WO2005105883A1 - ポリチオウレタン - Google Patents
ポリチオウレタン Download PDFInfo
- Publication number
- WO2005105883A1 WO2005105883A1 PCT/JP2005/008550 JP2005008550W WO2005105883A1 WO 2005105883 A1 WO2005105883 A1 WO 2005105883A1 JP 2005008550 W JP2005008550 W JP 2005008550W WO 2005105883 A1 WO2005105883 A1 WO 2005105883A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polythiol
- reaction
- polythiourethane
- polythiocarbonate
- hydrocarbon group
- Prior art date
Description
Claims