CN101842922A/zh
Publication of WO2010084526A1 publication Critical patent/WO2010084526A1/ja

Abstract

　非水電解質二次電池は、正極集電体上に正極活物質及び結着剤を含む正極合剤層が形成された正極４と、負極５と、正極４と負極５との間に介在された多孔質絶縁層６と、非水電解液とを有している。正極４の引っ張り伸び率は、３．０％以上である。非水電解質二次電池は、通常作動状態での充電終止電圧が、４．３Ｖ以上である。

Description

非水電解質二次電池及びその製造方法
　本発明は、非水電解質二次電池及びその製造方法に関し、特に、充電終止電圧が４．３Ｖ以上の非水電解質二次電池及びその製造方法に関する。
　近年、移動体通信機器、及び携帯電子機器の主電源として利用される非水電解質二次電池は、起電力が高く、高エネルギー密度である，という特徴を有する。非水電解質二次電池において用いられる正極活物質の材料としては、例えば、コバルト酸リチウム（ＬｉＣｏＯ2）、及びニッケル酸リチウム（ＬｉＮｉＯ2）等のリチウム遷移金属複合酸化物が挙げられる。
　リチウム遷移金属複合酸化物からなる正極活物質を用いた非水電解質二次電池（即ち、リチウムイオン二次電池）では、充電終止電圧（ここで、「充電終止電圧」とは、安全に充電を行うことが可能な充電電圧の最高値をいう）の高電圧化が検討されている。これにより、高容量の非水電解質二次電池を提供することが可能である。
　ここで、非水電解質二次電池において、正極活物質として、２種のリチウム遷移金属複合酸化物が混合されてなる正極活物質を用いることが提案されている（例えば特許文献１参照）。これにより、充放電サイクル特性及び熱安定性の低下を伴うことなく、充電終止電圧の高電圧化（例えば４．３Ｖ以上）を試みる。
　特許文献１には、ＬｉＣｏＯ2からなる正極活物質を用い、且つ充電終止電圧を４．３Ｖ以上に高めた非水電解質二次電池において、充放電サイクル特性が低下する（即ち、充放電サイクルが繰り返されるに伴い、電池の容量が低下する）要因は、非水電解液の分解、又はＬｉＣｏＯ2の結晶構造の破壊によるものと推測されている。
　そこで、特許文献１に記載の技術では、２種のリチウム遷移金属複合酸化物が混合されてなる正極活物質のうち、一方のリチウム遷移金属複合酸化物として、ＬｉＣｏＯ2に少なくともＺｒとＭｇとの双方を含有させたリチウム遷移金属複合酸化物を用いる。これにより、非水電解液の分解、又はＬｉＣｏＯ2の結晶構造の破壊を低減し、充放電サイクル特性の低下の防止を試みる。また、他方のリチウム遷移金属複合酸化物として、熱安定性の高いリチウム遷移金属複合酸化物を用いる。これにより、熱安定性の低下の防止を図る。
特開２００６－１６４９３４号公報 特開平５－１８２６９２号公報
　しかしながら、特許文献１に記載の技術のように、正極活物質に対して、充放電サイクル特性の低下防止対策を講じる、即ち、一方のリチウム遷移金属複合酸化物として、ＬｉＣｏＯ2に少なくともＺｒとＭｇとの双方を含有させたリチウム遷移金属複合酸化物を用いるだけでは、充放電サイクル特性の低下を充分に防止することはできない。
　前記に鑑み、本発明の目的は、充電終止電圧を４．３Ｖ以上に高めた非水電解質二次電池において、充放電サイクル特性の低下を防止することである。
　前記の目的を達成するために、本発明に係る非水電解質二次電池は、正極集電体上に正極活物質及び結着剤を含む正極合剤層が形成された正極と、負極と、正極と負極との間に介在された多孔質絶縁層と、非水電解液とを備えた非水電解質二次電池であって、正極の引っ張り伸び率は、３．０％以上であり、通常作動状態での充電終止電圧は、４．３Ｖ以上であることを特徴とする。
　本発明に係る非水電解質二次電池によると、正極の引っ張り伸び率を３．０％以上に高めることにより、充放電サイクルを繰り返しても、正極の断面形状が波打った形状とならない。そのため、全領域に亘って、正極と負極間の距離が均一に確保されるため、充放電反応が均一化する。そのため、充放電サイクルを繰り返しても、電池の容量が低下することはなく、充放電サイクル特性の低下を防止することができる。
　さらに、正極として、引っ張り伸び率が３．０％以上に高められた正極を用いることにより、圧壊によって電池が潰されることがあっても、正極が優先的に破断されることがないため、電池内部で短絡が発生することを防止することができる。
　特に、電池内部で短絡が発生した場合、短絡時に発生する熱エネルギー量は、充電終止電圧を高めるに連れて多くなるため、熱暴走に至る虞が高くなる。即ち、充電終止電圧が４．３Ｖ以上の電池は、一般的な電池（例えば、充電終止電圧が４．２Ｖの電池）に比べて、短絡時に発生する熱エネルギー量が多いため、熱暴走に至る虞が高い。そのため、充電終止電圧が４．３Ｖ以上の電池内部で短絡が発生することを防止することにより、熱暴走に至る虞を大幅に低減することができる。
　本発明に係る非水電解質二次電池において、負極の引っ張り伸び率は、３．０％以上であり、多孔質絶縁層の引っ張り伸び率は、３．０％以上であることが好ましい。
　本発明に係る非水電解質二次電池において、正極は、正極活物質を含む正極合剤スラリーが塗布乾燥された正極集電体を圧延した後、正極合剤スラリーが塗布乾燥された正極集電体に対し、所定温度で熱処理が施された正極であることが好ましい。
　本発明に係る非水電解質二次電池において、正極集電体は、鉄を含有しアルミニウムを主に含むことが好ましい。
　このようにすると、圧延後に施す熱処理の際に溶融された結着剤によって、正極活物質が被覆されることを抑制することができる。
　本発明に係る非水電解質二次電池において、正極集電体中に含有される鉄量は、１．２０重量％以上１．７０重量％以下であることが好ましい。
　前記の目的を達成するために、本発明に係る非水電解質二次電池の製造方法は、正極集電体上に正極活物質及び結着剤を含む正極合剤層が形成された正極と、負極と、正極と負極との間に介在された多孔質絶縁層と、非水電解液とを備えた非水電解質二次電池の製造方法であって、正極を準備する工程（ａ）と、負極を準備する工程（ｂ）と、工程（ａ）及び工程（ｂ）の後に、正極及び負極を、該正極と該負極との間に多孔質絶縁層を介して捲回する、又は積層する工程（ｃ）とを備え、工程（ａ）は、正極集電体上に、正極活物質及び結着剤を含む正極合剤スラリーを塗布乾燥させる工程（ａ１）と、正極合剤スラリーが塗布乾燥された正極集電体を圧延する工程（ａ２）と、工程（ａ２）の後に、所定温度の下、正極合剤スラリーが塗布乾燥された正極集電体に対し、熱処理を施す工程（ａ３）とを含み、正極の引っ張り伸び率は、３．０％以上であり、通常作動状態での充電終止電圧は、４．３Ｖ以上であることを特徴とする。
　本発明に係る非水電解質二次電池の製造方法によると、圧延後に施す熱処理により、正極の引っ張り伸び率を３．０％以上に高めることができる。
　本発明に係る非水電解質二次電池の製造方法において、所定温度は、正極集電体の軟化温度よりも高いことが好ましい。
　本発明に係る非水電解質二次電池の製造方法において、正極集電体は、鉄を含有するアルミニウムからなることが好ましい。
　このようにすると、正極の引っ張り伸び率を３．０％以上に高めるのに必要とされる熱処理温度を低くする、及び／又は正極の引っ張り伸び率を３．０％以上に高めるのに必要とされる熱処理時間を短くすることができるため、圧延後に施す熱処理の際に、溶融された結着剤によって、正極活物質が被覆されることを抑制することができる。
　本発明に係る非水電解質二次電池及びその製造方法によると、正極の引っ張り伸び率を３．０％以上に高めることにより、充放電サイクルを繰り返しても、正極の断面形状が波打った形状とならない。そのため、全領域に亘って、正極と負極間の距離が均一に確保されるため、充放電反応が均一化する。そのため、充放電サイクルを繰り返しても、電池の容量が低下することはなく、充放電サイクル特性の低下を防止することができる。
図１は、本発明の一実施形態に係る非水電解質二次電池の構成を示す断面図である。 図２は、本発明の一実施形態に係る非水電解質二次電池における電極群の構成を模式的に示す拡大断面図である。
符号の説明
　１　　電池ケース
　１ａ　開口
　２　　封口板
　３　　ガスケット
　４　　正極
　４ａ　正極リード
　４Ａ　正極集電体
　４Ｂ　正極合剤層
　５　　負極
　５ａ　負極リード
　５Ａ　負極集電体
　５Ｂ　負極合剤層
　６　　セパレータ（多孔質絶縁層）
　７ａ　上部絶縁板
　７ｂ　下部絶縁板
　８　　電極群
　本件発明者らは、充電終止電圧を４．３Ｖ以上に高めた非水電解質二次電池（以下、単に「電池」と称すこともある）において、充放電サイクル特性が低下する要因について、鋭意検討を重ねたところ、次のことを見出した。充放電サイクルが繰り返されるに伴い、正極の断面形状が波打った形状となる。そのため、全領域に亘って、正極と負極間の距離が均一化されずに不均一化するため、充放電反応が不均一化する。そのため、充放電サイクルが繰り返されるに伴い、電池の容量が低下する（即ち、充放電サイクル特性が低下する）。
　充放電サイクルが繰り返されるに伴い、正極の断面形状が波打った形状となる要因は、次のように推測される。充電終止電圧を高めるに伴い、充電による正極合剤層の膨張が大きくなるため、正極合剤層と正極集電体との界面に歪みが発生する。正極合剤層と正極集電体との界面に歪みが発生した状態で、充放電サイクルが繰り返されると、充放電サイクルが繰り返されるに伴い、正極の断面形状が波打った形状となる。
　上記から判るように、充電終止電圧を４．３Ｖ以上に高めた非水電解質二次電池において、充放電サイクル特性の低下を防止するには、充放電サイクルが繰り返されるに伴い、正極の断面形状が波打った形状となることを防止することが必要であり、正極に対して、充放電サイクル特性の低下防止対策を講じることが必要である（そのため、特許文献１に記載の技術のように、正極活物質に対して、充放電サイクル特性の低下防止対策を講じるだけでは、充放電サイクル特性の低下を充分に防止することはできない）。
　そこで、本件発明者らは、正極に対して講じる充放電サイクル特性の低下防止対策について、鋭意検討を重ねたところ、次のことを見出した。充電終止電圧が４．３Ｖ以上の非水電解質二次電池において、正極の引っ張り伸び率を３．０％以上に高めることにより、充放電サイクル特性の低下を防止することができる。これは、正極の引っ張り伸び率を３．０％以上に高めることにより、充放電サイクルを繰り返しても、正極の断面形状が波打った形状とならないことによるものと考えられる。
　さらに、正極の引っ張り伸び率を３．０％以上に高めることにより、充電終止電圧を高めても、正極合剤層と正極集電体との界面に歪みが発生することを防止することができるため、充放電サイクルを繰り返しても、正極の断面形状が波打った形状とならないものと推測される。
　そこで、本発明は、充電終止電圧が４．３Ｖ以上の非水電解質二次電池において、正極の引っ張り伸び率を３．０％以上に高めることにより、充放電サイクル特性の低下の防止を図るものである。
　ところで、本件出願人が、圧壊によって非水電解質二次電池が潰された場合に電池内部で短絡が発生する要因について、検討したところ、次のことが判った。電極群を構成する正極、負極、及びセパレータのうち、引っ張り伸び率の最も小さい正極が優先的に破断するため、正極の破断部がセパレータを突き破って、正極と負極とが短絡するので、電池内部で短絡が発生する。
　そこで、本件出願人が、正極の引っ張り伸び率を高める方法について、検討したところ、次のことを見出した。正極集電体上に、正極合剤スラリーが塗布乾燥された正極集電体を圧延した後、正極合剤スラリーが塗布乾燥された正極集電体に対し、正極集電体の軟化温度よりも高い温度で熱処理を施すことにより、正極の引っ張り伸び率を高めることができる。
　本件出願人は、上記の知見に基づいて、正極の引っ張り伸び率を所定率以上に高めることにより、圧壊によって潰された電池内部で短絡が発生することを防止する技術を、特願２００７－３２３２１７号（ＰＣＴ／ＪＰ２００８／００２１１４）の出願明細書に開示している。特願２００７－３２３２１７号に開示された技術では、正極の引っ張り伸び率を３．０％以上に高めることにより、圧壊によって電池が潰されることがあっても、正極が優先的に破断することはないため、電池内部で短絡が発生することを防止することができる。
　以下に、圧延後に熱処理を施さなかった正極、及び圧延後に熱処理を施した正極の各々が引っ張られて伸びるメカニズムについて、考察する。
　圧延後に熱処理を施さなかった正極を引っ張って伸ばした場合、正極合剤層に大きなクラックが発生すると同時に、正極が破断する。この要因は、次のように考えられる。正極が伸びるに連れて、正極合剤層に発生する引っ張り応力が増加し、正極集電体に印加される引っ張り応力が増加する。正極合剤層に大きなクラックが発生すると、正極集電体に印加される引っ張り応力が、大きなクラックの発生した箇所に集中する。そのため、クラックの発生と同時に、正極集電体が破断し、延いては、正極が破断する。
　一方、圧延後に熱処理を施した正極を引っ張って伸ばした場合、正極合剤層に多数の微小なクラックを発生しながら、正極は伸び続け、その後、正極が破断する。この要因は、次のように考えられる。正極集電体に印加される引っ張り応力が、多数の微小なクラックの発生した箇所に分散する。そのため、クラックの発生が正極集電体に及ぼす影響は小さく、クラックの発生と同時に、正極集電体が破断されることはない。そのため、クラックの発生後も、正極は伸び続け、分散した引っ張り応力の大きさが、ある大きさＸを超えた時点で正極集電体が破断し、延いては、正極が破断する。ここで、「ある大きさＸ」とは、多数の微小なクラックが発生した正極合剤層が両面に形成された正極集電体が破断されるのに必要とされる大きさをいう。例えば、「ある大きさＸ」とは、正極集電体のみを引っ張って伸ばした場合に正極集電体が破断されるのに必要とされる大きさに近い大きさをいう。
　このように、圧延後に熱処理を施さなかった正極と、圧延後に熱処理を施した正極とは、引っ張られて伸びるメカニズムが異なるため、圧延後に熱処理を施した正極は、圧延後に熱処理を施さなかった正極に比べて、引っ張り伸び率が高くなる。
　また、上記から判るように、正極は、正極集電体の両面に正極合剤層が形成された構成であるため、正極の引っ張り伸び率は、正極集電体の引っ張り伸び率のみによって規制されるものではない。
　さらに、本件出願人は、正極の引っ張り伸び率を高めることを目的に行う熱処理は、圧延後に施すことが必要である，ことを見出した。圧延前に熱処理を施しても、熱処理の際に、正極の引っ張り伸び率を高めることは可能なものの、その後に行う圧延の際に、正極の引っ張り伸び率が低下するため、最終的には、正極の引っ張り伸び率を高めることはできない。なお、両電極を積層する又は捲き取る際の電極材料の集電体からの脱落、又は電極材料の集電体に対する接着性の低下を抑制することを目的に、例えば、正極及び負極とこれら両電極間に介装されるべき多孔質絶縁層とを積層する前又は捲き取る前に、結着剤の再結晶化温度よりも高い温度で結着剤の分解温度より低い温度で、正極及び負極のいずれか一方の電極を熱処理する技術が提案されている（例えば特許文献２参照）。
　さらに、本件出願人が、圧延後に施す熱処理について検討したところ、次のことが判った。熱処理温度が高い場合、及び／又は熱処理時間が長い場合、高温の熱処理により、及び／又は長時間の熱処理により、正極の引っ張り伸び率を所定率以上に高めることは可能なものの、熱処理の際に、溶融された結着剤によって、正極活物質が被覆されるため、電池の容量の低下を招くという問題が新たに発生する。
　そこで、本件出願人が、熱処理温度を低くする、及び／又は熱処理時間を短くする手段について、鋭意検討を重ねたところ、次のことを見出した。正極集電体として、鉄を含有しアルミニウムを主に含む正極集電体を用いることにより、正極の引っ張り伸び率を所定率以上に高めるのに必要とされる熱処理温度を低くする、及び／又は正極の引っ張り伸び率を所定率以上に高めるのに必要とされる熱処理時間を短くすることができる。
　本件出願人は、上記の知見に基づいて、正極集電体として、鉄を含有しアルミニウムを主に含む正極集電体を用いることにより、熱処理の際に溶融された結着剤によって、正極活物質が被覆されることを抑制しながら、正極の引っ張り伸び率を所定率以上に高める技術を、特願２００７－３２３２１７号の出願明細書に開示している。
　以下に、本発明の実施形態について図面を参照しながら説明する。
　（一実施形態）
　以下に、本発明の一実施形態に係る非水電解質二次電池について、図１、及び図２を参照しながら説明する。
　－非水電解質二次電池の構成－
　以下に、本発明の一実施形態に係る非水電解質二次電池の構成について、図１を参照しながら説明する。図１は、本発明の一実施形態に係る非水電解質二次電池の構成を示す断面図である。
　図１に示すように、正極４及び負極５がセパレータ（多孔質絶縁層）６を介して捲回された電極群８が、非水電解液と共に、電池ケース１内に収容されている。電池ケース１の開口１ａは、ガスケット３を介して、封口板２によって封口されている。正極４に取り付けられた正極リード４ａは、正極端子を兼ねる封口板２に接続され、負極５に取り付けられた負極リード５ａは、負極端子を兼ねる電池ケース１に接続されている。電極群８の上端には上部絶縁板７ａが配置され、電極群８の下端には下部絶縁板７ｂが配置されている。
　－電極群の構成－
　以下に、本発明の一実施形態に係る非水電解質二次電池における電極群の構成について、図２を参照しながら説明する。図２は、本発明の一実施形態に係る非水電解質二次電池における電極群の構成を模式的に示す拡大断面図である。
　図２に示すように、正極集電体４Ａの両面に、正極合剤層４Ｂが形成され、負極集電体５Ａの両面に、負極合剤層５Ｂが形成され、正極４と負極５との間に、セパレータ６が介在されている。
　正極４は、圧延後に熱処理が施された正極である。また、正極４の引っ張り伸び率は、３．０％以上である。
　非水電解質二次電池は、通常作動状態での充電終止電圧が、４．３Ｖ以上である。
　正極集電体４Ａは、鉄を含有しアルミニウムを主に含む。正極集電体４Ａ中に含有される鉄量は、１．２０重量％以上１．７０重量％以下であることが好ましい。ここで、「鉄を含有しアルミニウムを主に含む」正極集電体とは、副成分として鉄を含み主成分としてアルミニウムを含み、鉄よりもアルミニウムを多く含む正極集電体である。
　負極５の引っ張り伸び率は、３．０％以上であり、セパレータ６の引っ張り伸び率は、３．０％以上である。
　ここで、「引っ張り伸び率」とは、引っ張る前の正極に対して、破断される直前の正極が伸びた割合をいう。引っ張り伸び率の測定方法は、具体的には例えば、次に示す通りである。正極を用いて作製された幅１５ｍｍ，長さ２０ｍｍの測定用正極において、測定用正極の一端を固定する一方、測定用正極の他端を長さ方向に沿って２０ｍｍ／ｍｉｎの速度で引っ張り、破断される直前の測定用正極の長さを測定し、引っ張る前の測定用正極の長さ（即ち、２０ｍｍ）と、破断される直前の測定用正極の長さとから、引っ張り伸び率を求める。
　なお、正極４を構成する正極合剤層４Ｂは、正極活物質、結着剤、及び導電剤等を含む。正極活物質、結着剤、及び導電剤の各材料としては、公知の材料を用いることができ、例えば、特願２００７－３２３２１７号の出願明細書に開示された材料と同様の材料を用いることができる。また、負極５を構成する負極集電体５Ａの材料としては、公知の材料を用いることができ、例えば、銅、ステンレス鋼、又はニッケル等が挙げられる。負極５を構成する負極合剤層５Ｂは、負極活物質、結着剤、及び導電剤等を含む。負極活物質の材料としては、公知の材料を用いることができ、例えば、特願２００７－３２３２１７号の出願明細書に開示された材料と同様の材料を用いることができる。また、セパレータ６の材料としては、公知の材料を用いることができ、例えば、特願２００７－３２３２１７号の出願明細書に開示された材料と同様の材料を用いることができる。また、非水電解液に含まれる非水溶媒、及び電解質等の各材料としては、公知の材料を用いることができ、例えば、特願２００７－３２３２１７号の出願明細書に開示された材料と同様の材料を用いることができる。
　以下に、本発明の一実施形態に係る非水電解質二次電池の製造方法について、図１を参照しながら説明する。
　－正極の作製－
　まず、正極活物質、結着剤、及び導電剤等を含む正極合剤スラリーを調製する。次に、正極合剤スラリーを、正極集電体上に塗布し、乾燥させる。次に、正極合剤スラリーが塗布乾燥された正極集電体を圧延し、所定厚さの正極用板を得る。次に、正極用板（即ち、圧延され、且つ正極合剤スラリーが塗布乾燥された正極集電体）に対し、所定温度で熱処理を施す。次に、正極用板を、所定幅、所定長さに裁断し、所定厚さ、所定幅、所定長さの正極を作製する。
　ここで、所定温度は、正極集電体の軟化温度よりも高い温度である。また、所定温度は、結着剤の分解温度よりも低い温度であることが好ましい。
　－負極の作製－
　まず、負極活物質、及び結着剤等を含む負極合剤スラリーを調製する。次に、負極合剤スラリーを、負極集電体上に塗布し、乾燥させる。次に、負極合剤スラリーが塗布乾燥された負極集電体を圧延し、所定厚さの負極用板を得る。次に、負極用板を、所定幅、所定長さに裁断し、所定厚さ、所定幅、所定長さの負極を作製する。
　－電池の作製－
　まず、図１に示すように、正極集電体（図２：４Ａ参照）に正極リード４ａを取り付け、負極集電体（図２：５Ａ参照）に負極リード５ａを取り付ける。次に、正極４と負極５とを、それらの間にセパレータ６を介して捲回し、電極群８を構成する。次に、電極群８の上端に上部絶縁板７ａを配置する一方、電極群８の下端に下部絶縁板７ｂを配置する。次に、負極リード５ａを電池ケース１に溶接すると共に、正極リード４ａを封口板２に溶接して、電極群８を電池ケース１内に収容する。次に、電池ケース１内に非水電解液を注液する。次に、電池ケース１の開口１ａを、ガスケット３を介して、封口板２によって封口することにより、電池を作製する。
　本実施形態によると、正極の引っ張り伸び率を３．０％以上に高めることにより、充放電サイクルを繰り返しても、正極の断面形状が波打った形状とならない。そのため、全領域に亘って、正極と負極間の距離が均一に確保されるため、充放電反応が均一化する。そのため、充放電サイクルを繰り返しても、電池の容量が低下することはなく、充放電サイクル特性の低下を防止することができる。
　さらに、正極として、引っ張り伸び率が３．０％以上に高められた正極を用いることにより、圧壊によって電池が潰されることがあっても、正極が優先的に破断されることがないため、電池内部で短絡が発生することを防止することができる。
　特に、電池内部で短絡が発生した場合、短絡時に発生する熱エネルギー量は、充電終止電圧を高めるに連れて多くなるため、熱暴走に至る虞が高くなる。即ち、充電終止電圧が４．３Ｖ以上の電池は、一般的な電池（例えば、充電終止電圧が４．２Ｖの電池）に比べて、短絡時に発生する熱エネルギー量が多いため、熱暴走に至る虞が高い。そのため、充電終止電圧が４．３Ｖ以上の電池内部で短絡が発生することを防止することにより、熱暴走に至る虞を大幅に低減することができる。
　ここで、負極５及びセパレータ６の引っ張り伸び率も、正極４と同様に３．０％以上であることが好ましい。その理由は、次に示す通りである。第１に例えば、正極及びセパレータの引っ張り伸び率が３．０％以上であっても、負極の引っ張り伸び率が３．０％未満であれば、圧壊によって電池が潰されると、負極が優先的に破断されて、電池内部で短絡が発生する。第２に例えば、正極及び負極の引っ張り伸び率が３．０％以上であっても、セパレータの引っ張り伸び率が３．０％未満であれば、圧壊によって電池が潰されると、セパレータが優先的に破断されて、電池内部で短絡が発生する。
　さらに、正極集電体として、鉄を含有しアルミニウムを主に含む正極集電体を用いることにより、正極の引っ張り伸び率を３．０％以上に高めるのに必要とされる熱処理温度を低くする、及び／又は正極の引っ張り伸び率を３．０％以上に高めるのに必要とされる熱処理時間を短くすることができるため、圧延後に施す熱処理の際に、溶融された結着剤によって、正極活物質が被覆されることを抑制することができる。
　なお、本実施形態では、熱処理の際に、溶融された結着剤によって、正極活物質が被覆されることを抑制することを目的に、正極集電体として、鉄を含有しアルミニウムを主に含む正極集電体を用いる場合を具体例に挙げて説明したが、本発明はこれに限定されるものではない。例えば、正極集電体として、鉄を含有せず純度の高いアルミニウムからなる正極集電体を用いてもよい。
　また、本実施形態では、電極群として、図１に示すように、正極４及び負極５がセパレータ６を介して捲回された電極群８を用いた場合を具体例に挙げて説明したが、本発明はこれに限定されるものではない。例えば、電極群として、正極及び負極がセパレータを介して積層された電極群を用いてもよい。
　なお、本発明が奏する効果として、既述の通り、本発明の目的を達成する効果の他に、圧壊によって潰された電池内部で短絡が発生することを防止する効果を、特に挙げたが、その他の効果として、異物が混入した電池内部で短絡が発生することを防止する効果、又は正極及び負極をセパレータを介して捲回する（又は積層する）際に、正極が切れることを防止する効果等を挙げることができる。
　また、本発明における充電終止電圧の範囲として、下限値を４．３Ｖ以上と規定する一方、上限値を規定しないが、上限値としては、例えば、４．５Ｖ以下が挙げられる。その理由は、次に示す通りである。充電終止電圧を４．３Ｖ以上４．５Ｖ以下の範囲内に高めた場合、電池の容量を効果的に高めることができる。一方、充電終止電圧を４．５Ｖ超に高めた場合、電池の容量を効果的に高めることは困難である。
　以下に、正極の引っ張り伸び率と、圧壊によって潰された電池内部で発生する短絡との関係について、表１に示す。表１は、電池１～５の各々における、正極の引っ張り伸び率、及び圧壊試験の結果（即ち、短絡深さ）を示す。
　電池１～４は、正極集電体として、鉄を含有しアルミニウムを主に含む正極集電体を用い、正極として、同一温度（詳細には２８０℃）の下、相異なる熱処理時間（電池１：１０秒，電池２：２０秒，電池３：１２０秒，電池４：１８０秒）の間、圧延後に熱処理が施された正極を用いた電池である。一方、電池５は、正極集電体として、鉄を含有しアルミニウムを主に含む正極集電体を用い、圧延後に熱処理が施されなかった正極を用いた電池である。
Figure JPOXMLDOC01-appb-T000001
　表１に示すように、圧延後に熱処理が施されなかった電池５の場合、正極の引っ張り伸び率は１．５％であるのに対し、圧延後に熱処理が施された電池１～４の場合、正極の引っ張り伸び率は３．０％以上（電池１：３．０％，電池２：５．０％，電池３：６．０％，電池４：６．５％）に高めることができる。
　表１に示すように、圧延後に熱処理が施されなかった電池５の場合、短絡深さは５ｍｍであるのに対し、圧延後に熱処理が施された電池１～４の場合、短絡深さは８ｍｍ以上（電池１：８ｍｍ，電池２：９ｍｍ，電池３：１０ｍｍ，電池４：１０ｍｍ）に深めることができる。
　表１から判るように、圧延後に施す熱処理により、正極の引っ張り伸び率を３．０％以上に高めることができ、これにより、圧壊によって潰された電池内部で短絡が発生することを防止することができる。
　なお、電池１～５の作製方法は、以下に示す通りである。
（電池１）
　（正極の作製）
　まず、平均粒子径が１０μｍのＬｉＮｉ0.82Ｃｏ0.15Ａｌ0.03Ｏ2を準備した。
　次に、導電剤として正極活物質１００．０vol％に対して４．５vol％のアセチレンブラックと、Ｎ－メチルピロリドン（ＮＭＰ）の溶剤に結着剤として正極活物質１００．０vol％に対して４．７vol％のポリフッ化ビニリデン（ＰＶＤＦ）を溶解させた溶液と、正極活物質としてＬｉＮｉ0.82Ｃｏ0.15Ａｌ0.03Ｏ2とを混合し、正極合剤スラリーを得た。この正極合剤スラリーを、正極集電体として厚さ１５μｍの日本製箔株式会社製アルミニウム箔（Ａ８０２１Ｈ－Ｈ１８－１５ＲＫ）の両面に塗布し、乾燥させた。次に、両面に正極合剤スラリーが塗布乾燥された正極集電体を圧延し、厚さ０．１５７ｍｍの正極用板を得た。この正極用板に対し、２８０℃の下、１０秒間、－３０℃の低湿度処理を施した熱風により熱処理を施した。次に、この正極用板を幅５７ｍｍ、長さ５６４ｍｍに裁断して、厚さ０．１５７ｍｍ、幅５７ｍｍ、長さ５６４ｍｍの正極を作製した。
　（負極の作製）
　まず、平均粒子径が約２０μｍになるように、鱗片状人造黒鉛を粉砕及び分級した。
　次に、負極活物質として１００重量部の鱗片状人造黒鉛に、結着剤としてスチレンブタジエンゴムを３重量部とカルボキシメチルセルロースを１重量％含む水溶液１００重量部とを加えて混合し、負極合剤スラリーを得た。この負極合剤スラリーを、負極集電体として厚さ８μｍの銅箔の両面に塗布し、乾燥させた。次に、両面に負極合剤スラリーが塗布乾燥された負極集電体を圧延し、厚さ０．１５６ｍｍの負極用板を得た。この負極用板に対し、窒素雰囲気中、１９０℃の下、８時間、熱風により熱処理を施した。次に、この負極用板を、幅５８．５ｍｍ、長さ７５０ｍｍに裁断して、厚さ０．１５６ｍｍ、幅５８．５ｍｍ、長さ７５０ｍｍの負極を作製した。負極の引っ張り伸び率は５％（即ち、３．０％以上）である。
　（非水電解液の調製）
　非水溶媒として体積比が１：３となるようにエチレンカーボネートとジメチルカーボネートとを混合した混合溶媒に、電池の充放電効率を高める添加剤として５重量％のビニレンカーボネートを添加すると共に、電解質として非水溶媒に対するモル濃度が１．４ｍｏｌ／ｍ3となるようにＬｉＰＦ6を溶解し、非水電解液を調製した。
　（円筒型電池の作製）
　まず、正極集電体にアルミニウム製の正極リードを取り付け、負極集電体にニッケル製の負極リードを取り付けた。次に、正極と負極とを、それらの間にポリエチレン製のセパレータ（引っ張り伸び率が８％（即ち、３．０％以上）のセパレータ）を介して捲回し、電極群を構成した。次に、電極群の上端に上部絶縁板を配置する一方、電極群の下端に下部絶縁板を配置した。次に、負極リードを電池ケースに溶接すると共に、正極リードを内圧作動型の安全弁を有する封口板に溶接して、電極群を電池ケース内に収容した。次に、減圧方式により、電池ケース内に非水電解液を注液した。最後に、電池ケースの開口を、ガスケットを介して、封口板によって封口することにより、電池を作製した。
　このように、２８０℃（即ち、正極集電体の軟化温度よりも高い温度）の下、１０秒間、熱処理が施された正極を有する電池を作製し、作製した電池を電池１と称する。
（電池２）
　（正極の作製）において、正極用板に対し、２８０℃の下、２０秒間、熱処理を施したこと以外は、電池１と同様に電池を作製し、作製した電池を電池２と称する。
（電池３）
　（正極の作製）において、正極用板に対し、２８０℃の下、１２０秒間、熱処理を施したこと以外は、電池１と同様に電池を作製し、作製した電池を電池３と称する。
（電池４）
　（正極の作製）において、正極用板に対し、２８０℃の下、１８０秒間、熱処理を施したこと以外は、電池１と同様に電池を作製し、作製した電池を電池４と称する。
（電池５）
　（正極の作製）において、圧延後に正極用板に対し熱処理を施さなかったこと以外は、電池１と同様に電池を作製し、作製した電池を電池５と称する。
　また、正極の引っ張り伸び率の測定方法は、以下に示す通りである。
　＜正極の引っ張り伸び率の測定＞
　まず、充電を行った各電池１～５を分解し、正極を取り出した。取り出した正極を、幅１５ｍｍ，長さ２０ｍｍに裁断し、測定用正極を作製した。測定用正極の一端を固定する一方、測定用正極の他端を長さ方向に沿って２０ｍｍ／ｍｉｎの速度で引っ張った。そして、破断される直前の測定用正極の長さを測定し、この長さと、引っ張る前の測定用正極の長さ（即ち、２０ｍｍ）とから、正極の引っ張り伸び率を求めた。
　また、圧壊試験における短絡深さの測定方法は、以下に示す通りである。
　＜圧壊試験＞
　まず、電池温度が３０℃の下、直径が６ｍｍの丸棒を、充電を行った各電池１～５に接触させて、丸棒を０．１ｍｍ／ｓｅｃの速度で電池の深さ方向に沿って移動させて、各電池１～５を圧壊した。そして、圧壊によって潰された各電池１～５の内部で短絡が発生した時の深さ方向の変形量（即ち、短絡深さ）を求めた。
　本発明は、充放電サイクル特性の低下を防止することができるため、充電終止電圧が４．３Ｖ以上に高められた非水電解質二次電池及びその製造方法に有用である。

Claims (8)

  1. 　正極集電体上に正極活物質及び結着剤を含む正極合剤層が形成された正極と、負極と、前記正極と前記負極との間に介在された多孔質絶縁層と、非水電解液とを備えた非水電解質二次電池であって、
    　前記正極の引っ張り伸び率は、３．０％以上であり、
    　通常作動状態での充電終止電圧は、４．３Ｖ以上である。
  2. 　請求項１に記載の非水電解質二次電池において、
    　前記負極の引っ張り伸び率は、３．０％以上であり、
    　前記多孔質絶縁層の引っ張り伸び率は、３．０％以上である。
  3. 　請求項１に記載の非水電解質二次電池において、
    　前記正極は、前記正極活物質を含む正極合剤スラリーが塗布乾燥された前記正極集電体を圧延した後、前記正極合剤スラリーが塗布乾燥された前記正極集電体に対し、所定温度で熱処理が施された正極である。
  4. 　請求項１に記載の非水電解質二次電池において、
    　前記正極集電体は、鉄を含有しアルミニウムを主に含む。
  5. 　請求項４に記載の非水電解質二次電池において、
    　前記正極集電体中に含有される鉄量は、１．２０重量％以上１．７０重量％以下である。
  6. 　正極集電体上に正極活物質及び結着剤を含む正極合剤層が形成された正極と、負極と、前記正極と前記負極との間に介在された多孔質絶縁層と、非水電解液とを備えた非水電解質二次電池の製造方法であって、
    　前記正極を準備する工程（ａ）と、
    　前記負極を準備する工程（ｂ）と、
    　前記工程（ａ）及び前記工程（ｂ）の後に、前記正極及び前記負極を、該正極と該負極との間に前記多孔質絶縁層を介して捲回する、又は積層する工程（ｃ）とを備え、
    　前記工程（ａ）は、
    　　前記正極集電体上に、前記正極活物質及び前記結着剤を含む正極合剤スラリーを塗布乾燥させる工程（ａ１）と、
    　　前記正極合剤スラリーが塗布乾燥された前記正極集電体を圧延する工程（ａ２）と、
    　　前記工程（ａ２）の後に、前記正極合剤スラリーが塗布乾燥された前記正極集電体に対し、所定温度で熱処理を施す工程（ａ３）とを含み、
    　前記正極の引っ張り伸び率は、３．０％以上であり、
    　通常作動状態での充電終止電圧は、４．３Ｖ以上である。
  7. 　請求項６に記載の非水電解質二次電池の製造方法において、
    　前記所定温度は、前記正極集電体の軟化温度よりも高い。
  8. 　請求項６に記載の非水電解質二次電池の製造方法において、
    　前記正極集電体は、鉄を含有しアルミニウムを主に含む。
PCT/JP2009/000238 2009-01-22 2009-01-22 非水電解質二次電池及びその製造方法 WO2010084526A1 (ja)